Next Article in Journal
A Mouse-Based Method to Monitor Wheat Allergens in Novel Wheat Lines and Varieties Created by Crossbreeding: Proof-of-Concept Using Durum and A. tauschii Wheats
Next Article in Special Issue
Development and Preliminary Testing of Porcine Blood-Derived Endothelial-like Cells for Vascular Tissue Engineering Applications: Protocol Optimisation and Seeding of Decellularised Human Saphenous Veins
Previous Article in Journal
What Genetics Can Do for Oncological Imaging: A Systematic Review of the Genetic Validation Data Used in Radiomics Studies
Previous Article in Special Issue
Mechanical Properties of the Modified Denture Base Materials and Polymerization Methods: A Systematic Review
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
IJMS
Volume 23
Issue 12
10.3390/ijms23126503
ijms-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Suitability of Chitosan Scaffolds with Carbon Nanotubes for Bone Defects Treated with Photobiomodulation

by
Samantha Ketelyn Silva
1,
Ana Maria Guzzi Plepis
2,3,
Virginia da Conceição Amaro Martins
3,
Marilia Marta Horn
4,
Daniela Vieira Buchaim
5,6,
Rogerio Leone Buchaim
7,8,
André Antônio Pelegrine
9,
Vinícius Rodrigues Silva
1,
Mateus Hissashi Matsumoto Kudo
1,
José Francisco Rebello Fernandes
1,
Fabricio Montenegro Nazari
1 and
Marcelo Rodrigues da Cunha
1,2,*
1
Department of Morphology and Pathology, Jundiaí Medical School, Jundiaí 13202-550, Brazil
2
Interunits Graduate Program in Bioengineering (EESC/FMRP/IQSC), University of Sao Paulo (USP), Sao Carlos 13566-590, Brazil
3
Sao Carlos Institute of Chemistry, University of Sao Paulo (USP), Sao Carlos 13566-590, Brazil
4
Physical Chemistry of Nanomaterials, Institute of Chemistry and Center for Interdisciplinary and Nanostructure Science and Technology (CINSaT), University of Kassel, 34109 Kassel, Germany
5
Postgraduate Program in Structural and Functional Interactions in Rehabilitation, Postgraduate Department, University of Marilia (UNIMAR), Marília 17525-902, Brazil
6
Teaching and Research Coordination of the Medical School, University Center of Adamantina (UniFAI), Adamantina 17800-000, Brazil
7
Department of Biological Sciences, Bauru School of Dentistry (FOB/USP), University of Sao Paulo, Bauru 17012-901, Brazil
8
Graduate Program in Anatomy of Domestic and Wild Animals, Faculty of Veterinary Medicine and Animal Science, University of Sao Paulo, Sao Paulo 05508-270, Brazil
9
School of Dentistry, Faculdade Sao Leopoldo Mandic, Campinas 13045-755, Brazil
*
Author to whom correspondence should be addressed.
Int. J. Mol. Sci. 2022, 23(12), 6503; https://doi.org/10.3390/ijms23126503
Submission received: 28 May 2022 / Revised: 6 June 2022 / Accepted: 9 June 2022 / Published: 10 June 2022
(This article belongs to the Special Issue Biomaterials and Regenerative Medicine)
Browse Figures
Versions Notes

Abstract

:
Biomaterials have been investigated as an alternative for the treatment of bone defects, such as chitosan/carbon nanotubes scaffolds, which allow cell proliferation. However, bone regeneration can be accelerated by electrotherapeutic resources that act on bone metabolism, such as low-level laser therapy (LLLT). Thus, this study evaluated the regeneration of bone lesions grafted with chitosan/carbon nanotubes scaffolds and associated with LLLT. For this, a defect (3 mm) was created in the femur of thirty rats, which were divided into 6 groups: Control (G1/Control), LLLT (G2/Laser), Chitosan/Carbon Nanotubes (G3/C+CNTs), Chitosan/Carbon Nanotubes with LLLT (G4/C+CNTs+L), Mineralized Chitosan/Carbon Nanotubes (G5/C+CNTsM) and Mineralized Chitosan/Carbon Nanotubes with LLLT (G6/C+CNTsM+L). After 5 weeks, the biocompatibility of the chitosan/carbon nanotubes scaffolds was observed, with the absence of inflammatory infiltrates and fibrotic tissue. Bone neoformation was denser, thicker and voluminous in G6/C+CNTsM+L. Histomorphometric analyses showed that the relative percentage and standard deviations (mean ± SD) of new bone formation in groups G1 to G6 were 59.93 ± 3.04a (G1/Control), 70.83 ± 1.21b (G2/Laser), 70.09 ± 4.31b (G3/C+CNTs), 81.6 ± 5.74c (G4/C+CNTs+L), 81.4 ± 4.57c (G5/C+CNTsM) and 91.3 ± 4.81d (G6/C+CNTsM+L), respectively, with G6 showing a significant difference in relation to the other groups (a ≠ b ≠ c ≠ d; p < 0.05). Immunohistochemistry also revealed good expression of osteocalcin (OC), osteopontin (OP) and vascular endothelial growth factor (VEGF). It was concluded that chitosan-based carbon nanotube materials combined with LLLT effectively stimulated the bone healing process.

1. Introduction

Bones are composed of dense and rigid connective tissue, but they are highly dynamic, and constantly remodeled [1]. Therefore, bone tissue is predisposed to different types of injuries caused by trauma, tumors, abnormalities and physiological imbalances, resulting in bone loss with difficulty in spontaneous regeneration [2,3]. Thus, considering these circumstances and the increasing demand for orthopedic and trauma treatment due to fractures caused by road accidents, it becomes necessary to develop or improve artificial bone substitutes, given the limitations of using autologous grafts and their postoperative complications, such as local infections and severe pain in the donor area [4,5]. In this scenario, it becomes necessary to study new biomaterials that mimic the components of bone tissue or have the ability to act as a scaffold that allows optimal adhesion and cell proliferation for the growth of new tissue [1,6].
Natural polymers have been highlighted because, when used to manufacture scaffolds, they can promote a support structure for tissue formation [7]. On the other hand, biopolymers that show similar composition as the extracellular matrix (ECM) can also be used to develop scaffolds, such as the polysaccharide chitosan. This polysaccharide can be obtained from squid pens of the species Doryteuthis spp., and it can be used in the preparation of scaffolds with minimal immune response [8].
Chitosan is a natural polymer obtained through the deacetylation of chitin [9] and presents important properties, such as biodegradability and biocompatibility, besides antibacterial action [10,11]. Chitosan based scaffolds lack in mechanical strength and structural stability in hydrated conditions, and thereby limit its application for bone tissue regeneration [12,13,14,15]. Therefore, modifications or addition of other products can help to improve the properties of chitosan [16,17], such as natural bioactive injectable composites for the purpose of inducing angiogenesis (Chitosan/Hydroxyapatite/Heparin) and improving bone regeneration, these hydrogels being modified by the use of glycerol, as an additive and a pre-sterile production strategy to increase its mechanical resistance [18].
Chitosan electrospinning and its composite formulations for creating fibers in combination with other natural polymers have potential for use in tissue engineering. There is evidence of favorable properties and biocompatibility of chitosan electrospun composite biomaterials for a variety of uses [19]. Carbon nanotubes can also be used to improve chitosan scaffolds, which may represent an attractive option due to their tensile strength, high flexibility, promising bioactivity and good electrical conductivity [20,21,22].
Considering the search for a mechanism that accelerates the cell migration process associated with the use of these biopolymers, it is also possible to develop mechanisms capable of promoting protein synthesis and cell growth. Therefore, the photobiomodulatory effects of low-level laser therapy (LLLT) have been used in the treatment of bone lesions [23,24,25,26,27], since infrared wavelengths can stimulate the proliferation of osteoblasts and collagen deposition [28].
Due to the absence of studies on this new biomaterial, especially associated with photobiomodulation, this study aimed to investigate the effects of an experimental proto-col for the treatment of bone lesions using the implantation of scaffolds constructed with chitosan and carbon nanotubes, in addition to the application of the LLLT protocol.

2. Results

There were no complications that needed to be reported, and there was no disease or sign that strongly motivated the removal of an animal.

2.1. Structure of Biomaterials

Once dissolved in diluted acid solutions, the amino group present in the chitosan structure is protonated, which allows electrostatic interaction among other compounds or polymers. This study observes an electrostatic formation between the protonated chitosan and the functionalized carboxylic groups in the nanotube walls. Recently, we found out that the 0.25 mg of functionalized single-wall carbon nanotubes (f-SWCN) is the threshold concentration for the nanofiller in the chitosan host scaffolds. In fact, an increase in SWCN concentration could result in the formation of nano-cracks and have a negative effect on the mechanical properties [29]. Nevertheless, one of the characteristics of implant materials is to provide enough mechanical response in the damaged area, which is possible by the addition of nanofillers, such as carbon nanotubes. For that reason, the formulation containing 0.25 mg of carbon nanotubes was selected for the present study.
The fingerprint region of the Fourier-transform infrared spectroscopy (FTIR) spectrum was used to analyse the characteristic bands of the chitosan and the functionalized carbon nanotubes. The molecular vibrations in this area are very accurate in characterizing chemical compounds. The chitosan spectrum (Figure 1a) showed the absorption bands characteristics of amides I and II at 1655 and 1560 cm−1, respectively. Additionally, -C-H banding at 1409 cm−1; C-O and C-O-C stretching vibrations at 1153, 1094 and 1026 cm−1, corresponding to the saccharide structure of chitosan. A typical band at 1716 cm−1 is attributed to the carboxyl groups, which evidence the effective functionalization of the carbon nanotubes, while the additional observed band at 1579 cm−1 is related to the aromatic C=C bond stretching of its structure, as indicated by the arrows (Figure 1b) [30].
The CN25 spectrum (Figure 1c) shows no changes or shifts in the characteristic bands, suggesting an electrostatic interaction between the components. The host polymer is comparatively in a higher concentration than the carbon nanotubes, overlapping its bands. The first evidence of the mineralization arises from the enhancement intensity of the PO43− band at 1024 cm−1. The sharp peak at this wavenumber is characteristic of phosphate compounds formed during the precipitation process (Figure 1d).
The nucleation and precipitation of calcium phosphate in scaffolds occur due to the ionic activity of calcium phosphate in solution and its stimulation to create favorable local conditions to allow the nucleation and growth of calcium phosphate. Indeed, calcium and phosphate ions diffuse into scaffolds and form nuclei of critical size for nucleation and further growth of calcium phosphate crystals [31]. Additionally, nucleated apatite crystals on three-dimensional scaffolds create a favorable environment for osteoconductivity.
The quantification of deposited calcium phosphate was evaluated by thermogravimetric analysis, as the amount of residue at 750 °C refers to the inorganic material remaining after the decomposition of the organic phase (Figure 2A).
The curve for the non-mineralized scaffold (CN25) showed a residue of 1.7%, while the mineralized one (CN25M), exhibits a value of 23.7%. This result confirms the presence of an inorganic phase in the scaffold. It is interesting to notice that the processability of the materials has a considerable influence on the mineralization process. Compared to films, scaffolds are three-dimensional structures that allow nucleation and precipitation on the surface and in the internal network structure, increasing the amount of deposited calcium phosphate [32].
Using random spot areas (indicated by the arrows), as shown in Figure 2B, the determination of the Ca/P ratio was performed. The chemical analyses achieved by EDX stated the presence of calcium, phosphorous, and oxygen peaks. The calculated value was 2.43 ± 0.07, higher than expected for the theoretical hydroxyapatite value (1.67). This might be possible due to excess residual chloride from the mineralization process, and also, the deposited hydroxyapatite is calcium-rich amorphous, as described in the literature [33].
The SEM images using a 500× magnification show the presence of porous homogeneity distributed on the surface of the chitosan/carbon nanotube scaffold (Figure 3A). This property remains after the mineralization process (Figure 3B), and porous are still visible in the scaffold structure, which is a critical feature for the subsequent implant process. Additionally, at high magnification (25,000×, Figure 3C), aggregates of calcium phosphate crystals are observed in a spherical shape, a similar morphology of that class of inorganic deposits [34]. An effective mineralization process is evidenced by the formation of a bioactive compound, with the ability to induce new bone tissue formation. The pore size of the scaffolds was determined by the analyses of the SEM structures. The calculated value for CN25 was 20.6 ± 3.2, while for CN25M 13.5 ± 3.3. This result revealed the decrease in pore size after the mineralization process due to the calcium phosphate deposits along the surface of the collagen fibers.
The mineralized sample was previously examined by X-ray diffraction, showing the characteristic peaks of a poor crystalline state of hydroxyapatite and a crystallite diameter of 15 ± 1 nm [32].
The swelling characteristics of the scaffolds are directly related to their composition and affect the stability and the in vivo performance of the scaffolds, especially those related to the vascularization process.
Figure 4 shows the swelling behavior of CN25 and CN25M in PBS pH 7.4. In both cases, the absorption of the buffer is fast, leading to percentage values higher than 1000%. This characteristic is typical for three-dimensional scaffolds composed of polymeric networks capable of swelling without the rupture of their structure. The measurement was carried out for 40 min, during which the buffer absorption equilibrium achievement was observed. A maximum swelling percentage of 1716% (CN25) and 1179% (CN25M) was noticed. Even though both samples exhibited a high swelling percentage, the mineralization process reduced the amount of PBS absorbed by the scaffold, probably by the reduction in the pore size. The reduction in the swelling property is expected in mineralized chitosan scaffolds, as observed in previous studies described in the literature [35].

2.2. Macroscopic and Radiological Analysis of the Bone Lesion

In all surgical areas of the animals evaluated in this study, no signs of anatomopathological changes were observed, such as local inflammatory process, bone non-union, ulcerative lesions, purulent secretions, cysts, infection suggestive of osteomelitis characterized by radiographic bone rarefaction or abnormal mass growth tissue with neoplastic characteristics. The anatomical architecture of the femur was maintained in all animals evaluated, with no secondary fractures or pseudarthrosis resulting from post-surgical complications. The normality pattern of the radiological characteristics of the femur, such as the radiopaque cortical margins of the bone and the radiotransparency of the medullary canal, could also be observed. However, the bone defects were not completely closed in the studied groups (Figure 5).

2.3. Morphology of the Bone Lesion Area

In all the groups studied, new bone formation was noted, projecting from the original bone from the edges of the lesion and towards the center of the surgical area. However, the morphology of this bone presented different characteristics for each group of animals.
In the control group (G1/Control), the young bone acquired a thinner and irregular aspect, with histological characteristics of immature tissue, with several cavities inside. In the animals treated only with LLLT (G2/Laser), subperiosteal bone formations extended along the lesion area, with some long trabeculae arranged in different directions. The group that received chitosan/carbon nanotubes (G3/C+CNTs) had a more porous bone formation, with bone cavities inside and remnants of the scaffolds surrounded by connective tissue. In the chitosan/carbon nanotubes group that received the LLLT (G4/C+CNTs+L), the bone neoformation filled the entire extension of the bone lesion, thus uniting the edges of the lesion extremities. When mineralization was added, it was observed that the G5/C+CNTsM group presented remnants of the biomaterial centralized close to the medullary canal, in addition to a neoformed bone tissue of a dense nature and with few cavities in its interior. In the last group evaluated, which received the scaffolds and the LLLT (G6/C+CNTsM+L), bone formation was relatively higher than in the other groups, with a thicker and compact aspect able to fill the entire lesion area (Figure 6).
Through picrosirius red staining and polarized light, the birefringence of collagen in the extracellular matrix of the tissue present in the surgical area was observed in all groups evaluated (Figure 7).

2.4. Histomorphometric and Statistical Analysis of the Bone Volume Formed in the Surgical Area

The means and standard deviation of the relative percentage volume of newly formed bone in the femoral defects in the study groups were, respectively: 59.93 ± 3.04a (G1/Control), 70.83 ± 1.21b (G2/Laser), 70.09 ± 4.31b (G3/C+CNTs), 81.6 ± 5.74c (G4/C+CNTs+L), 81.4 ± 4.57c (G5/C+CNTsM) and 91.3 ± 4.81d (G6/C+CNTsM+L) (a ≠ b ≠ c ≠ d; p < 0.05). In the comparative statistical analyses between the groups, it was observed that the treated experimental groups (G2/Laser to G6/C+CNTsM+L) showed satisfactory results, as they presented higher values when compared to the control group (G1/Control). Regarding the LLLT protocol, it was noted that the parameters used were essential for bone formation since G6/C+CNTsM+L showed greater bone volume compared to G5/C+CNTsM, as was also observed in the comparison between G4/C+CNTsM+L and G3/C+CNTs. In addition, it was found that there was a significant difference in formed bone volume in the animals that received mineralized scaffolds compared to the non-mineralized scaffold groups, as observed in the comparison between G3/C+CNTs vs. G5/C+CNTsM (Figure 8).

2.5. Immunohistochemical Analysis

In the newly formed bone matrix of the surgical area, it was possible to observe the formation of osteocytes due to the expression of osteocalcin (OC) and osteopontin (OPN). In the groups treated with LLLT, a more organized arrangement of osteocytes was observed (Figure 9 and Figure 10). Regarding the expression of vascular endothelial growth factor (VEGF), the formation of blood vessels was also noted in the surgical areas (Figure 11).

3. Discussion

The treatment of bone injuries is still a challenge [36] for regenerative medicine, and, thus, there is a need to manufacture biomaterials and improve treatment protocols that enable bone replacement quickly and safely [37], overcoming the limitations of conventional techniques of autograft and allograft, which can lead to unwanted infections and donor site morbidity [38]. However, some factors must be considered in the formulation of these products, such as their biocompatibility, surface type and porosity, mechanical strength, physical-chemical and biological composition, and the three-dimensional arrangement that allows osteoconduction [39]. The bone resorption capacity is also important as the degradation of the material is expected to occur as new bone tissue grows [10,40]. Thus, polymers stand out among the various materials that present these characteristics due to their greater bioactivity and the non-release of cytotoxic products during degradation [41,42].
Chitosan is a favorable biopolymer for tissue engineering, mainly due to its biodegradable, non-toxic, bioactive, biocompatible, non-immunogenic, and antibacterial features. Additionally, it shows a similar structure to glycosaminoglycans (GAGs) and proteoglycans found in the extracellular matrix (ECM), which are associated with essential physiological functions in the tissue [43,44]. Due to its cationic nature, chitosan interacts electrostatically with anionic molecules. This approach is usually applied to outcome some limitations of the chitosan, e.g. the mechanical properties. Consequently, the combination of chitosan and carbon nanotubes is an alternative to enhance the mechanical and structural properties of the material. Scaffolds should be capable of supporting tissue formation and also cooperate in the tissue repair permanently or temporarily. For that reason, the scaffold used in this study may be an alternative material to restore bone defects [45,46]. Scaffolds for bone tissue regeneration should have crucial characteristics, such as the interconnected pore structure to allow vascularization and the transport of nutrients, and adequate mechanical properties. Additionally, the mineralization process provides the deposit of calcium phosphate inorganic phase, which is essential in the biomineralization process during the repair of the damaged tissue [47].
Carbon nanotubes are considered a promising material due to their mechanical and magnetic properties [48]. Türk et al. (2018) evaluated the performance of carbon nanotube composites with chitosan/hydroxyapatite/collagen, and the results were satisfactory for bone tissue [49]. Cunha et al. (2017) showed the biocompatibility of chitosan/carbon nanotube scaffolds implanted in the calvaria of rats, as no macroscopic and radiological changes from inflammatory processes were observed in the surgical area [50]. In agreement with these data, an investigation performed on the femur of rats also did not find signs of the formation of a granulomatous foreign body that would indicate immunological rejection or any inflammatory processes after the grafting of biomaterials [51]. These results are attributed not only to the antimicrobial activity of chitosan but also to the physicochemical process of the manufacturing of these biopolymers [51]. These biocompatibility characteristics with the host tissue demonstrates the applicability of these biopolymers, however, a scaffold must also promote sufficient osteogenesis to initiate a bone repair process.
Bone formation observed in the group that received chitosan/carbon nanotubes (G3/C+CNTs) was statistically higher when compared to the control group (G1/Control), with the advantage to show a denser and more regular appearance. Thus, it is evident that these effects on bone tissue are due to chitosan properties, such as biodegradation [46] and the ability to form porous structures, additionally to the feature of the surface capability of promoting cell growth [8,52]. Accordingly, the histomorphometric data of this research points to chitosan as a promising option for use in the manufacture of scaffolds, but the isolated use of chitosan can compromise some essential functions of scaffolds, such as mechanical strength [53]. For this, the addition of composites that can improve biomaterials becomes interesting, and, in this way, carbon nanotubes can be a viable alternative since they are able to modulate the behavior of cells [54].
In a study that evaluated the effect on bone repair in rat tibiae grafted with carbon nanotubes and sodium hyaluronate, it was noted that the grafted groups showed greater osteoregenerative potential than the control group [55]. Xu et al. (2019) showed that multi-walled carbon nanotubes composite scaffolds prepared by freeze-drying promoted cell proliferation in vitro [56]. Thus, the addition of nanotubes to chitosan can potentiate cellular interactions [57], thus supporting the hypothesis that chitosan associated with carbon nanotubes can stimulate the bone repair process, as demonstrated in the histomor-phometric analyses of this research [58,59,60,61,62,63,64].
The mineralization of scaffolds can further potentiate the osteogenesis process [65], however, contradictory results were demonstrated by Munhoz et al. (2018), who reported that the mineralization of collagen and chitosan sponges did not stimulate bone neoformation sufficiently for tissue repair [66]. However, it must be considered that the experimental procedure was performed on the calvaria of rats, which is not subject to biomechanical load by muscle action. Therefore, other variables must also be considered in studies with scaffolds, such as the mineralization concentration of the materials, as well as the type of bone to be studied. Therefore, in the morphometric analysis of the surgical areas, it was observed that the groups that received the mineralized scaffolds presented a statistically higher bone volume, in relation to the groups that received the non-mineralized scaffolds, as noted in the comparison between G5/C+CNTsM with G3/C+CNTs, as well as in the comparison between G6/C+CNTsM+L and G4/C+CNTs+L, in which LLLT treatment constitutes an additional variable. There is evidence in the literature demonstrating the positive action of polymers [47] and LLLT [67,68] in bone repair; however, there is no evidence of the combination of these two resources on osteogenic potential.
Thus, the analysis of the action of LLLT in the surgical area allowed us to verify the effectiveness of the photobiomodulation on the process of stimulation of bone repair, because the groups that received LLLT showed greater bone volume than their respective control groups, as observed in the comparisons between G2/Laser vs. G1/Control, G4/C+CNTs+L vs. G3/C+CNTs and G6/C+CNTsM+L vs. G5/C+CNTsM, and these promising data related to bone formation are due to the photomodulatory effects of LLLT.
Photobiomodulation consists of the use of light in non-ionizing forms, including lasers and LEDs of the visible spectrum and infrared for therapeutic purposes [69]. Its mechanism occurs from specific photoreceptors that are responsible for absorbing the light beam and for stimulating calcium transport and the mitochondrial respiratory chain, which results in increased synthesis of RNA, DNA, and cell cycle regulatory proteins essential for the significant cell proliferation and, consequently, for the production of ATP [70]. Furthermore, the light at a low radiation dose is absorbed by intracellular chromophores [71], initiating cell signaling, which may improve the differentiation of mesenchymal stromal cells into osteoblasts [72].
There is no consensus in the scientific literature regarding the laser parameters that would be effective for the treatment of bone lesions. However, in this research, the photobiomodulation protocol was created based on studies that obtained favorable results using the laser in the treatment of bone lesions. The 904 nm aluminum gallium arsenide pulsed diode laser is the most indicated in the therapeutic process of serious injuries due to its greater ability to penetrate tissues [73,74,75]. The literature also cites that this wavelength is capable of promoting an increase in blood flow in live rats, creating an ideal scenario for healing due to good tissue vascularization and efficient collagen deposition [76].
The literature describes an increase in growth factors in the laser-modulated bone formation process [26]. LLLT shows the ability to stimulate alkaline phosphatase activity and osteocalcin gene expression [77,78,79]. In this way, bone formation markers, such as OC and OPN, allow the assessment of the rate of bone formation and resorption, which are important during bone remodeling [80]. Osteopontin is a non-collagenous phosphoprotein involved in the biomineralization of bone tissue, being described as a structural element of the bone matrix [81]. Osteopontin is a secreted protein related to many events of bone metabolism and, therefore, it is used as a parameter to assess angiogenesis and cellular activity [82]. Osteocalcin participates as an important marker of bone formation, being found mainly during the final stage of differentiation of osteoblasts and in the initial stage of mineralization [83]. In the immunohistochemical analyses of this research, it was possible to observe the expression of these markers in the osteocytes of the neoformed bone in the surgical areas, as well as the presence of blood vessels through VEGF.
In this way, these morphological and immunohistochemical analyses show that the scaffold together with the LLLT protocol used in this research allowed for a more homogeneous organization of the extracellular matrix, and favored the maturation of the newly formed bone tissue, which was essential for tissue repair.

4. Materials and Methods

4.1. Experimental—Raw Materials

All solvents and salts were analytical grade and were used as received. Functionalized multi-walled carbon nanotubes (carboxylic acid > 8%) (f-MWCN) were purchased from Sigma-Aldrich and had the following characteristics: average diameter L of 9.5 nm × 1.5 μm.
Chitosan was extracted from squid pens (Doryteuthis spp.), as previously described [8]. Briefly, demineralization and deproteinization steps are necessary to isolate β-chitin and were carried out using dilute solutions of HCl and NaOH, respectively. Deacetylation of N-acetyl groups was performed using a concentrated sodium hydroxide solution (40% NaOH, w/w). The chitosan powder was obtained after the washing and drying processes. The degree of acetylation (9.05% ± 0.35) and molecular weight (4.4 × 105 g mol−1) were determined by conductometric titration and capillary viscosimetry, respectively [8].

4.2. Sample Preparation

The chitosan powder was dissolved in 1% (v/w) aqueous acetic acid solution by magnetic stirring. A 1% (w/w) chitosan solution was used for the sample preparation. Then, 0.25 mg of functionalized MWCN was slowly added to the biopolymeric solution under mechanical stirring and then sonicated in an ultrasound bath (Único® USC 1400 A) for 60 min to obtain an adequate homogeneous dispersion of the carbon nanotubes. Finally, the sample labeled CN25 was freeze-dried [34]. The alternate immersion method consists of alternating immersion cycles in calcium chloride and disodium phosphate solutions. As previously described [8], 0.12 mol·L−1 CaCl2 buffered with 0.05 mol·L−1 Tris buffer (pH 7.4) and a 0.06 mol·L−1 Na2HPO4 solution buffered with 0.05 mol·L−1 Tris buffer (pH 9.0) were the calcium and phosphate sources for the nucleation and precipitation of the apatite salt. Scaffolds were alternately placed in the solutions for 60 min and rinsed with deionized water during every change of the solution. All experiments were conducted at 37 °C. The freeze-dried mineralized scaffold, named CNM25, was prepared using two mineralization cycles.

4.3. Sample Characterization

FTIR analysis was performed for the powder chitosan and carbon nanotube. Spectra were obtained using Shimadzu IR Affinity−1 equipment at the interval of 2000–400 cm−1 and a resolution of 4 cm−1 and 64 scans. The CN25 and CN25M scaffolds were analysed in an FTIR-ATR (attenuated total reflectance) using a Bruker Tensor 27 FT-IR spectrophotometer, in the range of 4000–600 cm−1, resolution of 2 cm−1 and 64 scans.
Prior to the PBS swelling test, the scaffolds were placed in a desiccator in the presence of NaOH (s) for 24 h. The dried scaffolds were weighed (dry weight) and placed in 10 mL of the buffer solution. At predetermined times, they were removed from the liquid and weighed (wet weight), until achieving equilibrium (40 min). The process was carried out 5 times for each sample. The percentage of absorbed buffer (% absorption) was calculated by the equation: % absorption = [(wet weight − dry weight)/dry weight] × 100.
Thermogravimetric analysis was carried out in a TGA Q50 (TA Instruments®) from 25 to 800 °C at a heating rate of 10 °C min−1. A synthetic airflow of 90 mL·min−1 and sample weight of around 9 mg was employed for the measurement. The surface and calcium phosphate deposits were analysed by Scanning Electron Microscopy (SEM) (Zeiss LEO 440®, Cambridge, UK) with an Oxford detector (model 7060) LEO 440 at an accelerating voltage of 20 keV. For that, the scaffolds obtained were placed in stubs and coated with a thin layer of gold (6 nm) to improve the conductivity of the samples. Simultaneously, energy dispersive X-ray analysis (EDX) was used to determine the Ca/P ratio of the mineralized scaffold. For this analysis, the EDX equipment LEO 440® (LEO Electron Microscopy Ltd., Cambridge, UK) Oxford detector mod. 7060® (Oxford Instruments Inc., Concord, CA, USA) and 133 eV resolution were used. The selected standards were CaCO3, quartz, GaP, and Wollas (CaSiO3). Scaffold images of the surface (at a 500× magnification) were adopted to measure the pore size, where at least 40 pores of each sample were used. The ImageJ software was employed to calculate the average pore size.

4.4. Experimental Design

This research used 30 male Wistar rats (Rattus norvegicus) with 16 weeks of age and an average body weight of 400 g. This study was conducted according to the guidelines of the Declaration of Helsinki and approved by the Institutional Ethics Committee on Animal Experimentation of the Faculty of Medicine of Jundiaí, Sao Paulo, Brazil (CEUA/FMJ), and protocol code CEUA/FMJ No. 282/2016.
Furthermore, this experimental study was carried out according to the ARRIVE guidelines (Animal Research: Reporting of In Vivo Experiments) and based on the principles of the National Centre for the Replacement, Refinement, and Reduction of Animals in Research (NC3Rs) [84,85,86]. During the experimentation, the animals were monitored regarding the expression of pain by observing whether the animal was apathetic, depressed, aggressive, or overexcited, and these characteristics constitute variables in their usual behavior. Changes in walking, posture, appearance, or facial expression were also observed. Water and food consumption and clinical symptoms were also investigated.
The animals were kept in the bioterium of the Faculty of Medicine of Jundiaí and submitted to create an experimental defect in the distal metaphysis of the femur. The rats were randomly distributed into 6 groups, without predetermined inclusion or exclusion criteria, according to the treatment received: Control (G1/Control), Laser (G2/Laser), Chitosan/Carbon Nanotubes (G3/C+CNTs), Chitosan/Carbon Nanotubes/Laser (G4/C+CNTs+L), Mineralized Chitosan/Carbon Nanotubes (G5/C+CNTsM), Mineralized Chitosan/Carbon Nanotubes/Laser (G6/C+CNTsM+L) (Figure 12).
The PBM protocol used for bone repair in this experimental protocol was based on previous experiments [23,24,26], which used a low-level laser in pulsed mode (Gallium Arsenide-GaAs), with a wavelength of 904 nm. The animals in groups G2/Laser, G4/C+CNTs+L and G6/C+CNTsM+L received this treatment of LLLT in the surgical area of the femur for 5 weeks, with application intervals of 48 h [87,88,89]. The complete photobiomodulation protocol is shown in Table 1.

4.5. Surgical Procedure

The animals were anesthetized with a solution of Xylazine (Vetaset®—Fort Dodge Saúde Animal Ltda., Campinas-SP, Brazil) and Ketamine (Dopalen®—Agibrands of Brazil LTDA, Campinas, Brazil) in the proportion of 1:1. This solution was applied at a dose of 1 mL/Kg of body mass, via the gluteal intramuscular route. After antisepsis with Riohex® 4% degerming agent and trichotomy of the left hind law, a skin incision was made on its anterior face, reflecting the adjacent muscles to expose the distal metaphysis of the femur. Using a surgical drill of 3 mm in diameter, coupled to the pen of a mini motor (Eltec LB-100®, Eltec Elektronik AG, Mainz, Germany), a bone defect was made until reaching the medullary canal. In groups C+CNTs, C+CNTs+L, C+CNTsM, and C+CNTsM+L, bone defects were grafted with chitosan scaffolds/carbon nanotubes. A sample size of 2.5 mm was used for the in vivo test.

4.6. Macroscopic and Radiological Analysis of the Surgical Area

Five weeks after surgery, the animals were submitted to painless death induced by a high dose of intraperitoneal anesthetic, followed by a surgical procedure of pneumothorax. After death was confirmed by the absence of vital signs in each animal, disarticulation was performed in the hip and knee region, preserving the left femur. The surgical area was photodocumented, and the macroscopic conditions of anatomopathological reactions were evaluated. Then, the surgical areas of the animals were radiographed with an Odel 300 mA device, focus with 100 mA, time of 0.06 s, and radiation of 40 kV (X-ray tube voltage). Radiographic images were digitized using the Agfa system. The radiographic images were studied in order to assess the integrity of the bone defect in the surgical area.

4.7. Histological Analysis of the Surgical Area

The samples from the operated femurs were fixed in formaldehyde solution, then decalcified and subsequently submitted to routine histological techniques. From each sample, 5 μm-thick semi-serial microscopic sections were obtained. Histological slides were stained with Masson’s Trichrome for the evaluation and differentiation of the original bone and new bone formation. Picrosirius Red (saturated aqueous solution of picric acid added to 0.1 g of Syrian Red F3b, Sirius Red F3B-Bayer®) was also used to label the fibrillar constituents of the extracellular matrix in the area of the bone lesion through polarized light microscopy. The qualitative analysis of the histological sections of the surgical area allowed the evaluation of the bone failure repair process through the observation of the characteristics of the newly formed bone. A Nikon Eclipse E200 optical microscope was used, and the digital images were analysed through objective lenses with 4× and 10× magnification.

4.8. Histomorphometric and Statistical Analyses of the Bone Volume Formed in the Surgical Area

Slides stained with Masson’s Trichrome and a Nikon Eclipse E200® light microscope with a 4× magnification objective were used in this analysis, and the slides were photographed. Using the Motic Image Plus 2.0 ML software, the volume of the bone defect area was delimited in the histological images, as well as the volume of the newly formed bone for each animal studied. From these values, the percentage of bone formed in the surgical area was obtained. These data were transcribed into the BioEstat 5.3 software, applying the ANOVA test followed by the Tukey’s test for statistical evaluation between the groups with a significance level of p < 0.05.

4.9. Immunohistochemical Analysis of Osteocalcin and Osteopontin Labeling

Anti-osteocalcin (Osteocalcin-BIOSS® Rabbit Policlonal bs-4917R AGO9294227) and anti-osteopontin (Osteopontin Polyclonal Antibody®-bs-0026R) antibodies were used for this analysis. Initially, the slides were deparaffinized in xylol and hydrated. Endogenous peroxidase was blocked with hydrogen peroxide for 10 min, followed by washing in running distilled water. The primary antibody (previously standardized) was diluted in bovine serum albumin (BSA). The slides were placed with the antibody on the sections in a humid chamber and incubated overnight in the refrigerator. Subsequently, they were washed with phosphate-buffered saline (PBS) pH 7.4 and incubated in a humid chamber with a secondary antibody (30 min in an incubator at 37 °C). Thereafter, the slides were washed with PBS, stained with diaminobenzidine (DAB) chromogen (5 min), and counterstained with Hematoxylin for approximately 1 min. In order to remove excess dye, the slides were washed in running water, and the sections were dehydrated and placed in the incubator to dry completely. Finally, the sections were covered with coverslips using Entellan (Merck) [25].

4.10. Immunohistochemical Analysis—VEGF

Immunohistochemistry was performed as previously described [90], on 3 µm whole sections, using VEFG (BioSB®—BSB 6053—Clone RBT-VEGF). Briefly, sections were deparaffinized with xylene and dehydrated in alcohol. Endogenous peroxidase was blocked with 3% hydrogen peroxide. Antigen retrieval was achieved by immersing slides in citrate buffer, pH 5.8 per 30 min, in a commercially available pressure cooker (Pascal®, Dako, Carpenteria, CA, USA). The sections were incubated in a humid chamber with the specific primary antibodies (1:200) at 37 °C, for 40 min, and after, at 4 °C overnight. Then, slides were washed in PBS 0.1 mol L−1, pH 7.4 and a secondary antibody was used (kit Novolink Leica®—Cod. RE 7280-K) during 30 min, at 37 °C. The Advance HRP Detection System® (Dako K3467) was used according to the manufacturer protocol. Finally, the slides were counterstained with Harris’ hematoxylin for 30 s, dehydrated, and mounted in Entellan® (Merck, Darmstadt, Germany). Internal and external, positive and negative controls were used in order to validate the reactions [87].

5. Conclusions

Based on histomorphometric and immunohistochemical evidence of bone formation in the surgical area, it was concluded that the chitosan/carbon nanotube scaffolds contribute to the regeneration of lesions in long bones, such as the femur of rats, and that additional factors, such as mineralization and LLLT, can stimulate this bone repair process. Thus, this scaffold can be considered as an alternative in trauma therapies that require surgical intervention, with bone grafting and rapid rehabilitation processes, as well as in the advancement of new studies of tissue engineering in polymeric biomaterials and photobiomodulators for bone regeneration.

Author Contributions

Conceptualization, S.K.S., M.R.d.C., A.M.G.P., M.M.H. and V.d.C.A.M.; Methodology, S.K.S., M.R.d.C., A.M.G.P., M.M.H. and V.d.C.A.M.; Validation, S.K.S. and M.R.d.C.; Formal Analysis, A.M.G.P.; V.d.C.A.M., M.M.H., F.M.N., A.A.P. and V.R.S.; Investigation, A.M.G.P., V.d.C.A.M., M.M.H., M.H.M.K. and J.F.R.F.; Writing—Original Draft Preparation, S.K.S., A.M.G.P., V.d.C.A.M., M.M.H., D.V.B. and R.L.B.; Writing—Review & Editing, S.K.S. and M.R.d.C.; Supervision, M.R.d.C.; Project Administration, M.R.d.C. All authors have read and agreed to the published version of the manuscript.

Funding

The present study was financed in part by the Coordenação de Aperfeiçoamento de Pessoal de Nível Superior—Brasil (CAPES)—Finance Code 001 (S.K.S. and M.M.H.).

Institutional Review Board Statement

The study was conducted according to the guidelines of the Declaration of Helsinki, and approved by the Institutional Review Board (or Ethics Committee) of the Animal Research Ethics Committee of the Faculty of Medicine of Jundiaí, Brazil (CEUA/FMJ), protocol code CEUA/FMJ No. 282/2016.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Acknowledgments

We thank the School of Medicine of Jundiaí, especially NAPED (Núcleo de Apoio à Pesquisa e à Docência).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Zhu, L.; Luo, D.; Liu, Y. Effect of the nano/microscale structure of biomaterial scaffolds on bone regeneration. Int. J. Oral. Sci. 2020, 12, 6. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  2. Ovsianikov, A.; Khademhosseini, A.; Mironov, V. The Synergy of Scaffold-Based and Scaffold-Free Tissue Engineering Strategies. Trends Biotechnol. 2018, 36, 348–357. [Google Scholar] [CrossRef] [PubMed]
  3. Pacelli, S.; Basu, S.; Whitlow, J.; Chakravarti, A.; Acosta, F.; Varshney, A.; Modaresi, S.; Berkland, C.; Paul, A. Strategies to develop endogenous stem cell-recruiting bioactive materials for tissue repair and regeneration. Adv. Drug Deliv. Rev. 2017, 120, 50–70. [Google Scholar] [CrossRef] [PubMed]
  4. Kumar, S.; Nehra, M.; Kedia, D.; Dilbaghi, N.; Tankeshwar, K.; Kim, K.H. Nanotechnology-based biomaterials for orthopaedic applications: Recent advances and future prospects. Mater. Sci. Eng. C Mater. Biol. Appl. 2020, 106, 110154. [Google Scholar] [CrossRef]
  5. Zhang, H.; Yang, L.; Yang, X.G.; Wang, F.; Feng, J.T.; Hua, K.C.; Li, Q.; Hu, Y.C. Demineralized Bone Matrix Carriers and their Clinical Applications: An Overview. Orthop. Surg. 2019, 11, 725–737. [Google Scholar] [CrossRef]
  6. Lopes, D.; Martins-Cruz, C.; Oliveira, M.B.; Mano, J.F. Bone physiology as inspiration for tissue regenerative therapies. Biomaterials 2018, 185, 240–275. [Google Scholar] [CrossRef]
  7. Grover, C.N.; Cameron, R.E.; Best, S.M. Investigating the morphological, mechanical and degradation properties of scaffolds comprising collagen, gelatin and elastin for use in soft tissue engineering. J. Mech. Behav. Biomed. Mater. 2012, 10, 62–74. [Google Scholar] [CrossRef]
  8. Horn, M.M.; Martins, V.C.A.; Plepis, A.M.G. Interaction of anionic collagen with chitosan: Effect on thermal and morphological characteristics. Carbohydr. Polym. 2009, 77, 239–243. [Google Scholar] [CrossRef]
  9. Aguilar, A.; Zein, N.; Harmouch, E.; Hafdi, B.; Bornert, F.; Offner, D.; Clauss, F.; Fioretti, F.; Huck, O.; Benkirane-Jessel, N.; et al. Application of Chitosan in Bone and Dental Engineering. Molecules 2019, 24, 1–17. [Google Scholar] [CrossRef] [Green Version]
  10. Thrivikraman, G.; Athirasala, A.; Twohig, C.; Boda, S.K.; Bertassoni, L.E. Biomaterials for Craniofacial Bone Regeneration. Dent. Clin. N. Am. 2017, 61, 835–856. [Google Scholar] [CrossRef]
  11. Zhou, D.; Qi, C.; Chen, Y.X.; Zhu, Y.J.; Sun, T.W.; Chen, F.; Zhang, C.Q. Comparative study of porous hydroxyapatite/chitosan and whitlockite/chitosan scaffolds for bone regeneration in calvarial defects. Int. J. Nanomed. 2017, 12, 2673–2687. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  12. Singh, B.N.; Veeresh, V.; Mallick, S.P.; Jain, Y.; Sinha, S.; Rastogi, A.; Srivastava, P. Design and evaluation of chitosan/chondroitin sulfate/nano-bioglass based composite scaffold for bone tissue engineering. Int. J. Biol. Macromol. 2019, 133, 817–830. [Google Scholar] [CrossRef] [PubMed]
  13. Brun, P.; Zamuner, A.; Battocchio, C.; Cassari, L.; Todesco, M.; Graziani, V.; Iucci, G.; Marsotto, M.; Tortora, L.; Secchi, V.; et al. Bio-Functionalized Chitosan for Bone Tissue Engineering. Int. J. Mol. Sci. 2021, 22, 5916. [Google Scholar] [CrossRef] [PubMed]
  14. Kowalczyk, P.; Podgórski, R.; Wojasiński, M.; Gut, G.; Bojar, W.; Ciach, T. Chitosan-Human Bone Composite Granulates for Guided Bone Regeneration. Int. J. Mol. Sci. 2021, 22, 2324. [Google Scholar] [CrossRef] [PubMed]
  15. Peranidze, K.; Safronova, T.V.; Kildeeva, N.R. Fibrous Polymer-Based Composites Obtained by Electrospinning for Bone Tissue Engineering. Polymers 2022, 14, 96. [Google Scholar] [CrossRef]
  16. Krystyjan, M.; Khachatryan, G.; Khachatryan, K.; Konieczna-Molenda, A.; Grzesiakowska, A.; Kuchta-Gładysz, M.; Kawecka, A.; Grzebieniarz, W.; Nowak, N. The Functional and Application Possibilities of Starch/Chitosan Polymer Composites Modified by Graphene Oxide. Int. J. Mol. Sci. 2022, 23, 5956. [Google Scholar] [CrossRef]
  17. Ilyas, R.A.; Aisyah, H.A.; Nordin, A.H.; Ngadi, N.; Zuhri, M.Y.M.; Asyraf, M.R.M.; Sapuan, S.M.; Zainudin, E.S.; Sharma, S.; Abral, H.; et al. Natural-Fiber-Reinforced Chitosan, Chitosan Blends and Their Nanocomposites for Various Advanced Applications. Polymers 2022, 14, 874. [Google Scholar] [CrossRef]
  18. Kocak, F.Z.; Yar, M.; Rehman, I.U. Hydroxyapatite-Integrated, Heparin- and Glycerol-Functionalized Chitosan-Based Injectable Hydrogels with Improved Mechanical and Proangiogenic Performance. Int. J. Mol. Sci. 2022, 23, 5370. [Google Scholar] [CrossRef]
  19. Qasim, S.B.; Zafar, M.S.; Najeeb, S.; Khurshid, Z.; Shah, A.H.; Husain, S.; Rehman, I.U. Electrospinning of Chitosan-Based Solutions for Tissue Engineering and Regenerative Medicine. Int. J. Mol. Sci. 2018, 19, 407. [Google Scholar] [CrossRef] [Green Version]
  20. Bellingeri, R.; Mulko, L.; Molina, M.; Picco, N.; Alustiza, F.; Grosso, C.; Vivas, A.; Acevedo, D.F.; Barbero, C.A. Nanocomposites based on pH-sensitive hydrogels and chitosan decorated carbon nanotubes with antibacterial properties. Mater. Sci. Eng. C Mater. Biol. Appl. 2018, 90, 461–467. [Google Scholar] [CrossRef] [Green Version]
  21. Eivazzadeh-Keihan, R.; Maleki, A.; de la Guardia, M.; Bani, M.S.; Chenab, K.K.; Pashazadeh-Panahi, P.; Baradaran, B.; Mokhtarzadeh, A.; Hamblin, M.R. Carbon based nanomaterials for tissue engineering of bone: Building new bone on small black scaffolds: A review. J. Adv. Res. 2019, 18, 185–201. [Google Scholar] [CrossRef] [PubMed]
  22. Lawton, K.; Le, H.; Tredwin, C.; Handy, R.D. Carbon Nanotube Reinforced Hydroxyapatite Nanocomposites As Bone Implants: Nanostructure, Mechanical Strength And Biocompatibility. Int. J. Nanomed. 2019, 14, 7947–7962. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  23. Buchaim, D.V.; Andreo, J.C.; Pomini, K.T.; Barraviera, B.; Ferreira, R.S.; Duarte, M.A.H.; Alcalde, M.P.; Reis, C.H.B.; Teixeira, D.B.; Bueno, C.R.S.; et al. A biocomplex to repair experimental critical size defects associated with photobiomodulation therapy. J. Venom. Anim. Toxins Incl. Trop. Dis. 2022, 28, e20210056. [Google Scholar] [CrossRef] [PubMed]
  24. De Oliveira Gonçalves, J.B.; Buchaim, D.V.; de Souza Bueno, C.R.; Pomini, K.T.; Barraviera, B.; Júnior, R.S.F.; Andreo, J.C.; de Castro Rodrigues, A.; Cestari, T.M.; Buchaim, R.L. Effects of low-level laser therapy on autogenous bone graft stabilized with a new heterologous fibrin sealant. J. Photochem. Photobiol. 2016, 162, 663–668. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  25. Dos Santos, A.B.; Binoki, D.; Silva, L.F.; de Araujo, B.B.; Otter, I.D.; Annoni, R.; Tsokos, M.; Stein, R.T.; Hiemstra, P.S.; Rabe, K.F.; et al. Immune cell profile in infants’ lung tissue. Ann. Anat. 2013, 195, 596–604. [Google Scholar] [CrossRef] [PubMed]
  26. Rosso, M.P.O.; Oyadomari, A.T.; Pomini, K.T.; Della Coletta, B.B.; Shindo, J.; Ferreira Júnior, R.S.; Barraviera, B.; Cassaro, C.V.; Buchaim, D.V.; Teixeira, D.B.; et al. Photobiomodulation Therapy Associated with Heterologous Fibrin Biopolymer and Bovine Bone Matrix Helps to Reconstruct Long Bones. Biomolecules 2020, 10, 383. [Google Scholar] [CrossRef] [Green Version]
  27. Theodoro, L.H.; Rocha, G.S.; Ribeiro Junior, V.L.; Sakakura, C.E.; de Mello Neto, J.M.; Garcia, V.G.; Ervolino, E.; Marcantonio Junior, E. Bone Formed After Maxillary Sinus Floor Augmentation by Bone Autografting with Hydroxyapatite and Low-Level Laser Therapy: A Randomized Controlled Trial with Histomorphometrical and Immunohistochemical Analyses. Implant. Dent. 2018, 27, 547–554. [Google Scholar] [CrossRef]
  28. Gurler, G.; Gursoy, B. Investigation of effects of low level laser therapy in distraction osteogenesis. J. Stomatol. Oral. Maxillofac. Surg. 2018, 119, 469–476. [Google Scholar] [CrossRef]
  29. Rodrigues, M.A.V.; Horn, M.M.; Martins, V.C.A.; Plepis, A.M.G. Single-wall carbon nanotubes-chitosan nanocomposites: Surface wettability, mechanical and thermal properties. Materialwiss. Werkstofftech. 2021, 52, 400–408. [Google Scholar] [CrossRef]
  30. Mahmoodian, H.; Moradi, O. Preparation and characterization of 2-hydroxyethyl methacrylate–chitosan functionalized multiwall carbon nanotubes nanocomposites. Polym. Compos. 2014, 35, 495–500. [Google Scholar] [CrossRef]
  31. Milan, E.P.; Rodrigues, M.A.V.; Martins, V.C.A.; Plepis, A.M.G.; Fuhrmann-Lieker, T.; Horn, M.M. Mineralization of phosphorylated fish skin collagen/mangosteen scaffolds as potential materials for bone tissue regeneration. Molecules 2021, 26, 2899. [Google Scholar] [CrossRef] [PubMed]
  32. Horn, M.M.; Martins, V.C.A.; Plepis, A.M.G. In vitro mineralization study of chitosan/carbon nanotubes scaffolds: Effect of mineralization cycles. Macromol. Symp. 2018, 378, 1600148. [Google Scholar] [CrossRef]
  33. Bilton, M.B.; Brown, A.P.; Milne, S.J. Sol-gel synthesis and characterisation of nano-scale hydroxyapatite. J. Phys. Conf. Ser. 2010, 241, 012052. [Google Scholar] [CrossRef]
  34. Wang, Y.; Yang, C.; Chen, X.; Zhao, N. Biomimetic formation of hydroxyapatite/collagen matrix composite. Adv. Eng. Mater. 2006, 8, 97–100. [Google Scholar] [CrossRef]
  35. Brahimi, S.; Ressler, A.; Boumchedda, K.; Hamidouche, M.; Kenzour, A.; Djafar, R.; Antunović, M.; Bauer, L.; Hvizdoš, P.; Ivanković, H. Preparation and characterization of biocomposites based on chitosan and biomimetic hydroxyapatite derived from natural phosphate rocks. Mater. Chem. Phys. 2022, 276, 125421. [Google Scholar] [CrossRef]
  36. Valtanen, R.S.; Yang, Y.P.; Gurtner, G.C.; Maloney, W.J.; Lowenberg, D.W. Synthetic and Bone tissue engineering graft substitutes: What is the future? Injury 2021, 52, S72–S77. [Google Scholar] [CrossRef]
  37. Gómez-Barrena, E.; Padilla-Eguiluz, N.; Rosset, P.; Gebhard, F.; Hernigou, P.; Baldini, N.; Rouard, H.; Sensebé, L.; Gonzalo-Daganzo, R.M.; Giordano, R.; et al. Early efficacy evaluation of mesenchymal stromal cells (MSC) combined to biomaterials to treat long bone non-unions. Injury 2020, 51, S63–S73. [Google Scholar] [CrossRef] [Green Version]
  38. Paramita, P.; Ramachandran, M.; Narashiman, S.; Nagarajan, S.; Sukumar, D.K.; Chung, T.W.; Ambigapathi, M. Sol-gel based synthesis and biological properties of zinc integrated nano bioglass ceramics for bone tissue regeneration. J. Mater. Sci. Mater. Med. 2021, 32, 5. [Google Scholar] [CrossRef]
  39. Yan, Y.; Cheng, B.; Chen, K.; Cui, W.; Qi, J.; Li, X.; Deng, L. Enhanced Osteogenesis of Bone Marrow-Derived Mesenchymal Stem Cells by a Functionalized Silk Fibroin Hydrogel for Bone Defect Repair. Adv. Healthc. Mater. 2019, 8, e1801043. [Google Scholar] [CrossRef]
  40. Anesi, A.; Generali, L.; Sandoni, L.; Pozzi, S.; Grande, A. From Osteoclast Differentiation to Osteonecrosis of the Jaw: Molecular and Clinical Insights. Int. J. Mol. Sci. 2019, 20, 4925. [Google Scholar] [CrossRef] [Green Version]
  41. Chen, D.; Gu, S.; Fu, Y.; Zhu, Y.; Liu, C.; Li, G.; Yu, G.; Pan, C. Tunable porosity of nanoporous organic polymers with hierarchical pores for enhanced CO2 capture. Polym. Chem. 2016, 7, 3416–3422. [Google Scholar] [CrossRef]
  42. Reddy, M.S.B.; Ponnamma, D.; Choudhary, R.; Sadasivuni, K.K. A Comparative Review of Natural and Synthetic Biopolymer Composite Scaffolds. Polymers 2021, 13, 1105. [Google Scholar] [CrossRef] [PubMed]
  43. Dodero, A.; Scarfi, S.; Mirata, S.; Sionkowska, A.; Vicini, S.; Alloisio, M.; Castellano, M. Effect of Crosslinking Type on the Physical-Chemical Properties and Biocompatibility of Chitosan-Based Electrospun Membranes. Polymers 2021, 13, 831. [Google Scholar] [CrossRef] [PubMed]
  44. Roffi, A.; Kon, E.; Perdisa, F.; Fini, M.; Di Martino, A.; Parrilli, A.; Salamanna, F.; Sandri, M.; Sartori, M.; Sprio, S.; et al. A Composite Chitosan-Reinforced Scaffold Fails to Provide Osteochondral Regeneration. Int. J. Mol. Sci. 2019, 20, 2227. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  45. Islam, M.M.; Shahruzzaman, M.; Biswas, S.; Nurus Sakib, M.; Rashid, T.U. Chitosan based bioactive materials in tissue engineering applications-A review. Bioact. Mater. 2020, 5, 164–183. [Google Scholar] [CrossRef]
  46. Midha, S.; Jain, K.G.; Bhaskar, N.; Kaur, A.; Rawat, S.; Giri, S.; Basu, B.; Mohanty, S. Tissue-specific mesenchymal stem cell-dependent osteogenesis in highly porous chitosan-based bone analogs. Stem Cells Trans. Med. 2021, 10, 303–319. [Google Scholar] [CrossRef]
  47. Oryan, A.; Sahvieh, S. Effectiveness of chitosan scaffold in skin, bone and cartilage healing. Int. J. Biol. Macromol. 2017, 104, 1003–1011. [Google Scholar] [CrossRef]
  48. Pei, B.; Wang, W.; Dunne, N.; Li, X. Applications of Carbon Nanotubes in Bone Tissue Regeneration and Engineering: Superiority, Concerns, Current Advancements, and Prospects. Nanomaterials 2019, 9, 1501. [Google Scholar] [CrossRef] [Green Version]
  49. Türk, S.; Altınsoy, I.; Çelebi Efe, G.; Ipek, M.; Özacar, M.; Bindal, C. 3D porous collagen/functionalized multiwalled carbon nanotube/chitosan/hydroxyapatite composite scaffolds for bone tissue engineering. Mater. Sci. Eng. C Mater. Biol. Appl. 2018, 92, 757–768. [Google Scholar] [CrossRef]
  50. Da Cunha, M.R.; Alves, M.C.; Calegari, A.R.A.; Iatecola, A.; Galdeano, E.A.; Galdeano, T.L.; de Azevedo e Souza Munhoz, M.; Plepis, A.M.G.; Martins, V.C.A.; Horn, M.M. In vivo study of the osteoregenerative potential of polymer membranes consisting of chitosan and carbon nanotubes. Mater. Res. 2017, 20, 819–825. [Google Scholar] [CrossRef] [Green Version]
  51. Sathiyaseelan, A.; Saravanakumar, K.; Mariadoss, A.V.A.; Wang, M.H. Antimicrobial and Wound Healing Properties of FeO Fabricated Chitosan/PVA Nanocomposite Sponge. Antibiotics 2021, 10, 524. [Google Scholar] [CrossRef] [PubMed]
  52. Kozusko, S.D.; Riccio, C.; Goulart, M.; Bumgardner, J.; Jing, X.L.; Konofaos, P. Chitosan as a Bone Scaffold Biomaterial. J. Craniofac. Surg. 2018, 29, 1788–1793. [Google Scholar] [CrossRef] [PubMed]
  53. LogithKumar, R.; KeshavNarayan, A.; Dhivya, S.; Chawla, A.; Saravanan, S.; Selvamurugan, N. A review of chitosan and its derivatives in bone tissue engineering. Carbohydr. Polym. 2016, 151, 172–188. [Google Scholar] [CrossRef] [PubMed]
  54. Ignat, S.R.; Lazăr, A.D.; Şelaru, A.; Samoilă, I.; Vlăsceanu, G.M.; Ioniţă, M.; Radu, E.; Dinescu, S.; Costache, M. Versatile Biomaterial Platform Enriched with Graphene Oxide and Carbon Nanotubes for Multiple Tissue Engineering Applications. Int. J. Mol. Sci. 2019, 20, 3868. [Google Scholar] [CrossRef] [Green Version]
  55. Andrade, V.B.; Sá, M.A.; Mendes, R.M.; Martins-Júnior, P.A.; Silva, G.A.B.; Sousa, B.R.; Caliari, M.V.; Ávila, E.S.; Ladeira, L.O.; Resende, R.R.; et al. Enhancement of Bone Healing by Local Administration of Carbon Nanotubes Functionalized with Sodium Hyaluronate in Rat Tibiae. Cells Tissues Organs 2017, 204, 137–149. [Google Scholar] [CrossRef]
  56. Xu, J.; Hu, X.; Jiang, S.; Wang, Y.; Parungao, R.; Zheng, S.; Nie, Y.; Liu, T.; Song, K. The Application of Multi-Walled Carbon Nanotubes in Bone Tissue Repair Hybrid Scaffolds and the Effect on Cell Growth In Vitro. Polymers 2019, 11, 230. [Google Scholar] [CrossRef] [Green Version]
  57. Lekshmi, G.; Sana, S.S.; Nguyen, V.H.; Nguyen, T.H.C.; Nguyen, C.C.; Le, Q.V.; Peng, W. Recent Progress in Carbon Nanotube Polymer Composites in Tissue Engineering and Regeneration. Int. J. Mol. Sci. 2020, 21, 6440. [Google Scholar] [CrossRef]
  58. Francis, A.P.; Devasena, T. Toxicity of carbon nanotubes: A review. Toxicol. Ind. Health 2018, 34, 200–210. [Google Scholar] [CrossRef]
  59. Kobayashi, N.; Izumi, H.; Morimoto, Y. Review of toxicity studies of carbon nanotubes. J. Occup. Health 2017, 59, 394–407. [Google Scholar] [CrossRef] [Green Version]
  60. Mohanta, D.; Patnaik, S.; Sood, S.; Das, N. Carbon nanotubes: Evaluation of toxicity at biointerfaces. J. Pharm. Anal. 2019, 9, 293–300. [Google Scholar] [CrossRef]
  61. Yuan, X.; Zhang, X.; Sun, L.; Wei, Y.; Wei, X. Cellular Toxicity and Immunological Effects of Carbon-based Nanomaterials. Part. Fibre Toxicol. 2019, 16, 18. [Google Scholar] [CrossRef] [PubMed]
  62. Liu, Y.; Zhao, Y.; Sun, B.; Chen, C. Understanding the toxicity of carbon nanotubes. Acc. Chem. Res. 2013, 46, 702–713. [Google Scholar] [CrossRef] [PubMed]
  63. Rodriguez-Yañez, Y.; Muñoz, B.; Albores, A. Mechanisms of toxicity by carbon nanotubes. Toxicol. Mech. Methods 2013, 23, 178–195. [Google Scholar] [CrossRef] [PubMed]
  64. Jafar, A.; Alshatti, Y.; Ahmad, A. Carbon nanotube toxicity: The smallest biggest debate in medical care. Cogent Med. 2016, 3, 1217970. [Google Scholar] [CrossRef]
  65. Rödel, M.; Baumann, K.; Groll, J.; Gbureck, U. Simultaneous structuring and mineralization of silk fibroin scaffolds. J. Tissue Eng. 2018, 9, 2041731418788509. [Google Scholar] [CrossRef] [Green Version]
  66. Munhoz, M.A.S.; Hirata, H.H.; Plepis, A.M.G.; Martins, V.C.A.; Cunha, M.R. Use of collagen/chitosan sponges mineralized with hydroxyapatite for the repair of cranial defects in rats. Injury 2018, 49, 2154–2160. [Google Scholar] [CrossRef]
  67. Pomini, K.T.; Buchaim, D.V.; Andreo, J.C.; Rosso, M.P.O.; Della Coletta, B.B.; German, I.J.S.; Biguetti, A.C.C.; Shinohara, A.L.; Rosa Júnior, G.M.; Cosin Shindo, J.V.T.; et al. Fibrin Sealant Derived from Human Plasma as a Scaffold for Bone Grafts Associated with Photobiomodulation Therapy. Int. J. Mol. Sci. 2019, 20, 1761. [Google Scholar] [CrossRef] [Green Version]
  68. Escudero, J.S.B.; Perez, M.G.B.; de Oliveira Rosso, M.P.; Buchaim, D.V.; Pomini, K.T.; Campos, L.M.G.; Audi, M.; Buchaim, R.L. Photobiomodulation therapy (PBMT) in bone repair: A systematic review. Injury 2019, 50, 1853–1867. [Google Scholar] [CrossRef]
  69. Hochman, L. Photobiomodulation Therapy in Veterinary Medicine: A Review. Top. Companion Anim. Med. 2018, 33, 83–88. [Google Scholar] [CrossRef]
  70. Hamblin, M.R. Mechanisms and applications of the anti-inflammatory effects of photobiomodulation. AIMS Biophys. 2017, 4, 337–361. [Google Scholar] [CrossRef]
  71. Ninomiya, T.; Miyamoto, Y.; Ito, T.; Yamashita, A.; Wakita, M.; Nishisaka, T. High-intensity pulsed laser irradiation accelerates bone formation in metaphyseal trabecular bone in rat femur. J. Bone Miner. Metab. 2003, 21, 67–73. [Google Scholar] [CrossRef] [PubMed]
  72. Kushibiki, T.; Hirasawa, T.; Okawa, S.; Ishihara, M. Low Reactive Level Laser Therapy for Mesenchymal Stromal Cells Therapies. Stem Cells Int. 2015, 2015, 974864. [Google Scholar] [CrossRef] [PubMed]
  73. Joensen, J.; Ovsthus, K.; Reed, R.K.; Hummelsund, S.; Iversen, V.V.; Lopes-Martins, R.; Bjordal, J.M. Skin penetration time-profiles for continuous 810 nm and Superpulsed 904 nm lasers in a rat model. Photomed. Laser Surg. 2012, 30, 688–694. [Google Scholar] [CrossRef] [PubMed]
  74. Anders, J.J.; Wu, X. Comparison of Light Penetration of Continuous Wave 810 nm and Superpulsed 904 nm Wavelength Light in Anesthetized Rats. Photomed. Laser Surg. 2016, 34, 418–424. [Google Scholar] [CrossRef]
  75. Haslerud, S.; Naterstad, I.F.; Bjordal, J.M.; Lopes-Martins, R.A.B.; Magnussen, L.H.; Leonardo, P.S.; Marques, R.H.; Joensen, J. Achilles Tendon Penetration for Continuous 810 nm and Superpulsed 904 nm Lasers Before and After Ice Application: An In Situ Study on Healthy Young Adults. Photomed. Laser Surg. 2017, 35, 567–575. [Google Scholar] [CrossRef]
  76. Gonçalves, R.V.; Mezêncio, J.M.; Benevides, G.P.; Matta, S.L.; Neves, C.A.; Sarandy, M.M.; Vilela, E.F. Effect of gallium-arsenide laser, gallium-aluminum-arsenide laser and healing ointment on cutaneous wound healing in Wistar rats. Braz. J. Med. Biol. Res. 2010, 43, 350–355. [Google Scholar] [CrossRef] [Green Version]
  77. Buchignani, V.C.; Germano, E.J.; Dos Santos, L.M.; Gulinelli, J.L.; Ishikiriama, B.L.C.; Orcini, W.A.; Rivera, L.M.L.; Santos, P.L. Effect of low-level laser therapy and zoledronic acid on bone repair process. Lasers Med. Sci. 2019, 34, 1081–1088. [Google Scholar] [CrossRef]
  78. Matos, F.S.; Godolphim, F.J.; Albuquerque-Júnior, R.L.; Paranhos, L.R.; Rode, S.M.; Carvalho, C.A.; Ribeiro, M.A. Laser phototherapy induces angiogenesis in the periodontal tissue after delayed tooth replantation in rats. J. Clin. Exp. Dent. 2018, 10, e335–e340. [Google Scholar] [CrossRef] [Green Version]
  79. Tas Deynek, G.; Ramoglu, S.I. Effects of different settings for 940 nm diode laser on expanded suture in rats. Angle Orthod. 2019, 89, 446–454. [Google Scholar] [CrossRef] [Green Version]
  80. Camati, P.R.; Giovanini, A.F.; de Miranda Peixoto, H.E.; Schuanka, C.M.; Giacomel, M.C.; de Araújo, M.R.; Zielak, J.C.; Scariot, R.; Deliberador, T.M. Immunoexpression of IGF1, IGF2, and osteopontin in craniofacial bone repair associated with autogenous grafting in rat models treated with alendronate sodium. Clin. Oral. Investig. 2017, 21, 1895–1903. [Google Scholar] [CrossRef]
  81. Depalle, B.; McGilvery, C.M.; Nobakhti, S.; Aldegaither, N.; Shefelbine, S.J.; Porter, A.E. Osteopontin regulates type I collagen fibril formation in bone tissue. Acta Biomater. 2021, 120, 194–202. [Google Scholar] [CrossRef] [PubMed]
  82. Si, J.; Wang, C.; Zhang, D.; Wang, B.; Zhou, Y. Osteopontin in Bone Metabolism and Bone Diseases. Med. Sci. Monit. 2020, 26, e919159. [Google Scholar] [CrossRef] [PubMed]
  83. Kresnoadi, U.; Rahmania, P.N.; Caesar, H.U.; Djulaeha, E.; Agustono, B.; Ari, M.D.A. The role of the combination of Moringa oleifera leaf extract and demineralized freeze-dried bovine bone xenograft (xenograft) as tooth extraction socket preservation materials on osteocalcin and transforming growth factor-beta 1 expressions in alveolar bone of Cavia cobaya. J. Indian Prosthodont Soc. 2019, 19, 120–125. [Google Scholar] [CrossRef] [PubMed]
  84. Burden, N.; Chapman, K.; Sewell, F.; Robinson, V. Pioneering better science through the 3Rs: An introduction to the national centre for the replacement, refinement, and reduction of animals in research (NC3Rs). J. Am. Assoc. Lab. Anim. Sci. 2015, 54, 198–208. [Google Scholar] [PubMed]
  85. Percie du Sert, N.; Ahluwalia, A.; Alam, S.; Avey, M.T.; Baker, M.; Browne, W.J.; Clark, A.; Cuthill, I.C.; Dirnagl, U.; Emerson, M.; et al. Reporting animal research: Explanation and elaboration for the ARRIVE guidelines 2.0. PLoS Biol. 2020, 18, e3000411. [Google Scholar] [CrossRef] [PubMed]
  86. Percie du Sert, N.; Hurst, V.; Ahluwalia, A.; Alam, S.; Avey, M.T.; Baker, M.; Browne, W.J.; Clark, A.; Cuthill, I.C.; Dirnagl, U.; et al. The ARRIVE guidelines 2.0: Updated guidelines for reporting animal research. PLoS Biol. 2020, 18, e3000410. [Google Scholar] [CrossRef]
  87. Barbosa, D.; de Souza, R.A.; Xavier, M.; da Silva, F.F.; Arisawa, E.A.; Villaverde, A.G. Effects of low-level laser therapy (LLLT) on bone repair in rats: Optical densitometry analysis. Lasers Med. Sci. 2013, 28, 651–656. [Google Scholar] [CrossRef]
  88. Pinheiro, A.L.; Gerbi, M.E. Photoengineering of bone repair processes. Photomed. Laser Surg. 2006, 24, 169–178. [Google Scholar] [CrossRef]
  89. Weber, J.B.; Pinheiro, A.L.; de Oliveira, M.G.; Oliveira, F.A.; Ramalho, L.M. Laser therapy improves healing of bone defects submitted to autologous bone graft. Photomed. Laser Surg. 2006, 24, 38–44. [Google Scholar] [CrossRef]
  90. Serra, K.P.; Sarian, L.O.; Rodrigues-Peres, R.M.; Vassallo, J.; Soares, F.A.; Pinto, G.A.; da Cunha, I.W.; Shinzato, J.Y.; Derchain, S.F. Expression of cyclooxygenase-2 (COX-2) and p53 in neighboring invasive and in situ components of breast tumors. Acta Histochem. 2012, 114, 226–231. [Google Scholar] [CrossRef]
Ijms 23 06503 g001 550
Figure 1. FTIR spectra of (a) chitosan, (b) carbon nanotubes, (c) CN25 and (d) CN25M.
Figure 1. FTIR spectra of (a) chitosan, (b) carbon nanotubes, (c) CN25 and (d) CN25M.
Ijms 23 06503 g001
Ijms 23 06503 g002 550
Figure 2. In (A), the thermogravimetric curves of: (I) CN25 and (II) CN25M. In (B), the SEM picture shows the calcium phosphate deposit used to determine the Ca/P ratio by energy dispersive X-ray analysis (EDX).
Figure 2. In (A), the thermogravimetric curves of: (I) CN25 and (II) CN25M. In (B), the SEM picture shows the calcium phosphate deposit used to determine the Ca/P ratio by energy dispersive X-ray analysis (EDX).
Ijms 23 06503 g002
Ijms 23 06503 g003 550
Figure 3. SEM images of (A), CN25; (B), CN25M at 500× magnification. In (C), CN25M at 25,000× magnification.
Figure 3. SEM images of (A), CN25; (B), CN25M at 500× magnification. In (C), CN25M at 25,000× magnification.
Ijms 23 06503 g003
Ijms 23 06503 g004 550
Figure 4. Swelling curves of (☐) CN25; (■) CN25M, performed in PBS pH 7.4.
Figure 4. Swelling curves of (☐) CN25; (■) CN25M, performed in PBS pH 7.4.
Ijms 23 06503 g004
Ijms 23 06503 g005 550
Figure 5. Radiological (a) and macroscopic (b) images of the left femur of rats in the study groups. Bone defects are indicated by the yellow arrows. Bone integrity is observed without injuries or secondary complications, as well as the presence of a bone defect that has not completely regenerated.
Figure 5. Radiological (a) and macroscopic (b) images of the left femur of rats in the study groups. Bone defects are indicated by the yellow arrows. Bone integrity is observed without injuries or secondary complications, as well as the presence of a bone defect that has not completely regenerated.
Ijms 23 06503 g005
Ijms 23 06503 g006 550
Figure 6. Optical microscope images of the bone defect created in the distal metaphysis of the femur of rats in the study groups, (a) panoramic view and (b) detailed view. Defect areas are indicated by black arrows. Note the neoformed bone in the surgical area, is more dense and voluminous in G6/C+CNTsM+L. Masson trichrome.
Figure 6. Optical microscope images of the bone defect created in the distal metaphysis of the femur of rats in the study groups, (a) panoramic view and (b) detailed view. Defect areas are indicated by black arrows. Note the neoformed bone in the surgical area, is more dense and voluminous in G6/C+CNTsM+L. Masson trichrome.
Ijms 23 06503 g006
Ijms 23 06503 g007 550
Figure 7. Picrosirius red optical microscope images in optical light (a) and respective polarized light (b) of the study groups, 10× magnification. Birefringence of the extracellular matrix is observed in the area of the bone lesion.
Figure 7. Picrosirius red optical microscope images in optical light (a) and respective polarized light (b) of the study groups, 10× magnification. Birefringence of the extracellular matrix is observed in the area of the bone lesion.
Ijms 23 06503 g007
Ijms 23 06503 g008 550
Figure 8. Bone volume (%) formed in the defect area. The means and standard deviation of the relative percentage volume of newly formed bone in the femoral defects in the study groups were: 59.93 ± 3.04 (G1/Control), 70.83 ± 1.21 (G2/Laser), 70.09 ± 4.31 (G3/C+CNTs), 81.6 ± 5.74 (G4/C+CNTs+L), 81.4 ± 4.57 (G5/C+CNTsM) and 91.3 ± 4.81 (G6/C+CNTsM+L), respectively. Different lowercase letters indicate a significant difference between the groups. (a ≠ b ≠ c ≠ d; p < 0.05).
Figure 8. Bone volume (%) formed in the defect area. The means and standard deviation of the relative percentage volume of newly formed bone in the femoral defects in the study groups were: 59.93 ± 3.04 (G1/Control), 70.83 ± 1.21 (G2/Laser), 70.09 ± 4.31 (G3/C+CNTs), 81.6 ± 5.74 (G4/C+CNTs+L), 81.4 ± 4.57 (G5/C+CNTsM) and 91.3 ± 4.81 (G6/C+CNTsM+L), respectively. Different lowercase letters indicate a significant difference between the groups. (a ≠ b ≠ c ≠ d; p < 0.05).
Ijms 23 06503 g008
Ijms 23 06503 g009 550
Figure 9. Optical microscope images of osteocalcin immunostaining of the groups studied. Osteocytes were identified by the expression of osteocalcin. The yellow arrows indicate the labeling of osteocytes.
Figure 9. Optical microscope images of osteocalcin immunostaining of the groups studied. Osteocytes were identified by the expression of osteocalcin. The yellow arrows indicate the labeling of osteocytes.
Ijms 23 06503 g009
Ijms 23 06503 g010 550
Figure 10. Optical microscope images of osteopontin immunostaining of the groups studied. Osteocytes were identified by the expression of osteopontin (yellow arrows).
Figure 10. Optical microscope images of osteopontin immunostaining of the groups studied. Osteocytes were identified by the expression of osteopontin (yellow arrows).
Ijms 23 06503 g010
Ijms 23 06503 g011 550
Figure 11. Optical microscope images of VEGF immunostaining of the groups studied. Note the bone defect and the presence of blood vessels (red arrows) distributed along the cortical bone.
Figure 11. Optical microscope images of VEGF immunostaining of the groups studied. Note the bone defect and the presence of blood vessels (red arrows) distributed along the cortical bone.
Ijms 23 06503 g011
Ijms 23 06503 g012 550
Figure 12. Design of the study groups and preparation of the scaffolds. Thirty male Wistar rats were divided into 6 groups: Control (G1/Control), Laser (G2/Laser), Chitosan and Carbon Nanotubes (G3/C+CNTs), Chitosan/Carbon Nanotubes/Laser (G4/C+CNTs+L), Mineralized Chitosan/Carbon Nanotubes (G5/C+CNTsM), Mineralized Chitosan/Carbon Nanotubes/Laser (G6/C+CNTsM+L). Analyses were performed after 5 weeks.
Figure 12. Design of the study groups and preparation of the scaffolds. Thirty male Wistar rats were divided into 6 groups: Control (G1/Control), Laser (G2/Laser), Chitosan and Carbon Nanotubes (G3/C+CNTs), Chitosan/Carbon Nanotubes/Laser (G4/C+CNTs+L), Mineralized Chitosan/Carbon Nanotubes (G5/C+CNTsM), Mineralized Chitosan/Carbon Nanotubes/Laser (G6/C+CNTsM+L). Analyses were performed after 5 weeks.
Ijms 23 06503 g012
Table
Table 1. Photobiomodulation protocol.
Table 1. Photobiomodulation protocol.
ParameterUnit/Description
Type of laserGaAs (gallium-arsenide)
Endophoton LLT 1307 (KLD® Biosistemas Equip. Elet. Ltda, Amparo, Brazil)
Output power70 mW
Wavelength904 nm (APLP 904, KLD® Biosistemas Equip. Elet. Ltda, Amparo, Brazil)
Pulse width100 ns
Power density7000 mW/cm2
Energy density616 J/cm2
Energy per point6.16 J
Beam area0.01 cm2
Total energy applied18.48 J
Beam typePunctual
Emission modeContinuous
Form of applicationThree points in the surgical area
Irradiation duration88 s per point
Total time of each application264 s
Treatment timeImmediately after the surgery and three times a week for five weeks
GaAs = gallium-arsenide; mW = milliwatts; nm = nanometer; ns = nanosecond; mW = milliwatts/centimeter2; J/cm2 = joules/centimeter2; cm² = centimeter2; J = joules.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Silva, S.K.; Plepis, A.M.G.; Martins, V.d.C.A.; Horn, M.M.; Buchaim, D.V.; Buchaim, R.L.; Pelegrine, A.A.; Silva, V.R.; Kudo, M.H.M.; Fernandes, J.F.R.; et al. Suitability of Chitosan Scaffolds with Carbon Nanotubes for Bone Defects Treated with Photobiomodulation. Int. J. Mol. Sci. 2022, 23, 6503. https://doi.org/10.3390/ijms23126503

AMA Style

Silva SK, Plepis AMG, Martins VdCA, Horn MM, Buchaim DV, Buchaim RL, Pelegrine AA, Silva VR, Kudo MHM, Fernandes JFR, et al. Suitability of Chitosan Scaffolds with Carbon Nanotubes for Bone Defects Treated with Photobiomodulation. International Journal of Molecular Sciences. 2022; 23(12):6503. https://doi.org/10.3390/ijms23126503

Chicago/Turabian Style

Silva, Samantha Ketelyn, Ana Maria Guzzi Plepis, Virginia da Conceição Amaro Martins, Marilia Marta Horn, Daniela Vieira Buchaim, Rogerio Leone Buchaim, André Antônio Pelegrine, Vinícius Rodrigues Silva, Mateus Hissashi Matsumoto Kudo, José Francisco Rebello Fernandes, and et al. 2022. "Suitability of Chitosan Scaffolds with Carbon Nanotubes for Bone Defects Treated with Photobiomodulation" International Journal of Molecular Sciences 23, no. 12: 6503. https://doi.org/10.3390/ijms23126503

APA Style

Silva, S. K., Plepis, A. M. G., Martins, V. d. C. A., Horn, M. M., Buchaim, D. V., Buchaim, R. L., Pelegrine, A. A., Silva, V. R., Kudo, M. H. M., Fernandes, J. F. R., Nazari, F. M., & da Cunha, M. R. (2022). Suitability of Chitosan Scaffolds with Carbon Nanotubes for Bone Defects Treated with Photobiomodulation. International Journal of Molecular Sciences, 23(12), 6503. https://doi.org/10.3390/ijms23126503

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.