In Vitro Comparison between Metal Sleeve-Free and Metal Sleeve-Incorporated 3D-Printed Computer-Assisted Implant Surgical Guides
Previous Article in Journal
Non-Destructive Imaging on Synthesised Nanoparticles
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 14
Issue 3
10.3390/ma14030614
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

High-Temperature Properties and Applications of Si-Based Polymer-Derived Ceramics: A Review

by
Zhongkan Ren
,
Shakir Bin Mujib
and
Gurpreet Singh
*
Department of Mechanical and Nuclear Engineering, Kansas State University, Manhattan, KS 66506, USA
*
Author to whom correspondence should be addressed.
Materials 2021, 14(3), 614; https://doi.org/10.3390/ma14030614
Submission received: 21 November 2020 / Revised: 20 January 2021 / Accepted: 26 January 2021 / Published: 29 January 2021
(This article belongs to the Special Issue Advanced Functional Polymer‐Derived Ceramic Fibers: Preparation, Properties and Applications)
Browse Figures
Review Reports Versions Notes

Abstract

:
Ceramics derived from organic polymer precursors, which have exceptional mechanical and chemical properties that are stable up to temperatures slightly below 2000 °C, are referred to as polymer-derived ceramics (PDCs). These molecularly designed amorphous ceramics have the same high mechanical and chemical properties as conventional powder-based ceramics, but they also demonstrate improved oxidation resistance and creep resistance and low pyrolysis temperature. Since the early 1970s, PDCs have attracted widespread attention due to their unique microstructures, and the benefits of polymeric precursors for advanced manufacturing techniques. Depending on various doping elements, molecular configurations, and microstructures, PDCs may also be beneficial for electrochemical applications at elevated temperatures that exceed the applicability of other materials. However, the microstructural evolution, or the conversion, segregation, and decomposition of amorphous nanodomain structures, decreases the reliability of PDC products at temperatures above 1400 °C. This review investigates structure-related properties of PDC products at elevated temperatures close to or higher than 1000 °C, including manufacturing production, and challenges of high-temperature PDCs. Analysis and future outlook of high-temperature structural and electrical applications, such as fibers, ceramic matrix composites (CMCs), microelectromechanical systems (MEMSs), and sensors, within high-temperature regimes are also discussed.

1. Introduction

Ceramics, which are often defined as nonmetallic, inorganic solid materials, have existed for more than 9000 years [1]. Wide varieties of ceramic compounds yield various bonding types (e.g., covalent, metallic, ionic, or mixed) and adjustable physical, and chemical properties [2,3]. Since the early 21st century, high-temperature structural ceramics have gained popularity due to their low density, high oxidation and chemical resistance, outstanding creep resistance, and thermal shock resistance as structural materials [4].
Conventional Si-based advanced ceramics such as SiC or Si3N4, which are manufactured via the powder route [5], have shown exceptional creep and oxidation resistance up to temperatures exceeding 1000 °C without loss of structure and functionality. However, the extremely high processing temperature of conventional ceramics complicates the production of complex-shaped ceramics, and the brittle nature of ceramics prohibits casting or machining. Although the development of additive manufacturing technologies means that powders can generate complex structures as easily as metals or polymers [6], energy-efficient fabrication of fibers, coatings, films, or ceramic matrix composites (CMCs) from powders is still difficult [5].
The polymer-derived ceramic (PDC) approach is an advanced ceramic manufacturing technique that designs or controls molecular structures of ceramic products at molecular or atomic levels [3]. There has been a rapid increase in PDC-related research, as well as PDCs for high-temperature applications, over last 30 years (Figure 1). PDCs are unique because amorphous ceramics are not achievable via other ceramic synthesis techniques (e.g., powder sintering or chemical vapor deposition) [7]. Polymeric network structures become amorphous microstructures during pyrolysis and form nanodomains of 1–3 nm, which provide good creep and oxidation resistance up to 1500 °C. Thereby, thermodynamically unstable ternary ceramics (e.g., SiCN, SiOC, and BCN) and quaternary ceramics (e.g., SiOCN, SiBCN, and SiAlOC) are achieved and exist as stable microstructures (e.g., free C, SiO2, Si3N4, SiC, BN, Al2O3). The detailed PDC synthesis processes are presented in Figure 2.
Silicon-based PDCs are produced via thermal pyrolysis of crosslinked organosilicon precursors that may contain light elements such as C, H, O, N, or B at temperatures as high as 1400 °C [8]. Depending on the specific ceramic elemental configuration, some PDCs have high-temperature applications such as coatings, reinforcement, sensors, or matrices [9]. SiCN amorphous ceramics are generally produced from preceramic precursors that contain Si, N, and C via high-temperature (usually ~1000 °C) annealing in inert environments. High-temperature (usually >1100 °C) environments cause the crystallization of amorphous SiCN with microstructures of mixed SiN4−xCx silicon tetrahedrons [9] and segregation into thermodynamically stable crystalline microstructures (e.g., SiC, Si3N4, C, or Si) at higher temperatures [8]. However, excessive carbon leads to the decomposition of ceramic structures at temperatures above 1500 °C (as shown in Figure 3). SiOC PDCs have amorphous microstructures of mixed SiO4−xCx that separate into SiO2, SiC and C at high temperatures and ultimately degrade into SiC and CO gas (>1300 °C).
Incorporating other elements, such as B [8,10,11,12], Al [13,14,15], Nb [16], Zr [4,17,18], Ti [19,20,21], or Hf [12,22,23,24], in the Si-C-N or Si-O-C systems may greatly enhance the thermostability of ceramic products by preventing or impeding the crystallization and phase segregation of the ceramic phases in inert or oxidizing environments [7]. Initially, at the crosslinking stage, B atoms may improve the formation of the crosslinking network and increase the yield and structural density of SiBOC [11,12]. Upon polymer-to-ceramic conversion, doped elements may form additional phases (e.g., TiO2, HfO2, ZrO2) and lead to nanocomposite-like structures of metal-oxide/amorphous ceramics [25] or dissolve into and alter the amorphous phase (e.g., SiBOC, SiAlOC) which eventually segregate into additional phases (BN, Al2O3) at higher temperatures. At the amorphous stage, the superior stability of the B- or Al-doped amorphous phase significantly enhances the oxidation resistance of SiBOC or SiAlOC ceramics [11,13]. For example, SiAlOC may stay amorphous at much higher temperatures (up to 1400–1500 °C) compared to SiOC phase (crystallize at ~1300 °C) [14]. The doped SiOC phase has been shown to impede the diffusion of O2 at high temperatures and inhibit the decomposition of the microstructure [11,15].
After forming additional microstructures, the presence of TiO2, HfO2 or ZrO2 in the amorphous PDC matrix prevent the crystallization and decomposition of the amorphous phase [18,21,24]. Recent work has shown that presence of TiO2 nanocrystals improves the viscosity of the PDC microstructures at elevated temperatures which deters collapse in the TiO2/SiO2 structure [21].
As previous studies have shown, the phase, microstructures, thermal stability, and high-temperature behaviors of synthesized ceramics can be modified by incorporating different types of hetero-elements into the Si-based precursors at the molecular level. Figure 3 shows the phase separation and thermal decomposition of various Si-based PDCs at elevated temperatures.
Further information on the processing/manufacturing [6,26,27,28,29,30,31,32], physical and mechanical properties [26,27,28,29,30,31,33,34,35,36,37] and micro/nanostructures [5,26,27,29,31,32,34,35,38,39,40] of PDCs can be found in the previously published review articles.

2. Applications

2.1. Fibers and Matrices

PDC fibers are popular PDC products due to the relentless demand for high-temperature, ceramic-matrix aerospace components [7]. Reinforcing PDC fibers provides strength and structural foundation or shape to the composite, generally in the form of a complex 3D woven structure designed to closely match the final shape of the component [41].
Ji et al. investigated high-temperature antioxidation of amorphous SiBCN fibers, derived from polyborosilazane for aerospace applications [42]. Initial structural characterization suggested amorphous fiber structures of silicon-nitride tetrahedrons (SN3C, SiN4), free carbon, BN hexatomic rings, and BN2C phases (Figure 4a). Crack-free fibers were exposed to air and an imitated combustion environment (with H2O, O2, and N2) at 1400 °C for 2 h. Although subsequent structural investigations indicated well-preserved fiber morphologies with crack-free surfaces and interiors with negligible compositional changes, microstructural changes were captured. Two extra layers formed at the surface of the fibers due to phase separation in which the outermost layer was the SiO2 phase, the intermediate layer consisted primarily of the hexagonal BN phase, and the core was the unaffected amorphous SiBCN structure. The combustion environment produced more crystalline SiO2 in the amorphous SiO2 surface layer than the samples annealed in the air, possibly due to the presence of H2O molecules.
As mentioned, excessive carbon in PDC structures often causes reduced thermal stability of the system due to direct oxidation in air or a reaction with other phases to form crystalline structures. Recent studies on a novel ternary system with only Si, B and N have shown an applicable synthesis of Si-based, carbon-free ceramic fibers from polyborosilanes. Specifically, the ceramics were synthesized from precursors without carbon. For example, Cl3Si-NH-BCl2 can crosslink into oligomers or polymers via polycondensation in NH3, and additional pyrolysis produces C-free SiBN ceramics, which have theoretical thermal stability up to 1700 °C. However, this type of precursor requires handling in a dry inert atmosphere due to hydrolysis reactions of the precursors with moisture. Liu et al. studied the hydrolysis effect of polyborosilazane on SiBN ceramic fibers, demonstrating evidence of the formation of Si-O-Si groups in the precursor (Figure 5) [43]. The incorporated oxygen altered the surface features of pyrolyzed PDC fibers and caused the formation of β-SiO2 at 1400 °C, leading to decreased thermal stability due to early crystallization.
In the 1990s, SiC/SiC composites were manufactured for high-temperature structural applications based on the highly thermal resistant SiC fibers [44]. Composites of ceramic matrices are known as ceramic matrix composites (CMCs). In general, four industrial techniques have been developed to produce matrices on preshaped woven fiber parts: chemical vapor infiltration (CVI), polymer impregnation and pyrolysis (PIP), reactive melt infiltration (RMI), and slurry infiltration and hot pressing (SI-HP) [45]. The PIP technique utilizes PDC routes with handling and processing advantages, such as low manufacturing temperature and pressure [46].
PIP-fabricated SiC matrices have up to 30% porosity, which reduces the strength of the composite product [44]. Infiltration is often necessary to minimize residual porosity of the ceramic matrix phase during the PIP process. Takeda et al. determined the effect of infiltration on total porosity and bending strength of PIP-fabricated SiC/SiC composites (Figure 6) [44]. The results showed that the porosities of SiC CMCs were decreased from 23% to 10% after 14 PIP cycles, and nominal bending strength had an approximately 50% increase from less than 400 to 600 MPa. Yang et al. investigated the thermal shock properties of a 3D woven carbon fiber (Cf)-reinforced PIP prepared SiC composite [47]. The thermal quench of the specimens was performed from 1500 °C in the air to 100 °C boiling water with a holding time of only 10 min between each environment. Thermal degradation (approximately 13% weight loss) of CMC and a significant decrease in specimen strength were observed after five cycles. Comparatively, the CVI-SiC-coated 3D Cf-reinforced SiC composite showed over 99% mass retention and less of a decrease in tensile strength under the same condition.
The PIP technique also allows the production of ternary ceramics, such as SiCN or SiOC. Mainzer et al. investigated the thermal stability of C and SiC fiber-reinforced SiCN CMCs derived from low viscous poly(methyl vinyl)silazane pyrolyzed at 1300 °C for 8 PIP cycles [49]. Two commercial fibers for each SiC and Cf were selected as the reinforcement for CMCs. The prepared specimen had a maximum mechanical performance of 478 MPa for tensile strength and 206 GPa for modulus. However, after exposing the samples to air at 1200 °C for 10 h, CMCs showed a significant decrease in tensile strength up to 43% for SiC-reinforced samples, and 98.6% for Cf-reinforced CMC. This expected phenomenon was due to oxidation of the fiber–matrix interface in which the cracked interface provided an oxygen-diffusion path and caused strong oxidation in the SiCN/SiCN interfaces. When the fibers were precoated with CVD-SiC, however, the tensile strength retention reached 89% under the same oxidation environment.
Lee et al. reported enhanced thermal stability, creep resistance and flexural strength of Cf-reinforced SiBCN composites compared to other matrices, such as SiOC (Figure 7) [50]. In a total of 16 cycles, polyacrylonitrile (PAN)-derived carbon fiber mats were infiltrated with preceramic polymers that converted to SiBCN after pyrolysis at 1400 °C. The resulting CMC reach 89% of relative density with crack-free interfaces. The in situ four-point bending test at 1500 °C in Ar suggested bending flexural strength up to 255 MPa without brittle fracture. Creep testing at 1400 °C for 60 h with 100 MPa pressure in Ar showed a total creep strain of 0.55%, and thermal stability testing showed that thermal degradation of the SiBCN matrix began at approximately 1500 °C. An additional increase in environment temperature drastically decreased flexural strength to 70 MPa at 1700 °C, and 43 MPa at 2000 °C.

2.2. Microelectromechanical Systems and Semiconductors

In the early 1990s, Mocaer et al. initially measured the electrical conductivity of SiCNO at a temperature range up to 500 °C, showing a semiconducting feature of PDCs [51]. Later, Ryu et al. measured and confirmed the semiconductive properties of SiCNO PDCs up to 1300 °C without dopants [51]. The band-gap change measured for SiCNO PDCs varied from 2.2 to 0.1 eV as the annealing temperature rose from 1100 to 1400 °C. The results also suggested tweakable semiconductive properties of PDCs by tailoring the elemental compositions. This semiconducting feature of PDCs have founded a new variety of high-temperature semiconducting field and is appealing to other applications, such as sensing or catalyzing. Further electrical characterization of SiCNO PDCs by Terauds et al. exposed significant temperature-dependent piezoresistivity at temperatures up to 1000 °C [52]. Their research identified the dominant (one order of magnitude higher) gauge factors of this PDC over other commercial materials, such as Ge, Si, SiC, or diamond at higher temperature limits, providing an efficient alternative material to high-temperature stress sensors. However, all the electrical properties are manipulatable by controlling the microstructures [53].
As PDC fibers and composites began to be utilized as critical components of advanced applications (e.g., turbine engine for aerospace purposes) in high-temperature environments, the simultaneous controlling and monitoring of high-temperature and harsh working environments became essential [54]. Silicon-based MEMSs have been used in applications such as sensors or actuators, but have demonstrated limited performance due to poor thermal and mechanical stabilities at temperatures above 250 and 600 °C, respectively [54]. SiC, a wide bandgap semiconductor, has also been proposed to overcome working temperature restrictions of Si MEMSs for high-temperature sensing. In addition to an outstanding thermal stability, their superior ant-corrosion, chemical stability and mechanical performance have also attracted wide attention for high-temperature semiconducting applications [54,55]. The shaping process and microscopic features of PDC MEMSs are presented in Figure 8 [56]. However, film-deposition-manufactured SiC is costly to produce and requires extra micromachining, which complicates productions [57]. In comparison, PDC materials have shown great flexibility for MEMS production; the polymer route utilizes micropatterning to allow the shaping of liquid precursors.
In the early 2000s, Liew et al. proposed SiCN ceramic microparts with a feature size of 20 microns for MEMSs derived from an injectable liquid precursor (Figure 9) [58]. The produced microparts showed approximately 150% and 66% improved strength and hardness, respectively, over powder-based PDC samples. The manufactured parts bonded without interface using the same liquid precursor as an adhesive via second crosslinking.

2.3. Membranes, Coatings and Adhesives

SiBCN is a promising high-temperature PDC material that has shown significant advantages over commercial alumina membranes, including ease of manufacturing via a sol-gel process and high thermal stability and resistance to oxidation and phase transformation [10]. Hauser et al. showed the potential of SiBCN as high-temperature separating membranes (Figure 10) [10]. They synthesized ceramic film on an alumina substrate surface by dip-coating the substates into the precursor solution. A thin SiBCN film with a thickness of 2.5 microns was produced on porous alumina, with pore sizes of 0.6–6 nm. This SiBCN, which was PDC-derived from a cyclic preceramic precursor and borane dimethylsulfide, showed high thermal stability at 1400 °C in an oxidizing environment with a mass drop of only 1 wt.% for 50 h, free of crystallization.
PDC ceramic coatings have also gained attention because, similar to membranes, they are easily manufacturable on large complex surfaces with fine structural and thermal performances at energy efficient pyrolysis temperatures as low as 800 °C [59]. Previously, the primary drawback of using PDCs was the coating thickness, which was limited to several microns due to thermal shrinkage upon pyrolysis. Consequently, active or passive filters were added to the system to control volumetric shrinkage and enhance functionalities such as thermal or electrical conductivities, altering thermal expansion and hardness, etc. [59].
Klausmann et al. demonstrated high-temperature structural evolution of one-micron-thick SiCN coatings derived from polysilylcarbodiimide-based linear and branched precursors via spin coating (Figure 11) [60]. Results showed that thermal and mechanical performances are directly related to the carbon content of the PDC: low carbon content showed up to an 80% increase in elastic modulus and hardness at ambient and lower crystallization at annealing of 1400 °C than high-carbon SiCN. A recent study by Alvi et al. investigated the tribological coating performance of SiOC PDCs with ZrSi2 and Ag fillers for superior tribological performance at a high load and high temperature (Figure 12) [59]. The characterization suggested well-controlled shrinkage and surface cracks with fillers with a coating thickness of more than 10 microns. X-ray diffraction (XRD) analysis showed the decomposition of ZrSi2 filler into ZrO2 and possibly SiO2 and Si, as well as the oxidation of Ag into Ag2O. The formation of ZrO2 caused SiOC-ZrSi2 coatings to demonstrate better tribological performances with negligible wear and lubricating features in ambient temperatures.
High-temperature adhesives are critical structural materials for aerospace and nuclear power applications. The adhesives must provide decent bonding strength in high-temperature environments. In 2018, Luan et al. conducted an adhesive performance investigation of SiCN for joining Al2O3 surfaces from polysilaznes with fillers such as polyborosilazane, polysiloxane and Al2O3 to address shrinkage and improve high-temperature bonding strength. Results showed an approximate 12 MPa bonding strength, obtained from modified adhesive, at room temperature and an approximate 50% decrease at 1000 °C, which was still twice the performance of pure SiCN at the elevated temperature. The coating showed improved thermal stability with nano-Al2O3 filler, possibly due to mixed bonding between Al2O3, SiO2 and B2O3 stabilizing the liquefaction of B2O3 at said temperature range. The research group conducted another investigation of TiB2-modified SiCN ceramic adhesive. The formation of SiO2, B2O, and TiO2 during the thermal pyrolysis process resulted in an approximate 10 MPa adhesive strength, which was found at room temperature and 8 MPa at 800 °C. The residual TiB2 continued to impede crack propagation.

2.4. Sensors

Sensors are often used in advanced systems that require detection and controls. For example, heat flux sensors are mandatory for monitoring gas turbine combustion chamber temperature, pressure and flow [61]. PDC sensors were produced because of their semiconductive behavior; more specifically, the temperature-dependent conductivity feature of PDCs. Silicon, or SiC, sensors have been widely studied and used for temperatures below 500 °C. Novel PDCs may be reliable for high-temperature microsensors. Another potential high-temperature pressure sensor, which is based on the piezoresistivity of doped PDCs, requires the sensing material to withstand the harsh environment at elevated temperatures without losing functionality and structures [62].
Nagaiah et al. proposed a high-temperature heat flux sensor design with micromachined SiCN as a thermal resistance layer and thin amorphous semiconducting SiAlCN layers as resistance temperature detectors (RTDs), as shown in Figure 13 [61]. Seo et al. then directly tested photolithography manufactured SiCN PDC thin films as RTDs at moderate temperatures, confirming the feasibility of heat flux sensing [53]. Zhao et al. fabricated, tested, and compared a complete temperature sensor with thermocouples using SiAlCN as the probe material (Figure 14). The results showed a repeatable, close-matching result to the thermocouple measurements at temperatures up to 845 °C [63]. In 2016, Yu et al. studied a high-temperature SiCNO sensor derived from polyvinlysilazane without metallic or semiconducting elements, similar to SiAlCN (Figure 15) [64]. SiCNO was functionalized with graphene oxide (GO), which enhanced the electrical conductivity of the ceramic matrix. The composite temperature sensor delivered a more accurate and sensitive measurement of temperature change than the SiCNO temperature sensor.
Based on the giant gauge factors Teraudes et al. found in SiCNO PDCs, Li et al. recently reported a full design and characterization of pressure sensors from Al-doped SiOC PDCs for potential high-temperature usage. The sensor was tested in ambient conditions and showed outstanding accuracy, repeatability and stability with changing pressures.
Another electronic application of PDCs was found as carbon-containing absorbing materials for waves. The use of PDCs resolved issues such as the high density of pure magnetic absorbing materials and the low thermal stability of pure carbon materials. Hou et al. proposed high-temperature oxidation resistive wave-absorbing SiC composites via the PDC route with the incorporation of Fe3Si and carbon nanotubes (CNTs) [65]. Experimental results demonstrated the high-temperature antioxidation and tunable wave absorption of SiC/Fe3Si/CNTs composite ceramics. The minimal reflection loss (RL) value reached −41.2 dB with a sample measuring 2 mm thick, although the RL value could be −40 dB (at 10.36 GHz with a sample thickness of 3 mm) after heat treatment at 800 °C in the air with mass loss < 4.9%.
High-temperature applications of PDCs are summarized in Table 1.

3. Conclusions and Outlook

In this work we highlighted high-temperature properties and corresponding high-temperature applications of PDCs. Specific applications, such as ceramic fibers, fiber-reinforced ceramic matrix composites, MEMSs, semiconductive applications, membranes, coatings, adhesives and sensors, were presented based on mechanical, electrical and thermal performances at elevated temperatures above 500 °C. Combining the outstanding intrinsic properties of ceramics with the unique features of the polymer route, PDCs were shown to have advantages over conventional powder-based ceramics and other types of materials in many fields. For example, PDCs demonstrated superior creep resistance and oxidation resistance compared to conventional powder-based advanced ceramics, as well as more controlled intrinsic porosity, complex shaping capability and lower processing temperatures. PDC-based fiber materials appear to retain high elastic modulus and mechanical strength similar to carbon reinforcement materials (e.g., carbon fibers) even at higher temperatures. PDC based composites offer enhanced toughness, high modulus and strength and increased oxidation resistance at higher working temperatures than traditional single-crystals or superalloys.
In addition, a fine-tuning of desired properties is possible by altering the initial composition of the preceramic polymer and optimizing the temperature and duration of the crosslinking and pyrolysis processes. The incorporation of new elements may also enhance the mechanical and thermal properties, or introduce new properties (e.g., semiconductive behavior) to the PDCs. The use of polymeric precursors allows advanced manufacturing techniques to generate micrometer to submicrometer-sized features, such as micropatterned MEMSs, coatings and nanofibers.
Future advancement of high-temperature PDCs are expected to be in CMCs and advanced manufacturing. Structural CMCs are presently being tested for commercial aerospace engine applications such as turbine components that generally operate in harsh environments; further improvements in mechanical and thermal reliability of the components are needed to ensure the safe use of these next-generation structural materials. On the other hand, advanced manufacturing, especially additive manufacturing (or 3D printing) of PDCs, reported over a decade ago, can now produce submicron feature sizes via laser-assisted techniques (e.g., stereolithography or selective laser sintering). However, sintering or pyrolysis for polymer-to-ceramic conversion often leads to shrinkage, residual porosity and related defects that significantly reduce the mechanical strengths and moduli of the printed components for high-temperature applications.

Author Contributions

Conceptualization G.S. and Z.R.; text, Z.R. and S.B.M.; schematics, Z.R.; figures, Z.R. All authors have read and agreed to the published version of the manuscript.

Funding

Financial support from National Science Foundation grant number 1743701 is gratefully acknowledged.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Greil, P. Near Net Shape Manufacturing of Polymer Derived Ceramics. J. Eur. Ceram. Soc. 1998, 18, 1905–1914. [Google Scholar] [CrossRef]
  2. Riedel, R. From molecules to materials—A novel route for the synthesis of advanced ceramics. Naturwissenschaften 1995, 82, 12–20. [Google Scholar] [CrossRef]
  3. Bill, J.; Aldinger, F. Precursor-derived Covalent Ceramics. Adv. Mater. 1995, 7, 775–787. [Google Scholar] [CrossRef]
  4. Ionescu, E.; Linck, C.; Fasel, C.; Müller, M.; Kleebe, H.; Riedel, R.; Müller, M. Polymer-Derived SiOC/ZrO2Ceramic Nanocomposites with Excellent High-Temperature Stability. J. Am. Ceram. Soc. 2010, 93, 241–250. [Google Scholar] [CrossRef]
  5. Wen, Q.; Yu, Z.; Riedel, R. The fate and role of in situ formed carbon in polymer-derived ceramics. Prog. Mater. Sci. 2020, 109, 100623. [Google Scholar] [CrossRef]
  6. Eckel, Z.C.; Zhou, C.; Martin, J.H.; Jacobsen, A.J.; Carter, W.B.; Schaedler, T.A. Additive manufacturing of polymer-derived ceramics. Science 2016, 351, 58–62. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  7. Colombo, P.; Mera, G.; Riedel, R.; Sorarù, G.D. Polymer-Derived Ceramics: 40 Years of Research and Innovation in Advanced Ceramics. J. Am. Ceram. Soc. 2010, 93, 1805–1837. [Google Scholar] [CrossRef]
  8. Müller, A.; Peng, J.; Seifert, H.J.; Bill, J.; Aldinger, F. Si−B−C−N Ceramic Precursors Derived from Dichlorodivinylsilane and Chlorotrivinylsilane. 2. Ceramization of Polymers and High-Temperature Behavior of Ceramic Materials. Chem. Mater. 2002, 14, 3406–3412. [Google Scholar] [CrossRef]
  9. Zimmermann, A.; Bauer, A.; Christ, M.; Cai, Y.; Aldinger, F. High-temperature deformation of amorphous Si–C–N and Si–B–C–N ceramics derived from polymers. Acta Mater. 2002, 50, 1187–1196. [Google Scholar] [CrossRef]
  10. Hauser, R.; Nahar-Borchard, S.; Riedel, R.; Ikuhara, Y.H.; Iwamoto, Y. Polymer-Derived SiBCN Ceramic and their Potential Application for High Temperature Membranes. J. Ceram. Soc. Jpn. 2006, 114, 524–528. [Google Scholar] [CrossRef] [Green Version]
  11. Xie, S.; Wang, Y.; Lei, Y.; Wang, B.; Wu, N.; Gou, Y.; Fang, D. A simply prepared flexible SiBOC ultrafine fiber mat with enhanced high-temperature stability and chemical resistance. RSC Adv. 2015, 5, 64911–64917. [Google Scholar] [CrossRef]
  12. Lyu, Y.; Tang, H.; Zhao, G. Effect of Hf and B incorporation on the SiOC precursor architecture and high-temperature oxidation behavior of SiHfBOC ceramics. J. Eur. Ceram. Soc. 2020, 40, 324–332. [Google Scholar] [CrossRef]
  13. Plachký, T.; Lenčéš, Z.; Hric, L.; Šajgalík, P.; Baláž, P.; Riedel, R.; Kleebe, H.-J. Processing and mechanical properties of Si3N4 composites employing polymer-derived SiAlOC as sintering aid. J. Eur. Ceram. Soc. 2010, 30, 759–767. [Google Scholar] [CrossRef]
  14. Harshe, R.; Balan, C.; Riedel, R. Amorphous Si(Al)OC ceramic from polysiloxanes: Bulk ceramic processing, crystallization behavior and applications. J. Eur. Ceram. Soc. 2004, 24, 3471–3482. [Google Scholar] [CrossRef]
  15. Wang, Y.; Fan, Y.; Zhang, L.; Zhang, W.; An, L. Polymer-derived SiAlCN ceramics resist oxidation at 1400 °C. Scr. Mater. 2006, 55, 295–297. [Google Scholar] [CrossRef]
  16. Thiyagarajan, G.B.; Koroleva, E.; Filimonov, A.; Vakhrushev, S.; Kumar, R. Tailorable Dielectric Performance of Niobium-Modified Poly(hydridomethylsiloxane) Precursor-Derived Ceramic Nanocomposites. Phys. Status Solidi 2020, 217, 2000417. [Google Scholar] [CrossRef]
  17. Su, D.; Yan, X.; Liu, N.; Li, X.; Ji, H. Preparation and characterization of continuous SiZrOC fibers by polyvinyl pyrrolidone-assisted sol–gel process. J. Mater. Sci. 2016, 51, 1418–1427. [Google Scholar] [CrossRef]
  18. Anand, R.; Nayak, B.B.; Behera, S.K. Coarsening kinetics of nanostructured ZrO2 in Zr-doped SiCN ceramic hybrids. J. Alloys Compd. 2019, 811, 151939. [Google Scholar] [CrossRef]
  19. Hering, N.; Schreiber, K.; Riedel, R.; Lichtenberger, O. Synthesis of polymeric precursors for the formation of nanocrystalline Ti-C-N/amorphous Si-C-N composites. Appl. Organomet. Chem. 2001, 15, 879–886. [Google Scholar] [CrossRef]
  20. Yu, Y.; Guo, Y.; Cheng, X.; Zhang, Y. Preparation of TiO2/SiO2 composite fiber by thermal decomposition of polycarbosilane–tetrabutyl titanate hybrid precursor. J. Mater. Chem. 2009, 19, 5637–5642. [Google Scholar] [CrossRef]
  21. Tang, X.; Yu, Y.; Yang, D. SiO2/TiO2 fibers from titanium-modified polycarbosilane. J. Mater. Sci. 2010, 45, 2670–2674. [Google Scholar] [CrossRef]
  22. Sujith, R.; Zimmermann, A.; Kumar, R. Crack Evolution and Estimation of Fracture Toughness of HfO2/SiCN(O) Polymer Derived Ceramic Nanocomposites. Adv. Eng. Mater. 2015, 17, 1265–1269. [Google Scholar] [CrossRef]
  23. Yan, X.; Su, D.; Duan, H.; Zhang, F. Preparation of SiOC/HfO2 fibers from silicon alkoxides and tetrachloride hafnium by a sol–gel process. Mater. Lett. 2015, 148, 196–199. [Google Scholar] [CrossRef]
  24. Sujith, R.; Kousaalya, A.B.; Kumar, R. Synthesis and phase stability of precursor derived HfO2/Si–C–N–O nanocomposites. Ceram. Int. 2012, 38, 1227–1233. [Google Scholar] [CrossRef]
  25. Sun, J.; Wen, Q.B.; Li, T.; Wiehl, L.; Fasel, C.; Feng, Y.; De Carolis, D.; Yu, Z.J.; Fu, Q.G.; Riedel, R. Phase evolution of SiOC-based ceramic nanocomposites derived from a polymethylsiloxane modified by Hf-and Ti-alkoxides. J. Am. Ceram. Soc. 2020, 103, 1436–1445. [Google Scholar] [CrossRef]
  26. Greil, P. Polymer derived engineering ceramics. Adv. Eng. Mater. 2000, 2, 339–348. [Google Scholar] [CrossRef]
  27. Riedel, R.; Mera, G.; Hauser, R.; Klonczynski, A. Silicon-Based Polymer-Derived Ceramics: Synthesis Properties and Applications—A Review. J. Ceram. Soc. Jpn. 2006, 114, 425–444. [Google Scholar] [CrossRef] [Green Version]
  28. Miele, P.; Bernard, S.; Cornu, D.; Toury, B. Recent Developments in Polymer-Derived Ceramic Fibers (PDCFs): Preparation, Properties and Applications—A Review. Soft Mater. 2007, 4, 249–286. [Google Scholar] [CrossRef]
  29. Flores, O.; Bordia, R.K.; Nestler, D.; Krenkel, W.; Motz, G. Ceramic Fibers Based on SiC and SiCN Systems: Current Research, Development, and Commercial Status. Adv. Eng. Mater. 2014, 16, 621–636. [Google Scholar] [CrossRef]
  30. Ichikawa, H. Polymer-Derived Ceramic Fibers. Annu. Rev. Mater. Res. 2016, 46, 335–356. [Google Scholar] [CrossRef]
  31. Viard, A.; Fonblanc, D.; Lopez-Ferber, D.; Schmidt, M.; Lale, A.; Durif, C.; Balestrat, M.; Rossignol, F.; Weinmann, M.; Riedel, R.; et al. Polymer Derived Si-B-C-N Ceramics: 30 Years of Research. Adv. Eng. Mater. 2018, 20, 1800360. [Google Scholar] [CrossRef]
  32. Fu, S.; Zhu, M.; Zhu, Y. Organosilicon polymer-derived ceramics: An overview. J. Adv. Ceram. 2019, 8, 457–478. [Google Scholar] [CrossRef] [Green Version]
  33. Shah, S.R.; Raj, R. Mechanical properties of a fully dense polymer derived ceramic made by a novel pressure casting process. Acta Mater. 2002, 50, 4093–4103. [Google Scholar] [CrossRef]
  34. Cross, T.; Raj, R.; Prasad, S.V.; Buchheit, T.; Tallant, D.R. Mechanical and Tribological Behavior of Polymer-Derived Ceramics Constituted from SiCxOyNz. J. Am. Ceram. Soc. 2006, 89, 3706–3714. [Google Scholar] [CrossRef]
  35. Barroso, G.; Li, Q.; Bordia, R.K.; Motz, G. Polymeric and ceramic silicon-based coatings—A review. J. Mater. Chem. A 2019, 7, 1936–1963. [Google Scholar] [CrossRef]
  36. Sujith, R.; Jothi, S.; Zimmermann, A.; Aldinger, F.; Kumar, R. Mechanical behaviour of polymer derived ceramics—A review. Int. Mater. Rev. 2020, 1–24. [Google Scholar] [CrossRef]
  37. Ricohermoso, E.; Rosenburg, F.; Klug, F.; Nicoloso, N.; Schlaak, H.F.; Riedel, R.; Ionescu, E. Piezoresistive carbon-containing ceramic nanocomposites—A review. Open Ceram. 2021, 5, 100057. [Google Scholar] [CrossRef]
  38. Bhandavat, R.; Pei, Z.; Singh, G. Polymer-derived ceramics as anode material for rechargeable Li-ion batteries: A review. Nanomater. Energy 2012, 1, 324–337. [Google Scholar] [CrossRef] [Green Version]
  39. Vakifahmetoglu, C.; Zeydanli, D.; Colombo, P. Porous polymer derived ceramics. Mater. Sci. Eng. R Rep. 2016, 106, 1–30. [Google Scholar] [CrossRef]
  40. Barrios, E.; Zhai, L. A review of the evolution of the nanostructure of SiCN and SiOC polymer derived ceramics and the impact on mechanical properties. Mol. Syst. Des. Eng. 2020, 5, 1606–1641. [Google Scholar] [CrossRef]
  41. Campbell, F.C. Structural Composite Materials; ASM international: Cleveland, OH, USA, 2010. [Google Scholar]
  42. Ji, X.; Wang, S.; Shao, C.; Wang, H. High-Temperature Corrosion Behavior of SiBCN Fibers for Aerospace Applications. ACS Appl. Mater. Interfaces 2018, 10, 19712–19720. [Google Scholar] [CrossRef]
  43. Liu, Y.; Chen, K.; Dong, F.; Peng, S.; Cui, Y.; Zhang, C.; Han, K.; Yu, M.; Zhang, H. Effects of hydrolysis of precursor on the structures and properties of polymer-derived SiBN ceramic fibers. Ceram. Int. 2018, 44, 10199–10203. [Google Scholar] [CrossRef]
  44. Takeda, M.; Kagawa, Y.; Mitsuno, S.; Imai, Y.; Ichikawa, H. Strength of a Hi-Nicalon™/Silicon-Carbide-Matrix Composite Fabricated by the Multiple Polymer Infiltration-Pyrolysis Process. J. Am. Ceram. Soc. 2004, 82, 1579–1581. [Google Scholar] [CrossRef]
  45. Naslain, R.R. SiC-Matrix Composites: Nonbrittle Ceramics for Thermo-Structural Application. Int. J. Appl. Ceram. Technol. 2005, 2, 75–84. [Google Scholar] [CrossRef]
  46. Schmidt, S.; Beyer, S.; Knabe, H.; Immich, H.; Meistring, R.; Gessler, A. Advanced ceramic matrix composite materials for current and future propulsion technology applications. Acta Astronaut. 2004, 55, 409–420. [Google Scholar] [CrossRef]
  47. Yang, X.; Hu, H.-F.; Zhang, Y.; Chen, Z.-H. Thermal shock properties of 3D-C/SiC composites prepared via polymer infiltration pyrolysis (PIP). Ceram. Int. 2014, 40, 9087–9094. [Google Scholar] [CrossRef]
  48. Mainzer, B.; Lin, C.; Jemmali, R.; Frieß, M.; Riedel, R.; Koch, D. Characterization and application of a novel low viscosity polysilazane for the manufacture of C- and SiC-fiber reinforced SiCN ceramic matrix composites by PIP process. J. Eur. Ceram. Soc. 2019, 39, 212–221. [Google Scholar] [CrossRef]
  49. Fabrication of Ceramic Matrix Composites by Polymer Infiltration and Pyrolysis (PIP). Available online: https://www.substech.com/dokuwiki/doku.php?id=fabrication_of_ceramic_matrix_composites_by_polymer_infiltration_and_pyrolysis_pip (accessed on 2 June 2012).
  50. Lee, S.H.; Weinmann, M.; Aldinger, F. Processing and properties of C/Si–B–C–N fiber–reinforced ceramic matrix composites prepared by precursor impregnation and pyrolysis. Acta Mater. 2008, 56, 1529–1538. [Google Scholar] [CrossRef]
  51. Ryu, H.-Y.; Wang, Q.; Raj, R. Ultrahigh-Temperature Semiconductors Made from Polymer-Derived Ceramics. J. Am. Ceram. Soc. 2010, 93, 1668–1676. [Google Scholar] [CrossRef]
  52. Terauds, K.; Sanchez-Jimenez, P.; Raj, R.; Vakifahmetoglu, C.; Colombo, P. Giant piezoresistivity of polymer-derived ceramics at high temperatures. J. Eur. Ceram. Soc. 2010, 30, 2203–2207. [Google Scholar] [CrossRef]
  53. Seo, D.; Jung, S.; Lombardo, S.J.; Feng, Z.; Chen, J.; Zhang, Y. Fabrication and electrical properties of polymer-derived ceramic (PDC) thin films for high-temperature heat flux sensors. Sens. Actuators A Phys. 2011, 165, 250–255. [Google Scholar] [CrossRef]
  54. Grossenbacher, J.; Gullo, M.R.; Bakumov, V.; Blugan, G.; Kuebler, J.; Brugger, J. On the micrometre precise mould filling of liquid polymer derived ceramic precursor for 300-µm-thick high aspect ratio ceramic MEMS. Ceram. Int. 2015, 41, 623–629. [Google Scholar] [CrossRef]
  55. Mehregany, M.; Zorman, C.A.; Rajan, N.; Wu, C.H. Silicon carbide MEMS for harsh environments. Proc. IEEE. 1998, 86, 1594–1609. [Google Scholar] [CrossRef]
  56. Mehregany, M.; Zorman, C.A. SiC MEMS: Opportunities and challenges for applications in harsh environments. Thin Solid Films 1999, 355, 518–524. [Google Scholar] [CrossRef]
  57. An, L.; Zhang, W.; Bright, V.M.; Dunn, M.L.; Raj, R. Development of injectable polymer-derived ceramics for high temperature MEMS. In Proceedings of the IEEE Thirteenth Annual International Conference on Micro Electro Mechanical Systems (Cat. No.00CH36308), Miyazaki, Japan, 23–27 January 2000; pp. 619–623. [Google Scholar] [CrossRef]
  58. Liew, L.-A.; Zhang, W.; Bright, V.M.; An, L.; Dunn, M.L.; Raj, R. Fabrication of SiCN ceramic MEMS using injectable polymer-precursor technique. Sens. Actuators A Phys. 2001, 89, 64–70. [Google Scholar] [CrossRef]
  59. Alvi, S.; Akhtar, F. High temperature tribology of polymer derived ceramic composite coatings. Sci. Rep. 2018, 8, 15105. [Google Scholar] [CrossRef] [Green Version]
  60. Klausmann, A.; Morita, K.; Johanns, K.E.; Fasel, C.; Durst, K.; Mera, G.; Riedel, R.; Ionescu, E. Synthesis and high-temperature evolution of polysilylcarbodiimide-derived SiCN ceramic coatings. J. Eur. Ceram. Soc. 2015, 35, 3771–3780. [Google Scholar] [CrossRef]
  61. Nagaiah, N.R.; Kapat, J.S.; An, L.; Chow, L. Novel polymer derived ceramic-high temperature heat flux sensor for gas turbine environment. In Proceedings of the Journal of Physics: Conference Series; IOP Publishing: Bristol, UK, 2006; Volume 34, pp. 458–463. [Google Scholar]
  62. Li, N.; Cao, Y.; Zhao, R.; Xu, Y.; An, L. Polymer-derived SiAlOC ceramic pressure sensor with potential for high-temperature application. Sens. Actuators A Phys. 2017, 263, 174–178. [Google Scholar] [CrossRef]
  63. Zhao, R.; Shao, G.; Cao, Y.; An, L.; Xu, C. Temperature sensor made of polymer-derived ceramics for high-temperature applications. Sens. Actuators A Phys. 2014, 219, 58–64. [Google Scholar] [CrossRef] [Green Version]
  64. Yu, Y.; Huang, Q.; Rhodes, S.; Fang, J.; An, L. SiCNO-GO composites with the negative temperature coefficient of resistance for high-temperature sensor applications. J. Am. Ceram. Soc. 2017, 100, 592–601. [Google Scholar] [CrossRef]
  65. Hou, Y.; Xiao, B.; Sun, Z.; Yang, W.; Wu, S.; Qi, S.; Wen, G.; Huang, X. High temperature anti-oxidative and tunable wave absorbing SiC/Fe3Si/CNTs composite ceramic derived from a novel polysilyacetylene. Ceram. Int. 2019, 45, 16369–16379. [Google Scholar] [CrossRef]
  66. Flores, O.; Schmalz, T.; Krenkel, W.; Heymann, L.; Motz, G. Selective cross-linking of oligosilazanes to tailored meltable polysilazanes for the processing of ceramic SiCN fibres. J. Mater. Chem. A 2013, 1, 15406. [Google Scholar] [CrossRef]
  67. Zhang, C.; Liu, Y.; Cui, Y.; Chen, K.; Peng, S.; Zhang, H.; Han, K.; Yu, M. Comparison of effects of nitrogen sources on the structures and properties of SiBNC ceramic fiber precursors. Ceram. Int. 2018, 44, 14878–14883. [Google Scholar] [CrossRef]
  68. Wu, N.; Wan, Y.; Wang, Y.; Ko, F. Conversion of hydrophilic SiOC nanofibrous membrane to robust hydrophobic materials by introducing palladium. Appl. Surf. Sci. 2017, 425, 750–757. [Google Scholar] [CrossRef]
  69. Su, D.; Wang, L.; Liang, K.; Zhang, F.; Lin, D.; Hu, Y.; Ji, H.; Li, X.; Chen, S.; Yan, X. Silicon oxycarbide/titanium dioxide fibers with wrinkle-like surface by electrospinning. Mater. Lett. 2016, 172, 202–206. [Google Scholar] [CrossRef]
  70. Xu, Y.; Su, D.; Feng, H.; Yan, X.; Liu, N.; Sun, Y. Continuous sol–gel derived SiOC/HfO2 fibers with high strength. RSC Adv. 2015, 5, 35026–35032. [Google Scholar] [CrossRef]
  71. Pillai, S.K.T.; Kretschmer, W.P.; Denner, C.; Motz, G.; Hund, M.; Fery, A.; Trebbin, M.; Förster, S.; Kempe, R. SiCN Nanofibers with a Diameter Below 100 nm Synthesized via Concerted Block Copolymer Formation, Microphase Separation, and Crosslinking. Small 2012, 9, 984–989. [Google Scholar] [CrossRef]
  72. Yan, C.; Liu, R.; Cao, Y.; Zhang, C.; Zhang, D. Ablation behavior and mechanism of C/ZrC, C/ZrC–SiC and C/SiC composites fabricated by polymer infiltration and pyrolysis process. Corros. Sci. 2014, 86, 131–141. [Google Scholar] [CrossRef]
  73. Laadoua, H.; Pradeilles, N.; Lucas, R.; Foucaud, S.; Clegg, W.J. Preparation of ZrC/SiC composites by using polymer-derived ceramics and spark plasma sintering. J. Eur. Ceram. Soc. 2020, 40, 1811–1819. [Google Scholar] [CrossRef]
  74. Wang, Y.; Tian, H.; Quan, D.; Guo, L.; Ouyang, J.; Zhou, Y.; Jia, D. Preparation, characterization and infrared emissivity properties of polymer derived coating formed on 304 steel. Surf. Coatings Technol. 2012, 206, 3772–3776. [Google Scholar] [CrossRef]
  75. Liu, J.; Zhang, L.; Hu, F.; Yang, J.; Cheng, L.; Wang, Y. Polymer-derived yttrium silicate coatings on 2D C/SiC composites. J. Eur. Ceram. Soc. 2013, 33, 433–439. [Google Scholar] [CrossRef]
  76. Jia, Y.; Ajayi, T.D.; Roberts, M.A., Jr.; Chung, C.-C.; Xu, C. Ultrahigh-Temperature Ceramic–Polymer-Derived SiOC Ceramic Composites for High-Performance Electromagnetic Interference Shielding. ACS Appl. Mater. Interfaces 2020, 12, 46254–46266. [Google Scholar] [CrossRef] [PubMed]
  77. Biesuz, M.; Zera, E.; Tomasi, M.; Jana, P.; Ersen, O.; Baaziz, W.; Lindemann, A.; Sorarù, G.D. Polymer-derived Si3N4 nanofelts for flexible, high temperature, lightweight and easy-manufacturable super-thermal insulators. Appl. Mater. Today 2020, 20, 100648. [Google Scholar] [CrossRef]
  78. Luan, X.; Chang, S.; Riedel, R.; Cheng, L. An air stable high temperature adhesive from modified SiBCN precursor synthesized via polymer-derived-ceramic route. Ceram. Int. 2018, 44, 8476–8483. [Google Scholar] [CrossRef]
  79. Wang, X.; Shi, J.; Wang, H. Preparation, properties, and structural evolution of a novel polyborosilazane adhesive, temperature-resistant to 1600 °C for joining SiC ceramics. J. Alloys Compd. 2019, 772, 912–919. [Google Scholar] [CrossRef]
  80. Luan, X.; Chang, S.; Riedel, R.; Cheng, L. The improvement in thermal and mechanical properties of TiB2 modified adhesive through the polymer-derived-ceramic route. Ceram. Int. 2018, 44, 19505–19511. [Google Scholar] [CrossRef]
  81. Luan, X.; Chang, S.; Yu, R.; Zou, Y.; Riedel, R.; Cheng, L. Effect of PSO and TiB2 content on the high temperature adhesion strength of SiBCNO ceramic. Ceram. Int. 2019, 45, 9515–9521. [Google Scholar] [CrossRef]
  82. Wang, X.; Wang, J.; Wang, H. Performance and structural evolution of high-temperature organic adhesive for joining Al2O3 ceramics. Int. J. Adhes. Adhes. 2013, 45, 1–6. [Google Scholar] [CrossRef]
  83. Wang, X.; Wang, J.; Wang, H. Synthesis of a novel preceramic polymer (V-PMS) and its performance in heat-resistant organic adhesives for joining SiC ceramic. J. Eur. Ceram. Soc. 2012, 32, 3415–3422. [Google Scholar] [CrossRef]
  84. Jeong, D.-H.; Septiadi, A.; Fitriani, P.; Yoon, D.-H. Joining of SiC f/SiC using polycarbosilane and polysilazane preceramic mixtures. Ceram. Int. 2018, 44, 10443–10450. [Google Scholar] [CrossRef]
  85. Zhao, C.-C.; Lin, R.-L.; Dai, M.-M.; Xu, X.; Zhu, L.-L.; Xue, J.-X.; Zhai, J.-H.; Ma, H.-B.; Guo, W.-M.; Lin, H.-T.; et al. Facile joining of SiC ceramics with screen-printed polycarbosilane without pressure. J. Eur. Ceram. Soc. 2021, 41, 2157–2161. [Google Scholar] [CrossRef]
  86. Chen, Y.; Cao, Y.; Wang, Y. Electrical property of joints made of polymer-derived SiAlCN ceramic via adhesive joining. Ceram. Int. 2021, 47, 3649–3656. [Google Scholar] [CrossRef]
  87. Liew, L.; Zhang, W.; An, L.; Shah, S.; Luo, R.; Liu, Y.; Cross, T.; Dunn, M.L.; Bright, V.; Daily, J.W. Ceramic MEMS. Am. Ceram. Soc. Bull. 2001, 80, 25. [Google Scholar]
  88. Kong, J.; Maute, K.; Frangopol, D.; Liew, L.-A.; Saravanan, R.; Raj, R. A real time human–machine interface for an ultrahigh temperature MEMS sensor–igniter. Sens. Actuators A Phys. 2003, 105, 23–30. [Google Scholar] [CrossRef]
  89. Yu, Y.; Liu, Y. A large-pressure-range, large-sensing-distance wireless passive pressure sensor based on polymer infiltration pyrolysis-enhanced polymer-derived ceramic films. Meas. Sci. Technol. 2020, 31, 075103. [Google Scholar] [CrossRef]
  90. Shao, G.; Jiang, J.; Jiang, M.; Su, J.; Liu, W.; Wang, H.; Xu, H.; Lit, H.; Zhang, R. Polymer-derived SiBCN ceramic pressure sensor with excellent sensing performance. J. Adv. Ceram. 2020, 9, 374–379. [Google Scholar] [CrossRef]
  91. Hu, L.-H.; Raj, R. Semiconductive Behavior of Polymer-Derived SiCN Ceramics for Hydrogen Sensing. J. Am. Ceram. Soc. 2015, 98, 1052–1055. [Google Scholar] [CrossRef]
  92. Luo, C.; Jiao, T.; Tang, Y.; Kong, J. Excellent Electromagnetic Wave Absorption of Iron-Containing SiBCN Ceramics at 1158 K High-Temperature. Adv. Eng. Mater. 2018, 20, 1701168. [Google Scholar] [CrossRef]
Materials 14 00614 g001 550
Figure 1. High-temperature-polymer-derived ceramics (PDCs) for different applications (left). Publication topics on the keywords “polymer derived ceramics” and “high temperature + polymer derived ceramics” (right). Data obtained from 1990 to September 2020 on from ISI web of science.
Figure 1. High-temperature-polymer-derived ceramics (PDCs) for different applications (left). Publication topics on the keywords “polymer derived ceramics” and “high temperature + polymer derived ceramics” (right). Data obtained from 1990 to September 2020 on from ISI web of science.
Materials 14 00614 g001
Materials 14 00614 g002 550
Figure 2. Schematics of polymer-derived ceramic processing route. The shaping of the preceramic polymer occurs at the crosslinking stage by thermal crosslinking. Organic to inorganic transition is completed at the thermal pyrolysis stage at elevated temperatures around 1000 °C.
Figure 2. Schematics of polymer-derived ceramic processing route. The shaping of the preceramic polymer occurs at the crosslinking stage by thermal crosslinking. Organic to inorganic transition is completed at the thermal pyrolysis stage at elevated temperatures around 1000 °C.
Materials 14 00614 g002
Materials 14 00614 g003 550
Figure 3. Schematics of phase separation and thermal decomposition of Si-based PDCs at elevated temperatures.
Figure 3. Schematics of phase separation and thermal decomposition of Si-based PDCs at elevated temperatures.
Materials 14 00614 g003
Materials 14 00614 g004 550
Figure 4. (a) Schematics of SiBCN fiber microstructures (a3) with a detailed illustration of the formation of two additional surface layers after annealing in (a1) air and (a2) imitated combustion environment. (b,d–f) Transmission electron microscopy (TEM) images of fiber cross-section showing different layers. (c) EDS data obtained from the marked area in (b). Reproduced with permission [42]. Copyright 2018, American Chemical Society.
Figure 4. (a) Schematics of SiBCN fiber microstructures (a3) with a detailed illustration of the formation of two additional surface layers after annealing in (a1) air and (a2) imitated combustion environment. (b,d–f) Transmission electron microscopy (TEM) images of fiber cross-section showing different layers. (c) EDS data obtained from the marked area in (b). Reproduced with permission [42]. Copyright 2018, American Chemical Society.
Materials 14 00614 g004
Materials 14 00614 g005 550
Figure 5. (a) Schematics of fiber hydrolysis and pyrolysis reaction. Scanning electron microscopy (SEM) images of pyrolyzed ceramic fibers from (b) preserved green fibers in an inert environment and (c) exposed green fibers to a humid atmosphere. TEM images of pyrolyzed ceramic fibers from (d) preserved green fibers and (e) exposed green fibers. Reproduced with permission [43]. Copyright 2018, Elsevier.
Figure 5. (a) Schematics of fiber hydrolysis and pyrolysis reaction. Scanning electron microscopy (SEM) images of pyrolyzed ceramic fibers from (b) preserved green fibers in an inert environment and (c) exposed green fibers to a humid atmosphere. TEM images of pyrolyzed ceramic fibers from (d) preserved green fibers and (e) exposed green fibers. Reproduced with permission [43]. Copyright 2018, Elsevier.
Materials 14 00614 g005
Materials 14 00614 g006 550
Figure 6. (a) Schematics of the polymer impregnation and pyrolysis (PIP) process [48]. SEM images of cross-sectional view of SiC/SiC composite after PIP cycle of (b) 3, (c) 8 and (d) 14. Plots of (e) total porosity vs. the number of PIP cycles, and (f) nominal bending stress vs. total porosity. Reproduced with permission [44]. Copyright 2004, John Wiley and Sons.
Figure 6. (a) Schematics of the polymer impregnation and pyrolysis (PIP) process [48]. SEM images of cross-sectional view of SiC/SiC composite after PIP cycle of (b) 3, (c) 8 and (d) 14. Plots of (e) total porosity vs. the number of PIP cycles, and (f) nominal bending stress vs. total porosity. Reproduced with permission [44]. Copyright 2004, John Wiley and Sons.
Materials 14 00614 g006
Materials 14 00614 g007 550
Figure 7. (a) Plot of relative density vs. number of impregnation cycles. (b) TGA curves of bulk and powdered SiBCN, Cf/SiBCN composite and calculated Cf/SiBCN. SEM images of (c) as-prepared crack-free interface, (d) crack propagated interface [50]. Copyright 2008, Elsevier.
Figure 7. (a) Plot of relative density vs. number of impregnation cycles. (b) TGA curves of bulk and powdered SiBCN, Cf/SiBCN composite and calculated Cf/SiBCN. SEM images of (c) as-prepared crack-free interface, (d) crack propagated interface [50]. Copyright 2008, Elsevier.
Materials 14 00614 g007
Materials 14 00614 g008 550
Figure 8. Schematics of shaping process of precursor for microelectromechanical systems (MEMSs), (a) mold filling, and (b) crosslinking and pyrolysis of samples. Optical microscopy of (c) mold filling process, (d) precursor drop on the mold surface. SEM images of (e) crosslinked sample and (f) pyrolyzed sample. Reproduced with permission [54]. Copyright 2008, Elsevier.
Figure 8. Schematics of shaping process of precursor for microelectromechanical systems (MEMSs), (a) mold filling, and (b) crosslinking and pyrolysis of samples. Optical microscopy of (c) mold filling process, (d) precursor drop on the mold surface. SEM images of (e) crosslinked sample and (f) pyrolyzed sample. Reproduced with permission [54]. Copyright 2008, Elsevier.
Materials 14 00614 g008
Materials 14 00614 g009 550
Figure 9. Optical images of SiCN MEMS sensor at (a) off state and (b) on state. (c) Schematics of the design of SiCN glow plug. (d) SEM image of SiCN plug. (e) Design and packed device image of the sensor part. Reproduced with permission [58]. Copyright 2003, Elsevier.
Figure 9. Optical images of SiCN MEMS sensor at (a) off state and (b) on state. (c) Schematics of the design of SiCN glow plug. (d) SEM image of SiCN plug. (e) Design and packed device image of the sensor part. Reproduced with permission [58]. Copyright 2003, Elsevier.
Materials 14 00614 g009
Materials 14 00614 g010 550
Figure 10. (a) Schematics of coating synthesis setup. (b) XRD of SiBCN PDC at different annealing temperatures, suggesting conversion of amorphous to crystalline at 1850 °C. (c) SEM images of the cross-section of SiBCN membrane on an alumina substrate. (d) TGA of SiBCN at 1400 °C for 50 h in the air [10].
Figure 10. (a) Schematics of coating synthesis setup. (b) XRD of SiBCN PDC at different annealing temperatures, suggesting conversion of amorphous to crystalline at 1850 °C. (c) SEM images of the cross-section of SiBCN membrane on an alumina substrate. (d) TGA of SiBCN at 1400 °C for 50 h in the air [10].
Materials 14 00614 g010
Materials 14 00614 g011 550
Figure 11. TEM images of (a) as-prepared SiCN multilayer coating on Si substrate pyrolyzed at 1100 °C and (b) SiCN multilayer coating on SiC substrate annealed at 1400 °C. (c) XRD of SiCN as-prepared and annealed samples, both showed amorphous structures. High-res TEM images of (d) as-prepared sample on Si substrate and (e) annealed sample on SiC substrate. Reproduced with permission [60]. Copyright 2015, Elsevier.
Figure 11. TEM images of (a) as-prepared SiCN multilayer coating on Si substrate pyrolyzed at 1100 °C and (b) SiCN multilayer coating on SiC substrate annealed at 1400 °C. (c) XRD of SiCN as-prepared and annealed samples, both showed amorphous structures. High-res TEM images of (d) as-prepared sample on Si substrate and (e) annealed sample on SiC substrate. Reproduced with permission [60]. Copyright 2015, Elsevier.
Materials 14 00614 g011
Materials 14 00614 g012 550
Figure 12. SEM images of (a) neat pyrolyzed SiOC ceramic coating with obvious cracks, (b) pyrolyzed SiOC-ZrO2 coating and (c) pyrolyzed SiOC-Ag coating at 700 °C. XRD spectra of (d) pyrolyzed SiOC-ZrO2 sample and (e) pyrolyzed SiOC-Ag sample, where both showed phase oxidation of incorporated particles into ZrO2 and Ag2O. (f) SEM image of wear track of SiOC-ZrO2 sample with a sliding distance of 18 m at a load of 3 N. Reproduced with permissions [59]. Copyright 2018, Springer Nature.
Figure 12. SEM images of (a) neat pyrolyzed SiOC ceramic coating with obvious cracks, (b) pyrolyzed SiOC-ZrO2 coating and (c) pyrolyzed SiOC-Ag coating at 700 °C. XRD spectra of (d) pyrolyzed SiOC-ZrO2 sample and (e) pyrolyzed SiOC-Ag sample, where both showed phase oxidation of incorporated particles into ZrO2 and Ag2O. (f) SEM image of wear track of SiOC-ZrO2 sample with a sliding distance of 18 m at a load of 3 N. Reproduced with permissions [59]. Copyright 2018, Springer Nature.
Materials 14 00614 g012
Materials 14 00614 g013 550
Figure 13. (a) Semiconducting behavior of SiAlCN indicated by the changing electric conductivity at different temperatures. Schematics of the design of heat-flux sensor of PDC materials, (b) sectional view and (c) top view. Reproduced with permission [61]. Copyright 2006, IOP Publishing.
Figure 13. (a) Semiconducting behavior of SiAlCN indicated by the changing electric conductivity at different temperatures. Schematics of the design of heat-flux sensor of PDC materials, (b) sectional view and (c) top view. Reproduced with permission [61]. Copyright 2006, IOP Publishing.
Materials 14 00614 g013
Materials 14 00614 g014 550
Figure 14. (a) Optical images of SiAlCN sensor attached to alumina rod via Pt wires and thermocouple for comparison. (b) SEM images of a cross-section of sensor head showing the interface between SiAlCN ceramic phase and Pt wire. (c) Schematics of temperature measurement testing setup. (d) The output voltage of the temperature sensor as a function of temperature. (e) The response of the temperature sensor to the changes of environmental temperature, and the comparison to thermal couple measurement. Reproduced with permission [63]. Copyright 2014, Elsevier.
Figure 14. (a) Optical images of SiAlCN sensor attached to alumina rod via Pt wires and thermocouple for comparison. (b) SEM images of a cross-section of sensor head showing the interface between SiAlCN ceramic phase and Pt wire. (c) Schematics of temperature measurement testing setup. (d) The output voltage of the temperature sensor as a function of temperature. (e) The response of the temperature sensor to the changes of environmental temperature, and the comparison to thermal couple measurement. Reproduced with permission [63]. Copyright 2014, Elsevier.
Materials 14 00614 g014
Materials 14 00614 g015 550
Figure 15. (a) Image of SiCNO-GO sensor. (b) SEM images of SiCNO-GO (1 wt.% GO) sensor with a magnified image (inset). (c) The voltage output of the sensor at the temperature range from 25 to 600 °C. (d) The resistance of probe material vs. temperature. Reproduced with permission [64]. Copyright 2016, John Wiley and Sons.
Figure 15. (a) Image of SiCNO-GO sensor. (b) SEM images of SiCNO-GO (1 wt.% GO) sensor with a magnified image (inset). (c) The voltage output of the sensor at the temperature range from 25 to 600 °C. (d) The resistance of probe material vs. temperature. Reproduced with permission [64]. Copyright 2016, John Wiley and Sons.
Materials 14 00614 g015
Table
Table 1. Applications, precursors, properties and thermal stabilities of high-temperature PDCs.
Table 1. Applications, precursors, properties and thermal stabilities of high-temperature PDCs.
ApplicationPDCFillerPrecursorRemarkable PropertiesThermal Stability (°C)Reference
FiberSiCN-PolysilazaneD = 100 μm1400[66]
SiBCN-PolyborosilazaneσT = 1.03 GPa1600 (Tp)[67]
SiBN-PolyborosilazaneσT = 0.91 GPa1400 (Tp)[43]
SiBCN-PolyborosilazaneD = 12 μm1400[42]
SiOCPbPolycarbosilaneWCA = 135°700[68]
SiOCTiO2Polyhydromethyl-siloxaneWCA = 130°1300[69]
SiOCHfO2Tetraethoxysilane + dimethyldiethoxyl-silaneσT = 1.5 GPa1000 (Tp)[70]
SiOCHfO2Tetraethoxysilane + dimethyldiethoxyl-silaneσT = 930 MPa
E = 155 GPa		1500[23]
SiBOC-PolyborosiloxaneD = 1 μm800[11]
SiCN-PolysilazaneD < 100 nm1100 (Tp)[71]
MatrixSiC-PolycarbosilaneσB = 600 MPa 1027 (Tp)[44]
SiCZrCPolycarbosilaneρ = 2.13 g/cm3
porosity = 15%		1700[72]
SiCZrCPolycarbosilanePorosity = 0.9%1950[73]
SiBCN-Oligovinylsilazane + tris(methyldihydridosilylethylene)boraneσB = 225 MPa1500[50]
SiOCZrO2Polymethylsilsesquioxaneρ = 2.3–3.5 g/cm31400[4]
Coating/MembraneSiO2AlPolyhydridomethylsiloxaneIE = 0.2 in 8–14 μm800[74]
SiOCY2O3PolysiloxaneCTE = 4.43–7.26 × 10−61400[75]
SiCN-PolysilylcarbodiimideE = 105–117 GPa
Hardness = 10–11 GPa		1400[60]
SiOCZrB2PolycarbosilaneSET = 72 dB at Ka1000[76]
SiOC-PolysiloxaneConductivity = 11 mW m−1 K−11000[77]
SiBCN-Polysilazane + borane dimethylsulfideCeramic yield = 65%1800[10]
AdhesiveSiBCNNano Al2O3Polyborosilazane + polysiloxaneBond strength = 6.65 MPa1000[78]
SiBCNborazinePolymethylsilaneBond strength = 7.9 MPa1600[79]
SiCNTiB2PolysilazaneBond strength = 8.0 MPa800[80]
SiBCNOTiB2Polysilazane + polysiloxaneBond strength = 12.3 MPa1000[81]
SiOCB4C, glass powderPolymethylsilane + polysiloxaneBond strength = 66.9 MPa1000[82]
SiOC-Polymethylsilane + PolysiloxaneBond strength = 50.8 MPa1200[83]
SiC-PolycarbosilaneBond strength = 120 MPa1750[84]
SiC-PolycarbosilaneBond strength = 105.8 MPa1500[85]
SiOC-PolycarbosilaneBond strength = 66.9
MPaR = 1.15–5.6 kΩ		850[86]
MEMS/SemiconductorSiCN-PolysilazaneE = 158 GPa1500[87]
SiCN--E = 80–225 GPa1650[88]
SiCN-PolysilazaneFS = 326 um/s-[54]
SiCNO-PolysilazaneBG = 2.2 eV1300[51]
SensorSiAlOC-Aluminum tri-sec-butoxideE = 150 GPa
GF = 16,000		1000[62]
SiAlCN--EC = 0–100/Ω/cm1400[61]
SiCNO-PolymethylsilsesquioxaneGF = 600–17001500[52]
SiCN-PolysilazaneR = 60 kΩ1400[53]
SiCN-PolysilazaneSensitivity = 290 kHz kPa−1800[89]
SiBCN-PolyborosilazaneGF = 55001000[90]
SiAlCN-Polysilzane + aluminum-tri-sec-butoxidec1 = −3235
c2 = −3.6		830[63]
SiCN-PolysilazaneBG = 0.08 eV1000[91]
SiCNOGOPolyvinylsilazaneEC = 1.39 × 10−7 600[64]
Wave absorbSiBCN-PolyborosilazaneRL = −12.62 dB at 3.2 GHz1400[92]
SiCFe3Si, CNTsPolysilylacetylene + ferric acetylacetonateRL = −40 dB at 10.36 GHz800[65]
TP: pyrolysis temperature; WCA: water contact angle; IE: infrared emissivity; CTE: coefficient of thermal expansion; COF: coefficient of friction; SET: electromagnetic interference shielding efficiency; FS: filling speed; BG: bandgap.GF: gauge factor; EC: electrical conductivity; RL: reflection loss.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Ren, Z.; Mujib, S.B.; Singh, G. High-Temperature Properties and Applications of Si-Based Polymer-Derived Ceramics: A Review. Materials 2021, 14, 614. https://doi.org/10.3390/ma14030614

AMA Style

Ren Z, Mujib SB, Singh G. High-Temperature Properties and Applications of Si-Based Polymer-Derived Ceramics: A Review. Materials. 2021; 14(3):614. https://doi.org/10.3390/ma14030614

Chicago/Turabian Style

Ren, Zhongkan, Shakir Bin Mujib, and Gurpreet Singh. 2021. "High-Temperature Properties and Applications of Si-Based Polymer-Derived Ceramics: A Review" Materials 14, no. 3: 614. https://doi.org/10.3390/ma14030614

APA Style

Ren, Z., Mujib, S. B., & Singh, G. (2021). High-Temperature Properties and Applications of Si-Based Polymer-Derived Ceramics: A Review. Materials, 14(3), 614. https://doi.org/10.3390/ma14030614

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.