Efficient Separation of Hydroxylamine from Metal Ions by PIM-ED Process

Abstract

Selective separation of hydroxylamine (HA) from metal ions to prepare high-purity HA remains a challenge. In this study, given that HA can react with carbonyl compounds, TTA (thenoyltrifluoroacetone) was screened as a carrier to prepare the polymer inclusion membrane (PIM), which was used to separate HA from metal and inorganic acid ions. The experimental results demonstrated that the PIM exhibited good selectivity for HA. During the PIM process, the proton gradient served as a driving force to transport NH₂OH(I). The electrodialysis (ED) process was used to efficiently and continuously provide proton gradient without introducing other ions, which coupled with PIM to separate HA. Under the optimum conditions, the separation factors of NH₂OH(I)/Na(I) and NH₂OH(I)/K(I) were 30.81 and 35.11; the purity of HA was 99.4%, indicating that the PIM-ED process can be used for high-purity preparation of HA.

1. Introduction

Hydroxylamine (HA) is widely used in the chemical, pharmaceutical, and electronic industries [1,2,3]. HA is primarily produced through the reaction of HA salts with inorganic bases and then separated by distillation or ion exchange [4]. The separation methods with low selectivity and efficiency result in the HA product containing certain metal ions and inorganic acid ions [4,5]. The residual metal ions and inorganic acid ions could accelerate the decomposition of HA products and limit their application [6,7,8].

A polymer inclusion membrane (PIM) is developed from a liquid membrane. PIMs are composed of a carrier and a base polymer, where the carrier is incorporated into the entangled chains of the base polymer and can separate target ions with high selectivity through specific binding of the carrier to the target ions [9,10,11,12]. Due to their advantages of simultaneous extraction and stripping, good flexibility, and high selectivity, PIMs have been used to separate metal ions and small organic molecules [11,12,13,14,15,16]. For instance, Cai et al. [12] prepared a PIM by selecting TTA and TOPO as carriers for the separation of Li(I) from Na(I) and K. The separation factors of Li(I)/Na(I) and Li(I)/K(I) were 54.25 and 50.60, respectively. O’Bryan [13] used Aliquat336 as a carrier and PVDF-HFP as a base polymer to separate SCN⁻, and the PIM showed good transport performance for SCN⁻. Almeida et al. [14] selected dinonylnaphthalene sulfonic acid (DNNS) as a carrier to prepare PIM, which has been used in monitoring ammonia contamination in waters; the PIM showed high selectivity for the ammonium ion. Mwakalesi et al. [15] used polymer inclusion membranes (PIMs) with anacardic acid (AA) as a carrier for the extraction and transport of 4-amino-2-chloropyridine (ACP), paraquat, and diquat as representative target solutes of organic pesticide residues in aqueous solutions. The transport efficiency of ACP, paraquat, and diquat reached 98%, 100%, and 100%. Casadellà et al. [16] developed a polymer inclusion membrane selective for ammonium using tripodal pyrazole substituted benzene as the ionophore. As the content of the ionophore increased from 2 wt.% to 5 wt.%, the selectivity of NH₄⁺/Na⁺ and NH₄⁺/K⁺ was reduced from 13.07 to 9.33 and from 14.15 to 9.57. Based on enhancing the different affinities between the metal ions and the carrier, a polymer inclusion membrane with Aliquat336 as the carrier was prepared to separate Mo (VI) and V(V) ions with similar properties; the separation factor of Mo(VI) and V(V) achieved 333.4 [17]. Depending on the property of HA to react with carbonyl compounds (such as aldehydes, ketones, and esters) [18,19,20,21], it may be possible to achieve selective separation of HA from metal ions by selecting suitable carriers.

In this work, depending on the steric effects and eletrophilicity, the reactivity of HA with carbonyl compounds is in descending order: aldehydes, ketones, and esters [22,23]. The ketones (TTA, SPEEK, and SMP-II) with higher boiling points and more carbonyl groups were selected as HA carriers for PIM preparation. The result showed that the PIM with TTA as a carrier exhibited good selectivity and permeability of HA. In the PIM process, the proton gradient was the driving force to transport NH₂OH(I). To continuously and efficiently supply a proton gradient without introducing other ions, the ED process was used to separate HA from metal. The effects of related factors such as carrier types, carrier content, current density, and initial concentration of HA were investigated. Under the optimal conditions, the separation factors of NH₂OH(I)/Na(I) and NH₂OH(I)/K(I) were 30.81 and 35.11; the purity of HA was 99.4%, indicating that the PIM-ED process can be used for the selective separation of HA from metal ions and inorganic acid ions.

2. Materials and Methods

2.1. Material

The PVDF was bought by Solvay Advanced Polymer Co., Ltd. (Shanghai, China). A.R. Thenoyltrifluoroacetone (TTA) was obtained from Shanghai Macklin Biochemical Technology Co., Ltd. (Shanghai, China). Sulfonated phenolic resin (SMP-II) with a molecular weight (Mw) of 80 was purchased from Hebei Yanxing Chemical Co., Ltd. (Xingtai, China). Poly(ether-ether-ketone) (PEEK) was acquired from Suyuan Plastic Material Sales Department(Shenzhen, China) in the form of a powder with a molecular weight (Mw) of 100,000. Deionized water with a conductivity of 1 μS·cm⁻¹ was produced by laboratory reverse osmosis equipment. Dimethylformamide (DMF) was purchased from Fuchen Chemical Reagent Co. (Tianjin, China). Hydroxylamine sulfate ((NH₂OH)₂·H₂SO₄), ammonium chloride (NH4Cl), sodium chloride (NaCl), and potassium chloride (KCl) were supplied by Aladdin Industrial Corporation (Shanghai, China). Carbon electrodes were purchased from Aimite (Dongguan) New Material Co. (Guangdong, China). Anion exchange membrane (AEM, types: AMI-7001) and cation exchange membrane (CEM, types: CMI-7000) were purchased from Beijing Apslong Technology Co., Ltd. (Beijing, China). Molecular structures of the PVDF, TTA, and SMP-II are shown in Figure 1.

2.2. Synthesis of SPEEK

SPEEK is obtained by sulfonation of PEEK, and the reaction equation is shown in Figure 2. PEEK was dried in a vacuum oven at 100 °C before use. Eight grams of PEEK was dissolved in 500 mL of concentrated sulfuric acid (98 wt.% H₂SO₄) and stirred at 70 °C for 5 h. After the sulfonation reaction, the obtained polymer solution was cooled below 5 °C to terminate the reaction, and then the solution was dropped into a large amount of ice-cold deionized water to form SPEEK fibers. The precipitate was repeatedly washed with deionized water until the pH value became neutral. Then, the polymer was dried at 60 °C for 48 h.

2.3. Membrane Preparation

In this study, PIMs with PVDF as the base polymer and TTA, SPEEK, or SMP-II as the carriers were prepared by the casting method. As shown in Figure 3, 1.0 g of the PIM component (as shown in

Table 1. Composition and proportions of the PIMs.

Carrier	Carrier Content (wt.%)	Base Polymer	Base Polymer Content (wt.%)
SMP-II	50	PVDF	50
SPEEK	50	PVDF	50
TTA	50	PVDF	50
TTA	40	PVDF	60
TTA	30	PVDF	70
TTA	20	PVDF	80
TTA	10	PVDF	90

) was dissolved in 20 mL of dimethylformamide (DMF) at 40 °C and degassed for 48 h at room temperature to obtain a uniform casting solution. The casting solution was poured onto a flat glass (12 × 12 cm), the casting gap was 3 mm, and it was completely dried at 30 °C to obtain the PIM.

2.4. Transport Experiment

In the feed phase, the HA is formed as NH₃OH⁺ (NH₂OH(I)). The traditional preparation of HA mainly used an inorganic base to react with HA salts. Therefore, a mixed solution of NaCl, KCl, and hydroxylamine sulfate ((NH₂OH)₂·H₂SO₄) was used as the feed phase for the transport experiments.

In order to screen suitable carriers and study the PIM transport mechanism of HA, experiments were carried out to separate HA by the PIM process. As shown in Figure 4, the experimental set-up consisted of two permeation chambers separated by a PIM with an effective area of 36 cm². The experiment was conducted at 20 °C. The feed phase (150 mL) consisted of a mixture of NH₂OH(I), Na(I), and K(I) with a concentration of 0.25 mol·L⁻¹, and the stripping phase (150 mL) was acids (H₂SO₄ or HCl) with a concentration of 0.0–0.1 mol·L⁻¹. The sample was removed from the feed and stripping phases and replaced with an equal volume of fresh material. The concentrations of NH₂OH(I), Na(I), and K(I) were monitored by ion chromatography.

2.5. PIM-ED Process Transport Experiment

As shown in Figure 5, the PIM-ED process consisted of four permeation cells separated by membranes. The external electric field was provided by a stable DC power supply with carbon electrodes, and different current densities (0–15 mA·cm⁻²) were selected for the transport experiments. The effective separation area of the membrane was 36 cm². The feed phase (150 mL) contained 0.125 mol·L⁻¹ (NH₂OH)₂·(H₂SO₄) and a 0.25 mol·L⁻¹ KCl and NaCl mixed solution, and the stripping phase was deionized water. The temperature in each of the four compartments was kept constant at 20 °C. At regular intervals, 0.5 mL of sample was taken from the feed and stripping phase solutions and replaced with an equal volume of fresh material. The concentrations of NH₂OH(I), K(I), and Na(I) were monitored by ion chromatography.

The k of NH₂OH(I) was calculated by the PIM-ED process based on the first-order reaction.

$$\ln \left({\displaystyle \frac{C_{i,t}}{C_{i,t=0}}}\right)=-kt$$

(1)

where k (s⁻¹) is the rate constant, C_i,t  = 0 (mol·L⁻¹) and C_i,t (mol·L⁻¹) refer to the initial concentration of ions in the feed phase and the concentration of ions at a given time in the feed phase, and t (s) is the transport time.

Permeability coefficient (P) was calculated as follows in Equation (2):

$$P={\displaystyle \frac{V}{A}}k$$

(2)

where P (μm·s⁻¹) represents the permeability coefficient, A (cm⁻²) is the membrane effective area, and V (mL) is the two-phase volume.

The initial flux (J₀) can be calculated using Equation (3) when the concentration of each ion in the feed phase is a constant:

$$J_0=P{C}_{i,t=0}$$

(3)

The extraction efficiency (E(%)) and stripping efficiency of ions in the feed phase was calculated as follows:

$$E\left(\%\right)={\displaystyle \frac{C_{i,t=0}-C_{i,t}}{C_{i,t=0}}}$$

(4)

$$R\left(\%\right)={\displaystyle \frac{C_{i,t}}{C_{i,t=0}}}$$

(5)

The formulae for the separation factors of NH₂OH(I) and Na(I) ions are given below:

$${\beta }_{{NH}_{2}OH\left(I\right)/Na\left(I\right)}={\displaystyle \frac{J_{{NH}_{2}OH\left(I\right)}/C_{{NH}_{2}OH\left(I\right)}}{J_{Na\left(i\right)}/C_{Na\left(I\right)}}}$$

(6)

where J_NH2OH(I) and J_Na(I) is the flux of the NH₂OH(I) and Na(I).

The formulae for the purity of HA as follows:

$$PR\left(\%\right)={\displaystyle \frac{C_{s,t}}{C_{tital,t}}}$$

(7)

where C_s,t (mol·L⁻¹) refer to the concentration of HA and C_tittal,t (mol·L⁻¹) refer to total ion concentration at a given time in the stripping phase.

The current efficiency (η) of the PIM-ED process was calculated using Equation (8):

$$\eta \left(\%\right)={\displaystyle \frac{Q_{{NH}_{2}OH\left(I\right)}}{Q_{tital}}}={\displaystyle \frac{F(C_{i,t=0}-C_{i,t})}{It}}$$

(8)

where η represented the current efficiency, Q_total(C) is the total quantity of electric charge through the PIM, Q_NH2OH(I)(C) is the quantity of NH₂OH(I) charge of through the PIM, F is the faraday constant, and I(A) is the total current.

3. Results and Discussion

3.1. PIM Process for HA Separation

3.1.1. Screening of Carrier Types

Based on the reactivity of HA with carbonyl compounds, SPEEK, SMP-II with sulfonic acid groups, and carbonyl groups and TTA rich in carbonyl groups were chosen as carriers for the preparation of PIM. The separation properties of NH₂OH(I) from Na(I) and K(I) were studied in the PIM process.

As can be seen from

Table 2. Effect of different carrier types. (PIM: 50 wt.% carrier (TTA, SMP-II, or SPEEK) + 50 wt.% base polymer (PVDF); Feed phase: 0.125 mol·L⁻¹ (NH₂OH)₂·H₂SO₄, 0.250 mol·L⁻¹ KCl, and NaCl, pH = 7; Stripping phase: 0.1 mol·L⁻¹ H₂SO₄; Experimental time: 16 h).

Carrier Types	J0NH2OH(I) (mol·m−2·h−1)	βNH2OH/K(I)	βNH2OH/Na(I)
SMP-II	0.14 ± 0.01	2.4 ± 0.4	0.7 ± 0.3
SPEEK	0.19 ± 0.01	1.1 ± 0.1	2.1 ± 0.1
TTA	0.44 ± 0.03	37.8 ± 0.7	39.9 ± 0.8

, PIM with TTA as the carrier had a better performance in the transport of NH₂OH(I). The reason could be that TTA contained more carbonyl groups, which provided abundant binding sites for NH₂OH(I) transport and promoted the transfer of NH₂OH(I). PIM with SMP-II or SPEEK as a carrier had similar NH₂OH(I), Na(I), and K(I) migration properties. The results showed that the sulfonic acid played a dominant role in ion transport compared to the carbonyl group in the PIM process. Therefore, TTA was screened as a carrier for subsequent experiments.

3.1.2. Effect of Feed and Stripping Condition

The chemical kinetics of the complexation reaction were critical for PIM selectivity and transport rate [24]. As shown in Equation (9), the reaction between NH₃OH⁺ and the carbonyl group on the carrier is a chemical equilibrium reaction. When NH₃OH⁺ reacts with a carrier, protons are released, while the dissociation of the NH₃OH⁺ from the complex needs the supply of protons. As shown in Figure 6, in PIM process, NH₃OH⁺ diffuses from the feed phase to the stripping phase. To maintain the reaction equilibrium and continuity of NH₃OH⁺ transport, protons need to transport in the opposite direction to that of NH₃OH⁺. Therefore, as the NH₃OH⁺ transport proceeds, the protons will be continuously transported from the stripping phase to the feed phase, resulting in a decrease in the pH of the feed phase. The proton gradient between the two phases was needed to supply the driving force for target ion transport [10,24,25].

$$N{H}_{3}O{H}^{+}+R=O\leftrightarrow R-NOH+H_3{O}^{+}$$

(9)

Figure 7 shows the influence of pH in the initial feed phase, which varied from 1.0 to 7.3 (the stripping phase was 0.70), on the transport of NH₂OH(I). The permeability coefficient and the extraction efficiency of PIM in transporting NH₂OH were improved by increasing the proton gradient (the pH of initial feed phase was from 1.0 to 7.3 and the stripping phase was 0.70). As the experiment proceeds, the proton concentration increases in the feed phase (as shown in Figure 7c and decreases in the stripping phase, resulting in a decrease in the driving force for NH₂OH(I) transported by PIM. The migration efficiency of NH₂OH(I) gradually decreased, which can be seen in Figure 7b. Therefore, increasing the proton gradient in the feed and stripping phase was useful for improving the NH₂OH(I) transport efficiency. In addition, HA decomposition was faster at higher alkalinity, so the initial pH of the feed for subsequent experiments was between 7–8.

To investigate the effect of the stripping solution on NH₂OH(I) transport in PIM system, experiments were carried out using different concentrations of HCl or H₂SO₄ as the stripping solution. As shown in Figure 8, the type of acid had little effect on the efficiency of the stripping phase. Moreover, when the stripping solution was deionized water (the initial pH of the stripping phase and feed phase was 7), NH₂OH(I) was hardly transported to the stripping phase, indicating that the proton gradient between the feed and stripping phases significantly affected the transport of NH₂OH(I) in the PIM process. Therefore, it is necessary to provide a proton gradient between the feed and stripping solutions in the PIM process for the transport of target species.

3.2. PIM-ED Process for HA Separation

In the PIM process, the proton gradient between the feed and stripping phases was the driving force for transporting NH₂OH(I), which introduced new ions. To provide an efficient and continuous proton gradient without introducing other ions, the ED process coupled with PIM was used to provide a proton gradient to separate HA from metal ions.

3.2.1. Effect of Carrier Content

PIMs with different TTA contents were characterized and analyzed by SEM-EDS techniques to understand the morphology, structure, and composition. As shown in Figure 9a–e, the morphology surface of all PIMs had a dense, crack-free, and non-porous structure. With increasing TTA content, the surface structure of the PIM gradually became rough, which can be attributed to the increase in TTA content on the membrane surface. It has been shown that increasing the roughness of the PIM surface provides a larger effective area, which promotes ion transport [26]. In addition, the composition of the PIM was analyzed by EDS. From Figure 9f,g, in the EDS spectra of the PIM with TTA as a carrier, the element S was uniformly distributed, indicating that TTA was a uniform arrangement of the membrane for the PIM and the successful preparation of the PIM.

PIM with the TTA content from 10 wt.% to 50 wt.% was used for the separation of NH₂OH(I) from Na(I) and K(I) in PIM-ED process. From Figure 10a, the permeability coefficient of NH₂OH(I) improved with increasing TTA content. This phenomenon was attributed to the fact that the surface of the membrane became significantly rougher with the increase in the carrier content (as shown in Figure 9b, which increased the effective area of the membrane and accelerated the membrane transfer rate of NH₂OH(I). In addition, increasing the carrier content would shorten the distance between the carriers in the membrane, reducing the diffusion resistance of the target substances [17,26] and further improving the permeability coefficient of NH₂OH(I). From Figure 10b, as the PVDF content increased from 50 wt.% to 90 wt.%, the thickness of the membrane increased from 148.6 μm to 356.8 μm, which led to an increased resistance to diffusion of the PIMs, resulting in a higher initial flux of PIMs. On the other hand, there was a trade-off effect between thickness and the mechanical strength of the membrane [27]. Therefore, this paper identified the preferred composition for PIM as 50 wt.% PVDF + 50 wt.% TTA.

3.2.2. Effect of Current Density

In previous studies, the introduction of an electric field reduced the resistance to ion transport across the membrane, which in turn significantly increased the transport efficiency of the target ions [17,26,28]. To explore the influence of the electric field on the selective separation of NH₂OH(I) from K(I) and Na(I) and the mechanism of ion transport facilitated by PIM-ED, the experiments were carried out with different current densities.

Figure 11 shows the variation of pH in the feed phase and the stripping phase at different current densities. The proton and hydroxide ions generated in the ED process are transported to the stripping phase and the feed phase, driven by electric field, causing changes in the proton gradient between the stripping phase and feed phase, increasing the driving force for proton transport and facilitating proton transport. As the current density increases, the proton generation rate increases, leading to an increase in the proton gradient and accelerating the opposite transport of NH₂OH(I) and protons, thus causing a change in pH on the feed side.

Figure 12 illustrated a significant increase in the permeability coefficient of NH₂OH(I) while maintaining selectivity with an applied electric field. The permeability coefficient of PIM was only 0.01 μm·s⁻¹ in the absence of an electric field (current density = 0 mA·cm⁻²). As the current density increased from 0 to 5 mA·cm⁻², the permeability coefficient of NH₂OH(I) increased smoothly from 0.01 to 1.42 μm·s⁻¹. Subsequently, the permeability coefficient of NH₂OH(I) rose sharply from 1.42 to 2.84 μm·s⁻¹ as the current density increased from 5 to 7 mA·cm⁻². As the current density was further increased, a higher operating voltage was required, and more energy was consumed in water electrolysis and heat generation, while the NH₂OH(I) transfer efficiency remained unchanged, resulting in a decrease in current efficiency. Therefore, the preferred current density for this study was 10 mA·cm⁻².

3.2.3. Effect of Concentration of NH₂OH(I) in Feed Phase

The PIM-ED process was used for producing high-purity HA. Experiments were carried out with various initial concentrations of NH₂OH(I).

From

Table 3. Effect of concentration in the feed phase on the synthesis of HA. (Feed phase: 0.025–0.255 mol·L⁻¹ (NH₂OH)₂·H₂SO₄, 0.250 mol·L⁻¹ KCl and NaCl, pH = 7; Stripping phase: deionized water, pH = 7; Experimental time: 10 h; PIM: 50 wt.% TTA + 50 wt.% PVDF: Current density: 10 mA·cm⁻²).

C0NH2OH(I)(mol·L−1)	J0 (mol·m2·h−1)	Extraction Efficiency (%)	Stripping Efficiency (%)	HA Purity (%)
0.05	0.72 ± 0.02	95.2 ± 1.2	90.3 ± 2.4	98.0 ± 0.2
0.11	1.31 ± 0.03	96.4 ± 1.2	94.0 ± 1.2	98.2 ± 0.3
0.25	2.84 ± 0.06	93.7 ± 0.9	92.3 ± 0.5	99.4 ± 0.1
0.51	3.79 ± 0.09	82.9 ± 0.5	65.7 ± 0.5	79.8 ± 0.6

, it can be seen that the flux and the purity of HA increased with increasing initial concentration of NH₂OH(I) from 0.05 mol·L⁻¹ to 0.25 mol·L⁻¹. The gradual increase in the initial concentration of NH₂OH(I) significantly increased the contact opportunity between NH₂OH(I) and carriers, which promoted the formation of ion-carrier complexes, thereby increasing the NH₂OH(I) flux. Furthermore, this process followed Fick’s law of diffusion, where increasing the feed concentration increased the initial flux by improving the concentration gradient between the feed and stripping solutions.

From Table 3 and Figure 13, the purity of HA was significantly reduced from 99.4% to 79.8% with the initial concentration of NH₂OH(I) increasing from 0.25 to 0.51 mol·L⁻¹. This phenomenon can be attributed to the fact that the carbon electrode may contain metal ions, which diffused through the membrane into the stripping phase, leading to the decomposition of HA at higher concentrations to form ammonia in the presence of metal ions [29]. The ammonia further increased the pH of the solution and accelerated the decomposition of HA [30,31,32]. The high-purity HA could be produced in the PIM-ED process by controlling metal ion concentrations and the pH of the stripping phase. In addition, under the optimal conditions, the yield and purity of HA were 92.3% and 99.4%, while through the distilling methods, a yield ranging from 75% to 90% and a purity of over 99% can be obtained. This indicates that the PIM-ED process provides an efficient method to prepare high-purity HA [33,34].

As shown in Figure 14, an electro-membrane extraction (EME) device without AEM and CEM was constructed to investigate the effect of the electrodes on HA synthesis. The new device was used to prepare HA. Other experimental conditions were the same with the original device: Current density:10 mA·cm⁻², feed phase (0.125 mol·L⁻¹ (NH₂OH)₂·H₂SO₄, 0.250 mol·L⁻¹ KCl and NaCl, pH = 7), stripping phase (deionized water, pH = 7), PIM (50 wt.% TTA + 50 wt.% PVDF).

From Figure 15, the permeability coefficient of NH₂OH(I) and the purity of HA in the stripping phase of the PIM-EME process were lower than those of the PIM-ED process. In the PIM-EME process, metal ions from the carbon electrode were released directly into the stripping solution, which accelerated the decomposition of HA in the stripping phase. In contrast, the other process prevented metal ions from passing from the anode chamber to the stripping chamber, which mitigated the decomposition of HA. In addition, compared with the PIM-ED process, the feed solution and the stripping solutions were directly electrolyzed in the EME process, resulting in solution loss and the generation of a large number of air bubbles, which reduced the transfer efficiency (as shown in Figure 15b).

3.3. Stability Study

Membrane stability plays a key role in determining the industrialization of PIM. Figure 16 shows the variation of permeability coefficients and selectivity in a transport experiment performed on the same membrane for five cycles.

After five cycles of experiments, the permeability coefficient of the PIM decreased from 3.13 μm·s⁻¹ to 2.89 μm·s⁻¹, indicating that the PIM had good stability. The main reason for the decrease in the PIM performance in the repeated experiments was the loss of carrier molecules on the membrane surface. As the experiment processed, carriers with relatively low binding to the PVDF on the membrane surface dissolved into the aqueous phase. In addition, the membrane performance gradually stabilized as the number of cycles increased (as shown in Figure 16), indicating that the carriers were better fixed in the interior of the membrane.

4. Conclusions

In this paper, the PIM process was employed to achieve the separation of Hydroxylamine (HA) from metal ions. TTA was screened as a carrier due to its abundant carbonyl sites. In the PIM process, the proton gradient was needed to provide the driving force to transport HA. The ED process has been employed to efficiently supply the proton gradient to separate HA from metal ions. In the ED process, the electric field could rapidly change the proton gradient between the feed phase and the stripping phase, which accelerates the reverse migration process of protons and target ions in the PIM process, thus promoting the transport of NH₂OH(I). The high purity of HA could be produced by controlling the metal ion concentrations and pH in the PIM-ED process. Under the optimized conditions, the separation factors of NH₂OH(I)/Na(I) and NH₂OH(I)/K(I) were 30.81 and 35.11; the purity of HA was 99.4%, providing a strategy for the preparation of high-purity hydroxylamine (HA).