Next Article in Journal
Spatio-Temporal Dynamic Characteristics and Landscape Connectivity of Heat Islands in Xiamen in the Face of Rapid Urbanization
Next Article in Special Issue
Adsorption Equilibrium of CO2 on Microporous Activated Carbon Produced from Avocado Stone Using H2SO4 as an Activating Agent
Previous Article in Journal
Effect of Adding Hexagonal Boron Nitride (hBN) Nano-Powder to Lubricant on Performance and Emissions in a Two-Stroke Gasoline Engine
Previous Article in Special Issue
The Application of Clinoptilolite as the Green Catalyst in the Solvent-Free Oxidation of α-Pinene with Oxygen
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Sustainability
Volume 15
Issue 19
10.3390/su151914606
sustainability-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Synthesis and Basic Properties of Y1−xYbxVO4 Obtained by High-Energy Ball Milling and High-Temperature Treatment

by
Mateusz Piz
1,*,
Elżbieta Filipek
1,
Daniel Klukowski
2 and
Paweł Kochmański
3
1
Department of Inorganic and Analytical Chemistry, Faculty of Chemical Technology and Engineering, West Pomeranian University of Technology in Szczecin, al. Piastów 42, 71-065 Szczecin, Poland
2
Department of Geoinformatics, Faculty of Navigation, Maritime University of Szczecin, Wały Chrobrego 1-2, 70-500 Szczecin, Poland
3
Faculty of Mechanical Engineering and Mechatronics, West Pomeranian University of Technology in Szczecin, al. Piastów 19, 70-310 Szczecin, Poland
*
Author to whom correspondence should be addressed.
Sustainability 2023, 15(19), 14606; https://doi.org/10.3390/su151914606
Submission received: 28 July 2023 / Revised: 19 September 2023 / Accepted: 28 September 2023 / Published: 9 October 2023
(This article belongs to the Special Issue Material Characterization and Heterogeneous Catalysis)
Browse Figures
Versions Notes

Abstract

:
The main objective of this work was to experimentally confirm that a continuous, substitutional solid solution of a general formula Y1−xYbxVO4 is formed in the pseudo-binary system YVO4–YbVO4, and to investigate its basic unknown properties as a function of composition for 0.00 < x < 1.00. To date, such a solid solution has been obtained and characterized to a limited extent, but only for a few selected compositions. This solution was obtained by a high temperature and, for the first time, using mechanochemical methods. For the solution obtained by the high-energy ball-milling method, unknown physicochemical properties were established over its entire range of homogeneity. The solution was synthesized from mixtures of yttrium orthovanadate (V) with ytterbium (III) orthovanadate (V) of different compositions and investigated by XRD, IR, SEM, and UV-Vis(DRS) methods. It was found that Y1−xYbxVO4 crystallizes in a tetragonal system. The results confirmed that the solid solution Y1−xYbxVO4 has a structure of YVO4 and YbVO4, and its structure is composed of YbO6 and YO6 octahedrons and VO4 tetrahedrons. Moreover, if the parameter (x) in the solid solution Y1−xYbxVO4 increases, its crystalline lattice contracts and the value of the energy gap decreases. This solid solution is stable in the air atmosphere at least up to ~1500 °C. The estimated band gap for this solid solution indicates that it belongs to the semiconductors.

1. Introduction

In recent decades, comprehensive and intensive research has been conducted, encompassing both theoretical and experimental approaches. The findings from these studies have led to the development of technologies producing new functional materials with the expected catalytic, magnetic, mechanical, electrical, or optical properties. Such new materials, undoubtedly competing with those used so far, should be characterized by improved desired properties, simultaneously with low-cost, waste-free, pro-ecological, and easily available manufacturing. Therefore, the dopant modification of the already existing material is a common method used for a new material development.
The mechanochemical method meets most of the requirements of “green chemistry”, as it does not generate harmful waste for disposal and is environmentally friendly. Its main advantage is simplicity, since the method is based on milling various types of substances in a high-energy mill. The mechanical energy generated during grinding is delivered to the substrates and accumulates in them in the form of all kinds of lattice stresses and defects, which can increase their reactivity. The process of high-energy grinding can lead to very fine grinding of the product, often down to nanoparticles. High-energy ball milling has been successfully used to synthesize many new functional materials, such as alloys, intermetallic compounds, polymers, and ceramic materials [1,2,3,4].
Among the diverse objects whose research is directed at the search for new functional materials, a significant group is bicomponent, ternary, and even quaternary systems of metal oxides. The choice of a given system for research is very often determined by the application-requiring modification of the properties of its components, i.e., oxides, as well as known compounds formed in binary systems that are lateral constraints of multicomponent systems. An example of a binary system constituting one cross-section of a ternary system of V2O5–Yb2O3–Y2O3 oxides is the YVO4–YbVO4 system [5,6,7,8,9,10,11,12,13,14,15,16,17,18,19,20,21,22,23,24,25,26,27,28,29,30]. Yttrium orthovanadate(V) and ytterbium are well characterized in the literature [27,28,29,30,31,32,33,34,35,36,37,38,39,40,41,42,43,44,45,46]. Methods for their syntheses are known, ranging from the solid-state reaction method to hydrothermal, Pechini, or co-precipitation [5,6,9,15,16,17,27,34,41]. It is also known that YVO4 and YbVO4 crystallize in a tetragonal system [7,11,30,31,32,35]. Depending on studies, the congruent melting temperature of YVO4 varies from 1780 to 1810 °C, while YbVO4 melts at ~1820 °C [18,19].
Literature data on yttrium orthovanadate(V) indicate that this compound doped with Ce3+, Eu3+, Dy3+, Sm3+, or Er3+ ion results in materials able to be applied in high-resolution devices, such as cathode ray tubes (CRT), flat panel displays, and field emission displays (FED) [20,36,37,39,42,43,44,45,46]. Data on the properties of YVO4 also point out that the compound is a useful matrix for the listed rare earth ions, making it possible to produce phosphors that emit light of different colors [20,21,33,42]. Yttrium orthovanadate(V) activated with Eu3+ ions is an important red phosphor used in color television, cathode ray tubes, and high-pressure mercury lamps. On the other hand, YVO4 activated with Dy3+ ions is a potential component of white phosphors and Nd3+ ions of blue ones [20,33,37].
Ytterbium orthovanadate(V), like yttrium orthovanadate(V), is an important optical material. Doping YVO4 with ytterbium ions and using it as a host material is a promising solution in the prospect of developing a low-threshold and high-performance solid-state erbium laser [12,20,38,40,41]. It is also possible to dope orthovanadium(V) ytterbium with other rare earth ions, such as neodymium, to produce lasers with a wavelength of 1.35 μm. YbVO4 crystals doped with neodymium can produce red, green, or blue light with high efficiency and beam quality [13,20]. The phases obtained in the work are most often with general formulas YVO4:Yb3+ and Yb:YVO4. The methods for obtaining such phases do not differ significantly from those for the synthesis of pure yttrium and ytterbium orthovanadates(V) [5,6,16,17,28,38]. The doping of YVO4 with Yb3+ ions using ytterbium orthovanadate(V) is rare, and if so, it is in a limited range of YbVO4 concentrations, namely in the range of 0.4 to 25% molar of orthovanadate(V) in a mixture with YVO4 [22,23,24,25]. In summary, to our knowledge and based on the performed literature review, comprehensive studies of the reactivity of yttrium orthovanadate(V) with ytterbium orthovanadate(V) over the entire concentration range of the components of the system comprising these compounds—i.e., in the YVO4–YbVO4 system—have not yet been carried out.
The published works [22,23,24,25] show that only a few samples from the mentioned system have been tested so far, including those containing no more than 25.00 mol% of Yb3+ ions in the YVO4 crystal lattice, corresponding to the Y1−xYbxVO4 solid solution for 0.004 < x < 0.25. Importantly, the study, mostly focused on monocrystalline samples, primarily examined their optical properties.
Taking into account the fact that the components of the YVO4–YbVO4 system are isostructural, and that the Y3+ and Yb3+ ions present in their structures have similar values of ionic radii (Yb3+—86.8 pm, Y3+—90.0 pm), the primary objective of our work was to experimentally demonstrate that a continuous substitutional solid solution with the general formula Y1−xYbxVO4 is formed in the YVO4–YbVO4 system. As the sustainability of solid solution Y1−xYbxVO4 is not known, the DTA-TGA measurements in the air atmosphere and in the temperature range 25–1500 °C were performed. In this range, no thermal effects were observed on DTA and TG curves. The results prove that the obtained phase is stable in an air atmosphere at least up to ~1500 °C. Considering the fact that for the first time the mechanochemical method was used to obtain the solid solution, an additional objective was to study the effect of the degree of incorporation of Yb3+ (x) ions into the YVO4 crystal lattice on the physicochemical properties of the Y1−xYbxVO4 solution, i.e., lattice parameters, density, particle size distribution, or energy gap value, etc. The results presented in this work have significantly advanced the knowledge of the solid solution formed in the YVO4–YbVO4 system. It was shown that the Y1−xYbxVO4 solid solution forms over the entire concentration range of the components of the studied system, i.e., for 0.00 < x < 1.00, and not only for 0.004 < x < 0.25. For the first time, such a nanometric solution was obtained mechanochemically. The unknown properties of the solution obtained both by high-temperature and mechanochemical methods were examined as a function of its composition.

2. Materials and Methods

The reagents used in our experiments are YVO4 and YbVO4, which were synthesized from the oxides Y2O3, a.p. (Alfa Aesar, Memphis, TN, USA), Yb2O3, a.p. (Alfa Aesar, Memphis, TN, USA), and V2O5, a.p. (POCh, Poland) by the mechanochemical and high-temperature methods described in refs. [1,22,23,24,30,31,32]. For the experiments, 10 samples were prepared from separately obtained YVO4 and YbVO4 (Table 1) by using two different methods:
(a) Mechanochemical synthesis (MECh) using laboratory planetary ball mill Pulverisette-6 (Fritsch GmbH, Idar-Oberstein, Germany) with vessel and balls of zirconia, rpm = 500, BPR = 1:20, time = 3.0 and once again 3.0 hrs under air atmosphere.
(b) High-temperature treatment (HTH) in a horizontal tube furnace PRC 50/170/M (Czylok, Jastrzębie-Zdrój, Poland) equipped with a stationary optical pyrometer MARATHON MM (Raytek, Wilmington, North Carolina, USA). Reagents weighed in suitable proportions were homogenized and calcined in the air atmosphere in the temperature range 1000–1500 °C. After each heating stage, the samples were gradually cooled in the furnace to room temperature by the method described, e.g., in [47,48,49,50].
The powder diffraction patterns of the samples obtained were recorded on a diffractometer EMPYREAN II (PANalytical, Almelo, The Netherlands) using CuKα with a graphite monochromator (2θ range 7–45°); time of counting 71.40 s, step 0.013.
The phases were identified on the basis of XRD characteristics contained in the PDF cards (Powder Diffraction File4+).
The parameters of selected unit cell solid solutions were refined using the REFINEMENT program of the DHN/PDS package.
Selected samples were examined using the following methods:
–
SEM using an FE-SEM Hitachi SU–70 microscope. Analyses were performed at an accelerating voltage of 5 and 15 kV and secondary electron images were acquired. (Thermo Fisher Scientific); the blowup of the SEM images was 20.000 and 100.000.
–
IR—the measurements were made within the wavenumber range of 1200–400 cm−1, using a spectrophotometer Nicolet iS5 (ThermoFisher, Memphis, TN, USA). The technique of pressing pellets with KBr at the mass ratio of 1:300 was applied.
–
LDS using Mastersizer 3000 (Malvern Panalytical, Malvern, UK), He-Ne laser (λ = 632.8 nm), LED (λ = 470.0 nm),
–
UV-Vis-DR spectra were measured using a UV-Vis spectrometer V-670 (JASCO, Japan) equipped with a reflecting attachment for the solid-state investigation (integrating sphere attachment with horizontal sample platform PIV-756/(PIN-757). The spectra were recorded in the wavelength region of 200–750 nm at room temperature.
The densities of solid solutions were determined in argon (5N purity) with the help of an Ultrapyc 1200e ultrapycnometer (Quantachrome Instruments, Boynton Beach, FL, USA).
The crystallite sizes of the solid solution were determined by using the Scherrer method according to the equation: L = Kλ/β∙Cosθ. The size of the nanocrystallites (L) was calculated using XRD radiation of the wavelength of λ (nm) from measuring the full width at half maximum of the peaks (β) in radians located at any 2θ in the pattern.

3. Results and Discussion

3.1. Mechanochemical Synthesis

The study of the YVO4–YbVO4 system began with the preparation of five mixtures of YVO4 with YbVO4 with the compositions shown in Table 1. The compositions of these samples were chosen to represent different ranges of concentrations of the components of the system under study.
Mixtures of isostructural vanadates, i.e., yttrium and ytterbium, were subjected to mechanochemical synthesis carried out in a high-energy planetary ball mill under an air atmosphere in two 3 h stages. An X-ray phase analysis of all samples proved a change in the initial composition after the first milling stage. The individual diffraction lines recorded on the diffractograms of these samples, corresponded to the interplane distances dhkl, whose values ranged from those identifying YVO4 (PDF-card number: 04-007-6542), to those corresponding to YbVO4 (PDF-cards number: 04-019-7298 and 04-008-3642). An analysis of the diffractograms of these samples therefore indicated that they were single phase and contained only a substitutional solid solution of YVO4 or YbVO4 structure. A subsequent 3 h milling step did not change the phase composition of all samples.
Based on the results obtained, it was found that a solid solution was obtained by the high-energy milling of mixtures of YVO4 with YbVO4 over the entire concentration range of the components of the system under study. Thus, it is a continuous substitution solid solution, the general formula of which can be written either as Y1−xYbxVO4(s.s.) or as Yb1−yYyVO4(s.s.). For the solution so obtained, in the further description of the results, it was assumed that the matrix of the continuous, substituted solid solution is the compound YVO4.
Table 1 shows the compositions of the tested samples prepared from mixtures of YVO4 with YbVO4, before and after the last stage of their synthesis.
Following, the solution is formed by incorporating Yb3+ ions into the YVO4 crystal lattice in place of Y3+ ions, according to the reaction:
(1 − x) YVO4 (s) + x YbVO4 (s) = Y1−xYbxVO4(s.s.)
Figure 1 presents fragments of the diffractograms of mechanochemically obtained compounds YVO4 (Figure 1a) and YbVO4 (Figure 1e), compared with fragments of the diffractograms of the Y1−xYbxVO4 solid solution obtained by the method for the first time for x = 0.10 (Figure 1b), x = 0.50 (Figure 1c), and x = 0.90 (Figure 1d).
The analysis of the diffractograms (XRD) of single-phase samples (Figure 1), i.e., those containing Y1−xYbxVO4(s.s.) solid solution, showed that since the content of YbVO4 increases in the initial mixtures of reactants, i.e., the value of x in the obtained solution, the XRD lines characterizing this phase are shifted toward higher angles 2Θ. This means that they correspond to smaller values of interplane distances dhkl relative to the X-ray characteristics of YbVO4.
This can be explained by the size of the radius of the Yb3+ ion in octahedral coordination, which equals 86.8 pm, which is smaller than the radius of the Y3+ ion, i.e., 90.0 pm. During the synthesis, a substitution of these ions takes place, leading to the contraction of the crystal lattice. These results are additional evidence for the formation of a substitutive continuous solid solution.
The extended diffraction lines in the diffractograms of the Y1−xYbxVO4 solid solution obtained for the first time by the mechanochemical method (Figure 2) indicate that the crystallites of the obtained phase are small in size. The crystallite sizes of mechanochemically synthesized Y1−xYbxVO4 determined using Scherrer’s method are ~17 nm (x = 0.10), ~19 nm (x = 0.25), ~18 nm (x = 0.50), ~18 nm (x = 0.75), and ~15 nm (x = 0.90).
The aim of the next stage of the study was to confirm that the Y1−xYbxVO4 solid solution synthesized for the first time by the mechanochemical method shows the crystalline structure of YVO4 and YbVO4, i.e., a tetragonal system. For this purpose, powder diffractograms of the obtained Y1−xYbxVO4 solution for x = 0.10, 0.25, 0.50, 0.75, and 0.90 were subjected to refinement using the REFINEMENT program. The results confirmed that the obtained solid solution crystallizes in a tetragonal system, and its lattice parameters were calculated as a function of the degree of incorporation of Yb3+ ions in place of Y3+ into the YVO4 crystal lattice. Table 2 shows the calculated elementary cell parameters of their volumes and densities: X-ray and experimental for the synthesized solid solution.
As can be seen from the data shown in Table 2, with an increase in the x value in the Y1−xYbxVO4 formula, manifesting a higher incorporation degree of Yb3+ ions and lower of the Y3+, the crystal lattice contracts and the volume of elementary cells decreases. Moreover, the density of the solid solution, determined using the gas ultrapycnometer, increases with an increase in the x value, which corresponds well with the calculated X-ray density. Close values obtained from two separate techniques substantiate the correctness of the selected solutions. Somewhat lower values of the experimental density are most likely a result of the measurement error originating, e.g., from the porosity and defects of the obtained material.
In a next step, both ytterbium orthovanadate(V) (Figure 3a) and yttrium (Figure 3b), as well as the Y1−xYbxVO4 solid solution for x = 0.50 (Figure 3c), were subjected to scanning electron microscopy (SEM) studies. Images of the obtained polycrystalline samples are shown in Figure 3.
Visible in Figure 3, the crystallites of the Y1−xYbxVO4 solid solution for x = 0.50 are very similar to the crystallites of the substrates, i.e., YbVO4 and YVO4, in terms of their shape. In their appearance, they resemble irregular, very fine, “disordered” polyhedrons of varying sizes with the size of a significant part of them not exceeding 100 nm (Figure 3c).
The particle size distribution of the solid solution Y1−xYbxVO4, obtained by the mechanochemical method, was determined using the LDS method (Figure 4).
Based on the LDS analysis (Figure 4, Table 3), the particle sizes of the Y1−xYbxVO4 solid solution were determined to be nanometer-sized, i.e., ~100 nm (including 10% of ~29 nm for x = 0.10), ~440 nm (including 10% of ~102 nm for x = 0.25), ~58 nm (including 10% of ~22 nm for x = 0.50), ~55 nm (including 10% of ~21 nm for x = 0.75), and ~75 nm (including 10% of ~21 nm for x = 0.90). According to the LDS curve, the Y1−xYbxVO4 solid solution was found to have bimodal distribution, that is, it does not have a homogeneous distribution. It is known that when a material is milled using high-energy ball milling technique, the milled material can be reduced to the nanosize and may have an inhomogeneous distribution [51,52].
Next, it was determined which oxygen polyhedrons of yttrium and ytterbium comprise the structure of the mechanochemically obtained solution Y1−xYbxVO4. For this purpose, selected single-phase samples of the solution were studied by using infrared spectroscopy (IR). In addition to the IR spectra of the compounds YVO4 (Figure 5a) and YbVO4 (Figure 5e), the IR spectra of the obtained solid solution Y1−xYbxVO4 for x = 0.10, 0.50, and 0.90 are also shown in the figure (Figure 5b–d, respectively).
In the IR spectra of the studied phases (in 400 to 1200 cm−1 wavenumber range), a broad absorption band (maxima of bands at 822–835 cm−1) with an inflection on the side of lower wavenumbers (maxima of bands at 735–750 cm−1) is present. Additionally, two very low intensity bands are also registered with maxima at around ~450 and 475 cm−1, respectively. The broad band at ~830 cm−1, according to literature data [14], is caused by stretching vibrations (ν) of V-O bonds in VO4 tetrahedra. However, it cannot be ruled out that the recorded band with an inflection at ~750 cm−1 is also related to stretching vibrations of Y-O or Yb-O bonds in YO6 or YbO6 octahedra [53,54,55]. In contrast, the bands at ~450 and 475 cm−1 are, according to the literature, associated with bending (deformation) vibrations (δ) of the O-Y-O and/or O-Yb-O bonds [55,56]. An analysis of the recorded spectra made it possible to conclude that the absorption bands of the individual phases studied do not differ significantly, which proves that the phases are isostructural with respect to each other. The maxima of the absorption bands with an increase in the concentration of Yb3+ ions in the crystal lattice of the obtained Y1−xYbxVO4 solid solution only slightly shift towards lower values of the wave numbers. Thus, the results of IR tests are additional confirmation that a continuous substitutional solid solution of Y1−xYbxVO4 with a YVO4 or YbVO4 structure is formed in the YVO4–YbVO4 system. The structure of this solution is built from interconnected corners and/or edges of VO4 tetrahedra and Y(Yb)O6 octahedra.
The next study in this work, to which the synthesized phases YVO4 (Figure 6a), YbVO4 (Figure 6e), and the solid solution Y1−xYbxVO4 for x = 0.10, 0.50, 0.90 (Figure 6b–d) were subjected, was the UV-Vis-DRS. The UV-Vis-DR reflectance spectra recorded for the samples as a function of radiation energy were subjected to the Kubelka–Munk transformation to estimate their energy gap value.
The value of the energy gap for the studied phases was determined from the intersection of the tangent drawn to the rectilinear part of the graph K2 = f(E) with the abscissa axis, i.e., the energy, as shown in Figure 6.
The determined values of the energy gap (Eg) for YVO4 and YbVO4 are ~3.52 eV and ~3.21 eV, while the value of the energy gap for the solid solution decreases with increasing x, i.e., from Eg = ~3.50 eV for Y0.90Yb0.10VO4 to ~3.32 eV for Y0.10Yb0.90VO4 [41].
Based on the results obtained, it was concluded that the Y1−xYbxVO4 solid solution belongs to the group of wide energy gap semiconductors.

3.2. High-Temperature Treatment

In addition to the mechanochemically synthesized solutions obtained from the YVO4–YbVO4 system, five samples of the solution (with identical compositions as in the first part of this work, Table 1) were prepared using the classical method of high-temperature solid-state reactions. Adequately, the substrates for the preparation of the mixtures, i.e., YVO4 and YbVO4, were also obtained by using the high-temperature method [3,5,6]. Mixtures of YVO4 with YbVO4 (Table 1) after homogenization were heated in the following steps: I—1000 °C (12 h) → II—1200 °C (12 h) → III—1400 °C (12 h) → IV—1500 °C (12 h) (Figure 7).
The heating conditions of the samples were chosen so that the reactions occurring in the mixtures would proceed in a solid state, i.e., the substrates would not undergo both melting and consolidation. It is safe to choose these temperatures so that they do not exceed both the temperature of any eutectic forming between the substrates and the Tamman temperature. Figure 7 presents fragments of diffractograms of an equimolar mixture of YVO4 + YbVO4 (Figure 7a) before heating compared with fragments of diffractograms of the Y1−xYbxVO4 solid solution for x = 0.50 (Figure 7b) after heating at a temperature of 1500 °C (12 h).
The XRD phase analysis showed that all the samples investigated changed their phase composition after the fourth stage of their heating. Based on the XRD phase analysis of samples 1–5 after this stage of their heating, i.e., at 1500 °C for 12 h, they were found to be monophasic and to contain only the Y1−xYbxVO4 solid solution (Figure 7b and Figure 8).
The fact that only the Y1−xYbxVO4 solid solution was present in the samples was evidenced by the lines registered on their diffractograms, which corresponded to interplane distances falling within the range of values characteristic of analogous lines in the XRD set of pure YVO4 and YbVO4. Both the position of the diffraction lines and their respective intensities were consistent with the results presented in the papers [5,6,35,38,41].
On the basis of the results obtained, it was confirmed that by the method of high-temperature reactions occurring in the solid state in an air atmosphere, a solid solution with the general formula Y1−xYbxVO4 was obtained over the entire range of concentrations of the components of the studied system.
Figure 8 presents fragments of the diffractograms of the high-temperature treatment obtained, compounds YVO4 (Figure 8a) and YbVO4 (Figure 8e), compared with fragments of the diffractograms of the Y1−xYbxVO4 solid solution for x = 0.10 (Figure 8b), x = 0.50 (Figure 8c), and x = 0.90 (Figure 8d).
Further experiments were aimed at confirming that the Y1−xYbxVO4 solid solution obtained by the high-temperature treatment method crystallizes in a tetragonal system. For this purpose, powder diffractograms of the Y1−xYbxVO4 solution for x = 0.10, 0.25, 0.50, 0.75, and 0.90 were subjected to refinement (REFINEMENT program). Based on the results obtained, it was confirmed that the solid solution obtained by this method also crystallizes in a tetragonal system, and the parameters of its elementary cells were determined. Table 4 presents the calculated parameters of the elementary cells of their volumes and X-ray and experimental densities for the synthesized solid solution.
The obtained results (Table 4) indicate that with an increasing value of x in Y1−xYbxVO4, i.e., with an increasing degree of the incorporation of Yb3+ ions in place of Y3+—similar to this solid solution obtained by the mechanochemical method—there is a contraction of the crystal lattice, i.e., the volume of elementary cells decreases. An analysis of these data in comparison with analogous ones for the mechanochemical method indicates, moreover, that the volume of elementary cells for the solution obtained by the high-temperature method is always smaller. It is this volume, among other things, that influences the higher values of density, both X-ray and experimental. These presented differences are due to the lower degree of structure defection and porosity of the solution obtained at high temperatures (from 1000–1500 °C).
Scanning electron microscopy (SEM) studies of the compounds YVO4 and YbVO4, as well as the solid solution Y1−xYbxVO4 for x = 0.50 (Figure 9) obtained by the high-temperature treatment method, allowed us to conclude that the crystallites of the solid solution Y0.5Yb0.5VO4 are very similar to those of the matrices, i.e., YVO4 and YbVO4, in terms of shape.
From the SEM images shown in Figure 9, with 10,000 zoom, it can be seen that the size of the solution crystallites differs from that of the substrates. Although the sizes are more diverse, some are larger, averaging 8µm. Moreover, these crystallites, as expected, are significantly larger than the crystallites of the solid solution obtained mechanochemically.
Using the LDS method, the particle size distribution of the Y1−xYbxVO4 solid solution obtained by the high-temperature treatment method was determined (Figure 10).
The particle sizes of the Y1−xYbxVO4 solid solution obtained by the high-temperature treatment method, unlike those of the solution obtained by the mechanochemical method, have micrometer sizes, i.e., of ~0.61 µm for x = 0.10, ~0.64 µm for x = 0.25, ~0.31 µm for x = 0.50, ~0.36 µm for x = 0.75, and ~0.33 µm for x = 0.90. In addition, based on the LDS curves, the particle size distribution of the Y1−xYbxVO4 solution obtained by the HT method was found to be inhomogeneous (Figure 10).
In order to initially confirm that the Y1−xYbxVO4 solution synthesized by the second method exhibits the YVO4 structure, IR investigations were carried out. In addition to the IR spectra of the YVO4 (Figure 11a) and YbVO4 (Figure 11e) compounds, the IR spectra of the obtained Y1−xYbxVO4 solid solution for x = 0.10, 0.50, 0.90 (Figure 11b–d) are also shown in Figure 11.
In the IR spectra of the studied phases obtained by the high-temperature treatment method in the wavelength number range from 400 to 1200 cm−1, two narrow absorption bands were registered (Figure 11), which are located in the same wavelength number ranges as the absorption bands registered on the IR spectra of the phases obtained by the high-energy ball milling method (Figure 5). The difference is that the bands for the HT method are much narrower and more formed. Based on the literature [53,54,55], these bands can be attributed to both the stretching vibrations of V-O bonds in VO4 tetrahedra, and the stretching vibrations of Y-O or Yb-O bonds in YO6 or YbO6 octahedra. At the same time, it was found that as the degree of the incorporation of Yb3+ ions in place of Y3+ into the YVO4 crystal lattice increased, the recorded absorption bands of the solid solution (Figure 11b–d) shifted slightly towards lower wave number values. The results of this part of the work also confirmed that the Y1−xYbxVO4 solid solution obtained by the high-temperature treatment method exhibits a YVO4 structure and is composed of VO4 tetrahedra and Y(Yb)O6 octahedra.
Phases obtained by high-temperature treatment (HT): YVO4 (Figure 12a), YbVO4 (Figure 12e) and the solid solution Y1−xYbxVO4 for x = 0.10, 0.50, 0.90 (Figure 12b–d) in the last stage of the work were subjected to UV-Vis-DRS to estimate their energy gap values.
The determined values of the energy gap (Eg) for YVO4 and YbVO4 are, respectively, ~3.66 eV and ~3.55 eV, while the value of the energy gap for the solid solution decreases with increasing x, i.e., from Eg = ~3.62 eV for Y0.90Yb0.10VO4 to ~3.57 eV for Y0.10Yb0.90VO4 [41]. It was additionally determined that the energy gap values for the Y1−xYbxVO4 solution obtained by high-temperature treatment are slightly higher than the gap values for this solution obtained by high-energy ball milling. These differences are undoubtedly influenced by the size of the crystallites (the larger the crystallites, the higher the Eg value). Based on the results, it was concluded that the Y1−xYbxVO4 solid solution obtained by both methods belongs to the group of semiconductors with a wide energy gap.
The obtained solid solution may find potential application not only as a photocatalyst, but also, for example, as a component of optoelectronic materials.

4. Conclusions

The results of the conducted research allowed us to achieve the main goal of the work, i.e., to experimentally confirm that a continuous substitution solid solution of the general formula Y1−xYbxVO4, where 0.00 < x < 1.00, is formed in the YVO4–YbVO4 system.
The solution was obtained from mixtures YVO4 with YbVO4 by the high-temperature method, as well as by the high-energy ball milling method, which was used for the first time for the presented purpose.
The solid solution obtained mechanochemically is nanocrystalline, while the high-temperature treatment one is microcrystalline. With the increase of x in Y1−xYbxVO4 obtained by both methods, the crystal lattice of the solid solution contracted. Based on the LDS curves, the particle size distribution of the Y1−xYbxVO4 solution obtained by the two methods was found to be inhomogeneous. The structure of the solid solution obtained by both alternative synthesis methods consists of connected VO4 tetrahedra with Y(Yb)O6 octahedra. The energy gap values for the Y1−xYbxVO4 solution obtained by the high-temperature treatment method are slightly higher than the gap values for this solution obtained by the high-energy ball milling method. Regardless of the method of synthesis, Y1−xYbxVO4 solid solutions belong to the group of wide energy gap semiconductors.
Differences in the physicochemical properties of the solution depending on the method of its synthesis are primarily due to differences in the size of their crystallites.

Author Contributions

Conceptualization, M.P. and E.F.; methodology, M.P. and E.F.; validation, M.P., E.F. and D.K.; formal analysis, M.P. and E.F.; investigation, M.P., E.F., D.K. and P.K.; data curation, M.P. and D.K.; writing—original draft preparation, M.P.; writing—review and editing, E.F.; visualization, M.P.; supervision, E.F. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Baláž, P.; Achimovicová, M.; Baláž, M.; Billik, P.; Zara, C.Z.; Criado, J.M.; Delogu, F.; Dutková, E.; Gaffet, E.; Gotor, F.J.; et al. Hallmarks of Mechanochemistry: From Nanoparticles to Technology. Chem. Soc. Rev. 2013, 42, 7571–7637. [Google Scholar] [CrossRef]
  2. Kutuk, S. Influence of Milling Parameters on Particle Size of Ulexite Material. Powder Technol. 2016, 301, 421–428. [Google Scholar] [CrossRef]
  3. Piz, M.; Dulian, P.; Filipek, E.; Wieczorek-Ciurowa, K.; Kochmanski, P. Characterization of Phases in the V2O5–Yb2O3 System Obtained by High-Energy Ball Milling and High-Temperature Treatment. J. Mater. Sci. 2018, 53, 13491–13500. [Google Scholar] [CrossRef]
  4. Dulian, P.; Bąk, W.; Piz, M.; Garbarz-Glos, B.; Sachuk, O.V.; Wieczorek-Ciurowa, K.; Lisińska-Czekaj, A.; Czekaj, D. Mg2+ Doping Effects on the Structural and Dielectric Properties of CaCu3Ti4O12 Ceramics Obtained by Mechanochemical Synthesis. Materials 2021, 14, 1187. [Google Scholar] [CrossRef]
  5. Levin, E.M. The System Y2O3-V2O5. J. Am. Ceram. Soc. 1978, 50, 381–382. [Google Scholar] [CrossRef]
  6. Brusset, H.; Madaule-Aubry, F.; Blanck, B.; Glaziou, J.P.; Laude, J.P. Etude Des Oxydes Mixtes de Lanthanides et de Vanadium(V). Can. J. Chem. 1971, 49, 3700–3707. [Google Scholar] [CrossRef]
  7. Yu, Y.; Cheng, Y.; Zhang, H.; Wang, J.; Cheng, X.; Xia, H. Growth and Thermal Properties of YbVO4 Single Crystal. Mater. Lett. 2006, 60, 1014–1018. [Google Scholar] [CrossRef]
  8. Eghbali-Arani, M.; Sobhani-Nasab, A.; Rahimi-Nasrabadi, M.; Ahmadi, F.; Pourmasoud, S. Ultrasound-Assisted Synthesis of YbVO4 Nanostructure and YbVO4/CuWO4 Nanocomposites for Enhanced Photocatalytic Degradation of Organic Dyes under Visible Light. Ultrason. Sonochem. 2018, 43, 120–135. [Google Scholar] [CrossRef]
  9. Gao, Y.; Fan, M.; Fang, Q.; Han, W. Controllable Synthesis, Morphology Evolution and Luminescence Properties of YbVO4 Microcrystals. New J. Chem. 2013, 37, 670–678. [Google Scholar] [CrossRef]
  10. Fuess, H.; Kallel, A.; Neutronique, D.; Cedex, C.E.N.G.; Temp, K. Refinement of the Crystal Structure of Some Rare Earth Vanadates RVO4 (R = Dy, Tb, Ho, Yb). J. Solid State Chem. 1972, 14, 11–14. [Google Scholar] [CrossRef]
  11. Baglio, J.A.; Sovers, O.J. Crystal Structures of the Rare-Earth Orthovanadates. J. Solid State Chem. 1971, 3, 458–465. [Google Scholar] [CrossRef]
  12. Cheng, Y.; Zhang, H.; Zhang, K.; Xin, Z.; Yang, X.; Xu, X.; Gao, W.; Li, D.; Zhao, C.; Xu, J. Growth and Spectroscopic Characteristics of Er3+:YbVO4 Crystal. J. Cryst. Growth 2009, 311, 3963–3968. [Google Scholar] [CrossRef]
  13. Liu, F.Q.; Sun, S.Q.; Gao, C.Y.; Xu, J.Q. Optical Properties of Nd:YbVO4 Crystal. Opt. Appl. 2015, 45, 63–70. [Google Scholar] [CrossRef]
  14. Miura, B.A.; Ferreira, N.H.; Oliveira, P.F.; De Faria, E.H.; Tavares, D.C.; Rocha, L.A.; Ciuffi, K.J.; Nassar, E.J. Functionalization of Luminescent YVO4:Eu3+ Nanoparticles by Sol-Gel. J. Lumin. 2015, 159, 93–99. [Google Scholar] [CrossRef]
  15. He, F.; Yang, P.; Niu, N.; Wang, W.; Gai, S.; Wang, D.; Lin, J. Hydrothermal Synthesis and Luminescent Properties of YVO4:Ln3+ (Ln = Eu, Dy, and Sm) Microspheres. J. Colloid Interface Sci. 2010, 343, 71–78. [Google Scholar] [CrossRef]
  16. Li, G.; Chao, K.; Peng, H.; Chen, K. Hydrothermal Synthesis and Characterization of YVO4 and YVO4:Eu3+ Nanobelts and Polyhedral Micron Crystals. J. Phys. Chem. C 2008, 112, 6228–6231. [Google Scholar] [CrossRef]
  17. Erdei, S.; Ainger, F.W.; Cross, L.E.; White, W.B. Hydrolyzed Colloid Reaction (HCR) Technique for Preparation of YVO4, YPO4, YVxP1−xO4. Mater. Lett. 1994, 21, 143–147. [Google Scholar] [CrossRef]
  18. LeBret, J.B.; Norton, M.G.; Bahr, D.F. Examination of Crystal Defects with High-KV X-Ray Computed Tomography. Mater. Lett. 2005, 59, 1113–1116. [Google Scholar] [CrossRef]
  19. Lebret, J.B.; Norton, M.G.; Bahr, D.F.; Field, D.P.; Lynn, K.G. Characterization of Low Angle Grain Boundaries in Yttrium Orthovanadate. J. Mater. Sci. 2005, 40, 3347–3353. [Google Scholar] [CrossRef]
  20. Yu, M.; Lin, J.; Wang, Z.; Fu, J.; Wang, S.; Zhang, H.J.; Han, Y.C. Fabrication, Patterning, and Optical Properties of Nanocrystalline YVO4:A (A = Eu3+, Dy3+, Sm3+, Er3+) Phosphor Films via Sol-Gel Soft Lithography. Chem. Mater. 2002, 14, 2224–2231. [Google Scholar] [CrossRef]
  21. Cheng, Z.; Xing, R.; Hou, Z.; Huang, S.; Lin, J. Patterning of Light-Emitting YVO4:Eu3+ Thin Films via Inkjet Printing. J. Phys. Chem. C 2010, 114, 9883–9888. [Google Scholar] [CrossRef]
  22. Chen, J.; Guo, F.; Zhuang, N.; Lan, J.; Hu, X.; Gao, S. A Study on the Growth of Yb:YVO4 Single Crystal. J. Cryst. Growth 2002, 243, 450–455. [Google Scholar] [CrossRef]
  23. Zhong, D.; Teng, B.; Li, J.; Zhang, S.; Zhang, B.; Wang, C.; Tian, X.; Liu, J. Growth and Laser Action of Yb: YVO4 Crystals with Low Yb Doping Concentration. J. Cryst. Growth 2012, 358, 16–19. [Google Scholar] [CrossRef]
  24. Voron’ko, Y.K.; Kochurikhin, V.V.; Sobol’, A.A.; Ushakov, S.N.; Shukshin, V.E. Growth and Spectroscopic Study of Yb3+-Activated YVO4 Crystals. Inorg. Mater. 2004, 40, 1083–1087. [Google Scholar] [CrossRef]
  25. Klassen, A.V.; Matsukura, M.; Nakamura, O.; Kochurikhin, V.V.; Ivanov, M.A.; Orlova, G.Y.; Miyamoto, A.; Furukawa, Y. Edge-Defined Film-Fed Growth of Yb:YVO4 Single Crystal Plates. J. Cryst. Growth 2008, 310, 2895–2898. [Google Scholar] [CrossRef]
  26. Zhang, Q.; Saito, F. A Review on Mechanochemical Syntheses of Functional Materials. Adv. Powder Technol. 2012, 23, 523–531. [Google Scholar] [CrossRef]
  27. Au, C.T.; Zhang, W.D.; Wan, H.L. Preparation and Characterization of Rare Earth Orthovanadates for Propane Oxidative Dehydrogenation. Catal. Lett. 1996, 37, 241–246. [Google Scholar] [CrossRef]
  28. Tojo, T.; Zhang, Q.; Saito, F. Mechanochemical Synthesis of Rare Earth Orthovanadates from R2O3 (R = Rare Earth Elements) and V2O5 Powders. J. Alloys Compd. 2007, 427, 219–222. [Google Scholar] [CrossRef]
  29. Erdei, S. Preparation of YVO4 Powder from the Y2O3 + V2O5 + H2O System by a Hydrolysed Colloid Reaction (HCR) Technique. J. Mater. Sci. 1995, 30, 4950–4959. [Google Scholar] [CrossRef]
  30. Wang, X.; Loa, I.; Syassen, K.; Hanfland, M.; Ferrand, B. Structural Properties of the Zircon- and Scheelite-Type Phases of YVO4 at High Pressure. Phys. Rev. B Condens. Matter 2004, 70, 3–8. [Google Scholar] [CrossRef]
  31. Souad, M.; Mohammed, S.; Mohamed, D.; Claude, D. The Effect of Pressure on the Structural and Electronic Properties of Yttrium Orthovanadate YVO4 Compound: Total-Energy Calculations. Z. FürKrist. Cryst. Mater. 2010, 225, 514–519. [Google Scholar] [CrossRef]
  32. Chakoumakos, B.C.; Abraham, M.M.; Boatner, L.A. Crystal Structure Refinements of Zircon-Type MVO4 (M = Sc, Y, Ce, Pr, Nd, Tb, Ho, Er, Tm, Yb, Lu). J. Solid State Chem. 1994, 109, 197–202. [Google Scholar] [CrossRef]
  33. Wiglusz, R.J.; Marciniak, L.; Pazik, R.; Strek, W. Structural and Spectroscopic Characterization of Nd3+-Doped YVO4 Yttrium Orthovanadate Nanocrystallites. Cryst. Growth Des. 2014, 14, 5512–5520. [Google Scholar] [CrossRef]
  34. Reitz, C.; Smarsly, B.; Brezesinski, T. General Synthesis of Ordered Mesoporous Rare-Earth Orthovanadate Thin Films and Their Use as Photocatalysts and Phosphors for Lighting Applications. ACS Appl. Nano Mater. 2019, 2, 1063–1071. [Google Scholar] [CrossRef]
  35. Errandonea, D.; Garg, A.B. Recent Progress on the Characterization of the High-Pressure Behaviour of AVO4 Orthovanadates. Prog. Mater. Sci. 2018, 97, 123–169. [Google Scholar] [CrossRef]
  36. Kolesnikov, I.E.; Golyeva, E.V.; Kurochkin, M.A.; Kolesnikov, E.Y.; Lähderanta, E. Concentration Series of Sm3+-Doped YVO4 Nanoparticles: Structural, Luminescence and Thermal Properties. J. Lumin. 2020, 219, 116946. [Google Scholar] [CrossRef]
  37. Getz, M.N.; Nilsen, O.; Hansen, P.A. Sensors for Optical Thermometry Based on Luminescence from Layered YVO4: Ln3+ (Ln = Nd, Sm, Eu, Dy, Ho, Er, Tm, Yb) Thin Films Made by Atomic Layer Deposition. Sci. Rep. 2019, 9, 1–11. [Google Scholar] [CrossRef]
  38. Dai, Y.; Chen, J.; Tang, Y.; Xiang, H.; Li, J.; Fang, L. Relationship between Bond Characteristics and Microwave Dielectric Properties of REVO4 (RE = Yb, Ho) Ceramics. Ceram. Int. 2023, 49, 875–881. [Google Scholar] [CrossRef]
  39. Wang, S.; Wang, P.; Ruan, Y.; Wang, Y.; Zhang, S. Photoluminescence Characteristics and Energy Transfer Phenomena in Ce3+-Doped YVO4 single Crystal. Sci. Eng. Compos. Mater. 2021, 28, 205–214. [Google Scholar] [CrossRef]
  40. Zhao, B.; Ye, Y.; Chen, J.; Lin, H.; Zhang, G.; Mateos, X.; Serres, J.M.; Aguiló, M.; Díaz, F.; Loiko, P.; et al. Growth, Spectroscopy, and Laser Operation of “Mixed” Vanadate Crystals Yb:Lu1−x-YYxLayVO4. Opt. Mater. Express 2018, 8, 493. [Google Scholar] [CrossRef]
  41. Vadivel, S.; Paul, B.; Kumaravel, M.; Hariganesh, S.; Rajendran, S.; Prasanga Gayanath Mantilaka, M.M.M.G.; Mamba, G.; Puviarasu, P. Facile Synthesis of YbVO4, and YVO4 Nanostructures through MOF Route for Photocatalytic Applications. Inorg. Chem. Commun. 2020, 115, 107855. [Google Scholar] [CrossRef]
  42. Ćirić, A.; Stojadinović, S.; Dramićanin, M.D. Time-Integrated Luminescence Thermometry of Eu3+ and Dy3+ Doped YVO4. Sens. Actuators A Phys. 2019, 295, 450–455. [Google Scholar] [CrossRef]
  43. Wang, Y.; Song, X.X.; Tang, W.J.; Jia, C.L. Multi-Wavelength Emission from Er-Implanted YbVO4 Crystal. Phys. Solid State 2020, 62, 1067–1073. [Google Scholar] [CrossRef]
  44. Kolesnikov, I.E.; Mamonova, D.V.; Kurochkin, M.A.; Kolesnikov, E.Y.; Lähderanta, E. Optical Thermometry by Monitoring Dual Emissions from YVO4 and Eu3+ in YVO4:Eu3+ Nanoparticles. ACS Appl. Nano Mater. 2021, 4, 1959–1966. [Google Scholar] [CrossRef]
  45. Pourmasoud, S.; Sobhani-Nasab, A.; Behpour, M.; Rahimi-Nasrabadi, M.; Ahmadi, F. Investigation of Optical Properties and the Photocatalytic Activity of Synthesized YbYO4 Nanoparticles and YbVO4/NiWO4 Nanocomposites by Polymeric Capping Agents. J. Mol. Struct. 2018, 1157, 607–615. [Google Scholar] [CrossRef]
  46. Rivera-Enríquez, C.E.; Fernández-Osorio, A.L. Synthesis of YVO4:Eu3+ Nanophosphors by the Chemical Coprecipitation Method at Room Temperature. J. Lumin. 2021, 236, 118110. [Google Scholar] [CrossRef]
  47. Blonska-Tabero, A.; Bosacka, M.; Filipek, E.; Piz, M.; Kochmanski, P. High-Temperature Synthesis and Unknown Properties of M3Cr4(PO4)6, Where M = Zn or Mg and a New Solid Solution Zn1.5Mg1.5Cr4(PO4)6. J. Therm. Anal. Calorim. 2020, 140, 2625–2631. [Google Scholar] [CrossRef]
  48. Filipek, E.; Paczesna, A.; Piz, M. Sr2InV3O11—New Ceramic Compound in Sr2V2O7–InVO4 System and Its Characteristic. Ceram. Int. 2016, 42, 14148–14154. [Google Scholar] [CrossRef]
  49. Piz, M.; Filipek, E. Synthesis and Homogeneity Range of Yb8−xYxV2O17 in the Yb8V2O17–Y8V2O17 System. J. Therm. Anal. Calorim. 2017, 130, 277–283. [Google Scholar] [CrossRef]
  50. Dąbrowska, G.; Filipek, E.; Tabero, P. New Solid Solution and Phase Equilibria in the Subsolidus Area of the Three-Component CuO–V2O5–Ta2O5 Oxide System. Materials 2022, 15, 232. [Google Scholar] [CrossRef]
  51. Kutuk-Sert, T. Stability Analyses of Submicron-Boron Mineral Prepared by Mechanical Milling Process in Concrete Roads. Constr. Build. Mater. 2016, 121, 255–264. [Google Scholar] [CrossRef]
  52. Kutuk-Sert, T.; Ozturk, M.; Kutuk, S. Digital Image Processing of Warm Mix Asphalt Enriched with Nanocolemanite and Nanoulexite Minerals. Constr. Build. Mater. 2023, 399, 132542. [Google Scholar] [CrossRef]
  53. Vucinic-Vasic, M.; Kremenovic, A.; Nikolic, A.S.; Colomban, P.; Mazzerolles, L.; Kahlenberg, V.; Antic, B. Core and Shell Structure of Ytterbium Sesquioxide Nanoparticles. J. Alloys Compd. 2010, 502, 107–111. [Google Scholar] [CrossRef]
  54. Garg, A.B.; Rao, R.; Sakuntala, T.; Wani, B.N.; Vijayakumar, V. Phase Stability of YbVO4 under Pressure: In Situ x-Ray and Raman Spectroscopic Investigations. J. Appl. Phys. 2009, 106, 063513. [Google Scholar] [CrossRef]
  55. Vasundhara, K.; Achary, S.N.; Patwe, S.J.; Sahu, A.K.; Manoj, N.; Tyagi, A.K. Structural and Oxide Ion Conductivity Studies on Yb1−xBixO1.5 (0.00 ≤ x ≤ 0.50) Composites. J. Alloys Compd. 2014, 596, 151–157. [Google Scholar] [CrossRef]
  56. Heiba, Z.K.; Akin, Y.; Sigmund, W.; Hascicek, Y.S. X-ray Structure and Microstructure Determination of the Mixed Sesquioxides (Eu1−xYbx)2O3 Prepared by a Sol-Gel Process. J. Appl. Crystallogr. 2003, 36, 1411–1416. [Google Scholar] [CrossRef]
Sustainability 15 14606 g001
Figure 1. Fragments of diffractograms: (a) YVO4 (◆ PDF-card no: 04-007-6542), (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4, (d) Y0.10Yb0.90VO4, (e) YbVO4 (■ PDF-cards no: 04-019-7298 and 04-008-3642).
Figure 1. Fragments of diffractograms: (a) YVO4 (◆ PDF-card no: 04-007-6542), (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4, (d) Y0.10Yb0.90VO4, (e) YbVO4 (■ PDF-cards no: 04-019-7298 and 04-008-3642).
Sustainability 15 14606 g001
Sustainability 15 14606 g002
Figure 2. Y1−xYbxVO4 obtained in a ball mill.
Figure 2. Y1−xYbxVO4 obtained in a ball mill.
Sustainability 15 14606 g002
Sustainability 15 14606 g003
Figure 3. SEM images of (a) YbVO4, (b) YVO4, (c) Y0.50Yb0.50VO4.
Figure 3. SEM images of (a) YbVO4, (b) YVO4, (c) Y0.50Yb0.50VO4.
Sustainability 15 14606 g003
Sustainability 15 14606 g004
Figure 4. Particle size distribution curve of: (a) Y0.90Yb0.10VO4, (b) Y0.75Yb0.25VO4, (c) Y0.50Yb0.50VO4, (d) Y0.25Yb0.75VO4, (e) Y0.10Yb0.90VO4.
Figure 4. Particle size distribution curve of: (a) Y0.90Yb0.10VO4, (b) Y0.75Yb0.25VO4, (c) Y0.50Yb0.50VO4, (d) Y0.25Yb0.75VO4, (e) Y0.10Yb0.90VO4.
Sustainability 15 14606 g004
Sustainability 15 14606 g005
Figure 5. IR spectrum of: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4 (d) Y0.10Yb0.90VO4, (e) YbVO4.
Figure 5. IR spectrum of: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4 (d) Y0.10Yb0.90VO4, (e) YbVO4.
Sustainability 15 14606 g005
Sustainability 15 14606 g006
Figure 6. The relationship (αhν)2 as a function of the photon energy hν with the determined value of the energy gap Eg for: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4, (d) Y0.10Yb0.90VO4, (e) YbVO4.
Figure 6. The relationship (αhν)2 as a function of the photon energy hν with the determined value of the energy gap Eg for: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4, (d) Y0.10Yb0.90VO4, (e) YbVO4.
Sustainability 15 14606 g006
Sustainability 15 14606 g007
Figure 7. Fragments of diffractograms: (a) YbVO4 (◆) + YVO4 (•), (b) Y0.50Yb0.50VO4 (■).
Figure 7. Fragments of diffractograms: (a) YbVO4 (◆) + YVO4 (•), (b) Y0.50Yb0.50VO4 (■).
Sustainability 15 14606 g007
Sustainability 15 14606 g008
Figure 8. Fragments of diffractograms: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4, (d) Y0.10Yb0.90VO4, (e) YbVO4.
Figure 8. Fragments of diffractograms: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4, (d) Y0.10Yb0.90VO4, (e) YbVO4.
Sustainability 15 14606 g008
Sustainability 15 14606 g009
Figure 9. SEM images of (a) YbVO4, (b) YVO4, (c) Y0.50Yb0.50VO4 obtained by high-temperature treatment.
Figure 9. SEM images of (a) YbVO4, (b) YVO4, (c) Y0.50Yb0.50VO4 obtained by high-temperature treatment.
Sustainability 15 14606 g009
Sustainability 15 14606 g010
Figure 10. Particle size distribution curve of: (a) Y0.90Yb0.10VO4, (b) Y0.75Yb0.25VO4, (c) Y0.50Yb0.50VO4, (d) Y0.25Yb0.75VO4, (e) Y0.10Yb0.90VO4 (high-temperature treatment).
Figure 10. Particle size distribution curve of: (a) Y0.90Yb0.10VO4, (b) Y0.75Yb0.25VO4, (c) Y0.50Yb0.50VO4, (d) Y0.25Yb0.75VO4, (e) Y0.10Yb0.90VO4 (high-temperature treatment).
Sustainability 15 14606 g010
Sustainability 15 14606 g011
Figure 11. IR spectrum of: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4 (d) Y0.10Yb0.90VO4, (e) YbVO4.
Figure 11. IR spectrum of: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4 (d) Y0.10Yb0.90VO4, (e) YbVO4.
Sustainability 15 14606 g011
Sustainability 15 14606 g012
Figure 12. The relationship (αhν)2 as a function of the photon energy hν with the determined value of the energy gap Eg for: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4, (d) Y0.10Yb0.90VO4, (e) YbVO4.
Figure 12. The relationship (αhν)2 as a function of the photon energy hν with the determined value of the energy gap Eg for: (a) YVO4, (b) Y0.90Yb0.10VO4, (c) Y0.50Yb0.50VO4, (d) Y0.10Yb0.90VO4, (e) YbVO4.
Sustainability 15 14606 g012
Table 1. Composition of initial mixtures and results of phase analysis of samples after the last stage of their ball milling and high-temperature treatment.
Table 1. Composition of initial mixtures and results of phase analysis of samples after the last stage of their ball milling and high-temperature treatment.
No.% molx
in Y1−xYbxVO4		Phase Composition of Samples after Synthesis by High-Energy Ball
Milling and High-Temperature Treatment
YVO4YbVO4
190.0010.000.10Y0.90Yb0.10VO4
275.0025.000.25Y0.75Yb0.25VO4
350.0050.000.50Y0.50Yb0.50VO4
425.0075.000.75Y0.25Yb0.75VO4
510.0090.000.90Y0.10Yb0.90VO4
Table 2. Unit cell parameters, volumes and densities of solid solution Y1−xYbxVO4 for x = 0.10, 0.25, 0.50, 0.75, and 0.90 obtained by mechanochemical method.
Table 2. Unit cell parameters, volumes and densities of solid solution Y1−xYbxVO4 for x = 0.10, 0.25, 0.50, 0.75, and 0.90 obtained by mechanochemical method.
x in
Y1−xYbxVO4		a, b [nm]c [nm]α, β, γ [°]V [nm3]dxrd/dexp [g/cm3]
0.100.705530.6750190.000.33604.20/4.09 ± 0.05
0.250.702070.6743590.000.3324 4.50/4.37 ± 0.05
0.500.701850.6713090.000.3307 4.95/4.67 ± 0.05
0.750.699290.6690890.000.3272 5.42/5.08 ± 0.05
0.900.698880.6587590.000.32175.77/5.43 ± 0.05
Table 3. Particle sizes of solid solution.
Table 3. Particle sizes of solid solution.
Formula of Solid SolutionParticle Size
[µm]
d90d50d10
Y0.90Yb0.10VO41.0100.1050.029
Y0.75Yb0.25VO42.4200.4320.102
Y0.50Yb0.50VO419.5000.0770.022
Y0.25Yb0.75VO40.4160.0690.021
Y0.10Yb0.90VO40.2330.0670.021
Table 4. Unit cell parameters, volumes and densities of solid solution Y1−xYbxVO4 for x = 0.10, 0.25, 0.50, 0.75, and 0.90 obtained by high-temperature treatment.
Table 4. Unit cell parameters, volumes and densities of solid solution Y1−xYbxVO4 for x = 0.10, 0.25, 0.50, 0.75, and 0.90 obtained by high-temperature treatment.
x in
Y1−xYbxVO4		a, b [nm]c [nm]α, β, γ [°]V [nm3]dxrd/dexp [g/cm3]
0.100.710970.6283290.000.31764.44/4.40 ± 0.05
0.250.709330.6273990.000.31574.73/4.71 ± 0.05
0.500.708030.6267790.000.3142 5.20/5.19 ± 0.05
0.750.705660.6252390.000.3113 5.70/5.67 ± 0.05
0.900.704730.6247590.000.31035.99/5.97 ± 0.05
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Piz, M.; Filipek, E.; Klukowski, D.; Kochmański, P. Synthesis and Basic Properties of Y1−xYbxVO4 Obtained by High-Energy Ball Milling and High-Temperature Treatment. Sustainability 2023, 15, 14606. https://doi.org/10.3390/su151914606

AMA Style

Piz M, Filipek E, Klukowski D, Kochmański P. Synthesis and Basic Properties of Y1−xYbxVO4 Obtained by High-Energy Ball Milling and High-Temperature Treatment. Sustainability. 2023; 15(19):14606. https://doi.org/10.3390/su151914606

Chicago/Turabian Style

Piz, Mateusz, Elżbieta Filipek, Daniel Klukowski, and Paweł Kochmański. 2023. "Synthesis and Basic Properties of Y1−xYbxVO4 Obtained by High-Energy Ball Milling and High-Temperature Treatment" Sustainability 15, no. 19: 14606. https://doi.org/10.3390/su151914606

APA Style

Piz, M., Filipek, E., Klukowski, D., & Kochmański, P. (2023). Synthesis and Basic Properties of Y1−xYbxVO4 Obtained by High-Energy Ball Milling and High-Temperature Treatment. Sustainability, 15(19), 14606. https://doi.org/10.3390/su151914606

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop