Next Article in Journal
Engineered Magnetization Dynamics of Magnonic Nanograting Filters
Next Article in Special Issue
Enrichment and Detection of Antigen-Binding B Cells for Mass Cytometry
Previous Article in Journal
Near-Infrared Emissive Cyanido-Bridged {YbFe2} Molecular Nanomagnets Sensitive to the Nitrile Solvents of Crystallization
Previous Article in Special Issue
Enrichment of Rabbit Primitive Hematopoietic Cells via MACS Depletion of CD45+ Bone Marrow Cells
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

The Effect of pH and Viscosity on Magnetophoretic Separation of Iron Oxide Nanoparticles

by
Leonie Wittmann
,
Chiara Turrina
and
Sebastian P. Schwaminger
*
Bioseparation Engineering Group, Department of Mechanical Engineering, Technical University of Munich, Boltzmanstr. 15, 85748 Garching bei München, Germany
*
Author to whom correspondence should be addressed.
Magnetochemistry 2021, 7(6), 80; https://doi.org/10.3390/magnetochemistry7060080
Submission received: 29 April 2021 / Revised: 29 May 2021 / Accepted: 30 May 2021 / Published: 3 June 2021
(This article belongs to the Special Issue Magnetic Cell Separation)

Abstract

:
Magnetic nanoparticles (MNPs) are used for magnetophoresis-based separation processes in various biomedical and engineering applications. Essential requirements are the colloidal stability of the MNPs and the ability to be separated even in low magnetic field gradients. Bare iron oxide nanoparticles (BIONs) with a diameter of 9.2 nm are synthesized via coprecipitation, exhibiting a high saturation magnetization of 70.84 Am2 kg−1 and no remanence. In our study, zeta potential, dynamic light scattering (DLS), and sedimentation analysis show that the aggregation behavior of BIONs is influenced by pH and viscosity. Small aggregate clusters are formed with either low or high pH values or increased viscosity. Regarding magnetophoresis-based separation, a higher viscosity leads to lower magnetophoretic velocities, similar to how small aggregates do. Additionally, cooperative magnetophoresis, the joint motion of strongly interacting particles, affects the separation of the BIONs, too. Our study emphasizes the effect of pH and viscosity on the physicochemical characteristics of MNPs, resulting in different aggregation behavior. Particularly, for high viscous working media in downstream processing and medicine, respectively, the viscosity should be taken into account, as it will affect particle migration.

Graphical Abstract

1. Introduction

Magnetic nanoparticles (MNPs) have become an important nanomaterial in biotechnology, in chemistry, and in medicine [1,2,3,4,5,6]. They entail characteristics such as biocompatibility, high binding capacities, and cost-efficient production via coprecipitation. Moreover, their superparamagnetic properties are advantageous during the separation process, as the MNPs show no remanence at room temperature. However, when applying a magnetic field, they possess a high magnetic susceptibility and can be easily separated [7,8]. For biological samples, it is challenging to separate a target entity from a complex mixture with different components. Here, magnetophoresis-based processes provide a simple and efficient method, where the desired entity (magnetic or magnetically labeled with MNPs) is isolated by applying an external magnetic field [9,10,11]. For the method of High Gradient Magnetic Separation (HGMS), a suspension containing the magnetic material is pumped through a separation chamber, and it is trapped by a magnetically susceptible matrix due to high magnetic field gradients (102–104 T m−1) [9,11,12]. In contrast, low magnetic field gradients (<100 T m−1) are used for Low Gradient Magnetic Separation (LGMS), where a magnet is placed outside the particle suspension without contacting the particles [13]. Both modes of operation can be realized with either a permanent magnet or an electromagnet. However, the latter brings up several challenges. The installation costs are higher than a permanent magnet, and cooling might be necessary to counteract the Joule heating. Thus, water usage is required besides energy consumption [14]. Therefore, a permanent magnet might be preferred in the biomedical field. Moreover, in microfluidics, the implementation of a permanent magnet with a high magnetic field gradient is more advantageous, as Alnaimat et al. summarize [15].
For LGMS or HGMS applications, such as in microfluidics [16] or in medicine [17,18,19,20,21,22], it is important to have a defined and stable particle size. Hence, MNPs need to meet the following requirements. On the one hand, they should be colloidal stable and not form aggregates so that they remain their defined size during fractionation or separation [5]. Particularly, for medical purposes, such as hyperthermia treatment or magnetic resonance imaging, the particle diameter should be smaller than 100 nm without forming large aggregates [17,19,23,24]. On the other hand, it should be possible to isolate the colloidal stable MNPs with the respective magnetic field gradient [25].
Regarding downstream processing, the handled liquids, e.g., cell lysates or hydrolysates coming out of fermentation, pose another challenge. Viscosity becomes an essential factor, influencing the separation performance [26,27,28]. Furthermore, in medical applications, the medium blood exhibits a higher viscosity, being fivefold higher than the one of water [29]. In addition to the higher viscosity, serum proteins or other blood components might influence the aggregation behavior [20,21]. However, the so-called biocorona, which is determined by the liquid components such as biomolecules, bacterial debris, proteins, or lipids, could also prevent the aggregation of MNPs [30]. Socoliuc et al. recently emphasized the importance of characterizing the aggregation behavior of MNPs in the respective medium, e.g., cell culture media, and not only in water [18]. Besides the intrinsic characteristics of the working liquid, an increase in viscosity could be advantageous for the microfluidic processing of magnetic particles [31]. In order to avoid sedimentation effects during the process, Solsona et al. developed a microfluidic chip for the magnetophoretic sorting of single-catalyst particles composed of iron [31]. Hence, working with different viscosities might facilitate process handling, or a specific medium might give another viscosity. We would like to point out that besides other parameters, e.g., pH, the viscosity might influence the particle aggregation behavior as well.
Concerning an LGMS process, the control of aggregation is important, as it has been shown that, despite low magnetic field gradients, the particles can be separated, mainly due to cooperative magnetophoresis [32,33,34]. By extending the DLVO theory with the magnetic interaction, this phenomenon can be explained [35]. Here, particles form aggregates because of the magnetic field gradient, as their magnetic dipoles align, and the cooperative effect speeds up the magnetophoretic separation. According to Faraudo et al., these aggregates are reversible for high zeta potentials. Electrostatic repulsion and magnetic attraction form a secondary minimum besides the primary one, separated by a potential barrier [35]. The magnetic Bjerrum length poses a parameter, which enables the evaluation of aggregation throughout a magnetophoretic process. It describes the distance of two parallel dipoles, where the magnetic force equals the thermal energy. Due to this parameter, it can be estimated if the magnetic dipoles are interacting with each other or not.
λ B = µ 0 · m 2 2 · π · k B · T 1 3
The Bjerrum length is dependent on the permeability of free space µ0 = 4π × 10−7 H m−1, the Boltzmann’s constant kB = 1.381 × 10−23 J K−1, the temperature T, and the magnetic dipole, which is written as
m = M S · ρ p · 4 3 · π · r 3 ,
where the saturation magnetization per unit mass of colloid is MS, the particle density is ρP, and the particle radius is r.
This study emphasizes the importance of understanding the aggregation behavior of bare iron oxide nanoparticles (BIONs) in different viscosities. The influence on a separation process in a low magnetic field gradient is investigated by the magnetophoretic sedimentation velocity with a sedimentation analyzer. The following hypotheses are proposed:
  • The aggregation behavior of BIONs in the gravity field is dependent on pH and viscosity, respectively. Therefore, the colloidal stability can be selectively controlled.
  • During magnetophoresis, these effects directly influence the separation process. The aggregate size, as well as viscosity, result in different magnetophoretic velocities.
Four different pH values between 4 and 9, which clearly show the pH’s influence on aggregate size and therefore on magnetophoretic sedimentation velocity, are chosen. The viscosity of water (η = 0.888 mPa s) is compared with the 2.5-fold viscosity. A higher viscosity can be beneficial for magnetophoretic sorting processes, as field-induced aggregation and convection only play a minor role at elevated viscosities [31,33]. The higher viscosity is obtained by adding sucrose (η = 2.227 mPa s).

2. Results and Discussion

2.1. Particle Characterization

BIONs are synthesized via coprecipitation. They exhibit a high saturation magnetization of 70.84 Am2 kg−1 (Figure 1a), no remanence and no hysteresis at 0 Oe [36,37,38]. The chemical composition and the crystalline spinel structure were previously described by Schwaminger et al. [39]. With Transmission Electron Microscopy (TEM) (Figure 1b), the optical diameter of the BIONs is examined, resulting in an average single particle diameter of 9.92 nm, which is similar to previous measurements of BIONs [38,39,40].

2.2. Influencing the Colloidal Stability of the BIONs due to Viscosity and pH

Zeta potential is the electrostatic potential at the particle’s slipping plane, which presents the interface between the moving fluid and the fluid attached to the particle surface. Therefore, the zeta potential is used as a relative measurand for the surface potential and, thus, for the magnitude of a particle’s charge. Due to the extent of electric repulsion between the particles in the solution, the colloidal stability can be evaluated. The repulsion energy is thereby dependent on the particles’ radius and the extent of shielding, which is affected by the ionic strength of the solvent [41]. Figure 2 illustrates the course of zeta potential versus pH and presents the amphiphilic character of the BIONs’ surface. At very low and high pH, it ranges between 20 and 35 mV or −20 and −35 mV, meaning the BIONs’ net charge is positive or negative, respectively. Thus, the particles’ repulsion is high, and they are colloidally stable, leading to less aggregation. The hydrodynamic diameter measurement goes in line with this assumption, as it shows low diameters for low and high pH values. While the isoelectric point (IEP), where the potential is 0, is 6.69 for the low viscous solution (η = 0.888 mPa s) (Figure 2a), it is 6.07 for the high viscous solution (η = 2.227 mPa s) (Figure 2b) [42]. Here, the particles form aggregates up to 3000 nm in both liquids because of their low superficial charge. Comparing the particle distributions of both solutions, the one with the low viscosity (Figure 2a) exhibits a wide distribution over pH. In contrast, for the other one (Figure 2b), large aggregates can only be observed at pH 5 and 6. Thus, in the higher viscous solution, the colloidal stability of the BIONs is given over a broader pH range from pH 2 to 4 and pH 7 to 10. In addition, the polydispersity index (PDI) of the measured samples (Figure S1) confirms these results, as it is between 0.18 ± 0.09 and 0.24 ± 0.04 for the high viscous solution, whereas it is between 0.22 ± 0.03 and 0.54 ± 0.20 for the low viscous solution. Compared to the literature, a PDI below 0.7 is considered as nearly monodisperse [43]. For pH 2, 3, 9, and 10, the PDI for both solutions is similar; however, for the low viscous samples, the PDI at pH 5, 6, 7, and 8 is higher. This indicates that the BIONs around the IEP possess a higher heterogeneity in aggregate size. Additionally, this effect can be seen in the intensity distributions of all samples in Figures S2 and S3. For the water solution, heterogeneous aggregates are detected between pH 4 and 8, while the particle distributions for the higher viscosity are uniform. Particularly, for low pH values, the particles might react with the acid and therefore possess a higher stability.
The analysis of BIONs in other sugar solutions, such as fructose and glucose, at pH 7 resulted in similar particle distributions as sucrose (Figure S4). In the literature, the effect on the colloidal stability of particles due to higher viscosity by sugars, such as sucrose, is confirmed. Previously, Szalai et al. synthesized ex situ coated magnetite nanoparticles with gelatin and sucrose. They reported higher colloidal stability of their particles when adding sucrose [44]. Sun et al. propose that the multiple hydroxyl groups, as they are present in sucrose, can adsorb or chelate onto the magnetite surface, resulting in steric hindrance, as it is known to conventional surfactants [45,46]. Benítez et al. describe another effect of sugars, where they claim that sucrose might influence particles’ colloidal stability because of the hydration capacity. They extend the DLVO theory by the hydration repulsive energy, which occurs as water molecules around the particle surface restrict them in their motion, known as hydration pressure [47,48]. We assume that stabilization due to the higher viscosity with sucrose is reached because of a synergy of the mentioned effects.

2.3. Dependence of the Magnetophoretic Velocity on Aggregate Size and Viscosity

The effect of pH and viscosity on the aggregation behavior of our BIONs indicates that it is essential to evaluate the influence of different aggregate sizes regarding a magnetophoresis-based separation process. The Space-and-Time-resolved Extinction Profiles (STEP) technology is based on the sedimentation of particles due to magnetophoresis. It describes the particles’ movement towards the magnetic field direction if the buoyancy and friction force is overcome (Figure 3).
Figure 4 presents the magnetophoretic velocity derived from STEPs over pH 4, 6, 7, and 9 at η = 0.888 and η = 2.227 mPa s. For pH 4 and 9, the magnetophoretic velocity is noticeably lower than for pH 6 and 7, which goes in line with the measured particle size distributions via dynamic light scattering (DLS) measurement (Figure 5). The latter pH values show around one power of ten higher diameters than pH 4 and 9 because the surface of the BIONs is charged positively or negatively, respectively. Hence, the attractive forces major the repulsive ones so that the particles do not resist aggregation. The same pattern can be observed for the high viscous samples. Here, at pH 6, which is almost the IEP of the BIONs, aggregates with a hydrodynamic diameter of 2764 ± 446 nm show a higher magnetophoretic velocity in contrast to other pH values where the hydrodynamic diameter is smaller (Figure 5b). Here, for pH 4, 7, and 9, a second mode with larger aggregates is detected, which is not visible in the intensity distributions (Figure S2). Even if the amount of these larger aggregates is lower compared to the first mode, they might influence the measured magnetophoretic velocity. The velocity differences are lower compared to the less viscous samples. Following Equation (7), the particle radius is directly proportional to the magnetophoretic force during the sedimentation process. Therefore, the measured velocities are in line with the theoretical assumptions.
Besides the aggregate size, viscosity is another parameter that influences the separation process. The magnetophoretic velocities of all measured pH values are lower for the higher viscosity (η = 2.227 mPa s) compared to the lower one (η = 0.888 mPa s), as the viscosity is indirectly proportional to the velocity, as written in Equation (10). Due to the higher viscosity, the drag force increases and slows down the particle motion along the magnetic field gradient. The gravitational force does not influence this effect, as values for the sedimentation velocity show very low values for both viscosities (Table 1). Here, the sedimentation velocity is similar when having the same size of aggregates at different pH values only in a gravitational field.
Taking these findings together, the viscosity influences the colloidal stability of the particles and the magnetophoresis process itself. These effects should be taken into account when working with high viscous liquids, such as cell lysates or blood, in order to obtain a distinct separation process.
Regarding a LGMS process, the particle size poses an essential factor in the kinetics of the separation and the resulting process efficiency. As mentioned above, mainly the cooperative effect of magnetic aggregation speeds up the magnetophoretic motion of the particles [49]. Here, the Bjerrum length can be used in order to evaluate the formation of aggregates in a magnetic field [9,50]. Therefore, we calculate the ratio of the Bjerrum length λB and the particle diameter d (Figure 6). As seen in Figure 6, particles do not form aggregates in a magnetic field if λB d−1 < 1 with a saturation magnetization of 70.84 Am2 kg−1 [49]. For our BIONs with a particle diameter of 9.92 nm, the ratio is 1.12, which implies magnetic aggregate formation. This value, measured by TEM, is close to one; however, this is the minimal limit, as the particle diameter in suspension is >100 nm, depending on the buffer conditions. Hence, the magnetophoretic velocity might be additionally influenced by this effect, but from a practical process view, cooperative magnetophoresis might be beneficial to implement such an LGMS process because the separation efficiency increases.
Besides the cooperative magnetophoresis, Leong et al. recently discussed the effect of convective magnetophoresis [33,41]. They introduce the dimensionless Grashof number Grm (Equation (3)), which is dependent on the magnetic field gradient B, the volumetric magnetization M, the particle concentration difference between the bulk solution, the collection plane cs − c and the length of the analyzed system Lc.
Gr m = ρ · B · ( M c ) H · ( c s c ) · L c 3 η 2
It describes the convection induced by an external magnetic field, which happens due to the rapid acceleration of the particles. Leong et al. state that the Grashof number is mostly dependent on the concentration, resulting in a higher magnetophoretic velocity for higher particle concentrations. However, in our study, all parameters are kept constant besides the viscosity. Its square is indirectly proportional to the dimensionless number, so one can say that an increase in viscosity lowers the convection and therefore, the magnetophoretic velocity as well.
In addition to both discussed effects, the cooperative and the convective magnetophoresis, the diffusion, described by the Stokes–Einstein Equation, is influenced by viscosity as shown in Equation (4) [51]:
D o = k B · T 6 · π · r · η
According to Equation (4), the diffusion coefficient is decreasing with a higher viscosity and thus, Brownian motion is lower as well. Hence, it evolves that viscosity noticeably influences various parameters during a magnetophoresis-based process and should be always considered.
To sum up, the colloidal stability of BIONs is controllable due to a change in pH value, but also a higher viscosity leads to stabilization. The former is based on electrostatic stabilization effects, whereas the various latter effects, such as a steric hindrance and/or hydration repulsion due to sucrose, might be involved. The different aggregate sizes and the viscosity influences the magnetophoresis process (Equations (5)–(10)). Particularly, for a separation process with high viscous liquids, the efficiency is lower [26]. Moreover, depending on the aggregate size, MNP–MNP interactions, as cooperative or convective magnetophoresis and Brownian motion, have to be considered, as these effects influence magnetophoretic processes, e.g., a microfluidic fractionation.

3. Materials and Methods

Coprecipitation of Fe2+/3+ ions was used to synthesize the BIONs [38]. For this, 28.9 g of sodium hydroxide (722 mmol, 4.10 equivalents (eq.), Carl Roth GmbH + Co. KG, Karlsruhe, Germany) was dissolved in 400 mL of degassed water under a nitrogen atmosphere. A solution, containing 86.6 g of FeCl3·6H2O (320 mmol, 1.82 eq., Sigma Aldrich Merck KGaA, Darmstadt, Germany) and 35.0 g of FeCl2·4H2O (176 mmol, 1.0 eq., Sigma Aldrich Merck KGaA, Darmstadt, Germany) in 160 mL of degassed water, was added slowly under continuous stirring. The temperature was kept constant at 27 °C via a water bath. A black precipitate built up immediately, and the reaction was continued under stable conditions for a further 30 min. Then, the precipitate was washed ~15 times with deionized water via magnetic decantation with a neodymium iron boron magnet in a glass bottle until the conductivity was below 200 µS cm−1. The BIONs were stored under a nitrogen atmosphere at 4 °C. The magnetic susceptibility was analyzed by the SQUID device Quantum Design MPMS XL-7 (Quantum Design GmbH, Darmstadt, Germany). Therefore, the particles were lyophilized, and then they were glued into a small tube. TEM was performed with the JEM 1400 Plus microscope (JEOL GmbH, Freising, Germany), and the recorded images were subsequently evaluated by using ImageJ software.
All experiments were performed either in water (η = 0.888 mPa s, 25 °C) or in a 24% (w/w) sucrose solution (η = 2.227 mPa s, 25 °C, Carl Roth GmbH + Co. KG, Karlsruhe, Germany), fructose solution (η = 1.9858 mPa s, Carl Roth GmbH + Co. KG), or glucose solution (η = 2.1201 mPa s, AppliChem GmbH, Darmstadt, Germany). The pH was adjusted by adding 0.1 M or 1 M sodium hydroxide (Carl Roth GmbH + Co. KG, Karlsruhe, Germany) or hydrochloric acid (VWR International GmbH, Darmstadt, Germany). A solution of 1 g L−1 BIONs was used, dispersed via an ultrasonication probe (5 min, 10 s on, 15 s off, 20%, Branson Ultrasonics Corporation, Danbury, United States of America). For zeta potential and hydrodynamic diameter by DLS evaluation, a ZetaSizer XS (Malvern Panalytical GmbH, Kassel, Germany) was used. Both measurements were performed at 25 °C in 1 mL of a 1 g L−1 solution in five and three measuring cycles in duplicates, respectively. The IEP was determined by applying a Boltzmann fit.
STEPs were recorded in duplicates at an optical wavelength of 870 nm (LUMiReader, LUM GmbH, Berlin, Germany) to calculate the magnetophoretic velocity. According to Newton’s second law of motion, magnetophoresis is composed of the gravitational force Fgrav, the magnetic force Fmag and the viscous drag force Fdrag, pointing in the opposite direction of the former two forces.
m p du dt = F grav + F mag + F drag
Here, mp and u are the mass and the velocity of the particle, respectively. For simplicity, the inertial term can be neglected [49,52].
0 = F grav + F mag + F drag
The magnetic force is determined by the magnetic field gradient H, the permeabilities µ0 and µr, the relative permittivity K, and the particle radius r:
F mag = 3 · µ 0 · µ r · K · H 2 · 2 · π · r 3
According to Stokes’ law, the movement of a spherical particle in an incompressible fluid can be described as follows, where η corresponds to the fluid viscosity:
F drag = 6 · u · π · η · r
The gravitational force is based on Newton’s law of gravitation,
F grav = 4 3 ( ρ p ρ f ) · g · π · r 3 ,
which is dependent on the density difference of particle and fluid ρp − ρf and the free-fall acceleration g. The force balance, as written in Equations (6)–(9), can be solved for the velocity as written in Equation (10):
v = 2 · ( ρ p ρ f ) · g · r 2 9 · η + µ 0 · µ r · K · H 2 · r 2 2 · η
For the measurement, a disposable cuvette (1 × 1 × 4.4 cm) filled with 1 mL of solution was placed onto a stack of five cylindrical neodymium boron ferrite (NdFeB) magnets (diameter = 12 mm, height = 2 mm, N45, Webcraft GmbH, Gottmadingen, Germany). The built-in temperature control assured a constant temperature of 25 °C. The magnetic flux density was measured with a Hall detector PCE-MF M 3000 (PCE Instruments UK Limited, Southampton Hampshire, United Kingdom). The obtained transmittance profiles were integrated over the sample height, leading to an integral transmittance for each measurement time. For data evaluation, it was converted into an integral extinction value, which is directly proportional to the particle concentration after Lambert–Beer’s law. Particle movement due to the magnetic and gravitational force induces the change in particle concentration. Therefore, the time-dependent variation of the extinction enables calculating the magnetophoretic velocity vmag, where L is the mean length defined by half of the sample height.
v = < L > t
A cumulative distribution function ϕ (vmag) is obtained by plotting the relative extinction over the magnetophoretic velocity [53]. The relative extinction Erel is determined by the initial extinction of the sample E0 and the minimal extinction Emin at the end of magnetophoresis measurement.
E rel ( t ) = E     E min E 0     E min ,  
For better comparability, the value at t0.5 was used, which is the distribution function’s median. It describes the velocity of 50% of the particles at the time t0.5, where the extinction has fallen by half. The sedimentation analysis experiments were performed with a magnetic flux density between 40 and 350 mT, which corresponds to a magnetization between 29.31 and 54.40 Am2 kg−1.

4. Conclusions

BIONs with an average diameter of 9.2 nm were synthesized via coprecipitation, showing a high saturation magnetization [38]. Zeta potential and hydrodynamic diameter measurements showed that pH and viscosity influence the colloidal stability of the particles. pH values close to the IEP resulted in large particle agglomerates; however, electrostatic stabilization was observed for high and low pH values. The particle distribution over different pHs narrowed due to the increase in viscosity with sucrose. This could be explained by the hydration repulsion and the steric stabilization effect of sucrose. The aggregate size and viscosity directly influence a magnetophoretic process. The particle diameter is proportional to the magnetophoretic velocity, which results in high velocities for large aggregates and lower velocities for small particle diameters. By increasing the viscosity, the drag force counteracts the magnetophoretic force and decreases the magnetophoretic velocity of all aggregate sizes. This study emphasizes the underestimated effect of viscosity by using the simple method of sedimentation analysis, in addition to zeta potential and DLS measurement. In downstream processing or medical applications, liquids such as cell suspension or blood will affect particle migration, resulting in a lower separation. Particularly, the stabilizing effect of sucrose should be further examined, as the formation of aggregates is one of the main reasons for using different coatings for the steric stabilization of the BIONs [54]. In further studies, these new findings can be used to control the aggregation behavior for applications in medicine or biotechnology.

Supplementary Materials

The following are available online at https://www.mdpi.com/article/10.3390/magnetochemistry7060080/s1, Figure S1: Polydispersity Index of BION suspension from pH 2 to 10 in deionized water (η = 0.888 mPa s) and sucrose solution (η = 2.227 mPa s), Figure S2: Intensity distribution data of pH 2 to 10 for high viscous BION suspension. Technical triplicates are shown for each duplicate, Figure S3: Intensity distribution data of pH 2 to 10 for low viscous BION suspension. Technical triplicates are shown for each duplicate, Figure S4: Number distribution of BIONs in fructose, glucose, and sucrose solution at pH 7.

Author Contributions

Conceptualization, L.W. and S.P.S.; methodology, L.W. and C.T.; software, L.W.; validation, L.W.; formal analysis, L.W., C.T.; investigation, L.W.; resources, S.P.S.; data curation, L.W.; writing—original draft preparation, L.W.; writing—review and editing, L.W. and S.P.S.; visualization, L.W.; supervision, S.P.S., project administration, S.P.S.; funding acquisition, S.P.S. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the German Research Foundation (DFG) (Project Number: 441672360). We appreciate the support from the German Research Foundation (DFG) and the Technical University of Munich (TUM) in the framework of the Open-Access Publishing Program and the support by TUM International Graduate School of Science and Engineering (IGSSE).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The original data related to this research can be asked any time to the corresponding author’s email: [email protected].

Acknowledgments

We would like to thank Sonja Berensmeier for laboratory resources and valuable discussions. In addition, we acknowledge Matthias Opel for the SQUID measurement and Carsten Peters for support with TEM imaging.

Conflicts of Interest

The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.

References

  1. Fraga-García, P.; Kubbutat, P.; Brammen, M.; Schwaminger, S.; Berensmeier, S. Bare Iron Oxide Nanoparticles for Magnetic Harvesting of Microalgae: From Interaction Behavior to Process Realization. Nanomaterials 2018, 8, 292. [Google Scholar] [CrossRef] [Green Version]
  2. Schnell, F.; Kube, M.; Berensmeier, S.; Schwaminger, S.P. Magnetic Recovery of Cellulase from Cellulose Substrates with Bare Iron Oxide Nanoparticles. ChemNanoMat 2019, 5, 422–426. [Google Scholar] [CrossRef]
  3. Zhang, H.; Ding, W.; Li, S.; Ya, S.; Li, F.; Qiu, B. On-chip analysis of magnetically labeled cells with integrated cell sorting and counting techniques. Talanta 2020, 220, 121351. [Google Scholar] [CrossRef]
  4. Puddu, M.; Paunescu, D.; Stark, W.J.; Grass, R.N. Magnetically Recoverable, Thermostable, Hydrophobic DNA/Silica Encapsulates and Their Application as Invisible Oil Tags. ACS Nano 2014, 8, 2677–2685. [Google Scholar] [CrossRef]
  5. Ling, W.; Wang, M.; Xiong, C.; Xie, D.; Chen, Q.; Chu, X.; Qiu, X.; Li, Y.; Xiao, X. Synthesis, surface modification, and applications of magnetic iron oxide nanoparticles. J. Mater. Res. 2019, 34, 1828–1844. [Google Scholar] [CrossRef]
  6. Liu, S.; Yu, B.; Wang, S.; Shen, Y.; Cong, H. Preparation, surface functionalization and application of Fe3O4 magnetic nanoparticles. Adv. Colloid Interface Sci. 2020, 281, 102165. [Google Scholar] [CrossRef]
  7. Kodama, R. Magnetic nanoparticles. Magnetochemistry 2020, 6. [Google Scholar] [CrossRef]
  8. Massart, R. Preparation of aqueous magnetic liquids in alkaline and acidic media. IEEE Trans. Magn. 1981, 17, 1247–1248. [Google Scholar] [CrossRef]
  9. Leong, S.S.; Yeap, S.P.; Lim, J. Working principle and application of magnetic separation for biomedical diagnostic at high- and low-field gradients. Interface Focus 2016, 6, 20160048. [Google Scholar] [CrossRef] [Green Version]
  10. Lozar, T.; Jesenko, T.; Prevodnik, V.K.; Cemazar, M.; Hosta, V.; Jericevic, A.; Nolde, N.; Kuhar, C.G. Preclinical and Clinical Evaluation of Magnetic-Activated Cell Separation Technology for CTC Isolation in Breast Cancer. Front. Oncol. 2020, 10, 1–10. [Google Scholar] [CrossRef]
  11. Miltenyi, S.; Müller, W.; Weichel, W.; Radbruch, A. High gradient magnetic cell separation with MACS. Cytometry 1990, 11, 231–238. [Google Scholar] [CrossRef]
  12. Fratzl, M.; Delshadi, S.; Devillers, T.; Bruckert, F.; Cugat, O.; Dempsey, N.M.; Blaire, G. Magnetophoretic induced convective capture of highly diffusive superparamagnetic nanoparticles. Soft Matter 2018, 14, 2671–2681. [Google Scholar] [CrossRef]
  13. Corchero, J.L.; Villaverde, A. Biomedical applications of distally controlled magnetic nanoparticles. Trends Biotechnol. 2009, 27, 468–476. [Google Scholar] [CrossRef] [PubMed]
  14. Toh, P.Y.; Yeap, S.P.; Kong, L.P.; Ng, B.W.; Chan, D.J.C.; Ahmad, A.L.; Lim, J.K. Magnetophoretic removal of microalgae from fishpond water: Feasibility of high gradient and low gradient magnetic separation. Chem. Eng. J. 2012, 211-212, 22–30. [Google Scholar] [CrossRef]
  15. Alnaimat, F.; Karam, S.; Mathew, B.; Mathew, B. Magnetophoresis and Microfluidics: A Great Union. IEEE Nanotechnol. Mag. 2020, 14, 24–41. [Google Scholar] [CrossRef]
  16. Robert, D.; Pamme, N.; Conjeaud, H.; Gazeau, F.; Iles, A.; Wilhelm, C. Cell sorting by endocytotic capacity in a microfluidic magnetophoresis device. Lab. Chip 2011, 11, 1902–1910. [Google Scholar] [CrossRef] [PubMed]
  17. Kievit, F.M.; Zhang, M. Surface Engineering of Iron Oxide Nanoparticles for Targeted Cancer Therapy. Acc. Chem. Res. 2011, 44, 853–862. [Google Scholar] [CrossRef] [Green Version]
  18. Socoliuc, V.; Peddis, D.; Petrenko, V.I.; Avdeev, M.V.; Susan-Resiga, D.; Szabó, T.; Turcu, R.; Tombácz, E.; Vékás, L. Magnetic Nanoparticle Systems for Nanomedicine—A Materials Science Perspective. Magnetochemistry 2020, 6, 2. [Google Scholar] [CrossRef] [Green Version]
  19. Dulińska-Litewka, J.; Łazarczyk, A.; Hałubiec, P.; Szafrański, O.; Karnas, K.; Karewicz, A. Superparamagnetic Iron Oxide Nanoparticles—Current and Prospective Medical Applications. Materials 2019, 12, 617. [Google Scholar] [CrossRef] [Green Version]
  20. Ansari, S.A.M.K.; Ficiarà, E.; Ruffinatti, F.A.; Stura, I.; Argenziano, M.; Abollino, O.; Cavalli, R.; Guiot, C.; D’Agata, F. Magnetic Iron Oxide Nanoparticles: Synthesis, Characterization and Functionalization for Biomedical Applications in the Central Nervous System. Materials 2019, 12, 465. [Google Scholar] [CrossRef] [Green Version]
  21. Vangijzegem, T.; Stanicki, D.; Laurent, S. Magnetic iron oxide nanoparticles for drug delivery: Applications and characteristics. Expert Opin. Drug Deliv. 2019, 16, 69–78. [Google Scholar] [CrossRef]
  22. Soetaert, F.; Korangath, P.; Serantes, D.; Fiering, S.; Ivkov, R. Cancer therapy with iron oxide nanoparticles: Agents of thermal and immune therapies. Adv. Drug Deliv. Rev. 2020, 163-164, 65–83. [Google Scholar] [CrossRef] [PubMed]
  23. Belanova, A.A.; Gavalas, N.; Makarenko, Y.M.; Belousova, M.M.; Soldatov, A.V.; Zolotukhin, P.V. Physicochemical Properties of Magnetic Nanoparticles: Implications for Biomedical Applications In Vitro and In Vivo. Oncol. Res. Treat. 2018, 41, 139–143. [Google Scholar] [CrossRef]
  24. Nam, J.; Huang, H.; Lim, H.; Lim, C.; Shin, S. Magnetic Separation of Malaria-Infected Red Blood Cells in Various Developmental Stages. Anal. Chem. 2013, 85, 7316–7323. [Google Scholar] [CrossRef] [PubMed]
  25. Pamme, N.; Wilhelm, C. Continuous sorting of magnetic cells via on-chip free-flow magnetophoresis. Lab. Chip 2006, 6, 974–980. [Google Scholar] [CrossRef] [PubMed]
  26. Roth, H.-C.; Prams, A.; Lutz, M.; Ritscher, J.; Raab, M.; Berensmeier, S. A high-gradient magnetic separator for highly viscous process liquors in industrial biotechnology. Chem. Eng. Technol. 2016, 39, 469–476. [Google Scholar] [CrossRef]
  27. Mishima, F.; Hayashi, S.; Akiyama, Y.; Nishijima, S. Development of a Superconducting High Gradient Magnetic Separator for a Highly Viscous Fluid. IEEE Trans. Appl. Supercond. 2011, 22, 3700204. [Google Scholar] [CrossRef]
  28. Gupta, A.K.; Gupta, M. Synthesis and surface engineering of iron oxide nanoparticles for biomedical applications. Biomaterials 2005, 26, 3995–4021. [Google Scholar] [CrossRef]
  29. Coppola, L.; Caserta, F.; De Lucia, D.; Guastafierro, S.; Grassia, A.; Coppola, A.; Marfella, R.; Varricchio, M. Blood viscosity and aging. Arch. Gerontol. Geriatr. 2000, 31, 35–42. [Google Scholar] [CrossRef]
  30. Alphandéry, E. Bio-synthesized iron oxide nanoparticles for cancer treatment. Int. J. Pharm. 2020, 586, 119472. [Google Scholar] [CrossRef]
  31. Solsona, M.; Nieuwelink, A.-E.; Meirer, F.; Abelmann, L.; Odijk, M.; Olthuis, W.; Weckhuysen, B.M.; Berg, A.V.D. Magnetophoretic Sorting of Single Catalyst Particles. Angew. Chem. Int. Ed. 2018, 57, 10589–10594. [Google Scholar] [CrossRef] [PubMed]
  32. Faraudo, J.; Andreu, J.S.; Calero, C.; Camacho, J. Predicting the Self-Assembly of Superparamagnetic Colloids under Magnetic Fields. Adv. Funct. Mater. 2016, 26, 3837–3858. [Google Scholar] [CrossRef]
  33. Leong, S.S.; Ahmad, Z.; Low, S.C.; Camacho, J.; Faraudo, J.; Lim, J. Unified View of Magnetic Nanoparticle Separation under Magnetophoresis. Langmuir 2020, 36, 8033–8055. [Google Scholar] [CrossRef]
  34. Yavuz, C.T.; Mayo, J.T.; Yu, W.W.; Prakash, A.; Falkner, J.C.; Yean, S.; Cong, L.; Shipley, H.J.; Kan, A.; Tomson, M.; et al. Low-Field Magnetic Separation of Monodisperse Fe3O4 Nanocrystals. Science 2006, 314, 964–967. [Google Scholar] [CrossRef]
  35. Faraudo, J.; Camacho, J. Cooperative magnetophoresis of superparamagnetic colloids: Theoretical aspects. Colloid Polym. Sci. 2009, 288, 207–215. [Google Scholar] [CrossRef]
  36. Schwaminger, S.P.; Fraga-García, P.; Selbach, F.; Hein, F.G.; Fuß, E.C.; Surya, R.; Roth, H.-C.; Blank-Shim, S.A.; Wagner, F.E.; Heissler, S.; et al. Bio-nano interactions: Cellulase on iron oxide nanoparticle surfaces. Adsorption 2016, 23, 281–292. [Google Scholar] [CrossRef]
  37. Bean, C.P.; Livingston, J.D. Superparamagnetism. J. Appl. Phys. 1959, 30, S120–S129. [Google Scholar] [CrossRef]
  38. Turrina, C.; Berensmeier, S.; Schwaminger, S. Bare Iron Oxide Nanoparticles as Drug Delivery Carrier for the Short Cationic Peptide Lasioglossin. Pharmaceuticals 2021, 14, 405. [Google Scholar] [CrossRef]
  39. Schwaminger, S.; Syhr, C.; Berensmeier, S. Controlled Synthesis of Magnetic Iron Oxide Nanoparticles: Magnetite or Maghemite? Crystals 2020, 10, 214. [Google Scholar] [CrossRef] [Green Version]
  40. Schwaminger, S.P.; Bauer, D.; Fraga-García, P.; Wagner, F.E.; Berensmeier, S. Oxidation of magnetite nanoparticles: Impact on surface and crystal properties. CrystEngComm 2016, 19, 246–255. [Google Scholar] [CrossRef] [Green Version]
  41. Schwaminger, S.P.; Schwarzenberger, K.; Gatzemeier, J.; Lei, Z.; Eckert, K. Magnetically Induced Aggregation of Iron Oxide Nanoparticles for Carrier Flotation Strategies. ACS Appl. Mater. Interfaces 2021, 13, 20830–20844. [Google Scholar] [CrossRef] [PubMed]
  42. Schwaminger, S.P.; Blank-Shim, S.A.; Scheifele, I.; Fraga-García, P.; Berensmeier, S. Peptide binding to metal oxide nanoparticles. Faraday Discuss. 2017, 204, 233–250. [Google Scholar] [CrossRef] [PubMed]
  43. Stetefeld, J.; McKenna, S.; Patel, T.R. Dynamic light scattering: A practical guide and applications in biomedical sciences. Biophys. Rev. 2016, 8, 409–427. [Google Scholar] [CrossRef] [PubMed]
  44. Szalai, A.J.; Manivannan, N.; Kaptay, G. Super-paramagnetic magnetite nanoparticles obtained by different synthesis and separation methods stabilized by biocompatible coatings. Colloids Surfaces A Physicochem. Eng. Asp. 2019, 568, 113–122. [Google Scholar] [CrossRef]
  45. Sun, X.; Zheng, C.; Zhang, F.; Yang, Y.; Wu, G.; Yu, A.; Guan, N. Size-Controlled Synthesis of Magnetite (Fe3O4) Nanoparticles Coated with Glucose and Gluconic Acid from a Single Fe(III) Precursor by a Sucrose Bifunctional Hydrothermal Method. J. Phys. Chem. C 2009, 113, 16002–16008. [Google Scholar] [CrossRef]
  46. Cushing, B.L.; Kolesnichenko, V.; O’Connor, C.J. Recent Advances in the Liquid-Phase Syntheses of Inorganic Nanoparticles. Chem. Rev. 2004, 104, 3893–3946. [Google Scholar] [CrossRef] [PubMed]
  47. Benítez, E.I.; Genovese, D.B.; Lozano, J.E. Effect of typical sugars on the viscosity and colloidal stability of apple juice. Food Hydrocoll. 2009, 23, 519–525. [Google Scholar] [CrossRef]
  48. Chalikian, T.V. Ultrasonic and Densimetric Characterizations of the Hydration Properties of Polar Groups in Monosaccharides. J. Phys. Chem. B 1998, 102, 6921–6926. [Google Scholar] [CrossRef]
  49. Leong, S.S.; Ahmad, Z.; Lim, J. Magnetophoresis of superparamagnetic nanoparticles at low field gradient: Hydrodynamic effect. Soft Matter 2015, 11, 6968–6980. [Google Scholar] [CrossRef]
  50. Cuevas, G.D.L.; Faraudo, J.; Camacho, J. Low-Gradient Magnetophoresis through Field-Induced Reversible Aggregation. J. Phys. Chem. C 2008, 112, 945–950. [Google Scholar] [CrossRef]
  51. Einstein, A. Über die von der molekularkinetischen Theorie der Wärme geforderte Bewegung von in ruhenden Flüssigkeiten suspendierten Teilchen. Ann. Phys. 1905, 322, 549–560. [Google Scholar] [CrossRef] [Green Version]
  52. Furlani, E.P. Analysis of particle transport in a magnetophoretic microsystem. J. Appl. Phys. 2006, 99, 024912. [Google Scholar] [CrossRef] [Green Version]
  53. Mykhaylyk, O.; Lerche, D.; Vlaskou, D.; Schoemig, V.; Detloff, T.; Krause, D.; Wolff, M.; Joas, T.; Berensmeier, S.; Plank, C.; et al. Biomagnetic Particles Magnetophoretic Velocity Determined by Space- and Time-Resolved Extinction Profiles. IEEE Magn. Lett. 2015, 6, 1–4. [Google Scholar] [CrossRef]
  54. Laurent, S.; Forge, D.; Port, M.; Roch, A.; Robic, C.; Elst, L.V.; Muller, R.N. Erratum: Magnetic Iron Oxide Nanoparticles: Synthesis, Stabilization, Vectorization, Physicochemical Characterizations, and Biological Applications. Chem. Rev. 2008, 110, 2574. [Google Scholar] [CrossRef]
Figure 1. (a) Superconducting quantum interference (SQUID) measurement for the bare iron oxide nanoparticles (BIONs) at 300 K with a LangevinMod fit. (b) Transmission Electron Microscopy (TEM) image of the BIONs.
Figure 1. (a) Superconducting quantum interference (SQUID) measurement for the bare iron oxide nanoparticles (BIONs) at 300 K with a LangevinMod fit. (b) Transmission Electron Microscopy (TEM) image of the BIONs.
Magnetochemistry 07 00080 g001
Figure 2. Hydrodynamic diameter and zeta potential measurements of BION suspension in pH 2 to 10 (a) in deionized water (η = 0.888 mPa s) (b) and sucrose solution (η = 2.227 mPa s).
Figure 2. Hydrodynamic diameter and zeta potential measurements of BION suspension in pH 2 to 10 (a) in deionized water (η = 0.888 mPa s) (b) and sucrose solution (η = 2.227 mPa s).
Magnetochemistry 07 00080 g002
Figure 3. (a) Schematic illustration of the sedimentation analyzer (LUMiReader) with the involved forces (magnetic force Fmag, the gravitational force Fgrav, and the drag force Fdrag). (b) Experimental set-up. The cuvette filled with sample fluid is placed on a magnet, and parallel light with a wavelength of 870 nm transmits the sample. A light sensor records transmission profiles, and the magnetophoretic velocity of the particles is calculated. The magnetic flux density in the direction of the particle movement is 40 mT at the sample top and 350 mT at the sample bottom. (c) Calculated magnetic flux density along the y-axis. Calculations were performed with COMSOL Multiphysics 5.6.
Figure 3. (a) Schematic illustration of the sedimentation analyzer (LUMiReader) with the involved forces (magnetic force Fmag, the gravitational force Fgrav, and the drag force Fdrag). (b) Experimental set-up. The cuvette filled with sample fluid is placed on a magnet, and parallel light with a wavelength of 870 nm transmits the sample. A light sensor records transmission profiles, and the magnetophoretic velocity of the particles is calculated. The magnetic flux density in the direction of the particle movement is 40 mT at the sample top and 350 mT at the sample bottom. (c) Calculated magnetic flux density along the y-axis. Calculations were performed with COMSOL Multiphysics 5.6.
Magnetochemistry 07 00080 g003
Figure 4. Magnetophoretic velocity over pH 4, 6, 7, and 9 of BION suspension in deionized water (η = 0.888 mPa s) and sucrose solution (η = 2.227 mPa s) with a corresponding mean diameter of DLS measurement.
Figure 4. Magnetophoretic velocity over pH 4, 6, 7, and 9 of BION suspension in deionized water (η = 0.888 mPa s) and sucrose solution (η = 2.227 mPa s) with a corresponding mean diameter of DLS measurement.
Magnetochemistry 07 00080 g004
Figure 5. Particle size distribution at pH 4, 6, 7, and 9 of BION suspension (a) in deionized water (η = 0.888 mPa s) (b) and sucrose solution (η = 2.227 mPa s).
Figure 5. Particle size distribution at pH 4, 6, 7, and 9 of BION suspension (a) in deionized water (η = 0.888 mPa s) (b) and sucrose solution (η = 2.227 mPa s).
Magnetochemistry 07 00080 g005
Figure 6. Log–log plot of the ratio of the Bjerrum length and the particle diameter over the particle diameter. The shaded region corresponds to particle diameters where no aggregation due to a magnetic field occurs, and the solid line describes the Bjerrum length for particles with the same magnetization. The symbol represents our particle size and indicates that magnetic aggregation takes place (transparent region).
Figure 6. Log–log plot of the ratio of the Bjerrum length and the particle diameter over the particle diameter. The shaded region corresponds to particle diameters where no aggregation due to a magnetic field occurs, and the solid line describes the Bjerrum length for particles with the same magnetization. The symbol represents our particle size and indicates that magnetic aggregation takes place (transparent region).
Magnetochemistry 07 00080 g006
Table 1. Measurement of the sedimentation velocity and the corresponding hydrodynamic diameter of the samples in the sedimentation analyzer.
Table 1. Measurement of the sedimentation velocity and the corresponding hydrodynamic diameter of the samples in the sedimentation analyzer.
η = 0.888 mPa sη = 2.227 mPa s
pHSedimentation Velocity (µm s−1)Hydrodynamic Diameter (nm)Sedimentation Velocity (µm s−1)Hydrodynamic Diameter (nm)
41.57 ± 0.09156 ± 1060.88 ± 0.70158 ± 108
63.82 ± 0.852986 ± 9202.30 ± 0.012764 ± 446
73.69 ± 0.142047 ± 4610.33 ± 0.28351 ± 58
91.43 ± 0.37331 ± 790.31 ± 0.06111 ± 35
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Wittmann, L.; Turrina, C.; Schwaminger, S.P. The Effect of pH and Viscosity on Magnetophoretic Separation of Iron Oxide Nanoparticles. Magnetochemistry 2021, 7, 80. https://doi.org/10.3390/magnetochemistry7060080

AMA Style

Wittmann L, Turrina C, Schwaminger SP. The Effect of pH and Viscosity on Magnetophoretic Separation of Iron Oxide Nanoparticles. Magnetochemistry. 2021; 7(6):80. https://doi.org/10.3390/magnetochemistry7060080

Chicago/Turabian Style

Wittmann, Leonie, Chiara Turrina, and Sebastian P. Schwaminger. 2021. "The Effect of pH and Viscosity on Magnetophoretic Separation of Iron Oxide Nanoparticles" Magnetochemistry 7, no. 6: 80. https://doi.org/10.3390/magnetochemistry7060080

APA Style

Wittmann, L., Turrina, C., & Schwaminger, S. P. (2021). The Effect of pH and Viscosity on Magnetophoretic Separation of Iron Oxide Nanoparticles. Magnetochemistry, 7(6), 80. https://doi.org/10.3390/magnetochemistry7060080

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.