Next Article in Journal
Cyclodextrin Polymers as Delivery Systems for Targeted Anti-Cancer Chemotherapy
Next Article in Special Issue
Metal Complexes—A Promising Approach to Target Biofilm Associated Infections
Previous Article in Journal
Stable and Oriented Liquid Crystal Droplets Stabilized by Imidazolium Ionic Liquids
Previous Article in Special Issue
Synthesis and Biological Evaluation of New N-Acyl-α-amino Ketones and 1,3-Oxazoles Derivatives
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 26
Issue 19
10.3390/molecules26196045
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Sintered and 3D-Printed Bulks of MgB2-Based Materials with Antimicrobial Properties

by
Petre Badica
1,*,
Nicolae Dan Batalu
2,
Mariana Carmen Chifiriuc
3,
Mihail Burdusel
1,
Mihai Alexandru Grigoroscuta
1,
Gheorghe Virgil Aldica
1,
Iuliana Pasuk
1,
Andrei Kuncser
1,
Marcela Popa
3,*,
Angelo Agostino
4,
Lorenza Operti
4,
Santanu Kumar Padhi
4,
Valentina Bonino
4,5 and
Marco Truccato
4
1
National Institute of Materials Physics, 405A Atomistilor Street, 077125 Magurele, Romania
2
Faculty of Material Science and Engineering, University Politehnica of Bucharest, 313 Splaiul Independentei, 060042 Bucharest, Romania
3
Faculty of Biology and The Research Institute of the University of Bucharest (ICUB), University of Bucharest, 91-95 Splaiul Independentei, 050095 Bucharest, Romania
4
Physics and Chemistry Departments, University of Turin, 1-7 Via Pietro Giuria, 10125 Turin, Italy
5
European Synchrotron Radiation Facility, 71 Avenue des Martyrs, 38000 Grenoble, France
*
Authors to whom correspondence should be addressed.
Molecules 2021, 26(19), 6045; https://doi.org/10.3390/molecules26196045
Submission received: 1 September 2021 / Revised: 27 September 2021 / Accepted: 28 September 2021 / Published: 6 October 2021
(This article belongs to the Special Issue Synthetic Antibiofilm Agents: Design, Synthesis and Applications)
Browse Figures
Versions Notes

Abstract

:
Pristine high-density bulk disks of MgB2 with added hexagonal BN (10 wt.%) were prepared using spark plasma sintering. The BN-added samples are machinable by chipping them into desired geometries. Complex shapes of different sizes can also be obtained by the 3D printing of polylactic acid filaments embedded with MgB2 powder particles (10 wt.%). Our present work aims to assess antimicrobial activity quantified as viable cells (CFU/mL) vs. time of sintered and 3D-printed materials. In vitro antimicrobial tests were performed against the bacterial strains Escherichia coli ATCC 25922, Pseudomonas aeruginosa ATCC 27853, Staphylococcus aureus ATCC 25923, Enterococcus faecium DSM 13590, and Enterococcus faecalis ATCC 29212; and the yeast strain Candida parapsilosis ATCC 22019. The antimicrobial effects were found to depend on the tested samples and microbes, with E. faecium being the most resistant and E. coli the most susceptible.

1. Introduction

Planktonic and biofilm-forming microbes are among the most important threats to human health. In the EU, 25,000 people die every year due to infections with antibiotic-resistant bacteria, and the management of these infections costs about 1.5 billion EUR/year [1]. This problem could be considered a crisis, because the rate of development and commercialization of novel effective antibiotics has slowed [2]. Moreover, government funds and efforts have recently been focused on other urgent problems, such as the COVID-19 pandemic crisis. From 1930 to 1962, 20 new types of antibiotics were developed; meanwhile, from 1962 to the present, only 2 new types of antibiotics have gone into production [3,4,5]. Modern antimicrobial strategies are needed [6], and among them, nanostructured materials such as powders, coatings, and bulks are promising candidates [7,8,9]. The literature also offers examples of many bioactive metals including Ag, Cu, Zn, Mg, Ce, Ti, Al, Si, Au, Bi, Ca, Fe, Pt, Sn, Hg, Cd, Cr, Tl, Al, Co, In, Ni, Mn, and Cr [10,11,12,13,14]. The first two, Ag and Cu [15], are the most popular, being already used in many antimicrobial applications. Metals are often used as oxides, hydroxides, halides, and sulfates [10,16] or they are introduced as active components in alloys (e.g., brasses, bronzes, copper–nickel–zinc) and in composite materials (e.g., steels, hydroxyapatite, polymer/resin matrices, and textiles [15,17]). Antimicrobial non-metals such as C (e.g., fullerene, carbon nanotubes, graphene oxide) [18,19,20,21,22] or B [23,24] and their compounds have also been reported to display antimicrobial functions. Other antimicrobial materials include quaternary ammonium compounds and synthetic or natural polymers (e.g., peptides, lactoferrin, chitosan) [11,15]. However, synthetic polymers often need physical, chemical, or mechanical surface modifications [15] to optimize their efficiency against microbes.
Magnesium diboride (MgB2) is well-known for its superconducting properties [25]. MgB2 can be prepared by a variety of methods, including spark plasma sintering (SPS) [26,27,28,29,30,31]. Our research group has recently reported for the first time in the scientific literature the potential for the antimicrobial applications of MgB2 materials (powders and biodegradable coatings based on polyvinylpyrrolidone) for the clinical field and for combating the negative impact of microbial colonization in different environments, as with the biodeterioration of heritage buildings [26,32,33,34,35]. We have previously shown that the antimicrobial activity of MgB2 powders depends on the fabrication process (e.g., MgB2 powders produced by reactive liquid infiltration (RLI) show superior performance to commercial powders) as well as their purity, microstructure, and pH behavior in water. Another important aspect revealed by our results was the good performance of these materials against a large spectrum of bacterial and fungal strains and their similar efficiency against microbes, both in the planktonic and the biofilm growth state. Biofilms are known to be significantly more resilient than individual microbes, and thus pose a higher health threat [36].
Considering the acute need for developing novel solutions to prevent and combat biofilms and the promising results reported in our previous papers for the antibiofilm potential of MgB2 coatings, we have continued our research in this direction. In the present paper, we focus on the bulk of this material to assess its in vitro antimicrobial activity against Gram-negative and Gram-positive bacteria, as well as yeast strains.
The bulk materials investigated in this work are sintered MgB2 high-density massive samples obtained by SPS and 3D printed samples of a polylactic acid (PLA) with the addition of MgB2 powder. For our study, we selected PLA for its wide availability, low price, biodegradability, and readiness for 3D printing [37,38,39]. PLA has great biocompatibility [39], and some of its applications are already in use (bone fixation screws, stent coating, bio-resorbable suture threads, etc.). The advantage of using the 3D-printing approach is that it allows the fabrication of functional medical devices with antimicrobial properties in diverse and complex shapes at low costs, and it is adapted for small series production. Bulks of sintered MgB2 were shown to have mechanical properties close to conventional structural SiC or Al2O3 ceramic (i.e., they are relatively hard and brittle) [40]. This makes it difficult to fabricate pristine MgB2 into precise and complex geometries by mechanical processing. Therefore, machinable MgB2 [41] sintered bulks with added hexagonal BN and 3D-printed materials with embedded MgB2 can provide the needed (complex) shape and size for applications.
The bulk materials based on MgB2 in this work that allow processing into complex shapes are envisioned for applications such as medical devices (artificial prosthetics and biodegradable implants [42,43], drug delivery systems) and self-sterilizing medical instruments with time- and space-controlled activity. Apart from the degradation and release of the active components with antimicrobial activity, the proposed bulks are also expected to allow mechanical support control. Other possible applications could be found in the packaging industry [44], such as for food transportation, preservation, and the enhancement of shelf life complimented by eco-friendly packaging with high levels of water biodegradability and biocompatibility. Other applications of bulk bioactive materials based on MgB2 could be found in industries where free surfaces of biological materials are necessary. The management of potable water could become a viable application [24], but other biofouling applications are also expected to emerge.

2. Materials and Methods

2.1. Bulks Fabrication

High-density (>95%, Table 1) bulk samples of MgB2 (Figure 1a) and MgB2-added with 10 wt.% hexagonal BN (hBN) were prepared by SPS in a vacuum at 1150 °C for 3 min, under a maximum uniaxial pressure of 95 MPa. The raw powders were MgB2 (LTS Research Laboratories Inc, 99.5% purity, <44 µm) and hBN (High Purity Chemicals, >99%, 10 µm). The details of sample fabrication by SPS were reported in [41,45]. The hBN-added MgB2 was demonstrated to be machinable by chipping in [41].
Composite filaments of PLA (Figure 1b) with embedded MgB2 particles (LTS Research Laboratories Inc, Orangeburg, NY, USA, 99.5% purity, <44 µm) were prepared in two steps. In the first step, commercial PLA was dissolved in chloroform and mixed with MgB2 powder (10 wt.%). In the second step, after the evaporation of chloroform, the PLA+MgB2 solid layer was cut into small pellets and extruded as filaments [46] with a Noztek extruder. The composite polymer–ceramic filaments had an average diameter of 1.65 mm (±0.05). Printing into square shapes (~10 mm × 10 mm) with a thickness of ~3 mm (Figure 1c) was performed with a WASP 2040 Turbo 2 3D printer (based on fused filament fabrication, FFF) with a 0.7 mm nozzle diameter. The printing temperature was 210 °C and the bed temperature was 60 °C, with 100% infill and a printing speed of 20 mm/s.

2.2. Antimicrobial Assays

The antimicrobial activity of the MgB2-hBN sintered bulk and PLA-MgB2 3D-printed samples was tested by using reference bacterial and fungal strains: Escherichia coli ATCC 25922, Pseudomonas aeruginosa ATCC 27853, Staphylococcus aureus ATCC 25923, Enterococcus faecium DSM 13590, Enterococcus faecalis ATCC 29212, and Candida parapsilosis ATCC 22019.
The MgB2 bulk disks were incubated in a humid atmosphere at 37 °C for 6 and 24 h, in contact with microbial suspensions of 105 CFU (colony-forming units)/mL density. After incubation, the materials were washed with distilled water to remove unadhered microorganisms and sonicated for 15 s at maximum power. Next, they were vortexed for 15 s at 3000 rpm to recover the adherent microorganisms that were quantified by determining the viable cells expressed as CFU/mL.
The antimicrobial activity of the bulk sintered MgB2-hBN was tested using a final inoculum density of 5 × 105 CFU/mL prepared in a 10 mL saline solution, with the microbial viability being assessed after different contact times (0.5 h, 1 h, 2 h, 3 h, 4 h, 5 h, 6 h, 24 h) and expressed as CFU/mL. The antibacterial activity of PLA samples with embedded MgB2 particles was assessed by the direct contact method: A ~108 CFU/mL microbial suspension was distributed over the sterile material samples and incubated in a humid atmosphere for 2 h, 4 h, and 24 h at 37 °C. After incubation, the colonized samples were placed in 2 mL of sterile saline and were vigorously shaken to detach the adherent bacterial cells. The harvested bacterial suspension was further used to prepare serial dilutions to quantify bacterial growth by counting the resulting colonies and calculating the colony-forming units (CFU/mL).
All the assays were performed in duplicate, and the statistical analysis of the obtained materials was performed using a paired t test with GraphPad Prism (version 8.0.0 for Windows, GraphPad Software, San Diego, CA, USA, www.graphpad.com, accessed on 4 October 2020).

2.3. Sample Characterization before and after Antimicrobial Test

The raw MgB2 powder and sintered bulk samples were subjected to X-ray diffraction (Bruker AXS D8 Advance diffractometer, CuKα radiation). Rietveld analysis (MAUD 2.31 [47]) was applied to determine the weight fraction of the phases, a and c lattice parameters of MgB2, the crystallite size, and the residual strain for different phases (Table 1). The amount of carbon (denoted y, Table 1) substituting boron in the crystal lattice of MgB2 (Mg(B1−yCy)2) was calculated with the empirical formula:
y = −21.9·a + 6.76 (a in nm)
considering mediated data from [48,49,50].
The apparent bulk density of the sintered samples (ra) was measured by the Archimedes method. The relative density, R = (ra/rt) × 100 (%), where rt is the theoretical mass density [51], was calculated by considering all identified phases (MgB2, MgO, MgB4, and Mg) as determined by Rietveld analysis [47]. The microstructure of the samples was observed using scanning electron microscopy (SEM, Lyra 3XMU/Tescan). Metallographic polishing of the sintered samples was made with different oil-based emulsions of Al2O3 down to a particle size of 1 µm. Saline suspensions with cultures (see Section 2.2) were placed on the as-polished surfaces.

3. Results and Discussion

We obtained, characterized, and bio-assessed the anti-biofilm activity of various types of samples based on MgB2 fabricated by SPS (pristine MgB2 and hBN-added MgB2) and FFF 3D printing. The obtained samples exhibited significant antimicrobial activity against adherent strains at short incubation times (less than 6 h) and against subsequently formed biofilms at longer incubation times of 24 h. This behavior represents an important advantage: the early occurrence of an inhibitory effect on bacterial growth prevents the development of bacterial biofilms on the surface of medical devices. The antimicrobial activity of MgB2, its good biodegradability and biocompatibility, as well as its anti-inflammatory properties promote this material as a useful candidate for a wide range of biomedical applications.
XRD spectra and the results of Rietveld analysis on as-sintered pristine MgB2 samples are presented in Figure 2a and Table 1. The MgB2 raw powder was 97 wt.% MgB2 phase, and the impurity phases were MgO and metallic Mg (Table 1). After sintering, the MgB2 phase decreased by about 10 wt.% in the pristine sample, and the newly formed secondary phases were MgB4 and MgO. In the hBN-added sample, the amount of MgB2 was 78 wt.%. If ~10 wt.% of hBN is not taken into consideration, the maximum amount in the added sample would be ~88 wt.%, which is comparable to the 87.5% value in the pristine sample. As previously reported, hBN has little influence, if any, on the decomposition reactions of MgB2 during SPS [45]. The crystallite size of MgB2 during SPS showed some increase, but it was within the range of experimental error. The crystallite sizes of MgB2, MgO, and MgB4 for pristine and hBN-added SPS-processed samples can be considered similar. This result also supports the inertness of hBN compared to MgB2. In addition, there was little difference in the carbon intake during SPS between the pristine and hBN-added samples. As presented in Section 2.3, insertion of carbon in the crystal lattice of MgB2 decreased the a-axis lattice parameter, while the c-axis lattice parameter remained almost constant (Table 1). In addition, this is usually accompanied by an increase in microstrain. This trend can be observed when raw powder and sintered samples are compared. However, in the sintered samples, this correlation did not hold up, since the higher y-carbon level in sample LTS SPS (0.0114) than in the sample LTS + (hBN)0.01 SPS (0.0076) induced a lower microstrain of 0.12% vs. 0.14%, respectively. The amount of carbon, a biocompatible material, was very low in the sintered samples [52].
The results of in vitro antimicrobial activity are presented in Figure 3, Figure 4 and Figure 5. The results demonstrate significant antimicrobial activity for the pristine MgB2 bulk material. Both the initial phase of adhesion of microorganisms quantified after 6 h of contact and the mature biofilm growth quantified after 24 h of incubation were inhibited. For pristine MgB2 sintered bulks, after 6 h of incubation there was a significant decrease in microbial growth for E. coli and S. aureus (Figure 3) and a total growth inhibition of the P. aeruginosa strain. After 24 h of incubation, the samples had completely inhibited the growth of four out of the five tested microbial strains (i.e., E. coli, P. aeruginosa, S. aureus, and C. parapsilosis). These results demonstrate significant antimicrobial activity of the pristine MgB2 bulk material. The initial phase of the microorganisms’ adhesion was quantified after 6 h of contact (statistically significant for E. coli and P. aeruginosa, P < 0.0005), and the mature biofilms’ growth was quantified after 24 h of contact.
The results for pristine MgB2 bulks were reproduced in machinable hBN-added MgB2 sintered samples (Figure 4). The results for the hBN-added samples showed that MgB2 had inhibitory and microbicidal effects on the microbial strains included in the study. Its efficacy was more pronounced for the Gram-negative strains E. coli and P. aeruginosa, which were no longer viable after 1 and 2 h of contact, respectively. Regarding the Gram-positive bacteria, the inhibitory effect of MgB2 against S. aureus started after 3 h of incubation and against E. faecalis after 6 h, and it was complete after 4 h and 24 h of incubation for S. aureus and E. faecalis, respectively. C. parapsilosis fungal strains are among the most frequently isolated fungi on human skin [53], and in our study the tested strain was the most resistant to the inhibitory effects of the tested samples. However, the fungicidal effect was initiated at 24 h. No viable cells of P. aeruginosa survived after 2 h of incubation. The comparison of the antimicrobial activity of the two types of sintered materials (i.e., pristine MgB2 bulk and hBN-added MgB2 sintered samples) reveals a higher efficacy of the latter against E. faecium after 6 h and 24 h of incubation, and similar activity against the other four tested microbial strains for those two incubation periods.
The 3D-printed PLA+10 wt.% MgB2 samples were tested for their anti-biofilm activity against two strains: the Gram-negative E. coli and the Gram-positive S. aureus (Figure 5). Statistical analysis was not performed for the polymer–MgB2 results. These results are preliminary, and more experiments are needed. The pristine PLA polymer is inert with respect to microbes [54], and therefore, if there is an antimicrobial effect it could likely be ascribed to the MgB2 from the 3D-printed samples. Analysis of the biofilm dynamics evidenced that the 3D-printed samples had an inhibitory effect on microbial cell adhesion after 2 h of incubation. At 24 h of incubation, the number of viable bacteria cells decreased by 5 log units, and no viable cells were observed at 48 h of incubation. These results suggest that it is necessary to carefully select the type and concentration of the composite components to improve and control antimicrobial activity over space and time.
The antimicrobial activity efficiency over time for a given material depends on the microbial strain. This raises the question of whether the adherent strains affect the surface structure of the colonized material over time. If this were the case, it could partially explain the differences observed in the intensity of the antimicrobial effect exhibited by different surfaces in contact with different strains for different contact times. Figure 2b shows the XRD spectra of the surface of the pristine MgB2 sintered bulk samples after removing the E. coli, E. faecium, and S. aureus biofilms. There are no notable differences among the samples. A similar result can be inferred from the microscopy data (Figure 6), where, to avoid redundancy, only the samples that were in contact with E. faecium are shown. When surfaces of samples in contact with other strains were investigated (not shown here) no particularities were revealed.
We conclude that the process of surface corrosion develops independently of the microbial strain, and it could be influenced by the saline solution. Corrosion-specific features are similar to those reported in [35]. More research is needed on corrosion vs. the antimicrobial effect of MgB2-based materials.
Taken together, the biological assays suggest significant antimicrobial activity of MgB2 materials (pristine, added, or composite), making them promising candidates for the development of novel antimicrobial strategies. Further studies are required to establish the detailed mechanisms of the antimicrobial activity revealed by the tested MgB2-based materials. However, we could speculate that the antimicrobial activity may be due to the release of Mg2+ ions, which could affect the integrity of microbial cell membranes or disrupt membrane potential and cause the leakage of cellular contents and eventually cell lysis [54,55,56,57,58]. The anti-biofilm effect of Mg2+ ions could result from downregulation of extracellular matrix gene expression [59] or from the enhancement of c-di-GMP degradation, which would decrease biofilm formation [60]. Moreover, considering the anti-inflammatory effects of magnesium, we expect that the use of these materials in antimicrobial formulations could lead to the attenuation of tissue lesions caused by an increased inflammatory response to the presence of pathogens [61].

4. Conclusions

In this paper, we outlined how we obtained, characterized, and bio-evaluated the anti-biofilm activity of samples based on MgB2 fabricated by SPS (pristine MgB2 and hBN-added MgB2) and as 3D-printed composite (PLA embedded with 10 wt.% MgB2 particles). These samples inhibited both the initial phases of biofilm development quantified after 6 h of incubation and the mature biofilms at 24 h. The antimicrobial activity of MgB2, its good biodegradability and biocompatibility, as well as its anti-inflammatory properties promote this material as a useful candidate for a wide range of biomedical applications, including the development of novel biomaterials resistant to microbial colonization that would present a low risk for developing medical device biofilm-associated infections.

Author Contributions

Conceptualization, P.B., N.D.B. and M.C.C.; funding acquisition, P.B. and M.T.; investigation, P.B., N.D.B., M.C.C., M.B., M.A.G., G.V.A., I.P., A.K., M.P., A.A., L.O., S.K.P., V.B. and M.T.; methodology, P.B. and M.C.C.; project administration, P.B., N.D.B., M.C.C. and M.T.; supervision, P.B.; validation, P.B. and M.C.C.; visualization, P.B., M.A.G. and G.V.A.; writing—original draft, P.B.; writing—review and editing, P.B., N.D.B., M.C.C. and M.T. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the Romanian National Authority for Scientific Research and Innovation (UEFISCDI); the Italian Ministry of Education, University and Research (MIUR) and EU, through the grant 74-COFUND-M-ERA.NET II—BIOMB. The Italian team was also funded through the grant “Departments of Excellence” (L. 232/2016).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The raw/processed data required to reproduce these findings cannot be shared at this time as the data also form part of an ongoing study. Data are available from the corresponding authors on request.

Acknowledgments

S.K.P., V.B. and M.T. also acknowledge partial support from the “Departments of Excellence” (L. 232/2016) grant, funded by MIUR. The funders had no role in the study, design, data collection and analysis, decision to publish, or preparation of the manuscript. Authors acknowledge MIUR, UEFISCDI, and EU for financial support. S.K.P., N.B., V.B. and M.T. also acknowledge partial support fromthe “Departments of Excellence” (L. 232/2016) grant, funded by MIUR.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. EU Action on Antimicrobial Resistance. Available online: https://ec.europa.eu/health/antimicrobial-resistance/eu-action-on-antimicrobial-resistance_en (accessed on 7 June 2021).
  2. Mantravadi, P.K.; Kalesh, K.A.; Dobson, R.C.J.; Hudson, A.O.; Parthasarathy, A. The Quest for Novel Antimicrobial Compounds: Emerging Trends in Research, Development, and Technologies. Antibiotics 2019, 8, 8. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  3. Boucher, H.W.; Talbot, G.H.; Bradley, J.S.; Edwards, J.E.; Gilbert, D.; Rice, L.B.; Scheld, M.; Spellberg, B.; Bartlett, J. Bad bugs, no drugs: No ESKAPE! An update from the Infectious Diseases Society of America. Clin. Infect Dis. 2009, 48, 1–12. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  4. Walsh, P. Where will new antibiotics come from? Nat. Rev. Microbiol. 2003, 1, 65–70. [Google Scholar] [CrossRef] [PubMed]
  5. Lewis, K. Platforms for antibiotic discovery. Nat. Rev. Drug Discov. 2013, 12, 371–387. [Google Scholar] [CrossRef]
  6. Khatoon, Z.; McTiernan, C.D.; Suuronen, E.J.; Mah, T.-F.; Alarcon, E.I. Bacterial biofilm formation on implantable devices and approaches to its treatment and prevention. Heliyon 2018, 4, e01067. [Google Scholar] [CrossRef] [Green Version]
  7. Pop, C.S.; Hussien, M.D.; Popa, M.; Mares, A.; Grumezescu, A.M.; Grigore, R.; Lazar, V.; Chifiriuc, M.C.; Sakizlian, M.; Bezirtzoglou, E.; et al. Metallic-based micro and nanostructures with antimicrobial activity. Curr. Top. Med. Chem. 2015, 15, 1577–1582. [Google Scholar] [CrossRef]
  8. Wu, J.; He, J.; Yin, K.; Zhu, Z.; Xiao, S.; Wu, Z.; Duan, J.-A. Robust Hierarchical Porous PTFE Film Fabricated via Femtosecond Laser for Self-Cleaning Passive Cooling. Nano Lett. 2021, 21, 4209–4216. [Google Scholar] [CrossRef]
  9. Yin, K.; Wu, Z.; Wu, J.; Zhu, Z.; Zhang, F.; Duan, J.-A. Solar-driven thermal-wind synergistic effect on laser-textured superhydrophilic copper foam architectures for ultrahigh efficient vapor generation. Appl. Phys. Lett. 2021, 118, 211905. [Google Scholar] [CrossRef]
  10. Grumezescu, A.M. Nanobiomaterials in Antimicrobial Therapy. Applications of Nanobiomaterials 6; Elsevier: Amsterdam, The Netherlands, 2016; ISBN 978-0-323-42864-4. [Google Scholar]
  11. Zhao, X. 5-Antibacterial bioactive materials. Bioact. Mater. Med. 2011, 97–123. [Google Scholar] [CrossRef]
  12. Luque-Agudo, V.; Fernández-Calderón, M.C.; Pacha-Olivenza, M.A.; Pérez-Giraldo, C.; Gallardo-Moreno, A.M.; González-Martín, L.M. The role of magnesium in biomaterials related infections. Colloids Surf. B Biointerfaces 2020, 191, 110996. [Google Scholar] [CrossRef]
  13. Hoseinzadeh, E.; Makhdoumi, P.; Taha, P.; Hossini, H.; Stelling, J.; Kamal, M.A.; Ashraf, G.M. A Review on Nano-Antimicrobials: Metal Nanoparticles, Methods and Mechanisms. Curr. Drug Metab. 2017, 18, 120–128. [Google Scholar] [CrossRef]
  14. Shao, Y.; Zeng, R.-C.; Li, S.-Q.; Cui, L.-Y.; Zou, Y.-H.; Guan, S.-K.; Zheng, Y.-F. Advance in Antibacterial Magnesium Alloys and Surface Coatings on Magnesium Alloys: A Review. Acta Metall. Sin. Engl. Lett. 2020, 33, 615–629. [Google Scholar] [CrossRef]
  15. Sun, D.; Babar Shahzad, M.; Li, M.; Wang, G.; Xu, D. Antimicrobial materials with medical applications. Adv. Perform. Mater. 2015, 30, B90–B95. [Google Scholar] [CrossRef]
  16. Sawai, J.; Kojima, H.; Igarashi, H.; Hashimoto, A.; Shoji, S.; Takehara, A.; Sawaki, T.; Kokugan, T.; Shimizu, M. Escherichia coli damage by ceramic powder slurries. J. Chem. Eng. Jpn. 1997, 30, 1034–1039. [Google Scholar] [CrossRef] [Green Version]
  17. Esteban-Cubillo, A.; Pecharromán, C.; Aguilar, E.; Santarén, J.; Moya, J.S. Antibacterial activity of copper monodispersed nanoparticles into sepiolite. J. Mater. Sci. 2006, 41, 5208. [Google Scholar] [CrossRef]
  18. Al-Jumaili, A.; Alancherry, S.; Bazaka, K.; Jacob, M.V. Review on the antimicrobial properties of Carbon nanostructures. Materials 2017, 10, 1066. [Google Scholar] [CrossRef]
  19. Badireddy, A.R.; Hotze, E.M.; Chellam, S.; Alvarez, P.J.J.; Wiesner, M.R. Inactivation of bacteriophages via photosensitization of fullerol nanoparticles. Environ. Sci. Technol. 2007, 41, 6627–6632. [Google Scholar] [CrossRef]
  20. Lyon, D.Y.; Fortner, J.D.; Sayes, C.M.; Colvin, V.L.; Hughes, J.B. Bacterial cell association and antimicrobial activity of a C60 water suspension. Environ. Toxicol. Chem. 2005, 24, 2757–2762. [Google Scholar] [CrossRef]
  21. Kang, S.; Herzberg, M.; Rodrigues, D.F.; Elimelech, M. Antibacterial effects of carbon nanotubes: Size does matter. Langmuir 2008, 24, 6409–6413. [Google Scholar] [CrossRef]
  22. Li, P.; Gao, Y.; Sun, Z.; Chang, D.; Gao, G.; Dong, A. Synthesis, characterization, and bactericidal evaluation of chitosan/guanidine functionalized graphene oxide composites. Molecules 2017, 22, 12. [Google Scholar] [CrossRef] [Green Version]
  23. Uluisik, I.; Karakaya, H.C.; Koc, A. The importance of boron in biological systems. J. Trace Elem. Med. Biol. 2018, 45, 156–162. [Google Scholar] [CrossRef] [PubMed]
  24. Yilmaz, M.T. Minimum inhibitory and minimum bactericidal concentrations of boron compounds against several bacterial strains. Turk. J. Med. Sci. 2012, 42, 1423–1429. [Google Scholar] [CrossRef]
  25. Nagamatsu, J.; Nakagawa, N.; Muranaka, T.; Zenitani, Y.; Akimitsu, J. Superconductivity at 39 K in magnesium diboride. Nature 2001, 410, 63–64. [Google Scholar] [CrossRef] [PubMed]
  26. Aldica, G.; Batalu, D.; Popa, S.; Ivan, I.; Nita, P.; Sakka, Y.; Vasylkiv, O.; Miu, L.; Pasuk, I.; Badica, P. Spark plasma sintering of MgB2 in the two-temperature route. Phys. C 2012, 477, 43–50. [Google Scholar] [CrossRef]
  27. Plapcianu, C.; Agostino, A.; Badica, P.; Aldica, G.V.; Bonometti, E.; Ieluzzi, G.; Popa, S.; Truccato, M.; Cagliero, S.; Sakka, Y.; et al. Microwave Synthesis of Fullerene-Doped MgB2. Ind. Eng. Chem. Res. 2012, 51, 11005–11010. [Google Scholar] [CrossRef]
  28. Locci, A.M.; Orru, R.; Cao, G.; Sanna, S.; Congiu, F.; Concas, G. Synthesis of bulk MgB2 superconductors by pulsed electric current. Aiche J. 2006, 52, 2618–2626. [Google Scholar] [CrossRef]
  29. Gajda, D.; Morawski, A.; Zaleski, A.; Kurnatowska, M.; Cetner, T.; Gajda, G.; Presz, A.; Rindfleisch, M.; Tomsic, M. The influence of HIP on the homogeneity, Jc, Birr, Tc and Fp in MgB2 wires. Supercond. Sci. Technol. 2015, 28, 015002. [Google Scholar] [CrossRef]
  30. Flukiger, R.; Al Hossain, M.S.; Senatore, C.; Buta, F.; Rindfleisch, M. A New Generation of In Situ MgB2 Wires With Improved J(c) and B-irr Values Obtained by Cold Densification (CHPD). IEEE Trans. Appl. Supercond. 2011, 21, 2649–2654. [Google Scholar] [CrossRef]
  31. Sasaki, T.; Naito, T.; Fujishiro, H. Trapped magnetic field of dense MgB2 bulks fabricated under high pressure. Phys. Procedia 2013, 45, 93–96. [Google Scholar] [CrossRef] [Green Version]
  32. Badica, P.; Batalu, N.D.; Chifiriuc, M.C.; Burdusel, M.; Grigoroscuta, M.A.; Aldica, G.; Pasuk, I.; Kuncser, A.; Enculescu, M.; Popa, M.; et al. MgB2 powders and bioevaluation of their interaction with planktonic microbes, biofilms, and tumor cells. J. Mater. Res. Technol. 2021, 12, 2168–2184. [Google Scholar] [CrossRef]
  33. Badica, P.; Batalu, N.D.; Burdusel, M.; Grigoroscuta, M.A.; Aldica, G.; Enculescu, M.; Gradisteanu Pircalabioru, G.; Popa, M.; Marutescu, L.G.; Dumitriu, B.G.; et al. Antibacterial composite coatings of MgB2 powders embedded in PVP matrix. Sci. Rep. 2021, 11, 9591. [Google Scholar] [CrossRef]
  34. Gheorghe, I.; Avram, I.; Corbu, V.M.; Măruţescu, L.; Popa, M.; Balotescu, I.; Blăjan, I.; Mateescu, V.; Zaharia, D.; Dumbravă, A.Ş.; et al. In Vitro Evaluation of MgB2 Powders as Novel Tools to Fight Fungal Biodeterioration of Heritage Buildings and Objects. Front. Mater. 2021, 7, 601059. [Google Scholar] [CrossRef]
  35. Batalu, D.; Stanciu, A.M.; Moldovan, L.; Aldica, G.; Badica, P. Evaluation of pristine and Eu2O3-added MgB2 ceramics for medical applications: Hardness, corrosion resistance, cytotoxicity and antibacterial activity. Mater. Sci. Eng. C 2014, 42, 350–361. [Google Scholar] [CrossRef]
  36. Davies, D. Understanding biofilm resistance to antibacterial agents. Nat. Rev. Drug Discov. 2003, 2, 114–122. [Google Scholar] [CrossRef]
  37. Garlotta, D. A literature review of Poly(lactic acid). J. Polym. Environ. 2002, 9, 63–84. [Google Scholar] [CrossRef]
  38. Santana, H.A.; Amorim, N.S.J.; Ribeiro, D.V.; Cilla, M.S.; Dias, C.M.R. 3D printed mesh reinforced geopolymer: Notched prism bending. Cement Concr. Composites 2021, 116, 103892. [Google Scholar] [CrossRef]
  39. Casalini, T.; Rossi, F.; Castrovinci, A.; Perale, G. A perspective of polylactic acid-based polymers use for nanoparticles synthesis and applications. Front. Bioeng. Biotechnol. 2019, 7, 259. [Google Scholar] [CrossRef]
  40. Badica, P.; Batalu, D.; Burdusel, M.; Grigoroscuta, M.A.; Aldica, G.V.; Enculescu, M.; Gabor, R.A.; Wang, Z.; Huang, R.; Li, P. Compressive properties of pristine and SiC-Te-added MgB2 powders, green compacts and spark-plasma-sintered bulks. Ceram. Int. 2018, 44, 10181–10191. [Google Scholar] [CrossRef]
  41. Aldica, G.V.; Burdusel, M.; Cioca, E.M.; Badica, P. Machinable Superconducting Material and Magnetic Field Concentrator/Storer Made of a Superconducting Material Based on MgB2, Machinable by Chip Remova. Patent No. RO130252-B1, 28 February 2020. [Google Scholar]
  42. Wagner, F.C.; Post, A.; Yilmaz, T.; Maier, D.; Neubauer, J.; Feucht, M.J.; Südkamp, N.P.; Reising, K. Biomechanical comparison of biodegradable magnesium screws and titanium screws for operative stabilization of displaced capitellar fractures. J. Shoulder Elbow Surgery 2020, 29, 1912–1919. [Google Scholar] [CrossRef]
  43. Seitz, J.-M.; Lucas, A.; Kirschner, M. Magnesium-Based Compression Screws: A Novelty in the Clinical Use of Implants. JOM 2016, 68, 1177–1182. [Google Scholar] [CrossRef]
  44. Appendini, P.; Hotchkiss, J.H. Review of antimicrobial food packaging. Innov. Food Sci. Emerg. Technol. Vol. 2002, 3, 113–126. [Google Scholar] [CrossRef]
  45. Badica, P.; Aldica, G.; Burdusel, M.; Popa, S.; Negrea, R.F.; Enculescu, M.; Pasuk, I.; Miu, L. Significant enhancement of the critical current density for cubic BN addition into ex situ spark plasma sintered MgB2. Supercond. Sci. Technol. 2014, 27, 095013. [Google Scholar] [CrossRef]
  46. Batalu, D.; Bunescu, A.; Badica, P. Functional Composite Material with Matrix of Polymer and MgB2 Powder Addition. Patent Request No. RO134554-A0, 27 November 2020. [Google Scholar]
  47. Lutterotti, L. Total pattern fitting for the combined size-strain-stress-texture determination in thin film diffraction. Nucl. Inst. Methods Phys. Res. B 2010, 268, 334–340. [Google Scholar] [CrossRef]
  48. Aldica, G.; Popa, S.; Enculescu, M.; Pasuk, I.; Ionescu, A.M.; Badica, P. Dwell time influence on spark plasma-sintered MgB2. J. Supercond. Nov. Mag. 2018, 31, 317–325. [Google Scholar] [CrossRef]
  49. Avdeev, M.; Jorgensen, J.D.; Ribeiro, R.A.; Budko, S.L.; Canfeld, P.C. Crystal chemistry of carbon-substituted MgB2. Phys. C 2003, 387, 301–306. [Google Scholar] [CrossRef] [Green Version]
  50. Lee, S.; Masui, T.; Yamamoto, A.; Uchiyama, H.; Tajima, S. Crystal growth of C-doped MgB2 superconductors: Accidental doping and inhomogeneity. Phys. C 2004, 412–414, 31–35. [Google Scholar] [CrossRef]
  51. Marks, G.W.; Monson, L.A. Effect of certain group IV oxides on dielectric constant and dissipation factor of barium titanate. Ind. Eng. Chem. 1955, 47, 1611–1620. [Google Scholar] [CrossRef]
  52. Park, C.; Park, S.; Lee, D.; Soon Choi, K.; Lim, H.-P.; Kim, J. Graphene as an Enabling Strategy for Dental Implant and Tissue Regeneration. Tissue Eng. Regen. Med. 2017, 14, 481–493. [Google Scholar] [CrossRef]
  53. Trofa, D.; Gaqcser, A.; Nosanchuk, J.D. Candida parapsilosis, an Emerging Fungal Pathogen. Clin. Microbiol. Rev. 2020, 21, 606–625. [Google Scholar] [CrossRef] [Green Version]
  54. Turalija, M.; Bischof, S.; Budimir, A.; Gaan, S. Antimicrobial PLA films from environment friendly additives. Compos. Part B Eng. 2016, 102, 94–99. [Google Scholar] [CrossRef]
  55. Xie, Y.; Yang, L. Calcium and Magnesium Ions Are Membrane-Active against Stationary-Phase Staphylococcus aureus with High Specificity. Sci. Rep. 2016, 6, 20628. [Google Scholar] [CrossRef]
  56. Hayat, S.; Muzammil, S.; Rasool, M.H.; Nisar, Z.; Hussain, S.Z.; Sabri, A.N.; Jamil, S. In vitro antibiofilm and anti-Adhesion effects of magnesium oxide nanoparticles against antibiotic resistant bacteria. Microbiol. Immunol. 2018, 62, 211–220. [Google Scholar] [CrossRef] [Green Version]
  57. Zaatreh, S.; Haffner, D.; Strauss, M.; Dauben, T.; Zamponi, C.; Mittelmeier, W.; Quandt, E.; Kreikemeyer, B.; Bader, R. Thin magnesium layer confirmed as an antibacterial and biocompatible implant coating in a coculture model. Mol. Med. Rep. 2017, 15, 1624–1630. [Google Scholar] [CrossRef] [Green Version]
  58. Zaatreh, S.; Haffner, D.; Strauss, M.; Wegner, K.; Warkentin, M.; Lurtz, C.; Zamponi, C.; Mittelmeier, W.; Kreikemeyer, B.; Willumeit-Romer, R.; et al. Fast corroding, thin magnesium coating displays antibacterial effects and low cytotoxicity. Biofouling 2017, 33, 294–305. [Google Scholar] [CrossRef]
  59. Lellouche, J.; Kahana, E.; Elias, S.; Gedanken, A.; Banin, E. Antibiofilm activity of nanosized magnesium fluoride. Biomaterials 2009, 30, 5969–5978. [Google Scholar] [CrossRef]
  60. Demishtein, K.; Reifen, R.; Shemesh, M. Antimicrobial Properties of Magnesium Open Opportunities to Develop Healthier Food. Nutrients 2019, 11, 2363. [Google Scholar] [CrossRef] [Green Version]
  61. Nielsen, F.H. Magnesium deficiency and increased inflammation: Current perspectives. J. Inflamm. Res. 2018, 11, 25–34. [Google Scholar] [CrossRef] [Green Version]
Molecules 26 06045 g001 550
Figure 1. (a) MgB2 sintered metallographically polished disc; (b) filament of PLA with embedded MgB2 particles (10 wt.%) used for fabrication of the (c) 3D-printed sample.
Figure 1. (a) MgB2 sintered metallographically polished disc; (b) filament of PLA with embedded MgB2 particles (10 wt.%) used for fabrication of the (c) 3D-printed sample.
Molecules 26 06045 g001
Molecules 26 06045 g002 550
Figure 2. XRD patterns of (a) MgB2 raw powder (LTS), MgB2 as-sintered pristine (LTS SPS), and hBN-added (LTS + (hBN)0.1) MgB2 discs; (b) MgB2 pristine sintered discs before and after being in contact with different bacterial cultures (Staphylococcus aureus (SA), Enterococcus faecium (Ef), and Escherichia coli (Ec)) for different amounts of time.
Figure 2. XRD patterns of (a) MgB2 raw powder (LTS), MgB2 as-sintered pristine (LTS SPS), and hBN-added (LTS + (hBN)0.1) MgB2 discs; (b) MgB2 pristine sintered discs before and after being in contact with different bacterial cultures (Staphylococcus aureus (SA), Enterococcus faecium (Ef), and Escherichia coli (Ec)) for different amounts of time.
Molecules 26 06045 g002
Molecules 26 06045 g003 550
Figure 3. The number of viable microbial cells in log10(CFU/mL) for pristine MgB2 bulk sintered samples. Notations: ns = P > 0.05; * = P ≤ 0.05; ** = P ≤ 0.01; *** = P ≤ 0.001; **** = P ≤ 0.0001.
Figure 3. The number of viable microbial cells in log10(CFU/mL) for pristine MgB2 bulk sintered samples. Notations: ns = P > 0.05; * = P ≤ 0.05; ** = P ≤ 0.01; *** = P ≤ 0.001; **** = P ≤ 0.0001.
Molecules 26 06045 g003
Molecules 26 06045 g004 550
Figure 4. The number of viable microbial cells in log10(CFU/mL) for hBN-added MgB2 bulk sintered samples. Notations: ns = P > 0.05; * = P ≤ 0.05; ** = P ≤ 0.01; *** = P ≤ 0.001; **** = P ≤ 0.0001.
Figure 4. The number of viable microbial cells in log10(CFU/mL) for hBN-added MgB2 bulk sintered samples. Notations: ns = P > 0.05; * = P ≤ 0.05; ** = P ≤ 0.01; *** = P ≤ 0.001; **** = P ≤ 0.0001.
Molecules 26 06045 g004
Molecules 26 06045 g005 550
Figure 5. The number of viable microbial cells in log10(CFU/mL) for 3D-printed PLA+10 wt.% MgB2 samples.
Figure 5. The number of viable microbial cells in log10(CFU/mL) for 3D-printed PLA+10 wt.% MgB2 samples.
Molecules 26 06045 g005
Molecules 26 06045 g006 550
Figure 6. (a) SEM images (secondary electrons SE and backscattering BSE regimes), (b) BSE images, EDS elemental maps of MgB2 sintered bulk sample (LTS SPS, Table 1) after being in contact with E. faecium, and RGB images obtained by overlapping the EDS maps. The presence of Cl and Na on the surface is from the saline solution used for the in vitro tests.
Figure 6. (a) SEM images (secondary electrons SE and backscattering BSE regimes), (b) BSE images, EDS elemental maps of MgB2 sintered bulk sample (LTS SPS, Table 1) after being in contact with E. faecium, and RGB images obtained by overlapping the EDS maps. The presence of Cl and Na on the surface is from the saline solution used for the in vitro tests.
Molecules 26 06045 g006
Table
Table 1. Samples (discs), apparent and relative densities, lattice constants a and c of MgB2, the level of carbon substitution y in Mg(B1−yCy)2, the residual strain of MgB2, phases content, and average crystalline size. Phases identified in XRD patterns of bulk MgB2: MgB2 (ICDD 38-1369), MgB4 (ICDD 73-1014), and MgO (ICDD 45-0946), Mg (ICDD 35–0821), and hBN (ICDD 34-0421).
Table 1. Samples (discs), apparent and relative densities, lattice constants a and c of MgB2, the level of carbon substitution y in Mg(B1−yCy)2, the residual strain of MgB2, phases content, and average crystalline size. Phases identified in XRD patterns of bulk MgB2: MgB2 (ICDD 38-1369), MgB4 (ICDD 73-1014), and MgO (ICDD 45-0946), Mg (ICDD 35–0821), and hBN (ICDD 34-0421).
SampleApparent Density, (g/cm3)/Relative Density, (%)MgB2 Lattice Parameter, a, (Å)MgB2 Lattice Parameter, c, (Å)Amount of Carbon y in Mg (B1−yCy)2Micro-Strain of MgB2 (%)
LTS pwdr.-3.0863 ± 0.00013.5221 ± 0.00010.0011 ± 0.00030.075
LTS SPS2.61/99.33.0821 ± 0.00023.5253 ± 0.00010.0114 ± 0.00060.12 ± 0.04
LTS + (hBN)0.01 SPS2.53/95.03.0840 ± 0.00023.5271 ± 0.00010.0076 ± 0.00050.14 ± 0.08
SamplePhase amount (wt.%)The average crystallite size from XRD (nm)
MgB2MgB4MgOMg/hBNMgB2 MgB4MgOMg/hBN
LTS pwdr.97 ± 0.501.8 ± 0.21.2 ± 0.1/-113 ± 5-45 ± 251 ± 30/-
LTS SPS87.5 ± 0.63.9 ± 0.18.6 ± 0.1-/-130 ± 15105 ± 2050 ± 6-
LTS + (hBN)0.01 SPS78.0 ± 0.43.6 ± 0.17.9 ± 0.2-/10.5 ± 0.2153 ± 14140 ± 6550 ± 8-/79 ± 19
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Badica, P.; Batalu, N.D.; Chifiriuc, M.C.; Burdusel, M.; Grigoroscuta, M.A.; Aldica, G.V.; Pasuk, I.; Kuncser, A.; Popa, M.; Agostino, A.; et al. Sintered and 3D-Printed Bulks of MgB2-Based Materials with Antimicrobial Properties. Molecules 2021, 26, 6045. https://doi.org/10.3390/molecules26196045

AMA Style

Badica P, Batalu ND, Chifiriuc MC, Burdusel M, Grigoroscuta MA, Aldica GV, Pasuk I, Kuncser A, Popa M, Agostino A, et al. Sintered and 3D-Printed Bulks of MgB2-Based Materials with Antimicrobial Properties. Molecules. 2021; 26(19):6045. https://doi.org/10.3390/molecules26196045

Chicago/Turabian Style

Badica, Petre, Nicolae Dan Batalu, Mariana Carmen Chifiriuc, Mihail Burdusel, Mihai Alexandru Grigoroscuta, Gheorghe Virgil Aldica, Iuliana Pasuk, Andrei Kuncser, Marcela Popa, Angelo Agostino, and et al. 2021. "Sintered and 3D-Printed Bulks of MgB2-Based Materials with Antimicrobial Properties" Molecules 26, no. 19: 6045. https://doi.org/10.3390/molecules26196045

APA Style

Badica, P., Batalu, N. D., Chifiriuc, M. C., Burdusel, M., Grigoroscuta, M. A., Aldica, G. V., Pasuk, I., Kuncser, A., Popa, M., Agostino, A., Operti, L., Padhi, S. K., Bonino, V., & Truccato, M. (2021). Sintered and 3D-Printed Bulks of MgB2-Based Materials with Antimicrobial Properties. Molecules, 26(19), 6045. https://doi.org/10.3390/molecules26196045

Article Metrics

Back to TopTop