Next Article in Journal
Optical and Physical Applications of Photocontrollable Materials: Azobenzene-Containing and Liquid Crystalline Polymers
Next Article in Special Issue
Temperature-Responsive Polymer Modified Surface for Cell Sheet Engineering
Previous Article in Journal
Preparation and Applications of Amylose Supramolecules by Means of Phosphorylase-Catalyzed Enzymatic Polymerization
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 4
Issue 1
10.3390/polym4010134
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Color-Tunable Etalons Assembled from Poly (N-Isopropylacrylamide) Based Microgels

by
Liang Hu
and
Michael J. Serpe
*
Department of Chemistry, University of Alberta, Edmonton, AB, T6G 2G2, Canada
*
Author to whom correspondence should be addressed.
Polymers 2012, 4(1), 134-149; https://doi.org/10.3390/polym4010134
Submission received: 18 November 2011 / Revised: 21 December 2011 / Accepted: 5 January 2012 / Published: 9 January 2012
(This article belongs to the Special Issue Stimuli-Responsive Polymers and Colloids)
Browse Figures
Versions Notes

Abstract

:
Photonic materials (PMs) that are capable of manipulating and controlling light in systems have immense potential for the computing and communications industries. These materials are formed by assembling components of differing refractive indices in a periodic array. Light then interacts with this assembly, which results in constructive and destructive interference, and hence color. While many three-dimensional PMs have been reported, and have the most potential for the applications mentioned above, one-dimensional PMs have a multitude of potential uses, e.g., light filtration. In this review, we focus on one-dimensional PMs; specifically poly (N-isopropylacrylamide) microgel based etalons. The etalons can be fabricated to exhibit a single bright color, and because the diameter of the microgels is dependent on temperature and pH, the mirror-mirror spacing can be dynamically tuned; therefore the etalon’s color is dynamically tunable.

Graphical Abstract

1. Introduction

Historically, photonic materials such as the natural opal, and butterfly wings have attracted much attention due to their beautiful colors. More recently, photonic materials have gained considerable interest due to their ability to manipulate and control the flow of light in systems, which could have a great impact on the computing and communications industries [1]. Their interesting properties, whether beautiful color or manipulation of light, are a result of refractive index/dielectric periodicity at the length scale of the wavelength of light striking the material, and not due to the addition of dyes or pigments to the materials [2,3,4]. For instance, opal gemstones have refractive index order periodicity in three dimensions (3D). Materials can also have structural periodicity in two dimensions (2D) and one dimension (1D), all of which yield their own interesting optical properties and colors.
Important to this submission, are 1D optical materials. For example, Bragg mirrors are generally composed of layers of alternating refractive index, which are periodically arranged in only one dimension; the reflected/refracted light at the interface of each layer leads to constructive/destructive interference, resulting in color. However, other 1D optical materials, such as Fabry-Pérot etalons, interferometers, and waveguides exist. While they are similar to Bragg stacks in that they are ordered in 1D, they are more specifically composed of a dielectric cavity confined between two reflective surfaces. An example of a typical Fabry-Pérot etalon (or simply etalon) is shown schematically in Figure 1(A). Light enters the etalon, and resonates in the cavity between the mirrors, resulting in light interference. This interference yields specific wavelengths of light that are reflected/transmitted. The material will appear visibly colored if the distance between the mirrors, or the refractive index of the dielectric, is such that visible light wavelengths are reflected. The specific wavelengths that are reflected/transmitted can be predicted from the following equation:
Polymers 04 00134 i001
where λ is the wavelength maximum of the peak (s), m is the peak order, n is the refractive index of the dielectric, d is the spacing between the mirrors, and θ is the angle of incidence [5].
Polymers 04 00134 g001 1024
Figure 1. (A) A traditional Fabry-Pérot etalon; (B) poly (N-isopropylacrylamide) based microgel etalons depicting (a,c) two reflective Au surfaces sandwiching (b) a microgel layer, all on (d) a cover glass support. Reproduced with permission from [15] Copyright (2011) WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Figure 1. (A) A traditional Fabry-Pérot etalon; (B) poly (N-isopropylacrylamide) based microgel etalons depicting (a,c) two reflective Au surfaces sandwiching (b) a microgel layer, all on (d) a cover glass support. Reproduced with permission from [15] Copyright (2011) WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Polymers 04 00134 g001
Our group fabricates etalons by sandwiching poly (N-isopropylacrylamide) (pNIPAm) microgels (colloidally stable hydrogel particles) between two thin metal planar surfaces, as in Figure 1(B). PNIPAm is one of the most well-known and studied “intelligent” polymers, which exhibits unique thermoresponsivity. That is, at room temperature, pNIPAm is in a random coil conformation, while it transitions to a globular conformation when heated >~31 °C. This process is accompanied by water expulsion from the polymer. This transition is fully reversible, so when the pNIPAm is returned to T < ~31 °C, the polymer transitions back to the random coil conformation and is resolvated with water. These unique properties of pNIPAm have been used to synthesize a variety of colloidally stable particles, also referred to as microgels/nanogels. Like linear pNIPAm, when the temperature of pNIPAm based microgels is raised above ~31 °C, they deswell by expelling their solvating water, and reswell by absorbing water below ~31 °C. The addition of comonomers to the pNIPAm based microgels can influence their responsivity, e.g., acrylic acid (AAc) is commonly added to pNIPAm based microgels to impart them with pH responsivity, and also to serve as a reactive group for further modification of the microgels [6,7,8,9]. AAc has a pKa of ~4.25, so when pNIPAm-co-AAc microgels are at a pH above the pKa for AAc the collapse transition is hindered due to Coulombic repulsion between the deprotonated AAc in the microgels. Interestingly, full thermoresponsivity can be recovered by simply lowering the pH to a value below 4.25. Additionally, pNIPAm based microgels can also be made responsive to ionic strength, glucose [10], protein binding [11], and DNA hybridization by introduction of various comonomers. Although pNIPAm based microgels can be modified to affect a myriad of material properties and functions, the most important aspect for the work here is their potential to tune “lattice” spacing and color in ordered materials, as in Figure 1(B) [12,13,14,15].
Previously, pNIPAm based microgels have been used to construct “colored” photonic materials. The Lyon group and others have made significant progress in developing pNIPAm microgel based colloidal crystals [16,17,18,19]. They found that the spacing between the microgels had a profound effect on the reflected light wavelength, and thus the resultant color. The Lyon group has also made significant strides to understand and characterize the assembly process [20,21,22,23,24]. The Kawaguchi group showed that by simply drying microgel suspensions of various concentrations on substrates, a photonic material could be generated; the concentration of the microgel suspension could control the resultant particle-particle spacing, and thus change the overall optical properties of the thin film [4]. Enlightened by Kawaguchi’s work, other researchers used capillary forces [25,26], the environment [27] and nature of the particle [28,29], and the surface chemistry [30] to control the spacing and color of the resultant films. Subsequent work has further expanded this knowledge to include an understanding of the effect of temperature [31,32], charge or magnetic field [33,34], pH [35], and hydrophobic/hydrophilic interactions [36] on the formation of microgel films and their optical properties.
In this submission, we show that pNIPAm microgel based etalons can be fabricated to exhibit a single bright color [12,13,15], and because the microgels exhibit a diameter that is dependent on temperature and pH, the mirror-mirror spacing can be dynamically tuned resulting in color tunability based on Equation (1). For these systems, it is known that the mirror-mirror distance dominates the etalon’s optical properties. These devices have been shown to be extremely sensitive to temperature, shifting >300 nm spectrally in response to an increase in temperature of ~15 °C, with the majority of the shift occurring over ~7 °C. This high sensitivity makes these devices excellent prospects for optical sensing applications. The rest of the submission is focused on microgel based etalons.

2. PNIPAm Microgel Based Etalons

Initial studies of pNIPAm microgel based etalons in our group began by drying a 775 µL of a 5% (v/v) solution of ~1.5 µm diameter pNIPAm-co-AAc microgels onto a Au coated glass cover slip (2 nm Cr was used as an adhesion layer followed by 15 nm Au). To make an etalon, a subsequent 2 nm Cr/15 nm Au overlayer was deposited on the initial microgel layer, a photograph of the etalon in air is shown in Figure 2(a). Figure 2(b,c) show differential interference microscopy (DIC) images of the resultant microgel film in Figure 2(a), prior to the Cr/Au overlayer addition. As seen from Figure 2(a–c), the film’s color and microgel packing density is nonuniform across the etalon surface, which is most likely due to the low concentration of the microgel solution being used to make the etalons, resulting in the so-called “coffee-ring effect” [37,38]. More concentrated microgel solutions were dried onto Au, but complete uniformity was never achieved with this approach.
Polymers 04 00134 g002 1024
Figure 2. Photographs and differential interference microscopy (DIC) images of films fabricated using (a) the drying method and corresponding DIC images of an area that is an (b) etalon corresponding to the solid circle in (a) and an area that (c) is not an etalon corresponding to the dashed circle in (a). (d) A photograph of a film fabricated using the “paint-on” method and the corresponding (e) DIC image of the film. DIC images were taken using a 100x oil immersion objective before the addition of Cr/Au overlayer, scale bars are 5 µm. Scale bars in the photographs are 5 mm. Reprinted with permission from [13] Copyright (2011) American Chemical Society.
Figure 2. Photographs and differential interference microscopy (DIC) images of films fabricated using (a) the drying method and corresponding DIC images of an area that is an (b) etalon corresponding to the solid circle in (a) and an area that (c) is not an etalon corresponding to the dashed circle in (a). (d) A photograph of a film fabricated using the “paint-on” method and the corresponding (e) DIC image of the film. DIC images were taken using a 100x oil immersion objective before the addition of Cr/Au overlayer, scale bars are 5 µm. Scale bars in the photographs are 5 mm. Reprinted with permission from [13] Copyright (2011) American Chemical Society.
Polymers 04 00134 g002
To overcome the coffee-ring effect we developed a novel microgel deposition technique, which involves “painting” microgels onto a metal substrate [12,13,14]. As illustrated in Scheme 1, concentrated microgels are continuously spread onto an annealed, clean, Au coated glass substrate until the layer is completely dry. Once completely dry, the film is rinsed with deionized water and soaked in a deionized water bath overnight at ~30 °C, in order to remove any microgels not directly bound to the Au substrate. Compared to the air dried films, this technique yields an extremely uniform etalon both visually, and microscopically, as can be seen in Figure 2(d,e).
Polymers 04 00134 g012 1024
Scheme 1. The “Paint-on” method used to fabricate etalons. Reprinted with permission from [13] Copyright (2011) American Chemical Society.
Scheme 1. The “Paint-on” method used to fabricate etalons. Reprinted with permission from [13] Copyright (2011) American Chemical Society.
Polymers 04 00134 g012
The spectral quality of the “painted” etalons is far superior to the air dried films, as determined by collecting reflectance spectra on random locations of the solvated etalon. Figure 3(a) shows spectra obtained at three randomly selected regions of a “painted” etalon; we can note that from spot to spot the spectra were comparable. However, the reflectance spectra for the same microgels using air-dried method were much more variable with position being probed on the etalon (Figure 3(b)). Moreover, one out of four randomly chosen regions did not exhibit reflectance spectra because that region did not have the required “monolithic” microgel layer required to form the optical cavity of the etalon.
The homogeneity of the response of the painted and air-dried etalons to temperature was also compared, Figure 3(c,d). Three random spots of the respective etalons were probed as a function of temperature, and it was observed that the regions of the painted etalon exhibit similar λmax values at all temperatures, while the air-dried regions were far less uniform from spot to spot. Therefore, the “paint-on” method is clearly superior to the drying protocol. This technique has also been used to deposit microgels containing various functionalities on Au, as well as to deposit microgels on a variety of metals including: Ti, Ni, Al, Fe, Ag, Cu (data not shown).
Polymers 04 00134 g003 1024
Figure 3. Reflectance spectra from three randomly selected areas of an etalon fabricated using the (a) “Paint-on” method and the (b) overnight drying method. Plots of λmax versus temperature for randomly selected regions (the three different regions in the spectra in (a,b) of films fabricated using the (c) “Paint-on” method and the (d) overnight drying method. All data were collected for in pH 3 water (I.S. = 1) solution. Reprinted with permission from [13] Copyright (2011) American Chemical Society.
Figure 3. Reflectance spectra from three randomly selected areas of an etalon fabricated using the (a) “Paint-on” method and the (b) overnight drying method. Plots of λmax versus temperature for randomly selected regions (the three different regions in the spectra in (a,b) of films fabricated using the (c) “Paint-on” method and the (d) overnight drying method. All data were collected for in pH 3 water (I.S. = 1) solution. Reprinted with permission from [13] Copyright (2011) American Chemical Society.
Polymers 04 00134 g003
As can be observed visually, the color of the painted etalon is uniform. While the spectra from spot-to-spot are reproducible, each spectrum exhibits multiple peaks at various wavelengths for a given n and d. These multiple peaks make prediction of the spectral and visible color difficult. For our future sensing efforts, we would like etalons that exhibit a single reflectance peak in the visible region of the spectrum. This will allow the desired device color and spectrum to be pre-decided and microgels rationally chosen such that the desired etalon can be fabricated. To fabricate etalons that exhibit single peaks in the visible spectral region, Equation (1) predicts that microgels with the correct combination of refractive index and diameter are needed. For example, large diameter microgels should lead to multiple reflectance peaks, while the opposite is true for microgels with a small diameter. To test this, microgels with various hydrodynamic diameters (DH) were synthesized and used to paint on Au coated substrates to yield etalons with variable dielectric thicknesses, see Table 1.
Table
Table 1. Physical properties of microgels.
Table 1. Physical properties of microgels.
MicrogelpNIPAm-co-AAc-1pNIPAm-co-AAc-2pNIPAm-co-AAc-3pNIPAm-co-AAm[c]pNIPAm-co-VAA[d]
Hydrodynamic diameter, DH [nm] [a]1,548 (±69)659 (±21)229 (±10)653 (±10)603 (±17)
Etalon thickness [nm] [b]1,004 (±98)440 (±36)127 (±16)544 (±56)347 (±46)
[a] Determined by photon correlation spectroscopy (±standard deviation of 5 measurements). [b] Determined by AFM imaging (±standard deviation of height over 100 line scan averages on three areas each for three images). [c] AAm is acrylamide. [d] VAA is vinylacetic acid.
Polymers 04 00134 g004 1024
Figure 4. Representative spectra for etalons composed of (a) pNIPAm-co-AAc-1, (b) pNIPAm-co-AAm, (c) pNIPAm-co-AAc-2, (d) pNIPAm-co-VAA, (e) pNIPAm-co-AAc-3 microgels (see Table 1), obtained in pH 3 formate buffer. The average peak position (± one standard deviation) from six spectra is shown in red above each spectrum. (f–j) Photographs for etalons in the dry state, and (k-o) hydrated in pH 3 formate buffer. The photographs are of the same etalons that exhibited the spectra in (a–e). Scale bars for photographs are 5 mm. Reproduced with permission from [12] Copyright (2011) WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Figure 4. Representative spectra for etalons composed of (a) pNIPAm-co-AAc-1, (b) pNIPAm-co-AAm, (c) pNIPAm-co-AAc-2, (d) pNIPAm-co-VAA, (e) pNIPAm-co-AAc-3 microgels (see Table 1), obtained in pH 3 formate buffer. The average peak position (± one standard deviation) from six spectra is shown in red above each spectrum. (f–j) Photographs for etalons in the dry state, and (k-o) hydrated in pH 3 formate buffer. The photographs are of the same etalons that exhibited the spectra in (a–e). Scale bars for photographs are 5 mm. Reproduced with permission from [12] Copyright (2011) WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Polymers 04 00134 g004
If we use a refractive index of 1.37 for a solvent swollen pNIPAm-co-AAc microgel, from Equation (1) the dielectric layer thickness should be less than 400 nm to achieve a single reflectance peak in the visible. From the data in Figure 4, we find that the number of the distinct peaks in the visible region of the reflectance spectra decrease with decreasing DH. Specifically, etalons which were constructed from microgels with a DH of ~230 nm yielded only 1 distinct peak at ~535 nm. From these data, it is apparent that slightly larger microgels would yield a slightly red-shifted reflectance peak, and vice versa. We went on to illustrate that microgels of a similar DH, but different mechanical properties, could also affect the number of reflectance peaks observed. Table 1 shows that “soft” microgels yielded an etalon with a smaller dielectric thickness compared to “stiff” microgels, even though the initial DH values were very similar. Stiffness was inferred by comparing the initial hydrodynamic diameter of the microgels to the AFM measured etalon thickness. Stiffer microgels yield a dielectric thickness that is close to their hydrodynamic diameter, while softer microgels yield a dielectric thickness much smaller than their hydrodynamic diameter.
In addition to determining the factors that control the optical properties of the etalons, the group is investigating what controls the deswelling rate of the etalons. To study this, we exploit the variable collapse transition temperature of the microgels in water with varying solvent concentrations—a phenomenon referred to as cononsolvency [39,40,41,42,43].
Specifically, the etalons were equilibrated in water at 25 °C (pH 3.0, ionic strength 2 mM). Following equilibration, methanol (MeOH) was added to bring the concentration to 30% (v/v) MeOH:H2O. Because of “cononsolvency”, the microgel’s collapse transition is lowered to ~18 °C and thus the microgels instantly collapse and the Au mirrors come close to each other, resulting in a spectral blue shift of a given reflectance peak, according to Equation (1). The shifts were monitored over time, for etalons with various overlayer thicknesses. To reduce any error caused by different absolute shifts in wavelength for different etalons, the percentage shift (% Shift) at a particular time was calculated using Equation (2):
Polymers 04 00134 i002
λmax is the wavelength of the monitored peak at a particular time point, λinitial is the initial peak position, and λfinal is the final peak position.
For this section, λmax was always the highest wavelength peak in each spectrum. Since the etalons were fabricated with the same microgels, and by the same “paint-on” method, the highest wavelength peaks in each etalon’s spectrum is assumed to be the same order of reflection, therefore they can all be directly compared.
From Figure 5 and Figure 6, it is apparent that the deswelling time increases as the overlayer thickness increases. For our system, we hypothesize that thicker Au overlayers have less pores than etalons with thin Au overlayers. Therefore, the exchange through the thinner layers is much easier, hence leading to faster kinetics. This hypothesis is also supported by the work of Norrman et al., [44] who observed that thick Au overlayers on glass have more surface coverage than thin Au layers. Furthermore, we observed that the rate of MeOH entering the etalon, via diffusion through the Au overlayer or the edges, increases as a function of increasing overlayer thickness. As the overlayer thickness increases, the etalon requires more time to initially respond to the introduction of MeOH.
Polymers 04 00134 g005 1024
Figure 5. Deswelling curves for two different sets of etalons (a,b), made of the same microgels, using the same painting method. The percent shift of the high wavelength peak in the reflectance spectrum is plotted as a function of time. Plots shown are: 5 nm (− · · −), 10 nm (− − −), 15 nm (···), 20 nm (solid), 25 nm (− · −), and 35 nm (— - —). Deswelling was induced by introducing a 30% (v/v) MeOH/water solution (2 mM I.S.) held at 25 °C. Reprinted with permission from [14] Copyright (2011) American Chemical Society.
Figure 5. Deswelling curves for two different sets of etalons (a,b), made of the same microgels, using the same painting method. The percent shift of the high wavelength peak in the reflectance spectrum is plotted as a function of time. Plots shown are: 5 nm (− · · −), 10 nm (− − −), 15 nm (···), 20 nm (solid), 25 nm (− · −), and 35 nm (— - —). Deswelling was induced by introducing a 30% (v/v) MeOH/water solution (2 mM I.S.) held at 25 °C. Reprinted with permission from [14] Copyright (2011) American Chemical Society.
Polymers 04 00134 g005
Polymers 04 00134 g006 1024
Figure 6. The time required for etalons of various overlayer thicknesses to reach 100% deswollen. Error bars are the standard deviations for the averages from two different sets of independently fabricated samples. Reprinted with permission from [14] Copyright (2011) American Chemical Society.
Figure 6. The time required for etalons of various overlayer thicknesses to reach 100% deswollen. Error bars are the standard deviations for the averages from two different sets of independently fabricated samples. Reprinted with permission from [14] Copyright (2011) American Chemical Society.
Polymers 04 00134 g006
Figure 6 shows the time required for etalons of various overlayer thickness to reach 100% deswollen, and reveals that the thinnest Au overlayer (5 nm) requires less time to reach 100% deswollen than any other film. Furthermore, the trend of increasing deswelling time with increasing overlayer thickness is observed. By defining the slope of the line in the deswelling phase as the maximum deswelling rate, in units of % shift per second (s−1), we see that the thinnest Au overlayers have greater max rates than thicker overlayers, again both suggesting the thin Au overlayers allow solvent to more easily exchange with the environment (Figure 7). Therefore, we assume that the preferred route of solvent exchange with the microgel layer is through the overlayer, although diffusion out of the side of the unsealed etalon can also occur.
Polymers 04 00134 g007 1024
Figure 7. Plot of maximum rate of deswelling for etalons with different overlayer thicknesses. Data averaged from two sets of independently fabricated etalons, with standard deviation shown using error bars. Reprinted with permission from [14] Copyright (2011) American Chemical Society.
Figure 7. Plot of maximum rate of deswelling for etalons with different overlayer thicknesses. Data averaged from two sets of independently fabricated etalons, with standard deviation shown using error bars. Reprinted with permission from [14] Copyright (2011) American Chemical Society.
Polymers 04 00134 g007
However, from the above data, we cannot conclude that solvent exchange occurs exclusively through the Au overlayer. That is because the sides of the etalon are not sealed, and therefore there is some possibility of solvent exchanging through the sides. To investigate this further, we observed the deswelling kinetics for etalons of varying dimensions. If solvent is exchanging through the sides of the etalon, then the time required for the etalon to completely deswell should decrease as the etalon’s dimensions decrease. To investigate this, a 6.25 cm2 (2.5 cm × 2.5 cm) etalon with a 25 nm Au overlayer was deswollen. The kinetics of this larger etalon was compared to a smaller etalon cut from the larger one (with a glass cutting tool), with an area of ~2.5 cm2 (~1.0 cm × ~2.5 cm), followed by further cutting this etalon down to ~0.9 cm2 (~0.9 cm × ~1.0 cm). The resultant deswelling curves probed at the same region (center of the etalon) are shown in Figure 8. It is apparent that when the etalon becomes smaller, it reaches 100% deswollen faster. Also, the lag phase for the smallest etalon is reduced. This behavior is hypothesized to be due to solvent exchange through the edges of the etalon, therefore requiring less distance for the solvent to diffuse out of the etalon before the microgels can fully contract, and change the etalon’s color. Our conclusion from all the kinetics observed above is that solvent preferentially exits the microgel dielectric layer through the Au overlayer, but more solvent exchanges through the sides when the overlayer thickness increases.
Polymers 04 00134 g008 1024
Figure 8. Plot of percent shift as a function of time for etalons with 25 nm overlayers and areas of (solid) 6.25 cm2, (···) ~2.5 cm2, and (− − −) ~0.9 cm2. Reprinted with permission from [14] Copyright (2011) American Chemical Society.
Figure 8. Plot of percent shift as a function of time for etalons with 25 nm overlayers and areas of (solid) 6.25 cm2, (···) ~2.5 cm2, and (− − −) ~0.9 cm2. Reprinted with permission from [14] Copyright (2011) American Chemical Society.
Polymers 04 00134 g008
Fast deswelling kinetics will be useful to the group, especially for our efforts with developing point-of-care (POC) diagnostics. To demonstrate the etalons potential for sensing applications, glucose sensitive microgels were synthesized by modification with of AAc modified pNIPAm based microgels with 3-aminophenylboronic acid (APBA). It is well known that APBA modified microgels increase their diameter in the presence of glucose [45,46]. Etalons were fabricated from the APBA modified microgels, and their spectral properties in the absence and presence of glucose were monitored. We exposed them to a 3 mg/mL solution of glucose in pH 9 carbonate buffer and monitored one reflection peak over time. From Figure 9(a), we see a ~134 nm spectral shift in the most red-shifted peak from 856 nm to 990 nm. As seen in Figure 9(b), the majority of the spectral shift occurs within 30 min of glucose introduction. Interestingly, the visual color of the APBA modified microgel based etalons varied after glucose introduction from green to red (Figure 10), which can allow us to read “diagnostic test” results visibly. Finally, we investigated if spatially isolated regions of a single etalon are capable of actuating independently. If so, the color of a single etalon can be changed in one area, without affecting the color of the etalon in another region. Etalons in this study were fabricated from pNIPAm-co-AAc microgels using the “paint-on” method. The experiment was conducted by locating three reflectance probes at different spots on a single etalon. pH 3.0, 4.0, 7.0 solutions were added between the reflectance probes and the etalon, and the reflectance spectra for the different spots collected as a function of temperature. From the data in Figure 11, it is apparent that the peak (~800 nm) significantly blue-shifts with increasing temperature, while the spots at pH 4.0 and 7.0 shift minimally over the same temperature range. This will be used by our group to develop biosensors for disease detection and environmental monitoring.
Polymers 04 00134 g009 1024
Figure 9. (a) Reflectance spectra over time after introduction of a 3 mg/mL glucose solution to an etalon constructed with APBA modified microgels. The black line represents the initial spectrum, the red, blue, yellow, and green lines represent the spectrum after 15, 30, 60, and 120 min respectively. (b) Plot of the high wavelength peak position in (a) as a function of time after glucose addition. Total spectral shift is ~134 nm.
Figure 9. (a) Reflectance spectra over time after introduction of a 3 mg/mL glucose solution to an etalon constructed with APBA modified microgels. The black line represents the initial spectrum, the red, blue, yellow, and green lines represent the spectrum after 15, 30, 60, and 120 min respectively. (b) Plot of the high wavelength peak position in (a) as a function of time after glucose addition. Total spectral shift is ~134 nm.
Polymers 04 00134 g009
Polymers 04 00134 g010 1024
Figure 10. APBA-functionalized microgel etalons show visible color differences when they are soaked in (a) 5 mM pH 9 carbonate buffer versus (b) a pH 9 carbonate buffer containing 3 mg/mL glucose for 2 hours. Various etalon controls, e.g., (c,d) etalons fabricated by exposure to APBA only, and (e,f) EDC only, show no significant color change (c, e) before and (d, f) after glucose exposure. Image insets show a cropped image of the approximate center ~1 cm2 for each etalon, where the etalons were monitored spectrally, to better display the color change. Note, the color intensity (not the color) was increased in the inset. Scale bars are ~5 mm.
Figure 10. APBA-functionalized microgel etalons show visible color differences when they are soaked in (a) 5 mM pH 9 carbonate buffer versus (b) a pH 9 carbonate buffer containing 3 mg/mL glucose for 2 hours. Various etalon controls, e.g., (c,d) etalons fabricated by exposure to APBA only, and (e,f) EDC only, show no significant color change (c, e) before and (d, f) after glucose exposure. Image insets show a cropped image of the approximate center ~1 cm2 for each etalon, where the etalons were monitored spectrally, to better display the color change. Note, the color intensity (not the color) was increased in the inset. Scale bars are ~5 mm.
Polymers 04 00134 g010
Polymers 04 00134 g011 1024
Figure 11. Optical properties of an etalon fabricated from pNIPAm-co-AAc microgels. Reflectance spectra for the etalon as a function of temperature at different spots (a) pH 3.0 (b) pH 4.0 (c) pH 7.0.
Figure 11. Optical properties of an etalon fabricated from pNIPAm-co-AAc microgels. Reflectance spectra for the etalon as a function of temperature at different spots (a) pH 3.0 (b) pH 4.0 (c) pH 7.0.
Polymers 04 00134 g011

3. Conclusions and Future Directions

PNIPAm microgel based etalons have been successfully fabricated, and show color tunability that mirrors the thermoresponsivity of the microgels they are assembled from. The assemblies are robust, and have been shown to be successfully fabricated from microgels with a variety of functionalities, on various metal surfaces utilizing the “paint-on” protocol. The number and order of the peaks observed in the reflectance spectra can be rationally tuned by changing the diameter of the microgels that are painted. We went on to show that the deswelling kinetics of the microgel etalons depend on Au overlayer thickness, which lead us to our hypothesis that solvent exchanges through the sides and the top of the etalon. However, the route of exchange through the Au overlayer is preferred. PNIPAM based etalons can be made to respond to biologically relevant concentrations of glucose, changing color considerably within 30 min of introduction of the APBA modified pNIPAm based microgel etalons to biologically relevant concentrations of glucose. Finally, we have demonstrated that pNIPAm microgel based etalons respond to the temperature and pH independently on spatially isolated regions of a single etalon.
PNIPAm microgel based photonic materials, specifically etalons, have a promising future, ranging from light filtration applications to POC sensing. By combining these properties with flexible substrates, these etalons can potentially transform display technology. The optical properties, combined with their ease of fabrication, cost effectiveness, and sensitivity make them extremely appealing.

Acknowledgements

M.J.S. acknowledges funding from the University of Alberta (the Department of Chemistry and the Faculty of Science) the Natural Science and Engineering Research Council (NSERC), the Canada Foundation for Innovation (CFI), and the Alberta Advanced Education & Technology Small Equipment Grants Program (AET/SEGP). LH would like to thank the China Scholarship Council (CSC) for financial support.

References

  1. Wang, J.X.; Zhang, Y.Z.; Wang, S.T.; Song, Y.L.; Jiang, L. Bioinspired colloidal photonic crystals with controllable wettability. Account. Chem. Res. 2011, 44, 405–415. [Google Scholar] [CrossRef]
  2. Bonifacio, L.D.; Lotsch, B.V.; Puzzo, D.P.; Scotognella, F.; Ozin, G.A. Stacking the nanochemistry deck: Structural and compositional diversity in one-dimensional photonic crystals. Adv. Mater. 2009, 21, 1641–1646. [Google Scholar] [CrossRef]
  3. Krieger, I.M.; Oneill, F.M. Diffraction of light by arrays of colloidal spheres. J. Am. Chem. Soc. 1968, 90, 3114–3120. [Google Scholar] [CrossRef]
  4. Tsuji, S.; Kawaguchi, H. Colored thin films prepared from hydrogel microspheres. Langmuir 2005, 21, 8439–8442. [Google Scholar] [CrossRef]
  5. Brooker, G. Modern Classical Optics; Oxford University Press: Oxford, UK, 2003. [Google Scholar]
  6. Jones, C.D.; Lyon, L.A. Synthesis and characterization of multiresponsive core-shell microgels. Macromolecules 2000, 33, 8301–8306. [Google Scholar] [CrossRef]
  7. Kratz, K.; Hellweg, T.; Eimer, W. Effect of connectivity and charge density on the swelling and local structural and dynamic properties of colloidal PNIPAM microgels. Ber. Bunsen. Phys. Chem. 1998, 102, 1603–1608. [Google Scholar]
  8. Kratz, K.; Hellweg, T.; Eimer, W. Influence of charge density on the swelling of colloidal poly(N-isopropylacrylamide-co-acrylic acid) microgels. Colloid. Surface. A 2000, 170, 137–149. [Google Scholar] [CrossRef]
  9. Snowden, M.J.; Chowdhry, B.Z.; Vincent, B.; Morris, G.E. Colloidal copolymer microgels of N-isopropylacrylamide and acrylic acid: pH, ionic strength and temperature effects. J. Chem. Soc. Fara. Trans. 1996, 92, 5013–5016. [Google Scholar] [CrossRef]
  10. Hoare, T.; Pelton, R. Engineering glucose swelling responses in poly(N-isopropylacrylamide)-based microgels. Macromolecules 2007, 40, 670–678. [Google Scholar] [CrossRef]
  11. Kim, J.; Singh, N.; Lyon, L.A. Influence of ancillary binding and nonspecific adsorption on bioresponsive hydrogel microlenses. Biomacromolecules 2007, 8, 1157–1161. [Google Scholar] [CrossRef]
  12. Sorrell, C.D.; Serpe, M.J. Reflection order selectivity of color-tunable poly(N-isopropylacrylamide) microgel based etalons. Adv. Mater. 2011, 23, 4088–4092. [Google Scholar] [CrossRef]
  13. Sorrell, C.D.; Carter, M.C.D.; Serpe, M.J. A “paint-on” protocol for the facile assembly of uniform microgel coatings for color tunable etalon fabrication. ACS Appl. Mater. Interfaces 2011, 3, 1140–1147. [Google Scholar] [CrossRef]
  14. Carter, M.C.D.; Sorrell, C.D.; Serpe, M.J. Deswelling kinetics of color tunable poly (N-isopropylacrylamide) microgel-based Etalons. J. Phys. Chem. B. 2011. [Google Scholar]
  15. Sorrell, C.D.; Carter, M.C.D.; Serpe, M.J. Color tunable poly (N-isopropylacrylamide)-co-acrylic acid microgel-Au hybrid assemblies. Adv. Funct. Mater. 2011, 21, 425–433. [Google Scholar] [CrossRef]
  16. Debord, J.D.; Eustis, S.; Debord, S.B.; Lofye, M.T.; Lyon, L.A. Color-tunable colloidal crystals from soft hydrogel nanoparticles. Adv. Mater. 2002, 14, 658–662. [Google Scholar] [CrossRef]
  17. Debord, J.D.; Lyon, L.A. Thermoresponsive photonic crystals. J. Phys. Chem. B 2000, 104, 6327–6331. [Google Scholar] [CrossRef]
  18. Lyer, A.S.; Lyon, L.A. Self-healing colloidal crystals. Angew. Chem.-Int. Edit. 2009, 48, 4562–4566. [Google Scholar] [CrossRef]
  19. Lyon, L.A.; Debord, J.D.; Debord, S.B.; Jones, C.D.; McGrath, J.G.; Serpe, M.J. Microgel colloidal crystals. J. Phys. Chem. B 2004, 108, 19099–19108. [Google Scholar]
  20. Gan, D.J.; Lyon, L.A. Tunable swelling kinetics in core-shell hydrogel nanoparticles. J. Am. Chem. Soc. 2001, 123, 7511–7517. [Google Scholar]
  21. Gan, D.J.; Lyon, L.A. Synthesis and protein adsorption resistance of PEG-modified poly(N-isopropylacrylamide) core/shell microgels. Macromolecules 2002, 35, 9634–9639. [Google Scholar] [CrossRef]
  22. Jones, C.D.; Lyon, L.A. Dependence of shell thickness on core compression in acrylic acid modified poly(N-isopropylacrylamide) core/shell microgels. Langmuir 2003, 19, 4544–4547. [Google Scholar] [CrossRef]
  23. Hu, X.; Tong, Z.; Lyon, L.A. Multicompartment core/shell microgels. J. Am. Chem. Soc. 2010, 132, 11470–11472. [Google Scholar]
  24. Hu, X.; Tong, Z.; Lyon, L.A. Control of poly(N-isopropylacrylamide) microgel network structure by precipitation polymerization near the lower critical solution temperature. Langmuir 2011, 27, 4142–4148. [Google Scholar] [CrossRef]
  25. Prevo, B.G.; Velev, O.D. Controlled, rapid deposition of structured coatings from micro- and nanoparticle suspensions. Langmuir 2004, 20, 2099–2107. [Google Scholar] [CrossRef]
  26. Cong, H.L.; Cao, W.X. Macroporous Au materials prepared from colloidal crystals as templates. J. Colloid Interface Sci. 2004, 278, 423–427. [Google Scholar] [CrossRef]
  27. Dimitrov, A.S.; Nagayama, K. Continuous convective assembling of fine particles into two-dimensional arrays on solid surfaces. Langmuir 1996, 12, 1303–1311. [Google Scholar] [CrossRef]
  28. Denkov, N.D.; Velev, O.D.; Kralchevsky, P.A.; Ivanov, I.B.; Yoshimura, H.; Nagayama, K. Mechanism of formation of 2-dimensional crystals from latex particles on substrates. Langmuir 1992, 8, 3183–3190. [Google Scholar] [CrossRef]
  29. Fudouzi, H. Fabricating high-quality opal films with uniform structure over a large area. J. Colloid Interface Sci. 2004, 275, 277–283. [Google Scholar] [CrossRef]
  30. Gu, Z.Z.; Fujishima, A.; Sato, O. Patterning of a colloidal crystal film on a modified hydrophilic and hydrophobic surface. Angew. Chem.-Int. Edit. 2002, 41, 2068–2070. [Google Scholar]
  31. Suzuki, D.; Kawaguchi, H. Hybrid microgels with reversibly changeable multiple brilliant color. Langmuir 2006, 22, 3818–3822. [Google Scholar] [CrossRef]
  32. Zhou, M.; Xing, F.; Ren, M.; Feng, Y.; Zhao, Y.; Qiu, H.; Wang, X.; Gao, C.; Sun, F.; He, Y.; Ma, Z.; Wen, P.; Gao, J. A facile method to assemble pNIPAM—containing microgel photonic crystals. Chemphyschem 2009, 10, 523–526. [Google Scholar] [CrossRef]
  33. Lu, Y.; Drechsler, M. Charge-induced self-Assembly of 2-dimensional thermosensitive microgel particle patterns. Langmuir 2009, 25, 13100–13105. [Google Scholar] [CrossRef]
  34. Miao, Y.H.; Geng, D.L.; Helseth, L.E. Order-disorder transition in a quasi-two-dimensional colloidal system. Langmuir 2006, 22, 5572–5574. [Google Scholar]
  35. Meng, Z.; Cho, J.K.; Debord, S.; Breedveld, V.; Lyon, L.A. Crystallization behavior of soft, attractive microgels. J. Phys. Chem. B 2007, 111, 6992–6997. [Google Scholar]
  36. Kuncicky, D.M.; Velev, O.D. Surface-guided templating of particle assemblies inside drying sessile droplets. Langmuir 2008, 24, 1371–1380. [Google Scholar] [CrossRef]
  37. Shmuylovich, L.; Shen, A.Q.; Stone, H.A. Surface morphology of drying latex films: Multiple ring formation. Langmuir 2002, 18, 3441–3445. [Google Scholar] [CrossRef]
  38. Deegan, R.D.; Bakajin, O.; Dupont, T.F.; Huber, G.; Nagel, S.R.; Witten, T.A. Capillary flow as the cause of ring stains from dried liquid drops. Nature 1997, 389, 827–829. [Google Scholar]
  39. Anac, I.; Aulasevich, A.; Junk, M.J.N.; Jakubowicz, P.; Roskamp, R.F.; Menges, B.; Jonas, U.; Knoll, W. Optical characterization of co-nonsolvency effects in thin responsive pNIPAAm-based gel layers exposed to ethanol/water mixtures. Macromol. Chem. Phys. 2010, 211, 1018–1025. [Google Scholar] [CrossRef]
  40. McPhee, W.; Tam, K.C.; Pelton, R. Poly(N-isopropylacrylamide) latices prepared with sodium dodecyl-sulfate. J. Colloid Interface Sci. 1993, 156, 24–30. [Google Scholar] [CrossRef]
  41. Schild, H.G.; Muthukumar, M.; Tirrell, D.A. Cononsolvency in mixed aqueous-solutions of poly(N-isopropylacrylamide). Macromolecules 1991, 24, 948–952. [Google Scholar]
  42. Winnik, F.M.; Ottaviani, M.F.; Bossmann, S.H.; Garciagaribay, M.; Turro, N.J. Cononsolvency of poly(N-isopropylacrylamide) in mixed water-methanol solutions—A look at spin-labeled polymers. Macromolecules 1992, 25, 6007–6017. [Google Scholar]
  43. Winnik, F.M.; Ringsdorf, H.; Venzmer, J. Methanol water as a co-nonsolvent system for poly(N-isopropylacrylamide). Macromolecules 1990, 23, 2415–2416. [Google Scholar] [CrossRef]
  44. Norrman, S.; Andersson, T.; Peto, G.; Somogyi, S. Quantitative evolution studies of particle separation, size, and shape for vapour-deposited ultrathin gold-films on glass substrates. Thin Solid Films 1981, 77, 359–366. [Google Scholar] [CrossRef]
  45. Alexeev, V.L.; Sharma, A.C.; Goponenko, A.V.; Das, S.; Lednev, I.K.; Wilcox, C.S.; Finegold, D.N.; Asher, S.A. High ionic strength glucose-sensing photonic crystal. Anal. Chem. 2003, 75, 2316–2323. [Google Scholar]
  46. Muscatello, M.M.W.; Stunja, L.E.; Asher, S.A. Polymerized crystalline colloidal array sensing of high glucose concentrations. Anal. Chem. 2009, 81, 4978–4986. [Google Scholar] [CrossRef]

Share and Cite

MDPI and ACS Style

Hu, L.; Serpe, M.J. Color-Tunable Etalons Assembled from Poly (N-Isopropylacrylamide) Based Microgels. Polymers 2012, 4, 134-149. https://doi.org/10.3390/polym4010134

AMA Style

Hu L, Serpe MJ. Color-Tunable Etalons Assembled from Poly (N-Isopropylacrylamide) Based Microgels. Polymers. 2012; 4(1):134-149. https://doi.org/10.3390/polym4010134

Chicago/Turabian Style

Hu, Liang, and Michael J. Serpe. 2012. "Color-Tunable Etalons Assembled from Poly (N-Isopropylacrylamide) Based Microgels" Polymers 4, no. 1: 134-149. https://doi.org/10.3390/polym4010134

APA Style

Hu, L., & Serpe, M. J. (2012). Color-Tunable Etalons Assembled from Poly (N-Isopropylacrylamide) Based Microgels. Polymers, 4(1), 134-149. https://doi.org/10.3390/polym4010134