Next Article in Journal
Hydrothermal and Entropy Investigation of Nanofluid Natural Convection in a Lid-Driven Cavity Concentric with an Elliptical Cavity with a Wavy Boundary Heated from Below
Next Article in Special Issue
2D Material and Perovskite Heterostructure for Optoelectronic Applications
Previous Article in Journal
Promoted Mid-Infrared Photodetection of PbSe Film by Iodine Sensitization Based on Chemical Bath Deposition
Previous Article in Special Issue
Optical Mode Tuning of Monolayer Tungsten Diselenide (WSe2) by Integrating with One-Dimensional Photonic Crystal through Exciton–Photon Coupling
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 12
Issue 9
10.3390/nano12091393
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Observation of Strong Interlayer Couplings in WS2/MoS2 Heterostructures via Low-Frequency Raman Spectroscopy

by
Ki Hoon Shin
1,†,
Min-Kyu Seo
1,†,
Sangyeon Pak
2,
A-Rang Jang
3,* and
Jung Inn Sohn
1,*
1
Division of Physics and Semiconductor Science, Dongguk University, Seoul 04620, Korea
2
School of Electronic and Electrical Engineering, Hongik University, Seoul 04066, Korea
3
Department of Electrical Engineering, Semyung University, Jecheon 27136, Korea
*
Authors to whom correspondence should be addressed.
†
These authors contributed equally to this work.
Nanomaterials 2022, 12(9), 1393; https://doi.org/10.3390/nano12091393
Submission received: 21 March 2022 / Revised: 14 April 2022 / Accepted: 16 April 2022 / Published: 19 April 2022
(This article belongs to the Special Issue 2D Nanostructures for Optoelectronic and Green Energy Devices)
Browse Figures
Review Reports Versions Notes

Abstract

:
Van der Waals (vdW) heterostructures based on two-dimensional (2D) transition metal dichalcogenides (TMDCs), particularly WS2/MoS2 heterostructures with type-II band alignments, are considered as ideal candidates for future functional optoelectronic applications owing to their efficient exciton dissociation and fast charge transfers. These physical properties of vdW heterostructures are mainly influenced by the interlayer coupling occurring at the interface. However, a comprehensive understanding of the interlayer coupling in vdW heterostructures is still lacking. Here, we present a detailed analysis of the low-frequency (LF) Raman modes, which are sensitive to interlayer coupling, in bilayers of MoS2, WS2, and WS2/MoS2 heterostructures directly grown using chemical vapor deposition to avoid undesirable interfacial contamination and stacking mismatch effects between the monolayers. We clearly observe two distinguishable LF Raman modes, the interlayer in-plane shear and out-of-plane layer-breathing modes, which are dependent on the twisting angles and interface quality between the monolayers, in all the 2D bilayered structures, including the vdW heterostructure. In contrast, LF modes are not observed in the MoS2 and WS2 monolayers. These results indicate that our directly grown 2D bilayered TMDCs with a favorable stacking configuration and high-quality interface can induce strong interlayer couplings, leading to LF Raman modes.

1. Introduction

Two-dimensional (2D) transition metal dichalcogenides (TMDCs), such as MoS2 and WS2, have attracted significant attention for flexible and transparent electronics and optoelectronics applications because of their superior mechanical, electrical, and optical properties, such as high mobility, good mechanical strength, superior transparency, and excellent flexibility, as well as strong light–matter interactions [1,2,3,4,5,6]. TMDCs have considered to be promising nanomaterials for nanoelectronics, optoelectronics, sensors, energy conversion, and energy storage devices over the past decades [7,8,9,10,11,12,13,14,15]. Recently, considerable efforts have been devoted to the vertical assembling and integration of distinct 2D TMDC monolayers into van der Waals (vdW) heterostructures with diverse band alignments to develop a wide range of optoelectronic devices [16,17,18]. Because the individual monolayers composing the heterostructure are held together only by weak vdW interactions, the physical properties of such devices are strongly dependent on the interlayer coupling that occurs at the interface of the TMDC-based vdW heterostructures [15,19,20]. Thus, understanding the underlying physics of the interlayer couplings in vdW heterostructures, which play an important role in determining the charge and energy transfer behavior, is crucial for designing and developing high-performance devices.
Among the various heterojunction configurations with the corresponding band structures, the WS2/MoS2 heterostructures are considered to be a promising platform for use in device applications to achieve a high device performance because of their type-II heterojunctions, which enable an efficient exciton dissociation and charge transport [21,22,23,24,25]. For instance, Tan et al. demonstrated that the interlayer coupling between WS2 and MoS2 can enable a long-lived trap state in WS2/MoS2 heterostructures, resulting in an enhanced photodetector performance with a large photoconductive gain and high responsivity [18]. Wang et al. reported that the strong interlayer coupling in WS2/MoS2 heterostructures reduces the energy intervals of electron transition, making it detectable under infrared light [19]. Thus, a fast and reliable method for characterizing the interlayer coupling within 2D TMDCs heterostructures is highly desirable for rapidly assessing the physics underlying the unique electronic structures and optical properties.
Raman spectroscopy is one of the most powerful nondestructive tools used for obtaining a detailed structural and electronic information on 2D layered TMDCs and vdW heterostructures [26]. In particular, it has been recently reported that low-frequency (LF) Raman modes can be used as an indicator to directly probe the interlayer coupling effects in vdW-based layered structures, including layered heterostructures, because the LF Raman vibrational modes originate from the weaker interlayer vdW restoring forces [27,28].
In a few studies, the interfaces of WS2/MoS2 heterostructures have been investigated using Raman scattering [29,30]. However, a detailed study on the interlayer coupling in WS2/MoS2 heterostructures through LF Raman analysis has not yet been conducted.
In this study, we investigated and compared the LF Raman modes in the bilayers of MoS2, WS2, and WS2/MoS2 heterostructures using a confocal Raman spectrometer to clearly distinguish the LF Raman modes. Moreover, we directly synthesized the MoS2, WS2, and WS2/MoS2 heterostructures on a SiO2/Si substrate via chemical vapor deposition (CVD) to rule out the undesirable effects, such as mismatch in the stacking angle between the monolayers and interface contaminations, which generally result in physically stacked TMDCs [27,28,31]. The thicknesses of the directly grown mono- and bilayers were confirmed using atomic force microscopy (AFM). Raman spectroscopy measurements were performed to characterize the vibrational modes in the high-frequency and LF ranges. Two characteristic LF Raman modes, the interlayer in-plane shear (C) and out-of-plane layer-breathing (LB) modes, were clearly observed in all the 2D bilayered homo- and heterostructures, including the MoS2 and WS2 bilayers, and WS2/MoS2 heterostructures, whereas no LF modes were detected in the MoS2 and WS2 monolayers. These results indicate that the LF modes can be ascribed to the strong coupling in our samples without interface contaminations/defects and/or misalignment effects, compared to mechanically stacked samples.

2. Materials and Methods

2.1. Sample Preparation

First, a solution was prepared by adding MoO3 powder (200 mg, Sigma-Aldrich, St. Louis, MO, USA) and WO3 powder (200 mg, Sigma-Aldrich, St. Louis, MO, USA) to NH4OH (10 mL, 28–30% solution, Sigma-Aldrich, St. Louis, MO, USA) in a small vial. A 20 μ L MoO3 and WO3 solution was dropped onto a substrate and spin coated at 3000 rpm for 1 min. The weight of the deposited MoO3 film and WO3 particles was found to be significantly small, around ~0.01 mg [32].
Bilayer MoS2 were grown using atmospheric pressure CVD (APCVD) (Figure 1a). The prepared MoO3 solution was coated on a 300-nm-thick SiO2/Si substrate and loaded into the center of a quartz tube furnace. A ceramic boat loaded with 100 mg of S powder was placed upstream of the furnace. The bilayer MoS2 growth was carried out at 730 °C for 10 min, and then the furnace was naturally cooled down to room temperature.
Bilayer WS2 were grown using low-pressure CVD (LPCVD), in which the quartz tube was evacuated to a base pressure of approximately 10−3 Torr, and a mixture of Ar and H2 was flowed into the furnace. The prepared WO3 solution and S powder were placed in the same position as that fixed during the bilayer MoS2 growth process. The bilayer WS2 growth was performed at 850 °C for 10 min, and throughout the process, the furnace pressure was maintained at 15 Torr.
Next, a WS2/MoS2 heterostructure was grown using the LPCVD method. The substrates coated with the MoO3 and WO3 solution were loaded on the bottom and top of the crucible in a furnace, respectively. The S powder was placed in the same position as that fixed during the bilayer MoS2 growth process, and the growth temperature, time, and pressure were the same as those used in the bilayer WS2 growth process. As the temperature of the furnace increased, MoO3 was deposited and sulfurized on the substrate located at the top of the crucible. The temperature of furnace reached at 850 °C, and the vertical and lateral MoS2/WS2 heterostructures were synthesized [32].

2.2. Characterization

The surface morphology and thicknesses of the CVD-grown bilayer TMDs were characterized using atomic force microscopy (AFM (Multimode 8, Bruker, Billerica, MA, USA)).
Observing the LF Raman modes in 2D layered TMDCs and vdW heterostructures is challenging, because it is difficult to distinguish them from the Rayleigh line using a conventional Raman microscope [33]. In this study, Raman spectroscopy measurements were performed at room temperature using a confocal Raman spectrometer (alpha 300 M+, WiTech, Ulm, Germany). A green laser beam with a wavelength of 488 nm and power of approximately 1 mW was focused onto the individual samples by a 50× objective (NA: 0.55) with a long working distance, as illustrated in Figure 1d. The estimated laser spot size was 1.08 μm.

3. Results and Discussion

3.1. MoS2 Bilayers

Monolayer and bilayer MoS2 were directly grown on a SiO2/Si substrate via the APCVD method, as shown in Figure 1a (see the Section 2 for more details).
Figure 1b,c show the AFM images of the triangular mono- and bilayer MoS2. The lateral size of both the layers was approximately 13–15 μm. The height profiles show that the thicknesses of the mono- and bilayer MoS2 were found to be approximately 0.8 and 1.7 nm, respectively.
Raman spectroscopy was performed to investigate the vibrational modes of the as-grown 2D bilayer MoS2, WS2, and WS2/MoS2 heterostructures. Figure 2a illustrates the four different vibrational modes with relative displacements between the metal and chalcogen atoms, which can be representatively observed in most few-layer TMDCs. These modes can be classified into two categories according to their frequencies: high-frequency and LF modes. In the high-frequency range (>300 cm−1), the E2g and A1g modes originate from the in-plane and out-of-plane atomic vibrations within the layers, respectively. It was observed that the E2g mode softens (red-shift), while the A1g mode stiffens (blue-shift) as the number of layers is increased. Consequently, the frequency difference between the two modes increases [34]. Because the high-frequency Raman modes of the mono- or multilayered TMDCs originate from the intralayer chemical bonds, the restoring forces are significantly affected by the strength of the intralayer bonding, resulting in less sensitivity to interlayer coupling [26,27,34,35]. In contrast, in the LF range (<50 cm−1), the interlayer in-plane shear (C) and out-of-plane layer-breathing (LB) modes are expected to have very low frequencies owing to the weak interlayer vdW restoring forces [36,37]. Thus, the analysis of the LF Raman modes can be treated as a more reliable method for directly probing the interlayer coupling in multilayered TMDCs.
Figure 2b shows the Raman spectra of the monolayer (black line) and bilayer MoS2 (red line), recorded in the high-frequency range of 320–480 cm−1. Note that the quality and lateral size of the MoS2 (and WS2) samples chosen for the Raman measurement were almost the same as those shown in Figure 1b,c. For the monolayer MoS2, two typical peaks were obtained at 386.7 and 404.7 cm−1, which correspond to the in-plane vibrational mode (E2g mode) and out-of-plane vibrational mode (A1g mode), respectively. Evidently, for the bilayer MoS2, the E2g and A1g modes shift in the opposite direction, and the frequency difference between these two modes increases from 18.1 cm−1 (for the monolayer MoS2) to 21.1 cm−1 [34,38,39].
Figure 2c shows the Raman spectra of the monolayer (black line) and bilayer MoS2 (red line), obtained in the LF range of −80 to 80 cm−1. Neither the C nor the LB modes are observed in the monolayer MoS2, as is generally expected for all the other monolayer TMDCs, because the interlayer restoring force is absent. In contrast to the monolayer MoS2, two distinct LF Raman peaks were observed in the spectra of the bilayer MoS2, as well as in the corresponding anti-Stokes spectra. A sharp peak at 40.2 cm−1 can be assigned to the LB mode of the bilayer MoS2. Another peak at 24.3 cm−1 can be assigned to the C mode of the bilayer MoS2, which is typically of lower frequency than that of the LB mode.
According to previous studies, the intensity and frequency of the Raman peaks corresponding to the C and LB modes in bilayer MoS2 depend on the twisting angles and interface quality between the top and bottom MoS2 layers. It has been reported that the C mode is clearly observed near 0° or 60°, and is even absent for certain twisting angles. [31] Thus, the clear observation of the C mode shown in Figure 2c implies that the bilayer MoS2 was grown with the 2H (60°) or 3R (0°) stacking configuration (as shown in Figure 1b,c), which is the most stable configuration of CVD-grown bilayer systems [40]. Furthermore, we observed that there exists only one peak corresponding to the LB mode. This finding indicates that unlike the mechanically stacked bilayer MoS2, the directly grown bilayer MoS2 had a uniform interlayer without localized strains, crystallographic defects, or wrinkles, which are usually introduced in mechanically transferred samples. Thus, these results suggest that our directly grown bilayer MoS2 can induce a strong interlayer coupling with highly ordered domains between the monolayers.

3.2. WS2 Bilayers

Monolayer and bilayer WS2 were directly grown on a SiO2/Si substrate via an LPCVD method (see Section 2 for more details).
Figure 3a shows the Raman spectra of the monolayer (black line) and bilayer WS2 (red line), obtained in the high-frequency range of 320–480 cm−1. For the monolayer WS2, two typical Raman signals were observed at 356.5 and 417.5 cm−1, corresponding to the in-plane vibrational mode (E2g mode) and out-of-plane vibrational mode (A1g mode) of WS2, respectively. Moreover, the E2g and A1g modes of the bilayer WS2 shifted in the opposite direction compared to those of the monolayer WS2, resulting in an increase in the frequency difference between them, which is consistent with the previously reported results [41,42].
Figure 3b shows the Raman spectra of the monolayer (black line) and bilayer WS2 (red line), obtained in the LF range of −80 to 80 cm−1. Similar to the results of MoS2 shown in Figure 2c, for the monolayer WS2, no peaks corresponding to the C and LB modes were observed. However, two different peaks at 17.9, and 33.8 cm−1 were observed in the LF Raman spectrum of the bilayer WS2, which can be assigned to the C and LB modes in a Stokes Raman spectrum, respectively. These findings indicate that the LF Raman modes can be attributed to the interlayer coupling effect.

3.3. WS2/MoS2 Heterostructures

A vertical WS2/MoS2 heterostructure, with WS2 on top of the MoS2 monolayer, was directly grown on a 300-nm-thick SiO2/Si substrate via the LPCVD method (see Section 2 for more details).
The Raman spectrum of the WS2/MoS2 heterostructure in the high-frequency range of 320–500 cm−1 is presented in Figure 4a. The characteristic peaks observed at 383.7 and 356.5 cm−1 can be ascribed to the E2g modes of the individual MoS2 and WS2 monolayers, respectively, whereas those located at 404.7 and 418.2 cm−1 can be attributed to the A1g modes of these individual MoS2 and WS2 monolayers, respectively, confirming the formation of the WS2/MoS2 heterostructure.
In the LF range, as shown in Figure 4b, we also observed two sharp characteristic peaks at 19.5 and 33.8 cm−1, which can be assigned to the C and LB modes, respectively. Figure 4c shows the LF modes of the WS2/MoS2 heterostructure. In general, two physically transferred layers composed of vdW heterostructures are usually misaligned, leading to a lack of in-plane restoring force, thus resulting in the disappearance of the C mode. Furthermore, nonuniform interfaces with variable local stacking can result in the presence of multiple LB modes [27]. Unlike the observations made in a previous study [29], here, we observed that in the WS2/MoS2 heterostructure, only one peak existed corresponding to each C and LB mode, which were associated with a good stacking configuration and interface uniformity, respectively [31]. Notably, directly grown heterostructures with epitaxial interfaces can exhibit a strong interlayer coupling compared to the mechanically transferred heterostructures prepared using a dry-transfer method or exfoliated suspension drop casting [28,43]. Thus, we believe that the clear observation of the C and LB mode peaks can be attributed to the strong interlayer coupling arising from the epitaxially grown bilayers with a clear interface and stable configuration.

4. Conclusions

In this study, we investigated the LF Raman modes to explore the interlayer coupling in the bilayered MoS2 structures, WS2 structures, and WS2/MoS2 heterostructures, which were directly synthesized via CVD. For all the 2D bilayered MoS2 and WS2 homostructures and WS2/MoS2 heterostructures, typical LF C and LB modes were observed, whereas no LB modes were detected in the MoS2 and WS2 monolayers. Moreover, we showed that the observed single LB mode and clear C mode peaks could be attributed to the high-quality homo- and heterojunctions with stable stacking configurations, which enable the induction of a strong interlayer coupling within the layers. Our results provide a fundamental understanding of the interlayer coupling in WS2/MoS2 heterostructures and other 2D TMDC-based vdW heterostructures and an ideal approach for designing and developing high-performance functional devices based on various vdW heterostructures.

Author Contributions

Conceptualization, A.-R.J. and J.I.S.; methodology, K.H.S. and M.-K.S.; validation, A.-R.J. and J.I.S.; formal analysis S.P. and A.-R.J.; investigation, K.H.S., M.-K.S. and S.P.; resources, A.-R.J. and J.I.S.; data curation, K.H.S., M.-K.S., A.-R.J. and J.I.S.; writing—original draft preparation, K.H.S. and M.-K.S.; writing—review and editing, S.P., A.-R.J. and J.I.S.; visualization, K.H.S.; supervision, J.I.S.; funding acquisition, A.-R.J. and J.I.S. All authors have read and agreed to the published version of the manuscript.

Funding

This research was supported by the National Research Foundation of Korea (NRF) grant funded by the Korean government (MSIT) (2019R1A2C1007883 and 2021R1I1A3049729). This work was also supported by 2022 Hongik University Research Fund.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Manzeli, S.; Ovchinnikov, D.; Pasquier, D.; Yazyev, O.V.; Kis, A. 2D transition metal dichalcogenides. Nat. Rev. Mater. 2017, 2, 17033. [Google Scholar] [CrossRef]
  2. Fuhrer, M.S.; Hone, J. Measurement of mobility in dual-gated MoS2 Transistors. Nat. Nanotechnol. 2013, 8, 146–147. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  3. Lee, J.; Pak, S.; Lee, Y.W.; Cho, Y.; Hong, J.; Giraud, P.; Shin, H.S.; Morris, S.M.; Sohn, J.I.; Cha, S.N.; et al. Monolayer optical memory cells based on artificial trap-mediated charge storage and release. Nat. Commun. 2017, 8, 14734. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  4. Choi, W.; Choudhary, N.; Han, G.H.; Park, J.; Akinwande, D.; Lee, Y.H. Recent development of two-dimensional transition metal dichalcogenides and their applications. Mater. Today 2017, 20, 116–130. [Google Scholar] [CrossRef]
  5. Liu, X.; Galfsky, T.; Sun, Z.; Xia, F.; Lin, E.C.; Lee, Y.H.; Kéna-Cohen, S.; Menon, V.M. Strong light-matter coupling in two-dimensional atomic crystals. Nat. Photonics 2014, 9, 30–34. [Google Scholar] [CrossRef]
  6. Pak, S.; Lee, J.; Jang, A.-R.; Kim, S.; Park, K.-H.; Sohn, J.I.; Cha, S. Strain-engineering of contact energy barriers and photoresponse behaviors in monolayer. Adv. Funct. Mater. 2020, 30, 2002023. [Google Scholar] [CrossRef]
  7. van der Zande, A.M.; Huang, P.Y.; Chenet, D.A.; Berkelbach, T.C.; You, Y.; Lee, G.H.; Heinz, T.F.; Reichman, D.R.; Muller, D.A.; Hone, J.C. Grains and grain boundaries in highly crystalline monolayer molybdenum disulphide. Nat. Mater. 2013, 12, 554–561. [Google Scholar] [CrossRef] [Green Version]
  8. Bilgin, I.; Liu, F.; Vargas, A.; Winchester, A.; Man, M.K.L.; Upmanyu, M.; Dani, K.M.; Gupta, G.; Talapatra, S.; Mohite, A.D.; et al. Chemical vapor deposition synthesized atomically thin molybdenum disulfide with optoelectronic-grade crystalline quality. ACS Nano 2015, 9, 8822–8832. [Google Scholar] [CrossRef] [Green Version]
  9. Voiry, D.; Yamaguchi, H.; Li, J.; Silva, R.; Alves, D.C.B.; Fujita, T.; Chen, M.; Asefa, T.; Shenoy, V.B.; Eda, G.; et al. Enhanced catalytic activity in strained chemically exfoliated WS2 nanosheets for hydrogen evolution. Nat. Mater. 2013, 12, 850–855. [Google Scholar] [CrossRef]
  10. Lee, D.; Jang, A.R.; Kim, J.Y.; Lee, G.; Jung, D.W.; Lee, T.I.; Lee, J.O.; Kim, J.J. Phase-dependent gas sensitivity of MoS2 chemical sensors investigated with phase-locked MoS2. Nanotechnology 2020, 31, 225504. [Google Scholar] [CrossRef]
  11. Huang, H.; Cui, Y.; Li, Q.; Dun, C.; Zhou, W.; Huang, W.; Chen, L.; Hewitt, C.A.; Carroll, D.L. Metallic 1T phase MoS2 nanosheets for high-performance thermoelectric energy harvesting. Nano Energy 2016, 26, 172–179. [Google Scholar] [CrossRef]
  12. Yu, X.; Chen, X.; Ding, X.; Yu, X.; Zhao, X.; Chen, X. Facile fabrication of flower-like MoS2/nanodiamond nanocomposite toward high-performance humidity detection. Sens. Actuators B Chem. 2020, 317, 128168. [Google Scholar] [CrossRef]
  13. Zhao, Z.; Hu, Z.; Li, Q.; Li, H.; Zhang, X.; Zhuang, Y.; Wang, F.; Yu, G. Designing two-dimensional WS2 layered cathode for high-performance aluminum-ion batteries: From micro-assemblies to insertion mechanism. Nano Today 2020, 32, 100870. [Google Scholar] [CrossRef]
  14. Lee, J.; Pak, S.; Giraud, P.; Lee, Y.-W.; Cho, Y.; Hong, J.; Jang, A.R.; Chung, H.-S.; Hong, W.-K.; Jeong, H.Y.; et al. Thermodynamically stable synthesis of large-scale and highly crystalline transition metal dichalcogenide monolayers and their unipolar n–n heterojunction devices. Adv. Mater. 2017, 29, 1702206. [Google Scholar] [CrossRef]
  15. Pak, S.; Lee, J.; Lee, Y.W.; Jang, A.R.; Ahn, S.; Ma, K.Y.; Cho, Y.; Hong, J.; Lee, S.; Jeong, H.Y.; et al. Strain-mediated interlayer coupling effects on the excitonic behaviors in an epitaxially Grown MoS2/WS2 van der Waals heterobilayer. Nano Lett. 2017, 17, 5634–5640. [Google Scholar] [CrossRef] [Green Version]
  16. Duan, X.; Wang, C.; Pan, A.; Yu, R.; Duan, X. Two-dimensional transition metal dichalcogenides as atomically thin semiconductors: Opportunities and challenges. Chem. Soc. Rev. 2015, 44, 8859–8876. [Google Scholar] [CrossRef]
  17. Zhu, J.; Li, W.; Huang, R.; Ma, L.; Sun, H.; Choi, J.H.; Zhang, L.; Cui, Y.; Zou, G. One-pot selective epitaxial growth of large WS2/MoS2 lateral and vertical heterostructures. J. Am. Chem. Soc. 2020, 142, 16276–16284. [Google Scholar] [CrossRef]
  18. Wang, S.; Cui, X.; Jian, C.; Cheng, H.; Niu, M.; Yu, J.; Yan, J.; Huang, W. Stacking engineered heterostructures in transition metal dichalcogenides. Adv. Mater. 2021, 33, 2005735. [Google Scholar] [CrossRef]
  19. Hong, X.; Kim, J.; Shi, S.F.; Zhang, Y.; Jin, C.; Sun, Y.; Tongay, S.; Wu, J.; Zhang, Y.; Wang, F. Ultrafast charge transfer in atomically thin MoS2/WS2 heterostructures. Nat. Nanotechnol. 2014, 9, 682–686. [Google Scholar] [CrossRef] [Green Version]
  20. Wu, X.; Chen, X.; Yang, R.; Zhan, J.; Ren, Y.; Li, K. Recent Advances on tuning the interlayer coupling and properties in van Der Waals heterostructures. Small 2022, 18, 2105877. [Google Scholar] [CrossRef]
  21. Gong, Y.; Lin, J.; Wang, X.; Shi, G.; Lei, S.; Lin, Z.; Zou, X.; Ye, G.; Vajtai, R.; Yakobson, B.I.; et al. Vertical and in-plane heterostructures from WS2/MoS2 monolayers. Nat. Mater. 2014, 13, 1135–1142. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  22. Yan, J.; Ma, C.; Huang, Y.; Yang, G. Tunable control of interlayer excitons in WS2/MoS2 heterostructures via strong coupling with enhanced Mie resonances. Adv. Sci. 2019, 6, 1802092. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  23. Susarla, S.; Manimunda, P.; Morais Jaques, Y.; Hachtel, J.A.; Idrobo, J.C.; Syed Amnulla, S.A.; Galvão, D.S.; Tiwary, C.S.; Ajayan, P.M. Deformation mechanisms of vertically stacked WS2/MoS2 heterostructures: The role of interfaces. ACS Nano 2018, 12, 4036–4044. [Google Scholar] [CrossRef] [PubMed]
  24. Tan, H.; Xu, W.; Sheng, Y.; Lau, C.S.; Fan, Y.; Chen, Q.; Tweedie, M.; Wang, X.; Zhou, Y.; Warner, J.H. Lateral graphene-contacted vertically stacked WS2/MoS2 hybrid photodetectors with large Gain. Adv. Mater. 2017, 29, 1702917. [Google Scholar] [CrossRef] [PubMed]
  25. Wang, G.; Li, L.; Fan, W.; Wang, R.; Zhou, S.; Lü, J.T.; Gan, L.; Zhai, T. Interlayer coupling induced infrared response in WS2/MoS2 heterostructures enhanced by surface plasmon resonance. Adv. Funct. Mater. 2018, 28, 1800339. [Google Scholar] [CrossRef]
  26. Zhang, X.; Qiao, X.F.; Shi, W.; Wu, J.B.; Jiang, D.S.; Tan, P.H. Phonon and Raman scattering of two-dimensional transition metal dichalcogenides from monolayer, multilayer to bulk material. Chem. Soc. Rev. 2015, 44, 2757–2785. [Google Scholar] [CrossRef] [Green Version]
  27. Liang, L.; Zhang, J.; Sumpter, B.G.; Tan, Q.H.; Tan, P.H.; Meunier, V. Low-frequency shear and layer-breathing modes in Raman scattering of two-dimensional materials. ACS Nano 2017, 11, 11777–11802. [Google Scholar] [CrossRef]
  28. Zhang, J.; Wang, J.H.; Chen, P.; Sun, Y.; Wu, S.; Jia, Z.Y.; Lu, X.B.; Yu, H.; Chen, W.; Zhu, J.Q.; et al. Observation of strong interlayer coupling in MoS2/WS2 heterostructures. Adv. Mater. 2016, 28, 1950–1956. [Google Scholar] [CrossRef]
  29. Zhang, F.; Lu, Z.; Choi, Y.; Liu, H.; Zheng, H.; Xie, L.; Park, K.; Jiao, L.; Tao, C. Atomically resolved observation of continuous interfaces between an as-grown MoS2 monolayer and a WS2/MoS2 heterobilayer on SiO2. ACS Appl. Nano Mater. 2018, 1, 2041–2048. [Google Scholar] [CrossRef] [Green Version]
  30. Saito, Y.; Kondo, T.; Ito, H.; Okada, M.; Shimizu, T.; Kubo, T.; Kitaura, R. Low frequency Raman study of interlayer couplings in WS2-MoS2 van der Waals heterostructures. Jpn. J. Appl. Phys. 2020, 59, 062004. [Google Scholar] [CrossRef]
  31. Huang, S.; Liang, L.; Ling, X.; Puretzky, A.A.; Geohegan, D.B.; Sumpter, B.G.; Kong, J.; Meunier, V.; Dresselhaus, M.S. Low-Frequency Interlayer Raman modes to probe interface of twisted bilayer MoS2. Nano Lett. 2016, 16, 1435–1444. [Google Scholar] [CrossRef] [PubMed]
  32. Lee, J.; Pak, S.; Lee, Y.W.; Park, Y.; Jang, A.R.; Hong, J.; Cho, Y.; Hou, B.; Lee, S.; Jeong, H.Y.; et al. Direct Epitaxial Synthesis of Selective Two-Dimensional Lateral Heterostructures. ACS Nano 2019, 13, 13047–13055. [Google Scholar] [CrossRef] [PubMed]
  33. Zhao, Y.; Luo, X.; Li, H.; Zhang, J.; Araujo, P.T.; Gan, C.K.; Wu, J.; Zhang, H.; Quek, S.Y.; Dresselhaus, M.S.; et al. Interlayer breathing and shear modes in few-trilayer MoS2 and WSe2. Nano Lett. 2013, 13, 1007–1015. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  34. Lee, C.; Yan, H.; Brus, L.E.; Heinz, T.F.; Hone, J.; Ryu, S. Anomalous lattice vibrations of single- and few-layer MoS2. ACS Nano 2010, 4, 2695–2700. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  35. Sun, Y.; Cai, D.; Yang, Z.; Li, H.; Li, Q.; Jia, D.; Zhou, Y. The Preparation, microstructure and mechanical properties of a dense MgO-Al2O3-SiO2 based glass-ceramic coating on porous BN/Si2N2O ceramics. RSC Adv. 2018, 8, 17569–17574. [Google Scholar] [CrossRef] [Green Version]
  36. Zeng, H.; Zhu, B.; Liu, K.; Fan, J.; Cui, X.; Zhang, Q.M. Low-frequency Raman modes and electronic excitations in atomically thin MoS2 films. Phys. Rev. B 2012, 86, 241301. [Google Scholar] [CrossRef] [Green Version]
  37. Sam, R.T.; Umakoshi, T.; Verma, P. Probing stacking configurations in a few layered MoS2 by low frequency Raman spectroscopy. Sci. Rep. 2020, 10, 21227. [Google Scholar] [CrossRef]
  38. Li, H.; Zhang, Q.; Yap, C.C.R.; Tay, B.K.; Edwin, T.H.T.; Olivier, A.; Baillargeat, D. From bulk to monolayer MoS2: Evolution of Raman scattering. Adv. Funct. Mater. 2012, 22, 1385–1390. [Google Scholar] [CrossRef]
  39. Najmaei, S.; Liu, Z.; Ajayan, P.M.; Lou, J. Thermal effects on the characteristic Raman spectrum of molybdenum disulfide (MoS2) of varying thicknesses. Appl. Phys. Lett. 2012, 100, 013106. [Google Scholar] [CrossRef] [Green Version]
  40. Puretzky, A.A.; Liang, L.; Li, X.; Xiao, K.; Wang, K.; Mahjouri-Samani, M.; Basile, L.; Idrobo, J.C.; Sumpter, B.G.; Meunier, V.; et al. Low-frequency Raman fingerprints of two-dimensional metal dichalcogenide layer stacking configurations. ACS Nano 2015, 9, 6333–6342. [Google Scholar] [CrossRef]
  41. Berkdemir, A.; Gutiérrez, H.R.; Botello-Méndez, A.R.; Perea-López, N.; Elías, A.L.; Chia, C.I.; Wang, B.; Crespi, V.H.; López-Urías, F.; Charlier, J.C.; et al. Identification of individual and few layers of WS2 using Raman spectroscopy. Sci. Rep. 2013, 3, 1755. [Google Scholar] [CrossRef] [Green Version]
  42. Zhao, W.; Ghorannevis, Z.; Amara, K.K.; Pang, J.R.; Toh, M.; Zhang, X.; Kloc, C.; Tan, P.H.; Eda, G. Lattice dynamics in mono- and few-layer sheets of WS2 and WSe2. Nanoscale 2013, 5, 9677–9683. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  43. Samad, L.; Bladow, S.M.; Ding, Q.; Zhuo, J.; Jacobberger, R.M.; Arnold, M.S.; Jin, S. Layer-controlled chemical vapor deposition growth of MoS2 vertical heterostructures via van der Waals epitaxy. ACS Nano 2016, 10, 7039–7046. [Google Scholar] [CrossRef] [PubMed]
Nanomaterials 12 01393 g001 550
Figure 1. (a) Schematic of the growth process of the 2D bilayered MoS2, WS2, and WS2/MoS2 heterostructures via CVD. AFM topography images of the directly grown (b) monolayer and (c) bilayer MoS2. (Scale bar: 5 μm) (d) Schematic of the Raman spectroscopy measurements with a 488 nm laser focused on the vdW heterostructures.
Figure 1. (a) Schematic of the growth process of the 2D bilayered MoS2, WS2, and WS2/MoS2 heterostructures via CVD. AFM topography images of the directly grown (b) monolayer and (c) bilayer MoS2. (Scale bar: 5 μm) (d) Schematic of the Raman spectroscopy measurements with a 488 nm laser focused on the vdW heterostructures.
Nanomaterials 12 01393 g001
Nanomaterials 12 01393 g002 550
Figure 2. (a) Schematic of the lattice structure and four different vibrational modes of the bilayered TMDCs. Raman spectra of the monolayer (black lines) and bilayer MoS2 (red lines), obtained in the (b) high-frequency and (c) LF ranges. The Raman peaks enclosed by the green- and blue-colored regions correspond to the C and LB modes, respectively.
Figure 2. (a) Schematic of the lattice structure and four different vibrational modes of the bilayered TMDCs. Raman spectra of the monolayer (black lines) and bilayer MoS2 (red lines), obtained in the (b) high-frequency and (c) LF ranges. The Raman peaks enclosed by the green- and blue-colored regions correspond to the C and LB modes, respectively.
Nanomaterials 12 01393 g002
Nanomaterials 12 01393 g003 550
Figure 3. Raman spectra of the mono- (black lines) and bilayer WS2 (red lines), recorded in the (a) high-frequency and (b) LF ranges. The Raman peaks enclosed by the green- and blue-colored regions correspond to the C and LB modes, respectively.
Figure 3. Raman spectra of the mono- (black lines) and bilayer WS2 (red lines), recorded in the (a) high-frequency and (b) LF ranges. The Raman peaks enclosed by the green- and blue-colored regions correspond to the C and LB modes, respectively.
Nanomaterials 12 01393 g003
Nanomaterials 12 01393 g004 550
Figure 4. Raman spectra of the WS2/MoS2 heterostructures recorded in the (a) high-frequency and (b) LF ranges. The Raman peaks enclosed by the green- and blue-colored regions correspond to the C and LB modes, respectively. (c) Schematic depicting the interlayer interaction categorized by the C and LB modes in the LF range for the WS2/MoS2 heterostructure.
Figure 4. Raman spectra of the WS2/MoS2 heterostructures recorded in the (a) high-frequency and (b) LF ranges. The Raman peaks enclosed by the green- and blue-colored regions correspond to the C and LB modes, respectively. (c) Schematic depicting the interlayer interaction categorized by the C and LB modes in the LF range for the WS2/MoS2 heterostructure.
Nanomaterials 12 01393 g004
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Shin, K.H.; Seo, M.-K.; Pak, S.; Jang, A.-R.; Sohn, J.I. Observation of Strong Interlayer Couplings in WS2/MoS2 Heterostructures via Low-Frequency Raman Spectroscopy. Nanomaterials 2022, 12, 1393. https://doi.org/10.3390/nano12091393

AMA Style

Shin KH, Seo M-K, Pak S, Jang A-R, Sohn JI. Observation of Strong Interlayer Couplings in WS2/MoS2 Heterostructures via Low-Frequency Raman Spectroscopy. Nanomaterials. 2022; 12(9):1393. https://doi.org/10.3390/nano12091393

Chicago/Turabian Style

Shin, Ki Hoon, Min-Kyu Seo, Sangyeon Pak, A-Rang Jang, and Jung Inn Sohn. 2022. "Observation of Strong Interlayer Couplings in WS2/MoS2 Heterostructures via Low-Frequency Raman Spectroscopy" Nanomaterials 12, no. 9: 1393. https://doi.org/10.3390/nano12091393

APA Style

Shin, K. H., Seo, M. -K., Pak, S., Jang, A. -R., & Sohn, J. I. (2022). Observation of Strong Interlayer Couplings in WS2/MoS2 Heterostructures via Low-Frequency Raman Spectroscopy. Nanomaterials, 12(9), 1393. https://doi.org/10.3390/nano12091393

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop