Next Article in Journal
Crystallinity of Amphiphilic PE-b-PEG Copolymers
Next Article in Special Issue
Evaluation of Improvements in the Separation of Monolayer and Multilayer Films via Measurements in Transflection and Application of Machine Learning Approaches
Previous Article in Journal
Fabrication of Textile-Based Dry Electrode and Analysis of Its Surface EMG Signal for Applying Smart Wear
Previous Article in Special Issue
Lifecycle Assessment for Recycling Processes of Monolayer and Multilayer Films: A Comparison
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 14
Issue 17
10.3390/polym14173642
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

One-Pot Reactive Melt Recycling of PLA Post-Consumer Waste for the Production of Block Copolymer Nanocomposites of High Strength and Ductility

by
Kalyanee Sirisinha
1,*,
Supa Wirasate
1,
Chakrit Sirisinha
2 and
Noppasorn Wattanakrai
1
1
Department of Chemistry, Faculty of Science, Mahidol University, Bangkok 10400, Thailand
2
Rubber Technology Research Centre (RTEC), Faculty of Science, Mahidol University, Nakhon Prathom 73170, Thailand
*
Author to whom correspondence should be addressed.
Polymers 2022, 14(17), 3642; https://doi.org/10.3390/polym14173642
Submission received: 16 August 2022 / Revised: 26 August 2022 / Accepted: 30 August 2022 / Published: 2 September 2022
(This article belongs to the Special Issue Advances in Sustainable Plastics and Polymer Composites)
Browse Figures
Versions Notes

Abstract

:
Post-consumer waste recycling is a crucial issue for building a sustainable society. However, mechanical recycling of poly(lactic acid) (PLA) often reduces the performance of the recycled material because PLA has a strong tendency to degrade during reprocessing. Therefore, it is of great interest to develop an effective recycling method to improve the mechanical performance of this material. This paper presents a one-pot melt process for turning PLA waste into a biodegradable block copolymer and its high strength and ductility composite. The process was conducted in a melt-mixer through a transesterification of PLA with poly(ethylene glycol) (PEG) or poly(propylene glycol) (PPG) as a soft component and clay as reinforcement. Effects of soft component content and sequence of clay addition on the mechanical performance of the prepared materials were focused. The results showed the successful preparation of PLA-based multiblock copolymers of high molecular weights (~100 kDa). Both virgin PLA and recycled source could serve as the starting material. PEG was more efficient than PPG in providing an intense improvement of PLA ductility. The nanocomposite of intercalated structure yielded nearly 100 times higher elongation at break (Eb = 506%) than the starting PLA (Eb = 5.6%) with high strength of 39.5 MPa and modulus of 1.4 GPa, considering the advantages of clay addition. Furthermore, the products with a broadened range of properties can be designed based on the ratio of PLA and soft component, as well as the organization and spatial distribution of clay in the copolymer matrices.

Graphical Abstract

1. Introduction

Poly(lactic acid) (PLA) has become an economically viable material due to its high potential for applicability in various areas, such as in biomedical, agricultural, or packaging fields. The global production capacity of PLA was around 400,000 tons in 2021 [1]. The demand for PLA in different industrial areas has increased as a consequence of the increasing environmental concerns and the depletion of crude oil for the production of traditional oil-based plastics. With its rising usage, more PLA will end in conventional post-consumer plastic waste streams. Although PLA is a biodegradable plastic, the degradation of PLA is slow in the environment. In soil or domestic composters, degradation can take up to a year with temperatures around 20 °C [2,3]. PLA may ultimately break down into its constituent parts (carbon dioxide and water) in a controlled industrial composting environment, requiring temperatures around its glass transition temperature (~60 °C) and high relative humidity [4,5]. In short, the main differences between domestic and industrial composters are temperature and relative humidity. However, degradation is not the only or the most effective treatment method for biodegradable PLA waste. The recycling of post-consumer waste as a secondary raw material, therefore, plays a major role in making the use of natural resources more efficient and reducing the negative impact of plastics on the environment.
Several methods for managing the PLA wastes include composting and depolymerization. According to life cycle analysis, mechanical recycling has more environmental benefits because of its relatively simple process and low pollution risk [6]. For most conventional petroleum-based plastics, such as polypropylene (PP) and polyethylene (PE), mechanical recycling has been studied quite in-depth [7]. With growing market volumes of PLA, there have been ongoing efforts to study the effect of reprocessing and recycling on the performance of PLA. Beltran and co-authors [8] found that mechanical recycling has a limited impact on the structure, thermal stability, and mechanical properties of PLA and suggested that the recycled PLA could be reused for applications such as packaging. However, adverse effects of mechanical recycling on the performance of PLA were reported in the literature [9]. The studies of Zenkiewicz et al. on the effect of repeated extrusion of neat PLA showed that the melt flow rate (MFR) values of the reprocessed samples steadily increased with increased extrusion cycles. The reductions of tensile and impact strength of the reprocessed materials were then resulted [9]. Pillin et al. [10] observed a substantial reduction of the tensile strength and elongation at break of PLA after repeated injection molding whereas the modulus of PLA was hardly changed. Similarly, the studies of Zhao et al. on the recyclability of 3D-printing PLA showed that the polymer could not be reprocessed beyond two cycles without severe loss of properties and viscosity [11].
Several strategies are proposed for increasing the properties of recycled PLA. For example, a specific multifunctional chain extender was added to the PLA in order to limit or inhibit the degradation of the PLA during processing, with the consequent improvement of the thermo-mechanical and rheological properties of the polymer [12,13]. Another approach concerned the possible use of additives that act by restoring the molecular weight of the PLA as affected by processability loss due to thermo-degradation phenomena [14,15]. Several authors achieved improvements in the mechanical and thermal properties of PLA by adding small amounts of nanofillers [16,17,18,19]. Using nanographene in combination with PLA has shown a reduction in the degradation rate of the material [16]. Clay nanoparticles have also been widely investigated as reinforcements for PLA. The addition of organically modified montmorillonite led to the improvement of the mechanical, thermal, and gas barrier properties of a PLA matrix [17,18,19].
Copolymerization of PLA with soft segment is among the effective ways for producing higher toughness PLA, apart from plasticization by small molecules or polymeric plasticizers, and melt-blending with flexible polymers or elastomers. PLA copolymers with a wide range of properties can be designed based on the innate properties of each constituent, the ratio of PLA and soft phase, and the organization of the repeating units [20,21,22,23,24,25]. A traditional method for producing PLA copolymer is ring-opening polymerization (ROP) of lactide monomer or direct condensation of lactic acid, with soft components such as polycaprolactone (PCL), and poly(ethylene glycol) (PEG), etc. The reaction is traditionally performed under reduced pressure for many hours, and a large amount of solvent is required in the process [21,22,23]. Our previous study demonstrated a solventless method for preparing PLA copolymers using a high molecular weight PLA as a feed material [24,25]. The transesterification of PLA and polyol was undertaken in a melt state in the presence of a catalyst. A chain extender was then introduced for the purpose of linking the short-chain copolymers to gain a high molecular weight PLA copolymer.
The present work expands the melt-transesterification approach for the production of copolymer nanocomposites based on PLA, intending to achieve a biodegradable material of balanced strength, stiffness, and ductility in a one-pot process. In this investigation, the starting PLA materials were those of commercially available grade PLA in pellet form and PLA regrind from post-consumer PLA disposable dome lid for cold drinking cups, which is the most common application of PLA in the household area. First, the PLA block copolymers and their nanocomposites containing clay filler were prepared in a melt-mixer. Next, nuclear magnetic resonance spectroscopy (NMR) and gel permeation chromatography (GPC) were employed to analyze the structure and molecular weight of the prepared block copolymers. X-ray diffraction (XRD) and transmission electron microscope (TEM) were used to investigate the morphology, especially the dispersion and spatial distribution of clay in the composite samples. Finally, tensile test was conducted to evaluate the effects of copolymer types and contents, and the sequence of clay filler addition on the mechanical performance of the products. Furthermore, the degradation behaviors of the PLA products were analyzed.

2. Materials and Methods

2.1. Materials

Commercial grade PLA, Ingeo™ 2003D, was from Natureworks® LLC, Minnetonka, MN, USA. The post-consumer PLA samples used in the study were disposable clear dome lids for cold drinking cups. The post-consumer wastes were ground and subjected to a washing process. Prior to processing, the washed materials were dried at 60 °C overnight in a vacuum oven. Poly(ethylene glycol) (PEG) with a molecular weight (Mw) of 4000 g mol−1 was purchased from Ajax Finechem Pty Ltd., and poly(propylene glycol) (PPG) of similar molecular weight was from Acros Organics. Tetrabutyl titanate (TBT) and hexamethylene diisocyanate (HDI) were purchased from Sigma-Aldrich Co., LLC, Missouri, USA. Phenolic antioxidant (Irganox 1010) was from BASF, Ludwigshafen, Germany. The clay used was a commercial organoclay montmorillonite (MMT) Cloisite 30B that was modified with an alkyl quaternary ammonium salt, from Southern Clay Products Inc, Gonzales, TX, USA.

2.2. Preparation of PLA Block Copolymers and Copolymer/Clay Composites

In contrast to the known procedure for the preparation of PLA-based block copolymers combining ROP of lactide monomer and controllable radical polymerization, PLA block copolymers of this study were synthesized via a transesterification reaction between a high molecular weight PLA (either virgin PLA pellets or PLA regrinds) and a polyol (PEG or PPG) in a melt state. The synthesis strategy started with a melt-transesterification of PLA with a polyol in the presence of a catalyst to form short-chain block copolymers, followed by chain extension to obtain long-chain multiblock copolymer products.
The melt reaction process was performed in a HAAKE PolyLab internal mixer equipped with cam-blade rotors. The PLA samples were melt-blending with PEG (or PPG) at 170 °C for 10 min using a rotor speed of 50 rpm. The 0.74 wt% TBT as a catalyst was then added, and the reaction was continued for 5 min. After this, the HDI chain extender was introduced. After 3 min of reaction, the PLA-based multiblock copolymers were obtained. The simple blends of PLA and polyol (plasticized PLA) were prepared, and the neat PLA was also thermally treated under the same conditions as above for comparison.
In the case of copolymer nanocomposites, 3 wt% of clay was introduced to the system as a reinforcing filler. The effect of processing sequences of clay addition was investigated. In Method A, PLA block copolymer was first prepared, and clay was then compounded with the copolymer in an internal mixer at 170 °C for 5 min. The composite was named “copolymer composite”. In Method B, PLA, PEG, and clay were thoroughly mixed in an internal mixer at 170 °C for 5 min, and then a transesterification reaction was performed by adding catalyst and chain extender to the formulation. The resulting material, in this case, was denoted as “reactive copolymer composite”. The obtained copolymers and copolymer composites were then compression-molded at 170 °C into specimens with dimensions specific to each test. The specimens were stored in a desiccator at 23 °C prior to testing.

2.3. Characterizations and Testing

Nuclear magnetic resonance spectroscopy (NMR) was used to analyze the structure of the PLA block copolymers. 1H NMR spectra of the purified samples were recorded on an NMR spectrometer (Bruker 500 MHz, Madison, WI, USA) operated at 25 °C with 25,000 scans to obtain high-resolution spectra. Deuterated chloroform (CDCl3) was used as a solvent. Gel permeation chromatography (GPC) instrument (Waters 1515, Milford, MA, USA) equipped with RI detector was used to determine the average molecular weights and polydispersity (PDI) of the block copolymers using tetrahydrofuran (THF) as an eluent (at 40 °C) and polystyrene (PS) as a standard.
XRD analysis was performed on a Malvern Panalytical Empyrean X-ray diffractometer with CuKα radiation (λ of 0.1540 nm) at a generator voltage of 45 kV and a generator current of 40 mA. The interlayer spacing (d001) of clay was calculated using Bragg’s law (λ = 2d sin θ). TEM was carried out on a Phillips TECNAI 20 transmission electron microscope using an acceleration voltage of 100 kV. Ultrathin samples for TEM were prepared using a Leica Ultracut R ultramicrotome.
Tensile testing was performed using an Instron Model 5566 Universal Tensile tester (Canton, MA, USA). The test was carried out at 23 °C, 50% RH according to ASTM D882 (gauge length of 25.4 mm) with a crosshead speed of 50 mm.min−1. At least five specimens were used for averaging. The correlation between stress and strain was studied. Young’s modulus, tensile strength, and elongation at break were determined.
Hydrolytic degradation test was conducted on square specimens of 10.0 × 10.0 mm2 with a thickness of 1.0 mm. Each specimen was immersed in 50 mL of 0.1 M pH 7 sodium phosphate buffer containing 2 wt% sodium azide (NaN3) antimicrobial substance. The tests were performed at 70 °C for different durations, after which the percentage of weight loss was determined using the following equation.
W e i g h t   l o s s   % = w i − w f w i × 100
where, wi is initial weight of sample before subjected to testing and wf is final weight of sample after testing.

3. Results and Discussion

3.1. PLA-Based Block Copolymers: Structure and Properties

Virgin PLA pellets were used as a starting material for producing PLA-based block copolymers, i.e., PLA-PEG and PLA-PPG, via a melt-transesterification process. The contents of PEG and PPG initially added were 20 wt%. The chemical structures of the two copolymers characterized by 1H NMR are given in Figure 1. The signals at 1.60 and 5.20 ppm belong to the methyl protons (a, -CH3) and methine protons (b, -CH) of the PLA unit, respectively. The PEG unit exhibits a characteristic signal of methylene protons (c, -CH2) at 3.60 ppm [26,27], while the PPG unit shows a signal of methyl protons (d, -CH3), methylene protons (e, -CH2), and methine protons (f, -CH) at 1.14, 3.55 and 3.40 ppm, respectively. The signals from 4.20 to 4.30 ppm correspond to the methylene protons (g, -CH2) of PEG that are attached to the PLA unit, while those belonging to PPG are observed at 4.15 ppm. The 1H NMR signal at a chemical shift of 4.35 ppm (-CH, i) of the PLA-PPG sample is assigned to the attached secondary hydroxyl protons of PPG. The molecular weights obtained by GPC are shown in Table 1. The PLA-PEG block copolymer exhibits the Mw of approximately 1.3 × 105 g mol−1 whereas the Mw of PLA-PPG copolymers is around 1.1 × 105 g mol−1. Compared to the starting PLA (Mw~1.7 × 105 g mol−1), the PLA-based copolymers yield slightly lower molecular weights and broader molecular weight distributions. NMR and GPC results thus confirm that the PLA-PEG and PLA-PPG multiblock copolymers of high molecular weights were successfully prepared by a melt-transesterification process employing PLA polymer as a starting material.
Table 2 contains the mechanical properties of a range of plasticized PLA and PLA-based block copolymers according to soft segment type and content. Neat PLA exhibits a high tensile strength of 64.73 MPa and modulus of 2.27 GPa with a very low elongation at break of only 6%. This is as expected, as the PLA resembles clear polystyrene in which it is stiff and brittle, and consequently needs modification for most practical applications (i.e., plasticization and/or copolymerization to increase its flexibility). Evidence of the plasticizing effect of PPG and PEG is clearly seen in Table 2, where the addition of either PPG or PEG makes PLA less brittle and enhances its extensibility significantly. PEG displays better plasticizing abilities than PPG. The plasticizing effect is amplified by increasing the amount of plasticizer in the blends. However, there is a limit of the plasticizer content in practice. The addition of plasticizer beyond the limit not only leads to a deterioration in mechanical strength and stiffness, but also facilitates phase separation. The separation of plasticizer causes increased stiffness and decreased drawability of the plasticized PLA. Moreover, the plasticizer may leach out and migrate from the bulk to the product surfaces thereafter. [28,29]. In some particular areas including food contact packaging, plasticizer migration from the packaging materials is not allowed.
An important factor in the commercial development of ductile PLA is the ability to maintain its ductility during functional use. Copolymerization of PLA with soft segment offers plasticizer-free solutions and, thus, is a beneficial approach for modifying its properties. It is clear from Table 2 that both PLA copolymers with a soft component in the structure yield higher elongation than the neat PLA. For example, the copolymer with 10%PEG (PLA-PEG) exhibits more than 100 times higher elongation (Eb~600%) than the starting PLA (Eb~6%) together with a strength of 30.25 MPa and modulus of 952.31 MPa. Despite having an equal molecular weight of 4000, PEG is more efficient than PPG in providing an intense improvement of PLA ductility. The primary hydroxyl terminated groups of PEG can react readily with the ester functions of PLA chains, enabling the achievement of a multiblock PLA-PEG copolymer with high ductility.

3.2. Nanocomposites of PLA Block Copolymer and Clay

Based on the results gained from the tensile study, PEG with its relatively high efficiency was selected as a soft block component for enhancing the ductility of PLA. MMT clay was introduced to the formulation to compensate the reduced stiffness and strength of PLA caused by the presence of soft PEG component in the system, aiming at obtaining a nanocomposite with a good balance of strength, stiffness, and ductility. In this part, post-consumer PLA regrind was used as a feed material. PEG contents were varied at 10 and 20 wt%. The effects of sequences of clay addition on the structure and mechanical properties of the composites were focused. Stress-strain dependencies for the materials studied are illustrated in Figure 2, and the average values of tensile strength, Young’s modulus, and elongation at break are summarized in Table 3.
In contrast to the neat PLA showing brittle failure at a low strain, the PLA-PEG copolymer exhibits dramatically increased ductility, and undergoes strain-hardening with the elongation at break of approximately 600%. The presence of strain hardening indicates a very intense effect of PEG on increased segmental mobility, thus facilitating the plastic deformation of the block copolymers upon tensile drawing. Other notable factors influencing the mechanical performance of PLA-based materials are the content of soft segment and the processing sequence of clay addition. Interestingly, the reactive copolymer composite prepared from Method B is capable of undergoing strain hardening, showing an extraordinarily high magnitude of elongation at break of >500% whereas the copolymer composite prepared from Method A shows a much lower elongation at break (80%).
The tensile data summarized in Table 3 reveal a similar trend of mechanical property changes for both composite series prepared from virgin PLA feedstock and post-consumer PLA regrind. The notably high strain at break value of 441.79% along with tensile strength of 35.98 MPa and Young’s modulus of 969.68 MPa are observed in the reactive copolymer composite sample with 20 wt% PEG soft segment using PLA regrind as a feed material. The magnitudes of tensile strength and Young’s modulus show an increasing trend when decreasing the content of PEG soft segment in the formulation. For example, a highly ductile nanocomposite with an elongation of ~500% and high modulus of 1417.70 MPa could be achieved from a one-pot reactive melt process using PLA regrind copolymerized with 10 wt% PEG in the presence of clay. The results also indicate that only a small amount of clay nanofiller (3 wt%) is needed for a great improvement in the stiffness and strength of PLA-based block copolymer. Better mechanical performance of the reactive copolymer nanocomposite deserves further investigation. In polymer/clay nanocomposites, great enhancement of mechanical properties and thermal stability are believed to result from synergistic interactions between the high surface area of clay galleries and the polymer, combined with the specific constitution of the system via intercalation and/or exfoliation phenomena [30,31,32]. In this study, the nanocomposite morphological characteristics were investigated by XRD and TEM.
The XRD patterns, shown in Figure 3a, reveal the structure of MMT clay (Cloisite 30B) and clay in the nanocomposites. The MMT clay exhibits a 2θ at 4.8 degree characterized by an interlayer distance (d001) of 1.8 nm, which is in line with the previous work [33,34,35,36]. By monitoring the position, shape, and intensity of the basal reflections from the distributed clay layers, the nanocomposite structure (intercalated or exfoliated) could be identified. The Cloisite 30B peak (2θ = 4.8 degree) could be observed in the XRD patterns of the two nanocomposites prepared by different techniques, suggesting that the MMT layered configuration existed. However, the appearance of a new basal reflection at a lower 2θ angle of 2.7 degree is found in the reactive copolymer composite, reflecting a larger interlayer distance (d001 = 3.3 nm) of clay in the material and the occurrence of an intercalated structure together with a partial preservation of MMT layered structure. The nanocomposite structure is further confirmed by the TEM micrographs of Figure 3b,c, revealing the presence of MMT layered configuration and more compacted sheets in the composite prepared from the conventional method A (Figure 3b). In contrast, the reactive composite presents more separated clay sheets and a better clay distribution (Figure 3c).
Schematic representation of the melt-copolymerization and nanocomposite formation has been presented in Figure 4. In the case of the nanocomposite prepared from Method A, a long-chain multiblock copolymer was formed in the first stage and then clay was added to a highly viscous melt, resulting in the clay arrangement in the form of tactoids- consisting of several stacked silicate layers. For the reactive nanocomposite, clay was thoroughly mixed with the polymers prior to performing the melt-copolymerization reaction. This allows the movement of short-chain block copolymer into the clay galleries, giving the sliding of the silicate sheets and increasing the separation between the clay layers, thus promoting an intercalation and partially exfoliated structure.
Visual examination of the 0.4 mm thick molded samples shows some opacity for the composite obtained from Method A, whereas the reactive composite prepared by Method B and the unfilled block copolymer are more transparent (Figure 5). The opacity of the composite prepared from Method A resulted from the light scattering on the filler particles. In turn, the transparency of the reactive nanocomposite confirms good dispersion and spatial distribution of clay within the polymer matrix.
Table 4 provides the tensile data of various bio-based and petroleum-based polymers, together with the similar PLA-based block copolymers prepared by different synthesis routes [37,38,39,40,41,42]. From the analysis of the mechanical data reported in Table 4, it is evident that the tensile properties of PLA-PEG block copolymers reported in the literatures are quite different. This different behavior is mainly related to the content of soft segment in the polymer chains and the molecular weight of the prepared copolymers. The increase of molecular weight seems to offer an enhanced tensile strength of the copolymers. With the high Mw of about 100 kDa, the PLA-PEG multiblock copolymers of this study yield high tensile strength (25–28 MPa), modulus (524–740 MPa), and elongation at break (>500%). Comparable values of tensile properties were observed by Mei et al., reporting a tensile strength of 32.6 MPa and elongation of about 500% for the PLA-PEG multiblock copolymer with a Mw of 145 kDa. However, this sample exhibited a modulus of only 28.4 MPa [38]. Biodegradable poly(butylene adipate-co-terephthalate) (PBAT, Ecoflex from BASF) is characterized by high elongation at break (>300%), with strength and modulus of 18.8 and 30 MPa, respectively [40]. A relatively higher modulus (450 MPa) is reported for poly(butylene succinate) (BioPBS, FZ91PD from PTT MCC Biochem), with a tensile strength of 33.3 MPa and elongation at break of 330% [41]. Considering the benefits obtained with a nanoscale distribution of clays within the polymer matrix in terms of improved mechanical properties at low filler content, PLA-based block copolymer composites of this study exhibit comparable properties to some petroleum-based polymers grade widely used in packaging applications such as polypropylene [42]. Our research, therefore, provides a facile method for making environmentally sustainable products of good mechanical performance from PLA post-consumer waste that would serve useful industrial markets such as disposable packaging and agricultural films. The process is economically feasible, as it can be carried out in the melt without solvent, thus providing a low environmental impact.
The primary degradation mechanism of PLA is hydrolysis, catalyzed by temperature, followed by bacterial attack on the fragmented residues. The end result of the process is carbon dioxide and water. In aqueous systems, the hydrolysis of PLA can be achieved by bulk or surface erosion [43]. The rate of degradation is influenced by the rate of water diffusion which in turn depends on the original molecular weight of the sample, crystallinity, sample dimensions, pH, and temperature. In this study, the hydrolysis of PLA, its block copolymers, and copolymer composites was carried out at 70 °C for up to 30 days. Regardless of the sample types, the degradation rate increases with increasing the hydrolysis time (Figure 6). The presence of PEG as either a plasticizer or a soft segment in the polymer chains elevates the rate of PLA hydrolysis traced by weight loss. PEG has a considerable affinity to water so its copolymer might have an increased hydrophilicity [44,45]. In addition, the PLA-PEG block copolymer exhibits a slightly lower molecular weight than the starting PLA. Both factors, therefore, are probably responsible for the higher degradation rate found in the block copolymer products.
The copolymer nanocomposites containing clay are hydrolyzed more readily than the unmodified PLA but still more difficult than the unfilled copolymer. The weight loss percentages after 30-day hydrolysis of PLA, its copolymer, and plasticized sample were 55, 63, and 65, respectively. The incorporation of clay gives somewhat reduction in the weight loss of the copolymers. The composite structure (microcomposite or intercalated nanocomposite) has been reported to play a determining role in the hydrolytic degradation process of PLA [46]. In this study, the reactive nanocomposites with their intercalated structure showed slightly lower weight loss value than those of tactoid structure.

4. Conclusions

PLA-based multiblock copolymers and their composites were prepared from post-consumer waste via melt-transesterification using TBT as a catalyst and HDI as a chain extender. It was evident by NMR and GPC analysis that copolymerization of PLA in the melt state did not induce a dramatic drop of PLA molecular weight. The block copolymers with Mw of approximately 105 g mol−1 were successfully prepared. Despite having an equal molecular weight of 4000, PEG was more efficient than PPG in enhancing the ductility of PLA. However, the presence of soft component reduced both tensile strength and modulus of the samples. The tensile results indicated that only a small amount of clay (3 wt%) was needed to drastically enhance the strength and stiffness of the copolymers. The localization and spatial distribution of clay in the copolymer matrices as well as the overall properties of the composites depended strongly on the PLA/PEG ratio and the sequence of clay addition. For the reactive composites where clay was thoroughly mixed with the polymers before performing the copolymerization reaction, the TEM investigation revealed the separation between the clay layers consistent with d spacing obtained from XRD. Due to the nanometer-range dispersion of clay layers, this material showed very high elongation at break of 500% and high modulus of 1.41 GPa with high transparency. In addition, the copolymer composites exhibited a slightly higher rate of hydrolysis than the PLA. Our research, therefore, provided an effective method for turning PLA post-consumer waste into sustainable and value-added products with appropriate properties to be used in industrial markets such as packaging and agricultural films.

Author Contributions

Conceptualization, K.S.; methodology, K.S. and S.W.; formal analysis, K.S. and N.W.; investigation, K.S., S.W. and N.W.; writing—original draft preparation, K.S. and N.W.; writing—review and editing, K.S., S.W. and C.S. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the National Research Council of Thailand (NRCT) under the Research University Network Initiative. The APC was funded by Mahidol University.

Institutional Review Board Statement

Not applicable.

Acknowledgments

The authors gratefully acknowledge the National Research Council of Thailand (NRCT) for research funding; and the Rubber Technology Research Centre (RTEC) at the Faculty of Science, Mahidol University for providing the support in terms of research facilities. The authors thank J. Luangkachao for the preparation of plasticized PLA; and the Microscopic Center at the Faculty of Science, Burapha University for the TEM measurements.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Bioplastics Market Data. Available online: https://www.european-bioplastics.org/market/ (accessed on 25 August 2022).
  2. Ho, K.-L.G.; Pometto, A.L.; Hinz, P.N.; Gadea-Rivas, A.; Briceño, J.A.; Rojas, A. Field Exposure Study of Polylactic Acid (PLA) Plastic Films in the Banana Fields of Costa Rica. J. Environ. Polym. Degrad. 1999, 7, 167–172. [Google Scholar] [CrossRef]
  3. Rudnik, E.; Briassoulis, D. Degradation behaviour of poly(lactic acid) films and fibres in soil under Mediterranean field conditions and laboratory simulations testing. Ind. Crops Prod. 2011, 33, 648–658. [Google Scholar] [CrossRef]
  4. Kale, G.; Auras, R.; Singh, S.P.; Narayan, R. Biodegradability of polylactide bottles in real and simulated composting conditions. Polym. Test. 2007, 26, 1049–1061. [Google Scholar] [CrossRef]
  5. Emadian, S.M.; Onay, T.T.; Demirel, B. Biodegradation of bioplastics in natural environments. Waste Manag. 2017, 59, 526–536. [Google Scholar] [CrossRef]
  6. Dilkes-Hoffman, L.S.; Pratt, S.; Lant, P.A.; Laycock, B. The Role of Biodegradable Plastic in Solving Plastic Solid Waste Accumulation. In Plastics to Energy; Al-Salem, S.M., Ed.; William Andrew Publishing: Norwich, NY, USA, 2019; pp. 469–505. [Google Scholar]
  7. Yin, S.; Tuladhar, R.; Shi, F.; Shanks, R.A.; Combe, M.; Collister, T. Mechanical reprocessing of polyolefin waste: A review. Polym. Eng. Sci. 2015, 55, 2899–2909. [Google Scholar] [CrossRef]
  8. Beltrán, F.R.; Lorenzo, V.; Acosta, J.; de la Orden, M.U.; Martínez Urreaga, J. Effect of simulated mechanical recycling processes on the structure and properties of poly(lactic acid). J. Environ. Manag. 2018, 216, 25–31. [Google Scholar] [CrossRef]
  9. Żenkiewicz, M.; Richert, J.; Rytlewski, P.; Moraczewski, K.; Stepczyńska, M.; Karasiewicz, T. Characterisation of multi-extruded poly(lactic acid). Polym. Test. 2009, 28, 412–418. [Google Scholar] [CrossRef]
  10. Pillin, I.; Montrelay, N.; Bourmaud, A.; Grohens, Y. Effect of thermo mechanical cycles on the physico-chemical properties of PLA. Polym. Degrad. Stab. 2008, 93, 321–328. [Google Scholar] [CrossRef]
  11. Zhao, P.; Rao, C.; Gu, F.; Sharmin, N.; Fu, J. Close-looped recycling of polylactic acid used in 3D printing: An experimental investigation and life cycle assessment. J. Clean. Prod. 2018, 197, 1046–1055. [Google Scholar] [CrossRef]
  12. Al-Itry, R.; Lamnawar, K.; Maazouz, A. Reactive extrusion of PLA, PBAT with a multi-functional epoxide: Physico-chemical and rheological properties. Eur. Polym. J. 2014, 58, 90–102. [Google Scholar] [CrossRef]
  13. Jaszkiewicz, A.; Bledzki, A.K.; Duda, A.; Galeski, A.; Franciszczak, P. Investigation of Processability of Chain-Extended Polylactides During Melt Processing—Compounding Conditions and Polymer Molecular Structure. Macromol. Mater. Eng. 2014, 299, 307–318. [Google Scholar] [CrossRef]
  14. Sirisinha, K.; Samana, K. Improvement of melt stability and degradation efficiency of poly (lactic acid) by using phosphite. J. Appl. Polym. Sci. 2021, 138, 49951. [Google Scholar] [CrossRef]
  15. Luo, J.; Meng, X.; Gong, W.; Jiang, Z.; Xin, Z. Improving the stability and ductility of polylactic acid via phosphite functional polysilsesquioxane. RSC Adv. 2019, 9, 25151–25157. [Google Scholar] [CrossRef] [PubMed]
  16. Botta, L.; Scaffaro, R.; Sutera, F.; Mistretta, M.C. Reprocessing of PLA/Graphene Nanoplatelets Nanocomposites. Polymers 2018, 10, 18. [Google Scholar] [CrossRef]
  17. Meng, Q.; Heuzey, M.-C.; Carreau, P.J. Control of thermal degradation of polylactide/clay nanocomposites during melt processing by chain extension reaction. Polym. Degrad. Stab. 2012, 97, 2010–2020. [Google Scholar] [CrossRef]
  18. Araújo, A.; Botelho, G.; Oliveira, M.; Machado, A.V. Influence of clay organic modifier on the thermal-stability of PLA based nanocomposites. Appl. Clay Sci. 2014, 88–89, 144–150. [Google Scholar] [CrossRef]
  19. Fukushima, K.; Tabuani, D.; Arena, M.; Gennari, M.; Camino, G. Effect of clay type and loading on thermal, mechanical properties and biodegradation of poly(lactic acid) nanocomposites. React. Funct. Polym. 2013, 73, 540–549. [Google Scholar] [CrossRef]
  20. Oh, J.K. Polylactide (PLA)-based amphiphilic block copolymers: Synthesis, self-assembly, and biomedical applications. Soft Matter 2011, 7, 5096–5108. [Google Scholar] [CrossRef]
  21. Stefaniak, K.; Masek, A. Green Copolymers Based on Poly(Lactic Acid)—Short Review. Materials 2021, 14, 5254. [Google Scholar] [CrossRef]
  22. Zhang, J.; Xu, J.; Wang, H.; Jin, W.; Li, J. Synthesis of multiblock thermoplastic elastomers based on biodegradable poly (lactic acid) and polycaprolactone. Mater. Sci. Eng. C 2009, 29, 889–893. [Google Scholar] [CrossRef]
  23. Buwalda, S.J.; Dijkstra, P.J.; Feijen, J. Poly(ethylene glycol)–poly(L-lactide) star block copolymer hydrogels crosslinked by metal–ligand coordination. J. Polym. Sci. Part A Polym. Chem. 2012, 50, 1783–1791. [Google Scholar] [CrossRef]
  24. Koosomsuan, W.; Phinyocheep, P.; Sirisinha, K. Facile melt processing technique for the preparation of super ductile PLA–PEG multiblock copolymers: The roles of catalyst and antioxidant loadings. Polym. Degrad. Stab. 2018, 157, 160–174. [Google Scholar] [CrossRef]
  25. Luangkachao, J.; Sirisinha, K. Role of Sn-based and Ti-based catalysts on melt copolymerization of PLA-Polyols. IOP Conf. Ser. Mater. Sci. Eng. 2020, 773, 012058. [Google Scholar] [CrossRef]
  26. Han, L.; Yu, C.; Zhou, J.; Shan, G.; Bao, Y.; Yun, X.; Dong, T.; Pan, P. Enantiomeric blends of high-molecular-weight poly(lactic acid)/poly(ethylene glycol) triblock copolymers: Enhanced stereocomplexation and thermomechanical properties. Polymer 2016, 103, 376–386. [Google Scholar] [CrossRef]
  27. Ding, Y.; Feng, W.; Lu, B.; Wang, P.; Wang, G.; Ji, J. PLA-PEG-PLA tri-block copolymers: Effective compatibilizers for promotion of the interfacial structure and mechanical properties of PLA/PBAT blends. Polymer 2018, 146, 179–187. [Google Scholar] [CrossRef]
  28. Ljungberg, N.; Wesslén, B. Tributyl citrate oligomers as plasticizers for poly (lactic acid): Thermo-mechanical film properties and aging. Polymer 2003, 44, 7679–7688. [Google Scholar] [CrossRef]
  29. Jia, Z.; Tan, J.; Han, C.; Yang, Y.; Dong, L. Poly(ethylene glycol-co-propylene glycol) as a macromolecular plasticizing agent for polylactide: Thermomechanical properties and aging. J. Appl. Polym. Sci. 2009, 114, 1105–1117. [Google Scholar] [CrossRef]
  30. Gao, F. Clay/polymer composites: The story. Mater. Today 2004, 7, 50–55. [Google Scholar] [CrossRef]
  31. Nofar, M.; Salehiyan, R.; Ray, S.S. Influence of nanoparticles and their selective localization on the structure and properties of polylactide-based blend nanocomposites. Compos. Part B Eng. 2021, 215, 108845. [Google Scholar] [CrossRef]
  32. Alexandre, M.; Dubois, P. Polymer-layered silicate nanocomposites: Preparation, properties and uses of a new class of materials. Mater. Sci. Eng. R Rep. 2000, 28, 1–63. [Google Scholar] [CrossRef]
  33. Gómez, M.; Palza, H.; Quijada, R. Influence of Organically-Modified Montmorillonite and Synthesized Layered Silica Nanoparticles on the Properties of Polypropylene and Polyamide-6 Nanocomposites. Polymers 2016, 8, 386. [Google Scholar] [CrossRef] [PubMed]
  34. Krikorian, V.; Pochan, D.J. Poly (l-Lactic Acid)/Layered Silicate Nanocomposite:  Fabrication, Characterization, and Properties. Chem. Mater. 2003, 15, 4317–4324. [Google Scholar] [CrossRef]
  35. Franco-Urquiza, E.A.; Cailloux, J.; Santana, O.; Maspoch, M.L.; Velazquez Infante, J.C. The Influence of the Clay Particles on the Mechanical Properties and Fracture Behavior of PLA/o-MMT Composite Films. Adv. Polym. Technol. 2015, 34, 21470. [Google Scholar] [CrossRef]
  36. Haji Abdolrsaouli, M.; Babaei, A.; Kaschta, J.; Nazockdat, H. Polylactide/organoclay nanocomposites: The effect of organoclay types on the structure development and the kinetic of cold crystallization. J. Vinyl Addit. Technol. 2019, 25, 48–58. [Google Scholar] [CrossRef]
  37. Maglio, G.; Migliozzi, A.; Palumbo, R. Thermal properties of di- and triblock copolymers of poly(l-lactide) with poly(oxyethylene) or poly(ε-caprolactone). Polymer 2003, 44, 369–375. [Google Scholar] [CrossRef]
  38. Mei, T.; Zhu, Y.; Ma, T.; He, T.; Li, L.; Wei, C.; Xu, K. Synthesis, characterization, and biocompatibility of alternating block polyurethanes based on PLA and PEG. J. Biomed. Mater. Res. Part A 2014, 102, 3243–3254. [Google Scholar] [CrossRef]
  39. Wan, Y.; Chen, W.; Yang, J.; Bei, J.; Wang, S. Biodegradable poly(l-lactide)-poly(ethylene glycol) multiblock copolymer: Synthesis and evaluation of cell affinity. Biomaterials 2003, 24, 2195–2203. [Google Scholar] [CrossRef]
  40. Sirisinha, K.; Somboon, W. Melt characteristics, mechanical, and thermal properties of blown film from modified blends of poly(butylene adipate-co-terephthalate) and poly(lactide). J. Appl. Polym. Sci. 2012, 124, 4986–4992. [Google Scholar] [CrossRef]
  41. Kajornprai, T.; Suttiruengwong, S.; Sirisinha, K. Manipulating Crystallization for Simultaneous Improvement of Impact Strength and Heat Resistance of Plasticized Poly(l-lactic acid) and Poly(butylene succinate) Blends. Polymers 2021, 13, 3066. [Google Scholar] [CrossRef]
  42. Premphet, K.; Horanont, P. Improving performance of polypropylene through combined use of calciuum carbonate and metallocene-produced impact modifier. Polym. -Plast. Technol. Eng. 2001, 40, 235–247. [Google Scholar] [CrossRef]
  43. Von Burkersroda, F.; Schedl, L.; Göpferich, A. Why degradable polymers undergo surface erosion or bulk erosion. Biomaterials 2002, 23, 4221–4231. [Google Scholar] [CrossRef]
  44. Xu, G.; Chen, S.; Yan, X.; Yang, C.; Chen, Z. Synthesis and Hydrophilic Performance of Poly(Lactic Acid)-Poly(Ethylene Glycol) Block Copolymers. Am. J. Anal. Chem. 2016, 07, 299–305. [Google Scholar] [CrossRef]
  45. Sheng, Y.; Yuan, Y.; Liu, C.; Tao, X.; Shan, X.; Xu, F. In vitro macrophage uptake and in vivo biodistribution of PLA–PEG nanoparticles loaded with hemoglobin as blood substitutes: Effect of PEG content. J. Mater. Sci. Mater. Med. 2009, 20, 1881–1891. [Google Scholar] [CrossRef] [PubMed]
  46. Paul, M.A.; Delcourt, C.; Alexandre, M.; Degée, P.; Monteverde, F.; Dubois, P. Polylactide/montmorillonite nanocomposites: Study of the hydrolytic degradation. Polym. Degrad. Stab. 2005, 87, 535–542. [Google Scholar] [CrossRef]
Polymers 14 03642 g001 550
Figure 1. 1H NMR spectrum of PLA-PEG and PLA-PPG copolymers.
Figure 1. 1H NMR spectrum of PLA-PEG and PLA-PPG copolymers.
Polymers 14 03642 g001
Polymers 14 03642 g002 550
Figure 2. Stress-strain curves of PLA, PLA-PEG (80–20) block copolymer, block copolymer composite (from Method A), and reactive copolymer composite (from Method B).
Figure 2. Stress-strain curves of PLA, PLA-PEG (80–20) block copolymer, block copolymer composite (from Method A), and reactive copolymer composite (from Method B).
Polymers 14 03642 g002
Polymers 14 03642 g003 550
Figure 3. XRD patterns for MMT clay, copolymer composite, and reactive copolymer composite (a), and TEM images of copolymer composite (b), and reactive copolymer composite (c).
Figure 3. XRD patterns for MMT clay, copolymer composite, and reactive copolymer composite (a), and TEM images of copolymer composite (b), and reactive copolymer composite (c).
Polymers 14 03642 g003
Polymers 14 03642 g004 550
Figure 4. Schematic illustration of melt-copolymerization and nanocomposite formation.
Figure 4. Schematic illustration of melt-copolymerization and nanocomposite formation.
Polymers 14 03642 g004
Polymers 14 03642 g005 550
Figure 5. Photographs of 0.4 mm thick films of PLA, PLA-PEG block copolymer, copolymer composite, and reactive copolymer composite.
Figure 5. Photographs of 0.4 mm thick films of PLA, PLA-PEG block copolymer, copolymer composite, and reactive copolymer composite.
Polymers 14 03642 g005
Polymers 14 03642 g006 550
Figure 6. Evolution of weight loss with increasing hydrolysis time for PLA, plasticized PLA, block copolymers and composite.
Figure 6. Evolution of weight loss with increasing hydrolysis time for PLA, plasticized PLA, block copolymers and composite.
Polymers 14 03642 g006
Table
Table 1. Molecular parameters for the virgin PLA, PLA regrind, and PLA-based copolymers.
Table 1. Molecular parameters for the virgin PLA, PLA regrind, and PLA-based copolymers.
PropertiesPLA VirginPLA
Regrind		PLA-PEG
Copolymer		PLA-PPG
Copolymer
Weight average molecular weight (Mw)1.7 × 1051.4 × 1051.3 × 1051.1 × 105
Number average molecular weight (Mn)8.1 × 1047.4 × 1045.0 × 1044.8 × 104
Polydispersity index (PDI)1.961.832.782.29
Table
Table 2. Tensile strength, Young’s modulus, and elongation at break of various plasticized PLA and PLA-based block copolymers.
Table 2. Tensile strength, Young’s modulus, and elongation at break of various plasticized PLA and PLA-based block copolymers.
Soft Segment
[%]		Plasticized PLAPLA-Based Block Copolymer
Strength
[MPa]		Modulus
[MPa]		Elongation
[%]		Strength
[MPa]		Modulus
[MPa]		Elongation
[%]
PLA64.73 ± 3.502269.03 ± 119.485.69 ± 1.12
PPG
1040.74 ± 0.981971.66 ± 143.0025.48 ± 60.4045.40 ± 1.211811.50 ± 71.655.60 ± 0.16
1534.83 ± 1.831893.64 ± 123.1849.90 ± 16.0133.89 ± 1.161613.92 ± 46.5536.27 ± 3.67
2032.31 ± 1.091804.29 ± 102.4953.66 ± 10.3425.23 ± 0.511418.90 ± 41.2014.04 ± 4.24
PEG
1052.88 ± 0.571657.66 ± 34.3425.71 ± 0.4030.25 ± 1.98952.31 ± 53.59606.31 ± 27.71
1541.37 ± 2.051095.88 ± 40.30528.17 ± 17.8226.90 ± 1.49546.33 ± 32.25644.52 ± 31.28
2035.23 ± 1.61549.12 ± 10.19478.51 ± 20.8124.92 ± 0.71523.95 ± 19.94620.14 ± 17.88
Table
Table 3. Tensile properties of a range of PLA-PEG block copolymers, copolymer composites, and reactive copolymer composites.
Table 3. Tensile properties of a range of PLA-PEG block copolymers, copolymer composites, and reactive copolymer composites.
SamplesPEG Content [%]Strength
[MPa]		Modulus [MPa]Elongation
[%]
PLA virgin-64.73 ± 3.502269.03 ± 119.485.69 ± 1.12
Block copolymer2024.92 ± 0.71523.95 ± 19.94620.14 ± 17.88
Copolymer composite2036.60 ± 1.201330.02 ± 60.5887.54 ± 3.28
Reactive copolymer composite2042.32 ± 1.131410.45 ± 70.58562.15 ± 42.39
PLA regrind-59.30 ± 1.702242 ± 201.026.15 ± 0.92
Block copolymer2027.42 ± 1.16740.04 ± 31.2587.20 ± 45.41
Copolymer composite2034.02 ± 2.17954.29 ± 53.59102.50 ± 17.00
Reactive copolymer composite2035.98 ± 1.47969.68 ± 58.92441.79 ± 20.87
PLA regrind
Block copolymer1026.25 ± 1.98952.31 ± 53.59572.31 ± 29.17
Copolymer composite1037.60 ± 0.711328.74 ± 64.6735.24 ± 3.28
Reactive copolymer composite1039.49 ± 1.301417.70 ± 71.16506.15 ± 42.39
Table
Table 4. Tensile data of various bio-based and petroleum-based polymers, together with the similar PLA-based block copolymers prepared by different synthesis routes.
Table 4. Tensile data of various bio-based and petroleum-based polymers, together with the similar PLA-based block copolymers prepared by different synthesis routes.
SystemType of CopolymerMw
[kDa]		PLA/PEG Ratio
[wt/wt]		Strength [MPa]Modulus [MPa]Elongation [%]Ref.
PLA-PEG copolymer
(Mw of PEG = 4000)		multiblock95–13080/2025–28524–740580–620This work
Copolymer composite (with 3 wt% clay)multiblockN/A80/2034–37954–133085–102
90/1037.6132835
Reactive copolymer composite
(with 3 wt% clay)		multiblockN/A80/2036–42970–1410500
90/1039.51418506
PLA-PEG copolymer synthesized from ring-opening polymerization of lactide in the presence of PEGdiblock32.979/217.032049[37]
triblock57.578/227.0225134
multiblock14548/5232.628.4546[38]
multiblock61.152/484.625.0561
triblock28.076/244.0N/A6.0[39]
triblock49.887/1311.7N/A6.8
multiblock55.375/2522.1N/A469
multiblock66.887/1325.2N/A59
Poly(butylene adipate-co-terephthalate) (PBAT)N/AN/AN/A18.830388[40]
Poly(butylene succinate) (PBS)N/AN/AN/A33.3450330[41]
Polypropylene (PP)N/AN/AN/A34.41620>350[42]
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Sirisinha, K.; Wirasate, S.; Sirisinha, C.; Wattanakrai, N. One-Pot Reactive Melt Recycling of PLA Post-Consumer Waste for the Production of Block Copolymer Nanocomposites of High Strength and Ductility. Polymers 2022, 14, 3642. https://doi.org/10.3390/polym14173642

AMA Style

Sirisinha K, Wirasate S, Sirisinha C, Wattanakrai N. One-Pot Reactive Melt Recycling of PLA Post-Consumer Waste for the Production of Block Copolymer Nanocomposites of High Strength and Ductility. Polymers. 2022; 14(17):3642. https://doi.org/10.3390/polym14173642

Chicago/Turabian Style

Sirisinha, Kalyanee, Supa Wirasate, Chakrit Sirisinha, and Noppasorn Wattanakrai. 2022. "One-Pot Reactive Melt Recycling of PLA Post-Consumer Waste for the Production of Block Copolymer Nanocomposites of High Strength and Ductility" Polymers 14, no. 17: 3642. https://doi.org/10.3390/polym14173642

APA Style

Sirisinha, K., Wirasate, S., Sirisinha, C., & Wattanakrai, N. (2022). One-Pot Reactive Melt Recycling of PLA Post-Consumer Waste for the Production of Block Copolymer Nanocomposites of High Strength and Ductility. Polymers, 14(17), 3642. https://doi.org/10.3390/polym14173642

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.