Next Article in Journal
Integration of an Aerosol-Assisted Deposition Technique for the Deposition of Functional Biomaterials Applied to the Fabrication of Miniaturised Ion Sensors
Next Article in Special Issue
Magnetic Nanoparticle-Based Dianthin Targeting for Controlled Drug Release Using the Endosomal Escape Enhancer SO1861
Previous Article in Journal
RETRACTED: Yang et al. Nitrogen Doped Intercalation TiO2/TiN/Ti3C2Tx Nanocomposite Electrodes with Enhanced Pseudocapacitance. Nanomaterials 2020, 10, 345
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 11
Issue 4
10.3390/nano11040937
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Co-Doped NdFeO3 Nanoparticles: Synthesis, Optical, and Magnetic Properties Study

by
Tien Anh Nguyen
1,2,
Thanh Le Pham
3,
Irina Yakovlevna Mittova
4,
Valentina Olegovna Mittova
5,
Truc Linh Thi Nguyen
3,
Hung Van Nguyen
6 and
Vuong Xuan Bui
7,*
1
Informetrics Research Group, Ton Duc Thang University, Ho Chi Minh City 700000, Vietnam
2
Faculty of Applied Sciences, Ton Duc Thang University, Ho Chi Minh City 700000, Vietnam
3
Faculty of Chemistry, Ho Chi Minh City University of Education, Ho Chi Minh City 700000, Vietnam
4
Faculty of Chemistry, Voronezh State University, Voronezh 394018, Russia
5
Department of Biochemistry, Voronezh State Medical University named after N. N. Burdenko, Voronezh 394036, Russia
6
Practice and Experimental Center for Dong Thap University, Cao Lanh City 81000, Vietnam
7
Faculty of Pedagogy in Natural Sciences, Sai Gon University, Ho Chi Minh City 700000, Vietnam
*
Author to whom correspondence should be addressed.
Nanomaterials 2021, 11(4), 937; https://doi.org/10.3390/nano11040937
Submission received: 25 February 2021 / Revised: 25 March 2021 / Accepted: 2 April 2021 / Published: 6 April 2021
(This article belongs to the Special Issue Structure and Properties of Functional Nanomaterials)
Browse Figures
Review Reports Versions Notes

Abstract

:
In this work, single-phase nanostructured NdFe1−xCoxO3 (x = 0, 0.1, 0.2, and 0.3) perovskite materials were obtained by annealing stoichiochemistry mixtures of their component hydroxides at 750 °C for 60 min. The partial substitution of Fe by Co in the NdFeO3 crystal lattice leads to significant changes in the structural characteristics, and as a consequence, also alters both the magnetic and optical properties of the resulting perovskites. The low optical band gap (Eg = 2.06 ÷ 1.46 eV) and high coercivity (Hc = 136.76 ÷ 416.06 Oe) give Co-doped NdFeO3 nanoparticles a huge advantage for application in both photocatalysis and hard magnetic devices.

1. Introduction

Perovskite orthoferrite materials have been intensively studied because of their diverse unique properties, variable formulae, variable structures, and wide technological applications. Especially, the substitution of Ln or Fe sites of the LnFeO3 perovskite-type oxides (where Ln is a rare-earth element such as La, Nd, and Pr) by other elements which can exhibit considerable multi-valence and defect sites in their structures, which lead to the tunable redox and electromagnetic characteristics of the materials [1,2,3]. In order to boost the performances and widen the applications of perovskite materials, much effort has been spent to downscale the structure into nano size. Indeed, in comparison with their bulk counterparts, perovskite nanomaterials show many advantages, such as high processing capability of thin film [4], rich and controllable catalyst active sites [5,6] or excellent optical, electrical, and magnetic properties [7,8,9].
In NdFeO3, the magnetic moments of Fe and Nd are two antiparallel coupled nonequivalent magnetic sublattices. The electrons in the 3d and 4f orbitals of these two sublattices interact with spin-lattice coupling, leading to a very unstable magnetic state and, thus, they result in unusually large magnetic anisotropy, magnetization reversal, and spin switching in low magnetic fields [10]. In order to adjust their optical, electrical, and magnetic properties and to enhance the performance of pristine perovskite, transition metal ions can be doped into their crystal lattices. Co-doped LnFeO3 materials have attracted extensive study thanks to their exciting dielectric, sensing, optical, and magnetic properties. Owing to the multiple spins and oxidation states of Co, the process of catalysts may be modified by changing the concentration of Co in solid solutions [3,6,11,12,13,14].
Several studies [15,16,17,18,19,20] described the formation of LnFeO3 orthoferrites nanoparticles (Ln = La, Y), including those doped with metals (for example, Mn, Co, Ni, and Ba) by a simple co-precipitation method via the hydrolysis of cations in boiling water followed by the addition of appropriate precipitants. In our recent work [21], NdFeO3 nanoparticles, of 30 nm in size, were obtained via the simple co-precipitation method mentioned above, their crystal structure and magnetic properties were also studied therein.
In this paper, single-phase Co-doped NdFeO3 nanoparticles were synthesized and the changes in their crystal structure, their magnetic and optical properties were also studied. To the best of our knowledge, similar work has not been reported elsewhere.

2. Materials and Methods

All reagents in this work are analytical grade and were used without any further purification. The procedure for synthesizing Co-doped NdFeO3 nanoparticles is similar to that of NdFeO3 [21], with NaOH 5% as the precipitant instead of a NH3 5% solution, in order to avoid the generation of soluble complex from the reaction of cobalt (II) hydroxide precipitate (Co(OH)2↓) and ammonium solution according to Equation (1) [22].
Co(OH)2↓ + 6NH3 → [Co(NH3)6](OH)2
The structure and phase composition of the samples were investigated by X-ray powder diffraction (XRD, D8-ADVANCE, Brucker, Bremen, Germany) with Cu Kα radiation (λ = 1.54056 Å), the step size is chosen to be 0.02 in range of 10° to 80°. The average crystal size was determined according to the Debye–Scherrer equation [23]; lattice constants a, b, c, and the unit cell volume V were determined using the Rietveld method [23] implemented in the X’pert High Score Plus 2.2b software package [18,19,20].
The energy-dispersive X-ray spectroscopy (EDX) was carried out with a FE-SEM S-4800 spectrometer (Hitachi, Tokyo, Japan). The average value of five different positions in each sample was taken as the final result of the corresponding sample. Particle size and morphology of Co-doped NdFeO3 nanoparticles were determined using transmission electron microscopy (TEM; JEOL-1400, Jeol Ltd, Tokyo, Japan).
The UV-Vis absorption spectra of NdFe1−xCoxO3 nanocrystals were studied on a UV-Visible spectrophotometer (UV-Vis, JASCO V-550, Shimadzu, Tokyo, Japan). The optical energy gap (Eg, eV) was determined by fitting the absorption data to the direct transition as in previous publication [24].
Magnetic properties of the samples (the saturation magnetization Ms in the maximal field, the coercive force Hc and remanent magnetization Mr) were investigated at 300 K via a vibrating sample magnetometer (VSM, MICROSENE EV11, Tokyo, Japan).

3. Result and Discussion

3.1. Structures and Morphologies of Nanostructured NdFe1−xCoxO3

The XRD patterns of the NdFe1−xCoxO3 products (x = 0, 0.1, 0.2, 0.3, and 0.4) compared with those of the Nd2O3, Fe2O3, and Co3O4 component oxides independently prepared under similar conditions (annealed at 750 °C during 60 min) are shown in Figure 1. The annealing condition was determined according to the previous work [21]. Those patterns confirmed that the NdFe1−xCoxO3 samples with x = 0, 0.1, 0.2, and 0.3 were pure orthoferrite phase perovskite structure (NdFeO3, JCPDS No. 01-074-1473), with no identified peaks of oxide impurities. Interestingly, Co3O4 oxide was obtained instead of CoO since Co(OH)2 hydroxide can be oxidized and decomposed after annealing at high temperature [24].
In the case of x = 0.4, aside from the peaks corresponding to the NdFeO3 phase, there were peaks of the Nd2O3 phase (JCPDS No. 00-041-1089) at 2θ = 25.71 and 30.74°, and Co3O4 phase (JCPDS No. 00-043-1003) at 2θ = 38.87°. Thus, the successful substitution of Co into NdFeO3 crystal structures only took place when x was less than 0.4. With the increase in Co concentration, the XRD peak shifted toward a higher 2θ (right shift) and gradually broadened while the intensity of peaks decreased. Consequently, there was a decrease in unit cell volume (from V = 238.56 to V = 233.29 Å3) and in crystal size (from DXRD = 28 ± 5 to DXRD = 19 ± 3 nm) Figure 2 and Table 1. Such a decrease is also a confirmation for the Co (III) substitution to Fe (III) in the NdFeO3 crystal lattice. The substitution of Fe3+ ions (rFe3+ = 0.65 Å [24]) by smaller Co3+ ions (rCo3+ = 0.55 Å [24]) led to the reduction of the unit cell parameters and crystal size following Vegard’s law, in which lattice parameters linearly varies with the degree of substitution of atoms or ions by others in ideal solid solution. The similar results were published in the previous research [12,13,18].
TEM images and particle size distribution for NdFe1−xCoxO3 samples (x = 0.1, 0.2, 0.3) are shown in Figure 3. As can be seen, the shape of the particles of the synthesized NdFe1−xCoxO3 samples is close to spherical, but agglomerates of particles are noticeable. For the NdFe0.9Co0.1O3 sample with the lowest level of cobalt doping, the particle size was in the range of 10–80 nm. The average particle diameter was 47 ± 5. For the other two samples (NdFe0.8Co0.2O3 and NdFe0.7Co0.3O3), the size of most particles was in the range of 20–70 nm. An analysis of the results of the size distribution of NdFe1−xCoxO3 particles Figure 3 allows us to conclude that the average crystallite size decreases monotonically with an increase in the dopant content in the synthesized samples. The lower values of Davg calculated based on the XRD data as compared to the TEM results were due to the peculiarities of the used methods. The determination of the average crystallite size by the calculation method according to the Debye–Scherrer formula leads to significant errors that can be caused by the choice of a mathematical model for analyzing the X-ray line profile for the determination of the particle size and the influence of various factors on the broadening effect of diffraction maxima. In addition, the diffraction method is volumetric and therefore determines the size of crystallites averaged over the entire volume, in contrast to electron microscopy, which is a local visual method for estimating the size of particles (not crystallites) [25]. TEM results, to a certain extent, depend on the possibility of investigating only a relatively small number of particles under real conditions and on the quality of preliminary dispersion of nanopowders, which introduces a certain amount of uncertainty into the obtained results. Nevertheless, transmission electron microscopy is a direct and accurate method for determining the size and shape of nanoobject particles.

3.2. Elemental Composition of NdFe1−xCoxO3 Samples

According to the EDX results, the composition of the obtained NdFe1−xCoxO3 samples included only Nd, Fe, Co, and O, and as the concentration of cobalt ions in the initial solutions increased, their content in the NdFe1−xCoxO3 samples increased Table 2. From Table 2 it follows that the real content of each element in the synthesized samples is quite close to their nominal composition.

3.3. Optical and Magnetic Properties of Nano-Structured NdFe1−xCoxO3 (x = 0, 0.1, 0.2, and 0.3) Materials

The magnetic and optical characterizations of the NdFe1−xCoxO3 (x = 0, 0.1, 0.2, and 0.3) nanomaterials (annealed at 750 °C for 60 min) were carried out at room temperature. The results prove that beside the structure, the substitution of Co in the NdFeO3 crystal lattice also impressively change the magnetic and optical properties of the samples Table 3 and Figure 4 and Figure 5.
Indeed, when the concentration of Co ions in NdFeO3 crystal lattice increased, all magnetic parameters, including Hc (258.22–416.04 Oe), Ms (0.93–0.98 emu/g), and Mr (0.13–0.18 emu/g) increased with the rise of Co concentration in the NdFeO3 lattice. In addition, these values were significantly higher than those of the original NdFeO3 material [21] (with the exception of Mr). It can be explained by the fact that the substitution of Co ions into the NdFeO3 lattice can intensify the magneto-crystalline anisotropy. Besides, Co substitution also led to a change in Fe–O–Fe angles, as well as the oxidation of a small amount of Fe3+ ions to Fe4+ ions, to compensate for the charge caused by the appearance of Co2+ at the sites of Fe3+. The similar phenomenon was also reported for HoFe1−xNixO3 [26], NdFe1−xNixO3 [27], GdFe1−xNixO3 [28], YFe1−xCoxO3 [18], and LaFe1−xNixO3 series [19]. Remarkably, under the same synthesis conditions, the magnetic parameters, especially Hc, of the NdFe1−xCoxO3 nano-crystalline perovskite oxides are higher than those of other perovskite oxides, such as YFe1−xMnxO3, YFe1−xCoxO3, and LaFe1−xNixO3 [17,18,19]. From those results, the magnetic properties of perovskite-type nanostructured materials can be easily tuned by varying the element and the degree of doping. This important feature of nanosized perovskites give them a wide variety of application in many different fields of magnetic materials.
The UV-Vis absorption spectra of the Co-doped NdFeO3 nanoparticles showed strong absorption in the ultraviolet (~300–400 nm) and visible light regions (~400–600 nm) Figure 4a. As the concentration of Co ions increased, there was a red-shift in the UV-Vis absorption spectra (toward the visible light region). The optical energy gaps (Eg, eV) of the NdFe1−xCoxO3 nanomaterials (x = 0, 0.1, 0.2, and 0.3) were calculated similarly to other publications [24,26] and are shown in Table 2 and Figure 4b. The estimated direct band gaps of all products are in the range of 2.06–1.46 eV and increase when Co content in NdFeO3 lattice increases. Particularly, the Co-doped NdFeO3 nanoparticles in this work exhibited much narrower band-gap compared to some other related orthoferrites synthesized by other methods. For instance, the direct band-gaps of NdFe1−xCoxO3 (x = 0–0.4) and HoFe1−xNixO3 (x = 0–0.5) nanoparticles were reported to be 3.35 ÷ 3.04 and 3.39 ÷ 3.28 eV, respectively [26,29], and the values for LaFe1−xTixO3 (x = 0.2 ÷ 0.8) nanoparticles prepared by co-precipitation technique were 2.05–2.61 eV [2]. The small band gaps of NdFe1−xCoxO3 can give an advantage for the application of this material series in photocatalysis, gas sensor, and electrode materials in solid oxide fuel cells [12,13,29,30,31].

4. Conclusions

The single-phase nanostructured NdFe1−xCoxO3 (x = 0, 0.1, 0.2, and 0.3) perovskites have been synthesized by the simple co-precipitation method. The maximum level of substitution of iron with cobalt, which was x < 0.4 (XRD) was established. At x = 0.4, the homogeneity region was impaired and a phase mixture, consisting of Nd2O3 and Co3O4 was formed.
Obtained Co-doped NdFeO3 nanoparticles, after annealing at 750 °C for 60 min, have their crystal size (DXRD = 25 ± 3 ÷ 19 ± 3 nm, DTEM = 47 ± 5 ÷ 42 ± 3 nm), unit cell volume (V = 238.56 ÷ 233.29 Å3).
The study of the effect of the degree of substitution in NdFe1−xCoxO3 crystals on their optical and magnetic characteristics showed that optical band-gap values (Eg = 2.06 ÷ 1.46 eV) decreased while the coercive force (Hc = 136.76 ÷ 416.06 Oe) and saturation magnetization (Ms = 0.80 ÷ 0.98 emu/g) increased with the increase of Co content. Co-doped NdFeO3 nanoparticles have low optical energy gaps and high coercivity, which are beneficial not only for application in photocatalysis, but also for hard magnetic devices (permanent magnets or recorders).

Author Contributions

Conceptualization, T.A.N. and T.L.P.; methodology, T.A.N.; validation, I.Y.M., V.O.M. and V.X.B.; formal analysis, T.L.T.N. and H.V.N.; investigation, V.X.B. and H.V.N.; data curation, T.A.N. and T.L.P.; writing—original draft preparation, T.A.N., T.L.T.N. and I.Y.M.; writing—review and editing, V.O.M. and V.X.B. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Data Availability Statement

Not Applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Ahmad, I.; Akhtar, M.J.; Siddique, M.; Iqbal, M.; Hasan, M.M. Origin of anomalous octahedral distortions and collapse of magnetic ordering in Nd1−xSrxFeO3 (0 ≤ x ≤ 0.5). Ceram. Int. 2013, 39, 8901–8909. [Google Scholar] [CrossRef]
  2. Sasikala, C.; Durairaj, N.; Baskaran, I.; Sathyaseelan, B.; Henini, M. Transition metal titanium (Ti) doped LaFeO3 nanoparticles for enhanced optical structure and magnetic properties. J. Alloys Compd. 2017, 712, 870–877. [Google Scholar] [CrossRef] [Green Version]
  3. Haron, W.; Thaweechai, T.; Wattanathana, W.; Laobuthee, A.; Manaspiya, H.; Veranitisagul, C.; Koonsaeng, N. Structure characteristics and dielectric properties of La1−xCoxFeO3 and LaFe1−xCoxO3 synthesized via metal organic complexes. Energy Procedia 2013, 34, 791–800. [Google Scholar] [CrossRef] [Green Version]
  4. Xu, J.J.; Xu, D.; Wang, Z.L.; Wang, H.G.; Zhang, L.L.; Zhang, X.B. Synthesis of perovskite-based porous La0.75Sr0.25MnO3 nanotubes as a highly efficient electrocatalyst for rechargeable lithium-oxygen batteries. Angew. Chem. Int. Ed. 2013, 52, 3887–3890. [Google Scholar] [CrossRef]
  5. Tijare, S.N.; Bakardjieva, S.; Subrt, J.; Joshi, M.V.; Rayalu, S.S.; Hishita, S.; Labhsetwar, N. Synthesis and visible light photocatalytic activity of nanocrystalline PrFeO3 perovskite for hydrogen generation in ethanol-water system. J. Chem. Sci. 2014, 125, 517–525. [Google Scholar] [CrossRef]
  6. Megarajan, S.K.; Rayalu, S.; Nishibori, M.; Labhsetwar, N. Improved catalytic activity of PrFeO3 (M = Co and Fe) perovskites: Synthesis of thermally stable nanoparticles by a novel hydrothermal method. N. J. Chem. 2015, 39, 2345–2348. [Google Scholar] [CrossRef]
  7. Shin, N.; Isao, A.; Yasuhiko, I.; Takeo, H. Preparation of Y(Mn1−xFex)O3 and electrical properties of the sintered bodies. Open J. Inorg. Chem. 2015, 5, 54514589. [Google Scholar]
  8. Fang, F.; Zhao, P.; Feng, N.; Wan, H.; Guan, G. Surface engineering on popous perovskite-type La0.6Sr0.4CoO3−δ nanotubes for an enhanced performance in diesel soot elimination. J. Hazadous Mater. 2020, 399, 123014. [Google Scholar] [CrossRef]
  9. Mir, F.A.; Sharma, S.K.; Kumar, R. Magnetizations and magneto-transport properties of Ni-doped PrFeO3 thin films. Chin. Phys. B 2014, 23, 048101. [Google Scholar] [CrossRef]
  10. Yuan, S.J.; Ren, W.; Hong, F.; Wang, Y.B.; Zhang, J.C.; Bellaiche, L.; Cao, S.X.; Cao, G. Spin switching and magnetization reversal in single-crystal NdFeO3. Phys. Rev. B 2013, 87, 184405. [Google Scholar] [CrossRef] [Green Version]
  11. Pekinchak, O.; Vasylechko, L.; Lutsyuk, I.; Vakhula, Y.; Prots, Y.; Cabrera, W.C. Sol-gel prepared nanoparticles of mixed praseodymium cobaltites ferrites. Nanoscale Res. Lett. 2016, 11, 75. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  12. Zhang, R.; Hu, J.; Han, Z.; Zhao, M.; Wu, Z.; Zhang, Y.; Qin, H. Electrical and CO-sensing properties of NdFe1−xCoxO3 perovskite system. J. Rare Earths 2010, 28, 591–595. [Google Scholar] [CrossRef]
  13. Feng, C.; Ruan, S.; Li, J.; Zou, B.; Luo, J.; Chen, W.; Dong, W.; Wu, F. Ethanol sensing properties of LaCoxFe1−xO3 nanoparticles: Effects of calcination temperature, Co-doping, and carbon nanotube-treatment. Sens. Actuators B Chem. 2011, 155, 232–238. [Google Scholar] [CrossRef]
  14. Zhou, Z.; Guo, L.; Yang, H.; Liu, Q.; Ye, F. Hydrothermal synthesis and magnetic properties of multiferroic rare-earth orthoferrites. J. Alloys Compd. 2014, 583, 21–31. [Google Scholar] [CrossRef]
  15. Nguyen, T.A.; Mittova, I.Y.; Almjasheva, O.V.; Kirillova, S.A.; Gusarov, V.V. Influence of the preparation conditions on the size and morphology of nanocrystalline lanthanum orthoferrite. Glass Phys. Chem. 2008, 34, 756–761. [Google Scholar]
  16. Nguyen, A.T.; Almjasheva, O.V.; Mittova, I.Y.; Stognei, O.V.; Soldatenko, S.A. Synthesis and magnetic properties of YFeO3 nanocrystals. Inorg. Mater. 2009, 45, 1304–1308. [Google Scholar]
  17. Nguyen, A.T.; Pham, V.N.; Nguyen, T.T.L.; Mittova, V.O.; Vo, Q.M.; Berezhnaya, M.V.; Mittova, I.Y.; Do, T.H.; Chau, H.D. Crystal structure and magnetic properties of perovskite YFe1−xMnxO3 nanopowders synthesized by co-precipitation method. Solid State Sci. 2019, 96, 105922. [Google Scholar] [CrossRef]
  18. Nguyen, T.A.; Chau, D.H.; Nguyen, L.T.T.; Mittova, V.O.; Do, H.T.; Mittova, I.Y. Structural and magnetic properties of YFe1−xCoxO3 (0.1 ≤ x ≤ 0.5) perovskite nanomaterials synthesized by co-precipitation method. Nanosyst. Phys. Chem. Math. 2018, 9, 424–429. [Google Scholar] [CrossRef]
  19. Nguyen, T.A.; Pham, V.N.T.; Le, H.T.; Chau, D.H.; Mittova, V.O.; Nguyen, L.T.T.; Dinh, D.A.; Hao, T.V.N.; Mittova, I.Y. Crystal structure and magnetic properties of LaFe1−xNixO3 nanomaterials prepared via a simple co-precipitation method. Ceram. Int. 2019, 45, 21768–21772. [Google Scholar] [CrossRef]
  20. Nguyen, T.A.; Pham, V.; Chau, D.H.; Mittova, V.O.; Mittova, I.Y.; Kopeychenko, E.L.; Nguyen, L.T.T.; Bui, V.X.; Nguyen, A.T.P. Effect of Ni substitution on phase transition, crystal structure and magnetic properties of nanostructured YFeO3 perovskite. J. Mol. Struct. 2020, 1215, 128293. [Google Scholar] [CrossRef]
  21. Nguyen, T.A.; Pham, V.; Pham, T.L.; Nguyen, L.T.T.; Mittova, I.Y.; Mittova, V.O.; Vo, L.N.; Nguyen, B.T.T.; Bui, V.X.; Viryutina, E.L. Simple synthesis of NdFeO3 by the so-precipitation method based on a study of thermal behaviors of Fe (III) and Nd (III) hydroxides. Crystals 2020, 10, 219. [Google Scholar] [CrossRef] [Green Version]
  22. Housecroft, C.E.; Sharpe, A.G. Inorganic Chemistry, 2nd ed.; Pearson, Prentice Hall: Upper Saddle River, NJ, USA, 2005; 950p. [Google Scholar]
  23. Yousefi, M.; Zeid, S.S.; Motlagh, M.K. Synthesis and characterization of nano-structured perovskite type neodymium orthoferrite NdFeO3. Curr. Chem. Lett. 2017, 6, 23–30. [Google Scholar] [CrossRef]
  24. Ghobadi, N. Band gap determination using absorption spectrum fitting procedure. Int. Nano Lett. 2013, 3, 2. [Google Scholar] [CrossRef] [Green Version]
  25. Knurova, M.V.; Mittova, I.Y.; Perov, N.S.; Al’myasheva, O.V.; Nguyen, T.A.; Mittova, V.O.; Bessalova, V.V.; Viryutina, E.L. Effect of the degree of doping on the size and magnetic properties of nanocrystals La1−xZnxFeO3 synthesized by the sol-gel method. Russ. J. Inorg. Chem. 2017, 62, 281–287. [Google Scholar] [CrossRef]
  26. Habib, Z.; Majid, K.; Ikram, M.; Sultan, K. Influence of Ni substitution at B-site for Fe3+ ions on morphological, optical, and magnetic properties of HoFeO3 ceramics. Appl. Phys. A Mater. Sci. Process. 2016, 12, 550. [Google Scholar] [CrossRef]
  27. Mir, S.A.; Ikram, M.; Asokan, K. Effect of Ni doping on optical, electrical and magnetic properties of Nd orthoferrite. J. Phys. Conf. Ser. 2014, 534, 012017. [Google Scholar] [CrossRef]
  28. Bashir, A.; Ikram, M.; Kumar, R.; Lisboa-Filho, P.N. Structural, electronic structure and magnetic studies of GdFe1−xNixO3 (x ≤ 0.5). J. Alloys Compd. 2012, 521, 183–188. [Google Scholar] [CrossRef]
  29. Somvanshi, A.; Husain, S.; Khan, W. Investigation of structure and physical properties of cobalt doped nano-crystalline neodymium orthoferrite. J. Alloys Compd. 2019, 778, 439. [Google Scholar] [CrossRef]
  30. Nguyen, T.A.; Nguyen, L.T.T.; Bui, V.X.; Nguyen, D.H.; Lieu, H.D.; Le, L.M.; Pham, V. Optical and magnetic properties of HoFeO3 nanocrystals prepared by a simple co-precipitation method using ethanol. J. Alloys Compd. 2020, 834, 155098. [Google Scholar] [CrossRef]
  31. Phokha, S.; Pinitsoontorn, S.; Maensiri, S.; Rujirawat, S. Structure, optical and magnetic properties of LaFeO3 nanoparticles prepared by polymerized complex method. J. Sol Gel Sci. Technol. 2014, 71, 333–341. [Google Scholar] [CrossRef]
Nanomaterials 11 00937 g001 550
Figure 1. X-ray powder diffraction (XRD) patterns of NdFe1−xCoxO3 samples (x = 0, 0.1, 0.2, 0.3, and 0.4) and Nd2O3, Fe2O3, and Co3O4 annealed at 750 °C for 60 min.
Figure 1. X-ray powder diffraction (XRD) patterns of NdFe1−xCoxO3 samples (x = 0, 0.1, 0.2, 0.3, and 0.4) and Nd2O3, Fe2O3, and Co3O4 annealed at 750 °C for 60 min.
Nanomaterials 11 00937 g001
Nanomaterials 11 00937 g002 550
Figure 2. Slow-scan XRD patterns of peak (112) of NdFe1−xCoxO3 samples annealed at 750 °C for 60 min.
Figure 2. Slow-scan XRD patterns of peak (112) of NdFe1−xCoxO3 samples annealed at 750 °C for 60 min.
Nanomaterials 11 00937 g002
Nanomaterials 11 00937 g003 550
Figure 3. Transmission electron microscopy (TEM) images and particle size distribution of NdFe1−xCoxO3 samples annealed at 750 °C.
Figure 3. Transmission electron microscopy (TEM) images and particle size distribution of NdFe1−xCoxO3 samples annealed at 750 °C.
Nanomaterials 11 00937 g003
Nanomaterials 11 00937 g004 550
Figure 4. (a) Room-temperature optical absorbance spectra and (b) plot of (Ahν)2 as a function of photon energy for NdFe1−xCoxO3 materials annealed at 750 °C for 60 min.
Figure 4. (a) Room-temperature optical absorbance spectra and (b) plot of (Ahν)2 as a function of photon energy for NdFe1−xCoxO3 materials annealed at 750 °C for 60 min.
Nanomaterials 11 00937 g004
Nanomaterials 11 00937 g005 550
Figure 5. Field dependence of the magnetization of NdFe1−xCoxO3 nanoparticles annealed at 750 °C for 60 min.
Figure 5. Field dependence of the magnetization of NdFe1−xCoxO3 nanoparticles annealed at 750 °C for 60 min.
Nanomaterials 11 00937 g005
Table
Table 1. Lattice parameters and crystallite sizes of NdFe1−xCoxO3 samples annealed at 750 °C for 60 min.
Table 1. Lattice parameters and crystallite sizes of NdFe1−xCoxO3 samples annealed at 750 °C for 60 min.
NdFe1−xCoxO32θo (112)Davg, nmLattice Constants, ÅV, Å3
XRDTEMabc
NdFeO3 [21]32.4928 ± 5-5.49905.59107.7592238.56
NdFe0.9Co0.1O332.5425 ± 347 ± 55.42575.59197.7638235.55
NdFe0.8Co0.2O332.5722 ± 245 ± 65.44255.52927.7616233.57
NdFe0.7Co0.3O332.6119 ± 342 ± 35.41135.55047.7673233.29
Table
Table 2. EDX results of NdFe1−xCoxO3 samples annealed at 750 °C for 60 min.
Table 2. EDX results of NdFe1−xCoxO3 samples annealed at 750 °C for 60 min.
Nominal Composition of SamplesElemental Composition (at. %)Real Composition of Samples
NdFeCoO
NdFeO318.25 ± 1.5720.45 ± 1.110.0061.30 ± 2.17NdFe1.120O3.359
NdFe0.9Co0.1O318.95 ± 1.0318.45 ± 1.071.43 ± 0.1761.17 ± 2.36NdFe0.973Co0.075O3.228
NdFe0.8Co0.2O319.01 ± 1.4216.03 ± 0.892.13 ± 0.3562.83 ± 3.21NdFe0.843Co0.112O3.305
NdFe0.7Co0.3O319.27 ± 1.3514.31 ± 0.735.41 ± 0.4261.01 ± 3.08NdFe0.743Co0.281O3.166
Table
Table 3. Optical and Magnetic characteristics of NdFe1−xCoxO3 nanomaterials annealed at 750 °C for 60 min.
Table 3. Optical and Magnetic characteristics of NdFe1−xCoxO3 nanomaterials annealed at 750 °C for 60 min.
NdFe1−xCoxO3Hc, OeMr, emu/gMs, emu/gEg, eV
NdFeO3 [21]136.760.680.802.06
NdFe0.9Co0.1O3258.220.130.931.74
NdFe0.8Co0.2O3395.790.150.971.53
NdFe0.7Co0.3O3416.060.180.981.46
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Nguyen, T.A.; Pham, T.L.; Mittova, I.Y.; Mittova, V.O.; Nguyen, T.L.T.; Nguyen, H.V.; Bui, V.X. Co-Doped NdFeO3 Nanoparticles: Synthesis, Optical, and Magnetic Properties Study. Nanomaterials 2021, 11, 937. https://doi.org/10.3390/nano11040937

AMA Style

Nguyen TA, Pham TL, Mittova IY, Mittova VO, Nguyen TLT, Nguyen HV, Bui VX. Co-Doped NdFeO3 Nanoparticles: Synthesis, Optical, and Magnetic Properties Study. Nanomaterials. 2021; 11(4):937. https://doi.org/10.3390/nano11040937

Chicago/Turabian Style

Nguyen, Tien Anh, Thanh Le Pham, Irina Yakovlevna Mittova, Valentina Olegovna Mittova, Truc Linh Thi Nguyen, Hung Van Nguyen, and Vuong Xuan Bui. 2021. "Co-Doped NdFeO3 Nanoparticles: Synthesis, Optical, and Magnetic Properties Study" Nanomaterials 11, no. 4: 937. https://doi.org/10.3390/nano11040937

APA Style

Nguyen, T. A., Pham, T. L., Mittova, I. Y., Mittova, V. O., Nguyen, T. L. T., Nguyen, H. V., & Bui, V. X. (2021). Co-Doped NdFeO3 Nanoparticles: Synthesis, Optical, and Magnetic Properties Study. Nanomaterials, 11(4), 937. https://doi.org/10.3390/nano11040937

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.