Next Article in Journal
Polyoxygenated Terpenoids and Polyketides from the Roots of Flueggea virosa and Their Inhibitory Effect against SARS-CoV-2-Induced Inflammation
Next Article in Special Issue
Semi-Embedding Zn-Co3O4 Derived from Hybrid ZIFs into Wood-Derived Carbon for High-Performance Supercapacitors
Previous Article in Journal
The Chemistry of Phenylimidotechnetium(V) Complexes with Isocyanides: Steric and Electronic Factors
Previous Article in Special Issue
3D Electron-Rich ZIF-67 Coordination Compounds Based on 2-Methylimidazole: Synthesis, Characterization and Effect on Thermal Decomposition of RDX, HMX, CL-20, DAP-4 and AP
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 27
Issue 23
10.3390/molecules27238547
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Highly Sensitive Adsorption and Detection of Iodide in Aqueous Solution by a Post-Synthesized Zirconium-Organic Framework

by
Jun Zhang
*,†,
Shanli Yang
†,
Lang Shao
,
Yiming Ren
,
Jiaolai Jiang
,
Huaisheng Wang
,
Hao Tang
,
Hui Deng
and
Tifeng Xia
*
Institute of Materials, China Academy of Engineering Physics, Huafeng Village, Mianyang 621907, China
*
Authors to whom correspondence should be addressed.
†
These authors contributed equally to this work.
Molecules 2022, 27(23), 8547; https://doi.org/10.3390/molecules27238547
Submission received: 1 November 2022 / Revised: 26 November 2022 / Accepted: 2 December 2022 / Published: 4 December 2022
(This article belongs to the Special Issue Multifunctional Metal-Organic Framework Materials)
Browse Figures
Versions Notes

Abstract

:
Effective methods of detection and removal of iodide ions (I−) from radioactive wastewater are urgently needed and developing them remains a great challenge. In this work, an Ag+ decorated stable nano-MOF UiO-66-(COOH)2 was developed for the I− to simultaneously capture and sense in aqueous solution. Due to the uncoordinated carboxylate groups on the UiO-66-(COOH)2 framework, Ag+ was successfully incorporated into the MOF and enhanced the intrinsic fluorescence of MOF. After adding iodide ions, Ag+ would be produced, following the formation of AgI. As a result, Ag+@UiO-66-(COOH)2 can be utilized for the removal of I− in aqueous solution, even in the presence of other common ionic ions (NO2−, NO3−, F−, SO42−). The removal capacity as high as 235.5 mg/g was calculated by Langmuir model; moreover, the fluorescence of Ag+@UiO-66-(COOH)2 gradually decreases with the deposition of AgI, which can be quantitatively depicted by a linear equation. The limit of detection toward I− is calculated to be 0.58 ppm.

Graphical Abstract

1. Introduction

Among efforts to balance the increasing energy demand of human society and sustainable development, nuclear energy has raised more and more attention as a zero-emission-based source of clean energy. Currently, nuclear power provides ~11% of the world’s electricity and it is estimated to rise substantially to around 80%, to a massive ~715 GW(e)/annum in nuclear energy by the year 2050 [1,2]; however, nuclear energy generated from atom fission produces several harmful radioactive isotopes, among which both radioactive 129I and 131I are regarded as extremely dangerous due to the large half-life and high volatility of 129I and severe metabolic processes interference of 131I [3,4,5]; besides, accidental release of radioactive iodine isotopes during an accident at a nuclear reactor holds a serious threat to the environment and human health [6]. For example, high levels of radioactive iodine (131I) have been found in the groundwater at the devastated nuclear facility after the nuclear accident at Fukushima [7,8]. In addition, 131I is widely utilized for the treatment of hyperthyroidism and thyroid cancer, while 125I is a good assistant for thyroid scanning and radioimmunoassay [9]. Overall, the wastes that contain radioactive iodine should be properly stored and disposed of to guarantee public safety [10,11]; therefore, it is undoubted that the development of effective methods for capture and sensing of radioactive iodine from wastewater is of great practical significance.
In environments with a pH of about 4–10, iodine mainly exists as iodide. In the nuclear accident, radioactive iodine was released primarily in the form of iodide, which was found as the dominant form in the marine environment [12,13]. Accordingly, several adsorbents for iodide in aqueous solution have been studied in the past few decades, including hydrotalcite [14], nanofibers [15], Cu/Ag-based material [16,17], bismuth oxide [13,18,19], porous organic polymers [3,20], and metal–organic frameworks (MOFs) [21,22]. Among these materials, MOFs which possess organic–inorganic hybrid features along with porous structures are considered to be promising candidates as scavengers for various environmental pollutants [23,24,25,26,27]. Due to their adjustable channel chemical environment and post-synthetic friendly character, MOFs have been developed as iodide adsorbents through the modification of pore environments or decorating of I− trap moieties, such as Ag+ [21,28,29,30] and bismuth [31], which show excellent adsorbent capacity for iodide in aqueous solution. It is not difficult to see that the timely determination of the concentration of iodide is also important after the adsorption process. In this regard, an adsorbent combined with a sensor should be practical. A few methods of sensing iodide are reported in the literature. Trace levels of iodide were usually detected with spectroscopy, which suffers from the need for frequent calibration and the bulky nature of the devices. For iodide sensors at ppm levels, various strategies have been developed, including luminescent sensors and electronic sensors [32,33,34]. These methods demonstrated promising application potential in real-time outdoors sensing, which is very suitable for monitoring environmental safety. MOFs have also been developed as fluorescent sensors in the past two decades [35,36,37,38,39]. Based on a MOF, an iodide adsorbent and sensor might be realized simultaneously.
Bearing these considerations in mind, we synthesized a water-stable UiO-66-(COOH)2 modified by Ag+ for the adsorption and sensing of iodide in aqueous solution. As a proof-of-concept demonstration (Scheme 1), the resulted Ag+@UiO-66-(COOH)2 was applied to capture iodide from aqueous solution, and afterwards the iodide concentrations can be determined by this material. To the best of our knowledge, this is the first time the iodide in aqueous solution was removed and measured simultaneously based on MOF material. As expected, Ag+@UiO-66-(COOH)2 exhibits excellent iodide adsorption capacity and ability to sense iodide, which is mainly due to the formation of AgI. Overall, our work demonstrates Ag+@UiO-66-(COOH)2 can serve as an effective iodide adsorbent and sensor and further suggests the wide application of MOF-based integrated devices.

2. Results and Discussion

2.1. Crystal Synthesis and Characterization

The synthesis of UiO-66-(COOH)2 was realized by reflux reaction reported by our previous work [40], which exhibited high thermal and chemical stability which raised significant research interest in the past decade. This porous framework is built by Zr6-octahedra second building units that are linked by benzene-1,2,4,5-tetracarboxylic acid (H4btec) ligand, shaped into a cubic three-dimensional (3D) structure involving tetrahedral and octahedral cages (Figure 1a) [41]. Scanning electron microscopy (SEM) images were taken to reveal the morphology and size of the as-synthesized UiO-66-(COOH)2, which demonstrated that the MOF presents the octahedral structure with the size of 500–700 nm (Figure 1b). As shown in Figure 2, the power X-ray diffraction pattern of UiO-66 simulated from the single-crystal structure data features two peaks at 7.4° and 8.5°, respectively, corresponding to the crystal plane (111) and (200) [42]. The well-matched PXRD patterns of UiO-66-(COOH)2 to the simulated UiO-66 indicates an isostructural framework topology. As depicted in Figure 1a, only two carboxylates of the H4btec were coordinated to SBU, and the remaining two uncoordinated –COOH groups point to the pores of the framework. The presence of the uncoordinated –COOH groups was also evidenced by FT-IR spectrum. As shown in Figure S1, a strong band was observed at 1716 cm−1 which is attributed to the C═O stretching vibration of free –COOH groups. The permanent porosity of as-synthesized UiO-66-(COOH)2 was confirmed by N2 adsorption isotherm after guest removal, demonstrating the Brunauer–Emmett–Teller (BET) surface areas of 809.03 m2 g−1 (Figure S2). The uncoordinated –COOH groups and the permanent porosity indicated that UiO-66-(COOH)2 is a good candidate for post modification; therefore, we metalized UiO-66-(COOH)2 by the reaction of Ag+ ions with the uncoordinated –COOH groups in aqueous solution at 60 °C for one day. After the post-synthesis process, the PXRD of the as-obtained Ag+@UiO-66-(COOH)2 remained the same as UiO-66-(COOH)2 (Figure 2), indicating the maintenance of structure integrity during the modification process. The Ag+ loading level that was quantified by ICP-MS measurement shows the molar ratio of Zr:Ag is 1:1.62. Notably, after the post-synthesis process, the C=O stretching vibration of free –COOH groups almost disappeared at 1716 cm−1, giving a very direct proof of the interactions between the free –COOH groups and Ag+; furthermore, XPS deconvolution of the survey and Ag 3d spectrum of Ag+@UiO-66-(COOH)2 and AgNO3 is shown in Figure S3. It can be seen that the biding energy corresponding to the Ag 3d3/2 and 3d5/2 electronic orbit of Ag+@UiO-66-(COOH)2 is a little higher than those of AgNO3, indicating the coordination between Ag+ and –COOH groups; besides, the Ag+ incorporated framework remained at its original morphology, as revealed by the SEM images (Figure 1c).

2.2. Iodide Adsorption

On the basis of the high KSP of AgI (8.3 × 10−17 mol2·L−2), the Ag+@UiO-66-(COOH)2 was expected to have a high affinity toward I− in aqueous medium. To check this hypothesis, the removal efficiency Ag+@UiO-66-(COOH)2 on different initial concentrations of iodine was first explored. Afterwards, we prepared 0.5 g/L I− solution in water and exposed sorbents to this solution while monitoring the concentration of I− solution in water by ICP-MS. For comparison, the I− adsorption ability of Ag+-free UiO-66-(COOH)2 was also investigated under the same experimental conditions. As shown in Figure 3a, more than 92% of equilibrium adsorption amounts were achieved within 60 min for I−. The adsorption to I− could reach the equilibrium state within 20 h. The sorption kinetic was analyzed in terms of the pseudo-second-order rate equation. The linearized forms of the pseudo-second-order rate equation are presented in Equation (1).
t q t = 1 k 2 q e 2 + t q e ,
where: qe and qt denote the amounts of iodide ions adsorbed at equilibrium e and at time t, respectively, and k2 (g/g min) is the second-order rate constant of adsorption.
The results and relevant parameters calculated from the fitting processes are shown in Figure 3b and listed in Table S1. The good fitting with the pseudo-second-order kinetic model suggests that the adsorption mechanism is chemisorption.
To determine the adsorption isotherms, the initial I− concentrations were set from 100 to 1000 mg/L and the results are shown in Figure 4a. Clearly, the amounts of I− adsorbed on the Ag+@UiO-66-(COOH)2 increased with increasing initial concentration. The adsorption isotherms of I− on the adsorbents were simulated using the Langmuir model, where its linear form can be described by Equation (2):
C e q e = 1 K L q m + C e q m ,
where KL (L/g) is the Langmuir adsorption coefficient and qm (g/g) is maximum adsorption capacity. Plots of 1/qe versus 1/Ce of I− for Ag+@UiO-66-(COOH)2 are shown in Figure 4b. The values of KL, qm, and R2 were obtained from the slope and intercept of linear correlation, as displayed in Table S2. From the Langmuir model, the maximum adsorption capacities of Ag+@UiO-66-(COOH)2 were determined to be 235.5 mg/g. In contrast, UiO-66-(COOH)2 can only adsorb 73.9 mg/g iodide under the same conditions as shown in Figure S4.
Furthermore, the complex exhibits outstanding adsorption behavior to I− in diverse interference ions. Commonly, contaminated water contains several anions, including nitrate (NO3−), nitrite (NO2−), sulphate (SO42−), and fluoride (F−), which may cause hindrance in the capture of I−. To check this, the removal of I− was tested using a binary mixture of anions (0.5 g/L I− and 1 × 10−2 M, other competing ions including NO3−, NO2−, SO42−, and F−) by ion chromatography. At room temperature, the standard curve of iodide in aqueous solution was determined by the standard addition method as shown in Figure S5. The experiment revealed that 92.5%, 89.5%, 88.6%, and 93% I− were the uptake percentages in the binary mixtures (Figure 5 and Figure S6), respectively, indicating exceptional binding for I− of Ag+@UiO-66-(COOH)2, even in the presence of other competing ions. Some representative adsorbents and their performances are listed in Table S3, from which it can be seen that Ag+@UiO-66-(COOH)2 possesses outstanding adsorption capacity.

2.3. Sensing Properties

The photoluminescent spectra of Ag+@UiO-66-(COOH)2 were examined in aqueous solution at room temperature. Upon the excitation of 381 nm, Ag+@UiO-66-(COOH)2 exhibited a broad emission peak with the center located at 497 nm, attributing to the ligand emission (Figure S7). As is well known, Ag+ is able to enhance the fluorescent emission of most emitters in aqueous solution [43]. Herein, the ligand-based emission intensity of Ag+@UiO-66-(COOH)2 was shown to be two times higher than UiO-66-(COOH)2 because of the sensitization of Ag+; however, due to the strong coordinating ability of Ag+ towards I−, it is expected that the Ag+ on the Ag+@UiO-66-(COOH)2 may be precipitated by I−, leading to a decease of the fluorescent intensity.
The above supposition was verified by the sensing experiments of Ag+@UiO-66-(COOH)2 and UiO-66-(COOH)2 towards I− in aqueous solution. The fluorescent spectra changes of Ag+@UiO-66-(COOH)2 and UiO-66-(COOH)2 upon the addition of different concentration of Ag+ in aqueous solution were monitored by spectrometer. As shown in Figure 6a, with the increase in the I− concentration (from 1 to 10 mg I−/L), the emission intensity of Ag+@UiO-66-(COOH)2 at 497 nm gradually decreases. Quantitatively, this phenomenon can be depicted using the linear equitation:
I497 = 39688.5 − 2721.6 × C(I−) (R2 = 0.986),
The detection limit (LOD) was determined to be 0.58 ppm based on the formula of LOD = 3δ/S, where δ is the standard deviation for 30 replicating fluorescence measurements of blank solutions and S is the slope of the calibration curve. In contrast, the luminescent intensity of UiO-66-(COOH)2 shows no obvious change with the addition of I− (Figure S8).
To verify the selectivity and anti-interference of this I− probe, we tested the fluorescence response of Ag+@UiO-66-(COOH)2 to the environmentally relevant species in aqueous solution. The emission intensity of Ag+@UiO-66-(COOH)2 is shown in Figure 7, where different interference ions (1 × 10−4 M) show slight fluctuations, especially in FeCl3 and Co(NO3)2 solutions; however, by adding 10 mg/L I− ions into the solution, the luminescence of Ag+@UiO-66-(COOH)2 in all solutions significantly quenched the process with a quenching ratio of approximately 2–3. These results demonstrate the great selectivity of I− in the presence of a wide range of environmentally interfering species. Table S4 listed the representative fluorescent iodide probes, from which one can see that Ag+@UiO-66-(COOH)2 shows comparable sensing ability with other MOF or small molecules sensors.

3. Conclusions

In summary, an Ag+ incorporated nano-MOF Ag+@UiO-66-(COOH)2 was prepared through post-synthetic method, and its adsorption and sensing performance towards I− in aqueous solution was investigated. The successful incorporation of Ag+ on UiO-66-(COOH)2 was confirmed by FI-IR and XPS results, and the intact MOF structure after modification process was verified by XRD and SEM tests. Due to the high affinity of I− to Ag+, Ag+@UiO-66-(COOH)2 can effectively remove I− in aqueous solution; moreover, after the precipitate of AgI, the fluorescent enhancement of Ag+ was reduced so that the luminescent of Ag+@UiO-66-(COOH)2 was quenched, resulting in outstanding sensing ability toward I−. This work demonstrates that Ag+@UiO-66-(COOH)2 is a good potential candidate for adsorption and sensing of iodide, which may raise research interests in the field of MOF-based adsorbents and sensors for the radioactive nuclide.

4. Materials and Methods

4.1. Synthesis of UiO-66-(COOH)2

10 mmol 1,2,4,5-benzenetetracarboxylic acid (H4btec) and 10.4 mmol zirconium tetrachloride (ZrCl4) were dispersed in 60 mL distilled water in a round-bottom flask equipped with reflux condenser and magnetic stirrer; then, 40 mL acetic acid was added into the mixture at room temperature under vigorous stirring and heated at 100 °C for 24 h, obtaining a white powder product. Afterwards, the powder was washed with distilled water, anhydrous methanol, and acetone sequentially three times, respectively. During each washing process, the extract was decanted, and fresh water, methanol, or acetone was added every time. After the last washing process, the sample was dried in a vacuum oven at 80 °C to yield the final product.

4.2. Preparation of Ag+@UiO-66-(COOH)2

Ag+@UiO-66-(COOH)2 was prepared by heating the mixture of UiO-66-(COOH)2 and AgNO3 in distilled water. Typically, the mixture of 0.1 g UiO-66-(COOH)2 and 0.17 g AgNO3 was mixed in distilled water and heated to 60 °C for 1 day; thereafter, the compound was isolated by centrifugation 8 min at 9000 rpm, and then washed three times with methanol followed by exchanging it with methanol for 1 day, followed by an activating process in a vacuum oven at 80 °C.

4.3. Analytical Methods and Characterization

The morphology of the compound was characterized by scanning electron microscopy (SEM, HITACHI S-4800, Tokyo, Japan). X-ray photoelectron spectroscopy (XPS, kratos, Manchester, UK ) was carried out to verify the coordination reaction between the metal ions and MOF. The binding energy data were calibrated with reference to C 1s signal at 285 eV. Flourier transformation infrared (FT-IR) spectra were recorded on a Nicolet iS10 FT-IR spectrometer (Thermofisher, Waltham, MA, USA). XRD patterns were produced on the Shimadzu XRD 7000 diffractometer (Shimadzu, Tokyo, Japan) with Cu-Kα radiation at room temperature. The ion chromatography was carried out on an ICS-3000 ion chromatograph (Dionex, California, USA). Inductively coupled plasma mass spectrometry (ICP-MS) was performed on a Thermo Scientific XSERIES 2 ICP-MS system (Thermofisher, Waltham, MA, USA). Luminescence spectra for Ag+@UiO-66-(COOH)2 in aqueous solution were recorded on a Hitachi F4600 fluorescence spectrometer (Hitachi, Tokyo, Japan).

4.4. Iodides Capture Studies

All the adsorption experiments were carried out in 10 mL centrifugal tubes at room temperature.
Kinetic Studies. 1 mg UiO-66-(COOH)2 or Ag+@UiO-66-(COOH)2 were added into 10 mL solution containing 0.5 g I−/L in a centrifugal tube; then, the absorbance value of the supernatant solution was recorded at regular time intervals with the help of ICP-MS.
Uptake Capacity Studies. 1 mg Ag+@UiO-66-(COOH)2 was kept in contact with 10 mL I− solution bearing different amounts of I− (100–1000 mg/L) for 24 h under stirring conditions. After 24 h, MOF was filtered out and the filtrate was analyzed by ICP-MS.
Selectivity Studies. 1 mg Ag+@UiO-66-(COOH)2 was kept in contact with a binary solution containing 4 mL of I− solution (0.5 g I−/L) and 4 mL each of various competing anions solution (1 × 10−2 M) for 24 h, including NO3−, NO2−, SO42−, and F−; then, the concentration of I− in the binary solution was detected by ion chromatograph.

4.5. Iodides Concentration Dependent Luminescence Spectra

0.5 mg of Ag+@UiO-66-(COOH)2 was dispersed in 1 mL of KI solution at the pH of 7.0 with different concentrations from 0 to 1 × 10−6 M and ultrasonic treatment for about 3 min to form a homogeneous suspension, and then the spectra were collected immediately. To investigate the influence of competing ions, 0.2 mg Ag+@UiO-66-(COOH)2 was dispersed into 1 mL of 1 × 10−4 M BaCl2, La(NO3)3, Na2S2O3, Ce(NO3)4, AgNO3, NaNO3, NaCl, CaCl2, Zn(NO3)2, NaHCO3, CdCl2, NaF, MnCl2, and AlCl3 aqueous solution separately.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/molecules27238547/s1, Figure S1: FT-IR spectra of UiO-66-(COOH)2 and Ag+@UiO-66-(COOH)2; Figure S2: Survey XPS spectra of Ag+@UiO-66-(COOH)2 and AgNO3; Figure S3: Standard curve of iodide in aqueous solution by ion chromatography; Figure S4: Ion chromatography of binary mixture containing I− and other competing anions; Figure S5: Excitation and emission spectra of Ag+@UiO-66-(COOH)2 in aqueous solution; Table S1: Kinetics parameters for I− adsorption on Ag+@UiO-66-(COOH)2; Table S2: The Langmuir isotherm model parameters for I− adsorption on Ag+@UiO-66-(COOH)2; Table S3: Comparison of the iodide adsorption in different adsorbents; Table S4: Comparison of the iodide sensing on different fluorescent probes [13,17,21,22,29,44,45,46,47,48,49,50,51].

Author Contributions

Conceptualization, J.Z. and T.X.; methodology, J.Z., S.Y., Y.R., H.W. and L.S.; validation, H.T., J.J. and H.D.; formal analysis, J.Z. and S.Y; investigation, J.Z. and S.Y.; resources, S.Y., Y.R., L.S. and H.W.; data curation, J.Z. and T.X.; writing—original draft preparation, J.Z. and S.Y.; writing—review and editing, J.Z., S.Y., and T.X.; supervision, H.D. and T.X.; project administration, H.D.; and funding acquisition, T.X. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by National Natural Science Foundation of China (grant number 52102190).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding authors.

Conflicts of Interest

The authors declare no conflict of interest.

Sample Availability

Samples of the compounds are not available from the authors.

References

  1. International Atomic Energy Agency. Energy, Electricity and Nuclear Power Estimates for the Period Up to 2050; International Atomic Energy Agency: Vienna, Austria, 2015; Volume 37. [Google Scholar]
  2. Gu, J.-M.; Kim, S.-J.; Kim, Y.; Huh, S. Structural isomerism of an anionic nanoporous In-MOF with interpenetrated diamond-like topology. CrystEngComm 2012, 14, 1819. [Google Scholar] [CrossRef]
  3. Xie, W.; Cui, D.; Zhang, S.-R.; Xu, Y.-H.; Jiang, D.-L. Iodine capture in porous organic polymers and metal–organic frameworks materials. Mater. Horiz. 2019, 6, 1571–1595. [Google Scholar] [CrossRef]
  4. Subrahmanyam, K.S.; Sarma, D.; Malliakas, C.D.; Polychronopoulou, K.; Riley, B.J.; Pierce, D.A.; Chun, J.; Kanatzidis, M.G. Chalcogenide Aerogels as Sorbents for Radioactive Iodine. Chem. Mater. 2015, 27, 2619–2626. [Google Scholar] [CrossRef]
  5. Han, S.; Um, W.; Kim, W.-S. Development of bismuth-functionalized graphene oxide to remove radioactive iodine. Dalton Trans. 2019, 48, 478–485. [Google Scholar] [CrossRef] [PubMed]
  6. Guo, X.; Li, Y.; Zhang, M.; Cao, K.; Tian, Y.; Qi, Y.; Li, S.; Li, K.; Yu, X.; Ma, L. Colyliform Crystalline 2D Covalent Organic Frameworks (COFs) with Quasi-3D Topologies for Rapid I2 Adsorption. Angew. Chem. Int. Ed. 2020, 59, 22697–22705. [Google Scholar] [CrossRef]
  7. Xu, S.; Freeman, S.P.H.T.; Hou, X.; Watanabe, A.; Yamaguchi, K.; Zhang, L. Iodine Isotopes in Precipitation: Temporal Responses to 129I Emissions from the Fukushima Nuclear Accident. Environ. Sci. Technol. 2013, 47, 10851–10859. [Google Scholar] [CrossRef] [PubMed]
  8. Hosoda, M.; Tokonami, S.; Tazoe, H.; Sorimachi, A.; Monzen, S.; Osanai, M.; Akata, N.; Kakiuchi, H.; Omori, Y.; Ishikawa, T.; et al. Activity concentrations of environmental samples collected in Fukushima Prefecture immediately after the Fukushima nuclear accident. Sci. Rep. 2013, 3, 2283. [Google Scholar] [CrossRef]
  9. Huang, R.; Zhao, Z.; Ma, X.; Li, S.; Gong, R.; Kuang, A. Targeting of tumor radioiodine therapy by expression of the sodium iodide symporter under control of the survivin promoter. Cancer Gene Therapy 2011, 18, 144–152. [Google Scholar] [CrossRef] [PubMed]
  10. Rose, P.S.; Swanson, R.L.; Cochran, J.K. Medically-derived 131I in municipal sewage effluent. Water Res. 2012, 46, 5663–5671. [Google Scholar] [CrossRef]
  11. Rose, P.S.; Smith, J.P.; Cochran, J.K.; Aller, R.C.; Swanson, R.L. Behavior of medically-derived 131I in the tidal Potomac River. Sci. Total Environ. 2013, 452–453, 87–97. [Google Scholar] [CrossRef] [PubMed]
  12. Hou, X.; Povinec, P.P.; Zhang, L.; Shi, K.; Biddulph, D.; Chang, C.-C.; Fan, Y.; Golser, R.; Hou, Y.; Ješkovsk, M.; et al. Iodine-129 in Seawater Offshore Fukushima_ Distribution, Inorganic Speciation, Sources, and Budget. Environ. Sci. Technol. 2013, 47, 3091–9098. [Google Scholar] [CrossRef] [PubMed]
  13. Lee, S.-H.; Takahashi, Y. Selective immobilization of iodide onto a novel bismuth-impregnated layered mixed metal oxide_ Batch and EXAFS studies. J. Hazard. Mater. 2020, 384, 121223. [Google Scholar] [CrossRef]
  14. Theiss, F.L.; Couperthwaite, S.J.; Ayoko, G.A.; Frost, R.L. A review of the removal of anions and oxyanions of the halogen elements from aqueous solution by layered double hydroxides. J. Colloid Interface Sci. 2014, 417, 356–368. [Google Scholar] [CrossRef]
  15. Mu, W.; Yu, Q.; Li, X.; Wei, H.; Jian, Y. Niobate nanofibers for simultaneous adsorptive removal of radioactive strontium and iodine from aqueous solution. J. Alloys Compd. 2017, 693, 550–557. [Google Scholar] [CrossRef]
  16. Mao, P.; Qi, L.; Liu, X.; Liu, Y.; Jiao, Y.; Chen, S.; Yang, Y. Synthesis of Cu_Cu2O hydrides for enhanced removal of iodide from water. J. Hazard. Mater. 2017, 328, 21–28. [Google Scholar] [CrossRef] [PubMed]
  17. Zhang, X.; Gu, P.; Li, X.; Zhang, G. Efficient adsorption of radioactive iodide ion from simulated wastewater by nano Cu2O_Cu modified activated carbon. Chem. Eng. J. 2017, 322, 129–139. [Google Scholar] [CrossRef]
  18. Liu, L.; Liu, W.; Zhao, X.; Chen, D.; Cai, R.; Yang, W.; Komarneni, S.; Yang, D. Selective Capture of Iodide from Solutions by Microrosette-like δ-Bi2O3. ACS Appl. Mater. Interfaces 2014, 6, 16082–16090. [Google Scholar] [CrossRef] [PubMed]
  19. Liu, S.; Kang, S.; Wang, H.; Wang, G.; Zhao, H.; Cai, W. Nanosheets-built flowerlike micro_nanostructured Bi2O2.33 and its highly efficient iodine removal performances. Chem. Eng. J. 2016, 289, 219–230. [Google Scholar] [CrossRef]
  20. Sen, A.; Sharma, S.; Dutta, S.; Shirolkar, M.M.; Dam, G.K.; Let, S.; Ghosh, S.K. Functionalized Ionic Porous Organic Polymers Exhibiting High Iodine Uptake from Both the Vapor and Aqueous Medium. ACS Appl. Mater. Interfaces 2021, 13, 34188–34196. [Google Scholar] [CrossRef]
  21. Mao, P.; Qi, B.; Liu, Y.; Zhao, L.; Jiao, Y.; Zhang, Y.; Jiang, Z.; Li, Q.; Wang, J.; Chen, S.; et al. AgII doped MIL-101 and its adsorption of iodine with high speed in solution. J. Solid State Chem. 2016, 237, 274–283. [Google Scholar] [CrossRef]
  22. Wan, J.; Li, Y.; Jiang, Y.; Lin, L.; Yin, Y. Silver-doped MIL-101(Cr) for rapid and effective capture of iodide in water environment_ exploration on adsorption mechanism. J. Radioanal. Nucl. Chem. 2021, 328, 1041–1054. [Google Scholar] [CrossRef]
  23. Ma, X.; Chai, Y.; Li, P.; Wang, B. Metal–Organic Framework Films and Their Potential Applications in Environmental Pollution Control. Acc. Chem. Res. 2019, 52, 1461–1470. [Google Scholar] [CrossRef]
  24. Mandal, S.; Natarajan, S.; Mani, P.; Pankajakshan, A. Post-Synthetic Modification of Metal–Organic Frameworks Toward Applications. Adv. Funct. Mater. 2021, 31, 2006291. [Google Scholar] [CrossRef]
  25. Shen, N.; Yang, Z.; Liu, S.; Dai, X.; Xiao, C.; Taylor-Pashow, K.; Li, D.; Yang, C.; Li, J.; Zhang, Y.; et al. 99TcO4− removal from legacy defense nuclear waste by an alkaline-stable 2D cationic metal organic framework. Nat. Commun. 2020, 11, 5571. [Google Scholar] [CrossRef]
  26. Chen, M.; Liu, T.; Zhang, X.; Zhang, R.; Tang, S.; Yuan, Y.; Xie, Z.; Liu, Y.; Wang, H.; Fedorovich, K.V.; et al. Photoinduced Enhancement of Uranium Extraction from Seawater by MOF_Black Phosphorus Quantum Dots Heterojunction Anchored on Cellulose Nanofiber Aerogel. Adv. Func. Mater. 2021, 31, 2100106. [Google Scholar] [CrossRef]
  27. Jin, K.; Lee, B.; Park, J. Metal-organic frameworks as a versatile platform for radionuclide management. Coord. Chem. Rev. 2020, 427, 213473. [Google Scholar] [CrossRef]
  28. Ji, Z.; Wang, H.; Canossa, S.; Wuttke, S.; Yaghi, O.M. Pore Chemistry of Metal–Organic Frameworks. Adv. Funct. Mater. 2020, 30, 2000238. [Google Scholar] [CrossRef]
  29. Zhao, X.; Han, X.; Li, Z.; Huang, H.; Liu, D.; Zhong, C. Enhanced removal of iodide from water induced by a metal-incorporated porous metal–organic framework. Appl. Surf. Sci. 2015, 351, 760–764. [Google Scholar] [CrossRef]
  30. Rio, M.d.; Villar, M.; Quesada, S.; Palomino, G.T.; Ferrer, L.; Cabello, C.P. Silver-functionalized UiO-66 metal-organic framework-coated 3D printed device for the removal of radioactive iodine from wastewaters. Appl. Mater. Today 2021, 24, 101130. [Google Scholar]
  31. Xu, W.; Zhang, W.; Kang, J.; Li, B. Facile synthesis of mesoporous Fe-based MOFs loading bismuth with high speed adsorption of iodide from solution. J. Solid State Chem. 2019, 269, 558–565. [Google Scholar] [CrossRef]
  32. Ghaedi, M.; Shojaie, A.F.; Montazerozohori, M.; Karami, B.; Gharaghani, S. Iodide-Selective Electrodes Based on Bis[N(2-methyl-phenyl) 4-Nitro-thiobenzamidato]mercury(II) and Bis[N-phenyl 3,5-Dinitro-thiobenzamidato]mercury(II) Carriers. Electroanalysis 2005, 19, 1746–1754. [Google Scholar] [CrossRef]
  33. Ibupoto, Z.H.; Khun, K.; Willander, M. A Selective Iodide Ion Sensor Electrode Based on Functionalized ZnO Nanotubes. Sensors 2013, 13, 1984–1997. [Google Scholar] [CrossRef] [PubMed]
  34. Terufumi, F.; Mohammadzai, I.U.; Inoue, H.; Takahiro, K. Chemiluminescence determination of iodide and/or iodine using a luminol-hexadecyltrimethylammonium chloride reversed micelle system following on-line oxidation and extraction. Analyst 2000, 125, 759–763. [Google Scholar]
  35. Yang, G.-L.; Jiang, X.-L.; Xu, H.; Zhao, B. Applications of MOFs as Luminescent Sensors for Environmental Pollutants. Small 2021, 17, 2005327. [Google Scholar] [CrossRef] [PubMed]
  36. Chen, X.; Mei, Q.; Yu, L.; Ge, H.; Yue, J.; Zhang, K.; Hayat, T.; Alsaedi, A.; Wang, S. Rapid and On-Site Detection of Uranyl Ions via Ratiometric Fluorescence Signals Based on a Smartphone Platform. ACS Appl. Mater. Interfaces 2018, 10, 42225–42232. [Google Scholar] [CrossRef] [PubMed]
  37. Xie, J.; Wang, Y.; Zhang, D.; Liang, C.; Liu, W.; Chong, Y.; Yin, X.; Zhang, Y.; Gui, D.; Chen, L.; et al. Photo-exfoliation of a highly photo-responsive two-dimensional metal–organic framework. Chem. Commun. 2019, 55, 11715–11718. [Google Scholar] [CrossRef] [PubMed]
  38. Xia, T.; Shao, Z.; Yan, X.; Liu, M.; Yu, L.; Wan, Y.; Chang, D.; Zhang, J.; Zhao, D. Tailoring the triplet level of isomorphic Eu_Tb mixed MOFs for sensitive temperature sensing. Chem. Commun. 2021, 57, 3143–3146. [Google Scholar] [CrossRef] [PubMed]
  39. Zhang, J.; Hu, E.; Liu, F.; Li, H.; Xia, T. Growth of robust metal-organic framework films by spontaneous oxidation of a metal substrate for NO2 sensing. Mater. Chem. Front. 2021, 5, 6476–6484. [Google Scholar] [CrossRef]
  40. Zhang, X.; Hu, Q.; Xia, T.; Zhang, J.; Yang, Y.; Cui, Y.; Chen, B.; Qian, G. Turn-on and Ratiometric Luminescent Sensing of Hydrogen Sulfide Based on Metal–Organic Frameworks. ACS Appl. Mater. Interfaces 2016, 8, 32259–32265. [Google Scholar] [CrossRef]
  41. Wu, D.; Maurin, G.; Yang, Q.; Serre, C.; Jobic, H.; Zhong, C. Computational exploration of a Zr-carboxylate based metal-organic framework as a membrane material for CO2 capture. J. Mater. Chem. A 2014, 2, 1657–1661. [Google Scholar] [CrossRef]
  42. Guillerm, V.; Gross, S.; Serre, C.; Devic, T.; Bauer, M.; Ferey, G. A zirconium methacrylate oxocluster as precursor for the low-temperature synthesis of porous zirconium(IV) dicarboxylates. Chem. Commun. 2010, 46, 767–769. [Google Scholar] [CrossRef]
  43. Zhang, X.; Fang, L.; Jiang, K.; He, H.; Yang, Y.; Cui, Y.; Li, B.; Qian, G. Nanoscale fluorescent metal–organic framework composites as a logic platform for potential diagnosis of asthma. Biosens. Bioelectron. 2019, 130, 65–72. [Google Scholar] [CrossRef]
  44. Mao, P.; Liu, Y.; Jiao, Y.; Chen, S.; Yang, Y. Enhanced uptake of iodide on Ag@Cu2O nanoparticles. Chemosphere 2016, 164, 396–403. [Google Scholar] [CrossRef] [PubMed]
  45. Rong, J.; Zhao, Z.; Jing, Z.; Zhang, T.; Qiu, F.; Xu, J. High-specifc surface area hierarchical Al2O3 carbon fber based on a waste paper fber template: Preparation and adsorption for iodide ions. J. Wood Chem. Technol. 2017, 37, 485–492. [Google Scholar] [CrossRef]
  46. Wang, M.; Wu, Z.; Yang, J.; Wang, G.; Wang, H.; Cai, H. Au25(SG)18 as a fluorescent iodide sensor. Nanoscale 2012, 4, 4087–4090. [Google Scholar] [CrossRef] [PubMed]
  47. Dai, R.; Wang, X.; Wang, Z.; Mu, S.; Liao, J.; Wen, Y.; Lv, J.; Huang, K.; Xiong, X. A sensitive and label-free sensor for melamine and iodide by target-regulating the formation of G-quadruplex. Microchem. J. 2019, 146, 592–599. [Google Scholar]
  48. Dang, Q.; Wan, H.; Zhan, X. Carbazolic porous framework with tetrahedral core for gas uptake and tandem detection of iodide and mercury. ACS Appl. Mater. Interfaces 2017, 9, 21438–21446. [Google Scholar] [CrossRef]
  49. Salomón-Flores, M.; Hernández-Juárez, C.; Bazany-Rodríguez, I.; Barroso-Flores, J.; Martínez-Otero, D.; López-Arteaga, R.; Valdés-Martínez, J.; Dorazco-González, A. Efficient fluorescent chemosensing of iodide based on a cationic meso-tetraarylporphyrin in pure water. Sens. Actuators B 2019, 281, 462–470. [Google Scholar] [CrossRef]
  50. Singha, D.; Majee, P.; Mondal, S.; Mahata, P. Luminescent cadmium based MOF as selective and sensitive iodide sensor in aqueous medium. J. Photochem. Photobiol. A 2018, 356, 389–396. [Google Scholar] [CrossRef]
  51. Chen, Z.; Sun, R.; Feng, S.; Wang, D.; Liu, H. Porosity-induced selective sensing of iodide in aqueous solution by a fluorescent imidazolium-based ionic porous framework. ACS Appl. Mater. Interfaces 2020, 12, 11104–11114. [Google Scholar] [PubMed]
Molecules 27 08547 sch001 550
Scheme 1. Illustration of the structure of UiO-66-(COOH)2 and Ag+@UiO-66-(COOH)2 as well as its iodide removal and off–on–off luminescent sensing mechanism.
Scheme 1. Illustration of the structure of UiO-66-(COOH)2 and Ag+@UiO-66-(COOH)2 as well as its iodide removal and off–on–off luminescent sensing mechanism.
Molecules 27 08547 sch001
Molecules 27 08547 g001 550
Figure 1. (a) Schematic illustration of the structure of UiO-66-(COOH)2. SEM morphology of (b) as-synthesized UiO-66-(COOH)2 and (c) Ag+@UiO-66-(COOH)2.
Figure 1. (a) Schematic illustration of the structure of UiO-66-(COOH)2. SEM morphology of (b) as-synthesized UiO-66-(COOH)2 and (c) Ag+@UiO-66-(COOH)2.
Molecules 27 08547 g001
Molecules 27 08547 g002 550
Figure 2. PXRD patterns of the simulated UiO-66, as-synthesized UiO-66-(COOH)2 and Ag+@UiO-66-(COOH)2.
Figure 2. PXRD patterns of the simulated UiO-66, as-synthesized UiO-66-(COOH)2 and Ag+@UiO-66-(COOH)2.
Molecules 27 08547 g002
Molecules 27 08547 g003 550
Figure 3. (a) The effect of contact time on the I− adsorption on Ag+@UiO-66-(COOH)2; (b) pseudo-second-order plots of the time-dependent I− adsorption.
Figure 3. (a) The effect of contact time on the I− adsorption on Ag+@UiO-66-(COOH)2; (b) pseudo-second-order plots of the time-dependent I− adsorption.
Molecules 27 08547 g003
Molecules 27 08547 g004 550
Figure 4. (a) Effect of initial concentration on the adsorption of I− by Ag+@UiO-66-(COOH)2; (b) Langmuir isotherm models for the adsorption of I−.
Figure 4. (a) Effect of initial concentration on the adsorption of I− by Ag+@UiO-66-(COOH)2; (b) Langmuir isotherm models for the adsorption of I−.
Molecules 27 08547 g004
Molecules 27 08547 g005 550
Figure 5. Relative uptake for I− anions in a binary mixture of competing anions.
Figure 5. Relative uptake for I− anions in a binary mixture of competing anions.
Molecules 27 08547 g005
Molecules 27 08547 g006 550
Figure 6. Emission spectra (a) and concentration dependence of the fluorescent intensity (b) of Ag+@UiO-66-(COOH)2 upon the addition of different concentrations of I−.
Figure 6. Emission spectra (a) and concentration dependence of the fluorescent intensity (b) of Ag+@UiO-66-(COOH)2 upon the addition of different concentrations of I−.
Molecules 27 08547 g006
Molecules 27 08547 g007 550
Figure 7. Changes of fluorescence intensity of Ag+@UiO-66-(COOH)2 towards various analytes (1 × 10−4 M) before I− addition (cyan column) and after I− (10 mg/L) addition (multi-color column).
Figure 7. Changes of fluorescence intensity of Ag+@UiO-66-(COOH)2 towards various analytes (1 × 10−4 M) before I− addition (cyan column) and after I− (10 mg/L) addition (multi-color column).
Molecules 27 08547 g007
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Zhang, J.; Yang, S.; Shao, L.; Ren, Y.; Jiang, J.; Wang, H.; Tang, H.; Deng, H.; Xia, T. Highly Sensitive Adsorption and Detection of Iodide in Aqueous Solution by a Post-Synthesized Zirconium-Organic Framework. Molecules 2022, 27, 8547. https://doi.org/10.3390/molecules27238547

AMA Style

Zhang J, Yang S, Shao L, Ren Y, Jiang J, Wang H, Tang H, Deng H, Xia T. Highly Sensitive Adsorption and Detection of Iodide in Aqueous Solution by a Post-Synthesized Zirconium-Organic Framework. Molecules. 2022; 27(23):8547. https://doi.org/10.3390/molecules27238547

Chicago/Turabian Style

Zhang, Jun, Shanli Yang, Lang Shao, Yiming Ren, Jiaolai Jiang, Huaisheng Wang, Hao Tang, Hui Deng, and Tifeng Xia. 2022. "Highly Sensitive Adsorption and Detection of Iodide in Aqueous Solution by a Post-Synthesized Zirconium-Organic Framework" Molecules 27, no. 23: 8547. https://doi.org/10.3390/molecules27238547

APA Style

Zhang, J., Yang, S., Shao, L., Ren, Y., Jiang, J., Wang, H., Tang, H., Deng, H., & Xia, T. (2022). Highly Sensitive Adsorption and Detection of Iodide in Aqueous Solution by a Post-Synthesized Zirconium-Organic Framework. Molecules, 27(23), 8547. https://doi.org/10.3390/molecules27238547

Article Metrics

Back to TopTop