Energy Absorption and Stiffness of Thin and Thick-Walled Closed-Cell 3D-Printed Structures Fabricated from a Hyperelastic Soft Polymer
Previous Article in Journal
Clinical and Radiographic Outcomes of Zirconia Dental Implants—A Clinical Case Series Study
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 15
Issue 7
10.3390/ma15072440
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Microstructure and Mechanical Properties of TiB2/AlSi7Mg0.6 Composites Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT)

by
Qingfeng Yang
1,
Cunjuan Xia
2,*,
Haowei Wang
2,
Mingyang Zhou
1,
Shixin Gao
1,
Bingjin Li
1 and
Shichao Liu
1
1
Science and Technology on Reactor System Design Technology Laboratory, Nuclear Power Institute of China, Chengdu 610213, China
2
The State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 200240, China
*
Author to whom correspondence should be addressed.
Materials 2022, 15(7), 2440; https://doi.org/10.3390/ma15072440
Submission received: 2 March 2022 / Revised: 17 March 2022 / Accepted: 22 March 2022 / Published: 25 March 2022
(This article belongs to the Topic Advanced Forming Technology of Metallic Materials)
Browse Figures
Versions Notes

Abstract

:
Wire and arc additive manufacturing based on cold metal transfer (WAAM-CMT), as a kind of clean and advanced technology, has been widely researched recently. It was analyzed in detail for the microstructure and mechanical properties of WAAM-CMT printed TiB2/AlSi7Mg0.6 samples fore-and-aft heat treatment in this study. Compared with the grain size of casted AlSi7Mg0.6 samples (252 μm), the grain size of WAAM-CMT printed AlSi7Mg0.6 samples (53.4 μm) was refined, showing that WAAM-CMT process could result in significant grain refinement. Besides, the grain size of WAAM-CMT printed TiB2/AlSi7Mg0.6 samples was about 35 μm, revealing that the addition of TiB2 particles played a role in grain refinement. Nevertheless, the grain size distribution was not uniform, showing a mixture of fine grain and coarse grain, and the mechanical properties were anisotropic of the as-printed samples. This study shows that T6 heat treatment is an efficient way to improve the nonuniform microstructure and eliminate the anisotropy in mechanical properties.

1. Introduction

Aluminium alloys, with high strength, low density, and good corrosion resistance, have been widely used in many industries [1,2,3]. Additive manufacturing (AM), as a kind of clean and advanced technology, has been popular recently, which fabricates the samples layer-by-layer according to 3D models. This technology could avoid material waste and reduce technological processes, which enable the formation of any complex components theoretically [4,5,6,7]. Additive manufacturing could be classified as laser additive manufacturing [8], electron beam additive manufacturing [9], and arc additive manufacturing according to the heat source [10]. Wire and arc additive manufacturing based on cold metal transfer (WAAM-CMT) technology is very appropriate for the formation of aluminium alloys because of its merits of low heat input and high process speed [11,12,13,14].
The forming characteristics of WAAM and the microstructure and properties of the printed parts have become a hot topic in the field of additive manufacturing. Blanka et al. [15] studied the microstructure and residual stress in Ti-6Al-4V AM components produced by Wire + Arc Additive Manufacturing (WAAM) and by laser cladding process (CLAD). Su et al. [16] studied the microstructure and properties of Al-Mg alloys fabricated by WAAM under different heat inputs, finding grain size varying in the range of 42.9–88.7 μm in the inner-layer region and 37.7–77.6 μm in the inter-layer region. Patel et al. [17] focused on the effects of different forming process parameters and heat-treatment regimens on the microstructure and properties of formed parts, holding a view that it was necessary for the printed parts to process heat treatment in order to meet the requirements. Jiang et al. [18] researched the effect of process parameters, such as current, scanning speed, and so on, on the forming quality of WAAM-CMT printed 5356 aluminum alloy, finding there was a difference in tensile strength in different directions. Bai et al. [19] studied the microstructure of 4043 aluminum alloy printed by WAAM, which consisted of texture and elements segregation. Moreover, Huang et al. [20] and Sun et al. [21] both found similar phenomena in printed 5A06 aluminum alloy and Al-6.3Cu aluminum alloy respectively. From the studies mentioned above, it might be a common phenomenon that there were anisotropy and non-uniform microstructure in printed samples, which was detrimental to the comprehensive performance of samples [15,22,23]. It is a key research point to enhance the microstructure and mechanical properties of printed samples. Besides, there is little research on parts fabricated with wire and arc additive manufacturing by feeding composite wire [24,25,26].
In this study, the microstructure and mechanical properties of TiB2/AlSi7Mg0.6 composites printed by WAAM-CMT technology were found. In addition, the effect of heat treatment on WAAM-CMT printed TiB2/AlSi7Mg0.6 composites was analyzed and the mechanisms of improving microstructure and mechanical properties were discussed correspondingly.

2. Materials and Methods

In this study, the in-situ authigenic TiB2/AlSi7Mg0.6 ingot was prepared first through the mixed-salt method, then the ingot was transformed into wire used in WAAM by a series of processing techniques, such as extrusion, drawing, and so on. The WAAM-CMT equipment (NanJing Enigma Automation CO., LTD, Nanjing, China) mainly consists of a welding robot, wire feeder system, cooling system, robot control system, and workbench, as shown in Figure 1, where Φ 1.6mm TiB2/AlSi7Mg0.6 composite wire and 4043 aluminum alloy as the substrate were used. During the whole additive manufacturing process, pure argon gas, as protective gas, was used to avoid the oxidation of materials.
During the process of WAAM-CMT, welding voltage, welding current, wire feed speed, and travel speed was 15.1V, 145A, 7.3 m/min, and 12 mm/s respectively. The WAAM-CMT printed TiB2/AlSi7Mg0.6 sample is shown in Figure 2a. The X direction was defined as along the travel direction, the Y direction was defined as perpendicular to the travel direction, and the Z direction was defined as along the height direction (Figure 2b). Additionally, the WAAM-CMT printed TiB2/AlSi7Mg0.6 sample was processed by T6 heat treatment (solid solution 535 ◦C/1h + quenching + artificial aging 120 ◦C/1h + 165 ◦C/8h).
In order to analyze the homogeneity of chemical composition, specimens were extracted from different locations, using ICAP6300 inductively coupled plasma optical, and the result is shown in Table 1.
Furthermore, optical microscopy (OM) (Carl Zeiss (Shanghai) Management Co., Ltd, Shanghai, China.) and scanning electron microscope (SEM) (TESCAN China, Shanghai, China) were selected to study the microstructure of the specimens. For elements analysis and statistical analysis of grain size, energy disperse spectroscopy (EDS) (TESCAN China, Shanghai, China) and electron backscattered diffraction (EBSD) (TESCAN China, Shanghai, China) equipment were used respectively. In addition, tensile tests at ambient temperature were performed with the strain rate 1 × 10−4 s−1.

3. Results and Discussion

3.1. Microstructure Evolution

The microstructures of the as-deposited TiB2/AlSi7Mg0.6 composites in face XOY and face XOZ, composed of fine grain and coarse grain, were similar (Figure 3). Besides, it seemed that the size of dendrites in face XOZ was larger than that in face XOY. Additionally, dendritic α-Al phase and strip-like Si phase occurred in the metallographic morphology of the WAAM-CMT-printed TiB2/AlSi7Mg0.6 sample in two faces.
The appearance of fine grain and coarse grain was connected with the WAAM-CMT process. During the formation process, dendritic crystals grew along the direction of the temperature gradient, which was along the height direction. In addition, the cooling rate at the bottom of the molten pool was very high, forming fine crystals. There were larger dendrites in the middle of the molten pool because of a higher temperature than that at the bottom. While, fine dendrites existed at the top of the molten pool on account of high heat dissipation. Furthermore, when forming at the upper layer, solidified materials at the lower layer would melt again, resulting in the growth of crystals in this region [27,28,29].
Figure 3a shows that there were pores with different sizes along the division of the fine grain zone and coarse grain zone, the larger diameter of which was up to about 40 µm. Some scholars hold a view that it is easier for pores to form at the solidification interface of dendrites because of the irregular shape of the solid-liquid interface, reducing the nucleation work of pores formation [30,31]. Shivkumar et al. [32] proposed that pores formed based on the dendrite arm and the shorter the distance between secondary branches was, the smaller the nucleation radius of pores was. The above was the reason why there were pores along the division of fine grain zone and coarse grain zone. The pore morphology of the WAAM-CMT formed samples was observed, as shown in Figure 4.
It could be seen that there were mainly Si particles and a small amount of segregated TiB2 particles on the inner wall of the pores. Moreover, the distribution of Si on the inner wall of the pores was obviously denser than that on the Al matrix.
For farther analysis of the microstructure of printed TiB2/AlSi7Mg0.6 composites in two faces (Figure 5), it could be seen that most parts of Si particles were distributed along the α-Al grain boundary and some TiB2 particles segregated at the grain boundary. The size of Si particles was about 3 to 6 µm. Furthermore, there was elements segregation at the grain boundary in printed TiB2/AlSi7Mg0.6 samples, which was a result of the high cooling velocity of the WAAM-CMT printing process. When the cooling velocity of molten pool was high, there would be less time for elements to diffuse sufficiently, finally causing the elements segregation [22,29].
After T6 heat treatment, the division between the coarse grain zone and fine grain zone seemed to disappear. Furthermore, it was evident that the elements distribution in Figure 6 was more uniform than that in Figure 5, because the elements had enough time and energy to diffuse during the process of T6 heat treatment. In addition, the shape of Si particles was changed to block from stripe, with a size of about 2–6 µm, which was also related to the element diffusion. In the microstructure of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites, the silicon atoms at the sharp corners had higher energies, which would migrate to the location with lower energies during the process of heat treatment, leading to the shape change of Si particles [33,34].
According to the average grain size and grain size distribution of the printed composites in face XOY and face XOZ (Figure 7a,b), it could be seen that those were a little different in two faces and the average grain size in face XOZ was larger than that in face XOY. After T6 heat treatment, the average grain size in XOY and XOZ had an evident increase of 78.57% and 49.43% respectively. The growth of grain size after heat treatment was because of the decrease of total free energy of the whole system. During the process of grain growth, grains with small size, less than a certain critical value, disappeared gradually, while the grains with large size grew further [35].
Besides, the average grain size of casted AlSi7Mg0.6 alloys was much larger than that of printed AlSi7Mg0.6 alloys, despite that of printed TiB2/AlSi7Mg0.6 composites, which indicated that WAAM-CMT printing process and the addition of TiB2 particles both played roles of refining grain. As the mass of the addition of TiB2 particles in composites was small, only about 0.5 wt%, the effect was limited for TiB2 particles to inhibit grain growth after T6 heat treatment.
The reason for grain refinement is explained as follows. Firstly, TiB2 particles was favorable to the increase of nucleation rate as there was a co-lattice relationship between TiB2 lattice and α-Al lattice [28]. Secondly, the cooling rate of the WAAM-CMT printing process, about 245 K/s, was much higher than that of the casting process [36]. The higher the cooling rate was, the higher the nucleation rate was, leading to eventual grain refinement. Finally, arc stir in the molten pool also exerted a positive effect on grain refinement. Even some scholars held a view that the arc stir effect of the CMT mode was most notable among other arc modes [37,38].

3.2. Mechanical Properties Analysis

For the purpose of researching the mechanical properties of TiB2/AlSi7Mg0.6 composites in different directions, samples were extracted from X and Z directions (Figure 2).
Tensile test results (Figure 8 and Table 2) showed that the yield strength (Rp0.2) and ultimate tensile strength (Rm) in the X direction were obvious higher than those in the Z direction, because the average grain size in face XOZ of printed composites was larger than that in face XOY. That was to say, there was anisotropy in mechanical properties of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites, which was related to the difference in microstructure in different directions. During the tensile test, dislocations would move along the force direction in general, and the movement of dislocations would be hindered because of the existence of grain boundary. The finer the grain size was, the higher the strength of sample was [35].
After T6 heat treatment, the value of yield strength, ultimate tensile strength, and elongation (A) in two directions were the same on the whole, indicating that T6 heat treatment was an effective method to eliminate the anisotropy of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites. Besides, the value of yield strength and ultimate tensile strength in two directions both clearly increased after heat treatment, while there was a decrease of elongation in two directions.
In general, the yield strength of samples would decrease if the grain sizes of samples increased [39]. However, even though the grain sizes of printed composites increased after heat treatment, there was an increase of yield strength, indicating that precipitation strengthening and the solid solution of Si particles led to the increase of yield strength. For one thing, the following was the general precipitation sequence in Al-Si-Mg alloy after heat treatment, super-saturated solid solution → GP zones → β” → β’ → β, among which the β” phase, as generally assumed, played the most important role in precipitate strengthening [40]. For another, TiB2 particles with micro or nano size could have a similar effect of precipitate strengthening. Besides, parts of Si particles, with high elasticity modulus, would dissolve in the α-Al matrix, increasing the yield strength as well [41]. It is proved that appropriate heat treatment is beneficial to improve the comprehensive mechanical properties of the parts made by WAAM-CMT.
SEM graphs of the fracture of the samples are shown in Figure 9a–d. It can be seen that there were dimples in the fracture morphologies of the as-deposited and T6 heat-treated samples. The dimples suggest that most of the failure is because of ductile fracture.

4. Conclusions

The microstructure and mechanical properties of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites were analyzed systematically, obtaining the following conclusions.
  • There were fine grain and coarse grain zones in the microstructure of printed TiB2/AlSi7Mg0.6 composites, and it seemed that T6 heat treatment had an advantage of eliminating the division between fine grain and coarse grain zones.
  • The grain size of the printed AlSi7Mg0.6 alloy was much smaller than that of the casted AlSi7Mg0.6 alloy as the result of the high cooling rate of WAAM-CMT printing process. The grain size of printed TiB2/AlSi7Mg0.6 samples was smaller than that of the printed AlSi7Mg0.6 alloy, indicating that TiB2 particles also played a role in refining grain.
  • After T6 heat treatment, there was an obvious increase of yield strength and ultimate tensile strength of the composites in X and Z directions, mainly on account of the precipitation strengthening and solid solution of Si particles.

Author Contributions

Design, C.X. and H.W.; investigation, M.Z. and B.L.; writing—original draft preparation, Q.Y.; writing—review and editing, S.G.; funding support, S.L. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the National Natural Science Foundation of China (Grant No.12005213).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

Many thanks for the technical support supplied by Nanjing Enigma automation Co., LTD.

Conflicts of Interest

The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.

References

  1. Sankar, V.; Muthu, S. Investigation of microstructure and mechanical behavior of AlSi7Mg. J. Appl. Sci. 2014, 14, 811–816. [Google Scholar] [CrossRef] [Green Version]
  2. Kuchariková, L.; Tillová, E.; Chalupová, M.; Hanusová, P. Investigation on microstructural and hardness evaluation in heat-treated and as-cast state of secondary alsimg cast alloys. Mater. Today Proc. 2020, 32, 63–67. [Google Scholar] [CrossRef]
  3. Tonelli, L.; Liverani, E.; Morri, A.; Ceschini, L. Role of direct aging and solution treatment on hardness, microstructure and residual stress of the A357 (AlSi7Mg0.6) alloy produced by powder bed fusion. Met. Mater. Trans. B 2021, 52, 2484–2496. [Google Scholar] [CrossRef]
  4. Zhang, J.L.; Song, B.; Wei, Q.S.; Bourell, D.; Shi, Y.S. A review of selective laser melting of aluminum alloys: Processing, microstructure, property and developing trends. J. Mater. Sci. Technol. 2019, 35, 270–284. [Google Scholar] [CrossRef]
  5. Herzog, D.; Seyda, V.; Wycisk, E.; Emmelmann, C. Additive manufacturing of metals. Acta Mater. 2016, 117, 371–392. [Google Scholar] [CrossRef]
  6. Chen, H.; Zhang, C.; Jia, D.; Wellmann, D.; Liu, W. Corrosion behaviors of selective laser melted aluminum alloys: A review. Metals 2020, 10, 102. [Google Scholar] [CrossRef] [Green Version]
  7. Wang, H.J.; Jiang, W.H.; Ouyang, J.H.; Kovacevic, R. Rapid prototyping of 4043 Al-alloy parts by VP-GTAW. J. Mater. Process. Technol. 2004, 148, 93–102. [Google Scholar] [CrossRef]
  8. Uzan, N.E.; Roni, S.; Ori, Y.; Nachum, F. Fatigue of AlSi10Mg specimens fabricated by additive manufacturing selective laser melting (AM-SLM). Mater. Sci. Eng. A 2017, 704, 229–237. [Google Scholar] [CrossRef]
  9. Yang, Y.; Suo, H.B.; Chen, Z.Y.; Wang, L. Effect of solution temperature on microstructure and mechanical properties of TC17 alloy fabricated by electron beam wire deposition. Heat Treat. Met. 2016, 41, 141–144. [Google Scholar]
  10. Cong, B.; Ding, J.; Williams, S.W. Effect of arc mode in cold metal transfer process on porosity of additively manufactured Al-6.3% Cu alloy. Int. J. Adv. Manuf. Technol. 2014, 76, 1593–1606. [Google Scholar] [CrossRef]
  11. Ding, J.; Colegrove, P.; Mehnen, J.; Ganguly, S.; Sequeira Almeida, P.M.; Wang, F.; Williams, S. Thermo-mechanical analysis of wire and arc additive layer manufacturing process on large multi-layer parts. Comp. Mater. Sci. 2011, 50, 3315–3322. [Google Scholar] [CrossRef] [Green Version]
  12. Wang, F.; Williams, S.; Colegrove, P.; Antonysamy, A. Microstructure and mechanical properties of wire and arc additive manufactured Ti-6Al-4V. Metall. Mater. Trans. A 2013, 44, 968–977. [Google Scholar] [CrossRef]
  13. Feng, J.C.; Zhang, H.T.; He, P. The CMT short-circuiting metal transfer process and its use in thin aluminium sheets welding. Mater. Des. 2009, 30, 1850–1852. [Google Scholar] [CrossRef]
  14. Cao, R.; Wen, B.F.; Chen, J.H.; Wang, P.C. Cold Metal Transfer joining of magnesium AZ31B-to-aluminum A6061-T6. Mater. Sci. Eng. A 2012, 560, 256–266. [Google Scholar] [CrossRef]
  15. Blanka, A.S.; Sofiane, T.; Filomeno, M.; Didier, B.; Anastasiia, P.; Thilo, P.; Michael, H.; David, J.J. A comparative study of additive manufacturing techniques: Residual stress and microstructural analysis of CLAD and WAAM printed Ti-6Al-4V components. Mater. Des. 2016, 89, 559–567. [Google Scholar]
  16. Su, C.; Chen, X.; Gao, C.; Wang, Y. Effect of heat input on microstructure and mechanical properties of Al-Mg alloys fabricated by WAAM. Appl. Surf. Sci. 2019, 486, 431–440. [Google Scholar] [CrossRef]
  17. Patel, M.; Mulgaonkar, S.; Desai, H.; Borse, T. Development and implementation of wire arc additive manufacturing (WAAM) based on pulse spray GMAW for aluminum alloy (AlSi7Mg). Trans. Indian Inst. Met. 2021, 7, 1129–1140. [Google Scholar] [CrossRef]
  18. Jiang, Y.L. Research on the Rapid Prototyping Technology and Forming Process of Aluminum Alloy Based on the CMT; Harbin Institute of Technology: Harbin, China, 2013. [Google Scholar]
  19. Bai, J.Y.; Wang, J.H.; Shi, J.X.; Lin, S.B.; Yang, C.L.; Fan, C.L. Microstructure and mechanical properties of 4043 Al alloy thin-walled components produced by additive manufacturing with TIG welding. Weld. Join. 2015, 706, 23–26. [Google Scholar]
  20. Huang, D.; Zhu, Z.H.; Geng, H.B. TIG wire and arc additive manufacturing of 5A06 aluminum alloy. J. Mater. Eng. 2017, 45, 66–72. [Google Scholar]
  21. Sun, H.Y.; Cong, B.Q.; Su, Y. Geometry, microstructure and properties of wire+ arc additive manufacturing Al-6.3Cu alloy deposits. Aeronaut. Manuf. Technol. 2016, 480, 36–42. [Google Scholar]
  22. Chlebus, E.; Gruber, K.; Kuz’nicka, B.; Kurzac, J.; Kurzynowski, T. Effect of heat treatment on the microstructure and mechanical properties of Inconel 718 processed by selective laser melting. Mater. Sci. Eng. A 2015, 639, 647–655. [Google Scholar] [CrossRef]
  23. Zhang, P.; Liu, D.B.; Bai, J.Y.; Lin, S.B.; Liu, N. Microstructure characteristics of thin-walled TC4 titanium alloy fabricated by arc additive manufacturing. Weld. Join. 2015, 706, 53–56. [Google Scholar]
  24. Campatelli, G.; Campanella, D.; Barcellona, A.; Fratini, L.; Ingarao, G. Microstructural, mechanical and energy demand characterization of alternative WAAM techniques for Al-alloy parts production. CIRP J. Manuf. Sci. Technol. 2020, 31, 492–499. [Google Scholar] [CrossRef]
  25. Gussev, M.N.; Sridharan, N.; Norfolk, M.; Terrani, K.A.; Babu, S.S. Effect of post weld heat treatment on the 6061 aluminum alloy produced by ultrasonic additive manufacturing. Mater. Sci. Eng. A 2017, 684, 606–616. [Google Scholar] [CrossRef] [Green Version]
  26. Cong, B.Q.; Qi, Z.W.; Qi, B.J.; Sun, H.Y.; Zhao, G.; Ding, J.L. A comparative study of additively manufactured thin wall and block structure with al-6.3%cu alloy using cold metal transfer process. Appl. Sci. 2017, 7, 275. [Google Scholar] [CrossRef]
  27. Lian, Q.; Wu, Y.; Wang, H.W.; Ma, N.H. Study on manufacturing processes and properties of TiB2 reinforced Al-Si composite by laser additive manufacturing. Hot Work. Technol. 2017, 46, 113–117. [Google Scholar]
  28. Uzan, N.E.; Ramati, S.; Shneck, R.; Yeheskel, O.; Frage, N. Microstructure and mechanical properties of AlSi10Mg components, fabricated by additive manufacturing-selective laser melting (AM-SLM). In Proceedings of the Technological Innovations in Metals Engineering (TIME 2018), Haifa, Israel, 30–31 May 2018. [Google Scholar]
  29. Wei, L.; Shuai, L.; Jie, L.; Zhang, A.; Yan, Z.; Wei, Q.; Yan, C.; Shi, Y. Effect of heat treatment on AlSi10mg alloy fabricated by selective laser melting: Microstructure evolution, mechanical properties and fracture mechanism. Mater. Sci. Eng. A 2016, 663, 116–125. [Google Scholar]
  30. Kubo, K.; PehlkeR, D. Porosity formation in solidifying castings. AFS Trans. 1986, 94, 753–756. [Google Scholar]
  31. Chen, X.G.; Engler, S. Formation of gas porosity in aluminium alloys. AFS Trans. 1994, 102, 673–682. [Google Scholar]
  32. Shivkumar, S.; Apelian, D.; Zou, J. Modeling of microstructure evolution and microporosity formation in cast aluminum alloys. AFS Trans. 1990, 98, 897–904. [Google Scholar]
  33. Wang, G.L. Study on the Treatment and Mechanical Behavior of Cast Al-11.9Si-3.5Cu-1.7Ni-0.8Mg Alloy. Master’s Thesis, Shanghai Jiaotong University, Shanghai, China, 2015. [Google Scholar]
  34. Zhu, M.; Jian, Z.Y.; Yang, G.C.; Zhou, Y.H. Effects of T6 heat treatment on the microstructure, tensile properties, and fracture behavior of the modified A356 alloys. Mater. Des. 2012, 36, 243–249. [Google Scholar] [CrossRef]
  35. Liu, Z.E. Material Science, 2nd ed.; Northwestern Polytechnical University Press: Xi’an, China, 2003; p. 213. [Google Scholar]
  36. Yang, Q.F.; Xia, C.J.; Deng, Y.Q.; Li, X.F.; Wang, H.W. Microstructure and Mechanical Properties of AlSi7Mg0.6 Aluminum Alloy Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT). Materials 2019, 8, 2525. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  37. Wang, F.; Williams, S.; Rush, M. Morphology investigation on direct current pulsed gas tungsten arc welded additive layer manufactured Ti6Al4V alloy. Int. J. Adv. Manuf. Technol. 2011, 57, 597–603. [Google Scholar] [CrossRef] [Green Version]
  38. Li, G.; Zhang, C.; Gao, M.; Zeng, X. Role of arc mode in laser-metal active gas arc hybrid welding of mild steel. Mater. Des. 2014, 61, 239–250. [Google Scholar] [CrossRef]
  39. Gallais, C.; Denquin, A.; Pic, A.; Simar, A.; Pardoen, T.; Brechet, Y. Modelling the relationship between process parameters, microstructural evolutions and mechanical behaviour in a friction stir weld 6xxx aluminium alloy. In Proceedings of the 5th International FSW Symposium, Metz, France, 14–16 September 2004; pp. 248–260. [Google Scholar]
  40. Ninive, P.H.; Strandlie, A.; Gulbrandsen-Dahl, S.; Lefebvre, W.; Marioara, C.D.; Andersen, S.J.; Friis, J.; Holmestad, R.; Løvvik, O.M. Detailed atomistic insight into the β″ phase in Al-Mg-Si alloys. Acta Mater. 2014, 69, 126–134. [Google Scholar] [CrossRef] [Green Version]
  41. Yang, Y. Study on the Evolution and Collaborative Strengthening Mechanism of Heat-Resistant Phases in Multicomponent Al-Si Alloys. Ph.D. Thesis, Shandong University, Jinan, China, 2013. [Google Scholar]
Materials 15 02440 g001 550
Figure 1. The schematic diagram of WAAM-CMT equipment.
Figure 1. The schematic diagram of WAAM-CMT equipment.
Materials 15 02440 g001
Materials 15 02440 g002 550
Figure 2. (a) WAAM-CMT printed TiB2/AlSi7Mg0.6 sample; (b) extraction locations of specimens and definition of X, Y, and Z directions.
Figure 2. (a) WAAM-CMT printed TiB2/AlSi7Mg0.6 sample; (b) extraction locations of specimens and definition of X, Y, and Z directions.
Materials 15 02440 g002
Materials 15 02440 g003 550
Figure 3. Metallographic morphology of the WAAM-CMT-printed TiB2/AlSi7Mg0.6 sample in face XOY and XOZ: (a) face XOY; (b) coarse grain zone in (a); (c) fine grain zone in (a); (d) face XOZ; (e) coarse grain zone in (d); (f) fine grain zone in (d).
Figure 3. Metallographic morphology of the WAAM-CMT-printed TiB2/AlSi7Mg0.6 sample in face XOY and XOZ: (a) face XOY; (b) coarse grain zone in (a); (c) fine grain zone in (a); (d) face XOZ; (e) coarse grain zone in (d); (f) fine grain zone in (d).
Materials 15 02440 g003
Materials 15 02440 g004 550
Figure 4. Stomata morphology of the WAAM-CMT-printed TiB2/AlSi7Mg0.6 sample in face XOY and XOZ: (a) face XOY; (b) face XOZ.
Figure 4. Stomata morphology of the WAAM-CMT-printed TiB2/AlSi7Mg0.6 sample in face XOY and XOZ: (a) face XOY; (b) face XOZ.
Materials 15 02440 g004
Materials 15 02440 g005 550
Figure 5. Microstructure of the WAAM-CMT-printed TiB2/AlSi7Mg0.6 sample in face XOY (a) and XOZ (b).
Figure 5. Microstructure of the WAAM-CMT-printed TiB2/AlSi7Mg0.6 sample in face XOY (a) and XOZ (b).
Materials 15 02440 g005
Materials 15 02440 g006 550
Figure 6. Microstructure of WAAM-CMT printed TiB2/AlSi7Mg0.6 composites after T6 heat treatment in face XOY (a) and XOZ (b).
Figure 6. Microstructure of WAAM-CMT printed TiB2/AlSi7Mg0.6 composites after T6 heat treatment in face XOY (a) and XOZ (b).
Materials 15 02440 g006
Materials 15 02440 g007a 550Materials 15 02440 g007b 550
Figure 7. EBSD graphs and grain size diagrams of samples: (a) face XOY of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites; (b) face XOZ of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites; (c) face XOY of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites after T6 heat treatment; (d) face XOZ of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites after T6 heat treatment; (e) WAAM-CMT-printed AlSi7Mg0.6 alloy; (f) casted AlSi7Mg0.6 alloy.
Figure 7. EBSD graphs and grain size diagrams of samples: (a) face XOY of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites; (b) face XOZ of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites; (c) face XOY of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites after T6 heat treatment; (d) face XOZ of WAAM-CMT-printed TiB2/AlSi7Mg0.6 composites after T6 heat treatment; (e) WAAM-CMT-printed AlSi7Mg0.6 alloy; (f) casted AlSi7Mg0.6 alloy.
Materials 15 02440 g007aMaterials 15 02440 g007b
Materials 15 02440 g008 550
Figure 8. Tensile test of TiB2/AlSi7Mg0.6 composites.
Figure 8. Tensile test of TiB2/AlSi7Mg0.6 composites.
Materials 15 02440 g008
Materials 15 02440 g009 550
Figure 9. Fracture morphology of tensile-tested specimens: (a) X direction in the as-deposited samples; (b) Z direction in the as-deposited samples; (c) X direction in the T6 heat-treated samples; (d) Z direction in the T6 heat-treated samples.
Figure 9. Fracture morphology of tensile-tested specimens: (a) X direction in the as-deposited samples; (b) Z direction in the as-deposited samples; (c) X direction in the T6 heat-treated samples; (d) Z direction in the T6 heat-treated samples.
Materials 15 02440 g009
Table
Table 1. Chemical composition of TiB2/AlSi7Mg0.6 wire and samples (mass fraction, wt%).
Table 1. Chemical composition of TiB2/AlSi7Mg0.6 wire and samples (mass fraction, wt%).
ElementSiMgTiBAl
Wire6.790.671.220.58Bal.
Upper location of the sample6.720.590.450.21Bal.
Lower location of the sample6.750.620.530.23Bal.
Table
Table 2. Mechanical properties of TiB2/AlSi7Mg0.6 composites fore-and-aft T6 heat treatment.
Table 2. Mechanical properties of TiB2/AlSi7Mg0.6 composites fore-and-aft T6 heat treatment.
StateRp0.2 (MPa)Rm (MPa)A (%)
Printed samples103 ± 7.26 (X)216 ± 10.87 (X)7 ± 0.89 (X)
83 ± 6.54 (Z)134 ± 9.99 (Z)7 ± 0.77 (Z)
T6 heat-treated samples270 ± 7.62 (X)340 ± 8.18 (X)6 ± 0.63 (X)
266 ± 7.43 (Z)335 ± 8.75 (Z)6 ± 0.58 (Z)
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Yang, Q.; Xia, C.; Wang, H.; Zhou, M.; Gao, S.; Li, B.; Liu, S. Microstructure and Mechanical Properties of TiB2/AlSi7Mg0.6 Composites Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT). Materials 2022, 15, 2440. https://doi.org/10.3390/ma15072440

AMA Style

Yang Q, Xia C, Wang H, Zhou M, Gao S, Li B, Liu S. Microstructure and Mechanical Properties of TiB2/AlSi7Mg0.6 Composites Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT). Materials. 2022; 15(7):2440. https://doi.org/10.3390/ma15072440

Chicago/Turabian Style

Yang, Qingfeng, Cunjuan Xia, Haowei Wang, Mingyang Zhou, Shixin Gao, Bingjin Li, and Shichao Liu. 2022. "Microstructure and Mechanical Properties of TiB2/AlSi7Mg0.6 Composites Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT)" Materials 15, no. 7: 2440. https://doi.org/10.3390/ma15072440

APA Style

Yang, Q., Xia, C., Wang, H., Zhou, M., Gao, S., Li, B., & Liu, S. (2022). Microstructure and Mechanical Properties of TiB2/AlSi7Mg0.6 Composites Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT). Materials, 15(7), 2440. https://doi.org/10.3390/ma15072440

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop