Next Article in Journal
Knowledge of Health Effects and Intentions to Quit Among Smokers in India: Findings From the Tobacco Control Policy (TCP) India Pilot Survey
Previous Article in Journal
Seasonality of Suicidal Behavior
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
IJERPH
Volume 9
Issue 2
10.3390/ijerph9020548
ijerph-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Application of Porous Nickel-Coated TiO2 for the Photocatalytic Degradation of Aqueous Quinoline in an Internal Airlift Loop Reactor

by
Suiyi Zhu
,
Xia Yang
*,
Wu Yang
,
Leilei Zhang
,
Jian Wang
and
Mingxin Huo
*
Department of Environmental Science and Engineering, Northeast Normal University, Changchun 130024, China
*
Authors to whom correspondence should be addressed.
Int. J. Environ. Res. Public Health 2012, 9(2), 548-563; https://doi.org/10.3390/ijerph9020548
Submission received: 31 December 2011 / Revised: 2 February 2012 / Accepted: 9 February 2012 / Published: 15 February 2012
Browse Figures
Versions Notes

Abstract

:
P25 film, prepared by a facile dip-coating method without any binder, was further developed in a recirculating reactor for quinoline removal from synthetic wastewater. Macroporous foam Ni, which has an open three-dimensional network structure, was utilized as a substrate to make good use of UV rays. Field emission scanning electron microscopy and X-ray diffraction analysis showed that the coated/calcinated P25 films consisted of two crystal phases, and had a number of uniform microcracks on the surface. The effects of initial quinoline concentration, light intensity, reaction temperature, aeration, and initial pH were studied. Increased reaction time, light intensity, environmental temperature, and gas aeration were found to significantly improve the quinoline removal efficiency. The aeration effect of oxygen dependency on the quinoline degradation had the trend pure oxygen > air > no gas > pure nitrogen with free O2. The solution pH crucially affected quinoline photodegradation; the high electrostatic adsorption of quinoline molecules on the TiO2 surface was strongly pH dependent. 2-Pyridine-carboxaldehyde, 3-pyridinecarboxaldehyde, and 2(1H)-quinolinone were identified as the major intermediates of quinoline degradation. Based on these intermediates, a primary degradation mechanism was proposed. This reusable P25 film benefits the photodegradation of water contaminants and has potential in other various applications.

1. Introduction

Quinoline, a representative heterocyclic nitrogen (N) compound, is widely used as a raw material in different industries (e.g., petroleum, chemical, medical, and pesticide). Due to the presence of N in this heterocyclic compound, quinoline has a low Henry constant and high water solubility. Hence, quinoline is difficultly biodegradable, tends to accumulate in natural water environments [1], and has toxic properties. Consequently, quinoline is gaining attention given the health risks it poses [2].
The use of TiO2 is an attractive technique for the complete destruction of undesirable liquid and gaseous contaminants by ultraviolet (UV) light or solar illumination. For quinoline degradation, many microscale/nanoscale catalysts like phase-pure TiO2, TiO2 (Degussa P25), doped TiO2, and WO3 [3,4,5,6] have been applied in different slurry systems. For example, the use of S-doped TiO2 powder in a stirred slurry reactor presented high degradation efficiency under these experimental conditions regardless of the catalyst recovery and reuse [5,6], whereas both OH·and O2·radicals generated in the photocatalytic process led to the opening of a heterocyclic ring [7]. Some cases mainly focused on suspended slurry systems and proved that nanometer TiO2 powders with high crystallinities and large specific surface areas are efficient for water purification at ambient conditions.
However, photocatalyst separation from a suspension and the aggregation of dispersed particles in a slurry reactor hamper the practical applications of TiO2 powders [8]. Hence, recent studies have focused on the development of nano-TiO2 immobilized on different substrates to increase the photocatalytic degradation efficiency as well as avoid the abovementioned separation and aggregation limitations. TiO2 coated/calcinated on a porous substrate has also been experimentally found to enhance the photocatalytic efficiency of TiO2 films by enlarging the Brunauer-Emmett-Teller (BET) surface area and TiO2 loaded amount [9,10]. A few researchers have reported a nano-TiO2-coated porous metal for the photocatalytic degradation of indoor volatile organic compounds [11]. However, to our knowledge, studies on the design and use of a photocatalytic reactor based on a TiO2 film-coated nickel (Ni) foam for the degradation of aqueous pollutants is very limited. Such studies have very significant implications in the treatment of industrial wastewater.
The present study aimed to investigate the applicability of a Degussa P25 TiO2 film coated/calcinated on porous Ni in a new tubular photocatalytic reactor for the minimization of model wastewater containing quinoline. The influence of various parameters (i.e., initial concentration, environmental temperature, light intensity, aeration, and pH) on the efficiency of the process was assessed to optimize the degradation. The photocatalytic stability of the P25 film was also evaluated.

2. Materials and Methods

2.1. Materials

Quinoline (C9H7N, MW = 129) was acquired from Sinopharm, China, and used without further purification. TiO2 (P25; ca. 80% anatase and 20% rutile) was purchased from Deguessa, Germany, and had a BET surface area of 55 m2/g. Anhydrous alcohol was obtained from Sigma. The natural pH of the synthetic wastewater containing quinoline was 6.7. Prior to photodegradation, the pH of the wastewater was adjusted using a small amount of either H2SO4 or NaOH, and was monitored by a digital pH meter (WTW Multi 340i, Germany). All chemicals used were reagent grade. The distilled water used to prepare all sample solutions was prepared in our laboratory.

2.2. Preparation and Characterization of the Photocatalyst

Degussa P25 TiO2 was immobilized on porous Ni (denoted as TiO2/Ni) via a facile dip-coating method without the use of coating equipment, as reported in our previous study [12]. P25 TiO2 was added to anhydrous alcohol [13], and then dispersed for 10 min under ultrasonic agitation to confect the P25 sol to 10% concentration.
Foam Ni with a specific surface area of 0.25 m2/g was used as a support because of its homogeneous vesicular structure and facile machining properties, which are beneficial to increasing the contact of photocatalysts with UV rays [14,15]. Pre-dried foam Ni was cut into tubes of 40 cm × Ø 7 cm, and then immersed into the P25 sol for 20 s. The tubes were taken out and air dried at room temperature. After ethanol volatilization overnight, the TiO2/Ni film was calcined at 90 °C for 60 min, and then at 450 °C for 30 min at a heating rate of 3 °C/min in a muffle furnace. The TiO2/Ni film obtained was washed with boiling water to remove uncoated TiO2 particles. The surface morphology of the prepared TiO2/Ni film and bare porous Ni substrate were observed using a field emission scanning electron microscopy (FESEM) system (XL-30 ESEM FEG, Philips). The crystal phase structures were measured by X-ray diffraction (XRD) on a Rigaku D/max-3c diffractometer (CuKα radiation, λ = 0.15405 nm). The specific surface area of the prepared TiO2/Ni film was 8.5 m2/g, as determined by nitrogen adsorption-desorption measurements (TriStar 3000).

2.3. Photocatalytic Reactor

An internal airlift loop photocatalytic reactor made of Pyrex glass was used for the photocatalytic experiments, as shown in Figure 1. The effective volume of the reactor was 3.5 L, and the dimensions were 55 cm × Ø 10 cm. A UV lamp (15 W, 254 nm) was longitudinally fixed in the center of the reactor. The prepared tubular TiO2/Ni film was placed on a fixed support outside the UV lamp, resulting in a 2.5 cm gap. A microporous aerator was fixed below the reactor to maintain aerobic conditions inside the TiO2/Ni tube. Gas bubbled up from the bottom and accelerated around the liquid. The liquid inside the TiO2/Ni tube flowed in two directions: (i) some liquid gradually flowed out through the tube pores, and (ii) the others flowed up to the top of the tube. Consequently, the liquid outside the tube flowed down from the top; (iii) due to the different internal and external flow rates, resulting in water circulation in the photocatalytic reactor. This process benefited the enhancement of the contacting probability between the water contaminant and the P25 TiO2 on the surface of porous Ni. The experimental temperature of the entire photoreactor was controlled by a surrounding external water-cooling jacket.
Ijerph 09 00548 g001 1024
Figure 1. Schematic diagram (a) and cross section (b) of the tubular photocatalytic reactor.
Figure 1. Schematic diagram (a) and cross section (b) of the tubular photocatalytic reactor.
Ijerph 09 00548 g001

2.4. Procedure and Analysis

In the photocatalytic process, 3.5 L of aqueous quinoline solution was poured into the reactor. The UV lamp was switched on to start the photo-oxidation process. Compressed gas was bubbled upward through the gas distributor at the bottom of the reactor. At pre-defined irradiation times, 50 μL of solution was collected and immediately analyzed to avoid further reaction. The dependences of the quinoline degradation rate on initial concentration, light intensity, reaction temperature, aeration, and pH were investigated. Each experiment was conducted three times under identical conditions. The data presented in the text and figures are the mean values. The light absorption characteristics of the solutions were recorded using Persee T6 UV/visible spectrophotometer at a distance of 100 cm from the light source per the manufacturer’s instructions [16]. The concentration of quinoline was analyzed using a high-performance liquid chromatography system (LC-20A). The chromatographic column was a Shim-pack VP-ODS-C18 (4.6 mm × 150 mm, 5 μm). The mobile phase was a mixture of methanol and water (60:40, v/v) with a flow rate of 1 mL/min. The testing wavelength was 275 nm.
To obtain the intermediate products of quinoline degradation, the experiment was performed in a photocatalytic reactor with 100 mg/L quinoline under ambient conditions. After 30 min of irradiation time, 200 mL of the effluent was collected in a separating funnel, and then extracted for qualitative analysis by gas chromatography (GC)/mass spectroscopy (MS). The effluent for the GC/MS sample was further assayed by the method of Li et al. [17], except that 30 mL of anhydrous ether was used as the extractant. The extracts were decanted into a rotary evaporator, and then dried at 35 °C to evaporate the ether. The residue was dissolved in 10 mL of anhydrous ether for the GC/MS analysis.
GC/MS analysis was performed on an Agilent GC system (6890N/MSD 5973) equipped with an HP-5MS fused silica capillary column (30 m × 0.25 mm i.d., 0.25 μm film thickness). The column was first heated to 80 °C, kept constant for 3 min, linearly programmed to increase to a final temperature of 300 °C at a rate of 10 °C/min, and then isothermally held for 2 min. The temperature for the MS ion source was 200 °C, and the electron energy was 70 eV.

3. Results and Discussion

3.1. TiO2/Ni Film Characterizations

The FESEM images of porous Ni and the TiO2/Ni film are shown in Figure 2. The surface of bare porous Ni without immobilized P25 was smooth (Figure 2a). After P25 TiO2 coating, the originally smooth surface of the coated TiO2/Ni film (Figure 2b) became relatively rough and had a number of microcracks. Then, the specific surface area increased remarkably from 0.25 m2/g to 8.5 m2/g. Consequently, a high photocatalytic efficiency was obtained because there were more interfaces between the catalyst and reactants.
Ijerph 09 00548 g002 1024
Figure 2. FESEM images of porous nickel substrate (a) and the TiO2/Ni film (b).
Figure 2. FESEM images of porous nickel substrate (a) and the TiO2/Ni film (b).
Ijerph 09 00548 g002
Figure 3 shows the XRD patterns of P25 TiO2 powder, TiO2/Ni film, and porous Ni. Three strong diffraction peaks found at 2θ = 44.5°, 51.8°, and 76.1° were ascribed to the (111), (200), and (220) planes of Ni (ICDD PDF Card 87-0712) (JCPDS. 2001), respectively, in accordance with earlier studies [18,19].
Ijerph 09 00548 g003 1024
Figure 3. XRD pattern of Degussa P25 TiO2 (a), the TiO2/Ni film (b) and the bare nickel substrate (c). A and R denotes the anatase and rutile crystal phases, respectively.
Figure 3. XRD pattern of Degussa P25 TiO2 (a), the TiO2/Ni film (b) and the bare nickel substrate (c). A and R denotes the anatase and rutile crystal phases, respectively.
Ijerph 09 00548 g003
Two diffraction peaks at 2θ = 37.2° and 68.3° were attributed to rutile phase (ICDD PDF Card 21-1276) [20]. The presence of other crystallographic plains labeled with “A” belongs to the anatase phase (ICDD PDF Card 21-1272) [20]. P25 TiO2 coated on porous Ni caused no apparent change in the half width of the anatase (101) XRD peak, regardless of the heating treatment, and the crystallite size was calculated to be 21 nm from the anatase (101) peak width using the Scherrer equation. This result indicated that nano-sized TiO2 particles in P25 sol have been reproduced onto the surface of porous Ni. Therefore, the TiO2/Ni film possessed good photocatalytic activity.

3.2. Photodegradation of Quinoline in the Photocatalytic Reactor

To analyze the degradation process of quinoline, a UV absorption experiment was performed on the reactants, as described in the Materials and Methods Section. With increased illumination time, a series of UV absorption spectra was recorded within the 180–380 nm range, as shown in Figure 4a. The characteristic absorption of quinoline significantly decreased with increased irradiation time, and almost disappeared at 60 min. The UV254 of the reaction solution initially increased and then gradually decreased. The peak appeared at 15 min (Figure 4b). This finding indicated that the aromatic or pyridine ring of quinoline opened in the initial stage, and formed a series of intermediate products containing conjugated double bond. As a result, UV254 absorbance was enhanced. UV absorbance within the range 180–240 nm also gradually decreased with prolonged irradiation time. This result indicated the further mineralization of aliphatic saturated as well as cyclic hydrocarbons and their derivatives in solution [21]. Interestingly, UV absorbance above 320 nm initially increased, reached the peak at 45 min, and then apparently decreased. These findings were in accordance with the color of the reaction solution changing from transparent to pale yellow, to yellow-green, and then back to transparent.
Ijerph 09 00548 g004 1024
Figure 4. Absorbance curves (a) and UV254 (b) of aqueous quinoline solution. Conditions: C0 = 40 mg/L, T = 290 K, flow rate = 0.35 L/min, pH = 6.7, and the maximum irradiation intensity.
Figure 4. Absorbance curves (a) and UV254 (b) of aqueous quinoline solution. Conditions: C0 = 40 mg/L, T = 290 K, flow rate = 0.35 L/min, pH = 6.7, and the maximum irradiation intensity.
Ijerph 09 00548 g004

3.2.1. Effect of the Initial Quinoline Concentration

The effect of the initial quinoline concentration on the degradation efficiency was investigated within the range 10–120 mg/L, as shown in Figure 5. An initial aqueous quinoline concentration of 10 mg/L can almost be completely removed after 60 min of irradiation. Increased quinoline concentrations from 10 mg/L to 120 mg/L resulted in the increase in irradiation time. Moreover, the total removal amount of quinoline also increased from 78.74 μmol to 818.78 μmol. This result suggested that increased initial concentration obviously decreased the degradation ratio, but resulted in a high total removal amount of quinoline. Generally, the formation of activated radicals (e.g., OH and O2−) on the TiO2 surface remains constant for a given light intensity, catalyst amount, air flow, and duration of irradiation. A higher quinoline concentration corresponded to a higher demand for activated radicals, resulting in prolonged reaction time for the complete decomposition. However, high initial concentrations may prompt the contact between the active radicals and quinoline molecules, thereby improving the total amount of quinoline removed.
Ijerph 09 00548 g005 1024
Figure 5. Effect of the initial quinoline concentration on the photocatalytic degradation. Conditions: T = 290 K, flow rate = 0.35 L/min, pH = 6.7, and the maximum irradiation intensity.
Figure 5. Effect of the initial quinoline concentration on the photocatalytic degradation. Conditions: T = 290 K, flow rate = 0.35 L/min, pH = 6.7, and the maximum irradiation intensity.
Ijerph 09 00548 g005

3.2.2. Effect of Light Intensity

A control signal processed by a digital PID regulator was used to control the input current and change the UV light output intensity. Figure 6a shows that under dark conditions, only about 5% of the quinoline was removed from synthetic water during the first 15 min, and remained constant for nearly 100 min regardless of air flow. This finding suggested that the main removal effect in the absence of UV irradiation is due to the adsorption on the TiO2 surface [22]. Interestingly, the oxidation and air stripping controlled by the gas aeration had little effect on quinoline photodegradation. However, UV irradiation benefited the removal efficiency of quinoline in water, and the degradation percent reached over 80% after 120 min of reaction at 152 μw/cm2 of light intensity. Increased light intensity also resulted in increased photodegradation efficiency. This finding may be due to the fact that the rate of electron-hole pair formation at the TiO2 surface increased with increased light intensity to improve the photocatalytic efficiency. Figure 6b shows an acceptably good linear correlation between the apparent first-order rate constant and light intensity. This tendency indicated that light intensity is an important control agent of photocatalytic reaction within the radiant flux range of 152 to 471 μW/cm2.
Ijerph 09 00548 g006 1024
Figure 6. Degradation percentage (a) and reaction rate (b) with respect to different radiant flux. Conditions: T = 290 K, flow rate = 0.35 L/min, pH = 6.7, and C0 = 40 mg/L.
Figure 6. Degradation percentage (a) and reaction rate (b) with respect to different radiant flux. Conditions: T = 290 K, flow rate = 0.35 L/min, pH = 6.7, and C0 = 40 mg/L.
Ijerph 09 00548 g006

3.2.3. Effect of Reaction Temperature

The dependence of the quinoline degradation rate on the reaction temperature within 4–40 °C was also determined. Figure 7 shows that compared with the degradation percent at 60 min, the degradation ratio rapidly increased within 4–30 °C, and then very gradually increased above 30 °C.
Warm temperatures enhance the collision frequency of molecules [23]. Hence, the movement of the reactant molecules continued to intensify and gradually reached a plateau. However, for TiO2 photocatalysis, electron-hole pair generation at ambient temperatures is mainly affected by light irradiation given that the band gap energy is too high to be overcome by thermal activation [24]. Therefore, the increase in percent quinoline degradation was most likely due to the enhanced collision frequency with the increased reaction temperature.
Ijerph 09 00548 g007 1024
Figure 7. Effect of temperature on the photocatalytic degradation of quinoline. Conditions: flow rate = 0.35 L/min, pH = 6.7, C0 = 40 mg/L, and the maximum irradiation intensity.
Figure 7. Effect of temperature on the photocatalytic degradation of quinoline. Conditions: flow rate = 0.35 L/min, pH = 6.7, C0 = 40 mg/L, and the maximum irradiation intensity.
Ijerph 09 00548 g007

3.2.4. Effect of Aeration

Molecular oxygen is generally used as an electron acceptor to capture photo-generated electrons and form an active radical (O2−). Therefore, quantum efficiencies may partly be increased by inhibiting electron-hole recombination to enhance the photocatalytic efficiency [25]. In the present study, compressed pure oxygen, pure nitrogen, and air were purged into the photocatalytic reactor to analyze the effect of dissolved oxygen on quinoline photodegradation. Figure 8 shows that the degradation percent of quinoline solution under pure oxygen aeration at the rate of 0.35 L/min reached 97% after continuous UV illumination for 60 min. This percentage was much higher than that under airflow or pure nitrogen aeration. Under pure nitrogen aeration, the percent quinoline degradation rapidly increased for the first 15 min, and then became constant with time. Therefore, molecular nitrogen clearly existed in air, and pure nitrogen aeration played a negative role in the photocatalytic reaction, playing a dual role. One was to reduce residual dissolved oxygen in water by continued stripping. The other was to relocate dissolved oxygen onto the TiO2 surface to inhibit the formation of active radicals, and retard the agitation effect to decrease the effective mass transfer for the photocatalytic process.
Ijerph 09 00548 g008 1024
Figure 8. Effect of air, pure nitrogen, and pure oxygen aeration on the photodegradation of quinoline. Conditions: flow rate = 0.35 L/min, pH = 6.7, T = 17 °C, C0 = 40 mg/L, and the maximum irradiation intensity.
Figure 8. Effect of air, pure nitrogen, and pure oxygen aeration on the photodegradation of quinoline. Conditions: flow rate = 0.35 L/min, pH = 6.7, T = 17 °C, C0 = 40 mg/L, and the maximum irradiation intensity.
Ijerph 09 00548 g008
The relationship between airflow and degradation efficiency was also investigated, as shown in Figure 9. Percent quinoline degradation increased with increased air flow rate to 1.0 L/min, which suggested that higher air aeration rate favors to increase dissolving oxygen in water and agitate the solution to speed up mass transfer.
However, compared with pure nitrogen aeration, percent quinoline degradation under no airflow was still up to 20% after irradiation for 120 min, a little above 5% of that under pure nitrogen aeration at a rate of 0.35 L/min, as illustrated in Figure 8, although a similar increased removal tendency presented in the initial stage because of the effect of residual dissolved oxygen. It’s proposed that molecular oxygen was recycled in a single photocatalytic system such that reoxygenation equilibrium existed between oxygen consumption and steady-state replenishment. The reoxygenation processes may have also proceeded at low levels under no airflow, but were inhibited by pure nitrogen stripping.
Ijerph 09 00548 g009 1024
Figure 9. Effect of air flow on the photocatalytic degradation of quinoline. Conditions: pH = 6.7, T = 17 °C, C0 = 40 mg/L, and the maximum irradiation intensity.
Figure 9. Effect of air flow on the photocatalytic degradation of quinoline. Conditions: pH = 6.7, T = 17 °C, C0 = 40 mg/L, and the maximum irradiation intensity.
Ijerph 09 00548 g009

3.2.5. Effect of pH

The pH value of a solution determines the surface charge of photocatalyts and the ionization or speciation (pKa) of an organic pollutant [26,27]. Hence, pH varies significantly and can play an important role in the photocatalytic degradation of organic contaminants [28]. The effect of pH on quinoline degradation was investigated, as shown in Figure 10a. The degradation rate significantly increased at pH below 4.1, and then gradually decreased with increased pH from 6.7 to 10.8. An alkaline medium appeared to retard quinoline degradation, with the degradation percent below 10% during the first 15 min. A combined pH change analysis Figure 10b) revealed that after UV irradiation for 30 min, the initial pH value of the solution shifted to the value of the point of zero charge (Pzc) of TiO2 (Deguessa P25), which is widely reported at pH 6.25 [29], i.e., the initial pH increased from 4.1 to 5.3. These observed behaviors can be explained in terms of the Pzc of TiO2 and the pKa (about pH 4.95) of quinoline [30]. At more alkaline pH values, the TiO2 surface is negatively charged. At pH values blow 6.25, the surface is positively charged [31].
Ijerph 09 00548 g010 1024
Figure 10. Effect of pH (a) on the photocatalytic degradation of quinoline and (b) after irradiation for 30 min. Conditions: flow rate = 0.35 L/min, T = 17 °C, C0 = 40 mg/L, and the maximum irradiation intensity. pH0 and pH30 represent the pH values of the aqueous solution after UV irradiation for 0 and 30 min, respectively.
Figure 10. Effect of pH (a) on the photocatalytic degradation of quinoline and (b) after irradiation for 30 min. Conditions: flow rate = 0.35 L/min, T = 17 °C, C0 = 40 mg/L, and the maximum irradiation intensity. pH0 and pH30 represent the pH values of the aqueous solution after UV irradiation for 0 and 30 min, respectively.
Ijerph 09 00548 g010
When the pH is above 6.25, the adsorption of quinoline molecules onto the TiO2 surface became difficult with increased pH due to the repellant effect of the two species with negative charges. However, within pH 4.95–6.25, the negatively charged quinoline molecules were easily adsorbed on the positively charged TiO2 surface. This phenomenon benefited the quinoline degradation. At pH values below the quinoline pKa value, the quinoline molecules are present in the protonated form (with a positive charge), which did not favor the absorption onto the TiO2 surface, which also had a positive charge. The protonated form appeared to enhance the UV absorbance of quinoline, which led to the improvement in its degradation under acidic conditions compared with alkaline medium [32]. Also, at low pH values, a number of sulfur anions were found when the pH of the water was adjusted. These anions strongly hindered the generation of active radicals via competitive adsorption with O2, H2O, and other molecules on the catalyst surface, resulting in decreased quinoline degradation in acidic medium. Therefore, the different pH values before and after the reaction for 30 min revealed that quinoline had a higher degradation rate at pH 4.95–6.25, whereas the degradation rate was moderately influenced by the solution pH.

3.2.6. Stability of the TiO2/Ni Film

The stability of the TiO2/Ni film in the fabricated reactor is one of the most important factors for its practical application. Therefore, a recycling experiment was carried out using the same TiO2/Ni film to investigate its stability. After each experiment, the TiO2/Ni film was washed with distilled water for 30 min under air aeration, dried at 105 °C for 60 min in an electric oven, and then reused under oneset of reaction conditions ([quinoline]0 = 40 mg/L, pH = 6.7, flow rate = 0.35 L/min, reaction temperature = 17 °C, and the maximum irradiation flux). An irradiation time of 60 min was selected for the recycling experiment due to the disappearance of the characteristic absorption of quinoline, as described in Figure 4. Figure 11 shows that the percent quinoline degradation remained constant during the first 16 runs of photocatalytic reaction, obviously decreased in subsequent runs, and then declined to 70% after 25 runs. This finding was in accordance with the TiO2/Ni film varying in color from white to pale yellow. However, complete reactivation occurred after the TiO2/Ni film was subjected to calcinations. This reactivation was due to the decomposition of the adsorbed reactants at a high temperature.
Ijerph 09 00548 g011 1024
Figure 11. Percent quinoline degradation of the TiO2/Ni film with consecutive runs under the conditions of T = 290 K, flow rate = 0.35L/min, pH = 6.7, C0 = 40mg/L, and the maximum irradiation flux. C denotes the re-calcinated TiO2/Ni film.
Figure 11. Percent quinoline degradation of the TiO2/Ni film with consecutive runs under the conditions of T = 290 K, flow rate = 0.35L/min, pH = 6.7, C0 = 40mg/L, and the maximum irradiation flux. C denotes the re-calcinated TiO2/Ni film.
Ijerph 09 00548 g011

3.3. Mechanism of Quinoline Degradation

The synthetic wastewater containing quinoline varied in color, as described in Section 3.2, indicating that there existed some intermediate products in the photocatalytic process. Based on the GC/MS analysis performed, the effluent of the synthetic wastewater after irradiation for 30 min contained 2-pyridinecarboxaldehyde, 3-pyridinecarboxaldehyde, quinoline, and 2(1H)-quinolinone. Figure 12 shows the possible mechanisms for the formation of the three intermediate products. The formation of the first two intermediates may have depended on the electrophilic substitution between quinoline and hydroxyl radicals. The initial oxidation mainly occurred at positions 5 and 8 of the aromatic ring, resulting in the formation of 5,8-quinolinedione. Further oxidation by active radicals resulted in the formation of 2-pyridinecarboxaldehyde or 3-pyridinecarboxaldehyde based on the phenyl ring opening process via quinoline-5,8-dione. This mechanism was in accordance with that reported by Thomsen [33] and Zhu et al. [34]. Considering that the electron cloud density of the pyridine ring is lower than that of an aromatic ring, the pyridine ring is relatively difficult to be oxidized. Hence, the formation of 2(1H)-quinolinone is related to the superoxide ion (O2−) generated by dissolved oxygen on the TiO2 surface trapped electron under UV irradiation. Ishibashi et al. [35] have reported that the superoxide ion (O2−) is generated at the water-TiO2 interface with a longer lifetime of about 70 s. Its absolute number pre-illuminated is calculated to be 2 × 1014/cm2, and it has a low mobility [36]. During the adsorption of quinoline onto the TiO2 surface, the initial addition reaction between quinoline and the superoxide ion (O2−) may take place at the C-2 position of the pyridine ring, similar with an ordinary nucleophile [34,37]. This phenomenon benefited the further reaction with active radicals to generate 2(1H)-quinolinone.
Ijerph 09 00548 g012 1024
Figure 12. Proposed pathways for the photocatalytic degradation of quinoline.
Figure 12. Proposed pathways for the photocatalytic degradation of quinoline.
Ijerph 09 00548 g012

4. Conclusions

A newly developed tubular photocatalytic reactor equipped with a TiO2/Ni film was used for the photodegradation of an aqueous quinoline solution under different operational conditions. The results showed that percent quinoline removal increased with increased light intensity and air aeration. A lower photocatalytic degradation rate was shown under pure nitrogen aeration than under pure oxygen, air, or without any aeration. Percent quinoline removal decreased with increased total quinoline amount removal from 10 to 104.4 mg/L when the initial quinoline concentration was increased from 10 to 120 mg/L. The reaction temperature and pH should be at 30 °C and below 6.25, respectively, to obtain a high removal efficiency of quinoline from synthetic wastewater. The major intermediates of quinoline degradation were identified as 2-pyridinecarboxaldehyde, 3-pyridinecarboxaldehyde, and 2(1H)-quinolinone. A primary degradation mechanism was proposed based on these intermediates. The new internal airlift loop tubular photocatalytic reactor based on a TiO2/Ni film was proven to be very effective for quinoline removal from synthetic wastewater. The use of this reactor could hopefully be extended to treat other types of industrial wastewater.

Acknowledgements

The present research was sponsored by the Nature Science Foundation of China (50778036, 51108069 and 51008056), the PhD. Programs Foundation of the Ministry of Education of China (20100043110009), and the Social Development Foundation of Jilin Province (20060405, 20086035 and 201101002).

References

  1. Seo, J.S.; Keum, Y.S.; Li, Q.X. bacterial degradation of aromatic compounds. Int. J. Environ. Res. Public Health 2009, 6, 278–309. [Google Scholar]
  2. Tao, X.Q.; Lu, G.N.; Liu, J.P.; Li, T.; Yang, L.N. Rapid Degradation of Phenanthrene by Using Sphingomonas sp. GY2B Immobilized in Calcium Alginate Gel Beads. Int. J. Environ. Res. Public Health 2009, 6, 2470–2480. [Google Scholar] [CrossRef]
  3. Kochany, J.; Maguire, R.J. Photodegradation of quinoline in water. Chemosphere 1994, 28, 1097–1110. [Google Scholar]
  4. Alexei, N.; John, K. Parameters affecting the homogeneous and heterogeneous degradation of quinoline solutions in light-activated processes. J. Photoch. Photobio. A 1997, 110, 149–157. [Google Scholar]
  5. Rockafellow, E.M.; Stewart, L.K.; Jenks, W.S. Is sulfur-doped TiO2 an effective visible light photocatalyst for remediation? Appl. Catal. B-Environ. 2009, 91, 554–562. [Google Scholar] [CrossRef]
  6. Stewart, L.K. Tungsten Trioxide and Titanium Dioxide Photocatalytic Degradations of Quinoline. 2009. [Google Scholar]
  7. Pichat, P. Photocatalytic degradation of aromatic and alicyclic pollutants in water: by-products, pathways and mechanisms. Water. Sci. Technol. 1997, 35, 73–78. [Google Scholar]
  8. Kim, S.B.; Jang, H.T.; Hong, S.C. Photodegradation of gas-phase methanol and toluene using thin-film TiO2 photocatalyst. 1. Influence of water vapor, molecular oxygen and temperature. J. Ind. Eng. Chem. 2002, 8, 156–161. [Google Scholar]
  9. Xu, X.; Ji, F.Y.; Fan, Z.H.; He, L. Degradation of Glyphosate in Soil Photocatalyzed by Fe3O4/SiO2/TiO2 under Solar Light. Int. J. Environ. Res. Public Health 2011, 8, 1258–1270. [Google Scholar]
  10. Rodriguez, P.; Meille, V.; Pallier, S.; Al Sawah, M.A. Deposition and characterisation of TiO2 coatings on various supports for structured (photo)catalytic reactors. Appl. Catal. A-Gen. 2009, 360, 154–162. [Google Scholar] [CrossRef]
  11. Yang, L.P.; Liu, Z.Y.; Shi, J.W.; Hu, H.; Shangguan, W.F. Design consideration of photocatalytic oxidation reactors using TiO2-coated foam nickels for degrading indoor gaseous formaldehyde. Catal. Today 2007, 126, 359–368. [Google Scholar]
  12. Zhu, S.Y.; Yang, X.; Wang, G.N.; Zhang, L.L.; Zhu, H.F.; Huo, M.X. Facile Preparation of P25 Films Dip-Coated Nickel Foam and High Photocatalytic Activity for the Degradation of Quinoline and Industrial Wastewater. Int. J. Chem. React. Eng. 2011, 9, A37. [Google Scholar]
  13. Taranto, J.; Frochot, D.; Pichat, P. Photocatalytic Treatment of Air: Comparison of Various TiO2, Coating Methods, and Supports Using Methanol or n-Octane as Test Pollutant. Ind. Eng. Chem. Res. 2009, 48, 6229–6236. [Google Scholar]
  14. Olivier, R.; Muthukonda, V.S.; Maithaa, K.D.; Loïc, S.; Nicolas, K.; Valérie, K. Solar light photocatalytic hydrogen production from water over Pt and Au/TiO2 (anatase/rutile) photocatalysts: Influence of noble metal and porogen promotion. J. Catal. 2010, 269, 179–190. [Google Scholar]
  15. Plantard, G.; Correia, F.; Goetz, V. Kinetic and efficiency of TiO2-coated on foam or tissue and TiO2-suspension in a photocatalytic reactor applied to the degradation of the 2,4-dichlorophenol. J. Photoch. Photobio. 2011, 222, 111–116. [Google Scholar]
  16. Barakat, M.A. Adsorption and photodegradation of procion yellow H-EXL dye in textile wastewater over TiO2 suspension. J. Hydro-Environ. Res. 2011, 5, 137–142. [Google Scholar] [CrossRef]
  17. Li, Y.M.; Gu, G.W.; Zhao, J.F.; Yu, H.Q.; Qiu, Y.L.; Peng, Y.Z. Treatment of coke-plant wastewater by biofilm systems for removal of organic compounds and nitrogen. Chemosphere 2003, 52, 997–1005. [Google Scholar]
  18. Zhang, Y.H.; Yang, Y.N.; Xiao, P.; Zhang, X.N.; Lu, L.; Li, L. Preparation of Ni nanoparticle-TiO2 nanotube composite by pulse electrodeposition. Mater Lett. 2009, 63, 2429–2431. [Google Scholar]
  19. Bidault, F.; Brett, D.J.L.; Middleton, P.H.; Abson, N.; Brandon, N.P. A new application for nickel foam in alkaline fuel cells. Int. J. Hydrogen. Energ. 2009, 34, 6799–6808. [Google Scholar]
  20. JCPDS PDF-2 Release 2001; ICDD: Newtown Square, PA, USA, 2001.
  21. Kulovaara, M.; Corin, N.; Backlund, P.; Tervo, J. Impact of UV254-radiation on aquatic humic substances. Chemosphere 1996, 33, 783–790. [Google Scholar]
  22. Bouanimba, N.; Zouaghi, R.; Laid, N.; Sehili, T. Factors influencing the photocatalytic decolorization of Bromophenol blue in aqueous solution with different types of TiO2 asphotocatalysts. Desalination 2011, 275, 224–230. [Google Scholar]
  23. Qian, Ch.X.; Zhao, L.F.; Fu, D.F.; Li, L.; Wang, R.X. Study on the effect of temperature, humidity and light intensity on photocatalytic oxidation of NO2 by Nano-TiO2 immobilized on cement-based materials. J. Environ. Sci. China 2005, 25, 623–630. [Google Scholar]
  24. Chen, D.W.; Ray, A.K. Photodegradation kinetics of 4-nitrophenol in TiO2 suspension. Water Res. 1998, 32, 3223–3234. [Google Scholar]
  25. Chung, H.H.; MariÑas, B.J. Role of Chlorine and Oxygen in the Photocatalytic Degradation of Trichloroethylene Vapor on TiO2 Films. Environ. Sci. Technol. 1997, 31, 562–568. [Google Scholar]
  26. Singh, H.K.; Saquib, M.; Haque, M.M.; Muneer, M. Heterogeneous photocatalyzed degradation of uracil and 5-bromouracil in aqueous suspensions of titanium dioxide. J. Hazard. Mater. 2007, 142, 425–430. [Google Scholar]
  27. Singh, H.K.; Saquib, M.; Haque, M.M.; Muneer, M. Heterogeneous photocatalysed decolorization of two selected dye derivatives neutral red and toluidine blue in aqueous suspensions. Chem. Eng. J. 2008, 136, 77–81. [Google Scholar]
  28. Lu, M.C.; Roam, G.D.; Chen, J.N.; Huang, C.P. Factors affecting the photocatalytic degradation of dichlorvos over titanium dioxide supported on glass. J. Photochem. Photobiol. A. 1993, 76, 103–110. [Google Scholar]
  29. Renault, N.J.; Pichat, P.; Foissy, A.; Mercier, R. Study of the effect of deposited Pt particles on the surface charge of TiO2 aqueous suspensions by potentiometry, electrophoresis and labeled ion adsorption. J. Phys. Chem. 1986, 90, 2733–2738. [Google Scholar]
  30. Wang, S.L.; Zheng, Z.; Li, M. Pulse radiolysis mechanism study of quinoline in dilute solutions. J. Radiat. Res. Proc. China 2004, 22, 334–338. [Google Scholar]
  31. Chen, D.W.; Ray, A.K. Photodegradation kinetics of 4-nitrophenol in TiO2 suspension. Water Res. 1998, 32, 3223–3234. [Google Scholar]
  32. Lapertot, M.; Pichat, P.; Parra, S.; Guillard, C.; Pulgarin, C. Photocatalytic degradation of p-halophenols in TiO2 aqueous suspensions: halogen effect on removal rate, aromatic intermediates and toxicity variations. J. Environ. Sci. Health A 2006, 41, 1009–1025. [Google Scholar]
  33. Thomsen, A.B. Degradation of quinoline by wet oxidation kinetic aspects and reaction mechanisms. Water Res. 1998, 32, 136–146. [Google Scholar]
  34. Zhu, D.Z.; Sun, D.M.; Jiang, Z.L.; Wang, S.L.; Sun, X.Y.; Ni, Y.M. Studies on the Respective Reactions of Quinoline and Isoquinoline with Transient Species by Pulse Radiolysis. Acta Phys. Chim. Sin. 2008, 24, 2321–2326. [Google Scholar]
  35. Ishibashi, K.I.; Fujishima, A.; Watanabe, T.; Hashimoto, K. Generation and Deactivation Processes of Superoxide Formed on TiO2 Film Illuminated by Very Weak UV Light in Air or Water. J. Phys. Chem. B 2000, 104, 4934–4938. [Google Scholar]
  36. Ishibashi, K.I.; Nosaka, Y.; Hashimoto, K.; Fujishima, A. Time-Dependent Behavior of Active Oxygen Species Formed on Photoirradiated TiO2 Films in air. J. Phys. Chem. B 1998, 102, 2117–2120. [Google Scholar]
  37. Wang, S.L.; Zhu, D.Z.; Sun, X.Y.; Shi, J.; Ni, Y.M.; Wang, W.F.; Yao, S.D. Spectral Analysis of Transient Species of Quinoline Degradation. Spectrosc. Spect. Anal. 2006, 26, 1479–1482. [Google Scholar]

Share and Cite

MDPI and ACS Style

Zhu, S.; Yang, X.; Yang, W.; Zhang, L.; Wang, J.; Huo, M. Application of Porous Nickel-Coated TiO2 for the Photocatalytic Degradation of Aqueous Quinoline in an Internal Airlift Loop Reactor. Int. J. Environ. Res. Public Health 2012, 9, 548-563. https://doi.org/10.3390/ijerph9020548

AMA Style

Zhu S, Yang X, Yang W, Zhang L, Wang J, Huo M. Application of Porous Nickel-Coated TiO2 for the Photocatalytic Degradation of Aqueous Quinoline in an Internal Airlift Loop Reactor. International Journal of Environmental Research and Public Health. 2012; 9(2):548-563. https://doi.org/10.3390/ijerph9020548

Chicago/Turabian Style

Zhu, Suiyi, Xia Yang, Wu Yang, Leilei Zhang, Jian Wang, and Mingxin Huo. 2012. "Application of Porous Nickel-Coated TiO2 for the Photocatalytic Degradation of Aqueous Quinoline in an Internal Airlift Loop Reactor" International Journal of Environmental Research and Public Health 9, no. 2: 548-563. https://doi.org/10.3390/ijerph9020548

APA Style

Zhu, S., Yang, X., Yang, W., Zhang, L., Wang, J., & Huo, M. (2012). Application of Porous Nickel-Coated TiO2 for the Photocatalytic Degradation of Aqueous Quinoline in an Internal Airlift Loop Reactor. International Journal of Environmental Research and Public Health, 9(2), 548-563. https://doi.org/10.3390/ijerph9020548