Next Article in Journal
Thermal Conductivity Enhancement Derived from Poly(Methyl Methacrylate)-Grafted Carbon Nanotubes in Poly(Methyl Methacrylate)/Polystyrene Blends
Previous Article in Journal
Piezoelectric Films Based on Polyethylene Modified by Aluminosilicate Filler
Previous Article in Special Issue
A Universal Photochemical Method to Prepare Carbohydrate Sensors Based on Perfluorophenylazide Modified Polydopamine for Study of Carbohydrate-Lectin Interactions by QCM Biosensor
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 11
Issue 8
10.3390/polym11081346
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Highly Selective and Reproducible Electrochemical Sensing of Ascorbic Acid Through a Conductive Polymer Coated Electrode

by
Salma Bilal
1,2,*,
Ayesha Akbar
1 and
Anwar-ul-Haq Ali Shah
3
1
National Centre of Excellence in Physical Chemistry, University of Peshawar, Peshawar 25120, Pakistan
2
TU Braunschweig Institute of Energy and Process Systems Engineering,Franz-Liszt-Straße 35, 38106 Braunschweig, Germany
3
Institute of Chemical Sciences, University of Peshawar, Peshawar 25120, Pakistan
*
Author to whom correspondence should be addressed.
Polymers 2019, 11(8), 1346; https://doi.org/10.3390/polym11081346
Submission received: 5 July 2019 / Revised: 11 August 2019 / Accepted: 12 August 2019 / Published: 13 August 2019
(This article belongs to the Special Issue Polymer Based Bio-Sensors)
Browse Figures
Versions Notes

Abstract

:
The surface of an Au-disc electrode was modified through electro polymerization of aniline, in the presence of dodecyl benzene sulphonic acid (DBSA) and sulphuric acid (H2SO4) solution. The polymerization conditions were pre-optimized so that micelle formation and solution coagulation could be minimized and surfactant doped polyaniline film could be obtained through a quick, simple and one step polymerization route. The synthesized material was characterized via Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA), scanning electron microscopy (SEM) and cyclic voltammetry (CV). The effective surface area of the Au-disc, calculated through cyclic voltammetry, was immensely increased through a polyaniline (PANI) coating (0.04 and 0.11 cm2 for bare and PANI coated gold respectively). The modified electrode was utilized for ascorbic acid (AA) sensing. The changing pH of electrolyte and scan rate influenced the PANI electrode response towards AA. The modified electrode was highly selective towards AA oxidation and showed a very low limit of detection i.e. 0.0267 μmol·L–1. Moreover, the PANI coating greatly reduced the sensing potential for AA by a value of around 140 mV when compared to that on a bare gold electrode.

Graphical Abstract

1. Introduction

Chemical sensors are of vital importance in different fields including monitoring of different species in the atmosphere, in industrial processes, biomedical analysis, and food quality control [1]. Among many analytes, ascorbic acid (AA), which is an important biomolecule, is frequently detected as it is a main nutrient and antioxidant found in vegetables, fruits and in other naturally occurring systems [2]. It is useful in activating an immune response, and it contributes in wound healing, iron absorption, osteogenesis collagen formation, and preservation of capillaries, bones and teeth [3]. It is usually recommended in the treatment of certain diseases such as Alzheimer’s, infertility HIV infections, atherosclerosis and cancer [4]. The normal level of AA in human plasma is in between 50 to 70 µM [5].
A high level of AA can cause gastric irritation, and its metabolites can lead to renal issues, while the deficiency of AA is responsible for the illness scurvy [6]. AA determination is also essential in the agricultural field. Some natural processes in food may get disturbed due to excessive amounts of AA which is responsible for deterioration in the taste and aroma [7].
Various techniques such as chromatography [8], chemiluminescence [9], and spectrometry [10] have been reported for the detection of AA. However, these techniques are expensive and require highly skilled personnel working on complex equipment. These techniques also involve difficult analytical procedures in multi sample preparation. Therefore, extensive research is underway develop a simple, fast, reliable and cost effective technique adequate for in-situ and on-time analyte detection [11].
In this context, electrochemical methods are more suitable, reliable, economic and user-friendly in-field applications. The electrochemical techniques have linear wide range responses with exceptional repeatability, accuracy and low detection limits [12]. During electrochemical sensing, electrodes are used for passing current to solution and the resulting electrical signals, caused by the electrochemical reactions occurring between analyte and electrode, are recorded.
The instrumentational setup of an electrochemical technique is mostly compact, portable and simple due to electrode miniaturization which makes this technique more effective for sensing analytes [13]. Generally, a three electrode setup including reference, counter and working electrodes is employed in electrochemical techniques. However, it has been reported that the direct oxidation of AA is irreversible at bare electrodes (such as glassy carbon, screen printed and gold). High over potential is required which results in low selectivity, fouling of electrodes, and poor reproducibility. Therefore, surface modification of electrodes leading to selective and sensitive AA detection with less over potential has received much attention [14]. Different materials have been employed for surface modification of the working electrode including silicon, metal oxides, metals, conducting polymers and carbon nanotubes [15].
Conducting polymers, have been particularly investigated because of their simple fabrication method, biocompatibility, optical and characteristic physical properties. Conducting polymer based sensors offer attractive advantages. They are effective at room temperature, diverse in structure and easy to fabricate [16,17,18]. The conducting polymer polyaniline (PANI) has exceptional properties, including stable mechanisms of electrical conduction, reversible and simple doping–dedoping ability, easy synthesis, high environmental stability and low cost. These properties make it a potential candidate for applications in electrochemical sensors [19,20,21]. It is such a versatile material that its properties can be very easily tuned, by developing different synthetic strategies, to make it suitable for various applications [22].
Most of the promising properties of PANI are observable when it is in its doped and conducting state. PANI can be doped simultaneously with many inorganic and organic materials in order to change its structure, rise mechanical strength, increase conductivity, improve solubility and to create more active sites to convert the targeted molecule into easily detectable species [22,23]. In previous reports electrodes modified with PANI in its doped state were effectively used for the electro-catalytic detection of AA [24,25]. It is supposed that PANI will not only have a large and adhesive surface area, but also provide a conductive medium which will favorably support the dopant materials for their effective role in AA electro-oxidation. These works show that PANI electrodes have a great potential to sense AA.
We report here a very simple and reproducible way of electrode modification by electrooxidation of aniline in the presence of dodecylbenzene sulfonic acid (DBSA) and sulphuric acid (H2SO4) solution. Although surfactant molecules such as DBSA can impart very promising properties to PANI, the polymerization of aniline in the presence of surfactants always remained a challenge due to micellization and coagulation. Unlike the surface modification of electrodes with chemically synthesized and doped PANI, which often requires more than a week to synthesize the polymer to use it as coating for electrode surfaces, the present methodology is very simple and can be done in a single step in a very short time [26,27]. Different characterization techniques support formation of PANI containing both DBSA and sulfuric acid as dopants. This modified PANI electrode exhibits rapid electro-catalytic activity towards AA oxidation along with enhanced linearity, comparable low detection limit (LOD), high sensitivity and good selectivity.

2. Experimental

2.1. Chemicals

Sulphuric acid solution (97.5%), dipotassium hydrogen phosphate (K2HPO4) and potassium hydroxide (KOH) (Scharlau, Sentmenat, Spain ), potassium dihydrogen phosphate (KH2PO4) and dopamine (DA) (Merck, Kenilworth, NJ, USA), ascorbic acid (AA) (Merck, Kenilworth, NJ, USA), uric acid (UA) (Alfa Aesar, ), DBSA (Sigma Aldrich, Hamburg, Germany) were used as received. Deionized water (H2O) (Millipore, Burlington, MA, USA) was used for solution preparation. Aniline () was double distilled ( Merck, Kenilworth, NJ, USA) and stored in a refrigerator.

2.2. Instrumentation

Fourier-transform infrared spectroscopy (FTIR) analysis of PANI was carried out in the range of 400–4000 cm−1 by using IRAffinity-1S Shimadzu Spectrophotometer (Shimadzu, Tokyo, Japan). Thermal stability of PANI samples were determined by using Perkin Elmer, Diamond series (Waltham, MA, USA) at heating rate of 10 °C/min under a nitrogen atmosphere. Surface imaging of the synthesized samples was carried out with a scanning electron microscope (SEM) (Helios G4 CX DualBeam microscope equipped with OctaneElite, EFI, Berlin Germany). Electrochemical characterization was done in a three electrode cell using Reference 600 ZRA potentiostat (Gamry, Warminster, PA, USA). A gold disc, saturated calomel electrode (SCE) and gold sheet were utilized as working, reference and counter electrode, respectively.

2.3. Cleaning of the Au-disc Electrode

The Au-disc electrode was first mechanically cleaned by polishing with alumina for 5 min. This polished Au-disc electrode was then washed with distilled water and further electrochemically cleaned by applying potential cycling in the range of −0.2 to 1.45 V at a scan rate of 100 mV/s in 0.5 M sulfuric acid solution, until the cyclic voltammograms become stable (40 cycles). After this, its cyclic voltammogram was recorded in 4 mM K3[Fe(CN)6]/1 M KNO3. The ΔEp of the bare Au- electrode was found to be 90 mV, indicating less surface imperfection of the electrode [28].

2.4. Fabrication of the Modified PANI Electrode

The surface of Au-disc electrode was modified with PANI by electro-oxidation of aniline in a single cell consisting of three electrodes (Scheme 1). 0.05M aniline was added to 1M H2SO4 solution, sonicated for 10 to 15 minutes and was then poured into 0.025M DBSA solution. This mixture was thoroughly shacked and transferred to the electrochemical cell where it was subjected to 10 potential cycles in the range of −0.2 to 0.8 V at 20 mV/s using Au-disc working electrode. A dark green layer was observed on the surface of the electrode. The modified electrode after polymerization was washed with distilled H2O and then dried. The PANI modified Au-disc was used as the working electrode for AA oxidation. Chronoamperometry was conducted to monitor AA at an optimized 0.24 V.

2.5. Preparation of the AA Solutions

The AA solutions were prepared in phosphate buffer (PB). PB solutions (PBS) of varying pH were made by means of the Henderson–Hasselbalch equation [29]. After PBS preparation, AA (0.88 g) was added to 0.1M PBS in order to make 100 mM AA stock solution which was further utilized for the preparation of different concentrated AA solutions.

3. Results and Discussions

3.1. Electropolymerization of Aniline

Aniline polymerization was carried out via cyclic voltammetry and its characteristic voltammogram are shown in Figure 1a. During polymerization no faradic process was observed until 0.6 V in the initial forward scan, and after this potential, the polymer growth and nucleation occurs up to 0.8 V. The cathodic peak Epc was observed at 0.06 V during the initial backward scan. During the first cycle, the increased in current between 0.60–0.75 V shows the anilinium cationic radicals’ formation. This peak current is further enhanced when potential is scanned again which indicates the coupling of cation radicals to form benzenoid and quinoid structures [30].
At the completion of the 3rd cycle, two visible anodic and cathodic peaks were developed indicating the polyaniline (PANI) thin layer formation at the bare Au-disc electrode. A green color film was observed on the surface of electrode after 10 cycles. This film was washed with deionized water, dried and then transferred to a monomer free electrolyte where a cyclic voltammogram was recorded in order to characterize the electrochemical response of polymer film. The potential was scanned between −0.2 and 1 V at the scan rate of 50 mV/s.
The interconversion of different PANIs between its different forms including reduced leucoemeraldine (LE), semi-oxidized and conducting emeraldine salt (ES) and oxidized pernagraniline (PG) [31] is indicated by the presence of two redox pairs in Figure 1b. The LE and ES inter conversion is shown by a redox pair at 0.12 and −0.002 V while the ES and PG interconversion is represented by a redox pair at 0.66 and 0.6 V. The interconversion of different PANI redox states is shown in Scheme 2. It is noteworthy to mention that the film obtained by electro-oxidation of aniline in the presence of DBSA in acidic solution showcases very well defined typical redox characteristics of PANI. Further insights into the properties of this PANI film were gained through different characterization techniques as discussed in the following sections.

3.2. FTIR Analysis

The presence of different functional groups in the PANI back bone was confirmed by FTIR analysis (Figure 2). For this purpose the PANI film, washed with deionized water, was scratched from the electrode in its doped form, and dried in the form of powder.
The benzenoid and quinoid stretching is denoted by the peaks at 1492 cm−1 and 1552 cm−1, respectively [33]. The polaron C–N* stretching is located at 1299 cm−1 indicating the conducting form of PANI [34]. The peak at 1110 cm−1 is attributed to the stretching of C–N= [35,36] while the peak at 808 cm−1 shows out of plane deformation of C–H [37]. The aliphatic C–H, due to DBSA, is represented by the bands at 2825–2911 cm−1. The HSO4¯ peak at 651 cm−1 proves the presence of acidic dopants in the PANI film [38]. The FTIR analysis effectively confirms the incorporation of both DBSA and sulfuric acid moieties into the PANI backbone.

3.3. SEM Analysis

The surface morphology of PANI in its undoped and doped state (Figure 3a,b respectively) was observed by taking scanning electron micrographs. Micro-spherical particles and compact globules can be seen in SEM images of doped PANI at high magnification. The surface morphology of PANI exhibits a cauliflower like structure. The DBSA presence in the polymer has a significant role in presenting this kind of morphology because it makes the PANI more granular, dense, and porous as compared to PANI without DBSA. This type of morphology is considered very important for application of PANI in sensors because it can offer more active sites to the target analyte leading to a low detection limit [39].

3.4. Thermal Analysis

The thermal decomposition and stability of PANI was determined via thermogravimetric analysis (TGA). The polymer mass vs temperature was measured between 40 to 800 °C. In Figure 4 the first weight loss at 248 °C indicates the removal of volatile materials i.e. adsorbed moisture on the sample surface, and residue of electrolyte and oligomers of lower molecular weights. The second weight loss at 250–450 °C is attributed to the removal of DBSA in the PANI. At 450–600 °C, the weight loss is due to thermo-oxidative PANI decomposition [40]. The TGA plot indicates that the synthesized PANI has quite high thermal stability.

3.5. Effective Area of PANI Modified Electrode

The better sensing performance of PANI is often related to the increase in effective surface area of the working electrode when modified with PANI. To confirm this argument, effective surface area of the bare and PANI coated Au-disc electrode was determined as follows.
Cyclic voltammograms were recorded for bare and PANI modified electrodes in 4 mM K3[Fe(CN)6] in 1 M KNO3 (Figure 5a,b). The anodic peak potential Epa of bare and modified PANI electrode was 0.266 and 0.258 V while the cathodic peak potential Epc of bare and PANI modified electrode was 0.179 and 0.190 V. The Epa and Epc of bare as well as modified electrode shifted towards more positive and negative value, respectively when scan rate increases. Linear plot was obtained when anodic peak current Ip was plotted vs square root of potential scan rate (Insets of Figure 5a,b). The Randles–Sevcik equation was used to measure the effective area of the bare and PANI coated electrodea [41].
Ip = (2.69 × 105) n3/2 A υ1/2D1/2 C
where the current peak is denoted by Ip, n represents the electron numbers involved during the reaction. Diffusion coefficient “D” of K3[Fe(CN)6] is approximately equal to 6.7 × 10-6 cm2/s, the K3[Fe(CN)6] molar concentration is C = 4 mM. The 0.04 and 0.11cm2/s are the calculated values of electroactive surface area of the bare and modified PANI electrode respectively. These values confirm that the PANI coating increases the active surface area of the Au disc electrode, hence providing more active sites for analyte oxidation [42].

3.6. Ascorbic Acid (AA) Sensing by PANI

PANI present in the form of emeraldine salt, is more highly conductive than the emeraldine base state due to dopant ions existence in PANI. Here the DBSA has a significant role in the sensing mechanism because of its large size and presence of anionic sulphate (SO3-) group and a dodecyl (C12H25) group. The dodecyl (C12H25) group is responsible for non-polar interaction with the surrounding aqueous medium and it resists the PANI being phased out. The interaction between the chains of conjugated PANI is also reduced due to DBSA. Thus DBSA in PANI creates more potential sites for better sensing of AA. In the current situation when AA comes near to PANI, a partial bond between H of AA and N of PANI appears which increases the inter-chain distance in PANI and the electron hopping mechanism among adjacent chains is disturbed [34]. Consequently, AA is oxidized into dehydroascorbic acid and emeraldine salt is changed into pernagraniline which can again be reduced at moderate electrode potential [25] (Scheme 3).

3.7. pH and Scan Rate Effect on AA oxidation

Figure 6 shows the pH influence on the AA oxidation in phosphate buffer solution. The anodic peak of AA is high at low pH and decreases gradually as the pH is increased. The Epa = 0.33 V of AA shift towards negative potential when the pH of PBS increases from 2 to 6. The regression equation of the linear plot between the pH of the electrolyte and peak potential Ep = 424.6 – 44 mVpH (R2 = 0.9733) indicates that AA oxidation is a pH dependent reaction, involving two electrons and one proton [43]. PANI shows high electrical conductivity in acidic solutions which decreases with the increasing pH. Hence, the electro-catalytic oxidation of AA on PANI modified electrode shows an inverse relation with pH of the PBS and the second anodic peak of PANI modified electrode is observed at 0.42V due to is shifted to negative potentials (0.42 V) in high pH PBS (pH = 6). It is also known that AA dissociation occurs into two steps with 4.1 and 11.8 pKa values, respectively. Hence, the reactions of oxidizable species HA- (ionized ascorbate) in high pH solutions are given as under:
HA- → [HA] + ē
HA- + [HA] → A + AA + ē.
The [HA] radical formed in the first step, further oxidized into dehydroascorbic acid (A) while AA is again generated at electrode/electrolyte interface [44].
The scan rate effect on the anodic current peak of AA was also investigated as depicted in Figure 7 which shows the enhancement in the current peak when the scan rate rises. The anodic-current peak linearly correlates to the υ with regression equation Ipa (µA) = 42.29 + 0.897x (R2 = 0.980), indicating that the oxidative-process of AA on the modified PANI electrode is electrochemically surface controlled. No well-defined reduction peaks are observed, suggesting that the process is quasi-reversible [45].

3.8. Effect of AA Concentration on Voltammetric Response of the PANI Modified Electrode

The electrochemical behavior of bare Au disc and PANI modified electrode towards 4 mM AA in 0.1 M PBS (pH = 4) was investigated by recording cyclic voltammograms (CVs) in the potential range of −0.2-0.7 V at 50 mVs−1 (Figure 8a). The PANI modified electrode shows a high response towards AA oxidation compared to the bare electrode. It is also evident that oxidation of AA occurs at around 0.26 V on the PANI modified electrode while on the bare gold electrode this value is around 0.4 V. This means the oxidation over potential of AA is decreased by almost 140 mV on the PANI modified electrode as compare to its oxidation potential on the bare gold electrode.
Figure 8b displays the CVs of the PANI modified electrode recorded for AA solutions of varying concentrations (2-14 mM in 0.1 M PBS (pH = 4)). Anodic peak current increases with increase in AA concentration. This suggests that effective surface area of the electrode is sufficient enough to cope with the increasing analyte concentration and provide sites for its oxidation. The correlation linear equation of the curve shown in the inset of Figure 8b is Ipa(µA) = 18.8x +19.36 (R2 = 0.997).
The AA sensing was also studied via linear sweep voltammetry (LSV) at 50 mVs−1 as presented in Figure 8c. The observed Epa of AA from LSV was 0.259 V which is approximately the same as found in CV. Again the oxidative-current peak increases with an increase in AA concentration. As discussed in the previous section, the semi-oxidized PANI oxidized AA into dehydroascorbic acid due to electron transfer, indicated by the anodic current peak.

3.9. Chronoamperometry

The current response of bare gold (Figure 9a) and PANI modified electrode (Figure 9b) with respect to time was examined when AA (0.05 mM) was successively added to 0.1 M PBS under moderate stirring at an optimized potential of 0.24 V. The response of the bare gold electrode is very low compared to that of the PANI modified electrode. A simple electron transfer process over the surface of the PANI electrode is represented by a steady state plateau which was obtained within 14 s after AA addition, indicating a sensitive response of the modified electrode towards AA oxidation. The steady-state current is linearly correlated to the AA concentration in the range of 0.05 mM to 0.5 mM. The chronoampermetry of PANI is shown in Figure 9b which gives a good calibration curve i.e. Ipa (µA) = 13.48x + 0.599 (R2 = 0.997). The LOD of the electrode was evaluated with the help of following formula
LOD = 3.3 S/b
where “S” is the standard deviation while “b” is the calibration plot slope.
Along with AA many interfering species are also present in the reported usual physiological sample which creates problems during the selective detection of AA. The modified PANI electrode selectivity was investigated by monitoring chronoamperometric responses when AA along with other interfering agents such as dopamine (DA), uric acid (UA) and glucose were added in 0.1 M PBS. Figure 10 shows that the PANI electrode generates significant signals during 0.3 mM AA addition while negligible current was produced when the same amount of interfering species were added. This means that the present PANI based sensor is highly selective towards oxidation of AA. A comparison of the obtained results with already published data by others is provided in Table 1.

3.10. Reproducibility of AA Sensor

Figure 11 depicts the reproducibility of the PANI electrode for detection of AA while the relevant values of peak current, standard deviation (SD) and relative standard deviation (RSD) are cited in Table 2. Five PANI electrodes were prepared and their CVs were measured in 0.1 M PBS containing 4 mM AA in order to determine the PANI electrode reproducibility for AA detection. The low RSD value (1.1964%) indicates that the PANI electrode is highly reproducible for AA sensing.

4. Conclusions

Electrode modification with conductive PANI via electrochemical polymerization in the presence of DBSA and sulfuric acid can be effectively utilized for selective and catalytic oxidation of ascorbic acid. The catalytic oxidation is attributed to the immense enhancement in the active surface area of the electrode through the PANI coating. The influence of PBS pH and different scan rates on analyte current response was determined in order to understand the optimized conditions for better AA detection. The electrode preparation process is simple and low cost while electrocatalytic behavior of the sensor can possibly pave the way for the fabrication of a reliable AA sensor. The sensor exhibits enhanced properties in terms of detection limit, response time, electrode fabrication and reproducibility in comparison with the other reported AA sensors.

Author Contributions

S.B. conceptualized and supervised. A.A. performed experimental work. All the authors contributed in writing, editing and analysis.

Funding

This research was funded by the Higher Education Commission Pakistan (project No. 20-1647 and 20--111/NRPU/R&D/HEC). The APC was funded by the German Research Foundation and the Open Access Publication Funds of the Technische Universität Braunschweig.

Acknowledgments

We acknowledge support from the German Research Foundation and the Open Access Publication Funds of the Technische Universität Braunschweig. Support from the Alexander von Humboldt Foundation Germany is gratefully acknowledged. Ingo Kampen and Louise Niemeyer, Institute für Partikeltechnik, TU Braunschweig, Germany, are also acknowledged for their kind support in the SEM.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Castillo-Ortega, M.; Del Castillo-Castro, T.; Ibarra-Bracamontes, V.; Nuno-Donlucas, S.; Puig, J.; Herrera-Franco, P. Urea sensing film prepared by extrusion from DBSA-doped polyaniline-poly (styrene-co-potassium acrylate) in a poly (n-butyl methacrylate) matrix. Sens. Actuators B Chem. 2007, 125, 538–543. [Google Scholar] [CrossRef]
  2. Pei, L.; Qiu, F.; Ma, Y.; Lin, F.; Fan, C.; Ling, X.; Zhu, S. Graphene/zinc bismuthate nanorods composites and their electrochemical sensing performance for ascorbic acid. Fuller. Nanotub. Carbon Nanostruct. 2019, 27, 58–64. [Google Scholar] [CrossRef]
  3. Erdurak-Kilic, C.; Uslu, B.; Dogan, B.; Ozgen, U.; Ozkan, S.; Coskun, M. Anodic voltammetric behavior of ascorbic acid and its selective determination in pharmaceutical dosage forms and some Rosa species of Turkey. J. Anal. Chem. 2006, 61, 1113–1120. [Google Scholar] [CrossRef]
  4. Xing, L.; Ma, Z. A glassy carbon electrode modified with a nanocomposite consisting of MoS2 and reduced graphene oxide for electrochemical simultaneous determination of ascorbic acid, dopamine, and uric acid. Microchim. Acta 2016, 183, 257–263. [Google Scholar] [CrossRef]
  5. Syed, A.A.; Knowlson, S.; Sculthorpe, R.; Farthing, D.; DeWilde, C.; Farthing, C.A.; Larus, T.L.; Martin, E.; Brophy, D.F.; Gupta, S. Phase I safety trial of intravenous ascorbic acid in patients with severe sepsis. J. Transl. Med. 2014, 12, 1–10. [Google Scholar] [CrossRef]
  6. Pakapongpan, S.; Mensing, J.P.; Phokharatkul, D.; Lomas, T.; Tuantranont, A. Highly selective electrochemical sensor for ascorbic acid based on a novel hybrid graphene-copper phthalocyanine-polyaniline nanocomposites. Electrochim. Acta 2014, 133, 294–301. [Google Scholar] [CrossRef]
  7. Pisoschi, A.M.; Pop, A.; Serban, A.I.; Fafaneata, C. Electrochemical methods for ascorbic acid determination. Electrochim. Acta 2014, 121, 443–460. [Google Scholar] [CrossRef]
  8. Kishida, E.; Nishimoto, Y.; Kojo, S. Specific determination of ascorbic acid with chemical derivatization and high-performance liquid chromatography. Anal. Chem. 1992, 64, 1505–1507. [Google Scholar] [CrossRef]
  9. Agater, I.B.; Jewsbury, R.A. Direct chemiluminescence determination of ascorbic acid using flow injection analysis. Anal. Chim. Acta 1997, 356, 289–294. [Google Scholar] [CrossRef]
  10. Yebra, M.; Cespon, R.; Moreno-Cid, A. Automatic determination of ascorbic acid by flame atomic absorption spectrometry. Anal. Chim. Acta 2001, 448, 157–164. [Google Scholar] [CrossRef]
  11. Ponnaiah, S.K.; Periakaruppan, P.; Vellaichamy, B. New Electrochemical Sensor Based on a Silver-Doped Iron Oxide Nanocomposite Coupled with Polyaniline and Its Sensing Application for Picomolar-Level Detection of Uric Acid in Human Blood and Urine Samples. J. Phys. Chem. B 2018, 122, 3037–3046. [Google Scholar] [CrossRef]
  12. Yusoff, N.; Pandikumar, A.; Ramaraj, R.; Lim, H.N.; Huang, N.M. Gold nanoparticle based optical and electrochemical sensing of dopamine. Microchim. Acta 2015, 182, 2091–2114. [Google Scholar] [CrossRef]
  13. Kudr, J.; Nguyen, H.; Gumulec, J.; Nejdl, L.; Blazkova, I.; Ruttkay-Nedecky, B.; Hynek, D.; Kynicky, J.; Adam, V.; Kizek, R. Simultaneous Automatic Electrochemical Detection of Zinc, Cadmium, Copper and Lead Ions in Environmental Samples Using a Thin-Film Mercury Electrode and an Artificial Neural Network. Sensors 2015, 15, 592–610. [Google Scholar] [CrossRef]
  14. Zhang, X.; Lai, G.; Yu, A.; Zhang, H. A glassy carbon electrode modified with a polyaniline doped with silicotungstic acid and carbon nanotubes for the sensitive amperometric determination of ascorbic acid. Microchim. Acta 2013, 180, 437–443. [Google Scholar] [CrossRef]
  15. Jadon, N.; Jain, R.; Sharma, S.; Singh, K. Recent trends in electrochemical sensors for multianalyte detection—A review. Talanta 2016, 161, 894–916. [Google Scholar] [CrossRef]
  16. Park, S.; Park, C.; Yoon, H. Chemo-electrical gas sensors based on conducting polymer hybrids. Polymers 2017, 9, 155. [Google Scholar] [CrossRef]
  17. Sabatini, V.; Pifferi, V.; Checchia, S.; Rebeccani, S.; Farina, H.; Aldo Ortenzi, M.; Falciola, L. A Combined XRD, Solvatochromic, and Cyclic Voltammetric Study of Poly (3, 4-Ethylenedioxythiophene) Doped with Sulfonated Polyarylethersulfones: Towards New Conducting Polymers. Polymers 2018, 10, 770. [Google Scholar] [CrossRef]
  18. Janata, J.; Josowicz, M. Conducting polymers in electronic chemical sensors. Nat. Mater. 2003, 2, 19–24. [Google Scholar] [CrossRef]
  19. Fratoddi, I.; Venditti, I.; Cametti, C.; Russo, M.V. Chemiresistive polyaniline-based gas sensors: A mini review. Sens. Actuator B Chem. 2015, 220, 534–548. [Google Scholar] [CrossRef]
  20. Prathap, M.A.; Srivastava, R. Tailoring properties of polyaniline for simultaneous determination of a quaternary mixture of ascorbic acid, dopamine, uric acid, and tryptophan. Sens. Actuator B Chem. 2013, 177, 239–250. [Google Scholar] [CrossRef]
  21. Ghanbari, K.; Moloudi, M. Flower-like ZnO decorated polyaniline/reduced graphene oxide nanocomposites for simultaneous determination of dopamine and uric acid. Anal. Biochem. 2016, 512, 91–102. [Google Scholar] [CrossRef]
  22. Sen, T.; Mishra, S.; Shimpi, N.G. Synthesis and sensing applications of polyaniline nanocomposites: A review. RSC Adv. 2016, 6, 42196–42222. [Google Scholar] [CrossRef]
  23. Das, M.; Sarkar, D. One-pot synthesis of zinc oxide-polyaniline nanocomposite for fabrication of efficient room temperature ammonia gas sensor. Ceram Int. 2017, 43, 11123–11131. [Google Scholar] [CrossRef]
  24. Ambrosi, A.; Morrin, A.; Smyth, M.R.; Killard, A.J. The application of conducting polymer nanoparticle electrodes to the sensing of ascorbic acid. Anal. Chim. Acta 2008, 609, 37–43. [Google Scholar] [CrossRef]
  25. Rana, U.; Paul, N.D.; Mondal, S.; Chakraborty, C.; Malik, S. Water soluble polyaniline coated electrode: A simple and nimble electrochemical approach for ascorbic acid detection. Synth Met. 2014, 192, 43–49. [Google Scholar] [CrossRef]
  26. Bhadra, S.; Khastgir, D.; Singha, N.K.; Lee, J.H. Progress in preparation, processing and applications of polyaniline. Prog. Polym. Sci. 2009, 34, 783–810. [Google Scholar] [CrossRef]
  27. Li, G.-R.; Feng, Z.-P.; Zhong, J.-H.; Wang, Z.-L.; Tong, Y.-X. Electrochemical synthesis of polyaniline nanobelts with predominant electrochemical performances. Macromolecules 2010, 43, 2178–2183. [Google Scholar] [CrossRef]
  28. Fischer, L.M.; Tenje, M.; Heiskanen, A.R.; Masuda, N.; Castillo, J.; Bentien, A.; Émneus, J.; Jakobsen, M.H.; Boisen, A. Gold cleaning methods for electrochemical detection applications. Microelectron. Eng. 2009, 86, 1282–1285. [Google Scholar] [CrossRef]
  29. Nguyen, T.H.; Venugopala, T.; Chen, S.; Sun, T.; Grattan, K.T.; Taylor, S.E.; Basheer, P.M.; Long, A.E. Fluorescence based fibre optic pH sensor for the pH 10–13 range suitable for corrosion monitoring in concrete structures. Sens. Actuator B Chem. 2014, 191, 498–507. [Google Scholar] [CrossRef]
  30. Singh, K.; Ohlan, A.; Kotnala, R.; Bakhshi, A.; Dhawan, S. Dielectric and magnetic properties of conducting ferromagnetic composite of polyaniline with γ-Fe2O3 nanoparticles. Mater. Chem. Phys. 2008, 112, 651–658. [Google Scholar] [CrossRef]
  31. Raj, J.A.; Mathiyarasu, J.; Vedhi, C.; Manisankar, P. Electrochemical synthesis of nanosize polyaniline from aqueous surfactant solutions. Mater. Lett. 2010, 64, 895–897. [Google Scholar] [CrossRef]
  32. Cao, P.-F.; Mangadlao, J.D.; Advincula, R.C. Stimuli-responsive polymers and their potential applications in oil-gas industry. Polym. Rev. 2015, 55, 706–733. [Google Scholar] [CrossRef]
  33. Arasi, A.Y.; Jeyakumari, J.J.L.; Sundaresan, B.; Dhanalakshmi, V.; Anbarasan, R. The structural properties of Poly (aniline)—Analysis via FTIR spectroscopy. Spectrochim. Acta A Mol. Biomol. Spectrosc. 2009, 74, 1229–1234. [Google Scholar] [CrossRef] [PubMed]
  34. Das, M.; Sarkar, D. Effect of oxidizing agent on ammonia sensing of DBSA doped polyaniline nanocomposite thin film. J. Mater. Sci. Mater. Electron. 2016, 27, 4109–4119. [Google Scholar] [CrossRef]
  35. Selvanayagam, A.S.; Jeyaprakash, B.; Rayappan, J.B.B. Preparation, characterization and chemical sensing properties of polyaniline thin films. J. Appl. Sci. 2012, 12, 1710–1713. [Google Scholar] [CrossRef]
  36. Silva, A.; Ugucioni, J.; Correa, S.; Ardisson, J.; Macedo, W.; Silva, J.; Cotta, A.; Brito, A. Synthesis and characterization of nanocomposites consisting of polyaniline, chitosan and tin dioxide. Mater. Chem. Phys. 2018, 216, 402–412. [Google Scholar] [CrossRef]
  37. Trchova, M.; Sedenkova, I.; Tobolkova, E.; Stejskal, J. FTIR spectroscopic and conductivity study of the thermal degradation of polyaniline films. Polym. Degrad. Stab. 2004, 86, 179–185. [Google Scholar] [CrossRef]
  38. Gul, S.; Shah, A.U.; Bilal, S. Effect of high temperature on the electrochemical and optical properties of emeraldine salt doped with DBSA and sulfuric acid. J. Chem. 2015, 2015, 1–9. [Google Scholar] [CrossRef]
  39. Mondal, S.; Sangaranarayanan, M. A novel non-enzymatic sensor for urea using a polypyrrole-coated platinum electrode. Sens. Actuator B Chem. 2013, 177, 478–486. [Google Scholar] [CrossRef]
  40. Ansari, M.O.; Mohammad, F. Thermal stability, electrical conductivity and ammonia sensing studies on p-toluenesulfonic acid doped polyaniline: Titanium dioxide (pTSA/Pani: TiO2) nanocomposites. Sens. Actuator B Chem. 2011, 157, 122–129. [Google Scholar] [CrossRef]
  41. Shi, J.; Claussen, J.C.; McLamore, E.S.; ul Haque, A.; Jaroch, D.; Diggs, A.R.; Calvo-Marzal, P.; Rickus, J.L.; Porterfield, D.M. A comparative study of enzyme immobilization strategies for multi-walled carbon nanotube glucose biosensors. Nanotechnology 2011, 22, 355502. [Google Scholar] [CrossRef] [PubMed]
  42. Singhal, C.; Malhotra, N.; Pundir, C.; Narang, J. An enzyme free vitamin C augmented sensing with different ZnO morphologies on SnO2/F transparent glass electrode: A comparative study. Mater. Sci. Eng. C 2016, 69, 769–779. [Google Scholar] [CrossRef] [PubMed]
  43. Ruiz, J.J.; Aldaz, A.; Dominguez, M. Mechanism of L-ascorbic acid oxidation and dehydro-L-ascorbic acid reduction on a mercury electrode. I. Acid medium. Can. J. Chem. 1977, 55, 2799–2806. [Google Scholar] [CrossRef]
  44. Kalakodimi, R.P.; Nookala, M. Electrooxidation of ascorbic acid on a polyaniline-deposited nickel electrode: Surface modification of a non-platinum metal for an electrooxidative analysis. Anal. Chem. 2002, 74, 5531–5537. [Google Scholar] [CrossRef] [PubMed]
  45. Xu, H.; Xiao, J.; Yan, L.; Zhu, L.; Liu, B. An electrochemical sensor for selective detection of dopamine based on nickel tetrasulfonated phthalocyanine functionalized nitrogen-doped graphene nanocomposites. J. Electroanal. Chem. 2016, 779, 92–98. [Google Scholar] [CrossRef]
  46. Xia, C.; Ning, W. A novel bio-electrochemical ascorbic acid sensor modified with Cu4 (OH)6SO4 nanorods. Analyst 2011, 136, 288–292. [Google Scholar] [CrossRef] [PubMed]
  47. Teymourian, H.; Salimi, A.; Khezrian, S. Fe3O4 magnetic nanoparticles/reduced graphene oxide nanosheets as a novel electrochemical and bioeletrochemical sensing platform. Biosens. Bioelectron. 2013, 49, 1–8. [Google Scholar] [CrossRef]
  48. Kumar, S.A.; Lo, P.-H.; Chen, S.-M. Electrochemical selective determination of ascorbic acid at redox active polymer modified electrode derived from direct blue 71. Biosens. Bioelectron. 2008, 24, 518–523. [Google Scholar] [CrossRef]
  49. Li, H.; Wang, Y.; Ye, D.; Luo, J.; Su, B.; Zhang, S.; Kong, J. An electrochemical sensor for simultaneous determination of ascorbic acid, dopamine, uric acid and tryptophan based on MWNTs bridged mesocellular graphene foam nanocomposite. Talanta 2014, 127, 255–261. [Google Scholar] [CrossRef]
  50. Long, W.; Fu, L. Hydrothermal synthesis of ZnO flower-reduced graphene oxide composite for electrochemical determination of ascorbic acid. Fuller. Nanotub. Carbon Nanostruct. 2017, 25, 404–409. [Google Scholar] [CrossRef]
  51. Saksena, K.; Shrivastava, A.; Kant, R. Chiral analysis of ascorbic acid in bovine serum using ultrathin molecular imprinted polyaniline/graphite electrode. J. Electroanal. Chem. 2017, 795, 103–109. [Google Scholar] [CrossRef]
Polymers 11 01346 sch001 550
Scheme 1. Schematic representation of polyaniline (PANI) electrode preparation and electrochemical oxidation of ascorbic acid (AA). Dodecylbenzene sulfonic acid (DBSA).
Scheme 1. Schematic representation of polyaniline (PANI) electrode preparation and electrochemical oxidation of ascorbic acid (AA). Dodecylbenzene sulfonic acid (DBSA).
Polymers 11 01346 sch001
Polymers 11 01346 sch002 550
Scheme 2. Interconversion of PANI into its different forms through oxidation reduction [32].
Scheme 2. Interconversion of PANI into its different forms through oxidation reduction [32].
Polymers 11 01346 sch002
Polymers 11 01346 g001 550
Figure 1. (a) Cyclic voltammograms recorded on Au-disc electrode at scan rate of 50 mV/s during polymerization of aniline from an acidic solution containing DBSA. (b) Cyclic voltammogram of the PANI film recorded in 1 M sulfuric acid at scan rate of 50 mV/s, indicating the interconversion of PANI film between its reduced leucoemeraldine (LE), semi-oxidized and conducting emeraldine salt (ES) and oxidized pernagraniline (PG) forms.
Figure 1. (a) Cyclic voltammograms recorded on Au-disc electrode at scan rate of 50 mV/s during polymerization of aniline from an acidic solution containing DBSA. (b) Cyclic voltammogram of the PANI film recorded in 1 M sulfuric acid at scan rate of 50 mV/s, indicating the interconversion of PANI film between its reduced leucoemeraldine (LE), semi-oxidized and conducting emeraldine salt (ES) and oxidized pernagraniline (PG) forms.
Polymers 11 01346 g001
Polymers 11 01346 g002 550
Figure 2. Fourier-transform infrared spectroscopy (FTIR) spectrum of the synthesized PANI.
Figure 2. Fourier-transform infrared spectroscopy (FTIR) spectrum of the synthesized PANI.
Polymers 11 01346 g002
Polymers 11 01346 g003 550
Figure 3. Scanning electron microscopy (SEM) image of (a) undoped PANI (b) PANI doped with DBSA and sulfuric acid.
Figure 3. Scanning electron microscopy (SEM) image of (a) undoped PANI (b) PANI doped with DBSA and sulfuric acid.
Polymers 11 01346 g003
Polymers 11 01346 g004 550
Figure 4. Thermogravimetric analysis (TGA) plot of the synthesized PANI.
Figure 4. Thermogravimetric analysis (TGA) plot of the synthesized PANI.
Polymers 11 01346 g004
Polymers 11 01346 g005 550
Figure 5. Cyclic voltammograms of (a) bare and (b) PANI modified Au disc electrodes, recorded in 4 mM K3Fe(CN)6 /1 M KNO3 at different scan rates (20–150 mVs−1). Inset: Dependence of anodic peak current on square root of scan rate.
Figure 5. Cyclic voltammograms of (a) bare and (b) PANI modified Au disc electrodes, recorded in 4 mM K3Fe(CN)6 /1 M KNO3 at different scan rates (20–150 mVs−1). Inset: Dependence of anodic peak current on square root of scan rate.
Polymers 11 01346 g005
Polymers 11 01346 sch003 550
Scheme 3. Sensing mechanism of AA by PANI. Charge neutrality is retained by dopant ions.
Scheme 3. Sensing mechanism of AA by PANI. Charge neutrality is retained by dopant ions.
Polymers 11 01346 sch003
Polymers 11 01346 g006 550
Figure 6. pH effect on the oxidative-current peak of the PANI electrode in AA solution (4mM). at 50 mVs−1.
Figure 6. pH effect on the oxidative-current peak of the PANI electrode in AA solution (4mM). at 50 mVs−1.
Polymers 11 01346 g006
Polymers 11 01346 g007 550
Figure 7. Cyclic voltammograms of the PANI modified electrode, in a solution of 4 mM AA in 0.1 M (pH = 4) phosphate buffer solution (PBS), at different scan rates (10 to 110 mV/s).
Figure 7. Cyclic voltammograms of the PANI modified electrode, in a solution of 4 mM AA in 0.1 M (pH = 4) phosphate buffer solution (PBS), at different scan rates (10 to 110 mV/s).
Polymers 11 01346 g007
Polymers 11 01346 g008 550
Figure 8. (a) Electro-chemical response of bare Au disc and PANI modified electrode towards 4 mM AA in 0.1 M PBS (pH = 4) at scan rate of 50 mV s−1. (b) Cyclic voltammograms of PANI modified electrode recorded in the presence of various AA concentrations (2–14 mM) in 0.1 M PBS (pH = 4) at scan rate of 50 mV s−1. (c) Linear sweep voltammetry of the PANI modified electrode in the presence of various AA concentrations (2–14 mM in 0.1 M PBS (pH = 4)) at scan rate of 50 mV s−1.
Figure 8. (a) Electro-chemical response of bare Au disc and PANI modified electrode towards 4 mM AA in 0.1 M PBS (pH = 4) at scan rate of 50 mV s−1. (b) Cyclic voltammograms of PANI modified electrode recorded in the presence of various AA concentrations (2–14 mM) in 0.1 M PBS (pH = 4) at scan rate of 50 mV s−1. (c) Linear sweep voltammetry of the PANI modified electrode in the presence of various AA concentrations (2–14 mM in 0.1 M PBS (pH = 4)) at scan rate of 50 mV s−1.
Polymers 11 01346 g008
Polymers 11 01346 g009 550
Figure 9. Chronoamperometry of (a) a bare Au-disc and (b) a PANI modified electrode recorded upon sequential addition of AA (0.05 mM) in 0.1 PBS (pH=4) at a constant voltage of 0.24 V. Inset: dependence of current on AA concentration.
Figure 9. Chronoamperometry of (a) a bare Au-disc and (b) a PANI modified electrode recorded upon sequential addition of AA (0.05 mM) in 0.1 PBS (pH=4) at a constant voltage of 0.24 V. Inset: dependence of current on AA concentration.
Polymers 11 01346 g009
Polymers 11 01346 g010 550
Figure 10. Chronoamperometric response of a PANI electrode to successive addition of 0.3 mM AA, 0.3 mM dopamine (DA), 0.3 mM uric acid (UA), 0.3 mM glucose in 0.1 M PBS at 0.24 V applied potential.
Figure 10. Chronoamperometric response of a PANI electrode to successive addition of 0.3 mM AA, 0.3 mM dopamine (DA), 0.3 mM uric acid (UA), 0.3 mM glucose in 0.1 M PBS at 0.24 V applied potential.
Polymers 11 01346 g010
Polymers 11 01346 g011 550
Figure 11. Plot of the current peak of five electrodes modified with PANI.
Figure 11. Plot of the current peak of five electrodes modified with PANI.
Polymers 11 01346 g011
Table
Table 1. Comparison of synthesized PANI electrode performance with previously reported data.
Table 1. Comparison of synthesized PANI electrode performance with previously reported data.
ElectrodeLinearity (mM)LOD/(μmol·L–1)Reference
Cu4(OH)6SO4 Nanorods0.017–66.4[46]
Fe3O4/r-GO/GC0.3–7.220[47]
Poly(DB71)/GC0.001–21[48]
MWNTs/MGF/GC0.1–618.28[49]
ZnO–GO/GC0.005–21.2[50]
(DBSA)-doped nanoPANI/SPCPE0.5–88.3[24]
PANI-FSA/PGE0.001–0.11[51]
DBSA and H2SO4 doped PANI / Au-disc0.05–0.50.0267This work
GO: graphene oxide, GC: glassy carbon, DB71: direct blue 71, MWNT: multiwall nano tubes, MGF: mesocellular graphene, SPE: screen ptinted carbon paste electrode, FSA/PGE: ferrocene sulfonic acid /pencil graphene oxide electrode.
Table
Table 2. Reproducibility of the PANI electrode for sensing AA.
Table 2. Reproducibility of the PANI electrode for sensing AA.
Electrode12345MeanSDRSD (%)
Peak Current (µA)107.4107.3106.3105.3104.4106.121.271.1964

Share and Cite

MDPI and ACS Style

Bilal, S.; Akbar, A.; Shah, A.-u.-H.A. Highly Selective and Reproducible Electrochemical Sensing of Ascorbic Acid Through a Conductive Polymer Coated Electrode. Polymers 2019, 11, 1346. https://doi.org/10.3390/polym11081346

AMA Style

Bilal S, Akbar A, Shah A-u-HA. Highly Selective and Reproducible Electrochemical Sensing of Ascorbic Acid Through a Conductive Polymer Coated Electrode. Polymers. 2019; 11(8):1346. https://doi.org/10.3390/polym11081346

Chicago/Turabian Style

Bilal, Salma, Ayesha Akbar, and Anwar-ul-Haq Ali Shah. 2019. "Highly Selective and Reproducible Electrochemical Sensing of Ascorbic Acid Through a Conductive Polymer Coated Electrode" Polymers 11, no. 8: 1346. https://doi.org/10.3390/polym11081346

APA Style

Bilal, S., Akbar, A., & Shah, A. -u. -H. A. (2019). Highly Selective and Reproducible Electrochemical Sensing of Ascorbic Acid Through a Conductive Polymer Coated Electrode. Polymers, 11(8), 1346. https://doi.org/10.3390/polym11081346

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop