Next Article in Journal
Impact of Operating Parameters on the Production of Nanoemulsions Using a High-Pressure Homogenizer with Flow Pattern and Back Pressure Control
Previous Article in Journal
Unique Fiber Morphologies from Emulsion Electrospinning—A Case Study of Poly(ε-caprolactone) and Its Applications
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Colloids and Interfaces
Volume 7
Issue 1
10.3390/colloids7010020
colloids-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Preparation of V2O5 Thin Film by Sol–Gel Technique and Pen Plotter Printing

by
Philipp Yu. Gorobtsov
*,
Tatiana L. Simonenko
,
Nikolay P. Simonenko
*,
Elizaveta P. Simonenko
and
Nikolay T. Kuznetsov
Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences, 31 Leninsky pr., Moscow 119991, Russia
*
Authors to whom correspondence should be addressed.
Colloids Interfaces 2023, 7(1), 20; https://doi.org/10.3390/colloids7010020
Submission received: 31 January 2023 / Revised: 5 March 2023 / Accepted: 11 March 2023 / Published: 15 March 2023
Browse Figures
Versions Notes

Abstract

:
The work is dedicated to study of thin V2O5 film formation by pen plotter printing using vanadyl alkoxyacetylacetonate as hydrolytically active precursor. Solution of the prepared vanadyl butoxyacetylacetonate complex with 87% of butoxyl groups was used as functional ink for pen plotter printing of thin V2O5 film on surface of specialized chip. According to atomic force microscopy (AFM) and scanning electron microscopy (SEM), oxide film consists of nanorods 35–75 nm in thickness and 120–285 nm in length, with crystallite size of 54 ± 4 nm. Data from Rietveld refinement of the X-ray powder diffraction results and work function value (4.54 eV) indicate high content of defects (such as oxygen vacancies) in the material. Electrophysical properties study suggests that correlated barrier hopping of the charge carriers is the main conductivity mechanism. Conductivity activation energy Ea was found to be 0.24 eV.

1. Introduction

Vanadium oxide-based thin films have recently been investigated for a variety of applications. For example, V2O5-based coatings are promising as electrochromic layers [1,2,3,4] due to their ability to change color from almost transparent yellow to dark green and dark blue when reduced, or to orange when oxidized on an anode [4,5], as well as their high capacity for lithium ion intercalation [3]. Due to the latter property, as well as high specific capacitance, cycling stability, and good kinetic characteristics upon ion intercalation, vanadium(V)-based thin films are promising cathode materials in lithium-ion batteries [6,7] and supercapacitors [8,9,10]. V2O5 thin films are also of great interest as components for solar cells and LEDs [11,12,13,14]. In addition, vanadium pentoxide coatings can demonstrate high selectivity and chemosensory response in the detection of nitrogen dioxide [15], ammonia [16] and various organic compounds [17,18,19].
At the same time, it is known that the properties of any material, including thin films, depend not only on its elemental or phase composition, but also on the preparation technique. For example, the technique and conditions of synthesis affect the microstructure of the material and amount of defects (such as oxygen vacancies) in it. Chemical precipitation [20,21], hydrothermal techniques [22,23] and various sol-gel technology modifications [24] are often used for V2O5 synthesis. Each of these has its own advantages, but the sol-gel technology from our point of view is one of the most variable both in terms of synthesis parameter control and in terms of possible combination with various techniques of thin film deposition. At the same time, the most widely encountered modifications in the literature regarding sol–gel technology for the preparation of vanadium pentoxide are the approaches utilizing vanadium acid condensation and the hydrolysis of vanadium(V) oxytriisopropoxide [24,25,26,27,28]. However, techniques based on the reaction of V2O5 with H2O2 or preparation of V2O5 sols by passing vanadate solutions through cation-exchange resins have a disadvantage of low control over the chemical process of oxide preparation. Consequently, these techniques are deprived of one of the main advantages of the classic sol-gel technology, namely, the ability to influence the microstructure of the resulting material at the initial stage of the formation of solid phase particles. The classical sol-gel approach, based on the hydrolysis of alkoxides, is much more flexible in this respect, since it allows one to control the hydrolysis and polycondensation processes by adding acidic or basic catalysts (for example, acetic acid, as in [25]), changing the composition of the hydrolytically active precursor. However, the latter approach is very rarely used to obtain V2O5, although it can, for example, eliminate such drawbacks as excessively rapid hydrolysis. In this regard, we consider it promising to use metal acetylacetonates with partial substitution of chelate ligands for alkoxy fragments as precursors for sol-gel synthesis of vanadium(V) oxide [29,30]. Besides, for practical applications of vanadium pentoxide, the content of vanadium in other oxidative states is an important factor, since it affects the properties of the resulting material. For some applications, the presence of significant amounts of vanadium(IV) is a positive factor [31,32]. Therefore, solutions containing vanadium(IV) may be promising as a precursor for preparation of V2O5, when vanadium dioxide formed at the first stage is oxidized to pentoxide after additional heat treatment in the air, preserving a certain concentration of vanadium(IV) ions.
As already mentioned, sol-gel technology is compatible with a wide range of thin film deposition techniques. For example, it is often combined with spin-coating and dip-coating [25,29]. Recently, however, more and more attention in the field of film deposition has been paid to printing technologies, such as ink-jet printing [28,33,34], microextrusion printing [35,36] or pen plotter printing [30,37,38]. These processes provide high reproducibility of the microstructural and functional characteristics of the films and simplify the production of multicomponent coatings, including those with complicated geometries. In addition to these, pen plotter printing has other advantages, such as affordability, availability of consumable materials, possibility of printing on surfaces of different texture and roughness, absence of strict requirements regarding the rheological properties of the so-called functional inks, and convenience of coating using precursor solutions for sol–gel synthesis of various nanomaterials. The pen plotter printing process can be described as follows. First, a pen, often stuffed inside with a special foamy ink absorber, is filled with functional ink. Then, the filled pen is put into a special holder on a plotter, which moves along the X and Y planes, normally without controlled movement on the Z axis, so this technique is only applicable to film preparation [39].
Thus, in this work we investigate the process of pen plotter printing of V2O5 thin films combined with sol-gel technology based on the use of hydrolytically active heteroligand complexes of the composition [VO(C5H7O2)2−x(C4H9O)x] as precursors.

2. Materials and Methods

2.1. Materials

The reagents used in the study were as follows: n-butanol (C4H9OH, 99%, Ekos-1, Moscow, Russia) for complex solution preparation, vanadyl acetylacetonate ([VO(C5H7O2)2], 98%, Sigma-Aldrich, St. Louis, MO, USA) as starting reagent for heteroligand complex preparation.

2.2. Hydrolytically Active Precursor Synthesis

Heteroligand complexes of the composition [VO(C5H7O2)2−x(C4H9O)x] were used as the vanadium oxide precursors. They were prepared by heat treatment of a solution of vanadyl acetylacetonate [VO(C5H7O2)2] in n-butanol. Heat treatment lasted 18 h, with the temperature of the oil bath (in which the flask with the solution and reflux condenser were immersed) being 140 °C. The formation of the alkoxoacetylacetonate complex was confirmed by infrared spectroscopy and UV-spectrophotometry.

2.3. Pen Plotter Printing of Oxide Films

The solution of the synthesized complex was further used as a functional ink in the application of V2O5 films by pen plotter printing. The scheme of the process is shown in Figure 1. A specialized Pt/Al2O3/Pt (further PAP) chip was used as a substrate for subsequent measurement of electrophysical properties. The chip which is an α-Al2O3 substrate (Ra = 100 nm) with platinum counter-pin electrodes on the front side and a platinum meander microheater on the back side. The solution film was applied to the front side of the chip in the area of the platinum counter-pin electrodes. The printing speed was 50 mm/min, the distance between the lines in the digital model was 100 µm. As a result, a 5-layer film was formed. After applying each layer, the sample was heat-treated in air at 200 °C for 10 min. After all layers had been applied, the sample was further heat-treated in air at 300 °C for 1 h to remove organic components and oxidize the material to V2O5. Similarly, a vanadium(V) oxide film was obtained on a glass substrate to clarify its crystal structure.

2.4. Instrumentation

An InfraLUM FT-08 infrared spectrometer (Lumex, St. Petersburg, Russia) was used to record vibrational spectra (IR spectra) of the complex solution. The spectra were recorded in the range of 350–2000 cm−1.
SF-56 spectrophotometer (OKB Spectr, St. Petersburg, Russia) was used to record UV spectra. Spectra were recorded in the wavelength range of 250–325 nm for solutions diluted to a complex concentration of 2–10−4 mol/L.
X-ray powder diffraction (XRD) of the deposited films was performed with a D8-Advance diffractometer (Bruker, Billerica, MA, USA; CuKα = 1.5418 Å, Ni filter, E = 40 keV, I = 40 mA, range 2θ 5–80°, signal accumulation time 0.3 s/point, resolution 0.02°).
The microstructure of V2O5 films was studied by scanning electron microscopy (SEM, NVision 40 dual-beam workstation, Carl Zeiss, Inc., Jena, Germany).
The printed V2O5 coatings were also examined by atomic force microscopy (AFM) on the NT-MDT Solver PRO (NT-MDT, Zelenograd, Russia). Both surface morphology and local electrophysical properties of the material were characterized. For the latter, the techniques of Kelvin Probe Force Microscopy (KPFM), Scanning Capacitive Microscopy (SCM), and Scanning Spreading Resistance Microscopy (SSRM) were used. Scanning in all techniques, except SSRM, was performed in the semicontact mode; ETALON HA_HR probes (ScanSens, Bremen, Germany) with W2C conductive coating (tip curvature radius ≤ 35 nm) were used. Within the framework of the KPFM, the value of the electron work function φoxide for the surface of the oxide film was measured. For this purpose, the surface was scanned five times with a probe with a predetermined work function φtip, then the average value of the contact potential φcpd was determined for each scan. The value of φoxide was then calculated as the difference between φtip and φcpd. The scanning with SSRMtechnique was performed in contact mode. Voltage was applied to the sample through a metal clamp in contact with the platinum electrode of the PAP substrate.
The electrical conductivity of the film printed on the surface of the Pt/Al2O3/Pt chip was measured by impedance spectroscopy in the temperature range 50–300 °C and frequency range 1 MHz–0.4 Hz using a potentiostat-galvanostat equipped with an electrochemical impedance measurement module (P-45X, Electrochemical Instruments, Chernogolovka, Russia). The chip was heated by applying voltage to the contacts of the meander microheater using a power supply (QJE, PS3003, Ningbo JiuYuan Electronic, Ningbo, China), and temperature control was performed using a Testo 868 thermal imager (Testo, Lenzkirch, Germany).

3. Results and Discussion

3.1. Precursor Synthesis and Characterization

The synthesis of [VO(C5H7O2)2−x(C4H9O)x] complexes proceeds with partial destructive substitution of chelate ligands during the heat treatment of vanadyl acetylacetonate in n-butyl alcohol according to the following reaction equation:
[VO(C5H7O2)2] + 2x C4H9OH = [VO(C5H7O2)2−x(C4H9O)x] + x CH3C(O)CH3 +
x CH3C(O)OC4H9
The progress of the synthesis carried out in this way can be monitored by spectral means, namely UV spectrophotometry and infrared spectroscopy. Thus, two absorption bands in the wavelength range of 250–320 nm are observed in the obtained UV spectra of the heteroligand complexes solution (Figure 2). The maximum of the first band is near 273 nm, and the maximum of the second is at ~308 nm. The first of these bands probably refers to the free acetylacetone, which may be present in the reaction system. The second band refers to the coordinated C5H7O2 ligand. It can be seen that the intensity of both bands significantly decreased as a result of the heat treatment, which confirms the occurance of the reaction with partial destruction of the acetylacetonate ligand (and the free acetylacetone impurity). Based on the spectral data obtained, we can quantitatively determine the degree to which the process of destructive substitution of chelate ligands proceeds by calculating the fraction of butoxy groups in the complex according to the following formula:
α = (1 − D′308/D308)·100%,
with α—fraction of butoxy groups in the complex, D’308—optical density of solution at 308 nm after heat treatment, D308—optical density of original solution at 308 nm. Taking the baseline into account, the α value after 18 h of heat treatment was about 87%. This content of alkoxyl groups in the composition of the complex should significantly increase its hydrolytic activity.
The results of IR spectroscopy (Figure 3) confirm the conclusions drawn from the analysis of the electron spectra. Thus, absorption bands with maxima at 1522 and 1560 cm−1, characteristic for vibrations of the C=O and C=C groups in the coordinated acetylacetonate ligands, observed on the spectrum of vanadyl acetylacetonate, are absent on the spectrum of the complex solution after its heat treatment. At the same time, an absorption band appears with two maxima (at 1743 and 1720 cm−1) related to vibrations of the carboxyl group C=O in the products of chelate ligand destruction (acetone and butyl acetate). There are also a few other differences between two spectra, such as slight change in the shape of absorption bands situated in the regions of ~1300–1500 cm−1, 900–1100 cm−1, and also varying intensity of the bands in these regions. Slight changes in shape can be attributed to the changes in complex geometry and structure due to chelate ligand substitution with butoxyl species, while intensity in these regions might be different due to a slightly different size of aliquot taken for IR spectroscopy.

3.2. V2O5 Thin Film Crystal Structure

X-ray powder diffraction analysis (XRD) was used to study the crystal structure of the oxide film obtained as a result of heat treatment (Figure 4). As can be seen from the diffractogram for the oxide film deposited on a glass substrate, the reflexes present agree well with the ICSD card #41030 for orthorhombic V2O5 and confirm that the chosen regime of heat treatment of the material leads to its crystallization and oxidation into vanadium pentaoxide. A full-profile analysis of this diffractogram was also performed, resulting in the calculation of the average size of crystallites and lattice parameters. Thus, the average crystallite size in this case was 54 ± 4 nm, and the lattice parameters have the following values: a = 11.502(3) Å, b = 3.559(1) Å, c = 4.388(2) Å, the cell volume was 179.61 Å3. When comparing the results with the literature data (a = 11.512 Å, b = 3.564 Å, c = 4.368 Å) [40,41], it can be noticed that in our case the cell is somewhat compressed by parameters a and b and expanded by parameter c. Due to the fact that the average crystallite size reaches a relatively large value, the degree of crystallinity of the material is quite high, respectively, the differences in the cell parameters are probably not due to the incomplete crystallization process. Consequently, they can be explained by the peculiarities of the structure and composition of the oxide, i.e., the presence of defects. It can be assumed that the obtained material has an increased concentration of oxygen vacancies, which leads to a decrease in parameters a and b. The increase in the parameter c is also presumably due to the high content of oxygen vacancies: the parameter c is related to the distance between the layers in the crystal structure of the oxide, and the layers are linked by the interaction between the oxygen at the top of the pyramidal structure surrounding the vanadium in one layer and vanadium from the neighboring layer [42].

3.3. Oxide Film Microstructure

SEM study of the microstructure of the oxide film on the PAP surface showed (Figure 5) that the film, although not completely covering the substrate area (which can be seen from presence of bare alumina grains of ~1 μm size), is continuous and formed by well-defined, elongated nanorods. Furthermore, some V2O5 particles are combined into agglomerates, fused by their lateral facets. Agglomeration and fusion of the nanorods is most likely caused by the heat treatment at 300 °C. The average length of the rods is 259 ± 25 nm and the width is 68 ± 6 nm. Comparison of the particle size observed by SEM with the average crystallite size determined by XRD suggests that the oxide nanorods are mostly composed of several crystallites.
The SEM data for the oxide film are basically confirmed by the AFM results (Figure 6). The topographic image of the oxide film surface (Figure 6a) and the phase contrast scan results (Figure 6b) also demonstrate that the material consists of nanorods 130 ± 13 nm long and 39 ± 3 nm wide (measurements based on phase contrast images), with thickness (from topography scans) of 23 ± 5 nm. Also, the AFM results show that the surface roughness of the oxide film has a smaller value (in the area of 342 μm2 the Ra value is 68 ± 6 nm) compared to the pure Al2O3 substrate (Ra = 100 ± 5 nm). Mapping of the surface potential distribution during KPFM (Figure 6c) showed that the film, despite its relatively low density, has a sufficiently high conductivity: the potential value is evenly distributed across the film surface (the maximum difference in the surface potential is ~15 mV). It can also be noted that a higher value of the contact potential difference corresponds to higher areas of the studied material, although the opposite is often observed for oxide semiconductor materials. The results of the capacitance gradient mapping for “probe tip-sample micro-region” capacitor (Figure 6d), obtained as a result of SCM, show a larger gradient (lighter areas) at the inter-particle boundaries, which indicates the preferential nature of inter-grain conductivity in the material.
The results of scanning spreading resistance microscopy (SSRM) (Figure 6e,f) further demonstrate the contact between the V2O5 particles over the entire area of the film: the bright areas in the image correspond to the areas where the current passes between the probe and the sample.
The value of the electron work function of the printed film, 4.54 ± 0.01 eV, was also calculated on the basis of the KPFM results. This value is outside the interval of 4.7–5.3 eV, in which, as a rule, the value for work function of V2O5 is observed. [25,43,44,45]. In particular, this is lower than the values for other vanadium(V) oxide-based materials obtained by us from similar precursors: 4.89 eV in the case of thin film deposition by dip-coating in alkoxoacetylacetonate solution [29] and 4.81 eV in the case of thick film deposition by microextrusion printing with the use of vanadium oxide powder obtained during hydrothermal treatment of the dispersed system resulting from the precursor hydrolysis [35]. This result indicates a significantly increased defectiveness of the V2O5 film obtained in the current study, which also agrees with the results of the full-profile analysis of the corresponding diffractogram.

3.4. Electrophysical Properties of Prepared V2O5 Film

Figure 7 shows frequency dependences of conductivity of V2O5 film under study on alternating current in the temperature range of 50–300 °C. They are characterized by a plateau (from 1 to 104 Hz) that does not depend on frequency and is caused by diffusion of charge carriers (ions) in the material arising when alternating current is applied to it. At higher frequencies, there is the so-called dispersion region, characterized by an increase in conductivity due to hopping of carriers. As can be seen from the above figure, the dispersion region gradually shifts to a higher frequency range with increasing temperature, while there is also an increase in the AC conductivity value (σac), which is typical for materials of similar composition and semiconductors in general [46].
The dependence of the conductivity of the studied film on frequency and temperature is well described by the Jonscher power law (3):
σac(ω,T) = σdc(T) + Aωs,
where σac is the value of total conductivity measured at alternating current, σdc is the conductivity at direct current, ω is the angular frequency of the applied electric current, and the parameters A and s are fitting factors determined by the nature of the material under study and dependent on temperature and frequency. The value of s determines the type of motion (translational or localized) of the charge carriers. It is assumed that if s < 1, the motion is translational, and if s > 1, the motion is localized. Analyzing the temperature dependence of the index s, it is possible to assume different mechanisms of jump conductivity [47]. In our case, the value of s decreases from 1 to 0.8 when the temperature increases from 50 to 300 °C, which further indicates a hopping mechanism of conductivity according to the correlated barrier hopping model in the case of AC conductivity. This model assumes unipolar or bipolar jumps of charge carriers over the Coulomb barrier WM separating the two defect centers, and predicts a decrease in the value of the parameter s as the temperature increases.
The σdc values calculated using Jonscher’s law were further used to construct the temperature dependence of conductivity, as well as to calculate its activation energy using the Arrhenius Equation (4):
σdc = σ0·exp(−Ea/kBT),
where σ0, kB, Ea are the pre-exponential factor, Boltzmann constant, and conductivity activation energy, respectively. It can be seen that σdc increases with temperature, which is a characteristic behavior of the semiconductor and confirms the thermoactivated conduction mechanism in the studied sample (Figure 8a). Using the graph of the temperature dependence of conductivity in Arrhenius coordinates (Figure 8b) and Equation (2), the value of film activation energy was estimated at 0.24 eV, which is in good agreement with the values of Ea for materials of similar composition [46]. Nevertheless, the electrical conductivity values obtained in our study are inferior to those for vanadium pentoxide-based planar materials described in the literature [48,49]. This fact may be due to the lower density of the printed coating, which reduces the contact area between the grains, increasing the resistance of the material.

4. Conclusions

As a result of the research, the process of V2O5 thin film formation by combining sol-gel technology and pen plotter printing was studied. A homogenous solution of synthesized hydrolytically active alkoxoacetylacetonate [VO(C5H7O2)2−x(C4H9O)x] was used as a functional ink. This approach made it possible to obtain thin films composed of vanadium(V) oxide, formed by nanorods with dimensions of 120–285 nm in length and 35–75 nm in width. The film has an activation energy of conductivity Ea = 0.24 eV, which agrees well with the literature data, and demonstrates the hopping character of conductivity. In addition, when studying the material by the SSRM method, it is further evident that the film conducts current rather well: in some areas the current between the probe and the sample reaches up to 2–3 nA. XRD results showed that the obtained V2O5 film is characterized by an orthorhombic crystal lattice, and compared with the literature data, there is a slight decrease in parameters a and b with a simultaneous increase in parameter c, which may indicate a high number of defects, in particular, oxygen vacancies, in the film composition. This hypothesis is confirmed by the low value of the electron work function for the material surface (4.54 eV), calculated using KPFM data. The results obtained confirm the promising application of the pen plotter printing technique combined with sol-gel technology based on the use of alkoxoacetylacetonate vanadyl as precursor for the preparation of V2O5 thin films for various purposes, including such as electrochromic devices, alternative energy devices, and resistive gas sensors

Author Contributions

Conceptualization, N.P.S. and P.Y.G.; investigation, P.Y.G., T.L.S. and N.P.S.; writing—original draft preparation, P.Y.G., T.L.S. and N.P.S.; writing—review and editing, N.P.S.; visualization, P.Y.G. and T.L.S.; supervision, N.P.S., E.P.S. and N.T.K. All authors have read and agreed to the published version of the manuscript.

Funding

The synthesis of the studied nanomaterials was funded by Russian Foundation for Basic Research, project no. 20-33-90136. The SEM and X-ray powder diffraction analyses was performed using shared experimental facilities supported by IGIC RAS state assignment.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Cheng, K.C.; Chen, F.R.; Kai, J.J. V2O5 Nanowires as a Functional Material for Electrochromic Device. Sol. Energy Mater. Sol. Cells 2006, 90, 1156–1165. [Google Scholar] [CrossRef]
  2. Wang, Y.; Cao, G. Li+-Intercalation Electrochemical/Electrochromic Properties of Vanadium Pentoxide Films by Sol Electrophoretic Deposition. Electrochim. Acta 2006, 51, 4865–4872. [Google Scholar] [CrossRef]
  3. Ramana, C.V.; Smith, R.J.; Hussain, O.M.; Chusuei, C.C.; Julien, C.M. Correlation between Growth Conditions, Microstructure, and Optical Properties in Pulsed-Laser-Deposited V2O5 Thin Films. Chem. Mater. 2005, 17, 1213–1219. [Google Scholar] [CrossRef]
  4. Jin, A.; Chen, W.; Zhu, Q.; Jian, Z. Multi-Electrochromism Behavior and Electrochromic Mechanism of Electrodeposited Molybdenum Doped Vanadium Pentoxide Films. Electrochim. Acta 2010, 55, 6408–6414. [Google Scholar] [CrossRef]
  5. Zanarini, S.; di Lupo, F.; Bedini, A.; Vankova, S.; Garino, N.; Francia, C.; Bodoardo, S. Three-Colored Electrochromic Lithiated Vanadium Oxides: The Role of Surface Superoxides in the Electro-Generation of the Red State. J. Mater. Chem. C Mater. 2014, 2, 8854–8857. [Google Scholar] [CrossRef]
  6. Wang, S.; Li, S.; Sun, Y.; Feng, X.; Chen, C. Three-Dimensional Porous V2O5 Cathode with Ultra High Rate Capability. Energy Environ. Sci. 2011, 4, 2854–2857. [Google Scholar] [CrossRef]
  7. Liu, Y.; Clark, M.; Zhang, Q.; Yu, D.; Liu, D.; Liu, J.; Cao, G. V2O5 Nano-Electrodes with High Power and Energy Densities for Thin Film Li-Ion Batteries. Adv. Energy Mater. 2011, 1, 194–202. [Google Scholar] [CrossRef]
  8. Narayanan, R. Single Step Hydrothermal Synthesis of Carbon Nanodot Decorated V2O5 Nanobelts as Hybrid Conducting Material for Supercapacitor Application. J. Solid State Chem. 2017, 253, 103–112. [Google Scholar] [CrossRef]
  9. Jeyalakshmi, K.; Vijayakumar, S.; Nagamuthu, S.; Muralidharan, G. Effect of Annealing Temperature on the Supercapacitor Behaviour of β-V2O5 Thin Films. Mater. Res. Bull. 2013, 48, 760–766. [Google Scholar] [CrossRef]
  10. De Freitas Neto, D.B.; Parmar, R.; Matsubara, E.Y.; Minicucci, M.; Gunnella, R.; Rosolen, J.M. Nanostructured V2O5.NH2O/Cup-Stacked Carbon Nanotube Composite with Remarkable Li+ Specific Capacity. Solid State Ion. 2021, 363, 115590. [Google Scholar] [CrossRef]
  11. Zhang, L.; Jiang, C.; Wu, C.; Ju, H.; Jiang, G.; Liu, W.; Zhu, C.; Chen, T. V2O5 as Hole Transporting Material for Efficient All Inorganic Sb2S3 Solar Cells. ACS Appl. Mater. Interfaces 2018, 10, 27098–27105. [Google Scholar] [CrossRef]
  12. Zilberberg, K.; Trost, S.; Schmidt, H.; Riedl, T. Solution Processed Vanadium Pentoxide as Charge Extraction Layer for Organic Solar Cells. Adv. Energy Mater. 2011, 1, 377–381. [Google Scholar] [CrossRef]
  13. Wang, D.; Elumalai, N.K.; Mahmud, M.A.; Wright, M.; Upama, M.B.; Chan, K.H.; Xu, C.; Haque, F.; Conibeer, G.; Uddin, A. V2O5 -PEDOT: PSS Bilayer as Hole Transport Layer for Highly Efficient and Stable Perovskite Solar Cells. Org. Electron. 2018, 53, 66–73. [Google Scholar] [CrossRef]
  14. Choi, S.G.; Seok, H.J.; Rhee, S.; Hahm, D.; Bae, W.K.; Kim, H.K. Magnetron-Sputtered Amorphous V2O5 Hole Injection Layer for High Performance Quantum Dot Light-Emitting Diode. J. Alloys Compd. 2021, 878, 160303. [Google Scholar] [CrossRef]
  15. Mane, A.A.; Suryawanshi, M.P.; Kim, J.H.; Moholkar, A.V. Fast Response of Sprayed Vanadium Pentoxide (V2O5) Nanorods towards Nitrogen Dioxide (NO2) Gas Detection. Appl. Surf. Sci. 2017, 403, 540–550. [Google Scholar] [CrossRef]
  16. Huotari, J.; Bjorklund, R.; Lappalainen, J.; Lloyd Spetz, A. Pulsed Laser Deposited Nanostructured Vanadium Oxide Thin Films Characterized as Ammonia Sensors. Sens. Actuators B Chem. 2015, 217, 22–29. [Google Scholar] [CrossRef]
  17. Wang, D.; Gu, K.; Zhao, Q.; Zhai, C.; Yang, T.; Lu, Q.; Zhang, J.; Zhang, M. Synthesis and Trimethylamine Sensing Properties of Spherical V2O5 Hierarchical Structures. New J. Chem. 2018, 42, 14188–14193. [Google Scholar] [CrossRef]
  18. Jin, W.; Yan, S.; An, L.; Chen, W.; Yang, S.; Zhao, C.; Dai, Y. Enhancement of Ethanol Gas Sensing Response Based on Ordered V2O5 Nanowire Microyarns. Sens. Actuators B Chem. 2015, 206, 284–290. [Google Scholar] [CrossRef]
  19. Vijayakumar, Y.; Mani, G.K.; Ponnusamy, D.; Shankar, P.; Kulandaisamy, A.J.; Tsuchiya, K.; Rayappan, J.B.B.; Reddy, M.V.R. V2O5 Nanofibers: Potential Contestant for High Performance Xylene Sensor. J. Alloys Compd. 2018, 731, 805–812. [Google Scholar] [CrossRef]
  20. Nandakumar, N.K.; Seebauer, E.G. Low Temperature Chemical Vapor Deposition of Nanocrystalline V2O5 Thin Films. Thin Solid Film. 2011, 519, 3663–3668. [Google Scholar] [CrossRef]
  21. Drosos, C.; Jia, C.; Mathew, S.; Palgrave, R.G.; Moss, B.; Kafizas, A.; Vernardou, D. Aerosol-Assisted Chemical Vapor Deposition of V2O5 Cathodes with High Rate Capabilities for Magnesium-Ion Batteries. J. Power Sources 2018, 384, 355–359. [Google Scholar] [CrossRef]
  22. Hu, B.; Cheng, H.; Huang, C.; Aslam, M.K.; Liu, L.; Xu, C.; Chen, P.; Yu, D.; Chen, C. The Controlled Study of Surfactants on the Morphologies of Three-Dimensional Turbine-like V2O5 for the Application of High Performance Lithium Ion Storage. Solid State Ion. 2019, 342, 115059. [Google Scholar] [CrossRef]
  23. Margoni, M.M.; Mathuri, S.; Ramamurthi, K.; Babu, R.R.; Ganesh, V.; Sethuraman, K. Hydrothermally Grown Nano and Microstructured V2O5 Thin Films for Electrochromic Application. Appl. Surf. Sci. 2018, 449, 193–202. [Google Scholar] [CrossRef]
  24. Moretti, A.; Giuli, G.; Trapananti, A.; Passerini, S. Electrochemical and Structural Investigation of Transition Metal Doped V2O5 Sono-Aerogel Cathodes for Lithium Metal Batteries. Solid State Ion. 2018, 319, 46–52. [Google Scholar] [CrossRef]
  25. Zilberberg, K.; Trost, S.; Meyer, J.; Kahn, A.; Behrendt, A.; Lützenkirchen-Hecht, D.; Frahm, R.; Riedl, T. Inverted Organic Solar Cells with Sol-Gel Processed High Work-Function Vanadium Oxide Hole-Extraction Layers. Adv. Funct. Mater. 2011, 21, 4776–4783. [Google Scholar] [CrossRef]
  26. Alsawafta, M.; Almoabadi, A.; Badilescu, S.; Truong, V.-V. Improved Electrochromic Properties of Vanadium Pentoxide Nanorods Prepared by Thermal Treatment of Sol-Gel Dip-Coated Thin Films. J. Electrochem. Soc. 2015, 162, H466–H472. [Google Scholar] [CrossRef]
  27. Cholant, C.M.; Westphal, T.M.; Balboni, R.D.C.; Moura, E.A.; Gündel, A.; Flores, W.H.; Pawlicka, A.; Avellaneda, C.O. Thin Films of V2O5/MoO3 and Their Applications in Electrochromism. J. Solid State Electrochem. 2017, 21, 1509–1515. [Google Scholar] [CrossRef]
  28. Costa, C.; Pinheiro, C.; Henriques, I.; Laia, C.A.T. Electrochromic Properties of Inkjet Printed Vanadium Oxide Gel on Flexible Polyethylene Terephthalate/Indium Tin Oxide Electrodes. ACS Appl. Mater. Interfaces 2012, 4, 5266–5275. [Google Scholar] [CrossRef] [PubMed]
  29. Gorobtsov, P.Y.; Fisenko, N.A.; Solovey, V.R.; Simonenko, N.P.; Simonenko, E.P.; Volkov, I.A.; Sevastyanov, V.G.; Kuznetsov, N.T. Microstructure and Local Electrophysical Properties of Sol-Gel Derived (In2O3-10%SnO2)/V2O5 Films. Colloids Interface Sci. Commun. 2021, 43, 100452. [Google Scholar] [CrossRef]
  30. Simonenko, T.L.; Simonenko, N.P.; Gorobtsov, P.Y.; Pozharnitskaya, V.M.; Simonenko, E.P.; Glumov, O.V.; Melnikova, N.A.; Sevastyanov, V.G.; Kuznetsov, N.T. Pen Plotter Printing of MnOx Thin Films Using Manganese Alkoxoacetylacetonate. Russ. J. Inorg. Chem. 2021, 66, 1416–1424. [Google Scholar] [CrossRef]
  31. Tamilselvan, M.; Sreekanth, T.V.M.; Yoo, K.; Kim, J. Self-Doped 2D-V2O5 Nanoflakes–A High Electrochemical Performance Cathode in Rechargeable Zinc Ion Batteries. Ceram Int. 2021, 47, 29832–29839. [Google Scholar] [CrossRef]
  32. Liu, F.; Chen, Z.; Fang, G.; Wang, Z.; Cai, Y.; Tang, B.; Zhou, J.; Liang, S. V2O5 Nanospheres with Mixed Vanadium Valences as High Electrochemically Active Aqueous Zinc-Ion Battery Cathode. Nano-Micro Lett. 2019, 11, 25. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  33. Zhang, R.; Qi, L.; Lian, H.; Luo, J. Fabricating Patterned Microstructures by Embedded Droplet Printing on Immiscible Deformable Surfaces. J. Ind. Eng. Chem. 2022, 105, 138–145. [Google Scholar] [CrossRef]
  34. Dobrozhan, O.; Baláž, M.; Vorobiov, S.; Baláž, P.; Opanasyuk, A. Morphological, Structural, Optical Properties and Chemical Composition of Flexible Cu2ZnSnS4 Thin Films Obtained by Ink-Jet Printing of Polyol-Mediated Nanocrystals. J. Alloys Compd. 2020, 842, 155883. [Google Scholar] [CrossRef]
  35. Gorobtsov, P.Y.; Mokrushin, A.S.; Simonenko, T.L.; Simonenko, N.P.; Simonenko, E.P.; Kuznetsov, N.T. Microextrusion Printing of Hierarchically Structured Thick V2O5 Film with Independent from Humidity Sensing Response to Benzene. Materials 2022, 15, 7837. [Google Scholar] [CrossRef] [PubMed]
  36. Seo, H.; Iwai, H.; Kishimoto, M.; Ding, C.; Saito, M.; Yoshida, H. Microextrusion Printing for Increasing Electrode–Electrolyte Interface in Anode-Supported Solid Oxide Fuel Cells. J. Power Sources 2020, 450, 227682. [Google Scholar] [CrossRef]
  37. Soum, V.; Cheong, H.; Kim, K.; Kim, Y.; Chuong, M.; Ryu, S.R.; Yuen, P.K.; Kwon, O.S.; Shin, K. Programmable Contact Printing Using Ballpoint Pens with a Digital Plotter for Patterning Electrodes on Paper. ACS Omega 2018, 3, 16866–16873. [Google Scholar] [CrossRef] [Green Version]
  38. Amin, R.; Ghaderinezhad, F.; Li, L.; Lepowsky, E.; Yenilmez, B.; Knowlton, S.; Tasoglu, S. Continuous-Ink, Multiplexed Pen-Plotter Approach for Low-Cost, High-Throughput Fabrication of Paper-Based Microfluidics. Anal. Chem. 2017, 89, 6351–6357. [Google Scholar] [CrossRef]
  39. Simonenko, N.P.; Fisenko, N.A.; Fedorov, F.S.; Simonenko, T.L.; Mokrushin, A.S.; Simonenko, E.P.; Korotcenkov, G.; Sysoev, V.V.; Sevastyanov, V.G.; Kuznetsov, N.T. Printing Technologies as an Emerging Approach in Gas Sensors: Survey of Literature. Sensors 2022, 22, 3473. [Google Scholar] [CrossRef]
  40. Yue, Y.; Liang, H. Micro- and Nano-Structured Vanadium Pentoxide (V2O5) for Electrodes of Lithium-Ion Batteries. Adv. Energy Mater. 2017, 7, 1602545. [Google Scholar] [CrossRef]
  41. Enjalbert, R.; Galy, J. A Refinement of the Structure of V2O5. Acta Crystallogr. Sect. C 1986, 42, 1467–1469. [Google Scholar] [CrossRef]
  42. Yao, J.; Li, Y.; Massé, R.C.; Uchaker, E.; Cao, G. Revitalized Interest in Vanadium Pentoxide as Cathode Material for Lithium-Ion Batteries and Beyond. Energy Storage Mater. 2018, 11, 205–259. [Google Scholar] [CrossRef]
  43. Meyer, J.; Zilberberg, K.; Riedl, T.; Kahn, A. Electronic Structure of Vanadium Pentoxide: An Efficient Hole Injector for Organic Electronic Materials. J. Appl. Phys. 2011, 110, 033710. [Google Scholar] [CrossRef]
  44. Shrotriya, V.; Li, G.; Yao, Y.; Chu, C.W.; Yang, Y. Transition Metal Oxides as the Buffer Layer for Polymer Photovoltaic Cells. Appl. Phys. Lett. 2006, 88, 073508. [Google Scholar] [CrossRef] [Green Version]
  45. Chiang, W.T.; Su, S.H.; Lin, Y.F.; Yokoyama, M. Increasing the Fill Factor and Power Conversion Efficiency of Polymer Photovoltaic Cell Using V2O5/CuPc as a Buffer Layer. Jpn. J. Appl. Phys. 2010, 49, 04DK14. [Google Scholar] [CrossRef]
  46. Khan, S.; Singh, K. Influence of Al3+ Doping for V5+ on the Structural, Optical, Thermal and Electrical Properties of V2-XAlxO5-δ (X=0–0.20) Ceramics. Ceram Int. 2021, 47, 10724–10732. [Google Scholar] [CrossRef]
  47. Sadykov, S.A.; Palchaev, D.K.; Murlieva, Z.K.; Alikhanov, N.M.R.; Rabadanov, M.K.; Gadzhimagomedov, S.K.; Kallaev, S.N. AC Conductivity of BiFeO3 Ceramics Obtained by Spark Plasma Sintering of Nanopowder. Phys. Solid State 2017, 59, 1771–1777. [Google Scholar] [CrossRef]
  48. Kang, M.; Jung, J.; Lee, S.Y.; Ryu, J.W.; Kim, S.W. Conductivity, Carrier Density, Mobility, Seebeck Coefficient, and Power Factor in V2O5. Thermochim. Acta 2014, 576, 71–74. [Google Scholar] [CrossRef]
  49. Schneider, K.; Dziubaniuk, M.; Wyrwa, J. Impedance Spectroscopy of Vanadium Pentoxide Thin Films. J. Electron. Mater. 2019, 48, 4085–4091. [Google Scholar] [CrossRef] [Green Version]
Colloids 07 00020 g001 550
Figure 1. Scheme of V2O5 thin film pen plotter printing process.
Figure 1. Scheme of V2O5 thin film pen plotter printing process.
Colloids 07 00020 g001
Colloids 07 00020 g002 550
Figure 2. UV spectra of the acetylacetonate solution (1) and the vanadyl alkoxoacetylacetonate solution (2) prepared as a result of its heat treatment for 18 h.
Figure 2. UV spectra of the acetylacetonate solution (1) and the vanadyl alkoxoacetylacetonate solution (2) prepared as a result of its heat treatment for 18 h.
Colloids 07 00020 g002
Colloids 07 00020 g003 550
Figure 3. IR spectra of acetylacetonate solution (1) and the vanadyl alkoxoacetylacetonate solution (2) obtained as a result of its heat treatment for 18 h.
Figure 3. IR spectra of acetylacetonate solution (1) and the vanadyl alkoxoacetylacetonate solution (2) obtained as a result of its heat treatment for 18 h.
Colloids 07 00020 g003
Colloids 07 00020 g004 550
Figure 4. Diffractogram of the obtained V2O5 film on a glass substrate.
Figure 4. Diffractogram of the obtained V2O5 film on a glass substrate.
Colloids 07 00020 g004
Colloids 07 00020 g005 550
Figure 5. Microstructure of the V2O5 film printed on the PAP surface (according to SEM data).
Figure 5. Microstructure of the V2O5 film printed on the PAP surface (according to SEM data).
Colloids 07 00020 g005
Colloids 07 00020 g006 550
Figure 6. Results of AFM of V2O5 film on PAP: topography in the semicontact mode (a), image in the phase contrast mode (b), surface potential distribution map (KPFM) (c), capacitor tip-sample microregion capacitance gradient distribution map (SCM) (d), topography during SSRM recording (e), current distribution between probe and sample (3 V bias voltage) (SSRM) (f).
Figure 6. Results of AFM of V2O5 film on PAP: topography in the semicontact mode (a), image in the phase contrast mode (b), surface potential distribution map (KPFM) (c), capacitor tip-sample microregion capacitance gradient distribution map (SCM) (d), topography during SSRM recording (e), current distribution between probe and sample (3 V bias voltage) (SSRM) (f).
Colloids 07 00020 g006
Colloids 07 00020 g007 550
Figure 7. Frequency dependences of AC conductivity in the temperature range 50–300 °C.
Figure 7. Frequency dependences of AC conductivity in the temperature range 50–300 °C.
Colloids 07 00020 g007
Colloids 07 00020 g008 550
Figure 8. Temperature dependence of σdc (a) and lnσdc of the studied sample (b).
Figure 8. Temperature dependence of σdc (a) and lnσdc of the studied sample (b).
Colloids 07 00020 g008
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Gorobtsov, P.Y.; Simonenko, T.L.; Simonenko, N.P.; Simonenko, E.P.; Kuznetsov, N.T. Preparation of V2O5 Thin Film by Sol–Gel Technique and Pen Plotter Printing. Colloids Interfaces 2023, 7, 20. https://doi.org/10.3390/colloids7010020

AMA Style

Gorobtsov PY, Simonenko TL, Simonenko NP, Simonenko EP, Kuznetsov NT. Preparation of V2O5 Thin Film by Sol–Gel Technique and Pen Plotter Printing. Colloids and Interfaces. 2023; 7(1):20. https://doi.org/10.3390/colloids7010020

Chicago/Turabian Style

Gorobtsov, Philipp Yu., Tatiana L. Simonenko, Nikolay P. Simonenko, Elizaveta P. Simonenko, and Nikolay T. Kuznetsov. 2023. "Preparation of V2O5 Thin Film by Sol–Gel Technique and Pen Plotter Printing" Colloids and Interfaces 7, no. 1: 20. https://doi.org/10.3390/colloids7010020

APA Style

Gorobtsov, P. Y., Simonenko, T. L., Simonenko, N. P., Simonenko, E. P., & Kuznetsov, N. T. (2023). Preparation of V2O5 Thin Film by Sol–Gel Technique and Pen Plotter Printing. Colloids and Interfaces, 7(1), 20. https://doi.org/10.3390/colloids7010020