Next Article in Journal
Highly Efficient Catalytic Reduction of Nitrobenzene Using Cu@C Based on a Novel Cu–MOF Precursor
Next Article in Special Issue
S–Modified MXene as a Catalyst for Accelerated Tetracycline Hydrochloride Electrocatalytic Degradation via ·OH and Active Chlorine Triggering Promotion
Previous Article in Journal
Hydrogenation of CO2 to Valuable C2-C5 Hydrocarbons on Mn-Promoted High-Surface-Area Iron Catalysts
Previous Article in Special Issue
Recent Progress in Electrocatalytic Reduction of CO2
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Catalysts
Volume 13
Issue 6
10.3390/catal13060955
catalysts-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Recent Progress in Electrocatalytic CO2 Reduction to Pure Formic Acid Using a Solid-State Electrolyte Device

by
Yeomin Kang
,
Taekyung Kim
,
Koo Young Jung
and
Ki Tae Park
*
Department of Chemical Engineering, Konkuk University, 120 Neungdong-ro, Gwangjin-gu, Seoul 05029, Republic of Korea
*
Author to whom correspondence should be addressed.
Catalysts 2023, 13(6), 955; https://doi.org/10.3390/catal13060955
Submission received: 28 April 2023 / Revised: 22 May 2023 / Accepted: 30 May 2023 / Published: 31 May 2023
(This article belongs to the Special Issue Electrocatalysis/Photocatalysis for CO2 Conversion, H2 Production, and Pollutant Removal)
Browse Figures
Versions Notes

Abstract

:
The electrocatalytic CO2 reduction reaction (CO2RR) to formic acid has gained significant attention as a potential environmentally friendly approach to reducing CO2 emissions and producing carbon-neutral liquid fuels. However, several challenges must be addressed to achieve the production of high-purity and high-concentration formic acid through CO2RR. One major challenge is the formation of a formate mixture instead of pure formic acid in conventional reactors. This requires costly downstream purification and concentration processes to obtain pure formic acid. To overcome this problem, a three-compartment reactor design has been proposed where a solid-state electrolyte (SSE) is inserted between the anode and cathode compartments to recover pure formic acid directly. This reactor design involves the use of an anion exchange membrane (AEM) and a cation exchange membrane (CEM) to separate the anode and cathode compartments, and a center compartment filled with high-conductivity SSE to minimize ohmic resistance. Several studies have implemented this reactor design for continuous CO2RR and have reported remarkable improvements in the concentration and purity of the formic acid product. In this review, we summarize the recent progress of the SSE reactor design for CO2RR to produce pure formic acid (HCOOH) and propose further research to scale up this technology for industrial-scale applications in the future.

1. Introduction

Anthropogenic activities, particularly the excessive usage of fossil fuels, have led to a significant increase in the level of CO2 in the atmosphere since the beginning of the industrial period [1]. This rise in CO2 levels has contributed to a climate crisis, evident from the recent occurrence of extreme weather events such as floods and forest fires. To address these challenges and reduce greenhouse gas emissions, substantial efforts have been directed toward finding ways to convert CO2 into value-added chemicals or fuels, including methanol (CH3OH), formate (HCOO−)/formic acid (HCOOH), carbon monoxide (CO), syngas (CO and H2), and ethylene (C2H4) [2]. Among the numerous CO2 conversion approaches such as biochemical, thermochemical, photochemical, and electrochemical methods, electrocatalytic CO2 reduction reaction (CO2RR) is attracting significant attention as an environmentally friendly approach. CO2RR can be coupled with intermittent renewable energies due to its mild operating conditions with room temperature and atmospheric pressure. It enables the conversion of CO2 into value-added products without additional emissions (Figure 1) [3,4,5,6]. Due to their high selectivity (>90%) and activity (>100 mA cm−2) for industrial applications, the cost of certain CO2RR products, particularly C1 chemicals such as CO and formic acid, has become economically competitive with traditional chemical processes [7,8,9,10,11,12]. This trend has been further supported by the decreasing price of renewable electricity.
Liquid products such as HCOO−/HCOOH offer significant advantages over gas-phase CO2RR products due to their high energy densities and ease of storage and distribution [13,14]. Formic acid, in particular, is a crucial chemical feedstock with a global production of approximately 800,000 metric tons per year, used in a wide range of applications, including chemical production, cleaning, the textile industry, and antiseptics [15,16,17,18]. Moreover, formic acid has gained attention as a promising hydrogen carrier due to its high volumetric hydrogen density (53 g H2 per liter of HCOOH), low toxicity, and the fact that it is in the liquid phase under ambient conditions [19,20]. It is also considered an energy carrier for fuel cell applications due to its stability, low volatility, and high volumetric capacity [21,22]. Thus, producing formic acid through electrochemical CO2RR can serve as a carbon-neutral liquid fuel, effectively offsetting carbon emissions [23]. However, several challenges must be addressed for the practical applications of CO2RR in renewable formic acid production: (i) improving the selectivity, activity, and durability of the catalysts; (ii) reducing the energy consumption and cost of the process; (iii) scaling up the technology and integrating it with renewable energy sources; (iv) separating the product from aqueous mixture. Additional purification steps are often required, increasing production costs [23,24,25,26].
To address the limitations in CO2RR for formic acid production, extensive research efforts have been focused on developing efficient electrocatalysts, suitable electrolytes, and reactor designs to achieve high productivity. In particular, catalyst development has received significant attention to improving the selectivity and activity toward HCOO−/HCOOH production. Recent studies have made notable progress in identifying and designing efficient electrocatalysts for the selective production of HCOO−/HCOOH. For example, studies on the development of nanostructured and bimetallic catalysts have shown promising results in achieving high selectivity and activity for CO2RR to HCOO−/HCOOH [27,28,29,30,31,32,33,34,35,36]. In addition, single-atom catalysts (SACs) for CO2RR to HCOO−/HCOOH have been investigated due to their high surface area and atomic-level dispersion of active sites, which can enhance their electrocatalytic performance [12].
Nevertheless, there are other practical challenges that require technological advancements beyond the scope of electrocatalyst design. One prominent challenge is the purity and concentration of the liquid products [37]. In recent years, research efforts have been focused on developing efficient and scalable reactors for CO2RR to formate/formic acid with a growing demand for technologies and devices that enable direct formic acid production. One promising approach is the use of an additional compartment of solid-state electrolyte (SSE) inserted between the anode and cathode compartments [23,26,38,39]. In this reactor design, the cathode and anode are in contact with an anion exchange membrane (AEM) and a cation exchange membrane (CEM), respectively. The HCOO- and H+ ions generated at the cathode and anode migrate across the AEM and CEM, respectively, into the center compartment, in which pure HCOOH molecules are formed via ionic recombination. In this review, we emphasize the significance and challenges associated with the direct production of high-purity formic acid by reviewing the recent progress of SSE devices for CO2RR and discussing strategies to enhance selectivity, activity, and purity for the direct production of pure formic acid. This work provides valuable insights and guidelines for the design of electrolyzers capable of producing pure liquid fuels through CO2RR, bringing us closer to large-scale applications in the future.

2. Electrocatalytic CO2 Reduction to Formate

2.1. CO2RR to Formate Using CO2-Dissolved Liquid Feed

In early CO2RR studies, numerous research groups have utilized reactors such as 3-electrode and H-type cells to produce formate in aqueous solutions. Figure 2 illustrates the typical configuration of an H-type cell, where the cathode and anode chambers are separated by an ion exchange membrane. This type of reactor has been widely employed for investigating various CO2RR catalysts due to its versatile setup. In these experiments, the catholyte is saturated with CO2 by continuous bubbling using a glass sparger before electrolysis. The CO2 gas is supplied continuously to the catholyte throughout the experiment to improve the absorption of the CO2 gas in the aqueous solution [27]. Researchers have utilized this reactor configuration to develop highly active and selective electrocatalysts for CO2RR [27,29,30,31,32,33,34,35,36,40]. Since the previous works by Hori et al. described the classification of metal catalysts according to product selectivity for CO2RR [41], extensive efforts have been made to develop various heterogeneous metal-based catalysts for selective CO2RR to formate. Table 1 summarizes some of the metal catalysts that have been investigated for their potential in CO2RR to formate, including tin (Sn), lead (Pb), bismuth (Bi), and indium (In).
Choi et al. studied the CO2RR to formate in an aqueous solution using tin–lead (Sn–Pb) alloys [27]. The study found that the Sn56.3Pb43.7 alloy exhibits high faradaic efficiency (FEformate of 79.8%) and current density (jformate of 45.7 mA cm−2) for formate synthesis; 16%, and 25% improved FEformate and jformate compared to the single metal electrodes (Figure 3).
Tan et al. reported a highly efficient CO2RR to formate on a tin (IV) oxide/zinc oxide (SnO2/ZnO) composite electrocatalyst with a grainy hollow nanofiber (HNF) structure [29]. The faradaic efficiency (FE) of formate on the SnO2/ZnO composite HNF reaches as high as 97.9% at −1.34 V (vs. RHE), outperforming many Sn-based catalysts. At −1.54 V (vs. RHE), the SnO2/ZnO HNF exhibits 2 times and 4 times higher current density for formate generation than those of SnO2 HNF and nanoparticles (NPs), respectively. This superior catalytic performance is attributed to its one-dimensional continuous structure as well as to the synergistic effects between SnO2 and ZnO, which facilitate faster electron transfer and improve the conductivity of SnO2/ZnO composite HNF (Figure 4).
Despite these significant results, the kinetics of CO2RR into formate is limited below 50 mA cm−2 (Table 1) due to the polarization losses caused by the low solubility of CO2 in the electrolyte, and the mass transfer limitation of OH− near the electrodes, inevitably limiting the productivity of CO2RR [42]. In particular, the low solubility of CO2 in the aqueous catholyte significantly limits the current density, thus hindering the large-scale application of the CO2RR.

2.2. CO2RR to Formate Using Gaseous CO2 Feed

There have been experiments in CO2 electroreduction that involve supplying gaseous CO2 to the cathode, allowing for sufficient CO2 delivery to the catalyst even at elevated current densities. Some research groups achieved remarkable improvement in the current density of CO2RR to formate using gas diffusion electrodes (GDEs) typically composed of a backing layer, a microporous layer (MPL), and a catalyst layer (CL) [42,43,44,45]. Several research groups have successfully utilized GDE-type CO2RR reactors (Figure 5a) and achieved high current densities for formate production, exceeding 200 mA cm−2 and even up to 1000 mA cm−2, with faradaic efficiencies (FE) higher than 90% as summarized in Table 2 [46,47,48,49,50,51,52,53]. However, one challenge with GDE-type electrolyzers is that they typically use aqueous electrolytes, such as KHCO3, K2CO3, or KOH, for the collection of liquid products. The presence of these aqueous electrolytes can dilute the liquid products, such as formate/formic acid, which increases the costs associated with product recovery and separation [54].
To overcome this challenge of GDE-type reactors, some research groups have studied CO2RR to formate in a zero-gap type electrolyzer, which eliminates the need for an aqueous electrolyte [54,55,56,57]. Lee et al. reported a facile strategy of catholyte-free electrocatalytic CO2 reduction (CF-CO2R) that avoids the solubility limitation by supplying an appropriate amount of water vapor with gaseous CO2 as a cathode reactant [54]. In this electrolyzer, the water vapor. In the CF-CO2R electrolyzer, water vapor acts as a carrier for supplying dissolved CO2 to the cathode by forming a CO2-saturated aqueous film on the catalyst surface as shown in Figure 5b. The advantage of this approach is that the consumed CO2 in the film can be immediately replenished from the bulk gas stream, enhancing the mass transfer of CO2 and improving the reaction kinetics. Lee et al. achieved a formate current density (jformate) of 51.7 mA cm−2 at a low cell voltage of 2.2 V using this CF-CO2R approach. They also obtained a significantly high concentration of formate solution, reaching 116.2 g-formate L−1, with a formate faradaic efficiency (FEformate) of 77.7% by reducing the vapor supply from 12.58 to 0.65 mg min−1 cm−2 at 2.2 V and 323 K.
The zero-gap electrolyzer has several advantages over the GDE-catholyte method, including (1) lower cell voltage and improved energy efficiency by eliminating a large ohmic resistance of the catholyte compartment; (2) reduced cost by removing the cost of the catholyte; and (3) zero-gap configuration, which makes the system simple and easy to scale up. However, the lower current density observed in this configuration is indeed due to the challenges associated with the discharge of liquid products and the formation of solid precipitates.
In the zero-gap type electrolyzer, the liquid products have to be discharged in the opposite direction of the CO2 supply, and ions (HCOO−, HCO3−, CO32−, K+, and Na+, etc.) in the liquid products form solid precipitates, which limits the supply of CO2. Additionally, the flow of aqueous liquid products through the gas diffusion electrode (GDE) can cause a decrease in the hydrophobicity of the electrode over time, a phenomenon known as electro-wetting. This leads to flooding of GDE that significantly inhibits the migration of CO2 to the catalyst layer, reducing the selective reduction of CO2 to formates while promoting the hydrogen evolution reaction (HER) as shown in Figure 6.
Recently, Díaz-Sainz et al. achieved a high jformate of 300 mA cm−2 by continuous operation using an anion exchange membrane (AEM, SustainionTM, Dioxide Materials) with a formate concentration of 6.7 g L−1 at a cell potential of 3.6 V [57]. In this configuration, the formate solution could be obtained at the anode because the HCOO− ions generated in the cathode are transferred to the anode side via the AEM. They even obtained higher jformate up to 600 mA cm−2 with a formate concentration of 10.8 g L−1 at a cell potential of 4.7 V. When AEM is used in a zero-gap type electrolyzer for formate production, the cathodic GDE flooding could be significantly reduced because HCOO− moves to the anode through AEM, and the crossover of water and the migration of cations (K+, Na+, etc.) from the anode is almost completely prevented.

3. Reactor Design for CO2RR to Pure Formic Acid

3.1. Three-Compartment Configurations

While the research and development in GDE and zero-gap designs have resulted in remarkable advances in both faradaic efficiency and current density for formate production, these devices still have a crucial challenge to overcome. The product obtained from these reactors (GDE and zero-gap types) consists of HCOO− mixed with other impurity ions such as K+, HCO3−, OH−, and so on. This mixture is required to be separated and acidified to obtain formic acid solutions, which require a considerable amount of energy and cost [19,23,38,39,58]. Zhu et al. reported that the additional costs associated with downstream purification and concentration, which greatly affect the economic viability of liquid products. This emphasizes the necessity of achieving high-purity and high-concentration liquid products directly from CO2 electrolyzers [37].
Therefore, the demand for technologies and devices for direct CO2 reduction to formic acid has increased. The utilization of an additional compartment of solid-state electrolyte (SSE) in a 3-compartment reactor design presents a promising approach for the direct recovery of pure formic acid from CO2 reduction as shown in Figure 7 [23,26,38,39]. In this design, the GDEs are employed on both the cathode and anode sides, which are in contact with an anion exchange membrane (AEM) and a cation exchange membrane (CEM), respectively. At the cathode, CO2 reacts with water (H2O) generating formate (HCOO−) and hydroxide (OH−) anions:
CO2 + H2O + 2e− → HCOO− + OH−
Simultaneously, the oxidation of water occurs at the anode supplied with deionized water, humidified H2, or acidic solution, forming oxygen gas and protons (H+):
2H2O → 4H+ + 4e− + O2
Both the HCOO− and OH− ions migrate through the AEM into the center compartment where they meet the H+ ions produced from the anode compartment which pass through the CEM. In the center compartment, ionic recombination occurs, leading to the formation of HCOOH and H2O:
HCOO− + H+ → HCOOH
OH− + H+ → H2O
The produced pure HCOOH in the center compartment can be recovered by passing deionized water or a humidified N2 stream through the porous SSE layer.
Side reactions that can occur on the cathode [26]:
CO2 + H2O + 2e− → CO + OH−
2H2O + 2e− → H2 + 2OH−
CO2 + OH− → HCO3−
The bicarbonate ion (HCO3−) can move to the central compartment through the AEM where it reacts with protons produced on the anode to produce CO2:
HCO3− + H+ → CO2 + H2O
Formic acid oxidation reaction that can occur on the anode [26]:
2HCOOH + O2 → 2CO2 + 2H2O
The 3-compartment cell design requires thin spacing in the central compartment and a high-conductivity SSE to minimize the cell IR drop. It is important to note that the conductivity of aqueous formic acid alone is relatively low, ranging between 5 and 10 mS cm−1 for formic acid concentrations of 5 to 20 wt% [26]. Therefore, the choice of a high-conductivity SSE is crucial to ensure efficient ionic transport and minimize energy losses within the electrolyzer system. Yang et al. investigated the ionic conductivity of four types of ion exchange resin including Amberlite® IR120, Amberlite® IRN77, Dowex® 50WX2, and Duolite C433 in water and in 5, 10, 15, and 20 wt% formic acid solutions [26]. The results of the study indicated that the use of cation ion exchange resins as SSE materials led to a significant increase in ionic conductivity compared to aqueous formic acid alone. The ion exchange resin/formic acid matrix mixtures exhibited an enhancement in ionic conductivity by a factor of approximately 6–10 compared to formic acid solutions alone. Among the SSEs tested, hydrogen-form sulfonic acid resins such as Amberlite® IR120 and Dowex® 50WX2 demonstrated high ionic conductivities. However, Dowex® 50WX2, with its fine particle size range of 100–200 mesh (75–150 μm), showed a notable pressure drop in the center flow compartment during evaluation.

3.2. Strategies for High-Purity Formic Acid Recovery

Several studies used three-compartment reactor configurations for continuous CO2 electroreduction to recover high-purity HCOOH solution (Table 3) [23,26,38,39]. Yang et al. introduced a new approach by incorporating an acidic center compartment in their system, allowing for the direct production of formic acid instead of formate salts [26]. In this configuration, only deionized (DI) water is introduced into the center flow compartment to recover the formic acid product from the cell. The cell design included an anode compartment, a center compartment containing a cation exchange SSE enclosed by a CEM (Nafion®) on the anode side and an AEM (Sustanion™) on the cathode side, and a cathode compartment with Sn-based GDE.
The details of the configuration of their cell assembly are illustrated and summarized in Figure 8a and Table 4. They investigated the cell performances with a different flow rate of DI water in the center compartment and various ion exchange resins for the center compartment. In addition, they compared two modes of cell operation, center compartment single-pass, and recirculation modes, and found that the single-pass mode was preferred due to differences in faradaic efficiency. The study achieved a high FE HCOOH of up to 94% at a current density of 140 mA cm−2 during 142 h or operation at a cell voltage of about 3.5 V. The HCOOH product concentration reached up to 9.4 wt% (Figure 8b). These results demonstrate the potential of the three-compartment reactor configuration for the continuous production of high-purity formic acid with improved efficiency and concentration.
Yang et al. also demonstrated the long-term stability of pure formic acid production by 1000 h operation of the 3-compartment design at industrially relevant current densities [39]. The electrolyzer (Figure 9a) can be operated at a current density as high as 300 mA cm−2 with a cell voltage below 4.0 V, and no significant change in FEHCOOH was observed at current densities between 100 and 250 mA cm−2. Typically, higher DI water flow rates led to higher FEHCOOH but lower HCOOH concentrations as shown in Figure 9b. The electrolyzer directly produced a 6.03–12.92 wt% formic acid product at FEHCOOH range of 73.0–91.3%, depending on the operating conditions. The highest formic acid FE of 91.3% was achieved using a center compartment DI water flow rate of 0.17 mL min−1 with an HCOOH concentration of 6.03 wt%. In addition, they confirmed that the FE HCOOH was mostly above 70% and HCOOH concentration above 11 wt% during the 1000 h long-term test at 200 mA cm−2 (Figure 9c).
Xia and Wang’s group also demonstrated the production of high-purity formic acid using the 3-compartment cell design using an ultrathin two-dimensional Bi (2D-Bi) catalyst for CO2RR to HCOOH [38]. They used a porous styrene–divinylbenzene (SVB) copolymer as SSE consisting of sulfonic acid functional groups for H+ conduction. They obtained a 0.112 M (~0.5 wt%) pure HCOOH solution with a peak FEHCOOH of 93.1% and a partial current density of 32.1 mA cm−2 at 3.08 V and at a DI water flowrate into the center compartment of 12 mL h−1.
However, they pointed out a few challenges that remain impeding its practical applications: (i) the concentration of the product was limited due to the use of DI water in the SSE layer; (ii) the rate of product generation was not sufficiently high to meet the demands of industrial applications; (iii) the system still relied on the use of a liquid electrolyte on the anode side for water oxidation [23]. To achieve a high concentration of formic acid solutions, it is necessary to reduce the flow rate of DI water. However, it should be noted that increasing the concentration of formic acid in the SSE layer can lead to a significant decrease in faradaic efficiency. This is because higher formic acid concentrations can increase the rate of the reverse reaction and result in increased crossover to the anode. In this concern, they suggested an all-solid-state reactor, where an inert gas (N2) flow is supplied to recover high-purity HCOOH vapor from the center compartment instead of DI water. High-purity HCOOH can be obtained by a simple cold condensation process. As a result, they accomplished HCOOH concentration up to 12.1 M (~49.3 wt%) using 10 sccm of humidified N2 gas [38], and nearly 100 wt% pure HCOOH using 20 sccm of dry N2 gas [23] instead of DI water flow to recover the generated HCOOH. This alternative approach of utilizing an all-solid-state reactor with N2 gas flow offers several advantages. It enables higher formic acid concentrations without sacrificing faradaic efficiency, as the dilution effect from DI water is eliminated. Additionally, the recovery of high-purity formic acid vapor through a cold condensation process simplifies the product separation step.

3.3. Opportunities and Challenges

The 3-compartment electrolyzer design using SSE offers a promising pathway for the direct production of high-purity formic acid (HCOOH) and represents a significant step towards commercializing CO2RR technologies. One key advantage of the SSE reactor design is its ability to prevent the crossover of cathode-generated carbonate ions [59]. In the typical 2-compartment electrolyzer, hydroxide ions (OH−) generated at the cathode during CO2RR react rapidly with the supplied CO2 to form carbonate (CO32−) or bicarbonate (HCO3−) ions, which move across the AEM to the anodic side, resulting in carbon loss. On the other hand, in the SSE reactor design, the CO32− or HCO3− ions migrate through AEM into the center compartment and then be recombined with protons from the anode to form CO2 gas again, which could be easily recirculated to the cathodic reactant.
While the SSE approach offers advantages in terms of product separation energy and cost, it introduces the challenge of increased ohmic resistance, which can reduce the energy efficiency of CO2RR. Thus, the energy penalty by increased ohmic resistance should be compared with the energy required to separate the liquid fuels from the electrolyte. It is possible to reduce the resistance of the solid-state electrolyte (SSE) by engineering ultra-thin SSE layers [38]. This can be achieved by decreasing the thickness of the SSE, which would enhance the ion conductivity within the solid electrolyte. Additionally, improving the contact interface between the SSE layer and the membranes can also contribute to reducing resistance [37]. Beyond the conventional formate production technology, there was remarkable progress in high-purity formic acid production via adopting a 3-compartment electrolyzer using SSE, which exhibited nearly 100 wt% pure formic acid. However, it is important to note that high-purity formic acid has not yet been produced at commercially relevant partial current densities (>200 mA cm−2). This highlights the need for further research and development efforts to optimize the SSE reactor design, enhance the current density, and improve the energy efficiency to make high-purity formic acid production economically viable at larger scales. Figure 10 illustrates the current status of high-purity formic acid production, indicating that there is still room for improvement in achieving commercially relevant partial current densities while maintaining high purity. Future research should aim to overcome these challenges and explore innovative strategies to enhance the performance and scalability of the SSE-based 3-compartment electrolyzer for efficient and commercially viable formic acid production.

4. Summary and Outlooks

In summary, recent research has been reviewed in reactor design for formic acid production to address the challenges of impurity and low concentration in conventional CO2RR reactors. Early studies focused on producing formate in aqueous solutions using 3-electrode and H-type cells. However, the limited solubility of CO2 in the aqueous catholyte restricted the current density and hindered the large-scale application of CO2RR. To overcome this limitation, researchers have introduced reactor designs that ensure sufficient CO2 supply to the catalyst. GDE-type reactors and zero-gap electrolyzers have shown significant improvements in formate current density, reaching up to 930 mA cm−2, and achieving concentrated formate products of up to 33.7 wt%. However, these products contain impurity ions, requiring downstream processes such as separation and acidification to obtain pure formic acid. One promising approach to obtaining pure formic acid is the incorporation of an additional SSE compartment between the anode and cathode. This 3-compartment electrolyzer has demonstrated the production of nearly 100 wt% pure formic acid. However, high-purity formic acid has not yet been produced at commercially relevant partial current densities.
Future research should focus on developing cost-effective and scalable technologies for formic acid production from CO2RR. This includes exploring catalyst materials that are abundant, low-cost, and highly efficient. Additionally, optimizing reactor designs and process parameters to maximize productivity and minimize energy consumption will be crucial for cost-effective large-scale production. To enhance the economic viability of the liquid products, it is crucial to achieve high-purity and high-concentration formic acid directly from the CO2 electrolyzer. This would eliminate or minimize the need for extensive downstream processing, reducing energy consumption, operational costs, and capital investments associated with purification and concentration steps. Future progress in this approach also provides a potential route to store H2 in liquid HCOOH and could be extended to the production of C2+ liquid fuels. This review contributes to the advancement of electrolyzer technology, bringing us closer to large-scale applications of CO2RR for the production of high-purity formic acid and other liquid fuels in the future.

Author Contributions

Conceptualization, K.T.P. and Y.K.; investigation, K.T.P., Y.K., T.K. and K.Y.J.; data curation, Y.K., T.K. and K.Y.J.; writing—original draft preparation, K.T.P. and Y.K.; writing—review and editing, K.T.P. and Y.K.; visualization, K.T.P.; supervision, K.T.P.; funding acquisition, K.T.P. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Konkuk University (2022-A019-0009).

Data Availability Statement

The data presented in this study are available in the corresponding references listed.

Acknowledgments

This paper was supported by Konkuk University in 2023.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Duarah, P.; Haldar, D.; Yadav, V.S.K.; Purkait, M.K. Progress in the electrochemical reduction of CO2 to formic acid: A review on current trends and future prospects. J. Environ. Chem. Eng. 2021, 9, 106394. [Google Scholar] [CrossRef]
  2. Zarandi, R.F.; Rezaei, B.; Ghaziaskar, H.S.; Ensafi, A.A. Electrochemical reduction of CO2 to ethanol using copper nanofoam electrode and 1-butyl-3-methyl-imidazolium bromide as the homogeneous co-catalyst. J. Environ. Chem. Eng. 2019, 7, 103141. [Google Scholar] [CrossRef]
  3. Jeon, Y.E.; Ko, Y.N.; Kim, J.; Choi, H.; Lee, W.; Kim, Y.E.; Lee, D.; Kim, H.Y.; Park, K.T. Selective production of ethylene from CO2 over CuAg tandem electrocatalysts. J. Ind. Eng. Chem. 2022, 116, 191–198. [Google Scholar] [CrossRef]
  4. Salimijazi, F.; Kim, J.; Schmitz, A.M.; Grenville, R.; Bocarsly, A.; Barstow, B. Constraints on the Efficiency of Engineered Electromicrobial Production. Joule 2020, 4, 2101–2130. [Google Scholar] [CrossRef]
  5. Gunasekar, G.H.; Park, K.; Jung, K.-D.; Yoon, S. Recent developments in the catalytic hydrogenation of CO2 to formic acid/formate using heterogeneous catalysts. Inorg. Chem. Front. 2016, 3, 882–895. [Google Scholar] [CrossRef]
  6. Ma, Z.; Wan, T.; Zhang, D.; Yuwono, J.A.; Tsounis, C.; Jiang, J.; Chou, Y.-H.; Lu, X.; Kumar, P.V.; Ng, Y.H.; et al. Atomically Dispersed Cu Catalysts on Sulfide-Derived Defective Ag Nanowires for Electrochemical CO2 Reduction. ACS Nano 2023, 17, 2387–2398. [Google Scholar] [CrossRef]
  7. Jouny, M.; Luc, W.; Jiao, F. General Techno-Economic Analysis of CO2 Electrolysis Systems. Ind. Eng. Chem. Res. 2018, 57, 2165–2177. [Google Scholar] [CrossRef]
  8. Gu, J.; Hsu, C.-S.; Bai, L.; Chen, H.M.; Hu, X. Atomically dispersed Fe3+ sites catalyze efficient CO2 electroreduction to CO. Science 2019, 364, 1091–1094. [Google Scholar] [CrossRef]
  9. Zheng, T.; Jiang, K.; Ta, N.; Hu, Y.; Zeng, J.; Liu, J.; Wang, H. Large-Scale and Highly Selective CO2 Electrocatalytic Reduction on Nickel Single-Atom Catalyst. Joule 2019, 3, 265–278. [Google Scholar] [CrossRef]
  10. Higgins, D.; Hahn, C.; Xiang, C.; Jaramillo, T.F.; Weber, A.Z. Gas-Diffusion Electrodes for Carbon Dioxide Reduction: A New Paradigm. ACS Energy Lett. 2018, 4, 317–324. [Google Scholar] [CrossRef]
  11. Lee, J.; Lee, W.; Ryu, K.H.; Park, J.; Lee, H.; Lee, J.H.; Park, K.T. Catholyte-free electroreduction of CO2 for sustainable production of CO: Concept, process development, techno-economic analysis, and CO2 reduction assessment. Green Chem. 2021, 23, 2397–2410. [Google Scholar] [CrossRef]
  12. Lee, S.; Eun Jeon, Y.; Lee, S.; Lee, W.; Kim, S.; Choi, J.; Park, J.; Woo Han, J.; Na Ko, Y.; Eun Kim, Y.; et al. Deciphering Mass Transport Behavior in Membrane Electrode Assembly by Manipulating Porous Structures of Atomically Dispersed Metal-Nx Catalysts for High-Efficiency Electrochemical CO2 Conversion. Chem. Eng. J. 2023, 464, 142593. [Google Scholar] [CrossRef]
  13. Eppinger, J.; Huang, K.-W. Formic Acid as a Hydrogen Energy Carrier. ACS Energy Lett. 2016, 2, 188–195. [Google Scholar] [CrossRef]
  14. Wang, L.; Nitopi, S.; Wong, A.B.; Snider, J.L.; Nielander, A.C.; Morales-Guio, C.G.; Orazov, M.; Higgins, D.C.; Hahn, C.; Jaramillo, T.F. Electrochemically converting carbon monoxide to liquid fuels by directing selectivity with electrode surface area. Nat. Catal. 2019, 2, 702–708. [Google Scholar] [CrossRef]
  15. Mardini, N.; Bicer, Y. Direct synthesis of formic acid as hydrogen carrier from CO2 for cleaner power generation through direct formic acid fuel cell. Int. J. Hydrog. Energy 2021, 46, 13050–13060. [Google Scholar] [CrossRef]
  16. Moret, S.; Dyson, P.J.; Laurenczy, G. Direct synthesis of formic acid from carbon dioxide by hydrogenation in acidic media. Nat. Commun. 2014, 5, 4017. [Google Scholar] [CrossRef]
  17. Wang, W.-H.; Himeda, Y.; Muckerman, J.T.; Manbeck, G.F.; Fujita, E. CO2 Hydrogenation to Formate and Methanol as an Alternative to Photo- and Electrochemical CO2 Reduction. Chem. Rev. 2015, 115, 12936–12973. [Google Scholar] [CrossRef]
  18. Álvarez, A.; Bansode, A.; Urakawa, A.; Bavykina, A.V.; Wezendonk, T.A.; Makkee, M.; Gascon, J.; Kapteijn, F. Challenges in the Greener Production of Formates/Formic Acid, Methanol, and DME by Heterogeneously Catalyzed CO2Hydrogenation Processes. Chem. Rev. 2017, 117, 9804–9838. [Google Scholar] [CrossRef]
  19. Orella, M.J.; Brown, S.M.; Leonard, M.E.; Román-Leshkov, Y.; Brushett, F.R. A General Technoeconomic Model for Evaluating Emerging Electrolytic Processes. Energy Technol. 2019, 8, 1900994. [Google Scholar] [CrossRef]
  20. Mellmann, D.; Sponholz, P.; Junge, H.; Beller, M. Formic acid as a hydrogen storage material—Development of homogeneous catalysts for selective hydrogen release. Chem. Soc. Rev. 2016, 45, 3954–3988. [Google Scholar] [CrossRef]
  21. Liu, L.-X.; Zhou, Y.; Chang, Y.-C.; Zhang, J.-R.; Jiang, L.-P.; Zhu, W.; Lin, Y. Tuning Sn3O4 for CO2 reduction to formate with ultra-high current density. Nano Energy 2020, 77, 105296. [Google Scholar] [CrossRef]
  22. Kumar, B.; Atla, V.; Brian, J.P.; Kumari, S.; Nguyen, T.Q.; Sunkara, M.; Spurgeon, J.M. Reduced SnO2 Porous Nanowires with a High Density of Grain Boundaries as Catalysts for Efficient Electrochemical CO2-into-COOH Conversion. Angew. Chem. Int. Ed. Engl. 2017, 56, 3645–3649. [Google Scholar] [CrossRef] [PubMed]
  23. Fan, L.; Xia, C.; Zhu, P.; Lu, Y.; Wang, H. Electrochemical CO(2) reduction to high-concentration pure formic acid solutions in an all-solid-state reactor. Nat. Commun. 2020, 11, 3633. [Google Scholar] [CrossRef]
  24. Liang, X.-D.; Tian, N.; Hu, S.-N.; Zhou, Z.-Y.; Sun, S.-G. Recent advances of bismuth-based electrocatalysts for CO2 reduction: Strategies, mechanism and applications. Mater. Rep. Energy 2023, 3, 100191. [Google Scholar] [CrossRef]
  25. Shin, H.; Hansen, K.U.; Jiao, F. Techno-economic assessment of low-temperature carbon dioxide electrolysis. Nat. Sustain. 2021, 4, 911–919. [Google Scholar] [CrossRef]
  26. Yang, H.; Kaczur, J.J.; Sajjad, S.D.; Masel, R.I. Electrochemical conversion of CO2 to formic acid utilizing Sustainion™ membranes. J. CO2 Util. 2017, 20, 208–217. [Google Scholar] [CrossRef]
  27. Choi, S.Y.; Jeong, S.K.; Kim, H.J.; Baek, I.-H.; Park, K.T. Electrochemical Reduction of Carbon Dioxide to Formate on Tin–Lead Alloys. ACS Sustain. Chem. Eng. 2016, 4, 1311–1318. [Google Scholar] [CrossRef]
  28. Kim, Y.E.; Lee, W.; Ko, Y.N.; Park, J.E.; Tan, D.; Hong, J.; Jeon, Y.E.; Oh, J.; Park, K.T. Role of Binder in Cu2O Gas Diffusion Electrodes for CO2 Reduction to C2+ Products. ACS Sustain. Chem. Eng. 2022, 10, 11710–11718. [Google Scholar] [CrossRef]
  29. Tan, D.; Lee, W.; Kim, Y.E.; Ko, Y.N.; Youn, M.H.; Jeon, Y.E.; Hong, J.; Jeong, S.K.; Park, K.T. SnO2/ZnO Composite Hollow Nanofiber Electrocatalyst for Efficient CO2 Reduction to Formate. ACS Sustain. Chem. Eng. 2020, 8, 10639–10645. [Google Scholar] [CrossRef]
  30. Tan, D.; Lee, W.; Kim, Y.E.; Ko, Y.N.; Youn, M.H.; Jeon, Y.E.; Hong, J.; Park, J.E.; Seo, J.; Jeong, S.K.; et al. In-Bi Electrocatalyst for the Reduction of CO(2) to Formate in a Wide Potential Window. ACS Appl. Mater. Interfaces 2022, 14, 28890–28899. [Google Scholar] [CrossRef]
  31. Tan, D.; Lee, W.; Park, K.T.; Jeon, Y.E.; Hong, J.; Ko, Y.N.; Kim, Y.E. Promoting CO2 reduction to formate selectivity on indium-doped tin oxide nanowires. Appl. Surf. Sci. 2023, 613, 155944. [Google Scholar] [CrossRef]
  32. Hu, H.; Gui, L.; Zhou, W.; Sun, J.; Xu, J.; Wang, Q.; He, B.; Zhao, L. Partially reduced Sn/SnO2 porous hollow fiber: A highly selective, efficient and robust electrocatalyst towards carbon dioxide reduction. Electrochim. Acta 2018, 285, 70–77. [Google Scholar] [CrossRef]
  33. Lv, W.; Zhou, J.; Bei, J.; Zhang, R.; Wang, L.; Xu, Q.; Wang, W. Electrodeposition of nano-sized bismuth on copper foil as electrocatalyst for reduction of CO2 to formate. Appl. Surf. Sci. 2017, 393, 191–196. [Google Scholar] [CrossRef]
  34. Wu, Z.; Wu, H.; Cai, W.; Wen, Z.; Jia, B.; Wang, L.; Jin, W.; Ma, T. Engineering Bismuth–Tin Interface in Bimetallic Aerogel with a 3D Porous Structure for Highly Selective Electrocatalytic CO2 Reduction to HCOOH. Angew. Chem. 2021, 133, 12662–12667. [Google Scholar] [CrossRef]
  35. Bai, X.; Chen, W.; Zhao, C.; Li, S.; Song, Y.; Ge, R.; Wei, W.; Sun, Y. Exclusive Formation of Formic Acid from CO2 Electroreduction by a Tunable Pd-Sn Alloy. Angew. Chem. 2017, 129, 12387–12391. [Google Scholar] [CrossRef]
  36. Luc, W.; Collins, C.; Wang, S.; Xin, H.; He, K.; Kang, Y.; Jiao, F. Ag–Sn Bimetallic Catalyst with a Core–Shell Structure for CO2 Reduction. J. Am. Chem. Soc. 2017, 139, 1885–1893. [Google Scholar] [CrossRef]
  37. Zhu, P.; Wang, H. High-purity and high-concentration liquid fuels through CO2 electroreduction. Nat. Catal. 2021, 4, 943–951. [Google Scholar] [CrossRef]
  38. Xia, C.; Zhu, P.; Jiang, Q.; Pan, Y.; Liang, W.; Stavitski, E.; Alshareef, H.N.; Wang, H. Continuous production of pure liquid fuel solutions via electrocatalytic CO2 reduction using solid-electrolyte devices. Nat. Energy 2019, 4, 776–785. [Google Scholar] [CrossRef]
  39. Yang, H.; Kaczur, J.J.; Sajjad, S.D.; Masel, R.I. Performance and long-term stability of CO2 conversion to formic acid using a three-compartment electrolyzer design. J. CO2 Util. 2020, 42, 101349. [Google Scholar] [CrossRef]
  40. Daiyan, R.; Lu, X.; Saputera, W.H.; Ng, Y.H.; Amal, R. Highly Selective Reduction of CO2 to Formate at Low Overpotentials Achieved by a Mesoporous Tin Oxide Electrocatalyst. ACS Sustain. Chem. Eng. 2018, 6, 1670–1679. [Google Scholar] [CrossRef]
  41. Hori, Y. Electrochemical CO2 Reduction on Metal Electrodes. In Modern Aspects of Electrochemistry; Springer: New York, NY, USA, 2008; pp. 89–189. [Google Scholar] [CrossRef]
  42. Song, J.; Song, H.; Kim, B.; Oh, J. Towards Higher Rate Electrochemical CO2 Conversion: From Liquid-Phase to Gas-Phase Systems. Catalysts 2019, 9, 224. [Google Scholar] [CrossRef]
  43. Verma, S.; Lu, X.; Ma, S.; Masel, R.I.; Kenis, P.J.A. The effect of electrolyte composition on the electroreduction of CO2 to CO on Ag based gas diffusion electrodes. Phys. Chem. Chem. Phys. 2016, 18, 7075–7084. [Google Scholar] [CrossRef] [PubMed]
  44. Kutz, R.B.; Chen, Q.; Yang, H.; Sajjad, S.D.; Liu, Z.; Masel, I.R. Sustainion Imidazolium-Functionalized Polymers for Carbon Dioxide Electrolysis. Energy Technol. 2017, 5, 929–936. [Google Scholar] [CrossRef]
  45. Dinh, C.-T.; García de Arquer, F.P.; Sinton, D.; Sargent, E.H. High Rate, Selective, and Stable Electroreduction of CO2 to CO in Basic and Neutral Media. ACS Energy Lett. 2018, 3, 2835–2840. [Google Scholar] [CrossRef]
  46. Fan, T.; Ma, W.; Xie, M.; Liu, H.; Zhang, J.; Yang, S.; Huang, P.; Dong, Y.; Chen, Z.; Yi, X. Achieving high current density for electrocatalytic reduction of CO2 to formate on bismuth-based catalysts. Cell Rep. Phys. Sci. 2021, 2, 100353. [Google Scholar] [CrossRef]
  47. Grigioni, I.; Sagar, L.K.; Li, Y.C.; Lee, G.; Yan, Y.; Bertens, K.; Miao, R.K.; Wang, X.; Abed, J.; Won, D.H.; et al. CO2 Electroreduction to Formate at a Partial Current Density of 930 mA cm–2 with InP Colloidal Quantum Dot Derived Catalysts. ACS Energy Lett. 2020, 6, 79–84. [Google Scholar] [CrossRef]
  48. Li, J.; Jiao, J.; Zhang, H.; Zhu, P.; Ma, H.; Chen, C.; Xiao, H.; Lu, Q. Two-Dimensional SnO2 Nanosheets for Efficient Carbon Dioxide Electroreduction to Formate. ACS Sustain. Chem. Eng. 2020, 8, 4975–4982. [Google Scholar] [CrossRef]
  49. Lu, X.; Leung, D.Y.C.; Wang, H.; Xuan, J. A high performance dual electrolyte microfluidic reactor for the utilization of CO2. Appl. Energy 2017, 194, 549–559. [Google Scholar] [CrossRef]
  50. Pavesi, D.; van de Poll, R.C.J.; Krasovic, J.L.; Figueiredo, M.; Gruter, G.-J.M.; Koper, M.T.M.; Schouten, K.J.P. Cathodic Disintegration as an Easily Scalable Method for the Production of Sn- and Pb-Based Catalysts for CO2 Reduction. ACS Sustain. Chem. Eng. 2020, 8, 15603–15610. [Google Scholar] [CrossRef]
  51. Díaz-Sainz, G.; Alvarez-Guerra, M.; Solla-Gullón, J.; García-Cruz, L.; Montiel, V.; Irabien, A. CO2 electroreduction to formate: Continuous single-pass operation in a filter-press reactor at high current densities using Bi gas diffusion electrodes. J. CO2 Util. 2019, 34, 12–19. [Google Scholar] [CrossRef]
  52. Wang, Z.; Qi, R.; Liu, D.; Zhao, X.; Huang, L.; Chen, S.; Chen, Z.; Li, M.; You, B.; Pang, Y.; et al. Exfoliated Ultrathin ZnIn(2) S(4) Nanosheets with Abundant Zinc Vacancies for Enhanced CO(2) Electroreduction to Formate. ChemSusChem 2021, 14, 852–859. [Google Scholar] [CrossRef]
  53. Gong, Q.; Ding, P.; Xu, M.; Zhu, X.; Wang, M.; Deng, J.; Ma, Q.; Han, N.; Zhu, Y.; Lu, J.; et al. Structural defects on converted bismuth oxide nanotubes enable highly active electrocatalysis of carbon dioxide reduction. Nat. Commun. 2019, 10, 2807. [Google Scholar] [CrossRef]
  54. Lee, W.; Kim, Y.E.; Youn, M.H.; Jeong, S.K.; Park, K.T. Catholyte-Free Electrocatalytic CO2 Reduction to Formate. Angew. Chem. Int. Ed. Engl. 2018, 57, 6883–6887. [Google Scholar] [CrossRef]
  55. Díaz-Sainz, G.; Alvarez-Guerra, M.; Solla-Gullón, J.; García-Cruz, L.; Montiel, V.; Irabien, A. Gas–liquid–solid reaction system for CO2 electroreduction to formate without using supporting electrolyte. AIChE J. 2020, 66, e16299. [Google Scholar] [CrossRef]
  56. Díaz-Sainz, G.; Alvarez-Guerra, M.; Ávila-Bolívar, B.; Solla-Gullón, J.; Montiel, V.; Irabien, A. Improving trade-offs in the figures of merit of gas-phase single-pass continuous CO2 electrocatalytic reduction to formate. Chem. Eng. J. 2021, 405, 126965. [Google Scholar] [CrossRef]
  57. Díaz-Sainz, G.; Alvarez-Guerra, M.; Irabien, A. Continuous electroreduction of CO2 towards formate in gas-phase operation at high current densities with an anion exchange membrane. J. CO2 Util. 2022, 56, 101822. [Google Scholar] [CrossRef]
  58. Bushuyev, O.S.; De Luna, P.; Dinh, C.T.; Tao, L.; Saur, G.; van de Lagemaat, J.; Kelley, S.O.; Sargent, E.H. What Should We Make with CO2 and How Can We Make It? Joule 2018, 2, 825–832. [Google Scholar] [CrossRef]
  59. Xing, Z.; Hu, L.; Ripatti, D.S.; Hu, X.; Feng, X. Enhancing carbon dioxide gas-diffusion electrolysis by creating a hydrophobic catalyst microenvironment. Nat. Commun. 2021, 12, 136. [Google Scholar] [CrossRef]
Catalysts 13 00955 g001 550
Figure 1. Carbon-neutral cycles of produced formic acid via CO2RR using renewable electricity.
Figure 1. Carbon-neutral cycles of produced formic acid via CO2RR using renewable electricity.
Catalysts 13 00955 g001
Catalysts 13 00955 g002 550
Figure 2. Schematic diagram of the electrocatalytic CO2 reduction (CO2RR) to formate in an H-type cell reaction system (Reprinted with permission from reference [27]. Copyright 2016 American Chemical Society).
Figure 2. Schematic diagram of the electrocatalytic CO2 reduction (CO2RR) to formate in an H-type cell reaction system (Reprinted with permission from reference [27]. Copyright 2016 American Chemical Society).
Catalysts 13 00955 g002
Catalysts 13 00955 g003 550
Figure 3. The faradaic efficiency and current density of formate generation on the Sn–Pb alloys in an H-type cell at −1.36 V (vs. RHE) compared with Sn and Pb (Reprinted with permission from reference [27]. Copyright 2016 American Chemical Society).
Figure 3. The faradaic efficiency and current density of formate generation on the Sn–Pb alloys in an H-type cell at −1.36 V (vs. RHE) compared with Sn and Pb (Reprinted with permission from reference [27]. Copyright 2016 American Chemical Society).
Catalysts 13 00955 g003
Catalysts 13 00955 g004 550
Figure 4. (a) Faradaic efficiency, (b) current density, (c) electrochemical surface area (ECSA), and (d) current stability of the SnO2/ZnO composite HNF catalyst for formate synthesis compared with SnO2 HNF and commercial SnO2 nanoparticles (Reprinted with permission from reference [29]. Copyright 2020 American Chemical Society).
Figure 4. (a) Faradaic efficiency, (b) current density, (c) electrochemical surface area (ECSA), and (d) current stability of the SnO2/ZnO composite HNF catalyst for formate synthesis compared with SnO2 HNF and commercial SnO2 nanoparticles (Reprinted with permission from reference [29]. Copyright 2020 American Chemical Society).
Catalysts 13 00955 g004
Catalysts 13 00955 g005 550
Figure 5. Electrochemical CO2 reduction systems using gaseous CO2 feed: (a) GDE-catholyte type and (b) zero-gap type cells.
Figure 5. Electrochemical CO2 reduction systems using gaseous CO2 feed: (a) GDE-catholyte type and (b) zero-gap type cells.
Catalysts 13 00955 g005
Catalysts 13 00955 g006 550
Figure 6. The schematic illustration for the problem of the GDE flooding in the zero-gap type electrolyzer by electro-wetting with electrolysis time.
Figure 6. The schematic illustration for the problem of the GDE flooding in the zero-gap type electrolyzer by electro-wetting with electrolysis time.
Catalysts 13 00955 g006
Catalysts 13 00955 g007 550
Figure 7. The schematic illustration of the electrolyzer configuration with solid-state electrolyte (SSE) to produce pure formic acid.
Figure 7. The schematic illustration of the electrolyzer configuration with solid-state electrolyte (SSE) to produce pure formic acid.
Catalysts 13 00955 g007
Catalysts 13 00955 g008 550
Figure 8. (a) The schematic illustration of 3-compartment cell configuration and (b) the cell performance using a titanium flow field, IrO2 coated titanium mesh anode, and Nafion® 324 (Reprinted with permission from reference [26]. Copyright 2017 Elsevier).
Figure 8. (a) The schematic illustration of 3-compartment cell configuration and (b) the cell performance using a titanium flow field, IrO2 coated titanium mesh anode, and Nafion® 324 (Reprinted with permission from reference [26]. Copyright 2017 Elsevier).
Catalysts 13 00955 g008
Catalysts 13 00955 g009 550
Figure 9. (a) A photo of an assembled electrolyzer (left) and the exploded view (right) (1: cathode flow field and current collector; 2: cathode GDE; 3, 5, 8, 10, 12: PTFE gaskets; 4: anion exchange membrane; 6: ion exchange media; 7: center compartment; 9: cation exchange membrane; 11: anode GDE; 13: O-rings; 14: anode flow field and current collector); (b) the HCOOH concentration and FEHCOOH as a function of the center compartment DI water flow rate; and (c) the HCOOH concentration and FEHCOOH during 1000 h operation (Reprinted with permission from reference [39]. Copyright 2020 Elsevier).
Figure 9. (a) A photo of an assembled electrolyzer (left) and the exploded view (right) (1: cathode flow field and current collector; 2: cathode GDE; 3, 5, 8, 10, 12: PTFE gaskets; 4: anion exchange membrane; 6: ion exchange media; 7: center compartment; 9: cation exchange membrane; 11: anode GDE; 13: O-rings; 14: anode flow field and current collector); (b) the HCOOH concentration and FEHCOOH as a function of the center compartment DI water flow rate; and (c) the HCOOH concentration and FEHCOOH during 1000 h operation (Reprinted with permission from reference [39]. Copyright 2020 Elsevier).
Catalysts 13 00955 g009
Catalysts 13 00955 g010 550
Figure 10. Comparison of the concentration of formate (HCOO−) and formic acid (HCOOH) products reported in the literature via CO2RR from GDE, zero-gap, and 3-compartment reactors as a function of partial current density [23,26,38,39,51,54,55,56,57].
Figure 10. Comparison of the concentration of formate (HCOO−) and formic acid (HCOOH) products reported in the literature via CO2RR from GDE, zero-gap, and 3-compartment reactors as a function of partial current density [23,26,38,39,51,54,55,56,57].
Catalysts 13 00955 g010
Table
Table 1. Figures of merits of studies reported in the literature for the CO2RR to formate in terms of reactor type, catalysts of the cathode, electrolytes (for 3-electrode cell) or catholyte (for H-type cell), applied potential (vs. reference electrode), faradaic efficiency, and current density for formate production.
Table 1. Figures of merits of studies reported in the literature for the CO2RR to formate in terms of reactor type, catalysts of the cathode, electrolytes (for 3-electrode cell) or catholyte (for H-type cell), applied potential (vs. reference electrode), faradaic efficiency, and current density for formate production.
Reactor TypeCathodeElectrolyte
(Catholyte)		Potential
(V vs. RHE)		FEformate
(%)		jformate
(mA cm−2)		Reference
3-electrodeSn/SnO2 porous hollow fiber0.1 M KHCO3−0.9582.122.9[32]
Bi on Cu foil0.5 M KHCO3−0.8691.33.08[33]
Bi-Sn0.1 M KHCO3−1.093.99.3[34]
H-typeSn-Pb alloy0.5 M KHCO3−1.3679.845.7[27]
SnO2/ZnO hollow nanofiber0.1 M KHCO3−1.3497.924.9[29]
Pd-Sn alloy/C0.5 M KHCO3−0.4399.6~2[35]
Mesoporous SnO20.1 M KHCO3−1.157510.8[40]
In16Bi84 nano-sphere0.5 M KHCO3−0.9410014.08[30]
AgSn/SnOx (core-shell)0.5 M KHCO3−0.88016[36]
In-doped SnO2 nanowires0.5 M KHCO3−1.04826.02[31]
Table
Table 2. Figures of merits of studies reported in the literature for the CO2RR to formate in terms of reactor type, catalysts of the cathode, type of membrane, applied reduction potential (vs. RHE) or cell potential, faradaic efficiency, and current density for formate production.
Table 2. Figures of merits of studies reported in the literature for the CO2RR to formate in terms of reactor type, catalysts of the cathode, type of membrane, applied reduction potential (vs. RHE) or cell potential, faradaic efficiency, and current density for formate production.
Reactor TypeCathodeMembraneCathodic Potential/Cell Voltage (V)FEformate
(%)		jformate
(mA cm−2)		Concentration of HCOO− (wt%)Reference
GDE-catholyteBi2O2CO3 nanosheetFumasep FAB-PK-130−1.55 (vs. RHE)93930-[46]
InP colloidal quantum dotsAEM−2.6 (vs. RHE)93930-[47]
SnO2 nanosheetSelemion−1.13 (vs. RHE)94.2471-[48]
Pb powder-490352 -[49]
Bi nanosheetNafion® 117−1.18 (vs. RHE)/3.192.483.20.204[51]
ZnIn2S4 nanosheetNafion® 212−1.2 (vs. RHE)94245-[52]
Bi nanotubeSelemion−0.56 (vs. RHE)98170-[53]
Sn/CNafion® 324−2.44 (vs. SHE)98200-[50]
Zero-gapBi/CNafion® 1173.171.732.33.39[55]
Bi/CNafion® 1173.089.240.133.7[56]
Sn nanoparticleNafion® 1152.293.351.74.15[54]
Sn nanoparticleNafion® 1152.277.729.811.62[54]
Bi/CSustainionTM3.691.6274.80.67[57]
Table
Table 3. Figures of merits of studies reported in the literature for the CO2RR to pure formic acid in terms of catalysts of the cathode, type of membranes, the material of SSE, type of feeds for cathode, anode, and SSE, applied cell voltage, faradaic efficiency, current density, and concentration of formic acid.
Table 3. Figures of merits of studies reported in the literature for the CO2RR to pure formic acid in terms of catalysts of the cathode, type of membranes, the material of SSE, type of feeds for cathode, anode, and SSE, applied cell voltage, faradaic efficiency, current density, and concentration of formic acid.
CathodeMembrane (AEM/CEM)SSE MaterialFeedsCell Voltage (V)FEHCOOH
(%)		jHCOOH
(mA cm−2)		Concentration of HCOOH (wt%)Reference
Cathode/AnodeSSE
SnSustanion/
Nafion® 324		Amberlite® IR120Humidified-CO2/H2OH2O3.594131.69.4[26]
2D-BiSustanion/
Nafion® 115		SVB copolymerHumidified-CO2/H2OH2O3.08 93.132.10.51[38]
Humidified-CO2/H2OHumidified-N22.75408049.3
Humidified-CO2/
Humidified-H2		Humidified-N21.3373.3163-
BiPSMIM/
Nafion® 115		SVB copolymerHumidified-CO2/
Humidified-H2		H2O2.1997450~3[23]
Humidified-N21.49408011
Dry N2-~2244~100
Bi2O3Sustanion/
Nafion® 324		Amberlite® IR120Humidified-CO2/H2OH2O3.7691.3182.66.03[39]
Table
Table 4. Formic acid cell assembly configuration summary of Yang et al. group (Reprinted with permission from reference [26]. Copyright 2017 Elsevier).
Table 4. Formic acid cell assembly configuration summary of Yang et al. group (Reprinted with permission from reference [26]. Copyright 2017 Elsevier).
Cathode configurationsCathodePOCO Graphite block with the serpentine flow path
GDE cathodeToray paper, 50% PTFE proofing
GDE catalystSn nanoparticles (99.9%, 60–80 nm, US Research Nanomaterials, Inc.), catalyst layer air atomized onto GDE cathode with varying amounts of PTFE suspension and 5% imidazolium-based ionomer, and 5% carbon nanotubes.
CO2 flowrate20 mL/min, not humidified for ambient temperature operation
Anode configurationsAnode 1POCO Graphite block with the serpentine flow path. The anode was a GDE electrode with a 2 mg cm−2 IrO2 catalyst (99.99%, Alfa Aesar) onto 5% PTFE proofing Toray paper
Anode 2Titanium Grade 2 anode block with the serpentine flow path. The Anode screen having IrO2-based metal oxide coating on expanded titanium (Water Star) was spot welded onto the titanium anode block
Anolyte recirculation rateDI water, 8–12 mL/min
Center flow compartmentIon exchange mediaAmberlite® IR120 strong acid ion exchange resin fill, 620–830 μm beads, and other selected ion exchange resins
Center compartment1 mm thickness, 2.25 cm × 2.25 cm, 0.50 mL (empty), estimated 40% void volume, i.e., 0.2 mL free volume with ion exchange resin
Center compartment framePolycarbonate, the machined flow path for solution flow in/out
DI water feedSelected rate of 0.03 1 mL/min into center flow compartment
Anion membrane Dioxide Materials Sustainion™ X37 imidazolium-based anion exchange membrane:60–80 μm thickness (wet), ion exchange capacity of 1.05 mEq/g (950 EW), membrane conductivity in water, through the plane, of about 60–70 mS cm−1
Cation membranes DuPont Nafion® Membranes Tested: 212, 115, 324
Active geometric area 5 cm2
Cell operating temperature Ambient, 20–25 °C
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Kang, Y.; Kim, T.; Jung, K.Y.; Park, K.T. Recent Progress in Electrocatalytic CO2 Reduction to Pure Formic Acid Using a Solid-State Electrolyte Device. Catalysts 2023, 13, 955. https://doi.org/10.3390/catal13060955

AMA Style

Kang Y, Kim T, Jung KY, Park KT. Recent Progress in Electrocatalytic CO2 Reduction to Pure Formic Acid Using a Solid-State Electrolyte Device. Catalysts. 2023; 13(6):955. https://doi.org/10.3390/catal13060955

Chicago/Turabian Style

Kang, Yeomin, Taekyung Kim, Koo Young Jung, and Ki Tae Park. 2023. "Recent Progress in Electrocatalytic CO2 Reduction to Pure Formic Acid Using a Solid-State Electrolyte Device" Catalysts 13, no. 6: 955. https://doi.org/10.3390/catal13060955

APA Style

Kang, Y., Kim, T., Jung, K. Y., & Park, K. T. (2023). Recent Progress in Electrocatalytic CO2 Reduction to Pure Formic Acid Using a Solid-State Electrolyte Device. Catalysts, 13(6), 955. https://doi.org/10.3390/catal13060955

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.