Next Article in Journal
Surface Structuring of Diamond-Like Carbon Films by Chemical Etching of Zinc Inclusions
Previous Article in Journal
Functional Performance of Stone Mastic Asphalt Pavements in Spain: Acoustic Assessment
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Coatings
Volume 9
Issue 2
10.3390/coatings9020124
coatings-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Coating Sand with New Hydrophobic and Superhydrophobic Silica/Paraffin Wax Nanocapsules for Desert Water Storage and Transportation

by
Ayman M. Atta
1,*,
Mahmood M. S. Abdullah
1,
Hamad A. Al-Lohedan
1 and
Nermen H. Mohamed
2
1
Department of Chemistry, College of Science, King Saud University, Riyadh 11451, Saudi Arabia
2
Refining Department, Egyptian Petroleum Research Institute (EPRI), Nasr City, Cairo 11727, Egypt
*
Author to whom correspondence should be addressed.
Coatings 2019, 9(2), 124; https://doi.org/10.3390/coatings9020124
Submission received: 6 January 2019 / Revised: 30 January 2019 / Accepted: 13 February 2019 / Published: 17 February 2019
Browse Figures
Versions Notes

Abstract

:
Paraffin wax emulsions have gained immense attention as a cheap, environment-friendly, and aroma-free material for preparing superhydrophobic coatings. In this work, paraffin wax (PWs) capsules consisting of hydrophobic silica nanoparticles were used for coating desert sand. Different types of the hydrophobic silica nanoparticles, modified with new oleylamino- and oleylamide silane precursors, were prepared in the presence and absence of paraffin waxes. The particle sizes, surface charges, thermal stability, surface morphologies, and wetting characteristics of these nanoparticles were investigated. The combination of these superhydrophobic silica nanoparticles and desert sand, showed excellent water repellency; stable water droplets remained on the sand surface, without any wetting or permeation. Furthermore, the mixing of the superhydrophobic sand with untreated sand (mixing ratio 1:10 wt %), with a thickness of 2 cm, sustained a great water-holding capacity with a water column height of 35 cm. The good thermal stability of the PWs capsules containing hydrophobic silica nanoparticles, along with their good water-holding capacity, make them potential candidates for developing superhydrophobic sand for desert water storage and transportation.

1. Introduction

Sand dunes are an abundant natural resource in the desert, are characterized with a low water storage capacity and suffer from a temporary shortage of water especially when cultivated under arid conditions. Sand consists of hydrophilic silica, which attracts water and facilitates its flow to the ground, thus, adversely affecting the plantation, even under expensive irrigation systems such as sprinkling or trickling. Previously, hydrogels were used to increase the water holding capacity of sandy soils [1,2,3,4,5,6]. Their biodegradation, difficult soil-particle coating, low water absorption because of the presence of salts, and high manufacture cost, has limited their applications [1]. Recently, the use of “superhydrophobic sand” has been proposed, to realize the storage and transportation of the surface water of sandy soils [7,8,9,10,11,12]. Various methods, such as the combustion of oil waste [13], crude oil emulsion [14], paraffin wax [15], natural wax [16], and oil and fatty acids [17] have been proposed for the development of hydrophobic coatings. The hydrophobic petroleum waxes were divided into three principle groups—paraffin waxes, microcrystalline waxes, and petrolatum. The paraffin waxes contained long-chain hydrocarbons that can be used to form a hydrophobic surface and exhibited water-repellency, on several substrates [15]. However, these coatings either did not adhere well to the sand surface or were mechanically unstable. Recently, it has been proposed that the application of nanomaterials on the sand surface, can combat desertification and encourage plant growth in arid climates. Moreover, superhydrophobic sand prevents the diffusion of underground salt, which affects the growth of plants. The application of the superhydrophobic property of certain nanomaterials for mitigating environmental and resource issues, is a promising research topic of global significance. The development of low-cost environmental-friendly superhydrophobic, thermally stable, and good adhesion nanomaterials, is a challenge for desert greening.
Silica nanomaterials and silicon derivatives have gained immense attention for the development of superhydrophobic sand because of their excellent adhesion with sand and glass surfaces [18,19,20,21,22,23]. Organic silicone derivatives, such as octadecyltrichlorosilane have also been used for coating sand to produce hydrophobic sand [24]. Raw hydrophobic sand, contaminated with oil, can also be used as a water repellent [25]. This work aims to modify new hydrophobic silane precursors to hydrolyze with tetramethoxysilane (TMS), for the formation of superhydrophobic silica nanoparticles (SNPs). In this respect, oleylamino- and oleylamide were prepared as hydrophobic silane precursors. The oleyl groups can act as hydrophobic coats, after hydrolyzing the alkoxy silane group with tetraethoxysilane (TEOS) in an alkaline-medium-based on sol–gel technique, to produce hydrophobic silica nanoparticles (HSNP). Moreover, the oleyl groups can be interacted with paraffin waxes, during the hydrolysis of silane precursors with TEOS, in the presence of paraffin wax emulsions, to produce hydrophobic silica capped with paraffin waxes (HOSNP). Hydrophobically coating fine raw sand, with HSNP and HOSNP, is another goal of the present work to increase the adhesion of paraffin waxes on the sand surfaces, due to the presence of the silica nanoparticles, to produce superhydrophobic sand. The water storage capacities of the superhydrophobic sand prepared and its blend with the unmodified desert sand, were investigated, to evaluate its water storage and transportation properties. The water-holding capacity, thermal stability, and anti-flow dragging performance of, both, the prepared and the unmodified blend were also evaluated.

2. Materials and Methods

2.1. Materials

All chemicals used in the present work were analytical with high purity grades and were supplied from Aldrich-Sigma Chemicals Co. (St. Louis, MO, USA). Vinyl trimethoxy silane (VTS), tetraethoxysilane (TEOS), and γ-aminopropyltriethoxysilane (APS) were modified with oleic acid (OA) and oleylamine (OAE), to synthesize hydrophobic silane precursors. Hexadecyltrimethylammonium bromide (CTAB) was used as a cationic surfactant, to prepare the wax emulsion. El-Ameria light slack wax (Alexanderia, Egypt) was subjected to fractional crystallization, using butyl acetate as the solvent, at a fractionating temperature of 20 °C, solvent feed ratio of 4/1, and washing ratio of 2/1, in order to separate the paraffin waxes [25]. The fine raw desert sand obtained from the Saudi desert was only cleaned with deionized water. The adhesive tape (3M) was obtained from a commercial source (3M Science applied for life company, Minneapolis, MN, USA).

2.2. Techniques

2.2.1. Preparation of Hydrophobic Silane Precursors

Alkoxy silane oleylamide (SOA) was prepared by reacting OA (1 mol) with APS (1.1 mol), in a reaction vessel, at 180 °C, for 2 h, under a nitrogen atmosphere. SOA was also synthesized at a low temperature, as follows: Equimolar ratios of OA and APS were evenly dispersed in an ethanol solution (ethanol/water = 9:1) and the mixture was stirred at room temperature, for 1.5 h. The SOA yields at high and low temperature were 92.1% and 83.5%, respectively.
Vinyltrimethoxy olylaminosilane (VOS) was prepared by reacting OAE (0.01 mol) with the vinyl group of VTS (0.05 mol), in an 80 mL tetrahydrofuran (THF), while stirring at 65 °C, for 4 h. THF was removed using a rotary evaporator under pressure, to obtain OVA (yield 93.7%).

2.2.2. Preparation of the Paraffin Wax Emulsion

Paraffin waxes have a narrow melting temperature range of 51–54 °C. The components of the wax used in this study were mainly normal alkenes, with C18–C38 carbon atoms. The paraffin wax emulsion was prepared by mixing the melted paraffin wax with the CTAB surfactant, by slowly adding water, under gentle agitation, using a magnetic stirrer. The addition rate of water was kept constant, at approximately 1.0 mL·min−1. The emulsification temperature was varied from 50 to 80 °C. The PWs concentration of the emulsion was kept constant at 20.0 wt %, while the CTAB surfactant concentration was 8.0 wt %.

2.2.3. Preparation of the Superhydrophobic Silica/Wax Capsules

Hydrophobic silica nanoparticles (HSNPs) were prepared as follows: TEOS (0.8 mL) was added to methanol (100 mL) and kept in a sonication bath. After 10 min, a known volume of VOS (0.4 g), and SOA (0.4 g) were added to it, while sonicating. After 20 min, 28% ammonium hydroxide (24 mL) was added to the reaction mixture, as the catalyst to promote the condensation reaction. Sonication was continued for a further 60 min, to obtain a white turbid suspension. The HSNPs were formed by hydrolyzing the silicon precursors (VOS and SOA) with TEOS, in the presence of ammonia and sonication. The obtained HSNPs suspension was dispersed in water/ethanol (50/50 vol %), under gentle agitation, for 5 min, in order to stop the hydrolysis, separate, and purify the HSNPs. The reaction mixture was then ultracentrifuged at 8000 rpm, for 30 min. This procedure was repeated five times, to purify the HSNPs. The same procedure was used to prepare HOSNPs in the presence of the PWs emulsion (2 g), which was added after its dispersion in methanol (100 mL).
In a typical procedure, the wax emulsion (2 g) was dissolved in 100 mL of deionized water, under stirring. To this mixture, concentrated ammonia solution (7.0 mL; 28 wt %) was added to form a clear solution. A mixture of n-hexane (20 mL), TEOS (3 mL), VOS (1 mL), and SOA (1 mL) was added, dropwise, for over 30 min, under continuous stirring, to the obtained clear solution. As the reaction proceeded at 35 °C, a homogeneous milky colloidal solution was gradually formed, under continuous stirring (200 rpm). This solution was dispersed in water/ethanol (50/50 vol %), under gentle agitation for 5 min, and the resulting mixture was ultracentrifuged at 8000 rpm, for 30 min, to separate the emulsified silica NPs (EOSNP1). This procedure was repeated five times to purify the EOSNP1. These procedures were repeated by using different weight percentages of the PWs, ranged from 1 to 20 wt %, related to the TEOS, the SOA, and the VOS, to prepare a series of EOSNP1 samples.
Emulsified silica NPs (EOSNP2) was prepared without using the n-hexane which was replaced by chloroform. The paraffin wax emulsion (2 g) was mixed with distilled water (100 mL), under vigorous magnetic stirring, for 1 h. The TEOS (2 g), the VOS (1 mL), and the SOA (1 mL) were dispersed in chloroform (20 mL) and then added to the reaction mixture, which was stirred for another 30 min. Emulsion was formed and stirred for a further 4 h, in the presence of APS (0.54 g and 1.5 mL of water). The resulting solution was aged, overnight, to obtain the silica-coated wax nanoparticles (EOSNP2).

2.3. Characterization of the PWs/Hydrophobic Silica Nanocapsules

Thermogravimetric analysis (TGA; STA 449 C instrument, Netzsch Group, New Castle, DE, USA) was carried out to determine the thermal stability and contents of the silica capsules. The samples were heated at a heating rate of 283 K·min−1, under a dynamic nitrogen flow of 45 mL·min−1. The morphology of the silica capsules was evaluated using a transmission electron microscope (TEM, JEM-2100 F (JEOL, Tokyo, Japan) at an acceleration voltage of 200 KV). A scanning electron microscope (SEM; JSM 6510LV, JEOL, Tokyo, Japan) was used to examine the surface morphology of the silica capsules. Dynamic light scattering (DLS; Zetasizer Nano ZS, Malvern Instrument Ltd., Malvern, UK) was used to investigate the particle size and the polydispersity indices (PDI) of the silica nanocapsules in the n-hexane solutions at 25 °C. The zeta potentials of the silica nanocapsules were determined in ethanol/water dispersions. A drop shape analyzer (DSA-100, Krüss GmbH, Hamburg, Germany) was used to determine the contact angles (with water) of the hydrophobic silica capsules using the sessile drop method, at room temperature. The receding and advancing contact angles were measured after polishing the glass plate, to produce a rough surface followed by washing with ethanol, 1 M HCl, detergent, and acetone. The glass plate was dried and treated with ozone, before applying and casting the dispersions of the HSNPs in the n-hexane (250 mg in 1 mL). The glass plate coated with the HSNPs was air dried and then placed in a cleaned glass cell on a small support, which was partially filled with HSNPs suspension. The glass cell was covered by the Parafilm through which a needle of the DSA-100 was inserted to produce the liquid–vapor saturated air, inside the glass cell. The contact angle measurements were repeated, five times, for reproducible and reliable contact angle measurements.

2.4. Coating of Sand with HSNPs

To obtain hydrophobic sand, 5 g of sand (diameter of 100–200 µm) was modified with 50 mL (hexane/ethanol) of 0.5% HSNPs solution, under continuous stirring for 3 h, at room temperature. All products were obtained after rinsing with ethanol, for three times, and drying at 60 °C for 1 h. The hydrophobic sand was mixed with the untreated sand (diameter of 1–3 mm), at various ratios, ranging from 1:1 to 1:10 wt %. The water absorbing capacities of the untreated and the sand treated with the HSNPs, were measured by pouring 5 mL of water into the simulated sand pits [8]. The water-holding capacities of the modified desert sand were determined from the time used to pass water (10 mL), from the 2 g of treated sand into the glass column (diameter 2 cm) [8].

3. Results and Discussion

The paraffin wax used in this study was extracted from a light slack wax, as discussed in the experimental section, and had an average carbon number of C18–C38 (Table 1). The isolated paraffin wax was also characterized by its high n-paraffin content (88.14 wt %), high iso- and cyclo-paraffin content (18.76 wt %), and very low aromatic content (2.26 wt %) (Table 1). The isolated PWs were utilized to prepare a stable PWs-in-water emulsion (PWs/W), in the presence of CTAB as a cationic surfactant (emulsion droplet sizes 750 nm). The prepared PWs emulsion was dispersed in water or methanol and was used as capping for the SNPs, as mentioned in the experimental section. The HSNPs prepared in the presence of the PWs emulsion were obtained in double oil/water/oil emulsion, as revealed by the optical microscope images shown in Figure 1a–c and the dropping test results. The silane precursors (SOA and VOS) and the TEOS used as the oil phase—in bulk or in combination with the n-hexane—were hydrolyzed in ammonia, at a reaction temperature of 35 °C, to obtain hydrophobic SNPs, in emulsion, as represented in Scheme 1. The silane and siloxane precursors were hydrolyzed at 35 °C, to prevent an increase in the size of the paraffin wax emulsion droplets. This facilitated the penetration of the paraffin wax at the interfacial film, allowing the capping of the SNPs [26]. The preparation of SNPs using this emulsion technique has been described elsewhere [27,28,29], where it was found that the morphology, particle size, and porosity of SNPs are affected by the emulsion type and the hydrolyzing conditions. Hydrophobic silica was prepared in the absence and presence of PWs (HSNP and HOSNP, respectively) in a methanol solvent. The capping of hydrophobic silica with EOSNP1 and EOSNP2, was carried out in water/hexane and water/chloroform emulsions, respectively. The wax content of the emulsions was 40 wt %. The effect of the paraffin wax on the morphology, particle size, surface charge, and thermal stability of the SNPs has been discussed in the forthcoming section.

3.1. Characterization of the PWs/Silica Nanocapsules

The particle sizes and surface charges of the HSNPs, capped with the PWs, were determined by DLS (Figure 2). The zeta potentials of the HSNPs were measured; shown in Figure 3a–d. Figure 2a–d show the particle size (nm) and PDI of the HSNPs. The SNPs, capped with wax in the hexane/water emulsion (EOSNP1; Figure 2c), showed monodispersed particles, with a size of 65 nm. Moreover, the particle size of the HOSNPs (Figure 2b) was lower than that of the HSNPs (Figure 2a). This could be attributed to the accelerated hydrolysis of the alkoxy groups of SOA and VOS, in the presence of the wax emulsion, because of the good compatibility between the wax and the oleyl groups of the SOA and the VOS, via a van der Waals interaction. The good compatibility between the reactants reduced the particle size of the resulting nanoparticles, as shown in Figure 2a,b. Moreover, the use of CTAB as the cationic surfactant as an emulsifier during the synthesis of HOSNPs, using oil-in-water (EOSNP1) or oil-in-water-oil (EOSNP2) emulsions, facilitated the dispersion of the SOA and the VOS as the oil phase, in a continuous water phase. Chloroform was added to control the hydrophilicity and particle size of the SNPs [27]. EOSNP2 showed a larger particle size than the EOSNP1 because of the use of chloroform during its synthesis, as illustrated in Figure 2c,d. This could be attributed to a better compatibility of the n-PWs with hexane, than with chloroform, as the solvent that facilitated the capping of the SNPs with PWs [30,31,32].
The surface charges of the HSNPs prepared in the absence of wax (Figure 3a) were negative, with an initial dispersion pH of about 5.4. This indicates that the absence of wax during the synthesis of the HSNPs, increased the number of hydroxyl groups, negative charges, on their surface because of the repulsive forces between the π electrons of the double bonds of the oleyl groups, in SOA and VOS [33]. The presence of wax during the preparation of the hydrophobic SNPs, changed their surface charges to positive (Figure 3b–d). These data elucidate that the CTAB (positive charges) used to prepare wax emulsion is responsible to neutralize the silica negative charges, in case of the HOSNP, EOSNP1, and EOSNP 2, due to the electrostatic attraction forces [34]. Moreover, the positive charges that originated from the amine and amide groups of the SOA and the VOS, can also add positive charges on the silica surfaces. The high surface charges of the EOSNP1 (Figure 3c) and the EOSNP2 (Figure 3d), more than that of the HOSNP (Figure 3b), elucidated that the formation of multiple emulsions by using n-hexane and chloroform is responsible for the dispersion–flocculation–redispersion of CTAB, on the prepared silica capped with paraffin wax [34].
The morphologies of the HSNP, HOSNP, EOSNP1, and the EOSNP2 samples were examined from their TEM images (Figure 4a–d). The absence of the paraffin wax, resulted in the formation of aggregates (Figure 4a). Additionally, needle-like (instead of spherical) HSNPs were obtained when the PWs emulsion was used (Figure 4b). This could be attributed to the weaker interactions of the paraffin wax with the unsaturated groups of the oleyl groups of the silicone precursors (SOA and OVS), at the silica surface. The presence of hexane, enhanced the stabilization of the paraffin wax, at the surface of the SNPs, to prevent the aggregation of the hydrocarbon chains, to produce spherical EOSNP1 (Figure 4c). The use of chloroform resulted in the formation of EOSNP2 aggregates, because of the poor solubility and dispersion of the paraffin wax in chloroform.

3.2. Thermal and Wetting Characteristics of the PWs/HSNPs Microcapsules

Thermal stability is considered to be a crucial factor affecting the applicability of hydrophobic silica capped with wax microcapsules, for coating desert sand. The thermal stabilities of the HSNP, HOSNP, EOSNP1, and EOSNP2 samples were estimated by TGA and the results are summarized in Table 2. The initial decomposition temperatures, 10% loss temperatures, degradation steps, and residual percentages (Y%) of the paraffin wax and the SNPs were determined. It should be noted that pure paraffin wax exhibits a typical one-step thermal degradation at 180–270 °C. The paraffin wax showed almost no char, indicating that it experienced simple evaporation. The HSNP prepared in absence of PWs had high silica contents of 38 wt % (as determined from their Y%). Except for the EOSNP2, all of the hydrophobic SNPs showed only one degradation step, confirming their compatibility with the paraffin wax [35]. The SNPs incorporated with paraffin wax (HOSNP) showed higher thermal stability, as their degradation started at 250 °C. The thermal stability of the hydrophobic SNPs decreased in the order of: HOSNP > EOSNP1 > EOSNP2 > HSNP. These data elucidate that the incorporation of paraffin wax into hydrophobic silica decreases the degradation of the ester and amine groups of the silane precursors. The evaporation of the paraffin wax at 250–350 °C, degraded the oleyl groups of the EOSNP1 more than those of the EOSNP2 and the HOSNP. This could be attributed to the good compatibility of the paraffin wax chain and the hydrophobic oleyl groups of silica, which acted as the heat isolators for the nanocomposites [35]. A second weight loss was observed at 360–470 °C, which could be attributed to the decomposition of the hydrophobic oleyl shell.
The wetting of the modified silica wax nano and microcapsules was evaluated by applying the thin films (with a thickness of 2 µm) onto glass panels and measuring their water contact angles (receding and advancing). The water contact angles of the treated and the untreated glass surfaces are listed in Table 3. The results showed that the PWs emulsion could not form a hydrophobic surface on the glass, leading to a low contact angle because of its poor adhesion to the glass and the formation of cracked film surfaces on it. All HSNPs showed high contact angles, especially EOSNP1. This could be attributed to the lower particle sizes of the HSNPs, and their positive surface charges, which attracted the negative surface charges of the silicate glass, as discussed in the previous section. Compared to the other hydrophobic SNPs, EOSNP1 formed a superhydrophobic film (contact angle > 150°) because of their good adhesion with glass and the combination of micro and nano roughness. This speculation was validated by the high-resolution SEM images of the EOSNP1 film (shown in Figure 5), which revealed the formation of the bridges between the EOSNP1 surface and its neighboring particles. Moreover, the rough surface of the EOSNP1 (Figure 5a) produced air pockets between the top of the microstructured silica capsules and the water droplets, which contributed to the highest contact angle and superhydrophobicity of the EOSNP1 [36]. The presence of silica inside the wax spheres of the EOSNP1 was confirmed by the SEM image (Figure 5b) of the crushed spheres after being soaked in liquid nitrogen. The appearance of the smooth film (Figure 5b) on the surface of the crushed EOSNP1 confirmed the wax layers formed on the surface of the spherical silica (present inside the wax layer as spherical particles).

3.3. Water Transportation of the Superhydrophobic Sand

It is well-known that desert sand particles (diameter of 100–200 μm) consist of hydrophilic silicates, which have low surface roughness and cannot absorb water, and hence, cannot store water [37]. This work aims to modify the surface wetting characteristics of sand by adhering with rough nanostructures to produce superhydrophobic sands having high water contact angles. In this study, we developed a rough coating of EOSNP1 on the sand surfaces. EOSNP1 samples with different weight percentages (1–20 wt %) of PWs were prepared. By dropping water onto the surfaces of the raw and treated sand, the wettability was evaluated. The water droplets quickly permeated the raw sand, indicating that the water contact angle of the raw sand was approximately 0°. The photographs of the water droplets on the EOSNP1-treated sand surface are shown in Figure 6a–d. The water droplets show an oblate shape without wetting the sand surface, indicating the formation of a superhydrophobic film on its surface. The water-absorbing capacities of the untreated sand were found to be 0.553 mL·g−1 and 5 mL of water was completely absorbed by the raw sand.
The surface morphologies of the EOSNP1-coated films with different PWs contents were examined using the SEM images shown in Figure 7a–d. The SEM of the EOSNP1-coated films were prepared by disperse-casting their dispersions in n-hexane on carbon grids. The roughness of the EOSNP1-coated sand surfaces increased with an increase in the wax content up to a 15 wt % (Figure 7a–c), and decreased with a further increase in the wax content up to a 20 wt % (Figure 7d). The adhesion of the superhydrophobic EOSNP1 coatings on the desert sand was investigated by adhesion tape peeling. The modified superhydrophobic sand was adhered onto the glass surface by a suitable glue, to form sand coating films with a thickness of 500 μm. A double-sided adhesive tape is pressed, at approximately 10 kPa, onto the superhydrophobic coated surface [8,36]. If the coating on the surface readily adheres to the adhesive tape without sand then it is said to have a poor adhesion with the surface and is considered to be attached to it only by van der Waals interactions [8,36]. The peel-off adhesion data of the EOSNP1-coated sand revealed that the EOSNP1 coatings with a paraffin wax content of up to 15 wt %, showed good adhesion, while the coating with the PWs content of 20 wt % showed poor adhesion. The adhesion data were consistent with the surface morphologies of the EOSNP1 (Figure 7a–d).
The superhydrophobicity of the sand mixtures, produced from the blending of the sand with the PWs emulsion and the EOSNP1 prepared in the presence of 10 wt % PWs, was inferred from their low ability to pass water, as reported in the experimental section. The time taken by the sands to pass 10 mL of water is shown in Table 4. The short duration taken by the untreated sand to pass water (2 s), elucidates its lower water storage ability. Moreover, it is clear from Table 4 that the PWs emulsion could not form superhydrophobic or hydrophobic sand. The ratio of the treated with the untreated sand (1:10) was economically preferred than a ratio of 1:1, which contained lower contents of the treated sand. The mixture of the untreated sand with the treated sand (containing EOSNP1 in the presence of 15 wt % of PWs) on the sand surface, at a, mixing ratio (wt %) of 1:10 (Table 4), showed a good amount of time to pass water, after 17 min. Water was not absorbed by this sand but steadily stayed and rolled on its surface. Such superhydrophobic sand has shown to have a great water-holding and low-flow-dragging capacities, and hence is of great importance for desert water storage and transportation.

4. Conclusions

The modification of desert sand with a well-adhered and thermally stable, rough superhydrophobic coatings is a key challenge for achieving superhydrophobic sand. Superhydrophobic PWs capsules containing hydrophobic silica nanoparticles (EOSNP1) were prepared using the emulsion technique, in the presence of n-hexane, to produce highly dispersed spherical and thermally stable nanoparticles. EOSNP1 coated onto the desert sand showed superhydrophobic characteristics with water droplet contact angles of 165°. The water droplet rolled and was not absorb by the treated sand with EOSNP1. The treatment of sand with the EOSNP1 achieved higher efficiencies to modify the hydrophobicity of sand to convert it to a superhydrophobic sand, even when mixed with the untreated sand with 1:10 wt %. The high thermal stability of the superhydrophobic sand treated with the PWs/EOSNP1 capsules is also a breakthrough, which would allow the hydrophobic sand to be applied in a wide range of harsh environments.

Author Contributions

Methodology, Investigation, Writing—Review and Editing, A.M.A; M.M.S.A; Supervision, H.A.A.-L.; Revision and Resources; Data Curation, N.H.M.

Funding

This research was funded by Deanship of Scientific Research at King Saud University, grant number RG-235.

Acknowledgments

The authors extend their appreciation to the Dean of Scientific Research at King Saud University for funding this work through Research Group No. (RGP-235, Saudi Arabia).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. El-Saied, H.; El-Hady, O.A.; Basta, A.H.; El-Dewiny, C.Y.; Abo-Sedera, S.A. Bio-chemical properties of sandy calcareous soil treated with rice straw-based hydrogels. J. Saudi Soc. Agric. Sci. 2016, 15, 188–194. [Google Scholar] [CrossRef] [Green Version]
  2. Narjary, B.; Aggarwal, P.; Singh, A.; Chakraborty, D.; Singh, R. Water availability in different soils in relation to hydrogel application. Geoderma 2012, 187, 94–101. [Google Scholar] [CrossRef]
  3. Montesano, F.F.; Parente, A.; Santamaria, P.; Sannino, A.; Serio, F. Biodegradable superabsorbent hydrogel increaseswater retention properties of growing media and plant growth. Agric. Agric. Sci. Procedia 2015, 4, 451–458. [Google Scholar] [CrossRef]
  4. Khodadadi Dehkordi, D. Effect of superabsorbent polymer on soil and plants on steep surfaces. Water Environ. J. 2018, 32, 158–163. [Google Scholar] [CrossRef]
  5. Dehkordi, D.K. Effect of hydrophilic polymers on seed germination and plant survival for sloping area. J. Soil Water Conserv. 2018, 73, 173–178. [Google Scholar] [CrossRef]
  6. Liao, R.; Wu, W.; Ren, S.; Yang, P. Effects of superabsorbent polymers on the hydraulic parameters and water retention properties of soil. J. Nanomater. 2016, 2016, 37. [Google Scholar] [CrossRef]
  7. González-Peñaloza, F.A.; Zavala, L.M.; Jordán, A.; Bellinfante, N.; Bárcenas-Moreno, G.; Mataix-Solera, J.; Granged, A.J.P.; Granja-Martins, F.M.; Neto-Paixão, H.M. Water repellency as conditioned by particle size and drying in hydrophobized sand. Geoderma 2013, 209, 31–40. [Google Scholar] [CrossRef]
  8. Chen, L.; Si, Y.; Guo, Z.; Liu, W. Superhydrophobic sand: A hope for desert water storage and transportation projects. J. Mater. Chem. A 2017, 5, 6416–6423. [Google Scholar] [CrossRef]
  9. Sun, X.; Liu, Y.; Mopidevi, S.; Meng, Y.; Huang, F.; Parisi, J.; Nieh, M.-P.; Cornelius, C.; Suib, S.L.; Lei, Y. Super-hydrophobic “smart” sand for buried explosive detection. Sens. Actuators B Chem. 2014, 195, 52–57. [Google Scholar] [CrossRef]
  10. Mitzel, M.R.; Sand, S.; Whalen, J.K.; Tufenkji, N. Hydrophobicity of biofilm coatings influences the transport dynamics of polystyrene nanoparticles in biofilm-coated sand. Water Res. 2016, 92, 113–120. [Google Scholar] [CrossRef]
  11. Han, Y.; Hwang, G.; Kim, D.; Bradford, S.A.; Lee, B.; Eom, I.; Kim, P.J.; Choi, S.Q.; Kim, H. Transport, retention, and long-term release behavior of ZnO nanoparticle aggregates in saturated quartz sand: Role of solution pH and biofilm coating. Water Res. 2016, 90, 247–257. [Google Scholar] [CrossRef] [PubMed]
  12. Sailor, M.J.; Link, J.R. “Smart dust”: Nanostructured devices in a grain of sand. Chem. Commun. 2005, 1375–1383. [Google Scholar] [CrossRef] [PubMed]
  13. Nazhipkyzy, M.; Temirgaliyeva, T.S.; Lesbayev, B.T.; Prikhodko, N.G.; Mansurov, Z.A. Obtaining superhydrophobic sand on the basis of soot synthesized during combustion of oil waste. Procedia Manuf. 2017, 12, 17–21. [Google Scholar] [CrossRef]
  14. Abousnina, R.M.; Manalo, A.; Shiau, J.; Lokuge, W. Effects of light crude oil contamination on the physical and mechanical properties of fine sand. Soil Sediment. Contam. Int. J. 2015, 24, 833–845. [Google Scholar] [CrossRef]
  15. Ovaskainen, L.; Olin, P.; Pettersson, T.; Wågberg, L.; Tuominen, M. The effect of different wear on superhydrophobic wax coatings. Nordic Pulp Paper Res. J. 2017, 32, 195–203. [Google Scholar] [CrossRef]
  16. Guan, Y.; Yu, C.; Zhu, J.; Yang, R.; Li, X.; Wei, D.; Xu, X. Design and fabrication of vapor-induced superhydrophobic surfaces obtained from polyethylene wax and silica nanoparticles in hierarchical structures. RSC Adv. 2018, 8, 25150–25158. [Google Scholar] [CrossRef]
  17. Bardet, J.P.; Jesmani, M.; Jabbari, N.; Nunes Lourenco, S.D. Permeability and compressibility of wax-coated sands. Géotechnique 2014, 64, 752–755. [Google Scholar] [CrossRef] [Green Version]
  18. Leelamanie, D.A.L.; Karube, J. Effects of hydrophobic and hydrophilic organic matter on the water repellency of model sandy soils. Soil Sci. Plant Nutr. 2009, 55, 462–467. [Google Scholar] [CrossRef] [Green Version]
  19. Ogihara, H.; Xie, J.; Okagaki, J.; Saji, T. Simple method for preparing superhydrophobic paper: Spray-deposited hydrophobic silica nanoparticle coatings exhibit high water-repellency and transparency. Langmuir 2012, 28, 4605–4608. [Google Scholar] [CrossRef]
  20. Manca, M.; Cannavale, A.; De Marco, L.; Arico, A.S.; Cingolani, R.; Gigli, G. Durable superhydrophobic and antireflective surfaces by trimethylsilanized silica nanoparticles-based sol−gel processing. Langmuir 2009, 25, 6357–6362. [Google Scholar] [CrossRef]
  21. Illescas, J.F.; Mosquera, M.J. Surfactant-synthesized PDMS/silica nanomaterials improve robustness and stain resistance of carbonate stone. J. Phys. Chem. C 2011, 115, 14624–14634. [Google Scholar] [CrossRef]
  22. Xu, L.; Geng, Z.; He, J.; Zhou, G. Mechanically robust, thermally stable, broadband antireflective, and superhydrophobic thin films on glass substrates. ACS Appl. Mater. Interfaces 2014, 6, 9029–9035. [Google Scholar] [CrossRef] [PubMed]
  23. Bravo, J.; Zhai, L.; Wu, Z.; Cohen, R.E.; Rubner, M.F. Transparent superhydrophobic films based on silica nanoparticles. Langmuir 2007, 23, 7293–7298. [Google Scholar] [CrossRef]
  24. Men, X.; Ge, B.; Li, P.; Zhu, X.; Shi, X.; Zhang, Z. Facile fabrication of superhydrophobic sand: Potential advantages for practical application in oil–water separation. J. Taiwan Inst. Chem. Eng. 2016, 60, 651–655. [Google Scholar] [CrossRef]
  25. Yong, J.; Chen, F.; Yang, Q.; Bian, H.; Du, G.; Shan, C.; Huo, J.; Fang, Y.; Hou, X. Oil-water separation: A gift from the desert. Adv. Mater. Interfaces 2016, 3, 1500650. [Google Scholar] [CrossRef]
  26. Li, C.; Mei, Z.; Liu, Q.; Wang, J.; Xu, J.; Sun, D. Formation and properties of paraffin wax submicron emulsions prepared by the emulsion inversion point method. Colloids Surf. Physicochem. Eng. Asp. 2010, 356, 71–77. [Google Scholar] [CrossRef]
  27. Kong, L.; Uedono, A.; Smith, S.V.; Yamashita, Y.; Chironi, I. Synthesis of silica nanoparticles using oil-in-water emulsion and the porosity analysis. J. Sol-Gel Sci. Technol. 2012, 64, 309–314. [Google Scholar] [CrossRef]
  28. Roy, I.; Ohulchanskyy, T.Y.; Pudavar, H.E.; Bergey, E.J.; Oseroff, A.R.; Morgan, J.; Dougherty, T.J.; Prasad, P.N. Ceramic-based nanoparticles entrapping water-insoluble photosensitizing anticancer drugs: A novel drug—Carrier system for photodynamic therapy. J. Am. Chem. Soc. 2003, 125, 7860–7865. [Google Scholar] [CrossRef]
  29. Kumar, R.; Roy, I.; Ohulchanskky, T.Y.; Vathy, L.A.; Bergey, E.J.; Sajjad, M.; Prasad, P.N. In vivo biodistribution and clearance studies using multimodal organically modified silica nanoparticles. ACS Nano 2010, 4, 699–708. [Google Scholar] [CrossRef]
  30. Srivastava, S.P.; Saxena, A.K.; Tandon, R.S.; Shekher, V. Measurement and prediction of solubility of petroleum waxes in organic solvents. Fuel 1997, 76, 625–630. [Google Scholar] [CrossRef]
  31. Qian, J.W.; Qi, G.R.; Xu, Y.L.; Yang, S.L. Solvent effect on the action of ethylene–vinyl acetate copolymer pour point depressant in waxy solutions. J. Appl. Polym. Sci. 1996, 60, 1575–1578. [Google Scholar] [CrossRef]
  32. Qian, J.W.; Zhou, G.H.; Yang, W.Y.; Xu, Y.L. Studies on pour point depression of EVA polymers in solvent mixtures containing wax. J. Appl. Polym. Sci. 2002, 83, 815–821. [Google Scholar] [CrossRef]
  33. Atta, A.M.; Al-Lohedan, H.A.; Al-Hussain, S.A. Functionalization of magnetite nanoparticles as oil spill collector. Int. J. Mol. Sci. 2015, 16, 6911–6931. [Google Scholar] [CrossRef] [PubMed]
  34. Lan, Q.; Yang, F.; Zhang, S.; Liu, S.; Xu, J.; Sun, D. Synergistic effect of silica nanoparticle and cetyltrimethyl ammonium bromide on the stabilization of O/W emulsions. Colloids Surf. A Physicochem. Eng. Asp. 2007, 302, 126–135. [Google Scholar] [CrossRef]
  35. Luyt, A.S.; Krupa, I. Phase change materials formed by uv curable epoxy matrix and Fischer–Tropsch paraffin wax. Energy Convers. Manag. 2009, 50, 57–61. [Google Scholar] [CrossRef]
  36. Deng, X.; Mammen, L.; Zhao, Y.; Lellig, P.; Müllen, K.; Li, C.; Butt, H.-J.; Vollmer, D. Transparent, thermally stable and mechanically robust superhydrophobic surfaces made from porous silica capsules. Adv. Mater. 2011, 23, 2962–2965. [Google Scholar] [CrossRef] [PubMed]
  37. Schoonover, J.E.; Crim, J.F. An introduction to soil concepts and the role of soils in watershed management. J. Contemp. Water Res. Educ. 2015, 154, 21–47. [Google Scholar] [CrossRef]
Coatings 09 00124 sch001 550
Scheme 1. Preparation scheme of the hydrophobic silica nanoparticles (SNP).
Scheme 1. Preparation scheme of the hydrophobic silica nanoparticles (SNP).
Coatings 09 00124 sch001
Coatings 09 00124 g001 550
Figure 1. Optical microscope photos of (a) PWs emulsion and (b) silicon precursor PWs emulsion.
Figure 1. Optical microscope photos of (a) PWs emulsion and (b) silicon precursor PWs emulsion.
Coatings 09 00124 g001
Coatings 09 00124 g002 550
Figure 2. Dynamic light scattering (DLS) data of the hydrophobic SNPs. (a) Hydrophobic silica nanoparticles (HSNP), (b) HOSNP, (c) Emulsified silica NPs (EOSNP1), and (d) EOSNP2 in n-hexane, at 25 °C.
Figure 2. Dynamic light scattering (DLS) data of the hydrophobic SNPs. (a) Hydrophobic silica nanoparticles (HSNP), (b) HOSNP, (c) Emulsified silica NPs (EOSNP1), and (d) EOSNP2 in n-hexane, at 25 °C.
Coatings 09 00124 g002
Coatings 09 00124 g003 550
Figure 3. Zeta potential data of the hydrophobic SNP. (a) HSNP, (b) HOSNP, (c) EOSNP1, and (d) EOSNP2 in ethanol/water, at 25 °C.
Figure 3. Zeta potential data of the hydrophobic SNP. (a) HSNP, (b) HOSNP, (c) EOSNP1, and (d) EOSNP2 in ethanol/water, at 25 °C.
Coatings 09 00124 g003
Coatings 09 00124 g004 550
Figure 4. TEM micrographs of (a) HSNP, (b) HOSNP, (c) EOSNP1, and (d) EOSNP2.
Figure 4. TEM micrographs of (a) HSNP, (b) HOSNP, (c) EOSNP1, and (d) EOSNP2.
Coatings 09 00124 g004
Coatings 09 00124 g005 550
Figure 5. SEM images of (a) EOSNP1 on the sand surface, and (b) the crushed EOSNP1 film.
Figure 5. SEM images of (a) EOSNP1 on the sand surface, and (b) the crushed EOSNP1 film.
Coatings 09 00124 g005
Coatings 09 00124 g006 550
Figure 6. Photos of water on the treated sand with EOSNP1 prepared in the presence of different wt % of PWs (a) 20 wt %, (b) 10 wt %, (c) 5 wt %, and (d) 1 wt %.
Figure 6. Photos of water on the treated sand with EOSNP1 prepared in the presence of different wt % of PWs (a) 20 wt %, (b) 10 wt %, (c) 5 wt %, and (d) 1 wt %.
Coatings 09 00124 g006
Coatings 09 00124 g007 550
Figure 7. SEM images of the EOSNP1 films, prepared using different percentages of PWs (a) 5, (b) 10, (c) 15, and (d) 20 wt %.
Figure 7. SEM images of the EOSNP1 films, prepared using different percentages of PWs (a) 5, (b) 10, (c) 15, and (d) 20 wt %.
Coatings 09 00124 g007
Table
Table 1. Physical characteristics of the El-Ameria light slack wax according to American Society for Testing and Materials (ASTM) standard methods.
Table 1. Physical characteristics of the El-Ameria light slack wax according to American Society for Testing and Materials (ASTM) standard methods.
CharacteristicsLight Slack Wax (Waste By-Product)Paraffin Waxes (PWs)
Yield10054.5
Congealing point, °C4653
Kinematic viscosity, 98.9 °C, cSt 2.832.88
Refractive index, 98.9 °C1.42141.4187
Density, 70 °C, g/cm30.79100.7750
Oil content, wt %4.250.25
Sulfur content, wt %0.080.00
Cone penetration, 25 °C23–
Needle penetration, 25 °C6722
Color (ASTM-D 1500)0.50.0
Refractive Index by TAPPI Equation–1.4242
Molecular Type Composition
Total saturates, wt %97.74100
n-Paraffins content, wt %78..9888.14
Iso & cycloparaffins content, wt %18.7611.86
Total aromatics, wt %2.260.00
Mono-aromatics, wt %0.640.00
Di-aromatics, wt %1.620.00
Table
Table 2. Thermogravimetric analysis (TGA) data of the SNPs coated with PWs.
Table 2. Thermogravimetric analysis (TGA) data of the SNPs coated with PWs.
SampleStepsWeight Loss (%)IDT (°C)T10% (°C)Y (%)
Start Temp (°C)End Temp (°C)
HSNP02505.513032038
25045019.5
45065037
HOSNP02501.025036018
25045050.0
45065031.0
EOSNP1025030.015017020
25045025.0
45065025.0
EOSNP2025010.014025030
25045030.0
45065030.0
Table
Table 3. Contact angle of the water droplet on the hydrophobic SNP microcapsule films, at 25 °C.
Table 3. Contact angle of the water droplet on the hydrophobic SNP microcapsule films, at 25 °C.
Sample CodeContact Angle (Degree)
RecedingAdvancing
Glass45 ± 448 ± 3
PWs55 ± 358 ± 2
HSNP110 ± 1118 ± 1
HOSNP120 ± 4125 ± 1
EOSNP1165 ± 2168 ± 2
EOSNP2118 ± 3123 ± 1
Table
Table 4. Efficiency of the mixed sand with the different ratios of sand treated with the EOSNP1, on the preservation of water.
Table 4. Efficiency of the mixed sand with the different ratios of sand treated with the EOSNP1, on the preservation of water.
SamplesTime (s) for Water PreservationSand Composition (Treated Sand: Untreated Sand wt %)
Untreated Sand1:101:51:1
Blank (untreated Sand only)2 s–––
EOSNP1 in the presence of 10 wt % of PWs111517
EOSNP1 in the presence of 15 wt % of PWs171925

Share and Cite

MDPI and ACS Style

Atta, A.M.; Abdullah, M.M.S.; Al-Lohedan, H.A.; Mohamed, N.H. Coating Sand with New Hydrophobic and Superhydrophobic Silica/Paraffin Wax Nanocapsules for Desert Water Storage and Transportation. Coatings 2019, 9, 124. https://doi.org/10.3390/coatings9020124

AMA Style

Atta AM, Abdullah MMS, Al-Lohedan HA, Mohamed NH. Coating Sand with New Hydrophobic and Superhydrophobic Silica/Paraffin Wax Nanocapsules for Desert Water Storage and Transportation. Coatings. 2019; 9(2):124. https://doi.org/10.3390/coatings9020124

Chicago/Turabian Style

Atta, Ayman M., Mahmood M. S. Abdullah, Hamad A. Al-Lohedan, and Nermen H. Mohamed. 2019. "Coating Sand with New Hydrophobic and Superhydrophobic Silica/Paraffin Wax Nanocapsules for Desert Water Storage and Transportation" Coatings 9, no. 2: 124. https://doi.org/10.3390/coatings9020124

APA Style

Atta, A. M., Abdullah, M. M. S., Al-Lohedan, H. A., & Mohamed, N. H. (2019). Coating Sand with New Hydrophobic and Superhydrophobic Silica/Paraffin Wax Nanocapsules for Desert Water Storage and Transportation. Coatings, 9(2), 124. https://doi.org/10.3390/coatings9020124

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop