Next Article in Journal
Foam Glass Granule Usage in Tile Glue Mixtures That Use a Reduced Portland Cement Amount
Next Article in Special Issue
Sub-ps Pulsed Laser Deposition of Boron Films for Neutron Detector Applications
Previous Article in Journal
Thermal Diffusivity of Concrete Samples Assessment Using a Solar Simulator
Previous Article in Special Issue
A Novel Red-Emitting Na2NbOF5:Mn4+ Phosphor with Ultrahigh Color Purity for Warm White Lighting and Wide-Gamut Backlight Displays
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 16
Issue 3
10.3390/ma16031267
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Sub-ps Laser Deposited Copper Films for Application in RF Guns

by
Antonella Lorusso
1,*,
Zsolt Kovács
2,
Barnabás Gilicze
3,
Sándor Szatmári
3,
Alessio Perrone
1 and
Tamás Szörényi
4
1
Department of Mathematics and Physics “E. De Giorgi”, University of Salento and National Institute of Nuclear Physics, 73100 Lecce, Italy
2
Department of High Energy Experimental Particle and Heavy Ion Physics, Wigner Research Centre for Physics, H-1121 Budapest, Hungary
3
Institute of Physics, University of Szeged, H-6720 Szeged, Hungary
4
Department of Optics and Quantum Electronics, University of Szeged, H-6720 Szeged, Hungary
*
Author to whom correspondence should be addressed.
Materials 2023, 16(3), 1267; https://doi.org/10.3390/ma16031267
Submission received: 4 January 2023 / Revised: 24 January 2023 / Accepted: 30 January 2023 / Published: 2 February 2023
(This article belongs to the Special Issue Materials Light Life)
Browse Figures
Review Reports Versions Notes

Abstract

:
Copper thin films are intended to serve as a cover layer of photocathodes that are deposited by ablating copper targets in a high vacuum by temporally clean 600 fs laser pulses at 248 nm. The extremely forward-peaked plume produced by the ultrashort UV pulses of high-energy contrast ensures fast film growth. The deposition rate, defined as peak thickness per number of pulses, rises from 0.03 to 0.11 nm/pulse with an increasing ablated area while keeping the pulse energy constant. The material distribution over the surface-to-be-coated can also effectively be controlled by tuning the dimensions of the ablated area: surface patterning from airbrush-like to broad strokes is available. The well-adhering films of uniform surface morphology consist of densely packed lentil-like particles of several hundred nm in diameter and several ten nm in height. Task-optimized ultrashort UV laser deposition is thereby an effective approach for the production of thin film patterns of predetermined geometry, serving e.g., as critical parts of photocathodes.

1. Introduction

Being the most robust against degradation for its chemical inertness and resistance to high electric breakdown due to its high surface fields, copper-based photocathodes are preferred in S-band radio-frequency guns [1,2,3,4]. Since the quantum efficiency of the order of 10−5 at 266 nm laser driven-photoemission of copper, QECu [5,6] is relatively low compared to those of other metallic photocathodes, e.g., QEY = 3 × 10−4 and QEMg = 7.6 × 10−4 [7], several solutions were proposed to increase the photoemissive properties of the photocathodes. Wang et al. inserted a Mg disc into the copper base by friction welding [8], while Qian and collaborators did the same by press fitting [9]. These structures suffered from RF breakdown at the Mg–Cu interface [10]. Deposition of a high QE material onto the Cu back plate of the RF gun cavity was another approach [11,12,13]. Among the deposition techniques applied, pulsed laser deposition (PLD), proved to be rather promising since it provided uniform and adherent films, even at room temperature [14,15,16,17,18]. However, fast thinning of the high QE film during frequent laser cleaning, mandatory for removing the surface contaminations to preserve the photoemission performance [19,20], set hard lifetime limits to the photocathodes of this type. To avoid these shortcomings, Lorusso et al. [21] proposed a new photocathode configuration coined “non-conventional”, in which a disc of durable Y or Mg was covered by a copper layer with a central 5 mm diameter emitting area left open. In this structure, the source of photoemission is a robust, long lasting bulk piece of high photoemission efficiency material, while the copper cover layer ensures electrical compatibility with the RF gun made of Cu.
In this paper, results of a feasibility study intended for assessing the potential of sub-ps PLD at 248 nm in producing the copper cover layer of the reversed photocathode structure [21] are reported. Highly efficient localized deposition of well sticking particulate-free films of micrometer thickness is realized by exploiting the unique characteristics of the laser used, with particular regard to the role of the laser spot size on the target surface in controlling the material distribution over the surface to be covered.
In PLD, the habitual control parameter is the energy density. Both probe- and film-based techniques proved that in ns PLD, the plasma broadened with decreasing energy density at fixed spot size. Otherwise, when keeping the energy density constant, the polar distributions became more sharply forward-peaked as the spot size increased. Out of the two parameters, the spot size appeared to be more effective in controlling the distribution [22].
When ablating with ultrashort lasers, the scenario became a bit more complex: while the angular width of the deposits increased with increasing fluence, the ion flux narrowed [23,24,25,26]. To make the picture even more complicated, the angular divergence of the atomic species within the plume was larger than that of the nanoparticles [27]. The effect of changing spot size remained the same: keeping the energy of the ablating pulses constant, the plume geometry deviated from spherical to cylindrical symmetry with increasing spot size [28], leading to narrowing in the angular distribution of the resulting film with a concomitant increase in film thickness [29,30].
Though relevant experiments are relatively scarce, those available e.g., [28,29,30] suggest that in PLD, the size of the ablating laser spot on the target surface controls effectively (yet not independently) both the growth rate and the lateral distribution of the film material. In this report we reveal how the potential of this effect can be exploited for production of thin film patterns of predetermined geometries.

2. Materials and Methods

A critical parameter of the ultrashort laser system is the temporal contrast defined as the main pulse–background intensity ratio. In materials processing applications where the pulse energy, rather than the intensity, is the principal parameter, the ratio of the energy of the main fs pulse to the energy of the background, i.e., the energy contrast, is critical. A peculiarity of the Szatmári-type laser system used in this series of experiments is that it has been optimized for high energy contrast by amplifying the frequency converted from 248 nm pulses in a twin-tube amplifier module with a 2-pass amplification geometry in each tube. Thereby producing pulses of 20 mJ maximum energy with an energy contrast, Efs/EASE of 19 [31]. The 600 fs pulse duration was measured by autocorrelation technique using a two-photon ionization based non-linear detector. A 500 mm f/10 Suprasil lens focused the beam at an angle of 45° onto a 99.99% pure copper target of 1” diameter producing an elliptical spot of fairly homogeneous energy distribution on the target surface. The laser impact area was varied by translating the focusing lens along the optical axis while keeping the focal point inside the target. Though using UV grade optical components, the energy loss accounting for the steering optics, focusing lens, the entrance window, and the protective quartz plate behind the window resulted in Etotal = 4.4 ± 0.2 mJ at the target surface, meaning thereby Efs = 4.18 ± 0.19 mJ and EASE = 0.22 ± 0.01 mJ. All results reported refer to these fixed pulse energies while changing the geometry of the elliptical spot.
Depositions were performed in a UHV chamber with a base pressure of 10−4 Pa at room temperature (Figure 1a). Preliminary experiments revealed that several thousand pulses were necessary and enough to grow films with thicknesses of hundreds of nanometers, thus the number of shots was fixed to 10,000. The normal operational condition of the hybrid dye-excimer laser system used was to produce single pulses with repetition rates up to 10 Hz. In the experiments it was running at 2 Hz. The Si substrates placed parallel to and in front of the target at a distance of 30 mm were covered with copper meshes of 1.00 ± 0.02 mm aperture and 0.25 ± 0.01 mm wire diameter (Figure 1b). Deposition through these masks resulted in an array of columns of ~1.0 × 1.0 mm2 cross-sectional areas providing more than 900 height values per sample for the accurate determination of the thickness distribution. The topography of the pattern was measured by a Veeco Dektak-8 stylus profilometer (Bruker Corporation, MA, USA). The surface morphology of the films was characterized by scanning electron microscopy, model JEOL JSM-6480 LV (JEOL Ltd., Tokyo, Japan), and atomic force microscopy, model PSIA XE-100 (Park Systems, Suwon, Republic of Korea) in tapping mode.

3. Results

As exemplified in Figure 1, the expanding plasma was extremely forward directed for all focusing conditions, a consequence of the cleanliness of the ablating laser pulse. This jet-like character of the plasma plume was responsible for the striking growth rates and lateral distributions to be reported.
Films were grown at five positions of the focusing lens along the optical axis, resulting in five pairs of spot sizes in the plane of the target surface, since, due to the differences in the directional properties the sub-ps and ns components of the ablating pulse produced different impact areas. The larger areas, referring to the ASE part, extended from 0.30 to 3.30 mm2 as measured on highly sensitive UV photopaper. The area ratios were in good agreement with those derived from intensity contrast measurements based on far-field focus diagnostics, underpinning the reliability of the results. Spot areas ranging from 0.085 to 1.01 mm2 were derived for the fs component from the analysis of SEM images taken on the processed Cu target surface, as exemplified in Figure 2, again in perfect agreement with the calculated ones.
The deposition rate is routinely quantified as the ratio of maximum thickness to the number of pulses e.g., [29,30]. The dependence of the maximum film thickness on the impact area produced by the sub-ps component of the processing pulse is shown in Figure 3. While the tendency is in line with the expectations [28,29,30], the extent of the effect is intriguing: the thickness steeply rises with increasing area from 0.085 up to 0.34 mm2, even with diminishing fluence, followed by an apparent leveling, ending up with 1130 ± 50 nm at 1.01 mm2, thus yielding an impressive growth rate of 0.113 nm/pulse here.
The maximum thickness without the lateral distribution of the film material provides not only an incomplete description, but could even be misleading when assessing the effectiveness of film growth. The matrix of columns defined by the mask covered a fairly large area ranging up to ±30° in both directions, constituting a solid base for the derivation of the thickness distributions. As exemplified in Figure 4, for the smallest and largest spot sizes, the changes in the lateral distributions of the film material are equally impressive. Indeed, the increase in maximum thickness with increasing spot area is associated with a striking narrowing in distribution. The results show, within a 10% respect to the maximum thickness value, a lateral angular distribution of around 8° and 25° for 1.01 mm2 and 0.085 mm2, respectively. The effect is again in line with the observations [28,29,30] and theoretical predictions [22], however, the concentration of the material deposited from the extremely forward-peaked plasma in such close vicinity to the center of symmetry is unique.
Low magnification SEM micrographs revealed that the films consisted of particles of several hundred nanometer diameters distributed homogeneously throughout the whole area (Figure 5). The lateral dimensions of the overwhelming majority of the building blocks constituting the films were no larger than 4–500 nm in diameter.
Dektak records parallel to the major and minor axes of the deposits yielded not only hundreds of height figures, but also a tremendous amount of data on the axial and lateral dimensions of the constituting particles without notable differences either in their size or in the lateral distributions as a function of spot size. AFM images of surface areas exemplified in Figure 6 confirmed the results derived from the SEM analysis and Dektak data: the films were composed of lentil shaped particles of several tens of nanometer in height and approximately one order of magnitude larger in diameter.
Showing typical landscapes after ablation of a material of high thermal diffusivity with sub-ps pulses [32], close-ups of the processed surface exemplified in Figure 7 revealed the origin of the particles: traces of rapid solidification following melting with sharp burrs and small droplets either remained riding on the ridges or redeposited as frozen monuments of the violent ejection of molten material are shown. The overwhelming majority of the droplets are within the 100–500 nm diameter range. In the 0.5–1 µm diameter domain, the number of the globules steeply decreases with increasing diameter and with very few species above one micrometer. This morphology is consistent with rapid expulsion of liquid and vapor droplets which then cooled quickly and resolidified onto the substrate with partial redeposition, giving a clue about the morphology of the films presented in the preceding paragraph.

4. Discussion

The camera snapshots (Figure 1) clearly documented the extremely forward directed appearance of the plume. It is worth noting that while results had rather different thickness distributions depending on the actual spot size, the visual appearance of the plume remained apparently unchanged. Though observation of such a high plume length/width ratio is exceptional indeed, for initial plasma thicknesses of tens of nanometers with millimeter lateral dimensions, the theoretical considerations admit even higher ratios [33].
To reveal what is behind this behavior, let’s first assess the contributions of the fs vs. ns components of the processing pulse to the process. Since the energies of the ASE and the main pulse and the respective spot sizes on the target surface are different, the effects of two fluence (and intensity) series should be examined. Table 1 displays the process parameter window of the experiments in terms of fluence and intensity, calculated separately for the 600 fs main pulse of 4.18 ± 0.19 mJ energy and the ASE background conveying 0.22 ± 0.01 mJ energy in 15 ns. Since the main pulse lies in the middle of the background, the ASE contribution to the ablation was calculated with 0.11 mJ and 7.5 ns.
The ns ablation thresholds of copper range from 0.3 J/cm2 [34] through 0.5 J/cm2 [35] and 2.0–2.5 J/cm2 [36] up to 5–6 J/cm2 [35,37,38]. In the context of this study the most relevant figure is 3.4 ± 0.5 J/cm2 reported for KrF excimer laser processing [39,40]. Since, in our case, the highest ASE fluence value of 0.037 J/cm2 calculated for 0.30 mm2 spot size was two orders of magnitude lower than the most relevant figure [39,40] and even the absolute lowest one of 0.3 J/cm2 reported [34] is one order of magnitude higher, it is safe to say that in our experiments the ns component did not ablate. The intensity figures in Table 1 further strengthen this statement: since below a prepulse level of 107 W/cm2, the amplified spontaneous emission of the amplifier did not cause measurable preplasma formation or photo-evaporation of the target material [41], the 4.9 × 106 maximum ASE intensity was definitely not enough for producing plasma components. In conclusion: due to the high-energy contrast ratio, a unicity of the laser system used, in our case the ns pedestal did not contribute to the ablation and had no impact on the fs part either, consequently all effects obtained should be assigned exclusively to the sub-ps main pulse.
For pulses shorter than ~1 ps, the melting depth proved to be independent of pulse duration for copper [42]. Therefore, the excellent agreement in the ablation thresholds reported at Fth = 0.50 ± 0.05 J/cm2 [42,43,44,45,46] is reasonable. Nevertheless, material removal at extremely low rates, slowly increasing with fluence was shown to be possible even below 0.5 J/cm2 [47,48,49], while 0.35 and 0.15 J/cm2 were derived as thresholds in 500 fs@248 nm PLD [40,50].
In the light of these figures, it is apparent that all fluence values derived for the main pulse (Table 1) were above threshold. Lying in the high-fluence regime, 4.92 J/cm2 should have produced high ablation/deposition rate, while approaching the threshold, 0.41 J/cm2 should have been much less effective. The intriguing effect is that the rise in the spot areas from 0.085 to 1.01 mm2 not only compensated for the concomitant decrease in fluence, but even resulted in a continuous rise in maximum film thickness. Certainly, the concentration of the material in close vicinity of the center of symmetry as a result of the narrowing angular distribution of the ejecta also contributed to the evolution of the maximum thickness with increasing spot size. Nevertheless, despite the fact that the decreasing removal rate, due to the vanishing fluence with increasing spot area, the total amount of material deposited also proved to be apparently higher for 1.01 mm2 (Figure 4.) This revealed that the size of the ablating laser spot on the target surface more effectively controlled both the growth rate and the lateral distribution of the film material than the fluence. From a practical viewpoint: the control of the material distribution by tuning the spot area allows for optimalization of the deposition process for the actual application by writing patterns through moving the plume on the surface to be covered like an airbrush using large spot sizes or painting with broad strokes produced by small spots.
In order to judge the efficiency of our approach, the growth rates derived were compared to those reported in [40], actually one of the first studies performed using a 500 fs@248 nm laser. In this study, focusing the beam onto a 0.05 mm2 spot resulted in growth rates between 2 × 10−3 and 3 × 10−3 nm/pulse within the 0.4–6.0 J/cm2 fluence domain. Since at the same fluence, the amount of material ablated scales with the spot area [34] the figures given in [40] have been recalculated for the spot areas referring to the main pulse in Table 1. The growth rates obtained this way and those calculated from Figure 3 are compared in Figure 8.
The similarity of the two plots reveals that the spot size dependence is real and characteristic of the lasers of this class. The 3–4 times higher growth rates of magnitude 0.1 nm/pulse reported in our case are impressive even in comparison with the literature’s data [40,49,51]. What makes a difference is that the early version of the laser system [40] definitely possessed lower energy contrast due to the single-pass on-axis amplification scheme. The high growth rates produced by ablating with clean pulses highlight the decisive role of the energy contrast in determining the efficiency of the process.
In the process parameter domain covered in this study, the ablated material is predominately decomposed as nanoparticles, with atoms and ions as minor components e.g., [24,52]. As evidenced by SEM/AFM mapping, the morphology of the films resembles the surface of copper films deposited by pulses of 5 ps duration@248 nm [49]. The reason for the presence of relatively large sized particles in the films is their origin: they are ejected directly from the molten target surface [47].
Excellent sticking is a characteristic feature of the unusually high forward peaking. When forward peaking is increased, the amount of energy converted from thermal energy to directed plume expansion kinetic energy increases [53]. The increasing electron density leads to increased pressure gradients at the plume edge, resulting in increased flow speeds. High forward peaking also means high ion density. Even around 1013 W/cm2, the ions arrive at the substrate surface with velocities in the range of 106–107 cm/s [54,55]. The high-energy ions penetrate into the substrate several atomic layers deep, practically realizing ion implantation, anchoring the film to the substrate [56]. Excellent sticking even with the maximum thickness of 1.2 μm to the flat Si wafer surface was verified, indeed: the films not only passed the “Scotch tape’’ test but could hardly be removed even by sandpaper.
The extremely forward-peaked plume produced by the ultrashort UV pulses of high-energy contrast ensures fast film growth of thickness higher than 1 μm obtained in a reasonable time of 1 h and 30 min, with the highest spot area of 1.01 mm2, and a deposition rate of 0.11 nm/pulse. Achieving such a high adherent film within a short deposition time makes PLD induced by sub-ps laser very interesting for developing metallic photocathodes that are useful in RF guns. In these guns, operating at the S-band (2.856 GHz), the features of photocathodes based on thin films are of a thickness comparable with the copper skin depth of 1.2 μm and, at the same time, the appropriate morphological and structural characteristics to face the harsh working conditions in an RF environment.

5. Conclusions

The results presented demonstrate that in an ultrashort temporal regime, the tuning of the ablating spot area offers a broad dynamic range in controlling both the maximum thickness and the lateral distribution of the film material. Ablation with pulses of high energy contrast composed of a 600 fs component of (4.18 ± 0.19) mJ energy and an ASE background conveying (0.22 ± 0.01) mJ energy in 15 ns produces excellently sticking films with a maximum thickness exceeding 1.1 μm for 1.01 mm2 laser spot area with a very forward-peaked shape, while a quite uniform lateral distribution was found for an 0.085 mm2 laser spot area with a maximum thickness of 300 nm. This study was important for understanding that PLD with clean UV pulses is thereby a versatile effective technique for growing metallic thin films with appropriate characteristics to be used as photocathodes for application in RF guns operating at the S-band.

Author Contributions

Conceptualization, T.S., A.L. and A.P.; methodology, A.L., T.S. and S.S.; software, Z.K. and B.G.; data curation, Z.K. and A.L.; writing—original draft preparation, T.S. and A.L.; funding acquisition, A.L., A.P. and S.S. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the Italian National Institute of Nuclear Physics (INFN), the European Union’s Horizon 2020 research and innovation programme at Laserlab-Europe (grant agreement #654148, Access Programme project DP-USZ002584), and the European Social Fund EFOP-3.6.2-16-2017-00005 “Ultrafast physical processes in atoms, molecules, nanostructures and biological systems”. The project also received funding from the National Research, Development, and Innovation Office (OTKA K138339 project) of Hungary.

Data Availability Statement

The data presented in this study are available on request from Tamás Szörényi, [email protected].

Acknowledgments

The authors wish to thank Judit Kopniczky, Department of Optics and Quantum Electronics, University of Szeged, for her essential contribution to the characterization of the films by profilometry and AFM.

Conflicts of Interest

The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript; or in the decision to publish the results.

References

  1. Musumeci, P.; Cultrera, L.; Ferrario, M.; Filippetto, D.; Gatti, G.; Gutierrez, M.S.; Moody, J.T.; Moore, N.; Rosenzweig, J.B.; Scoby, C.M.; et al. Multiphoton Photoemission from a Copper Cathode Illuminated by Ultrashort Laser Pulses in an rf Photoinjector. Phys. Rev. Lett. 2010, 104, 84801–84804. [Google Scholar] [CrossRef] [PubMed]
  2. Divall, M.C.; Prat, E.; Bettoni, S.; Vicario, C.; Trisorio, A.; Schietinger, T.; Hauri, C.P. Intrinsic emittance reduction of copper cathodes by laser wavelength tuning in an rf photoinjector. Phys. Rev. Spec. Top. Accel. Beams 2015, 18, 33401–33406. [Google Scholar] [CrossRef]
  3. Chiadroni, E.; Bacci, A.; Bellaveglia, M.; Boscolo, M.; Castellano, M.; Cultrera, L.; diPirro, G.; Ferrario, M.; Ficcadenti, L.; Filippetto, D.; et al. The SPARC linear accelerator based terahertz source. Appl. Phys. Lett. 2013, 102, 94101–94105. [Google Scholar] [CrossRef]
  4. Scifo, J.; Alesini, D.; Anania, M.P.; Bellaveglia, M.; Bellucci, S.; Biagioni, A.; Bisesto, F.; Cardelli, F.; Chiadroni, E.; Cianchi, A.; et al. Nano-machining surface analysis and emittance measurements of a copper photocathode at SPARC_LAB. Nucl. Instrum. Methods Phys. Res. Sect. A 2018, 909, 233–238. [Google Scholar] [CrossRef]
  5. Maldonado, J.R.; Liu, Z.; Dowell, D.H.; Kirby, R.E.; Sun, Y.; Pianetta, P.; Pease, F. Robust CsBr/Cu photocathodes for the linac coherent light source. Phys. Rev. ST Accel. Beams 2008, 11, 060702. [Google Scholar] [CrossRef]
  6. Zhou, F.; Brachmann, A.; Decker, F.-J.; Emma, P.; Gilevich, S.; Iverson, R.; Stefan, P.; Turner, J. High-brightness electron beam evolution following laser-based cleaning of a photocathode. Phys. Rev. ST Accel. Beams 2012, 15, 090703. [Google Scholar] [CrossRef]
  7. Lorusso, A.; Gontad, F.; Solombrino, L.; Chiadroni, E.; Broitman, E.; Perrone, A. Tight comparison of Mg and Y thin film photocathodes obtained by the pulsed laser deposition technique. Nucl. Instrum. Meth. Phys. Res. A 2016, 836, 57–60. [Google Scholar] [CrossRef]
  8. Wang, X.J.; Babzien, M.; Chang, X.Y.; Lynch, D.; Pjerov, S.; Woodle, M.; Wu, Z. Band high duty photo-injection system. In Proceedings of the 19th IEEE Particle Accelerator Conference, Chicago, IL, USA, 18–22 June 2001; Volume 1822. [Google Scholar]
  9. Qian, J.; Murphy, J.B.; Shen, Y.; Tang, C.X.; Wang, X.J. Surface photoemission in a high-brightness electron beam radio frequency gun. Appl. Phys. Lett. 2010, 97, 253504. [Google Scholar] [CrossRef]
  10. Wang, X.J.; Srinivasan-Rao, T.; Batchelor, K.; Ben-Zvi, I.; Fischer, J. Measurements on photoelectrons from a magnesium cathode in a microwave electron gun. Nucl. Instrum. Meth. Phys. Res. A 1995, 356, 159–166. [Google Scholar] [CrossRef]
  11. Srinivasan-Rao, T.; Schill, J.; Ben-Zvi, I.; Woodle, M. Sputtered magnesium as a photocathode material for rf injectors. Rev. Sci. Instrum. 1998, 69, 2292–2296. [Google Scholar] [CrossRef]
  12. Perrone, A.; D’Elia, M.; Gontad, F.; DiGiulio, M.; Maruccio, G.; Cola, A.; Stankova, N.E.; Kovacheva, D.G.; Broitman, E. Non conventional photocathodes based on Cu thin films deposited on Y substrate by sputtering. Nucl. Instrum. Methods Phys. Res. Sect. A 2014, 752, 27–32. [Google Scholar] [CrossRef]
  13. Srinivasan-Rao, T.; Fischer, J.; Tsang, T. Photoemission studies on metals using picosecond ultraviolet laser pulses. J. Appl. Phys. 1991, 69, 3291–3296. [Google Scholar] [CrossRef]
  14. Cultrera, L.; Gatti, G.; Tazzioli, F.; Perrone, A.; Miglietta, P.; Ristoscu, C.; Orlanducci, S.; Fiori, A. Mg based photocathodes for high brightness RF photoinjectors. Appl. Surf. Sci. 2007, 253, 6531–6534. [Google Scholar] [CrossRef]
  15. Lorusso, A.; Trovò, M.; Demidovich, A.; Cinquegrana, P.; Gontad, F.; Broitman, E.; Chiadroni, E.; Perrone, A. Pulsed laser deposition of yttrium photocathode suitable for use in radio-frequency guns. Appl. Phys. A 2017, 123, 1–7. [Google Scholar] [CrossRef]
  16. Cultrera, L.; Gatti, G.; Miglietta, P.; Tazzioli, F.; Perrone, A.; Moody, J.T.; Musumeci, P. Electron emission characterization of Mg photocathode grown by Pulsed Laser Deposition within an S-band RF gun. Phys. Rev. Spec. Top.-Accel. Beams 2009, 12, 043502. [Google Scholar] [CrossRef]
  17. Lorusso, A.; Anni, M.; Caricato, A.P.; Gontad, F.; Perulli, A.; Taurino, A.; Perrone, A.; Chiadroni, E. Deposition of Y thin films by nanosecond UV pulsed laser ablation for photocathode application. Thin Solid Film. 2016, 603, 441–445. [Google Scholar] [CrossRef]
  18. Gontad, F.; Lorusso, A.; Panareo, M.; Monteduro, A.G.; Maruccio, G.; Broitman, E.; Perrone, A. Nanomechanical and electrical properties of Nb thin films deposited on Pb substrates by pulsed laser deposition as a new concept photocathode for superconductor cavities. Nucl. Instrum. Methods Phys. Res. Sect. A 2015, 84, 132–136. [Google Scholar] [CrossRef]
  19. Lorusso, A. Overview and development of metallic photocathodes prepared by laser ablation. Appl. Phys. A 2013, 110, 869–875. [Google Scholar] [CrossRef]
  20. Cultrera, L.; Grigorescu, S.; Gatti, G.; Miglietta, P.; Tazzioli, F.; Perrone, A.; Nanosci, J. Photoelectron emission from yttrium thin films prepared by pulsed laser deposition. J. Nanosci. Nanotechnol. 2009, 9, 1585–1588. [Google Scholar] [CrossRef]
  21. Lorusso, A.; Cola, A.; Gontad, F.; Koutselas, I.; Panareo, M.; Vainos, N.A.; Perrone, A. New configuration of metallic photocathodes prepared by pulsed laser deposition. Nucl. Instrum. Methods Phys. Res. Sect. A 2013, 724, 72–75. [Google Scholar] [CrossRef]
  22. Saenger, K.L. Angular Distribution of Ablated Material, in Pulsed Laser Deposition of Thin Films. In Pulsed Laser Deposition of Thin Films; Chrisey, D.B., Hubler, G.K., Eds.; John Wiley&Sons: New York, NY, USA, 1994; p. 199 and references therein. [Google Scholar]
  23. Na, L.; Xiaochang, N.; Ru, H.; Tony, D.; Xuan, W.; Amoruso, S.; Ching-yue, W. The spatial detection on distribution of metal nano-particles during femtosecond laser ablation. Proc. SPIE 2009, 7381, 738109. [Google Scholar]
  24. Donnelly, T.; Lunney, J.G.; Amoruso, S.; Bruzzese, R.; Wang, X.; Ni, X. Angular distributions of plume components in ultrafast laser ablation of metal targets. Appl. Phys. A 2010, 100, 569–574. [Google Scholar] [CrossRef]
  25. Anoop, K.K.; Polek, M.P.; Bruzzese, R.; Amoruso, S.; Harilal, S.S. Multidiagnostic analysis of ion dynamics in ultrafast laser ablation of metals over a large fluence range. J. Appl. Phys. 2015, 117, 83108–83109. [Google Scholar] [CrossRef]
  26. Toftmann, B.; Doggett, B.; Budtz-Jørgensen, C.; Schou, J.; Lunney, J.G. Femtosecond ultraviolet laser ablation of silver and comparison with nanosecond ablation. J. Appl. Phys. 2013, 113, 083304. [Google Scholar] [CrossRef]
  27. Amoruso, S.; Bruzzese, R.; Wang, X.; Nedialkov, N.N.; Atanasov, P.A. Femtosecond laser ablation of nickel in vacuum. J. Phys. D Appl. Phys. 2007, 40, 331–340. [Google Scholar] [CrossRef]
  28. Harilal, S.S.; Diwakar, P.K.; Polek, M.P.; Phillips, M.C. Morphological changes in ultrafast laser ablation plumes with varying spot size. Opt. Express 2015, 23, 15608–15615. [Google Scholar] [CrossRef]
  29. Garrelie, F.; Loir, A.S.; Donnet, C.; Rogemond, F.; LeHarzic, R.; Belin, M.; Audouard, E.; Laporte, P. Femtosecond pulsed laser deposition of diamond-like carbon thin films for tribological applications. Surf. Coat. Technol. 2003, 163–164, 306–312. [Google Scholar] [CrossRef]
  30. Loir, A.S.; Garrelie, F.; Donnet, C.; Rogemond, F.; Subtil, J.L.; Forest, B.; Belin, M.; Laporte, P. Towards the deposition of tetrahedral diamond-like carbon films on hip joints by femtosecond pulsed laser ablation. Surf. Coat. Technol. 2004, 188–189, 728–734. [Google Scholar] [CrossRef]
  31. Gilicze, B.; Barna, A.; Kovács, Z.; Szatmári, S.; Földes, I.B. Plasma mirrors for short pulse KrF lasers. Rev. Sci. Instrum. 2016, 87, 083101. [Google Scholar] [CrossRef]
  32. Simon, P.; Ihlemann, J. Ablation of submicron structures on metals and semiconductors by femtosecond UV-laser pulses. Appl. Surf. Sci. 1997, 109–110, 25–29. [Google Scholar] [CrossRef]
  33. Komashko, A.M.; Feit, M.D.; Rubenchik, A.M. Modeling of long-term behavior of ablation plumes produced with ultrashort laser pulses. Proc. SPIE 2000, 3935, 97–103. [Google Scholar]
  34. Jordan, R.; Cole, D.; Lunney, J.G.; Mackay, K.; Givord, D. Pulsed laser ablation of copper. Appl. Surf. Sci. 1995, 86, 24–28. [Google Scholar] [CrossRef]
  35. Shin, B.S.; Oh, J.Y.; Sohn, H. Theoretical and experimental investigations into laser ablation of polyimide and copper films with 355-nm Nd:YVO4 laser. J. Mater. Process. Technol. 2007, 187–188, 260–263. [Google Scholar] [CrossRef]
  36. Tang, G.; Abdolvand, A. Laser-assisted highly organized structuring of copper. Opt. Mater. Express 2011, 1, 1425–1432. [Google Scholar] [CrossRef]
  37. Zhang, W.; Yao, Y.L.; Chen, K. Modelling and Analysis of UV Laser Micromachining of Copper. Int. J. Adv. Manuf. Technol. 2001, 18, 323–331. [Google Scholar] [CrossRef]
  38. Tunna, L.; Kearns, A.; O’Neill, W.; Sutcliffe, C.J. Micromachining of copper using Nd:YAG laser radiation at 1064, 532 and 355 nm wavelengths. Opt. Laser Technol. 2001, 33, 135–143. [Google Scholar] [CrossRef]
  39. Lorusso, A.; Nassisi, V.; Buccolieri, A.; Buccolieri, G.; Castellano, A.; Leo, L.S.; DiGiulio, M.; Torrisi, L.; Caridi, F.; Borrielli, A. Laser ablation threshold of culturalheritage metals. Radiat. Eff. Defects Solids 2008, 163, 325–329. [Google Scholar] [CrossRef]
  40. Müller, F.; Mann, K.; Simon, P.; Bernstein, J.S.; Zaal, G.J. A Comparative Study of Deposition of Thin Films by Laser Induced PVD with Femtosecond and Nanosecond Laser Pulses. Proc. SPIE 1993, 1858, 464–475. [Google Scholar]
  41. Földes, I.B.; Bakos, J.; Gal, K.; Juhász, Z.; Kedves, M.Á.; Kocsis, G.; Szatmari, S.; Veres, G. Properties of high harmonics generated by ultrashort UV laser pulses on solid surfaces. Laser Phys. 2000, 10, 264–269. [Google Scholar]
  42. Byskov-Nielsen, J.; Savolainen, J.M.; Snogdahl, M.; Balling, P. Ultra-short pulse laser ablation of copper, silver and tungsten: Experimental data and two-temperature model simulations. Appl. Phys. A 2011, 103, 447–453. [Google Scholar] [CrossRef]
  43. Mannion, P.T.; Magee, J.; Coyne, E.; O’Connor, G.M.; Glynn, T.J. The effect of damage accumulation behaviour on ablation thresholds and damage morphology in ultrafast laser micro-machining of common metals in air. Appl. Surf. Sci. 2004, 233, 275–287. [Google Scholar] [CrossRef]
  44. Momma, C.; Nolte, S.; Chichkov, B.N.; Alvensleben, F.V.; Tünnermann, A. Precise laser ablation with ultrashort pulses. Appl. Surf. Sci. 1997, 109-110, 15–19. [Google Scholar] [CrossRef]
  45. Cheng, C.W.; Wang, S.Y.; Chang, K.P.; Chen, J.K. Femtosecond laser ablation of copper at high laser fluence: Modeling and experimental comparison. Appl. Surf. Sci. 2016, 361, 41–48. [Google Scholar] [CrossRef]
  46. Gamaly, E.G.; Rode, A.V.; Luther-Davies, B.; Tikhonchuk, V.T. Ablation of solids by femtosecond lasers: Ablation mechanism and ablation thresholds for metals and dielectrics. Phys. Plasmas 2002, 9, 949–957. [Google Scholar] [CrossRef]
  47. Axente, E.; Noël, S.; Hermann, J.; Sentis, M.; Mihailescu, I.N. Subpicosecond laser ablation of copper and fused silica: Initiation threshold and plasma expansion. Appl. Surf. Sci. 2009, 255, 9734–9737. [Google Scholar] [CrossRef]
  48. Hashida, M.; Semerok, A.F.; Gobert, O.; Petite, G.; Izawa, Y.; Wagner, J.F. Ablation threshold dependence on pulse duration for copper. Appl. Surf. Sci. 2002, 197–198, 862–867. [Google Scholar] [CrossRef]
  49. Gontad, F.; Lorusso, A.; Klini, A.; Manousaki, A.; Perrone, A.; Fotakis, C. Growth of poly-crystalline Cu films on Y substrates by picosecond pulsed laser deposition for photocathode applications. Nucl. Instrum. Methods Phys. Res. Sect. A 2015, 799, 70–74. [Google Scholar] [CrossRef]
  50. Preuss, S.; Demchuk, A.; Stuke, M. Sub-picosecond UV laser ablation of metals. Appl. Phys. A 1995, 61, 33–37. [Google Scholar] [CrossRef]
  51. Weaver, I.; Lewis, C.L.S. Polar distribution of ablated atomic material during the pulsed laser deposition of Cu in vacuum: Dependence on focused laser spot size and power density. J. Appl. Phys. 1996, 79, 7216–7222. [Google Scholar] [CrossRef]
  52. Eliezer, S.; Eliaz, N.; Grossman, E.; Fisher, D.; Gouzman, I.; Henis, Z.; Pecker, S.; Horovitz, Y.; Fraenkel, M.; Maman, S.; et al. Synthesis of nanoparticles with femtosecond laser pulses. Phys. Rev. B 2004, 69, 144119. [Google Scholar] [CrossRef]
  53. Singh, R.K.; Narayan, J. Pulsed-laser evaporation technique for deposition of thin films: Physics and theoretical model. Phys. Rev. B 1990, 41, 8843–8859. [Google Scholar] [CrossRef] [PubMed]
  54. Teubner, U.; Uschmann, I.; Gibbon, P.; Altenbernd, D.; Förster, E.; Feurer, T.; Theobald, W.; Sauerbrey, R.; Hirst, G.; Key, M.; et al. Absorption and hot electron production by high intensity femtosecond uv-laser pulses in solid targets. Phys. Rev. E 1996, 54, 4167–4177. [Google Scholar] [CrossRef] [PubMed]
  55. Tóth, Z.; Hopp, B.; Klebniczki, J.; Kresz, N.; Bor, Z.; Anglos, D.; Kalpouzos, C.; Fotakis, C. Expansion velocities of 0.5 ps KrF excimer laser induced plasma by Doppler-shift analysis of pump and probe measurements. Appl. Phys. A 2004, 79, 1287–1290. [Google Scholar] [CrossRef]
  56. Haverkamp, J.; Mayo, R.M.; Bourham, M.A.; Narayan, J.; Jin, C.; Duscher, G. Plasma plume characteristics and properties of pulsed laser deposited diamond-like carbon films. J. Appl. Phys. 2003, 93, 3627–3634. [Google Scholar] [CrossRef]
Materials 16 01267 g001 550
Figure 1. (a) The plasma plume expansion during ablation; (b) the mesh used for defining the array of patterns deposited.
Figure 1. (a) The plasma plume expansion during ablation; (b) the mesh used for defining the array of patterns deposited.
Materials 16 01267 g001
Materials 16 01267 g002 550
Figure 2. Low magnification SEM images of tracks written by tight and loose focusing with: (a) marking the contour of a spot of 1.01 mm2 area and (b) a close-up of the track written focusing to the smallest spot of 0.085 mm2.
Figure 2. Low magnification SEM images of tracks written by tight and loose focusing with: (a) marking the contour of a spot of 1.01 mm2 area and (b) a close-up of the track written focusing to the smallest spot of 0.085 mm2.
Materials 16 01267 g002
Materials 16 01267 g003 550
Figure 3. The evolution of maximum thickness and the growth rate derived with rising spot area. The numbers 1.–5. refer to lens positions to facilitate the assignment of the thickness data to the respective process parameters listed in Table 1.
Figure 3. The evolution of maximum thickness and the growth rate derived with rising spot area. The numbers 1.–5. refer to lens positions to facilitate the assignment of the thickness data to the respective process parameters listed in Table 1.
Materials 16 01267 g003
Materials 16 01267 g004 550
Figure 4. The thickness distribution of films deposited at: (a) 0.085 mm2 and (b) at 1.01 mm2 spot areas. The thickness scales have been set identical intentionally to highlight the difference.
Figure 4. The thickness distribution of films deposited at: (a) 0.085 mm2 and (b) at 1.01 mm2 spot areas. The thickness scales have been set identical intentionally to highlight the difference.
Materials 16 01267 g004
Materials 16 01267 g005 550
Figure 5. A low magnification SEM micrograph taken on a Cu film deposited by 10,000 pulses focused onto 0.085 mm2 area on the target surface.
Figure 5. A low magnification SEM micrograph taken on a Cu film deposited by 10,000 pulses focused onto 0.085 mm2 area on the target surface.
Materials 16 01267 g005
Materials 16 01267 g006 550
Figure 6. An AFM image and line profiles revealing the axial dimensions of the building blocks of the films.
Figure 6. An AFM image and line profiles revealing the axial dimensions of the building blocks of the films.
Materials 16 01267 g006
Materials 16 01267 g007 550
Figure 7. SEM image taken on a segment of a track ablated by 10,000 pulses focused onto 0.085 mm2 area on the target surface.
Figure 7. SEM image taken on a segment of a track ablated by 10,000 pulses focused onto 0.085 mm2 area on the target surface.
Materials 16 01267 g007
Materials 16 01267 g008 550
Figure 8. Comparison of growth rates of copper films deposited by sub-ps UV pulses: this work (■) and data points from [40] converted for the same spot sizes (●).
Figure 8. Comparison of growth rates of copper films deposited by sub-ps UV pulses: this work (■) and data points from [40] converted for the same spot sizes (●).
Materials 16 01267 g008
Table
Table 1. The process parameter windows.
Table 1. The process parameter windows.
Lens Position12345
Main PulseArea (mm2)0.0850.210.340.591.01
Fluence (J/cm2)4.921.991.220.710.41
Intensity (W/cm2)8.2 × 10123.3 × 10122.0 × 10121.2× 10120.7 × 1012
ASEArea (mm2)0.300.901.482.163.30
Fluence (J/cm2)0.0370.0120.00740.00510.0033
Intensity (W/cm2)4.9 × 1061.6 × 1069.9 × 1066.8 × 1064.4 × 106
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Lorusso, A.; Kovács, Z.; Gilicze, B.; Szatmári, S.; Perrone, A.; Szörényi, T. Sub-ps Laser Deposited Copper Films for Application in RF Guns. Materials 2023, 16, 1267. https://doi.org/10.3390/ma16031267

AMA Style

Lorusso A, Kovács Z, Gilicze B, Szatmári S, Perrone A, Szörényi T. Sub-ps Laser Deposited Copper Films for Application in RF Guns. Materials. 2023; 16(3):1267. https://doi.org/10.3390/ma16031267

Chicago/Turabian Style

Lorusso, Antonella, Zsolt Kovács, Barnabás Gilicze, Sándor Szatmári, Alessio Perrone, and Tamás Szörényi. 2023. "Sub-ps Laser Deposited Copper Films for Application in RF Guns" Materials 16, no. 3: 1267. https://doi.org/10.3390/ma16031267

APA Style

Lorusso, A., Kovács, Z., Gilicze, B., Szatmári, S., Perrone, A., & Szörényi, T. (2023). Sub-ps Laser Deposited Copper Films for Application in RF Guns. Materials, 16(3), 1267. https://doi.org/10.3390/ma16031267

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop