Next Article in Journal
Pathological Nuclear Hallmarks in Dentate Granule Cells of Alzheimer’s Patients: A Biphasic Regulation of Neurogenesis
Next Article in Special Issue
Photocatalytic Activity of TiO2 Coatings Obtained at Room Temperature on a Polymethyl Methacrylate Substrate
Previous Article in Journal
Expanding the Landscape of Amino Acid-Rich Antimicrobial Peptides: Definition, Deployment in Nature, Implications for Peptide Design and Therapeutic Potential
Previous Article in Special Issue
Influence of Different Salts on the G-Quadruplex Structure Formed from the Reversed Human Telomeric DNA Sequence
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
IJMS
Volume 23
Issue 21
10.3390/ijms232112871
ijms-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Boosted Activity of g-C3N4/UiO-66-NH2 Heterostructures for the Photocatalytic Degradation of Contaminants in Water

by
Rafael R. Solís
*,
María Alejandra Quintana
,
María Ángeles Martín-Lara
,
Antonio Pérez
,
Mónica Calero
and
Mario J. Muñoz-Batista
*
Department of Chemical Engineering, University of Granada, Avda. Fuentenueva, 18071 Granada, Spain
*
Authors to whom correspondence should be addressed.
Int. J. Mol. Sci. 2022, 23(21), 12871; https://doi.org/10.3390/ijms232112871
Submission received: 21 September 2022 / Revised: 19 October 2022 / Accepted: 20 October 2022 / Published: 25 October 2022
(This article belongs to the Collection Feature Papers in Molecular Nanoscience)
Browse Figures
Versions Notes

Abstract

:
The combination of graphitic carbon nitride and the metal-organic framework UiO-66-NH2 has been developed with the aim to enhance the photocatalytic activity of pure semiconductors. Different proportions of g-C3N4 and UiO-66-NH2 were combined. Complete characterization analysis of the resulting photocatalytic materials was conducted, including N2 adsorption isotherms, XRD, FTIR, STEM-EDX microscopy, DRS-UV-visible, and photoluminescence. The photocatalytic activity was tested in an aqueous solution for the removal of acetaminophen as the target pollutant. From the obtained results, less than 50% of UiO-66-NH2 incorporated in the g-C3N4 structure enhanced the photocatalytic degradation rate of both bare semiconductors. Concretely, 75% of g-C3N4 in the final g-C3N4/UiO-66-NH2 heterostructure led to the best results, i.e., complete acetaminophen elimination initially at 5 mg·L−1 in 2 h with a pseudo-first order rate constant of ca. 2 h−1. The presence of UiO-66-NH2 in the g-C3N4 enhanced the optoelectronic properties, concretely, the separation of the photo-generated charges was improved according to photoluminescence characterization. The better photo-absorption uptake was also confirmed by the determination of the quantum efficiency values of the heterostructure if compared to either pure g-C3N4 or UiO-66-NH2. This photocatalyst with the best activity was further tested at different pH values, with the best degradation rate at a pH close to the pHpzc ~4.15 of the solid. Sequential recycling tests demonstrated that the heterostructure was stable after five cycles of use, i.e., 15 h. A high contribution of photo-generated holes in the process of the degradation of acetaminophen, followed marginally by superoxide radicals, was suggested by scavenger tests.

1. Introduction

Freshwater is one of the most important resources on Earth, which has been threatened in recent decades by anthropogenic activities, raising the need for the removal of pollutants to potentiate the reuse and the implementation of the circular economy concept [1]. The need to ensure the availability and sustainable management of water and sanitation is included in the sixth sustainable development goal of the United Nations 2030 agenda [2]. The traditional water treatment technologies developed for urban sewage must be updated to accommodate current human lifestyle in which multiple different organic compounds are discharged into wastewater effluents. Commonly, many of these complex pollutants are not easily removed by the conventional biological oxidation processes based on activated sludge [3,4]. These organic anthropogenic compounds have been labeled as contaminants of emerging concern, and have been detected at low concentrations, i.e., at the μg·L−1 level in the effluent of urban wastewater treatment plants [4,5]. The nature of these pollutants is diverse and includes pharmaceutical compounds, pesticides, personal care products, detergents, flame retardants, plasticizers, and other industrial chemical compounds [6]. Although the consequences for living beings are unknown in the long term in many cases, some of them have been reported as endocrine disruptors since they can alter the functions of hormones, which results in diverse health effects [7,8].
Chemical processes have been demonstrated as an efficient strategy to remove aqueous pollutants that cannot be addressed by traditional methods [9,10]. Among them, diverse techniques, namely advanced oxidation processes, are based on the generation of hydroxyl radicals, a powerful species capable of unselectively oxidizing organic matter. Photocatalysis is a process respectful of the environment and capable of taking advantage of radiation to transform it into chemical energy. The process consists of the activation of a semiconductor when irradiated with photons of energy larger than their bandgap. Then, the electrons of the valence band can move to the conduction band, producing holes in the valence band. The electron–hole pairs can migrate to the surface of the photocatalyst where some reactive species can be produced. Due to the powerful oxidant capability of these species, including superoxide and hydroxyl radicals or photo-generated holes, the photocatalytic abatement of contaminants of emerging concern has been raised as an efficient technology for water treatment [11,12].
Titanium dioxide has been exploited as a semiconductor for water photocatalytic applications due to its abundance, inexpensiveness, low toxicity, and bandgap energy of approximately 3.2 eV, which allows photo-excitation with radiation up to 387 nm [13]. However, great efforts have been paid to overcome the main limitations of titanium dioxide as a semiconductor, i.e., limited absorption of the solar spectrum in the visible region and the high recombination rate of the photo-generated electron–hole pair [14]. In this sense, many materials with photocatalytic activity have been developed to address these issues. For example, graphitic carbon nitride (g-C3N4) is a two-dimensional π-conjugated polymeric graphitic-like structure built from the covalent bonds between carbon and nitrogen, which has been recognized as a promising semiconductor for environmental applications [15]. g-C3N4 displays high chemical and thermal stability with a mild bandgap energy of 2.7 eV, which enables the excitation with radiation up to 460 nm [16]. Metal–Organic Frameworks (MOFs) are porous structures built by metal oxo clusters or secondary building units (SBU) and organic linkers acting as a bridge between the SBU. As a result, a highly porous structure with active redox behavior is produced, which can be used as a potential photocatalyst for water purification [13,17]. MOFs display the advantage of an easy design of certain properties such as the size of the porous cages by selecting appropriate organic ligands, or the tuning of the photocatalytic response by the functionalization of the ligand with certain organic groups. UiO-66 is a Zr-MOF first synthesized at the University of Oslo [18]. The structure is made of Zr6O4(OH)4 octahedron oxo clusters as SBU 12-coordinates with benzenedicarboxylic acid molecules, which act as ligands. The UiO-66 structure is extraordinarily stable in an aqueous solution [19]. Moreover, the bandgap energy of UiO-66 can be tuned by the functionalization of the aromatic ring [20,21], giving the functionalized UiO-66-NH2 a promising photocatalytic response and lower bandgap since the amino group acts as the antenna of the visible radiation.
The coupling of two semiconductors to build a heterojunction is one of the most interesting strategies to minimize the individual withdrawals of bare photocatalysts; therefore, enhancing the photocatalytic response. An adequate choice of the relative conduction and valence bands positions of the two selected photocatalysts leads to a selective charge transfer, guiding the electrons to the surface of the desired phase of the composite [22]. Thus, the combination of graphitic carbon nitride with other semiconductors, such as TiO2 and/or Ag particles, has been proven efficient [23]. The heterojunctions based on UiO-66-NH2 have been also reported as a proficient approach [24]. One-pot synthesis routes, when possible, are preferred for promoting good hetero-interfacial contact between the two semiconductors [25]. However, the synthesis of the heterojunction is not always possible in only one step. This is the case for the g-C3N4/UiO-66-NH2 composite. g-C3N4 is prepared from the thermal decomposition of nitrogen-rich organic precursors under a controlled atmosphere at temperatures as high as 500 °C [16], which is incompatible with the hydrothermal synthesis of MOFs under mild conditions [17]. For that reason, a two-step route in which the MOF grows onto the surface of a previously synthesized g-C3N4 is required [26].
This work reports the synthesis, characterization, and photocatalytic activity assessment of the heterostructure that combines g-C3N4 and UiO-66-NH2, intending to overcome the limitations of these two semiconductors and produce a synergistic activity in the removal of aqueous pollutants. Although the g-C3N4/UiO-66-NH2 heterojunction has been demonstrated as effective for CO2 [27] and Cr6+ reduction [28] or H2 production, this work is focused on the characterization, catalytic assessment of acetaminophen removal, and quantification of the absorbed radiation based on intrinsic kinetic parameters of the reaction as the quantum efficiency. For the synthesis, UiO-66-NH2 has been grown onto the surface of the g-C3N4 to ensure good interfacial contact between the two semiconductors. Acetaminophen has been selected as the target pollutant since it is labeled as ubiquitous in the list of pollutants of emerging concern due to its frequent detection and the high concentration that is reported [29,30]. Different ratios of g-C3N4 to UiO-66-NH2 have been considered to establish the optimum relative proportion that minimizes the undesirable recombination effect. The photocatalytic response of the optimum sample has been further assessed at different pH values, the reusability in sequential cycles has been tested, and a photocatalytic activation mechanism has been proposed based on a chemical scavenger study.

2. Results and Discussion

2.1. Characterization of the g-C3N4/UiO-66-NH2 Heterostructures

The crystalline structure of the heterostructures was assessed by XRD. Figure 1A depicts the XRD diffractograms obtained for pure g-C3N4, UiO-66-NH2, and their combination at different proportions. The patterns obtained for the MOF structure are in good accordance with what is reported in the literature, file CCDC-1405751 [31]. This structure displays two intense peaks located at 2θ = 7.4° and 8.5°, corresponding to (111) and (200) crystallographic planes, respectively. On the other side, the XRD pattern of the graphitic carbon nitride structure generates two peaks [32,33,34]. One is located at 2θ = 13.4°, attributed to the (100) plane, usually at low intensity, corresponding to the heptazine units. In the obtained XRD pattern of g-C3N4, this peak was poorly defined. However, the second peak that is attributed to the (002) plane, which appears as the consequence of the graphitic character of the interlayered construction, was well-defined. The heterostructures with different g-C3N4 to UiO-66-NH2 ratios displayed the peaks of both crystalline phases, with a clear increase in the (002) peak of g-C3N4, as the amount of this component was raised. This tendency in the XRD patterns has been observed in the case of this heterostructure [35] or other MOFs, such as NH2-MIL-125, when combined with graphitic carbon nitride [26].
FTIR analysis was conducted to confirm the formation of the structures of the carbon graphitic nitride and MOF UiO-66-NH2. Figure 1B depicts the FTIR spectra of the synthesized heterostructures and pure components. In the case of g-C3N4, the typical footprint of the vibration of the tri-s-triazine structure was obtained. The vibration of –NH−H and –NH− groups generate a wide band located between 3000 and 3500 cm−1. The stretching of the aromatic C−N rings of the tri-s-triazine group produces a group of peaks between 1000 and 1800 cm−1. Among them, the most intense peaks, located at 1620 and 1530 cm−1 are attributed to the aromatic C−N vibration, while the bands at 1310 and 1230 cm−1 are responsible for the stretching vibration of C−N−(C)−C or C−NH−C bonds [36,37]. A very characteristic peak at 810 cm−1 is registered in the g-C3N4 structure due to the interaction of the different layers of triazine rings [38]. The FTIR spectra of UiO-66-NH2 displayed some characteristic peaks in response to the vibration of the bonds in the MOF structure, i.e., 2-amino-terephthalic acid (ATA) and the [Zr6O6(OH)4] oxo cluster. At ca. 1660 cm−1, a peak appears, representative of the in-plane scissoring bending on N−H2 [39]. Two characteristic peaks at ~1390 and 1570 cm−1 are attributed to symmetric and asymmetric vibration of the O−C=O bond, respectively [40]. A very low-intensity peak located at approximately 1500 cm−1 is representative of C=C aromatic bonds [41]. The bond between the aromatic carbon and the N of the amino group of the ATA molecule generates a peak located at 1280 cm−1 [42]. The very intense peak at 765 cm−1 is characteristic of the C−H bond [43,44]. Finally, the vibration of the [Zr6O6(OH)4] oxo cluster produces an intense peak at ca. 655 cm−1 [21,45]. If the FTIR spectra of pure g-C3N4 and UiO-66-NH2 are compared to the heterostructures containing both, a gradual contribution of the peaks can be observed in each case.
The morphological properties were studied by the STEM technique, see Figure 2. From the micrographs obtained, two well-distinguishable phases were observed. The UiO-66-NH2 displayed very small particles, ranging from 20–50 nm with an octahedral shape, which were aggregated in bigger groups. The g-C3N4 appeared joined to some of these aggregations as irregular particles of bigger size, i.e., 200 nm. This heterogeneous interaction has been reported for this heterostructure [27]. An EDX analysis allowed for the mapping of the element composition to ensure the identification of both phases. As depicted in Figure 2, the presence of the carbon nitride region was confirmed as the proportion of nitrogen was higher, see EDX analysis on area #1, Figure 2E. Zr, C, and N at lower intensity were detected in the small particles, a reminder of the octahedral shape as a probe of the UiO-66-NH2 presence. An EDX analysis on these particles, area #2, confirmed this hypothesis (Figure 2F). Good contact between the two semiconductors was observed due to the smaller size of the MOF. The UiO-66-NH2 particles, ten times smaller, appeared surrounding the g-C3N4 sheets. However, due to the agglomeration nature of the MOFs particles, not all of them have the same opportunity to be in contact with the g-C3N4. This aspect predicts that there should be an optimum ratio of UiO-66-NH2 proportion, a ratio that promotes the presence of a layer of the MOF with enhanced contact with g-C3N4. A MOF excess would not necessarily improve the photocatalytic activity since those MOF particles in excess would grow connected to MOF particles onto the already covered g-C3N4 core. The photocatalytic activity of the samples, discussed in the next subsection, corroborates this theory, proving that the prepared heterostructures with an MOF of less than 50% led to the best results.
N2-adsorption isotherms (Table 1) were carried out to assess the textural properties of the synthesized solids. The isotherm of UiO-66-NH2 depicted a sharp N2 uptake typical of Type I-like isotherms, see Figure S1, with a small hysteresis loop, which confirms the high microporosity and surface area reached in the MOF, specific BET surface area 665 m2·g−1. This highly developed porosity is in accordance with the literature, in which values up to 900 m2·g−1 have been reported for the UiO-66 family [46]. In contrast, g-C3N4 described a Type IV-like isotherm with almost negligible N2 adsorption uptake except at high relative pressures, i.e., the BET surface area barely displayed 20 m2·g−1 and pore volume 0.101 cm3·g−1. This fact provides evidence of the fairly scarce mesoporosity of a non-porous material. The hybrid heterostructures showed textural properties within the extremes of both phases. Higher porosity was obtained if the relative amount of the MOF was raised. Moreover, the reduction in N2 uptake does not necessarily follow a linear tendency with the expected proportion of the MOF in the final solid. This aspect has been attributed to a partial blockage of MOF pores by g-C3N4 particles [26].
The optical properties were studied by the DRS-UV-visible technique. Figure 3 depicts the absorbance spectra and the estimation of the bandgap values by the Tauc plot method considering them as indirect semiconductors [21]. The absorption spectra of the UiO-66-NH2 displayed two well-defined peaks in the UV region. The first one located at ca. 250 nm appears as a consequence of electronic transitions in the secondary built unit of the MOF, i.e., electronic transition from the O atom to Zr in the oxo cluster [47]. A second peak located between 320 and 380 nm is attributed to the ligand-to-metal charge transfer mechanism [48], which means transitions of π electrons from the amino group of the linker to the metal oxo cluster [49]. These two bands in the heterostructures were less defined as g-C3N4 was incorporated. All the samples extend their radiation harvesting to the visible region, i.e., from 400–420 nm. From the values obtained for the bandgap values (see Table 1), pure UiO-66-NH2 presents a higher value than g-C3N4, i.e., 2.84 vs. 2.70 eV, which is consistent with the already reported values in the literature [16,47]. The bandgap values of the heterostructures obtained by their combination are in accordance with the relative content of both phases, within the limits of the pure phases.

2.2. Photocatalytic Activity of the g-C3N4/UiO-66-NH2 Heterostructures

The photocatalytic activity of the g-C3N4/UiO-66-NH2 heterostructures at different relative proportions was tested in the degradation of a target pollutant of emerging concern as acetaminophen (ACE), whose presence in wastewater effluents has been frequently reported [5,50]. Figure 4A shows the results obtained. A negligible contribution of adsorption was observed in all the heterostructures, including the pure g-C3N4 and UiO-66-NH2, during the 30 min adsorption step carried out before irradiation. The sole contribution of 365 nm radiation, i.e., photolysis, led to 40% of ACE degradation in 4 h. The photocatalytic tests led to the complete removal of ACE in all the samples tested after 4 h of treatment. The pure UiO-66-NH2 sample displayed less photocatalytic activity than graphitic carbon nitride. If the pseudo-first order rate constants (kObs) are calculated as a mere comparative tool, the g-C3N4 sample performed ~1.6 times higher value if compared to the MOF, i.e., kObs (g-C3N4) = 1.17 h−1 vs. kObs (UiO-66-NH2) = 0.74 h−1. Regarding the heterostructures, it was observed that the combination of both semiconductors enhanced the photocatalytic activity, reaching improved results if the UiO-66-NH2 was minor in the final heterojunction, e.g., less than 50%. According to the pseudo-first order rate constant calculated in each case (Figure 4B), the values followed the order 75%-g-C3N4/UiO-66-NH2 > 50%-g-C3N4/UiO-66-NH2 > g-C3N4 > 25%-g-C3N4/UiO-66-NH2 > UiO-66-NH2. The samples containing 50% and 75% of g-C3N4 led to a synergistic effect with boosted degradation, which cannot be explained as the relative contribution of the pure phases. Concretely, the sample 75%-g-C3N4/UiO-66-NH2 displayed a kObs = 2.0 h−1, which means ~1.7 folded value concerning pure g-C3N4 and ~2.7 times the obtained with the pure MOF. An adsorption blank test was carried out with this optimized sample, leading to no removal of ACE during the whole period tested.
The outstanding photocatalytic activity of 75%-g-C3N4/UiO-66-NH2 was also corroborated in terms of radiation uptake efficiency. The values of quantum efficiency at the beginning of the photocatalytic reaction, e.g., time zero, shown in Table 2, after the estimation of the local volume rate of photon absorption and the initial reaction rate. The values also followed an outstanding performance of the sample 75%-g-C3N4/UiO-66-NH2, QE,0 = 0.052%.
The optimum activity response of the heterostructures compared to the pure phases cannot be explained according to the bandgap values obtained since the values were higher than the 2.70 eV of pure g-C3N4 and the radiation used was monochromatic (365 nm). For that purpose, an extra further analysis with the photoluminescence technique was used to assess the effect of the recombination effect of the electron–hole pair, as a plausible reason for the differences observed in the photocatalytic activity. The intensity of the PL peak is linked to the rate of the recombination of the photo-generated charges. Thus, the higher the intensity of the PL peak, the higher the recombination effect, which is undesirable for the process [51]. The PL spectra of all the prepared samples are depicted in Figure 5. From this figure, it is observed that the g-C3N4 displayed a higher PL intensity located at 462 nm compared with UiO-66-NH2, whose maximum was moved slightly to a lower wavelength. It can be deduced that the higher recombination rate of g-C3N4 is probably due to the higher photo-activity of this sample. If the behavior of the heterostructures is analyzed, the optimum ratios of 50 and 75% obtained in the tests of ACE degradation match the lowest intensity of the PL peak. As the sample 75%-g-C3N4/UiO-66-NH2 performed the best results, it was selected as the optimum sample for further study.

2.3. Effect of the pH

The effect of the solution pH on the photocatalytic performance of the 75%-g-C3N4/UiO-66-NH2 sample was assessed. Figure 6A depicts the influence of pH on the pseudo-first order rate constant. This figure shows an important influence of the pH on kObs. At pH values between 4 and 5, the highest value of kObs ~2 h−1 was obtained. If the pH was raised or decreased from this interval, a drastic drop in the kinetic constant was registered.
The determination of the pH of zero charge was carried out to explain this behavior. Figure 6B depicts the determination of the pHpzc by the drift method. A value of pHpzc = 4.15 was estimated, which means that the surface of the photocatalyst was positively charged below this value and negatively charged over the pHpzc. The values reported in the literature for either UiO-66-NH2 or g-C3N4 are close to that obtained in this work for the heterostructure. A high acidic character of the MOF UiO-66-NH2 has been reported, with a value for the pHpzc of 4.3 [52] or even lower, i.e., 3.9 [47]. This acidic character has been ascribed to the change in the protonation stage of the Zr oxo cluster rather than the presence of the amino group [53]. In the case of g-C3N4, whose presence is a majority in the 75%-g-C3N4/UiO-66-NH2 sample, the pHpzc has been reported at approximately 4.2 [54].
The acetaminophen molecule displays a weak acid behavior, with a pKa = 9.6–9.8 [55,56]. Over the pKa, the –OH group is deprotonated, leading to the ACE− anion. However, in the pH range studied during the photocatalytic degradation tests, the acetaminophen molecule was present in the neutral form (ACE0); thus, the influence of electrostatic interaction between the ACE0 molecule and the surface of the photocatalyst seems to have a low impact on the adsorption step required for approaching the surface where the reactions preferably take place. Other interactions described for ACE with the solid include π-π and hydrogen bonds [57], which would explain why the optimum results reached pH = 4–5, i.e., around the circumneutral conditions for surface charge (pHpzc).

2.4. Stability and Reusability

The sample with the optimum ratio of graphitic carbon nitride and the MOF, i.e., 75%-g-C3N4-UiO-66-NH2, was tested in sequential tests of recycling and reusing. Figure 7A shows the results obtained after five consecutive runs. In terms of conversion, it is observed that no significant loss was observed, with acetaminophen being completely removed after 180 min. The kinetics of the process followed a slight decrease in the calculated pseudo-first order rate constant; i.e., 1.90 h−1 (1st run), 1.45 h−1 (2nd run), 1.42 h−1 (3rd run), 1.31 h−1 (4th run), and 1.26 h−1 (5th run). This marginal decrease in the kinetics parameter could be due to the adsorption of final oxidation products onto the surface of the photocatalyst, subtracting photocatalytic active points for oxidation of new acetaminophen molecules. The stability of the solid was also assessed by analyzing the structure after the final run. As depicted in Figure 7B, no changes in the XRD pattern were registered. The characteristic points of both phases, g-C3N4 and UiO-66-NH2, were well-defined in the reused sample. Less than 10% loss of intensity in the highest peak was reached in the reused sample. Regarding the FTIR spectra, a very similar pattern was obtained after the fifth cycle, with the most characteristic peaks of the heterostructure well-defined, as in the fresh sample. Concretely, the peak located at 810 cm−1, characteristic of the interaction of different layers of triazine rings, did not lose intensity. The aromatic C−N vibration (1620 and 1530 cm−1) was also well-defined. The peaks responsible for the UiO-66-NH2 structure, such as O−C=O (1390 and 1570 cm−1), the in-plane scissoring bending on N−H2 (1660 cm−1), the C−H in the aromatic ring (765 cm−1), or the peak at 655 cm−1 that appears due to the presence of the oxo cluster unit, were defined in a very similar intensity and shape similar to the fresh sample. Therefore, it can be concluded that the sample displayed stability in terms of photocatalytic activity and structure after five sequential reusing cycles.

2.5. Plausible Mechanism of Photocatalytic Degradation

The influence of the reactive oxidation species (ROS) involved in the process of the photocatalytic degradation of ACE with the 75%-g-C3N4/UiO-66-NH2 sample was tentatively studied by the addition of specific chemical scavengers. Figure 8A depicts the pseudo-first order rate constant for the blank test and the values registered in the presence of different specific chemical scavengers. The role played by superoxide radicals (O2•−) was studied by replacing the O2 bubbling with N2. The kObs in the presence of N2 was reduced ~2.3 times compared to the blank test, which provides evidence of the importance played by O2•− in the overall photocatalytic scheme. The hydroxyl radical contribution was evaluated by adding ethanol (EtOH), due to the high potential of alcohols to react with HO• [58]. In this case, ca. 26% of reduction in kObs with respect to the blank test was recorded. It is important to highlight that alcohols have been reported as good HO• scavengers but their presence can also alter the adsorption mechanism of ACE since they may compete with ACE for the initial adsorption sites, which trigger the photocatalytic reactions. Oxalic acid has been reported as a good inhibitor of photo-generated holes (h+) [59,60]. Under the presence of oxalic acid, the photocatalytic performance was negligible and the kObs obtained was very close to that reached under photolysis, therefore, highlighting the importance of the holes in the photocatalytic process.
Taking into consideration the results attained in the scavenger tests, a mechanism scheme based on the band alignment of both semiconductors in the heterostructure was proposed. The energy of the conduction band for pure UiO-66-NH2 has been reported as nearly −0.80 V vs. NHE [47,61,62]. In the case of g-C3N4, the conduction band is located at ca. −1.25 V vs. NHE [63,64]. That means that the conduction band of the graphitic carbon nitride is more negative than the MOF. Considering the bandgaps values calculated for the pure phases, the conduction bands were located at +2.84 and 2.70 V vs. NHE for the MOF and g-C3N4, respectively. The resulting heterojunction follows a Type II scheme [65], displayed in Figure 8A. According to this mechanism, g-C3N4 as the majority species in the heterojunction, would be photo-activated by the UVA radiation; however, UiO-66-NH2 could be also. Photo-generated electrons of g-C3N4 have the possibility of migration to the conduction band of UiO-66-NH2. Additionally, they could be recombined with the holes in g-C3N4 [28]. This band structure would enhance the spatially effective separation of photo-induced charges [27], minimizing the undesirable recombination effect, as suggested in the PL results.
Considering this bands scheme, neither UiO-66-NH2 nor g-C3N4 display positive enough valence band energy to generate HO•. This is the reason why the contribution of HO• was not as important in the ACE degradation, as the test in the presence of EtOH suggested. However, both holes and O2− would participate in the oxidation of ACE, with a higher contribution of the first if compared to the second. According to the literature, in the case of UiO-66-NH2, the photocatalytic activity has been attributed to the photo-generated holes and/or superoxide radical [47,52] since the valence band is not positive enough to trigger the formation of HO•. In the case of g-C3N4, the superoxide radical has been reported as the main radical species responsible for aqueous pollutants oxidation [66].

3. Materials and Methods

3.1. Chemicals and Synthesis of the Photocatalytic Heterostructures

The chemicals were at least analytical grade, purchased from Merck®, and used as received. HPLC quality acetonitrile (99.9%) was used as a mobile phase in chromatographic analysis. All the stock solutions were prepared in ultrapure water (18.2 MΩ·cm) from a Direct-Q®-UV device (Millipore®).
The graphitic carbon nitride, g-C3N4, was synthesized by pyrolysis of melamine (99%) at 500 °C for 2 h. The resulting yellowish solid was suspended in water and the higher particles that decanted were discharged, collecting the suspended particles that were filtered and dried at 80 °C.
The UiO-66-NH2 was obtained by a hydrothermal method in the presence of dimethylformamide (DMF, 99.9%), adapting a recipe from the literature [21,47]. Briefly, 3 mmol of ZrOCl2·8H2O (98%) and 3 mmol of 2-amino-terephthalic acid (99%) were dissolved in 40 mL of DMF in a Scotch bottle of 100 mL. Next, 20 mL of acetic acid (99.7%) was added. The bottles were sealed and introduced in an oven at 120 °C for 24 h. The as-obtained yellowish solid was recovered by centrifugation (4200 rpm, 5 min) and washed with methanol and water.
The hetero-structures g-C3N4/UiO-66-NH2 were prepared following the same procedure during the synthesis of pure UiO-66-NH2. Different ratios were considered by adding a certain amount of g-C3N4, according to the yield achieved for pure UiO-66-NH2. The desired amount of g-C3N4 was added during the precipitation of the MOF precursors in the DMF solution, therefore, promoting the formation of the metalorganic structure onto the suspended graphitic carbon nitride particles. Different mass percentages of g-C3N4 (X: 25, 50, and 75%) were tested, labeling the resulting photocatalysts as X-g-C3N4/UiO-66-NH2.

3.2. Characterization of the Photocatalytic Heterostructures

The crystalline structure was assessed by the X-ray Diffraction (XRD) technique. A Bruker D8 Discover diffractometer equipped with a PILATUS3R 100K-A detector was used, working with a radiation source of Cu Kα (λ = 1,5406 Å). The signal was registered within a 2θ range from 2–65° (30 s·step−1, step = 0.02°).
The textural and morphological properties were studied by N2 adsorption–desorption isotherms at 77 K in a 3P Sync 200 apparatus (3P instruments©). The total surface area was determined by the BET method (SBET), the micropore area (SMP) by the t-plot method, the total pore volume (VT) from the adsorbed amount at P/P0 = 0.99, and the volume of the micropore (VMP) by the t-plot method.
The Fourier Transform InfraRed (FTIR) analysis was used to study the nature of the organic stretching bonds and was carried out in a Perkin–Elmer device model Spectrum65 between wavenumber 400–4000 cm−1.
The morphology and distribution of the carbon nitride sheet and UiO-66-NH2 particles in the generated heterostructure were studied by Scan Transmission Electron Microscopy (STEM) coupled to High-Angle Annular Dark Field (HAADF) detection and Electron Disperse X-Ray (EDX) analysis in a Thermo Fisher Scientific TALOS F200X device.
The optical properties were analyzed by Diffuse Reflectance Spectroscopy (DRS-UV-visible) in a Varian Cary 5E spectrophotometer. The absorbance and reflectance spectra were recorded and the bandgap values were calculated from the application of the Tauc plot method [67,68]. The photoluminescence (PL) technique was carried out as an indirect analysis of the recombination rate of the electron–hole pair. The analysis was conducted in a Varian Cary Eclipse fluorescence spectrometer, fixing 365 nm as the excitation wavelength.
The pH of the point of zero charge in an aqueous solution (pHpzc) was determined by the pH drift method [69]. Basically, 50 mL of solutions containing 0.1 M NaCl (99.7%) were placed in Erlenmeyer flasks and the pH was adjusted to a certain desired value between 2 and 9 by adding diluted solutions of NaOH (98%) and/or HCl (37%). Then, 100 mg of the solid sample was added and kept under stirring at 25 °C for 48 h. The final pH value was then measured. The pHpzc was calculated from the intercept between the plotted final vs. the initial pH with the bisector.

3.3. Photocatalytic Degradation Tests

The photocatalytic activity of the prepared materials was tested in a UVA photo-reactor equipped with two 9 W lamps emitting at 365 nm. The lamps were placed in the inner space of a jacketed annular reactor made of borosilicate glass, circulating the liquid solution through the jacketing space and magnetically stirred in the bottom. The liquid was pumped and recirculated to an auxiliary tank, also stirred, and equipped with a refrigeration system to maintain the temperature of the solution to 20 °C. Air was bubbled into this tank to keep the solution saturated in O2. Figure 9 depicts a scheme of the photo-reactor setup. The irradiating intensity of the lamps was quantified by an in situ chemical actinometry consisting of the photo-reduction of the ferrioxalate complex combined with a polyoxometalate salt (Na2SiW12O6) to register the temporal abatement of the ferrioxalate complex into CO2 [70]. The experimental conditions for this determination were oxalic acid (98%) 60 mM, FeCl3·6 H2O (97%) 5 mM, and H4SiW12O40 (99.9%) 1 mM. The pH of the solution was kept at 4.5 with HCl and NaOH adjustment to prevent the plausible auto-decomposition of the polyoxometalate complex. Taking into account the quantum yield value during the photo-production of (SiW12O40)5− (ϕ = 0.18 mol·Einstein−1 at 365 ± 10 nm) [70], the radiation intensity value estimated was I0 = (3.5 ± 0.2) 10−4 Einstein L−1·min−1.
The photocatalytic tests started by loading the aqueous acetaminophen (98%) solution with an initial concentration of 5 mg·L−1. Next, the photocatalyst at a dose of 0.5 g·L−1 was added to the tank until a homogeneous dispersion was reached. Before irradiation, a 30 min adsorption step was carried out in darkness. After switching the lamps on, samples were extracted from the tank at regular intervals and the photocatalyst was removed with syringe filters (nylon, 0.45 μm). In the experiments carried out in the presence of scavengers, the desired amount of the scavenger (10 mM) was added to the aqueous solution before loading the catalyst. N2 was replaced by air in the quenching experiment that assessed the importance of O2 (superoxide radical). Oxalic acid was used for suppressing the effect of photo-generated holes and ethanol (96%, vol.) for hydroxyl radicals.
The concentration of the contaminants was quantified by High-Pressure Liquid Chromatography (HPLC) in a Shimadzu LC-10 HPLC device coupled with diode array UV-visible detection. The stationary phase consisted of a Zorbax Bonus-RP column (4.6 × 150 mm, 5 μm). The injection volume was 90 μL. The mobile phase, pumped at 1 mL·min−1 under the isocratic mode, was a mixture of 20% acetonitrile (A) and 80% acidified water (B, 0.1% v/v H3PO4), performing the quantification at 247 nm.
The quantum efficiency value (QE) was obtained following the IUPAC recommendations, which establishes the QE as the ratio of the number of ACE molecules reacting, i.e., the reaction rate, by the number of photons that interact with the photocatalyst, i.e., the local volume rate of photon absorption (LVRPA, eα,ν):
Q E 0 = r ACE 0   mol   ACE · m − 3 · s − 1 e α , ν E · m − 3 · s − 1
where the initial degradation rate (rACE,0) was obtained considering pseudo-first order kinetics, and the photon absorption rate was determined from the radiative transfer equation (RTE), which was solved for the photoreactor from the determination of the optical properties of the photocatalytic suspensions. The followed methodology consisted of a discrete ordinate method in rectangular spectrophotometer cells in combination with a nonlinear, multiparameter regression procedure [71], see Figure S2. The simulation of the photoreactor led to the definition of the photon absorption profiles depicted in Figure 10. The study was carried out for the sample with the best photocatalytic activity as will be discussed in the discussion and results section, i.e., 75%-g-C3N4-UiO-66-NH2. Bare g-C3N4 and UiO-66-NH2 were also considered for comparison purposes. Detailed information about the procedure of the simulation of the LVRPA profiles is described in the Supplementary Information. The LVRPA profiles show that the highest absorption rate was located, as expected, in the center of the z-axis, and gradually decreased with the radial distance. The order among the samples was UiO-66-NH2 > 75%-g-C3N4/UiO-66-NH2 > g-C3N4, which drives the detection of some differences in light penetration through the r coordinate. The relatively high absorption of pristine UiO-66-NH2 in comparison with g-C3N4-containing samples increases the edge absorption effects, which reduces the progressing of radiation in the r-coordinate. Such effect is detected at all the z-positions evaluated. The identification of an absorption profile dominated by the g-C3N4 structure as well, suggests that the activity enhancement detected must be unequivocally associated with an improvement in the charges photo-handling caused by an optimized g-C3N4/UiO-66-NH2 interface.

4. Conclusions

The combination of graphitic carbon nitride with the MOF UiO-66-NH2 results in an efficient heterostructure that enhances the photocatalytic activity of the pure phases during the degradation of acetaminophen in water. The optimum proportion suggests a preference for g-C3N4 as the majority in the final heterojunction, i.e., around 75%, according to the pseudo-first order kinetics and the estimation of the quantum efficiency. This boosted ratio was suggested, according to the characterization of the catalyst, by the lowest recombination effect registered with photoluminescence analysis. STEM pictures combined with EDX mapping confirmed good contact between the two phases, a relevant aspect to promote the electronic transfer between the semiconductors. In addition, as the analysis of the optical properties suggests, the light absorption profile (LVRPA) is dominated by the phase g-C3N4 of the binary systems, which seems to be in line with obtaining a maximum for the sample 75%-gC3N4/UiO-66-NH2.
The pH during the reaction highly affected the performance of the process and the best results were achieved at a pH close to the pHpzc of the photocatalyst. The solid demonstrated stability and reusability with marginal loss of photocatalytic activity and practically negligible modification of XRD and FTIR patterns. Superoxide radicals, and, especially, photo-generated holes, were the reactive oxidant species responsible for acetaminophen degradation. The bands’ scheme suggests a Type II heterojunction with no contribution to hydroxyl radical formation.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/ijms232112871/s1.

Author Contributions

Conceptualization, R.R.S. and M.J.M.-B.; methodology, R.R.S.; software, M.J.M.-B.; validation, M.Á.M.-L., A.P., and M.C.; formal analysis, R.R.S. and M.J.M.-B.; investigation, R.R.S. and M.A.Q.; resources, M.C.; writing—original draft preparation, R.R.S.; writing—review and editing, M.Á.M.-L., A.P., M.C., and M.J.M.-B.; project administration, R.R.S. and M.J.M.-B.; funding acquisition, R.R.S. and M.J.M.-B. All authors have read and agreed to the published version of the manuscript.

Funding

The authors are grateful to the University of Granada for the “Precompetitive Research Projects for Young Researchers Modality A—Young Doctors” of the 2019 and 2021 calls of the UGR Researching Plan (PPJIA2019-09 and PPJIA2021-34 grants).

Institutional Review Board Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

The authors also thank the supporting analyses provided by the external services of the University of Granada (CIC).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Guerra-Rodríguez, S.; Oulego, P.; Rodríguez, E.; Singh, D.N.; Rodríguez-Chueca, J. Towards the Implementation of Circular Economy in the Wastewater Sector: Challenges and Opportunities. Water 2020, 12, 1431. [Google Scholar] [CrossRef]
  2. Hering, J.G.; Maag, S.; Schnoor, J.L. A Call for Synthesis of Water Research to Achieve the Sustainable Development Goals by 2030. Environ. Sci. Technol. 2016, 50, 6122–6123. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  3. Kümmerer, K.; Dionysiou, D.D.; Olsson, O.; Fatta-Kassinos, D. A Path to Clean Water. Science 2018, 361, 222–224. [Google Scholar] [CrossRef] [Green Version]
  4. Bunting, S.Y.; Lapworth, D.J.; Crane, E.J.; Grima-Olmedo, J.; Koroša, A.; Kuczyńska, A.; Mali, N.; Rosenqvist, L.; van Vliet, M.E.; Togola, A.; et al. Emerging Organic Compounds in European Groundwater. Environ. Pollut. 2021, 269, 115945. [Google Scholar] [CrossRef]
  5. Desbiolles, F.; Malleret, L.; Tiliacos, C.; Wong-Wah-Chung, P.; Laffont-Schwob, I. Occurrence and Ecotoxicological Assessment of Pharmaceuticals: Is There a Risk for the Mediterranean Aquatic Environment? Sci. Total Environ. 2018, 639, 1334–1348. [Google Scholar] [CrossRef]
  6. Gavrilescu, M.; Demnerová, K.; Aamand, J.; Agathos, S.; Fava, F. Emerging Pollutants in the Environment: Present and Future Challenges in Biomonitoring, Ecological Risks and Bioremediation. New Biotechnol. 2015, 32, 147–156. [Google Scholar] [CrossRef] [PubMed]
  7. Rivera-Utrilla, J.; Sánchez-Polo, M.; Ferro-García, M.Á.; Prados-Joya, G.; Ocampo-Pérez, R. Pharmaceuticals as Emerging Contaminants and Their Removal from Water. A Review. Chemosphere 2013, 93, 1268–1287. [Google Scholar] [CrossRef]
  8. Gonsioroski, A.; Mourikes, V.E.; Flaws, J.A. Endocrine Disruptors in Water and Their Effects on the Reproductive System. Int. J. Mol. Sci. 2020, 21, 1929. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  9. Ahmed, M.B.; Zhou, J.L.; Ngo, H.H.; Guo, W.; Thomaidis, N.S.; Xu, J. Progress in the Biological and Chemical Treatment Technologies for Emerging Contaminant Removal from Wastewater: A Critical Review. J. Hazard. Mater. 2017, 323, 274–298. [Google Scholar] [CrossRef]
  10. Rout, P.R.; Zhang, T.C.; Bhunia, P.; Surampalli, R.Y. Treatment Technologies for Emerging Contaminants in Wastewater Treatment Plants: A Review. Sci. Total Environ. 2021, 753, 141990. [Google Scholar] [CrossRef]
  11. Pillai, S.C.; Štangar, U.L.; Byrne, J.A.; Pérez-Larios, A.; Dionysiou, D.D. Photocatalysis for Disinfection and Removal of Contaminants of Emerging Concern. Chem. Eng. J. 2015, 261, 1–2. [Google Scholar] [CrossRef]
  12. Ahmed, S.; Khan, F.S.A.; Mubarak, N.M.; Khalid, M.; Tan, Y.H.; Mazari, S.A.; Karri, R.R.; Abdullah, E.C. Emerging Pollutants and Their Removal Using Visible-Light Responsive Photocatalysis—A Comprehensive Review. J. Environ. Chem. Eng. 2021, 9, 106643. [Google Scholar] [CrossRef]
  13. Ezugwu, C.I.; Sonawane, J.M.; Rosal, R. Redox-Active Metal-Organic Frameworks for the Removal of Contaminants of Emerging Concern. Sep. Purif. Technol. 2022, 284, 120246. [Google Scholar] [CrossRef]
  14. Loeb, S.K.; Álvarez, P.J.J.; Brame, J.A.; Cates, E.L.; Choi, W.; Crittenden, J.; Dionysiou, D.D.; Li, Q.; Li-Puma, G.; Quan, X.; et al. The Technology Horizon for Photocatalytic Water Treatment: Sunrise or Sunset? Environ. Sci. Technol. 2019, 53, 2937–2947. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  15. Mamba, G.; Mishra, A.K. Graphitic Carbon Nitride (g-C3N4) Nanocomposites: A New and Exciting Generation of Visible Light Driven Photocatalysts for Environmental Pollution Remediation. Appl. Catal. B Environ. 2016, 198, 347–377. [Google Scholar] [CrossRef]
  16. Ismael, M. A Review on Graphitic Carbon Nitride (g-C3N4) Based Nanocomposites: Synthesis, Categories, and Their Application in Photocatalysis. J. Alloy Compd. 2020, 846, 156446. [Google Scholar] [CrossRef]
  17. Bedia, J.; Muelas-Ramos, V.; Peñas-Garzón, M.; Gómez-Avilés, A.; Rodríguez, J.J.; Belver, C. A Review on the Synthesis and Characterization of Metal Organic Frameworks for Photocatalytic Water Purification. Catalysts 2019, 9, 52. [Google Scholar] [CrossRef] [Green Version]
  18. Cavka, J.H.; Jakobsen, S.; Olsbye, U.; Guillou, N.; Lamberti, C.; Bordiga, S.; Lillerud, K.P. A New Zirconium Inorganic Building Brick Forming Metal Organic Frameworks with Exceptional Stability. J. Am. Chem. Soc. 2008, 130, 13850–13851. [Google Scholar] [CrossRef]
  19. Bůžek, D.; Adamec, S.; Lang, K.; Demel, J. Metal-Organic Frameworks vs. Buffers: Case Study of UiO-66 Stability. Inorg. Chem. Front. 2021, 8, 720–734. [Google Scholar] [CrossRef]
  20. Cedeno, R.M.; Cedeno, R.; Gapol, M.A.; Lerdwiriyanupap, T.; Impeng, S.; Flood, A.; Bureekaew, S. Bandgap Modulation in Zr-Based Metal-Organic Frameworks by Mixed-Linker Approach. Inorg. Chem. 2021, 60, 8908–8916. [Google Scholar] [CrossRef]
  21. Wang, Y.L.; Zhanb, S.; Zhab, Y.F.; Bedia, J.; Rodriguez, J.J.; Belver, C. UiO-66 Based Metal Organic Frameworks for the Photodegradation of Acetaminophen under Simulated Solar Irradiation. J. Environ. Chem. Eng. 2021, 9, 106087. [Google Scholar] [CrossRef]
  22. Marschall, R. Semiconductor Composites: Strategies for Enhancing Charge Carrier Separation to Improve Photocatalytic Activity. Adv. Funct. Mater. 2014, 24, 2421–2440. [Google Scholar] [CrossRef]
  23. Jiménez-Calvo, P.; Caps, V.; Keller, V. Plasmonic Au-Based Junctions onto TiO2, GC3N4, and TiO2-GC3N4 Systems for Photocatalytic Hydrogen Production: Fundamentals and Challenges. Renew. Sustain. Energy Rev. 2021, 149, 111095. [Google Scholar] [CrossRef]
  24. Zhao, C.; Li, Y.; Chu, H.; Pan, X.; Ling, L.; Wang, P.; Fu, H.; Wang, C.C.; Wang, Z. Construction of Direct Z-Scheme Bi5O7I/UiO-66-NH2 Heterojunction Photocatalysts for Enhanced Degradation of Ciprofloxacin: Mechanism Insight, Pathway Analysis and Toxicity Evaluation. J. Hazard. Mater. 2021, 419, 126466. [Google Scholar] [CrossRef] [PubMed]
  25. Lin, M.; Wang, J.; Kim, G.H.; Liu, J.; Pan, L.; Lee, Y.; Oh, J.W.; Jung, Y.; Seo, S.; Son, Y.; et al. One-Pot Heterointerfacial Metamorphosis for Synthesis and Control of Widely Varying Heterostructured Nanoparticles. J. Am. Chem. Soc. 2021, 143, 3383–3392. [Google Scholar] [CrossRef] [PubMed]
  26. Muelas-Ramos, V.; Sampaio, M.J.; Silva, C.G.; Bedia, J.; Rodriguez, J.J.; Faria, J.L.; Belver, C. Degradation of Diclofenac in Water under LED Irradiation Using Combined G-C3N4/NH2-MIL-125 Photocatalysts. J. Hazard. Mater. 2021, 416, 126199. [Google Scholar] [CrossRef]
  27. Wang, Y.; Guo, L.; Zeng, Y.; Guo, H.; Wan, S.; Ou, M.; Zhang, S.; Zhong, Q. Amino-Assisted NH2-UiO-66 Anchored on Porous g-C3N4 for Enhanced Visible-Light-Driven CO2 Reduction. ACS Appl. Mater. Interfaces 2019, 11, 30673–30681. [Google Scholar] [CrossRef]
  28. Ren, J.; Lv, S.; Wang, S.; Bao, M.; Zhang, X.; Gao, Y.; Liu, Y.; Zhang, Z.; Zeng, L.; Ke, J. Construction of Efficient G-C3N4/NH2-UiO-66 (Zr) Heterojunction Photocatalysts for Wastewater Purification. Sep. Purif. Technol. 2021, 274, 118973. [Google Scholar] [CrossRef]
  29. Phong Vo, H.N.; Le, G.K.; Hong Nguyen, T.M.; Bui, X.T.; Nguyen, K.H.; Rene, E.R.; Vo, T.D.H.; Thanh Cao, N.D.; Mohan, R. Acetaminophen Micropollutant: Historical and Current Occurrences, Toxicity, Removal Strategies and Transformation Pathways in Different Environments. Chemosphere 2019, 236, 124391. [Google Scholar] [CrossRef]
  30. Deo, R.P. Pharmaceuticals in the Surface Water of the USA: A Review. Curr. Environ. Health Rep. 2014, 1, 113–122. [Google Scholar] [CrossRef]
  31. Trickett, C.A.; Gagnon, K.J.; Lee, S.; Gándara, F.; Bürgi, H.B.; Yaghi, O.M. Definitive Molecular Level Characterization of Defects in UiO-66 Crystals. Angew. Chem.-Int. Ed. 2015, 54, 11162–11167. [Google Scholar] [CrossRef] [PubMed]
  32. Fina, F.; Callear, S.K.; Carins, G.M.; Irvine, J.T.S. Structural Investigation of Graphitic Carbon Nitride via XRD and Neutron Diffraction. Chem. Mater. 2015, 27, 2612–2618. [Google Scholar] [CrossRef] [Green Version]
  33. Chebanenko, M.I.; Zakharova, N.V.; Lobinsky, A.A.; Popkov, V.I. Ultrasonic-Assisted Exfoliation of Graphitic Carbon Nitride and Its Electrocatalytic Performance in Process of Ethanol Reforming. Semiconductors 2019, 53, 2072–2077. [Google Scholar] [CrossRef]
  34. Islam, M.R.; Chakraborty, A.K.; Gafur, M.A.; Rahman, M.A.; Rahman, M.H. Easy Preparation of Recyclable Thermally Stable Visible-Light-Active Graphitic-C3N4/TiO2 Nanocomposite Photocatalyst for Efficient Decomposition of Hazardous Organic Industrial Pollutants in Aqueous Medium. Res. Chem. Intermed. 2019, 45, 1753–1773. [Google Scholar] [CrossRef]
  35. Zhang, S.; Chen, K.; Peng, W.; Huang, J. G-C3N4/UiO-66-NH2 Nanocomposites with Enhanced Visible Light Photocatalytic Activity for Hydrogen Evolution and Oxidation of Amines to Imines. New J. Chem. 2020, 44, 3052–3061. [Google Scholar] [CrossRef]
  36. Kim, M.; Hwang, S.; Yu, J.S. Novel Ordered Nanoporous Graphitic C3N4 as a Support for Pt–Ru Anode Catalyst in Direct Methanol Fuel Cell. J. Mater. Chem. 2007, 17, 1656–1659. [Google Scholar] [CrossRef]
  37. Sunasee, S.; Leong, K.H.; Wong, K.T.; Lee, G.; Pichiah, S.; Nah, I.W.; Jeon, B.H.; Yoon, Y.; Jang, M. Sonophotocatalytic Degradation of Bisphenol A and Its Intermediates with Graphitic Carbon Nitride. Environ. Sci. Pollut. Res. 2019, 26, 1082–1093. [Google Scholar] [CrossRef]
  38. Zhao, D.; Dong, C.-L.; Wang, B.; Chen, C.; Huang, Y.-C.; Diao, Z.; Li, S.; Guo, L.; Shen, S.; Zhao, D.; et al. Synergy of Dopants and Defects in Graphitic Carbon Nitride with Exceptionally Modulated Band Structures for Efficient Photocatalytic Oxygen Evolution. Adv. Mater. 2019, 31, 1903545. [Google Scholar] [CrossRef]
  39. Kandiah, M.; Usseglio, S.; Svelle, S.; Olsbye, U.; Lillerud, K.P.; Tilset, M. Post-Synthetic Modification of the Metal–Organic Framework Compound UiO-66. J. Mater. Chem. 2010, 20, 9848–9851. [Google Scholar] [CrossRef]
  40. Shangkum, G.Y.; Chammingkwan, P.; Trinh, D.X.; Taniike, T. Design of a Semi-Continuous Selective Layer Based on Deposition of UiO-66 Nanoparticles for Nanofiltration. Membranes 2018, 8, 129. [Google Scholar] [CrossRef]
  41. Decoste, J.B.; Peterson, G.W.; Jasuja, H.; Glover, T.G.; Huang, Y.G.; Walton, K.S. Stability and Degradation Mechanisms of Metal–Organic Frameworks Containing the Zr6O4(OH)4 Secondary Building Unit. J. Mater. Chem. A 2013, 1, 5642–5650. [Google Scholar] [CrossRef]
  42. Vellingiri, K.; Deep, A.; Kim, K.H.; Boukhvalov, D.W.; Kumar, P.; Yao, Q. The Sensitive Detection of Formaldehyde in Aqueous Media Using Zirconium-Based Metal Organic Frameworks. Sens. Actuators B Chem. 2017, 241, 938–948. [Google Scholar] [CrossRef]
  43. Valenzano, L.; Civalleri, B.; Chavan, S.; Bordiga, S.; Nilsen, M.H.; Jakobsen, S.; Lillerud, K.P.; Lamberti, C. Disclosing the Complex Structure of UiO-66 Metal Organic Framework: A Synergic Combination of Experiment and Theory. Chem. Mater. 2011, 23, 1700–1718. [Google Scholar] [CrossRef]
  44. Kandiah, M.; Nilsen, M.H.; Usseglio, S.; Jakobsen, S.; Olsbye, U.; Tilset, M.; Larabi, C.; Quadrelli, E.A.; Bonino, F.; Lillerud, K.P. Synthesis and Stability of Tagged UiO-66 Zr-MOFs. Chem. Mater. 2010, 22, 6632–6640. [Google Scholar] [CrossRef]
  45. Ding, J.; Yang, Z.; He, C.; Tong, X.; Li, Y.; Niu, X.; Zhang, H. UiO-66(Zr) Coupled with Bi2MoO6 as Photocatalyst for Visible-Light Promoted Dye Degradation. J. Colloid Interface Sci. 2017, 497, 126–133. [Google Scholar] [CrossRef] [PubMed]
  46. Winarta, J.; Shan, B.; Mcintyre, S.M.; Ye, L.; Wang, C.; Liu, J.; Mu, B. A Decade of UiO-66 Research: A Historic Review of Dynamic Structure, Synthesis Mechanisms, and Characterization Techniques of an Archetypal Metal−organic Framework. Cryst. Growth Des. 2020, 20, 1347–1362. [Google Scholar] [CrossRef]
  47. Peñas-Garzón, M.; Sampaio, M.J.; Wang, Y.L.; Bedia, J.; Rodriguez, J.J.; Belver, C.; Silva, C.G.; Faria, J.L. Solar Photocatalytic Degradation of Parabens Using UiO-66-NH2. Sep. Purif. Technol. 2022, 286, 120467. [Google Scholar] [CrossRef]
  48. Nasalevich, M.A.; Hendon, C.H.; Santaclara, J.G.; Svane, K.; Van Der Linden, B.; Veber, S.L.; Fedin, M.V.; Houtepen, A.J.; Van Der Veen, M.A.; Kapteijn, F.; et al. Electronic Origins of Photocatalytic Activity in d0 Metal Organic Frameworks. Sci. Rep. 2016, 6, 1–9. [Google Scholar] [CrossRef] [Green Version]
  49. Long, J.; Wang, S.S.; Ding, Z.; Wang, S.S.; Zhou, Y.; Huang, L.; Wanga, X. Amine-Functionalized Zirconium Metal–Organic Framework as Efficient Visible-Light Photocatalyst for Aerobic Organic Transformations. Chem. Commun. 2012, 48, 11656–11658. [Google Scholar] [CrossRef]
  50. Cai, Z.; Dwivedi, A.D.; Lee, W.-N.; Zhao, X.; Liu, W.; Sillanpää, M.; Zhao, D.; Huang, C.-H.; Fu, J. Application of Nanotechnologies for Removing Pharmaceutically Active Compounds from Water: Development and Future Trends. Environ. Sci. Nano 2018, 5, 27–47. [Google Scholar] [CrossRef]
  51. Liqiang, J.; Yichun, Q.; Baiqi, W.; Shudan, L.; Baojiang, J.; Libin, Y.; Wei, F.; Honggang, F.; Jiazhong, S. Review of Photoluminescence Performance of Nano-Sized Semiconductor Materials and Its Relationships with Photocatalytic Activity. Sol. Energy Mater. Sol. Cells 2006, 90, 1773–1787. [Google Scholar] [CrossRef]
  52. Solís, R.R.; Peñas-Garzón, M.; Belver, C.; Rodriguez, J.J.; Bedia, J. Highly Stable UiO-66-NH2 by the Microwave-Assisted Synthesis for Solar Photocatalytic Water Treatment. J. Environ. Chem. Eng. 2022, 10, 107122. [Google Scholar] [CrossRef]
  53. Ibrahim, A.H.; El-Mehalmey, W.A.; Haikal, R.R.; Safy, M.E.A.; Amin, M.; Shatla, H.R.; Karakalos, S.G.; Alkordi, M.H. Tuning the Chemical Environment within the UiO-66-NH2 Nanocages for Charge-Dependent Contaminant Uptake and Selectivity. Inorg. Chem. 2019, 58, 15078–15087. [Google Scholar] [CrossRef] [PubMed]
  54. Li, F.; Li, T.; Zhang, L.; Jin, Y.; Hu, C. Enhancing Photocatalytic Performance by Direct Photo-Excited Electron Transfer from Organic Pollutants to Low-Polymerized Graphitic Carbon Nitride with More C-NH/NH2 Exposure. Appl. Catal. B Environ. 2021, 296, 120316. [Google Scholar] [CrossRef]
  55. Djokić, A.; Dumanović, D.; Marković, D.; Muk, A. Spectrophotometric Characterization of Some Analgesics and Antipyretics. Talanta 1989, 36, 931–935. [Google Scholar] [CrossRef]
  56. Ruiz, R.; Rosés, M.; Ràfols, C.; Bosch, E. Critical Validation of a New Simpler Approach to Estimate Aqueous PKa of Drugs Sparingly Soluble in Water. Anal. Chim. Acta 2005, 550, 210–221. [Google Scholar] [CrossRef]
  57. Igwegbe, C.A.; Aniagor, C.O.; Oba, S.N.; Yap, P.S.; Iwuchukwu, F.U.; Liu, T.; de Souza, E.C.; Ighalo, J.O. Environmental Protection by the Adsorptive Elimination of Acetaminophen from Water: A Comprehensive Review. J. Ind. Eng. Chem. 2021, 104, 117–135. [Google Scholar] [CrossRef]
  58. Buxton, G.V.; Greenstock, C.L.; Helman, W.P.; Ross, A.B. Critical Review of Rate Constants for Reactions of Hydrated Electrons, Hydrogen Atoms and Hydroxyl Radicals (⋅OH/⋅O−) in Aqueous Solution. J. Phys. Chem. Ref. Data 1988, 17, 513–886. [Google Scholar] [CrossRef] [Green Version]
  59. Anderson, J.A. Simultaneous Photocatalytic Degradation of Nitrate and Oxalic Acid over Gold Promoted Titania. Catal. Today 2012, 181, 171–176. [Google Scholar] [CrossRef]
  60. Kinoshita, A.; Nakanishi, K.; Tanaka, A.; Hashimoto, K.; Kominami, H. Photocatalytic Selective Ring Hydrogenation of Phenol to Cyclohexanone over a Palladium-Loaded Titanium(IV) Oxide under Hydrogen-Free Conditions. ChemPhotoChem 2019, 3, 559–567. [Google Scholar] [CrossRef]
  61. Chen, Y.F.; Tan, L.L.; Liu, J.M.; Qin, S.; Xie, Z.Q.; Huang, J.F.; Xu, Y.W.; Xiao, L.M.; Su, C.Y. Calix[4]Arene Based Dye-Sensitized Pt@UiO-66-NH2 Metal-Organic Framework for Efficient Visible-Light Photocatalytic Hydrogen Production. Appl. Catal. B Environ. 2017, 206, 426–433. [Google Scholar] [CrossRef]
  62. Li, Y.X.; Wang, X.; Wang, C.C.; Fu, H.; Liu, Y.; Wang, P.; Zhao, C. S-TiO2/UiO-66-NH2 Composite for Boosted Photocatalytic Cr(VI) Reduction and Bisphenol A Degradation under LED Visible Light. J. Hazard. Mater. 2020, 399, 123085. [Google Scholar] [CrossRef]
  63. Baudys, M.; Paušová, Š.; Praus, P.; Brezová, V.; Dvoranová, D.; Barbieriková, Z.; Krýsa, J. Graphitic Carbon Nitride for Photocatalytic Air Treatment. Materials 2020, 13, 3038. [Google Scholar] [CrossRef] [PubMed]
  64. Liu, S.; Chen, F.; Li, S.; Peng, X.; Xiong, Y. Enhanced Photocatalytic Conversion of Greenhouse Gas CO2 into Solar Fuels over g-C3N4 Nanotubes with Decorated Transparent ZIF-8 Nanoclusters. Appl. Catal. B Environ. 2017, 211, 1–10. [Google Scholar] [CrossRef]
  65. Low, J.; Yu, J.; Jaroniec, M.; Wageh, S.; Al-Ghamdi, A.A. Heterojunction Photocatalysts. Adv. Mater. 2017, 29, 1601694. [Google Scholar] [CrossRef]
  66. Yang, K.; Yu, Q.; Li, H.; Ren, X.; Pan, J.; Li, X. Design of a Higher Positive Valence Band in G-C3N4 Photocatalyst for Enhanced Photocatalytic Activity by Copper Hydroxide Deposition. Mater. Technol. 2022, 37, 1459–1466. [Google Scholar] [CrossRef]
  67. Tauc, J. Optical Properties and Electronic Structure of Amorphous Ge and Si. Mater. Res. Bull. 1968, 3, 37–46. [Google Scholar] [CrossRef]
  68. Makuła, P.; Pacia, M.; Macyk, W. How to Correctly Determine the Band Gap Energy of Modified Semiconductor Photocatalysts Based on UV-Vis Spectra. J. Phys. Chem. Lett. 2018, 9, 6814–6817. [Google Scholar] [CrossRef] [Green Version]
  69. Rajah, Z.; Guiza, M.; Solís, R.R.R.; Becheikh, N.; Rivas, F.J.J.; Ouederni, A. Clopyralid Degradation Using Solar-Photocatalytic/Ozone Process with Olive Stone Activated Carbon. J. Environ. Chem. Eng. 2019, 7, 102900. [Google Scholar] [CrossRef]
  70. Lee, J.; Kim, J.; Choi, W. Ferrioxalate-Polyoxometalate System as a New Chemical Actinometer. Environ. Sci. Technol. 2007, 41, 5433–5438. [Google Scholar] [CrossRef]
  71. Duderstadt, J.J.; Martin, W.R. Transport Theory; John Wiley & Sons, Inc.: New York, NY, USA, 1979. [Google Scholar]
Ijms 23 12871 g001 550
Figure 1. XRD patterns (A) and FTIR spectra (B) of the g-C3N4/UiO-66-NH2 heterostructures.
Figure 1. XRD patterns (A) and FTIR spectra (B) of the g-C3N4/UiO-66-NH2 heterostructures.
Ijms 23 12871 g001
Ijms 23 12871 g002 550
Figure 2. STEM micrographs of the 75%-g-C3N4/UiO-66-NH2 heterostructure. (A) STEM picture at 200 nm. (B) UiO-66-NH2 nanoparticles at 20 nm. (C) HAAF image. (D) Mapping of C, N, and Zr. (E) EDX analysis of g-C3N4. (F) EDX analysis of UiO-66-NH2.
Figure 2. STEM micrographs of the 75%-g-C3N4/UiO-66-NH2 heterostructure. (A) STEM picture at 200 nm. (B) UiO-66-NH2 nanoparticles at 20 nm. (C) HAAF image. (D) Mapping of C, N, and Zr. (E) EDX analysis of g-C3N4. (F) EDX analysis of UiO-66-NH2.
Ijms 23 12871 g002
Ijms 23 12871 g003 550
Figure 3. DRS-UV-vis spectra of the g-C3N4/UiO-66-NH2 heterostructures (A) and bandgap determination by the Tauc plot method (B).
Figure 3. DRS-UV-vis spectra of the g-C3N4/UiO-66-NH2 heterostructures (A) and bandgap determination by the Tauc plot method (B).
Ijms 23 12871 g003
Ijms 23 12871 g004 550
Figure 4. Photocatalytic degradation of acetaminophen (ACE) with g-C3N4/UiO-66-NH2 heterostructures. (A) Temporal evolution of acetaminophen with the different samples. (B) Pseudo-first order rate constant (kObs) of the different samples. Experimental conditions: V = 350 mL; T = 20 °C, CACE = 5 mg·L−1; CCAT = 0.5 g·L−1.
Figure 4. Photocatalytic degradation of acetaminophen (ACE) with g-C3N4/UiO-66-NH2 heterostructures. (A) Temporal evolution of acetaminophen with the different samples. (B) Pseudo-first order rate constant (kObs) of the different samples. Experimental conditions: V = 350 mL; T = 20 °C, CACE = 5 mg·L−1; CCAT = 0.5 g·L−1.
Ijms 23 12871 g004
Ijms 23 12871 g005 550
Figure 5. PL spectra of the g-C3N4/UiO-66-NH2 heterostructures.
Figure 5. PL spectra of the g-C3N4/UiO-66-NH2 heterostructures.
Ijms 23 12871 g005
Ijms 23 12871 g006 550
Figure 6. Influence of the pH on the photocatalytic degradation of acetaminophen with 75%-g-C3N4/UiO-66-NH2. (A) Pseudo-first order rate constant (kObs). Experimental conditions: V = 350 mL; T = 20 °C, CACE = 5 mg·L−1; CCAT = 0.5 g·L−1. (B) Determination of the pHpzc of 75%-g-C3N4/UiO-66-NH2 sample by the drift method.
Figure 6. Influence of the pH on the photocatalytic degradation of acetaminophen with 75%-g-C3N4/UiO-66-NH2. (A) Pseudo-first order rate constant (kObs). Experimental conditions: V = 350 mL; T = 20 °C, CACE = 5 mg·L−1; CCAT = 0.5 g·L−1. (B) Determination of the pHpzc of 75%-g-C3N4/UiO-66-NH2 sample by the drift method.
Ijms 23 12871 g006
Ijms 23 12871 g007 550
Figure 7. Stability tests of 75%-g-C3N4/UiO-66-NH2 sample. (A) Photocatalytic degradation of acetaminophen in sequential experiments of photocatalyst reuse. Experimental conditions: V = 350 mL; T = 20 °C, CACE = 5 mg·L−1; CCAT = 0.5 g·L−1. (B) XRD diffractograms before and after use in the 5th run. (C) FTIR spectra before and after use in the 5th run.
Figure 7. Stability tests of 75%-g-C3N4/UiO-66-NH2 sample. (A) Photocatalytic degradation of acetaminophen in sequential experiments of photocatalyst reuse. Experimental conditions: V = 350 mL; T = 20 °C, CACE = 5 mg·L−1; CCAT = 0.5 g·L−1. (B) XRD diffractograms before and after use in the 5th run. (C) FTIR spectra before and after use in the 5th run.
Ijms 23 12871 g007
Ijms 23 12871 g008 550
Figure 8. (A) Influence of scavengers over 75%-g-C3N4/UiO-66-NH2 sample on the pseudo-first order rate constant. Experimental conditions: V = 350 mL; T = 20 °C, CACE = 5 mg·L−1; Cscavenger = 10 mM; CCAT = 0.5 g·L−1. (B) Bandgap alignment proposal of g-C3N4/UiO-66-NH2 heterostructure.
Figure 8. (A) Influence of scavengers over 75%-g-C3N4/UiO-66-NH2 sample on the pseudo-first order rate constant. Experimental conditions: V = 350 mL; T = 20 °C, CACE = 5 mg·L−1; Cscavenger = 10 mM; CCAT = 0.5 g·L−1. (B) Bandgap alignment proposal of g-C3N4/UiO-66-NH2 heterostructure.
Ijms 23 12871 g008
Ijms 23 12871 g009 550
Figure 9. Scheme of the photo-reactor setup (dimensions in mm). Experimental conditions: Virradiated = 200 mL; Vtank = 150 mL; T = 20 °C.
Figure 9. Scheme of the photo-reactor setup (dimensions in mm). Experimental conditions: Virradiated = 200 mL; Vtank = 150 mL; T = 20 °C.
Ijms 23 12871 g009
Ijms 23 12871 g010 550
Figure 10. LVRPA profiles of 75%-g-C3N4/UiO-66-NH2 sample and g-C3N4 and UiO-66-NH2 references. The z dimension means the longitudinal distance from the top of the photo-reactor and r the radial position of the jacketed annular space.
Figure 10. LVRPA profiles of 75%-g-C3N4/UiO-66-NH2 sample and g-C3N4 and UiO-66-NH2 references. The z dimension means the longitudinal distance from the top of the photo-reactor and r the radial position of the jacketed annular space.
Ijms 23 12871 g010
Table
Table 1. Textural and optical properties of the g-C3N4/UiO-66-NH2 heterostructures.
Table 1. Textural and optical properties of the g-C3N4/UiO-66-NH2 heterostructures.
SampleN2 IsothermDRS-UV-Vis
SBET (m2·g−1)SMP (m2·g−1)VT (cm3·g−1)VMP (cm3·g−1)EBG (eV)
UiO-66-NH26654631.2560.2502.84
25%-g-C3N4/UiO-66-NH25053460.8390.1772.82
50%-g-C3N4/UiO-66-NH23792520.6480.1302.80
75%-g-C3N4/UiO-66-NH21961320.3150.0652.78
g-C3N42000.10102.70
SBET: total specific surface area by BET method; SMP: micropore surface area by t-plot method; VT: total pore volume; VMP: micropore volume by t-plot method; EBG: bandgap by Tauc plot method.
Table
Table 2. Quantum efficiency values of the g-C3N4/UiO-66-NH2 heterostructures.
Table 2. Quantum efficiency values of the g-C3N4/UiO-66-NH2 heterostructures.
Sampleeα,ν (Einstein·cm−3·s−1)rACE,0 (mmol·cm−3·s−1)QE,0 (%)
UiO-66-NH23.50 × 10−86.82 × 10−90.019
25%-g-C3N4/UiO-66-NH23.50 × 10−88.73 × 10−90.024
50%-g-C3N4/UiO-66-NH23.55 × 10−81.42 × 10−80.040
75%-g-C3N4/UiO-66-NH23.55 × 10−81.83 × 10−80.052
g-C3N43.63 × 10−81.07 × 10−80.031
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Solís, R.R.; Quintana, M.A.; Martín-Lara, M.Á.; Pérez, A.; Calero, M.; Muñoz-Batista, M.J. Boosted Activity of g-C3N4/UiO-66-NH2 Heterostructures for the Photocatalytic Degradation of Contaminants in Water. Int. J. Mol. Sci. 2022, 23, 12871. https://doi.org/10.3390/ijms232112871

AMA Style

Solís RR, Quintana MA, Martín-Lara MÁ, Pérez A, Calero M, Muñoz-Batista MJ. Boosted Activity of g-C3N4/UiO-66-NH2 Heterostructures for the Photocatalytic Degradation of Contaminants in Water. International Journal of Molecular Sciences. 2022; 23(21):12871. https://doi.org/10.3390/ijms232112871

Chicago/Turabian Style

Solís, Rafael R., María Alejandra Quintana, María Ángeles Martín-Lara, Antonio Pérez, Mónica Calero, and Mario J. Muñoz-Batista. 2022. "Boosted Activity of g-C3N4/UiO-66-NH2 Heterostructures for the Photocatalytic Degradation of Contaminants in Water" International Journal of Molecular Sciences 23, no. 21: 12871. https://doi.org/10.3390/ijms232112871

APA Style

Solís, R. R., Quintana, M. A., Martín-Lara, M. Á., Pérez, A., Calero, M., & Muñoz-Batista, M. J. (2022). Boosted Activity of g-C3N4/UiO-66-NH2 Heterostructures for the Photocatalytic Degradation of Contaminants in Water. International Journal of Molecular Sciences, 23(21), 12871. https://doi.org/10.3390/ijms232112871

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop