Next Article in Journal
A Robust and Energy-Efficient Transport Protocol for Cognitive Radio Sensor Networks
Previous Article in Journal
Multifrequency Excitation Method for Rapid and Accurate Dynamic Test of Micromachined Gyroscope Chips
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Sensors
Volume 14
Issue 10
10.3390/s141019517
sensors-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Gas Sensitivity and Sensing Mechanism Studies on Au-Doped TiO2 Nanotube Arrays for Detecting SF6 Decomposed Components

by
Xiaoxing Zhang
*,
Lei Yu
,
Jing Tie
and
Xingchen Dong
State Key Laboratory of Power Transmission Equipment & System Security and New Technology, Chongqing University, Chongqing 400044, China
*
Author to whom correspondence should be addressed.
Sensors 2014, 14(10), 19517-19532; https://doi.org/10.3390/s141019517
Submission received: 25 August 2014 / Revised: 29 September 2014 / Accepted: 8 October 2014 / Published: 17 October 2014
(This article belongs to the Section Chemical Sensors)
Browse Figures
Versions Notes

Abstract

: The analysis to SF6 decomposed component gases is an efficient diagnostic approach to detect the partial discharge in gas-insulated switchgear (GIS) for the purpose of accessing the operating state of power equipment. This paper applied the Au-doped TiO2 nanotube array sensor (Au-TiO2 NTAs) to detect SF6 decomposed components. The electrochemical constant potential method was adopted in the Au-TiO2 NTAs' fabrication, and a series of experiments were conducted to test the characteristic SF6 decomposed gases for a thorough investigation of sensing performances. The sensing characteristic curves of intrinsic and Au-doped TiO2 NTAs were compared to study the mechanism of the gas sensing response. The results indicated that the doped Au could change the TiO2 nanotube arrays' performances of gas sensing selectivity in SF6 decomposed components, as well as reducing the working temperature of TiO2 NTAs.

1. Introduction

Sulfur hexafluoride (SF6) gas has excellent insulating and arc-extinguishing abilities and greatly improves the dielectric strength as an insulating medium. As a result, SF6 gas has been widely used in gas-insulated switchgear (GIS) [1–3]. A large number of domestic and international studies have indicated that partial discharge (PD) usually occurs and causes the decomposition of SF6 with trace moisture and oxygen into various products, such as SOF4, SOF2, SO2F2, SO2, H2S and HF [4,5], at the early stages of the electrical equipment insulation degradation. Such active gases produced by discharge energy will accelerate the aging of insulation and corrode metal surfaces, which may eventually lead to GIS failure. There have been no feasible and effective on-line monitoring methods so far.

Over the past decade, metal oxide semiconductor systems have obtained considerable achievements in sensing application, because of their specific surface geometry, unique functionality and various modification methods. For a recent review in the sensing field, metal doping, metal oxide synthesis and an innovative electrochemical structure are all utilized for the purpose of TiO2 modification [6]. Most of the literature in this area adopts resistive electrical sensors, where the active materials are powders or thin or films [7–10]. For example, Enrico et al. reported the gas sensing properties of TiO2-NiO thin films containing Au nanoparticles toward H2, CO, propane and H2S [11]. The metal modified TiO2 system is proven to have the potential to be an excellent chemical sensor for O2, H2, NO2 and NO [12–14]. Some theory studies based on first-principles calculation are also introduced to explore the surface interaction mechanism [15–17]. However, to the best of our knowledge, detections of SO2F2, as well as of SOF2 are rarely involved, and few examples of SO2 sensors upon metal-doped TiO2 have been reported.

Since the probable sensing mechanism involves the film pores and the surface oxygen adsorbed on component particles during the diffusion process, the morphology plays a crucial role in the sensing property. In order to explore the effect of the morphology on the sensing properties, several researchers have investigated this issue preliminarily. Existing achievements confirm that the gas sensitivity increases with decreasing crystal size as the quantum size effect and predict that crystals in different shapes would affect the sensitivity [18–20]. For example, Min-Hyun Seo et al. prepared TiO2 with different morphologies, nanoparticles and nanotubes on the basis of a hydrothermal treatment method with different treating temperatures [21]. However, other groups have mentioned that the accurate relationship between the electric resistance change of the sensor films and their morphology is a complex problem; the resistance change is not correlated well with their morphology [20,21]. This issue is a consequence of the fact that the electric resistance relies on various parameters, such as tube length, film thickness, grain size, crystal structure and physical factors, such as carrier density and effective mobility. According to our accomplished research on intrinsic [22] and Pt-doped [23] TiO2 nanotube array sensors (TiO2 NTAs) detecting SF6 decomposed components and previous achievements on common gases acquired by other research groups, a precious metal catalyst Au was chosen for this research. However, in the pure gold sensing application, the surface of pure Au is known to be unreactive to most gases, including CO and O2 [24]. While the quantum size effect in gold on a metal oxide support turns out to have an influence on the sensing performance, it is speculated that the reactivity of Au towards oxygen may depend on the small grain size of Au [25,26].

Herein, the present study is part of a systematic investigation of detections for SF6 decomposed products on different materials [27] for the purpose of setting up a practical sensing network for multi-gases detection. In this paper, nano-Au-deposited TiO2 NTAs were developed with the deposition-precipitation method. Then, gas sensing experiments were carried out to detect the main components of SF6 decomposition.

2. Experimental Section

2.1. Preparation of Au-TiO2 Nanotube Arrays

To prepare the Au-TiO2 nanotube arrays, the intrinsic TiO2 nanotubes were first fabricated and then Au was deposited onto the TiO2 nanotubes using the deposition-precipitation method. The intrinsic TiO2 nanotube arrays used in this paper were prepared by the anodic oxidation method [22], and NaOH was selected as the precipitating agent. Firstly, the pH of the 1.01 × 10−3 mol/L HAuCl4 solution was adjusted to 9 using NaOH solution. Then, the intrinsic TiO2 nanotubes were subsequently added to the above solution, resulting in the pH value decreasing. At the moment, a little more NaOH solution was needed to maintain the pH value at 9. Next, the resulting suspension was stirred for 2 h at 70 °C to allow the Au to be supported on the carrier sufficiently. During the process, the suspension became pale purple gradually, and the pH value remained at 9 after cooling. TiO2 nanotubes were picked out, washed, filtered, dried at room temperature and calcined for 4 h at 100 °C to finally obtain the Au-TiO2 nanotube sensors [28].

As for the reasons for keeping the pH at 9, the selection of a pH value of 8–9 is in agreement with several previous experimental investigations [29,30]. A number of groups have proven that the selection of pH leads to different geometries of TiO2 [31], and the pH of an aqueous solution dramatically affects the particle size of Au [32]. Though a finite value for the size cannot be deduced from the activity, since the electronic factors depend on the interaction with the support, the morphology of the particle or the chemical state of the gold, there is general agreement that the activity increases as the particle size decreases [33]. Hence, the pH value of the solution has significant influence on the catalytic activity. A low pH causes a big Au particle, while a high pH causes a low Au deposition amount. The optimum pH aims to not only cause Au to be completely precipitated, but also leads to an appropriate diameter [34]. Ivanova et al. have proven that when the pH value is above 8, the main species of Au in the solution is transformed from AuCl4− to Au(OH)4, leading to a smaller particle diameter. In order to remove Cl− ions completely [35], we chose a pH of 9.

2.2. Equipment and Methods for Gas Sensing Experiments of TiO2 NTAs

Figure 1 exhibits the detection test device in the TiO2 NTAs' response measurements to SF6 decomposed components. Standard gases of SF6 decomposed components were injected through the inlet port. A gas flow meter was used to control and detected the flow rate of the measured gas. A ceramic heater chip and thermal resistance probe were used to control and measure the surface temperature of the sensor. An impedance analyzer was utilized for recording the resistance value of the whole process. The relative changes of the sensor's resistance (i.e., sensitivity) were calculated according to the following formula:

R % = ( R − R 0 ) / R 0 × 100 %
where R represents the resistance value of the sensor after the detected gas injection and R0 indicates the resistance value in a N2 atmosphere. The response time of the sensor is defined as the time that the resistance change reaches 90% of the maximum.

Considering that TiO2 nanotube arrays have the ability to adsorb oxygen and water vapor in the air, a dynamic method was introduced in this experiment to exclude the impact of this factor [36]. The specific steps were as follows.

Firstly, the TiO2 nanotube sensor was placed on the ceramic heating chip, and then, the relative position of the two electrodes and sensors was adjusted, making the two platinum chips full touch the sensor with moderate intensity. Confined space was required in cylinder, and the vacuum pump was turned on to ensure that no sensitive gases remained in the cylinder. High purity N2 at a flow rate of 0.1 L/min along with the heating power on the sensor were appropriate. Besides, the sensor surface temperature was set to a pre-designed operating temperature by adjusting the regulator. Then, the stable resistance of the TiO2 NTAs was recorded as R0.

Secondly, one of the decomposed components of SF6 was pumped in, such as SO2, at the same flow rate as N2. At that moment, the sensor resistance changed dramatically and quickly stabilized (fluctuating around a resistance), which was recorded as the final response resistance.

Finally, after the resistance of the sensor was stable, the high-purity N2 flowed in at a flow rate of 0.1 L/min until the sensor resistance was gradually stabilized at a certain value again, which was recorded as R'0.

3. Results and Discussion

3.1. Morphological Characterization and Analysis of Au-TiO2 Nanotube Arrays

The sample morphology was analyzed by scanning electron microscopy (SEM). The SEM images were obtained by JEOLJSM7000 field emission SEM equipment operated at 10 kV.

Figure 2 shows SEM images of the pore size distribution of films composed of (a) intrinsic TiO2 nanotubes and aggregates and (b) the Au nanoparticles distribution of Au-TiO2 prepared by the deposition-precipitation method. The surfaces of the films were observed before and after Au deposition. It is obvious that the morphology of the TiO2 films is significantly changed after the Au nanoparticle modification. The adopted fabrication method results in the formation of tubular TiO2 of 25 nm in diameter. After the Au deposition treatment, the diameter of the tubes remains about the same. However, on the Au-TiO2 surface, the pipes are covered with Au nanoparticles of a dozen nanometers in size, aggregating at the pipe orifices. The SEM images confirm that the formed films, whether composed of intrinsic or Au-TiO2, are homogeneous with a uniform distribution of pores or Au nanoparticles, respectively, as expected.

The crystal structures of the obtained intrinsic TiO2 and Au-TiO2 nanotubes were analyzed by X-ray diffraction, measured on an X'pert Pro (PANalytical, The Netherland) using Cu Kα radiation (λ = 0.15405 nm) at 40 kV, 35 mA. The wide-angle XRD patterns were collected at a scanning speed of 10°/min over the 2θ range of 20°–100°. Figure 3 gives the XRD patterns of the products prepared by the deposition-precipitation treatment. Previously, Varghese et al. observed both the anatase and rutile phases of TiO2 by annealing treatment in ambient oxygen [37,38]. In our study, the labels A at 25.3° are observed in intrinsic, as well as in Au-doped TiO2, indicating that the crystal phases of TiO2 are both anatase according to previous structural characterizations [39], for which it can be confirmed that, in these preparation conditions, the TiO2 nanotubes adopt an anatase crystal structure, while a rutile structure is not observed. The labels T and Au××× represent the reflections from the titanium substrate and different Au crystallographic forms. It is clearly seen from Figure 3 that characteristic gold peaks come into existence in XRD analysis observed at 38.2° (111), 44.2° (200), 64.3° (220) and 98.1° (400), respectively. The main Au (111) characteristic peak suggests that approximately 10-nm gold nanoparticles are coated onto the anodized TiO2 nanotubes on the basis of the Scherer formula [40]. Meanwhile, a certain amount of 200, 220 and 400 Au particle crystal forms do exist.

3.2. Effects of Different Working Temperatures on the Gas Sensing Properties of Au-TiO2 NTAs

There is a popular belief that the characteristics of a metal oxide semiconductor are greatly affected by the doped metal or metalloid, which would also influence the operating temperature in a sensing application further. Therefore, it is necessary to investigate the gas sensing response of Au-TiO2 NTAs to SF6 decomposed components (i.e., 50 ppm SOF2, SO2F2 and SO2) in an operating range of 20 °C to 200 °C in order to find out the optimum operating temperature.

Figure 4 depicts the curves of the resistance changes' rate (i.e., the response value) of Au-doped and intrinsic TiO2 NTAs to SO2, SOF2 and SO2F2 at different operating temperatures. The response value of the intrinsic TiO2 nanotube to SF6 decomposed components increases as the surface temperature rises, reaching saturation around 180 °C, which is considered the optimum operating temperature. In the case of Au-TiO2, the resistance response increases with increasing operating temperature before 110 °C, following the typical behavior of an oxide semiconductor. However, the resistance response dramatically drops down when the temperature exceeds 110 °C. Hence, the optimum operating temperature of the Au-TiO2 nanotube sensor is taken as 110 °C. A comparison of Au-doped and intrinsic TiO2 indicates that Au-doping reduces the working temperature of TiO2 NTAs along with obvious changes in the temperature characteristic curve.

The performance of the intrinsic TiO2 nanotube sensors maintaining its response value after it reaches 180 °C might be attributed to the dynamic equilibrium of the gas adsorption and desorption rate on the sensor's surface in the meantime. As for Au-TiO2, the Au nanoparticles change the microscopic structure and charge distribution of the surface, and the doped Au results in a promoted chemical desorption rate when the temperature surpasses 110 °C , causing the oxygen desorption rate to be faster than its adsorption rate. As a result, the oxygen chemisorption density on the surface decreases, leading to a rapid drop of the response value [23].

3.3. Sensing Performances of Au-TiO2 NTAs for Detecting SF6 Decomposed Components

The gas sensing response curves of SO2, SOF2 and SO2F2 for Au-TiO2 NTAs were recorded at different concentrations (i.e., 25 ppm, 50 ppm, 75 ppm, 100 ppm) under the optimal operating temperature (110 °C). The results were linearly fit to investigate the linear relationship between the sensor's resistance change and the gas concentration. Therefore, the concentration of target gases in real power equipment could be estimated through the linear relationship acquired by these sample gases.

3.3.1. Sensing Performances of Au-TiO2 NTAs for SO2

As Figure 5 shows, the resistance change rates of the Au-TiO2 nanotube gas sensor for SO2 at 25 ppm, 50 ppm, 75 ppm and 100 ppm are −2.14%, −8.73%, −15.76% and −23.75%, respectively. The linear relationship between the sensor's resistance change rate and the SO2 concentration is fitted as y = −0.287x + 5.37 with a linear correlation coefficient (R2) of 0.997.

3.3.2. Sensing Performances of Au-TiO2 NTAs for SOF2

Figure 6 exhibits the sensing response curves of the Au-TiO2 nanotube sensor for SOF2 at different concentrations under 110 °C. From Figure 6a, the resistance change rates that correspond to 25 ppm, 50 ppm, 75 ppm and 100 ppm of SOF2 are separately −3.00%, −9.97%, −18.42% and −28.37%. After linear fitting, the linear function is calculated to be y = −0.338x + 6.197, as shown in Figure 6b, with R2 equaling 0.991. It can be concluded that, within a certain range of concentrations, a linear relationship between the resistance change rate of the Au-TiO2 nanotube sensor and the SOF2 concentration is also displayed.

3.3.3. Sensing Performances of Au-TiO2 NTAs for SO2F2

Resistance change rates of Au-TiO2 nanotube gas sensor for SOF2 with different concentrations at 25 ppm, 50 ppm, 75 ppm and 100 ppm are respectively −4.04%, −19.58%, −30.93% and −42.31%, as shown in Figure 7a. The linear fitting relationship is y = −0.503x + 7.13,8 and the linear correlation coefficient R2 equals 0.991.

3.4. Selective Gas Sensing Performances of Au-TiO2 NTAs

Figure 8 shows the gas sensing response comparison chart of intrinsic and Au-doped TiO2 NTAs at their optimum operating temperatures for 50 ppm SF6 decomposed gases, i.e., SO2, SOF2 and SO2F2, where the gas sensing properties of intrinsic TiO2 NTAs have been discussed in [22]. The responses of intrinsic and Au-doped TiO2 NTAs both exhibit a negative behavior, i.e., the resistances of intrinsic and Au-doped TiO2 NTAs decrease after introducing these gases.

The gas sensing response values of the intrinsic TiO2 nanotube sensor are SO2 (−74.6%) > SOF2 (−7.82%) > SO2F2 (−5.52%), while for the Au-TiO2 nanotube sensor are SO2F2 (−19.95%) > SOF2 (−9.97%) > SO2 (−8.73%). It is worth noting that the experimental results in our study are statistically significant, the values of which are at the average level according to dozens of experiments. Obviously, the response value of SO2F2 dramatically increases, while SO2 is reduced, and the response of SOF2 remains constant. The selective detection of SO2F2 was actually achieved in our experimental research by the modification of Au nanoparticles at the appropriate operation temperature. Hence, the Au-TiO2 NTAs are potential substrates for the SO2F2 detection application. Furthermore, combined Au-doped and intrinsic TiO2 arrays are promising substrates for SF6 decomposition component detection.

3.5. Stability Investigation of Au-TiO2 NTAs

Serious repeated experiments of SO2 detection at 110 °C were carried out to study the anti-sulfuration ability of a noble metal catalyst for stability investigation. The experimental results are depicted in Figure 9. At the beginning, after 100 ppm SO2 gas is introduced, apparent changes in the sensor's resistance occur. The pure N2 is injected after the sensor's resistance becomes stable, and then, the resistance gradually restores to the initial value. Once the resistance of the sensor exposure to N2 becomes stable, two more times detection procedures are needed continuously. The sensitivity is found to be unchanged along with the resistance value, which always returns to the initial one. This observation indicates that the sensing behavior of Au-TiO2 NTAs prefers a reversible interaction with SO2. When the experiment repeatedly detects SO2 about 20 times, the reduced sensitivity of the sensor is observed. Not even pure N2 can restore the resistance to the original one yet. Then, UV irradiation is adopted; the sensor's resistance rapidly decreases again and remains at a value below the initial resistance when it reaches stability. N2 is introduced again and makes the resistance value gradually increase, to achieve stability ultimately. When SO2 passes into the equipment, the gas sensor's sensitivity obtains the same level as the initial detection. When the Au-TiO2 nanotube sensor is utilized to test the other two gases, its stability curve is basically the same as that of SO2, which will not be displayed here again. The present work demonstrates that the Au-TiO2 in this method provides reusable features, due to its self-cleaning property [41].

As can be concluded, sulfur has certain toxicity for the Au-TiO2 nanotube sensor, which will seriously affect the initial resistance and the sensitivity of the sensor. This obstacle has proven to be effectively solvable by UV irradiation to make the S ions desorb. Compared with the results in the literature [23], the repeatability of Au-doped sensors is greater than that of Pt-doped TiO2 sensors. The gas sensing property begins to decline when Au-TiO2 is repeatedly exposed to SO2 about 20 times, while in the Pt-TiO2 case, it immediately presents an inactive state after the second time, which demonstrates a significant sulfur poisoning phenomenon. Hence, from the experimental observations, we speculate that the anti-sulfide ability of Au is stronger than that of Pt. In all, a comparison of the recovery curves of Au-doped and Pt-doped TiO2 sensors reveals that Au-doped sensors have better repeatability and a superior ability of anti-sulfurization, which is due to the fact that it is more difficult for Au to bond to S compared to Pt [42]. Therefore, Au-doped sensors exhibit better stability, which is a promising property in sensing applications.

3.6. Gas Sensing Mechanism Study of Au-TiO2 NTAs

In order to find out the sensing mechanism, we will discuss the nature of the bonding between Au on TiO2 in the first place. Theoretical studies have been done to find out the deep principle of Au and TiO2. Rodriguez et al. have found essentially covalent bonding between Au and Ti sites [43]. Besides, a minor depletion of electrons on Au was observed when Au was bonded to O centers on the surface [44,45]. Moreover, previous research indicates that gold grows on TiO2 epitaxially, generating two- or three-dimensional particles (Volmer–Weber growth mode) [24,46], which is in accordance with our SEM analysis. A general agreement has been reached that two key phenomena are basically responsible for the prominent sensitivity found for Au-TiO2 in our experimental study and previous catalytic investigations. On the one hand, interactions with TiO2 electronically perturb gold, making it more chemically active [47–49]. On the other hand, gold increases the concentration of O vacancies at the surface of the oxide [50], enhancing the chemical activity of TiO2, as well.

As shown in Figure 8, the gas sensing response values of intrinsic and Au-doped TiO2 nanotube sensors for SO2, SOF2 and SO2F2 are concurrently negative responses. According to the existing achievements, three measured gases all play the role of an electron donating gas. The following reaction occurs:

R + O ads − ⇔ R O ads + e −

R represents the resistance of SO2, SOF2 and SO2F2, three SF6 decomposed components; Oads− denotes the adsorbed oxygen on the sensor's surface.

The charge transfer that results in the negative responses is important during the processes occurring at the gases/oxide interfaces. Oxygen ions at the TiO2 boundaries between the grains cause a higher potential barrier, which will block the charge carriers' transfer, leading to a relatively large resistance [51]. When a reducing gas or an electron donating gas comes into contact with the TiO2 nanotube sensor, the chemical reaction of the gases and the adsorbed oxygen on the sensor's surface occurs, resulting in a sharp decrease of the adsorbed oxygen. Thereby, the potential barrier of the grain boundary on the surface is reduced and then contributes to more charge carrier transfers and a decrease in the resistance of the TiO2 nanotube sensor to obtain the sensing response.

A detailed understanding of the processes occurring at the Au/oxide interfaces and their relationship to the sensing performance of sensor devices could lead to enhancements in the selective phenomenon displayed in Figure 8, where the SO2F2 response value increases greatly, while that of SOF2 remains essentially unchanged and the response for SO2 decreases. This is probably a consequence of poisoning effect of sulfur (being less sensitive to the presence of S-containing molecules) for a noble metal on the sensing performances. A fundamental understanding of the chemistry of S-containing molecules, like CH3SH, H2S and S2, on a metal/oxide surface (Al2O3, ZnO, Cu2O etc.) has been achieved [52,53]. On the surface of a metal oxide, sulfur prefers to interact with the supported metal sites rather than the oxide support, producing sulfide or sulfate that has a different electronic property [54]. The toxicity order of these three gases is SO2 > SOF2 > SO2F2, according to [55]. Sulfate produced by the adsorption of SO2 blocks the electron holes on TiO2, causing a reduction of O2 or O2− adsorption on the vacancies. The strongest poisoning effect of SO2 might account for the detrimental situation for SO2 detection.

The surface adsorption-controlled mechanism [56] for the Au/TiO2 surface interactions to these three SF6 components is another reason for this selectivity case. For TiO2 semiconductor-based gas sensors, target gases diffuse on the TiO2 sensing film through pores and interact with surface oxygen, as well as adsorbed Au particles, to induce the electronic resistance change [57]. The concentration of these gases decreases inside the TiO2 film as a consequence of the diffusion. The doped Au particles provide more chemically active sites on the TiO2 surface, while making the TiO2 film be insufficiently porous at the same time. We have found that the intrinsic TiO2 NATs have a remarkable sensitivity to SO2 in our previous published research [22]. The porosity of intrinsic TiO2 is found to be the dominant reason for the pronounced sensitivity of SO2. Such macropores of intrinsic TiO2 provide effect-diffusivity paths for molecules and enhance the utility factor of the sensing film. Besides, the insensitivity of intrinsic TiO2 to SO2F2 and SOF2 is probably because they are difficult to diffuse deep inside the TiO2 films with relatively large molecular sizes [21,58]. However, in this work, the Au nanoparticles cover the efficient porous morphology, which leads to a decrease in the sensor response for SO2, due to a decrease in the utility factor of the TiO2 sensing film or a decrease in the accessibility of this gas. Hence, the doping is actually disadvantageous for SO2 detection. However, things change to another way when it comes to SO2F2 upon Au-TiO2. At the optimum temperature, Au exhibits an active catalytic activity that leads to a rupture of the S-F bonds. A similar phenomenon of SO2F2 dissociation has been observed at the crystal oxygen vacancy on the TiO2 surface through the first-principles calculations [59]. Thus, the chemisorption effect of Au-TiO2 for SO2F2 is a reliable reason that accounts for the experimental response. As for the SOF2 adsorption case, from the experimental observation, the interaction between Au-TiO2 and SOF2 is not as strong as the SO2F2 case. In all, we have reasons to speculate that the poisoning effect and the surface adsorption-controlled mechanism induce the selective properties in sensing performances.

4. Conclusions

The detection of SF6 decomposed gases is becoming ever more important due to the significant relationship with insulation faults in power equipment. Current methods of detection suffer from the shortage of on-line monitoring. Thus, there is value in developing an effective method for detection. The electrochemistry sensor is proven to be a promising path to achieve on-line detection.

Here, SF6 decomposed gas sensors incorporating Au and TiO2 were fabricated through the deposition-precipitation method and studied under a spectrum of different operating temperatures. The study of the sensing response of Au-TiO2 sensors reveals the dependency on the optimum temperature. These Au-TiO2 sensors were capable of detecting 50 ppm SO2F2, SOF2 and SO2 with reproducible performances. Meanwhile, the responses for SO2F2, SOF2 and SO2 at the optimum temperature (110 °C) indicate selectivity for SO2F2 detection, which we attribute to the poisoning effect of SO2 and the surface adsorption-controlled mechanism of all gases at the Au/TiO2 surface. A comparative study of the optimum operation temperature of intrinsic TiO2 and Au-TiO2 reveals that the doped Au nanoparticles reduce the working temperature. In addition, the differences in the recovery curves of Au-doped and Pt-doped TiO2 nanotube sensors confirm that Au-doped TiO2 has a better anti-sulfuration ability and stability.

In the future, we aim to evaluate the relationship between the morphology of the Au-TiO2 composite and the sensing properties, since the morphology was considered to have a significant effect on the sensor response in previous research. We believe that this could make the method of producing SF6 decomposed gas sensors viable in practical application.

Acknowledgments

This work is supported by the Basic Science Research Program through the National Natural Science Foundation of China (NSFC. 51277188) and the 985 National Key Discipline Construction Project. The School of Chemistry and Chemical Engineering of Chongqing University, which supports some experimental instruments, is also appreciated.

Author Contributions

Xiaoxing Zhang designed the project, instructed the research and modified the manuscript. Lei Yu and Jing Tie performed the experiments and wrote the manuscript. Xingchen Dong modified the manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Ju, T.; Ping, F.Z.; Yu, J.P.; Xing, X.Z.; Qiang, Y.; He, J.; Hou, X. Correlation analysis between formation process of SF6 decomposed components and partial discharge qualities. IEEE Trans. Dielectr. Electr. Insul. 2013, 20, 864–875. [Google Scholar]
  2. Ju, T.; Fan, L.; Xing, X.Z.; Meng, Q.; Zhou, J.H. Partial Discharge Recognition through an Analysis of SF6 Decomposition Products Part 1: Decomposition characteristics of SF6 under four different partial discharges. IEEE Trans. Dielectr. Electr. Insul. 2012, 19, 29–36. [Google Scholar]
  3. Ju, T.; Fan, L.; Meng, Q.; Xing, X.Z.; Tao, J. Partial Discharge Recognition through an Analysis of SF6 Decomposition Products Part 2: Feature Extraction and Decision Tree-Based Pattern Recognition. IEEE Trans. Dielectr. Electr. Insul. 2012, 19, 37–44. [Google Scholar]
  4. Beyer, C.; Jenett, H.; Klockow, D. Influence of reactive SFx gases on electrode surfaces after electrical discharges under SF6 atmosphere. IEEE Trans. Dielectr. Electr. Insul. 2000, 7, 234–240. [Google Scholar]
  5. Brunt, R.J.V.; Herron, J.T. Fundamental processes of SF6 decomposition andoxidation in glow and corona discharges. IEEE Trans. Dielectr. Electr. Insul. 1990, 25, 75–94. [Google Scholar]
  6. Azad, A.M.; Akbar, S.A.; Mhaisalkar, S.G.; Birkefeld, L.D.; Goto, K.S. Solid-state gas sensors: A review. J. Electrochem. Soc. 1992, 139, 3690–3704. [Google Scholar]
  7. Kapse, V.D.; Ghosh, S.A.; Chaudhari, G.N.; Raghuwanshi, F.C. Nanocrystalline In2O3-based H2S sensors operable at low temperatures. Talanta 2008, 76, 610–616. [Google Scholar]
  8. Wang, Y.; Wang, Y.M.; Cao, J.; Kong, F.; Xia, H.; Zhang, J.; Zhu, B.; Wang, S.; Wu, S. Low-temperature H2S sensors based on Ag-doped α-Fe2O3 nanoparticles. Sens. Actuators B Chem. 2008, 131, 183–189. [Google Scholar]
  9. Rumyantseva, M.; Labeau, M.; Delabouglise, G.; Ryabova, L.; Kutsenok, I.; Gaskov, A. Copper and nickel doping effect on interaction of SnO2 films with H2S. J. Mater. Chem. 1997, 7, 1785–1790. [Google Scholar]
  10. Jain, G.H.; Patil, L.A.; Wagh, M.S.; Patil, D.R.; Patil, S.A.; Amalnerkar, D.P. Surface modified BaTiO3 thick film resistors as H2S gas sensors. Sens. Actuators B Chem. 2006, 117, 159–165. [Google Scholar]
  11. Della Gaspera, E.; Guglielmi, M.; Agnoli, S.; Granozzi, G.; Post, M.L.; Bello, V.; Giovanni Mattei, G.; Martucci, A. Au Nanoparticles in Nanocrystalline TiO2-NiO Films for SPR-Based, Selective H2S Gas Sensing. Chem. Mater. 2010, 22, 3407–3417. [Google Scholar]
  12. Zeng, W.; Liu, T.; Wang, Z.; Tsukimoto, S.; Saito, M.; Ikuhara, Y. Selective detection of formaldehyde gas using a Cd-doped TiO2-SnO2 sensor. Sensors 2009, 9, 9029–9038. [Google Scholar]
  13. Mohammadi, M.R.; Fray, D.J.; Cordero-Cabrera, M.C. Sensor performance of nanostructured TiO2 thin films derived from particulate sol-gel route and polymeric fugitive agents. Sens. Actuators B Chem. 2007, 124, 74–83. [Google Scholar]
  14. Traversa, E.; di Vona, M.L.; Licoccia, S.; Sacerdoti, M.; Carotta, M.C.; Crema, L.; Martinelli, G. Sol-gel processed TiO2-based nano-sized powders for use in thick-film gas sensors for atmospheric pollutant monitoring. J. Sol-Gel Sci. Technol. 2001, 22, 167–179. [Google Scholar]
  15. Rodriguez, J.A.; Jirsak, T.; Liu, G.; Hrbek, J.; Dvorak, J.; Maiti, A. Chemistry of NO2 on oxide surfaces: Formation of NO3 on TiO2 (110) and NO2 ↔ O vacancy interactions. J. Am. Chem. Soc. 2001, 123, 9597–9605. [Google Scholar]
  16. Rodriguez, J.A.; Hrbek, J.; Dvorak, J.; Jirsak, T.; Maiti, A. Interaction of sulfur with TiO2(110): Photoemission and density-functional studies. Chem. Phys. Lett. 2001, 336, 377–384. [Google Scholar]
  17. Wen, Z.; Tian-mo, L. Hydrogen sensing characteristics and mechanism of nanosize TiO2 dope with metallic ions. Phys. B Condens. Matter 2010, 405, 564–568. [Google Scholar]
  18. Yamazoe, N.; Shimanoe, K. Roles of shape and size of component crystals in semiconductor gas sensors I. Response to oxygen. J. Electrochem. Soc. 2008, 155, 85–92. [Google Scholar]
  19. Yamazoe, N.; Shimanoe, K.; Sawada, C. Contribution of electron tunneling transport in semiconductor gas sensor. Thin Solid Films 2007, 515, 8302–8309. [Google Scholar]
  20. Frasco, M.F.; Chaniotakis, N. Semiconductor quantum dots in chemical sensors and biosensors. Sensors 2009, 9, 7266–7286. [Google Scholar]
  21. Min-Hyun, S.; Masayoshi, Y.; Tetsuya, K.; Jeung, H.; Kengo, S.; Noboru, Y. Gas sensing characteristics and porosity control of nanostructured films composed of TiO2 nanotubes. Sens. Actuators B Chem. 2009, 137, 513–520. [Google Scholar]
  22. Xing, X.Z.; Bin, J.Z.; Jia, Y.; Peng, X.; Ju, T. TiO2 Nanotube Array Sensor for Detecting the SF6 Decomposition Product SO2. Sensors 2012, 12, 3302–3313. [Google Scholar]
  23. Xing, X.Z.; Jing, T.; Bin, J.Z. A Pt-Doped TiO2 Nanotube Arrays Sensor for Detecting SF6 Decomposition Products. Sensors 2013, 13, 14764–14776. [Google Scholar]
  24. Zhang, L.; Persaud, R.; Madey, T.E. Ultrathin metal films on a metal oxide surface: Growth of Au on TiO2 (110). Phys. Rev. B 1997, 56, 10549. [Google Scholar]
  25. Haruta, M.; Yamada, N.; Kobayashi, T.; Iijima, S. Gold catalysts prepared by coprecipitation for low-temperature oxidation of hydrogen and of carbon monoxide. J. Catal. 1989, 115, 301. [Google Scholar]
  26. Kobayashi, T.; Haruta, M.; Sano, H.; Nakane, M. A selective CO sensor using Ti-doped α-Fe2O3 with coprecipitated ultrafine particles of gold. Sens. Actuators B Chem. 1988, 13, 339. [Google Scholar]
  27. Zhang, X.X.; Liu, W.T.; Tang, J.; Xiao, P. Study on PD detection in SF6 using multi-wall carbon nanotube films sensor. IEEE Trans. Dielectr. Electr. Insul. 2010, 17, 833–838. [Google Scholar]
  28. Zhu, B.; Guo, Q.; Huang, X.; Wang, S.; Zhang, S.; Wu, S.; Huang, W. Characterization and catalytic performance of TiO2 nanotubes-supported gold and copper particles. J. Mol. Catal. A Chem. 2006, 249, 211–217. [Google Scholar]
  29. Cunningham, D.A.H.; Vogel, W.; Kageyama, H.; Tsubota, S.; Haruta, M. The relationship between the structure and activity of nanometer size gold when supported on Mg(OH)2. J. Catal. 1998, 177, 1–10. [Google Scholar]
  30. Dekkers, M.A.P.; Lippits, M.J.; Nieuwenhuys, B.E. Supported gold/MOx catalysts for NO/H2 and CO/O2 reactions. Catal. Today 1999, 54, 381–390. [Google Scholar]
  31. Macak, J.M.; Schmuki, P. Anodic growth of self-organized anodic TiO2 nanotubes in viscous electrolytes. Electrochim. Acta 2006, 52, 1258–1264. [Google Scholar]
  32. Xu, Q.; Kharas, K.C.; Datye, A.K. The preparation of highly dispersed Au/Al2O3 by aqueous impregnation. Catal. Lett. 2003, 85, 229–235. [Google Scholar]
  33. Guczi, L.; Beck, A.; Pászti, Z. Gold catalysis: Effect of particle size on reactivity towards various substrates. Catal. Today 2012, 181, 26–32. [Google Scholar]
  34. Ivanova, S.; Petit, C.; Pitchon, V. A new preparation method for the formation of gold nanoparticles on an oxide support. Appl. Catal. A Gen. 2004, 267, 191–201. [Google Scholar]
  35. Haruta, M.; Ueda, A.; Tsubota, S.; Torres Sanchez, R.M. Low-temperature catalytic combustion of methanol and its decomposed derivatives over supported gold catalysts. Catal. Today. 1996, 29, 443–447. [Google Scholar]
  36. Garzella, C.; Comini, E.; Tempesti, E.; Frigeri, C.; Sberveglieri, G. TiO2 thin films by a novel sol–gel processing for gas sensor applications. Sensor Actuators B Chem. 2000, 68, 189–196. [Google Scholar]
  37. Şennik, E.; Çolak, Z.; Kılınç, N.; Öztürk, Z.Z. Synthesis of highly-ordered TiO2 nanotubes for a hydrogen sensor. Int. J. Hydrog. Energy 2010, 35, 4420–4427. [Google Scholar]
  38. Sun, X.M.; Yadong, L. Synthesis and characterization of ion-exchangeable titanate nanotubes. Chem. Eur. J. 2003, 9, 2229–2238. [Google Scholar]
  39. Varghese, O.K.; Gong, D.; Paulose, M.; Ong, K.G.; Grimes, C.A. Hydrogen sensing using titania nanotubes. Sens. Actuators B Chem. 2003, 93, 338–344. [Google Scholar]
  40. Patterson, A.L. The Scherrer formula for X-ray particle size determination. Phys. Rev. 1939, 56, 978. [Google Scholar]
  41. Fujishima, A.; Honda, K. Photolysis-decomposition of water at the surface of an irradiated semiconductor. Nature 1972, 238, 37–38. [Google Scholar]
  42. Henry, W. Mechanisms of catalyst poisoning by sulfur species. Stud. Surf. Sci. Catal. 1991, 68, 497–504. [Google Scholar]
  43. Wahlström, E.; Lopez, N.; Schaub, R.; Thostrup, P.; Rønnau, A.; Africh, C.; Besenbacher, F. Bonding of Gold Nanoclusters to Oxygen Vacancies on Rutile TiO2 (110). Phys. Rev. Lett. 2003. [Google Scholar] [CrossRef]
  44. Okazaki, K.; Morikawa, Y.; Tanaka, S.; Tanaka, K.; Kohyama, M. Electronic structures of Au on TiO2 (110) by first-principles calculations. Phys. Rev. B. 2004. [Google Scholar] [CrossRef]
  45. Liu, Z.P.; Gong, X.Q.; Kohanoff, J.; Sanchez, C.; Hu, P. Catalytic role of metal oxides in gold-based catalysts: A first principles study of CO oxidation on TiO2 supported Au. Phys. Rev. Lett. 2003, 91. [Google Scholar] [CrossRef]
  46. Parker, S.C.; Grant, A.W.; Bondzie, V.A.; Campbell, C.T. Island growth kinetics during the vapor deposition of gold onto TiO2 (110). Surf. Sci. 1999, 441, 10–20. [Google Scholar]
  47. Cosandey, F.; Zhang, L.; Madey, T.E. Effect of substrate temperature on the epitaxial growth of Au on TiO2(110). Surf. Sci. 2001, 474, 1–13. [Google Scholar]
  48. Valden, M.; Lai, X.; Goodman, D.W. Onset of catalytic activity of gold clusters on titania with the appearance of nonmetallic properties. Science 1998, 281, 1647–1650. [Google Scholar]
  49. Cosandey, F.; Madey, T.E. Growth, morphology, interfacial effects and catalytic properties of Au on TiO2. Surf. Rev. Lett. 2001, 8, 73–93. [Google Scholar]
  50. Rodriguez, J.A.; Liu, G.; Jirsak, T.; Hrbek, J.; Chang, Z.; Dvorak, J.; Maiti, A. Activation of gold on titania: Adsorption and reaction of SO2 on Au/TiO2 (110). J. Am. Chem. Soc. 2002, 124, 5242–5250. [Google Scholar]
  51. Choi, B.J.; Jeong, D.S.; Kim, S.K.; Rohde, C.; Choi, S.; Oh, J.H.; Kim, H.J.; Hwang, C.S.; Szot, K.; Waser, R.; et al. Resistive switching mechanism of TiO2 thin films grown by atomic-layer deposition. J. Appl. Phys. 2005. [Google Scholar] [CrossRef]
  52. Rodriguez, J.A.; Dvorak, J.; Jirsak, T. Chemistry of SO2, H2S, and CH3SH on carbide-modified Mo(110) and Mo2C powders: Photoemission and XANES studies. J. Phys. Chem. B. 2000, 104, 11515–11521. [Google Scholar]
  53. Choi, S.J.; Jang, B.H.; Lee, S.J.; Min, B.K.; Rothschild, A.; Kim, I.D. Selective detection of acetone and hydrogen sulfide for the diagnosis of diabetes and halitosis using SnO2 nanofibers functionalized with reduced graphene oxide nanosheets. ACS Appl. Mater. Inter. 2014, 6, 2588–2597. [Google Scholar]
  54. Rodriguez, J.A.; Hrbek, J. Interaction of sulfur with well-defined metal and oxide surfaces: Unraveling the mysteries behind catalyst poisoning and desulfurization. Accounts Chem. Res. 1999, 32, 719–728. [Google Scholar]
  55. Kim, M.R.; Woo, S.I. Poisoning effect of SO2 on the catalytic activity of Au/TiO2 investigated with XPS and in situ FT-IR. Appl. Catal. A Gen. 2006, 299, 52–57. [Google Scholar]
  56. Hall, S.B.; Khudaish, E.A.; Hart, A.L. Electrochemical oxidation of hydrogen peroxide at platinum electrodes. Part 1. An adsorption-controlled mechanism. Electrochim. Acta 1997, 43, 579–588. [Google Scholar]
  57. Nian, Y.B.; Strozier, J.; Wu, N.J.; Chen, X.; Ignatiev, A. Evidence for an oxygen diffusion model for the electric pulse induced resistance change effect in transition-metal oxides. Phys. Rev. Lett. 2007. [Google Scholar] [CrossRef]
  58. Chen, D.; Huang, F.; Cheng, Y.B.; Caruso, R.A. Mesoporous Anatase TiO2 beads with high surface areas and controllable pore sizes: A superior candidate for high-performance dye sensitized solar cells. Adv. Mater. 2009, 21, 2206–2210. [Google Scholar]
  59. Xing, X.Z.; Chuan, Q.C.; Ju, T.; Hua, W.H.; Bin, J.Z. Adsorption of SF6 decomposed gas on anatase (101) and (001) surfaces with oxygen defect: A density functional theory study. Sci. Rep.—UK 2014, 4, 1–11. [Google Scholar]
Sensors 14 19517f1 1024
Figure 1. Detection test device in the TiO2 nanotube array (NTA) response measurements to SF6 decomposed components.
Figure 1. Detection test device in the TiO2 nanotube array (NTA) response measurements to SF6 decomposed components.
Sensors 14 19517f1 1024
Sensors 14 19517f2 1024
Figure 2. (a) SEM image of the intrinsic TiO2 nanotubes. (b) SEM image of the Au-TiO2 nanotubes.
Figure 2. (a) SEM image of the intrinsic TiO2 nanotubes. (b) SEM image of the Au-TiO2 nanotubes.
Sensors 14 19517f2 1024
Sensors 14 19517f3 1024
Figure 3. XRD of Au-TiO2 nanotubes.
Figure 3. XRD of Au-TiO2 nanotubes.
Sensors 14 19517f3 1024
Sensors 14 19517f4 1024
Figure 4. Sensor responses for 50 ppm SO2 (black dots), SOF2 (red dots) and SO2F2 (green dots), respectively, for the intrinsic (short dashed lines, in the range of 20 °C∼240 °C) and Au-doped TiO2 (solid lines, in the range of 20 °C∼200 °C) nanotubular films at different working temperatures.
Figure 4. Sensor responses for 50 ppm SO2 (black dots), SOF2 (red dots) and SO2F2 (green dots), respectively, for the intrinsic (short dashed lines, in the range of 20 °C∼240 °C) and Au-doped TiO2 (solid lines, in the range of 20 °C∼200 °C) nanotubular films at different working temperatures.
Sensors 14 19517f4 1024
Sensors 14 19517f5 1024
Figure 5. (a) Au-TiO2 NTAs' response to different concentrations of SO2 at the 110 °C working temperature. (b) Linear relationship between the sensor's response value and the SO2 concentration.
Figure 5. (a) Au-TiO2 NTAs' response to different concentrations of SO2 at the 110 °C working temperature. (b) Linear relationship between the sensor's response value and the SO2 concentration.
Sensors 14 19517f5 1024
Sensors 14 19517f6 1024
Figure 6. (a) Au-doped TiO2 NTAs' response to different concentrations of SOF2 at the 110 °C working temperature. (b) Linear relationship between the sensor's response value and the SOF2 concentration.
Figure 6. (a) Au-doped TiO2 NTAs' response to different concentrations of SOF2 at the 110 °C working temperature. (b) Linear relationship between the sensor's response value and the SOF2 concentration.
Sensors 14 19517f6 1024
Sensors 14 19517f7 1024
Figure 7. (a) Au-doped TiO2 NTAs response to different concentrations of SO2F2 at the 110 °C working temperature. (b) Linear relationship between the sensor's response value and the SO2F2 concentration.
Figure 7. (a) Au-doped TiO2 NTAs response to different concentrations of SO2F2 at the 110 °C working temperature. (b) Linear relationship between the sensor's response value and the SO2F2 concentration.
Sensors 14 19517f7 1024
Sensors 14 19517f8 1024
Figure 8. Sensor responses of Au-doped and intrinsic TiO2 nanotube arrays for SF6 decomposition components.
Figure 8. Sensor responses of Au-doped and intrinsic TiO2 nanotube arrays for SF6 decomposition components.
Sensors 14 19517f8 1024
Sensors 14 19517f9 1024
Figure 9. Recovery curve of the Au-TiO2 nanotubes sensor.
Figure 9. Recovery curve of the Au-TiO2 nanotubes sensor.
Sensors 14 19517f9 1024

Share and Cite

MDPI and ACS Style

Zhang, X.; Yu, L.; Tie, J.; Dong, X. Gas Sensitivity and Sensing Mechanism Studies on Au-Doped TiO2 Nanotube Arrays for Detecting SF6 Decomposed Components. Sensors 2014, 14, 19517-19532. https://doi.org/10.3390/s141019517

AMA Style

Zhang X, Yu L, Tie J, Dong X. Gas Sensitivity and Sensing Mechanism Studies on Au-Doped TiO2 Nanotube Arrays for Detecting SF6 Decomposed Components. Sensors. 2014; 14(10):19517-19532. https://doi.org/10.3390/s141019517

Chicago/Turabian Style

Zhang, Xiaoxing, Lei Yu, Jing Tie, and Xingchen Dong. 2014. "Gas Sensitivity and Sensing Mechanism Studies on Au-Doped TiO2 Nanotube Arrays for Detecting SF6 Decomposed Components" Sensors 14, no. 10: 19517-19532. https://doi.org/10.3390/s141019517

APA Style

Zhang, X., Yu, L., Tie, J., & Dong, X. (2014). Gas Sensitivity and Sensing Mechanism Studies on Au-Doped TiO2 Nanotube Arrays for Detecting SF6 Decomposed Components. Sensors, 14(10), 19517-19532. https://doi.org/10.3390/s141019517