Next Article in Journal
Thermoelectric-Powered Sensors for Internet of Things
Next Article in Special Issue
Lifetime Comparisons of Organic Light-Emitting Diodes Fabricated by Solution and Evaporation Processes
Previous Article in Journal
Editorial for the Special Issue on Micro-Electro Discharge Machining: Principles, Recent Advancements and Applications, Volume II
Previous Article in Special Issue
Recent Progress in Blue Thermally Activated Delayed Fluorescence Emitters and Their Applications in OLEDs: Beyond Pure Organic Molecules with Twist D-π-A Structures
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Micromachines
Volume 14
Issue 1
10.3390/mi14010030
micromachines-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effects of Thermal Treatment on DC Voltage-Driven Color Conversion in Organic Light-Emitting Diode

by
Tae Jun Ahn
1,2,
Bum Ho Choi
3,*,
Jae-Woong Yu
4,
Young Baek Kim
2 and
Yun Seop Yu
1,*
1
Department of Electrical, Electronic and Control Engineering, AISPC Laboratory, IITC, Hankyong National University, 327 Jungang-ro, Anseong-si 17579, Republic of Korea
2
Green Energy Nano Research Group, Korea Institute of Industrial Technology, 6, Cheomdangwagi-ro 208 beon-gil, Buk-gu, Gwangju 61012, Republic of Korea
3
PJPTECH, 36-2, Hagal-ro 86, Giheung-gu, Yongin-si 17096, Republic of Korea
4
Department of Advanced Materials Engineering for Information & Electronics, Kyung Hee University, Deogyeong-daro 1732, Giheung-gu, Yongin-si 17104, Republic of Korea
*
Authors to whom correspondence should be addressed.
Micromachines 2023, 14(1), 30; https://doi.org/10.3390/mi14010030
Submission received: 31 October 2022 / Revised: 16 December 2022 / Accepted: 20 December 2022 / Published: 23 December 2022
(This article belongs to the Special Issue Organic Light Emitting Diodes (OLEDs))
Browse Figures
Review Reports Versions Notes

Abstract

:
A DC voltage-dependent color-tunable organic light-emitting diode (CTOLED) was proposed for lighting applications. The CTOLED consists of six consecutive organic layers: the hole injection layer, the hole transport layer (HTL), two emission layers (EMLs), a hole blocking layer (HBL), and an electron transport layer (ETL). Only one metal-free phthalocyanine (H2Pc) layer with a thickness of 5 nm was employed as the EML in the CTOLED on a green organic light-emitting diode (OLED) structure using tris (8-hydroxyquinoline) aluminum (III) (Alq3). The current density-voltage-luminance characteristics of the CTOLEDs before and after thermal treatment were characterized and analyzed. Several Gaussian peaks were also extracted by multipeak fitting analysis of the electroluminescent spectra. In the CTOLED before thermal treatment, green emission was dominant in the entire voltage range from low to high voltages, and blue and infrared were emitted simultaneously and at relatively low intensities at low and high voltages, respectively. In the CTOLED after thermal treatment, the dominant color conversion from blue to green was observed as the applied voltage increased, and the infrared emission was relatively low over the entire voltage range. By simulating the CTOLED with and without traps at the H2Pc interface using a technology computer-aided design simulator, we observed the following: 1. After thermal treatment, the CTOLED emitted blue light by exciton generation at the H2Pc–HBL interface because of the small electron transport through the H2Pc thin film due to the dramatic reduction of traps in the low-voltage regime. 2. In the high-voltage regime, electrons reaching the HBL were transferred to Alq3 by resonant tunneling in two quantum wells; thus, green light was emitted by exciton generation at the HTL–Alq3 interface.

1. Introduction

Organic light-emitting diodes (OLEDs) are rapidly replacing conventional liquid crystal displays (LCDs) in the display industry because of their unique properties, such as vivid full color, fast response times, wide viewing angles, and self-luminescence [1,2,3]. OLEDs are rapidly developing as a next-generation solid-state light source that replaces conventional incandescent and fluorescent bulbs and inorganic LED light sources [4,5,6]. The performance and lifetime of OLED lights pose potential stability issues; thus, there have been research efforts to improve the power efficiency and lifetime [7]. The characteristics of OLEDs, such as internal efficiency, outcoupling efficiency, and lifetime, have been developed to the level of commercialization [8,9]. Many studies have reported a power efficiency of 90 lm/W and a long lifetime of 20,000 h at an illuminance level of 1000 cd/m2 in white OLEDs (WOLEDs) [10,11,12]. Unlike inorganic LEDs, OLEDs are promising candidates for innovative lighting applications because they are thin, light, and can emit over a large area [13,14]. They can also be applied to various types of lighting, such as medical treatment, visual art, and architectural lighting. Various flexible and transparent OLEDs that provide uniform emission over a large area can be produced, which makes them suitable for various applications, such as medical treatment, visual art, and architecture lighting [15,16,17,18]. Recently, the impact of lighting environments on human emotions has received increased attention, and the need for OLED lighting that enables real-time color adjustment (color shift) has also increased [19,20]. Various types of color-tunable OLEDs (CTOLEDs) have been reported [21,22,23,24,25,26,27]. Initially, a color-tunable OLED that took advantage of the voltage-dependent change in the emission color was fabricated from a polymer blend [21,22,23]. Mechanisms that induce voltage-dependent color changes have the disadvantage of being difficult to control and resulting in undesired changes in device brightness. Subsequently, CTOLEDs that have a stacked tandem structure with multiple subpixels emitting light of different colors have been reported [24]. CTOLEDs control the emission spectrum much better but require an additional electrode for the connection between two adjacent devices to individually address each sub-pixel. This additional electrode must be made of a thin metal film layer or a transparent electrode such as indium tin oxide (ITO). Metal-thin films absorb a significant amount of light and exhibit a microcavity effect, which leads to efficiency issues. More recently, OLEDs that insert a MoO3 layer for charge generation and color tunability using AC voltage have also been reported [25]. An OLED for wearable devices that converts color using an exciton block layer (EBL) that manipulates the charge balance between two adjacent light-emitting layers has been reported [26]. A color-temperature-tunable white OLED (WOLED) using two undoped ultrathin (<1 nm) emitters has also been reported [27]. Existing CTOLEDs require a complicated fabrication process because they have multiple tandem structures with multiple electrodes, which can increase the manufacturing costs. In addition, CTOLEDs have efficiency and AC voltage drive issues owing to their additional electrodes. Third, CTOLEDs with a single-cell structure that has a single emission layer (EML) or multiple EMLs have also been reported [28,29,30,31]. A host-dopant-based EML is used to achieve high-efficiency WOLED, which requires fine doping of red, green, and blue, or blue and yellow fluorescent or phosphorescent dopants into the EML [28,29]. A co-host-in-double-EML device for color-tunable OLEDs based on a single tetradentate Pt(II) emitter has been reported [30]. A CTOLED with a simplified structure, including a dopant-free PN heterojunction as an EML, has been reported [31]. The reported single-cell CTOLEDs require complicated processes, such as fine doping or bandgap engineering, and additional power sources. Therefore, stable and simple DC-voltage CTOLED lighting that can be applied to various applications is required.
In this paper, we propose a DC voltage-dependent color-tunable single-cell OLED lighting system that employs only one metal-free phthalocyanine (H2Pc) layer on a green OLED structure using tris (8-hydroxyquinoline) aluminum (III) (Alq3) as the EML. In Section 2, the structure, fabrication, and characterization of the proposed CTOLED are explained. In Section 3, the characteristics of the CTOLED before and after thermal treatment are compared, and the effects of thermal treatment are investigated. Blue and near-infrared emissions were observed simultaneously at low voltages, whereas a color change from blue to green was observed at high voltages. To physically interpret the color-tunable phenomenon of the single-cell CTOLED, a technology computer-aided design (TCAD) simulation [32] was performed. Finally, Section 4 presents the conclusions.

2. Experiment

Figure 1a shows a schematic of single-cell-structured CTOLED lighting devices fabricated on ITO-coated glass substrates. The CTOLED consists of six consecutive organic layers: the hole injection layer (HIL), the hole transport layer (HTL), two emission layers (EMLs), a hole blocking layer (HBL), and an electron transport layer (ETL). KHI-001, KHT-001, bathocuproine (BCP), and LG-201 were used as the HIL, HTL, HBL, and ETL, respectively. Figure 1b,c show the chemical structures of Alq3 and H2Pc, respectively, used as EMLs in the CTOLED.
An OLED whose EML layer uses only Alq3 can emit green light, as shown in the energy band diagram in Figure 2a [33]. In the proposed CTOLED, 5 nm-thick H2Pc and 30 nm-thick Alq3 were employed as the EMLs, and the H2Pc layer was prepared on the Alq3 layer. As shown in the energy band diagram in Figure 2b, the H2Pc and Alq3 layers can emit blue/red or green colors as electrons or holes, respectively, move through the H2Pc layer. It is well known that there are two energy band gaps for H2Pc: the Soret (B)-band and Q-band (visible). Excitons generated in the B-band and Q-band of the H2Pc can be created and dissipated independently of each other and can play different roles in the recombination process [34,35,36]. In Figure 2b, the red dashed line denotes the energy bandgap of the Q-band of the H2Pc.
All organic materials, including H2Pc, were prepared using a thermal evaporator at a base pressure of 3 × 10−6 torr, and their deposition rate was precisely controlled by adjusting the tooling factor. An ITO with a thickness of 150 nm and sheet resistance of 10 ohm/square and Liq/aluminum with a thickness of 150 nm were used as the anode and cathode electrodes, respectively. The fabricated OLEDs were thermally treated (annealed) for 30 min at 120 °C. Typical glass encapsulation technology with getter paste has been employed to protect organic materials from water vapor and oxygen in an atmospheric environment. The emission area, which was defined during shadow mask patterning for the Al cathode formation, was 2 × 2 mm2.
The electroluminescence (EL) spectra and typical current density-voltage-luminance (J-V-L) characteristics were tested using a J-V-L Measurement system M6100, which consists of a spectroradiometer CS-2000, a Keithley 2400 source meter, and a Keithley 2100 digital multimeter.

3. Results and Discussions

3.1. Characterization of the CTOLED before Thermal Treatment

Figure 3a,b show the J-V-L characteristics and Commission Internationale de L’Eclairage (CIE) coordinates of the CTOLED before thermal treatment, respectively. Empty squares (□) and filled circles (●) denote current density and luminance, respectively. In Figure 3a, each voltage was marked by setting a voltage section of the current density and luminance from A to C. Points, A, B, and C denote 9, 10.5, and 12 V, respectively. In Figure 3b, the color coordinate values of the CTOLED before thermal treatment at voltages corresponding to A–C are marked in CIE coordinates. SG (0.325, 0.55) and SB (0.142, 0.14) denote the color coordinate values of single green and single blue OLEDs using Alq3 and H2Pc, respectively, as a single EML. A (0.277, 0.415) denotes the color coordinate value of a low voltage (9 V), which represents a value between green and blue. The color coordinate values from B to E are almost the same as those of SG (0.325, 0.55). Green with the same color coordinates as SG is continuously emitted at 12 V or higher, where the initial current density changes.
Figure 4 shows the electroluminescence (EL) spectra of the CTOLED before thermal treatment at the applied voltages corresponding to A–C (Figure 3a). Figure 5 shows several Gaussian peaks extracted by multipeak fitting analysis [37] of the EL spectra at the applied voltages corresponding to A and C, respectively. In Figure 3b, the color coordinate values at A and C are (0.277, 0.415) and (0.325, 0.515), respectively. In the multipeak fitting analysis, blue, green, and infrared correspond to 450, 518, and 710 nm, respectively. In the EL spectrum at the applied voltage of 9 V (denoted as solid lines), the green and blue peaks were observed simultaneously. This shows that green and blue were emitted simultaneously from Alq3 and H2Pc (B-band), respectively. The ratio of the green, blue, and infrared peak intensities was approximately 1:10:0. That is, from the color coordinate analysis at 9 V, green was mostly emitted, while blue was simultaneously emitted at a relatively weak intensity. In the EL spectrum at the applied voltage of 12 V (denoted as dashed lines), the green and infrared spectra were observed simultaneously. This shows that green and infrared light were emitted simultaneously from Alq3 and H2Pc (Q-band), respectively. The ratio of the green, blue, and infrared peak intensities was approximately 0:19:1. Above 12 V, green was mostly emitted, while infrared was simultaneously emitted at a very weak frequency. Green emission was observed over the entire voltage range from low to high.

3.2. Characterization of the CTOLED after Thermal Treatment

Figure 6a,b show the J-V-L characteristics and CIE coordinates of the CTOLED after thermal treatment, respectively. Empty squares (□) and filled circles (●) denote current density and luminance, respectively. In Figure 6a, each voltage was marked by setting the low voltage section and peak and valley (PV) of the current density and luminance from A to E. The applied voltages of A, B, C, D, and E denote 10, 12, 15.2, 15.4, and 15.8 V, respectively. A PV current was observed in the D–E section. A PV current is well known as the current that occurs when the flow of electrons is controlled by resonant tunneling [38,39]. When the current density is greatly increased and decreased, the luminance also increases and decreases, respectively, which represents the characteristics of a typical current driving device. In Figure 6b, the color coordinate values of the CTOLED after thermal treatment at the voltages corresponding to A–E are marked in CIE coordinates. The data was divided into two groups in the blue and green regions for easy identification using the CIE coordinates: Group 1 represents points of A, B, and C, and Group 2 represents D and E. The color coordinate values from Groups 1 and 2 are almost the same as those of SB (0.142, 0.14) and SG (0.325, 0.55), respectively. As the applied voltage increases, a color shift from blue to green was observed after the first peak of the current density. The highest luminance value of blue emission was 85 cd/m2 at the applied voltage of C, and after color conversion, the luminance of green emission was 2.25 cd/m2, which was relatively lower than that before color conversion. This indicates that the color conversion from blue to green in the proposed CTOLED is driven by DC voltage.
Figure 7 shows the EL spectra of the CTOLED after thermal treatment at applied voltages from A to E (Figure 6a). At all points of the CTOLEDs after thermal treatment, a near-infrared emission spectrum was observed, whereas a weak near-infrared emission spectrum was observed at high voltages in the case of the CTOLED before thermal treatment. Figure 8 shows several Gaussian peaks extracted by multi-peak fitting analysis of the EL spectra at the applied voltages of C (15.2 V) and D (15.4 V), respectively. In the EL spectra fitted with the multi-peak analysis at the applied voltage of C (denoted as solid lines), blue emission at wavelengths of 452 and 474 nm is dominant, whereas in those at the applied voltage of D (denoted as dashed lines), green emissions at wavelengths of 518 and 568 nm are dominant.

3.3. Analysis of Thermal Treatment Effect

In this section, we discuss why the color conversion from blue and green emissions occurs only in the CTOLED after thermal treatment. Figure 9a,b show atomic force microscope (AFM) images of H2Pc thin film before and after thermal treatment, respectively. The thickness of the H2Pc thin film was 5 nm, the measurement area was 5 μm × 5 μm, and it was scanned in a non-contact mode. The temperature and time of thermal treatment were set to 120 °C and 30 min, respectively. Before thermal treatment, the H2Pc thin film with a thickness of 5 nm can be maintained in the form of a cluster or multi-grain in an unstable state, as shown in Figure 9a, and it can include many traps [40,41,42]. As shown in the schematic in Figure 10a, electrons reaching the HBL can easily be transferred to Alq3 through trap energy levels in the unstable H2Pc thin film; thus, most excitons are generated at the Alq3 interface, emitting a green color. Consequently, green was continuously observed over the entire voltage range. As shown in Figure 9a,b, it was confirmed that the coalescence phenomenon in which the grain boundaries of the thin film coalesce after thermal treatment was observed and the number of grains decreased; thus, the number of traps, that is, the grain boundaries of the H2Pc thin film, can decrease and the uniformity of the thin film was improved [40,41,42]. As shown in the schematic diagram in Figure 10b, only a small number of electrons reaching the HBL can be transferred to Alq3 through the stable H2Pc thin film, and a large number of electrons are captured in the HBL; thus, most excitons are generated at the H2Pc interface, emitting mainly a blue color.
To investigate the trap effect in the H2Pc thin film on the emission color, TCAD simulations were carried out by dividing the state of the H2Pc thin film before and after thermal treatment into a case where there are traps at the H2Pc interface (device 1) and a case without traps (device 2), respectively. The traps were set as 1 × 109 #/cm3 acceptor type using a Gaussian distribution with an average energy level of 3.2 eV and a capture cross section of σ = 0.6. Figure 11 shows the TCAD simulation results for the recombination positions and ratios for exciton generation at an applied voltage of 10 V with and without traps. Recombination was observed at the HTL–Alq3 and H2Pc–HBL interfaces. In the case of device 1 with traps at the H2Pc interface, there were recombination rates of 5 × 1018 #/cm3 and 3 × 1014 #/cm3 at the HTL–Alq3 and H2Pc–HBL interfaces, respectively, whereas in device 2 without any traps at the H2Pc interface, there were recombination rates of 8 × 105 #/cm3 and 1 × 1022 #/cm3 at the HTL–Alq3 and H2Pc–HBL interfaces, respectively. This suggests that the trap can affect electron transport, as shown in the schematic in Figure 10. It can be concluded that the instability of the H2Pc thin film is resolved through thermal treatment; thus, blue is emitted by exciton generation at the H2Pc–HBL interface owing to a small electron transport through the H2Pc thin film by the dramatic reduction of traps in the low-voltage regime. In the high-voltage regime, electrons reaching the HBL are transferred to Alq3 by resonant tunneling [38,39] through the H2Pc thin film in two quantum wells (the HBL and Alq3 layers); thus, green is emitted by exciton generation at the HTL–Alq3 interface. The emitted color changes from blue at low voltages to green at high voltages.
Figure 12 shows the external quantum efficiency (EQE)–voltage (V) characteristics of the CTOLEDs before and after thermal treatment. The EQE after thermal treatment is higher than one before thermal treatment, so it can be analyzed that the stable state of the H2Pc thin film by thermal treatment makes a higher EQE. However, because the EQE is very low, the structure and process on the improvement of EQE must be studied in the future.
The lifetime of thermally treated CTOLEDs was also measured and compared with that of non-treated ones. The conditions of the lifetime measurement were 38 °C of temperature and 85% relative humidity. The lifetime at the LT 95 level obtained from the non-treated one was 92 h. On the other hand, that from thermally treated CTOLED was measured to be 108 h, which was improved by 17.4%. By applying thermal treatment, it can be expected that the interface between adjacent organic emitting layers was improved by reducing traps, as mentioned before. Therefore, by employing thermal treatment on the fabricated OLED, we have observed color tunability from green to blue and white as well as an elongated lifetime.

4. Conclusions

We proposed and experimented on a DC voltage-dependent CTOLED that employs only one H2Pc layer with a thickness of 5 nm on a green OLED structure using Alq3 as the EML. To investigate the thermal treatment effects of the CTOLED, J-V-L characteristics and energy band diagrams of the CTOLEDs before and after the thermal treatment were characterized and analyzed. Several Gaussian peaks were also extracted by multi-peak fitting analysis of the EL spectra. In the CTOLED before thermal treatment, green emission was dominant in the entire voltage range from low to high voltages, and blue and infrared were emitted simultaneously and had relatively low intensities at low and high voltages, respectively. In the CTOLED after thermal treatment, the dominant color conversion from blue to green was observed as the applied voltage increased, and the infrared emission was relatively low over the entire voltage range. To investigate the reason why the CTOLED, after thermal treatment, resulted in color conversion from blue to green emissions, CTOLEDs with and without traps at the H2Pc interface were simulated using a TCAD simulator. Traps in the H2Pc layer and interface with sub-nanometer thickness can be reduced due to improved stability from thermal treatment. In the TCAD simulation, the CTOLED before thermal treatment emitted green by exciton generation at the HTL–Alq3 interface in the entire voltage regime because the electrons reaching the HBL could easily be transferred to Alq3 through trap energy levels in the unstable H2Pc thin film. The CTOLED after thermal treatment emitted blue by exciton generation at the H2Pc–HBL interface due to a small electron transport through the H2Pc thin film in the low voltage regime. In the high-voltage regime, electrons reaching the HBL are transferred to Alq3 by resonant tunneling in two quantum wells; thus, green was emitted by exciton generation at the HTL–Alq3 interface. In conclusion, the H2Pc thin film with the thickness of 5 nm can be stabilized by thermal treatment; thus, the emitted color of the proposed OLED is shifted from blue to green as the applied voltage increases and the EQE is relatively higher than before thermal treatment. However, as both EQEs before and after thermal treatment are very low, research on the improvement of EQE needs to be conducted in the future with other fabrication techniques [43].

Author Contributions

Conceptualization, T.J.A., B.H.C., Y.B.K., J.-W.Y. and Y.S.Y.; Methodology, T.J.A., B.H.C., J.-W.Y. and Y.S.Y.; Investigation, T.J.A., B.H.C. and Y.S.Y.; Data Curation, T.J.A.; Writing—Original Draft Preparation, T.J.A.; Writing—Review & Editing, T.J.A., B.H.C. and Y.S.Y.; Supervision, B.H.C. and Y.S.Y.; Project Administration, B.H.C. and Y.S.Y.; Funding Acquisition, Y.B.K. and Y.S.Y. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Data Availability Statement

Not applicable.

Acknowledgments

This work was supported by the IDEC (EDA tool).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Geffroy, B.; Roy, P.; Prat, C. Organic light-emitting diode (OLED) technology: Materials, devices and display technologies. Polym. Int. 2006, 55, 572–582. [Google Scholar] [CrossRef]
  2. Singh, M.; Jou, J.-H.; Sahoo, S.; Sujith, S.S.; He, Z.-K.; Krucaite, G.; Grigalevicius, S.; Wang, C.W. High light-quality OLEDs with a wet-processed single emissive layer. Sci. Rep. 2018, 8, 7133. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  3. Shin, H.J.; Takasugi, S.; Park, K.-M.; Choi, S.-H.; Jeong, Y.-S.; Song, B.-C.; Kim, H.-S.; Oh, C.-H.; Ahn, B.-C. 7.1: Invited Paper: Novel OLED display technologies for large-size UHD OLED TVs. SID Symp. Dig. Tech. Pap. 2015, 46, 53–56. [Google Scholar] [CrossRef]
  4. So, F.; Kido, J.; Burrows, P. Organic light-emitting devices for solid-state lighting. MRS Bull. 2011, 33, 663–669. [Google Scholar] [CrossRef]
  5. Pu, Y.J.; Nakata, G.; Satoh, F.; Sasabe, H.; Yokoyama, D.; Kido, J. Optimizing the charge balance of fluorescent organic light-emitting devices to achieve high external quantum efficiency beyond the conventional upper limit. Adv. Mater. 2012, 24, 1765–1770. [Google Scholar] [CrossRef]
  6. Ji, W.; Zhao, J.; Sun, Z.; Xie, W. High-color-rendering flexible top-emitting warm-white organic light emitting diode with a transparent multilayer cathode. Org. Electron. 2011, 12, 1137–1141. [Google Scholar] [CrossRef]
  7. Xia, S.C.; Kwong, R.C.; Adamovich, V.I.; Weaver, M.S.; Brown, J. OLED Device Operational Lifetime: Insights and Challenges. In Proceedings of the 2007 IEEE International Reliability Physics Symposium, Phoenix, AZ, USA, 15–19 April 2007; pp. 253–257. [Google Scholar]
  8. Brutting, W.; Frischeisen, J.; Schmidt, T.D.; Scholz, B.J.; Mayr, C. Device efficiency of organic light-emitting diodes: Progress by improved light outcoupling. Phys. Status Solidi A 2012, 210, 44–65. [Google Scholar] [CrossRef]
  9. Kim, H.-G.; Kim, K.-H.; Kim, J.-J. Highly efficient, conventional, fluorescent organic light-emitting diodes with extended lifetime. Adv. Mater. 2017, 29, 1702159. [Google Scholar] [CrossRef]
  10. He, G.; Rothe, C.; Murano, S.; Werner, A.; Zeika, O.; Brinstock, J. White stacked OLED with 38 lm/W and 100,000-hour lifetime at 1000 cd/m2 for display and lighting applications. J. Soc. Inf. Disp. 2012, 17, 159–165. [Google Scholar] [CrossRef]
  11. Ide, N.; Tsuji, H.; Ito, N.; Matsuhisa, Y.; Houzumi, S.; Nishimori, T. White OLED Devices and Processes for Lighting Applications. In Proceedings of the SPIE Photonics Europe, Brussels, Belgium, 18 May 2010; pp. 772202.1–772202.8. [Google Scholar]
  12. Komoda, T.; Tsuji, H.; Yamae, K.; Varutt, K.; Matsuhisa, Y.; Ide, N. High performance white OLEDs for next generation solid state lightings. SID Symp. Dig. Tech. Pap. 2012, 42, 1056–1059. [Google Scholar] [CrossRef]
  13. Park, J.W.; Shin, D.C.; Park, S.H. Large-area OLED lightings and their applications. Semicond. Sci. Technol. 2011, 26, 034002. [Google Scholar] [CrossRef]
  14. Huang, Y.; Hsiang, E.-L.; Deng, M.-Y.; Wu, S.-T. Mini-LED, Micro-LED and OLED displays: Present status and future perspectives. Light Sci. Appl. 2020, 9, 105. [Google Scholar] [CrossRef] [PubMed]
  15. Sugimoto, A.; Ochi, H.; Fujimura, S.; Yoshida, A.; Miyadera, T.; Tsuchida, M. Flexible OLED displays using plastic substrates. IEEE J. Sel. Top. Quantum Electron. 2004, 10, 107–114. [Google Scholar] [CrossRef]
  16. Auch, M.D.J.; Soo, O.K.; Ewald, G.; Soo-Jin, C. Ultrathin glass for flexible OLED application. Thin Solid Film. 2002, 417, 47–50. [Google Scholar] [CrossRef]
  17. Yang, C.M.; Kim, C.W.; Kwon, H.J.; Kim, M.C.; Kim, P.R. Evaluation of perceived see-through level for transparent OLED displays. SID Symp. Dig. Tech. Pap. 2017, 48, 1363–1366. [Google Scholar] [CrossRef]
  18. Lee, J.-K.; Yim, J.-H. Alternating current input LED lighting control system using Fuzzy theory. J. Inf. Commun. Converg. Eng. 2021, 19, 214–220. [Google Scholar] [CrossRef]
  19. Cupkova, D.; Kajati, E.; Mocnej, J.; Papcun, P.; Koziorek, J.; Zolotova, I. Intelligent human-centric lighting for mental wellbeing improvement. Int. J. Distrib. Sens. Netw. 2019, 15, 1550147719875878. [Google Scholar] [CrossRef]
  20. Pelowski, M.; Graser, A.; Specker, E.; Forster, M.; Hinuber, J.V.; Leder, H. Does gallery lighting really have an impact on appreciation of art? An ecologically valid study of lighting changes and the assessment and emotional experience with representational and abstract paintings. Front. Psychol. 2019, 10, 2148. [Google Scholar] [CrossRef]
  21. Burrows, P.E.; Forrest, S.R.; Sibley, S.P.; Thompson, M.E. Color-tunable organic light-emitting devices. Appl. Phys. Lett. 1996, 69, 2959–2962. [Google Scholar] [CrossRef]
  22. Yang, Y.; Pei, Q. Voltage controlled two color light-emitting electrochemical cells. Appl. Phys. Lett. 1996, 68, 2708–2711. [Google Scholar] [CrossRef]
  23. Huang, C.C.; Meng, H.F.; Ho, G.K.; Chen, C.H. Color-tunable multilayer light-emitting diodes based on conjugated polymers. Appl. Phys. Lett. 2004, 84, 1195–1198. [Google Scholar] [CrossRef] [Green Version]
  24. Frobel, M.; Schwab, T.; Kliem, M.; Hofmann, S.; Leo, K.; Gather, M.C. Get it white: Color-tunable AC/DC OLEDs. Light Sci. Appl. 2015, 4, e247.1–e247.6. [Google Scholar] [CrossRef] [Green Version]
  25. Zhao, Y.; Chen, R.; Gao, Y.; Leck, K.S.; Yang, X.; Liu, S.; Abiyasa, A.P.; Divayana, Y.; Mutlugun, E.; Tan, S.T.; et al. AC-driven, color- and brightness-tunable organic light-emitting diodes constructed from an electron only device. Org. Electron. 2013, 14, 3195–3200. [Google Scholar] [CrossRef]
  26. Koo, J.H.; Jeong, S.J.; Shim, H.J.; Son, D.H.; Kim, J.M.; Kim, D.C.; Choi, S.J.; Hong, J.I.; Kim, D.H. Wearable electrocardiogram monitor using carbon nanotube electronics and color-tunable organic light-emitting diodes. ACS Nano 2017, 11, 10032–10041. [Google Scholar] [CrossRef] [PubMed]
  27. Xu, T.; Yang, M.; Liu, J.; Wu, X.; Murtaza, I.; He, G.; Meng, H. Wide color-range tunable and low roll-off fluorescent organic light emitting devices based on double undoped ultrathin emitters. Org. Electron. 2016, 37, 93–99. [Google Scholar] [CrossRef]
  28. Chen, K.; Wei, Z. High-efficiency single emissive layer color-tunable all-fluorescent white organic light-emitting diodes. Chem. Phys. Lett. 2022, 786, 139145. [Google Scholar] [CrossRef]
  29. Li, W.X.; Hagen, J.; Jones, R.; Heikenfeld, J.; Steckl, A.J. Color tunable organic light emitting diodes using Eu complex doping. Solid-State Electron. 2007, 51, 500–504. [Google Scholar] [CrossRef]
  30. Mao, M.; Lam, T.; To, W.; Lao, X.; Liu, W.; Xu, S.; Cheng, G.; Che, C. Stable, High-efficiency voltage-dependent color-tunable organic light-emitting diodes with a single tetradentate platinum(II) emitter having long operational lifetime. Adv. Mater. 2020, 33, 2004873. [Google Scholar] [CrossRef]
  31. Wang, Q.; Bai, J.; Zhao, C.; Ali, M.U.; Miao, J.; Meng, H. Simplified dopant-free color-tunable organic light-emitting diodes. Appl. Phys. Lett. 2021, 118, 253301. [Google Scholar] [CrossRef]
  32. Silvaco Int. ATLAS, version 5.32.1. R Manual; Silvaco Int.: Santa Clara, CA, USA, 2022. [Google Scholar]
  33. Tang, C.W.; VanSlyke, S.A. Organic electroluminescent diodes. Appl. Phys. Lett. 1987, 51, 913–915. [Google Scholar] [CrossRef]
  34. Fujii, A.; Yoshida, M.; Ohmori, Y.; Yoshino, K. Two-band electroluminescent emission in organic electroluminescent diode with phthalocyanine film. Jpn. J. Appl. Phys. 1996, 35, L37–L39. [Google Scholar] [CrossRef]
  35. El-Nahass, M.M.; Farid, A.M.; Attia, A.A.; Ali, H.A.M. Structural properties and UV to NIR absorption spectra of metal-free phthalocyanine (H2Pc) thin films. Fiz. A 2006, 15, 147–164. [Google Scholar]
  36. Fan, Z.; Cheng, C.; Yu, S.; Ye, K.; Sheng, R.; Xia, D.; Ma, C.; Wang, X.; Chang, Y.; Du, G. Red and near-infrared electroluminescence from organic light-emitting devices based on a soluble substituted metal-free phthalocyanine. Opt. Mater. 2009, 31, 889–894. [Google Scholar] [CrossRef]
  37. Yoon, J.-A.; Kim, Y.-H.; Kim, N.H.; Moon, C.-B.; He, G.; Kim, W.Y. Study of energy transfer in single and multi-emissive layer using Gaussian peak fitting. J. Lumin. 2014, 153, 104–108. [Google Scholar] [CrossRef]
  38. Park, T.J.; Lee, Y.K.; Kwon, S.K.; Kwon, J.H.; Jang, J. Resonant tunneling diode made of organic semiconductor superlattice. Appl. Phys. Lett. 2006, 89, 151114. [Google Scholar] [CrossRef]
  39. Zhu, Y.; Wang, H.; Chen, W.; Wang, Y.; Yan, D. Organic quantum wells with multiple negative differential resistance peaks and its photoswitch effect. Org. Electron. 2016, 35, 24–32. [Google Scholar] [CrossRef]
  40. El-Nahass, M.M.; Farid, A.M.; Attia, A.A.; Ali, H.A.M. Electrical transport properties of thermally evaporated phthalocyanine (H2Pc) thin films. Appl. Surf. Sci. 2006, 252, 7553–7561. [Google Scholar] [CrossRef]
  41. Mindorff, M.S.; Brodie, D.E. Some properties of metal-free amorphous phthalocyanine vacuum deposited films. Can. J. Phys. 1981, 59, 249–254. [Google Scholar] [CrossRef]
  42. Lee, E.K. Simulation of the thin-film thickness distribution for an OLED thermal evaporation process. Vacuum 2009, 83, 848–852. [Google Scholar] [CrossRef]
  43. Ji, Y.; Wang, M.; Yang, Z.; Ji, S.; Qiu, H. Nanowire-assisted self-assembly of one-dimensional nanocrystal superlattice chains. J. Mater. Chem. C 2019, 7, 8471–8476. [Google Scholar] [CrossRef]
Micromachines 14 00030 g001 550
Figure 1. (a) Schematic of proposed single-cell color tunable organic light-emitting diode (CTOLED) and chemical structures of (b) tris (8-hydroxyquinoline) aluminum (III) (Alq3) and (c) phthalocyanine (H2Pc).
Figure 1. (a) Schematic of proposed single-cell color tunable organic light-emitting diode (CTOLED) and chemical structures of (b) tris (8-hydroxyquinoline) aluminum (III) (Alq3) and (c) phthalocyanine (H2Pc).
Micromachines 14 00030 g001
Micromachines 14 00030 g002 550
Figure 2. Energy band diagram of the CTOLED. (a) An OLED with only Alq3 as the EML and (b) a CTOLED with H2Pc and Alq3 as EMLs.
Figure 2. Energy band diagram of the CTOLED. (a) An OLED with only Alq3 as the EML and (b) a CTOLED with H2Pc and Alq3 as EMLs.
Micromachines 14 00030 g002
Micromachines 14 00030 g003 550
Figure 3. (a) Current density (J), voltage (V), and luminance (L) characteristics and (b) CIE coordinates of the CTOLED before thermal treatment.
Figure 3. (a) Current density (J), voltage (V), and luminance (L) characteristics and (b) CIE coordinates of the CTOLED before thermal treatment.
Micromachines 14 00030 g003
Micromachines 14 00030 g004 550
Figure 4. Electroluminescent (EL) spectra of the CTOLED before thermal treatment at the voltages of A, B, and C shown in Figure 3a.
Figure 4. Electroluminescent (EL) spectra of the CTOLED before thermal treatment at the voltages of A, B, and C shown in Figure 3a.
Micromachines 14 00030 g004
Micromachines 14 00030 g005 550
Figure 5. Multi-peak fit of the CTOLED before thermal treatment using a Gaussian function at applied voltages of 9 and 12 V. At the applied voltage of 9 V, original and multi-peak fitted data of ELs are shown to be amplified 10 times.
Figure 5. Multi-peak fit of the CTOLED before thermal treatment using a Gaussian function at applied voltages of 9 and 12 V. At the applied voltage of 9 V, original and multi-peak fitted data of ELs are shown to be amplified 10 times.
Micromachines 14 00030 g005
Micromachines 14 00030 g006 550
Figure 6. (a) J-V-L characteristics and (b) CIE color coordinates of the CTOLED after thermal treatment.
Figure 6. (a) J-V-L characteristics and (b) CIE color coordinates of the CTOLED after thermal treatment.
Micromachines 14 00030 g006
Micromachines 14 00030 g007 550
Figure 7. EL spectra of the CTOLED after thermal treatment at applied voltages of A, B, and C, D, and E shown in Figure 6a. At the applied voltages of D and E, ELs are shown to be amplified 10 times.
Figure 7. EL spectra of the CTOLED after thermal treatment at applied voltages of A, B, and C, D, and E shown in Figure 6a. At the applied voltages of D and E, ELs are shown to be amplified 10 times.
Micromachines 14 00030 g007
Micromachines 14 00030 g008 550
Figure 8. Multi-peak fit of the CTOLED after thermal treatment using a Gaussian function at an applied voltage of 15.2 and 15.4 V. At the applied voltage of 15.4 V, original and multi-peak fitted data of ELs are shown to be amplified 10 times.
Figure 8. Multi-peak fit of the CTOLED after thermal treatment using a Gaussian function at an applied voltage of 15.2 and 15.4 V. At the applied voltage of 15.4 V, original and multi-peak fitted data of ELs are shown to be amplified 10 times.
Micromachines 14 00030 g008
Micromachines 14 00030 g009 550
Figure 9. Atomic force microscope (AFM) images of H2Pc thin film with a thickness of 5 nm. (a) as-dep and (b) 120 °C thermal treatment for 30 min.
Figure 9. Atomic force microscope (AFM) images of H2Pc thin film with a thickness of 5 nm. (a) as-dep and (b) 120 °C thermal treatment for 30 min.
Micromachines 14 00030 g009
Micromachines 14 00030 g010 550
Figure 10. Schematic of electron transport in the case of (a) a large number of traps before thermal treatment and (b) a small number of traps after thermal treatment.
Figure 10. Schematic of electron transport in the case of (a) a large number of traps before thermal treatment and (b) a small number of traps after thermal treatment.
Micromachines 14 00030 g010
Micromachines 14 00030 g011 550
Figure 11. Simulation results of Langevin recombination rate at an applied voltage of 10 V with and without trap using technology computer-aided design (TCAD).
Figure 11. Simulation results of Langevin recombination rate at an applied voltage of 10 V with and without trap using technology computer-aided design (TCAD).
Micromachines 14 00030 g011
Micromachines 14 00030 g012 550
Figure 12. External quantum efficiency (EQE)-voltage (V) characteristics of the CTOLED before and after thermal efficiency.
Figure 12. External quantum efficiency (EQE)-voltage (V) characteristics of the CTOLED before and after thermal efficiency.
Micromachines 14 00030 g012
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Ahn, T.J.; Choi, B.H.; Yu, J.-W.; Kim, Y.B.; Yu, Y.S. Effects of Thermal Treatment on DC Voltage-Driven Color Conversion in Organic Light-Emitting Diode. Micromachines 2023, 14, 30. https://doi.org/10.3390/mi14010030

AMA Style

Ahn TJ, Choi BH, Yu J-W, Kim YB, Yu YS. Effects of Thermal Treatment on DC Voltage-Driven Color Conversion in Organic Light-Emitting Diode. Micromachines. 2023; 14(1):30. https://doi.org/10.3390/mi14010030

Chicago/Turabian Style

Ahn, Tae Jun, Bum Ho Choi, Jae-Woong Yu, Young Baek Kim, and Yun Seop Yu. 2023. "Effects of Thermal Treatment on DC Voltage-Driven Color Conversion in Organic Light-Emitting Diode" Micromachines 14, no. 1: 30. https://doi.org/10.3390/mi14010030

APA Style

Ahn, T. J., Choi, B. H., Yu, J. -W., Kim, Y. B., & Yu, Y. S. (2023). Effects of Thermal Treatment on DC Voltage-Driven Color Conversion in Organic Light-Emitting Diode. Micromachines, 14(1), 30. https://doi.org/10.3390/mi14010030

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop