Next Article in Journal
Newly-Obtained Two Organic-Inorganic Hybrid Compounds Based on Potassium Peroxidomolybdate and Dicarboxypyridinic Acid: Structure Determination, Catalytic Properties, and Cytotoxic Effects of Eight Peroxidomolybdates in Colon and Hepatic Cancer Cells
Previous Article in Journal
Bandstructure and Size-Scaling Effects in the Performance of Monolayer Black Phosphorus Nanodevices
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 15
Issue 1
10.3390/ma15010244
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effects of Different Air Particle Abrasion Protocols on the Biaxial Flexural Strength and Fractography of High/Ultra-Translucent Zirconia

by
Reem AlMutairi
*,
Hend AlNahedh
,
Ahmed Maawadh
and
Ahmed Elhejazi
Department of Restorative Dental Sciences, College of Dentistry, King Saud University, P.O. Box 93504, Riyadh 11683, Saudi Arabia
*
Author to whom correspondence should be addressed.
Materials 2022, 15(1), 244; https://doi.org/10.3390/ma15010244
Submission received: 23 November 2021 / Revised: 22 December 2021 / Accepted: 28 December 2021 / Published: 29 December 2021
(This article belongs to the Section Advanced and Functional Ceramics and Glasses)
Browse Figures
Versions Notes

Abstract

:
In this study, the biaxial flexural strength (BFS) and fractography of high/ultra-translucent monolithic zirconia ceramics subjected to different mechanical surface pretreatments were evaluated. A total of 108 disc-shaped samples (12 mm diameter, 1.2 mm thickness) of three zirconia materials (5Y-ZP KATANA Zirconia UTML (ML), 3Y-TZP DD Bio ZX2 (DB), and 5Y-ZP DD cube X2 (DC)) were used. The BFS was investigated after subjecting the samples to surface treatment using air abrasion particles of two types (aluminum oxide or glass microbeads). The data were analyzed using two-way analysis of variance, followed by Scheffe’s post hoc test for multiple comparisons. The mean ± standard deviation BFS for DB was highest after treatment with 50 µm Al2O3 (1626.05 ± 31.9 MPa), with lower values being observed following treatment with 50 µm glass microbeads (1399.53 ± 24.2 MPa) and in the control sample (1198.51 ± 21.1 MPa). The mean ± standard deviation (SD) BFSs for DC and ML were the highest in the control groups. Surface air abrasion with 50 µm Al2O3 particles and 2 bar pressure is recommended for 3Y-TZP translucent zirconia, while no abrasion of 5Y-ZP translucent zirconia ceramic.

1. Introduction

All-ceramic-based dental restorations are of particular importance due to their superior biocompatibility and aesthetics compared to porcelain fused to metal restorations [1]. More specifically, 3 mol% yttria-stabilized tetragonal zirconia polycrystalline (3Y-TZP) has become one of the main substitutes for metal ceramic restorations because of its high flexural strength and fracture toughness, in addition to its low enamel and material wear [2]. However, zirconia exhibits a lower translucency and a high opacity compared to lithium disilicate ceramics, thereby resulting in inferior aesthetics [3].
To improve the material translucency and overcome this shortcoming, newer generations of zirconia with higher translucency parameters have been developed. More specifically, first-generation materials consisted of 3Y-TZP and contained 0.25 wt% alumina (Al2O3) [4]. Although the strength and fracture toughness of this generation of materials were higher than those of newer generations, they exhibited a high opacity due to the presence of tetragonal zirconia phases, which resulted in light scattering from the grain boundaries, additive inclusions, and pores [4]. This type of zirconia is therefore recommended for the fabrication of framework materials in fixed partial dentures and porcelain-layered crowns. The second generation of 3Y-TZP materials was characterized by a reduced porosity that was achieved using a higher firing temperature and by reducing the amount of alumina within the material [5,6]. Such improvements resulted in a 3Y-TZP material with a higher translucency, which is otherwise known as highly translucent zirconia. Although the second generation of 3Y-TZP materials showed an improved translucency, their aesthetics were insufficient for use as monolithic ceramic restorations in the anterior aesthetic zone [4].
Subsequently, third generation materials were developed using an yttria content of 5 mol% (5Y-ZP), which is referred to by manufacturers as ultra-translucent (or super-high-translucent) zirconia, while fourth generation materials were based on zirconia with an yttria content of 4 mol% (4Y-ZP), which exhibited enhanced mechanical properties [7]. Both the third and fourth generation materials contained increased amounts of the cubic phase, which imparted the material with its superior translucency [4]. Such materials therefore become suitable for use in the fabrication of anterior crowns and fixed partial dentures [4]. Due to the increased amounts of the cubic phase present in the newer generation materials, stress-induced transformations do not take place, ultimately resulting in a marked decrease in their strength and fracture toughness properties [8,9,10]. Bonding of zirconia to tooth structure presents a clinical problem as zirconia cannot be etched with acids as in glass-based systems. A previous meta-analysis reported that a combination of mechanical and chemical surface pre-treatment processes is essential to obtain durable bonding to zirconia [11].
To alter the internal surface of zirconia and increase both its mechanical retention and its bonding to the resin cement, air abrasion is commonly employed [12] using airborne particles such as aluminum oxide [13]. The air abrasion of 3Y-TZP results in the formation of a compressive layer that acts as a protective surface, and this can be attributed to a transformation toughening from the tetragonal to the monoclinic phase [14]. Moreover, it leads to the formation of surface flaws that limit the strength owing to crack propagation [14]. A further study reported that the use of an air particle abrasion pressure of 0.2 MPa for this process resulted in a more stable and reliable bond strength between the resin cement and three zirconia materials with varying translucency values [15].
However, the effect of air particle abrasion on the flexural strength of 3Y-TZP zirconia is controversial, since it depends on the size of the abrading particles, their type, and the air pressure employed [12]. For example, some studies have reported an increased flexural strength after air particle abrasion, and this could be accounted for by considering that the transformation toughening mechanism counterbalances any potential critical defect introduced by airborne particle abrasion [16,17,18,19,20]. In contrast, other works have reported a decreased strength after air particle abrasion owing to the introduction of large surface flaws [21,22,23].
Currently, limited evidence is available regarding the use of low abrasive particles and low air pressures when treating high-translucent zirconia [24]. Air abrasion on tooth enamel, dentin, and nickel-chromium alloys with glass beads is commonly used [25,26], which results in low bond strength values for nickel–chromium alloys when compared with aluminum oxide treatment [25]. In addition, air abrasion with glass beads has been found to decrease the bonding strengths of materials to enamel and dentin, whereas air abrasion with alumina decreased the adhesion to enamel but not to dentin [26]. Due to the fact that glass beads are softer than alumina particles, they could be considered an alternative surface treatment for high-translucent zirconia [27].
To date, the effects of different air particle abrasion protocols on the flexural strength of highly translucent zirconia have yet to be examined in detail. The aim of this study is therefore to evaluate the biaxial flexural strength (BFS) values and carry out a qualitative fractographic analysis of high-translucent and ultra-translucent monolithic zirconia ceramics subjected to different mechanical surface treatment protocols. Two null hypotheses are tested: (1) the biaxial flexural strengths of high-translucent and ultra-translucent zirconia ceramics are not affected by air abrasion surface treatment with 50 µm aluminum oxide particles, and (2) the BFSs of high-translucent zirconia and ultra-translucent zirconia ceramics are not affected by air abrasion surface treatment with 50 µm glass microbead particles.

2. Materials and Methods

2.1. Preparation of the Samples

Table 1 lists the various materials employed in this study along with their compositions and commercial sources.
A total of 108 zirconia discs (15 mm diameter, 1.5 mm thickness) were prepared from pre-sintered zirconia blocks (KATANA Zirconia UTML, Kuraray Noritake Dental, Tokyo, Japan; DD Bio ZX2, Dental Direkt Materials, Germany; and DD Cube X2, Dental Direkt Materials, Germany) using computer-aided design and computer-aided-manufacture techniques (DWOS, Dental Wings, Montreal, QC, Canada) [28]. The sintering of all samples was performed according to the manufacturer’s recommendations, as outlined in Table 2. Both sides of each sample were polished with 600 and 1200 grit silicon carbide paper under wet conditions for 15 s [15]. The samples were ultrasonically cleaned in distilled water for 10 min and then air-dried prior to surface treatment. The samples were subsequently divided into nine subgroups (n = 12 per group) according to the surface treatment employed (Figure 1). More specifically, the control group underwent no surface treatment; the DB1, DC1, and ML1 subgroups were subjected to air abrasion with 50 µm aluminum oxide particles; and the DB2, DC2, and ML2 groups were subjected to air abrasion with 50 µm glass microbeads.
Each air abrasion procedure was performed under a standardized pressure of 2 bar with a nozzle placed at a 90° incidence angle from the center of the sample. The nozzle was placed at a distance of 10 mm and air abrasion was carried out for 20 s using a sandblaster (Duostar Plus, BEGO, Germany) [15,29,30].

2.2. Biaxial Flexural Strength (BFS)

A total of 108 samples were ultrasonically cleaned with 99% isopropanol for 180 s, air-dried, and subjected to biaxial flexural strength testing according to ISO 6872 [31]. The samples were placed on three steel balls measuring 3.2 mm in diameter, which were in turn placed on a 10 mm diameter support circle with an angle of 120° between the steel balls. A mechanical testing machine (Type 5567, Instron, Canton, MA, USA) was employed to impart a 5 kN load onto the sample with a crosshead speed of 0.5 mm/min until sample fracture occurred. The load was applied using a piston-shaped indenter with a diameter of 1.2 mm, and the load was directed to the center of the sample. The BFS was measured according to ISO 6872 [28,30,31] and was calculated as follows:
S = −0.2387P (X − Y)/d2
X = (1 + v)In(r2/r3)2 + ([1 − v]/2) (r2/r3)2
Y = (1 + v) (1 + In[r1/r3]2) + (1 − v)(r1/r3)2
where S is the BFS (MPa), P is the fracture load (N), d is the disc specimen thickness at the fracture site (mm), v is Poisson’s ratio (0.25), r1 is the radius of the support circle (5 mm), r2 is the radius of the loaded area (0.6 mm), and r3 is the radius of the specimen (6 mm).

2.3. Fractographic Analysis

The fractured surfaces were ultrasonically cleaned for 10 min using distilled water, then air-dried and examined using a digital microscope (DIGITAL MICROSCOPE KH-7700, Hirox, Tokyo, Japan) for determination of the fracture origin in relation to the fractography principles of ceramics [32]. The selected representative fractured samples were evaluated by scanning electron microscopy (JSM-6360LV, JEOL Ltd., Tokyo, Japan) with magnification ranges from 50× to 400×. The samples were coated with a thin coating of gold via ion sputtering (JFC-1100, JEOL Ltd., Tokyo, Japan). The fracture origins were determined on the fracture surface by recognizing specific fracture patterns, tracing back to the fracture origin sites, and examining the progression of fracture. A number of fracture patterns were identified in the descriptive fractographic analysis of fractured zirconia samples, including hackles, twist hackles, arrest lines, compression curls, and void defects [33].

2.4. Statistical Analysis

Data were collected and grouped for statistical analysis using a statistical software package (SPSS version 23). Statistical analysis was performed using the Shapiro–Wilk test of normal distribution (p > 0.05). Two-way analysis of variance (ANOVA) was conducted to evaluate the null hypothesis, followed by Scheffe’s post hoc tests for multiple comparisons (p < 0.05). The level of significance was set at p ≤ 0.05.

3. Results

3.1. Biaxial Flexural Strength (BFS) Testing

Two-way ANOVA showed a statistically significant difference in the BFS between the various surface pre-treatment groups (p < 0.05), and the interaction effect between the ceramic material group and the surface pre-treatment group was also found to be statistically significant (p < 0.05). In addition, one-way ANOVA showed a statistically significant difference between the BFS values of the surface pre-treatment groups for all ceramic materials (p < 0.05) (Table 3).
The mean ± SD BFS for the DD Bio ZX2 (DB) sample reached its highest value after treatment with 50 µm Al2O3, with a lower value being obtained following treatment with 50 µm glass microbeads, and the lowest value being observed for the control. In contrast, the mean ± SD BFSs for the DC and ML samples reached their highest values in the control and became lower after treatment with the 50 µm glass microbeads and the 50 µm Al2O3 particles (Figure 2).
Scheffe’s post hoc test showed that for the DB, DC, and ML materials, statistically significant differences were present in the BFS values between the various sample groups (p < 0.05). More specifically, for the DB samples, the mean ± SD BFS after treatment with 50 µm Al2O3 was significantly higher than the control sample and after treatment with the 50 µm glass microbeads (p < 0.05). In contrast, both the DC and ML samples showed mean ± SD BFS values that were statistically significantly higher in the control group than after treatment with either the 50 µm Al2O3 beads or the 50 µm glass microbeads (p < 0.05) (Table 4).

3.2. Fractographic Analysis

Significant differences in the topography of the abraded ceramic surfaces in comparison with control can be seen (Figure 3). The use of 50 µm Al2O3 particles resulted in the generation of rougher surfaces, while for the groups treated with 50 µm glass microbeads, pitting of the surface was observed in all cases. The various fractured discs obtained following surface treatment of the samples are shown in Figure 4. Compared to the sintered control group, it can be seen that the airborne particle-abraded DB samples shattered into multiple fragments of varying sizes, while fewer fragments were obtained for the airborne particle-abraded DC and ML samples.
SEM examinations revealed numerous characteristic features for the fractured zirconia ceramic surfaces, wherein the fracture origins (*), direction of crack propagation (dotted arrows), secondary cracks, hackles, river delta, arrest lines, and compression curls were clearly evident (Figure 5, Figure 6 and Figure 7). Twist hackles formed when the principal tension axis undergoes a lateral rotation and the crack twists (Figure 5c). As the crack approaches the compression side of the sample, the crack slows down to leave a curved lip (compression curl) just before the total fracture of the material indicating the end of the fracture (Figure 5d, Figure 6c, and Figure 7d). An arrest line can also be observed (black arrow), indicating a change in direction of the crack propagation (Figure 5h). The DB sample tended to exhibit a smoother fractured surface than the other tested zirconia materials, although multiple secondary cracks were also present, which led to the generation of smaller ceramic fragments (Figure 5). For the DC sample, cracks began to appear at areas that exhibited surface and subsurface porosity, wherein the cracks progressed in multiple planes (Figure 6b), and secondary cracks were frequently observed in the fractured specimens (Figure 6). Furthermore, for the ML sample, clear fracture lines and smooth fracture surfaces were observed (Figure 7).

4. Discussion

In the present study, we evaluated the BFSs of three highly translucent monolithic zirconia ceramics after subjecting them to different mechanical surface treatment protocols. Previous studies have demonstrated that sandblasting with aluminum oxide particles at 0.2 MPa improved the BFSs of both conventional and high-translucent 3Y-TZP zirconia ceramics [34,35,36]. In our study, a similar result was observed for the DB high-translucent zirconia ceramic, which showed an increased flexural strength following air abrasion with both aluminum oxide and glass microbeads. However, we found that air abrasion decreased the BFS values for both DC and ML zirconia ceramics. Thus, the null hypothesis was rejected since it was found that the BFS was affected by the use of aluminum oxide or glass microbead air abrasion surface treatments.
The flexural strength of dental ceramics can be determined using 4-point and 3-point bending tests or a BFS test [37]. However, it should be noted that the fabrication of samples for uniaxial flexure testing methods can produce defects or flaws within the edges of samples, which can result in great variations in their resulting strength values when subjected to a load [35]. In contrast, the BFS test is advantageous for preventing premature failures from such flaws or cracks because these defective areas are not subjected directly to the load [38]. Moreover, strength tests using multiaxial loading could mimic the loading during the mastication process and so could be considered beneficial for examining the relevant mechanical properties of brittle dental materials [39]. Thus, the BFS test was employed for the purpose of this study. Previously, BFS tests have been carried out using different types of load configurations, such as ball on three balls, ball-on-ring, ring-on-ring, and piston-on-three-ball biaxial loadings [40,41]. For the piston-on-three-ball test, the load is applied by a piston at the center of the disc-shaped sample, which is supported by three metallic balls [31,37]. Although the piston-on-three-ball test can produce a non-uniform stress distribution under the piston, the strain will be increased to a greater degree than what is expected within the sample [42], and this is the only test that has been selected by the International Organization for Standardization (ISO 6782) for testing the BFS of dental ceramic materials [31]. Therefore, the piston-on-three-ball BFS test was implemented for the purpose of this study.
Air abrasion by alumina particles is known to promote a transformation toughening mechanism within the zirconia, in which the tetragonal to monoclinic phase transformation is accompanied by a volumetric expansion that limits the propagation of the initiated cracks [6,37,43]. This transformation toughening mechanism releases a residual compressive stress on the surface, which results in an increase in the fracture toughness and the BFS of the high-translucent 3Y-TZP material [44,45]. This could explain the high BFS values observed for the DB ceramic when subjected to airborne particle abrasion with either 50 µm aluminum oxide or 50 µm glass microbeads. Similar to our findings, a previous study evaluated the effects of different surface treatments, including surface abrasion with 50 µm alumina particles, and concluded that such treatment methods increased the BFSs of conventional and high-translucent 3Y-TZP zirconia [34,35]. In contrast, reduced BFS values were observed for both 5Y-TZP DC and ML zirconia ceramics when the surfaces were treated with either aluminum oxide or glass microbeads. These results were in agreement with a previous study that reported a negative correlation between the BFS and the translucency of zirconia [37]. It should also be noted here that transformation of the tetragonal phase to the monoclinic phase within zirconia is highly dependent on the yttria content and the ceramic microstructure [46]. Thus, the increased yttria content of the 5Y-TZP ceramics resulted in a lower transformability of the tetragonal phase and hence a reduced release of compressive stresses and a decreased flexural strength [44,46]. In addition, the decreased strength was attributed to the lack of transformation toughening with an increased content of the cubic phase in these high-translucent zirconia ceramics [9]. Furthermore, it was previously reported that the mechanical stress caused by airborne particle abrasion could promote rhombohedral phase transformation in high-translucent zirconia, thereby resulting in lower mechanical properties [47]. A recent study also evaluated the effects of the alumina particle size on the release of residual compressive stresses from conventional and high-translucent 5Y-ZP zirconia ceramics, and as a result, the use of 110 µm aluminum oxide particles was suggested to treat the 3Y-TZP zirconia surface, while a particle size of only 25 µm was suggested for 5Y-ZP zirconia ceramics [48].
Fractography allows for the accurate examination of fractured surfaces that contain microscopic features in which the direction of crack propagation is pointing toward the fracture origin site [49]. The qualitative fractography technique used in this study involves a description of the microscopic surface and the subsurface fracture features that indicate the crack origin site and the direction of crack propagation within each ceramic material. Various characteristic ceramic fracture features, such as hackles, twist hackles, fracture origins, arrest lines, and compression curls, were evident in the tested translucent zirconia fractured discs. When the maximum velocity of the crack is reached during crack propagation, a secondary crack hackle line is formed, and this line runs parallel to the direction of crack propagation and perpendicular to the crack origin site [33]. Twist hackles separate portions of the crack surface in which they rotate from the principal crack plane as a result of twisting in the principal tension axis [33]. Another characteristic feature is an arrest line, in which a well-defined sharp line occurs when the crack changes its direction while propagating, and this could be helpful in indicating the failure origin [50]. When the discs were loaded for flexural testing, a crack was initiated and propagated perpendicular to the tensile surface; this represents the crack origin site. As the crack propagates, it approaches the compression side of the sample and slows down, causing a compression curl to form, which is a common feature in ceramic failure and indicates the end of the fracture [50]. The presence of a compression curl is an important feature, since it indicates that the sample possessed a bending component when loaded [33]. It should be noted here that the fracture origin is usually located on the side opposite to that of the compression curl [33,50].
We found that the DB sample exhibited multiple secondary cracks that likely led to shattering of the ceramic disc into multiple fractured pieces of varying sizes and the loss of smaller fragments of ceramics. For the DB sample, the resulting surface and subsurface porosities promoted crack initiation in these areas, and progress in multiple planes was frequently observed wherein secondary cracks were also present. Furthermore, in the case of the ML sample, a smooth fracture surface with clear fracture lines was generally observed.
Thus, based on the results of this study, the use of 50 µm aluminum oxide particles for air abrasion at 0.2 MPa pressure could be recommended for the surface treatment of high-translucent 3Y-TZP zirconia ceramics. In the case of 5Y-ZP ceramics, the use of 50 µm glass microbeads for surface treatment negatively affected the BFS values, and so a smaller particle size should be considered in further studies.
The limitations of the current study include the fact that we concentrated on the type of air abrasion particles, while all other parameters were maintained constant. A limitation of the methodology used in this research is that the samples were machined, leaving micro-grooves that could affect the transformation at the surface, and this could impact durability and strength of zirconia. Moreover, the effect of aging was not examined. Future studies should therefore investigate additional parameters, such as different air abrasion pressures and particle sizes.

5. Conclusions

Within the limitations of this study, it could be concluded that the air abrasion of a 3 mol% yttria-stabilized tetragonal zirconia polycrystalline (3Y-TZP) translucent zirconia surface with 50 µm Al2O3 particles at a pressure of 2 bar resulted in the highest BFS values. In addition, the BFS of the tested 5Y-ZP ultra-translucent zirconia ceramic was negatively affected when air abrasion was carried out using either 50 µm Al2O3 particles or 50 µm glass microbeads. Smaller particle size should be considered in future research.

Author Contributions

Conceptualization, R.A., H.A., and A.M.; methodology, R.A., H.A., and A.E; software, H.A. and R.A.; validation, R.A. and A.M.; formal analysis, R.A. and A.E.; investigation, R.A., H.A., and A.E.; resources, R.A.; data curation, R.A., H.A., and A.M.; writing—original draft preparation, R.A. and H.A.; writing—review and editing, R.A.; supervision, H.A., A.M., and A.E.; project administration, R.A.; funding acquisition, R.A. All authors have read and agreed to the published version of the manuscript.

Funding

The authors would like to thank the Deanship of Scientific Research at King Saud University, Riyadh, Saudi Arabia, for the funding and support during the completion of this study.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Data sharing is not applicable to this article.

Acknowledgments

This study was registered and approved by the College of Dentistry Research Center (registration number: PR 0098). This manuscript is part of a DScD dissertation.

Conflicts of Interest

There are no known conflicts of interest associated with this study, and there has been no significant financial interest in any company or any products mentioned in this manuscript that could have influenced the outcome.

References

  1. Yoshida, K. Influence of alumina air-abrasion for highly translucent partially stabilized zirconia on flexural strength, surface properties, and bond strength of resin cement. J. Appl. Oral Sci. 2020, 28, e20190371. [Google Scholar] [CrossRef]
  2. Zhang, X.; Liang, W.; Jiang, F.; Wang, Z.; Zhao, J.; Zhou, C.; Wu, J. Effects of air-abrasion pressure on mechanical and bonding properties of translucent zirconia. Clin. Oral Investig. 2020, 25, 1979–1988. [Google Scholar] [CrossRef]
  3. Rinke, S.; Fischer, C. Range of indications for translucent zirconia modifications: Clinical and technical aspects. Quintessence Int. 2013, 44, 557–566. [Google Scholar] [CrossRef]
  4. Zhang, Y.; Lawn, B. Novel Zirconia Materials in Dentistry. J. Dent. Res. 2017, 97, 140–147. [Google Scholar] [CrossRef] [PubMed]
  5. Tong, H.; Tanaka, C.B.; Kaiser, M.R.; Zhang, Y. Characterization of three commercial Y-TZP ceramics produced for their high translucency. Ceram. Int. 2016, 42, 1077–1085. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  6. Kwon, S.J.; Lawson, N.C.; McLaren, E.E.; Nejat, A.H.; Burgess, J.O. Comparison of the mechanical properties of translucent zirconia and lithium disilicate. J. Prosthet. Dent. 2018, 120, 132–137. [Google Scholar] [CrossRef]
  7. Güth, J.F.; Stawarczyk, B.; Edelhoff, D.; Liebermann, A. Zirconia and its novel compositions: What do clinicians need to know? Quintessence Int. 2019, 50, 512–520. [Google Scholar]
  8. Zhang, F.; Inokoshi, M.; Batuk, M.; Hadermann, J.; Naert, I.; van Meerbeek, B.; Vleugels, J. Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations. Dent. Mater. 2016, 32, e327–e337. [Google Scholar] [CrossRef] [PubMed]
  9. Zhang, Y. Making yttria-stabilized tetragonal zirconia translucent. Dent. Mater. 2014, 30, 1195–1203. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  10. Harada, K.; Raigrodski, A.J.; Chung, K.-H.; Flinn, B.D.; Dogan, S.; Mancl, L.A. A comparative evaluation of the translucency of zirconias and lithium disilicate for monolithic restorations. J. Prosthet. Dent. 2016, 116, 257–263. [Google Scholar] [CrossRef]
  11. Inokoshi, M.; de Munck, J.; Minakuchi, S.; van Meerbeek, B. Meta-analysis of Bonding Effectiveness to Zirconia Ceramics. J. Dent. Res. 2014, 93, 329–334. [Google Scholar] [CrossRef]
  12. Mao, L.; Kaizer, M.; Zhao, M.; Guo, B.; Song, Y.; Zhang, Y. Graded Ultra-Translucent Zirconia (5Y-PSZ) for Strength and Functionalities. J. Dent. Res. 2018, 97, 1222–1228. [Google Scholar] [CrossRef]
  13. Nobuaki, A.; Keiichi, Y.; Takashi, S. Effects of air abrasion with alumina or glass beads on surface characteristics of CAD/CAM composite materials and the bond strength of resin cements. J. Appl. Oral Sci. 2015, 23, 629–636. [Google Scholar] [CrossRef]
  14. Zhang, Y.; Lawn, B.R.; Malament, K.A.; van Thompson, P.; Rekow, E.D. Damage accumulation and fatigue life of particle-abraded ceramics. Int. J. Prosthodont. 2007, 19, 442–448. [Google Scholar]
  15. San, S.; Phyo, M.; Takagaki, T.; Kham, S. Effects of alumina-blasting pressure on the bonding to super/ultra-translucent zirconia. Dent. Mater. 2019, 35, 730–739. [Google Scholar]
  16. Inokoshi, M.; Shimizu, H.; Nozaki, K.; Takagaki, T.; Yoshihara, K.; Nagaoka, N.; Zhang, F.; Vleugels, J.; van Meerbeek, B.; Minakuchi, S. Crystallographic and morphological analysis of sandblasted highly translucent dental zirconia. Dent. Mater. 2018, 34, 508–518. [Google Scholar] [CrossRef]
  17. Passos, S.P.; Linke, B.; Major, P.W.; Nychka, J.A. The effect of air-abrasion and heat treatment on the fracture behavior of Y-TZP. Dent. Mater. 2015, 31, 1011–1021. [Google Scholar] [CrossRef]
  18. Amaral, M.; Valandro, L.F.; Bottino, M.A.; Souza, R.O.A. Low-temperature degradation of a Y-TZP ceramic after surface treatments. J. Biomed. Mater. Res. Part B Appl. Biomater. 2013, 101, 1387–1392. [Google Scholar] [CrossRef]
  19. Papanagiotou, H.P.; Morgano, S.M.; Giordano, R.A.; Pober, R. In vitro evaluation of low-temperature aging effects and finishing procedures on the flexural strength and structural stability of Y-TZP dental ceramics. J. Prosthet. Dent. 2006, 96, 154–164. [Google Scholar] [CrossRef]
  20. Guazzato, M.; Quach, L.; Albakry, M.; Swain, M. Influence of surface and heat treatments on the flexural strength of Y-TZP dental ceramic. J. Dent. 2005, 33, 9–18. [Google Scholar] [CrossRef] [PubMed]
  21. Zhang, Y.; Lawn, B.R.; Rekow, E.D.; Thompson, V.P. Effect of sandblasting on the long-term performance of dental ceramics. J. Biomed. Mater. Res. 2004, 71B, 381–386. [Google Scholar] [CrossRef]
  22. Guazzato, M.; Albakry, M.; Quach, L.; Swain, M.V. Influence of surface and heat treatments on the flexural strength of a glass-infiltrated alumina/zirconia-reinforced dental ceramic. Dent. Mater. 2005, 21, 454–463. [Google Scholar] [CrossRef]
  23. Uo, M.; Sjögren, G.; Sundh, A.; Goto, M.; Watari, F.; Bergman, M. Effect of Surface Condition of Dental Zirconia Ceramic (Denzir) on Bonding. Dent. Mater. J. 2006, 25, 626–631. [Google Scholar] [CrossRef] [Green Version]
  24. McLaren, E.A.; Lawson, N.; Choi, J.; Kang, J.; Trujillo, C. New High-Translucent Cubic-Phase-Containing Zirconia: Clinical and Laboratory Considerations and the Effect of Air Abrasion on Strength. Compend. Contin. Educ. Dent. 2017, 38, e13–e16. [Google Scholar] [PubMed]
  25. Coelho, C.M.P.; Rubo, J.H.; Pegoraro, L.F. Tensile bond strength of a resinous cement to a nickel-chromium alloy modified with five surface treatments. J. Prosthet. Dent. 1996, 76, 246–249. [Google Scholar] [CrossRef]
  26. Nikaido, T.; Kataumi, M.; Burrow, M.F.; Inokoshi, S.; Yamada, T.; Takatsu, T. Bond strengths of resin to enamel and dentin treated with low-pressure air abrasion. Oper. Dent. 1996, 21, 218–224. [Google Scholar] [PubMed]
  27. Martins, A.R.M.; Gotti, V.B.; Shimano, M.; Borges, G.; Gonçalves, L.D.S. Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment. Braz. Oral Res. 2015, 29, 54. [Google Scholar] [CrossRef] [PubMed]
  28. Sen, N.; Us, Y.O. Mechanical and optical properties of monolithic CAD-CAM restorative materials. J. Prosthet. Dent. 2018, 119, 593–599. [Google Scholar] [CrossRef]
  29. Okutan, Y.; Yucel, M.T.; Gezer, T.; Donmez, M.B. Effect of airborne particle abrasion and sintering order on the surface roughness and shear bond strength between Y-TZP ceramic and resin cement. Dent. Mater. J. 2019, 38, 241–249. [Google Scholar] [CrossRef] [Green Version]
  30. Martins, S.B.; Trindade, F.Z.; Góes, M.S.; Adabo, G.L.; Dovigo, L.N.; Fonseca, R.G. Does airborne-particle abrasion before, rather than after, zirconia sintering lead to higher mechanical strength even under aging challenge? J. Prosthet. Dent. 2020, 123, 155–162. [Google Scholar] [CrossRef] [Green Version]
  31. International Organization for Standardization. ISO 6872: Dentistry-Ceramic Materials; ISO: Geneva, Switzerland, 2008. [Google Scholar]
  32. Quinn, G.D. Fractography of Ceramics and Glasses (Special Publication 960-16); NIST—National Institute of Standards and Technology: Gaithersburg, MD, USA, 2007; Chapter 5; pp. 1–78. [Google Scholar]
  33. Quinn, G.D. A NIST Recommended Practice Guide: Fractography of Ceramics and Glasses; Special Publication960-16e2; National Institute of Standardsand Technology: Washington, DC, USA, 2016. Available online: http://nvlpubs.nist.gov/nistpubs/specialpublications/NIST.SP.960-16e2.pdf (accessed on 22 December 2021).
  34. Moqbel, N.M.; Al-Akhali, M.; Wille, S.; Kern, M. Influence of Aging on Biaxial Flexural Strength and Hardness of Translucent 3Y-TZP. Materials 2019, 13, 27. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  35. Souza, R.O.A.; Valandro, L.F.; Melo, R.M.; Machado, J.P.B.; Bottino, M.A.; Özcan, M. Air-particle abrasion on zirconia ceramic using different protocols: Effects on biaxial flexural strength after cyclic loading, phase transformation and surface topography. J. Mechan. Behav. Biomed. Mater. 2013, 26, 155–163. [Google Scholar] [CrossRef] [PubMed]
  36. Okada, M.; Taketa, H.; Torii, Y.; Irie, M.; Matsumoto, T. Optimal sandblasting conditions for conventional-type yttria-stabilized tetragonal zirconia polycrystals. Dent. Mater. 2018, 35, 169–175. [Google Scholar] [CrossRef]
  37. Reyes, A.R.; Dennison, J.B.; Powers, J.M.; Sierraalta, M.; Yaman, P. Translucency and flexural strength of translucent zirconia ceramics. J. Prosthet. Dent. 2021, in press. [Google Scholar]
  38. Börger, A.; Supancic, P.; Danzer, R. The ball on three balls test for strength testing of brittle discs: Stress distribution in the disc. J. Eur. Ceram. Soc. 2002, 22, 1425–1436. [Google Scholar] [CrossRef]
  39. Ban, S.; Anusavice, K. Influence of Test Method on Failure Stress of Brittle Dental Materials. J. Dent. Res. 1990, 69, 1791–1799. [Google Scholar] [CrossRef]
  40. Zeng, K.; Odén, A.; Rowcliffe, D. Flexure tests on dental ceramics. Int. J. Prosthodont. 1996, 9, 434–439. [Google Scholar]
  41. Morrell, R. Biaxial flexural strength testing of ceramic materials. In A National Measurement Good Practice Guide; No. 12; NPL: Teddigton, UK, 2007. [Google Scholar]
  42. Choi, B.-J.; Yoon, S.; Im, Y.-W.; Lee, J.-H.; Jung, H.-J.; Lee, H.-H. Uniaxial/biaxial flexure strengths and elastic properties of resin-composite block materials for CAD/CAM. Dent. Mater. 2018, 35, 389–401. [Google Scholar] [CrossRef]
  43. Kelly, J.R.; Denry, I. Stabilized zirconia as a structural ceramic: An overview. Dent. Mater. 2008, 24, 289–298. [Google Scholar] [CrossRef]
  44. Inokoshi, M.; Shimizubata, M.; Nozaki, K.; Takagaki, T.; Yoshihara, K.; Minakuchi, S.; Vleugels, J.; van Meerbeek, B.; Zhang, F. Impact of sandblasting on the flexural strength of highly translucent zirconia. J. Mech. Behav. Biomed. Mater. 2020, 115, 104268. [Google Scholar] [CrossRef]
  45. Hjerppe, J.; Närhi, T.O.; Vallittu, P.K.; Lassila, L.V. Surface roughness and the flexural and bend strength of zirconia after different surface treatments. J. Prosthet. Dent. 2016, 116, 577–583. [Google Scholar] [CrossRef] [PubMed]
  46. Zhang, F.; van Meerbeek, B.; Vleugels, J. Importance of tetragonal phase in high-translucent partially stabilized zirconia for dental restorations. Dent. Mater. 2020, 36, 491–500. [Google Scholar] [CrossRef]
  47. Maruo, Y.; Yoshihara, K.; Irie, M.; Nishigawa, G.; Nagaoka, N.; Matsumoto, T.; Minagi, S. Flexural properties, bond ability, and crystallographic phase of highly translucent multi-layered zirconia. J. Appl. Biomater. Funct. Mater. 2020, 18, 2–5. [Google Scholar] [CrossRef]
  48. Kim, H.-K.; Ahn, B. Effect of Al2O3 Sandblasting Particle Size on the Surface Topography and Residual Compressive Stresses of Three Different Dental Zirconia Grades. Materials 2021, 14, 610. [Google Scholar] [CrossRef] [PubMed]
  49. Scherrer, S.S.; Lohbauer, U.; Della Bona, A.; Vichi, A.; Tholey, M.J.; Kelly, J.R.; van Noort, R.; Cesar, P.F. ADM guidance—Ceramics: Guidance to the use of fractography in failure analysis of brittle materials. Dent. Mater. 2017, 33, 599–620. [Google Scholar] [CrossRef]
  50. Scherrer, S.S.; Quinn, J.B.; Quinn, G.D.; Kelly, J.R. Failure analysis of ceramic clinical cases using qualitative fractography. Int. J. Prosthodont. 2006, 19, 185–192. [Google Scholar] [PubMed]
Materials 15 00244 g001 550
Figure 1. Schematic representation of the different ceramic material groups to be subjected to surface pre-treatment with different types of air abrasion particles. These specimens were then employed in the biaxial flexural strength test. * DB: DD Bio ZX2 ceramic material, DC: DD Cube X2 ceramic material, ML: KATANA UTML ceramic material, BFS: biaxial flexural strength.
Figure 1. Schematic representation of the different ceramic material groups to be subjected to surface pre-treatment with different types of air abrasion particles. These specimens were then employed in the biaxial flexural strength test. * DB: DD Bio ZX2 ceramic material, DC: DD Cube X2 ceramic material, ML: KATANA UTML ceramic material, BFS: biaxial flexural strength.
Materials 15 00244 g001
Materials 15 00244 g002 550
Figure 2. Mean biaxial flexural strengths (MPa) of the various experimental groups.
Figure 2. Mean biaxial flexural strengths (MPa) of the various experimental groups.
Materials 15 00244 g002
Materials 15 00244 g003 550
Figure 3. Representative SEM images showing the effects of abrasion using 50 µm aluminum oxide particles and 50 µm glass microbeads on the surfaces of different zirconia ceramics.
Figure 3. Representative SEM images showing the effects of abrasion using 50 µm aluminum oxide particles and 50 µm glass microbeads on the surfaces of different zirconia ceramics.
Materials 15 00244 g003
Materials 15 00244 g004 550
Figure 4. Representative fractured discs for the different zirconia groups.
Figure 4. Representative fractured discs for the different zirconia groups.
Materials 15 00244 g004
Materials 15 00244 g005 550
Figure 5. Representative SEM images of the ceramic DB fractured discs. (a–c) The control as sintered group, (d–f) the 50 µm Al2O3-treated group, and (g–i) the 50 µm glass microbead-treated group.
Figure 5. Representative SEM images of the ceramic DB fractured discs. (a–c) The control as sintered group, (d–f) the 50 µm Al2O3-treated group, and (g–i) the 50 µm glass microbead-treated group.
Materials 15 00244 g005
Materials 15 00244 g006 550
Figure 6. Representative SEM images of the ceramic DC fractured discs. (a–c) The 50 µm Al2O3-treated group, and (d–f) the 50 µm glass microbead-treated group.
Figure 6. Representative SEM images of the ceramic DC fractured discs. (a–c) The 50 µm Al2O3-treated group, and (d–f) the 50 µm glass microbead-treated group.
Materials 15 00244 g006
Materials 15 00244 g007 550
Figure 7. Representative SEM images of the ceramic ML fractured discs. (a–c) The 50 µm Al2O3-treated group, and (d–f) the 50 µm glass microbead-treated group.
Figure 7. Representative SEM images of the ceramic ML fractured discs. (a–c) The 50 µm Al2O3-treated group, and (d–f) the 50 µm glass microbead-treated group.
Materials 15 00244 g007
Table
Table 1. Materials employed during this study.
Table 1. Materials employed during this study.
MaterialBrand NameShadeCompositionManufacturer
High-translucent 3Y-TZP ceramicDD Bio ZX2White≥99% ZrO2 + HfO2 + Y2O3,
<6% Y2O3, ≤0.15% Al2O3, <1.0% other oxides.		Dental Direkt Materials, Germany
Superhigh-translucent
5Y-TZP ceramic		DD Cube X2White≥99% ZrO2 + HfO2 + Y2O3, <10% Y2O3, ≤0.01% Al2O3, <1.0% other oxides.Dental Direkt Materials, Germany
Ultra-translucent
5Y-ZP ceramic		KATANA zirconia UTMLWhite87–92% ZrO2, 8–11% Y2O3, <2% other oxides.Kuraray Noritake Dental, Tokyo, Japan
50 µm glass microbead particlesRolloblast Glass microbeadsRenfert, Germany
50 µm aluminum oxide particlesCobra Aluminum oxideRenfert, Germany
Table
Table 2. Sintering conditions for preparation of the different zirconia materials.
Table 2. Sintering conditions for preparation of the different zirconia materials.
Material (Brand Name)Sintering TemperatureHolding Time
DD Bio ZX21450 °C9 h
DD Cube X21450 °C9 h
KATANA zirconia UTML1550 °C2 h
Table
Table 3. Mean (and SD) biaxial flexural strengths (MPa) of the various experimental groups.
Table 3. Mean (and SD) biaxial flexural strengths (MPa) of the various experimental groups.
MeanStandard DeviationStandard Error95% Confidence Interval for MeanMinMaxp Value
Lower BoundUpper Bound
DD Bio ZX2 (DB)Control1198.52 c21.206.121185.051211.981162.091225.260.000 *
50 µm Al2O31626.06 a31.949.221605.761646.351588.831676.23
50 µm glass microbeads1399.53 b24.257.001384.121414.941346.511439.88
DD Cube X2 (DC)Control856.73 a26.897.76839.64873.82800.96923.320.000 *
50 µm Al2O3490.40 c6.962.01485.98494.83477.24501.06
50 µm glass microbeads712.64 b19.385.59700.32724.95687.15740.27
KATANA UTML (ML)Control761.91 a19.445.61749.55774.26728.21789.290.000 *
50 µm Al2O3437.92 c29.578.54419.12456.71396.21487.36
50 µm glass microbeads711.76 b10.393.00705.16718.36694.05730.08
* Statistically significant at p ≤ 0.05. * Different small letters indicate significant differences at p ≤ 0.05.
Table
Table 4. Scheffe’s post hoc test for the BFS (MPa).
Table 4. Scheffe’s post hoc test for the BFS (MPa).
DD Bio ZX2 (DB)DD Cube X2 (DC)KATANA UTML (ML)
Mean Differencep ValueMean Differencep ValueMean Differencep Value
50 µm Al2O350 µm glass microbeads226.5240 *0.000−222.2337 *0.000−273.8480 *0.000
Control427.5403 *0.000−366.3253 *0.000−323.9907 *0.000
50 µm glass microbeadsControl201.0163 *0.000−144.0916 *0.000−50.1427 *0.000
* Statistically significant at p ≤ 0.05.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

AlMutairi, R.; AlNahedh, H.; Maawadh, A.; Elhejazi, A. Effects of Different Air Particle Abrasion Protocols on the Biaxial Flexural Strength and Fractography of High/Ultra-Translucent Zirconia. Materials 2022, 15, 244. https://doi.org/10.3390/ma15010244

AMA Style

AlMutairi R, AlNahedh H, Maawadh A, Elhejazi A. Effects of Different Air Particle Abrasion Protocols on the Biaxial Flexural Strength and Fractography of High/Ultra-Translucent Zirconia. Materials. 2022; 15(1):244. https://doi.org/10.3390/ma15010244

Chicago/Turabian Style

AlMutairi, Reem, Hend AlNahedh, Ahmed Maawadh, and Ahmed Elhejazi. 2022. "Effects of Different Air Particle Abrasion Protocols on the Biaxial Flexural Strength and Fractography of High/Ultra-Translucent Zirconia" Materials 15, no. 1: 244. https://doi.org/10.3390/ma15010244

APA Style

AlMutairi, R., AlNahedh, H., Maawadh, A., & Elhejazi, A. (2022). Effects of Different Air Particle Abrasion Protocols on the Biaxial Flexural Strength and Fractography of High/Ultra-Translucent Zirconia. Materials, 15(1), 244. https://doi.org/10.3390/ma15010244

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.