Next Article in Journal
Effects of TiB2 Particles on the Microstructure Evolution and Mechanical Properties of B4C/TiB2 Ceramic Composite
Next Article in Special Issue
Biochemical Interaction between Materials Used for Interim Prosthetic Restorations and Saliva
Previous Article in Journal
Stress Impact of the Annealing Procedure of Cu-Filled TSV Packaging on the Performance of Nano-Scaled MOSFETs Evaluated by an Analytical Solution and FEA-Based Submodeling Technique
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 14
Issue 18
10.3390/ma14185225
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Cytotoxic and Genotoxic Effects of Composite Resins on Cultured Human Gingival Fibroblasts

by
Francesco De Angelis
1,†,
Domitilla Mandatori
1,2,†,
Valeria Schiavone
1,2,
Francesco Paolo Melito
1,2,
Silvia Valentinuzzi
2,3,
Mirco Vadini
1,
Pamela Di Tomo
1,2,
Lorenzo Vanini
1,
Letizia Pelusi
1,2,
Caterina Pipino
1,2,
Piero Del Boccio
2,3,
Camillo D’Arcangelo
1,‡ and
Assunta Pandolfi
1,2,*,‡
1
Department of Medical, Oral and Biotechnological Sciences, University “G. d’Annunzio” of Chieti-Pescara, 66100 Chieti, Italy
2
Center for Advanced Studies and Technology—CAST (ex CeSI-MeT), University “G. d’Annunzio” of Chieti-Pescara, 66100 Chieti, Italy
3
Department of Pharmacy, University “G. d’Annunzio” of Chieti-Pescara, 66100 Chieti, Italy
*
Author to whom correspondence should be addressed.
†
These authors contributed equally to this work.
‡
These authors also contributed equally to this work.
Materials 2021, 14(18), 5225; https://doi.org/10.3390/ma14185225
Submission received: 3 August 2021 / Revised: 2 September 2021 / Accepted: 8 September 2021 / Published: 11 September 2021
(This article belongs to the Special Issue Behaviour of Dental Composite Materials)
Browse Figures
Review Reports Versions Notes

Abstract

:
The aim of the study was to evaluate the cytotoxic and genotoxic potential of five commercially available dental composite resins (CRs), investigating the effect of their quantifiable bisphenol-A-glycidyl-methacrylate (Bis-GMA) and/or triethylene glycol dimethacrylate (TEGDMA) release. Experiments were performed using the method of soaking extracts, which were derived from the immersion of the following CRs in the culture medium: Clearfil-Majesty-ES-2, GrandioSO, and Enamel-plus-HRi (Bis-GMA-based); Enamel-BioFunction and VenusDiamond (Bis-GMA-free). Human Gingival Fibroblasts (hGDFs) were employed as the cellular model to mimic in vitro the oral cavity milieu, where CRs simultaneously release various components. Cell metabolic activity, oxidative stress, and genotoxicity were used as cellular outcomes. Results showed that only VenusDiamond and Enamel-plus-HRi significantly affected the hGDF cell metabolic activity. In accordance with this, although no CR-derived extract induced a significantly detectable oxidative stress, only VenusDiamond and Enamel-plus-HRi induced significant genotoxicity. Our findings showed, for the CRs employed, a cytotoxic and genotoxic potential that did not seem to depend only on the actual Bis-GMA or TEGDMA content. Enamel-BioFunction appeared optimal in terms of cytotoxicity, and similar findings were observed for Clearfil-Majesty-ES-2 despite their different Bis-GMA/TEGDMA release patterns. This suggested that simply excluding one specific monomer from the CR formulation might not steadily turn out as a successful approach for improving their biocompatibility.

1. Introduction

Dental restorative materials based on composite resins (CRs) are commonly used to perform adhesive restorations, with direct or indirect techniques. Being bonded to tooth structures, they allow for the preservation of sound dental tissues and represent an excellent aesthetic solution which can easily be repaired even after many years. However, following their widespread diffusion, increasing doubts have been raised over the last years about their safety [1,2].
Biocompatibility is the ability of a material to induce an appropriate biological response following a specific application [3]; it is a complex and dynamic process that can change over time due to the interaction between the host environment (the patient), the material, and the function that it should perform. Under this perspective, almost every material that is placed in the oral cavity cannot be considered as inert; when in contact with a tissue, they may interact and a biological response may be generated. In this context, several in vitro studies have shown that some components included in CRs can be potentially cytotoxic [1,4,5,6,7]. In particular, CRs are composed of an organic polymeric matrix, fillers (inorganic particles such as crystalline quartz, pyrogenic silica, glasses of barium, zinc and strontium, ceramic), bonding agents, pigments, catalysts, and inhibitors [8]. Organic components present in the matrix, above all bisphenol-A-glycidyl-methacrylate (Bis-GMA) derived monomers, but also triethylene glycol dimethacrylate (TEGDMA), urethane dimethacrylate (UDMA), and 2-hydroxyethyl methacrylate (HEMA), seem able to affect the biological compatibility [2,9,10,11]. Indeed, although methacrylate compounds are commonly employed to improve clinically relevant CR features such as viscosity, flexural strength, water sorption/solubility, and volumetric shrinkage [12], several adverse effects have been associated with their use. The potential cytotoxicity of the CR organic components is mainly due to the residues of free methacrylate monomers following the phase of polymerization, which may trigger the production of prostaglandin E2 (PGE2), the expression of cyclooxygenase 2 (COX2), and a pro-inflammatory activation through the increase of interleukin-1β (IL-1β), IL-6, and nitric oxide (NO) [13,14,15]. Direct CR restorations are light-cured at body temperature, while indirect restorations are subjected to supplementary heat-curing cycles, and both seem to undergo an additional post-curing process at body temperature after restoration placement [16]. The final degree of conversion value has been reported to widely range between 50% and 90%, 24 h after light-curing [17]. This incomplete reaction leads to the release of monomers into the oral cavity during a variable period [18]. Subsequently, in later stages, biocompatibility can be further influenced by other factors such as erosion, degradation, and the presence of bacteria at the interface between restoration and dental tissues [11,18,19,20,21,22,23].
Beyond the biological effect of resin monomers, great attention has also recently been focused on the cytotoxic potential of nano-fillers within nanofilled/nanohybrid CRs [24,25,26,27,28,29,30], which seem to be dependent on particle size, surface area and structure, chemical composition, solubility, shape, and aggregation. Small agglomerates or the non-agglomerated form may easily penetrate physiological barriers and travel within the circulatory systems of a host [31]; in an agglomerate state, nanoparticles appear less dangerous.
As a response to the potential hazards due to cytotoxic free monomers and/or non-agglomerated nanoparticles, numerous efforts have been made by manufacturers over the last years to provide alternative solutions that could reduce CR cytotoxicity. One possible approach could be the exclusion of some well-known cytotoxic components from the CR formulation; Bis-GMA-free composites have also been made commercially available for several years. Nevertheless, the real effect on living cells of every new CR formulation that is placed on the market is not always completely foreseeable and would definitely benefit from any possible additional investigation.
To date, most of the studies on dental composite cytotoxicity and genotoxicity have dealt with the effects of single CR components [32,33,34]. However, less information is available about cytotoxicity, ROS release, or DNA damages induced by composite extracts (or soaking media), which consist of multiple components. Indeed, extract-based experiments might represent a better option than single-component experiments, since they mimic a situation that more closely resembles the oral milieu [2].
Based on these, the aim of this in vitro study was to evaluate, by means of the dental composite extract approach, the potential cytotoxic effects of five different CRs on hGDFs, while investigating the effects of the Bis-GMA and/or TEGDMA content. Experiments were carried out taking into account cell metabolic activity, reactive oxygen species (ROS) production, and genotoxicity (phosphorylated-Gamma-H2A histone, γH2AX cell expression) outcomes.

2. Materials and Methods

2.1. Realization of Composite Disks and Soaking Extracts

The list of the five CRs (Bis-GMA based or free) selected for the study is given in Table 1. The cytotoxic and genotoxic effects of CRs on hGDFs were tested using the soaking-derived extracts, which were produced according to the International Organization for Standardization (ISO; no. 10993-5:2009).
Cylindrical composite disks were manufactured for each CR, having a total surface of 50.27 mm2 (diameter 4 mm, height 2 mm), positioning the uncured material in different polyvinylsiloxane molds. To avoid contamination, a different mold was used for every different type of resin. Then, molds were inserted between two glass slides and stuck with a paper clip for 20 s to extrude the excess material.
The disks were light-cured for 40 s from the upper surface using a lamp (Celalux 3, VOCO, Cuxhaven, Germany) with an 8 mm diameter tip and an output power of 1300 mW/cm2, and were kept dry for 24 h, sterilized under a hood, by UV radiation, for 15 min on each side [35].
For every different composite, 2 CR disks with a 50.27 mm2 surface were placed in a plastic tube with 1 mL of culture medium composed of Dulbecco’s Modified Eagle Medium (DMEM) low glucose (cat. D6046, Sigma-Aldrich, Saint Louis, MO, USA), supplemented with 10% fetal bovine serum (FBS), 100 mM glutamine (L-Glu), and 1% penicillin/streptomycin (P/S) (CTRL). This led to a ratio between the surface area of exposed composite disks and the volume of the culture medium equal to 100.54 mm2/mL. CR disks were kept immersed in the control medium for 24 h and 14 days (CR soaking extracts) at 37 °C in static conditions (Figure 1).

2.2. Soaking Extract Preparation for LC–MS/MS Analysis

The actual presence or not of Bis-GMA and TEGDMA in the soaking extracts was investigated through LC–MS/MS analysis, which required the following procedures. A total of 200 µL of soaking samples underwent protein precipitation with 3 volumes (600 µL) of cold methanol following incubation on ice for 30 min; samples were centrifuged for 30 min at 13,000× g (4 °C), and supernatants were evaporated to dryness under nitrogen.
Finally, residues were reconstituted with 2 volumes (400 µL) of acetonitrile:water (ACN:H20) 30:70 (v/v) containing 0.1% formic acid (FA). For quantitative purposes, a calibration curve was assessed, preparing calibration standards in a culture medium DMEM supplemented with 10% FBS, 100 mM L-Glu, and 1% P/S, with known concentrations of TEGDMA and Bis-GMA provided by Sigma-Aldrich (linear range 0.8–100 ng/mL, r2 = 0.997 for TEGDMA; linear range 3–800 ng/mL, r2 = 0.984 for Bis-GMA). Samples were analyzed in triplicates as they were for the TEGDMA determination and diluted 1:10 for Bis-GMA quantification; hence, standard concentrations covered the entire range of possible concentrations encountered during the analysis. The analytical blank consisted of the cell culture media without the presence of composite materials. The limit of quantification (LOQ) was 0.8 ng/mL for TEGDMA and 3 ng/mL for Bis-GMA.

2.3. LC–MS/MS Analysis

LC–MS/MS analysis was carried out following the work of Polydorou et al. [36] and using an Alliance High Throughput (HT) 2795 HPLC system (Waters Corp., Milford, MA, USA) coupled with a Micromass Quattro Ultima Pt mass spectrometer (Waters Corp., Milford, MA, USA). Five µL of samples were injected at a flow rate kept at 250 µL/minute, and analytes were separated on a Phenomenex Luna 3μ C8 (2) 100 Å HPLC column (50 × 4.6 mm) (Phenomenex, Castel Maggiore, Italy) with a SecurityGuard™ cartridge (Phenomenex, Castel Maggiore, Italy). The binary gradient consisted of (A) H2O and (B) ACN, both containing 0.1% FA, using the following conditions: 30% B, isocratic for 1 min; linear increase to 95% B within 6 min; linear increase to 99% B within 2 min, kept for 1 min; return to the initial condition within 6 min and kept for 5 min. Mass Spectrometry (MS) parameters used to acquire in multiple reaction monitoring (MRM) mode are listed in Table 2, in terms of cone potential, collision energy, and parent/daughter ion transitions. Data acquisition was performed in positive electrospray ionization mode (ESI+), with a total run time of 21 min, injection-to-injection. Raw data were processed by QuanLynx™ (Waters Corp., Milford, MA, USA). Representative MS/MS spectrum and extracted ion chromatogram (EIC) for both the analytes are shown in Supplementary Figure S1.

2.4. Cell Culture

The cytotoxicity of the five CRs was assessed on hGDFs isolated from human gingival biopsies obtained from seven patients undergoing partial gingivectomy procedures in the dental clinic of the University G. D’Annunzio Chieti-Pescara (CE, N° 1968-24/07/2020). Briefly, gingival specimens were subjected to an enzymatic digestion for 1 h at 37 °C using a solution of collagenase type 1A (Sigma Aldrich, Saint Louis, MO, USA) and dispase (Sigma Aldrich, Saint Louis, MO, USA).
Then, the residual gingival samples were placed in a petri dish with the culture medium (CTRL) to favor a final spontaneous migration of the cells. The isolated hGDFs were grown in a controlled atmosphere (5% CO2 and 37 °C) upon reaching the confluence and were used for all experiments between the 3° and the 6° passage.
The characterization of hGDFs was performed by evaluating the expression of the following markers: CD105 (FITC-conjugated antibody; Becton Dickinsons BD Bioscience, cat.326-040), CD73 (PE-conjugated antibody; Becton Dickinsons BD Bioscienc, cat.550257), CD90 (FITC-conjugated antibody; Becton Dickinsons BD Bioscience, cat.555595), CD326 (PerCP-Cy5.5-conjugated antibody; Becton Dickinsons BD Bioscience, cat.347199), and CD45 (FITC-conjugated antibody; Becton Dickinsons BD Bioscience, cat.196-040). FACSVerse (BD Bioscences, San Jose, CA, USA), FACSDiva v 6.1.3, IDEAS software (BD Biosciences, San Jose, CA, USA), and FlowJo 8.3.3 software (Tree Star Inc, Ashland, OR, USA) were used for the cytometric analysis.
For cellular experiments, hGDFs were treated for 48 h with the culture medium (CTRL condition) or with the soaking extracts derived from the five selected CRs, obtained at two different times of soaking (24 h and 14 days), as previously reported. Soaking extracts were used at three different concentrations (100%, 50%, and 25%) (Figure 1).

2.5. 3-(4, 5-dimethylthiazolyl-2-yl)-2, 5-diphenyltetrazolium Bromide (MTT) Cell Viability Analysis

The effect of the CR soaking extracts on hGDF metabolic activity was assessed by performing the MTT assay (cat. M211281G, Sigma Aldrich), according to the manufacturer’s instructions.
Cells were seeded in a 96-well plate at the density of 5000 cells/well (20,000 cells/mL) and were incubated with the culture medium (CTRL) or CR extracts (100%, 50%, and 25%) obtained at soaking times of 24 h and 14 days. After 48 h of treatment, 20 µL of MTT solution (5 mg/mL) were added to each well and incubated for 3 h at 37 °C. Then, 200 µL of Dimethyl sulfoxide (DMSO) were added (30 min at 37 °C) and the spectrophotometric reading was carried out at a wavelength of 540 nm using a microplate absorbance reader (SpectraMAX 190, Molecular Devices, San Jose, CA, USA).

2.6. Reactive Oxygen Species (ROS) Flow Cytometry Analysis

ROS released by hGDFs cells (20,000 cells/mL) were measured following the treatment with the culture medium (CTRL) or the CR extracts (100%, 50%, and 25%) obtained at soaking times of 24 h and 14 days. The hydrogen peroxide (H2O2, 300 µM for 30 min) was used as positive control. After 48 h of exposure, cells were collected and stained using the cell fluorescent reagent “CellROXTM Green Reagent” (C10444, Molecular Probes, ThermoFisher Scientific, MA, USA) at 2.5 µM in PBS for 30 min at 37 °C. Each sample was processed using a FACS Canto II flow cytometer (BD Bioscences, San Jose, CA, USA). All data were analyzed using FACSDiva v 6.1.3, IDEAS software (BD Biosciences) and FlowJo 8.3.3 software (Tree Star Inc., Ashland, OR, USA). The results were obtained as an MFI (Mean Fluorescence Intensity) Ratio calculated by dividing the MFI of positive events by the MFI of negative events (MFI of secondary antibody).

2.7. γH2AX Evaluation by Immunofluorescence

Immunofluorescence analysis was used to evaluate DNA damage induced in the hGDFs treated with the culture medium (CTRL) or the undiluted CR-derived extracts obtained at soaking times of 24 h and 14 days. Doxorubicine (DOXO, 1µM for 30 min) was used as a positive control. The level of γH2AX was detected by immunostaining with γH2AX (Ser139) primary antibody (1:800, Cell Signaling Technology, Danvers, MA, USA) and Alexa Fluor 488 anti-rabbit secondary antibody (cat. A11034, Invitrogen, ThermoFisher Scientific, MA, USA). Immunofluorescence experiments were performed on hGDFs seeded on sterile glass cover slips (12 mm diameter) in 24-well plates (20,000 cells/well; 20,000 cells/mL). Following 48 h of treatment, cells were fixed in 4% Paraformaldehyde (10 min RT), permeabilized with Triton (0.1%; 10 min RT), stained with anti-γH2AX primary antibody (cat. 2577, Cell Signaling Technology; 1:800, overnight 4 °C) and with Alexa Fluor 488 anti-rabbit secondary antibody (cat. A11034, Invitrogen; 1:1000, 1 h RT). 4′, 6-diamidino-2-phenylindole (DAPI; cat. D9542, Sigma-Aldrich; 1:1000, 15 min RT) was used to stain the nuclei and to observe the cells through a confocal microscope (Zeiss LSM-800, Carl Zeiss Meditec AG, Oberkochen, Germany). Data, calculated as γH2AX percentage (%) of positive cells, were obtained by analyzing at least three different fields for each image with ImageJ software (NIH, US, ImageJ software).

2.8. Statistical Analysis

Data were expressed as mean ± standard error (SEM). Statistical analysis was performed using the Kruskal–Wallis and the Dunn’s post hoc tests. The Shapiro–Wilk normality test was used to verify the normal distribution of the data. The α value was set at 0.05. Analyses and graphs were performed using GraphPad Prism Software Analysis (version 6).

3. Results

3.1. Quantification of TEGDMA and Bis-GMA from Soaking Extracts by LC–MS/MS Analysis

Results from the quantification of TEGDMA and Bis-GMA by LC–MS/MS analysis on soaking extracts obtained by the immersion of CRs in culture media (24 h and 14 days; scheme in Figure 1) are shown in Figure 2.
As reported in Figure 2a, observable levels of TEGDMA were found only after 24 h of exposure to VD and VOCO resins (1.2 ng/mL and 7.9 ng/mL, respectively).
On the other hand, the quantification of Bis-GMA revealed a detectable concentration of this monomer, not only at the first time point but also after 14 days of immersion (Figure 2b). More specifically, Bis-GMA levels were found to be higher than 70 ng/mL and 800 ng/mL in all the samples after 24 h and 14 days of exposure, respectively. A general upward trend, following the soaking time, is appreciable, except for samples exposed to the VOCO composite; concerning UE and ES-2, the growing measure of Bis-GMA reached dramatically high concentrations by µg/mL orders of magnitude. Interestingly, the difference of the Bis-GMA levels at the two soaking times was found to be statistically significant for the VD (p-value: 0.0003), ES-2 (p-value: 0.02), and BF-2 (p-value < 0.0001) resins.

3.2. Effects of CRs on hGDFs Viability

Before setting up the cell metabolic activity experiments, hGDFs were firstly characterized for their phenotype. As shown in Figure 3a, cells obtained from gingival biopsies through our combined isolation method based on enzymatic digestion and spontaneous migration exhibited the characteristic fibroblast-like morphology and expressed the typical markers CD105, CD73, CD90, but not CD45 and the epithelial marker CD326 (Figure 3b).
Successively, based on the experimental plan reported in Figure 1, hGDFs were treated for 48 h with the two soaking times for extracts (24 h and 14 days) derived from each type of CR.
As shown in Figure 4, the treatment with all three concentrations (100%, 50%, and 25%) of the BF-2, VOCO, and ES-2 extracts (24 h and 14 days: Figure 4a,b respectively) did not induce significant effects on cells metabolic activity. On the other hand, the Bis-GMA free resin VD and the Bis-GMA-based UE significantly reduced cell numbers compared to the basal condition (CTRL) at both soaking times (Figure 4).

3.3. Effects of Dental Resins on the hGDF Cell ROS Production

The ROS cytometric analysis revealed that the BF-2, VOCO, and ES-2-derived extracts induced a slight increase in oxidative stress, which did not reach statistical significance compared to basal conditions (CTRL; at both times of soaking used (24 h and 14 days; Figure 5a,b respectively).
As regards the VD and UE resins, the low number of metabolically active cells induced by the treatment with undiluted extracts did not allow ROS quantification in both experimental conditions. However, the exposure to their dilution (50% and 25%) reduced the hGDF mortality and, notably, the ROS levels, at soaking times of 14 days in both cases; levels comparable to those induced by the positive control H2O2 were also reached (Figure 5b).

3.4. Effects of Dental Resins on Phosphorylated γH2AX

In order to better investigate the effects of CRs, a possible DNA damage induced in hGDFs cells was investigated through the evaluation of the γH2AX expression. Worthy of note is the fact that compared to CTRL (basal condition), the treatment with the undiluted extracts of almost every CR increased the percentage of positive cells for γH2AX (Figure 6a,b).
DOXO was employed as positive control, and the percentage of positive cells for γH2AX in cell cultures treated for 48 h with VOCO (24 h extracts) and ES-2 (24 h and 14 day extracts) was significantly lower compared to DOXO condition (Figure 6a,b). The Bis-GMA free resin VD increased the percentage of positive cells for γH2AX at both times of soaking, while, as expected, the resin UE showed significance with the 14-day soaking extract treatment.
All these results were confirmed by representative immunofluorescence images showed in Figure 6a,b.

4. Discussion

Cytotoxicity evaluation is one of the essential tests used to assess the biocompatibility of materials that have to be employed on human beings. Nowadays, despite the undiscussed popularity of dental CRs, there are increasing concerns about the potential cytotoxicity and genotoxicity of the components that these materials may release [2,9,10,11,18,19,20,21,22,23].
In relation to this, Bis-GMA and other methacrylate monomers such as TEGDMA are the most commonly employed in composite material fabrication since they allow for the positive adjustment of clinically relevant features such as viscosity, flexural strength, water sorption/solubility, and volumetric shrinkage [12]. However, a wide range of adverse effects have been associated with their use. In particular, several in vitro studies demonstrated that Bis-GMA may stimulate the production of PGE2, COX2 expression, and the pro-inflammatory activation of IL-1β, IL-6, and NO [13,14,15]. As a consequence, the attempt to switch towards Bis-GMA-free composite materials has become of particular interest for manufacturers in order to minimize the cytotoxic potential of their products.
For this reason, in the present study, after having assessed the quantifiable methacrylate Bis-GMA and TEGDMA residual monomers, the effects of the soaking extracts obtained from five commercially available dental CRs (Table 1) were tested in terms of cytotoxicity, ROS production, and DNA damages. To this aim, a cellular model of primary isolated human gingival fibroblasts (hGDFs; Figure 1) was used. In particular, the cells were not placed in direct contact with the CRs but were treated with the soaking extracts obtained from the immersion of dental CR disks in the culture medium for 24 h and 14 days. Indeed, this experimental method simulated a condition closer to the oral milieu [2], where the oral soft tissues could be negatively affected by the residual monomers derived from the various CR components following saliva interaction [37]; this resulted in the most commonly used approach in the literature at the moment [38,39].
First of all, although the CRs selected for the study presented various components (Table 1) in their formulation that could influence the CR properties, we confirmed by LC–MS/MS analysis of our soaking extracts the actual residual (or not) of the most common methacrylate monomers, with potential cytotoxicity employed in dental resin formulations such as Bis-GMA and TEGDMA.
Our results showed that observable levels of TEGDMA monomers were found only after 24 h of exposure to VD and VOCO resins. The higher amount of residual TEGDMA monomer found within the first 24 h is in accordance with the evidence that small molecular weight monomers such as TEGDMA have higher mobility and polarity that enable them to be released faster than other large molecules; thus, TEGDMA-based CRs can release a high quantity of monomers into aqueous environments, as already reported by Moharamzadeh K et al. [40]. The same authors demonstrated that TEGDMA monomers disappear after seven days of incubation of TEGDMA-based CRs in culture media due to their enzymatic degradation and aggregation, mainly with albumin. Our data agree with this phenomenon, showing undetectable levels of TEGDMA monomers after 14 days of exposure (Figure 2a). Based on these observations, we can speculate that enzymatic degradation and protein aggregation occurring in culture media over time could lead to a decrease in the measurable TEGDMA monomer by our LC–MS/MS method. Therefore, more in-depth kinetic studies of this phenomenon are needed to better evaluate the cytotoxicity of different TEGDMA isoforms and derivatives. In this context, further proof is provided by several other studies demonstrating that an enzyme-catalyzed hydrolysis of CRs can occur by esterases, as those typically present in inflammatory sites and saliva. Accordingly, the complexity and enzymatic heterogeneity of serum-addicted culture media can mimic the rate of hydrolysis in methacrylate-based polymers, as shown by Finer and Santerre in terms of decreasing the amount of the residual TEGDMA monomer by esterases when compared to PBS soaking [41,42]. On the other hand, regarding the increasing levels of Bis-GMA, there is a general consensus that esterases do not show the same specificity for monomers and that CR degradation relies on the specific enzyme dose response [43].
Actually, Bis-GMA monomers were found at noticeable concentrations at both 24 h and 14 days of exposure, in almost all the investigated CRs (Figure 2b). These data confirmed the presence of such a compound in the composition of the investigated resins and are in partial agreement with their specific manufactures’ formulation reported in Table 1. Indeed, although BF-2 and VD CRs were indicated as Bis-GMA-free by their material composition declaration, through LC–MS/MS, low levels of Bis-GMA monomers were measured in both the resins. These results are consistent with data recently published by Šimková M and colleagues [44], and in agreement with this, it is important to point out that this study also showed the release percentage of Bis-GMA from Bis-GMA-free resins to be very low compared to the average release of other resins. Indeed, by contrast, the resins containing Bis-GMA (VOCO, UE, and ES-2) were associated with the release of high levels of monomers in the culture media, reaching concentrations of µg/mL orders of magnitude, which might be considered clinically relevant as their magnitude is close to the maximum levels of Bis-GMA clinically quantified in human saliva by Michelsen et al. (2.149 µg/mL) [45,46].
On the other hand, the residual percentage of Bis-GMA from Bis-GMA-free resins (BF-2 and VD) compared to the average release of others (considered 100%) is about 2% at 24 h and 15% at 14 days, respectively, for both CRs evaluated.
Focusing on cell metabolic activity, a 48 h exposure to the diluted or undiluted extracts of all CRs tested did not significantly affect this aspect, except for the VD and UE resins (Figure 4). Unexpectedly, the use of an undiluted extract (100%) coming from the Bis-GMA-free VD resin was comparable to the effect of the Bis-GMA-based UE, since both had the most harmful effect on cell cultures among the different experimental groups. On the contrary, the effect on hGDF metabolic activity of another Bis-GMA-free material tested in this study (BF-2) and the Bis-GMA-based material (VOCO and ES-2) were comparable to the control condition. Those data support the concept that simply excluding the monomer Bis-GMA from CR formulation does not provide a steadily successful approach for reducing their cytotoxicity, since side effects can still occur due to the presence of other chemical components in the CR formulation. Indeed, multiple factors might concurrently contribute to the ultimate CR profile, whose assessment should be better accomplished by focusing on the whole material formulation instead of its individual components, thus opening the way for the in-depth investigation of such products and their effects.
To support this, a previous study reported that all the different components simultaneously present in the complex CR composition may induce effects that are different from what is expected by their action alone, as they could mutually influence one another through synergistic and/or antagonistic behaviors [22]. Therefore, an experimental plan based on the soaking of derived extracts, such as the one selected for this and for similar studies [2,38,39], appears to be the most suitable approach as it seems to better simulate a more clinically relevant scenario. However, future studies based on the approach of the direct contact between the CR disk and cells have been planned to confirm the role of dental resins at the cellular level.
Cell viability is not the only available outcome in the investigation of a potential cytotoxic effect towards cell cultures. The capability of resin monomers to influence cellular physiology and adaptive cell responses by increasing ROS production has already been reported by previous studies [33,47].
In this study, in accordance with cells metabolic activity results, ROS production induced by the exposure to undiluted extracts (Figure 5) was not even quantifiable in the VD and UE groups due to the extremely reduced number of living cells left after 48 h of treatment. However, it is important to underline that the cell treatments with the respective diluted extracts (50% and 25%) significantly increased fibroblast viability (Figure 5A,B), allowing for ROS quantification and suggesting a possible concentration-dependent mechanism, which could be used as a protective factor against their cytotoxic effects. Regarding BF-2, VOCO, and ES-2, a relatively low oxidative stress was recorded in these experimental groups since a ROS production comparable to the control was observed following the exposure to their respective 24-h and 14-day derived extracts.
An additional way through which CRs may express their cytotoxic potential is represented by their capability to induce DNA damages such the DNA-Double Strand Breaks (DNA-DSBs) [48]. Therefore, the biological impact of our selected CRs was better investigated trough the evaluation of γH2AX expression, which is the early step in response to the induction of DNA-DSBs and its resulting damage [49].
As expected, immunofluorescence data confirmed that soaking extracts derived from BF-2, VOCO, and ES-2 were less genotoxic compared to VD and UE (Figure 6). Interestingly, despite VD being a Bis-GMA-free resin, it was the only resin characterized by a higher level of genotoxicity compared to the DOXO positive control at both times of soaking (24 h and 14 days), confirming its enhanced cytotoxic potential compared to the other CRs tested.
It is important to underline that the present results are in line with what was observed by other research groups regarding the effect of CRs on oxidative stress [50] as well as cytotoxicity and genotoxicity [4,35,51]. Furthermore, we also confirmed data related to cell metabolic activity and ROS release by applying the same soaking-extracts approach to a murine fibroblast model (Balb/c-3T3 cells purchased from ATCC®, LGC Standards S.r.l.) (Figure S2). Indeed, VD and UE resins showed the highest cytotoxic potential, as far as the murine model was concerned and toward cells not belonging to the oral cavity, while BF-2, VOCO, and ES-2 again appeared as the most biocompatible resins (Figure S1).
Overall, these results confirm an extended potential cytotoxicity of CRs in vitro. However, we may suppose that the present findings, especially the worst cytotoxic effects herein observed, might be somewhat modulated following the clinical application of CRs in vivo, where oral cells and tissues can actively respond to monomer-induced stress with the activation of specific adaptive pathways. Therefore, further studies on the mechanisms underlying adaptive cell responses seem mandatory in order to improve the properties of dental restorative materials that encounter oral tissues and to develop effective strategies in dental therapy.

5. Conclusions

Enamel-BioFunction appeared definitely optimal in terms of cytotoxic effects. Similar findings were observed for Clearfil Majesty ES-2, despite the two resins showing different Bis-GMA/TEGDMA release patterns. Overall, our findings confirmed that the investigated CRs present cytotoxic and genotoxic potential, which do not only seem dependent on their actual Bis-GMA or TEGDMA release. Likewise, Enamel-plus HRi seemed notably more cytotoxic and genotoxic compared to Clearfil Majesty ES-2, notwithstanding their similar monomer releases. This suggests that simply excluding one specific and potentially cytotoxic monomer from CR formulation, such as Bis-GMA, might not steadily provide a successful approach for the improvement of their properties, which depends on the whole chemical composition of the material.

Supplementary Materials

The following are available online at https://www.mdpi.com/article/10.3390/ma14185225/s1, Figure S1: LC–MS/MS data for TEGDMA and Bis-GMA; Figure S2: Effects of CRs on Balb/c 3T3.

Author Contributions

Conceptualization, F.D.A., D.M., C.D. and A.P.; methodology, F.D.A., D.M., V.S., F.P.M., S.V., P.D.T. and L.P.; formal analysis, F.D.A., D.M., S.V., P.D.B.; writing—original draft preparation, F.D.A., D.M.; writing—review and editing M.V., L.V., C.P., P.D.B., C.D. and A.P.; supervision, C.D. and A.P.; funding acquisition, C.D. and A.P. All authors have read and agreed to the published version of the manuscript.

Funding

This research was partially funded by POR FESR ABRUZZO 2014–2020 Asse I Determinazione (SANI) number: 39 DPG013/12222017.

Institutional Review Board Statement

The study was conducted according to the guidelines of the Declaration of Helsinki, and approved by the Institutional Review Board (or Ethics Committee) of University G. d’Annunzio Chieti-Pescara, Italy (protocol code CE, N° 1968-24/07/2020).

Informed Consent Statement

Informed consent was obtained from all subjects involved in the study.

Data Availability Statement

Data available on request.

Acknowledgments

The authors would like to acknowledge Bologna Giuseppina, for her technical support.

Conflicts of Interest

The authors declare no potential conflict of interest with respect to the authorship and/or publication of this article.

References

  1. Ferracane, J.L. Resin composite—State of the art. Dent. Mater. 2011, 27, 29–38. [Google Scholar] [CrossRef] [PubMed]
  2. Yang, Y.; Reichl, F.-X.; Shi, J.; He, X.; Hickel, R.; Högg, C. Cytotoxicity and DNA double-strand breaks in human gingival fibroblasts exposed to eluates of dental composites. Dent. Mater. 2018, 34, 201–208. [Google Scholar] [CrossRef] [PubMed]
  3. Ratner, B.D. A pore way to heal and regenerate: 21st century thinking on biocompatibility. Regen. Biomater. 2016, 3, 107–110. [Google Scholar] [CrossRef] [Green Version]
  4. Longo, D.L.; Paula-Silva, F.W.G.; Faccioli, L.H.; Gatón-Hernández, P.M.; De Queiroz, A.M.; Da Silva, L.A.B. Cytotoxicity and cytokine expression induced by silorane and methacrylate-based composite resins. J. Appl. Oral Sci. 2016, 24, 338–343. [Google Scholar] [CrossRef]
  5. da Fonseca Roberti Garcia, L.; Pontes, E.C.; Basso, F.G.; Hebling, J.; de Souza Costa, C.A.; Soares, D.G. Transdentinal cytotoxicity of resin-based luting cements to pulp cells. Clin. Oral Investig. 2016, 20, 1559–1566. [Google Scholar] [CrossRef] [PubMed]
  6. Roman, A.; Páll, E.; Moldovan, M.; Rusu, D.; Şoriţău, O.; Feştilă, D.; Lupşe, M. Cytotoxicity of Experimental Resin Composites on Mesenchymal Stem Cells Isolated from Two Oral Sources. Microsc. Microanal. 2016, 22, 1018–1033. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  7. Peutzfeldt, A. Resin composites in dentistry: The monomer systems. Eur. J. Oral Sci. 1997, 105, 97–116. [Google Scholar] [CrossRef]
  8. Fong, H.; Dickens, S.H.; Flaim, G.M. Evaluation of dental restorative composites containing polyhedral oligomeric silsesquioxane methacrylate. Dent. Mater. 2005, 21, 520–529. [Google Scholar] [CrossRef]
  9. Wataha, J.C. Predicting clinical biological responses to dental materials. Dent. Mater. 2012, 28, 23–40. [Google Scholar] [CrossRef]
  10. Styllou, M.; Reichl, F.-X.; Styllou, P.; Urcan, E.; Rothmund, L.; Hickel, R.; Högg, C.; Scherthan, H. Dental composite components induce DNA-damage and altered nuclear morphology in gingiva fibroblasts. Dent. Mater. 2015, 31, 1335–1344. [Google Scholar] [CrossRef]
  11. Goldberg, M. In vitro and in vivo studies on the toxicity of dental resin components: A review. Clin. Oral Investig. 2008, 12, 1–8. [Google Scholar] [CrossRef]
  12. He, J.; Kopperud, H.M. Preparation and characterization of Bis-GMA-free dental composites with dimethacrylate monomer derived from 9, 9 -Bis[4-(2-hydroxyethoxy)phenyl]fluorene. Dent. Mater. 2018, 34, 1003–1013. [Google Scholar] [CrossRef]
  13. Kuan, Y.-H.; Huang, F.-M.; Lee, S.-S.; Li, Y.-C.; Chang, Y.-C. Bisgma stimulates prostaglandin E2 production in macrophages via cyclooxygenase-2, cytosolic phospholipase A2, and mitogen-activated protein kinases family. PLoS ONE 2013, 8, e82942. [Google Scholar] [CrossRef] [Green Version]
  14. Kuan, Y.-H.; Huang, F.-M.; Li, Y.-C.; Chang, Y.-C. Proinflammatory activation of macrophages by bisphenol A-glycidyl-methacrylate involved NFκB activation via PI3K/Akt pathway. Food Chem. Toxicol. 2012, 50, 4003–4009. [Google Scholar] [CrossRef]
  15. Huang, F.-M.; Chang, Y.-C.; Lee, S.-S.; Yeh, C.-H.; Lee, K.G.; Huang, Y.-C.; Chen, C.-J.; Chen, W.-Y.; Pan, P.-H.; Kuan, Y.-H. BisGMA-induced cytotoxicity and genotoxicity in macrophages are attenuated by wogonin via reduction of intrinsic caspase pathway activation. Environ. Toxicol. 2014, 31, 176–184. [Google Scholar] [CrossRef]
  16. Moore, R.; Watts, J.; Hood, J.; Burritt, D. Intra-oral temperature variation over 24 h. Eur. J. Orthod. 1999, 21, 249–261. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  17. Alshali, R.Z.; Silikas, N.; Satterthwaite, J.D. Degree of conversion of bulk-fill compared to conventional resin-composites at two time intervals. Dent. Mater. 2013, 29, e213–e217. [Google Scholar] [CrossRef]
  18. Schmalz, G.; Krifka, S.; Schweikl, H. Toll-like Receptors, LPS, and Dental Monomers. Adv. Dent. Res. 2011, 23, 302–306. [Google Scholar] [CrossRef] [PubMed]
  19. Perduns, R.; Volk, J.; Schertl, P.; Leyhausen, G.; Geurtsen, W. HEMA modulates the transcription of genes related to oxidative defense, inflammatory response and organization of the ECM in human oral cells. Dent. Mater. 2019, 35, 501–510. [Google Scholar] [CrossRef]
  20. Kleinsasser, N.H.; Schmid, K.; Sassen, A.W.; Harréus, U.A.; Staudenmaier, R.; Folwaczny, M.; Glas, J.; Reichl, F.-X. Cytotoxic and genotoxic effects of resin monomers in human salivary gland tissue and lymphocytes as assessed by the single cell microgel electrophoresis (Comet) assay. Biomaterials 2006, 27, 1762–1770. [Google Scholar] [CrossRef]
  21. Urcan, E.; Scherthan, H.; Styllou, M.; Haertel, U.; Hickel, R.; Reichl, F.-X. Induction of DNA double-strand breaks in primary gingival fibroblasts by exposure to dental resin composites. Biomaterials 2010, 31, 2010–2014. [Google Scholar] [CrossRef] [PubMed]
  22. Wisniewska-Jarosinska, M.; Poplawski, T.; Chojnacki, C.J.; Pawlowska, E.; Krupa, R.; Szczepanska, J.; Blasiak, J. Independent and combined cytotoxicity and genotoxicity of triethylene glycol dimethacrylate and urethane dimethacrylate. Mol. Biol. Rep. 2011, 38, 4603–4611. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  23. Kermanshahi, S.; Santerre, J.; Cvitkovitch, D.; Finer, Y. Biodegradation of Resin-Dentin Interfaces Increases Bacterial Microleakage. J. Dent. Res. 2010, 89, 996–1001. [Google Scholar] [CrossRef]
  24. Schmalz, G.; Hickel, R.; van Landuyt, K.L.; Reichl, F.-X. Scientific update on nanoparticles in dentistry. Int. Dent. J. 2018, 68, 299–305. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  25. Schmalz, G.; Hickel, R.; van Landuyt, K.L.; Reichl, F.-X. Nanoparticles in dentistry. Dent. Mater. 2017, 33, 1298–1314. [Google Scholar] [CrossRef]
  26. Noronha, V.; Paula, A.J.; Durán, G.; Galembeck, A.; Cogo-Muller, K.; Franz-Montan, M.; Durán, N. Silver nanoparticles in dentistry. Dent. Mater. 2017, 33, 1110–1126. [Google Scholar] [CrossRef]
  27. Priyadarsini, S.; Mukherjee, S.; Mishra, M. Nanoparticles used in dentistry: A review. J. Oral Biol. Craniofacial Res. 2018, 8, 58–67. [Google Scholar] [CrossRef] [Green Version]
  28. Cokic, S.; Duca, R.-C.; Godderis, L.; Hoet, P.; Seo, J.W.; Van Meerbeek, B.; Van Landuyt, K. Release of monomers from composite dust. J. Dent. 2017, 60, 56–62. [Google Scholar] [CrossRef] [PubMed]
  29. Schubert, A.; Ziegler, C.; Bernhard, A.; Burgers, R.; Miosge, N. Cytotoxic effects to mouse and human gingival fibroblasts of a nanohybrid ormocer versus dimethacrylate-based composites. Clin. Oral Investig. 2019, 23, 133–139. [Google Scholar] [CrossRef]
  30. Van Landuyt, K.L.; Cokic, S.M.; Asbach, C.; Hoet, P.; Godderis, L.; Reichl, F.X.; Van Meerbeek, B.; Vennemann, A.; Wiemann, M. Interaction of rat alveolar macrophages with dental composite dust. Part Fibre Toxicol. 2016, 13, 62. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  31. Nel, A.; Xia, T.; Mädler, L.; Li, N. Toxic potential of materials at the nanolevel. Science. 2006, 311, 622–627. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  32. Mahaney, B.L.; Meek, K.; Lees-Miller, S.P. Repair of ionizing radiation-induced DNA double-strand breaks by non-homologous end-joining. Biochem. J. 2009, 417, 639–650. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  33. Lottner, S.; Shehata, M.; Hickel, R.; Reichl, F.-X.; Durner, J. Effects of antioxidants on DNA-double strand breaks in human gingival fibroblasts exposed to methacrylate based monomers. Dent. Mater. 2013, 29, 991–998. [Google Scholar] [CrossRef]
  34. Tsitrou, E.; Kelogrigoris, S.; Koulaouzidou, E.; Antoniades-Halvatjoglou, M.; Koliniotou-Koumpia, E.; van Noort, R. Effect of extraction media and storage time on the elution of monomers from four contemporary resin composite materials. Toxicol. Int. 2014, 21, 89–95. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  35. Salehi, S.; Gwinner, F.; Mitchell, J.C.; Pfeifer, C.; Ferracane, J. Cytotoxicity of resin composites containing bioactive glass fillers. Dent. Mater. 2015, 31, 195–203. [Google Scholar] [CrossRef] [Green Version]
  36. Polydorou, O.; Huberty, C.; Wolkewitz, M.; Bolek, R.; Hellwig, E.; Kümmerer, K. The effect of storage medium on the elution of monomers from composite materials. J. Biomed. Mater. Res. Part B Appl. Biomater. 2012, 100, 68–74. [Google Scholar] [CrossRef]
  37. Șaramet, V.; Meleșcanu-Imre, M.; Țâncu, A.; Albu, C.; Ripszky-Totan, A.; Pantea, M. Molecular Interactions between Saliva and Dental Composites Resins: A Way Forward. Materials 2021, 14, 2537. [Google Scholar] [CrossRef]
  38. Bandarra, S.; Neves, J.; Paraíso, A.; Mascarenhas, P.; Ribeiro, A.C.; Barahona, I. Biocompatibility of self-adhesive resin cement with fibroblast cells. J. Prosthet. Dent. 2021, 705. [Google Scholar] [CrossRef]
  39. Landenberger, P.; Baumann, L.; Gerhardt-Szép, S.; Rüttermann, S. The effect of new anti-adhesive and antibacterial dental resin filling materials on gingival fibroblasts. Dent. Mater. 2021, 37, 1416–1424. [Google Scholar] [CrossRef]
  40. Moharamzadeh, K.; Van Noort, R.; Brook, I.M.; Scutt, A.M. HPLC analysis of components released from dental composites with different resin compositions using different extraction media. J. Mater. Sci. Mater. Electron. 2007, 18, 133–137. [Google Scholar] [CrossRef]
  41. Finer, Y.; Santerre, J.P. Biodegradation of a dental composite by esterases: Dependence on enzyme concentration and specificity. J. Biomater. Sci. Polym. Ed. 2003, 14, 837–849. [Google Scholar] [CrossRef]
  42. Shajii, L.; Santerre, J.P. Effect of filler content on the profile of released biodegradation products in micro-filled bis-GMA/TEGDMA dental composite resins. Biomaterials 1999, 20, 1897–1908. [Google Scholar] [CrossRef]
  43. Santerre, J.P.; Shajii, L.; Leung, B.W. Relation of Dental Composite Formulations to Their Degradation and the Release of Hydrolyzed Polymeric-Resin-Derived Products. Crit. Rev. Oral Biol. Med. 2001, 12, 136–151. [Google Scholar] [CrossRef] [Green Version]
  44. Šimková, M.; Tichý, A.; Dušková, M.; Bradna, P. Dental Composites–A Low-Dose Source of Bisphenol A? Physiol. Res. 2020, 69, S295–S304. [Google Scholar] [CrossRef] [PubMed]
  45. Paula, A.B.; Toste, D.; Marinho, A.; Amaro, I.; Marto, C.-M.; Coelho, A.; Marques-Ferreira, M.; Carrilho, E. Once Resin Composites and Dental Sealants Release Bisphenol-A, How Might This Affect Our Clinical Management?-A Systematic Review. Int. J. Environ. Res. Public Heal 2019, 16, 1627. [Google Scholar] [CrossRef] [Green Version]
  46. Michelsen, V.B.; Kopperud, H.B.M.; Lygre, G.B.; Björkman, L.; Jensen, E.; Kleven, I.S.; Svahn, J.; Lygre, H. Detection and quantification of monomers in unstimulated whole saliva after treatment with resin-based composite fillings in vivo. Eur. J. Oral Sci. 2012, 120, 89–95. [Google Scholar] [CrossRef]
  47. Gallorini, M.; Petzel, C.; Bolay, C.; Hiller, K.-A.; Cataldi, A.; Buchalla, W.; Krifka, S.; Schweikl, H. Activation of the Nrf2-regulated antioxidant cell response inhibits HEMA-induced oxidative stress and supports cell viability. Biomaterials 2015, 56, 114–128. [Google Scholar] [CrossRef] [PubMed]
  48. Krifka, S.; Spagnuolo, G.; Schmalz, G.; Schweikl, H. A review of adaptive mechanisms in cell responses towards oxidative stress caused by dental resin monomers. Biomaterials 2013, 34, 4555–4563. [Google Scholar] [CrossRef]
  49. Ivashkevich, A.N.; Martin, O.A.; Smith, A.J.; Redon, C.E.; Bonner, W.M.; Martin, R.F.; Lobachevsky, P.N. γH2AX foci as a measure of DNA damage: A computational approach to automatic analysis. Mutat. Res. Mol. Mech. Mutagen. 2011, 711, 49–60. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  50. Krifka, S.; Seidenader, C.; Hiller, K.-A.; Schmalz, G.; Schweikl, H. Oxidative stress and cytotoxicity generated by dental composites in human pulp cells. Clin. Oral Investig. 2011, 16, 215–224. [Google Scholar] [CrossRef]
  51. Blasiak, J.; Synowiec, E.; Tarnawska, J.; Czarny, P.; Poplawski, T.; Reiter, R.J. Dental methacrylates may exert genotoxic effects via the oxidative induction of DNA double strand breaks and the inhibition of their repair. Mol. Biol. Rep. 2012, 39, 7487–7496. [Google Scholar] [CrossRef] [PubMed] [Green Version]
Materials 14 05225 g001 550
Figure 1. Experimental Plan. Soaking-derived extracts were obtained following the immersion of each type of CR disks of 50.27 mm2 surface in the culture medium (CTRL) for 24 h and 14 days (i.e., 2 CR disks in 1 mL of CTRL). The hGDFs isolated from human gingival biopsies were treated for 48 h with the culture medium (CTRL) or with the soaking extracts (24 h and 14 days) derived from the five selected CRs. Cell viability, ROS production, and genotoxicity were chosen as cellular outcomes.
Figure 1. Experimental Plan. Soaking-derived extracts were obtained following the immersion of each type of CR disks of 50.27 mm2 surface in the culture medium (CTRL) for 24 h and 14 days (i.e., 2 CR disks in 1 mL of CTRL). The hGDFs isolated from human gingival biopsies were treated for 48 h with the culture medium (CTRL) or with the soaking extracts (24 h and 14 days) derived from the five selected CRs. Cell viability, ROS production, and genotoxicity were chosen as cellular outcomes.
Materials 14 05225 g001
Materials 14 05225 g002 550
Figure 2. LC–MS/MS quantification. Levels of (a) TEGDMA and (b) Bis-GMA quantified in culture media following 24 h (in grey) and 14 days (in black) of CR disk immersion. Results are shown as mean ± standard error (SEM) (n = 3) (* p < 0.05 vs. 24 h).
Figure 2. LC–MS/MS quantification. Levels of (a) TEGDMA and (b) Bis-GMA quantified in culture media following 24 h (in grey) and 14 days (in black) of CR disk immersion. Results are shown as mean ± standard error (SEM) (n = 3) (* p < 0.05 vs. 24 h).
Materials 14 05225 g002
Materials 14 05225 g003 550
Figure 3. Characterization of hGDFs. (a) Representative phase contrast image of isolated hOBs. (b) Representative histograms of the CD105, CD73, CD90, CD45, and CD326 expressions evaluated through cytometric analysis.
Figure 3. Characterization of hGDFs. (a) Representative phase contrast image of isolated hOBs. (b) Representative histograms of the CD105, CD73, CD90, CD45, and CD326 expressions evaluated through cytometric analysis.
Materials 14 05225 g003
Materials 14 05225 g004 550
Figure 4. Cells metabolic activity. Effect of CRs on hGDF cell metabolic activity following 48 h of treatment with the (a) 24-h and (b) 14-day CR-derived extracts, undiluted (100%) or not (50% and 25%). Results are shown as mean ± standard error (SEM) (n ≥ 3) of the percentage (%) of metabolically active cells. (* p < 0.05 vs. CTRL).
Figure 4. Cells metabolic activity. Effect of CRs on hGDF cell metabolic activity following 48 h of treatment with the (a) 24-h and (b) 14-day CR-derived extracts, undiluted (100%) or not (50% and 25%). Results are shown as mean ± standard error (SEM) (n ≥ 3) of the percentage (%) of metabolically active cells. (* p < 0.05 vs. CTRL).
Materials 14 05225 g004
Materials 14 05225 g005 550
Figure 5. ROS levels. Cytometric analysis of ROS levels in hGDFs following 48 h of treatment with the (a) 24-h and (b) 14-day CR-derived extracts, undiluted (100%) or not (50% and 25%). Results, expressed as mean ± standard error (SEM) (n ≥ 3), are shown as the MFI ratio (fold increase) of ROS levels. (* p < 0.05 vs. CTRL). The red crosses indicate values not quantifiable (n.q.) in VD and UE groups due to the high level of cell mortality.
Figure 5. ROS levels. Cytometric analysis of ROS levels in hGDFs following 48 h of treatment with the (a) 24-h and (b) 14-day CR-derived extracts, undiluted (100%) or not (50% and 25%). Results, expressed as mean ± standard error (SEM) (n ≥ 3), are shown as the MFI ratio (fold increase) of ROS levels. (* p < 0.05 vs. CTRL). The red crosses indicate values not quantifiable (n.q.) in VD and UE groups due to the high level of cell mortality.
Materials 14 05225 g005
Materials 14 05225 g006 550
Figure 6. DNA damage. Graphs and representative fluorescence images show the expression of γH2AX in hGDFs (stained with anti-γH2AX, DAPI, and merged; 40x) following 48 h of treatment with the (a) 24-h and (b) 14-day CR-derived extracts, undiluted (100%). Results are expressed as mean ± standard error (SEM) (n ≥ 3). Data, calculated as percentage (%) of positive cells for γH2AX, were obtained by analyzing at least three different fields for each image with ImageJ software (NIH, USA). (* p < 0.05 vs. CTRL; # p < 0.05 vs. DOXO).
Figure 6. DNA damage. Graphs and representative fluorescence images show the expression of γH2AX in hGDFs (stained with anti-γH2AX, DAPI, and merged; 40x) following 48 h of treatment with the (a) 24-h and (b) 14-day CR-derived extracts, undiluted (100%). Results are expressed as mean ± standard error (SEM) (n ≥ 3). Data, calculated as percentage (%) of positive cells for γH2AX, were obtained by analyzing at least three different fields for each image with ImageJ software (NIH, USA). (* p < 0.05 vs. CTRL; # p < 0.05 vs. DOXO).
Materials 14 05225 g006
Table
Table 1. List and characteristics of the CRs included in the experimental design.
Table 1. List and characteristics of the CRs included in the experimental design.
GroupNameShadeManufacturerBatchCompositionCategory
BF-2Enamel BioFunctionBF2Micerium S.p.A.201900814974% wt fillers (5–50 nm silicon dioxide; 0,2–3 μm glass fillers)Nanohybrid
(Avegno, Italy)UDMA, Tricyclodecane dimethanol dimethacrylate
VOCOGrandioSOA2Voco GmbH184731389 % wt fillers (1 μm glass ceramic fillers; 20–40 nm silicon dioxide fillers)Nanohybrid
(Cuxhaven, Germany)Bis-GMA, Bis-EMA, TEGDMA
VDVenus Diamond A2Kulzer GmbHK01007080–82% wt fillers (5 nm–20 μm barium aluminum fluoride glass fillers)Nanohybrid
(Hanau, Germany)TCD-Urethaneacrylate, UDMA, TEGDMA
UEEnamel-plus HRi Micerium S.p.A. 80% fillers wt (0.1 µm glass fillers, 20 nm zirconium nanoxides)Nanohybrid
(Avegno, GE, Italy)UDMA, Bis-GMA, 1,4 Butanediol dimethacrylat (BDDMA)
ES-2Clearfil Majesty ES-2 ClassicA2Kuraray7D00878% fillers wt (0.37 μm–1.5 μm silanated barium glass fillers, pre-polymerized organic fillers)Nanohybrid
(Chiyoda, Tokyo, Japan) Bis-GMA, Hydrophobic aromatic dimethacrylate
UDMA (urethane dimethacrylate); Bis-GMA (bisphenol-A-glycidyl-methacrylate); Bis-EMA (bisphenol-A-diglycidyl-methacrylate ethoxylated); TEGDMA (triethylene glycol dimethacrylate).
Table
Table 2. MRM transition, cone potential, and collision energy for each analyte.
Table 2. MRM transition, cone potential, and collision energy for each analyte.
AnalyteParent (m/z)Daughter (m/z)Cone (V)Collision Energy (eV)
TEGDMA287.2113.1508
Bis-GMA513.2143.15015
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

De Angelis, F.; Mandatori, D.; Schiavone, V.; Melito, F.P.; Valentinuzzi, S.; Vadini, M.; Di Tomo, P.; Vanini, L.; Pelusi, L.; Pipino, C.; et al. Cytotoxic and Genotoxic Effects of Composite Resins on Cultured Human Gingival Fibroblasts. Materials 2021, 14, 5225. https://doi.org/10.3390/ma14185225

AMA Style

De Angelis F, Mandatori D, Schiavone V, Melito FP, Valentinuzzi S, Vadini M, Di Tomo P, Vanini L, Pelusi L, Pipino C, et al. Cytotoxic and Genotoxic Effects of Composite Resins on Cultured Human Gingival Fibroblasts. Materials. 2021; 14(18):5225. https://doi.org/10.3390/ma14185225

Chicago/Turabian Style

De Angelis, Francesco, Domitilla Mandatori, Valeria Schiavone, Francesco Paolo Melito, Silvia Valentinuzzi, Mirco Vadini, Pamela Di Tomo, Lorenzo Vanini, Letizia Pelusi, Caterina Pipino, and et al. 2021. "Cytotoxic and Genotoxic Effects of Composite Resins on Cultured Human Gingival Fibroblasts" Materials 14, no. 18: 5225. https://doi.org/10.3390/ma14185225

APA Style

De Angelis, F., Mandatori, D., Schiavone, V., Melito, F. P., Valentinuzzi, S., Vadini, M., Di Tomo, P., Vanini, L., Pelusi, L., Pipino, C., Del Boccio, P., D’Arcangelo, C., & Pandolfi, A. (2021). Cytotoxic and Genotoxic Effects of Composite Resins on Cultured Human Gingival Fibroblasts. Materials, 14(18), 5225. https://doi.org/10.3390/ma14185225

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop