Next Article in Journal
Evaluation of Dosimetric Effect of Bone Scatter on Nanoparticle-Enhanced Orthovoltage Radiotherapy: A Monte Carlo Phantom Study
Next Article in Special Issue
An Efficient Voltammetric Sensor Based on Graphene Oxide-Decorated Binary Transition Metal Oxides Bi2O3/MnO2 for Trace Determination of Lead Ions
Previous Article in Journal
Reduced Graphene Oxide Derived from Low-Grade Coal for High-Performance Flexible Supercapacitors with Ultrahigh Cyclability
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 12
Issue 17
10.3390/nano12172990
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Synthesis of Co3O4 Nanoplates by Thermal Decomposition for the Colorimetric Detection of Dopamine

by
Zengmin Tang
1,
Ling Zhang
1,
Sijia Tang
1,
Junping Li
2,
Jianxiong Xu
1,
Na Li
3,
Lijian Xu
1 and
Jingjing Du
4,*
1
Hunan Key Laboratory of Biomedical Nanomaterials and Devices, College of Life Sciences and Chemistry, Hunan University of Technology, Zhuzhou 412007, China
2
Yichun Fangke Sewage Treatment Co., Ltd., Mingyue North Road 542, Yichun 336000, China
3
Hunan Key Laboratory of Electrochemical Green Metallurgy Technology, College of Materials and Advanced Manufacturing, Hunan University of Technology, Zhuzhou 412007, China
4
College of Packaging and Materials Engineering, Hunan University of Technology, Zhuzhou 412007, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2022, 12(17), 2990; https://doi.org/10.3390/nano12172990
Submission received: 5 August 2022 / Revised: 23 August 2022 / Accepted: 27 August 2022 / Published: 29 August 2022
(This article belongs to the Special Issue Nanomaterials-Based Electrochemical (Bio)Sensors: Design, Fabrication, and Applications)
Browse Figures
Review Reports Versions Notes

Abstract

:
Inorganic nanomaterials with enzyme-like activity have been attracting much attention due to their low cost, favorable stability, convenient storage, and simple preparation. Herein, Co3O4 nanoplates with a uniform nanostructure were prepared by the thermolysis of cobalt hydroxide at different temperatures, and the influence of the annealing temperature on the performance of the mimetic enzyme also was reported for the first time. The results demonstrated that Co3O4 nanoplates obtained at an annealing temperature of 200 °C possessed strong oxidase activity and efficiently catalyzed the oxidation of 3,3′,5,5′-tetramethylbenzidine (TMB) without the addition of hydrogen peroxide to generate the blue color product ox-TMB. Once the annealing temperature was increased to 500 °C and 800 °C, the oxidase activity of Co3O4 decreased rapidly, and was even inactivated. This might be attributed to the relatively large specific surface area of Co3O4 annealed at 200 °C. Besides this, based on the TMB-Co3O4 nanoplate system, a colorimetric analysis method was developed to detect dopamine with a limit of 0.82 μmol/L in a linear range from 1.6 μmol/L to 20 μmol/L.

1. Introduction

Dopamine is a well-known considerable catecholamine neurotransmitter in the human central nervous, cardiovascular, and hormone systems [1]. A deficient level of dopamine may cause Parkinson’s disease, and an excessive level of dopamine also may bring about abnormalities including schizophrenia and euphoria, etc. [2,3]. For the sake of convenience, it is necessary to develop point-of-care testing (POCT) for dopamine detection. The POCT system is an in vitro monitoring platform with a short turnout time; it can even can be operated by an unskilled user, which can promote the development of clinical testing and bring significant economic benefits [4]. Recently, various methods have been applied in POCT, such as fluorescence sensors, electrochemical methods, and colorimetric sensors [5,6,7,8,9,10,11].
In recent decades, electrochemical sensors to detect dopamine have received wide attention due to their facile operation and response [12,13,14]. However, the actual test experiments found that the research on the stability and reproducibility of the sensors still faces significant challenges. In addition, the recently developed colorimetric sensors based on oxidase-like nano-enzyme materials present a change in color and absorbance during the process of detecting dopamine, which also applies to the POCT system due to its low cost, simplicity, rapid measurement, and sensitive readout [15,16,17]. Compared with natural enzymes, nano-enzyme materials possess the advantage of high stability. The oxidase mimic can more effectively oxidize the colorless TMB into ox-TMB with a blue color in the absence of hydrogen peroxide [18]. The addition of dopamine can absorb the dissolved oxygen or reactive oxygen, eventually leading to the fading of the color and the reduction of absorbance. Recently, precious metal nanomaterials have been considered as promising oxidase mimic candidates for application in colorimetric sensors [19], such as gold nanoparticles [20], platinum nanoparticles [21], silver nanoparticles [22], gold–platinum alloy nanoparticles [23], and silver–platinum alloy nanoparticles [24], etc. However, their high cost and limited resources inhibit their development and wide application. Therefore, transitional metal oxides performing comparable oxidase-like activity have also received considerable attention as a low-cost and available alternative [25,26,27].
As a transitional oxide, Co3O4 is an important p-type semiconductor with wide applications in supercapacitors, batteries, and catalysis, etc. [28,29,30,31,32]. In addition, Co3O4 nanoparticles also exhibit the behavior of mimic enzymes, and have received much attention for colorimetric sensors, enzyme-mimicking catalyzers, and so on [33,34]. In 2012, Mu et al. first reported Co3O4 with a catalase-like activity, which was applied to detect the concentration of H2O2 [35]. Shortly afterward, Qin et al., in 2014, found that the synthesized Co3O4 showed oxidase-like activity and could oxidize TMB to form colored ox-TMB, which has been applied for the detection of sulfite in food [36]. These results also demonstrated the great potential of Co3O4 for the detection of dopamine [37].
Two-dimensional nanoparticles are particles with one dimension that is limited to the nanometer scale; they have received wide attention due to their unique shape, anisotropic physical and chemical properties, and high surface-to-volume ratios [38]. In this study, the Co3O4 nanoplates were synthesized by the thermal decomposition of the as-prepared precursor Co(OH)2 at different temperatures for 30 min. The mimic enzyme behaviors of Co3O4 obtained at different annealing temperatures were discussed. The oxidase activity of Co3O4 was evaluated by Michaelis–Menten. Eventually, performances such as the sensitivity, selectivity, and lowest detection limit in the detection of dopamine were investigated.

2. Chemical and Methods

The cobalt chloride hexahydrate (CoCl2 6H2O), glacial acetic acid (CH3COOH), sodium acetate (CH3COONa), branched polyethyleneimine solution (BPEI, Mw: 60,000, 50 wt% in water), octylamine (C8H19N), ethanol (C2H5OH), 3,3′,5,5′-tetramethylbenzidine (TMB), potassium chloride (KCl), magnesium chloride (MgCl2), ferric chloride(FeCl3), and cupric sulfate (CuSO4) were obtained from InnoChem science and technology Co. Ltd. (Beijing, China).
Regarding the fabrication of the Co3O4 nanoplates, Co3O4 nanoplates were prepared through two steps. First, Co(OH)2 was synthesized using the hydrothermal method, as described in the previous literature [39]. Briefly, 2 mmol CoCl2 was added to 10 mL distilled water in the presence of 0.06 g BPEI, and was agitated constantly at 90 °C in a water bath. Then, the reaction was caused by adding 1 mL octylamine, and was maintained for around 40 min. After cooling, washing, and separation, the precursor Co(OH)2 was obtained. The second step was the decomposition of Co(OH)2 at different temperatures (200, 500, and 800 °C) for 30 min in a tube furnace in order to fabricate Co3O4 nanoplates. The samples synthesized at different calcination temperatures were named Co3O4-200, Co3O4-500, and Co3O4-800.
Regarding the catalytic activity of the Co3O4 and kinetic analysis, briefly, 0.1 mL of various Co3O4 suspensions with a concentration of 3 mg/mL and 0.2 mL TMB with a concentration of 2 mmol/L were added to 2.7 mL CH3COOH-CH3COONa buffer solution (0.2 mol/L, pH = 4.0), and then the mixture was incubated at 40 °C for 30 min. In this system, the concentration of Co3O4 was 100 μg/mL, and the concentration of TMB was 133.3 μmol/L. Then, the ultraviolet–visible absorptions of the above solution between the range of 550–750 nm were recorded. The kinetic parameters were conducted at 40 °C using different concentrations of TMB whilst keeping the other conditions constant. Kinetic analysis was performed by recording the absorbance at 652 nm after incubation for 30 min at 40 °C. The corresponding Michaelis–Menten constant was calculated by a Lineweaver-Burk plot [37]:
1/υ = Km/Vm (1/[C] + 1/Km)
where Km is the Michaelis–Menten constant, which is an indicator of Co3O4-200’s affinity for its TMB, [C] is the concentration of TMB, υ is the initial velocity, and Vm represents the maximal reaction velocity.
Regarding the colorimetric detection of dopamine, for the dopamine analysis, the absorption spectra of mixtures containing Co3O4-200 (0.1 mL, 3 mg/mL), CH3COOH–CH3COONa buffer solution (2.7 mL, 0.2 mol/L), TMB (0.2 mL, 2 mmol/L), and dopamine with different concentrations from 1.6 to 20 μmol/L were recorded from 550 to 750 nm. The change of absorbance (△A = A0 − A, where A0 and A are the absorbances of the solution without and within the dopamine sample) at 652 nm versus the concentration of dopamine was applied to obtain the calibration curve. For the determation of the anti-interference performance, dopamine was detected in the presence of KCl, MgCl2, FeCl3, CuSO4, H2O2, glucose, and urea with a concentration of 100 μmol/L.
Regarding the characterization, the morphology of the samples was characterized using a scanning electron microscope (SEM, Zeiss Gemini 300, Jena, Germany). The crystal structure was analyzed by X-ray diffraction (XRD, Bruker D8, Karlsruhe, Germany). The absorption spectrum in the range of 550–750 nm was measured using a UV-vis spectrophotometer (TU-1901). The surface area was detected by BET (Nova, Quantachrome, Boynton Beach, FL, USA).

3. Results and Discussion

3.1. Fabrication of Co3O4 Nanoplates

Based on the previous synthetic strategy [39], the pre-prepared Co(OH)2 nanoplates were first prepared and employed as the precursor to fabricate the Co3O4 nanoplates by regulating the annealing temperature. The thermal decomposition reaction only took 30 min at the designed temperature. The surface structure and oxidase-mimic activity of the Co3O4 nanoplates were significantly affected by the annealing temperature, as shown in Scheme 1.
Powder XRD was used to characterize the crystal structure of the samples. Compared with the XRD pattern of Co(OH)2 (Figure 1a), the XRD pattern of Co3O4-200 in Figure 1b changes with the intensity of the peaks and the new diffraction peaks. Several weak diffraction peaks at 2θ = 19.0°, 31.3°, 36.8°, 44.8°, 59.3°, and 65.2° were assigned to the (111), (220), (311), (400), (511), and (440) crystal facets of cubic phase Co3O4, respectively. Besides this, the crystal structures of the products are not affected by the higher calcination temperatures, such as 500 °C and 800 °C. Therefore, calcination at 200 °C for 30 min can achieve the transformation of Co3O4 from Co(OH)2, which is 20 times shorter than the calcination time reported in the previous research [40].
SEM was applied to observe the morphology of samples obtained at the different annealing temperatures. The SEM image in Figure 2a confirms that the precursor Co(OH)2 presents a hexagonal plate shape with a smooth surface, which is consistent with the previous study [39]. After the thermal decomposition of Co(OH)2 nanoplates at 200 °C for 30 min, a black powder was obtained. As shown in the SEM image in Figure 2b, the obtained Co3O4-200 remains in the shape of a hexagonal plate with a size range of 2–15 μm. Compared with Co(OH)2, cracks on the surface of the black samples can be observed due to the evaporation of water produced in the process of the thermal decomposition of Co(OH)2. In addition, the cracks are supposed to increase the surface area, and should eventually enhance the adsorption capacity and catalytic capacity. The surface structure of the samples hardly changed at the temperature of 500 °C (Figure 2c). As the temperature increased to 800 °C, pore structures were produced due to the fusion and recrystallization of the samples in the process at a high calcination temperature (Figure 2d). As shown in Table 1, the Co3O4-200 nanoplates have a relatively large specific surface area, which is 15 times greater than the specific surface area of the Co3O4-500 and Co3O4-800. The Co3O4-800 presented a macropore structure, and the process of fusion and recrystallization would cause agglomeration, as shown in the insert SEM image in Figure 2d. In addition, the distribution of pore and pore size also was not uniform. Therefore, the sample Co3O4-800 has a lower surface area according to the comprehensive analysis combined with agglomeration and uneven macropores.

3.2. Oxidase-like Activity of the Co3O4 Nanoplates

The oxidase-like activities of various types of Co3O4 were investigated by the catalytic oxidation of TMB in the absence of hydrogen peroxide, and the corresponding absorption at the range of wavelength from 550–750 nm was measured after incubation at 40 °C for 30 min. The results are shown in Figure 3a. Curve 1 demonstrates that the direct oxidation of TMB by dissolved oxygen in the absence of Co3O4 can be ignored. The obtained Co3O4-200 nanoplates can catalyze the oxidation of colorless TMB to produce a blue product (ox-TMB), which has an obvious absorption peak at 652 nm (curve 4). On the contrary, the very weak absorption peaks in curve 2 and curve 3 reveal the sharply weakened oxidase enzyme behavior of the Co3O4-500 and Co3O4-800 nanoplates. Therefore, the oxidase activity of the obtained Co3O4 is seriously affected by the annealing temperature. In the process of catalysis, through adsorption for dissolved oxygen on the surface, the Co3O4 nanoplates are capable of catalyzing the dissolved oxygen to release reactive oxygen species accompanied by the oxidation of Co2+ to Co3+ [41]. In various reactive oxygen species, superoxide anions (O2−) acted as the main reactive oxygen species for the oxidation of TMB to blue ox-TMB. Due to its loose surface structure and larger surface area, Co3O4-200 nanoplates can adsorb and catalyze more dissolved oxygen to release more superoxide anions, showing stronger catalytic activity for the oxidation of TMB. The curve in Figure 3b demonstrates that the oxidation of TMB catalyzed by Co3O4-200 needs to take around 24 min to enter the steady state.
In order to better understand the Co3O4 nanoplates’ performance of an oxidase-like activity, the kinetic parameters of TMB alone were determined by varying the concentration of TMB, keeping the concentration of Co3O4 constant at 3 mg/mL. The absorbance change versus the concentration of TMB at 652 nm for 30 min is shown in Figure 3c. A typical Michaelis–Menten curve is shown in Figure 3d. The Michaelis–Menten constant (Km) and maximum initial velocity (Vm) for the Co3O4-200 nanoplate with TMB are 0.058 mmol/L and 1.27 μmol/(L·s), which are greater than the kinetic parameters reported for Co3O4, Co3O4/CuO, and CoOOH [35,37,42]. It is suggested that synthesized Co3O4-200 nanoplates possess a high affinity for TMB.
Additionally, the effects of temperature and pH on the oxidase-like activity of Co3O4 were explored. Firstly, the TMB-Co3O4-200 suspension was incubated for 30 min at different temperatures while the pH was maintained at 4.0. The absorbance was recorded, and is shown in Figure 4a,b, which shows a similar absorbance in the range of 20 to 60 °C and a decrease of absorbance as the temperature increases to 70 °C. Then, the pH of the CH3COOH-CH3COONa buffer solution was controlled at 3.6, 4.0, 4.4, 4.8, and 5.2 as the temperature was kept at 40 °C. Figure 4c,d demonstrates that Co3O4 nanoplates possess a good oxidase-like activity at a pH of 3.6–4.4. The absorbance decreases once the pH rises to 4.8 and 5.2. Therefore, the results illustrate that the Co3O4 can maintain a high oxidase-like activity in a wide temperature range from 20 to 60 °C with a pH of around 4.0.

3.3. Detection of Dopamine Employing the Co3O4 Nanoplates

As we found above, Co3O4-200 can be used as an oxidase mimic, and can catalyze TMB to produce colored ox-TMB without the presence of hydrogen peroxide. In this research, in order to investigate the applicability of the oxidase-like Co3O4-200, colorimetric detection for dopamine was conducted due to its inhibiting effect on the oxidase-like Co3O4-200 nanoplates. Figure 5a shows that the blue color gradually fades with the increasing concentration of dopamine. Figure 5b further shows that the absorbance of the Co3O4-TMB mixtures at 652 nm also gradually reduce with the increase of the dopamine concentration from 1.6 μmol/L to 25 μmol/L, and a further increase in the concentration of dopamine only has a minor change in absorbance. The fading of the blue demonstrates that the oxidase-like mimic of Co3O4-200 is inhibited by dopamine. This might be attributed to the fact that dopamine can induce the reduction of ox-TMB, or that dopamine more easily consumes the dissolved oxygen, which eventually leads to the decrease of the amounts of reactive oxygen species [43]. The corresponding ΔA versus the concentration of dopamine is shown in Figure 5c, which demonstrates that the concentration of detectible dopamine is around 1.6 μmol/L in a linear range from 1.6 μmol/L to 20 μmol/L. The limit of detection (LOD) for dopamine is as low as 0.82 μmol/L (S/N = 3).

3.4. Analytic Performance for the Selectivity of Dopamine Detection

Selectivity is an important property of mimetic enzymes. Figure 6 shows the selectivity of oxidase Co3O4-200 for dopamine detection in the presence of various substances, including K+, Mg2+, Fe3+, Cu2+, Cl−, SO42−, H2O2, glucose, and urea. The absorbance of the TMB-buffer-Co3O4-200 system at 652 nm shows a significant decrease in the presence of 10 μmol/L dopamine, while there are no significant changes in the absorbance for other substances with a concentration of 50 μmol/L. These results indicate that the oxidase Co3O4-200 displays good selectivity for the detection of dopamine.

4. Conclusions

Herein, Co3O4 nanoplates synthesized by thermal deposition possessed oxidase activity. The annealing temperature played an important role in tuning the oxidase activity of Co3O4 nanoplates. In these samples, Co3O4 nanoplates obtained at an annealing temperature of 200 °C showed excellent oxidase activity due to their relatively large specific surface area and loose structure. As oxidase mimics, Co3O4 nanoplates were employed to develop a colorimetric sensor of dopamine with a limit of 0.82 μmol/L in a linear range from 1.6 μmol/L to 20 μmol/L.

Author Contributions

Conceptualization, Z.T. and J.D.; Methodology, Z.T.; validation, Z.T., L.Z., S.T. and J.L.; formal analysis, J.X.; investigation, N.L.; resources, L.X.; data curation, Z.T.; writing—original draft preparation, Z.T; writing—review and editing, L.X. and J.D.; project administration, L.X. and J.D. All authors have read and agreed to the published version of the manuscript.

Funding

Projects 51974116 and 51874128 were supported by the National Science Foundation of China; Projects 2020JJ4273 and 2020JJ5130 were supported by the Science Foundation of Hunan Province.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. He, Q.; Liu, J.; Liu, X.; Li, G.; Deng, P.; Liang, J. Preparation of Cu2O-reduced graphene nanocomposite modified electrodes towards ultrasensitive dopamine detection. Sensors 2018, 18, 199. [Google Scholar] [CrossRef] [PubMed]
  2. Liu, X.; Liu, J. Biosensors and sensors for dopamine detection. View 2021, 2, 20200102. [Google Scholar] [CrossRef]
  3. Gitler, A.D.; Dhillon, P.; Shorter, J. Neurodegenerative disease: Models, mechanisms, and a new hope. Dis. Models Mech. 2017, 10, 499–502. [Google Scholar] [CrossRef] [PubMed]
  4. Yang, J.; Wang, K.; Xu, H.; Yan, W.; Jin, Q.; Cui, D. Detection platforms for point-of-care testing based on colorimetric, luminescent and magnetic assays: A review. Talanta 2019, 202, 96–110. [Google Scholar] [CrossRef] [PubMed]
  5. He, Z.; Tong, Z.; Tan, B.; He, X.; Zhang, T.; Guo, Y.; Jin, L.; He, N.; Li, S.; Chen, Z. Rapid Detection of DNA Methylation with a Novel Real-Time Fluorescence Recombinase-Aided Amplification Assay. J. Biomed. Nanotechnol. 2021, 17, 1364–1370. [Google Scholar] [CrossRef]
  6. Li, T.; Yi, H.; Liu, Y.; Wang, Z.; Liu, S.; He, N.; Liu, H.; Deng, Y. One-step synthesis of DNA templated water-soluble Au–Ag bimetallic nanoclusters for ratiometric fluorescence detection of DNA. J. Biomed. Nanotechnol. 2018, 14, 150–160. [Google Scholar] [CrossRef]
  7. Yang, H.; Liu, M.; Jiang, H.; Zeng, Y.; Jin, L.; Luan, T.; Deng, Y.; He, N.; Zhang, G.; Zeng, X. Copy number variation analysis based on gold magnetic nanoparticles and fluorescence multiplex ligation-dependent probe amplification. J. Biomed. Nanotechnol. 2017, 13, 655–664. [Google Scholar] [CrossRef]
  8. He, Q.; Liu, J.; Liu, X.; Li, G.; Chen, D.; Deng, P.; Liang, J. Fabrication of amine-modified magnetite-electrochemically reduced graphene oxide nanocomposite modified glassy carbon electrode for sensitive dopamine determination. Nanomaterials 2018, 8, 194. [Google Scholar] [CrossRef]
  9. Liu, J.; Sun, L.; Li, G.; Hu, J.; He, Q. Ultrasensitive detection of dopamine via electrochemical route on spindle-like α-Fe2O3 Mesocrystals/rGO modified GCE. Mater. Res. Bull. 2021, 133, 111050. [Google Scholar] [CrossRef]
  10. Li, F.; Ni, B.; Zheng, Y.; Huang, Y.; Li, G. A simple and efficient voltammetric sensor for dopamine determination based on ZnO nanorods/electro-reduced graphene oxide composite. Surf. Interfaces 2021, 26, 101375. [Google Scholar] [CrossRef]
  11. Wu, Y.; Deng, P.; Tian, Y.; Feng, J.; Xiao, J.; Li, J.; Liu, J.; Li, G.; He, Q. Simultaneous and sensitive determination of ascorbic acid, dopamine and uric acid via an electrochemical sensor based on PVP-graphene composite. J. Nanobiotechnol. 2020, 18, 112. [Google Scholar] [CrossRef] [PubMed]
  12. Li, G.; Zhong, P.; Ye, Y.; Wan, X.; Cai, Z.; Yang, S.; Xia, Y.; Li, Q.; Liu, J.; He, Q. A highly sensitive and stable dopamine sensor using shuttle-like α-Fe2O3 nanoparticles/electro-reduced graphene oxide composites. J. Electrochem. Soc. 2019, 166, B1552. [Google Scholar] [CrossRef]
  13. He, Q.; Liu, J.; Liu, X.; Li, G.; Chen, D.; Deng, P.; Liang, J. A promising sensing platform toward dopamine using MnO2 nanowires/electro-reduced graphene oxide composites. Electrochim. Acta 2019, 296, 683–692. [Google Scholar] [CrossRef]
  14. Liu, H.; Xiong, R.; Zhong, P.; Li, G.; Liu, J.; Wu, J.; Liu, Y.; He, Q. Nanohybrids of shuttle-like α-Fe2O3 nanoparticles and nitrogen-doped graphene for simultaneous voltammetric detection of dopamine and uric acid. New J. Chem. 2020, 44, 20797–20805. [Google Scholar] [CrossRef]
  15. Liu, X.; He, F.; Zhang, F.; Zhang, Z.; Huang, Z.; Liu, J. Dopamine and melamine binding to gold nanoparticles dominates their aptamer-based label-free colorimetric sensing. Anal. Chem. 2020, 92, 9370–9378. [Google Scholar] [CrossRef]
  16. Chen, Q.; Liang, C.; Zhang, X.; Huang, Y. High oxidase-mimic activity of Fe nanoparticles embedded in an N-rich porous carbon and their application for sensing of dopamine. Talanta 2018, 182, 476–483. [Google Scholar] [CrossRef]
  17. Liang, L.; Zhao, Z.; Ye, F.; Zhao, S. Rapid and sensitive colorimetric detection of dopamine based on the enhanced-oxidase mimicking activity of cerium (IV). New J. Chem. 2021, 45, 6780–6786. [Google Scholar] [CrossRef]
  18. Wang, H.; Wan, K.; Shi, X. Recent advances in nanozyme research. Adv. Mater. 2019, 31, 1805368. [Google Scholar] [CrossRef]
  19. Chen, W.; Li, S.; Wang, J.; Sun, K.; Si, Y. Metal and metal-oxide nanozymes: Bioenzymatic characteristics, catalytic mechanism, and eco-environmental applications. Nanoscale 2019, 11, 15783–15793. [Google Scholar] [CrossRef]
  20. Lou-Franco, J.; Das, B.; Elliott, C.; Cao, C. Gold nanozymes: From concept to biomedical applications. Nano-Micro Lett. 2021, 13, 10. [Google Scholar] [CrossRef]
  21. Deng, H.; He, S.; Lin, X.; Yang, L.; Lin, Z.; Chen, R. Target-triggered inhibiting oxidase-mimicking activity of platinum nanoparticles for ultrasensitive colorimetric detection of silver ion. Chin. Chem. Lett. 2019, 30, 1659–1662. [Google Scholar] [CrossRef]
  22. Xu, D.; Li, R.; Wang, Q.; Yang, Y.; Wang, G.; Li, Z. Synthesis of silver nanocrystal with an excellent oxidase-like activity and its application in colorimetric detection of D-penicillamine. Microchem. J. 2021, 166, 106204. [Google Scholar]
  23. Chi, H.; Cui, X.; Lu, Y.; Yu, M.; Fei, Q.; Feng, G. Colorimetric determination of cysteine based on Au@Pt nanoparticles as oxidase mimetics with enhanced selectivity. Microchim. Acta 2022, 189, 13. [Google Scholar] [CrossRef] [PubMed]
  24. Cai, S.; Jia, X.; Han, Q.; Yan, X.; Yang, R.; Wang, C. Porous Pt/Ag nanoparticles with excellent multifunctional enzyme mimic activities and antibacterial effects. Nano Res. 2017, 10, 2056–2069. [Google Scholar] [CrossRef]
  25. Chen, Z.J.; Huang, Z.; Sun, Y.M.; Xu, Z.L.; Liu, J. The most active oxidase-mimicking Mn2O3 nanozyme for biosensor signal generation. Chem. Eur. J. 2021, 27, 9597–9604. [Google Scholar] [CrossRef]
  26. Wang, X.; Feng, S.; He, D.; Jiang, P. Porous manganese–cobalt oxide microspheres with tunable oxidase mimicking activity for sulfide ion colorimetric detection. Chem. Commun. 2020, 56, 14098–14101. [Google Scholar] [CrossRef]
  27. Huang, L.; Zhang, W.; Chen, K.; Zhu, W.; Liu, X.; Wang, R.; Zhang, X.; Hu, N.; Suo, Y.; Wang, J. Facet-selective response of trigger molecule to CeO2{110} for up-regulating oxidase-like activity. Chem. Eng. J. 2017, 330, 746–752. [Google Scholar] [CrossRef]
  28. Lu, Y.; Liu, Y.; Mo, J.; Deng, B.; Wang, J.; Zhu, Y.; Xiao, X.; Xu, G. Construction of hierarchical structure of Co3O4 electrode based on electrospinning technique for supercapacitor. J. Alloys Compd. 2021, 853, 157271. [Google Scholar] [CrossRef]
  29. Li, N.; Yuan, K.; Gao, T.; Li, S.; Qin, J.; Zhu, Y.; Du, J.; Xu, L.; Xu, J. Controllable synthesis of hierarchical nanoporous carbon@Ni(OH)2 rambutan-like composite microspheres for high-performance hybrid supercapacitor. Arab. J. Chem. 2022, 15, 103580. [Google Scholar] [CrossRef]
  30. Cordeiro, P.V.O.; Carvalho, N.M. Water oxidation reaction catalyzed by Co3O4 treated with organic compounds. Ind. Eng. Chem. Res. 2018, 57, 11259–11264. [Google Scholar] [CrossRef]
  31. Yi, C.; Zou, J.; Yang, H.; Leng, X. A facile hydrothermal synthesis of graphene/RuO2/Co3O4 nanocomposites with high pseudocapacity. New J. Chem. 2018, 42, 7066–7072. [Google Scholar] [CrossRef]
  32. Zhang, J.; Feng, J.; Tian, Y.; Wu, Y.; Liu, X.; He, Q. Ultrasensitive electrochemical determination of tyrosine based on the α-Fe2O3@ Co3O4-NRGO modified electrode. Microchem. J. 2021, 171, 106867. [Google Scholar] [CrossRef]
  33. Wang, T.; Su, P.; Li, H.; Yang, Y.; Yang, Y. Triple-enzyme mimetic activity of Co3O4 nanotubes and their applications in colorimetric sensing of glutathione. New J. Chem. 2016, 40, 10056–10063. [Google Scholar] [CrossRef]
  34. Liu, X.; Yan, L.; Ren, H.; Cai, Y.; Liu, C.; Zeng, L.; Guo, J.; Liu, A. Facile synthesis of magnetic hierarchical flower-like Co3O4 spheres: Mechanism, excellent tetra-enzyme mimics and their colorimetric biosensing applications. Biosens. Bioelectron. 2020, 165, 112342. [Google Scholar] [CrossRef]
  35. Mu, J.; Wang, Y.; Zhao, M.; Zhang, L. Intrinsic peroxidase-like activity and catalase-like activity of Co3O4 nanoparticles. Chem. Commun. 2012, 48, 2540–2542. [Google Scholar] [CrossRef] [PubMed]
  36. Qin, W.; Su, L.; Yang, C.; Ma, Y.; Zhang, H.; Chen, X. Colorimetric detection of sulfite in foods by a TMB–O2–Co3O4 nanoparticles detection system. J. Agric. Food Chem. 2014, 62, 5827–5834. [Google Scholar] [CrossRef] [PubMed]
  37. Zhuang, Y.; Zhang, X.; Chen, Q.; Li, S.; Cao, H.; Huang, Y. Co3O4/CuO hollow nanocage hybrids with high oxidase-like activity for biosensing of dopamine. Mater. Sci. Eng. C 2019, 94, 858–866. [Google Scholar] [CrossRef]
  38. Chimene, D.; Alge, D.L.; Gaharwar, A.K. Two-Dimensional Nanomaterials for Biomedical Applications: Emerging Trends and Future Prospects. Adv. Mater. 2015, 27, 7261–7284. [Google Scholar] [CrossRef]
  39. Wen, P.; Huang, J.; Kang, M.; Chen, S.; Xu, L.; Tang, Z. A facile synthesis of cobalt hydroxide nanoplates and electrochemical performance in supercapacitor application. Mater. Express 2021, 11, 551–556. [Google Scholar]
  40. Xu, L.; Zhang, L.; Tang, S.; Tang, Z. Preparation of Co3O4 and Its Application in Electrochemical Detection of H2O2. Packaing J. 2022, 14, 1–8. [Google Scholar]
  41. Zhao, Q.; Zheng, X.Y.; Xing, L.; Tang, Y.L.; Zhou, X.M.; Hu, L.; Yao, W.L.; Yan, Z.Q. 2D Co3O4 stabilizing Rh nano composites developed for visual sensing bioactive urea and toxic p-aminophenol in practice by synergetic-reinforcing oxidase activity. J. Hazard. Mater. 2021, 409, 125019. [Google Scholar] [CrossRef] [PubMed]
  42. Wang, Y.M.; Liu, J.W.; Jiang, J.H.; Zhong, W. Cobalt oxyhydroxide nanoflakes with intrinsic peroxidase catalytic activity and their application to serum glucose detection. Anal. Bioanal. Chem. 2017, 409, 4225–4232. [Google Scholar] [CrossRef] [PubMed]
  43. Darbin, O. The aging striatal dopamine function. Parkinsonism Relat. Disord. 2012, 18, 426–432. [Google Scholar] [CrossRef] [PubMed]
Nanomaterials 12 02990 sch001 550
Scheme 1. Schematic diagrams for (a) the synthetic pathway and (b) the oxidase performance of the Co3O4 nanoplates.
Scheme 1. Schematic diagrams for (a) the synthetic pathway and (b) the oxidase performance of the Co3O4 nanoplates.
Nanomaterials 12 02990 sch001
Nanomaterials 12 02990 g001 550
Figure 1. XRD patterns of (a) Co(OH)2 and (b) Co3O4.
Figure 1. XRD patterns of (a) Co(OH)2 and (b) Co3O4.
Nanomaterials 12 02990 g001
Nanomaterials 12 02990 g002 550
Figure 2. SEM image of samples including (a) Co(OH)2, (b) Co3O4-200, (c) Co3O4-500, and (d) Co3O4-800.
Figure 2. SEM image of samples including (a) Co(OH)2, (b) Co3O4-200, (c) Co3O4-500, and (d) Co3O4-800.
Nanomaterials 12 02990 g002
Nanomaterials 12 02990 g003 550
Figure 3. (a) Reaction between Co3O4 and TMB (curve 1-TMB + buffer, curve 2-TMB + buffer + Co3O4-800, curve 3-TMB + buffer + Co3O4-500, curve 4-TMB + buffer + Co3O4-200), (b) the absorbance change of TMB in the presence of Co3O4-200 over the time at 40 °C, (c) the absorbance change for different concentrations of TMB, and (d) the Michaelis–Menten curve of Co3O4-200 with TMB.
Figure 3. (a) Reaction between Co3O4 and TMB (curve 1-TMB + buffer, curve 2-TMB + buffer + Co3O4-800, curve 3-TMB + buffer + Co3O4-500, curve 4-TMB + buffer + Co3O4-200), (b) the absorbance change of TMB in the presence of Co3O4-200 over the time at 40 °C, (c) the absorbance change for different concentrations of TMB, and (d) the Michaelis–Menten curve of Co3O4-200 with TMB.
Nanomaterials 12 02990 g003
Nanomaterials 12 02990 g004 550
Figure 4. Effect of temperature (a,b) and pH (c,d) on the oxidase-like activity of Co3O4-200.
Figure 4. Effect of temperature (a,b) and pH (c,d) on the oxidase-like activity of Co3O4-200.
Nanomaterials 12 02990 g004
Nanomaterials 12 02990 g005 550
Figure 5. (a) Visual color changes of TMB-buffer-Co3O4-200 with the increase of the concentration of dopamine, (b) the corresponding UV-vis absorption spectra, and (c) the plots of the net absorbance (ΔA) with the concentration of dopamine.
Figure 5. (a) Visual color changes of TMB-buffer-Co3O4-200 with the increase of the concentration of dopamine, (b) the corresponding UV-vis absorption spectra, and (c) the plots of the net absorbance (ΔA) with the concentration of dopamine.
Nanomaterials 12 02990 g005
Nanomaterials 12 02990 g006 550
Figure 6. Change of △A in the presence of various substances.
Figure 6. Change of △A in the presence of various substances.
Nanomaterials 12 02990 g006
Table
Table 1. Specific surface area of the samples.
Table 1. Specific surface area of the samples.
SamplesSpecific Surface Area (m2/g)
Co3O4-20080.472
Co3O4-5006.796
Co3O4-8005.158
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Tang, Z.; Zhang, L.; Tang, S.; Li, J.; Xu, J.; Li, N.; Xu, L.; Du, J. Synthesis of Co3O4 Nanoplates by Thermal Decomposition for the Colorimetric Detection of Dopamine. Nanomaterials 2022, 12, 2990. https://doi.org/10.3390/nano12172990

AMA Style

Tang Z, Zhang L, Tang S, Li J, Xu J, Li N, Xu L, Du J. Synthesis of Co3O4 Nanoplates by Thermal Decomposition for the Colorimetric Detection of Dopamine. Nanomaterials. 2022; 12(17):2990. https://doi.org/10.3390/nano12172990

Chicago/Turabian Style

Tang, Zengmin, Ling Zhang, Sijia Tang, Junping Li, Jianxiong Xu, Na Li, Lijian Xu, and Jingjing Du. 2022. "Synthesis of Co3O4 Nanoplates by Thermal Decomposition for the Colorimetric Detection of Dopamine" Nanomaterials 12, no. 17: 2990. https://doi.org/10.3390/nano12172990

APA Style

Tang, Z., Zhang, L., Tang, S., Li, J., Xu, J., Li, N., Xu, L., & Du, J. (2022). Synthesis of Co3O4 Nanoplates by Thermal Decomposition for the Colorimetric Detection of Dopamine. Nanomaterials, 12(17), 2990. https://doi.org/10.3390/nano12172990

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop