Next Article in Journal
Acetic Acid Can Catalyze Succinimide Formation from Aspartic Acid Residues by a Concerted Bond Reorganization Mechanism: A Computational Study
Previous Article in Journal
Ponicidin Induces Apoptosis via JAK2 and STAT3 Signaling Pathways in Gastric Carcinoma
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
IJMS
Volume 16
Issue 1
10.3390/ijms16011590
ijms-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

TiO2 Immobilized on Manihot Carbon: Optimal Preparation and Evaluation of Its Activity in the Decomposition of Indigo Carmine

by
Cynthia M. Antonio-Cisneros
1,2,
Martín M. Dávila-Jiménez
3,
María P. Elizalde-González
1,* and
Esmeralda García-Díaz
1
1
Centro de Química -ICUAP, Universidad Autónoma de Puebla Ciudad Universitaria, Edif. H103, Puebla 72570, Mexico
2
Instituto de Agroingeniería, Universidad del Papaloapan, Campus Loma Bonita, Oaxaca 68400, Mexico
3
Facultad de Ciencias Químicas, Universidad Autónoma de Puebla, Ciudad Universitaria, Edif. H105, Puebla 72570, Mexico
*
Author to whom correspondence should be addressed.
Int. J. Mol. Sci. 2015, 16(1), 1590-1612; https://doi.org/10.3390/ijms16011590
Submission received: 27 October 2014 / Accepted: 31 December 2014 / Published: 12 January 2015
(This article belongs to the Section Materials Science)
Browse Figures
Versions Notes

Abstract

:
Applications of carbon-TiO2 materials have attracted attention in nanotechnology due to their synergic effects. We report the immobilization of TiO2 on carbon prepared from residues of the plant Manihot, commercial TiO2 and glycerol. The objective was to obtain a moderate loading of the anatase phase by preserving the carbonaceous external surface and micropores of the composite. Two preparation methods were compared, including mixing dry precursors and immobilization using a glycerol slurry. The evaluation of the micropore blocking was performed using nitrogen adsorption isotherms. The results indicated that it was possible to use Manihot residues and glycerol to prepare an anatase-containing material with a basic surface and a significant SBET value. The activities of the prepared materials were tested in a decomposition assay of indigo carmine. The TiO2/carbon eliminated nearly 100% of the dye under UV irradiation using the optimal conditions found by a Taguchi L4 orthogonal array considering the specific surface, temperature and initial concentration. The reaction was monitored by UV-Vis spectrophotometry and LC-ESI-(Qq)-TOF-MS, enabling the identification of some intermediates. No isatin-5-sulfonic acid was detected after a 60 min photocatalytic reaction, and three sulfonated aromatic amines, including 4-amino-3-hydroxybenzenesulfonic acid, 2-(2-amino-5-sulfophenyl)-2-oxoacetic acid and 2-amino-5-sulfobenzoic acid, were present in the reaction mixture.

Graphical Abstract

1. Introduction

Semiconductor photocatalytic processes are emerging as a water and wastewater treatment technology under the “zero waste” scheme [1]. Concerning semiconductors, TiO2 is the most important material in environmental purification systems due to its photoelectrochemical and photo-induced superhydrophilic properties, as reviewed by Ochiai and Fujishima [2]. Combinations of TiO2 and carbon represent interesting materials and are under active study [3]. The most extensively studied combinations include TiO2 nanoparticles coated with carbon, carbon impregnated with TiO2 and mechanical mixtures of TiO2 and carbon. Carbon-TiO2 materials are interesting because (a) the materials are more easily recovered after use in a wide range of applications [4] and (b) their texture [5] and pH [6] are different from those of the starting materials.
Applications of photocatalytic carbon-TiO2 have attracted widespread attention due to the decomposition activity of the material toward effluents [7]. Whereas carbon doping promotes band-gap narrowing, the presence of carbon in TiO2 samples promotes adsorption. A critical review by Lim clearly illustrated several of the practical issues surrounding the preparation of carbon-TiO2 composites [8]. These materials can be designed with carbon powders, fibers, nanotubes, fullerenes or graphene [3]. Noteworthy studies of Zhang et al. did not show any difference between the photoactivity displayed by composites containing different allotropic forms of carbon, both in gas and liquid phase degradations [9,10]. However, the different carbon-TiO2 systems enhance in a different way their photocatalytic activity through one or all of the three primary mechanisms: minimization of the electron-hole recombination rate, band gap tuning and improvement of adsorption sites [3]. Because we used a biomass carbonized at relatively low temperature, we have purposely confined the discussion to activated carbon. In most of the investigations where carbon-TiO2 materials have been prepared, the authors have preferred to use commercial activated carbon [7,11,12,13]. Research on the thermochemical conversion of biomass to develop the carbonaceous component of a carbon-TiO2 composite is limited.
Biomass, such as bamboo leaves [14], pine sawdust [15], maize corncob residues [16], canola hull [17] and corn straw powder [18], has been used as a carbon precursor to prepare powdered carbon-TiO2 materials via the mixing and hydrothermal procedure. The carbon-TiO2 ratios were 1:0.01 [17,18], 1:0.1 [14,15,17] and 1:2 [18], and the carbonization temperature in these studies varied over a broad range from 400 °C [14] to 800 °C [16,18]. Cordero et al. used Tabebuia pentaphylla wood to produce carbon for use in the presence of TiO2 particles in a photocatalytic experiment [19]. In this investigation, no carbon-TiO2 composite was actually prepared. However, aggregation of nanoparticles of TiO2 on the prepared carbon samples was observed. Interestingly, the photocatalytic activity upon photodegradation of 4-chlorophenol was correlated with the texture and surface chemistry of the activated carbon that was added. The immobilization of TiO2 particles onto solid supports has been a key technical strategy for a cost effective solid-liquid separation. In this sense, this work aims to use as support a carbon material obtained from a no cost agricultural waste. Furthermore, the use of a carbonaceous support is justified because it has been proven that the delocalized conjugated π-structures of carbon materials promote a rapid photoinduced charge separation and slow the charge recombination rate in electron-transfer processes [2].
The methods used to load TiO2 onto carbon include four possible procedures as follows: (i) mixing activated carbon with a previously prepared TiO2 powder; (ii) coating carbon with films of TiO2 precursors using sol-gel and hydrothermal techniques or chemical vapor deposition; (iii) mixing a carbon precursor with a TiO2 sol-gel and in situ one-step carbonization/calcination and (iv) combining a carbon precursor with finished TiO2 particles followed by carbonization. Depending on the nature of the precursor, methods (iii) and (iv) may involve two hydrophilic raw components or one hydrophobic component and one hydrophilic component. Processes (i) and (ii) require the creation of real contact between the hydrophobic and hydrophilic components of the composite. The use of an additive acting as an intermicellar liquid may stabilize one hydrophilic (TiO2) component and one hydrophobic (carbon) component. However, little is reported on the use of additives in the preparation of carbon-TiO2 composites. One of our goals was to develop a rapid method for the optimum immobilization of moderate amounts of the anatase-phase of TiO2 on carbon using thermal processing (at 800 °C) of Manihot residues with the aid of glycerol. This material is referred to as TiO2/carbon. In addition, we assessed the performance of the prepared materials by employing them for the photocatalytic decomposition of indigo carmine (IC).

2. Results and Discussion

2.1. Texture of the Composites Obtained from Dry Mixtures

The raw Manihot residues had an irregular elongated shape, which was retained in the carbonized samples. A preliminary trial consisted of mechanical dry mixing of the Manihot carbon C800 with TiO2 in a weight ratio 1:1. This corresponded to procedure (i) mentioned in the introduction. The resulting material exhibited a specific surface SBET of 345 m2·g−1, ~60% microporosity and an average pore diameter of 7.4 nm. However, the TiO2 particles were not permanently immobilized on the carbon surface. This observation led us to develop two different one-step preparation methods using raw residues according to procedure (iv). The two variants of the preparation method are shown in Figure 1.
Figure 2a shows the nitrogen adsorption isotherms of the sieved samples of the MT, MT-W and MT-G composites prepared by dry mixing by variant (a), as shown in n Figure 1. As a reference, the N2 adsorption isotherms of the Manihot carbon C800 and commercial TiO2 are shown in Figure 2b. Table 1 lists the texture parameters of the precursors (TiO2 and Manihot) and the carbon obtained at 800 °C using the vascular system of the Manihot stems.
Ijms 16 01590 g001 1024
Figure 1. General scheme depicting two preparation variants and labels of the materials prepared from the Manihot residues at 800 °C.
Figure 1. General scheme depicting two preparation variants and labels of the materials prepared from the Manihot residues at 800 °C.
Ijms 16 01590 g001
Ijms 16 01590 g002 1024
Figure 2. N2 adsorption (empty symbols) and desorption (filled symbols) isotherms at 77 K for (a) the materials prepared from dry mixtures of raw Manihot residues and TiO2 (variant (a) in Figure 1) and (b) Manihot carbon C800 (dp 0.25 mm) and the photocatalyst TiO2.
Figure 2. N2 adsorption (empty symbols) and desorption (filled symbols) isotherms at 77 K for (a) the materials prepared from dry mixtures of raw Manihot residues and TiO2 (variant (a) in Figure 1) and (b) Manihot carbon C800 (dp 0.25 mm) and the photocatalyst TiO2.
Ijms 16 01590 g002
Table
Table 1. Texture parameters of the precursors, carbon C800 and TiO2/C materials prepared in a 1:1 Manihot: TiO2 ratio by variant (a) as depicted in Figure 1, and the corresponding isotherms are shown in Figure 2.
Table 1. Texture parameters of the precursors, carbon C800 and TiO2/C materials prepared in a 1:1 Manihot: TiO2 ratio by variant (a) as depicted in Figure 1, and the corresponding isotherms are shown in Figure 2.
MaterialSpecific Surface (m2·g−1)Vμ, cm3·g−1Vtot, cm3·g−1Average Pore Diameter, nm
BETS0t (%)Set
PrecursorsTiO258---0.678-
raw Manihot72 a-----
CarbonC800449318 (71)1300.1600.2632.6
TiO2/CMT226100 (44)1260.0510.7126.9
MT-W493245 (50)2480.1250.6115.4
MT-G8724 (28)630.0130.35317.6
a measured by the adsorption of methylene blue from solution.
A comparison of the texture parameters in Table 1 demonstrates the effect of the addition of water or glycerol on the dry Manihot + TiO2 mixture. The specific surface area obtained for composite MT (SBET = 226 m2·g−1) increased when the sample was prepared in the presence of water (i.e., MT-W, SBET = 493 m2·g−1) and decreased in the presence of glycerol (SBET = 87 m2·g−1). A comparison of the micropore surface S0t (318 m2·g−1) of carbon C800 with that of MT-G (24 m2·g−1) indicated that glycerol partially inhibited micropore development because the contribution of the micropore surface S0t to the total specific surface decreased from 71% in C800 to 28% in MT-G.
Without glycerol, the TiO2 nanoparticles settled on the raw Manihot residues prior to carbonization in MT and MT-W. The contribution of S0t to SBET was similar (i.e., 44% and 50% in MT and MT-W, respectively). Because the values of microporosity were lower than those in carbon C800 (71%), the TiO2 nanoparticles also hindered the microporosity to some extent.
The prepared composites substantially exceeded the SBET of bare TiO2 (58 m2·g−1). However, the total pore volume Vtot, measured at p/p0 = 0.99 for the MT and MT-W samples was similar to that of the precursor TiO2 (0.678 cm3·g−1). The total pore volume of sample MT-G (0.353 cm3·g−1), which was prepared with glycerol, was comparable to that of carbon C800 (0.263 cm3·g−1). However, the glycerol prevented micropore formation, and the external surface provided the greatest contribution (72%) to the magnitude of the specific surface in MT-G. Nevertheless, the composites prepared by this methodology can be regarded as mesoporous materials with a broad pore size distribution because the average pore width varies within 5.4 ≤ Dp ≤ 17.6 nm (see Table 1).
The raw Manihot residues exhibited hydrophilic and nearly neutral characteristics with a pHpzc of 6.7 [20], which is very close to the pHpzc of anatase (6.5) [21]. Therefore, a certain chemical affinity can be expected between both materials.
However, the composites prepared using the dry mixture approach (variant (a) in Figure 1) did not exhibit a satisfactorily homogeneous aspect when they were observed under the microscope, which may be due to a “like agglomerates like” effect (i.e., the attraction of TiO2 to TiO2 and carbon to carbon) during mixing. Furthermore, the addition of water in MT-W or glycerol in MT-G affected the texture properties of the composites very differently. Because the strongest effect occurred in the micropore volume of MT-G, the glycerol additive aids in the formation of a homogeneous mixture of raw Manihot residues and TiO2 and favors the development of the external surface (up to 72% in MT-G). Carbonization of glycerol itself yields a smooth carbonaceous surface and hinders the TiO2 nanoparticles from being trapped in the micropores, which improves exposure to irradiation.

2.2. Morphology and Texture of the Composites Obtained from Glycerol Slurries

All of the prepared TiO2/carbon composites were black, and their morphologies were similar. Figure 3 shows the SEM images of the samples prepared by mixing the TiO2 slurry with the raw residues in glycerol suspensions (variant (b) in Figure 1): MT-G05 (a), MT-G5 (b) and MT-G50 (c). The incorporation of the TiO2 nanoparticles or aggregates into the striae of the Manihot carbon trunks was possible. The images indicated immobilization of TiO2 agglomerates on the surface of MT-G5 as well as the presence of a free carbonaceous surface. The surface of composite MT-G50 (Figure 3c), which contained 10-fold more TiO2, exhibited a crust of TiO2 covering the carbonaceous surface to a greater extent. For this material, we could expect near semiconductor behavior.
Ijms 16 01590 g003 1024
Figure 3. Scanning electron microscopy images of the TiO2/carbon composites (left) and EDS spectra obtained at magnification 200× for semi-quantitative analysis (right). MT-G05 (a); MT-G5 (b) and MT-G50 (c).
Figure 3. Scanning electron microscopy images of the TiO2/carbon composites (left) and EDS spectra obtained at magnification 200× for semi-quantitative analysis (right). MT-G05 (a); MT-G5 (b) and MT-G50 (c).
Ijms 16 01590 g003
The surface analysis by SEM revealed that MT-G05 was comprised of TiO2 immobilized aggregates (<1 μm in size), and MT-G5 contained irregular aggregates ~5 μm in size. Sreethawong et al. also used glycerol as a mesopore-controlling agent and obtained clusters of uniform TiO2 nanoparticles, which is in agreement with our results [22].
The loaded amount of TiO2 influenced the textural characteristics of the composites prepared by mixing glycerol slurries, as demonstrated by measuring the N2 adsorption–desorption isotherms. The specific surface area (SBET) and other textural parameters of the composites prepared by variant (b) (see Figure 1) are listed in Table 2. The nitrogen adsorption isotherms of samples MT-G05 and MT-G5 were significantly different from the typical isotherm for the commercial nonporous anatase TiO2 (Figure 4). Remarkably, the curves of both composites with low and medium TiO2 loading were located below the isotherm corresponding to Manihot carbon C800 prepared at the same temperature. The decrease (see Table 2) in the magnitude of SBET (244 ± 22 m2·g−1 for low TiO2 loading and 203 ± 9 m2·g−1 for medium TiO2 loading) with respect to C800 (449 m2·g−1) was a direct result of the blockage of micropores by glycerol and TiO2 nanoparticles in MT-G05 and agglomerates in MT-G5.
Ijms 16 01590 g004 1024
Figure 4. N2 adsorption (empty symbols)-desorption (filled symbols) isotherms at 77 K for the composites prepared by mixing slurries of the precursors in glycerol (variant (b) in Figure 1) using different residue: TiO2 ratios.
Figure 4. N2 adsorption (empty symbols)-desorption (filled symbols) isotherms at 77 K for the composites prepared by mixing slurries of the precursors in glycerol (variant (b) in Figure 1) using different residue: TiO2 ratios.
Ijms 16 01590 g004
Table
Table 2. Specific surface SBET, micropore S0t, external surface Set and point of zero charge pHpzc of the TiO2/C materials prepared by mixing the precursors in a glycerol suspension in different Manihot: TiO2 ratios according to variant (b) in Figure 1, and the corresponding isotherms are shown in Figure 4.
Table 2. Specific surface SBET, micropore S0t, external surface Set and point of zero charge pHpzc of the TiO2/C materials prepared by mixing the precursors in a glycerol suspension in different Manihot: TiO2 ratios according to variant (b) in Figure 1, and the corresponding isotherms are shown in Figure 4.
CompositeManihot: TiO2 RatioSpecific Surface, m2·g−1Vμ, cm3·g−1Vtot, cm3·g−1D, nmpHpzc
BETS0tSet
MT-G051:0.52441181260.0600.2043.611.4
MT-G51:5203104990.0530.1783.8 7.7
MT-G501:5040-40-0.15826.76.0
The nitrogen adsorption isotherm (lowest curve in Figure 4) for sample MT-G50 with a maximum TiO2 load was in agreement with the isotherm of bare commercial TiO2 (curve without points in Figure 4). Correspondingly, the SBET of composite MT-G50 (40 ± 3 m2·g−1) was similar to that of TiO2 (58 m2·g−1).
As expected, composites MT-G05 and MT-G5 (Figure 4) exhibited a type IIb hybrid isotherm. The hybrid isotherm was consistent with a combination of adsorption isotherms corresponding to the textural characteristics of two materials with different adsorption isotherms (i.e., carbon (type I) and TiO2 (type II)). The isotherms of these two composites exhibited a low-pressure hysteresis (LPH), which has been observed for some microporous adsorbents. The pore size distribution of composite MT-G50 (not shown here) indicated macropores.
Samples MT-G05 and MT-G5 exhibited mesoporosity with Dp > 2 nm, micropores with diameters ≤2 nm and a similar micropore volume (see Table 2) due to partial blockage of the micropores. The micropore volumes of the composites with reduced TiO2 content were similar, and in composite MT-G50, the micropores disappeared (i.e., Vμ = 0.160 cm3·g−1 in carbon C800, Vμ = 0.060 cm3·g−1 in MT-G05 and Vμ = 0.053 cm3·g−1 in MT-G5). However, both composites exhibited a micropore/mesopore ratio of ~50%. Velasco et al. demonstrated that immobilization of TiO2 only occurred on the outer surface of the carbon when they prepared their carbon-TiO2 composite by infiltration of TiO2 nanoparticles into commercial carbon [23]. The S0t and Set values of our TiO2/carbon samples indicated no substantial difference in the contribution of the micropores to the magnitude of the specific surface area when the material was prepared with 0.5 and 5 mg of TiO2. Notably, in solid-liquid photocatalytic reactions, large reactants do not diffuse into micropores. However, the creation of micropores directly leads to an increase in the specific surface area. As shown in our work, micropores and mesopores coexist, and their ratio can be affected by the immobilized TiO2. The evidence for micropore (Dp < 2 nm) blocking by TiO2 nanoparticles (dp < 50 nm) complements Velasco’s et al. demonstration of the immobilization of TiO2 on the outer surface of commercial carbon [23]. Furthermore, our results indicate that in addition to pore blocking, inhibition of pore formation also occurs because the formed TiO2 nanoparticles settled on the raw Manihot residues prior to carbonization, as described in this and the previous section.
Composites containing more than 20% TiO2 have been reported to exhibit operational problems, and nearly 100% of the phenol from the aqueous solution was removed [23]. In comparison, the TiO2 loadings used in our work exhibited excellent wettability and could be separated from the solution by precipitation without additional operations.
The achievement of a high surface area is a challenge in the preparation of a crystalline TiO2-containing photocatalyst, which is primarily due to the Degussa TiO2 nanoparticles being non-porous. Notably, composites MT-G05 and MT-G5 exhibited SBET magnitudes much higher than that of TiO2 and approximately 50% microporosity. Despite the considerable number of publications on the preparation of TiO2 loaded carbon, the reproducibility of the textural characteristics of the resulting composites has never been reported. In the current work, four lots of each composite were prepared, and their specific surface areas, which are shown in Table 2, represent mean values with STD ≤ 9%. Based on the known error in the BET measurements, these results indicate the acceptable reproducibility of the preparation method. As previously reported [19], the photocatalytic activity is also related to the texture of the material. We succeeded in preparing two composites (i.e., MT-G05 and MT-G5) that exhibit similar textural properties but different TiO2 loads. This fact has economic implications, and one cannot rule out that a low population of well-dispersed TiO2 nanoparticles can perform differently from TiO2 clusters (compare Figure 3a,b). The photocatalytic performance of the samples prepared by this methodology will be discussed below.

2.3. Surface Acidity of the TiO2/Carbon Samples Obtained from Glycerol Suspensions

Activated carbon is an amphoteric material with acidic and basic sites on its surface. The point of zero charge (pHpzc) (see Table 2) differs depending on the TiO2/carbon ratio. At 800 °C, we achieved sa basic carbon with a pHpzc value of 11.4. Table 2 indicates that the low concentration of TiO2 in sample MT-G05 produced pHpzc values identical to the corresponding carbon C800. Medium and high TiO2 loadings in composites MT-G5 and MT-G50 reflected the influence of TiO2 on the acidity of the composite (pHpzc = 7.7 and 6.0). This result demonstrates one of the features of a composite (i.e., a different acidity with respect to the composite constituents).
The surface acidity is rarely discussed in the characterization of carbon-TiO2 composites. Lim et al. remarked that high values of pHpzc from carbons prepared at high temperatures (H-type activated carbon) increased electron transfer between carbon and TiO2 [8]. Velasco et al. observed a small change in the pHpzc of their composite [23]. In contrast, the pHpzc of the materials prepared by Matos et al. varied due to the carbon preparation parameters [6]. In addition, these authors demonstrated that the pHpzc of the surface influenced the photocatalytic degradation of 4-chlorophenol more than the texture, reactant adsorption mechanism and intermediate product distribution [24]. Therefore, we might expect a distinct behavior in acidic/basic media and different performances of our composites in photocatalytic experiments, which will be demonstrated later.

2.4. Crystal Structure of TiO2 Immobilized on Manihot Carbon and the Structure of the Carbon

The phase content of P25 Degussa TiO2 is not consistent, and it may vary from batch to batch. Nevertheless, P25 Degussa TiO2 is a mixture of anatase and rutile phases with a predominance of anatase (>80%). Figure 5a shows the XRD pattern of the MT-G5 composite. Despite the low intensity of the peaks, the persistence of the anatase phase was observed (PDF 96-900-9087 from the Crystallography Open Database). The series of composites prepared in this work exhibited similar diffractograms with the main peak corresponding to the (101) plane of anatase at approximately 2θ = 25.32°.
Ijms 16 01590 g005 1024
Figure 5. (a) X-ray powder diffraction patterns of sample MT-G5 showing the characteristic planes of anatase (A); (b) Micro-Raman spectra at five different sites of MT-G05. * = sample holder.
Figure 5. (a) X-ray powder diffraction patterns of sample MT-G5 showing the characteristic planes of anatase (A); (b) Micro-Raman spectra at five different sites of MT-G05. * = sample holder.
Ijms 16 01590 g005
The phase transition from anatase to rutile occurs at approximately 600 °C, but in the materials prepared at 800 °C, this phase transition did not occur. Here, the presence of glycerol may link TiO2 nuclei via hydrogen bonds and stabilize the anatase phase [25]. Another possible explanation is that the carbon formed in the vicinity of TiO2 suppresses the phase transformation at high temperature [26].
A widely accepted notion is that the anatase phase is more active than the rutile phase [27], although there are studies reporting the effectiveness of mixtures with different anatase-rutile ratios [18]. However, both phases are used in the photodegradation of pollutants. The content of the rutile phase in Degussa TiO2 can be observed as a very small peak at 2θ = 27.4° corresponding to the (110) plane. This peak is the most intense peak for the rutile phase, and this peak is less intense than the most intense peak for anatase in the Degussa TiO2. The low intensity of the peak for rutile in the diffractograms of the prepared composites may be due to the low loading of TiO2. In addition, the glycerol may produce linkages between the TiO2 nanoparticles and the raw Manihot residues creating a stabilizing effect against the transition of anatase to rutile during heating. If this linkage exists, this effect should occur before glycerol decomposes at 246 °C [28]. In comparison, the vascular residues of Manihot are completely decomposed at 400 °C [20].
For the organic residues, the carbonization temperature (800 °C) was low to ensure complete graphitization in the TiO2/carbon samples. Therefore, the peak at ca. 2θ = 25° cannot be assigned to the reflections of the (002) plane of two-dimensional graphite and was unequivocally attributed to anatase. Figure 5b shows the Raman spectra resulting from five micro-Raman measurements. These spectra contain the defect-derived D (1375 cm−1) and the graphite structure-derived G (1550 cm−1) bands, which are characteristic of carbonaceous materials that are specific for each material. The prepared composites exhibited a large D-band peak (ID/IG ~ 2.7), indicating an amorphous carbon content of approximately 75%. Because only slightly lower values were obtained in the absence of glycerol (ID/IG ~ 2.4 and the amorphism ID/(ID + IG) ~ 70%), this additive did not substantially contribute to the amorphism of the carbonaceous component in the TiO2/carbon materials.

2.5. Adsorption of IC

Figure 6 shows the isotherms describing the adsorption of IC onto the raw Manihot residues, carbon sample C800 and commercial TiO2 without any adjustment. The Degussa TiO2 used in this work exhibited a saturation capacity of 0.20 molecules·nm−2 compared to 0.13 molecules·nm−2 reported by Vautier et al. [29] for an adsorbent dose of 2.5 mg·cm−3. Alahiane et al. [30] reported a saturation capacity of 0.21 molecules·nm−2 for an adsorbent dose of 1.0 mg·dm−3. Carbon C800 exhibited a slightly higher saturation capacity of 0.27 molecules·nm−2. The corresponding Langmuir constant (kL) was calculated by the non-linear form of the Langmuir equation, and these constants were 189 L·mg−1 on the raw residue, 0.4 L·mg−1 on TiO2 and 256 L·mg−1 on carbon C800.
Once the relative adsorption affinity of IC on the semiconductor TiO2 and carbon was determined, we explored the acidity/basicity of the drained surface immediately after adsorption. The dotted line in Figure 6 indicates that there is no variation in the pH, within the experimental error, with the IC concentration. The pH on the surface of the wet composites was measured after the adsorption process. The pH of the TiO2 surface remained near the values of the IC solution and near the pHpzc of TiO2 at all of the concentrations. In contrast, the pH of the carbon C800 surface decreased from a pHpzc value of 11.7 to 9.5 because the dye acted as a neutralizing agent. As previously discussed, the results in Figure 6b indicate that the pHpzc of MT-G05 resembles that of carbon C800, the pHpzc of MT-G50 resembles that of Degussa TiO2, and the pHpzc of MT-G5 is midway between carbon and TiO2. The results in Figure 6b suggest that the adsorption of IC (pKa 12.2) in basic medium (pH > 8) should only occur on composite MT-G05 because pH ˂ pHpzc. In an acidic solution (pH ˂ 6), the adsorption occurs on all the composites because pH ˂ pHpzc.
Ijms 16 01590 g006 1024
Figure 6. (a) Adsorption isotherms of IC on raw Manihot residue, TiO2 and carbon C800 at 25 °C. Adsorbent dose: 33.3 mg·cm−3; (b) Variation in the pH of the IC solution as well as of the surface of TiO2 and the carbon C800 after adsorption of different concentrations of IC. The levels of pHpzc of the materials are denoted with dashed lines.
Figure 6. (a) Adsorption isotherms of IC on raw Manihot residue, TiO2 and carbon C800 at 25 °C. Adsorbent dose: 33.3 mg·cm−3; (b) Variation in the pH of the IC solution as well as of the surface of TiO2 and the carbon C800 after adsorption of different concentrations of IC. The levels of pHpzc of the materials are denoted with dashed lines.
Ijms 16 01590 g006

2.6. Photocatalytic Decomposition of IC

TiO2/carbon materials can exhibit enhanced photoactivity because the synergistic effect that causes a rapid photoinduced charge separation and a diminution of the recombination of the electron-hole pairs in TiO2. To better estimate the photoactivity of a series of samples, photoelectrochemical analysis offers an excellent opportunity to assess differences in the transfer of photogenerated electron-hole pairs from TiO2. Zhang et al. demonstrated that the higher and more stable photocurrent of the sample, the higher photoactivity and they showed the importance of the carriers lifetime in graphene-TiO2 [31].
The photocatalytic performance test of carbon-TiO2 materials produced using biomass as carbon source has involved methylene blue [14], Rhodamine B [15], basic red 18 and basic red 46 [17]. The decay of the TOC [14] and COD [15] values of the dye solutions was faster on the carbon-TiO2 materials than on TiO2. However, this result could be related with an adsorption effect. In contrast, Mahmoodi et al. demonstrated that two azo dyes degraded faster using TiO2 immobilized on activated carbon in comparison to TiO2 [17]. Total mineralization occurred after 80–100 min irradiation at 200–280 nm. One of the purposes of the current paper was to evaluate the performance of our TiO2/carbon materials for the photocatalytic decomposition of IC. Research conducted for this purpose has been reported by Subramani et al. [32] by mixing both commercial TiO2 and carbon (SBET 1025 m2·g−1) in HNO3 followed by heating in an autoclave at 150 °C. Recently, some novel visible-light photocatalytic materials have also been tested for photodegradation of IC [33]. However, in contrast to those doped semiconductors, we investigated the simple preparation of a TiO2/carbon composite to observe the adsorption and photocatalysis phenomena during the removal of IC.
Figure 7 shows the concentration decay of the irradiated IC solutions at 254 nm after photolysis (Figure 7a) and photocatalysis (Figure 7b). As expected [34], IC decomposed by photolysis and more readily in air atmosphere due to the presence of oxygen (Figure 7a). Surprisingly, the prepared TiO2/C MT-G50 sample exhibited superior elimination efficiency compared to TiO2 (Figure 7b) due to the adsorption capacity of the uncovered segments of the carbonaceous support in the composite.
As shown in Figure 7b, carbon C800 completely adsorbs the dye after 40 min of contact. In addition, the carbon C800 reached saturation with 14 mg·g−1 of IC, and the specific surface decreased from 434–346 m2·g−1 for the saturated adsorbent [35]. However, the adsorption of IC on C800 was reversible because after contact with water, the original magnitude of SBET was reestablished (i.e., 437 m2·g−1).
Ijms 16 01590 g007 1024
Figure 7. Kinetic curves of (a) photolysis at 50 °C in a nitrogen and air atmosphere and (b) photocatalysis of the dye IC at 50 °C in an air atmosphere. Adsorption experiment of IC on MT-G50 in the dark.
Figure 7. Kinetic curves of (a) photolysis at 50 °C in a nitrogen and air atmosphere and (b) photocatalysis of the dye IC at 50 °C in an air atmosphere. Adsorption experiment of IC on MT-G50 in the dark.
Ijms 16 01590 g007
Since the study of Vautier et al. was reported, the photocatalytic degradation of IC as model indigoid dye has been studied extensively via UV irradiation [29]. The most widely used photocatalysts are TiO2, doped TiO2, and TiO2 containing composites. Barka et al. [36] demonstrated that the apparent degradation rate constant of IC was affected by the temperature, concentration, pH, and previous adsorption in the dark. After demonstration of the adsorption affinity between IC and the constituents of our TiO2/carbon composites, the photocatalytic degradation of the dye under different conditions was explored. Figure 8 shows the decrease in the concentration of IC as a function of time at different temperatures and pH values for IC initial concentrations varying by two orders of magnitude using the photocatalysis conditions provided in the experimental section. The study of other factors influencing the photodegradation process, such as the volume of the IC solution and the mass of the photocatalyst, were excluded because they involve the design of the photoreactor. By comparing the results in Figure 8a with those in Figure 8b,c, we observed that an extreme initial concentration of 3000 mg·dm−3 exhibited the slowest degradation rate independent of the composite and temperature. Despite the large differences in the initial concentrations used by us and other authors [31,36,37], the effect was similar. The kinetic curves in Figure 8a obeyed a second order rate equation, and the rate constants were 0.5 × 10−2 for MT-G5 at 25 °C and 1.5 × 10−2 g·mg−1·h−1 for MT-G50 at 50 °C. Using a concentration of 300 mg·dm−3 (Figure 8b), 90% degradation was achieved after 60 min of irradiation, and this degradation occurred more readily at 50 °C. The rate constant (k2) at 25 °C was 8.4 × 10−2 g·mg−1·h−1 using MT-G50 and 0.5 × 10−2 g·mg−1·h−1 using MT-G5. Alahiane et al. observed a first order degradation rate of 2 × 10−2 min−1 for 20 mg·dm−3 IC using Degussa TiO2 [30], and Barka et al. obtained a first rate constant of 3 × 10−2 min−1 using fibers coated with PC500 TiO2 [36]. However, Barka et al. reported an unsatisfactory first order kinetic behavior at higher initial concentrations and suggested a competing adsorption/degradation mechanism.
Ijms 16 01590 g008 1024
Figure 8. Photocatalytic decomposition of the IC dye with three concentration levels at natural pH and different temperatures (a,b) as well as at 25 °C in basic and acidic solutions (c) using two composites in an air atmosphere.
Figure 8. Photocatalytic decomposition of the IC dye with three concentration levels at natural pH and different temperatures (a,b) as well as at 25 °C in basic and acidic solutions (c) using two composites in an air atmosphere.
Ijms 16 01590 g008
The results in Figure 8c indicate that IC degradation occurred slowly at pH 10 using composite MT-G50 with a pHpzc of 6.0, (see Figure 6b) where the surface is negatively charged resulting in repulsion of the dye molecule. In contrast, a pH of 4.0 favored the attraction between the positively charged surface and the dye, as discussed in the previous section. These results agree with those obtained for the adsorption of IC on TiO2 PC500 [36].
In addition, we decided to optimize the photodegradation of IC using the prepared TiO2/carbon materials. Abaamrane et al. reported on the optimal decolorization of IC using TiO2/UV and the response surface methodology [37]. In the current work, we used the Taguchi method [38] for the evaluation of the color removal produced by IC through a small number of trials. This technique included transformation to a signal to noise ratio (S/N), which is a measure of the variations observed. An L4 orthogonal array was applied, and the three factors selected included the specific surface (40 m2·g−1 in MT-G50 and 203 m2·g−1 in MT-G5), initial concentration (30 and 300 mg·dm−3) and temperature (25 and 50 °C). The pH of the solution was maintained at 4 for all of the experiments because (i) composite MT-G05 was excluded due to a pHpzc value that was very close to that of its precursor carbon C800. The removal involves both adsorption and photocatalysis occurring on prepared composites MT-G5 and MT-G50 with different TiO2 loadings, the representative factor describing their whole removal capacity was the specific surface, which was determined to be 203 m2·g−1 for MT-G5 and 40 m2·g−1 for MT-G50; (ii) As demonstrated in Figure 8c, the performance of MT-G50 at a pH of 4 was much better than that at a pH of 10. Therefore, according to Figure 6b, the selected materials were used in acidic solutions of the IC dye, and the pH was not used as a factor in the optimization study. The array of experimental factors with two levels and the results are reported in Table 3. The extent of decolorization varied from 10%–99% in the different combinations.
Table
Table 3. Experimental L4 Taguchi orthogonal array with the color percentage removal as an output variable. Factors and levels: A: SBET (40, 203 m2·g−1); B: concentration (30, 300 mg·dm−3); C: temperature (25, 50 °C).
Table 3. Experimental L4 Taguchi orthogonal array with the color percentage removal as an output variable. Factors and levels: A: SBET (40, 203 m2·g−1); B: concentration (30, 300 mg·dm−3); C: temperature (25, 50 °C).
Factor LevelsColor Removal, %S/NRemoved TOC, %
ABCExper. 1Exper. 2
11110161861
12299984055
21294943954
22140373148
The array indicated that the temperature was the most influential factor (S/N = 40), and an experiment to confirm these results was carried using the optimal level of each factor (combination A2,B2,C2), and this experiment produced 95% removal (T = 50 °C, initial concentration = 300 mg·dm−3 and specific surface = 203 m2·g−1 of the composite MT-G5). The specific surface influenced the removal of the dye rather than the amount of TiO2 loaded on the materials. Regarding the decolorization, the elimination of the total organic carbon was slightly lower for a high initial concentration. For example (see last column in Table 3), a 55% TOC removal was observed using an initial concentration of 300 mg·dm−3 compared to a 61% TOC removal using 30 mg·dm−3. The inconsistency between the high removal of color (e.g., 94% in the combination A2,B1,C2) and the 54% removal of TOC is due to the formation of uncolored products, and these products identification will be discussed in the next section.

2.7. Identification of the Photodegradation Products of IC

For product identification, we monitored selected aliquots of the IC solutions subjected to the photocatalytic experiments. Figure 9 shows the LC-MS chromatograms of the stock solution of IC and one reaction mixture. Table 4 lists the retention times, exact masses of the molecular ions (m/z), error values (Δm/z), and the proposed structure of the products detected in Figure 9.
Table
Table 4. Retention time and possible structures identified by LC-ESI-Qq-TOF-MS as products of IC during the photocatalytic reaction at 254 nm. The references reporting the same compound are given in brackets.
Table 4. Retention time and possible structures identified by LC-ESI-Qq-TOF-MS as products of IC during the photocatalytic reaction at 254 nm. The references reporting the same compound are given in brackets.
Proposed structure Ijms 16 01590 i001 Ijms 16 01590 i002 Ijms 16 01590 i003
Name4-amino-3-hydroxybenzenesulfonic acid2-(2-amino-5-sulfophenyl)-2-oxoacetic acid2-amino-5-sulfobenzoic acid
Peak nr.12 [39,40,41]3 [39,40]
tR (min)2.002.633.20
FormulaC6H7NO4SC8H7NO6SC7H7NO5S
m/zexper188.0032243.9924215.9981
m/zcalc188.0023243.9921215.9972
Δm4.791.234.17
Proposed structure Ijms 16 01590 i004 Ijms 16 01590 i005 Ijms 16 01590 i006
Name1-hydroxy-3,4-dioxo-3,4-dihydro-1H-benzo[c][1,2]oxazine-6-sulfonic acid2-(3-oxo-6-sulfo-3H-indol-2-yl)benzo[d]oxazole-6-sulfonic acid(E)-3,3’-dioxo-[2,2’-biindo-linylidene]-5,5’-disulfonic acid
Peak nr.45IC
tR (min)4.9310.813.23
FormulaC8H5NO7SC15H8N2 O8S2C16H10N2 O8S2
m/zexper257.9717406.9653420.9817
m/zcalc257.9714407.9649420.9806
Δm1.160.982.61
Ijms 16 01590 g009 1024
Figure 9. LC-MS chromatogram of the stock solution of IC (300 mg·dm−3) and a selected reaction mixture after 60 min of photocatalytic reaction using composite MT-G5 (200 m2·g−1) at a pH of 10 and 15 °C. The peak numbering is shown in Table 4.
Figure 9. LC-MS chromatogram of the stock solution of IC (300 mg·dm−3) and a selected reaction mixture after 60 min of photocatalytic reaction using composite MT-G5 (200 m2·g−1) at a pH of 10 and 15 °C. The peak numbering is shown in Table 4.
Ijms 16 01590 g009
At least 6 new peaks eluted prior to the appearance of the dye peak in the aliquot chromatogram, and all of cases carried out under the Taguchi conditions exhibited the same products in different proportions. The mass error accuracy of the proposed structures was less than 5 ppm. In addition, the molecular ions with m/z 244 (peak 2) and 216 (peak 3) are the most abundant products and coincide with the compounds formed by photocatalysis on SnO2 [39] and photoelectrocatalysis on Ti/TiO2/WO3 electrodes [40]. Interestingly, under visible-light irradiation, the ZnBiSbO4 photocatalyst produced 2-amino benzoic acid, which is the non-sulfonated form of compound 2 in Table 4 [42]. Electrochemical [43] and biological degradation processes [41] have also been reported to produce the aromatic compound isatin-5-sulfonic acid (mass 226) as an important degradation product of IC. We did not detect this product from the oxidative breaking of the indigoid C=C bond under any experimental condition. In contrast, we identified 2-(2-amino-5-sulfophenyl)-2-oxoacetic acid (peak 2, m/z 243.9924), which easily forms from isatin-5-sulfonic acid by addition of H2O [44].
In addition to the sulfonated amines (peaks 1–3 in Table 4) bearing only one phenyl ring, the structures proposed for two of the other products (i.e., peaks 4 and 5 in Figure 9) are given in Table 4. The oxazine compound (peak 4), which has not been previously reported, was confirmed by MS/MS yielding the following product ions: 194 [258-SO2]−, 178 [258-SO3]−, 160 [258-H2SO4]−, 150 [258-C6H4O2]−, 133 [258-H3O5S]−, 123 [258-CHO5S]−, and 80 [258-C8H4O4N]−.

3. Experimental Section

3.1. Materials

Aeroxide P25 titanium oxide (batch number 1036070711; Degussa, Parsippany, NJ, USA) and glycerol (GR, 87%; Merck, Darmstadt, Germany) were used as the starting reagents. The average particle size certified by the producer was 25 nm. The residues obtained from the vascular system of Manihot stems have previously been thoroughly characterized by our group [20] and were used with a constant moisture value of 50% ± 4%. Indigo carmine (C.I. 73015) was purchased from Sigma-Aldrich (St. Louis, MO, USA).

3.2. Samples Preparation

The yield of vascular system residues after removal of the rind and pith was 55% weight from the Manihot stems. The residues were passed through a sieve to obtain a particle size of 0.45 mm. The particles density was 0.1 g·cm−3. Two variants of the preparation method were used: (a) Raw Manihot residues were mixed manually with dry commercial TiO2 (1:1 weight ratio) for subsequent wetting with water or glycerol (10 cm3) to produce samples MT, MT-W and MT-G; and (b) a glycerol slurry of raw Manihot residues was mixed with an aqueous suspension of commercial TiO2 for subsequent carbonization to fabricate samples MT-G05, MT-G5 and MT-G50. The composites of this series were prepared using the raw Manihot residues, water, glycerol and TiO2 nanoparticles in different ratios. Slurries of different quantities of TiO2 in 10 cm3 of water were added to a suspension of 10 g of the raw Manihot residues in 10 cm3 of glycerol for the different composites and stirred. The mass of the residues was obtained by considering the carbon yield, which was 25% by weight from the raw Manihot residues. The resulting homogeneous suspensions were maintained in a combustion boat at room temperature for 24 h. A horizontal tubular furnace (Carbolite, Ubstadt-Weiher, Germany) with a quartz tube was used to heat the composites from room temperature to 800 °C. The temperature regime was designed according to the thermal behavior of the residues, as reported in our previous publication [20]. This regime consisted of two heating ramps involving heating from room temperature to 50 °C at 4 °C·min−1, holding at 50 °C for 1 h and heating from 50 to 800 °C at 4 °C·min−1. The materials were maintained at the maximum temperature in the carbonization atmosphere for 4 h. Then, the oven was cooled to room temperature. The sample labels correspond to the carbon: TiO2 weight ratios and the use of water (W) or glycerol (G), as shown in the scheme in Figure 1.

3.3. Characterization of the Materials

The morphology of the samples was determined using a JEOL JSM 6610 LV scanning electron microscope (SEM) (Peabody, MA, USA). The EDS analysis was performed with a microprobe Quest Noran sonde coupled to the microscope. The micrographs were recorded at 15 kV, and the samples were prepared by gold sputtering.
The BET surface area was measured by nitrogen adsorption at 77 K using an Autosorb-1 instrument from Quantachrome (Boyton Beach, FL, USA) after outgassing at 573 K for 24 h. The specific surface area was calculated using the Brunauer–Emmett–Teller (BET) equation. The extent of microporosity and mesoporosity was calculated using the V-t method and the micropore volume obtained from the nitrogen adsorption isotherms. All of the nitrogen adsorption data were evaluated according to standard gas adsorption research procedures. The reproducibility of the preparation of several lots was tested by measuring 11 adsorbed volumes in the range 5 × 10−2 ≤ p/p0 ≤ 3 × 10−1 and applying the BET equation.
The pH of the point of zero charge (pHpzc) of the raw residue and the carbon was measured by potentiometric titration. For this purpose, 10 mg of the residue particles was stirred for 24 h in 3 cm3 of solutions with different pHinitial. Then, the final pH was measured with a Titrando Metrohm and plotted as a function of pHinitial, and the pHpzc was determined as the point where pHfinal = pHinitial. For the TiO2-carbon composites, the pHpzc values were determined according to the method of potentiometric mass titration [45].
X-ray diffraction (XRD) measurements were carried out using a D8 Advance diffractometer from Bruker AXS (Karlsruhe, Germany) with CuKα1 radiation (α = 1.5406 Å). The data were collected over a 2θ range of 10°–70° with a step size of 0.026° and a measurement time of 43.2 s/step. The micro-Raman spectra were measured using a high-resolution dispersive Jobin Yvon-Horiba (Villeneuve d’Ascq, France) LabRAM HR model spectrophotometer equipped with a 632.8 nm (17 mW) He-Ne laser and a Nikon BX41 microscope with a 100× objective and a resolution of 1 cm−1.

3.4. Adsorption of IC from Aqueous Solution

Adsorption tests were performed at 25 °C in thermostated batch experiments. The stem residues (dp 0.125 mm), carbon, and TiO2 were dried for 24 h at 75 °C. Then, 50 mg of each material was weighed into polycarbonate cylindrical cells with a lid and placed in contact with 1.5 cm3 of an IC solution with concentrations in the range of 100–1500 for the raw residues and 100–3000 mg·dm−3 for TiO2 and carbon C800. The pH was not adjusted and was measured to be 6.0 in deionized water. The solution that resulted from the adsorption equilibrium obtained after 24 h was separated from the exhausted adsorbent and centrifuged (12,000 rpm) followed by analysis with a UV-Vis Beckman DU 7500 spectrophotometer. A ten point calibration curve was constructed at 610 nm in the concentration range of 100–1500 mg·dm−3 with a determination coefficient (R2) of 0.999. In addition, the pH of the solutions and drained materials was measured using a Tritando Metrohm 809 (Riverview, FL, USA) and the LL Biotrode and LL flat membrane electrodes, respectively.

3.5. Photocatalytic Experiments

For the irradiation experiments, a 15 cm3 temperature-controlled quartz reactor from Ace Glass Inc. (Vineland, NJ, USA) was used. A 2⅛-inch Pen-Ray light source (254 nm, 5.5 Watt) from Ultra-Violet Products (Upland, CA, USA) was immersed into the reactor in a quartz jacket. The reactor was equipped with a water jacket to avoid IR irradiation of the lamp and control the temperature (25 °C) of the solution. The entire assembly was enclosed in a dark chamber, and the lamp was switched on after 30 min to establish adsorption equilibrium. In each experiment, 10 mg of the composite was added to 5 cm3 of a solution containing 3000, 300 or 30 mg·dm−3 of IC. Because the particles of the prepared material settled readily, no centrifugation step was required to collect aliquots at regular time intervals during irradiation for spectroscopic and chromatographic analysis, which is in contrast with studies using nude anatase nanoparticles. The pH of the IC solutions was adjusted in selected experiments with 0.5 N NH4OH to achieve a pH of 10 and with 0.025 N HCl to achieve a pH of 4.0.

3.6. Analysis of Photocatalysis Products

Aliquots of all of the IC solutions subjected to photocatalytic testing with the TiO2-carbon composites were analyzed using a Hach DR 5000 UV-Vis spectrophotometer over a wavelength range of 200–800 nm. Decolorization was evaluated at 610 nm. The collected aliquots were also analyzed by liquid chromatography using an LC-MS instrument (Series 1260 chromatograph coupled with an ESI-(Qq)-TOF-MS 6520 detector from Agilent Technologies, Santa Clara, CA, USA). The separation was carried out at 25 °C using a Nucleodur EC C18 Isis (5 µm, 250 × 4.6 mm) column from Macherey–Nagel (Düren, Germany). Gradient elution at 1 cm3·min−1 with a methanol-water (10%–50%) mobile phase between 0 and 20 min and 90% methanol up to 25 min was performed. The water contained 40 mM acetic acid-triethylamine reagent from Fluka (Buchs, Switzerland) as an ion pair agent. To methanol (Burdick-Jackson, Muskegon, MI, USA), 0.1% HCOOH from Aldrich (St. Louis, CA, USA) was added. The injection volume was 100 µL.
ESI-TOF-MS was performed in the negative ionization mode (ESI(-)) with nitrogen as the drying gas at 11 dm3·min−1 using a TOF fragmentor voltage of 175 V in the negative ionization mode, a capillary voltage of 3500 V over a m/z range of 50–700, gas temperature of 350 °C and a nebulizer pressure of 60 psi. For the MS/MS analysis, ESI-Qq-TOF-MS was used in the negative ionization mode using a CE of 30 V over an m/z range of 50–300 and an isolation width of 1.3 m/z.

4. Conclusions

The preparation method of the TiO2/carbon materials containing the photocatalytically active anatase phase was simple and inexpensive. The glycerol additive allowed for the conservation of the anatase phase despite treatment at 800 °C. The composites were fibrous trunks with improved density. The use of dry precursors produced mesoporous materials, but the reproducibility of their properties was low. The glycerol-aided fabrication of the TiO2/C composite led to optimal immobilization of TiO2. A low Manihot: TiO2 ratio (1:0.5) yielded a basic material with SBET 244 m2·g−1, ~50% microporosity and an average pore diameter of <4 nm. The moderate TiO2 loading in composite MT-G5 (203 m2·g−1) also generated a basic material with the same microporosity percentage and average pore diameter. The TiO2 loading on the carbon directly affected the acidity (pHpzc) of the TiO2/carbon composites. The photodegradation of IC was complete, and most of the products were produced due to cleavage of the exocyclic C=C. Some products were persistent because they remained at the end of the photocatalytic process applied using the prepared composite. The identified degradation products of IC are similar to those reported by other electrolysis and advanced oxidation processes with exception of a new oxazine compound. Due to its density and topography, the prepared composites allowed for the identification of the products during the photoreaction avoiding a long centrifugation step. The study of the toxicity of the reaction mixtures is a logical extension of the current work.

Acknowledgments

This publication is based on work conducted under project CB-2008-01-100439 sponsored by CONACyT (Mexico) and INFR-123779-2009. We thank the financial funding of the university (UAP) within the last project. We are grateful to Efraín Rubio Rosas and Eric Reyes Cervantes (CUVyTT, Universidad Autónoma de Puebla, Puebla, Mexico) for the use of the SEM instrument. CMAC is grateful for grant No. 227566 from CONACyT.

Author Contributions

Cynthia M. Antonio-Cisneros performed the preparation and textural characterization of the composites. She also carried out the adsorption and photocatalytic experiments. Martín M. Dávila-Jiménez worked on the microscopic and spectroscopic methods. María P. Elizalde-González designed the investigation and wrote the paper. Esmeralda García-Díaz analyzed the solutions of indigo carmine subjected to photocatalysis under different conditions and interpreted the chromatographic results. All authors read and approved the publication.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Chong, M.N.; Jin, B.; Chow, C.W.K.; Saint, C. Recent developments in photocatalytic water treatment technology: A review. Water Res. 2010, 44, 2997–3027. [Google Scholar] [CrossRef] [PubMed]
  2. Ochiai, T.; Fujishima, A. Photoelectrochemical properties of TiO2 photocatalysis and its applications for environmental purification. J. Photochem. Photobiol. C Photochem. Rev. 2012, 13, 247–262. [Google Scholar] [CrossRef]
  3. Leary, R.; Westwood, A. Carbonaceous nanomaterials for the enhancement of TiO2 photocatalysis. Carbon 2011, 49, 741–772. [Google Scholar] [CrossRef]
  4. Foo, K.Y.; Hameed, B.H. Decontamination of textile wastewater via TiO2/activated carbon composite materials. Adv. Colloid Interface Sci. 2010, 159, 130–143. [Google Scholar] [CrossRef] [PubMed]
  5. Chen, M.L.; Lim, C.S.; Oh, W.C. Preparation with different mixing ratios of anatase to activated carbon and their photocatalytic performance. J. Ceramic Proc. Res. 2007, 8, 119–124. [Google Scholar]
  6. Matos, J.; Garcia, A.; Cordero, T.; Chovelon, J.-M.; Ferronato, C. Eco-friendly TiO2-AC photocatalyst for the selective photooxidation of 4-chlorophenol. Catal. Lett. 2009, 130, 568–574. [Google Scholar] [CrossRef]
  7. Zhu, B.; Zou, L. Trapping and decomposing of color compounds from recycled water by TiO2 coated activated carbon. J. Environ. Manag. 2009, 90, 3117–3225. [Google Scholar]
  8. Lim, T.T.; Yap, P.S.; Srinivasan, M.; Fane, A.G. TiO2/AC composites for synergistic adsorption-photocatalysis processes: Present challenges and further developments for water treatment and reclamation. Crit. Rev. Environ. Sci. Technol. 2011, 41, 1173–1230. [Google Scholar] [CrossRef]
  9. Yang, M.Q.; Zhang, N.; Pagliaro, M.; Xu, Y.J. Artificial photosynthesis over graphene-semiconductor composites. Are we getting better? Chem. Soc. Rev. 2014, 43, 8240. [Google Scholar] [CrossRef] [PubMed]
  10. Zhang, Y.; Tang, Z.R.; Fu, X.; Xu, Y.J. TiO2-Graphene nanocomposites for gas-phase photocatalytic degradation of volatile aromatic pollutants: Is TiO2-graphene truly different from other TiO2-carbon composite materials? ACS Nano 2010, 4, 7303. [Google Scholar] [CrossRef] [PubMed]
  11. Haro, M.; Velasco, L.F.; Ania, C.O. Carbon-mediated photoinduced reactions as a key factor in the photocatalytic performance of C/ TiO2. Catal. Sci. Technol. 2012, 2, 2264–2272. [Google Scholar] [CrossRef]
  12. Hou, D.; Feng, L.; Zhang, J.; Dong, S.; Zhou, D.; Lim, T.T. Preparation, characterization and performance of a novel visible light responsive spherical activated carbon-supported and Er3+:YFeO3-doped TiO2 photocatalyst. J. Hazard Mater. 2012, 199–200, 301–308. [Google Scholar] [CrossRef] [PubMed]
  13. Keng, C.S.; Zainal, Z.; Abdullah, A.H. Removal of cationic and anionic dyes by immobilized titanium dioxide loaded activated carbon. Malays. J. Anal. Sci. 2008, 12, 451–457. [Google Scholar]
  14. Huang, D.; Miyamoto, Y.; Matsumoto, T.; Tojo, T.; Fan, T.; Ding, J.; Guo, Q.; Zhang, D. Preparation and characterization of high-surface-area TiO2/activated carbon by low-temperature impregnation. Sep. Purif. Technol. 2011, 78, 9–15. [Google Scholar] [CrossRef]
  15. Asiltürk, M.; Şener, Ş. TiO2-activated carbon photocatalyst: Preparation, characterization and photocatalytic activities. Chem. Eng. J. 2012, 180, 354–363. [Google Scholar] [CrossRef]
  16. Sabinas Hernández, S.A. Preparación y Caracterización de Composites de CA-TiO2 con Propiedades Fotocatalíticas. MSc Thesis, Universidad Autónoma de Puebla, Puebla, México, 12 May 2011. [Google Scholar]
  17. Mahmoodi, N.M.; Arami, M.; Zhang, J. Preparation and photocatalytic activity of immobilized composite photocatalyst (titania nanoparticle/activated carbon). J. Alloys Comp. 2011, 509, 4754–4764. [Google Scholar] [CrossRef]
  18. Chen, Y.X.; Luo, B.H.; Zhao, B.Y.; Lai, Y.J.; Wang, H.Z.; Gao, M.Y.; Zhang, W.X.; Chen, K.B. Method to control the phase of TiO2 in porous carbon-TiO2 composite. J. Inorg. Organomet. Polym. 2012, 22, 90–96. [Google Scholar] [CrossRef]
  19. Cordero, T.; Chovelon, J.-M.; Duchamp, C.; Ferronato, C.; Matos, J. Surface-nanoaggregation and photocatalytic activity of TiO2 on H-type activated carbons. Appl. Catal. B: Environ. 2007, 73, 227–235. [Google Scholar] [CrossRef]
  20. Antonio Cisneros, C.M.; Elizalde González, M.P. Characterization of Manihot residues and preparation of activated carbon. Biomass Bioenergy 2010, 34, 389–395. [Google Scholar] [CrossRef]
  21. Bandara, J.; Mielczarski, J.A.; Kiwi, J. Molecular mechanism of surface recognition. Azo dyes degradation on Fe, Ti, and Al oxides through metal sulfonate complexes. Langmuir 1999, 15, 7670–7679. [Google Scholar]
  22. Sreethawong, T.; Ngamsinlapasathian, S.; Yoshikawa, S. Glycerol as an efficient mesopore-controlling agent for synthesis of mesoporous-assembled TiO2 nanocrystals and their remarkable photocatalytic H2 production activity. Mater. Res. Bull. 2012, 47, 199–205. [Google Scholar] [CrossRef]
  23. Velasco, L.F.; Parra, J.B.; Ania, C.O. Phenol adsorption and photo-oxidation on porous carbon/titania composites. Adsorpt. Sci. Technol. 2010, 28, 727–738. [Google Scholar] [CrossRef]
  24. Matos, J.; Chovelon, J.-M.; Cordero, T.; Ferronato, C. Influence of Surface properties of activated carbon on photocatalytic activity of TiO2 in 4-chlorophenol degradation. Open Environ. Eng. J. 2009, 2, 21–29. [Google Scholar] [CrossRef]
  25. Trung, T.; Cho, W.-J.; Ha, C.-S. Preparation of TiO2 nanoparticles in glycerol-containing solutions. Mater. Lett. 2003, 57, 2746–2750. [Google Scholar] [CrossRef]
  26. Shanmugam, S.; Gabashvili, A.; Jacob, D.S.; Yu, J.C.; Gedanken, A. Synthesis and characterization of TiO2@C core-shell composite nanoparticles and evaluation of their photocatalytic activities. Chem. Mater. 2006, 18, 2275–2282. [Google Scholar] [CrossRef]
  27. Luttrell, T.; Halpegamage, S.; Tao, J.; Kramer, A.; Sutter, E.; Batzill, M. Why is anatase a better photocstalyst than rutile?–Model studies on epitaxial TiO2 films. Sci. Rep. 2014, 4, 4043. [Google Scholar] [CrossRef] [PubMed]
  28. Castelló, M.L.; Dweck, J.; Aranda, D.A.G. Thermal stability and water content determination of glycerol by thermogravimetry. J. Therm. Anal. Calorim. 2009, 97, 627–630. [Google Scholar] [CrossRef]
  29. Vautier, M.; Guillard, C.; Herrmann, J.-M. Photocatalytic degradation of dyes in water: Case study of indigo and indigo carmine. J. Catal. 2001, 201, 46–59. [Google Scholar] [CrossRef]
  30. Alahiane, S.; Qourzal, S.; El Ouardi, M.; Belmouden, M.; Assabbane, A.; Ait-Ichou, Y. Adsorption and photocatalytic degradation of indigo carmine dye in aqueous solutions using TiO2 /UV/O2. J. Mater. Environ. Sci. 2013, 4, 239–250. [Google Scholar]
  31. Zhang, Y.; Zhang, N.; Tang, Z.R.; Xu, Y.J. Improving the photocatalytic performance of graphene-TiO2 nanocomposites via a combined strategy of decreasing defects of graphene and increasing interfacial contact. Phys. Chem. Chem. Phys. 2012, 14, 9167–9175. [Google Scholar] [CrossRef] [PubMed]
  32. Subramani, A.K.; Byrappa, K.; Ananda, S.; Lokanatha Rai, K.M.; Ranganathaiah, C.; Yoshimura, M. Photocatalytic degradation of indigo carmine dye using TiO2 impregnated carbon. Bull. Mater. Sci. 2007, 30, 37–41. [Google Scholar] [CrossRef]
  33. Bae, S.; Kim, S.; Lee, S.; Choi, W. Dye decolorization test for the activity assessment of visible light photocatalysts: Realities and limitations. Catal. Today 2014, 224, 21–28. [Google Scholar] [CrossRef]
  34. Galindo, C.; Jacques, P.; Kalt, A. Photochemical and photocatalytic degradation of an indigoid dye: A case study of acid blue 74 (AB74). J. Photochem. Photobiol. A Chem. 2001, 141, 47–56. [Google Scholar] [CrossRef]
  35. Antonio Cisneros, C.M. Equilibrio de Adsorción-Desorción de Colorantes Naturales Sobre Composites Carbonáceos. DSc Thesis, Universidad Autónoma de Puebla, Puebla, México, 30 September 2010. [Google Scholar]
  36. Barka, N.; Assabbane, A.; Nounah, A.; Aît Ichou, Y. Photocatalytic degradation of indigo carmine in aqueous solution by TiO2-coated non-woven fibres. J. Hazard Mater. 2008, 152, 1054–1059. [Google Scholar] [CrossRef] [PubMed]
  37. Abaamrane, A.; Qourzal, S.; Barka, N.; Billah, S.M.; Assabbane, A.; Ait-Ichou, Y. Optimal decolorization efficiency of indigo carmine by TiO2/UV photocatalytic process coupled with response surface methodology. Orient. J. Chem. 2012, 28, 1091–1098. [Google Scholar] [CrossRef]
  38. Ross, P. Taguchi Techniques for Quality Engineering; McGraw-Hill International Editions; McGraw-Hill Professional: New York, NY, USA, 1996; p. 267. [Google Scholar]
  39. Coelho, M.G.; de Lima, G.M.; Augusti, R.; Maria, D.A.; Ardisson, J.D. New materials for photocatalytic degradation of indigo carmine-Synthesis, characterization and catalytic experiments of nanometric tin dioxide-based composites. Appl. Catal. B Environ. 2010, 96, 67–71. [Google Scholar] [CrossRef]
  40. Guaraldo, T.T.; Zanoni, T.B.; de Torresi, S.I.C.; Gonçales, V.R.; Zocolo, G.J.; Oliveira, D.P.; Zanoni, M.V.B. On the application of nanostructured electrodes prepared by Ti/TiO2/WO3 “template”: A case study of removing toxicity of indigo using visible irradiation. Chemosphere 2013, 91, 586–593. [Google Scholar] [CrossRef] [PubMed]
  41. Ramya, M.; Anusha, B.; Kalavathy, S. Decolorization and biodegradation of indigo carmine by a textile soil isolate Paenibacillus larvae. Biodegradation 2008, 19, 283–291. [Google Scholar] [CrossRef] [PubMed]
  42. Luan, J.; Chen, M.; Hu, W. Synthesis, characterization and photocatalytic activity of new photocatalyst ZnBiSbO4 under visible light irradiation. Int. J. Mol. Sci. 2014, 15, 9459–9480. [Google Scholar] [CrossRef] [PubMed]
  43. Ammar, S.; Abdelhedi, R.; Flox, C.; Arias, C.; Brillas, E. Electrochemical degradation of the dye indigo carmine at boron-doped diamond anode for wastewater remediation. Environ. Chem. Lett. 2006, 4, 229–233. [Google Scholar] [CrossRef]
  44. Dalmazio, I.; de Urzedo, A.P.F.M.; Alves, T.M.A.; Catharino, R.R.; Eberlin, M.N.; Nascentes, C.C.; Augusti, R. Electrospray ionization mass spectrometry monitoring of indigo carmine degradation by advanced oxidative processes. J. Mass Spectrom. 2007, 42, 1273–1278. [Google Scholar] [CrossRef] [PubMed]
  45. Bourikas, K.; Vakros, J.; Kordulis, C.; Lycourghiotis, A. Potentiometric mass titrations: Experimental and theoretical establishment of a new technique for determining the point of zero charge (PZC) of metal (hydr)oxides. J. Phys. Chem. B 2003, 107, 9441–9451. [Google Scholar] [CrossRef]

Share and Cite

MDPI and ACS Style

Antonio-Cisneros, C.M.; Dávila-Jiménez, M.M.; Elizalde-González, M.P.; García-Díaz, E. TiO2 Immobilized on Manihot Carbon: Optimal Preparation and Evaluation of Its Activity in the Decomposition of Indigo Carmine. Int. J. Mol. Sci. 2015, 16, 1590-1612. https://doi.org/10.3390/ijms16011590

AMA Style

Antonio-Cisneros CM, Dávila-Jiménez MM, Elizalde-González MP, García-Díaz E. TiO2 Immobilized on Manihot Carbon: Optimal Preparation and Evaluation of Its Activity in the Decomposition of Indigo Carmine. International Journal of Molecular Sciences. 2015; 16(1):1590-1612. https://doi.org/10.3390/ijms16011590

Chicago/Turabian Style

Antonio-Cisneros, Cynthia M., Martín M. Dávila-Jiménez, María P. Elizalde-González, and Esmeralda García-Díaz. 2015. "TiO2 Immobilized on Manihot Carbon: Optimal Preparation and Evaluation of Its Activity in the Decomposition of Indigo Carmine" International Journal of Molecular Sciences 16, no. 1: 1590-1612. https://doi.org/10.3390/ijms16011590

APA Style

Antonio-Cisneros, C. M., Dávila-Jiménez, M. M., Elizalde-González, M. P., & García-Díaz, E. (2015). TiO2 Immobilized on Manihot Carbon: Optimal Preparation and Evaluation of Its Activity in the Decomposition of Indigo Carmine. International Journal of Molecular Sciences, 16(1), 1590-1612. https://doi.org/10.3390/ijms16011590