Next Article in Journal
Synthesis and Characterization of Bio-Oil Phenol Formaldehyde Resin Used to Fabricate Phenolic Based Materials
Next Article in Special Issue
Fabrication of Nanosized Island-Like CdO Crystallites-Decorated TiO2 Rod Nanocomposites via a Combinational Methodology and Their Low-Concentration NO2 Gas-Sensing Behavior
Previous Article in Journal
Thermal Stability and Fire Properties of Salen and Metallosalens as Fire Retardants in Thermoplastic Polyurethane (TPU)
Previous Article in Special Issue
Nanoscaled Mechanical Properties of Cement Composites Reinforced with Carbon Nanofibers
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 10
Issue 6
10.3390/ma10060667
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Biosynthesis and Characterization of AgNPs–Silk/PVA Film for Potential Packaging Application

by
Gang Tao
1,
Rui Cai
2,
Yejing Wang
2,*,
Kai Song
1,
Pengchao Guo
1,
Ping Zhao
1,
Hua Zuo
3 and
Huawei He
1,4,*
1
State Key Laboratory of Silkworm Genome Biology, Southwest University, Chongqing 400715, China
2
College of Biotechnology, Southwest University, Chongqing 400715, China
3
College of Pharmaceutical Sciences, Southwest University, Chongqing 400715, China
4
Chongqing Engineering and Technology Research Center for Novel Silk Materials, Southwest University, Chongqing 400715, China
*
Authors to whom correspondence should be addressed.
Materials 2017, 10(6), 667; https://doi.org/10.3390/ma10060667
Submission received: 8 May 2017 / Revised: 6 June 2017 / Accepted: 13 June 2017 / Published: 17 June 2017
(This article belongs to the Special Issue Improving Performance of Nanocomposite Materials)
Browse Figures
Versions Notes

Abstract

:
Bionanocomposite packaging materials have a bright future for a broad range of applications in the food and biomedical industries. Antimicrobial packaging is one of the bionanocomposite packaging materials. Silver nanoparticle (AgNP) is one of the most attractive antimicrobial agents for its broad spectrum of antimicrobial activity against microorganisms. However, the traditional method of preparing AgNPs-functionalized packaging material is cumbersome and not environmentally friendly. To develop an efficient and convenient biosynthesis method to prepare AgNPs-modified bionanocomposite material for packaging applications, we synthesized AgNPs in situ in a silk fibroin solution via the reduction of Ag+ by the tyrosine residue of fibroin, and then prepared AgNPs–silk/poly(vinyl alcohol) (PVA) composite film by blending with PVA. AgNPs were synthesized evenly on the surface or embedded in the interior of silk/PVA film. The prepared AgNPs–silk/PVA film exhibited excellent mechanical performance and stability, as well as good antibacterial activity against both Gram-negative and Gram-positive bacteria. AgNPs–silk/PVA film offers more choices to be potentially applied in the active packaging field.

1. Introduction

Bionanocomposite packaging materials have a bright future for a broad range of applications in the food and biomedical industries, in addition to innovative active and intelligent food packaging with biofunctional properties. Antimicrobial packaging is a form of active packaging that is usually achieved by the incorporation or immobilization of potent antimicrobial agents into the packaging system [1]. Nowadays, the ever-growing demand for safe and minimally-processed products presents a major challenge for the packaging industry to develop active packaging materials that can maintain the safety and quality of packaged items [2]. To improve the safety and the shelf-life of packaged products, increasing attention has been paid to the design, development and characterization of films, blends, coatings, and nanocomposite formulations with antimicrobial or antioxidant properties [3,4,5,6]. Various organic acids, enzymes, bacteriocins, chelating agents, spice extracts, and essential oils have been directly incorporated into the films to develop antimicrobial packaging [7,8,9,10]. Among the antibacterial materials, nanoparticles or nanocomposite antimicrobial materials have long been exploited for high efficiency in inhibiting the growth of microorganisms due to high surface-to-volume ratio and enhanced surface reactivity [11,12]. Silver nanoparticle (AgNP) is one of the most attractive antibacterial materials for its broad spectrum of antimicrobial activities against foodborne microorganisms. Such nanocomposite materials with profound antimicrobial function have great value in active packaging for shelf life extension and the safety enhancement of packaged products [13,14].
The traditional method of preparing AgNPs-functionalized material is cumbersome and not environmentally friendly. The synthesis and immobilization of AgNPs requires at least two steps. This approach has been gradually abandoned due to the complicated and tedious procedure [15]. Increasing attentions toward sustainable and environmentally-friendly technologies have promoted the development of AgNPs synthesized via green biological systems. In recent years, the biomineralization approach—a combination of biotechnology and nanotechnology—has developed and provided unparalleled opportunities for natural biomaterials [16,17,18]. Natural macromolecules serve as a biotemplate to prepare novel nanomaterials [19,20].
Silk fibroin is a natural protein from silkworm silk, and is a common biomacromolecule with unique sequence-specific self-assembly behavior [21]. Over the past decade, silk fibroin has been applied in tissue engineering as degradable surgical sutures and scaffolds [22,23] for its good biocompatibility, controllable biodegradability, and easy fabrication into different forms, such as fibers, films, gels, and three-dimensional scaffolds [24]. Silk fibroin is a good candidate for biomineralization. Previous works have indicated that silk fibroin regulates the morphologies of inorganic nanoparticles during the biomineralization process [25,26]. Silk fibroin contains 18 types of amino acid residues, including some polar amino acids such as tyrosine (Tyr). Tyr endows silk fibroin with electron-donating property. The electron-donating property of the phenolic hydroxyl group of Tyr could directly reduce silver ion to AgNP [27]. Thus, it is possible to synthesize AgNPs through the reduction of Ag+ by silk fibroin in situ to prepare the antibacterial silk film.
Biopolymer film such as AgNPs–silk is limited in its packaging application due to its poor mechanical property. To improve the mechanical property, biopolymer–polymer interaction is developed by blending natural biopolymers with polymers. Poly(vinyl alcohol) (PVA) is a biodegradable, biocompatible, water-soluble and non-toxic semi-crystalline polymer. It offers good thermo-mechanical property, thermal stability, mechanical strength and flexibility, as well as good optical and physical properties that are crucial for packaging application [28,29]. Moreover, PVA is approved by the food and drug administration as an indirect food additive for flexible food packaging [30,31]. The combination of AgNPs, silk fibroin, and PVA will be promising for active packaging.
The aim of this work was to prepare a kind of biodegradable film with antimicrobial activity for packaging application. Here, we have developed a green biosynthesis method to prepare AgNPs–silk/PVA film. Fourier transform infrared spectroscopy (FTIR) and field emission scanning electron microscopy (FESEM) were performed to characterize the chemical groups and the surface morphologies of AgNPs–silk/PVA films, respectively. The mechanical and thermal properties of the prepared films were investigated by the stress–strain assay and thermogravimetric analyzer (TGA), respectively. The antimicrobial activities of AgNPs–silk/PVA films are evaluated by the bacterial growth curve and inhibition zone assays. Our studies suggest that the prepared AgNPs–silk/PVA film has great potential in active packaging applications.

2. Results and Discussion

2.1. Preparation of AgNPs–Silk/PVA Film

AgNPs synthesis via the reduction of Ag+ by Tyr residue has been developed [32,33,34]. The aim of this study is to prepare AgNPs–silk film as an antibacterial packaging material. However, the poor mechanical performance of AgNPs–silk film limits its application in packaging material. The mechanical property of a film can be improved via crosslinking, copolymerizing, and blending with other macromolecular materials [35,36]. PVA has good film-forming properties [37]. PVA blending is widely applied in packaging materials for its good mechanical property and excellent barrier property toward hydrocarbons and gases [38,39]. However, bacteria can easily adhere and grow on PVA film, thus resulting in the deformation and the degradation of PVA film. Therefore, it is highly desired to prepare a PVA composite film with broad antimicrobial activity to facilitate its application in packaging material. In this study, we developed a green, facile, and economical approach to prepare AgNPs–silk/PVA film without the addition of any other chemical agents, as illustrated in Figure 1.

2.2. Characterization of Silk Fibroin

To determine whether silk fibroin was successfully extracted from silk cocoon, UV-vis spectroscopy was applied to measure the characteristic absorption peaks of peptide bonds and aromatic amino acids. Two peaks at 227 nm and 275 nm were observed in the absorbance spectra of silk fibroin (Figure 2A), which could be attributed to the absorbance of the aromatic amino acids and peptide bonds of silk fibroin, respectively [40].
Fluorescence spectroscopy is an efficient method to analyze silk fibroin, as it has inherent fluorescence from the tyrosine, tryptophan, and phenylalanine residues of silk fibroin. The fluorescence emission spectrum showed two peaks at 311 nm and 350 nm (Figure 2B), which may be attributed to the fluorescence from tyrosine and phenylalanine residues, respectively [41]. These results suggested silk fibroin was successfully extracted from silk cocoon.

2.3. Stability of AgNPs–Silk Fibroin Solution

Individual AgNP is easily oxidized to aggregate in air, which may affect its antibacterial activity; therefore, the stability of AgNP is a critical consideration for its application [42]. In this study, AgNPs–silk solutions were treated at different pHs and temperatures to characterize their stability with UV-vis spectroscopy The results showed the band at 445 nm did not change in either pH 5.0, 7.4, and 10.0 (Figure 3A) or at 50 °C, 75 °C, and 100 °C (pH 5.0) (Figure 3B). When placed at 37 °C, 50 °C, and 65 °C (pH 5.0) for 15 days, the UV absorption spectra of AgNPs–silk did not change (Figure 3C). These results suggested AgNPs–silk solutions had good stability at different temperatures or under different conditions. Silk fibroin could enhance the stability of AgNPs in aqueous dispersions via the interactions with AgNPs. However, under low-temperature conditions, the UV absorption of AgNPs was lower than that at room temperature (Figure 3D). This may be attributed to the aggregation of fibroin under low-temperature conditions.

2.4. Characterization of AgNPs–Silk/PVA Film

To detect the formation of AgNPs, the UV-vis spectrum of AgNPs–silk solution was scanned, as shown in Figure 4A. The result showed a broad absorption band centered at 445 nm, indicating the formation of AgNPs in the solution. The 445 nm absorbance peak may be assigned to the surface plasmon resonance band of AgNP [43]. A typical absorbance peak of AgNP is located around 400 nm. The absorbance peak of AgNPs–silk red-shifted from 400 nm to 445 nm. This may be caused by the high dielectric constant of the peptide matrix, which reduces the plasmon resonance frequency of AgNPs in solution [44].
FESEM images were captured to explore the surface morphologies of silk/PVA and AgNPs- silk/PVA films. Silk/PVA film had smooth surfaces (Figure 4B), implying that the film had a dense structure and good mechanical property. It was noted that some small dots appeared on the surface of the AgNPs–silk/PVA film (Figure 4C), indicating the efficient synthesis of AgNPs in situ. The uniform distribution of AgNPs on the film suggested that silk fibroin was a good dispersant. Aggregations of AgNPs were not observed on the film, and thus it is expected to have a better antimicrobial performance.
Energy dispersive X-ray spectroscopy (EDS) was carried out to further determine the synthesis of AgNPs in situ on the film. A distinct peak was observed in the EDS spectrum (Figure 4D), which could be assigned to metallic silver. The results suggested that AgNPs were successfully synthesized in situ on the silk/PVA film.
The thermal behaviors of silk/PVA and AgNPs–silk/PVA films were analyzed by TGA. The mass of the film as a function of temperature is shown in Figure 5A. The TGA curves of AgNPs–silk/PVA films showed a similar tendency. Compared to silk/PVA film, the residual mass of AgNPs–silk/PVA films were in the range of 3–10%, implying the presence of AgNPs in the silk/PVA film. The mass percentages of AgNPs in A-S80P20, A-S67P33, and A-S50P50 films were calculated to be 10.8%, 6.2%, and 3.6%, respectively, which were consistent with the residual mass percentages of AgNPs–silk/PVA films.
At the first stage, while increasing temperature to 100 °C, water evaporation caused the initial mass reduction of all films. The mass reduction of the film was almost 8%, indicating that the film was a slightly hygroscopic material. At the second stage, while increasing temperature from 200 °C to 330 °C, the mass reduction of the films could be ascribed to the degradation of exposed side chains of silk fibroin or PVA. The dramatic mass reduction occurred in the temperature range of 330–550 °C. This may be attributed to the breakdown of main chain groups of silk fibroin and the decomposition of PVA [45]. At the last stage, silk/PVA film was almost completely lost, whereas AgNPs–silk/PVA films had residual mass ranging from 3% to 10%, indicating the successful synthesis of AgNPs in the silk/PVA film. The A-S50P50 film reached equilibrium at around 420 °C on the TGA curve, which was lower than that of the A-S80P20 film. This result indicated that a high content of silk fibroin could enhance the thermostability of silk/PVA films and delay the thermal degradation process.
It was noted that S50P50 and A-S50P50 showed a plateau at near 3% in a large temperature interval from 450 °C to 700 °C, and only afterwards did S50P50 degrade to zero mass. A-S50P50 had 3% residual mass after 450 °C, which may be ascribed the existence of about 3% AgNPs in the film. The thermal behavior of S50P50 in 450–700 °C may be due to the existence of strong interactions between silk and PVA, which stabilized the S50P50 film and kept 3% residual mass of the film. However, after 700 °C, high temperature destroyed the strong interactions of silk and PVA and resulted in the complete mass loss of S50P50 film.
FTIR spectroscopy was applied to characterize the chemical groups of silk/PVA and AgNPs- silk/PVA films (Figure 5B). All films showed similar peaks. The bands at 3284–3287 cm−1 were assigned to the hydroxyl groups of silk and PVA. The bands at 2943 cm−1 were attributed to the saturated C–H groups (–CH3). The bands at 2908 cm−1 were attributed to C–H stretching vibrations (–CH2). The amide I (1624–1638 cm−1), II (1514–1527 cm−1), and III (1232–1250 cm−1) bands were believed from silk fibroin in the films [46]. While AgNPs were synthesized in situ on the silk/PVA film, the characteristic peaks such as 3285 cm−1, 1624–1630 cm−1, 1522–1525 cm−1, and 1234–1238 cm−1 did not change, suggesting that AgNPs modification did not affect the inherent structure of silk/PVA film.

2.5. Mechanical Property of AgNPs–Silk/PVA Film

The mechanical properties of AgNPs–silk/PVA films were characterized by their stress–strain curves, as shown in Figure 6. The results showed that with increasing PVA concentration from 20% to 50%, the tensile strength of AgNPs–silk/PVA film increased significantly (Figure 6A). The tensile strength of the A-S50P50 film was 42 ± 6 MPa, which was the highest among all of the tested films. The A-S80P20 film had 5% elongation percentage (Figure 6B), which was the lowest among all of the tested films. With increasing PVA concentration from 20% to 50%, the elongation percentage increased from 5% to 78%, respectively. The elongation percentage of A-S50P50 film was 77 ± 10%, which was the highest among all of the tested films. These results suggested that increasing the PVA concentration could enhance the tensile strength and the elongation at break of AgNPs–silk/PVA film. The A-S50P50 film had the best mechanical performance among all of the tested films, which may be suitable for potential packaging applications.

2.6. Hydrophobicity Measurement

Water contact angle measurements were carried out to determine the hydrophobicity of the silk/PVA film and the AgNPs–silk/PVA film. As shown in Figure 7A, the water contact angle of silk/PVA film was 95°, indicating that it had a relatively hydrophobic surface property. This may be because silk contains some non-polar amino acids. While blending with PVA in different ratios, the water contact angles increased to 103°, 105°, and 106° (Figure 7B–D), indicating AgNPs–silk/PVA film exhibited a certain degree of hydrophobicity. Compared to silk/PVA film, the increase of water contact angles may be due to the presence of AgNPs in the silk/PVA film. Regardless, the resulting water contact angles suggested AgNPs–silk/PVA film had a certain degree of hydrophobicity which may be suitable for packaging applications.

2.7. Antibacterial Assay of AgNPs–Silk/PVA Film

The antibacterial activity of silk/PVA and AgNPs–silk/PVA films were carefully investigated by the bacterial growth curve assay. E. coli and S. aureus were selected as the models of Gram-negative and Gram-positive bacteria, respectively [40]. Silk/PVA film itself did not affect the growth of bacteria (Figure 8, curve b). However, AgNPs–silk/PVA films significantly inhibited the growth of bacteria. In the presence of AgNPs–silk/PVA films, the lag phase of both E. coli and S. aureus lasted from less than 1 h to about 6 h (Figure 8, curves c–e). Even at the exponential phase, the growth rate of bacteria in the presence of AgNPs–silk/PVA film was not as fast as that of control (Figure 8, curves a,b), indicating that the prepared AgNPs–silk/PVA films had good antibacterial activity.
In this study, we prepared the AgNPs–silk/PVA films with different ratios of AgNPs–silk and PVA (4:1, 4:2, and 4:4). Thus, the AgNPs contents were different in these prepared AgNPs–silk/PVA films, which resulted in the difference of the antibacterial ability of AgNPs–silk/PVA films (Figure 8). A-S67P33 and A-S50P50 showed almost the same tendency from 0 h to 8 h. However, A-S67P33 and A-S50P50 showed small differences in the antibacterial ability for the difference in the AgNPs contents after 8 h. As A-S80P20 had greater AgNPs contents than A-S67P33 and A-S50P50, and A-S80P20 showed a more obvious inhibitory effect on bacterial growth than A-S67P33 and A-S50P50.
The FESEM results showed that AgNPs were evenly dispersed on the surface of silk/PVA film. In addition, the synthesized AgNPs were wrapped in the interior of silk/PVA film. During the bacterial growth, AgNPs exposed on the surface of film were gradually released into the media to inhibit bacterial growth, then AgNPs embedded in the interior of the film were released into the media to continuously inhibit the growth of bacteria.
An inhibition zone assay was performed to further evaluate the antibacterial ability of AgNPs- silk/PVA film, as shown in Figure 9. The results showed that silk/PVA film did not affect the growth of E. coli and S. aureus, which was consistent with the observation of the growth curve assay. However, AgNPs–silk/PVA films inhibited the growth of bacteria both for E. coli and S. aureus, as observed by the formation of obvious inhibition zones (Figure 9). These results suggested that AgNPs–silk/PVA film could effectively inhibit the growth of both Gram-negative and Gram-positive bacteria.

2.8. Degradation of AgNPs–Silk/PVA Film

The stability of a film is directly related to its performance. Additionally, the controllable degradation of antibacterial film is essential for the delayed release of AgNPs to maintain sustained antibacterial activity. To evaluate the degradation of AgNPs–silk/PVA film in the real world, the mass reduction resulting from the degradation of AgNPs–silk/PVA film was examined in PBS buffers with different pHs. After 120 days of treatment in pH 4.0 buffer, AgNPs–silk/PVA film still maintained a good shape. The mass reduction of AgNPs–silk/PVA film was less than 30% (Figure 10A). In contrast, in pH 7.4 and 10.0 buffers, the shape of the films had been changed after 120 days of treatment. The mass reduction was close to 30% in pH 7.4 buffer or 40% in pH 10.0 buffer (Figure 10B,C).
Silk has an isoelectric point of 4.6. In addition, PVA shows weak acidity in water. Thus, under acidic conditions, AgNPs–silk/PVA film had a relatively better stability. The degradation of AgNPs–silk/PVA film in a neutral environment was faster than that in an acidic environment. Of note, the degradation behavior of all films was similar under acidic or neutral conditions—the content of silk fibroin affected the degradation rate. The higher the silk fibroin content, the slower the degradation rate. However, under alkaline conditions, the lower the silk fibroin content, the slower the degradation rate. These results suggested that the prepared AgNPs–silk/PVA films had good stability under different conditions.

3. Materials and Methods

3.1. Materials

Silkworm cocoons were kindly provided by the State Key Laboratory of Silkworm Genome Biology, Southwest University, China. Poly(vinyl alcohol) (PVA) and silver nitrate (AgNO3) (AR, 99.99%) were purchased from Aladdin Corp. (Shanghai, China). Mili-Q water was prepared by a water purification system (Millipore, Billerica, MA, USA) and used in all experiments.

3.2. Preparation of Regenerated Silk Fibroin Solution

Silk cocoon consists of fibroin and sericin, wherein fibroin is wrapped by sericin. Degumming and dissolving of silk fibroin followed the established procedures. In brief, silk fibers were degummed twice with 0.5% NaHCO3 (wt %) solution at 100 °C for 30 min, then washed with water twice and air-dried at room temperature. The degummed silk fibers were dissolved in 9.3 mol/L LiBr solution, and then dialyzed against water for 48 h at room temperature with a semipermeable membrane (MEMBRA-CEL, 12,000–14,000 MWCO) to remove LiBr. Silk fibroin solution was centrifuged after dialysis. Then, the supernatant was collected and stored at 4 °C.

3.3. Synthesis of AgNPs

AgNO3 powders (400 mg) were added to 100 mL of 2% silk solution (wt %). The final AgNO3 concentration was 4 mg/mL. Then, the AgNO3–silk solution was irradiated with natural light at room temperature for 24 h to prepare AgNPs–silk solution.

3.4. Preparation of AgNPs–Silk/PVA Film

PVA powder was dissolved in water to a final concentration of 2% (wt %) under a constant stirring speed of 200 rpm/min at 85 °C until it was completely dissolved. AgNPs–silk solution (2%) and PVA solution (2%) were mixed thoroughly as the volume ratios of 4:1, 4:2, and 4:4. The mixed solution was placed onto the petri-plates (diameter = 90 mm), and then frozen under −20 °C and thawed at room temperature for four cycles to form AgNPs–silk/PVA hydrogel. The hydrogel was further dried at 65 °C to form AgNPs–silk/PVA film, which were termed as A-S80P20, A-S67P33, and A-S50P50, respectively.

3.5. Characterization of AgNPs–Silk/PVA Film

The surface structure and morphology of AgNPs–silk/PVA films were studied on a field emission-SEM of JSM-7800F (JEOL, Tokyo, Japan). EDS spectra were measured by INCA X-Max 250 (Oxford Instruments, Concord, MA, USA) during SEM tests for the analysis of chemical elements. All samples were sputter-coated with platinum for 90 s before observation. The FTIR spectrum was collected in the range of 400–4000 cm−1 on a Nicolet iz10 IR microscope (Thermo Fisher Scientific, Waltham, MA, USA). UV-vis spectra were measured on a DU-800 UV-vis spectrophotometer (Beckman Coulter, Brea, CA, USA) in a 1 cm light path cuvette from 300 nm to 800 nm. Fluorescence emission spectra were recorded at room temperature on a Hitachi F-7000 fluorescence spectrophotometer (Hitachi, Tokyo, Japan). The excitation wavelength was 280 nm and the detection wavelength range was 290–500 nm. Thermal stability was measured on a TGA-Q50 thermogravimetric analyzer (TA instruments, New Castle, DE, USA). The heating rate was 10 °C/min in N2 with the flow rate of 20 mL/min. The tensile strength and the elongation at break of the films were determined according to ASTM standard method on an AG-X plus universal testing machine (Shimadzu, Kyoto, Japan). The films were cut into rectangular shapes with a dimension of 1 cm × 3 cm (length × width) and then used for measurement.

3.6. Bacterial Growth Curve Assay

Bacterial growth curve assay was performed to evaluate the antibacterial activity of AgNPs–silk/PVA film according to a previous method [47]. Bacteria in lag phase were inoculated into 10 mL Luria-Bertani (LB) medium, and cultured at 37 °C in the presence of silk/PVA or AgNPs–silk/PVA films. Bacterial suspensions (0.5 mL) were collected at different intervals to measure the optical density at the wavelength of 600 nm (OD600). All growth curve tests were made in triplicate to ensure that the results were repeatable.

3.7. Inhibition Zone Assay

The antimicrobial activity of AgNPs–silk/PVA film against E. coli and S. aureus was evaluated by an inhibition zone assay as a previous report [48]. About 100 μL of bacterial suspension (1 × 108 CFU/mL) was spread on LB agar plate, then the circular film with a diameter of 1 cm was placed on the surface of agar plate. After 12 h incubation at 37 °C, the diameters of inhibition zones were measured to evaluate the antibacterial activities of the films.

3.8. In Vitro Degradation Analysis

AgNPs–silk/PVA films (2 cm × 2 cm) were immersed in pH 4.0, 7.4 and 10.0 buffers at 37 °C. PBS buffer was replaced daily. At given time points, the films were taken out from PBS buffers, washed, dried, and weighed. The degradation was calculated as the difference between the initial and dry masses at given time points divided by the initial dry mass. All tests were performed in triplicate.

4. Conclusions

In this study, we have developed an efficient and convenient biosynthesis method to prepare AgNPs–silk/PVA films using natural silk as the reducing and stabilizing agent. AgNPs are synthesized evenly on the surface or embedded in the interior of silk/PVA film. The prepared AgNPs–silk/PVA film has good mechanical performance and stability, as well as good antibacterial activity against both Gram-negative and Gram-positive bacteria, which offers more choices for potential applications in the active packaging field.

Acknowledgments

This work was supported by the State Key Program of National Natural Science of China (No. 31530071), National Natural Science Foundation of China (No. 31572465, 31402139), Chongqing Research Program of Basic Research and Frontier Technology (cstc2015jcyjA00040, cstc2015jcyjBX0035), Fundamental Research Funds for Central Universities (XDJK2017D117, XDJK2017D187), Open Project Program of Chongqing Engineering and Technology Research Center for Novel Silk Materials (silkgczx2016003) and Start-up Grant from Southwest University (SWU112111).

Author Contributions

G.T. designed and performed the experiments; G.T., R.C. and Y.W. analyzed the data and wrote the manuscript draft; P.G. and K.S. assisted the experiments; H.Z. and P.Z. assisted the format of manuscript draft; Y.W. and H.H. supervised the research and revised the manuscript.

Conflicts of Interest

The authors declare that they have no competing interests, including specific financial interests and relationships and affiliations relevant to the subject of this manuscript.

References

  1. De Azeredo, H.M.C. Nanocomposites for food packaging applications. Food Res. Int. 2009, 42, 1240–1253. [Google Scholar] [CrossRef]
  2. Rhim, J.W.; Park, H.M.; Ha, C.S. Bio-nanocomposites for food packaging applications. Prog. Polym. Sci. 2013, 38, 1629–1652. [Google Scholar] [CrossRef]
  3. Kasirga, Y.; Oral, A.; Caner, C. Preparation and characterization of chitosan/montmorillonite- k10 nanocomposites films for food packaging applications. Polym. Compos. 2012, 33, 1874–1882. [Google Scholar] [CrossRef]
  4. Heydari, A.; Alemzadeh, I.; Vossoughi, M. Functional properties of biodegradable corn starch nanocomposites for food packaging applications. Mater. Des. 2013, 50, 954–961. [Google Scholar] [CrossRef]
  5. Butnaru, E.; Cheaburu, C.N.; Yilmaz, O.; Pricope, G.M.; Vasile, C. Poly(vinyl alcohol)/chitosan/montmorillonite nanocomposites for food packaging applications: Influence of montmorillonite content. High Perform. Polym. 2016, 28, 1124–1138. [Google Scholar] [CrossRef]
  6. Munoz-Bonilla, A.; Fernandez-Garcia, M. Polymeric materials with antimicrobial activity. Prog. Polym. Sci. 2012, 37, 281–339. [Google Scholar] [CrossRef]
  7. Duncan, T.V. Applications of nanotechnology in food packaging and food safety: Barrier materials, antimicrobials and sensors. J. Colloid Interface Sci. 2011, 363, 1–24. [Google Scholar] [CrossRef] [PubMed]
  8. Sanuja, S.; Agalya, A.; Umapathy, M.J. Synthesis and characterization of zinc oxide-neem oil-chitosan bionanocomposite for food packaging application. Int. J. Biol. Macromol. 2015, 74, 76–84. [Google Scholar] [CrossRef] [PubMed]
  9. Ollier, R.P.; Perez, C.J.; Alvarez, V.A. Preparation and characterization of micro and nanocomposites based on poly(vinyl alcohol) for packaging applications. J. Mater. Sci. 2013, 48, 7088–7096. [Google Scholar] [CrossRef]
  10. Mihindukulasuriya, S.D.F.; Lim, L.T. Oxygen detection using uv-activated electrospun poly(ethylene oxide) fibers encapsulated with tio2 nanoparticles. J. Mater. Sci. 2013, 48, 5489–5498. [Google Scholar] [CrossRef]
  11. Palza, H. Antimicrobial polymers with metal nanoparticles. Int. J. Mol. Sci. 2015, 16, 2099–2116. [Google Scholar] [CrossRef] [PubMed]
  12. Munoz-Bonilla, A.; Fernandez-Garcia, M. The roadmap of antimicrobial polymeric materials in macromolecular nanotechnology. Eur. Polym. J. 2015, 65, 46–62. [Google Scholar] [CrossRef]
  13. Lu, Z.; Gao, J.T.; He, Q.F.; Wu, J.; Liang, D.H.; Yang, H.; Chen, R. Enhanced antibacterial and wound healing activities of microporous chitosan-Ag/ZnO composite dressing. Carbohydr. Polym. 2017, 156, 460–469. [Google Scholar] [CrossRef] [PubMed]
  14. Alvarez-Paino, M.; Munoz-Bonilla, A.; Fernandez-Garcia, M. Antimicrobial polymers in the nano-world. Nanomaterials 2017, 7, 48. [Google Scholar] [CrossRef] [PubMed]
  15. Yin, J.; Yang, Y.; Hu, Z.Q.; Deng, B.L. Attachment of silver nanoparticles (AgNPs) onto thin-film composite (TFC) membranes through covalent bonding to reduce membrane biofouling. J. Membr. Sci. 2013, 441, 73–82. [Google Scholar] [CrossRef]
  16. Mann, S. Molecular tectonics in biomineralization and biomimetic materials chemistry. Nature 1993, 365, 499–505. [Google Scholar] [CrossRef]
  17. Weiner, S.; Addadi, L. Design strategies in mineralized biological materials. J. Mater. Chem. 1997, 7, 689–702. [Google Scholar] [CrossRef]
  18. Addadi, L.; Weiner, S. Biomineralization—A pavement of pearl. Nature 1997, 389, 912–915. [Google Scholar] [CrossRef]
  19. Zhao, S.; Yao, J.R.; Fei, X.; Shao, Z.Z.; Chen, X. An antimicrobial film by embedding in situ synthesized silver nanoparticles in soy protein isolate. Mater. Lett. 2013, 95, 142–144. [Google Scholar] [CrossRef]
  20. Zhou, Y.; Kogiso, M.; Asakawa, M.; Dong, S.; Kiyama, R.; Shimizu, T. Antimicrobial nanotubes consisting of ag-embedded peptidic lipid-bilayer membranes as delivery vehicles. Adv. Mater. 2009, 21, 1742–1745. [Google Scholar] [CrossRef]
  21. Fei, X.; Li, W.; Shao, Z.Z.; Seeger, S.; Zhao, D.Y.; Chen, X. Protein biomineralized nanoporous inorganic mesocrystals with tunable hierarchical nanostructures. J. Am. Chem. Soc. 2014, 136, 15781–15786. [Google Scholar] [CrossRef] [PubMed]
  22. Wang, Y.Z.; Kim, U.J.; Blasioli, D.J.; Kim, H.J.; Kaplan, D.L. In vitro cartilage tissue engineering with 3D porous aqueous-derived silk scaffolds and mesenchymal stem cells. Biomaterials 2005, 26, 7082–7094. [Google Scholar] [CrossRef] [PubMed]
  23. Wang, Y.Z.; Kim, H.J.; Vunjak-Novakovic, G.; Kaplan, D.L. Stem cell-based tissue engineering with silk biomaterials. Biomaterials 2006, 27, 6064–6082. [Google Scholar] [CrossRef] [PubMed]
  24. Vepari, C.; Kaplan, D.L. Silk as a biomaterial. Prog. Polym. Sci. 2007, 32, 991–1007. [Google Scholar] [CrossRef] [PubMed]
  25. Fei, X.; Shao, Z.Z.; Chen, X. Synthesis of hierarchical three-dimensional copper oxide nanostructures through a biomineralization-inspired approach. Nanoscale 2013, 5, 7991–7997. [Google Scholar] [CrossRef] [PubMed]
  26. Mi, R.X.; Liu, Y.X.; Chen, X.; Shao, Z.Z. Structure and properties of various hybrids fabricated by silk nanofibrils and nanohydroxyapatite. Nanoscale 2016, 8, 20096–20102. [Google Scholar] [CrossRef] [PubMed]
  27. Selvakannan, P.R.; Swami, A.; Srisathiyanarayanan, D.; Shirude, P.S.; Pasricha, R.; Mandale, A.B.; Sastry, M. Synthesis of aqueous au core-ag shell nanoparticles using tyrosine as a pH-dependent reducing agent and assembling phase-transferred silver nanoparticles at the air-water interface. Langmuir 2004, 20, 7825–7836. [Google Scholar] [CrossRef] [PubMed]
  28. Liu, B.; Xu, H.; Zhao, H.Y.; Liu, W.; Zhao, L.Y.; Li, Y. Preparation and characterization of intelligent starch/PVA films for simultaneous colorimetric indication and antimicrobial activity for food packaging applications. Carbohydr. Polym. 2017, 157, 842–849. [Google Scholar] [CrossRef] [PubMed]
  29. Chiellini, E.; Cinelli, P.; Chiellini, F.; Imam, S.H. Environmentally degradable bio-based polymeric blends and composites. Macromol. Biosci. 2004, 4, 218–231. [Google Scholar] [CrossRef] [PubMed]
  30. Dailey, L.A.; Wittmar, M.; Kissel, T. The role of branched polyesters and their modifications in the development of modern drug delivery vehicles. J. Control. Release 2005, 101, 137–149. [Google Scholar] [CrossRef] [PubMed]
  31. Cano, A.; Fortunati, E.; Chafer, M.; Gonzalez-Martinez, C.; Chiralt, A.; Kenny, J.M. Effect of cellulose nanocrystals on the properties of pea starch-poly(vinyl alcohol) blend films. J. Mater. Sci. 2015, 50, 6979–6992. [Google Scholar] [CrossRef]
  32. Zhou, Y.; Chen, W.X.; Itoh, H.; Naka, K.; Ni, Q.Q.; Yamane, H.; Chujo, Y. Preparation of a novel core-shell nanostructured gold colloid-silk fibroin bioconjugate by the protein in situ redox technique at room temperature. Chem. Commun. 2001, 23, 2518–2519. [Google Scholar] [CrossRef]
  33. Xie, J.P.; Lee, J.Y.; Wang, D.I.C.; Ting, Y.P. Silver nanoplates: From biological to biomimetic synthesis. ACS Nano 2007, 1, 429–439. [Google Scholar] [CrossRef] [PubMed]
  34. Fei, X.; Jia, M.H.; Du, X.; Yang, Y.H.; Zhang, R.; Shao, Z.Z.; Zhao, X.; Chen, X. Green synthesis of silk fibroin-silver nanoparticle composites with effective antibacterial and biofilm-disrupting properties. Biomacromolecules 2013, 14, 4483–4488. [Google Scholar] [CrossRef] [PubMed]
  35. Gil, E.S.; Hudson, S.M. Effect of silk fibroin interpenetrating networks on swelling/deswelling kinetics and rheological properties of poly(n-isopropylacrylamide) hydrogels. Biomacromolecules 2007, 8, 258–264. [Google Scholar] [CrossRef] [PubMed]
  36. Yao, M.Z.; Huang-Fu, M.Y.; Liu, H.N.; Wang, X.R.; Sheng, X.X.; Gao, J.Q. Fabrication and characterization of drug-loaded nano-hydroxyapatite/polyamide 66 scaffolds modified with carbon nanotubes and silk fibroin. Int. J. Nanomed. 2016, 11, 6181–6194. [Google Scholar] [CrossRef] [PubMed]
  37. Wang, X.Q.; Yucel, T.; Lu, Q.; Hu, X.; Kaplan, D.L. Silk nanospheres and microspheres from silk/PVA blend films for drug delivery. Biomaterials 2010, 31, 1025–1035. [Google Scholar] [CrossRef] [PubMed]
  38. Pour, Z.S.; Makvandi, P.; Ghaemy, M. Performance properties and antibacterial activity of crosslinked films of quaternary ammonium modified starch and poly(vinyl alcohol). Int. J. Biol. Macromol. 2015, 80, 596–604. [Google Scholar] [CrossRef] [PubMed]
  39. Madera-Santana, T.J.; Freile-Pelegrin, Y.; Azamar-Barrios, J.A. Physicochemical and morphological properties of plasticized poly(vinyl alcohol)-agar biodegradable films. Int. J. Biol. Macromol. 2014, 69, 176–184. [Google Scholar] [CrossRef] [PubMed]
  40. Li, X.G.; Wu, L.Y.; Huang, M.R.; Shao, H.L.; Hu, X.C. Conformational transition and liquid crystalline state of regenerated silk fibroin in water. Biopolymers 2008, 89, 497–505. [Google Scholar] [CrossRef] [PubMed]
  41. Partlow, B.P.; Bagheri, M.; Harden, J.L.; Kaplan, D.L. Tyrosine templating in the self-assembly and crystallization of silk fibroin. Biomacromolecules 2016, 17, 3570–3579. [Google Scholar] [CrossRef] [PubMed]
  42. Lok, C.N.; Ho, C.M.; Chen, R.; He, Q.Y.; Yu, W.Y.; Sun, H.; Tam, P.K.H.; Chiu, J.F.; Che, C.M. Silver nanoparticles: Partial oxidation and antibacterial activities. J. Biol. Inorg. Chem. 2007, 12, 527–534. [Google Scholar] [CrossRef] [PubMed]
  43. Burda, C.; Chen, X.B.; Narayanan, R.; El-Sayed, M.A. Chemistry and properties of nanocrystals of different shapes. Chem. Rev. 2005, 105, 1025–1102. [Google Scholar] [CrossRef] [PubMed]
  44. Drury, A.; Chaure, S.; Kroell, M.; Nicolosi, V.; Chaure, N.; Blau, W.J. Fabrication and characterization of silver/polyaniline composite nanowires in porous anodic alumina. Chem. Mater. 2007, 19, 4252–4258. [Google Scholar] [CrossRef]
  45. Feng, X.X.; Zhang, L.L.; Chen, J.Y.; Guo, Y.H.; Zhang, H.P.; Jia, C.I. Preparation and characterization of novel nanocomposite films formed from silk fibroin and nano-TiO2. Int. J. Biol. Macromol. 2007, 40, 105–111. [Google Scholar] [CrossRef] [PubMed]
  46. Meng, M.; He, H.W.; Xiao, J.; Zhao, P.; Xie, J.L.; Lu, Z.S. Controllable in situ synthesis of silver nanoparticles on multilayered film-coated silk fibers for antibacterial application. J. Colloid Interface Sci. 2016, 461, 369–375. [Google Scholar] [CrossRef] [PubMed]
  47. Tao, G.; Wang, Y.J.; Liu, L.N.; Chang, H.P.; Zhao, P.; He, H.W. Preparation and characterization of silver nanoparticles composited on polyelectrolyte film coated sericin gel for enhanced antibacterial application. Sci. Adv. Mater. 2016, 8, 1547–1552. [Google Scholar] [CrossRef]
  48. Cai, R.; Tao, G.; He, H.; Song, K.; Zuo, H.; Jiang, W.; Wang, Y. One-step synthesis of silver nanoparticles on polydopamine-coated sericin/polyvinyl alcohol composite films for potential antimicrobial applications. Molecules 2017, 22, 721. [Google Scholar] [CrossRef] [PubMed]
Materials 10 00667 g001 550
Figure 1. Illustration of the preparation and analysis of silver nanoparticles (AgNPs)–silk/poly(vinyl alcohol) (PVA) film.
Figure 1. Illustration of the preparation and analysis of silver nanoparticles (AgNPs)–silk/poly(vinyl alcohol) (PVA) film.
Materials 10 00667 g001
Materials 10 00667 g002 550
Figure 2. Characterization of silk fibroin solution by (A) UV-vis spectra and (B) fluorescence spectra.
Figure 2. Characterization of silk fibroin solution by (A) UV-vis spectra and (B) fluorescence spectra.
Materials 10 00667 g002
Materials 10 00667 g003 550
Figure 3. Comparison of UV-vis spectra of AgNPs–silk solutions: (A) in pH 5.0, 7.4, and 10.0; (B) at room temperature (RT), 50 °C, 75 °C, and 100 °C; (C) at room temperature, 37 °C, 50 °C, and 65 °C for 15 days; (D) at room temperature, −20 °C, −80 °C, and −196 °C for 15 days.
Figure 3. Comparison of UV-vis spectra of AgNPs–silk solutions: (A) in pH 5.0, 7.4, and 10.0; (B) at room temperature (RT), 50 °C, 75 °C, and 100 °C; (C) at room temperature, 37 °C, 50 °C, and 65 °C for 15 days; (D) at room temperature, −20 °C, −80 °C, and −196 °C for 15 days.
Materials 10 00667 g003
Materials 10 00667 g004 550
Figure 4. (A) UV-vis spectra of AgNPs–silk solution; (B,C) SEM images of silk/PVA and AgNPs–silk/PVA films; (D) EDS of a selected area of AgNPs–silk/PVA film.
Figure 4. (A) UV-vis spectra of AgNPs–silk solution; (B,C) SEM images of silk/PVA and AgNPs–silk/PVA films; (D) EDS of a selected area of AgNPs–silk/PVA film.
Materials 10 00667 g004
Materials 10 00667 g005 550
Figure 5. Characterization of silk/PVA and AgNPs–silk/PVA films by (A) thermogravimetric analysis (TGA) and (B) Fourier transform infrared spectroscopy (FTIR).
Figure 5. Characterization of silk/PVA and AgNPs–silk/PVA films by (A) thermogravimetric analysis (TGA) and (B) Fourier transform infrared spectroscopy (FTIR).
Materials 10 00667 g005
Materials 10 00667 g006 550
Figure 6. Mechanical properties of AgNPs–silk/PVA film: (A) tensile strength and (B) elongation at break.
Figure 6. Mechanical properties of AgNPs–silk/PVA film: (A) tensile strength and (B) elongation at break.
Materials 10 00667 g006
Materials 10 00667 g007 550
Figure 7. Water contact angles of S50P50 (A), A-S80P20 (B), A-S67P33 (C), and A-S50P50 (D) films.
Figure 7. Water contact angles of S50P50 (A), A-S80P20 (B), A-S67P33 (C), and A-S50P50 (D) films.
Materials 10 00667 g007
Materials 10 00667 g008 550
Figure 8. Effects of films on the growth of (A) E. coli and (B) S. aureus in the absence of a film (curve a), and in the presence of S50P50, A-S80P20, A-S67P33, and A-S50P50 films (curves b–e).
Figure 8. Effects of films on the growth of (A) E. coli and (B) S. aureus in the absence of a film (curve a), and in the presence of S50P50, A-S80P20, A-S67P33, and A-S50P50 films (curves b–e).
Materials 10 00667 g008
Materials 10 00667 g009 550
Figure 9. Inhibition zone assay of silk/PVA and AgNPs–silk/PVA films on the growth of (A) E. coli and (B) S. aureus.
Figure 9. Inhibition zone assay of silk/PVA and AgNPs–silk/PVA films on the growth of (A) E. coli and (B) S. aureus.
Materials 10 00667 g009
Materials 10 00667 g010 550
Figure 10. Degradation kinetics of AgNPs–silk/PVA films in (A) pH 4.0, (B) 7.4, and (C) 10.0 buffers at 37 °C.
Figure 10. Degradation kinetics of AgNPs–silk/PVA films in (A) pH 4.0, (B) 7.4, and (C) 10.0 buffers at 37 °C.
Materials 10 00667 g010

Share and Cite

MDPI and ACS Style

Tao, G.; Cai, R.; Wang, Y.; Song, K.; Guo, P.; Zhao, P.; Zuo, H.; He, H. Biosynthesis and Characterization of AgNPs–Silk/PVA Film for Potential Packaging Application. Materials 2017, 10, 667. https://doi.org/10.3390/ma10060667

AMA Style

Tao G, Cai R, Wang Y, Song K, Guo P, Zhao P, Zuo H, He H. Biosynthesis and Characterization of AgNPs–Silk/PVA Film for Potential Packaging Application. Materials. 2017; 10(6):667. https://doi.org/10.3390/ma10060667

Chicago/Turabian Style

Tao, Gang, Rui Cai, Yejing Wang, Kai Song, Pengchao Guo, Ping Zhao, Hua Zuo, and Huawei He. 2017. "Biosynthesis and Characterization of AgNPs–Silk/PVA Film for Potential Packaging Application" Materials 10, no. 6: 667. https://doi.org/10.3390/ma10060667

APA Style

Tao, G., Cai, R., Wang, Y., Song, K., Guo, P., Zhao, P., Zuo, H., & He, H. (2017). Biosynthesis and Characterization of AgNPs–Silk/PVA Film for Potential Packaging Application. Materials, 10(6), 667. https://doi.org/10.3390/ma10060667

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop