Next Article in Journal
CAR-T Cells in the Treatment of Ovarian Cancer: A Promising Cell Therapy
Next Article in Special Issue
The Impact of Flavonoid-Loaded Nanoparticles in the UV Protection and Safety Profile of Topical Sunscreens
Previous Article in Journal
Exploring the Formation Kinetics of Octacalcium Phosphate from Alpha-Tricalcium Phosphate: Synthesis Scale-Up, Determination of Transient Phases, Their Morphology and Biocompatibility
Previous Article in Special Issue
Recent Developments in Biopolymer-Based Hydrogels for Tissue Engineering Applications
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Biomolecules
Volume 13
Issue 3
10.3390/biom13030464
biomolecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Surface Treatments of PEEK for Osseointegration to Bone

by
Jay R. Dondani
,
Janaki Iyer
and
Simon D. Tran
*
McGill Craniofacial Tissue Engineering and Stem Cells Laboratory, Faculty of Dental Medicine and Oral Health Sciences, McGill University, 3640 University Street, Montreal, QC H3A 0C7, Canada
*
Author to whom correspondence should be addressed.
Biomolecules 2023, 13(3), 464; https://doi.org/10.3390/biom13030464
Submission received: 29 January 2023 / Revised: 24 February 2023 / Accepted: 28 February 2023 / Published: 2 March 2023
(This article belongs to the Special Issue Novel Materials for Biomedical Applications)
Browse Figures
Review Reports Versions Notes

Abstract

:
Polymers, in general, and Poly (Ether-Ether-Ketone) (PEEK) have emerged as potential alternatives to conventional osseous implant biomaterials. Due to its distinct advantages over metallic implants, PEEK has been gaining increasing attention as a prime candidate for orthopaedic and dental implants. However, PEEK has a highly hydrophobic and bioinert surface that attenuates the differentiation and proliferation of osteoblasts and leads to implant failure. Several improvements have been made to the osseointegration potential of PEEK, which can be classified into three main categories: (1) surface functionalization with bioactive agents by physical or chemical means; (2) incorporation of bioactive materials either as surface coatings or as composites; and (3) construction of three-dimensionally porous structures on its surfaces. The physical treatments, such as plasma treatments of various elements, accelerated neutron beams, or conventional techniques like sandblasting and laser or ultraviolet radiation, change the micro-geometry of the implant surface. The chemical treatments change the surface composition of PEEK and should be titrated at the time of exposure. The implant surface can be incorporated with a bioactive material that should be selected following the desired use, loading condition, and antimicrobial load around the implant. For optimal results, a combination of the methods above is utilized to compensate for the limitations of individual methods. This review summarizes these methods and their combinations for optimizing the surface of PEEK for utilization as an implanted biomaterial.

1. Introduction

The quest for materials that conform to the physiology of the human bone has been arduous in orthopaedics and implant dentistry. The human bone is a unique type of connective tissue as its form is determined by the nature of forces exerted on it. Therefore, a biomaterial used with bone has to mimic it mechanically and bind without inciting any local or systemic immune response. Orthopaedic and dental implants are medical devices that receive external load and transmit it to the bone. Dental as well as orthopaedic implants transmit stresses to the bone in a cyclic manner, making them susceptible to fatigue failure. Therefore, the implant biomaterial has to possess a similar modulus of elasticity (resistance to deformation) and fracture strength (stress level at which the material fractures) as that of human bone, while maintaining a robust interface with it. Materials like metals, autogenous bone, ceramics, polymers, and others have been used for orthopaedic implants. Metals, for example, have a high elastic modulus, which allows the metal to absorb stress that would otherwise be carried by the bone. This process is known as stress shielding and causes a reduction in bone density in vivo. The presence of metals also leads to the development of artifacts in radiographs. Autogenous bone grafts can cause bone defects at the donor site, leading to compromised form and function [1]. Ceramics have a similar limitation of high elastic modulus to metals, which is compounded by the inherent brittleness and lack of ductility. This can lead to an increased propensity for fracture of the prosthesis in vivo. Recently, polymers, in general, and PEEK have emerged as potential alternatives to conventional biomaterials. Due to its distinct advantages over metallic implants, PEEK has been gaining increasing attention as a prime candidate for orthopaedic and dental implants. PEEK has similar mechanical strength to bone. PEEK is radiolucent, chemically inert and resistant to sterilization, lacks metal allergies, and can be manufactured more easily [2,3,4]. PEEK has a modulus of elasticity similar to that of cortical bone, leading to proportionate flexure when loading is applied to the implant.
The phenomenon of osseointegration between the implant and bone warrants a hydrophilic surface for initiation by adsorption of plasma proteins (Figure 1). However, PEEK has a highly hydrophobic, bioinert surface that [a] attenuates osteoblast adhesion to PEEK surface, which prevents osteoblastic differentiation and proliferation, [b] leads to fibro-integration (foreign body reaction leading to a fibrous capsule around the implant instead of a bony union), and [c] weakens the contact between the implant and the bone (osseointegration), leading to implant failure, preventing clinical application [2,3,4,5,6]. Similar to other oral biomaterials, PEEK can accumulate oral biofilms that cause peri-implant or periodontal inflammation [7,8]. There are two types of inflammatory reactions around implants: reversible soft tissue inflammation known as mucositis and irreversible bone loss known as periimplantitis [9,10,11]. Since dental as well as orthopaedic implants osseointegrate with the bone for transmission of forces, the surface improvements of PEEK orthopaedic implants can also be translated to PEEK dental implants. It can be categorized into three main categories: surface functionalization with bioactive agents by physical or chemical means, incorporation of bioactive materials either as surface coatings or composites, and construction of three-dimensional porous structures on surfaces [12,13,14]. The physical treatments usually subject PEEK to plasma treatments of various elements, accelerated neutron beams, or conventional techniques like sandblasting and laser or ultraviolet radiation. The chemical treatments change the surface composition of PEEK and should be titrated against the time of exposure, and they can severely affect the performance of the bone–implant interface. In addition to these methods, the surface of the implants can be incorporated with bioactive materials [2]. The purpose of adding a bioactive material should be based on the desired use, loading condition, and antimicrobial load around the implant. This purpose dictates the extent to which the bioactive material will be incorporated with PEEK. First, the nanometer-scale coating can be applied to PEEK implants by spin-coating, gas plasma etching, electron beam deposition, or plasma ion immersion. Second, nanoparticles can be combined with PEEK through the process of melt-blending to produce bioactive nanocomposites [15]. The former is a surface-level phenomenon that does not affect the mechanical properties of the material, whereas the latter contributes significantly to the improvement of the strength and modulus of elasticity of PEEK. For optimal results, a combination of the aforementioned methods is utilized to compensate for the limitations of individual methods.

2. Background

Before considering PEEK as an implant biomaterial, a significant number of studies were conducted to assess and optimize the bonding strength of PEEK with other biomaterials. Parker et al. assessed different surface treatments and shear bond characteristics of PEEK to resin cement and glass ionomer cement. They concluded that sulfuric acid-treated samples had the highest shear bond strength [16]. However, it was evident that the physical alteration of the surface introduces a favourable morphology for adhesion but does not improve the hydrophilicity of the material. For the phenomenon of osseointegration to initiate between the implant and the bone, platelets and plasma proteins from the blood need to be adsorbed onto the implant surface. The surface of PEEK has to be altered to increase the surface energy and adsorption of adherends. Miyagaki et al. attempted the surface optimization of PEEK through the Friedel–Crafts reaction and demonstrated that the reaction followed by epoxidation increases the adhesion strength of PEEK to epoxy resins [17]. However, because of the direct modification of the main chains of PEEK, chemical treatments decrease its crystallinity, which must be preserved in order to maintain its mechanical properties [18]. It is essential to modify the depth of the surface in the direction of thickness in order to ensure sustained adhesion [19]. Lu et al. studied the effects of a plasma treatment on carbon fibers/PEEK hybrid composite and inferred that radiofrequency plasma activated by air, argon, or air–argon increases the interfacial strength of the composite. This is attributed to the increased roughness induced by the plasma treatment, leading to improved mechanical interlocking [20]. Among the various elements of plasma treatments, oxygen and hydrogen/oxygen plasma treatments were reported to be the most effective [21]. These studies have improved our understanding of the qualitative and quantitative reactions of PEEK to different treatments and how they can be employed in dental and orthopedic implantology.

3. Surface Treatments

Although a myriad of permutations and combinations of different surface treatments are employed to alter the surface topography of PEEK, for the sake of simplicity, these treatments have been classified into the following categories: physical treatment, chemical treatment, surface coating, and composite preparation (Figure 2), with the first surface treatment in the combination determining the classification. Though these terms are arbitrary and could lead to considerable overlap, physical and chemical treatments can be grouped into a subtractive form of surface modification while surface coating can be regarded as an additive form.

3.1. Physical Treatment

Physical treatments constitute plasma treatment, accelerated neutron atom beam (ANAB), photodynamic therapy, sandblasting, and laser irradiation.

3.1.1. Plasma Treatment

Plasma treatments primarily aim to decrease the contact angle of the PEEK surface by increasing the surface energy. Secondarily, the plasma treatments incorporate the element constituting the plasma onto the surface of a PEEK (Plasma Immersion Ion Implantation). This improves its response to human osteoblasts. Several elements have been successfully tested for the plasma treatment of PEEK (Table 1).
As evident from the studies, plasma treatments are utilized as a pre-treatment for several other surface treatments. Oxygen plasma was tested with various forms of radiation, whereas Argon plasma was combined with various chemical treatments. However, the rationale for the preference for such combinations could not be deciphered. Considering the decrease in contact angle and increase in the bioactivity of PEEK, nitrogen plasma was found to be most suited for implant applications of PEEK. Plasma treatments and sulphonation are the most common surface treatments used to increase the surface energy of PEEK to receive a bioactive coating. The two treatments are also used extensively together. In addition to increasing the surface energy and hydrophilicity of the surface, plasma immersion ion implantation also increases the hardness of the surface [38]. This property may decrease the tribological wear of orthopaedic implants due to gliding surfaces but is not important for dental implants [39]. However, due to the nature of electromagnetic radiation, plasma treatments are restricted by line-of-sight limitations. Therefore, it is difficult to utilize plasma for modifying implants with complex geometry [40].

3.1.2. Accelerated Neutral Atom Beam (ANAB)

Accelerated Neutral Atom Beam (ANAB) is a technique for employing an intensely directed beam of neutral gas atoms that improves the bioactivity of PEEK without altering its chemical or mechanical properties. Studies have demonstrated a decreased contact angle and increased bioactivity of osteogenic cells in response to ANAB-treated PEEK in-vitro [41,42,43,44] and an increased bond strength to bone in-vivo [42], as shown in Table 2. An in-vitro decrease in the bacterial colonization of Methicillin-resistant Staphylococcus aureus (MRSA), Staphylococcus epidermidis (S. epidermidis), and Escherichia coli (E.coli) have been demonstrated following treatment of PEEK with ANAB [43]. Though ANAB has exhibited significant improvement when used as a solitary treatment, its synergy with other treatments is yet to be tested. ANAB-treated PEEK surfaces are capable of osteoblast differentiation following osteoinduction in an osteogenic medium. However, ANAB-treated PEEK surfaces have not demonstrated independent osteoinduction ability [44].

3.1.3. Photodynamic Treatment

Photodynamic treatment is primarily a therapeutic approach to decrease the microbial load on the surface. It involves the introduction of a drug on the surface of the biomaterial, followed by irradiation with a laser beam. It has been proven to decrease the microbial load and can be used in cases of inflammation around PEEK implants [45,46] (as given in Table 3). However, any potential role of photodynamic treatment in improving osseointegration in the absence of a periodontal pathology is yet to be investigated. However, significant improvements are required in light sources, absorption rates, and penetrating abilities of photosensitizers to decrease the exposure time required to modify PEEK surfaces with photodynamic treatment [46].

3.1.4. Sandblasting

Sandblasting is a widely used procedure in the surface treatment of titanium implants. It was broadly used when the surface roughening of implants was first advocated to enhance osseointegration. It is a process of physically roughening the surface by subjecting it to a stream of abrasive particles. This method has been shown to increase the proliferation and differentiation of mesenchymal stem cells and also to mitigate inflammatory mediators around the implant [47] (Table 3). As observed in titanium implants, blasting is one of the most widely used surface treatments but is insufficient to improve tissue response and bone-implant contact. [38] Due to the advent of newer physical methods to treat PEEK surfaces, sandblasting has been restricted as a pre-treatment before the application of a bioactive coating.

3.1.5. Laser

A femtosecond laser can be employed to induce periodic grooves on the surface of the PEEK implant, which improves the surface characteristics. Xie et al. confirmed that the PEEK surface after exposure to a femtosecond laser showed increased adhesion, proliferation, and differentiation of mouse bone marrow mesenchymal stem cells (mBMSC) cells and increased expression and activity of alkaline phosphatase [48] (Table 3). However, these findings will require substantiation with in vivo studies.
Table
Table 3. Results of photodynamic therapy, sandblasting, and laser on PEEK.
Table 3. Results of photodynamic therapy, sandblasting, and laser on PEEK.
TreatmentResultAuthor
Photodynamic therapy
(Temporfin/Ampicillin) + Diode laserIn vitro: Increase in resistance to microbial loadPeng et al. [46]
PDT/Sulphuric acid (H2SO4)/Air abrasion (Al/Diamond)In vitro: Lower shear bond strength and microroughness of samples treated with PDT as compared to H2SO4 and Alumina particle air abrasion (Highest: H2SO4)Binhasan et al. [45]
Sandblasting
Alumina particlesIn vitro: Increased proliferation and differentiation of rat MSCs and mitigation of inflammatory chemokine (C-C motif) Ligand 2 (CCL2)Sunarso et al. [47]
Laser
Femtosecond laserIn vitro: Increased adhesion, proliferation and differentiation of mBMSC cells and increased expression and activity of alkaline phosphataseXie et al. [48]

3.2. Chemical Treatment

3.2.1. Sulphonation

One of the most common surface treatments employed for PEEK, sulphonation, involves the exposure of the surface to concentrated sulphuric acid. (H2SO4). The term ‘sulphonation’ refers to the exposure to H2SO4 as well as its removal from the surface by an alkali, although in some studies it has been used exclusively for the exposure to the acid. In Table 4, ‘sulphonation’ is inclusive of alkali treatment, or any other method employed to remove H2SO4 from the surface of PEEK.
Studies demonstrating the exposure time of H2SO4 have yielded conflicting results; however, most studies have employed an exposure time of 3–5 min. Ma et al. proved that an exposure time of 5 min to 98% sulphuric acid yielded optimal surface topography [49]. Cheng et al. demonstrated that a 3 min sulphonation decreased the contact angle and increased pre-osteoblastic activity [51]. On the other hand, Wang et al. found that a short exposure time of 30 s was optimal for decreasing the contact angle of PEEK; however, the longest time of exposure in the study was only 90 s [50]. If an additive coating will be applied after sulphonation, the time of exposure is determined by the other treatments used in the combination, as well as the nature of the coating. The time of exposure is a critical factor as the chemical composition of PEEK, which imparts superior mechanical properties to PEEK, gets altered as a function of time.
There is a statistically significant influence of sulphonation on the contact angle of PEEK. This phenomenon makes sulphonation acceptable as a pre-treatment before the application of a surface coating on PEEK. Furthermore, sulphonation has been extensively used in combination with plasma treatment for activation of the PEEK surface to receive organic and inorganic coatings and continues to be the most studied chemical treatment for the PEEK surface.

3.2.2. Phosphonation

Phosphonation is the introduction of a phosphate group on the surface of a biomaterial. Various methods, such as diazonium chemistry and polymerization of Vinyl phosphonic acid, have been used to graft the functional group on the surface of PEEK, which has increased cell adhesion, spreading, proliferation, and differentiation in vitro and the bone–implant contact ratio in vivo [66,67,68], as shown in Table 5. It serves as an optimal surface treatment, but the compatibility of phosphonation with other treatments will have to be assessed.

3.2.3. Silanization

Silanization is the introduction of a silane group to an object or surface. Silanization is utilized to improve the surface characteristics of materials like glass and metal oxides. It has been proven to increase the cell adhesion, spreading, proliferation, and differentiation of pre-osteoblasts in vitro (Table 5), but in vivo studies confirming the same are not available.
Table
Table 5. Results of phosphonation and silanization on PEEK.
Table 5. Results of phosphonation and silanization on PEEK.
TreatmentResultAuthor
Phosphonation
Diazonium chemistryIn vitro: Decreased contact angle, increased deposition of HA and increased MC3T3-E1 cell viability and metabolic activity

In vivo: Increased osseointegration		Mahjoubi et al. [68]
VinylphosphonateIn vitro: Dose dependent increase in MC3T3-E1 cell metabolic activity

In vivo: Dose dependent increase in bone-to-implant contact ratio and bond strength		Liu et al. [66]
VinylphosphonateIn vitro: Increased MC3T3-E1 cell adhesion, spreading, proliferation and differentiation

In vivo: Increased bone-to-implant contact ratio		Zheng et al. [67]
Silanization
Dimethyl sulfoxide and Sodium borohydride + Silanization layers +FunctionalizationIn vitro: Increased MC3T3-E1 cell adhesion, spreading, proliferation and differentiationZheng et al. [69]

3.3. Surface Coatings

3.3.1. Hydroxyapatite Coating

Hydroxyapatite (HA) is the main inorganic component of the human bone; hence, it is intuitive to incorporate HA on the surface of PEEK to increase its bioactivity. HA has regularly been employed as a surface treatment to increase the bioactivity of metallic implants. However, the temperature required to incorporate HA is higher than the temperature range at which PEEK is chemically stable. Hence, in most studies, an intermediate layer of Titanium or Yttria Stabilized Zirconia (YSZ) was used to shield PEEK from thermal insult [70,71,72] (Figure 3). The thickness of the intermediate layer has been found to influence the coating’s bond strength to PEEK. [72] HA coating is thermally treated to transform it into a crystalline state from an amorphous bioinert state. This finding is consistent with the fact that HA found in the human bone occurs in a crystalline state. In terms of bioactivity and bone strength to PEEK, heat-treated crystalline HA outperformed untreated amorphous HA [70,71,72,73] (Table 6).

3.3.2. Titanium Coating

Titanium is the most widely used implant biomaterial due to its biocompatibility and osseointegration potential. The phenomenon of osseointegration was also accidentally discovered using titanium when titanium chambers that were used for studying the circulation of a healing fibula in a rabbit could not be removed due to their fusion with the bone [74]. A stable layer of titanium dioxide is formed on the surface of titanium on exposure to air [75,76]. This oxide layer has a high dielectric constant, which leads to the adsorption of proteins from blood on the surface, which is the first step in the cascade of events leading to osseointegration. Therefore, a coating of titanium or titanium oxide on the surface of PEEK would give the implant the favorable mechanical properties of PEEK and the higher bond strength of titanium with bone. In vitro studies have shown an increase in adhesion, proliferation, and differentiation of pre-osteoblasts in reaction to a titanium coating. In vivo studies have also inferred that the coating increases osseointegration and bond strength with bone (Table 7). However, titanium as an implant biomaterial has been reported to cause isolated cases of hypersensitivity in vivo [77], which currently remains unevaluated. Additionally, titanium and titanium alloys have a significantly higher elastic modulus than the supporting bone, leading to higher stress levels at the first point of contact on the bone. These stresses result in microfractures in the bone, leading to bone loss [78]. PEEK implants coated with titanium or titanium oxide benefit from the similar elastic modulus of PEEK and supporting bone, as well as the superior surface characteristics of titanium. Despite titanium allergies and mechanical mismatch with bone, titanium continues to be used in more than 92% of all dental implants and is a promising coating material for PEEK.

3.3.3. Anti-Microbial Agent Coating

Anti-microbial coatings like gentamycin and selenium have been used in vitro [83,84] as well as in vivo [83] in combination with a carrier agent. These coatings have also been shown to increase the bioactivity of PEEK in addition to its antimicrobial activity against microbes, such as S. aureus and Pseudomonas aeruginosa (P. aeruginosa), as shown in Table 8. However, the sustainability of the release of these agents will have to be titrated against the complexity of the surface treatments to determine their feasibility. Additional studies quantifying antimicrobial action as a function of time are required to establish the durability of these coatings in an in vivo environment.

3.3.4. Biomolecule Coating

Anti-inflammatory agents such as dexamethasone have been used to combat acute and chronic inflammatory responses of the body to noxious stimuli. Combinations of dexamethasone with other anti-inflammatory agents like interleukin-6 (IL-6) or metal-organic frameworks like Zn-Mg-MOF-74 have been proven to increase the anti-inflammatory response and antimicrobial activity of PEEK, respectively [86,87] (Table 9). Dexamethasone can be used as an implant coating in cases where the prognosis is compromised due to decreased local host immunity to infections, as supported by the current evidence.

3.3.5. Polymer Coating

A coating of polymers like 2-methacryloyloxyethyl phosphorylcholine (MPC) on PEEK surfaces has been studied and shown to decrease the contact angle of PEEK, increase its wettability, and facilitate osseointegration [88] (Table 9). However, in vivo demonstration of the increase in hydrophilicity has not been documented.
Table
Table 9. Results of biomolecule and polymer coatings on PEEK.
Table 9. Results of biomolecule and polymer coatings on PEEK.
TreatmentResultsAuthor
Surface coatings—Biomolecules
Dexamethasone + Nitrogen plasma treatment + IL-6In vitro: Decreased peri-implant inflammatory mediators

In vivo: Increased osseointegration		Xie et al. [86]
Zn−Mg-MOF-74 + DexamethasoneIn vitro: Increased antimicrobial activity against S. aureus and E. coli and angiogenic ability

In vivo: Increased antimicrobial activity and angiogenic ability and osseointegration		Xiao et al. [87]
Surface coatings: Polymers
2-methacryloyloxyethyl phosphorylcholine (MPC)In vitro: Decrease in contact angleKyomoto et al. [88]

3.4. Composites of Poly (Ether-Ether-Ketone)

Composites of PEEK with various metals, oxides, inorganic fibers, and polymers have been used for improving the clinical performance of individual constituent biomaterials. The selection of material to be used with PEEK and the method of fabrication depend on the intended use of the implant. However, the main purpose of combining PEEK with other biomaterials is to improve the mechanical properties, with the improved surface characteristics being a by-product of the combination. Moreover, most composites of PEEK require an additional surface treatment for osseointegration. An exception in the following studies is a composite of HA and PEEK that did not require additional surface treatment and increased the adhesion, proliferation, and differentiation of pre-osteoblasts (Table 10), though in vivo studies are missing to substantiate the same. Most composites of PEEK are carbon-fiber reinforced PEEK (CFR PEEK) composites, which always require additional additive treatments for osseointegration.

4. Conclusions

PEEK is regarded as the future of dental and orthopedic implantology and is currently the only biomaterial that mimics bone biomechanically. However, its bio-inertness and hydrophobicity have restricted its commercialization as an implant biomaterial. PEEK’s low surface energy, which limits microbe colonization on its surface, also inhibits plasma protein adsorption and the adhesion and proliferation of undifferentiated mesenchymal cells on its surface, both of which are required for osseointegration.
Recently, numerous surface treatments that have been used conventionally to improve the implant surface characteristics of titanium have been applied to PEEK surfaces. The main objectives of these treatments are to increase the wettability and bioactivity of the surface as well as decrease the inflammatory mediators around it. These treatments either physically or chemically alter the surface or place a bioactive or antimicrobial coating on the surface. In practice, a combination of these methods is used to reduce the limitations of each individual method.
Among the physical treatments, plasma ion implantation is the most widely researched and used. Plasma treatments have demonstrated compatibility with nearly all other surface treatments, making them a preferred pre-treatment method. ANAB has also been proven to significantly improve surface characteristics, but it needs to be evaluated for compatibility with other treatments. Other surface treatments, such as photodynamic therapy, sandblasting, and femtosecond lasers, have been studied in a limited capacity, and their use as a surface treatment for PEEK will warrant additional scientific evidence.
Among the chemical treatments, sulphonation has universal acceptability and compatibility with other treatments. Sulphonation has been combined with most other surface treatments and has demonstrated exceptional synergism. The combination of plasma treatment and sulphonation has been employed as a pre-treatment for several bio-active coatings, further confirming that a combination of physical and chemical treatment is more effective than individual constituent treatments. Phosphonation has emerged as a promising treatment, but its effectiveness in a combination of treatments is yet to be evaluated.
Surface coatings have drastically improved the bioactivity of PEEK surfaces, although this effect is compounded by pre-treatment with physical or chemical treatments. HA and titanium coatings are the two most suitable treatments. HA application is particularly advantageous as it is the main constituent of the inorganic component of human bone. Crystallization of HA has been proven to improve the bioactivity of the PEEK surface considerably, and the intermediate layer used to thermally insulate the PEEK surface during crystallization does not decrease the bond strength of the coating. On the other hand, titanium is the most implanted material in human bone, which translates to adequate clinical use with academic evidence. In vitro and in vivo studies have substantiated the improvement in bioactivity and other surface characteristics of PEEK with the use of titanium as a coating after plasma treatment. Antimicrobial coatings have also been employed with success, but the inhibitory effects of these coatings over time will have to be studied further. Biomolecules and polymer coatings have shown favorable results in isolated studies, but additional evidence will be required to consolidate and confirm the results.
Composites of PEEK have also been attempted as a method to enhance the surface characteristics. Apart from composites of PEEK with HA, most other composites require an external surface treatment for their use as an implant biomaterial. Conventional classifications cite composites as a method to improve surface characteristics, but current studies have shown little evidence of the same.
Although these surface treatments have shown considerable in vitro and in vivo promise, there is a paucity of human studies confirming the same. In vivo studies cited in this work are conducted primarily on mice, rats, and rabbits and are short-term studies conducted over the past five years. The in vitro ‘efficacy’ and in vivo ‘effectiveness’ of these treatments, although demonstrated, mandate clinical ‘efficiency’. Some treatments will still require additional in vitro studies to establish repeatable and predictable results. Other treatments that have demonstrated in vitro efficacy require long-term human studies to justify their commercialization. Furthermore, currently, there are no studies comparing the clinical performance of commercially pure titanium with surface-treated PEEK to establish PEEK as a superior implant biomaterial after surface treatment. Nevertheless, the increase in the number of studies evaluating PEEK as an implant material is an attestation to the fact that PEEK is the future of dental and orthopedic implantology.

Author Contributions

Conceptualization, J.R.D.; writing—original draft preparation, J.R.D.; writing—review and editing, J.I. and S.D.T.; visualization, J.I.; supervision, S.D.T. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Institutional Review Board Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

Abbreviations

ANABAccelerated Neutron Atom Beam
mBMSAMouse Mesenchymal Stem Cells-Bone Marrow
MC3T3-E1Osteoblast precursor cell line derived from Mus musculus (mouse) calvaria
MG63Cell-line that has fibroblast morphology isolated from the bone of a white, 14-year-old male patient with osteosarcoma.
NaOHSodium Hydroxide
Nd-YAGNeodymium-Doped Yttrium Aluminium Garnet
PDAPolydopamine
PEEKPoly (Ether-Ether-Ketone)
rBMSRat Bone Marrow Mesenchymal Cells
SAOS-2Human osteosarcoma cell line
SBFSimulated Body Fluid
U2-OSHuman osteosarcoma cell line derived in 1964 from a moderately differentiated sarcoma of the tibia of a 15-year-old, White, female osteosarcoma patient
UVUltraviolet radiation
YSZYttrium Stabilized Zirconia

References

  1. Zheng, Z.; Liu, P.; Zhang, X.; Xin, J.; Wang, Y.; Zou, X.; Mei, X.; Zhang, S.; Zhang, S. Strategies to improve bioactive and antibacterial properties of polyetheretherketone (PEEK) for use as orthopedic implants. Mater. Today Bio 2022, 16, 100402. [Google Scholar] [CrossRef] [PubMed]
  2. Ma, R.; Tang, T. Current Strategies to Improve the Bioactivity of PEEK. Int. J. Mol. Sci. 2014, 15, 5426–5445. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  3. Kurtz, S.M.; Devine, J.N. PEEK biomaterials in trauma, orthopedic, and spinal implants. Biomaterials 2007, 28, 4845–4869. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  4. Buck, E.; Li, H.; Cerruti, M. Surface Modification Strategies to Improve the Osseointegration of Poly(etheretherketone) and Its Composites. Macromol. Biosci. 2020, 20, 1900271. [Google Scholar] [CrossRef]
  5. Sagomonyants, K.B.; Jarman-Smith, M.L.; Devine, J.N.; Aronow, M.S.; Gronowicz, G.A. The in vitro response of human osteoblasts to polyetheretherketone (PEEK) substrates compared to commercially pure titanium. Biomaterials 2008, 29, 1563–1572. [Google Scholar] [CrossRef]
  6. Olivares-Navarrete, R.; Hyzy, S.L.; Slosar, P.J.; Schneider, J.M.; Schwartz, Z.; Boyan, B.D. Implant Materials Generate Different Peri-implant Inflammatory Factors: Poly-ether-ether-ketone Promotes Fibrosis and Microtextured Titanium Promotes Osteogenic Factors. Spine 2015, 40, 399–404. [Google Scholar] [CrossRef]
  7. da Silva-Neto, J.P.; Prudente, M.S.; Carneiro, T.D.A.P.N.; de Arruda Nóbilo, M.A.; Penatti, M.P.A.; das Neves, F.D. Micro-leakage at the implant-abutment interface with different tightening torques in vitro. J. Appl. Oral Sci. 2012, 20, 581–587. [Google Scholar] [CrossRef] [Green Version]
  8. Teughels, W.; Van Assche, N.; Sliepen, I.; Quirynen, M. Effect of material characteristics and/or surface topography on biofilm development. Clin. Oral Implant. Res. 2006, 17, 68–81. [Google Scholar] [CrossRef]
  9. Zitzmann, N.U.; Abrahamsson, I.; Berglundh, T.; Lindhe, J. Soft tissue reactions to plaque formation at implant abutments with different surface topography: An experimental study in dogs. J. Clin. Periodontol. 2002, 29, 456–461. [Google Scholar] [CrossRef]
  10. Heitz-Mayfield, L.J.A. Peri-implant diseases: Diagnosis and risk indicators. J. Clin. Periodontol. 2008, 35, 292–304. [Google Scholar] [CrossRef]
  11. Zitzmann, N.U.; Berglundh, T. Definition and prevalence of peri-implant diseases. J. Clin. Periodontol. 2008, 35, 286–291. [Google Scholar] [CrossRef] [PubMed]
  12. Wang, H.; Lu, T.; Meng, F.; Zhu, H.; Liu, X. Enhanced osteoblast responses to poly ether ether ketone surface modified by water plasma immersion ion implantation. Colloids Surf. B Biointerfaces 2014, 117, 89–97. [Google Scholar] [CrossRef] [PubMed]
  13. Xu, X.; Li, Y.; Wang, L.; Li, Y.; Pan, J.; Fu, X.; Luo, Z.; Sui, Y.; Zhang, S.; Wang, L.; et al. Triple-functional polyetheretherketone surface with enhanced bacteriostasis and anti-inflammatory and osseointegrative properties for implant application. Biomaterials 2019, 212, 98–114. [Google Scholar] [CrossRef] [PubMed]
  14. Yuan, X.; Ouyang, L.; Luo, Y.; Sun, Z.; Yang, C.; Wang, J.; Liu, X.; Zhang, X. Multifunctional sulfonated polyetheretherketone coating with beta-defensin-14 for yielding durable and broad-spectrum antibacterial activity and osseointegration. Acta Biomater. 2019, 86, 323–337. [Google Scholar] [CrossRef]
  15. Najeeb, S.; Khurshid, Z.; Matinlinna, J.P.; Siddiqui, F.; Nassani, M.Z.; Baroudi, K. Nanomodified Peek Dental Implants: Bioactive Composites and Surface Modification—A Review. Int. J. Dent. 2015, 2015, 381759. [Google Scholar] [CrossRef] [Green Version]
  16. Parkar, U.; Dugal, R.; Madanshetty, P.; Devadiga, T.; Khan, A.; Godil, A. Assessment of different surface treatments and shear bond characteristics of poly-ether-ether-ketone: An in vitro SEM analysis. J. Indian Prosthodont. Soc. 2021, 21, 412. [Google Scholar]
  17. Miyagaki, A.; Kamaya, Y.; Matsumoto, T.; Honda, K.; Shibahara, M.; Hongo, C.; Nishino, T. Surface Modification of Poly(ether ether ketone) through Friedel–Crafts Reaction for High Adhesion Strength. Langmuir 2019, 35, 9761–9768. [Google Scholar]
  18. Manolakis, I.; Cross, P.; Colquhoun, H.M. Exchange Reactions of Poly(arylene ether ketone) Dithioketals with Aliphatic Diols: Formation and Deprotection of Poly(arylene ether ketal)s. Macromolecules 2017, 50, 9561–9568. [Google Scholar] [CrossRef] [Green Version]
  19. Matsumoto, T.; Shimizu, Y.; Nishino, T. Analyses of the Adhesion Interphase of Isotactic Polypropylene Using Hot-Melt Polyolefin Adhesives. Macromolecules 2021, 54, 7226–7233. [Google Scholar] [CrossRef]
  20. Lu, C.; Qiu, S.; Lu, X.; Wang, J.; Xiao, L.; Zheng, T.; Wang, X.; Zhang, D. Enhancing the Interfacial Strength of Carbon Fiber/Poly(ether ether ketone) Hybrid Composites by Plasma Treatments. Polymers 2019, 11, 753. [Google Scholar] [CrossRef] [Green Version]
  21. Fu, Q.; Gabriel, M.; Schmidt, F.; Müller, W.-D.; Schwitalla, A.D. The impact of different low-pressure plasma types on the physical, chemical and biological surface properties of PEEK. Dent. Mater. 2021, 37, e15–e22. [Google Scholar] [CrossRef] [PubMed]
  22. Waser-Althaus, J.; Salamon, A.; Waser, M.; Padeste, C.; Kreutzer, M.; Pieles, U.; Müller, B.; Peters, K. Differentiation of human mesenchymal stem cells on plasma-treated polyetheretherketone. J. Mater. Sci. Mater. Med. 2014, 25, 515–525. [Google Scholar] [CrossRef] [PubMed]
  23. Gan, K.; Liu, H.; Jiang, L.; Liu, X.; Song, X.; Niu, D.; Chen, T.; Liu, C. Bioactivity and antibacterial effect of nitrogen plasma immersion ion implantation on polyetheretherketone. Dent. Mater. 2016, 32, e263–e274. [Google Scholar] [CrossRef] [PubMed]
  24. Han, X.; Sharma, N.; Spintzyk, S.; Zhou, Y.; Xu, Z.; Thieringer, F.M.; Rupp, F. Tailoring the biologic responses of 3D printed PEEK medical implants by plasma functionalization. Dent. Mater. 2022, 38, 1083–1098. [Google Scholar] [CrossRef]
  25. Ha, S.-W.; Kirch, M.; Birchler, F.; Eckert, K.-L.; Mayer, J.; Wintermantel, E.; Sittig, C.; Pfund-Klingenfuss, I.; Textor, M.; Spencer, N.D.; et al. Surface activation of polyetheretherketone (PEEK) and formation of calcium phosphate coatings by precipitation. J. Mater. Sci. Mater. Med. 1997, 8, 683–690. [Google Scholar] [CrossRef]
  26. Liu, C.; Bai, J.; Wang, Y.; Chen, L.; Wang, D.; Ni, S.; Liu, H. The effects of three cold plasma treatments on the osteogenic activity and antibacterial property of PEEK. Dent. Mater. 2021, 37, 81–93. [Google Scholar] [CrossRef]
  27. Tsougeni, K.; Vourdas, N.; Tserepi, A.; Gogolides, E.; Cardinaud, C. Mechanisms of Oxygen Plasma Nanotexturing of Organic Polymer Surfaces: From Stable Super Hydrophilic to Super Hydrophobic Surfaces. Langmuir 2009, 25, 11748–11759. [Google Scholar] [CrossRef]
  28. Rochford, E.T.J.; Subbiahdoss, G.; Moriarty, T.F.; Poulsson, A.H.C.; van der Mei, H.C.; Busscher, H.J.; Richards, R.G. An in vitro investigation of bacteria-osteoblast competition on oxygen plasma-modified PEEK: An in vitro investigation of bacteria-osteoblast competition. J. Biomed. Mater. Res. A 2014, 102, 4427–4434. [Google Scholar]
  29. Czwartos, J.; Budner, B.; Bartnik, A.; Wachulak, P.; Butruk-Raszeja, B.A.; Lech, A.; Ciach, T.; Fiedorowicz, H. Effect of Extreme Ultraviolet (EUV) Radiation and EUV Induced, N2 and O2 Based Plasmas on a PEEK Surface’s Physico-Chemical Properties and MG63 Cell Adhesion. Int. J. Mol. Sci. 2021, 22, 8455. [Google Scholar] [CrossRef]
  30. Kizuki, T.; Matsushita, T.; Kokubo, T. Apatite-forming PEEK with TiO2 surface layer coating. J. Mater. Sci. Mater. Med. 2015, 26, 41. [Google Scholar] [CrossRef]
  31. Chen, M.; Ouyang, L.; Lu, T.; Wang, H.; Meng, F.; Yang, Y.; Ning, C.; Ma, J.; Liu, X. Enhanced Bioactivity and Bacteriostasis of Surface Fluorinated Polyetheretherketone. ACS Appl. Mater. Interfaces 2017, 9, 16824–16833. [Google Scholar] [CrossRef] [PubMed]
  32. Ouyang, L.; Chen, M.; Wang, D.; Lu, T.; Wang, H.; Meng, F.; Yang, Y.; Ma, J.; Yeung, K.W.K.; Liu, X. Nano Textured PEEK Surface for Enhanced Osseointegration. ACS Biomater. Sci. Eng. 2019, 5, 1279–1289. [Google Scholar] [CrossRef] [PubMed]
  33. Akkan, C.K.; Hammadeh, M.E.; May, A.; Park, H.-W.; Abdul-Khaliq, H.; Strunskus, T.; Aktas, O.C. Surface topography and wetting modifications of PEEK for implant applications. Lasers Med. Sci. 2014, 29, 1633–1639. [Google Scholar] [CrossRef] [PubMed]
  34. Chen, T.; Chen, Q.; Fu, H.; Wang, D.; Gao, Y.; Zhang, M.; Liu, H. Construction and performance evaluation of a sustained release implant material polyetheretherketone with antibacterial properties. Mater. Sci. Eng. C 2021, 126, 112109. [Google Scholar] [CrossRef]
  35. Wakelin, E.A.; Yeo, G.C.; McKenzie, D.R.; Bilek, M.M.M.; Weiss, A.S. Plasma ion implantation enabled bio-functionalization of PEEK improves osteoblastic activity. APL Bioeng. 2018, 2, 026109. [Google Scholar] [CrossRef] [Green Version]
  36. Qin, S.; Lu, Z.; Gan, K.; Qiao, C.; Li, B.; Chen, T.; Gao, Y.; Jiang, L.; Liu, H. Construction of a BMP -2 gene delivery system for polyetheretherketone bone implant material and its effect on bone formation in vitro. J. Biomed. Mater. Res. B Appl. Biomater. 2022, 110, 2075–2088. [Google Scholar] [CrossRef]
  37. Liu, X.; Han, F.; Zhao, P.; Lin, C.; Wen, X.; Ye, X. Layer-by-layer self-assembled multilayers on PEEK implants improve osseointegration in an osteoporosis rabbit model. Nanomed. Nanotechnol. Biol. Med. 2017, 13, 1423–1433. [Google Scholar] [CrossRef]
  38. Jemat, A.; Ghazali, M.J.; Razali, M.; Otsuka, Y. Surface Modifications and Their Effects on Titanium Dental Implants. BioMed Res. Int. 2015, 2015, 791725. [Google Scholar] [CrossRef] [Green Version]
  39. Albrektsson, T.; Becker, W.; Coli, P.; Jemt, T.; Mölne, J.; Sennerby, L. Bone loss around oral and orthopedic implants: An immunologically based condition. Clin. Implant. Dent. Relat. Res. 2019, 21, 786–795. [Google Scholar] [CrossRef]
  40. Lu, T.; Wen, J.; Qian, S.; Cao, H.; Ning, C.; Pan, X.; Jiang, X.; Liu, X.; Chu, P.K. Enhanced osteointegration on tantalum-implanted polyetheretherketone surface with bone-like elastic modulus. Biomaterials 2015, 51, 173–183. [Google Scholar] [CrossRef]
  41. Khoury, J.; Selezneva, I.; Pestov, S.; Tarassov, V.; Ermakov, A.; Mikheev, A.; Lazov, M.; Kirkpatrick, S.R.; Shashkov, D.; Smolkov, A. Surface bioactivation of PEEK by neutral atom beam technology. Bioact. Mater. 2019, 4, 132–141. [Google Scholar] [CrossRef] [PubMed]
  42. Khoury, J.; Maxwell, M.; Cherian, R.E.; Bachand, J.; Kurz, A.C.; Walsh, M.; Assad, M.; Svrluga, R.C. Enhanced bioactivity and osseointegration of PEEK with accelerated neutral atom beam technology: Enhanced Bioactivity and Osseointegration of Peek. J. Biomed. Mater. Res. B Appl. Biomater. 2017, 105, 531–543. [Google Scholar] [CrossRef] [PubMed]
  43. Webster, T.J.; Shallenberger, J.R.; Edelman, E.R.; Khoury, J. Accelerated Neutral Atom Beam (ANAB) Modified Poly-Ether-Ether-Ketone for Increasing In Vitro Bone Cell Functions and Reducing Bacteria Colonization without Drugs or Antibiotics. J. Biomed. Nanotechnol. 2022, 18, 788–795. [Google Scholar] [CrossRef]
  44. Ajami, S.; Coathup, M.J.; Khoury, J.; Blunn, G.W. Augmenting the bioactivity of polyetheretherketone using a novel accelerated neutral atom beam technique: Bioactivity of polyetheretherketone. J. Biomed. Mater. Res. B Appl. Biomater. 2017, 105, 1438–1446. [Google Scholar] [CrossRef] [PubMed]
  45. Binhasan, M.; Alhamdan, M.M.; Al-Aali, K.A.; Vohra, F.; Abduljabbar, T. Shear bond characteristics and surface roughness of poly-ether-ether-ketone treated with contemporary surface treatment regimes bonded to composite resin. Photodiagnosis Photodyn. Ther. 2022, 38, 102765. [Google Scholar] [CrossRef]
  46. Peng, T.-Y.; Lin, D.-J.; Mine, Y.; Tasi, C.-Y.; Li, P.-J.; Shih, Y.-H.; Chiu, K.-C.; Wang, T.-H.; Hsia, S.-M.; Shieh, T.-M. Biofilm Formation on the Surface of (Poly)Ether-Ether-Ketone and In Vitro Antimicrobial Efficacy of Photodynamic Therapy on Peri-Implant Mucositis. Polymers 2021, 13, 940. [Google Scholar] [CrossRef]
  47. Sunarso; Tsuchiya, A.; Fukuda, N.; Toita, R.; Tsuru, K.; Ishikawa, K. Effect of micro-roughening of poly(ether ether ketone) on bone marrow derived stem cell and macrophage responses, and osseointegration. J. Biomater. Sci. Polym. Ed. 2018, 29, 1375–1388. [Google Scholar] [CrossRef] [PubMed]
  48. Xie, H.; Zhang, C.; Wang, R.; Tang, H.; Mu, M.; Li, H.; Guo, Y.; Yang, L.; Tang, K. Femtosecond laser-induced periodic grooves and nanopore clusters make a synergistic effect on osteogenic differentiation. Colloids Surf. B Biointerfaces 2021, 208, 112021. [Google Scholar] [CrossRef]
  49. Ma, R.; Wang, J.; Li, C.; Ma, K.; Wei, J.; Yang, P.; Guo, D.; Wang, K.; Wang, W. Effects of different sulfonation times and post-treatment methods on the characterization and cytocompatibility of sulfonated PEEK. J. Biomater. Appl. 2020, 35, 342–352. [Google Scholar] [CrossRef]
  50. Wang, W.; Luo, C.J.; Huang, J.; Edirisinghe, M. PEEK surface modification by fast ambient-temperature sulfonation for bone implant applications. J. R. Soc. Interface 2019, 16, 20180955. [Google Scholar] [CrossRef] [Green Version]
  51. Cheng, Q.; Yuan, B.; Chen, X.; Yang, X.; Lin, H.; Zhu, X.; Zhang, K.; Zhang, X. Regulation of surface micro/nano structure and composition of polyetheretherketone and their influence on the behavior of MC3T3-E1 pre-osteoblasts. J. Mater. Chem. B 2019, 7, 5713–5724. [Google Scholar] [CrossRef] [PubMed]
  52. Dos Santos, F.S.F.; Vieira, M.; da Silva, H.N.; Tomás, H.; Fook, M.V.L. Surface Bioactivation of Polyether Ether Ketone (PEEK) by Sulfuric Acid and Piranha Solution: Influence of the Modification Route in Capacity for Inducing Cell Growth. Biomolecules 2021, 11, 1260. [Google Scholar] [CrossRef] [PubMed]
  53. Li, Y.; Wang, J.; He, D.; Zhu, G.; Wu, G.; Chen, L. Surface sulfonation and nitrification enhance the biological activity and osteogenesis of polyetheretherketone by forming an irregular nano-porous monolayer. J. Mater. Sci. Mater. Med. 2020, 31, 11. [Google Scholar] [CrossRef] [PubMed]
  54. Huo, S.; Meng, X.; Zhang, S.; Yue, B.; Zhao, Y.; Long, T.; Nie, B.; Wang, Y. Hydrofluoric acid and nitric acid cotreatment for biofunctionalization of polyetheretherketone in M2 macrophage polarization and osteogenesis. J. Biomed. Mater. Res. A 2021, 109, 879–892. [Google Scholar] [CrossRef]
  55. Montero, J.F.D.; Barbosa, L.C.A.; Pereira, U.A.; Barra, G.M.; Fredel, M.C.; Benfatti, C.A.M.; Magini, R.S.; Pimenta, A.L.; Souza, J.C.M. Chemical, microscopic, and microbiological analysis of a functionalized poly-ether-ether-ketone-embedding antibiofilm compounds: SPEEK Containing Antibiofilm Compound. J. Biomed. Mater. Res. A 2016, 104, 3015–3020. [Google Scholar] [CrossRef]
  56. Yang, X.; Chai, H.; Guo, L.; Jiang, Y.; Xu, L.; Huang, W.; Shen, Y.; Yu, L.; Liu, Y.; Liu, J. In situ preparation of porous metal-organic frameworks ZIF-8@Ag on poly-ether-ether-ketone with synergistic antibacterial activity. Colloids Surf. B Biointerfaces 2021, 205, 111920. [Google Scholar] [CrossRef]
  57. Guo, C.; Lu, R.; Wang, X.; Chen, S. Antibacterial activity, bio-compatibility and osteogenic differentiation of graphene oxide coating on 3D-network poly-ether-ether-ketone for orthopaedic implants. J. Mater. Sci. Mater. Med. 2021, 32, 135. [Google Scholar] [CrossRef]
  58. Deng, L.-J.; Wu, Y.-L.; He, X.-H.; Xie, K.-N.; Xie, L.; Deng, Y. Simvastatin delivery on PEEK for bioactivity and osteogenesis enhancements. J. Biomater. Sci. Polym. Ed. 2018, 29, 2237–2251. [Google Scholar] [CrossRef]
  59. Dong, T.; Duan, C.; Wang, S.; Gao, X.; Yang, Q.; Yang, W.; Deng, Y. Multifunctional Surface with Enhanced Angiogenesis for Improving Long-Term Osteogenic Fixation of Poly(ether ether ketone) Implants. ACS Appl. Mater. Interfaces 2020, 12, 14971–14982. [Google Scholar] [CrossRef]
  60. Li, N.; Bai, J.; Wang, W.; Liang, X.; Zhang, W.; Li, W.; Lu, L.; Xiao, L.; Xu, Y.; Wang, Z.; et al. Facile and Versatile Surface Functional Polyetheretherketone with Enhanced Bacteriostasis and Osseointegrative Capability for Implant Application. ACS Appl. Mater. Interfaces 2021, 13, 59731–59746. [Google Scholar] [CrossRef]
  61. Masamoto, K.; Fujibayashi, S.; Yabutsuka, T.; Hiruta, T.; Otsuki, B.; Okuzu, Y.; Goto, K.; Shimizu, T.; Shimizu, Y.; Ishizaki, C.; et al. In vivo and in vitro bioactivity of a “precursor of apatite” treatment on polyetheretherketone. Acta Biomater. 2019, 91, 48–59. [Google Scholar] [CrossRef] [PubMed]
  62. Zhu, Y.; Cao, Z.; Peng, Y.; Hu, L.; Guney, T.; Tang, B. Facile Surface Modification Method for Synergistically Enhancing the Biocompatibility and Bioactivity of Poly(ether ether ketone) That Induced Osteodifferentiation. ACS Appl. Mater. Interfaces 2019, 11, 27503–27511. [Google Scholar] [CrossRef] [PubMed]
  63. Wang, S.; Deng, Y.; Yang, L.; Shi, X.; Yang, W.; Chen, Z.-G. Enhanced antibacterial property and osteo-differentiation activity on plasma treated porous polyetheretherketone with hierarchical micro/nano-topography. J. Biomater. Sci. Polym. Ed. 2018, 29, 520–542. [Google Scholar] [CrossRef]
  64. Wu, J.; Li, L.; Fu, C.; Yang, F.; Jiao, Z.; Shi, X.; Ito, Y.; Wang, Z.; Liu, Q.; Zhang, P. Micro-porous polyetheretherketone implants decorated with BMP-2 via phosphorylated gelatin coating for enhancing cell adhesion and osteogenic differentiation. Colloids Surf. B Biointerfaces 2018, 169, 233–241. [Google Scholar] [CrossRef] [PubMed]
  65. Kim, H.; Lee, Y.H.; Kim, N.K.; Kang, I.K. Immobilization of Collagen on the Surface of a PEEK Implant with Monolayer Nanopores. Polymers 2022, 14, 1633. [Google Scholar] [CrossRef] [PubMed]
  66. Liu, L.; Zheng, Y.; Zhang, Q.; Yu, L.; Hu, Z.; Liu, Y. Surface phosphonation treatment shows dose-dependent enhancement of the bioactivity of polyetheretherketone. RSC Adv. 2019, 9, 30076–30086. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  67. Zheng, Y.; Liu, L.; Xiao, L.; Zhang, Q.; Liu, Y. Enhanced osteogenic activity of phosphorylated polyetheretherketone via surface-initiated grafting polymerization of vinylphosphonic acid. Colloids Surf. B Biointerfaces 2019, 173, 591–598. [Google Scholar] [CrossRef]
  68. Mahjoubi, H.; Buck, E.; Manimunda, P.; Farivar, R.; Chromik, R.; Murshed, M.; Cerruti, M. Surface phosphonation enhances hydroxyapatite coating adhesion on polyetheretherketone and its osseointegration potential. Acta Biomater. 2017, 47, 149–158. [Google Scholar] [CrossRef]
  69. Zheng, Y.; Xiong, C.; Zhang, S.; Li, X.; Zhang, L. Bone-like apatite coating on functionalized poly(etheretherketone) surface via tailored silanization layers technique. Mater. Sci. Eng. C 2015, 55, 512–523. [Google Scholar] [CrossRef]
  70. Durham, J.W.; Allen, M.J.; Rabiei, A. Preparation, characterization and in vitro response of bioactive coatings on polyether ether ketone: Response Of Bioactive Coatings on Polyether Ether Ketone. J. Biomed. Mater. Res. B Appl. Biomater. 2017, 105, 560–567. [Google Scholar] [CrossRef] [Green Version]
  71. Rabiei, A.; Sandukas, S. Processing and evaluation of bioactive coatings on polymeric implants: Processing and Evaluation of Bioactive HA Coatings on PEEK. J. Biomed. Mater. Res. A 2013, 101A, 2621–2629. [Google Scholar] [CrossRef] [PubMed]
  72. Ozeki, K.; Masuzawa, T.; Aoki, H. Fabrication of hydroxyapatite thin films on polyetheretherketone substrates using a sputtering technique. Mater. Sci. Eng. C 2017, 72, 576–582. [Google Scholar] [CrossRef] [PubMed]
  73. Johansson, P.; Jimbo, R.; Kjellin, P.; Chrcanovic, B.; Wennerberg, A.; Currie, F. Biomechanical evaluation and surface characterization of a nano-modified surface on PEEK implants: A study in the rabbit tibia. Int. J. Nanomed. 2014, 9, 3903. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  74. Dhinakarsamy, V.; Jayesh, R. Osseointegration. J. Pharm. Bioallied Sci. 2015, 7, 228. [Google Scholar] [CrossRef]
  75. Karthik, K.; Sivakumar; Sivaraj; Thangaswamy, V. Evaluation of implant success: A review of past and present concepts. J. Pharm. Bioallied Sci. 2013, 5, 117. [Google Scholar] [CrossRef]
  76. Tschernitschek, H.; Borchers, L.; Geurtsen, W. Nonalloyed titanium as a bioinert metal—A review. Quintessence Int. Berl. Ger. 2005, 36, 523–530. [Google Scholar] [CrossRef]
  77. Singh, R.; Lehl, G.; Hussain, A.B.; Abhang, T.N.; Kulkarni, M.M.; Elagib, M.F.A.; Tiwari, R.V.C. Prevalence of Titanium Hypersensitivity in Patients with Titanium Implants: A Systematic Review and Meta-analysis. J. Pharm. Bioallied Sci. 2021, 13, S1345–S1349. [Google Scholar]
  78. Pérez-Pevida, E.; Brizuela-Velasco, A.; Chávarri-Prado, D.; Jiménez-Garrudo, A.; Sánchez-Lasheras, F.; Solaberrieta-Méndez, E.; Diéguez-Pereira, M.; Fernández-González, F.J.; Dehesa-Ibarra, B.; Monticelli, F. Biomechanical Consequences of the Elastic Properties of Dental Implant Alloys on the Supporting Bone: Finite Element Analysis. BioMed Res. Int. 2016, 2016, 1850401. [Google Scholar] [CrossRef]
  79. Liu, C.; Zhang, Y.; Xiao, L.; Ge, X.; Öner, F.C.; Xu, H. Vacuum plasma sprayed porous titanium coating on polyetheretherketone for ACDF improves the osteogenic ability: An in vitro and in vivo study. Biomed. Microdevices 2021, 23, 21. [Google Scholar] [CrossRef]
  80. Yang, Y.; Zhang, H.; Komasa, S.; Kusumoto, T.; Kuwamoto, S.; Okunishi, T.; Kobayashi, Y.; Hashimoto, Y.; Sekino, T.; Okazaki, J. Immunomodulatory Properties and Osteogenic Activity of Polyetheretherketone Coated with Titanate Nanonetwork Structures. Int. J. Mol. Sci. 2022, 23, 612. [Google Scholar] [CrossRef]
  81. Shimizu, T.; Fujibayashi, S.; Yamaguchi, S.; Yamamoto, K.; Otsuki, B.; Takemoto, M.; Tsukanaka, M.; Kizuki, T.; Matsushita, T.; Kokubo, T.; et al. Bioactivity of sol–gel-derived TiO2 coating on polyetheretherketone: In vitro and in vivo studies. Acta Biomater. 2016, 35, 305–317. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  82. Tsou, H.-K.; Chi, M.-H.; Hung, Y.-W.; Chung, C.-J.; He, J.-L. In Vivo Osseointegration Performance of Titanium Dioxide Coating Modified Polyetheretherketone Using Arc Ion Plating for Spinal Implant Application. BioMed Res. Int. 2015, 2015, 328943. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  83. Xue, Z.; Wang, Z.; Sun, A.; Huang, J.; Wu, W.; Chen, M.; Hao, X.; Huang, Z.; Lin, X.; Weng, S. Rapid construction of polyetheretherketone (PEEK) biological implants incorporated with brushite (CaHPO4·2H2O) and antibiotics for anti-infection and enhanced osseointegration. Mater. Sci. Eng. C 2020, 111, 110782. [Google Scholar] [CrossRef] [PubMed]
  84. Wang, Q.; Mejía Jaramillo, A.; Pavon, J.J.; Webster, T.J. Red selenium nanoparticles and gray selenium nanorods as antibacterial coatings for PEEK medical devices: Antibacterial Coatings for Peek Medical Devices. J. Biomed. Mater. Res. B Appl. Biomater. 2016, 104, 1352–1358. [Google Scholar] [CrossRef] [PubMed]
  85. Hu, C.-C.; Kumar, S.R.; Vi, T.T.T.; Huang, Y.-T.; Chen, D.W.; Lue, S.J. Facilitating GL13K Peptide Grafting on Polyetheretherketone via 1-Ethyl-3-(3-dimethylaminopropyl)carbodiimide: Surface Properties and Antibacterial Activity. Int. J. Mol. Sci. 2021, 23, 359. [Google Scholar] [CrossRef]
  86. Xie, L.; Wang, G.; Wu, Y.; Liao, Q.; Mo, S.; Ren, X.; Tong, L.; Zhang, W.; Guan, M.; Pan, H.; et al. Programmed surface on poly(aryl-ether-ether-ketone) initiating immune mediation and fulfilling bone regeneration sequentially. Innovation 2021, 2, 100148. [Google Scholar] [CrossRef] [PubMed]
  87. Xiao, T.; Fan, L.; Liu, R.; Huang, X.; Wang, S.; Xiao, L.; Pang, Y.; Li, D.; Liu, J.; Min, Y. Fabrication of Dexamethasone-Loaded Dual-Metal–Organic Frameworks on Polyetheretherketone Implants with Bacteriostasis and Angiogenesis Properties for Promoting Bone Regeneration. ACS Appl. Mater. Interfaces 2021, 13, 50836–50850. [Google Scholar] [CrossRef]
  88. Kyomoto, M.; Moro, T.; Takatori, Y.; Kawaguchi, H.; Nakamura, K.; Ishihara, K. Self-initiated surface grafting with poly(2-methacryloyloxyethyl phosphorylcholine) on poly(ether-ether-ketone). Biomaterials 2010, 31, 1017–1024. [Google Scholar] [CrossRef]
  89. Díez-Pascual, A.M.; Díez-Vicente, A.L. Nano-TiO2 Reinforced PEEK/PEI Blends as Biomaterials for Load-Bearing Implant Applications. ACS Appl. Mater. Interfaces 2015, 7, 5561–5573. [Google Scholar] [CrossRef]
  90. Oladapo, B.I.; Ismail, S.O.; Bowoto, O.K.; Omigbodun, F.T.; Olawumi, M.A.; Muhammad, M.A. Lattice design and 3D-printing of PEEK with Ca10(OH)(PO4)3 and in-vitro bio-composite for bone implant. Int. J. Biol. Macromol. 2020, 165, 50–62. [Google Scholar] [CrossRef]
  91. Li, J.; Qian, S.; Ning, C.; Liu, X. rBMSC and bacterial responses to isoelastic carbon fiber-reinforced poly(ether-ether-ketone) modified by zirconium implantation. J. Mater. Chem. B 2016, 4, 96–104. [Google Scholar] [CrossRef] [PubMed]
  92. Yamane, Y.; Yabutsuka, T.; Takaoka, Y.; Ishizaki, C.; Takai, S.; Fujibayashi, S. Surface Modification of Carbon Fiber-Polyetheretherketone Composite to Impart Bioactivity by Using Apatite Nuclei. Materials 2021, 14, 6691. [Google Scholar] [CrossRef]
  93. Du, T.; Zhao, S.; Dong, W.; Ma, W.; Zhou, X.; Wang, Y.; Zhang, M. Surface Modification of Carbon Fiber-Reinforced Polyetheretherketone with MXene Nanosheets for Enhanced Photothermal Antibacterial Activity and Osteogenicity. ACS Biomater. Sci. Eng. 2022, 8, 2375–2389. [Google Scholar] [CrossRef] [PubMed]
  94. Miyazaki, T.; Matsunami, C.; Shirosaki, Y. Bioactive carbon–PEEK composites prepared by chemical surface treatment. Mater. Sci. Eng. C 2017, 70, 71–75. [Google Scholar] [CrossRef] [PubMed]
  95. Yabutsuka, T.; Fukushima, K.; Hiruta, T.; Takai, S.; Yao, T. Fabrication of Bioactive Fiber-reinforced PEEK and MXD6 by Incorporation of Precursor of Apatite: Fabrication of bioactive fiber-reinforced peek and mxd6. J. Biomed. Mater. Res. B Appl. Biomater. 2018, 106, 2254–2265. [Google Scholar] [CrossRef] [PubMed]
  96. Addai Asante, N.; Wang, Y.; Bakhet, S.; Kareem, S.; Owusu, K.A.; Hu, Y.; Appiah, M. Ambient temperature sulfonated carbon fiber reinforced PEEK with hydroxyapatite and reduced graphene oxide hydroxyapatite composite coating. J. Biomed. Mater. Res. B Appl. Biomater. 2021, 109, 2174–2183. [Google Scholar] [CrossRef]
Biomolecules 13 00464 g001 550
Figure 1. Process of osseointegration.
Figure 1. Process of osseointegration.
Biomolecules 13 00464 g001
Biomolecules 13 00464 g002 550
Figure 2. Classification of surface treatments of PEEK.
Figure 2. Classification of surface treatments of PEEK.
Biomolecules 13 00464 g002
Biomolecules 13 00464 g003 550
Figure 3. Insulation of PEEK by Titanium or YSZ intermediate layer from heated HA during crystallisation process.
Figure 3. Insulation of PEEK by Titanium or YSZ intermediate layer from heated HA during crystallisation process.
Biomolecules 13 00464 g003
Table
Table 1. Various plasma surface treatments of PEEK.
Table 1. Various plasma surface treatments of PEEK.
TreatmentResultsAuthor
Plasma
Oxygen/AmmoniaIn-vitro: Increased adhesion, proliferation, and osteogenic differentiation of cells as compared to controlAlthaus et al. [22]
NitrogenIn-vitro: Increase in bioactivity and antibacterial properties with reference to S. aureus.Gan et al. [23]
Oxygen/ArgonIn-vitro: Increased wettability and cell adhesion, spreading, proliferation, and differentiation of SAOS-2 osteoblastsHan et al. [24]
Oxygen/NitrogenIn-vitro: Decrease in contact angle and no disadvantageous effect on cytocompatibility;Ha et al. [25]
Nitrogen/Argon/(Nitrogen + Argon)In-vitro: Increase in osteogenic activity (Highest: Nitrogen) and antibacterial property (Highest: Nitrogen + Argon)Liu et al. [26]
OxygenIn-vitro: Decrease in contact angleTsougeni et al. [27]
OxygenIn-vitro: Increased cell adhesion and spreading of U2-OS osteoblasts in the presence of S. epidermidisRochford et al. [28]
Water vapour/ArgonIn-vitro: Increased wettability and cell adhesion, spreading, proliferation, and differentiation of osteoblast precursor cell line derived from Mus musculus (mouse) calvaria (MC3T3-E1).Wang et al. [12]
Plasma treatment + Radiation
EUV + (low temperature Nitrogen/Oxygen)In-vitro: Decreased contact angle and increased cell adhesion of MG63 cells, Cell adhesion higher with Nitrogen plasmaCzwartos et al. [29]
Oxygen/UVIn-vitro: Increase in the bond strength to TiO2 sol solution after exposure to O2 plasma/UV radiationKizuki et al. [30]
Plasma + Chemical treatment
Argon + Hydrofluoric acidIn-vitro: Decreased contact angle and increased cell proliferation and differentiation of rBMS cells (Higher with Nitrogen)

In-vivo: Increased resistance to Porphyromonas gingivalis (P. gingivalis)		Chen et al. [31]
Argon/(Argon + Hydrogen peroxide)In-vitro: Increased cell adhesion, collagen secretion, and extra-cellular matrix deposition (Higher with Argon, Peroxide combination)

In-vivo: Increased fibrous tissue filtration inhibition and osseointegration with Argon, Peroxide combination		Ouyang et al. [32]
Plasma + Laser
Oxygen + Nd:YAGIn vitro: Decrease in contact angleAkkan et al. [33]
Plasma + Biomolecules/Inorganic coating
Argon + Polydopamine (PDA) + Vancomycin gelatin nanoparticlesIn vitro: No cytotoxicity and increased antibacterial resistance to Staphylococcus aureus (S. aureus) and Streptococcus mutans (S. mutans)Chen et al. [34]
Nitrogen + TropoelastinIn vitro: Increased bioactivity of osteogenic cellsWakelin et al. [35]
Nitrogen + PDA + Poly (lactic-co-glycolic acid) carrying Bone Morphogenic Protein-2 (BMP-2) geneIn vitro: Increased osteogenic activityQin et al. [36]
(Argon/Oxygen) + Acrylic acid vapours + Polystyrene sulfonate (PSS) and polyallylamine hydrochloride (PAH) multilayersIn vitro: Increased adhesion and proliferation of bone marrow stromal cells

In vivo: Increased osseointegration		Liu et al. [37]
Table
Table 2. Results of ANAB of PEEK.
Table 2. Results of ANAB of PEEK.
TreatmentResultAuthor
ANABIn vitro: Decreased contact angle and increased bioactivity of osteogenic cellsKhoury et al. [41]
ANABIn vitro: Increased wettability and cell adhesion, spreading, proliferation, and differentiation of SAOS-2 osteoblasts

In vivo: Increased bond strength to bone		Khoury et al. [42]
ANABIn vitro: Improved osteoblastic response and decrease in bacterial colonization of MRSA, S. epidermidis, and E. coliWebster et al. [43]
ANABIn vitro: Decreased contact angle and increased bioactivity of osteogenic cellsAjami et al. [44]
Table
Table 4. Results of sulphonation on PEEK.
Table 4. Results of sulphonation on PEEK.
TreatmentResultAuthor
Sulphonation
H2SO4+ (Acetone/Hydrothermal treatment/Sodium Hydroxide (NaOH) immersion)In vitro: Optimal surface characteristics after 5 min exposure to 98% H2SO4; Comparable efficiency by Acetone, hydrothermal treatment and NaOH immersion in removal of residual acidMa et al. [49]
H2SO4+ NaOHIn vitro: Optimal contact angle reduction after exposure of 30 s to 98% H2SO4Wang et al. [50]
H2SO4 + NaOHIn vitro: Decreased contact angle and increased bioactivity of MC3T3-E1 pre-osteoblasts cellsCheng et al. [51]
Sulphonation + Other chemical treatments
H2SO4/ [H2SO4 + Hydrogen peroxide (Piranha solution)]In vitro: Decreased contact angle and increased adhesion and proliferation of human fibroblast cellsdos Santos et al. [52]
(H2SO4 + Nitric acid)/H2SO4In vitro: Decreased contact angle and increased adhesion and proliferation of pre-osteoblasts cells (Highest with combination of H2SO4 and Nitric acid)

In vivo: Increased bone formation around PEEK		Li et al. [53]
H2SO4 + Nitric acidIn vitro: Decreased contact angle and increased bioactivity of osteogenic cellsHuo et al. [54]
Sulphonation + Organic/Inorganic coatings
H2SO4 + LactamsIn vitro: Decrease in growth on S. mutans biofilmMontero et al. [55]
H2SO4 + zeolitic imidazolate framework-8 containing Ag ionsIn vitro: Increase antimicrobial activity against S. aureus and, E. coliYang et al. [56]
H2SO4+ graphene oxideIn vitro: Increase in bioactivity and antibacterial activity against S. mutans and P. gingivalisGuo et al. [57]
H2SO4+ [Simvastatin/Poly(lactic)acid] + Hyaluronic acidIn vitro: Increased MC3T3-E1 cell adhesion and proliferationDeng et al. [58]
H2SO4 + Nickel nanoparticles + HydroxyapatiteIn vitro: Increase in angiogenesis and osteoblastic differentiation

In vivo: Improved osseointegration		Dong et al. [59]
H2SO4+ lithium-ion-loaded Antimicrobial peptide (AMP)In vitro: Increase in bioactivity and antibacterial activity

In vivo: Increased antimicrobial activity and osseointegration		Li et al. [60]
Sulphonation + Plasma + Coatings
H2SO4 + Oxygen plasma + alkaline Simulated Body Fluid (SBF)In vitro: No cytotoxicity to MC3T3-E1 pre-osteoblasts

In vivo: Increased osseointegration		Masomoto et al. [61]
H2SO4 + Oxygen plasma + Poly (Dopamine) + TripeptideIn vitro: Decreased contact angle and increased bioactivity of osteogenic cellsZhu et al. [62]
H2SO4 + Argon plasma + Polar amino functional groupsIn vitro: Increase in bioactivity and antibacterial activity against S. aureus and E. coliWang et al. [63]
Sulphonation + Other chemical treatments + Organic coatings
H2SO4 + Sodium borohydride + Phosphorylated gelatin + BMP-2In vitro: Increased cell bioactivity of MC3T3-E1 pre-osteoblastsWu et al. [64]
H2SO4 + Nitric acid + Dopamine + CollagenIn vitro: Increased cell bioactivity of MC3T3-E1 pre-osteoblastsKim et al. [65]
Table
Table 6. Results of Hydroxyapatite coating on PEEK.
Table 6. Results of Hydroxyapatite coating on PEEK.
TreatmentResultAuthor
Surface coatings—Hydroxyapatite
HydroxyapatiteIn vivo: Increased removal torque and biocompatibilityJohansson et al. [73]
[Hydroxyapatite/(Hydroxyapatite + Microwave annealing)] + YSZ intermediate layerIn vitro: Increased cell adhesion and proliferation with Hydroxyapatite crystallization with microwave annealingRabiei et al. [71]
Hydroxyapatite + Titanium intermediate layer + Hydrothermal treatmentIn vitro: Bond strength of HA with PEEK with <10 nm Ti layer greater than that with >50 nm Ti layerOzeki et al. [72]
[Hydroxyapatite/(Hydroxyapatite + Microwave annealing + Autoclaving)] + YSZ intermediate layerIn vitro: Increased cell adhesion and proliferation with Hydroxyapatite crystallization with heat treatmentDurham et al. [70]
Table
Table 7. Results of Titanium coating on PEEK.
Table 7. Results of Titanium coating on PEEK.
TreatmentResultAuthor
Surface coatings: Titanium
Titanium [Pre-treated with grit blasting + Vacuum plasma (element unspecified)]In vitro: Increased proliferation and differentiation of MC3T3-E1 cells

In vivo: Increased osseointegration		Liu et al. 2021 [79]
Titanium + alkali treatmentIn vitro: Increased adhesion and proliferation of pre-osteoblastsYang et al. [80]
(Oxygen plasma/Sandblasting) + Titanium sol + Hydrochloric acidIn vitro: Increased cell response

In vivo: Increased osseointegration		Shimizu et al. [81]
Titanium dioxide (Pre-treatment: Argon ion + Titanium layer)In vivo: Increased osseointegration and bond strength in pull-out testTsou et al. [82]
Table
Table 8. Results of anti-microbial agent coatings on PEEK.
Table 8. Results of anti-microbial agent coatings on PEEK.
TreatmentResultsAuthor
Surface coatings—Antibiotic agents with carrier
Brushite + Gentamycin sulphateIn vitro: Sustained biocompatibility and increased proliferation and differentiation of pre-osteoblastic cells

In vivo: Increased antimicrobial resistance and osseointegration		Xue et al. [83]
Antimicrobial peptide (AMP) of GL13K/[AMP of GL13K + 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC)]In vitro: Increased antibacterial activity against S. aureusHu et al. [85]
Red selenium nanorods/Gray selenium nanoparticlesIn vitro: Increased antimicrobial activity to P. aeruginosaWang et al. [84]
Table
Table 10. Composites of PEEK and surface treatments.
Table 10. Composites of PEEK and surface treatments.
TreatmentResultsAuthor
PEEK + Poly (ether imide) +Titanium dioxide coatingIn vitro: Antibacterial resistance against gram-positive and gram-negative bacteriaDíez-Pascual et al. [89]
3D printed PEEK + crystalline HydroxyapatiteIn vitro: Increased adhesion, proliferation and differentiation of pre-osteoblasts and osteogenesisOladapo et al. [90]
Carbon reinforced PEEK + Zirconium ions using PIIIIn vitro: Increased bioactivity of mBMSC cells and increased expression and activity of alkaline phosphatase, increased antibacterial activity against S. aureus, no effect against E. coliLi et al. [91]
Carbon reinforced PEEK + H2SO4 + Oxygen plasma + Calcium phosphateIn vitro: Increased precipitation of apatite nuclei in SBF mediumYamane et al. [92]
Carbon reinforced PEEK + H2SO4 + Dopamine HCl + Titanium carbideIn vitro: Evidence of photothermal antibacterial activity and cytocompatibility

In vivo: Evidence of osseointegration		Du et al. [93]
Carbon reinforced PEEK + H2SO4 + Calcium chlorideIn vitro: Increased precipitation of apatite nuclei in SBFMiyasaki et al. [94]
Carbon reinforced PEEK + H2SO4 + Oxygen plasma + amorphous Calcium phosphateIn vitro: Increased precipitation of apatite nuclei in SBF mediumYabutsuka et al. [95]
Carbon reinforced PEEK + H2SO4 + HydroxyapatiteIn vitro: Decrease in contact angleAsante et al. [96]
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Dondani, J.R.; Iyer, J.; Tran, S.D. Surface Treatments of PEEK for Osseointegration to Bone. Biomolecules 2023, 13, 464. https://doi.org/10.3390/biom13030464

AMA Style

Dondani JR, Iyer J, Tran SD. Surface Treatments of PEEK for Osseointegration to Bone. Biomolecules. 2023; 13(3):464. https://doi.org/10.3390/biom13030464

Chicago/Turabian Style

Dondani, Jay R., Janaki Iyer, and Simon D. Tran. 2023. "Surface Treatments of PEEK for Osseointegration to Bone" Biomolecules 13, no. 3: 464. https://doi.org/10.3390/biom13030464

APA Style

Dondani, J. R., Iyer, J., & Tran, S. D. (2023). Surface Treatments of PEEK for Osseointegration to Bone. Biomolecules, 13(3), 464. https://doi.org/10.3390/biom13030464

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop