Next Article in Journal
Rheological Assessment of Oil-Xanthan Emulsions in Terms of Complex, Storage, and Loss Moduli
Next Article in Special Issue
Investigation of Morphological, Chemical, and Thermal Properties of Biodegradable Food Packaging Films Synthesised by Direct Utilisation of Cassava (Monihot esculanta) Bagasse
Previous Article in Journal
In Vitro Biocompatibility of Hydrogel Polyvinyl Alcohol/Moringa oleifera Leaf Extract/Graphene Oxide for Wound Dressing
Previous Article in Special Issue
Influence of Herbal Fillers Addition on Selected Properties of Silicone Subjected to Accelerated Aging
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 15
Issue 2
10.3390/polym15020469
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Extraction and Characterization of Fiber and Cellulose from Ethiopian Linseed Straw: Determination of Retting Period and Optimization of Multi-Step Alkaline Peroxide Process

by
Kibrom Feleke
1,
Ganesh Thothadri
2,*,
Habtamu Beri Tufa
1,
Ali A. Rajhi
3 and
Gulam Mohammed Sayeed Ahmed
1,4
1
Department of Manufacturing Engineering, School of Mechanical, Chemical and Materials Engineering, Adama Science and Technology University, Adama P.O. Box 1888, Ethiopia
2
Department of Materials Engineering, School of Mechanical, Chemical and Materials Engineering, Adama Science and Technology University, Adama P.O. Box 1888, Ethiopia
3
Department of Mechanical Engineering, College of Engineering, King Khalid University, Abha 61421, Saudi Arabia
4
Centre of Excellence (COE) for Advanced Manufacturing Engineering, Program of Mechanical Design and Manufacturing Engineering, School of Mechanical, Chemical and Materials Engineering, ASTU, Adama P.O. Box 1888, Ethiopia
*
Author to whom correspondence should be addressed.
Polymers 2023, 15(2), 469; https://doi.org/10.3390/polym15020469
Submission received: 27 October 2022 / Revised: 20 November 2022 / Accepted: 25 November 2022 / Published: 16 January 2023
(This article belongs to the Special Issue Eco-Friendly Polymers: Synthesis, Characterization and Applications)
Browse Figures
Versions Notes

Abstract

:
Flax is a commercial crop grown in many parts of the world both for its seeds and for its fibers. The seed-based flax variety (linseed) is considered less for its fiber after the seed is extracted. In this study, linseed straw was utilized and processed to extract fiber and cellulose through optimization of retting time and a multi-step alkaline peroxide extraction process using the Taguchi design of experiment (DOE). Effects of retting duration on fiber properties as well as effects of solvent concentration, reaction temperature, and time on removal of non-cellulosic fiber components were studied using the gravimetric technique, Fourier transform infrared (FTIR) spectroscopy and thermal studies. Based on these findings, retting for 216 h at room temperature should offer adequate retting efficiency and fiber characteristics; 70% cellulose yield was extracted successfully from linseed straw fiber using 75% ethanol–toluene at 98 °C for 4 h, 6% NaOH at 75 °C for 30 min, and 6% H2O2 at 90 °C for 120 min.

1. Introduction

Agricultural crop by-products are considered inexpensive, abundant, annually renewable, and sustainable sources of fiber and cellulose. Finding alternate sources for present natural and synthetic fibers is critical for ensuring sufficient supply of fibers at reasonable rates in the future. Limitations in availability of land, water, and other resources required to grow natural fibers such as cotton, bamboo, sisal, hemp, and kenaf could limit availability and/or raise prices of those fibers, rendering them unaffordable for commodity applications. As a result, attempts to identify alternate fiber sources, particularly from cheap, copious, and renewable lignocellulose wastes, are considered extremely useful [1].
Flax (Linum usitatissimum) is a fibrous plant that is used as a commercial crop in milder climate regions [2]. Flax is produced for both its seeds and its fiber, although it is mostly farmed for its seeds, leading to its diversification into oilseed (linseed) and fibrous plant types [3]. The phenotypes and physiology of both types differ significantly from each other. Linseed may reach a height of 40–60 cm and has a highly branched stem, whereas the fibrous plant can reach a height of 80–120 cm and has a less branched stem [4]. Linseed and fibrous flax generate different amounts of stalks (30 and 85 dt ha−1, respectively), seeds (20 and 5 dt ha−1, respectively), and fiber (15 and 30%, respectively) [5]. In Ethiopia, flax is cultivated only for its seeds, which are used for oil, and the production capacity is on average 100,000 tons/year from around a 200,000 ha This ranked Ethiopia seventh among the top linseed producer countries in the world [6]. Many studies focus on flax fibers that are grown for textile applications and used to strengthen polymeric matrices [7]. However, fiber obtained from linseed straw every year has not been studied or promoted widely, even though properties of individual oilseed flax fibers [7,8,9], fiber extraction methods [10,11,12], and fiber and seed yields [5] are described comparatively in some studies. Subsequently, after seed harvest, linseed straw left in open fields is abandoned and/or burned, causing significant environmental harm. Many nations are now dealing with the problem of utilizing linseed straw [12].
Appropriate natural fiber extraction represents a major test faced during processing of plant fibers. Extraction methods to separate plant fibers include retting and mechanical extraction processes [13,14]. Common retting methods are water, dew, chemical, and enzyme retting [15,16]. Water retting is the most common method to extract high-quality fibers. In the retting process, existence of bacteria and moisture in the plants allows them to break down large parts from cellular tissues and adhesive substances that surround fibers, enabling separation of individual fibers from the plant. Depending on the fiber category, this process requires approximately 7 to 14 days [17,18]. Water retting is critical to processing of fibers; it influences qualities of generated fibers, and retting quality is a primary issue for industries that use natural fibers in their products [17]. Therefore, reaction time must be carefully evaluated when water retting is used, because under- or excessive retting can cause difficulties in separation of individual fibers, or may weaken fiber strength [19,20].
Cellulose is the most prevalent substance on the planet and the major component of plant-cell walls. The principal components of plant fibers include cellulose, hemicellulose, lignin, pectin, and wax [21,22]. However, cellulose is dependent on plant type and the geographical area in which it is cultivated [23]. As a result, suggests development of novel cellulose-based materials and demands detailed examination of their physical and chemical properties [24]. In this context, there has been a surge in interest in extracting cellulose from natural fibers in recent years. Several experiments have been conducted, utilizing natural fibers, including sisal, rice husk, sugarcane bagasse, cotton, hemp, jute, bamboo, and kenaf, among others, as sources of cellulose [23,25,26,27].
Extraction processes and methods for extracting cellulose vary and may include acid and alkaline media; each process yields unique properties for each type of cellulose produced. Because amount of cellulose and extraction process vary from plant to plant, it is crucial to note that cellulose tests and investigations are carried out separately [23]. The purpose of the extraction process is to obtain cellulose with a high yield and purity through elimination of non-cellulosic components—mainly extractives, hemicellulose, and lignin—using different solvents with various concentrations, reaction temperatures, and times for each step of extraction. This allows for extraction-process variable adjustments that lead to optimization strategies [23]. Therefore, in this study, the retting-time duration endpoint and influence of retting-time duration on fibers’ physical, tensile, and thermal properties were investigated. Chemical compositions of fiber retted at optimal water-retting duration were analyzed, and cellulose was extracted and characterized using optimized multistep cellulose-extraction-process parameters.

2. Materials and Methods

2.1. Materials

Chemicals utilized were ethanol LR (96%; Wasse Pharma PLC, Addis Ababa, Ethiopia), toluene AR (99.9%; Blulux Laboratories Pvt. Ltd., Faridabad, India), sulfuric acid AR (98%; Loba Chemie Pvt. Ltd., Mumbai, India), sodium hydroxide pellets LR (98%; Blulux Laboratories Pvt. Ltd., India), and hydrogen peroxide solution LR (30%; Fine Chemical General Trading PLC, Addis Ababa, Ethiopia).
Processing and characterization equipment used were a Soxhlet apparatus (M500-mL flask, Soxhlet tube, 300 mm condenser, medium-porosity cellulose thimbles, heating mantle, chiller, pH meter (AD8000 pH/mV/EC/TDS/Temperature); Adwa Instruments, Inc., Szeged, Hungary), an electronic balance (JF-2004; Tsingtao Unicom-Optics Instruments Co., Ltd., Laixi, China), a Clifton drying oven (NE9-56S; Nickel-Electro Ltd., Weston-Super-Mare, UK), a box-type resistance furnace (SX-2.5-12; Taisite Lab science INC., New York, NY, USA), a shaking water bath (GFL 1083; GFL Water Baths, Hamburg, Germany), a vertical autoclave (AVI-017B; Avishkar International Pvt. Ltd., Mumbai, India), a single-fiber electronic strength tester (Fiber Tenso-Lab-331A; Mesdan-Lab, Raffa, Italy), a FTIR-6600 spectrometer (JASCO Inc. Ltd., Easton, MD, USA), and a thermogravimetric and differential thermal analyzer (TG-DTA, HCT-3; Beijing Henven Instruments, Beijing, China).

2.2. Fiber Extraction and Characterization Methods

A 50 g linseed straw bundle with a 20 cm length and a 3 mm mean stalk diameter was cut from the center section of the stems for uniformity of samples. Next, the bundled stalks were immersed in transparent plastic bottles, each filled with the same amount of water, with a 1:33 solid-to-liquid ratio [28]. After immersion, the bottles were stored at room temperature for 48–264 h, without lids, for retting, as shown in Table 1 [29,30].
About 275 mL of retted water was taken from all samples and tested every 24 h using a calibrated pH meter to find pH measurement [31,32]. Increase in weight of wetted linseed stalks (mw) from initial dry linseed stalk weight (md) due to water absorption from each retting time was recorded, and stalk water-absorption percentage (wa%) was estimated based on Equation (1) [33,34].
w a % = m w − m d m d × 100
The percentage of mass change between dry non-retted (w1) and dry retted (w2) linseed stalks was used to calculate stalk weight loss (wl%) using Equation (2) [29,35].
w l % = w 1 − w 2 w 1 × 100
Weight of linseed fiber extracted (mo) from the initial linseed stalk weight (mi) was recorded for each retting time, and the fiber yield percentage (Y%) was determined using Equation (3) [28,36].
Y % = m o m i × 100
Density of oven-dried stalks amounted to a constant weight [34,37,38]; non-, under-, optimally, and over-retted linseed fiber bundles were measured for distilled water density (ρw) using the liquid pycnometer technique. Mass of an empty pycnometer (m1), a pycnometer filled with chopped fibers (m2), a pycnometer filled with water (m3), and a pycnometer filled with water and chopped fibers (m4) was measured and calculated. Density of fibers (ρf) was estimated based on Equation (4) [38,39].
ρ f = m 2 − m 1 m 3 − m 1 − m 4 − m 2 × ρ w
Diameter of linseed fibers was measured using an optical microscope. Three samples, from under-, optimally, and over-retted fibers, were prepared; then three equidistant points were marked on a single fiber, and the diameters of these points were measured with two replications. The average diameter was then calculated; this could be considered the mean diameter of the fibers [40].
Fiber samples with different degrees of water retting were kept in the open air at room temperature and 55–65% RH for one week. Then, after drying in an oven to a constant weight, weights of wetted (Ww) and oven-dried (Wd) samples were measured. Moisture content percentage (MC%) of the fiber was calculated using Equation (5) [33,34].
M C   % = W w − W d W w × 100
A tensile test of single fibers with different retting durations was performed according to ASTM D 3822–07, using a single-fiber electronic strength tester. The test was carried out at room temperature and 65% RH, with a gauge length of 100 mm, a load range of 5 N, and a test speed of 100 mm/min [41].
A chemical composition analysis (dry-weight basis) of the fiber was conducted to quantify mainly the percentage amounts of cellulose, hemicellulose, lignin, and extractives. This analysis used 1:2 ethanol–toluene for 6 h at 98 °C in a Soxhlet apparatus to determine extractive content [42,43,44,45], 17.5% NaOH at 95 °C for 60 min in a reciprocating water bath to quantify hemicellulose content [46,47], and 72% H2SO4 at room temperature for 120 min; hydrolyzed samples were diluted with distilled water to a 3% acid concentration (adapted from TAPPI T-222 om-02) [48]. Samples were autoclaved for 1 h at 121 °C and cooled for about 20 min at room temperature; the diluted suspensions were centrifuged at 5000 rpm for 15 min and vacuum-filtered. The residues were burned in a muffle furnace at 550 ℃ for 3 h to quantify the amount of ash in the acid-insoluble lignin [41,49], as shown in Figure 1.
Percentage amounts of non-cellulosic constituents (wt.%) were calculated from the difference between initial (wi) and final (wf) fiber weights, using the gravimetric method based on Equation (6) [50,51].
w t . % = w i − w f w i × 100
The ash content of dry, chopped raw fiber was determined via burning in a 550 °C furnace for 4 h [48], allowance to cool to room temperature in a desiccator, and weighing (adapted from TAPPI (T 211 om-02)). Finally, the cellulose percentage in wt.% of biomass was calculated using Equation (7), assuming that extractives, hemicellulose, lignin, ash, and cellulose were the main chemical compositions of the linseed fiber [52,53,54].
Cellulose % = 100 % − ( Extractives + Hemicellulose + Lignin + Ash ) %

2.3. Cellulose Extraction and Characterization Methods

Cellulose was extracted from linseed straw through sequential chemical treatments to remove extractives, hemicellulose, and lignin, as shown in Figure 2.
Removal percentage of non-cellulosic components (R%) of linseed fiber in each step of the cellulose extraction process was calculated via taking the weight difference between initial (mi) and final (mf) fiber weights, using the gravimetric method based on Equation (8).
R % = m i − m f m i × 100

2.4. Fourier Transform Infrared (FTIR)

In the FTIR analysis, FTIR spectra of the fibers (non-retted, retted, extracted, alkalized, and bleached) were recorded using a FT–IR spectrometer with a 2 mm/s scanning speed and a 4 cm−1 resolution in a range of 400–4000 cm−1 wavenumbers [48,55,56,57].

2.5. Thermogravimetric Analysis (TGA)

In the thermal study, thermal degradation characteristics of fibers (non-retted, retted, extracted, alkalized, and bleached) were analyzed using a thermogravimetric and differential thermal analyzer, from room temperature to 700 °C, at a heating rate of 20 °C min−1 in N2 atmospheres, and using an 8 mg sample weight [1,58,59,60].

2.6. Statistical Method for Optimization

The selected factors (concentration, temperature, and time) and levels (low, medium and high) for the extraction processes are shown in Table 2. The Taguchi L9 Orthogonal Array (OA) design of experiments was employed to investigate contribution of selected extraction conditions (concentration of solvents, reaction temperature, and time) to yield removal of extractives, hemicellulose, and lignin, as shown in Table S1.

3. Results and Discussion

3.1. Retted Water pH, Stalk Water Absorption and Stalk Weight Loss Analysis

Figure 3a,b illustrate the effect of water-retting time on pH value of retting water, stalk water absorption, and stalk weight loss. When the pH value of the retted water dropped from 7.00 to 4.86, after 216 h, it remained steady and then increased again.
Many bacteria isolated from bast fibers are capable of promoting retting. The most important phase of this process is hydrolysis of pectic matter that surrounds and cements fibers, thereby loosening fibers from the stem and helping to extract those fibers [31]. Due to absence of pectic matter to be hydrolyzed and utilization of D-galacturonic acid (GA) by bacteria, concentration of GA, which is the end product of bacterial hydrolysis in retting water, began to fall [31,32].
The effect of retting-time duration on the water absorption percentage of linseed stalks showed that water absorption increased rapidly to 172.47% during the first 48 h, then increased slowly to the equilibrium water-absorption percentage of 187.21% at 168 h. After this immersion-time duration had passed, percentage of water absorption became stable, which means less than 1% of variations were observed, and no more weight gain of the wetted linseed stalk was observed during retting-time increments, as shown in Figure 3b. Forty-eight hours after equilibrium water absorption was the optimum retting time for successful fiber extraction.
Water retting occurs when water penetrates the center-stalk section of the plant, swelling the interior cells and shattering the outermost layer to enhance absorption of water and produce bacteria that promotes retting [61,62]. Therefore, retting up to equilibrium water absorption helps with removal of pectin and successful fiber extraction during water retting.
Extending duration of water retting resulted in a considerable increase in weight loss, as can be shown in Figure 3a. When the duration was extended from 48 to 168 h, the weight loss increased from 5.74 to 12.3% due to removal of impurities and pectin components of the fiber. From 168 to 216 h, weight-loss variations were nearly stable or less than 1%, and at the end of this time, 12.67% fiber yield was obtained. However, after 216 h of retting, weight loss was slightly increased due to removal of other non-cellulosic constituents [35,63,64]. As a result, the retted water pH, stalk water absorption, and stalk weight loss values obtained can be used to predict optimal retting time.

3.2. Effect of Retting Duration on Fiber Properties

Effects of retting duration on physical and tensile properties of fibers that were extracted under different retting durations, shown in Figure 4, were investigated.

3.2.1. Physical Properties

Table 3 demonstrates effects of retting duration on physical properties—mainly diameter, density, and moisture—of (R0) non-retted, (R1) under-retted, (R2) optimally retted, and (R3) over-retted fibers.
These results revealed that as degree of retting increased, average diameter of the fiber reduced due to removal of surface components via retting [65,66]. Initially, an increment in density values was observed, with increasing retting degree due to removal of less-dense constituents and impurities such as pectin [67,68], but over-retted fibers showed a relative reduction in density as a result of cell-wall decompression [69,70].
The mean density of optimal retted fiber was 1.52 g/cm3 and the density values of flax fiber reported in previous works of the literature were from 1.40 to 1.55 g/cm3 [71,72]. These values were obtained with different methods, such as a helium pycnometer (1.54 g/cm3) [73], a gas pycnometer (1.49 to 1.52 g/cm3) [74], and immersion in water (1.54 g/cm3) [75]. Moisture content was reduced with increasing retting degree due to the high amount of cortical parenchyma components remaining on the surface of non-retted and under-retted fibers; these fibers may have high water interaction [76].

3.2.2. Tensile Properties

The effect of retting duration on tensile properties—specifically breaking force; breaking elongation; and tenacity of (R1) under-retted, (R2) optimally retted, and (R3) over-retted fibers—were tested as shown in Table 3. Initially, mean breaking force and tenacity of each single fiber were enhanced due to removal of a larger amounts of weak substances, such as pectin and other impurities; results were reduced with further increments of retting duration due to cellulose-component degradation resulting in presence of more weak spots and reduction in diameter of the fibers [65,77,78].
These results showed that mean elongation values decreased with an increasing degree of retting due to removal of non-cellulosic components; this tends to result in fiber brittleness [30,79].

3.3. Chemical Composition Analysis

The primary chemical compositions of linseed straw are cellulose, hemicellulose, lignin, and extractives. The chemical constituents of linseed fiber are 68, 20, 5, 4, and 3% of cellulose, hemicellulose, lignin, extractives, and ash, respectively. Cellulose content is comparatively higher than are different lignocellulose biomasses from agricultural wastes, as shown in Table 4.
These variations may be due to the type of agricultural crop and the geographic area where the plants were cultivated; the amount of these constituents might vary even among the same plants. Uniquely, all fibers contain the same constituents, but in different percentages, which results in different behaviors [83].

3.4. Cellulose Extraction, Characterization and Optimization

The cellulose extraction process was conducted in multi-step extraction processes via optimization of extraction-process conditions, including solvent concentration, reaction temperature, and time. The extraction steps mainly focused on removal of extractives, hemicellulose, and lignin using ethanol–toluene, sodium hydroxide, and hydrogen peroxide solvents, respectively, under different extraction-process conditions. The results for a fiber after each step of extraction are shown in Figure 5.

3.4.1. Statistical Analysis

The experimental results showed that the maximum removal values of extractives, hemicellulose, and lignin were 4.90, 18.10, and 4.00% respectively; these results were observed at extraction-variable combinations of 75% at 98 °C for 4 h, 6% at 75 °C for 30 min, and 6% at 90 °C for 120 min, respectively. However, the predicted mean removal (%) of extractives, hemicellulose, and lignin tested under optimum values from the signal to noise ratio (SNR) graph was calculated as 4.88, 18.25, and 4.19% at extraction-variable combinations of 75% at 98 °C for 8 h, 6% at 75 °C for 90 min, and 10% at 90 °C for 120 min, with error values of 0.40, 0.82, and 4.53%, respectively. This indicates that the experimental and predicted results were in good agreement, as shown in Table 5.
The ANOVA results shown in Tables S2–S4 explain the significant level, contribution percentage, and rank of each factor in removal of extractives, hemicellulose, and lignin, respectively. The concentrations of the solvents in removal of extractives, hemicellulose, and lignin were statistically significant (p ≤ 0.05), contributing 97.25, 64.5, and 81.47% to the response, respectively. The reaction temperatures in removal of extractives and hemicellulose were statistically significant, contributing 2.74 and 35.09%, respectively. This value, however, was not significant in removal of lignin (p ≥ 0.05), contributing only 7.48%. The reaction time in removal of extractives, hemicellulose, and lignin was not significant, with no contribution, 0.29%, and 9.26%, respectively.
The ANOVA findings of the linear model equations shown in Equations (S1)–(S4) can appropriately explain removal of extractives, hemicellulose, and lignin within a wide range of operating circumstances, with coefficients of determination (R2) of 0.569, 0.879, and 0.8974 at a 95% level of confidence. The response models examined in this study can explain removal of extractives, hemicellulose and lignin; they contributed 56.95, 87.92, and 89.74% to the response, respectively.

3.4.2. Fourier Transform Infrared (FTIR) Analysis

The FTIR spectra of the non-retted, retted, extracted, alkalized, and bleached linseed fibers shown in Figure 6 were interpreted and discussed according to reported studies regarding the sources of FTIR peaks and their assignments, as shown in Table 6. For every stage of the extraction procedure, FTIR analysis was carried out to identify presence of chemical functional group changes [84]. All samples presented two main absorbance regions: the fingerprint region (700–1800 cm−1) and the functional group region (2700–3500 cm−1). However, specific absorption peaks can be identified for each particular component [42].
The presence of nearly similar functional groups at 3,425, 2,917, 1,636, 1,114, and 617 cm−1 in all fibers justified preservation of the basic chemical structure of cellulose fiber and water, even after all treatments during the extraction process. It was expected that during the extraction process, non-cellulosic components of the fiber—hemicellulose, lignin, and extractive (pectin, wax) contents—could be completely or partially removed. Therefore, corresponding absorption peaks to these components disappeared or diminished in intensity value. The treatments, on the other hand, increased intensity of bands that corresponded to cellulose [85].
The absorption peaks that corresponded to the extractives were 2917, 2853, 1114, and 1032 cm−1. The absorbance peak at 2853 cm−1 disappeared, and others were reduced after retting and extraction due to removal or reduction of pectin and wax. The absorption peaks at 3425, 2917, 1732, 1426, 1383, 1114, 1032 and 901 cm−1 are related to hemicellulose. The absorption peak at 1731 cm−1 disappeared, and the others were diminished in peak intensity because of hemicellulose removal during the alkalization process. Absorption peaks observed at 3425, 2917, 1731 and 1426 cm−1 are associated with lignin. The absorption peak at 1731 cm−1 disappeared, and the others diminished in peak intensity because of lignin removal during the bleaching process.

3.4.3. Thermogravimetric Analysis (TGA)

Decomposition of lignocellulose materials mainly shows three stages of degradation; due to differences in chemical structures between extractives, hemicellulose, cellulose, and lignin, they usually decompose at different temperatures [77,88]. Degradation of linseed straw fiber went through three phases, as shown in Figure 7: light-component drying and evaporation, hemicellulose and amorphous cellulose decomposition, and crystalline cellulose and lignin decomposition.
Weight loss, decomposition temperature ranges, and residue contents of fibers in each degradation stage are summarized in Table 7.
The thermal stability of the raw, extracted, alkalized, and bleached fibers was 179, 205, 250, and 269 °C, respectively. All extraction steps resulted in thermal stability improvement of the fiber due to retention and improvement of the structural order, as well as reduction in amorphous content [89].
Each fiber showed dissimilar weight losses and temperature ranges in all degradation stages. Weight loss (%) in the first stage was higher for raw fiber compared to that of extracted and alkalized fibers due to presence of extractives and higher moisture content. It was reduced after removal of extractives and hemicellulose, which are responsible for moisture absorption of fibers, and on the other hand, the bleached fiber showed the highest weight loss (%) due to more moisture-absorption properties of the fiber after removal of lignin, which is naturally hydrophobic [90].
An increase in weight loss was observed in the second degradation stage after the extraction process due to the removal of extractives, which increased the proportions of cellulose and hemicellulose [77]. However, weight loss decreased after the alkalization and bleaching processes due to removal of hemicellulose and lignin. The decomposition temperature range decreased after each extraction step in all stages, since degradation of non-cellulosic components occurred over a low, broad temperature range due to presence of low molecular weight components [91]. Finally, residues that corresponded to ash content decreased during the extraction steps as a result of removal of non-cellulosic matter, which is responsible for ash content [92,93].

4. Conclusions

The linseed plant is a dual-purpose crop. Even if it is first and foremost cultivated for its seeds, its straw can be also useful, possibly contributing to an additional source of income for farmers as a source of fiber and cellulose due to its comparable bast-fiber and cellulose contents. This study reported optimum extraction of fiber and cellulose, as well as characterization from linseed straw. According to the experiments and analyses performed, pH, stalk water absorption, and weight loss were found to be good indicators for termination time of the water-retting process and optimum retting time. Effects of retting-time duration on tensile and physical properties of the fibers were tested, analyzed, and discussed. At the recommended optimum retting time (216 h), fibers with a density of 1.52 g/cm3, a diameter of 104.65 µm, and a moisture content of 8.32% had a mean breaking force of 278.4 cN, a breaking elongation of 2.06%, and a tenacity value of 59.1 cN/tex. The chemical composition of the optimum retted fiber had content of 68% cellulose, 20% hemicellulose, 5% lignin, 4% extractives, and 3% ash. Cellulose was present at the highest levels; therefore, extraction of cellulose from linseed straw is feasible and a promising sustainable cellulose source for different applications, such as packaging, filtration, composites, implants, paper, and pulp. Cellulose is extracted through successful optimization of multi-step extraction-process parameters for linseed straw. The recommended optimum cellulose extraction conditions for linseed fiber were identified as 75% ethanol–toluene at 98 °C for 4 h, 6% NaOH at 75 °C for 30 min, and 6% H2O2 at 90 °C for 120 min, for successful removal of non-cellulosic constituents.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/polym15020469/s1. Table S1: Taguchi L9 orthogonal array layout for cellulose extraction. Table S2: ANOVA results for removal of extractives (%) under different extraction conditions. Table S3: ANOVA for removal of hemicellulose (%) under different extraction conditions. Table S4: ANOVA for removal of lignin (%) under different extraction conditions.

Author Contributions

Conceptualization, methodology, formal analysis, investigation, visualization, and writing of original draft, K.F.; data curation, validation, project administration, resources, investigation, resources, writing—review, editing, and supervision, G.T.; project administration, resources, supervision, writing—review, and editing, H.B.T.; funding acquisition, resources, and project administration, A.A.R.; funding acquisition, software, writing—review, and editing, G.M.S.A. All authors have read and agreed to the published version of the manuscript.

Funding

We thank Adama Science and Technology University School of Mechanical, Chemical and Material Science and Engineering for Ph.D. research funding and laboratory access. Furthermore, the authors extend their appreciation to the Deanship of Scientific Research at King Khalid University, Saudi Arabia, for funding this work through the Research Group Program under grant No. RGP. 2/129/43.

Institutional Review Board Statement

Not applicable.

Acknowledgments

The authors extend their appreciation to the Deanship of Scientific Research at King Khalid University, Saudi Arabia, for funding this work through the Research Group Program under grant No. RGP. 2/129/43. The authors also extend their appreciation to the Department of Mechanical Engineering and the Department of Material Science and Engineering of Adama Science and Technology University, Ethiopia, for financial assistance to successfully perform experiments and for technical expertise.

Conflicts of Interest

The authors declare no conflict of interest. The authors have no relevant financial or non-financial interests to disclose.

References

  1. Karthik, T.; Murugan, R. Characterization and analysis of ligno-cellulosic seed fiber from Pergularia daemia plant for textile applications. Fiber. Polym. 2013, 14, 465–472. [Google Scholar] [CrossRef]
  2. Saleem, M.H.; Ali, S.; Hussain, S.; Kamran, M.; Chattha, M.S.; Ahmad, S.; Aqeel, M.; Rizwan, M.; Aljarba, N.H.; Alkahtani, S. Flax (Linum usitatissimum L.): A potential candidate for phytoremediation? Biological and economical points of view. Plants 2020, 9, 496. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  3. Jhala, A.J.; Hall, L.M. Flax (Linum usitatissimum L.): Current uses and future applications. Aust. J. Basic Appl. Sci 2010, 4, 4304–4312. [Google Scholar]
  4. Zuk, M.; Richter, D.; Matuła, J.; Szopa, J. Linseed, the multipurpose plant. Ind. Crops Prod. 2015, 75, 165–177. [Google Scholar] [CrossRef]
  5. Praczyk, M.; Wielgusz, K. Agronomic Assessment of Fibrous Flax and Linseed Advanced Breeding Lines as Potential New Varieties. Agronomy 2021, 11, 1917. [Google Scholar] [CrossRef]
  6. FAOSTAT. Linseed World Production. Available online: https://www.fao.org/faostat/en/#rankings/countries_by_commodity (accessed on 15 December 2020).
  7. Pillin, I.; Kervoelen, A.; Bourmaud, A.; Goimard, J.; Montrelay, N.; Baley, C. Could oleaginous flax fibers be used as reinforcement for polymers? Ind. Crops Prod. 2011, 34, 1556–1563. [Google Scholar] [CrossRef]
  8. Rennebaum, H.; Grimm, E.; Warnstorff, K.; Diepenbrock, W. Fibre quality of linseed (Linum usitatissimum L.) and the assessment of genotypes for use of fibres as a by-product. Ind. Crops Prod. 2002, 16, 201–215. [Google Scholar] [CrossRef]
  9. Tomljenović, A.; Erceg, M. Characterisation of Textile and Oleaginous Flax Fibrous and Shives Material as Potential Reinforcement for Polymer Composites. Tekstilec 2016, 59, 350–366. [Google Scholar] [CrossRef]
  10. Ouagne, P.; Barthod-Malat, B.; Evon, P.; Labonne, L.; Placet, V. Fibre Extraction from Oleaginous Flax for Technical Textile Applications: Influence of Pre-processing parameters on Fibre Extraction Yield, Size Distribution and Mechanical Properties. Procedia Eng. 2017, 200, 213–220. [Google Scholar] [CrossRef]
  11. Khan, S.U.; Labonne, L.; Ouagne, P.; Evon, P. Continuous mechanical extraction of fibres from linseed flax straw for subsequent geotextile applications. Coatings 2021, 11, 852. [Google Scholar] [CrossRef]
  12. Shaimerdenov, Z.N.; Dalabayev, A.B.; Temirova, I.Z.; Aldiyeva, A.B.; Sakenova, B.A.; Zhunussova, K.Z.; Iztayev, A. Fibre extraction from oilseed flax straw for various technical applications. EurAsian J. BioSci. 2020, 14, 7. [Google Scholar]
  13. Tahir, P.M.; Ahmed, A.; Saifulazry, S.; Ahmed, Z. Review of bast fiber retting. BioResources 2011, 6, 5260–5281. [Google Scholar]
  14. Easson, D.L.; Molloy, R. Retting—A key process in the production of high value fibre from flax. Outlook Agric. 1996, 25, 235–242. [Google Scholar] [CrossRef]
  15. Akin, D.E.; Foulk, J.A.; Dodd, R.B.; McAlister, D.D., III. Enzyme-retting of flax and characterization of processed fibers. J. Biotechnol. 2001, 89, 193–203. [Google Scholar] [CrossRef] [PubMed]
  16. Jayamani, E.; Heng, S.K.; Khui, P.L.N.; Bin Bakri, M.K. Comparative Study of Compressive Strength of Epoxy Based Bio-Composites. Key Eng. Mater. 2018, 775, 68–73. [Google Scholar] [CrossRef]
  17. Foulk, J.; Akin, D.; Dodd, R. Influence of pectinolytic enzymes on retting effectiveness and resultant fiber properties. Bio. Resour. 2008, 3, 155–169. [Google Scholar]
  18. Jonoobi, M.; Khazaeian, A.; Tahir, P.M.; Azry, S.S.; Oksman, K. Characteristics of cellulose nanofibers isolated from rubberwood and empty fruit bunches of oil palm using chemo-mechanical process. Cellulose 2011, 18, 1085–1095. [Google Scholar] [CrossRef]
  19. Adamsen, A.P.S.; Akin, D.E.; Rigsby, L.L. Chelating agents and enzyme retting of flax. Text. Res. J. 2002, 72, 296–302. [Google Scholar] [CrossRef]
  20. Gusovius, H.-J.; Lühr, C.; Hoffmann, T.; Pecenka, R.; Idler, C. An alternative to field retting: Fibrous materials based on wet preserved hemp for the manufacture of composites. Agriculture 2019, 9, 140. [Google Scholar] [CrossRef] [Green Version]
  21. Faruk, O.; Bledzki, A.K.; Fink, H.-P.; Sain, M. Biocomposites reinforced with natural fibers: 2000–2010. Prog. Polym. Sci. 2012, 37, 1552–1596. [Google Scholar] [CrossRef]
  22. Gurukarthik Babu, B.; Prince Winston, D.; SenthamaraiKannan, P.; Saravanakumar, S.; Sanjay, M. Study on characterization and physicochemical properties of new natural fiber from Phaseolus vulgaris. J. Nat. Fibers 2019, 16, 1035–1042. [Google Scholar] [CrossRef]
  23. Manzato, L.; Takeno, M.L.; Pessoa-Junior, W.A.G.; Mariuba, L.A.M.; Simonsen, J. Optimization of cellulose extraction from jute fiber by Box-Behnken design. Fiber. Polym. 2018, 19, 289–296. [Google Scholar] [CrossRef]
  24. Ummartyotin, S.; Manuspiya, H. A critical review on cellulose: From fundamental to an approach on sensor technology. Renew. Sust. Energ. Rev. 2015, 41, 402–412. [Google Scholar] [CrossRef]
  25. Lavanya, D.; Kulkarni, P.; Dixit, M.; Raavi, P.K.; Krishna, L.N.V. Sources of cellulose and their applications—A review. IJDFR 2011, 2, 19–38. [Google Scholar]
  26. de Oliveira, J.P.; Bruni, G.P.; Lima, K.O.; El Halal, S.L.M.; da Rosa, G.S.; Dias, A.R.G.; da Rosa Zavareze, E. Cellulose fibers extracted from rice and oat husks and their application in hydrogel. Food Chem. 2017, 221, 153–160. [Google Scholar] [CrossRef]
  27. Rasheed, M.; Jawaid, M.; Parveez, B.; Zuriyati, A.; Khan, A. Morphological, chemical and thermal analysis of cellulose nanocrystals extracted from bamboo fibre. Int. J. Biol. Macromol. 2020, 160, 183–191. [Google Scholar] [CrossRef]
  28. Pandey, R. Fiber Extraction from Dual-Purpose Flax. J. Nat. Fibers 2016, 13, 565–577. [Google Scholar] [CrossRef]
  29. Ruan, P.; Raghavan, V.; Gariepy, Y.; Du, J. Characterization of flax water retting of different durations in laboratory condition and evaluation of its fiber properties. BioResources 2015, 10, 3553–3563. [Google Scholar] [CrossRef] [Green Version]
  30. Yu, H.; Yu, C. Influence of various retting methods on properties of kenaf fiber. J. Text. Inst. 2010, 101, 452–456. [Google Scholar] [CrossRef]
  31. Rosemberg, J.A.; De França, F.P. Importance of Galacturonic Acid in Controlling the Retting of Flax. Appl. Microbiol. 1967, 15, 484–486. [Google Scholar] [CrossRef]
  32. de Franca, F.; Rosemberg, J.; de Jesus, A. Retting of flax by Aspergillus niger. Appl. Microbiol. 1969, 17, 7–9. [Google Scholar] [CrossRef] [PubMed]
  33. Mittal, M.; Chaudhary, R. Experimental study on the water absorption and surface characteristics of alkali treated pineapple leaf fiber and coconut husk fiber. Int. J. Appl. Eng. Res. 2018, 13, 12237–12243. [Google Scholar]
  34. Baley, C.; Morvan, C.; Grohens, Y. Influence of the Absorbed Water on the Tensile Strength of Flax Fibers. Macromol. Symp. 2005, 222, 195–202. [Google Scholar] [CrossRef]
  35. Nair, G.; Singh, A.; Zimniewska, M.; Raghavan, V. Comparative Evaluation of Physical and Structural Properties of Water Retted and Non-retted Flax Fibers. Fibers 2013, 1, 59–69. [Google Scholar] [CrossRef] [Green Version]
  36. Dhanani, T.; Shah, S.; Gajbhiye, N.; Kumar, S. Effect of extraction methods on yield, phytochemical constituents and antioxidant activity of Withania somnifera. Arab. J. Chem. 2017, 10, S1193–S1199. [Google Scholar] [CrossRef] [Green Version]
  37. Rude, T.; Strait, L., Jr.; Ruhala, L. Measurement of fiber density by helium pycnometry. J. Compos. Mater. 2000, 34, 1948–1958. [Google Scholar] [CrossRef]
  38. Truong, M.; Zhong, W.; Boyko, S.; Alcock, M. A comparative study on natural fibre density measurement. J. Text. Inst. 2009, 100, 525–529. [Google Scholar] [CrossRef]
  39. Manimaran, P.; Sanjay, M.; Senthamaraikannan, P.; Yogesha, B.; Barile, C.; Siengchin, S. A new study on characterization of Pithecellobium dulce fiber as composite reinforcement for light-weight applications. J. Nat. Fibers 2018, 17, 359–370. [Google Scholar] [CrossRef]
  40. Widnyana, A.; Rian, I.G.; Surata, I.W.; Nindhia, T.G.T. Tensile Properties of coconut Coir single fiber with alkali treatment and reinforcement effect on unsaturated polyester polymer. Mater. Today Proc. 2020, 22, 300–305. [Google Scholar] [CrossRef]
  41. Arul Marcel Moshi, A.; Ravindran, D.; Sundara Bharathi, S.R.; Suganthan, V.; Kennady Shaju Singh, G. Characterization of New Natural Cellulosic Fibers—A Comprehensive Review. IOP Conf. Ser. Mater. Sci. Eng. 2019, 574, 012013. [Google Scholar] [CrossRef]
  42. Morán, J.I.; Alvarez, V.A.; Cyras, V.P.; Vázquez, A. Extraction of cellulose and preparation of nanocellulose from sisal fibers. Cellulose 2008, 15, 149–159. [Google Scholar] [CrossRef]
  43. Borchani, K.E.; Carrot, C.; Jaziri, M. Untreated and alkali treated fibers from Alfa stem: Effect of alkali treatment on structural, morphological and thermal features. Cellulose 2015, 22, 1577–1589. [Google Scholar] [CrossRef]
  44. Teli, M.; Pandit, P. Novel method of ecofriendly single bath dyeing and functional finishing of wool protein with coconut shell extract biomolecules. ACS Sustain. Chem. Eng. 2017, 5, 8323–8333. [Google Scholar] [CrossRef]
  45. D’Auria, M.; Mecca, M.; Bruno, M.R.; Todaro, L. Extraction Methods and Their Influence on Yield When Extracting Thermo-Vacuum-Modified Chestnut Wood. Forests 2021, 12, 73. [Google Scholar] [CrossRef]
  46. Zhu, Z.; Hao, M.; Zhang, N. Influence of contents of chemical compositions on the mechanical property of sisal fibers and sisal fibers reinforced PLA composites. J. Nat. Fibers 2018, 17, 101–112. [Google Scholar] [CrossRef]
  47. Kang, L.Y.; Haslija, A.A. Optimization of Alkaline Pulp Extraction from Napier Grass Using Response Surface Methodology. In Proceedings of the IOP Conference Series: Earth and Environmental Science, Kuala Lumpur, Malaysia, 11–14 December 2018; p. 012051. [Google Scholar]
  48. Kale, R.D.; Taye, M.; Chaudhary, B. Extraction and characterization of cellulose single fiber from native Ethiopian Serte (Dracaena steudneri Egler) plant leaf. J. Macromol. Sci. 2019, 56, 837–844. [Google Scholar] [CrossRef]
  49. Manimaran, P.; Saravanan, S.P.; Sanjay, M.R.; Siengchin, S.; Jawaid, M.; Khan, A. Characterization of new cellulosic fiber: Dracaena reflexa as a reinforcement for polymer composite structures. J. Mater. Res. Technol. 2019, 8, 1952–1963. [Google Scholar] [CrossRef]
  50. McCleary, B.V. Total dietary fiber (CODEX definition) in foods and food ingredients by a rapid enzymatic-gravimetric method and liquid chromatography: Collaborative study, first action 2017.16. J. AOAC Int. 2019, 102, 196–207. [Google Scholar] [CrossRef] [Green Version]
  51. Huang, J.; Yu, C. Determination of cellulose, hemicellulose and lignin content using near-infrared spectroscopy in flax fiber. Text. Res. J. 2019, 89, 4875–4883. [Google Scholar] [CrossRef]
  52. Lin, L.; Yan, R.; Liu, Y.; Jiang, W. In-depth investigation of enzymatic hydrolysis of biomass wastes based on three major components: Cellulose, hemicellulose and lignin. Bioresour. Technol. 2010, 101, 8217–8223. [Google Scholar] [CrossRef]
  53. Adeeyo, O.; Oresegun, O.M.; Oladimeji, T.E. Compositional analysis of lignocellulosic materials: Evaluation of an economically viable method suitable for woody and non-woody biomass. Am. J. Eng. Res. 2015, 4, 14–19. [Google Scholar]
  54. Li, S.; Xu, S.; Liu, S.; Yang, C.; Lu, Q. Fast pyrolysis of biomass in free-fall reactor for hydrogen-rich gas. Fuel Process. Technol. 2004, 85, 1201–1211. [Google Scholar] [CrossRef]
  55. Alix, S.; Philippe, E.; Bessadok, A.; Lebrun, L.; Morvan, C.; Marais, S. Effect of chemical treatments on water sorption and mechanical properties of flax fibres. Bioresour. Technol. 2009, 100, 4742–4749. [Google Scholar] [CrossRef] [PubMed]
  56. Suaniti, N.M.; Adnyana, I.W.B. Biodiesel Synthesis from Used frying Oil through Phosphoric Acid Refined and CaO Catalyzed Transesterification. In Proceedings of the IOP Conference Series: Materials Science and Engineering, Jakarta, Indonesia, 22–23 November 2018; p. 012098. [Google Scholar]
  57. Prabhu, P.; Fernandes, T.; Chaubey, P.; Kaur, P.; Narayanan, S.; Ramya, V.; Sawarkar, S.P. Mannose-conjugated chitosan nanoparticles for delivery of rifampicin to osteoarticular tuberculosis. Drug Deliv. Transl. Res. 2021, 11, 1509–1519. [Google Scholar] [CrossRef] [PubMed]
  58. George, M.; Mussone, P.G.; Bressler, D.C. Surface and thermal characterization of natural fibres treated with enzymes. Ind. Crops Prod. 2014, 53, 365–373. [Google Scholar] [CrossRef]
  59. Hossain, M.K.; Karim, M.R.; Chowdhury, M.R.; Imam, M.A.; Hosur, M.; Jeelani, S.; Farag, R. Comparative mechanical and thermal study of chemically treated and untreated single sugarcane fiber bundle. Ind. Crops Prod. 2014, 58, 78–90. [Google Scholar] [CrossRef]
  60. Syafri, E.; Kasim, A.; Abral, H.; Sulungbudi, G.T.; Sanjay, M.; Sari, N.H. Synthesis and characterization of cellulose nanofibers (CNF) ramie reinforced cassava starch hybrid composites. Int. J. Biol. Macromol. 2018, 120, 578–586. [Google Scholar] [CrossRef]
  61. Ray, D.P.; Banerjee, P.; Ghosh, R.K.; Nag, D. Accelerated retting of jute for economic fibre yield. Econ. Aff. 2015, 60, 693. [Google Scholar] [CrossRef]
  62. Ramesh, M. Kenaf (Hibiscus cannabinus L.) fibre based bio-materials: A review on processing and properties. Prog. Mater Sci. 2016, 78, 1–92. [Google Scholar] [CrossRef]
  63. Duchemin, B.; Thuault, A.; Vicente, A.; Rigaud, B.; Fernandez, C.; Eve, S. Ultrastructure of cellulose crystallites in flax textile fibres. Cellulose 2012, 19, 1837–1854. [Google Scholar] [CrossRef]
  64. Meijer, W.; Vertregt, N.; Rutgers, B.; van de Waart, M. The pectin content as a measure of the retting and rettability of flax. Ind. Crops Prod. 1995, 4, 273–284. [Google Scholar] [CrossRef]
  65. Sain, M.; Panthapulakkal, S. Bioprocess preparation of wheat straw fibers and their characterization. Ind. Crops Prod. 2006, 23, 1–8. [Google Scholar] [CrossRef]
  66. Mazian, B.; Bergeret, A.; Benezet, J.-C.; Malhautier, L. Influence of field retting duration on the biochemical, microstructural, thermal and mechanical properties of hemp fibres harvested at the beginning of flowering. Ind. Crops Prod. 2018, 116, 170–181. [Google Scholar] [CrossRef]
  67. Nayak, S.Y.; Heckadka, S.S.; Seth, A.; Prabhu, S.; Sharma, R.; Shenoy, K.R. Effect of chemical treatment on the physical and mechanical properties of flax fibers: A comparative assessment. Mater. Today Proc. 2021, 38, 2406–2410. [Google Scholar] [CrossRef]
  68. Abbass, A.; Paiva, M.C.; Oliveira, D.V.; Lourenço, P.B.; Fangueiro, R. Insight into the effects of solvent treatment of natural fibers prior to structural composite casting: Chemical, physical and mechanical evaluation. Fibers 2021, 9, 54. [Google Scholar] [CrossRef]
  69. Amel, B.A.; Paridah, M.T.; Sudin, R.; Anwar, U.; Hussein, A.S. Effect of fiber extraction methods on some properties of kenaf bast fiber. Ind. Crops Prod. 2013, 46, 117–123. [Google Scholar] [CrossRef]
  70. Kandemir, A.; Pozegic, T.R.; Hamerton, I.; Eichhorn, S.J.; Longana, M.L. Characterisation of natural fibres for sustainable discontinuous fibre composite materials. Materials 2020, 13, 2129. [Google Scholar] [CrossRef]
  71. Stamboulis, A.; Baillie, C.; Peijs, T. Effects of environmental conditions on mechanical and physical properties of flax fibers. Compos. Part Appl. Sci. Manuf. 2001, 32, 1105–1115. [Google Scholar] [CrossRef]
  72. Le Gall, M.; Davies, P.; Martin, N.; Baley, C. Recommended flax fibre density values for composite property predictions. Ind. Crops Prod. 2018, 114, 52–58. [Google Scholar] [CrossRef] [Green Version]
  73. Sawsen, C.; Fouzia, K.; Mohamed, B.; Moussa, G. Optimizing the formulation of flax fiber-reinforced cement composites. Constr. Build Mater. 2014, 54, 659–664. [Google Scholar] [CrossRef]
  74. Amiri, A.; Triplett, Z.; Moreira, A.; Brezinka, N.; Alcock, M.; Ulven, C.A. Standard density measurement method development for flax fiber. Ind. Crops Prod. 2017, 96, 196–202. [Google Scholar] [CrossRef]
  75. Kharine, A.; Manohar, S.; Seeton, R.; Kolkman, R.G.; Bolt, R.A.; Steenbergen, W.; de Mul, F.F. Poly (vinyl alcohol) gels for use as tissue phantoms in photoacoustic mammography. Phys. Med. Biol. 2003, 48, 357. [Google Scholar] [CrossRef] [PubMed]
  76. Alix, S.; Colasse, L.; Morvan, C.; Lebrun, L.; Marais, S. Pressure impact of autoclave treatment on water sorption and pectin composition of flax cellulosic-fibres. Carbohydr. Polym. 2014, 102, 21–29. [Google Scholar] [CrossRef] [PubMed]
  77. Martin, N.; Mouret, N.; Davies, P.; Baley, C. Influence of the degree of retting of flax fibers on the tensile properties of single fibers and short fiber/polypropylene composites. Ind. Crops Prod. 2013, 49, 755–767. [Google Scholar] [CrossRef] [Green Version]
  78. Marrot, L.; Lefeuvre, A.; Pontoire, B.; Bourmaud, A.; Baley, C. Analysis of the hemp fiber mechanical properties and their scattering (Fedora 17). Ind. Crops Prod. 2013, 51, 317–327. [Google Scholar] [CrossRef]
  79. Reddy, N.; Yang, Y. Properties and potential applications of natural cellulose fibers from cornhusks. Green Chem. 2005, 7, 190–195. [Google Scholar] [CrossRef]
  80. Sun, J.X.; Xu, F.; Sun, X.F.; Sun, R.C.; Wu, S.B. Comparative study of lignins from ultrasonic irradiated sugar-cane bagasse. Polym. Int. 2004, 53, 1711–1721. [Google Scholar] [CrossRef]
  81. Xu, Q.-Q.; Zhao, M.-J.; Yu, Z.-Z.; Yin, J.-Z.; Li, G.-M.; Zhen, M.-Y.; Zhang, Q.-Z. Enhancing enzymatic hydrolysis of corn cob, corn stover and sorghum stalk by dilute aqueous ammonia combined with ultrasonic pretreatment. Ind. Crops Prod. 2017, 109, 220–226. [Google Scholar] [CrossRef]
  82. Khandanlou, R.; Ahmad, M.B.; Shameli, K.; Hussein, M.Z.; Zainuddin, N.; Kalantari, K. Mechanical and thermal stability properties of modified rice straw fiber blend with polycaprolactone composite. J. Nanomater. 2014, 2014, 675258. [Google Scholar] [CrossRef]
  83. Komuraiah, A.; Kumar, N.S.; Prasad, B.D. Chemical composition of natural fibers and its influence on their mechanical properties. Mech. Compos. Mater. 2014, 50, 359–376. [Google Scholar] [CrossRef]
  84. Arnata, I.W.; Suprihatin, S.; Fahma, F.; Richana, N.; Sunarti, T.C. Cationic modification of nanocrystalline cellulose from sago fronds. Cellulose 2020, 27, 3121–3141. [Google Scholar] [CrossRef]
  85. Herlina Sari, N.; Wardana, I.N.G.; Irawan, Y.S.; Siswanto, E. Characterization of the Chemical, Physical, and Mechanical Properties of NaOH-treated Natural Cellulosic Fibers from Corn Husks. J. Nat. Fibers 2017, 15, 545–558. [Google Scholar] [CrossRef]
  86. Horikawa, Y.; Hirano, S.; Mihashi, A.; Kobayashi, Y.; Zhai, S.; Sugiyama, J. Prediction of lignin contents from infrared spectroscopy: Chemical digestion and lignin/biomass ratios of Cryptomeria japonica. Appl. Biochem. Biotechnol. 2019, 188, 1066–1076. [Google Scholar] [CrossRef]
  87. Boudjellal, A.; Trache, D.; Bekhouche, S.; Khimeche, K.; Razali, M.S.; Guettiche, D. Preparation and characterization of Alfa fibers/graphene nanoplatelets hybrid for advanced applications. Mater. Lett. 2021, 289, 129379. [Google Scholar] [CrossRef]
  88. Draman, S.F.S.; Daik, R.; Latif, F.A.; El-Sheikh, S.M. Characterization and thermal decomposition kinetics of kapok (Ceiba pentandra L.)–based cellulose. BioResources 2014, 9, 8–23. [Google Scholar] [CrossRef] [Green Version]
  89. Saravanakumar, S.; Kumaravel, A.; Nagarajan, T.; Moorthy, I.G. Effect of chemical treatments on physicochemical properties of Prosopis juliflora fibers. Int. J. Polym. Anal. Charact. 2014, 19, 383–390. [Google Scholar] [CrossRef]
  90. Begum, H.A.; Tanni, T.R.; Shahid, M.A. Analysis of Water Absorption of Different Natural Fibers. J. Text. Sci. Technol. 2021, 7, 152–160. [Google Scholar] [CrossRef]
  91. Poletto, M.; Júnior, H.L.O.; Zattera, A.J. Thermal decomposition of natural fibers: Kinetics and degradation mechanisms. React. Mech. Therm. Anal. Adv. Mater. 2015, 1, 515–545. [Google Scholar] [CrossRef]
  92. Angelini, L.G.; Scalabrelli, M.; Tavarini, S.; Cinelli, P.; Anguillesi, I.; Lazzeri, A. Ramie fibers in a comparison between chemical and microbiological retting proposed for application in biocomposites. Ind. Crops Prod. 2015, 75, 178–184. [Google Scholar] [CrossRef]
  93. Jankauskienė, Z.; Butkutė, B.; Gruzdevienė, E.; Cesevičienė, J.; Fernando, A.L. Chemical composition and physical properties of dew-and water-retted hemp fibers. Ind. Crops Prod. 2015, 75, 206–211. [Google Scholar] [CrossRef]
Polymers 15 00469 g001 550
Figure 1. Flowchart of retting and chemical-composition analysis.
Figure 1. Flowchart of retting and chemical-composition analysis.
Polymers 15 00469 g001
Polymers 15 00469 g002 550
Figure 2. Flowchart of the cellulose-extraction process.
Figure 2. Flowchart of the cellulose-extraction process.
Polymers 15 00469 g002
Polymers 15 00469 g003 550
Figure 3. (a) Retting water pH with stalk weight loss. (b) Retting water pH with stalk water absorption at different retting times.
Figure 3. (a) Retting water pH with stalk weight loss. (b) Retting water pH with stalk water absorption at different retting times.
Polymers 15 00469 g003
Polymers 15 00469 g004 550
Figure 4. Images of (a) under-, (b) optimally, and (c) over-retted fibers.
Figure 4. Images of (a) under-, (b) optimally, and (c) over-retted fibers.
Polymers 15 00469 g004
Polymers 15 00469 g005 550
Figure 5. Images of (a) non-retted, (b) retted, (c) dewaxed, (d) alkalized, and (e) bleached fibers.
Figure 5. Images of (a) non-retted, (b) retted, (c) dewaxed, (d) alkalized, and (e) bleached fibers.
Polymers 15 00469 g005
Polymers 15 00469 g006 550
Figure 6. The FTIR spectra of (a) non-retted, (b) retted, (c) dewaxed, (d) alkalized, and (e) bleached fibers.
Figure 6. The FTIR spectra of (a) non-retted, (b) retted, (c) dewaxed, (d) alkalized, and (e) bleached fibers.
Polymers 15 00469 g006
Polymers 15 00469 g007 550
Figure 7. TGA graphs of (a) raw, (b) dewaxed, (c) alkalized, and (d) bleached fibers.
Figure 7. TGA graphs of (a) raw, (b) dewaxed, (c) alkalized, and (d) bleached fibers.
Polymers 15 00469 g007
Table
Table 1. Sample names and corresponding retting-time durations.
Table 1. Sample names and corresponding retting-time durations.
SampleRT0RT1RT2RT3RT4RT5RT6RT7RT8
Retting Time (h)04896144168192216240264
Table
Table 2. Factors and levels of solvents for extraction processes.
Table 2. Factors and levels of solvents for extraction processes.
SolventFactors (Parameters)
Concentration (%)Temp. (°C)Time (h)
LevelLevelLevel
−10+1−10+1−10+1
C2H5OH:C7H85075100788898468
NaOH26105062.5751/211 & 1/2
H2O22610809010011 & 1/22
−1, 0, and +1 are levels related to low, medium, and high values of the selected extraction process variables, respectively.
Table
Table 3. Summary of the mean values of tensile and physical properties of fibers.
Table 3. Summary of the mean values of tensile and physical properties of fibers.
SampleTensile PropertiesPhysical Properties
Breaking
Force (cN)		Breaking
Elongation (%)		Tenacity
(cN/tex)		Diameter
(µm)		Density
(g/cm3)		Moisture
(%)
R0----1.339.34
R1219.92.1741.7128.221.438.57
R2278.42.0659.1104.651.528.32
R3193.41.7354.690.361.417.72
Table
Table 4. Chemical composition of lignocellulose biomasses from agricultural wastes.
Table 4. Chemical composition of lignocellulose biomasses from agricultural wastes.
Lignocellulose
Biomass		Cellulose
(%)		Hemicellulose
(%)		Lignin
(%)		Extractives
(%)		References
Linseed Straw682054This study
Oleaginous Flax 472421-[9]
Sugar Bagasse43.633.518.13.1[80]
Corn Cob4535155[81]
Corn Stover40251718[81]
Rice Straw38.331.618.811.3[82]
Table
Table 5. Experimental and predicted removals of non-cellulosic components of fiber.
Table 5. Experimental and predicted removals of non-cellulosic components of fiber.
RunVariablesResponse (%)
C (%)T (°C)t (h)Extractive RemovalHemicellulose RemovalLignin Removal
EXPPREDERREXPPREDERREXPPREDERR
1−1−1−12.522.400.1210.09.810.191.61.450.15
2−1002.673.88−1.2111.913.72−1.822.02.46−0.46
3−1+1+12.852.730.1213.713.420.282.62.63−0.03
40−104.543.980.5614.513.401.103.03.12−0.12
500+14.694.150.5416.215.460.744.03.400.60
60+1−14.904.350.5518.117.180.923.22.960.24
7+1−1+13.503.86−0.3614.414.85−0.453.63.71−0.11
8+10−13.654.00−0.3515.315.84−0.543.83.730.07
9+1+103.834.18−0.3517.818.16−0.363.43.69−0.29
Table
Table 6. Sources of FTIR peaks and their assignments [1,84,86,87].
Table 6. Sources of FTIR peaks and their assignments [1,84,86,87].
Wavenumber
(cm−1)		BondVibrationSources
3425O-HStretchingCellulose, hemicellulose, lignin, and pectin
2917C-H, C-H2StretchingCellulose, hemicellulose, lignin, pectin, wax, and fat
2853C-H2Symmetric StretchingWax
1731C=OUnconjugatedHemicellulose and lignin
1636O-HStretchingAbsorbed water
1426O-H, C-HBendingCellulose, hemicellulose, and lignin
1383COO-StretchingHemicellulose
1157C-O-CAsymmetric StretchingCellulose, hemicellulose, and lignin
1114C-OStretchingCellulose, hemicellulose, and pectin
1032C-O-CBendingCellulose, hemicellulose, pectin, wax, and fat
901C-O-CStretchingCellulose and hemicellulose
617C-OHOut-of-Plane BendingCellulose
Table
Table 7. Thermogravimetric analysis of fibers at different extraction steps.
Table 7. Thermogravimetric analysis of fibers at different extraction steps.
Sample1st Stage2nd Stage3rd StageAsh (%)
Wt. Loss (%)T (°C)Wt. Loss (%)T (°C)Wt. Loss (%)T (°C)
Raw Fiber 11.3626–14556.26179–42628.46426–6093.00
Extracted Fiber 7.5137–13970.45205–43818.79430–5102.25
Alkalized Fiber 7.4438–12157.20250–44030.69440–5911.72
Bleached Fiber 23.5037–11049.89269–42722.55427–5101.13
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Feleke, K.; Thothadri, G.; Beri Tufa, H.; Rajhi, A.A.; Ahmed, G.M.S. Extraction and Characterization of Fiber and Cellulose from Ethiopian Linseed Straw: Determination of Retting Period and Optimization of Multi-Step Alkaline Peroxide Process. Polymers 2023, 15, 469. https://doi.org/10.3390/polym15020469

AMA Style

Feleke K, Thothadri G, Beri Tufa H, Rajhi AA, Ahmed GMS. Extraction and Characterization of Fiber and Cellulose from Ethiopian Linseed Straw: Determination of Retting Period and Optimization of Multi-Step Alkaline Peroxide Process. Polymers. 2023; 15(2):469. https://doi.org/10.3390/polym15020469

Chicago/Turabian Style

Feleke, Kibrom, Ganesh Thothadri, Habtamu Beri Tufa, Ali A. Rajhi, and Gulam Mohammed Sayeed Ahmed. 2023. "Extraction and Characterization of Fiber and Cellulose from Ethiopian Linseed Straw: Determination of Retting Period and Optimization of Multi-Step Alkaline Peroxide Process" Polymers 15, no. 2: 469. https://doi.org/10.3390/polym15020469

APA Style

Feleke, K., Thothadri, G., Beri Tufa, H., Rajhi, A. A., & Ahmed, G. M. S. (2023). Extraction and Characterization of Fiber and Cellulose from Ethiopian Linseed Straw: Determination of Retting Period and Optimization of Multi-Step Alkaline Peroxide Process. Polymers, 15(2), 469. https://doi.org/10.3390/polym15020469

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop