Fabrication of Luminescent Antireflective Coatings with CaMoO4:Eu3+/Ag Composite Structure
Next Article in Special Issue
Oxidation Behavior and Mechanism of Al4SiC4 in MgO-C-Al4SiC4 System
Previous Article in Journal
Ammonia Generation via a Graphene-Coated Nickel Catalyst
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Coatings
Volume 7
Issue 6
10.3390/coatings7060073
coatings-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Combustion Synthesis of UHTC Composites from Ti–B4C Solid State Reaction with Addition of VIb Transition Metals

by
Chun-Liang Yeh
* and
Wei-Zuo Lin
Department of Aerospace and Systems Engineering, Feng Chia University, Taichung 40724, Taiwan
*
Author to whom correspondence should be addressed.
Coatings 2017, 7(6), 73; https://doi.org/10.3390/coatings7060073
Submission received: 10 May 2017 / Revised: 24 May 2017 / Accepted: 27 May 2017 / Published: 1 June 2017
(This article belongs to the Special Issue Ultrahigh Temperature Ceramic Coatings and Composites)
Browse Figures
Versions Notes

Abstract

:
UHTC composites were prepared by self-propagating high-temperature synthesis (SHS) from the Ti–B4C reaction system with addition of Cr, Mo, and W. The starting sample composition was formulated as (3−x)Ti + B4C + xMe with x = 0.1–1.0 and Me = Cr, Mo, or W. For all samples conducted in this study, self-sustaining combustion was well established and propagated with a distinct reaction front. With no addition of Cr, Mo, or W, solid state combustion of the 3Ti + B4C sample featuring a combustion front temperature (Tc) of 1766 °C and a combustion wave velocity (Vf) of 16.5 mm/s was highly exothermic and produced an in situ composite of 2TiB2 + TiC. When Cr, Mo, or W was adopted to replace a portion of Ti, the reaction exothermicity was lowered, and hence, a significant decrease in Tc (from 1720 to 1390 °C) and Vf (from 16.1 to 3.9 mm/s) was observed. With addition of Cr, Mo, and W, the final products were CrB-, MoB-, and WB-added TiB2–TiC composites. The absence of CrB2, MoB2, and WB2 was attributed partly to the loss of boron from thermal decomposition of B4C and partly to lack of sufficient reaction time inherent to the SHS process.

1. Introduction

Several borides and carbides of transition metals of the groups IVb and Vb are considered as ultra-high temperature ceramics (UHTCs) based on their melting temperatures in excess of 3000 °C and other properties, such as high hardness, high flexural strength, high thermal conductivity, and excellent resistance to thermal shock and corrosion [1,2,3]. UHTC composites—for example TiB2–TiC, ZrB2–SiC, ZrB2–TaB2, and NbB2–SiC—have been of great importance for extreme environment applications requiring high thermal-shock resistance and durability against a rapid temperature change [4,5,6,7]. In addition, borides of chromium and tungsten have been recognized as effective reinforcements for UHTCs to improve densification, mechanical properties, and oxidation resistance [8,9].
Hot pressing (HP) and spark plasma sintering (SPS) are two most commonly-used fabrication routes to prepare UHTCs and composites on their basis [2,3,4,5,6,7,8]. Combustion synthesis in the mode of self-propagating high-temperature synthesis (SHS) has been a promising alternative, which takes advantage of highly exothermic reactions, and hence, has merits of low energy requirement, short processing time, simplicity, and high-purity products [10,11,12]. A number of borides and carbides of transition metals (mostly the groups IVb and Vb) have been produced by the SHS process from the elemental powder compacts of their corresponding stoichiometries [13,14,15,16,17]. Due to the low reaction enthalpy, however, solid state combustion between the transition metals of the group-VIb (Cr, Mo, and W) and boron or carbon is not feasible [12].
Of particular interest for this study is the TiB2–TiC composite, because not only is it an outstanding UHTC [18,19], but it can also be produced through the SHS scheme with Ti and B4C as the precursors [20,21,22,23,24,25]. The SHS process allows in situ synthesis of multi-phase materials, as in the case of TiB2–TiC composites. The direct reaction of Ti with B4C at stoichiometry of Ti:B4C = 3:1 was sufficiently exothermic (∆H = −686 kJ/mol) to be self-sustaining and produced an in situ composite with TiB2:TiC = 2:1 [20]. The exothermic mixture of 3Ti + B4C has also been employed to fabricate TiB2/TiC-based cermets with different metal binders such as Al, Cu, and Ni [21,22,23]. By combining a thermite reagent of CrO3 + 2Al into the 3Ti + B4C reaction system, Huang et al. [24] obtained TiB2–TiC composites through combustion synthesis under an ultra-high gravity field which improved microstructure refinement, relative density, fracture toughness, and bending strength of the final products. Combustion synthesis of the TiC-rich composites with TiB2:TiC = 1:2 and 1:4 was carried out in the Ti–B4C–C reaction system [20,25]. Deorsola et al. [25] adopted carbon nanotubes in partial substitution for graphite in the sample of 6Ti + B4C + 3C to facilitate the formation of nanostructured TiB2–TiC composite powders.
The SHS method allows the formation of a variety of powders (including TiB2, TiC, ZrB2, ZrC, Cr3C2, TiN, NiAl, TiAl, FeAl, and MoSi2) in size ranges and with an external morphology suitable as feedstock materials for different thermal spraying techniques [26]. Different kinds of plasma spraying (PS) methods [27,28], as well as detonation spraying (DS), flame spraying (FS), and high-velocity oxygen-fuel spraying (HVOF) are in common use for depositing protective coatings from SHS powders [26,29,30].
This study made the first attempt to explore in situ UHTC composites formed from the Ti–B4C combustion system with addition of Cr, Mo, and W. As mentioned above, borides of the group-VIb metals were effective reinforcements for UHTCs, but they failed to be produced by the SHS method. Therefore, this study aimed to achieve simultaneous formation of borides of the group-VIb metals along with TiB2 and TiC from the Ti–B4C–Me (Me = Cr, Mo, and W) combustion systems. The phase composition of the SHS-derived products was examined. The influence of Cr, Mo, and W addition was investigated on combustion sustainability, flame-front velocity, and reaction temperature.

2. Materials and Methods

The starting materials adopted by this study included Ti (Alfa Aesar, Ward Hill, MA, USA, <45 µm, 99.5%), Cr (Alfa Aesar, <45 µm, 99.5%), Mo (Strem Chemicals, Newburyport, MA, USA, <45 µm, 99.9%), W (Alfa Aesar, <45 µm, 99.9%), and B4C (Showa Chemical, Tokyo, Japan, <10 µm, 99.5%). The reactant mixtures were prepared based on a modification of the 3Ti + B4C stoichiometry. The VIb group transition metal (Me = Cr, Mo, and W) was introduced to replace a portion of Ti, as expressed in Reaction (1).
(3 − x)Ti + B4C + xMe → (2 − x)TiB2 + TiC + xMeB
where the stoichiometric coefficient, x, signifies the content of Cr, Mo, or W in the reactant mixture. The amounts of Cr, Mo, and W varying from x = 0.1–1.0 were considered. Because the reaction mechanism of simultaneous synthesis of TiB2 and TiC is characterized firstly by the formation of TiC phase [18,31], the group-VIb metal added into the Ti–B4C reaction system is supposed to react with boron and yield a boride compound denoted by MeB in Reaction (1).
The reactant powders were well mixed and compressed into cylindrical test specimens 7 mm in diameter, 12 mm in length, with a relative density of 55%. The SHS reaction was conducted under high-purity (99.99%) argon of 0.15 MPa. The ignition was accomplished by a heated tungsten coil with a voltage of 60 V and a current of 1.5 A. The combustion process was recorded by a color CCD video camera (Pulnix TMC-7, Babb, MT, USA) at 30 frames per second. The exposure time of each recorded image was set at 0.1 ms. The combustion wave velocity was determined from the time sequences of recorded images. To facilitate the accurate measurement of instantaneous locations of the combustion front, a beam splitter (Rolyn Optics, Covina, CA, USA), with a mirror characteristic of 75% transmission and 25% reflection, was used to optically superimpose a scale onto the image of the test sample. The combustion temperature of the sample was measured by a fine-wire (125 µm) Pt/Pt-13% Rh thermocouple attached on the sample surface. The synthesized products were analyzed by an X-ray diffractometer (XRD) (Bruker, D8 SSS, Billerica, MA, USA) to identify the phase constituents. Details of the experimental methods were reported elsewhere [32].

3. Results and Discussion

3.1. Combustion Front Velocity and Combustion Temperature

Two typical combustion sequences illustrated in Figure 1a,b are associated with powder compacts of 2.5Ti + B4C + 0.5Mo and 2.1Ti + B4C + 0.9Cr, respectively. For either SHS process, a distinct combustion front formed upon ignition and propagated along the sample compact in a self-sustaining manner. It is evident that solid state combustion of Figure 1a is not only faster but more glowing than that of Figure 1b. This was caused by the fact that the formation enthalpy of MoB (∆Hf = −123.9 kJ/mol) is larger than that of CrB (∆Hf = −78.9 kJ/mol) [33]. As a result, the Mo-added sample is more energetic than the sample containing Cr. Besides, the content of Mo (x = 0.5) in the sample of Figure 1a is less than that of Cr (x = 0.9) in the sample of Figure 1b. To be presented later, the existence of TiB was found in the final products of Cr- and Mo-added samples and a larger amount of TiB was detected from the sample containing Mo. Because the formation of TiB (∆Hf = −160.2 kJ/mol) is very exothermic, the stronger combustion luminosity observed in Figure 1a might be due partly to the formation of more TiB. It should be noted that the addition of Cr, Mo, or W into the Ti–B4C combustion system reduces the overall reaction exothermicity, since TiB2 has a much larger formation enthalpy (∆Hf = −315.9 kJ/mol) than CrB, MoB, and WB [33]. As shown in Figure 1, the burned samples were slightly elongated. This resulted in the synthesized composites with a relative density of about 50–53%.
Figure 2 presents the effect of Cr, Mo, and W addition on Vf of the sample. As can be seen in Figure 2, the flame-front velocity of the 3Ti + B4C sample is as high as 16.5 mm/s but the flame velocity decreases significantly with increasing content of Cr, Mo, and W. This implies a dilution effect on combustion. Among three different Me-containing samples, the Mo-added sample exhibits the highest combustion wave velocity which decreases from 16.1 to 7.0 mm/s as the content of Mo increases from x = 0.1 to 1.0. For the other two types of samples with x = 0.1 to 1.0, the Cr-added sample has a higher flame-front velocity descending from 15.9 to 4.6 mm/s, compared to a declining velocity from 15.6 to 3.9 mm/s for the W-added sample. The slow combustion wave observed for the W-added sample was attributed to the relatively low formation enthalpy of WB (∆Hf = −66.1 kJ/mol).
Typical combustion temperature profiles of the powder compacts containing different amounts of Cr, Mo, and W are plotted in Figure 3. The abrupt rise in temperature signifies rapid arrival of the combustion wave and the peak value stands for the combustion front temperature. Profile #1 of Figure 3 is associated with the 3Ti + B4C sample which shows a reaction front temperature reaching up to 1766 °C. Profiles #2 and #3, having their peak temperatures of 1684 and 1582 °C, were measured from Mo-added samples with x = 0.4 and 0.7, respectively. Temperature profiles (#4 and #5) of the Cr-added samples with x = 0.6 and 0.9 exhibited combustion front temperatures of 1511 and 1462 °C, respectively. In addition, the lowest reaction front temperature of about 1394 °C was observed in the W-added sample of 2Ti + B4C + W (x = 1.0). In summary, the temperature measurement indicated that the addition of Cr, Mo, or W caused a decrease in the combustion front temperature that was further lowered as the amounts of Cr, Mo, and W increased. In agreement with the above observations, the Mo-added sample is the most exothermic while the W-containing sample is the least. The presence of TiB in the synthesized composites of Cr- and Mo-added samples could contribute partly to the findings that Vf and Tc of the Cr- and Mo-added samples are higher than those of the W-added samples. Moreover, the dependence of combustion temperature on sample stoichiometry is in a manner consistent with that of combustion wave velocity.

3.2. Phase Constituents of Synthesized Composites

The XRD pattern of Figure 4a indicates that phase constituents of the final product obtained from the 3Ti + B4C sample consists of no more than TiB2 (JCPDS 85-2083) and TiC (JCPDS 89-3828). This implies a complete conversion from the reactants to products. For the Cr-added sample of 2Ti + B4C + Cr, Figure 4b shows the production of CrB (JCPDS 89-3587) and TiB (JCPDS 89-3922) in addition to TiB2 and TiC. Formation of chromium monoboride (CrB) rather than diboride (CrB2) suggests the possibility of loss of boron from thermal decomposition of B4C during the SHS process. Because thermal dissociation of B4C yielded gaseous boron [34], a small amount of B(g) escaped from the porous powder compact during the SHS process. This caused a loss of boron, which was also responsible for the presence of TiB.
Figure 5a reveals that the composite synthesized from the Mo-added sample of 2Ti + B4C + Mo is composed of TiB2, TiC, TiB (JCPDS 73-2148), and MoB (JCPDS 06-0644). The presence of MoB and TiB was likely due to the loss of boron at the elevated temperatures. It should be noted that TiB of the cubic phase was formed in the final product of the Cr-added sample, while TiB of the orthorhombic phase was identified in the product of the Mo-added sample. The XRD signatures of TiB in Figure 4a and Figure 5a correspond to their different phases.
When W was utilized as the substituent for a part of Ti, as shown in Figure 5b, the SHS-derived composite was a mixture of TiB2, TiC, and WB (JCPDS 73-1769). It is noteworthy that monoborides (CrB, MoB, and WB) were produced from the Ti–B4C system with additions of Cr, Mo, and W. The absence of diborides (CrB2, MoB2, and WB2) might be also due to the lack of sufficient reaction time stemming from the fast combustion wave and rapid cooling rate inherent to the SHS process. This study demonstrated the production of Cr-, Mo-, and WB-added TiB2–TiC composites by an energy- and time-saving fabrication route.
Figure 6a reveals the typical microstructure of fracture surface of the composite synthesized from the 3Ti + B4C sample. The microstructure consisted of equiaxed TiC grains and TiB2 platelets with an aspect ratio of about 2. For the Cr-added sample of 2Ti + B4C + Cr, Figure 6b exhibits a granular morphology for its resultant composite which is a mixture of TiB2, TiC, TiB, and CrB. Agglomeration of micro-sized grains is obvious. Figure 6c illustrates the microstructure of a WB-added TiB2–TiC composite obtained from the W-added sample of 2Ti + B4C + W. As can be seen in Figure 6c, TiB2 platelets and TiC and WB grains are tightly aggregated. According to Figure 6a–c, it is suggested that the morphologies of SHS-derived products from the Ti–B4C samples with and without addition of Cr, Mo, and W have no substantial difference.

4. Conclusions

Fabrication of in situ UHTC composites from Cr-, Mo-, and W-added Ti–B4C systems was studied by the SHS process. The reactant stoichiometry was designed as (3−x)Ti + B4C + xMe with x = 0.1–1.0 and Me = Cr, Mo, or W. With no addition of Cr, Mo, and W, solid state combustion of the 3Ti + B4C sample was highly exothermic and characterized by a reaction front temperature of 1766 °C and a combustion wave velocity of 16.5 mm/s. The product of the 3Ti + B4C sample was a 2TiB2 + TiC composite. When Cr, Mo, and W were adopted in partial substitution for Ti, the reaction exothermicity was reduced, thus leading to a considerable decrease in the combustion temperature and velocity. With the increase of Cr, Mo, and W from x = 0.1–1.0, the reaction front temperature decreased from about 1720 to 1390 °C and flame-front speed from 16.1 to 3.9 mm/s. Depending on the formation enthalpies of CrB, MoB, and WB, the Mo-added reaction is the most exothermic and the W-containing sample is the least. The XRD patterns showed that with the addition of Cr, Mo, and W, the final products contained CrB, MoB, and WB simultaneously formed along with TiB2 and TiC. Besides, the presence of TiB was detected in the products of Cr- and Mo-added samples. Formation of monoborides (TiB, CrB, MoB, and WB) could be a consequence of the loss of boron at elevated temperatures and lack of sufficient reaction time for further phase transformation. In summary, the SHS process was shown to be an in situ fabrication route to preparing Cr-, Mo-, and WB-added TiB2–TiC composites.

Acknowledgments

This research was sponsored by the Ministry of Science and Technology (Taiwan) under the grant of MOST 105-2221-E-035-039-MY2. Authors are grateful for the Precision Instrument Support Center of Feng Chia University in providing materials analytical facilities.

Author Contributions

Chun-Liang Yeh conceived and designed the experiments, analyzed the experimental data, supervised the work, and wrote the paper. Wei-Zuo Lin performed the SHS experiments and materials analysis.

Conflicts of Interest

The authors declare no conflict of interest. The founding sponsors had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.

References

  1. Fahrenholtz, W.G.; Hilmas, G.E.; Talmy, I.G.; Zaykoski, J.A. Refractory diborides of zirconium and hafnium. J. Am. Ceram. Soc. 2007, 90, 1347–1364. [Google Scholar] [CrossRef]
  2. Chakraborty, S.; Debnath, D.; Mallick, A.R.; Das, P.K. Mechanical and thermal properties of hot pressed ZrB2 system with TiB2. Int. J. Refract. Met. Hard Mater. 2014, 46, 35–42. [Google Scholar] [CrossRef]
  3. Gürcan, K.; Ayas, E. In-situ synthesis and densification of HfB2 ceramics by the spark plasma sintering technique. Ceram. Int. 2017, 43, 3547–3555. [Google Scholar] [CrossRef]
  4. Wang, L.; Liu, H.; Huang, C.; Liu, X.; Zou, B.; Zhao, B. Microstructure and mechanical properties of TiC–TiB2 composite cermet tool materials at ambient and elevated temperature. Ceram. Int. 2016, 42, 2717–2723. [Google Scholar] [CrossRef]
  5. Guo, W.M.; Yang, Z.G.; Zhang, G.J. Comparison of ZrB2–SiC ceramics with Yb2O3 additive prepared by hot pressing and spark plasma sintering. Int. J. Refract. Met. Hard Mater. 2011, 29, 452–455. [Google Scholar] [CrossRef]
  6. Demirskyi, D.; Vasylkiv, O. Flexural strength behavior of a ZrB2–TaB2 composite consolidated by non-reactive spark plasma sintering at 2300 °C. Int. J. Refract. Met. Hard Mater. 2017, 66, 31–35. [Google Scholar] [CrossRef]
  7. Demirskyi, D.; Vasylkiv, O. Mechanical properties of SiC–NbB2 eutectic composites by in situ spark plasma sintering. Ceram. Int. 2016, 42, 19372–19385. [Google Scholar] [CrossRef]
  8. Murthy, T.S.R.Ch.; Sonber, J.K.; Subramanian, C.; Fotedar, R.K.; Gonal, M.R.; Suri, A.K. Effect of CrB2 addition on densification, properties and oxidation resistance of TiB2. Int. J. Refract. Met. Hard Mater. 2009, 27, 976–984. [Google Scholar] [CrossRef]
  9. Momozawa, A.; Telle, R. Controlled precipitation of W2B4 platelets and of β-WB nanolaminates for the in situ reinforcement of ternary TiB2–W2B4–CrB2 ceramics. J. Eur. Ceram. Soc. 2012, 32, 85–95. [Google Scholar] [CrossRef]
  10. Merzhanov, A.G. Combustion and explosion processes in physical chemistry and technology of inorganic materials. Russ. Chem. Rev. 2003, 72, 289–310. [Google Scholar] [CrossRef]
  11. Liu, G.; Li, J.; Chen, K. Combustion synthesis of refractory and hard materials: A review. Int. J. Refract. Met. Hard Mater. 2013, 39, 90–102. [Google Scholar] [CrossRef]
  12. Yeh, C.L. Combustion synthesis: Principles and applications. In Reference Module in Materials Science and Materials Engineering; Hashmi., S., Ed.; Elsevier: Amsterdam, The Netherlands, 2016; pp. 1–8. [Google Scholar]
  13. Radev, D.D.; Klissurski, D. Mechanochemical synthesis and SHS of diborides of titanium and zirconium. J. Mater. Synth. Process. 2001, 9, 131–136. [Google Scholar] [CrossRef]
  14. Yeh, C.L.; Chen, W.H. A comparative study on combustion synthesis of Nb-B compounds. J. Alloy. Compd. 2006, 422, 78–85. [Google Scholar] [CrossRef]
  15. Yeh, C.L.; Wang, H.J. A comparative study on combustion synthesis of Ta-B compounds. Ceram. Int. 2011, 37, 1569–1573. [Google Scholar] [CrossRef]
  16. Dunmead, S.D.; Readey, D.W.; Semler, C.E.; Holt, J.B. Kinetics of combustion synthesis in the Ti-C and Ti-C-Ni systems. J. Am. Ceram. Soc. 1989, 72, 2318–2324. [Google Scholar] [CrossRef]
  17. Yeh, C.L.; Liu, E.W. Combustion synthesis of tantalum carbides TaC and Ta2C. J. Alloy. Compd. 2006, 415, 66–72. [Google Scholar] [CrossRef]
  18. Vallauri, D.; Atías Adrián, I.C.; Chrysanthou, A. TiC-TiB2 composites: A review of phase relationships, processing and properties. J. Eur. Ceram. Soc. 2008, 28, 1697–1713. [Google Scholar] [CrossRef]
  19. Wang, D.; Wang, H.; Sun, S.; Zhu, X.; Tu, G. Fabrication and characterization of TiB2/TiC composites. Int. J. Refract. Met. Hard Mater. 2014, 45, 95–101. [Google Scholar] [CrossRef]
  20. Yeh, C.L.; Chen, Y.L. Combustion synthesis of TiC-TiB2 composites. J. Alloy. Compd. 2008, 463, 373–377. [Google Scholar] [CrossRef]
  21. Shen, P.; Zou, B.; Jin, S.; Jiang, Q. Reaction mechanism in self-propagating high temperature synthesis of TiC-TiB2/Al composites from an Al-Ti-B4C system. Mater. Sci. Eng. A 2007, 454–455, 300–309. [Google Scholar] [CrossRef]
  22. Liang, Y.H.; Wang, H.Y.; Yang, Y.F.; Zhao, R.Y.; Jiang, Q.C. Effect of Cu content on the reaction behaviors of self-propagating high-temperature synthesis in Cu-Ti-B4C system. J. Alloy. Compd. 2008, 462, 113–118. [Google Scholar] [CrossRef]
  23. Yang, Y.F.; Wang, H.Y.; Zhao, R.Y.; Liang, Y.H.; Jiang, Q.C. Effect of Ni content on the reaction behaviors of self-propagating high-temperature synthesis in the Al-Ti-B4C system. Int. J. Refract. Met. Hard Mater. 2008, 26, 77–83. [Google Scholar] [CrossRef]
  24. Huang, X.; Zhao, Z.; Zhang, L.; Wu, J. The effects of ultra-high-gravity field on phase transformation and microstructure evolution of the TiC-TiB2 ceramics fabricated by combustion synthesis. Int. J. Refract. Met. Hard Mater. 2014, 43, 1–6. [Google Scholar] [CrossRef]
  25. Deorsola, F.A.; Atias Adrian, I.C.; Ortigoza Villalba, G.A.; DeBenedatti, B. Nanostructured TiC-TiB2 composites obtained by adding carbon nanotubes into the self-propagating high-temperature synthesis process. Mater. Res. Bull. 2011, 46, 995–999. [Google Scholar] [CrossRef]
  26. Talako, T.; Ilyuschenko, A.; Letsko, A. SHS powders for thermal spray coating. KONA Powder Part. J. 2009, 27, 55–72. [Google Scholar] [CrossRef]
  27. Licheri, R.; Orrù, R.; Cao, G.; Crippa, A.; Scholz, R. Self-propagating combustion synthesis and plasma spraying deposition of TiC-Fe powders. Ceram. Int. 2003, 29, 519–526. [Google Scholar] [CrossRef]
  28. Xu, J.; Zou, B.; Zhao, S.; Hui, Y.; Huang, W.; Zhou, X.; Wang, Y.; Cai, X.; Cao, X. Fabrication and properties of ZrC–ZrB2/Ni cermet coatings on a magnesium alloy by atmospheric plasma spraying of SHS powders. Ceram. Int. 2014, 40, 15537–15544. [Google Scholar] [CrossRef]
  29. Xanthopoulou, G.; Marinou, A.; Vekinis, G.; Lekatou, A.; Vardavoulias, M. Ni-Al and NiO-Al composite coatings by combustion-assisted flame spraying. Coatings 2014, 4, 231–252. [Google Scholar] [CrossRef]
  30. Xanthopoulou, G.; Marinou, A.; Karanasios, K.; Vekinis, G. Combustion synthesis during flame spraying (“CAFSY”) for the production of catalysts on substrates. Coatings 2017, 7, 14. [Google Scholar] [CrossRef]
  31. Contreras, L.; Turrillas, X.; Vaughan, G.B.M.; Kvick, Å.; Rodríguez, M.A. Time-resolved XRD study of TiC-TiB2 composites obtained by SHS. Acta Mater. 2004, 52, 4783–4790. [Google Scholar] [CrossRef]
  32. Yeh, C.L.; Chen, Y.L. An experimental study on self-propagating high-temperature synthesis in the Ta-B4C system. J. Alloy Compd. 2009, 478, 163–167. [Google Scholar] [CrossRef]
  33. Binnewies, M.; Milke, E. Thermochemical Data of Elements and Compounds; Wiley-VCH Verlag GmbH: Weinheim, NY, USA, 2002. [Google Scholar]
  34. Hildenbrand, D.L.; Hall, W.F. The decomposition pressure of boron carbide and the heat of sublimation of boron. J. Phys. Chem. 1964, 68, 989–993. [Google Scholar] [CrossRef]
Coatings 07 00073 g001 550
Figure 1. Time sequences of recorded images illustrating self-sustaining combustion propagating along powder compacts with stoichiometries of (a) 2.5Ti + B4C + 0.5Mo and (b) 2.1Ti + B4C + 0.9Cr.
Figure 1. Time sequences of recorded images illustrating self-sustaining combustion propagating along powder compacts with stoichiometries of (a) 2.5Ti + B4C + 0.5Mo and (b) 2.1Ti + B4C + 0.9Cr.
Coatings 07 00073 g001
Coatings 07 00073 g002 550
Figure 2. Variations of flame-front velocity with contents of Cr, Mo, and W added into Ti-B4C samples.
Figure 2. Variations of flame-front velocity with contents of Cr, Mo, and W added into Ti-B4C samples.
Coatings 07 00073 g002
Coatings 07 00073 g003 550
Figure 3. Combustion temperature profiles of Ti-B4C samples added with different amounts of Cr, Mo, or W.
Figure 3. Combustion temperature profiles of Ti-B4C samples added with different amounts of Cr, Mo, or W.
Coatings 07 00073 g003
Coatings 07 00073 g004 550
Figure 4. XRD patterns of SHS-derived composites from samples with stoichiomerties of (a) 3Ti + B4C and (b) 2Ti + B4C + Cr.
Figure 4. XRD patterns of SHS-derived composites from samples with stoichiomerties of (a) 3Ti + B4C and (b) 2Ti + B4C + Cr.
Coatings 07 00073 g004
Coatings 07 00073 g005 550
Figure 5. XRD patterns of SHS-derived composites from samples with stoichiomerties of (a) 2Ti + B4C + Mo and (b) 2Ti + B4C + W.
Figure 5. XRD patterns of SHS-derived composites from samples with stoichiomerties of (a) 2Ti + B4C + Mo and (b) 2Ti + B4C + W.
Coatings 07 00073 g005
Coatings 07 00073 g006 550
Figure 6. SEM micrographs of SHS-derived composites from samples with stoichiomerties of (a) 3Ti + B4C, (b) 2Ti + B4C + Cr, and (c) 2Ti + B4C + W.
Figure 6. SEM micrographs of SHS-derived composites from samples with stoichiomerties of (a) 3Ti + B4C, (b) 2Ti + B4C + Cr, and (c) 2Ti + B4C + W.
Coatings 07 00073 g006

Share and Cite

MDPI and ACS Style

Yeh, C.-L.; Lin, W.-Z. Combustion Synthesis of UHTC Composites from Ti–B4C Solid State Reaction with Addition of VIb Transition Metals. Coatings 2017, 7, 73. https://doi.org/10.3390/coatings7060073

AMA Style

Yeh C-L, Lin W-Z. Combustion Synthesis of UHTC Composites from Ti–B4C Solid State Reaction with Addition of VIb Transition Metals. Coatings. 2017; 7(6):73. https://doi.org/10.3390/coatings7060073

Chicago/Turabian Style

Yeh, Chun-Liang, and Wei-Zuo Lin. 2017. "Combustion Synthesis of UHTC Composites from Ti–B4C Solid State Reaction with Addition of VIb Transition Metals" Coatings 7, no. 6: 73. https://doi.org/10.3390/coatings7060073

APA Style

Yeh, C. -L., & Lin, W. -Z. (2017). Combustion Synthesis of UHTC Composites from Ti–B4C Solid State Reaction with Addition of VIb Transition Metals. Coatings, 7(6), 73. https://doi.org/10.3390/coatings7060073

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.