Next Article in Journal
Computational Study of the Plasma Actuator Flow Control for an Airfoil at Pre-Stall Angles of Attack
Next Article in Special Issue
Few-Layer Graphene as an Efficient Buffer for GaN/AlN Epitaxy on a SiO2/Si Substrate: A Joint Experimental and Theoret-ical Study
Previous Article in Journal
Towards Urban Sustainability: Developing Noise Prediction Model in an Informal Setting
Previous Article in Special Issue
Mechanical and Thermal Properties of Aluminum Matrix Composites Reinforced by In Situ Al2O3 Nanoparticles Fabricated via Direct Chemical Reaction in Molten Salts
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Applied Sciences
Volume 12
Issue 18
10.3390/app12189072
applsci-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effect of Zinc Aluminum Magnesium Coating on Spot-Welding Joint Properties of HC340LAD + ZM Steel

by
Xiang Chen
1,
Xinjie Peng
1,
Xinjian Yuan
1,*,
Ziliu Xiong
2,
Yue Lu
2,
Shenghai Lu
2 and
Jian Peng
1
1
State Key Laboratory of Mechanical Transmission, College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China
2
HBIS Group Technology Research Institute, Shijiazhuang 050023, China
*
Author to whom correspondence should be addressed.
Appl. Sci. 2022, 12(18), 9072; https://doi.org/10.3390/app12189072
Submission received: 2 August 2022 / Revised: 3 September 2022 / Accepted: 5 September 2022 / Published: 9 September 2022
(This article belongs to the Special Issue Metal-Based Composite Materials: Preparation, Structure, Properties, and Applications)
Browse Figures
Versions Notes

Abstract

:
Zn-Al-Mg (zinc, aluminum and magnesium)-coated steel is gradually replacing traditional hot-dip galvanized steel due to its excellent corrosion resistance, self-healing properties and good surface hardness. However, the effect of Zn-Al-Mg coating on the resistance spot-welding joint properties of HC340LAD + ZM steel plates is not clear, and there are few systematic studies on it. In this paper, L16 (43) orthogonal experiments were designed on Zn-Al-Mg-coated steel HC340LAD + ZM (thickness = 1 mm). In addition, taking the tensile shear force as the main evaluation standard, the optimal spot-welding process properties could be achieved when the welding current, the welding time and the electrode loading were 10 kA, 14 cycles and 2.6 kN, respectively. On this basis, the formation mechanism, microstructure and corrosion properties of two plates of steels, with or without zinc, aluminum and magnesium coating under different welding times, were studied. The presence of Zn-Al-Mg coating slightly affected the mechanical properties of welding joints. However, the corrosion current of the body material containing Zn-Al-Mg plating was 7.17 times that of the uncoated plate.

1. Introduction

Hot-dip galvanized steel is widely used in automobiles, construction, home appliances and other industries due to its good welding performance and excellent corrosion resistance [1,2,3]. In addition, the corrosion resistance of hot-dip galvanized steel is mainly through the physical barrier protection of the surface coating and the electrochemical protection of zinc as an anode for steel under the action of corrosive media [4,5,6]. With technological development and industrial upgrading, when appropriate amounts of Mg and Al (usually 1–4 wt%) are added to zinc coating, a Zn-Al-Mg coating is formed, which can greatly improve the corrosion resistance of hot-galvanized steel [7,8,9,10,11,12]. Thus, the Zn-Al-Mg-coated steel comes into being.
Zn-Al-Mg-coated steel, as an upgrade product of hot-dip galvanized steel, not only has a much lower corrosion rate than hot-dip galvanized steel in the same environment but also has a good bending strength ratio, excellent surface hardness, low cost and other advantages. Therefore, Zn-Al-Mg-coated steel is widely used in automotive outer plates, brackets and internal components [13,14,15].
As we all know, resistance spot-welding has become the main welding process of automobile steel plate links due to its fast welding speed, excellent welding quality, high degree of automation and low cost [16,17,18,19,20,21]. The coating of Zn-Al-Mg-plated steel is melted first in the process of spot-welding due to the existence of plating, and the Zn element in the coating is the first to evaporate, reducing the temperature of the steel [9,15,22]. However, a part of the Al-Mg elements will remain in the weld, the formation process of the melting core is more complex than that of traditional galvanized steel.
Therefore, improving the quality of the spot-welding joint of Zn-Al-Mg-coated steel and its welding process parameters are key problems. In addition, the main factors affecting the mechanical properties of resistance spot-welding joints are welding current, welding time and electrode loading [23,24,25]. Welding current mainly provides heat for the welding process. When the temperature exceeds the melting temperature at the workpiece–workpiece interface, the welding core begins to produce. Not only is the size of the welding core related to the size of the welding current, but also the welding time and electrode loading have a great impact on it [26,27].
In order to explore the influence of Zn-Al-Mg coating on the resistance spot-welded joint properties of HC340LAD + ZM steel, the optimal welding process parameters of HC340LAD + ZM steel were explored through an orthogonal experiment design. Then, based on the optimal parameters, HC340LAD + ZM with Zn-Al-Mg coating and HC340LA without coating were designed as experimental welding parameters to explore the nucleation process of the spot-welding joint and the influence of the coating on the properties of the spot-welding joint and, further, to study the influence of the Zn-Al-Mg coating on the corrosion resistance of the spot-welding joint.

2. Materials and Methods

In order to study the effect of the coating on HC340LAD + ZM steel resistance spot welding, a cold-rolled, low-alloy, high-strength HC340LA steel (sheet thickness = 1.4 mm) was prepared as the experimental material. The other one was an HC340LAD + ZM steel, which was developed from HC340LA steel after adding zinc, aluminum and magnesium coating; the amount of coating was 180 g/m2. The chemical composition and mechanical properties of the matrix are shown in Table 1.
The matrix micromorphology and the coating cross-section morphology are also shown in Figure 1. The mechanical properties and matrix microstructure of the two kinds of steel plates are almost consistent. In addition, the matrix microstructure of both is composed of ferrite and a small amount of pearlite. The differences only lie in the presence of Zn-Al-Mg coating.
The two experimental steel plates were cut and processed into several 125 mm × 40 mm plate samples, and the processed samples were cleaned and dried with ethanol (99.5%) to avoid the metallurgical contamination of the spot-welding experiment by oil pollution and other factors. The cleaned samples were tested for spot-welding experiments under the lap state, as shown in Figure 2, and the tensile samples and metallographic samples were prepared. In addition, the metallographic samples were welded twice, and a spot-welding experiment was carried out on the OBARA SIV21 small original spot-welding machine.
The tensile shear force of the spot-welding samples was measured by the SANS microcomputer servo-controlled hydraulic universal testing machine with a tensile speed of 2 mm/min. The rectangular samples (15 mm × 7.5 mm) of the metallographic and scanning samples were prepared from the spot-welding joints. The corrosion solution was 4% nitrate alcohol solution, and the corresponding corrosion time was 14 s. Then, the Leica DM 2000 microscope and TESCAN VEGA3 tungsten filament scanning electron microscope were used to observe the metallographic and scanning section of the welding joint. The micro-hardness value was measured with the HXS-1000AKY hardness meter (300 g, 10 s), and its micro-hardness distribution was measured along the horizontal and vertical direction of the welding joint.
Firstly, welding current, welding time and electrode loading were chosen as variables to design the orthogonal experiment. Then, mechanical properties and spot-welding joint parameters (pressure down rate, welding joint diameter, welding joint thickness) were measured systematically. Furthermore, the splash degree was assessed according to the vast amount of splash distance generated in the spot-welding process, and the splash size was graded in a section of 50 cm. The A/B/C/D splashes were, respectively, represented by splash distances of 150–100 cm; 100–50 cm; 50–0 cm; and no splash. The value range of welding current, welding time and electrode loading was preliminarily selected according to the thickness, strength and galvanizing layer of the plate and combined with previous tests and related documents (the current = 8–11 kA, the time = 12–18 cycles (1 cycle = 0.02 s), the electrode loading = 1.8–3.0 kN). The optimal welding parameters of HC340LAD + ZM were obtained through the orthogonal experiment, then the welding current and electrode loading of two kinds of steel, HC340LAD + ZM with Zn-Al-Mg coating and HC340LA without coating, were fixed under the optimal parameters. Taking welding time as the main variable, the nucleation process of the spot-welding joint of two kinds of steels and the effect of coating on the properties of the spot-welding joint were explored, and the change in corrosion resistance before and after welding was studied. The welding joint and the unwelded body material with the optimal welding parameters of 10 kA, 14 cycles and 2.6 kN for HC340LAD + ZM steel with Zn-Al-Mg coating and HC340LA without coating were selected, and three sets of 15 mm × 15 mm samples were prepared with wire cutting. Then, the polarization curve was tested after alcohol cleaning, with a scanning speed of 2 mV/s.

3. Experimental Results

3.1. Orthogonal Experiments

Then, the orthogonal tests were designed, and the specific test process parameters are shown in Table 2.
With tensile shear as the main parameter, the mechanical properties of joints under each group of parameters were inserted into SPSS for multi-factor variance and extreme difference analysis, and the optimal process parameters were as follows: welding current, welding time and electrode loading were 10 kA, 14 cycles and 2 kN, respectively; the order of the influence of the three factors on tensile shear was current > pressure > time.

3.2. Macro- and Micro-Morphology

According to the orthogonal experiment results, the optimal welding process parameters were as follows: welding current, welding time and electrode loading were 10 kA, 14 cycles and 2 kN, respectively. Then, the two kinds of steel with coating and without coating were welded separately on the basis of the optimal welding process parameters by fixing the welding current and electrode loading and by changing the welding time to explore the dynamic nucleation process of the spot-welding process and the influence of the coating on the nucleation quality of the welding joint. The macroscopic morphology of the welds under different welding times is shown in Figure 3. With the increase in welding time, the diameter of the welds of the two plates of steel also increased. In addition, with the increase in welding time, the HC340LA steel without coating showed a better quality welding spot surface without splash, while HC340LAD + ZM steel with coating had rough joints on the welding spot surface with fluctuations. Furthermore, the splash phenomenon appeared after 10 cycles, and the center of the welding point became yellow.
Figure 4 shows the change in the welding joint’s diameter, thickness, pressure down rate and tensile shear force with welding time. It can be clearly seen from Figure 4 that the joule heat and the welding joint diameter of HC340LAD + ZM and HC340LA increased with the increase in welding time. When the welding time was one cycle, the welding joint diameter of HC340LA without coating was 0.83 mm larger than that of the HC340LAD + ZM steel with coating. With the increase in welding time, the gap in the welding joint diameter became smaller. When the welding time was 10 cycles, the welding joint diameter was almost the same, and then the increase in the welding joint diameter tended to be flat, while the thickness of the welding points was the opposite, and the thickness of both plates of steel showed a downward trend. When the welding time exceeded 14 cycles, the welding point thickness of the two plates of steel tended to coincide. The welding joint thickness of the 16 cycles was 2.56 mm and 2.5 mm, respectively. The corresponding downpressure rate was 14.88% and 10.71%.
Figure 4d shows the tensile shear force of HC340LA steel without coating and HC340LAD + ZM steel with Zn-Al-Mg coating. As the welding time increased, the tensile shear force rose first and then decreased, reaching its maximum after 14 cycles with the tensile shear forces of 14.28 kN and 15.75 kN. However, the tensile shear force of HC340LA steel without coating was higher than that of HC340LAD + ZM steel with Zn-Al-Mg coating under the same welding parameters. When the welding time of HC340LA without coating was one cycle, the welding core had already appeared, and the tensile shear force at this time was 5.34 kN. HC340LAD + ZM with coating did not nucleate until the welding time was eight cycles, and the corresponding tensile shear force was 4.44 kN. Combined with the diameter and the thickness of the welding point, the existence of the Zn-Al-Mg coating reduced the weldability. Although the diameter of the welding point was large enough after six cycles, an effective welding core was still not formed at this time. Because of the existence of Zn-Al-Mg coating, the contact resistance between the two plates was smaller, and there was less heat input from the welding center area, thus failing to effectively form the welding core. Therefore, with the increase in the welding time, the impact of the coating on the welding time became smaller, and HC340LAD + ZM with coating did not nucleate until the welding time was eight cycles. Meanwhile, the zinc with a low melting point evaporated and gasified the heat during welding, which reduced the effective heat input generated during welding, resulting in more difficult nucleation.
Figure 5 and Figure 6 show the cross-section morphologies of the HC340LA without coating and the HC340LAD + ZM with coating at different welding times. Figure 5 shows the cross-section morphology of HC340LA steel without coating when the welding time was 1~18 cycles. As shown in the figure, the uncoated HC340LA steel was very sensitive to the change in welding time, and the width of the molten core gradually increased with the increase in welding time, and the thickness of the welding point also decreased. When the welding time was one cycle, there was no complete nucleation, but a union appeared between the plates. When the welding time was two cycles, the nucleation began to obviously appear, forming a small welding core area. After four cycles, nucleation completed, and the columnar crystal appeared obviously perpendicular to the plastic ring. At this time, a shrinkage hole defect appeared. Because there was so little molten metal, it shrank as it cooled, and holes formed. As the welding time increased, the height of the melting core decreased, and the width of the melting core also gradually increased, which was basically unchanged after reaching 14 cycles. Figure 6 shows the cross-section morphology of the HC340LAD + ZM steel with coating when the welding time was 1~18 cycles. Due to the existence of the coating, the welding of the coated HC340LAD + ZM steel requires a greater welding heat input. On the one hand, the existence of the coating made the contact resistance between the plates smaller and made the heat input generated during welding lower, resulting in difficult nucleation. On the other hand, because of the low melting point of Zn, the main heat generated was first absorbed by the coating, resulting in less heat input obtained by the parent material, Fe, which could not effectively nucleate. Thence, nucleation appeared initially when the welding time was eight cycles; when the welding time reached 10 cycles, the welded joint nucleated completely.

3.3. Fracture Form and Hardness Distribution

The failure modes of the welding point fracture of HC340LAD + ZM with Zn-Al-Mg coating and HC340LA without coating are mainly divided into two types: interface fracture (IF = interfacial failure) and pull-out fracture (PF = plug failure). Figure 7a,b reveal the morphologies of IF macroscopic tensile shear fracture and IF fracture, respectively. The macroscopic fracture shows that the fracture occurred at the two interfaces of the welding point, while the morphology of the microscopic fracture is an obvious cleavage step. Figure 7c,d show the morphologies of PF macroscopic tensile shear fracture and PF fracture, respectively. The macroscopic fracture illustrates that pull-out tear occurred in the parent material zone around the welding joint; the welding point was well fused, and no fracture occurred, while the morphology of the microscopic fracture had countless axial dimples.
According to Figure 4d, due to the existence of coating, the HC340LAD + ZM steel did not nucleate at a low welding time. Nucleation completed after eight cycles, and the tensile shear force was 4.44 kN. In addition, the quality of the welding joint was poor, and the welding core was not firmly bonded. In this context, an IF-type interface fracture of the welding joint occurred. After 14 cycles, the quality of the welding joint nucleation was better, and the tensile shear force was 14.28 kN. At this time, a PF-type pull-out fracture occurred. The HC340LA steel without coating had good malleability due to the existence of no coating. After one cycle, although the plates did not melt in the process of chemical metallurgy at this time, the two plates combined under the action of electrode loading. At this time, the tensile shear force was 5.34 kN, and an IF-type interface fracture occurred. When the welding time was four cycles, a welding point with good quality formed, and a PF-type pull-out fracture occurred with a pull shear force of 12.36 kN. This was because, when the welding time was short, the two plates in the welding core area were not closely combined, and the shear force between the welding points was less than the tensile strength of the parent material. At this time, the fracture position occurred in the welding core. When the welding time was long enough, the welding heat was enough; the nucleation was complete, and the shear force of the welding core area was greater than the tensile strength of the parent material, thus, the pull-out fracture occurs. Under the same welding parameters, the tensile shear force of the welding joint with a Zn-Al-Mg coating was smaller than that of the welding joint without coating, which may owe to the existence of the coating, which affected the temperature and thermal cycle of the welding joint, resulting in the low tensile shear force.
Figure 8 and Figure 9 show the hardness value distribution of the welding point under different welding times for HC340LA without coating and HC340LAD + ZM with coating. As shown in the figure, the hardness value distribution of the welding points of both steel results in a “π”, high on both sides and low in the middle.
As can be seen in Figure 8, nucleation occurred after one cycle, and even the obvious welding core zone, heat-affected zone and welding core zone appeared. The hardness value of the parent material was 150 HV; the average hardness of the welding core zone was 375 HV, and the hardness value of the heat-affected zone was between the two. In the horizontal direction, it is obvious that the welding core zone widened as the welding time increased. In the vertical direction, it was distributed high on both sides and low in the middle, and the hardness value near the electrode head was 280~300 HV.
As shown in Figure 9, after one cycle and three cycles, the peak temperature of the welding point did not exceed the A3 line, and the tissue of the welding core zone was mixed with martensite and ferrite. At this time, the hardness value of the central position was low (180 HV). After four cycles, the temperature of some areas near the welding core area exceeded the A1 line, and a small amount of martensite formed. In this condition, the hardness value of the welding core zone reached 250 HV. After six cycles, on the one hand, due to the influence of the coating, there was no effective connection between the plates, but at this time, the welding core zone was completely austenitic, and a large number of martensite was obtained. In addition, the hardness value rose. On the other hand, due to the existence of the coating, the mechanical properties of the welding joints deteriorated, and the average hardness value of the welding core zone was 355 HV, which was lower than that of the welding joints of HC340LA without coating. In the vertical direction, the hardness value near the two sides of the electrode cap was 240 HV, which was lower than that of the welding joint of the HC340LA without coating (280 HV). This is because, during welding, the surface coating evaporated, splashed and took away the heat; thus, the surface area obtained less heat, eventually forming less martensite, and it had a lower hardness value.

3.4. Corrosion Behaviour Study

The results of the polarization curves for each zone are shown in Figure 10 and Table 2.
According to Figure 10 and Table 3, compared with the parent material and the welding point polarization curve of the same material, the corrosion potential of the welding point was lower than that of the corresponding parent material, which illustrates that the corrosion tendency of the welding point was greater than that of the body material, and the change in corrosion current was also consistent. The corrosion currents of the body material and the welding joint of the HC340LA steel without coating were 4.258 × 10−4 mA·cm−2 and 3.602 × 10−3 mA·cm−2. The corrosion current decreased by 8.46 times, while the corrosion currents of the parent material and the welding joint of the HC340LAD + ZM with Zn-Al-Mg coating were 5.934 × 10 −5 mA·cm−2 and 1.323 × 10−4 mA·cm−2. The corrosion current decreased by 2.23 times. This is because the welding heat input increased in the welding process, which led to tissue transformation and the loss of the surface coating of the welding point during the welding process, thus leading to the deterioration of corrosion resistance.
The corrosion potentials of the HC340LAD + ZM base material and the welding joint containing zinc aluminum magnesium coating were (−1.167 V) and (−1.218 V), respectively; the corrosion potentials of the base material and the welding joint of HC340LA without coating were (−0.5721 V) and (−0.705 V), respectively. According to the longitudinal comparison, the HC340LAD + ZM had a lower corrosion potential at both the base material and the welding joint, so its corrosion tendency was greater. The corrosion current was just the opposite. The corrosion currents of the parent material of the zinc–aluminum–magnesium-coated plate and the uncoated plate were 5.934 × 10−5 mA·cm−2 and 4.258 × 10−4 mA·cm−2, respectively. The corrosion current of the zinc–aluminum–magnesium plate was 7.17 times that of the uncoated plate. The corrosion currents of the welding joint of the zinc–aluminum–magnesium-coated plate and the uncoated plate were 1.323 × 10−4 mA·cm−2 and 3.602 × 10−3 mA·cm−2. The gap in the corrosion current was 27 times greater. The reason why the corrosion potential of the Zn-Al-Mg-coated plate was higher than that of the uncoated plate and the corrosion current was smaller is that the corrosion of the Zn-Al-Mg-coated plate was the first to develop surface corrosion. The coating was mainly zinc, whose corrosion potential is higher (−1 V), and the uncoated plate was the corrosive matrix ferrite (−0.4 V). Due to the presence of primary crystal phase Zn; Al; MgZn2; binary co-crystal tissue Zn/MgZn2; and ternary co-crystal tissue Zn/MgZn2/Al in the zinc–aluminum–magnesium coating—in which MgZn2 and Mg2Zn11 had higher microhardness, better compactness and better single-phase corrosion resistance—the zinc and aluminum magnesium plates had higher corrosion potential, but a slower corrosion rate [28,29,30].

4. Conclusions

(1) The orthogonal tests showed that the optimal parameters of HC340LAD + ZM steel resistance spot-welding are as follows: welding current, welding time and electrode loading were 10 kA, 14 cycles, and 2.6 kN, respectively. The influence of welding current, welding time and electrode loading on the tensile shear force can be successively ranked as current > pressure > time.
(2) When the fixed welding current (10 kA) and the electrode loading (2.6 kN) increased, the welding point diameter of both steel plates also increased as the welding time increased. Under the same welding parameters, the mechanical properties of the spot-welding joint of the HC340LA steel without coating were slightly better than those of the HC340LAD + ZM with coating. The HC340LA steel without coating began to nucleate after one cycle, and the tensile shear force was 5.34 kN. The nucleation completed after four cycles, and the tensile shear force reached 12.36 kN. The HC340LAD + ZM with coating started to nucleate after eight cycles, and the tensile shear force was 4.44 kN.
(3) In the nucleation test, the tensile shear force of the welding joint of the HC340LA steel without coating was greater than that of the welding joint of the HC340LAD + ZM steel with zinc–aluminum–magnesium coating. The tensile shear forces of the zinc-and-magnesium-coated steel and the uncoated steel increased first and then decreased as the welding time increased, and the tensile shear reached the maximum after 14 cycles. At this time, the tensile shear forces of the welding joint of the zinc-and-magnesium-coated steel and the uncoated steel were 14.28 kN and 15.75 kN, respectively.
(4) The fracture modes of the welding joint of the two kinds of steel can be divided into two types: pull-out fracture and interface fracture. When the welding time was short, and the heat input was small, the nucleation of the welding joint was insufficient, and the tensile shear force was small. Then, an interface fracture occurred. When the welding time increased, and the heat input increased, the nucleation of the welding joint was fully complete, and the tensile shear force exceeded 11.6 kN. At this time, the welding joint was pulled and broken at the parent material near the heat-affected zone.
(5) The hardness of the welding point of the uncoated steel and the coated steel was distributed in a “π” shape, which was high on both sides and low in the middle. The HC340LA steel without coating completed nucleation after one cycle, and the corresponding hardness values of the parent material and the welding joint were 150 HV and 375 HV. However, the hardness value for the HC340LAD + ZM steel with coating was very low after one and two cycles, and the hardness values of the welding core zone were 180 HV and 250 HV, respectively. A large number of martensite appeared in the center of the welding point after four cycles, and the hardness value of the welding core zone reached 355 HV. Compared with the hardness value of the welding joint of the HC340LA steel without coating and the HC340LAD + ZM steel with coating, the hardness value in the welding core zone and near the surface of the welding joint was higher than that of the same area with the coating.
(6) The corrosion resistance of the welding point was lower than that of the parent material. The corrosion current of the HC340LAD + ZM with zinc–aluminum–magnesium coating was 2.23 times that of the parent material, and the corrosion current of the welding joint of the HC340LA without coating was 8.46 times that of the parent material. The corrosion current of the welding joint of the zinc–aluminum–magnesium-coated steel was 27 times that of the welding joint of the uncoated steel, while the corrosion current of the parent material of the zinc–aluminum–magnesium-coated plate was 7.17 times that of the uncoated plate.

Author Contributions

Conceptualization, X.C. and X.Y.; investigation, Y.L.; resources, Y.L.; data curation, X.C.; writing—original draft preparation, X.C. and X.P.; writing—review and editing, X.C. and X.P.; visualization, Z.X., S.L. and J.P.; supervision, J.P. and X.Y.; project administration, X.Y.; funding acquisition, Z.X. and S.L. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by HBIS Company Limited. The authors thank Ba Gen, a senior engineer of Tangshan Iron and Steel company, for their technical support and valuable suggestions.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Oh, M.S.; Kim, S.H.; Kim, J.S.; Lee, J.W.; Shon, J.H.; Jin, Y.S. Surface and Cut-edge Corrosion Behavior of Zn-Mg-Al Alloy-Coated Steel Sheets as a Function of the Alloy Coating Microstructure. Met. Mater. Int. 2016, 22, 26–33. [Google Scholar] [CrossRef]
  2. Marder, A.R. The metallurgy of zinc-coated steel. Prog. Mater. Sci. 2000, 45, 191–271. [Google Scholar] [CrossRef]
  3. Qu, Q.; Yan, C.W.; Wan, Y.; Cao, C.N. Effects of NaCl and SO2 on the initial atmospheric corrosion of zinc. Corros Sci. 2002, 44, 2789–2803. [Google Scholar] [CrossRef]
  4. Al-Negheimish, A.; Hussain, R.R.; Alhozaimy, A.; Singh, D.D.N. Corrosion performance of hot-dip galvanized zinc-aluminum coated steel rebars in comparison to the conventional pure zinc coated rebars in concrete environment. Constr. Build. Mater. 2021, 274, 121921. [Google Scholar] [CrossRef]
  5. Zhang, J.; Yu, Z.H. Corrosion Performance of Hot Dip Galvanized Steel. Adv. Manuf. Syst. 2011, 201–203, 2611–2614. [Google Scholar] [CrossRef]
  6. Ramezanzadeh, B.; Attar, M.M.; Farzam, M. Corrosion performance of a hot-dip galvanized steel treated by different kinds of conversion coatings. Surf. Coat. Technol. 2010, 205, 874–884. [Google Scholar] [CrossRef]
  7. Dutta, M.; Halder, A.K.; Singh, S.B. Morphology and properties of hot dip Zn-Mg and Zn-Mg-Al alloy coatings on steel sheet. Surf. Coat. Technol. 2010, 205, 2578–2584. [Google Scholar] [CrossRef]
  8. LeBozec, N.; Thierry, D.; Persson, D.; Stoulil, J. Atmospheric Corrosion of Zinc-Aluminum Alloyed Coated Steel in Depleted Carbon Dioxide Environments. J. Electrochem. Soc. 2018, 165, C343–C353. [Google Scholar] [CrossRef]
  9. Shimizu, T.; Yoshizaki, F.; Miyoshi, Y.; Andoh, A. Corrosion products of hot-dip Zn-6%Al-3%Mg coated steel sheet subjected to atmospheric exposure. Tetsu-to-Hagane 2003, 89, 166–173. [Google Scholar] [CrossRef]
  10. Zhang, Y.J.; Xu, M.Y.; Ma, R.N.; Du, A.; Fan, Y.Z.; Zhao, X.; Cao, X.M. Effect of Oxide Scale on Hot Dip Zn-Al-Mg Alloy Coating Prepared by Reduction Combined with Induction Heating. Metals 2020, 10, 1519. [Google Scholar] [CrossRef]
  11. Zhang, Z.Y.; Yue, Z.W.; Li, X.G.; Jiang, B.; Wang, F.F.; Fan, Z.B.; Yan, F.J.; Li, W.J.; Wu, Y.P.; Mi, C.X.; et al. Microstructure and Corrosion Resistance of Zn-Al-Mg Alloy Diffusion Coating developed on Carbon Steel by Hot Dipping. Int. J. Electrochem. Sci. 2020, 15, 5512–5519. [Google Scholar] [CrossRef]
  12. Chang, B.H.; Xiao, H.; Zeng, J.L.; Yang, S.; Du, D.; Song, J.L.; Han, G.L. Fluid Flow Characteristics and Weld Formation Quality in Gas Tungsten Arc Welding of a Thick-Sheet Aluminum Alloy Structure by Varying Welding Position. Appl. Sci. 2018, 8, 1215. [Google Scholar] [CrossRef]
  13. Long, W.Y.; Wu, Y.P.; Gao, W.W.; Hong, S. Corrosion Resistance Behavior and Mechanism of Zn-Al-Mg-RE Coating in Seawater with SRB. Cailiao Gongcheng 2018, 46, 91–97. [Google Scholar] [CrossRef]
  14. Prosek, T.; Nazarov, A.; Goodwin, F.; Serak, J.; Thierry, D. Improving corrosion stability of Zn-Al-Mg by alloying for protection of car bodies. Surf.Coat. Technol. 2016, 306, 439–447. [Google Scholar] [CrossRef]
  15. Jiang, G.R.; Chen, L.F.; Wang, H.Q.; Liu, G.H. Microstructure and Corrosion Resistance Property of a Zn-Al-Mg Alloy with Different Solidification Processes. MATEC Web Conf. 2017, 109. [Google Scholar] [CrossRef]
  16. Gomes, G.F.; Vieville, P.; Durrenberger, L. Dynamic behavior investigation of spot welding machines and its influence on weld current range by modal analysis. J. Braz. Soc. Mech. Sci. 2017, 39, 765–773. [Google Scholar] [CrossRef]
  17. Tarasov, N.M. Resistance Welding with Compression of Peripheral Zone of Weld Spot. Weld Prod+ 1973, 20, 49–51. [Google Scholar]
  18. Oikawa, M.; Atsumi, K.; Otsuka, Y.; Kawada, N. Development of Condition Monitoring System for Electric Resistance Spot Welding Used to Manufacture Railway Car Bodies. J. Robot. Mechatron. 2021, 33, 421–431. [Google Scholar] [CrossRef]
  19. Ambroziak, A.; Korzeniowski, M. Using resistance spot welding for joining aluminium elements in automotive industry. Arch. Civ. Mech. Eng. 2010, 10, 5–13. [Google Scholar] [CrossRef]
  20. Jung, W.; Oh, H.; Yun, D.H.; Kim, Y.G.; Youn, J.P.; Park, J.H. Modified Recurrence Plot for Robust Condition Monitoring of Electrode Tips in a Resistance Spot Welding System. Appl. Sci. 2020, 10, 5860. [Google Scholar] [CrossRef]
  21. Chen, S.J.; Wu, N.; Xiao, J.; Li, T.M.; Lu, Z.Y. Expulsion Identification in Resistance Spot Welding by Electrode Force Sensing Based on Wavelet Decomposition with Multi-Indexes and BP Neural Networks. Appl. Sci. 2019, 9, 4028. [Google Scholar] [CrossRef] [Green Version]
  22. Cao, R.; Chang, J.H.; Huang, Q.; Zhang, X.B.; Yan, Y.J.; Chen, J.H. Behaviors and effects of Zn coating on welding-brazing process of Al-Steel and Mg-steel dissimilar metals. J. Manuf. Processes 2018, 31, 674–688. [Google Scholar] [CrossRef]
  23. Pouranvari, M.; Marashi, S.P.H. Factors affecting mechanical properties of resistance spot welds. Mater. Sci. Technol. 2013, 26, 1137–1144. [Google Scholar] [CrossRef]
  24. Onar, V.; Ozen, F.; Kekik, M.; Aslanlar, Y.S.; Ozderin, Y.; Aslan, H.; Aslanlar, S. Effect of current and welding time on tensile-peel strength of resistance spot welded TWIP 1000 and martensitic steels. Indian J. Chem. Technol. 2019, 26, 248–251. [Google Scholar]
  25. Kim, T.; Park, H.; Rhee, S. Optimization of welding parameters for resistance spot welding of TRIP steel with response surface methodology. Int. J. Prod. Res. 2005, 43, 4643–4657. [Google Scholar] [CrossRef]
  26. Podrzaj, P.; Polajnar, I.; Diaci, J.; Kariz, Z. Overview of resistance spot welding control. Sci. Technol. Weld. Join. 2008, 13, 215–224. [Google Scholar] [CrossRef]
  27. Wang, N.N.; Qiu, R.F.; Peng, W.J.; Shi, H.X. Resistance Spot Welding between Mild Steel and Stainless Steel. Appl. Mech. Mater. 2014, 675–677, 23–26. [Google Scholar] [CrossRef]
  28. Zhang, H.T.; Song, J.Q. Microstructural evolution of aluminum/magnesium lap joints welded using MIG process with zinc foil as an interlayer. Mater. Lett. 2011, 65, 3292–3294. [Google Scholar] [CrossRef]
  29. Guo, L.; Zhang, F.; Lu, J.C.; Zeng, R.C.; Li, S.Q.; Song, L.; Zeng, J.M. A comparison of corrosion inhibition of magnesium aluminum and zinc aluminum vanadate intercalated layered double hydroxides on magnesium alloys. Front. Mater. Sci. 2018, 12, 198–206. [Google Scholar] [CrossRef]
  30. Bolton, R.; Dunlop, T.; Sullivan, J.; Searle, J.; Heinrich, H.; Westerwaal, R.; Boelsma, C.; Williams, G. Studying the Influence of Mg Content on the Microstructure and Associated Localized Corrosion Behavior of Zn-Mg PVD Coatings Using SVET-TLI. J. Electrochem. Soc. 2019, 166, C3305–C3315. [Google Scholar] [CrossRef]
Applsci 12 09072 g001 550
Figure 1. (a) Micromorphology of matrix and (b) coating cross-section morphology.
Figure 1. (a) Micromorphology of matrix and (b) coating cross-section morphology.
Applsci 12 09072 g001
Applsci 12 09072 g002 550
Figure 2. Size diagram of tensile sample and metallographic sample.
Figure 2. Size diagram of tensile sample and metallographic sample.
Applsci 12 09072 g002
Applsci 12 09072 g003 550
Figure 3. Macroscopic morphology under different welding times (10 kA, 2.6 kN).
Figure 3. Macroscopic morphology under different welding times (10 kA, 2.6 kN).
Applsci 12 09072 g003
Applsci 12 09072 g004 550
Figure 4. The change in (a) welding diameter, (b) thickness, (c) down−rate and (d) tensile shear with welding time.
Figure 4. The change in (a) welding diameter, (b) thickness, (c) down−rate and (d) tensile shear with welding time.
Applsci 12 09072 g004
Applsci 12 09072 g005 550
Figure 5. Morphology of HC340LA joint at different welding times (10 kA, 2.6 kN).
Figure 5. Morphology of HC340LA joint at different welding times (10 kA, 2.6 kN).
Applsci 12 09072 g005
Applsci 12 09072 g006 550
Figure 6. Morphology of HC340LAD + ZM joint at different welding times (10 kA, 2.6 kN).
Figure 6. Morphology of HC340LAD + ZM joint at different welding times (10 kA, 2.6 kN).
Applsci 12 09072 g006
Applsci 12 09072 g007 550
Figure 7. Macroscopic and microscopic morphology of typical failure modes: (a) IF, (b) SEM of IF, (c) PF and (d) SEM of PF.
Figure 7. Macroscopic and microscopic morphology of typical failure modes: (a) IF, (b) SEM of IF, (c) PF and (d) SEM of PF.
Applsci 12 09072 g007
Applsci 12 09072 g008 550
Figure 8. HC340LA nugget test hardness changes at different welding times (a) in a horizontal direction and (b) a vertical direction.
Figure 8. HC340LA nugget test hardness changes at different welding times (a) in a horizontal direction and (b) a vertical direction.
Applsci 12 09072 g008
Applsci 12 09072 g009 550
Figure 9. HC340LAD + ZM nugget test hardness changes at different welding times (a) in a horizontal direction and (b) a vertical direction.
Figure 9. HC340LAD + ZM nugget test hardness changes at different welding times (a) in a horizontal direction and (b) a vertical direction.
Applsci 12 09072 g009
Applsci 12 09072 g010 550
Figure 10. HC340LA (a) and Zn−Al−Mg−coated HC340LAD + ZM (b) polarization curves.
Figure 10. HC340LA (a) and Zn−Al−Mg−coated HC340LAD + ZM (b) polarization curves.
Applsci 12 09072 g010
Table
Table 1. Chemical composition and mechanical properties of HC340LAD + ZM steel.
Table 1. Chemical composition and mechanical properties of HC340LAD + ZM steel.
Chemical Composition/wt%Mechanical Property
CMnSiPSNbTiYield Strength/MPaTensile Strength/MPaElongation/%
≤0.1≤0.05≤1.3≤0.03≤0.045≤0.03≤0.0338547528
Table
Table 2. Welding results of HC340LAD + ZM orthogonal test.
Table 2. Welding results of HC340LAD + ZM orthogonal test.
NumberWelding Current (kA)Welding Time (Cycles)Electrode Loading (kN)Pull Shear (kN)Splash SituationMelting Core Diameter (mm)Welding Point Thickness (mm)Down Rate (%) < 30%
18121.86.58CCCD5.732.703.57
28142.29.41CCDD6.162.694.11
38162.69.51CDDD6.172.723.04
481837.74CDDD6.412.558.93
59122.28.75CCCC6.442.616.79
69141.87.47CDCC6.412.635.98
791639.54BBBC6.442.4711.88
89182.68.74BBBC6.672.3516.25
910122.610.67BBBD6.442.665.18
101014310.21BBBB6.542.597.50
1110161.88.55BBBC6.672.4512.41
1210182.29.85BBBB6.832.3815.18
13111239.07BBBB6.722.3815.18
1411142.69.34BBBB6.442.2420.09
1511162.210.21BBBB6.672.3017.86
1611181.810.55BBBB6.862.3815.00
Note: Splash “A”, “B”, “C” and “D” mean “A splash”, “B splash”, “C splash” and “no splash”, respectively.
Table
Table 3. Electrochemical parameters of HC340LAD + ZM and HC340LA polarization curves.
Table 3. Electrochemical parameters of HC340LAD + ZM and HC340LA polarization curves.
SampleRegionEcorr/VIcorr/(mA·cm−2)
HC340LABase metal−0.5724.258 × 10−4
Soldered dot−0.7053.602 × 10−3
HC340LAD + ZMBase metal−1.1675.934 × 10−5
Soldered dot−1.2181.323 × 10−4
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Chen, X.; Peng, X.; Yuan, X.; Xiong, Z.; Lu, Y.; Lu, S.; Peng, J. Effect of Zinc Aluminum Magnesium Coating on Spot-Welding Joint Properties of HC340LAD + ZM Steel. Appl. Sci. 2022, 12, 9072. https://doi.org/10.3390/app12189072

AMA Style

Chen X, Peng X, Yuan X, Xiong Z, Lu Y, Lu S, Peng J. Effect of Zinc Aluminum Magnesium Coating on Spot-Welding Joint Properties of HC340LAD + ZM Steel. Applied Sciences. 2022; 12(18):9072. https://doi.org/10.3390/app12189072

Chicago/Turabian Style

Chen, Xiang, Xinjie Peng, Xinjian Yuan, Ziliu Xiong, Yue Lu, Shenghai Lu, and Jian Peng. 2022. "Effect of Zinc Aluminum Magnesium Coating on Spot-Welding Joint Properties of HC340LAD + ZM Steel" Applied Sciences 12, no. 18: 9072. https://doi.org/10.3390/app12189072

APA Style

Chen, X., Peng, X., Yuan, X., Xiong, Z., Lu, Y., Lu, S., & Peng, J. (2022). Effect of Zinc Aluminum Magnesium Coating on Spot-Welding Joint Properties of HC340LAD + ZM Steel. Applied Sciences, 12(18), 9072. https://doi.org/10.3390/app12189072

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.