Next Article in Journal
Effect of Cover Plate on the Ballistic Performance of Ceramic Armor
Next Article in Special Issue
Characterization and Evaluation of Hydrothermal Liquefaction Char from Alkali Lignin in Subcritical Temperatures
Previous Article in Journal
Alpha Spectrometry of Radon Short-Lived Progeny in Drinking Water and Assessment of the Public Effective Dose: Results from the Cilento Area, Province of Salerno, Southern Italy
Previous Article in Special Issue
Pre-Treatment of Furniture Waste for Smokeless Charcoal Production
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 13
Issue 24
10.3390/ma13245841
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Impact of Pyrolysis Temperature on the Properties of Eucalyptus Wood-Derived Biochar

by
Bruno Caio Chaves Fernandes
1,*,
Kassio Ferreira Mendes
2,
Ananias Francisco Dias Júnior
3,
Vinícius Patrício da Silva Caldeira
4,
Taliane Maria da Silva Teófilo
1,
Tatiane Severo Silva
1,
Vander Mendonça
1,
Matheus de Freitas Souza
1 and
Daniel Valadão Silva
1
1
Departamento de Ciências Agronômicas e Florestais, Centro de Ciências Vegetais, Universidade Federal Rural do Semi-Árido, Av. Francisco Mota, 572, Costa e Silva, 59625-900 Mossoró, Brazil
2
Departamento de Ciências Agronômicas, Universidade Federal de Viçosa (UFV), 36570-900 Viçosa, Brazil
3
Departamento de Ciências Florestais e da Madeira, Universidade Federal do Espírito Santo (UFES), 29550-000 Jerônimo Monteiro, Brazil
4
Departamento de Química, Universidade Estadual do Rio Grande do Norte (UERN), 59600-195 Mossoró, Brazil
*
Author to whom correspondence should be addressed.
Materials 2020, 13(24), 5841; https://doi.org/10.3390/ma13245841
Submission received: 10 November 2020 / Revised: 26 November 2020 / Accepted: 29 November 2020 / Published: 21 December 2020
(This article belongs to the Special Issue Carbon Materials Applied for Biomass Conversion)
Browse Figures
Versions Notes

Abstract

:
Pyrolysis conditions directly influence biochar properties and, consequently, influence the potential use of biochar. In this study, we evaluated the effects of different pyrolysis temperatures (450, 550, 650, 750, 850, and 950 °C) on the hydrogen potential, electrical conductivity, ash content, yield, volatile matter content, elemental analysis, Fourier-transform infrared spectroscopy results, X-ray diffraction results, scanning electron microscopy results, specific surface area, and micropore volume of eucalyptus wood-derived biochar. The degree of linear association between pyrolysis temperatures and biochar properties was examined using the Pearson correlation coefficient. The results showed a positive correlation of the pyrolysis temperature with the hydrogen potential value, electrical conductivity, and elemental carbon. There was a negative correlation of the pyrolysis temperature with the yield, volatile matter content, elemental oxygen, elemental hydrogen, surface area, aromaticity, hydrophilicity, and polarity indexes. The Fourier-transform infrared spectroscopy data indicated an increase in aromaticity and a decrease in the polarity of high-temperature biochar. The increased pyrolysis temperature caused the loss of cellulose and crystalline mineral components, as indicated by X-ray diffraction analysis and scanning electron microscopy images. These results indicated that changing the pyrolysis temperature enables the production of biochar from the same raw material with a wide range of physicochemical properties, which allows its use in various types of agricultural and environmental activities.

1. Introduction

Biochar is a carbon-rich porous material produced by biomass pyrolysis under an environment with limited oxygen or anoxic conditions [1,2]. Its use is a potential alternative that can promote agricultural yield benefits, carbon sequestration, waste management, clean energy production, and reclamation of degraded areas [3,4,5].
A wide variety of biomass feedstocks can be used to produce biochar. Large amounts of agricultural waste are generated worldwide and are not always properly discarded or recycled. Wood production in Brazil annually generates approximately 50.8 million m3 of lignocellulosic waste [6]; eucalyptus is the most cultivated forest species with 7.83 million hectares of planted trees [7] and contributes largely to the creation of this lignocellulosic waste. Waste conversion into biochar by pyrolysis can reduce lignocellulosic waste volume and contribute to power generation, improvements in crop nutrient efficiency, elimination of pathogens, and generation of products with high agronomic and environmental value [8].
Pyrolysis can be carried out in different temperature ranges, heating rates, and residence times of biomass. These conditions promote wide variation in yield [9] and the properties of the produced biochar [10]. Even produced from the same material, the pyrolysis conditions can produce biochar with different chemical-physical characteristics and textures [11,12] and can thus change its efficiency or purpose of use.
Several studies have evaluated the relationships between various biochars and their pyrolysis conditions [13,14,15]. Huff et al. (2014) [16] reported an increase in aromaticity of biochars from pine wood, peanut shell, and bamboo biomass at higher temperatures, and they reported on the possibility of using these biochars for the potential removal of organic molecules. Jones et al. (2011) [17] studied the effect of biochar from eucalyptus wood (Eucalyptus marginatus) on simazine leaching and degradation and noted that a high sorption of this product reduced its mobility; however, herbicide persistence was increased with the reduced availability of microorganisms in soil.
The use of biochar produced from eucalyptus residues, which is an abundant material and is easy to acquire in several countries [18], can improve the destination of residues from the forestry industry. However, as reported, the temperature of pyrolysis influences the properties of biochar, which can influence the effectiveness of its use. Thus, the objective of this research was to determine the effect of pyrolysis temperature on the physicochemical characteristics of the eucalyptus waste biochar in order to inform biochar producers and stakeholders about the most suitable characteristics for agronomic and environmental applications.

2. Material and Methods

2.1. Biochar Production

Eucalyptus residue was acquired from a clone wood resulting from the crossing between Eucalyptus urophylla and Eucalyptus grandi. The material was crushed into small pieces using a TECNAL knife mill (Willey TE 340, Piracicaba, Brazil). Then, the biomass powder was passed through a 2 mm sieve and dried in an oven with air circulation at 103 ± 2 °C. Biomass pyrolysis was performed in a metal cylinder inside a muffle furnace (Q318M, Quimis, Diadema, São Paulo, Brazil). Carbonization was performed at final temperatures of 450, 550, 650, 750, 850, and 950 °C. The amount of residue used for each repetition was 200 ± 10 g; the temperature was increased by 1.7 °C min−1 and maintained at the final temperature for 1 h under a limited air supply [19]. After cooling, the biochar samples were ground, sieved (<0.9 mm) and stored in a desiccator. The biochar yield was calculated by its mass difference in relation to the dry wood.

2.2. Biochar Characterization

2.2.1. Elemental and Energy Dispersion X-ray Fluorescence Spectrometry Analyses

An elemental analyzer was used to determine the amount of carbon (C), oxygen (O), hydrogen (H), and nitrogen (N) (Vario MACRO Cube, Elementar, Cheadle Hulme, United Kingdom). One hundred milligrams of each dried biochar sample was weighed in a tin capsule; next, the capsule was closed and placed in an apparatus, which was operated by subjecting the samples to combustion under a pure oxygen atmosphere (99.999%). Gases formed by this combustion were measured with a thermal conductivity detector. The O content was estimated by mass balance: O = 100 − (C + H + N + mineral).
The inorganic mineral content was determined by energy-dispersive X-ray fluorescence spectrometry (EDXRF). One gram of the biochar sample was weighed and ground; next, the biochar sample was packed in a 20 mm-diameter polyethylene beaker and covered with a 6 µm thick polypropylene film. The samples were irradiated in triplicate for 300 s under vacuum using an EDXRF instrument (EDXRF-720, Shimadzu, Kyoto, Japan). The samples were irradiated using an X-ray tube operated at 15 kV (sodium a scandium) and 50 kV (titanium a uranium). The current was adjusted automatically (maximum: 1 mA) using a 10 mm collimator. Detection was performed with a liquid nitrogen-cooled Si (Li) detector (Shimadzu, Kyoto, Japan).

2.2.2. Ash and Volatile Matter (VM) Contents

Ash and VM contents were evaluated by using the American Society for Testing and Materials (ASTM) methods. Each sample was analyzed in triplicate. For ash analysis, porcelain crucibles were preheated in an oven at 650 °C for 10 min; next, the crucibles were cooled in a desiccator at room temperature and preweighed. The ash content was determined by measuring the mass loss after the combustion of 1 g of biochar sample in each porcelain crucible at 105 °C for 1 h and 750 °C for 6 h [20].
The VM content was determined by heating the dried sample at 900 °C in a muffle furnace (SP-1200DM/B, Splabor, Presidente Prudente, São Paulo, Brazil). Approximately 1 g of the dried biochar sample was weighed and placed in a preweighed and preheated porcelain crucible. The crucible was placed in the preheated muffle door at 900 °C for 3 min and then placed inside a muffle furnace for 7 min. After the oven was cooled, the samples were removed and placed in a desiccator at room temperature and then weighed. The VM content was determined by the mass difference in the crucible before being placed and after being removed from the muffle furnace [21].

2.2.3. pH Value and Electrical Conductivity (EC)

For pH measurements, 2 g of each biochar sample was weighed into a 25 mL beaker; next, 10 mL of a 0.01 M CaCl2 was added to a beaker and stirred with a glass rod; and then, the mixture was allowed to sit for 1 h [22]. The pH measurement was performed with a digital pH meter (Mpa-210, Tecnopon, Piracicaba, São Paulo, Brazil).
The EC was determined by the BGK method [23]. A solution of 2 g of dry biochar and 10 mL of deionized water was prepared and stirred for 1 h. Then, the measurements were performed on a digital conductivity meter (MA 521, Marconi, Piracicaba, São Paulo, Brazil). The pH and EC analyses were performed in triplicate.

2.2.4. Specific Surface Area (SSA) and Morphology

Scanning electron microscopy (SEM) was used to evaluate the changes in the physical morphology of the biochar surface caused by variations in pyrolysis temperature. The biochar particles were placed in a metal sample holder using a carbon conductive tape (PELCO Tabs™, Ted Pella, Inc., Redding, CA, USA) and sputtered (Q150R ES, Quorum Technologies Ltd., Laughton, East Sussex, UK) with a 9 nm thick gold layer. This procedure was used to improve material conductivity, generating a higher-quality image. Images were captured with a secondary electron detector (SE) in SEM (VEGA 3 LMU, Tescan, Czech Republic), operating with an electron beam of 20 kV.
The textural properties of the biochar surface were characterized with the Brunauer–Emmett–Teller (BET) method by using results from the physical adsorption of N2 at 77 K with the aid of a surface area analyzer (ASAP-2020, Micromeritics, Norcross, GA, USA) at a relative pressure range (P/P0) of 0.01–0.99. At each pressure, the physically adsorbed N2 produced a change in the output composition recorded by a thermal conductivity detector connected to a potentiometric recorder. By heating the sample, there was a loss in contact with the sample liquid N2, and the N2 was desorbed. The peak area is proportional to the mass of the desorbed N2. From the N2 volume obtained in the assay and using the BET equation, the SSA and total pore volume (TPV) were determined.

2.2.5. Chemical Analysis

The spatial arrangements and presence of minerals in the samples were identified using the X-ray diffraction (XRD) technique; the bands were scanned in a 2θ range from 10° to 80° at low and medium angles (XRD 6000, Shimadzu, Quioto, Japan) with a radiation source of CuKα (λ  = 0.15406 nm) and a nickel filter operating at 30 kV and a rate of 30 mA at 0.6° min−1.
The surface functional groups were analyzed by Fourier-transform infrared spectroscopy (FT-IR) in a wavelength range of 400–4000 cm−1 (by 64 scans with a 4 cm−1 resolution). Before FT-IR analysis, the samples were oven-dried at 200 °C, and then 0.5 mg of the sample was mixed with 300 mg of KBr and ground. Thereafter, each sample was pressed in a hydraulic press (Shimadzu, SSP-10A, Tokyo, Japan) at an 80 kN force to form a tablet that was analyzed on a spectrometer (IRPrestige-21, Shimadzu, Tokyo, Japan).
Due to the need for a relative scale of the absorption intensity, a background spectrum was measured, which aimed to compare the sample-free beam measurement to the sample-beam measurement to determine the percent transmittance. All spectral information was strictly due to the sample. As the background spectrum is a feature of the instrument, only one measurement of this spectrum was performed.

2.3. Data Analysis

The degree of linear association between two measured variables was analyzed using the Pearson correlation coefficient. The relationships between pyrolysis conditions (independent variables) and biochar-derived properties (dependent variables) were evaluated. A significance rate was considered (p ≤ 0.05). R values were calculated using Statistica® software version 7.0 (StatSoft, Boston, MA, USA).

3. Results and Discussion

3.1. Effects of Pyrolysis Temperature on Yield, VM Content, Ash Content, pH Value, EC, and Inorganic Minerals from Biochar Produced

A significantly negative correlation occurred between the pyrolysis temperature and the biochar yield (R = −0.90), indicating a decrease in yield due to the increased pyrolysis temperature (Table 1). The yield declined sharply, as the temperature increased from 450 to 650 °C (Table 1). The VM content showed a similar behavior to yield, and there was an exponential reduction in VM content from 450 to 650 °C and a significant correlation of −0.90 (Table 1). The main transformation observed over this temperature range was the thermal decomposition of lignocellulosic materials and the release of water vapor and VM compounds such as CO, CO2, H2, and CH4, resulting in a high yield loss at lower temperatures [24,25]. Between 750 and 850 °C, the decline in biochar yield was proportionally lower and constant, indicating the formation of the most stable carbonaceous compound in terms of material loss. Other studies have shown a similar correlation for other materials reacted at different pyrolysis temperatures; that is, other materials show a rapid initial decline in yield at lower temperatures, followed by a smaller and constant reduction at higher temperatures [26,27,28,29].
Unlike yield and VM content, ash content, pH values, and EC increased due to the temperature increase, with significant positive correlations of 0.89, 0.83, and 0.85, respectively (Table 1). Higher ash contents observed at higher temperatures were caused by the stability of minerals in the pyrolyzed product, such as K, Ca, and P, following a progressive loss in VM from the devolatilization process [30]. The positive correlation of these minerals explained this observation with the temperature increase (Table 2). Another observed effect associated with higher ash content is the increase in pH value and EC. Lehmann and Joseph (2015) [31] developed a meta-analysis and reported a close relationship between pyrolysis temperature and pH value. These authors observed that the average pH value of pyrolyzed biochar was 5 at temperatures of <400 °C, while the pH value of pyrolyzed biochar was 9 at temperatures of >600 °C. The ability of biochar to neutralize the acidity has been acknowledged in several studies, showing biochar is a potential agent for correcting pH values in acidic soils, reducing the toxicity of aluminum and increasing the availability of nutrients [32,33].
In addition to the pH value, increased cation concentrations due to the pyrolysis temperature increase favored higher ECs of the material. Biochars with the highest concentration of salts can be a problem in areas with the limited ability to leach salts. The application of biochar with high EC values can reduce seed germination and crop yields with higher sensitivity to salt in a soil solution [34]. However, most studies showed a positive correlation between biochar use and lower crop toxicity due to water and saline stress [35,36,37,38]. The increase in biochar EC due to a higher pyrolysis temperature was mainly caused by a higher K concentration observed in this work (Table 2). The K supply via the biochar application can improve osmotic control and potassium/sodium ratios, which increases the crop tolerance to water and saline stress [39].

3.2. Elemental Analysis

The pyrolysis temperature changed the elemental composition of the eucalyptus wood waste-derived biochar (Table 3). Increasing the temperature from 450 to 950 °C increased the C content from 74.96% to 86.93%, respectively, with a significant positive correlation (R = 0.84) (Table 2). The H and O contents were negatively correlated with the increase in pyrolysis temperature (R = 0.72 and 0.84, respectively), with a decrease of 3.76% to 0.9% in H content and 19.41% to 10.75% in O content. The gradual increase in C content of the biochar due to the increase in temperature was caused by a higher release rate of hydrogen and oxygen in the form of water vapor (dehydration) and the loss of functional groups associated with these atoms (carboxyl groups and hydroxyls). During the carbonization process, the relative loss in hydrogen and oxygen is higher than the relative loss in carbon [30]; this behavior was also observed for the eucalyptus-derived biochar, changing the atomic ratios of biochars.
C, elemental carbon; H, elemental hydrogen; O, elemental oxygen; N, elemental nitrogen; H/C, aromaticity index; (O/C), hydrophilicity index; (O + N)/C, polarity index. * indicates significant correlations (p ≤ 0.05). N = 3; data are presented as mean ± stand deviation.
The elemental oxygen (O) (R = 0.84) and hydrogen (H) (R = 0.84) positively correlated with the pyrolysis temperature. The O/C ratio significantly negatively correlated with the increase in temperature (R = −0.85) (Table 3). The correlation with the H/C and (O + N)/C ratios was not significant, although the correlation showed high values (R = −0.8 and −0.81, respectively) (Table 2). The reduction in atomic ratios due to the increased temperature pyrolysis indicated that the material formed had higher aromaticity and recalcitrance values but a smaller polarity [4,26,40]. These properties ensure that biochar has a greater resistance to degradation when applied to soils [12,41,42]. For the biochar derived from eucalyptus produced at 850 and 950 °C, the increased stability of these carbonaceous materials provided carbon sequestration in soil since they were hardly changed in their elemental structure. Despite the lower H/C and O/C ratios of biochars produced at pyrolysis temperatures of 850 and 950 °C, all the other biochars produced at the lowest temperatures in this research were within the parameters required by the European Biochar Certificate [43]: C% > 50, H/C ratio < 0.7, and O/C ratio < 0.4.
The pyrolysis temperature did not change the N content, showing a nonsignificant correlation (R = 0.08) (Table 3). Generally, the N content depends on the type of raw material used for biochar production and does not rely on the pyrolysis conditions [4,44]. Moreover, in woody matrices, N-containing structures are more resistant to degradation with increasing temperature. According to Enders et al. 2012 [18], N is highly retained in raw material wood-derived biochars, which is probably due to the formation of heterocyclic N such as pyridines and pyrroles.
The van Krevelen diagram allows us to identify changes in the H/C and O/C ratios in eucalyptus-derived biochar (Figure 1). An increase in the pyrolysis temperature from 450 to 550 °C promoted an intense reduction in aliphatic groups (H/C). At temperatures above 550 °C, the aliphatic degree of biochar changed little. The main change from 550 °C was the reduction in the O/C ratio, providing biochar with a greater similarity for the H/C and O/C ratios. Pyrolysis at 950 °C promoted another decrease in the H/C ratio. This behavior observed for the higher pyrolysis temperatures suggested the beginning of the formation process of a carbonaceous material with a high amount of metamorphism called coal anthracite [45].

3.3. SSA, TPV, Surface Morphology, Crystalline Phase, and Functional Groups

The pyrolysis temperature showed a significant negative correlation with the biochar SSA (R = −0.89) (Table 3). As the pyrolysis temperature increased from 650 to 950 °C, the SSA decreased from 410.48 to 224.43 m2 g−1. This reduction in the SSA due to material burning at higher temperatures is not common. Most studies show that a higher pyrolysis temperature provides a higher SSA [4,46]. For eucalyptus-derived biochar, the reduction in the SSA can be attributed to the higher ash content observed at temperatures above 650 °C (Table 1), which can decrease the microporous formation structure [14]. In addition, micropores can be destroyed by the polymerization reaction during the heating process [47], resulting in a lower SSA found in biochar produced at higher pyrolysis temperatures.
The increased pyrolysis temperature showed no significant correlation with the TPV (R = −0.34). The TPV increased from 0.05 to 0.07 mm3 g−1 with the temperature increased from 650 to 850 °C and decreased to 0.02 mm3 g−1 at 950 °C. Increasing the temperature to 950 °C may have destroyed or blocked the micropores. Moreover, the XRD analysis results showed that the microcrystalline graphite structure was more present in high-temperature biochars (Figure 2). The process of converting amorphous carbon into graphite microcrystalline structures can cause decreases in the TPV and SSA, as reported by Chen et al. 2012 [48], when evaluating the effect of pyrolysis temperature on cotton stalks. At temperatures of 450 and 550 °C, the device could not determine the SSA and TPV. The amount of uncarbonized biomass at these temperatures may have interfered with the measurements, and this prevents the gas adsorption measurements (N2-BET), which allow for the estimation of the surface area and pore volume [49,50].
The SEM images at 200× and 1000× magnifications showed that increasing the pyrolysis temperature promoted the loss of the outer biochar layer (Figure 3). The removal of the outer biochar layer exposed pores located in the carbonaceous skeleton of the biological capillary structure of the raw material. A greater number of porous structures were observed with increasing pyrolysis temperature (Figure 3). However, the accumulation of particles on the biochar surface, mainly ash, was also increased due to the higher temperature (Figure 3). The presence of this greater amount of ash on the surface of biochars produced at higher temperatures justifies the evidence that these particles could clog the micropores, reducing both the SSA and TPV measured with the BET analysis.
The crystalline phase shape and biochar purity were determined using XRD analysis. The spectrum showed no sharp peaks representing the presence of crystalline mineral structures (Figure 2). The XRD peak intensities increased with increasing pyrolysis temperature. The 2θ angle peak at approximately 22.7° was attributed to the crystallographic planes hkl (101) of the crystalline regions of cellulose [51,52]. Pyrolysis temperatures above 650 °C resulted in a wider peak at a 2θ value of approximately 23.5°, indicating that some partial crystalline structure of the cellulose was lost [26]. A new 2θ peak of approximately 43.7° became clearer in biochars at pyrolysis temperatures of 750 to 950 °C. This new observed peak indicated the development of graphite-like atomic order in the increasingly charred material [26]. This peak resulted in the successive ordering of carbon in aromatic structures [53], indicating the highest crystallization of the carbonaceous material [54]. These findings point to the formation of more stable (less reactive) graphitic carbon at higher pyrolysis temperatures.
The functional groups observed in the eucalyptus wood residue-derived biochar by FT-IR analysis are shown in Table 4. Aromatic, aliphatic, and phenolic groups were seen as the predominant peaks. A high intensity peak at 3.424 cm−1, corresponding to the stretching vibrations of the –OH groups, became weaker with increasing temperature (Table 3 and Figure 4). There was a reduction in peaks from 1000 to 1700 cm−1 with increasing pyrolysis temperature (Figure 4). At lower temperatures (450, 550, and 650 °C), peaks at 1.604 cm−1 (C = O) [55] and 1.240 cm−1 (C–O acetyls) were observed, suggesting the presence of woody and cellulosic constituents and the incomplete degradation of the original biomass [13].
The peak at 2.920 cm−1 (C–H, CH2, or CH3) [50] for aliphatic components was observed only at lower temperatures (450 and 550 °C) (Figure 3). With increasing pyrolysis temperature to above 550 °C, the aliphatic C-H stretching observed at peak of 2.920 cm−1 was eliminated, suggesting the degradation of hemicellulose and cellulose [40]. The peak representing the aromatic carbon at 1.638 cm−1 (C=C) [51,56] narrowed at the temperature of 750 °C (Table 4 and Figure 4). The higher peak intensity for the C=C group confirmed the increased aromaticity of the eucalyptus-derived biochar when produced at temperatures above 750 °C. The peak intensity at 1.430 cm−1 for C–H decreased dramatically with increasing temperature, reaching close to zero intensities when the material was pyrolyzed at 950 °C.
Increasing the pyrolysis temperature reduced the intensity of some biochar functional groups. This loss of functional groups, especially the hydroxyl and carboxyl groups, was caused by the degradation and transformation of hemicellulose (200–260 °C), cellulose (315–400 °C), and lignin (> 400 °C) in homogeneous and highly aromatic carbon structures [59]. The FT-IR spectra confirmed the transformation of the eucalyptus-derived material into more recalcitrant compounds when high pyrolysis temperatures were used during biochar synthesis. However, the absence of functional groups (carboxylic, phenolic, and alcohol) can make it impossible to use biochar for some specific purposes. The application of highly aromatic biochar without functional groups to reduce nutrient leaching [60] or remove soil contaminants [61] can be inefficient due to the absence of surface charges that are capable of interacting with nutrients or contaminants.

4. Conclusions

Some physicochemical properties of eucalyptus wood-derived biochar are affected by pyrolysis temperature. The results showed that the pyrolysis temperature was positively correlated with pH value, EC, ash content, and elemental carbon and negatively correlated with yield, VM, elemental oxygen, elemental hydrogen, surface area, and H/C, O/C, and (O + N)/C ratios. An increase in temperature promoted a loss in biochar surface layers, reduced surface functional groups and formed a more stable carbon. Overall, the research indicated that the pyrolysis temperature makes it possible to produce biochar from the same raw material with a wide range of physicochemical properties, allowing its use in various agricultural and environmental activities, such as soil conditioning, carbon sequestration, or the immobilization of contaminants.

Author Contributions

Supervision: K.F.M. and D.V.S.; Methodology: T.M.d.S.T. and V.P.d.S.C.;Writing—original draft preparation: B.C.C.F., M.d.F.S. and T.S.S.; Writing—review and editing: B.C.C.F. and T.S.S. Resources: A.F.D.J., K.F.M. and D.V.S.; Funding acquisition: D.V.S. and V.M. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the Coordenação de Aperfeiçoamento de Pessoal de Nível Superior-Brasil (CAPES)—Finance Code 001 and Conselho Nacional de Desenvolvimento Científico e Tecnológico-CNPq.

Conflicts of Interest

The authors declare no conflicts interest.

References

  1. Ronsse, F.; Van Hecke, S.; Dickinson, D.; Prins, W. Production and characterization of slow pyrolysis biochar: Influence of feedstock type and pyrolysis conditions. GCB Bioenergy 2012, 5, 104–115. [Google Scholar] [CrossRef]
  2. Lin, Q.; Xu, X.; Wang, L.; Chen, Q.; Fang, J.; Shen, X.; Lou, L.; Tian, G. The speciation, leachability and bioaccessibility of Cu and Zn in animal manure-derived biochar: Effect of feedstock and pyrolysis temperature. Front. Environ. Sci. Eng. 2017, 11, 5. [Google Scholar] [CrossRef]
  3. Kookana, R.; Sarmah, A.; Van Zwieten, L.; Krull, E.; Singh, B. Biochar Application to Soil. Adv. Agron. 2011, 112, 103–143. [Google Scholar] [CrossRef]
  4. Zhao, B.; O’Connor, D.; Zhang, J.; Peng, T.; Shen, Z.; Tsang, D.C.; Hou, D. Effect of pyrolysis temperature, heating rate, and residence time on rapeseed stem derived biochar. J. Clean. Prod. 2018, 174, 977–987. [Google Scholar] [CrossRef]
  5. Manna, S.; Singh, N. Biochars mediated degradation, leaching and bioavailability of pyrazosulfuron-ethyl in a sandy loam soil. Geoderma 2019, 334, 63–71. [Google Scholar] [CrossRef]
  6. IPEA. Instituto de Pesquisas Aplicadas Diagnóstico dos Resíduos Orgânicos do Setor Agrossilvopastoril e Agroindústrias Associadas: Relatório de Pesquisa. Governo Federal. Brasília. 2012. Available online: https://www.ipea.gov.br/portal/images/stories/PDFs/relatoriopesquisa/120917_relatorio_residuos_organicos.pdf (accessed on 12 October 2019).
  7. IBÁ Indústria Brasileira de Árvores (Brazilian Tree Industry). Annual Report 2017; IBÁ: São Paulo, Brazil, 2017; Available online: http://iba.org/images/shared/Biblioteca/IBA_RelatorioAnual2017.pdf (accessed on 12 October 2019).
  8. Spokas, K.A.; Cantrell, K.B.; Novak, J.M.; Archer, D.W.; Ippolito, J.A.; Collins, H.P.; Boateng, A.A.; Lima, I.M.; Lamb, M.C.; McAloon, A.J.; et al. Biochar: A Synthesis of Its Agronomic Impact beyond Carbon Sequestration. J. Environ. Qual. 2012, 41, 973–989. [Google Scholar] [CrossRef]
  9. Bartoli, M.; Giorcelli, M.; Jagdale, P.; Rovere, M.; Tagliaferro, A. A Review of Non-Soil Biochar Applications. Materials 2020, 13, 261. [Google Scholar] [CrossRef] [Green Version]
  10. Li, S.; Chen, G. Thermogravimetric, thermochemical, and infrared spectral characterization of feedstocks and biochar derived at different pyrolysis temperatures. Waste Manag. 2018, 78, 198–207. [Google Scholar] [CrossRef]
  11. Tripathi, M.; Sahu, J.; Ganesan, P. Effect of process parameters on production of biochar from biomass waste through pyrolysis: A review. Renew. Sustain. Energy Rev. 2016, 55, 467–481. [Google Scholar] [CrossRef]
  12. Li, S.; Harris, S.; Anandhi, A.; Chen, G. Predicting biochar properties and functions based on feedstock and pyrolysis temperature: A review and data syntheses. J. Clean. Prod. 2019, 215, 890–902. [Google Scholar] [CrossRef]
  13. Al-Wabel, M.I.; Al-Omran, A.; El-Naggar, A.H.; Nadeem, M.; Usman, A.R. Pyrolysis temperature induced changes in characteristics and chemical composition of biochar produced from conocarpus wastes. Bioresour. Technol. 2013, 131, 374–379. [Google Scholar] [CrossRef] [PubMed]
  14. Liu, X.; Zhang, Y.; Li, Z.; Feng, R.; Zhang, Y. Characterization of corncob-derived biochar and pyrolysis kinetics in comparison with corn stalk and sawdust. Bioresour. Technol. 2014, 170, 76–82. [Google Scholar] [CrossRef] [PubMed]
  15. Suliman, W.; Harsh, J.B.; Abu-Lail, N.I.; Fortuna, A.-M.; Dallmeyer, I.; Garcia-Perez, M. Influence of feedstock source and pyrolysis temperature on biochar bulk and surface properties. Biomass-Bioenergy 2016, 84, 37–48. [Google Scholar] [CrossRef]
  16. Huff, M.D.; Kumar, S.; Lee, J.W. Comparative analysis of pinewood, peanut shell, and bamboo biomass derived biochars produced via hydrothermal conversion and pyrolysis. J. Environ. Manag. 2014, 146, 303–308. [Google Scholar] [CrossRef]
  17. Jones, D.; Edwards-Jones, G.; Murphy, D. Biochar mediated alterations in herbicide breakdown and leaching in soil. Soil Biol. Biochem. 2011, 43, 804–813. [Google Scholar] [CrossRef]
  18. Heidari, A.; Khaki, E.; Younesi, H.; Lu, H.R. Evaluation of fast and slow pyrolysis methods for bio-oil and activated carbon production from eucalyptus wastes using a life cycle assessment approach. J. Clean. Prod. 2019, 241, 118394. [Google Scholar] [CrossRef]
  19. Júnior, A.F.D.; Pirola, L.P.; Takeshita, S.; Lana, A.Q.; Brito, J.O.; De Andrade, A.M. Higroscopicity of charcoal produced in different temperatures. CERNE 2016, 22, 423–430. [Google Scholar] [CrossRef] [Green Version]
  20. Standards ASTM International. Ash in the Analysis Sample of Coal and Coke from Coal. D3174-12; Standards ASTM International: West Conshohocken, PA, USA, 2018. [Google Scholar]
  21. Standards ASTM International. Volatile Matter in the Analysis Sample of Coal and Coke. D3175; Standards ASTM International: West Conshohocken, PA, USA, 2018. [Google Scholar]
  22. ISO 10390. Soil Quality–Determination of pH; ISO (International Standards Organization): Chiswick, UK, 2005. [Google Scholar]
  23. BGK. Methodenbuch zur Analyse von Kompost; Bundesgütegemeinschaft Kompost e.V. (Federal Compost Quality Assurance Organisation FCQAO): Stuttgart, Germany, 1994. [Google Scholar]
  24. Liu, W.-J.; Jiang, H.; Yu, H.-Q. Development of Biochar-Based Functional Materials: Toward a Sustainable Platform Carbon Material. Chem. Rev. 2015, 115, 12251–12285. [Google Scholar] [CrossRef]
  25. Li, S.; Barreto, V.; Li, R.; Chen, G.; Hsieh, Y.P. Nitrogen retention of biochar derived from different feedstocks at variable pyrolysis temperatures. J. Anal. Appl. Pyrolysis 2018, 133, 136–146. [Google Scholar] [CrossRef]
  26. Keiluweit, M.; Nico, P.S.; Johnson, M.G.; Kleber, M. Dynamic Molecular Structure of Plant Biomass-Derived Black Carbon (Biochar). Environ. Sci. Technol. 2010, 44, 1247–1253. [Google Scholar] [CrossRef] [Green Version]
  27. Xiao, X.; Chen, B.; Zhu, L. Transformation, Morphology, and Dissolution of Silicon and Carbon in Rice Straw-Derived Biochars under Different Pyrolytic Temperatures. Environ. Sci. Technol. 2014, 48, 3411–3419. [Google Scholar] [CrossRef] [PubMed]
  28. Yuan, H.; Lu, T.; Huang, H.; Zhao, D.; Kobayashi, N.; Chen, Y. Influence of pyrolysis temperature on physical and chemical properties of biochar made from sewage sludge. J. Anal. Appl. Pyrolysis 2015, 112, 284–289. [Google Scholar] [CrossRef]
  29. Wei, S.; Zhu, M.; Fan, X.; Song, J.; Peng, P.; Li, K.; Jia, W.; Song, H. Influence of pyrolysis temperature and feedstock on carbon fractions of biochar produced from pyrolysis of rice straw, pine wood, pig manure and sewage sludge. Chemosphere 2019, 218, 624–631. [Google Scholar] [CrossRef] [PubMed]
  30. Weber, K.; Quicker, P. Properties of biochar. Fuel 2018, 217, 240–261. [Google Scholar] [CrossRef]
  31. Lehmann, J.; Joseph, S. (Eds.) Biochar for Environmental Management. Science, Technology and Implementation; Routledge: London, UK, 2015. [Google Scholar]
  32. Zhao, R.; Coles, N.; Kong, Z.; Wu, J. Effects of aged and fresh biochars on soil acidity under different incubation conditions. Soil Tillage Res. 2015, 146, 133–138. [Google Scholar] [CrossRef]
  33. Paz-Ferreiro, J.; Álvarez, M.L.; De Figueiredo, C.C.; Méndez, A.; Gascó, G. Effect of Biochar and Hydrochar on Forms of Aluminium in an Acidic Soil. Appl. Sci. 2020, 10, 7843. [Google Scholar] [CrossRef]
  34. Paz-Ferreiro, J.; Nieto, A.; Méndez, A.; Askeland, M.P.J.; Gascó, G. Biochar from Biosolids Pyrolysis: A Review. Int. J. Environ. Res. Public Health 2018, 15, 956. [Google Scholar] [CrossRef] [Green Version]
  35. Bouqbis, L.; Daoud, S.; Koyro, H.W.; Kammann, C.I.; Ainlhout, F.Z.; Harrouni, M.C. Phytotoxic effects of argan shell biochar on salad and barley germination. Agric. Nat. Resour. 2017, 51, 247–252. [Google Scholar] [CrossRef]
  36. Olszyk, D.M.; Shiroyama, T.; Novak, J.M.; Johnson, M.G. A rapid-test for screening biochar effects on seed germination. Commun. Soil Sci. Plant Anal. 2018, 49, 2025–2041. [Google Scholar] [CrossRef]
  37. Mumme, J.; Getz, J.; Prasad, M.; Lüder, U.; Kern, J.; Mašek, O.; Buss, W. Toxicity screening of biochar-mineral composites using germination tests. Chemosphere 2018, 207, 91–100. [Google Scholar] [CrossRef] [Green Version]
  38. Mehdizadeh, L.; Moghaddam, M.; Lakzian, A. Alleviating negative effects of salinity stress in summer savory (Satureja hortensis L.) by biochar application. Acta Physiol. Plant. 2019, 41, 98. [Google Scholar] [CrossRef]
  39. Rezaie, N.; Razzaghi, F.; Sepaskhah, A.R. Different Levels of Irrigation Water Salinity and Biochar Influence on Faba Bean Yield, Water Productivity, and Ions Uptake. Commun. Soil Sci. Plant Anal. 2019, 50, 611–626. [Google Scholar] [CrossRef]
  40. Usman, A.R.; Abduljabbar, A.; Vithanage, M.; Ok, Y.S.; Ahmad, M.; Ahmad, M.; Elfaki, J.; Abdulazeem, S.S.; Al-Wabel, M.I. Biochar production from date palm waste: Charring temperature induced changes in composition and surface chemistry. J. Anal. Appl. Pyrolysis 2015, 115, 392–400. [Google Scholar] [CrossRef]
  41. A Spokas, K. Review of the stability of biochar in soils: Predictability of O:C molar ratios. Carbon Manag. 2010, 1, 289–303. [Google Scholar] [CrossRef] [Green Version]
  42. Huang, H.-J.; Yang, T.; Lai, F.-Y.; Wu, G.-Q. Co-pyrolysis of sewage sludge and sawdust/rice straw for the production of biochar. J. Anal. Appl. Pyrolysis 2017, 125, 61–68. [Google Scholar] [CrossRef]
  43. Comparison of European Biochar Certificate Version 4. 8 and IBI Biochar Standards Version 2.0. March 2012; pp. 1–5. Available online: https://www.biochar-international.org/wp-content/uploads/2018/04/IBI-EBC_comparison_Oct2014.pdf (accessed on 21 December 2020).
  44. Zhang, J.; Liu, J.; Liu, R. Effects of pyrolysis temperature and heating time on biochar obtained from the pyrolysis of straw and lignosulfonate. Bioresour. Technol. 2015, 176, 288–291. [Google Scholar] [CrossRef]
  45. Haykiri-Acma, H.; Yaman, S. Interaction between biomass and different rank coals during co-pyrolysis. Renew. Energy 2010, 35, 288–292. [Google Scholar] [CrossRef]
  46. Sun, Y.; Gao, B.; Yao, Y.; Fang, J.; Zhang, M.; Zhou, Y.; Chen, H.; Yang, L. Effects of feedstock type, production method, and pyrolysis temperature on biochar and hydrochar properties. Chem. Eng. J. 2014, 240, 574–578. [Google Scholar] [CrossRef]
  47. Neves, D.S.F.; Thunman, H.; Matos, M.A.A.; Tarelho, L.A.D.C.; Gómez-Barea, A. Characterization and prediction of biomass pyrolysis products. Prog. Energy Combust. Sci. 2011, 37, 611–630. [Google Scholar] [CrossRef]
  48. Chen, Y.; Yang, H.; Wang, X.; Zhang, S.; Chen, H. Biomass-based pyrolytic polygeneration system on cotton stalk pyrolysis: Influence of temperature. Bioresour. Technol. 2012, 107, 411–418. [Google Scholar] [CrossRef]
  49. Essandoh, M.; Wolgemuth, D.; Pittman, C.U.; Mohan, D.; Mlsna, T.E. Phenoxy herbicide removal from aqueous solutions using fast pyrolysis switchgrass biochar. Chemosphere 2017, 174, 49–57. [Google Scholar] [CrossRef] [PubMed]
  50. Essandoh, M.; Kunwar, B.; Pittman, C.U.; Mohan, D.; Mlsna, T.E. Sorptive removal of salicylic acid and ibuprofen from aqueous solutions using pine wood fast pyrolysis biochar. Chem. Eng. J. 2015, 265, 219–227. [Google Scholar] [CrossRef]
  51. Jiang, Z.; Yang, Z.; So, C.-L.; Hse, C.-Y. Rapid prediction of wood crystallinity in Pinus elliotii plantation wood by near-infrared spectroscopy. J. Wood Sci. 2007, 53, 449–453. [Google Scholar] [CrossRef]
  52. Biswas, B.; Pandey, N.; Bisht, Y.; Singh, R.; Kumar, J.; Bhaskar, T. Pyrolysis of agricultural biomass residues: Comparative study of corn cob, wheat straw, rice straw and rice husk. Bioresour. Technol. 2017, 237, 57–63. [Google Scholar] [CrossRef]
  53. Paris, O.; Zollfrank, C.; Zickler, G.A. Decomposition and carbonisation of wood biopolymers—A microstructural study of softwood pyrolysis. Carbon 2005, 43, 53–66. [Google Scholar] [CrossRef]
  54. Tushar, M.S.H.K.; Mahinpey, N.; Khan, A.; Ibrahim, H.; Kumar, P.; Idem, R. Production, characterization and reactivity studies of chars produced by the isothermal pyrolysis of flax straw. Biomass-Bioenergy 2012, 37, 97–105. [Google Scholar] [CrossRef]
  55. Uchimiya, M.; Wartelle, L.H.; Klasson, K.T.; Fortier, C.A.; Lima, I.M. Influence of Pyrolysis Temperature on Biochar Property and Function as a Heavy Metal Sorbent in Soil. J. Agric. Food Chem. 2011, 59, 2501–2510. [Google Scholar] [CrossRef]
  56. Chen, B.; Zhou, D.; Zhu, L. Transitional Adsorption and Partition of Nonpolar and Polar Aromatic Contaminants by Biochars of Pine Needles with Different Pyrolytic Temperatures. Environ. Sci. Technol. 2008, 42, 5137–5143. [Google Scholar] [CrossRef]
  57. Adel, A.M.; El–Wahab, Z.H.A.; Ibrahim, A.A.; Al–Shemy, M.T. Characterization of microcrystalline cellulose prepared from lignocellulosic materials. Part I. Acid catalyzed hydrolysis. Bioresour. Technol. 2010, 101, 4446–4455. [Google Scholar] [CrossRef]
  58. Marx, S.; Chiyanzu, I.; Piyo, N. Influence of reaction atmosphere and solvent on biochar yield and characteristics. Bioresour. Technol. 2014, 164, 177–183. [Google Scholar] [CrossRef]
  59. Yang, F.; Gao, Y.; Sun, L.; Zhang, S.; Li, J.; Zhang, Y. Effective sorption of atrazine by biochar colloids and residues derived from different pyrolysis temperatures. Environ. Sci. Pollut. Res. 2018, 25, 18528–18539. [Google Scholar] [CrossRef] [PubMed]
  60. Gao, S.; Hoffman-Krull, K.; Bidwell, A.L.; DeLuca, T.H. Locally produced wood biochar increases nutrient retention and availability in agricultural soils of the San Juan Islands, USA. Agric. Ecosyst. Environ. 2016, 233, 43–54. [Google Scholar] [CrossRef]
  61. Yuan, P.; Wang, J.; Pan, Y.; Shen, B.; Wu, C. Review of biochar for the management of contaminated soil: Preparation, application and prospect. Sci. Total Environ. 2019, 659, 473–490. [Google Scholar] [CrossRef] [PubMed]
Materials 13 05841 g001 550
Figure 1. Van Krevelen diagram showing the correlations between the H/C and O/C ratios of pyrolyzed eucalyptus wood-derived biochar at different temperatures.
Figure 1. Van Krevelen diagram showing the correlations between the H/C and O/C ratios of pyrolyzed eucalyptus wood-derived biochar at different temperatures.
Materials 13 05841 g001
Materials 13 05841 g002 550
Figure 2. Diffracted beam intensity as a function of the Bragg angle (2θ in degrees) of eucalyptus wood-derived biochar at different pyrolysis temperatures.
Figure 2. Diffracted beam intensity as a function of the Bragg angle (2θ in degrees) of eucalyptus wood-derived biochar at different pyrolysis temperatures.
Materials 13 05841 g002
Materials 13 05841 g003 550
Figure 3. Scanning electron microscopy (SEM) images of eucalyptus wood-derived biochar produced at 200× and 1000× magnifications at different pyrolysis temperatures: (a) 450 °C; (b) 550 °C; (c) 650 °C; (d) 750 °C; (e) 850 °C; and (f) 950 °C.
Figure 3. Scanning electron microscopy (SEM) images of eucalyptus wood-derived biochar produced at 200× and 1000× magnifications at different pyrolysis temperatures: (a) 450 °C; (b) 550 °C; (c) 650 °C; (d) 750 °C; (e) 850 °C; and (f) 950 °C.
Materials 13 05841 g003
Materials 13 05841 g004 550
Figure 4. Fourier-transform infrared spectra (FT-IR) of eucalyptus wood-derived biochar samples at different pyrolysis temperatures (a) 450, 550 and 650 °C and (b) 750, 850 and 950 °C.
Figure 4. Fourier-transform infrared spectra (FT-IR) of eucalyptus wood-derived biochar samples at different pyrolysis temperatures (a) 450, 550 and 650 °C and (b) 750, 850 and 950 °C.
Materials 13 05841 g004
Table
Table 1. Yield, ash, volatile matter (VM) contents, pH, and electrical conductivity (EC) of pyrolyzed eucalyptus wood-derived biochar at different temperatures.
Table 1. Yield, ash, volatile matter (VM) contents, pH, and electrical conductivity (EC) of pyrolyzed eucalyptus wood-derived biochar at different temperatures.
Temperature (°C)Yield (%)Ash (%)(VM) (%)pH (CaCl2)EC µS/cm
45042.76 ± 0.540.60 ± 0.00130.32 ± 1.095.3 ± 0.070123.3 ± 1.414
55038.00 ± 0.440.74 ± 0.01216.49 ± 0.206.7 ± 0.14297.4 ± 2.121
65034.69 ± 0.790.63 ± 0.00911.92 ± 0.509.7 ± 0.260134.3 ± 1.697
75034.27 ± 0.440.84 ± 0.0025.52 ± 0.679.8 ± 0.035164.6 ± 1.272
85032.44 ± 0.370.82 ± 0.0123.43 ± 0.659.1 ± 0.106161.6 ± 1.187
95033.47 ± 0.611.06 ± 0.0313.63 ± 0.749.2 ± 0.084273.1 ± 1.626
Correlation−0.90 *0.89 *−0.90 *0.83 *0.85 *
* indicates significant correlations (p ≤ 0.05). N = 3; data are presented as mean ± stand deviation.
Table
Table 2. Eucalyptus wood-derived biochar inorganic minerals produced at different pyrolysis temperatures.
Table 2. Eucalyptus wood-derived biochar inorganic minerals produced at different pyrolysis temperatures.
Temperature (°C)K (%)Ca (%)P (%)Fe (%)S (%)Mn (%)Zn (%)Cr (%)Si (%)
4500.182 ± 0.0010.085 ± 0.0020.016 ± 0.0020.001 ± 0.00030.014 ± 0.0010.002 ± 0.0002
5500.140 ± 0.0070.104 ± 0.0010.016 ± 0.0240.003 ± 0.00030.013 ± 0.0010.003 ± 0.0001 0.045 ± 0.0007
6500.164 ± 0.0010.115 ± 0.0040.023 ± 0.0010.006 ± 0.00020.016 ± 0.00070.003 ± 0.00010.0002 ± 0.000060.002 ± 0.0001
7500.210 ± 0.0030.130 ± 0.0020.017 ± 0.0010.006 ± 0.00070.010 ± 0.00070.003 ± 0.0002
8500.210 ± 0.0040.104 ± 0.0020.025 ± 0.00030.004 ± 0.00010.016 ± 0.00070.002 ± 0.0002
9500.286 ± 0.0110.176 ± 0.0040.031 ± 0.0020.004 ± 0.00010.013 ± 0.00140.003 ± 0.0002
Correlation0.82 *0.82 *0.84 *0.51−0.050.21
* indicates significant correlations (p ≤ 0.05). N = 3; data are presented as mean ± stand deviation.
Table
Table 3. Elemental analysis, specific surface area (SSA), and total pore volume (TPV) of pyrolyzed eucalyptus wood biochar at different temperatures.
Table 3. Elemental analysis, specific surface area (SSA), and total pore volume (TPV) of pyrolyzed eucalyptus wood biochar at different temperatures.
Temperature (°C)Elemental AnalysisSSA and TPV
C (%)H (%)O (%)N (%)H/CO/C(O + N)/CSSA (m2 g−1)TPV (mm3 g−1)
45074.96 ± 0.073.76 ± 0.3819.41 ± 0.691.25 ± 0.210.050 ± 0.0050.25 ± 0.0090.27 ± 0.006
55079.25 ± 0.241.00 ± 0.1418.01 ± 0.781.49 ± 0.680.012 ± 0.0010.22 ± 0.010.25 ± 0.001
65087.06 ± 0.681.60 ± 0.4110.70 ± 0.270.000.018 ± 0.0040.12 ± 0.0040.12 ± 0.004410.48 ± 0.820.05 ± 0.002
75087.74 ± 0.910.87 ± 0.109.47 ± 0.811.06 ± 0.0070.019 ± 0.0010.11 ± 0.010.12 ± 0.01402.51 ± 0.910.07 ± 0.003
85088.01 ± 1.030.89 ± 0.248.99 ± 0.251.27 ± 0.510.010 ± 0.0020.10 ± 0.0040.14 ± 0.01362.90 ± 1.410.08 ± 0.003
95086.90 ± 0.130.90 ± 0.0410.57 ± 0.111.34 ± 0.1830.002 ± 0.00050.12 ± 0.0010.17 ± 0.01224.43 ± 2.900.02 ± 0.002
Correlation0.84 *0.720.84 *0.08−0.80−0.85 *−0.81−0.89 *−0.34
* indicates significant correlations (p ≤ 0.05). N = 3; data are presented as mean ± stand deviation.
Table
Table 4. Absorption peak intensity as a function of the wavelength and the pyrolysis temperature of eucalyptus wood biochar.
Table 4. Absorption peak intensity as a function of the wavelength and the pyrolysis temperature of eucalyptus wood biochar.
FT-IR Peak (cm−1)Pyrolysis Temperature (°C)VibrationReferences
450550650750850950
3.424StrongMediumWeakMediumMedium WeakO–H Alcohol or phenol[56]
2.920WeakWeak----CH2–CH3 Aliphatic[52]
1.638WeakWeakMediumStrongStrongStrongC=C[52]
1.604MediumMediumWeak---C=O/C=C Aromatics, ketones [55]
1.430StrongStrongWeakWeakWeakWeakC–H carboxymethyl-cellulose[57]
870WeakWeakStrongWeakWeakWeakC–H in polycyclic aromatic [58]
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Chaves Fernandes, B.C.; Ferreira Mendes, K.; Dias Júnior, A.F.; da Silva Caldeira, V.P.; da Silva Teófilo, T.M.; Severo Silva, T.; Mendonça, V.; de Freitas Souza, M.; Valadão Silva, D. Impact of Pyrolysis Temperature on the Properties of Eucalyptus Wood-Derived Biochar. Materials 2020, 13, 5841. https://doi.org/10.3390/ma13245841

AMA Style

Chaves Fernandes BC, Ferreira Mendes K, Dias Júnior AF, da Silva Caldeira VP, da Silva Teófilo TM, Severo Silva T, Mendonça V, de Freitas Souza M, Valadão Silva D. Impact of Pyrolysis Temperature on the Properties of Eucalyptus Wood-Derived Biochar. Materials. 2020; 13(24):5841. https://doi.org/10.3390/ma13245841

Chicago/Turabian Style

Chaves Fernandes, Bruno Caio, Kassio Ferreira Mendes, Ananias Francisco Dias Júnior, Vinícius Patrício da Silva Caldeira, Taliane Maria da Silva Teófilo, Tatiane Severo Silva, Vander Mendonça, Matheus de Freitas Souza, and Daniel Valadão Silva. 2020. "Impact of Pyrolysis Temperature on the Properties of Eucalyptus Wood-Derived Biochar" Materials 13, no. 24: 5841. https://doi.org/10.3390/ma13245841

APA Style

Chaves Fernandes, B. C., Ferreira Mendes, K., Dias Júnior, A. F., da Silva Caldeira, V. P., da Silva Teófilo, T. M., Severo Silva, T., Mendonça, V., de Freitas Souza, M., & Valadão Silva, D. (2020). Impact of Pyrolysis Temperature on the Properties of Eucalyptus Wood-Derived Biochar. Materials, 13(24), 5841. https://doi.org/10.3390/ma13245841

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop