Effect of Polycondensation Catalyst on Fiber Structure Development in High-Speed Melt Spinning of Poly (Ethylene Terephthalate)
Previous Article in Journal
Lignin Redistribution for Enhancing Barrier Properties of Cellulose-Based Materials
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 11
Issue 12
10.3390/polym11121930
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Carborane-Containing Aromatic Polyimide Films with Ultrahigh Thermo-Oxidative Stability

by
Fulin Liu
1,2,
Guangqiang Fang
3,
Haixia Yang
1,*,
Shiyong Yang
1,*,
Xuezhong Zhang
1 and
Zhijie Zhang
1
1
Laboratory of Advanced Polymer Materials, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100190, China
2
School of Chemical Sciences, University of Chinese Academy of Sciences, Beijing 100049, China
3
Shanghai Institute of Aerospace Systems Engineering, Shanghai 201108, China
*
Authors to whom correspondence should be addressed.
Polymers 2019, 11(12), 1930; https://doi.org/10.3390/polym11121930
Submission received: 28 October 2019 / Revised: 11 November 2019 / Accepted: 12 November 2019 / Published: 22 November 2019
(This article belongs to the Section Polymer Processing and Engineering)
Browse Figures
Versions Notes

Abstract

:
Carborane-containing aromatic polyimide (CPI) films with ultrahigh thermo-oxidative stability at 700 °C have been prepared by casting poly(amic acid) (PAA) resin solution on a glass surface, followed by thermal imidization at elevated temperatures. The PAA solution was prepared by copolymerization of an aromatic dianhydride and an aromatic diamine mixture, including carborane-containing aromatic diamine in an aprotic solvent. The CPI films showed excellent thermo-oxidative stability at 700 °C due to the multilayered protection layers formed on the film surface by thermal conversion of the carborane group into boron oxides. The boron oxide layer enhanced the degradation activation energy and suppressed the direct contact of inner polymer materials with oxygen molecules in a high-temperature environment, acting as a “self-healing” skin layer on the polyimide materials. The CPI-50 film was still flexible and maintained 50% retention of mechanical strength even after thermo-oxidative aging at 700 °C/5 min. The mechanism of thermo-oxidative degradation was proposed.

Graphical Abstract

1. Introduction

Aromatic polyimide films have been extensively utilized in a variety of applications from microelectronic and optoelectronic devices to aerospace industries, owing to its excellent thermal stability, dielectric and electrical insulating performance, mechanical properties, and chemical and radiation resistance [1,2,3,4,5,6,7]. With the rapid development of high-tech fields, polyimide films have also been attempted to be used as gas separation membranes [8,9,10,11], battery separators [12,13,14,15], thermally conductive films [16,17,18], transparent electrodes [19,20,21,22], etc. Although polyimide is one of the most thermal stable polymers, it starts rapid thermal or thermo-oxidative decomposition at the beginning from 500–550 °C and loses most of its original weight at about 600–650 °C, which restricts its application in extreme environments, such as engine culverts in airplanes, nuclear power stations, and submarines. In those circumstances, high temperatures and repeated thermal cycles require thermal and thermos-oxidative stability of materials at elevated temperatures. In order to improve the thermal or thermo-oxidative stability, polyimide films are usually coated with metal or inorganic oxide protection layer or blended with inorganic fillers [23,24,25,26,27]. However, the mismatching of the coefficient of thermal expansion (CTE) between inorganic coatings and polymer matrices might result in serious troubles such as delamination, curl, or crack after harsh heat shocking [28]. Although the addition of inorganic fillers into polymer matrices to form hybrid structures is an effective pathway in enhancing thermo-oxidative stability of polymer materials, the limited filler loadings and the poor miscibility of inorganic fillers and organic matrices are the big issues [26,27,29,30]. Hence, developing intrinsic thermo-oxidative stable polymers is still the desirable pathway.
Incorporating the carborane (C2B10H12) cage structure into the polymer backbone has been found to provide a promising pathway to improve the thermo-oxidative stability of polymer materials due to the reaction of carborane with oxygen atoms to yield a boron oxide layer [31]. The icosahedral carborane structure has two carbon atoms in a symmetrical polyhedral cage, exhibiting three-dimensional aromaticity [32,33,34]. Y.P. Bai et al. synthesized wholly carborane-containing polyesters exhibiting a char yield of 64% in air and 47% in N2 at 700 °C, respectively, much superior to the carborane-free polyesters [35]. Zh. J. Zhang et al. synthesized a series of exactly alternating carborane-siloxane polymers showing excellent thermal stability with char yields of ≥83% both in air at 800 °C and in nitrogen at 1000 °C, respectively [36]. X. D. Jia et al. introduced a meta-carborane structure into the polybenzoxazine main-chain via click reaction showing a 5% weight loss at temperatures above 400 °C and high char yield of 76% in air at 800 °C [37].
In this paper, a series of carborane-containing aromatic polyimide (CPI) films with carborane cage structures in the polymer backbone have been prepared by copolymerization of aromatic dianhydride and a mixture of aromatic diamines, including 1,7-bis(aminophenyl)-meta-carborane. Experimental results indicated that the carborane containing polyimide films demonstrated great thermo-oxidative stability at temperatures of as high as 700 °C. The effect of polyimide structures on the thermal properties have been systematically investigated, and a mechanism of thermo-oxidative degradation was proposed. Combined with the neutron-trapping ability of the boron atoms, the thermal-oxidative stable CPI we reported were potential candidates in nuclear power applications.

2. Materials and Methods

2.1. Materials

3,3′,4,4′-biphenyltetracarboxylic dianhydride (s-BPDA), 4,4′-diaminodiphenyl ether (4,4′-ODA), and 1,4-benzenediamine (PDA) were obtained from Changzhou Sunlight Pharmaceutical Co., Ltd. (Changzhou, China), and dried in a vacuum at 160 °C, 80 °C, 80 °C for 12 h before use, respectively. The 1,7-bis(aminophenyl)-meta-carborane (BACB) was synthesized in our lab, and the details are shown in Scheme S1 in Supporting Information. N-methyl-2-pyrrolidinone (NMP) was purchased from J&K Scientific Co. Ltd. (Beijing, China), then distilled under reduced pressure with CaH2 and stored with 4Å molecular sieves before use. Other solvents and reagents were directly used without further purification.

2.2. Synthesis of the Carborane-Containing Polyimide Films

According to previous research, n(PDA)/n(4,4′-ODA) = 7/3 was the optimal molar ratio for thermal stability and mechanical property of the PI film to be in equilibrium [38]. Thus, the molar ratio of PDA and 4,4′-ODA was kept at 7/3 for all PI systems in this research. A typical polymerization process of CPI-20 was prepared in the following procedure: in a dried three-necked flask, equipped with an electric agitation, nitrogen gas inlet and outlet, PDA (1.8168 g, 16.8 mmoL), 4,4′-ODA (1.4417 g, 7.2 mmoL), BACB (1.9586 g, 6 mmoL), and part of anhydrous NMP (32 mL) were added. The mixture was stirred at room temperature until the diamine was completely dissolved, then an equimolar amount of dianhydride s-BPDA (8.8266 g, 30 mmoL) and residual NMP (10 mL) were added into the solution to adjust the solid content to approximately 25 wt.%. The mixture was continuously stirred at room temperature in N2 atmosphere for a further 48 h to get a homogeneous poly(amic acid) (PAA) solution. Then the viscous PAA solution was filtrated by G1 sand cored funnel and degassed under vacuum for 2 h in order to prepare a defect-free film. Subsequently, the PAA solution was coated onto a pre-cleaned glass plate and thermally imidized according to the following schedule: 120 °C/2 h, 200 °C/1 h, 300 °C/1 h, 400 °C/0.5 h with a heating rate of 2 °C min−1 to prepare the self-supporting films. As a consequence, reddish-brown CPI films with a thickness of about 50 µm were obtained. This series of CPI films were named as CPI-x, in which x represents the molar ratio of BACB. As a comparison, CPI-0 was based on s-BPDA, 4,4′-ODA, and PDA without any BACB, and its preparation and imidization processes were the same as above.

2.3. Characterization and Measurements

FT-IR spectra were measured in the range of 400–4000 cm−1 on a Tensor-27 Fourier transform spectrophotometer (Bruker, Germany). 1H-NMR spectra of PAA resins were acquired on a 400 MHz Avance 400 spectrometer (Bruker, Germany) in deuterated dimethyl sulfoxide (DMSO-d6). The elemental analysis of PAA resins was carried out with a Varlo ELIII elementar (Elementar, Langenselbold, Germany). The mechanical properties were conducted on an Instron 5567 universal testing machine (Instron, Norwood, MA, USA) with a specimen size of 80 × 10 × 0.05 mm3 in agreement with GB1447-2005 at a drawing rate of 2.0 mm min−1. Dynamic mechanical analyses were performed on a DMA Q800 thermal analysis system (TA, USA) with a heating rate of 5 °C min−1 under nitrogen atmosphere at a flow rate of 40 cm3 min−1. Thermogravimetric analyses were recorded on a TGA Q50 thermal analysis system (TA, USA) with a heating rate of 20 °C min−1 under both nitrogen and air atmosphere at a flow rate of 40 cm3 min−1. Thermo-oxidative aging was also carried out on a TGA Q50 thermogravimetric analyzer with a heating rate of 50 °C min−1 ramping from 50 to 700 °C and isothermal aging in air at 700 °C for 150 min. Surface chemistry of CPI samples and PAA resins were investigated by X-ray photoelectron spectroscopy (XPS, VG ESCALab 250Xi, USA) using 200 W monochromatic Al Kα radiation. Surfaces morphologies of the PI films were imaged by scanning electron microscopy (SEM, Hitachi S-4800, Tokyo, Japan) at 15 kV voltage.

3. Results and Discussions

3.1. Preparation and Characterization of CPI Films

The polyimide precursor resin—PAA resin solution was synthesized by polycondensation of equimolar aromatic dianhydride (s-BPDA) with a mixture of three different aromatic diamines, including PDA, 4,4′-ODA, and 1,7-bis(aminophenyl)-meta-carborane (BACB) in NMP (Figure 1a). The PAA solution was first coated on glass surface, followed by prebaking at 120 °C/2 h to remove part of the solvent, then thermally imidized in a vacuum at 200 °C/1 h, 300 °C/1 h, and 400 °C/0.5 h, respectively, to give a self-supporting CPI film with thickness of around 50 µm. A series of CPI-x films with various boron-loadings (x represents the molar ratio of BACB in diamine monomers and is equal to 0, 5, 10, 20, 30, 40, and 50, respectively) were obtained.
The PAA solution of CPI was trickled into excess ethanol to form a reddish-brown precipitate, which was immersed in ethanol for 48 h and dried under vacuum at 180 °C for 12 h to eliminate the NMP. Afterward, the dried PAA resin of CPI was characterized by 1H-NMR, XPS, and elemental analysis. Figure 1b shows 1H-NMR of a representative PAA resin (PAA-50), which was used for the preparation of CPI-50 film. The distinct splitting patterns were in well accordance with the expected PAA-50 chemical structure. Additionally, Table 1 illustrates the XPS and elemental analysis results of the PAA resin (PAA-50); although the XPS and elemental analysis could not detect specific elements, the contents of other elements were in great agreement with the calculated values. Furthermore, the chemical structures were also characterized by FT-IR spectroscopic measurements (Figure 1c). The intensity of the B-H characteristic absorptions around 2600 cm−1 became stronger and stronger with the increasing of boron loadings. The strong absorptions around 1775 and 1720 cm−1 referred to the asymmetric and symmetric stretching vibrations of C=O bands of imide rings in the polymer backbone. Other absorption bands collected near 1366 cm−1 and 3070 cm−1 were assigned to C–N and Carom–H, respectively. No signals around 3300~3500 cm−1 were detected in the FT-IR spectra, which meant neither –NH2 of BACB nor –CONH– of PAA existed in CPI films. That is, all the BACB was reacted with dianhydride, and the CPI film was completely imidized.
Furthermore, no phase separation was detected by the polarizing microscopic images in all of the CPI films (Figure 2). The CPI films showed homogeneous and transparent images under polarized light, demonstrating that the carborane cage structures were linked into the polymer backbone instead of simply being dispersed as an inorganic filler. Since BACB is a characteristic reddish-brown powder, the color of the PAA solution deepened with increasing carborane loadings, as shown in Figure S1. Therefore, the color of the resultant CPI film deepened with increasing carborane loadings.

3.2. Thermal and Thermo-Oxidative Stabilities

Thermal stability characterized by DMA and TGA were compared in Table S1. The Tg values (tan δ in DMA) increased from 304 °C (CPI-0) to 371 °C (CPI-50) with increasing boron loadings (Figure 3a). Although the bulky carborane cage structure enlarged the distance of polymer chain to chain, it also contrarily restricted the mobility of polymer chains in large-scale due to its big steric hindrance, and the movements induced by larger inter-chain space were too short in size scale to change polymers from a glassy state to rubbery state resulting in increased Tg values.
Compared with the boron-free film (CPI-0), incorporating carborane into the polyimide backbone structure greatly enhanced polymer thermal and thermo-oxidative stabilities (Figure 3b,c). Both thermal and thermo-oxidative stability were improved with increasing boron-loadings. The initial thermal decomposition temperature (<1.0 wt.% of the original weight) were detected over 550 °C in air, 50 °C higher than that of CPI-0. The T5 in N2 were measured in the range of 595–601 °C, 13–19 °C higher than CPI-0, and apparently did not change with the boron-loadings. However, the T5 in air increased from 602 °C (CPI-5) to 632 °C (CPI-50) with increasing boron-loadings. At 50 mol.% of carborane loading (CPI-50), the T10 was measured at 657 °C (in N2) and 749 °C (in air), respectively, and the char yield at 750 °C was as high as 87.9% (in N2) and 90.0%(in air), indicating obvious improvement in thermo-oxidative stability. Moreover, the TGA analysis manifested that some weight gains were observed for the CPI films beginning at about 500 °C in air, which was probably attributed to the oxidation of boron atoms in the carborane cage to produce a boron oxide layer on the film surface, which could retard the further erosion of inner polymers [39].

3.3. Mechanical Properties

During copolymerization with aromatic dianhydride, BACB is less reactive than the other two aromatic diamines (4,4′-ODA and PDA) due to the strong electron-withdrawing ability and the large steric hindrance effect of the carborane cage structure, diminishing the polymerization reactivity of the diamine monomer. Although it was hard for BACB to form high Mw polymer, the BACB still reacted with dianhydride to form a lower Mw polymer. As a consequence, the molecular weight of PAA resins was reduced, and the polymer inter-chain interaction was weakened with increasing boron-loadings, leading to a decreased tensile strength and modulus (Figure 4). Thus, the CPI-50 film showed the lowest mechanical performance with a tensile strength (TS) of 108 MPa and tensile modulus (TM) of 3.7 GPa, respectively, compared with CPI-20 (TS: 161 MPa, TM: 4.9 GPa).
CPI films with different boron-loadings (CPI-0, CPI-20, and CPI-50) were thermally treated in a muffle furnace under various thermo-oxidative aging conditions (600 °C/30 min, 600 °C/60 min, 700 °C/5 min, 700 °C/15 min, 700 °C/30 min, etc.). The flexibility of the CPI films was estimated by bend testing, and the tensile properties were measured on an Instron 5567 universal testing machine with a drawing rate of 2.0 mm min−1. Table 2 summarized the results of bend testing, after thermo-oxidative aging at 600 °C for 30 to 60 min, the boron-free films (CPI-0) were damaged into ashes or volatiles due to the violent degradation, and could not be tested. However, all the boron-containing films could be bent 180° under the same condition, showing great retention of the flexibility (Figure 5a). Additionally, after thermo-oxidative aging at 700 °C/30 min, although the CPI-20 film was broken into two pieces during bend testing, the CPI-50 film still exhibited good flexibility.
Regarding the tensile tests, both CPI-20 and CPI-50 films showed measurable tensile strength after thermo-oxidative aging at 600 to 700 °C (Figure 5b); the specific data are displayed in Table S2. The unaged CPI-20 and CPI-50 films have a tensile strength of 161 and 108 MPa, respectively. After thermo-oxidative aging at 600 °C/30 min, the tensile strength reduced to 88 MPa for CPI-20 and 79 MPa for CPI-50. When the aging time extended to 60 min at 600 °C, the tensile strength was reduced to 23 MPa (CPI-20) and 42 MPa (CPI-50), indicating that the thermo-oxidation at 600 °C increased with extending aging time. Moreover, after aging at 700 °C for 5, 15, and 30 min, the CPI-50 film still kept a tensile strength of 63, 35, and 18 MPa, successfully, and its strength retention was much higher than that of CPI-20 (Figure 5c). Compared with boron-free films, the incorporation of a carborane cage into the polyimide backbone structure significantly improved the polymer thermo-oxidative stability at 700 °C.

3.4. Mechanism of Thermo-Oxidative Resistance

The extraordinary thermo-oxidative stabilities of the CPI films might be attributed to the formation of the boron oxide protective layer on the film surface, preventing the direct contact of inner polymer with oxygen molecules and resulting in the reduced decomposition rate of the inner polymer. Hence, the sheltered inner polymer could still provide the film with certain mechanical strength and flexibility even after thermo-oxidative aging at 700 °C. The thermal degradation kinetics in air was analyzed via TGA with the Flynn-Wall-Ozawa method [40,41], based on the following Equation (2), which is a derivate from Equation (1):
log β = log A E a R g ( α ) − 2.315 − 0.457 E a R T ,
d log β d ( 1 / T ) = 0.457 E a R ,
where β is the heating rate (K min−1), R is the gas constant (8.314 J moL−1 K−1), Ea is the activation energy (kJ moL−1), T is the absolute temperature (K), and g(α) is the function of conversion rate α.
TGA of the CPI films with various boron-loadings (CPI-0, CPI-20, CPI-50) were performed in air at different heating rates. Figure 6 compares the DTG (Derivative Thermogravimetry) curves of CPI films with different carborane loadings. The two intersection points of the two tangents of the decomposition peak and baseline were set as initial degradation temperature (Ti) and terminal degradation temperature (Tt). The initial weight residue was regarded as the weight residue at the initial degradation temperature and the same as the terminal weight residue. Then, the section between the initial and terminal weight residue was equally divided into 10 pieces, and each weight residue represented a certain conversion rate α. According to the conversion rate α and heating rate β, Tα (temperature at conversion rate α) could be directly determined in the corresponding TGA curves. Subsequently, plots of lg β against 1000/T were linearly fitted to a series of straight lines in which the slopes were used to compute the activation energy Ea at the corresponding conversion rate α, as exhibited in Figure 7a. All of the generated lines were in excellent linear dependence with R2 > 0.98, as summarized in Table S3.
Obviously, the incorporation of carborane lowered the initial activation energy of the polyimide system (Figure 7b). Since the degradation activation energy Ea was defined as the energy barrier that should be overcome to activate the thermal decomposition, the introduction of a flexible, bulky carborane cage loosened the chain packing, resulting in the lower initial Ea. With an increase in oxidation time, the Ea of CPI-0 diminished drastically while that of CPI-50 ascended gradually, probably due to the formation of a boron oxide protective layer during the decomposition. The formed boron oxide layer covered on the film surface could shelter the inner polymer, thus enhancing the energy barrier. In addition, the increase in the energy barrier, in turn, slowed down the decomposition process of the inner polymer, and the degradation rate decreased little by little as decomposition proceeded. At the conversion rate α > 0.5, the Ea of CPI-50 exceeded that of CPI-0, and it continued to grow while the Ea of CPI-0 continued to diminish (Figure 7b). Furthermore, the Ea of CPI-20 film declined at first and then rose up later, implying that the boron content was too low to yield a sufficient protective layer to enhance the Ea at the beginning. Compared with CPI-0, the protective layer only retarded the degradation rate of CPI-20, but when the conversion rate α > 0.6, the layer was dense enough to protect the inner polymer, leading to the growth of Ea in which the value was between CPI-0 and CPI-50.
To further investigate the mechanism, three representatives with different carbon-loadings (CPI-0, CPI-20, and CPI-50) were isothermally aged by TGA in air at 700 °C for 150 min (Figure 8a). Apparently, the thermo-oxidative stability was greatly improved by increasing the carborane loadings. Since the boron-free CPI film (CPI-0) was completely decomposed into volatiles rapidly, whereas the CPI-20 and CPI-50 film still maintained more than 29% and 76% weight residue after 150 min of thermo-oxidative degradation at 700 °C, respectively. In addition, the boron-free CPI film (CPI-0) was easier to decompose with a degradation peak more intense than the carborane-containing films (CPI-20 and CPI-50). Combined with DTG curves (Figure 8b), a second sharp weight loss peak immediately followed the first for CPI-0 in air. However, only one decomposition peak was observed for CPI-50 in air. This could be interpreted by the fact that the further degradation of the CPI-50 films was postponed due to the higher Ea of the boron oxide passivation layer generated during the thermal treatment. It was noteworthy that a new broad peak was generated between the sharp decomposition peak and the slow degradation region for CPI-20 in the DTG curves (Figure 8c), manifesting that there was a distinctive degradation from 5 to 60 min in isothermal treatment.
XPS was measured to investigate the chemical changes in the binding energies of boron and oxygen elements of the CPI films thermally treated at different conditions (Figure 9). The test samples of the CPI-20 film were cleaned by deionized water and ethanol for several times to wash out the impurities on the surfaces and then heated to 700 °C in a muffle furnace standing for various times (5 min, 15 min, 30 min, 60 min, and 120 min). After thermo-oxidative aging for 5 min, the polyimide located on the out of surface was initially decomposed, evidenced by the disappearance of the carborane cage peaks (189.6 eV) and C=O bonds (531.6 eV), respectively, and the absorption intensities of C-O (533.3 eV) in the O 1s spectrum became more conspicuous. Furthermore, the signal that occurred around 192.2 eV was assigned to the partially destroyed carborane cage, owing to the pyrolysis [42]. Meanwhile, the boron atoms linked in the carborane cage were reacted with oxygen to form a boron oxide layer on the surface evidenced by the appearance of B-O bonds in B 1s (193.4 eV) and O 1s (532.2 eV) spectra in the initial 5 min. Then, a dense passivation layer was covered on the surface, because only the B-O peak was observed both in B 1s and O 1s spectra (15 min). Nevertheless, when the aging time extended to 30 min, the partially broken carborane cage (192.3 eV) and C-O (533.3 eV) signals were reappeared in B 1s and O 1s spectra, respectively, which was in well accordance with the fact that the degradation rate of CPI-20 during 5 to 60 min was faster than that of CPI-50 while slower than CPI-0′s. It was presumed that, during 5 to 60 min, there was a dynamic equilibrium in the breakage and regeneration of the passivation layer, as a result of the disappearance and reappearance of partially damaged carborane cage and C-O peaks. With the aging time increased, the boron oxide layer became increasingly denser, evidenced by the fact that only the B-O peak was collected.
Figure 10 compares the surface morphologies of CPI-20 samples after thermo-oxidative aging at 700 °C for different times. The thermal degradation could be divided into three stages, as shown in Figure 11. Based on the XPS analysis, the first stage was the decomposition of the external polymer, and the surface was gradually rougher. In this stage, the outmost film was reacted with oxygen, and the volatiles, such as oxynitride, oxycarbide, and hydroxide, were eliminated, accompanied by the formation of a B-O bond. The second stage was the generation of the boron oxide protective layer on the film surface. Initially, part of the surface was covered by that oxidative layer, as shown in Figure 9 (5 min) and Figure 10b. Then, the polymer next to the opened hole on the outmost passivation layer was degraded and formed a new passivation layer in situ, which enabled the hybrid polyimide surface to be “self-healing” [43], as shown in Figure 9. In this stage, breakage and regeneration of the passivation layer were in a dynamic equilibrium, but the regenerated layers gradually repaired the breakage of the previous one, ultimately forming the multilayered protective layer (Figure 10e). This layer covered the film surface and prevented the direct contact of the inner polymer and oxygen, thus significantly reducing the degradation rate. Although a “self-healing”, multilayered, dense passivation layer was generated on the film surface during the second stage, the heat could still be transferred into the interior via the protective layer, so the polymer was slowly degraded in the last stage.

4. Conclusions

Carborane-containing polyimide (CPI) films with ultrahigh thermal and thermo-oxidative stability up to 700 °C were successfully synthesized. The excellent thermal and thermo-oxidative stability was attributed to the multilayered protection layers formed on the film surface by thermal conversion of the carborane group into boron oxides. The boron oxide layer enhanced the degradation activation energy and suppressed the direct contact of inner polymer materials with oxygen molecules in a high-temperature environment, acting as a “self-healing” skin layer on the polyimide materials. Compared with the corresponding carborane-free films, the CPI films retained much higher mechanical strength and flexibility even after thermo-oxidative aging at 700 °C/30 min. It was this “self-healing”, multilayered, dense boron oxide protective layer that slowed down the further erosion process of the inner polymer and prolonged the service life of materials at high temperatures.

Supplementary Materials

The following are available online at https://www.mdpi.com/2073-4360/11/12/1930/s1, Figure S1: The images of the carborane containing PAA solutions, Table S1: Thermal properties of the CPI films, Table S2: Tensile properties of CPI-20 and CPI-50 after thermo-oxidative aging, Table S3: Degradation Ea and linearly dependent coefficients R2 of CPI-0, CPI-20 and CPI-50 and Scheme S1: Synthesis of 1,7-bis (aminophenyl)-meta-carborane (BACB).

Author Contributions

Investigation and writing—original draft preparation, F.L.; writing—review and editing, S.Y. and H.Y.; supervision, S.Y. and H.Y.; funding acquisition, S.Y., H.Y. and G.F.; validation, X.Z., Z.Z. and G.F.; project administration, S.Y.

Funding

This work was supported by the National Natural Science Foundation of China (NSFC grant 51973225 and 51573094).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Kreuz, J.A.; Edman, J.R. Polyimide Films. Adv. Mater. 1998, 10, 1229–1232. [Google Scholar] [CrossRef]
  2. Liaw, D.-J.; Wang, K.-L.; Huang, Y.-C.; Lee, K.-R.; Lai, J.-Y.; Ha, C.-S. Advanced polyimide materials: Syntheses, physical properties and applications. Prog. Polym. Sci. 2012, 37, 907–974. [Google Scholar] [CrossRef]
  3. Tomczyk, M.; Bretos, I.; Jiménez, R.; Mahajan, A.; Ramana, E.V.; Calzada, M.L.; Vilarinho, P.M. Direct fabrication of BiFeO3 thin films on polyimide substrates for flexible electronics. J. Mater. Chem. C 2017, 5, 12529–12537. [Google Scholar] [CrossRef]
  4. Ma, H.; Jen, A.K.-Y.; Dalton, L.R. Polymer-Based Optical Waveguides: Materials, Processing, and Devices. Adv. Mater. 2002, 14, 1339–1365. [Google Scholar] [CrossRef]
  5. Govindaraj, B.; Sarojadevi, M. Microwave-assisted synthesis of nanocomposites from polyimides chemically cross-linked with functionalized carbon nanotubes for aerospace applications. Polym. Adv. Technol. 2018, 29, 1718–1726. [Google Scholar] [CrossRef]
  6. Zhu, Z.; Yao, H.; Dong, J.; Qian, Z.; Dong, W.; Long, D. High-mechanical-strength polyimide aerogels crosslinked with 4,4′-oxydianiline-functionalized carbon nanotubes. Carbon 2019, 144, 24–31. [Google Scholar] [CrossRef]
  7. Choi, M.-C.; Kim, Y.; Ha, C.-S. Polymers for flexible displays: From material selection to device applications. Prog. Polym. Sci. 2008, 33, 581–630. [Google Scholar] [CrossRef]
  8. Xiao, Y.; Low, B.T.; Hosseini, S.S.; Chung, T.S.; Paul, D.R. The strategies of molecular architecture and modification of polyimide-based membranes for CO2 removal from natural gas—A review. Prog. Polym. Sci. 2009, 34, 561–580. [Google Scholar] [CrossRef]
  9. Rodenas, T.; van Dalen, M.; García-Pérez, E.; Serra-Crespo, P.; Zornoza, B.; Kapteijn, F.; Gascon, J. Visualizing MOF Mixed Matrix Membranes at the Nanoscale: Towards Structure-Performance Relationships in CO2/CH4Separation Over NH2-MIL-53(Al)@PI. Adv. Funct. Mater. 2014, 24, 249–256. [Google Scholar] [CrossRef]
  10. Wang, Z.; Wang, D.; Zhang, S.; Hu, L.; Jin, J. Interfacial Design of Mixed Matrix Membranes for Improved Gas Separation Performance. Adv. Mater. 2016, 28, 3399–3405. [Google Scholar] [CrossRef]
  11. Rogan, Y.; Malpass-Evans, R.; Carta, M.; Lee, M.; Jansen, J.C.; Bernardo, P.; Clarizia, G.; Tocci, E.; Friess, K.; Lanč, M.; et al. A highly permeable polyimide with enhanced selectivity for membrane gas separations. J. Mater. Chem. A 2014, 2, 4874–4877. [Google Scholar] [CrossRef]
  12. Wang, H.; Wang, T.; Yang, S.; Fan, L. Preparation of thermal stable porous polyimide membranes by phase inversion process for lithium-ion battery. Polymer 2013, 54, 6339–6348. [Google Scholar] [CrossRef]
  13. Liang, X.; Yang, Y.; Jin, X.; Huang, Z.; Kang, F. The high performances of SiO2 /Al2O3 -coated electrospun polyimide fibrous separator for lithium-ion battery. J. Membr. Sci. 2015, 493, 1–7. [Google Scholar] [CrossRef]
  14. Miao, Y.-E.; Zhu, G.-N.; Hou, H.; Xia, Y.-Y.; Liu, T. Electrospun polyimide nanofiber-based nonwoven separators for lithium-ion batteries. J. Power Sources 2013, 226, 82–86. [Google Scholar] [CrossRef]
  15. Shi, J.; Hu, H.; Xia, Y.; Liu, Y.; Liu, Z. Polyimide matrix-enhanced cross-linked gel separator with three-dimensional heat-resistance skeleton for high-safety and high-power lithium ion batteries. J. Mater. Chem. A 2014, 2, 9134–9141. [Google Scholar] [CrossRef]
  16. Tsai, M.H.; Tseng, I.H.; Chiang, J.C.; Li, J.J. Flexible polyimide films hybrid with functionalized boron nitride and graphene oxide simultaneously to improve thermal conduction and dimensional stability. ACS Appl. Mater. Interfaces 2014, 6, 8639–8645. [Google Scholar] [CrossRef]
  17. Sato, K.; Horibe, H.; Shirai, T.; Hotta, Y.; Nakano, H.; Nagai, H.; Mitsuishi, K.; Watari, K. Thermally conductive composite films of hexagonal boron nitride and polyimide with affinity-enhanced interfaces. J. Mater. Chem. 2010, 20, 2749–2752. [Google Scholar] [CrossRef]
  18. Li, T.-L.; Hsu, S.L.-C. Preparation and properties of thermally conductive photosensitive polyimide/boron nitride nanocomposites. J. Appl. Polym. Sci. 2011, 121, 916–922. [Google Scholar] [CrossRef]
  19. Spechler, J.A.; Koh, T.-W.; Herb, J.T.; Rand, B.P.; Arnold, C.B. A Transparent, Smooth, Thermally Robust, Conductive Polyimide for Flexible Electronics. Adv. Funct. Mater. 2015, 25, 7428–7434. [Google Scholar] [CrossRef]
  20. Kim, Y.; Ryu, T.I.; Ok, K.-H.; Kwak, M.-G.; Park, S.; Park, N.-G.; Han, C.J.; Kim, B.S.; Ko, M.J.; Son, H.J.; et al. Inverted Layer-By-Layer Fabrication of an Ultraflexible and Transparent Ag Nanowire/Conductive Polymer Composite Electrode for Use in High-Performance Organic Solar Cells. Adv. Funct. Mater. 2015, 25, 4580–4589. [Google Scholar] [CrossRef]
  21. Lu, H.-Y.; Chou, C.-Y.; Wu, J.-H.; Lin, J.-J.; Liou, G.-S. Highly transparent and flexible polyimide–AgNW hybrid electrodes with excellent thermal stability for electrochromic applications and defogging devices. J. Mater. Chem. C 2015, 3, 3629–3635. [Google Scholar] [CrossRef]
  22. Chen, D.; Liang, J.; Liu, C.; Saldanha, G.; Zhao, F.; Tong, K.; Liu, J.; Pei, Q. Thermally Stable Silver Nanowire-Polyimide Transparent Electrode Based on Atomic Layer Deposition of Zinc Oxide on Silver Nanowires. Adv. Funct. Mater. 2015, 25, 7512–7520. [Google Scholar] [CrossRef]
  23. Quédé, A.; Cardoso, J.; Le Bras, M.; Delobel, R.; Goudmand, P.; Dessaux, O.; Jama, C. Thermal stability and flammability studies of coated polymer powders using a plasma fluidized bed process. J. Mater. Sci. 2002, 37, 1395–1399. [Google Scholar] [CrossRef]
  24. Saccani, A.; Toselli, M.; Pilati, F. Improvement of the thermo-oxidative stability of low-density polyethylene films by organic–inorganic hybrid coatings. Polym. Degrad. Stab. 2011, 96, 212–219. [Google Scholar] [CrossRef]
  25. Kim, S.; Jang, M.; Park, M.; Park, N.-H.; Ju, S.-Y. A self-assembled flavin protective coating enhances the oxidative thermal stability of multi-walled carbon nanotubes. Carbon 2017, 117, 220–227. [Google Scholar] [CrossRef]
  26. Williams, J.M.; Kelly, R.G. An analysis of corrosive species ingress into IM7/PETI-5 Ti honeycomb composites. Compos. Sci. Technol. 2004, 64, 1875–1883. [Google Scholar] [CrossRef]
  27. Lincoln, J.E.; Hout, S.; Flaherty, K.; Curliss, D.B.; Morgan, R.J. High temperature organic/inorganic addition cure polyimide composites, part 1: Matrix thermal properties. J. Appl. Polym. Sci. 2008, 107, 3557–3567. [Google Scholar] [CrossRef]
  28. Shi, C.; Dai, J.; Shen, X.; Peng, L.; Li, C.; Wang, X.; Zhang, P.; Zhao, J. A high-temperature stable ceramic-coated separator prepared with polyimide binder/Al2O3 particles for lithium-ion batteries. J. Membr. Sci. 2016, 517, 91–99. [Google Scholar] [CrossRef]
  29. Lincoln, J.E.; Morgan, R.J.; Curliss, D.B. Effect of matrix chemical structure on the thermo-oxidative stability of addition cure poly(imide siloxane) composites. Polym. Compos. 2008, 29, 585–596. [Google Scholar] [CrossRef]
  30. Chang, T.C.; Wu, K.H.; Liao, C.L.; Lin, S.T.; Wang, G.P. Thermo-oxidative degradation of siloxane-containing polyimide and unmodified polyimide. Polym. Degrad. Stab. 1998, 62, 299–305. [Google Scholar] [CrossRef]
  31. Packirisamy, S. Decaborane(14)-based polymers. Prog. Polym. Sci. 1996, 21, 707–773. [Google Scholar] [CrossRef]
  32. Heying, T.L.; Jr, J.W.A.; Clark, S.L.; Mangold, D.J.; Goldstein, H.L.; Hillman, M.; Polak, R.J.; Szymanski, J.W. A New Series of Organoboranes. I. Carboranes from the Reaction of Decaborane with Acetylenic Compounds. Inorg. Chem. 1963, 2, 1089–1092. [Google Scholar] [CrossRef]
  33. Jemmis, E.D. Overlap control and stability of polyhedral molecules. closo-Carboranes. J. Am. Chem. Soc. 1982, 104, 7017–7020. [Google Scholar] [CrossRef]
  34. Dash, B.P.; Satapathy, R.; Maguire, J.A.; Hosmane, N.S. Polyhedral boron clusters in materials science. New J. Chem. 2011, 35, 1955–1972. [Google Scholar] [CrossRef]
  35. Li, N.; Zeng, F.; Qu, D.; Zhang, J.; Shao, L.; Bai, Y. Synthesis and characterization of carborane-containing polyester with excellent thermal and ultrahigh char yield. J. Appl. Polym. Sci. 2016, 133. [Google Scholar] [CrossRef]
  36. Zhang, X.; Kong, L.; Dai, L.; Zhang, X.; Wang, Q.; Tan, Y.; Zhang, Z. Synthesis, characterization, and thermal properties of poly(siloxane-carborane)s. Polymer 2011, 52, 4777–4784. [Google Scholar] [CrossRef]
  37. Huang, X.; Zhang, Q.; Meng, Z.; Gu, J.; Jia, X.; Xi, K. Greatly enhanced thermo-oxidative stability of polybenzoxazine thermoset by incorporation ofm-carborane. J. Polym. Sci. Part A Polym. Chem. 2015, 53, 973–980. [Google Scholar] [CrossRef]
  38. Hasegawa, M.; Koseki, K. Poly(ester imide)s Possessing Low Coeffcient of Thermal Expansion and Low Water Absorption. High Perform. Polym. 2016, 18, 697–717. [Google Scholar] [CrossRef]
  39. Xing, T.; Zhang, K. Syntheses of novel soluble carborane polyimides with ultrahigh thermal stability. Polym. Int. 2015, 64, 1715–1721. [Google Scholar] [CrossRef]
  40. Nayak, L.; Rahaman, M.; Khastgir, D.; Chaki, T.K. Thermal degradation kinetics of polyimide nanocomposites from different carbon nanofillers: Applicability of different theoretical models. J. Appl. Polym. Sci. 2018, 135, 45862. [Google Scholar] [CrossRef]
  41. Yang, K.-K.; Wang, X.-L.; Wang, Y.-Z.; Wu, B.; Jin, Y.-D.; Yang, B. Kinetics of thermal degradation and thermal oxidative degradation of poly(p-dioxanone). Eur. Polym. J. 2003, 39, 1567–1574. [Google Scholar] [CrossRef]
  42. Lou, P.; Zhang, X.; Liu, B.; Gao, X.; Zhang, Z.; Xie, Z. Synthesis and thermal degradation mechanism of polyorganocarboranesiloxanes containing m -carboranylmethyl unit. Polym. Degrad. Stab. 2017, 144, 304–314. [Google Scholar] [CrossRef]
  43. Lei, X.F.; Chen, Y.; Zhang, H.P.; Li, X.J.; Yao, P.; Zhang, Q.Y. Space survivable polyimides with excellent optical transparency and self-healing properties derived from hyperbranched polysiloxane. ACS Appl. Mater. Interfaces 2013, 5, 10207–10220. [Google Scholar] [CrossRef] [PubMed]
Polymers 11 01930 g001a 550Polymers 11 01930 g001b 550
Figure 1. (a) Synthesis of the carborane-containing aromatic polyimide (CPI) films; (b) 1H-NMR spectrum of a representative poly(amic acid) (PAA) resin (CPI-50) and (c) FT-IR spectra of the CPI films.
Figure 1. (a) Synthesis of the carborane-containing aromatic polyimide (CPI) films; (b) 1H-NMR spectrum of a representative poly(amic acid) (PAA) resin (CPI-50) and (c) FT-IR spectra of the CPI films.
Polymers 11 01930 g001aPolymers 11 01930 g001b
Polymers 11 01930 g002 550
Figure 2. Polarizing microscopic images of the CPI films (the inserted images were the films covered on the logo of the Chinese Academy of Sciences).
Figure 2. Polarizing microscopic images of the CPI films (the inserted images were the films covered on the logo of the Chinese Academy of Sciences).
Polymers 11 01930 g002
Polymers 11 01930 g003 550
Figure 3. Thermal and thermo-oxidative stabilities of the CPI films; (a) DMA curves; (b) TGA curves in air; (c) TGA curves in N2.
Figure 3. Thermal and thermo-oxidative stabilities of the CPI films; (a) DMA curves; (b) TGA curves in air; (c) TGA curves in N2.
Polymers 11 01930 g003
Polymers 11 01930 g004 550
Figure 4. Tensile modulus and tensile strength of the CPI films vs. boron loadings.
Figure 4. Tensile modulus and tensile strength of the CPI films vs. boron loadings.
Polymers 11 01930 g004
Polymers 11 01930 g005 550
Figure 5. (a) The effects of bend testing; (b) tensile strength, and (c) retention of tensile strength of the CPI film samples after thermo-oxidative aging at various conditions.
Figure 5. (a) The effects of bend testing; (b) tensile strength, and (c) retention of tensile strength of the CPI film samples after thermo-oxidative aging at various conditions.
Polymers 11 01930 g005
Polymers 11 01930 g006 550
Figure 6. DTG curves of (a) CPI-0, (b) CPI-20, and (c) CPI-50 under various heating rates.
Figure 6. DTG curves of (a) CPI-0, (b) CPI-20, and (c) CPI-50 under various heating rates.
Polymers 11 01930 g006
Polymers 11 01930 g007 550
Figure 7. (a) Flynn-Wall-Ozawa plots for CPI-20 and (b) activation energy against conversion rate in the CPI films.
Figure 7. (a) Flynn-Wall-Ozawa plots for CPI-20 and (b) activation energy against conversion rate in the CPI films.
Polymers 11 01930 g007
Polymers 11 01930 g008 550
Figure 8. (a) TGA and (b) DTG curves of CPI-0, CPI-20, and CPI-50 isothermally treated at 700 °C for 150 min in air, and (c) three degradation stages of CPI-20 film.
Figure 8. (a) TGA and (b) DTG curves of CPI-0, CPI-20, and CPI-50 isothermally treated at 700 °C for 150 min in air, and (c) three degradation stages of CPI-20 film.
Polymers 11 01930 g008
Polymers 11 01930 g009 550
Figure 9. (a) B 1s and (b) O 1s XPS spectra of CPI-20 isothermally treated at 700 °C.
Figure 9. (a) B 1s and (b) O 1s XPS spectra of CPI-20 isothermally treated at 700 °C.
Polymers 11 01930 g009
Polymers 11 01930 g010 550
Figure 10. SEM images of the surfaces of CPI-20 samples heated at 700 °C in air for (a) 0 min; (b) 5 min; (c) 15 min; (d) 30 min; (e) 60 min, and (f) 120 min.
Figure 10. SEM images of the surfaces of CPI-20 samples heated at 700 °C in air for (a) 0 min; (b) 5 min; (c) 15 min; (d) 30 min; (e) 60 min, and (f) 120 min.
Polymers 11 01930 g010
Polymers 11 01930 g011 550
Figure 11. Mechanism of the three stages during thermal degradation.
Figure 11. Mechanism of the three stages during thermal degradation.
Polymers 11 01930 g011
Table
Table 1. Calculated and experimental values of each element in the PAA resin (PAA-50).
Table 1. Calculated and experimental values of each element in the PAA resin (PAA-50).
Elemental ContentsC (%)N (%)H (%)O (%)B (%)
Calculated values61.515.334.1418.7310.29
Elemental analysis62.015.444.02--
XPS analysis60.304.94-19.5511.07
-: The elemental analysis cannot detect the contents of B and O; XPS analysis can not detect the content of H, but the contents of other elements were in great agreement with the calculated values.
Table
Table 2. Bending results of the CPI films after thermo-oxidative aging at various conditions.
Table 2. Bending results of the CPI films after thermo-oxidative aging at various conditions.
Temperature/Time600 °C/30 min600 °C/60 min700 °C/5 min700 °C/15 min700 °C/30 min
CPI-0----------
CPI-20+++++++++
CPI-50++++++++++
++: bendable; +: unbendable but can be conducted on tensile test; --: broken.

Share and Cite

MDPI and ACS Style

Liu, F.; Fang, G.; Yang, H.; Yang, S.; Zhang, X.; Zhang, Z. Carborane-Containing Aromatic Polyimide Films with Ultrahigh Thermo-Oxidative Stability. Polymers 2019, 11, 1930. https://doi.org/10.3390/polym11121930

AMA Style

Liu F, Fang G, Yang H, Yang S, Zhang X, Zhang Z. Carborane-Containing Aromatic Polyimide Films with Ultrahigh Thermo-Oxidative Stability. Polymers. 2019; 11(12):1930. https://doi.org/10.3390/polym11121930

Chicago/Turabian Style

Liu, Fulin, Guangqiang Fang, Haixia Yang, Shiyong Yang, Xuezhong Zhang, and Zhijie Zhang. 2019. "Carborane-Containing Aromatic Polyimide Films with Ultrahigh Thermo-Oxidative Stability" Polymers 11, no. 12: 1930. https://doi.org/10.3390/polym11121930

APA Style

Liu, F., Fang, G., Yang, H., Yang, S., Zhang, X., & Zhang, Z. (2019). Carborane-Containing Aromatic Polyimide Films with Ultrahigh Thermo-Oxidative Stability. Polymers, 11(12), 1930. https://doi.org/10.3390/polym11121930

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.