Next Article in Journal
Challenges of Co–Cr Alloy Additive Manufacturing Methods in Dentistry—The Current State of Knowledge (Systematic Review)
Next Article in Special Issue
Aggregate Roundness Classification Using a Wire Mesh Method
Previous Article in Journal
Fabrication of 3D Printing Scaffold with Porcine Skin Decellularized Bio-Ink for Soft Tissue Engineering
Previous Article in Special Issue
The Use of Wavelet Analysis to Improve the Accuracy of Pavement Layer Thickness Estimation Based on Amplitudes of Electromagnetic Waves
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 13
Issue 16
10.3390/ma13163523
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Acoustic Emission for Determining Early Age Concrete Damage as an Important Indicator of Concrete Quality/Condition before Loading

by
Wiesław Trąmpczyński
*,
Barbara Goszczyńska
and
Magdalena Bacharz
Faculty of Civil Engineering and Architecture, Kielce University of Technology, Al. Tysiąclecia Państwa Polskiego 7, 25-314 Kielce, Poland
*
Author to whom correspondence should be addressed.
Materials 2020, 13(16), 3523; https://doi.org/10.3390/ma13163523
Submission received: 24 June 2020 / Revised: 28 July 2020 / Accepted: 5 August 2020 / Published: 10 August 2020
(This article belongs to the Special Issue Testing of Materials and Elements in Civil Engineering)
Browse Figures
Versions Notes

Abstract

:
Phenomena occurring during the curing of concrete can decrease its mechanical properties, specifically strength, and serviceability, even before it is placed. This is due to excessive stresses caused by temperature gradients, moisture changes, and chemical processes arising during the concreting and in hardened concrete. At stress concentration sites, microcracks form in the interfacial transition zones (ITZ) in the early phase and propagate deeper into the cement paste or to the surface of the element. Microcracks can contribute to the development of larger cracks, reduce the durability of structures, limit their serviceability, and, in rare cases, lead to their failure. It is thus important to search for a tool that allows objective assessment of damage initiation and development in concrete. Objectivity of the assessment lies in it being independent of the constituents and additives used in the concrete or of external influences. The acoustic emission-based method presented in this paper allows damage detection and identification in the early age concrete (before loading) for different concrete compositions, curing conditions, temperature variations, and in reinforced concrete. As such, this method is an objective and effective tool for damage processes detection.

1. Introduction

All engineering projects encounter a range of challenges associated with the most widely used building material, concrete. Being a major problem in current concrete construction, concrete cracking or damage requires a continuous search for new methods and improvement of the existing concrete assessment techniques. This is especially important for fresh concrete, which affects the behavior of concrete under load.
Due to the multilevel nature of concrete, with qualitatively distinct mechanisms taking place during the formation of the concrete, the interaction of various parameters must be considered and the ways to study these relationships and effects have to be found to detect damage. Concrete deterioration occurs primarily through technological cracks (microcracks) and different interfacial properties (cracks) formed at various structural levels, which propagate and initiate operational cracks affecting the usability and strength of concrete elements. The composition of the concrete largely affects its properties. Concrete has high compressive strength and is durable. It can be formed into virtually any shape. Weak points of this material include low tensile strength, shrinkage during the hardening process, and susceptibility to external influences, such as moisture [1], temperature, chemical influences, etc. [2,3].
Particularly important for concrete elements is the early period accompanied by a number of phenomena related to cement hydration [4,5,6].
Chemical reactions occurring in the cement paste during the hydration process, drying out (water evaporation), the cement paste properties themselves (e.g., bleeding in fresh concrete and temperature changes), as well as volumetric changes due to external factors (temperature and air humidity) cause swelling and chemical, plastic, autogenous, and drying shrinkage. These volume changes of hardening concrete generate natural stress, including “micro” stress. Stresses occur most often in the interfacial transition zones (ITZ) between the grains of aggregate and cement paste and decide on the mechanical properties of these zones and their microcracking. At stress concentrations exceeding the tensile strength of concrete, the microcracks may propagate into the deeper layer of the cement paste or to the surface of the element. Examples of damages in the concrete elements shown in Figure 1.
To mitigate microcracking in concrete, an addition of fly ash, an application of the blast-furnace slag cement or low density aggregate is good practice, as demonstrated in [8]. However, in the case of normal-weight concrete, under the influence of destructive external factors, such as high temperature, frost, and loading, these microcracks can develop into cracks, thereby reducing structural durability and serviceability and in rare cases lead to failures, e.g., walls in tanks [9], concrete slabs [10,11], precast elements [12], or other structural elements [13].
Objective assessment of damage formation and development in concrete, which is independent of the components, additives, and external impacts is essential.
Various non-destructive methods have been used for this purpose [14,15,16]. Acoustic emission (AE) is the technique capable of detecting, classifying [17], and locating [18,19] damage in concrete. Traditional use of acoustic emission methods in the building industry includes the monitoring of damage [20,21] and crack development under load [22,23,24,25,26], cement setting and curing [27,28,29,30,31,32], or an assessment of the ASR (alkali–silica reaction) in concrete [33,34].
The research analyzing stress in concrete is especially related to the acoustic emission phenomenon. The acoustic emission method enables the determination of basic parameters of fracture mechanics necessary to analyze the course of stress affecting concrete destruction. Depending on the grade of concrete tested, the criteria for the estimation of the level of stress were established [35,36]. Another approach aimed at estimating the correlation between acoustic emission and stress in compressed concrete is the technique that relies on the Gutenberg–Richter (GBR) law [37]. It was observed that the event frequency in concrete samples during compression corresponds to about 70% of the maximum stress.
Progressive damage of structural elements (Reinforced Concrete beams—RC beams) under bending is assessed using the Keiser effect by monitoring AE activity during cyclic loading [38]. The Keiser effect is used to estimate the stress to which the structural element was previously exposed. To estimate the Kaiser effect (according to NDIS-2421 by JSNDI—the Japanese Society for Non-Destructive Inspection) two ratios are calculated: the load ratio and calm ratio. Their values are the basis for damage qualification as intermediate, minor, or heavy. Digital image correlation (DIC) techniques supporting the AE method are applied for providing information about the level of damage in the RC beams [39]. The relaxation ratio may also be a good indicator of damage status. During initial stages of loading the deflections increase slightly (loading phase). The element is in a serviceable state up to 50% of the deflection limit. In a higher deflection range (50–85%) the structural element is no longer serviceable. Deflection higher than 85% represents the failure of the element. The acoustic emission method is also used for the observation of the crack mouth opening displacement (CMOD). The different nature of dissipated and emitted energy rates was observed in [38] during the loading process.
The methods performed on concrete subjected to compression and bending do not consider an influence of internal stress on concrete strength. At the initial stage of concrete setting, the cement paste shrinks and meets the resistance of aggregate grains that do not shrink. A self-balancing state of compressive and tensile stress arises. If the tensile stresses in the cement paste exceed the tensile strength, microdefects occur. These defects may form in the matrix and in the interfacial transition zone (ITZ) around the aggregate [4] (first destructive process). Internal microcracks interact with each other; they can join together in a damage network. This happens when the structure surrounding the internal microcracks in the cement paste is not able to transfer accumulated stresses. This is when the second destructive process arises. Furthermore, the heterogeneous increase in temperature in the cross-section of the element, as well as water evaporation from the surface layers causes the stretching in the outer zones and compression of the inner zones of the element. These non-stationary and non-linear temperature and humidity areas generate macrostress in the cross-section [36] that can lead to microcracks on the concrete surface (third destructive process) and then their propagation (fourth destructive process). These destructive processes result in discontinuities in the structure. Local structural defects initiate future destruction of the concrete and may reduce the strength of elements, causing their linear deformation and affecting serviceability functions [4,36,40].
There is no information about the assessment procedure of fresh concrete quality by acoustic emission before loading. In most cases analysis of non-loaded concrete is based on ring-down counting, which involves counting how many times the amplitude passes the fixed threshold or event-counting corresponding to number of AE waves recorded by a single sensor [41]. In these cases, acoustic emission signals the damage (crack formation) without being able to identify the underlying processes. Only some of the AE techniques, such as the methods described in [19,23,24], allow for effective identification and location of the destructive process.
The non-invasive acoustic emission method (modified IADP method—Identification of Active Destructive Processes method) presented in [42,43,44] has been shown to be suitable for investigating defect formation process at the early stage of hardening of young concrete.
The study presented in this paper demonstrates that this method is of a general nature and allows observation and identification of destruction processes regardless of the aggregate used, cement types, admixtures added, hardening conditions, temperature, or the presence of reinforcement. It also enables quantitative assessment of destructive processes, which can be important when assessing the strength properties of concrete.
The method can thus be applied to diagnosing elements made of reinforced concrete, controlling the concrete hardening stage, and supporting decision making (e.g., related to demolding), thereby ensuring the reliability of the structure.

2. Materials and Methods

A total of 30 samples (ten concrete series, W2, W3, W4, W5, W6, W7, W8, B2, B3, and B4, of three samples each—A, B, and C) were tested.
Twenty-one samples (W2–W8) were made of C30/37 concrete, six samples (B2, B3) were made of C40/50 concrete and three (W2) of C25/30 concrete. Except for sample W2 (100 mm × 100 mm × 500 mm), all samples had square cross-sections with 150 mm on each side and the length of 600 mm. Samples B2 were made with chemical admixtures (plasticizer and air entraining agent), other samples without admixtures. Samples denoted by “W” were made with limestone aggregate from the Trzuskawica quarry, while these marked with “B” with basalt aggregate from Górażdże quarry. All samples were made with cement CEMI 42,5N—MSR/NA from the Warta cement plant (Cementownia Warta S.A., Trębaczew, Poland) (except B4—CEMIII/A 42,5N—LH/HSR/NA from the cement plant in Małogoszcz, (Cementownia Lafarge Małogoszcz, Poland). The chemical compositions of the cements are compiled in Table 1. Mixture proportions of samples W2–W8 and B2–B4 are listed in Table 2.
Three samples B4 were made with basalt aggregate, blast furnace slag, and cement CEM III without any additions.
The W3 and W4 samples after fabrication were cured in water for 10 days and then tested for 58 days under cyclic temperature variations (Figure 2). Additionally, steel reinforcement was embedded in the W4 samples (Figure 3a).
The samples in series W7 were tested for 58 days without water curing at a constant temperature (+22 ± 2 °C).
Before the test, the AE (Acoustic Emission) sensors were attached to one side of each sample (Figure 3b,c).
To provide appropriate conditions, the test stand was developed, comprising of a thermally and acoustically insulated chamber. A list of samples examined is shown in Table 3.
AE signals were recorded for 58 days in 12-h stages.
The proposed identification of active damage processes (IADP) method was presented in [19,21,24] and applied for damage identification and location in reinforced concrete beams under loading [22]. It relies on the study of AE signals produced by the process causing the deterioration of strength properties in structural elements. The results recorded in samples (AE signals) were compared with the reference signals obtained in the laboratory.
Then the modified version of this method was applied to detect damage in young concrete [23,42].
The IADP method outline is shown in Figure 4. This concept is based on the comparative analysis of waves generated by defects in concrete (detected by sensors) with a database of reference signals created earlier. Preamplifiers with a gain of 35 dB were used to amplify signals generated by defects. Then the signals were detected, transformed into electric signals, measured, recorded, analyzed, and assigned to the reference signals in the database using Noesis software and unsupervised learning methods.
Figure 3 shows the AE sensors arrangement on the test sample. Two piezoelectric sensors with a gain of 25–80 kHz allow not only detection of destructive processes (AE source) but also finding their linear location.
The preliminary reference signal database was developed based on 12 parameters of the AE signal: counts, counts to the peak, amplitude signal duration, signal rise time, signal amplitude, signal energy, signal strength average, effective voltage, absolute energy, average frequency, reverberation frequency, and initiation frequency. There are four destructive processes, described in [2,3,4,7], which may be a source of AE in freshly made concrete before loading. In [42,43,45] damage processes were ascribed to four signal classes recorded in non-loaded concrete (Table 4).

3. Results

3.1. Test Results

The method of assessing the quality of early-age concrete must enable identification of internal defects, regardless of the components used for its manufacture or the conditions under which the structure of hardened concrete forms. The potential of the IADP method was analyzed in this context. Damage processes were identified based on the assessment of signal classes recorded during the test.
The AE signals were recorded for 12 h on days: 1–8, 12, 16, 20, 24, 28, 38, 46, and 57 using MISTRAS software. Then the proposed IADP method was used to analyze the signals (hits). The signals from the tests were compared by 12 AE parameters with signals from the database and assigned to particular classes. The reference database was first developed using K-means clustering and then verified in [43].
An analysis was performed on averaged results of the number of recorded signals (hits) with respect to destructive processes assigned to them. Concrete of each series was investigated by 6 sensors (two sensors were attached to one side of each of the three samples (A, B, and C) in a given series). All signals recorded by these 6 sensors capturing the processes were averaged for each series. The number of signals recorded on average by one sensor was analyzed.
The development of damage processes in series W3, W4, W6, and W7 and B2, B3, and B4 is shown in Figures 5, 7, 9, 10, 12, and 13. Corresponding images of side surface cracks (for samples A, B, and C) are presented in Figures 6, 8, and 11, except W6 and B2-B4 samples, because no cracks were observed on their surfaces.

3.1.1. Concrete W3—Curing in Water, Variable Hardening Temperature (+42 to −5 °C)

Figure 5 shows the values of destructive processes I–III captured during 56 days in samples W3. Throughout the test, 5195 signals (hits) were assigned to the initiation of internal microcracks (damage process I) and 94 AE signals were assigned to damage process II.
Twenty-three hits assigned to surface microcrack formation (destructive process III) were captured in samples A, B, and C (Figure 6).

3.1.2. Reinforced Concrete W4—Curing in Water, Variable Hardening Temperature (+42 to −5 °C)

Figure 7 shows the values of destructive processes I–III captured during 56 days in samples W4. Most processes I and II were recorded during 20 days, later their number decreased. Throughout the test, 8608 hits were assigned to the initiation of internal microcracks (damage process I) and 90 AE signals were assigned to damage process II.
Ten signals assigned to destructive process III (surface microcracks formation) were detected in samples A, B, and C (Figure 8) until day 46.

3.1.3. Concrete W6—Curing in Water, Constant Hardening Temperature of 22 °C

Figure 9 shows the values of destructive processes I and II recorded during 56 days in samples W6. Most processes were recorded during the first week of the test, then their number decreased. Throughout the test, 2560 hits were assigned to the initiation of internal microcracks (damage process I) and 94 AE signals were assigned to damage process II but not on every measuring day.
Class III signals were not captured in the test and no microcracks at the surface of the samples were observed.

3.1.4. Concrete W7—Curing in Water, Constant Hardening Temperature of 22 °C

Figure 10 shows the values of destructive processes I-III captured during 56 days in samples W7. Most processes denoted as I were recorded during 20 days, later their number decreased. Throughout the test, 2795 hits were assigned to the initiation of internal microcracks (damage process I) and six AE signals were assigned to damage process II until day 24.
A few signals Class III assigned to the formation of surface microcracks were recorded in W7 samples. A single surface microcracks were detected on the sides of the samples (Figure 11).

3.1.5. Concrete B2 (with Admixtures)—Curing in Water, Constant Hardening Temperature of 22 °C

Figure 12 shows the values of destructive processes I and II recorded during 56 days in samples B2. Most processes were recorded during the initial days of the test, then their number decreased. Throughout the test, 4519 hits assigned to the initiation of internal microcracks (damage process I) were recorded together with 52 AE signals assigned to damage process II, which practically faded out after day 24 of the test.
Class III signals were not captured in the test and no microcracks at the surface of the samples were observed.

3.1.6. Concrete B4—Curing in Water, Constant Hardening Temperature of 22 °C

Figure 13 shows the values of damage processes I and II captured during 56 days in samples B4. Throughout the test, 2886 hits assigned to the initiation of internal microcracks (damage process I) and 19 AE signals assigned to damage process II were recorded.
Class III signals were not captured in the test and no microcracks at the surface of the samples were observed.

3.2. Destructive Processes Analysis

The analysis of the destructive processes confirmed that the internal structure of the concrete was affected by a range of factors such as aggregate and cement type, curing conditions (especially moisture and ambient temperature) that influence cement hydration, dimensions of the tested element as well as reinforcing bars embedded in the samples.
The identified processes, number of signals and curing conditions are shown in Table 1.
Analysis of the results shows that Class 1 signals were recorded most often in the test. These signals correspond to internal microcrack formation. Most damage processes I were observed during the first week. Their number decreased over time but they did not fade out during 56 days.
The number of Class 2 signals assigned to damage process II (internal microcracks development) was almost an order of magnitude smaller.
Class 3 signals were not recorded in (W2, W6, and B2–B4) concrete samples cured after demolding during 10 days and then hardened at constant temperature (22 ± 2 °C). This indicates that destructive processes III (surface microcrack formation) did not occur, which was confirmed by the observation of the sample.
In addition to tracking the growth of individual destructive processes in time, the number of destructive processes recorded at any given time interval can be also analyzed. Several analyses based on this precise information about damage and damage development in early age concrete were performed.
The results selected for W3 and W4 concrete samples (Figure 14) show that in the case when reinforcement was used, the number of damage processes I (internal microcrack formation) increased (in the analyzed concrete samples by about 65%) due to the occurrence of additional interfacial transition zones (ITZ) between reinforcing bars and cement paste. Damage processes II (propagation of internal microcracks) in the analyzed samples slightly decreased and damage processes III (formation of microcracks on the surface of concrete) were limited by embedded reinforcement.
In Table 5 shown the testing conditions of the samples with the results of number of AE signals and destructive processes in non-loaded concrete obtained by modified IADP acoustic emission method.
Figure 15 shows an influence of variable temperature on the number of damage processes in concrete hardening without initial curing. In the samples hardened at variable temperatures (−5 to +42 °C), far more destructive processes (I–III) were recorded compared to constant temperature conditions. This indicates a significant impact of the heating and cooling cycles on damage processes development in the early-age concrete, which may influence the strength of hardened concrete.

4. Discussion

The presented results for concrete tested under different curing conditions, hardening temperature, aggregate type, concrete strength, dimensions of the sample, presence of the admixtures, and presence of reinforcement show that the proposed AE method is the general method that allows for early age damage identification, damage tracking, and location.
In each of the analyzed cases, it was possible to select damage classes. The emergence of class 1 and class 2 signals does not represent direct effects on the strength level.
Evaluation of concrete strength based on the presented AE method has a qualitative nature. Therefore, it seems expedient to look for a correlation between the intensity of destructive processes and the strength of the concrete obtained.
The data obtained can also be used in several analyses of practical significance such as:
  • In the case of hardening at varied temperature, class II damage (internal microcrack development) increases but class III (surface microcracks) decreases in reinforced concrete, which confirms that the reinforcement restricts most dangerous class III damage (Figure 14),
  • All damage processes increase in the case of hardening at variable temperature (Figure 15).

Author Contributions

Conceptualization, B.G. and W.T.; Methodology, B.G. and W.T.; Software, M.B.; Validation, B.G., W.T. and M.B.; Formal Analysis, B.G.; Investigation, M.B.; Resources, B.G.; Data Curation, M.B.; Writing—Original Draft Preparation, W.T.; Writing—Review and Editing, W.T., B.G. and M.B.; Visualization, M.B.; Supervision, W.T.; Project Administration, B.G.; Funding Acquisition, B.G. and W.T. All authors have read and agreed to the published version of the manuscript.

Funding

This experiments were funded by Project POIG No.01.01.02-10-106/09-01

Acknowledgments

Research was carried out as part of the Project POIG No.01.01.02-10-106/09-01

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Wu, Z.; Wong, H.S.; Buenfeld, N.R. Transport properties of concrete after drying-wetting regimes to elucidate the effects of moisture content hysteresis and microcracking. Cem. Concr. Res. 2017, 98, 136–154. [Google Scholar] [CrossRef]
  2. Kurdowski, W. Cement and Concrete Chemistry; Springer: London, UK, 2014; pp. 1–677. ISBN 978-94-007-7944-0. [Google Scholar]
  3. Neville, A.M. Properties of Concrete, 5th ed.; Prentice Hall: Lincoln, UK, 2011; pp. 1–872. ISBN 978-0-273-75580-7. [Google Scholar]
  4. Bischop, J.; van Mier, J.G.M. How to study drying shrinkage microcracking in cement-based materials using optical and scanning electron microscopy? Cem. Concr. Res. 2002, 279–287. [Google Scholar] [CrossRef]
  5. Boshoff, W.; Combrinck, R. Modelling the severity of plastic shrinkage cracking in concrete. Cem. Concr. Res. 2013, 48, 34–39. [Google Scholar] [CrossRef]
  6. Flaga, K. Impact of residual stress on stress destruction and strength parameters of concrete [Wpływ naprężeń własnych na destrukcję naprężeniową i parametry wytrzymałościowe betonu—in Polish]. Inżynieria Bud. 1995, 6, 315–322. [Google Scholar]
  7. Golewski, G.; Sadowski, T. Analysis of brittle defects in concrete composites [Analiza kruchych uszkodzeń w kompozytach betonowych in Polish]. Czas. Tech. (Bud.) 2007, 104, 55–62. [Google Scholar]
  8. Schindler, A.; Byard, B.; Tankasala, A. Mitigation of early-age cracking in concrete structures. MATEC Web Conf. 2019, 284, 07005. [Google Scholar] [CrossRef]
  9. Flaga, K.; Furtak, K. Problem of thermal and shrinkage cracking in tanks vertical walls and retaining walls near their contact with solid foundation slabs. Archit. Civil Eng. Environ. 2009, 2, 23–30. [Google Scholar]
  10. Linek, M.; Nita, P. Thermal Stress in Concrete Slab of the Airfield Pavement. J. KONBiN 2020, 50. [Google Scholar] [CrossRef]
  11. Kwak, H.G.; Ha, S.J. Plastic shrinkage cracking in concrete slabs. Part I Mag. Concr. Res. 2006, 58, 505–516. [Google Scholar] [CrossRef]
  12. Raczkiewicz, W.; Bacharz, K.; Bacharz, M.; Grzmil, W. Manufacturing Errors of Concrete Cover as a Reason of Reinforcement Corrosion in Precast Element—Case Study. Coatings 2019, 9, 702. [Google Scholar] [CrossRef] [Green Version]
  13. Klemczak, B.; Knoppik-Wróbel, A. Early age thermal and shrinkage cracks in concrete structures—description of the problem. Archit. Civil Eng. Environ. 2011, 2, 35–47. [Google Scholar]
  14. Ranachowski, Z. Application of acoustic emission to fault diagnosis in civil engineering. Roads Bridges 2012, 2, 65–87. [Google Scholar]
  15. Ohtsu, M.; Isoda, T.; Tomoda, Y. Acoustic Emission Techniques Standardized for Concrete Structures. J. Acoust. Emiss. 2007, 25, 21–32. [Google Scholar]
  16. Hoła, J.; Schabowicz, K. State-of-the-art. Non-destructive methods for diagnostics testing of building structures anticipated development trends. Arch. Civil Mech. Eng. 2010, 10, 5–18. [Google Scholar] [CrossRef]
  17. Ohno, K.; Ohtsu, M. Crack classification in concrete based on acoustic emission. Constr. Build. Mater. 2010, 24, 2339–2346. [Google Scholar] [CrossRef]
  18. Ohtsu, M.; Shigeishi, M.; Iwase, H.; Kyotanagit, W. Determination of crack location type and orientation in a concrete structures by acoustic emission. Mag. Concr. Res. 1991, 43, 127–134. [Google Scholar] [CrossRef]
  19. Goszczyńska, B.; Świt, G.; Trąmpczyński, W.; Krampikowska, A.; Tworzewska, J.; Tworzewski, P. Experimental Validation of Concrete Crack Identification and Location with Acoustic Emission Method. Arch. Civil Mech. Eng. 2012, 12, 23–28. [Google Scholar] [CrossRef]
  20. Nair, A.; Cai, C.S. Acoustic emission monitoring of bridges Review and case studies. Eng. Struct. 2010, 32, 1704–1714. [Google Scholar] [CrossRef]
  21. Goszczyńska, B.; Świt, G.; Trąmpczyński, W. Monitoring of active destructive processes as a diagnostic tool for the structure technical state evaluation. Bull. Polish Acad. Sci. Tech. Sci. 2013, 6, 97–109. [Google Scholar] [CrossRef]
  22. Goszczyńska, B.; Świt, G.; Trąmpczyński, W. Analysis of the microcracking process with the Acoustic Emission method with respect to the service life of reinforced concrete structures with the example of the RC beams. Bull. Polish Acad. Sci. Tech. Sci. 2015, 63, 55–63. [Google Scholar] [CrossRef] [Green Version]
  23. Goszczyńska, B. Analysis of the process of crack initiation and evolution in concrete with acoustic emission testing. Arch. Civil Mech. Eng. 2014, 14, 134–143. [Google Scholar] [CrossRef]
  24. Świt, G. Predicting Failure Processes for Bridge—Type Structures made of Prestressed Concrete Beams Using the Acoustic Emission Method [Analiza Procesów Destrukcyjnych w Obiektach Mostowych z Belek Strunobetonowych z Wykorzystaniem Zjawiska Emisji Akustycznej in Polish]; Kielce University of Technology: Kielce, Poland, 2011; pp. 1–179. [Google Scholar]
  25. Karcili, M.; Alver, N.; Ohtsu, M. Application od AE rate-process analysis to damaged concrete structures due to earthquake. Mater. Struct. 2016, 49, 2117–2178. [Google Scholar] [CrossRef]
  26. Wu, K.; Chen, B.; Yao, W. Study on the AE characteristics of fracture process of mortar concrete and steel-fiber-reinforced concrete beams. Cem. Concr. Res. 2000, 30, 1495–1500. [Google Scholar] [CrossRef]
  27. Lura, P.; Couch, J.; Jensen, O.M.; Weiss, J. Early-age Acoustic emission measurements in hydrating cement paste: Evidence for cavitation during solidification due to self-desiccation. Cem. Concr. Res. 2009, 39, 426–432. [Google Scholar] [CrossRef]
  28. Van, D.; Abeele, K.; Desadeleer, W.; De Schutter, G.; Wevers, M. Active and passive monitoring of the early hydration process in concrete using linear and non linear acoustics. Cem. Concr. Res. 2009, 39, 426–432. [Google Scholar]
  29. Watanabe, T.; Ohno, T.; Hashimoto, C. Detection of Thermal Cracks in Early-Age Concrete by AE. Concr. Res. Lett. 2011, 2, 290–294. [Google Scholar]
  30. Iliopoulos, S.N.; Khattabi, Y.E.; Angelis, D.G. Towards the establishment of a continuous nondestructive monitoring technique for fresh concrete. J. Nondestruct. Eval. 2016, 35, 37. [Google Scholar] [CrossRef]
  31. Bischop, J.; van Mier, J.G.M. Drying shrinkage microcracking in cement-based materials. Heron 2002, 47, 163–184. [Google Scholar]
  32. Chotard, T.J.; Smith, A.; Rotureau, D.; Fargot, D.; Gault, C. Acoustic emission characterization of calcium aluminate cement hydration at an early stage. J. Eur. Ceram. Soc. 2003, 23, 387–398. [Google Scholar] [CrossRef]
  33. Sargolzahi, M.; Kodjo, S.A.; Rivard, P.; Rhazi, J. Effectiveness of nondestructive testing for the evaluation of alkali–silica reaction in concrete. Constr. Build. Mater. 2010, 24, 1398–1403. [Google Scholar] [CrossRef]
  34. Świt, G.; Zapała-Sławeta, J. Application of acoustic emission to monitoring the course alkali-silica reaction. Bull. Polish Acad. Sci. Tech. Sci. 2020, 68, 169–178. [Google Scholar]
  35. Newman, K.; Newman, I.B. Failure theories and design criteria for plain concrete. In Proceedings of the Civil Engineering Materials Conference; Te’eni, M., Ed.; Wiley-Interscience: London, UK, 1969; Part 2; pp. 963–996. [Google Scholar]
  36. Hoła, J. Determination of initiating and critical stress levels in compressed plain and high-strength concrete by Acoustic Emission. Arch. Acoust. 2000, 25, 57–65. [Google Scholar]
  37. Carni, D.L.; Scuro, C.; Lamonaca, F.; Sante Olivito, R. Damage analysis of concrete structures by means of acoustic emissions technique. Compos. Part B 2017, 115, 79–86. [Google Scholar] [CrossRef]
  38. Sagar, R.V.; Prasad, B.K.R. Damage limit states of reinforced concrete beams subjected to incremental cyclic loading using ratio analysis of AE parameters. Constr. Build. Mater. 2012, 35, 139–148. [Google Scholar] [CrossRef]
  39. Carpinteri, A.; Lacidogna, G.; Corrado, M.; Di Battista, E. Cracking and crackling in concrete-like materials: A dynamic energy balance. Eng. Fract. Mech. 2016, 155, 130–144. [Google Scholar] [CrossRef]
  40. Kiernożycki, W. Massive Caoncrete Structures [Betonowe Konstrukcje Masywne in Polish]; Polski Cement: Cracow, Poland, 2003. [Google Scholar]
  41. Miller, R.K. Acoustic Emission Testing. In Nondestructive Testing Handbook, 3rd ed.; Moore, P.O., Hill, E.v.K., Eds.; American Society for Nondestructive Testing: Columbus, OH, USA, 2005; Volume 6, pp. 1–446. [Google Scholar]
  42. Bacharz, M. Application of the Acoustic Emission Method to the Evaluation of Destructive Processes in Unloaded Concrete [Wykorzystanie Metody Emisji Akustycznej do Badania Procesów Destrukcyjnych w Betonie Nieobciążonym in Polish]; Kielce University of Technology: Kielce, Poland, 2016. [Google Scholar]
  43. Bacharz, M.; Trąmpczyński, W.; Goszczyńska, B. Acoustic emission method as a tool for the assessment of influence of the temperature variation on destructive processes created in early age concrete. MATEC Web Conf. 2019, 284, 1–12. [Google Scholar] [CrossRef]
  44. Bacharz, M.; Goszczyńska, B.; Trąmpczyński, W. Analysis of destructive processes in non-loaded early-age concrete with acoustic emission method. Procedia Eng. 2015, 108, 245–253. [Google Scholar] [CrossRef] [Green Version]
  45. Bacharz, M.; Trąmpczyński, W. Identification of active destructive processes in unloaded early-age concrete with the use of Acoustic Emission method. In Proceedings of the 2016 Prognostics and System Health Management Conference (PHM-Chengdu), Chengdu, China, 19–21 October 2016; pp. 1–6. [Google Scholar]
Materials 13 03523 g001 550
Figure 1. Examples of damages in the concrete microstructure, adapted from [6,7].
Figure 1. Examples of damages in the concrete microstructure, adapted from [6,7].
Materials 13 03523 g001
Materials 13 03523 g002 550
Figure 2. Temperature conditions during the first 14-days of test.
Figure 2. Temperature conditions during the first 14-days of test.
Materials 13 03523 g002
Materials 13 03523 g003 550
Figure 3. (a) Schematic diagram of reinforcement of W4 samples; (b) sample during the test; and (c) acoustic emission (AE) sensor arrangement (unit: mm).
Figure 3. (a) Schematic diagram of reinforcement of W4 samples; (b) sample during the test; and (c) acoustic emission (AE) sensor arrangement (unit: mm).
Materials 13 03523 g003
Materials 13 03523 g004 550
Figure 4. The concept of the method—IADP (Identification of Active Destructive Processes).
Figure 4. The concept of the method—IADP (Identification of Active Destructive Processes).
Materials 13 03523 g004
Materials 13 03523 g005 550
Figure 5. Number of damage processes I–III obtained from W3 samples.
Figure 5. Number of damage processes I–III obtained from W3 samples.
Materials 13 03523 g005
Materials 13 03523 g006 550
Figure 6. Surface microcrack distribution on sides of the W3 samples. Linear location of destructive processes III (AE signal class 3) in W3 samples obtained by the AE (Acoustic Emission) method is marked in red.
Figure 6. Surface microcrack distribution on sides of the W3 samples. Linear location of destructive processes III (AE signal class 3) in W3 samples obtained by the AE (Acoustic Emission) method is marked in red.
Materials 13 03523 g006
Materials 13 03523 g007 550
Figure 7. Number of damage processes I–III obtained from W4 samples.
Figure 7. Number of damage processes I–III obtained from W4 samples.
Materials 13 03523 g007
Materials 13 03523 g008 550
Figure 8. Surface microcracks distribution on sides of the W4 samples. Linear location of destructive processes III (AE signal class 3) in W4 samples obtained by the AE method is marked in red.
Figure 8. Surface microcracks distribution on sides of the W4 samples. Linear location of destructive processes III (AE signal class 3) in W4 samples obtained by the AE method is marked in red.
Materials 13 03523 g008
Materials 13 03523 g009 550
Figure 9. Number of damage processes I–III obtained from W6 samples.
Figure 9. Number of damage processes I–III obtained from W6 samples.
Materials 13 03523 g009
Materials 13 03523 g010 550
Figure 10. Number of damage processes I–III obtained from W7 samples.
Figure 10. Number of damage processes I–III obtained from W7 samples.
Materials 13 03523 g010
Materials 13 03523 g011 550
Figure 11. Surface microcracks distribution on sides of the W7 samples.
Figure 11. Surface microcracks distribution on sides of the W7 samples.
Materials 13 03523 g011
Materials 13 03523 g012 550
Figure 12. Number of damage processes I–III obtained from B2 samples.
Figure 12. Number of damage processes I–III obtained from B2 samples.
Materials 13 03523 g012
Materials 13 03523 g013 550
Figure 13. Number of damage processes I–III obtained from B4 samples.
Figure 13. Number of damage processes I–III obtained from B4 samples.
Materials 13 03523 g013
Materials 13 03523 g014 550
Figure 14. Number of hits accompanying processes I–III recorded in W3 and W4 samples (10 days curing, varied temperature, and with and without reinforcement).
Figure 14. Number of hits accompanying processes I–III recorded in W3 and W4 samples (10 days curing, varied temperature, and with and without reinforcement).
Materials 13 03523 g014
Materials 13 03523 g015 550
Figure 15. Number of hits accompanying processes I–III recorded in W7 and W8 samples (without curing and constant and varied temperature).
Figure 15. Number of hits accompanying processes I–III recorded in W7 and W8 samples (without curing and constant and varied temperature).
Materials 13 03523 g015
Table
Table 1. Cement composition (%).
Table 1. Cement composition (%).
CementCaOMgOSiO2Al2O3Fe2O3SO3Na2OeqCl−
CEM I66.030.7921.233.663.212.630.430.076
CEM III 2.690.810.066
Table
Table 2. Mixture proportions (kg/m3).
Table 2. Mixture proportions (kg/m3).
SymbolAggregate 2–16Sand 0–2CEMI/CEMIIIWaterAir Entraining AgentPlasticizer
W3–W81110 1740338 (CEMI)16900
W21073 1777290 (CEMI)18800
B21312 2691360 (CEMI)1500.361.98
B3, B41312 2691360 (CEMIII)18000
1 limestone aggregate, 2 basalt aggregate.
Table
Table 3. Sample parameters and testing conditions.
Table 3. Sample parameters and testing conditions.
SeriesWater Curing (days)Hardening TemperatureCement TypeConcrete Class
W210constant 22 ± 2 °CCEMIC25/30
W310varied −5 to + 42 °CCEMIC30/37
W4 (reinforced)10varied −5 to + 42 °CCEMIC30/37
W510constant 22 ± 2 °CCEMIC30/37
W6 (100 × 100 × 500)10constant 22 ± 2 °CCEMIC30/37
W7 (without curing)noneconstant 22 ± 2 °CCEMIC30/37
W8 (without curing)nonevaried −5 to +42 °CCEMIC30/37
B2 (with admixtures)10constant 22 ± 2° CCEMIC40/50
B3 different agregate type)10constant 22 ± 2 °CCEMIC40/50
B410constant 22 ± 2 °CCEM IIIC30/37
Table
Table 4. Destructive processes by the IADP (Identification of Active Destructive Processes) method.
Table 4. Destructive processes by the IADP (Identification of Active Destructive Processes) method.
DenotationAE (Acoustic Emission) Signal ClassNumber of Destructive ProcessThe Source of the Destructive Process
●Class 1Iformation of internal microcracks
●Class 2IIpropagation of internal microcracks
●Class 3IIIformation of surface microcracks
●Class 4IVpropagation of surface cracks
Table
Table 5. Sample parameters, testing conditions, results, and detected damage.
Table 5. Sample parameters, testing conditions, results, and detected damage.
SeriesCuring Conditions (Days of Curing)Hardening TemperatureCement TypeConcrete Strength
after 28 Days (MPa)		ProcessNo of Signals
W210constant 22 ± 2 °CCEMI36.0I5980
II31
III0
W310variable −5 to +42 °CCEMI44.5I5195
II94
III23
W4 (reinforced)10variable −5 to +42 °CCEMI44.5I8608
II90
III10
W5 110constant 22 ± 2 °CCEMI40.1I2192
II9
III0
W6 (100 × 100 × 500)10constant 22 ± 2 °CCEMI40.1I2560
II6
III0
W7 (without curing)noneconstant 22 ± 2°CCEMI45.8I2795
II6
III1
W8 1 (without curing)nonevariable −5 to +42°CCEMI41.2I5200
II42
III7
B2 2 (with admixtures)10constant 22 ± 2 °CCEMI63.5I4519
II52
III0
B3 2 different agregate type)10constant 22 ± 2 °CCEMI55.8I2984
II18
III0
B410constant 22 ± 2 °CCEM III48.1I2886
II19
1 The tests and analysis of W5 and W8 samples results were described in [45], 2 the test results of the B2 and B3 samples were described in [44].

Share and Cite

MDPI and ACS Style

Trąmpczyński, W.; Goszczyńska, B.; Bacharz, M. Acoustic Emission for Determining Early Age Concrete Damage as an Important Indicator of Concrete Quality/Condition before Loading. Materials 2020, 13, 3523. https://doi.org/10.3390/ma13163523

AMA Style

Trąmpczyński W, Goszczyńska B, Bacharz M. Acoustic Emission for Determining Early Age Concrete Damage as an Important Indicator of Concrete Quality/Condition before Loading. Materials. 2020; 13(16):3523. https://doi.org/10.3390/ma13163523

Chicago/Turabian Style

Trąmpczyński, Wiesław, Barbara Goszczyńska, and Magdalena Bacharz. 2020. "Acoustic Emission for Determining Early Age Concrete Damage as an Important Indicator of Concrete Quality/Condition before Loading" Materials 13, no. 16: 3523. https://doi.org/10.3390/ma13163523

APA Style

Trąmpczyński, W., Goszczyńska, B., & Bacharz, M. (2020). Acoustic Emission for Determining Early Age Concrete Damage as an Important Indicator of Concrete Quality/Condition before Loading. Materials, 13(16), 3523. https://doi.org/10.3390/ma13163523

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.