Upcycling Biodegradable PVA/Starch Film to a Bacterial Biopigment and Biopolymer
Next Article in Special Issue
Solid-Phase Extraction of Active Compounds from Natural Products by Molecularly Imprinted Polymers: Synthesis and Extraction Parameters
Previous Article in Journal
Effect of Eco-Friendly Peanut Shell Powder on the Chemical Resistance, Physical, Thermal, and Thermomechanical Properties of Unsaturated Polyester Resin Composites
Previous Article in Special Issue
Superabsorbents and Their Application for Heavy Metal Ion Removal in the Presence of EDDS
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 13
Issue 21
10.3390/polym13213691
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Synthesis, Characterization and Application of Polypyrrole Functionalized Nanocellulose for the Removal of Cr(VI) from Aqueous Solution

by
Norah Salem Alsaiari
1,
Khadijah Mohammedsaleh Katubi
1,*,
Fatimah Mohammed Alzahrani
1,*,
Abdelfattah Amari
2,3,*,
Haitham Osman
2,
Faouzi Ben Rebah
4 and
Mohamed A. Tahoon
5,6
1
Chemistry Department, College of Science, Princess Nourah Bint Abdulrahman University, Riyadh 11671, Saudi Arabia
2
Department of Chemical Engineering, College of Engineering, King Khalid University, Abha 61411, Saudi Arabia
3
Research Laboratory of Energy and Environment, Department of Chemical Engineering, National School of Engineers, Gabes University, Gabes 6072, Tunisia
4
Higher Institute of Biotechnology of Sfax (ISBS), Sfax University, P.O. Box 263, Sfax 3000, Tunisia
5
Department of Chemistry, College of Science, King Khalid University, P.O. Box 9004, Abha 61413, Saudi Arabia
6
Chemistry Department, Faculty of Science, Mansoura University, Mansoura 35516, Egypt
*
Authors to whom correspondence should be addressed.
Polymers 2021, 13(21), 3691; https://doi.org/10.3390/polym13213691
Submission received: 7 October 2021 / Revised: 22 October 2021 / Accepted: 23 October 2021 / Published: 26 October 2021
(This article belongs to the Special Issue Functional Polymeric Adsorbents)
Browse Figures
Versions Notes

Abstract

:
Heavy metals are toxic substances that pose a real danger to humans and organisms, even at low concentration. Therefore, there is an urgent need to remove heavy metals. Herein, the nanocellulose (NC) was synthesized by the hydrolysis of cellulose using sulfuric acid, and then functionalized using polypyrrole (ppy) through a polymerization reaction to produce polypyrrole/nanocellulose (ppy/NC) nanocomposite. The synthesized nanocomposite was characterized using familiar techniques including XRD, FT-IR, SEM, TEM, and TGA. The obtained results showed a well-constructed nanocomposite with excellent thermal stability in the nano-sized scale. The adsorption experiments showed that the ppy/NC nanocomposite was able to adsorb hexavalent chromium (Cr(VI)). The optimum pH for the removal of the heavy metal was pH 2. The interfering ions showed minor effect on the adsorption of Cr(VI) resulted from the competition between ions for the adsorption sites. The adsorption kinetics were studied using pseudo 1st order and pseudo 2nd order models indicating that the pseudo second order model showed the best fit to the experimental data, signifying that the adsorption process is controlled by the chemisorption mechanism. Additionally, the nanocomposite showed a maximum adsorption capacity of 560 mg/g according to Langmuir isotherm. The study of the removal mechanism showed that Cr(VI) ions were removed via the reduction of high toxic Cr(VI) to lower toxic Cr(III) and the electrostatic attraction between protonated ppy and Cr(VI). Interestingly, the ppy/NC nanocomposite was reused for Cr(VI) uptake up to six cycles showing excellent regeneration results. Subsequently, Cr(VI) ions can be effectively removed from aqueous solution using the synthesized nanocomposite as reusable and cost-effective adsorbent.

1. Introduction

Heavy metals pollution is becoming a serious environmental problem around the world [1]. Various toxic metals can cause serious problems to human and marine organisms [2]. Among these metals, chromium (Cr) is considered to be one of the most dangerous metals. Cr naturally exists in two oxidation states Cr(VI) and Cr(III) [3]. The two oxidation states have different mobilities and poisonousness. Cr(III) is stated to be 500 times less poisonous than Cr(VI) [4]. At low quantities, Cr(III) is less hazardous micronutrient and is required for body metabolism [5]. In contrast, Cr(VI) exhibits a variety of toxic, mutagenic, and carcinogenic effects to humans. It is expected to cause very dangerous chromosomal mutations by modifying DNA transcription steps [6]. Additionally, Cr(VI) ions can cause gastric, liver, and kidney damage as well as lung cancer [7].
Generally, photography, textile industries, fertilizers production, wood preservation, chrome coating, leather tanning, stainless steel production, and pigment manufacturing are the main sources of Cr(VI) ions [8]. Thus, the treatment of wastewater generated by these industries is crucial to prevent pollution to make the environment safe and clean. In recent years, the removal of Cr (VI) ions from wastewaters before their release into the environment has been considered as a major challenge facing scientists. The treatment strategy aims to reduce Cr(VI) concentrations from water/wastewater to acceptable levels. According to the World Health Organization (WHO), the permitted level of Cr(VI) ions is 50.0 µg/L for drinking water is 50.0 µg/L [9], while this level is 5.0 µg/L and 200.0 µg/L for underground water and industrial wastewater, respectively, according to European Union [10].
The removal of Cr(VI) ions from aqueous solutions was achieved using different techniques such as membrane separation, reverse osmosis, solvent extraction, ion exchange, reduction, chemical and electrochemical precipitations, dialysis, and adsorption [11,12,13,14,15,16]. Among all methods, adsorption is widely used for the removal of Cr(VI) ions from aqueous solutions due to many reasons such as ease regeneration of adsorbents, high efficiency, simple operation, and cost-effectiveness [17]. However, the using of conventional adsorbents for the removal of Cr (VI) ions face many problems such as insufficient hydrophilic surface and functional groups that led to secondary contamination besides the low adsorption capacity due to the low surface area [18]. These limitations of conventional adsorbents can be overcome by using nanomaterials (NMs) as adsorbents. NMs have exceptional properties such as high surface area providing high capacity for metal capturing, ease synthesis, simple functionalization, and low cost [19]. However, the using of NMs as adsorbents for the removal of metals from aqueous solutions was associated with poisonous problems [20]. So, eco-friendly NMs such as nanostructured polysaccharide have been recently examined as friendly adsorbents for the removal of metals from aqueous solutions [21,22]. Interestingly, cellulose is one of the most attractive materials useful as adsorbents to remove organic and inorganic pollutants from wastewater. In this context, the developments of the use of nanocellulose for various applications in environmental remediation, such as its use as adsorbent for enhanced and selective capturing of metallic ions, are well documented in the literature [23,24,25]. However, the breakdown and agglomeration of cellulose in water limits its use as adsorbent. This limitation can be overcome by the chemical modification of cellulose using polymeric material via the OH groups. This chemical modification of cellulose helps in increasing the adsorption capacity of nanocellulose besides the increasing of adsorbent mechanical strength [26]. Among various polymers, polypyrrole (ppy) has received considerable interest because of its interesting properties (excellent chemical stability, conductivity, biocompatibility, low oxidation potential, easy synthesis, low cost, etc.) and its good compatibility with different nanoparticles. The use of ppy to adsorb pollutants has been reported as adsorbent for the removal of metals. Additionally, ppy was used for the modification of magnetic Fe3O4/SiO2 nanocomposite for the enhanced adsorption of Congo red dye and Cr(VI) ions [27]. However, its use in large scale wastewater treatment processes is limited by its poor processability and lack of mechanical properties. Therefore, the recorded disadvantages can be eliminated by compositing ppy with other materials (biological materials, chemical polymers, agro-industrial wastes, etc.). Interestingly, the ppy is very suitable for the functionalization of nanocellulose due to good ion exchange performance and high chemical stability [28].
Herein, the nanocellulose was synthesized via the hydrolysis of cellulose using sulfuric acid followed by the functionalization of nanocellulose by the ppy polymer to form the nanocomposite (ppy/NC). The ppy/NC nanocomposite was characterized using different techniques and examined for the removal of Cr(VI) ions from water.

2. Materials and Methods

2.1. Chemicals

Cellulose with high purity was supplied from HiMedia. Sulfuric acid (H2SO4), ammonium persulfate ((NH4)2S2O8), and pyrrole were supplied from Aladdin (Shanghai, China). Hydrochloric acid (HCl) was supplied from Winlab Chemical (India). Potassium dichromate (K2Cr2O7) was supplied from Sigma-Aldrich (Schnelldorf, Germany). All chemicals were used as received without any modification. Distilled water was used for the preparation of all solutions.

2.2. Nanocellulose Synthesis

Nanocellulose (NC) was synthesized as described in the literature [29] with some modifications. Firstly, a colloidal solution of cellulose was prepared by suspending 20.0 g of cellulose powder in water followed by hydrolysis process in which the colloidal solution was treated by 60 mL of 65.0% sulfuric acid with continuous stirring for 4.0 h at a temperature of 40 °C. Then, the suspension was centrifuged for 10 min at 8000× g rpm followed by dialysis to remove the excess of acid. Then, the suspension was dialyzed against deionized water using membranes of 12,000–14,000 Da molecular weight cutoff until the neutral pH value was achieved. The obtained suspension was finally ultra-sonicated for 45 min in an ice bath then stored at a temperature of 4 °C. Subsequently, the suspension was ready to be used in the next step.

2.3. Synthesis of Nanocellulose/Polypyrrole Nanocomposite

Firstly, the polypyrrole was synthesized via the polymerization of pyrrole (1.35 mL of pyrrole in 200 mL of water) by using (NH4)2S2O8 (40.0 mL of 0.15 M) with continuous stirring until the color changed from white to black. The pyrrole was mixed with the suspension solution of nanocellulose under sonication process for 40 min at 3 °C using a tip sonicator at a fixed power of 30 W. Then, the mixture was reserved for half-hour at a temperature of 3.0 °C followed by the removal of the top layer from the mixture. Finally, the lyophilization at −80 °C and 20 Pa besides the solvent exchange with t-butanol was used to get the powder of ppy/NC nanocomposite. The obtained nanocomposite was stored at room temperature until use for characterization and application.

2.4. Adsorption Experiments

The adsorption experiments were conducted by mixing the solution of Cr(VI) with the adsorbent at certain conditions of initial concentration, adsorbent dosage, contact time, and pH in shaker at 200 rpm. After each adsorption experiment, the adsorbent was separated using a 0.45 µm filter and the remaining solution was examined for the presence of Cr(VI) ions using UV spectrophotometer (λmax = 540 nm) after a complex formation between chromium ions and 1,5-diphenylcarbazide. To study the pH effect on the adsorption, 60 mL of Cr(VI) solution (100 mg/L) was mixed with 15 mg of adsorbent at different pH values, ranging from 2.0 to 8.0. Additionally, the removal efficiency of Cr(VI) ions was determined in the presence of competing ions (NaCl, Ca2+, Zn2+, CO32−, PO43−, and SO42−) added at 0.1 M. To study the adsorption kinetics, 300 mL of Cr(VI) ions solutions with different initial concentrations ranged from 100 mg/L to 200 mg/L were mixed with 75 mg of adsorbent at a pH of 2. To study the adsorption isotherm, Cr(VI) ions solutions with different initial concentrations ranged from 50 mg/L to 300 mg/L were mixed with the adsorbent at pH of 2. The adsorption capacity (qe) of the adsorbent was calculated using Equation (1).
qe = ((Co − Ce)/m) × V,
where Co, Ce, m, and V denote the initial concentration (mg/L), equilibrium concentration (mg/L), the mass of adsorbent (g), and volume of the solution, respectively. The removal percentage (%) was calculated using Equation (2).
Removal (%) = (Co − Ce/Co) × 100
Moreover, the reusability of ppy/NC nanocomposite for the removal of Cr(VI) ions was studied up to five successive cycles using 1 M HCl as eluent. In each cycle, 60 mL of metallic ions solution was mixed with 15.0 mg of the adsorbent and agitated for 1 day followed by the collection of the adsorbent. Then, the adsorbent was regenerated using the eluent solution for 1.0 h. After that, the adsorbent was washed using water until neutral pH and subsequently, the adsorbent was ready for the next adsorption–desorption cycle. For errors determination, all experiments were done triplicate.

3. Results and Discussion

3.1. The Characterization of ppy/NC Nanocomposite

The synthesized materials including NC, ppy, and ppy/NC nanocomposite were characterized using the familiar techniques (FT-IR, XRD, TGA, SEM, and TEM). For the determination of functional groups, FT-IR spectra were shown in Figure 1a. According to Figure 1a, the synthesized NC showed the characteristic cellulose absorption bands like the peaks at 1058 cm−1, 2896 cm−1, and 3346 cm−1 that are attributed to the stretching vibrations of C–O–C, CH2, and OH, respectively [30].
However, the FT-IR of ppy/NC nanocomposite showed only the appearance of ppy representative peaks like band of N–H wagging at 850 cm−1, C–H in-plane bending at 966 cm−1, and C–H out-plane bending at 1035 cm−1 [31,32]. Additionally, the peak at 1166 cm−1 is attributed to the pyrrole ring breathing while the peak at 1306 cm−1 is attributed to C–N in-plane deformation. Additionally, the stretching vibrations of C–N and C–C bonds were represented by the peaks at 1457 cm−1 and 1555 cm−1, respectively. It is clear that the ppy chain vibrations were affected by the H-bond formation between NH groups of pyrrole ring and OH groups of NC that caused blue shift of peaks compared to the ppy peaks [33]. To study the crystallinity of the synthesized materials, XRD pattern was performed as shown in Figure 1b. According to Figure 1b, cellulose showed the appearance of major three peaks at angle of 2θ = 34.05, 16.45, and 22.84. From the diffractogram of ppy and ppy/NC, there was a slight difference at 2θ= 22.84 due to the overlap of ppy peak [34]. Additionally, the cellulose crystalline order was not affected by the hydrolysis reaction using sulfuric acid [35]. The amorphous nature of the nanocomposite was confirmed from the amorphous region at 2θ = 22.84 that is related to ppy as indicated from XRD of pure ppy [36]. To study the thermal stability of synthesized materials, thermogravimetric analysis (TGA) of materials was conducted by heating the materials up to 600 °C in argon gas atmosphere as shown in Figure 1c. According to Figure 1c, ppy showed a weight loss of 6% when the temperature raised to 100 °C due to the evaporation of water content. However, the ppy/NC nanocomposite showed weight loss of 4% when the temperature raised to 200 °C due to the evaporation of water residues. At 225 °C, there was a sharp weight loss resulting from thermal decomposition of the pyrolysis of NC. When the temperature was raised to 350 °C, ppy/NC showed a small weight loss due to the decomposition of organic matter of the nanocomposite (cellulose and polypyrrole). Subsequently, the decomposition of organic matter was started above 225 °C and completed at 600 °C (53% wt). The TGA results indicated the high thermal stability of the synthesized ppy/NC nanocomposite. We can conclude that the combination between ppy and cellulose enhances the composite thermal stability. Additionally, Figure 1d showed the zeta potential measurement of the synthesized ppy/NC nanocomposite. According to Figure 1d, the isoelectric point occurred at a value below 6. This point is the zero charge, below which the protonation of nitrogen centers was achieved which eased the attraction between cations and anions.
To study the surface morphology of the nanocomposite, SEM images at different magnification as well as TEM images were carried out (Figure 2). Figure S1 (Supplementary Material) showed the SEM image of unmodified nanocellulose with smooth surface. Figure 2a,b showed the SEM images of ppy/NC nanocomposite at different resolutions. SEM images of ppy/NC nanocomposite indicated the homogenous and uniform appearance of the particles with a spherical-like shape in the range of nanometer that help the capture of more toxic metals due to the high surface area. Comparing the SEM images of NC and ppy/NC nanocomposite, the surface of NC was greatly changed due to the introduction of ppy indicating the successful modification of NC surface.
Figure S2 (Supplementary Material) showed the SEM image of ppy/NC nanocomposite after the adsorption of Cr(VI) ions. Figure S2 showed that the surface of the nanocomposite became smooth comparing to the nanocomposite surface due to the capturing of metal ions. Figure 2c showed the TEM image of the nanocomposite. According to Figure 2d, the nanoparticles of nanocellulose are agglomerated in some parts and separated in the others. Additionally, there is a major uniform distribution of the nanocellulose particles in the nanometer range. As concluded from the TEM image, the average size of nanocellulose particles is 40 nm to 50 nm.

3.2. Effect of pH on Cr(VI) Adsorption

The pH value of solution is a critical factor affecting the adsorption behavior [37] specially for Cr(VI) ions. Therefore, the pH effect on the adsorption of Cr(VI) on the surface of ppy/NC nanocomposite was studied at pH ranging from 2 to 8 as shown in Figure 3. According to Figure 3a, the ppy/NC nanocomposite showed the highest removal efficiency for Cr(VI) ions at pH value of 2 (98%) while this removal efficiency was decreased gradually by increasing pH value until reached its lowest efficiency at pH 8 (32%). These results of pH effect on the adsorption could be interpreted according to the ionic behavior of chromium ions at different pH as illustrated in Figure 3b.
According to Figure 3b, Cr2O72− and HCrO4− are the two oxidation states of chromium ions in the pH range of 2 to 6 while at higher pH the chromium phase becomes CrO42− [38]. Subsequently, at pH between 2 and 6, the adsorption of Cr(VI) ions exists from the electrostatic attraction between the positively charged adsorbent and the negatively charged chromium species. Additionally, the functionalization of nano-cellulose with polypyrrole helps the ion exchange between the adsorbent and chromium species that increases the adsorption efficiency. However, at the pH value > 6, there was a great competition between the OH− ions and negatively charged chromium species for the adsorption sites on the adsorbent surface decreasing the adsorption efficiency. From the study of the pH effect, we can conclude that the pH increase changed the adsorption of Cr(VI) ions on the surface of ppy/NC nanocomposite from the electrostatic attraction to the electrostatic repulsion. In other words, the adsorption was changed from promotion to competition which would cause the decrease of the removal efficiency.

3.3. Effect of Co-Existing Ions on Cr(VI) Removal

Different ions such as NaCl, Ca2+, Zn2+, CO32−, PO43−, and SO42− may exist in real wastewater and could affect the adsorption of Cr(VI) ions [39,40]. So, the effect of different co-existing ions on the adsorption of Cr(VI) ions on the surface of ppy/NC nanocomposite was studied in the presence of 0.1 M of each ion as shown in Figure 4.
According to Figure 4, the removal efficiency of Cr(VI) ions was 98% in the absence of any interfering ions. Then, this removal efficiency was decreased on the addition of different ions in the order of NaCl > Ca2+ > Zn2+ > CO32− > PO43− > SO42− with removal efficiencies of 77%, 72%, 68%, 59%, 55%, and 54%, respectively. This decrease in the removal efficiency of Cr(VI) ions was attributed to the competition of interfering ions with chromium ions for the adsorption sites on the adsorbent surface. This order of removal efficiencies is attributed to the differences in the solvated ionic radii between the co-existing ions. Generally, small ions have the ability to reach the adsorption sites easily and compete with toxic metals leading to the drop of the removal efficiency of this metal. According to these results, the ppy/NC nanocomposite can be efficiently used for the removal of hexavalent chromium ions even in the presence of interfering ions.

3.4. Adsorption Kinetics

To study the contact time effect on the adsorption of Cr(VI) on the surface of ppy/NC nanocomposite, the adsorption capacities were studied at different time intervals from 0 to 35 h using different initial concentrations of chromium ions as shown in Figure 5a. According to Figure 5a, the first 3 h showed a rapid increase of the adsorption capacity followed by a slow increase of this capacity until it reached the equilibrium. The rapid increase of adsorption capacity during the first hours could be attributed to the availability of large number of active sites for the uptake of toxic ions [41]. After that, there was a slow increase in the adsorption capacity due to the repulsion between already adsorbed ions on the adsorbent and the other ions until reach the equilibrium at which the adsorbent surface becomes saturated, and the time does not have a significant effect on the adsorption capacity.
The two kinetic models pseudo 1st order and pseudo 2nd order were used to study the adsorption kinetics of Cr(VI) ions on the surface of ppy/NC nanocomposite. The linear form of pseudo 1st order and pseudo 2nd order is given by Equations (3) and (4), respectively.
ln (qe − qt) = ln qe − k1t
t/qt = (1/k2qe2) + t/qe
where k1 (1/min) and k2 (g/mg·min) are the rate constants for pseudo 1st order model and pseudo 2nd order model, respectively. The two constants can be calculated from the slop and intercept of the Equations (3) and (4) plots as shown in Figure 5b,c. The kinetic parameters for Cr(VI) removal on the surface of ppy/NC were listed in Table 1.
According to data in Table 1, the correlation coefficient (R2) value indicated that the adsorption kinetic data were more fitted with the pseudo 2nd order model than the pseudo 1st order model. This means that the pseudo 2nd order model is more suitable to describe the adsorption mechanism of Cr(VI) ions on the surface of ppy/NC nanocomposite. These results indicated that the chemical sorption is the essential mechanism of Cr(VI) removal on the surface of ppy/NC nanocomposite rather than a usual mass transport [42,43]. Additionally, several previous works on the adsorption of Cr(VI) ions showed the applicability of pseudo 2nd order as a better model for the description of the removal mechanism than other kinetic models [44,45,46,47].

3.5. Adsorption Isotherm

The interaction between the adsorbent surface and toxic particles can be well-interpreted by the study of the adsorption isotherms. The two isotherms models Freundlich and Langmuir were used to study the experimental data of Cr(VI) removal on the surface of ppy/NC nanocomposite. Freundlich and Langmuir isotherms can be described in the linearized form according to Equations (5) and (6), respectively.
ln qe = ln KF + 1/n ln Ce,
1/qe = (1/qmkL)Ce + 1/qm,
where 1/n, KF, KL, and qm denote the adsorption intensity, Freundlich constant, Langmuir constant, and the maximum adsorption capacity, respectively. It is well-known that Freundlich isotherm suggests the exponential distribution of the adsorption sites as well as the heterogeneous properties of the surface while the Langmuir isotherm suggests the presence of finite amount of identical adsorption sites on the surface of adsorbent as well as the formation of monolayer of adsorbates [48,49]. The fitting of experimental data to Freundlich and Langmuir isotherm models are shown in Figure 6 and their parameters were tabulated in Table 2. The Freundlich and Langmuir parameters were calculated by the plot of ln qe against ln Ce and Ce/qe against Ce, respectively. According to the results, 1/n value is less than 1 indicating the favorable adsorption of Cr(VI) on the surface of ppy/NC nanocomposite [50,51].
The values of correlation coefficients (R2) were 0.948 for Freundlich isotherm and 0.997 for Langmuir isotherm indicated that the adsorption of Cr(VI) can be better defined by the Langmuir isotherm model. The isotherm results indicated that the capture of Cr(VI) ions on the surface of ppy/NC nanocomposite was reached via a monolayer adsorption by identical adsorption active sites [52,53]. Moreover, the maximum adsorption capacity of the nanocomposite was reached 560 mg/L toward Cr(VI) ions that is considered excellent results when compared to other adsorbents as discussed in the comparative study section.

3.6. Discussion on the Mechanism of Removal

To understand the mechanism of the removal of Cr(VI) ions on the surface of ppy/NC nanocomposite very well, XPS spectra of the nanocomposite before and after adsorption are reported in Figure 7. Figure 7a shows the scan survey of the nanocomposite. According to Figure 7a, the C 1s, N1s, and O 1s peaks appeared at binding energies of 285.0 eV, 400.0 eV, and 532.4, respectively [54]. A peak related to Cr 2p was appeared after the capturing process indicated the uptake of the metal. This peak appeared as a twin attributed to Cr 2p3/2 and Cr 2p1/2 at 577.0 and 586.9 eV, respectively. The oxygen content of the adsorbed chromium ions made the C/O ratio of the composite increased considerably after the adsorption as shown in the O 1s peak. Additionally, the N 1s spectra of the nanocomposite were completed before and after the metal uptake as shown in Figure 7b.
According to Figure 7b, N+, NH-, and N- peaks were observed with molar ratios equal to 13.8, 28.5, and 57.7%, respectively. These ratios by the action of strong oxidation of Cr(VI) were increased to 30.4, 24.4, and 45.2%, respectively. Moreover, the Cr 2p spectra of the nanocomposite were performed to explain the mechanism of metal removal deeply as shown in Figure 7c. After the adsorption, the nanocomposite showed the appearance of Cr (III) and Cr (VI) peaks with molar ratios of 59.7% and 40.3%, respectively, meaning that the ppy electrons reduces the hexavalent chromium to the trivalent chromium and the adsorption process included both ions. This removal mechanism was described by many previous studies [55,56,57,58].

3.7. Reusability Study

For the large-scale application of any adsorbent, its reusability and regeneration must be studied as it is very important economically, and a good reusability may reduce the overall cost of treatment [59]. Subsequently, the reusability of ppy/NC nanocomposite for the removal of Cr(VI) ions was studied for six successive cycles as shown in Figure 8. Each cycle is consisting of adsorption process followed by desorption process. The adsorbent was agitated with the metallic ion solution followed by the treatment of the adsorbent surface with 1 M of HCl as eluent. Finally, the adsorbent became ready for the next cycle.
According to Figure 8, the ppy/NC nanocomposite showed good reusability results for the removal of Cr(VI) ions up to six cycles. The first cycle showed the highest removal efficiency due to the existence of fresh unused adsorption sites on the surface of adsorbent. After that, the removal efficiency was decreased gradually due to the destroyed non-renewable sites during each cycle. The last cycle showed a removal efficiency of 70% indicated the excellent stability of the nanocomposite toward the removal of Cr(VI) ions. These results indicated the effective regeneration of adsorption sites during the adsorption process which reduces the overall cost of process and encourages the application of the nanocomposite for large scale treatment.

3.8. Comparative Study

To assess the performance of ppy/NC as an adsorbent for the removal of Cr(VI) from aqueous solution, the adsorption capacities of previously reported adsorbents were compared with the present study as listed in Table 3. According to Table 3, the ppy/NC showed an excellent adsorption capacity toward Cr(VI) ions. This good capacity encourages its use as adsorbent for real samples treatment. Additionally, this adsorbent could be examined for the removal of many other pollutants.

4. Conclusions

In the present study, cellulose was hydrolyzed using sulfuric acid to produce the nanocellulose, and then functionalized using polypyrrole through a polymerization reaction to fabricate a nanocomposite of polypyrrole/nanocellulose (ppy/NC). The familiar techniques were used for the characterization of the nanocomposite. The crystalline nature of the synthesized NC was approved using XRD. Additionally, the nanosized cellulose was approved through SEM images. Thermal analysis study showed the excellent stability of the nanocomposite with a decomposition point at 225 °C. The synthesized nanocomposite was examined for the adsorption of Cr(VI) ions. The pH effect on the adsorption of metallic ions was studied showing an optimum at pH 2.0. Additionally, the effect of interfering ions on the removal efficiency (%) was studied with minor decrease in the Cr(VI) removal due to the competition between ions for the adsorption sites. The nanocomposite showed a maximum adsorption capacity of 560 mg/g according to Langmuir isotherm model. The study of the removal mechanism showed that the hexavalent chromium was removed via two ways of adsorption and reduction which enhanced the performance of the adsorbent. Additionally, the ppy/NC adsorbent was reused for the removal of Cr(VI) ions up to six cycles with excellent regeneration results. The comparative study of ppy/NC nanocomposite with other reported adsorbents confirmed its higher performance for Cr(VI) uptake. Hopefully, this nanocomposite is an excellent choice for water treatment and should be investigated toward additional pollutants in the near future.

Supplementary Materials

The following are available online at www.mdpi.com/2073-4360/13/21/3691/s1, Figure S1: SEM image of nanocellulose, Figure S2: SEM image of ppy/NC nanocomposite after Cr(VI) ions adsorption.

Author Contributions

Conceptualization, F.B.R.; methodology, N.S.A.; software, A.A.; validation, N.S.A. and F.M.A.; formal analysis, K.M.K.; investigation, F.M.A. and H.O.; resources, F.B.R.; data curation, F.B.R.; writing—original draft preparation, F.B.R. and H.O.; writing—review and editing, A.A.; visualization, M.A.T.; supervision, M.A.T.; project administration, A.A.; funding acquisition, N.S.A. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Deanship of Scientific Research at King Khalid University. Additionally, this research was funded by the Deanship of Scientific Research at Princess Nourah bint Abdulrahman University through the Fast-track Research Funding Program.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

The authors extend their appreciation to the Deanship of Scientific Research at King Khalid University for funding this work through the research groups program under grant number RGP.2/157/42. Additionally, this research was funded by the Deanship of Scientific Research at Princess NourahBint Abdulrahman University through the Fast-track Research Funding Program.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Kobielska, P.A.; Howarth, A.J.; Farha, O.K.; Nayak, S. Metal–organic frameworks for heavy metal removal from water. Coord. Chem. Rev. 2018, 358, 92–107. [Google Scholar] [CrossRef]
  2. Amari, A.; Alzahrani, F.M.; Mohammedsaleh Katubi, K.; Alsaiari, N.S.; Tahoon, M.A.; Rebah, F.B. Clay-polymer nanocomposites: Preparations and utilization for pollutants removal. Materials 2021, 14, 1365. [Google Scholar] [CrossRef]
  3. Rahman, Z.; Singh, V.P. The relative impact of toxic heavy metals (THMs)(arsenic (As), cadmium (Cd), chromium (Cr)(VI), mercury (Hg), and lead (Pb)) on the total environment: An overview. Environ. Monit. Assess. 2019, 191, 1–21. [Google Scholar] [CrossRef] [PubMed]
  4. Benimeli, C.S.; Polti, M.A.; Albarracín, V.H.; Abate, C.M.; Amoroso, M.J. Bioremediation Potential of Heavy Metal–Resistant Actinobacteria and Maize Plants in Polluted Soil. In Biomanagement of Metal-Contaminated Soils; Springer: Berlin/Heidelberg, Germany, 2011; pp. 459–477. [Google Scholar]
  5. Zhan, M.; Yu, H.; Li, L.; Nguyen, D.T.; Chen, W. Detection of hexavalent chromium by copper sulfide nanocomposites. Anal. Chem. 2019, 91, 2058–2065. [Google Scholar] [CrossRef] [PubMed]
  6. Du, Y.; Zhang, S.; Wang, J.; Wu, J.; Dai, H. Nb2O5 nanowires in-situ grown on carbon fiber: A high-efficiency material for the photocatalytic reduction of Cr (VI). J. Environ. Sci. 2018, 66, 358–367. [Google Scholar] [CrossRef]
  7. Kaušpėdienė, D.; Kazlauskienė, E.; Gefenienė, A.; Binkienė, R. Comparison of the efficiency of activated carbon and neutral polymeric adsorbent in removal of chromium complex dye from aqueous solutions. J. Hazard. Mater. 2010, 179, 933–939. [Google Scholar] [CrossRef]
  8. Dhal, B.; Thatoi, H.; Das, N.; Pandey, B. Chemical and microbial remediation of hexavalent chromium from contaminated soil and mining/metallurgical solid waste: A review. J. Hazard. Mater. 2013, 250, 272–291. [Google Scholar] [CrossRef]
  9. Anirudhan, T.; Nima, J.; Divya, P. Adsorption of chromium (VI) from aqueous solutions by glycidylmethacrylate-grafted-densified cellulose with quaternary ammonium groups. Appl. Surf. Sci. 2013, 279, 441–449. [Google Scholar] [CrossRef]
  10. Di Natale, F.; Erto, A.; Lancia, A.; Musmarra, D. Equilibrium and dynamic study on hexavalent chromium adsorption onto activated carbon. J. Hazard. Mater. 2015, 281, 47–55. [Google Scholar] [CrossRef]
  11. Choudhury, P.R.; Majumdar, S.; Sahoo, G.C.; Saha, S.; Mondal, P. High pressure ultrafiltration CuO/hydroxyethyl cellulose composite ceramic membrane for separation of Cr (VI) and Pb (II) from contaminated water. Chem. Eng. J. 2018, 336, 570–578. [Google Scholar] [CrossRef]
  12. Mnif, A.; Bejaoui, I.; Mouelhi, M.; Hamrouni, B. Hexavalent chromium removal from model water and car shock absorber factory effluent by nanofiltration and reverse osmosis membrane. Int. J. Anal. Chem. 2017, 2017, 7415708. [Google Scholar] [CrossRef] [PubMed]
  13. Ying, Z.; Ren, X.; Li, J.; Wu, G.; Wei, Q. Recovery of chromium (VI) in wastewater using solvent extraction with amide. Hydrometallurgy 2020, 196, 105440. [Google Scholar] [CrossRef]
  14. Farooqi, Z.H.; Akram, M.W.; Begum, R.; Wu, W.; Irfan, A. Inorganic nanoparticles for reduction of hexavalent chromium: Physicochemical aspects. J. Hazard. Mater. 2021, 402, 123535. [Google Scholar] [CrossRef]
  15. Peng, H.; Guo, J. Removal of chromium from wastewater by membrane filtration, chemical precipitation, ion exchange, adsorption electrocoagulation, electrochemical reduction, electrodialysis, electrodeionization, photocatalysis and nanotechnology: A review. Environ. Chem. Lett. 2020, 18, 2055–2068. [Google Scholar] [CrossRef]
  16. Jang, E.-H.; Pack, S.P.; Kim, I.; Chung, S. A systematic study of hexavalent chromium adsorption and removal from aqueous environments using chemically functionalized amorphous and mesoporous silica nanoparticles. Sci. Rep. 2020, 10, 1–20. [Google Scholar] [CrossRef] [PubMed]
  17. Alsaiari, N.S.; Amari, A.; Katubi, K.M.; Alzahrani, F.M.; Rebah, F.B.; Tahoon, M.A. Innovative magnetite based polymeric nanocomposite for simultaneous removal of methyl orange and hexavalent chromium from water. Processes 2021, 9, 576. [Google Scholar] [CrossRef]
  18. Hokkanen, S.; Bhatnagar, A.; Repo, E.; Lou, S.; Sillanpää, M. Calcium hydroxyapatite microfibrillated cellulose composite as a potential adsorbent for the removal of Cr (VI) from aqueous solution. Chem. Eng. J. 2016, 283, 445–452. [Google Scholar] [CrossRef]
  19. Siddeeg, S.M.; Amari, A.; Tahoon, M.A.; Alsaiari, N.S.; Rebah, F.B. Removal of meloxicam, piroxicam and Cd+2 by Fe3O4/SiO2/glycidyl methacrylate-S-SH nanocomposite loaded with laccase. Alex. Eng. J. 2020, 59, 905–914. [Google Scholar] [CrossRef]
  20. Batley, G.E.; Kirby, J.K.; McLaughlin, M.J. Fate and risks of nanomaterials in aquatic and terrestrial environments. Acc. Chem. Res. 2013, 46, 854–862. [Google Scholar] [CrossRef]
  21. Hammi, N.; El Hankari, S.; Katir, N.; Marcotte, N.; Draoui, K.; Royer, S.; El Kadib, A. Polysaccharide templated biomimetic growth of hierarchically porous metal-organic frameworks. Microporous Mesoporous Mater. 2020, 306, 110429. [Google Scholar] [CrossRef]
  22. Nasrollahzadeh, M.; Sajjadi, M.; Iravani, S.; Varma, R.S. Starch, cellulose, pectin, gum, alginate, chitin and chitosan derived (nano) materials for sustainable water treatment: A review. Carbohydr. Polym. 2021, 251, 116986. [Google Scholar] [CrossRef] [PubMed]
  23. Joseph, B.; Sagarika, V.; Sabu, C.; Kalarikkal, N.; Thomas, S. Cellulose nanocomposites: Fabrication and biomedical applications. J. Bioresour. Bioprod. 2020, 5, 223–237. [Google Scholar] [CrossRef]
  24. Zou, Y.; Zhao, J.; Zhu, J.; Guo, X.; Chen, P.; Duan, G.; Liu, X.; Li, Y. A Mussel-Inspired Polydopamine-Filled Cellulose Aerogel for Solar-Enabled Water Remediation. ACS Appl. Mater. Interfaces 2021, 13, 7617–7624. [Google Scholar] [CrossRef] [PubMed]
  25. Xia, Z.; Li, J.; Zhang, J.; Zhang, X.; Zheng, X.; Zhang, J. Processing and valorization of cellulose, lignin and lignocellulose using ionic liquids. J. Bioresour. Bioprod. 2020, 5, 79–95. [Google Scholar] [CrossRef]
  26. Yang, J.; Ma, C.; Tao, J.; Li, J.; Du, K.; Wei, Z.; Chen, C.; Wang, Z.; Zhao, C.; Ma, M. Optimization of polyvinylamine-modified nanocellulose for chlorpyrifos adsorption by central composite design. Carbohydr. Polym. 2020, 245, 116542. [Google Scholar] [CrossRef] [PubMed]
  27. Alzahrani, F.M.; Alsaiari, N.S.; Katubi, K.M.; Amari, A.; Ben Rebah, F.; Tahoon, M.A. Synthesis of Polymer-Based Magnetic Nanocomposite for Multi-Pollutants Removal from Water. Polymers 2021, 13, 1742. [Google Scholar] [CrossRef] [PubMed]
  28. Mahmud, H.N.M.E.; Huq, A.O.; binti Yahya, R. The removal of heavy metal ions from wastewater/aqueous solution using polypyrrole-based adsorbents: A review. Rsc Adv. 2016, 6, 14778–14791. [Google Scholar] [CrossRef]
  29. Lu, P.; Hsieh, Y.-L. Preparation and characterization of cellulose nanocrystals from rice straw. Carbohydr. Polym. 2012, 87, 564–573. [Google Scholar] [CrossRef]
  30. Cai, M.; Shafi, S.; Zhao, Y. Preparation of compressible silica aerogel reinforced by bacterial cellulose using tetraethylorthosilicate and methyltrimethoxylsilane co-precursor. J. Non-Cryst. Solids 2018, 481, 622–626. [Google Scholar] [CrossRef]
  31. Yuan, X.; Floresyona, D.; Aubert, P.-H.; Bui, T.-T.; Remita, S.; Ghosh, S.; Brisset, F.; Goubard, F.; Remita, H. Photocatalytic degradation of organic pollutant with polypyrrole nanostructures under UV and visible light. Appl. Catal. B Environ. 2019, 242, 284–292. [Google Scholar] [CrossRef]
  32. Wang, Y.; Zou, B.; Gao, T.; Wu, X.; Lou, S.; Zhou, S. Synthesis of orange-like Fe 3 O 4/PPy composite microspheres and their excellent Cr (VI) ion removal properties. J. Mater. Chem. 2012, 22, 9034–9040. [Google Scholar] [CrossRef]
  33. Xu, J.; Zhu, L.; Bai, Z.; Liang, G.; Liu, L.; Fang, D.; Xu, W. Conductive polypyrrole–bacterial cellulose nanocomposite membranes as flexible supercapacitor electrode. Org. Electron. 2013, 14, 3331–3338. [Google Scholar] [CrossRef]
  34. Yue, Y.; Wang, X.; Han, J.; Yu, L.; Chen, J.; Wu, Q.; Jiang, J. Effects of nanocellulose on sodium alginate/polyacrylamide hydrogel: Mechanical properties and adsorption-desorption capacities. Carbohydr. Polym. 2019, 206, 289–301. [Google Scholar] [CrossRef]
  35. Zhou, Y.; Zhang, M.; Hu, X.; Wang, X.; Niu, J.; Ma, T. Adsorption of cationic dyes on a cellulose-based multicarboxyl adsorbent. J. Chem. Eng. Data 2013, 58, 413–421. [Google Scholar] [CrossRef]
  36. Ford, E.N.J.; Mendon, S.K.; Thames, S.F.; Rawlins, J.W. X-ray diffraction of cotton treated with neutralized vegetable oil-based macromolecular crosslinkers. J. Eng. Fibers Fabr. 2010, 5, 155892501000500102. [Google Scholar] [CrossRef] [Green Version]
  37. Tang, H.; Zhang, S.; Huang, T.; Cui, F.; Xing, B. pH-Dependent adsorption of aromatic compounds on graphene oxide: An experimental, molecular dynamics simulation and density functional theory investigation. J. Hazard. Mater. 2020, 395, 122680. [Google Scholar] [CrossRef]
  38. Zhang, W.; Zhang, L.; Hua, T.; Li, Y.; Zhou, X.; Wang, W.; You, Z.; Wang, H.; Li, M. The mechanism for adsorption of Cr (VI) ions by PE microplastics in ternary system of natural water environment. Environ. Pollut. 2020, 257, 113440. [Google Scholar] [CrossRef]
  39. Yuan, C.; Zhang, Y.; Yao, J.; Liu, Q.; Kong, F.-G. Facile Synthesis of Polyethylene Glycol@ Tannin-Amine Microsphere towards Cr (VI) Removal. Polymers 2021, 13, 1035. [Google Scholar] [CrossRef] [PubMed]
  40. Khan, S.U.; Zaidi, R.; Shaik, F.; Farooqi, I.H.; Azam, A.; Abuhimd, H.; Ahmed, F. Evaluation of Fe-Mg binary oxide for As (III) adsorption—synthesis, characterization and kinetic modelling. Nanomaterials 2021, 11, 805. [Google Scholar] [CrossRef] [PubMed]
  41. Bakhtiari, N.; Azizian, S. Adsorption of copper ion from aqueous solution by nanoporous MOF-5: A kinetic and equilibrium study. J. Mol. Liq. 2015, 206, 114–118. [Google Scholar] [CrossRef]
  42. Liakos, E.V.; Mone, M.; Lambropoulou, D.A.; Bikiaris, D.N.; Kyzas, G.Z. Adsorption evaluation for the removal of nickel, mercury, and barium ions from single-component and mixtures of aqueous solutions by using an optimized biobased chitosan derivative. Polymers 2021, 13, 232. [Google Scholar] [CrossRef] [PubMed]
  43. El Kaim Billah, R.; Khan, M.A.; Wabaidur, S.M.; Jeon, B.-H.; Am, A.; Majdoubi, H.; Haddaji, Y.; Agunaou, M.; Soufiane, A. Chitosan/Phosphate Rock-Derived Natural Polymeric Composite to Sequester Divalent Copper Ions from Water. Nanomaterials 2021, 11, 2028. [Google Scholar] [CrossRef] [PubMed]
  44. Murad, H.A.; Ahmad, M.; Bundschuh, J.; Hashimoto, Y.; Zhang, M.; Sarkar, B.; Ok, Y.S. A remediation approach to chromium-contaminated water and soil using engineered biochar derived from peanut shell. Environ. Res. 2021, 204, 112125. [Google Scholar] [CrossRef] [PubMed]
  45. Mahmoud, A.; Fawzy, M.; Hosny, G.; Obaid, A. Equilibrium, kinetic, and diffusion models of chromium (VI) removal using Phragmites australis and Ziziphus spina-christi biomass. Int. J. Environ. Sci. Technol. 2021, 18, 2125–2136. [Google Scholar] [CrossRef]
  46. Gao, K.; Li, J.; Chen, M.; Jin, Y.; Ma, Y.; Ou, G.; Wei, Z. ZIF-67 derived magnetic nanoporous carbon coated by poly (m-phenylenediamine) for hexavalent chromium removal. Sep. Purif. Technol. 2021, 277, 119436. [Google Scholar] [CrossRef]
  47. Khalil, U.; Shakoor, M.B.; Ali, S.; Ahmad, S.R.; Rizwan, M.; Alsahli, A.A.; Alyemeni, M.N. Selective Removal of Hexavalent Chromium from Wastewater by Rice Husk: Kinetic, Isotherm and Spectroscopic Investigation. Water 2021, 13, 263. [Google Scholar] [CrossRef]
  48. Albadarin, A.B.; Collins, M.N.; Naushad, M.; Shirazian, S.; Walker, G.; Mangwandi, C. Activated lignin-chitosan extruded blends for efficient adsorption of methylene blue. Chem. Eng. J. 2017, 307, 264–272. [Google Scholar] [CrossRef] [Green Version]
  49. Shahnaz, T.; Patra, C.; Sharma, V.; Selvaraju, N. A comparative study of raw, acid-modified and EDTA-complexed Acacia auriculiformis biomass for the removal of hexavalent chromium. Chem. Ecol. 2020, 36, 360–381. [Google Scholar] [CrossRef]
  50. Pete, S.; Kattil, R.A.; Thomas, L. Polyaniline-multiwalled carbon nanotubes (PANI-MWCNTs) composite revisited: An efficient and reusable material for methyl orange dye removal. Diam. Relat. Mater. 2021, 117, 108455. [Google Scholar] [CrossRef]
  51. Zhao, Y.; Yang, H.; Sun, J.; Zhang, Y.; Xia, S. Enhanced Adsorption of Rhodamine B on Modified Oil-Based Drill Cutting Ash: Characterization, Adsorption Kinetics, and Adsorption Isotherm. ACS Omega 2021, 6, 17086–17094. [Google Scholar] [CrossRef]
  52. Verma, M.; Tyagi, I.; Kumar, V.; Goel, S.; Vaya, D.; Kim, H. Fabrication of GO–MnO2 nanocomposite using hydrothermal process for cationic and anionic dyes adsorption: Kinetics, isotherm, and reusability. J. Environ. Chem. Eng. 2021, 9, 106045. [Google Scholar] [CrossRef]
  53. Sintakindi, A.; Ankamwar, B. Uptake of methylene blue from aqueous solution by naturally grown daedalea africana and phellinus adamantinus fungi. ACS Omega 2020, 5, 12905–12914. [Google Scholar] [CrossRef]
  54. Wan, C.; Jiao, Y.; Li, J. Flexible, highly conductive, and free-standing reduced graphene oxide/polypyrrole/cellulose hybrid papers for supercapacitor electrodes. J. Mater. Chem. A 2017, 5, 3819–3831. [Google Scholar] [CrossRef]
  55. Wang, Z.; Wang, Y.; Cao, S.; Liu, S.; Chen, Z.; Chen, J.; Chen, Y.; Fu, J. Fabrication of core@ shell structural Fe-Fe2O3@ PHCP nanochains with high saturation magnetization and abundant amino groups for hexavalent chromium adsorption and reduction. J. Hazard. Mater. 2020, 384, 121483. [Google Scholar] [CrossRef] [PubMed]
  56. Wang, Y.; Zhao, D.; Feng, S.; Chen, Y.; Xie, R. Ammonium thiocyanate functionalized graphene oxide-supported nanoscale zero-valent iron for adsorption and reduction of Cr (VI). J. Colloid Interface Sci. 2020, 580, 345–353. [Google Scholar] [CrossRef] [PubMed]
  57. Ji, Y.; Xu, F.; Zhang, P.; Xu, Y.; Zhang, G. Green synthesis of poly (pyrrole methane)-based adsorbent for efficient removal of chromium (VI) from aqueous solution. J. Clean. Prod. 2021, 293, 126197. [Google Scholar] [CrossRef]
  58. Lei, C.; Wang, C.; Chen, W.; He, M.; Huang, B. Polyaniline@ magnetic chitosan nanomaterials for highly efficient simultaneous adsorption and in-situ chemical reduction of hexavalent chromium: Removal efficacy and mechanisms. Sci. Total Environ. 2020, 733, 139316. [Google Scholar] [CrossRef] [PubMed]
  59. Sharma, S.; Kumar, A.S.K.; Rajesh, N. A perspective on diverse adsorbent materials to recover precious palladium and the way forward. Rsc Adv. 2017, 7, 52133–52142. [Google Scholar] [CrossRef] [Green Version]
  60. Sharma, G.; Naushad, M.; Ala’a, H.; Kumar, A.; Khan, M.R.; Kalia, S.; Bala, M.; Sharma, A. Fabrication and characterization of chitosan-crosslinked-poly (alginic acid) nanohydrogel for adsorptive removal of Cr (VI) metal ion from aqueous medium. Int. J. Biol. Macromol. 2017, 95, 484–493. [Google Scholar] [CrossRef]
  61. Al-Othman, Z.A.; Ali, R.; Naushad, M. Hexavalent chromium removal from aqueous medium by activated carbon prepared from peanut shell: Adsorption kinetics, equilibrium and thermodynamic studies. Chem. Eng. J. 2012, 184, 238–247. [Google Scholar] [CrossRef]
  62. Dognani, G.; Hadi, P.; Ma, H.; Cabrera, F.C.; Job, A.E.; Agostini, D.L.; Hsiao, B.S. Effective chromium removal from water by polyaniline-coated electrospun adsorbent membrane. Chem. Eng. J. 2019, 372, 341–351. [Google Scholar] [CrossRef]
  63. Huang, D.; Liu, C.; Zhang, C.; Deng, R.; Wang, R.; Xue, W.; Luo, H.; Zeng, G.; Zhang, Q.; Guo, X. Cr (VI) removal from aqueous solution using biochar modified with Mg/Al-layered double hydroxide intercalated with ethylenediaminetetraacetic acid. Bioresour. Technol. 2019, 276, 127–132. [Google Scholar] [CrossRef]
  64. Zhang, Y.; Li, M.; Li, J.; Yang, Y.; Liu, X. Surface modified leaves with high efficiency for the removal of aqueous Cr (VI). Appl. Surf. Sci. 2019, 484, 189–196. [Google Scholar] [CrossRef]
  65. Fang, W.; Jiang, X.; Luo, H.; Geng, J. Synthesis of graphene/SiO2@ polypyrrole nanocomposites and their application for Cr (VI) removal in aqueous solution. Chemosphere 2018, 197, 594–602. [Google Scholar] [CrossRef] [PubMed]
  66. Jia, B.-B.; Wang, J.-N.; Wu, J.; Li, C.-J. “Flower-Like” PA6@ Mg (OH) 2 electrospun nanofibers with Cr (VI)-removal capacity. Chem. Eng. J. 2014, 254, 98–105. [Google Scholar] [CrossRef]
  67. Mohamed, A.; Nasser, W.; Osman, T.; Toprak, M.; Muhammed, M.; Uheida, A. Removal of chromium (VI) from aqueous solutions using surface modified composite nanofibers. J. Colloid Interface Sci. 2017, 505, 682–691. [Google Scholar] [CrossRef] [PubMed]
  68. Wang, J.; Pan, K.; He, Q.; Cao, B. Polyacrylonitrile/polypyrrole core/shell nanofiber mat for the removal of hexavalent chromium from aqueous solution. J. Hazard. Mater. 2013, 244, 121–129. [Google Scholar] [CrossRef]
  69. He, X.; Cheng, L.; Wang, Y.; Zhao, J.; Zhang, W.; Lu, C. Aerogels from quaternary ammonium-functionalized cellulose nanofibers for rapid removal of Cr (VI) from water. Carbohydr. Polym. 2014, 111, 683–687. [Google Scholar] [CrossRef]
Polymers 13 03691 g001a 550Polymers 13 03691 g001b 550
Figure 1. FT-IR (a) XRD (b), TGA (c), and zeta potential at various pH (d) of the synthesized ppy, cellulose, and ppy/NC nanocomposite.
Figure 1. FT-IR (a) XRD (b), TGA (c), and zeta potential at various pH (d) of the synthesized ppy, cellulose, and ppy/NC nanocomposite.
Polymers 13 03691 g001aPolymers 13 03691 g001b
Polymers 13 03691 g002 550
Figure 2. SEM images at different resolution (a,b) and TEM image (c) of the synthesized ppy/NC nanocomposite.
Figure 2. SEM images at different resolution (a,b) and TEM image (c) of the synthesized ppy/NC nanocomposite.
Polymers 13 03691 g002
Polymers 13 03691 g003 550
Figure 3. The effect of pH on Cr(VI) adsorption on the ppy/NC surface (a) and the abundance of Cr(VI) species in aqueous solution at pH range of 2 to 9 (b).
Figure 3. The effect of pH on Cr(VI) adsorption on the ppy/NC surface (a) and the abundance of Cr(VI) species in aqueous solution at pH range of 2 to 9 (b).
Polymers 13 03691 g003
Polymers 13 03691 g004 550
Figure 4. The effect of interfering ions on the Cr(VI) removal over the surface of ppy/NC nanocomposite.
Figure 4. The effect of interfering ions on the Cr(VI) removal over the surface of ppy/NC nanocomposite.
Polymers 13 03691 g004
Polymers 13 03691 g005 550
Figure 5. The effect of contact time at different initial Cr(VI) concentrations (a), fit of experimental data to pseudo 1st order model (b), and fit of experimental data to pseudo 2nd order model (c) for the removal of Cr(VI) ions on the surface of ppy/NC nanocomposite.
Figure 5. The effect of contact time at different initial Cr(VI) concentrations (a), fit of experimental data to pseudo 1st order model (b), and fit of experimental data to pseudo 2nd order model (c) for the removal of Cr(VI) ions on the surface of ppy/NC nanocomposite.
Polymers 13 03691 g005
Polymers 13 03691 g006 550
Figure 6. The fit of experimental data to Freundlich isotherm (a) and Langmuir isotherm (b) for the removal of Cr(VI) ions on the surface of ppy/NC nanocomposite.
Figure 6. The fit of experimental data to Freundlich isotherm (a) and Langmuir isotherm (b) for the removal of Cr(VI) ions on the surface of ppy/NC nanocomposite.
Polymers 13 03691 g006
Polymers 13 03691 g007 550
Figure 7. XPS spectra of ppy/NC nanocomposite with survey scan (a), N 1s spectra (b), and (c) Cr 2p spectra before and after adsorption process.
Figure 7. XPS spectra of ppy/NC nanocomposite with survey scan (a), N 1s spectra (b), and (c) Cr 2p spectra before and after adsorption process.
Polymers 13 03691 g007
Polymers 13 03691 g008 550
Figure 8. The reusability study of ppy/NC nanocomposite for the removal of Cr(VI) ions up to six successive cycles.
Figure 8. The reusability study of ppy/NC nanocomposite for the removal of Cr(VI) ions up to six successive cycles.
Polymers 13 03691 g008
Table
Table 1. The parameters of pseudo 1st order and pseudo 2nd order models for the removal of Cr(VI) on the surface of ppy/NC nanocomposite.
Table 1. The parameters of pseudo 1st order and pseudo 2nd order models for the removal of Cr(VI) on the surface of ppy/NC nanocomposite.
Cr(VI) Concentration (mg/L)Pseudo 1st Order Pseudo 2nd Order
qe(exp) (mg/g)qe(cal) (mg/g)K1R2qe(cal) (mg/g)K2R2
1003791720.18800.9388385.10.00310.9993
150432.11990.14330.9499443.20.00190.9988
200496.2233.20.13950.9499508.60.00180.9979
Table
Table 2. The parameters of Freundlish and Langmuir isotherm models for the removal of Cr(VI) on the surface of ppy/NC nanocomposite.
Table 2. The parameters of Freundlish and Langmuir isotherm models for the removal of Cr(VI) on the surface of ppy/NC nanocomposite.
LangmuirFreundlich
qm (mg/g)KLR2KF1/nR2
5600.23000.997350.10.09410.949
Table
Table 3. The comparison between the removal of Cr(VI) ions on the surface of ppy/NC nanocomposite and reported studies.
Table 3. The comparison between the removal of Cr(VI) ions on the surface of ppy/NC nanocomposite and reported studies.
AdsorbentAdsorption Capacity (mg/g)Ref.
ppy/NC560.0This study
Chitosan-crosslinked-poly(alginic acid) nanohydrogel26.42[60]
Activated carbon from peanut shell16.27[61]
Polyaniline-coated electrospun adsorbent membrane15.09[62]
Biochar modified with Mg/Al-layered double hydroxide intercalated with EDTA38.0[63]
Sulfuric acid modified leaves107.55[64]
Graphene/SiO2@PPy nanocomposites429.0[65]
PA6@Mg(OH)2 electrospun nanofibers296.0[66]
PAN-NH2 nanofibers138.0[67]
PAN/polypyrrole core/shell nanofiber mat75.0[68]
Ammonium-functionalized cellulose nanofibers18.0[69]
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Alsaiari, N.S.; Katubi, K.M.; Alzahrani, F.M.; Amari, A.; Osman, H.; Rebah, F.B.; Tahoon, M.A. Synthesis, Characterization and Application of Polypyrrole Functionalized Nanocellulose for the Removal of Cr(VI) from Aqueous Solution. Polymers 2021, 13, 3691. https://doi.org/10.3390/polym13213691

AMA Style

Alsaiari NS, Katubi KM, Alzahrani FM, Amari A, Osman H, Rebah FB, Tahoon MA. Synthesis, Characterization and Application of Polypyrrole Functionalized Nanocellulose for the Removal of Cr(VI) from Aqueous Solution. Polymers. 2021; 13(21):3691. https://doi.org/10.3390/polym13213691

Chicago/Turabian Style

Alsaiari, Norah Salem, Khadijah Mohammedsaleh Katubi, Fatimah Mohammed Alzahrani, Abdelfattah Amari, Haitham Osman, Faouzi Ben Rebah, and Mohamed A. Tahoon. 2021. "Synthesis, Characterization and Application of Polypyrrole Functionalized Nanocellulose for the Removal of Cr(VI) from Aqueous Solution" Polymers 13, no. 21: 3691. https://doi.org/10.3390/polym13213691

APA Style

Alsaiari, N. S., Katubi, K. M., Alzahrani, F. M., Amari, A., Osman, H., Rebah, F. B., & Tahoon, M. A. (2021). Synthesis, Characterization and Application of Polypyrrole Functionalized Nanocellulose for the Removal of Cr(VI) from Aqueous Solution. Polymers, 13(21), 3691. https://doi.org/10.3390/polym13213691

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop