Flame-Retardance Functionalization of Jute and Jute-Cotton Fabrics
Next Article in Special Issue
Hydrodeoxygenation of Lignin-Based Compounds over Ruthenium Catalysts Based on Sulfonated Porous Aromatic Frameworks
Previous Article in Journal
Thiol-Surface-Engineered Cellulose Nanocrystals in Favor of Copper Ion Uptake
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 15
Issue 11
10.3390/polym15112565
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Catechol-Based Porous Organic Polymers for Effective Removal of Phenolic Pollutants from Water

by
Xiaoxiao Zhao
,
Yiqiong Liu
,
Qimeng Zhu
and
Weitao Gong
*
School of Chemical Engineering, Dalian University of Technology, Dalian 116024, China
*
Author to whom correspondence should be addressed.
Polymers 2023, 15(11), 2565; https://doi.org/10.3390/polym15112565
Submission received: 16 April 2023 / Revised: 30 May 2023 / Accepted: 1 June 2023 / Published: 2 June 2023
(This article belongs to the Special Issue Porous Organic Polymer Materials: Synthesis, Characterization and Applications)
Browse Figures
Versions Notes

Abstract

:
Phenolic pollutants released from industrial activities seriously damage natural freshwater resources, and their elimination or reduction to safe levels is an urgent challenge. In this study, three catechol-based porous organic polymers, CCPOP, NTPOP, and MCPOP, were prepared using sustainable lignin biomass-derived monomers for the adsorption of phenolic contaminants in water. CCPOP, NTPOP, and MCPOP showed good adsorption performance for 2,4,6-trichlorophenol (TCP) with theoretical maximum adsorption capacities of 808.06 mg/g, 1195.30 mg/g, and 1076.85 mg/g, respectively. In addition, MCPOP maintained a stable adsorption performance after eight consecutive cycles. These results indicate that MCPOP is a potential material for the effective treatment of phenol pollutants in wastewater.

1. Introduction

Global population growth and industrial expansion have led to an increasing demand for freshwater resources, but water pollution has become a serious problem impeding freshwater supplies [1,2,3]. Phenolic pollutants in water present a particularly high potential risk because of their toxicity, non-biodegradability, and carcinogenicity, which makes them susceptible to human enrichment and poses serious health risks [4,5]. The development of new methods for the efficient removal of phenolic pollutants from water has become a pressing issue [6]. Adsorption [7,8] has the advantages of a wide processing range, low cost, and easy operation compared to other water treatment methods such as membrane separation [9,10,11], ion exchange [12,13,14,15], and electrochemical [16,17] and photodegradation [18,19]. However, conventional adsorbent materials such as activated carbon [20], chitosan [21], and mesoporous silica nanoparticles [22] have shown a relatively lower adsorption capacity and still need further improvement to meet the practical requirements for removing phenolic pollutants. In this sense, finding efficient, eco-friendly phenol adsorbents is always highly desired and represents a great challenge for relative researchers.
Porous organic polymers (POPs) are an emerging class of functionalized porous materials designed and assembled from organic precursors [23]. They have tremendous tunable functional properties in terms of high specific surface area, rich pore structure, and type/number of chemical groups [24,25,26,27]. However, most of the current POPs feedstock is derived from petrochemicals, and the development and reuse process inevitably results in secondary damage [28]. Accordingly, the development of sustainable renewable raw materials for the preparation of POPs as alternatives is attractive and essential. It is known that lignin is the most abundant natural renewable source of organic carbon as a supplementary resource to petroleum products [29]. The depolymerization of lignin provides various sustainable aromatic monomers [30,31], which can be used for the construction of novel biomass-derived POPs sorbents [32,33]. By selecting and assembling different biomass monomers and linkers, many fascinating POPs have been found to exhibit impressive adsorption capabilities [34,35,36,37]. Catechol has certain functional monomeric advantages as a typical lignin-derived monomer with hydrophilic o-hydroxy functional groups and different post-synthetic strategies [38]. Although some POPs prepared based on catechol have proved to have potential applications in the field of adsorption and separation, studies on their phenolic adsorption properties are still less explored [39,40].
Herein, to obtain green and efficient biomass adsorbents and to investigate the effect of catechol derivatives on the structure and adsorption properties of polymers, we chose sustainable catechol (Ccol), 2,3-naphthalene diol (Ntdiol), and 4-methyl catechol (Mcol) as monomers and formaldehyde dimethyl acetal (FDA) as a cross-linker to obtain three new POPs (CCPOP, NTPOP, and MCPOP), by using the Friedel–Crafts alkylation reaction. Cross-linked networks are formed by polymerization to form polymers with a high specific surface area, a rich pore structure, and a polyhydroxylated structure, thus enabling the more efficient adsorption of pollutants in water. The adsorption of three POPs for phenolic pollutants in water was studied systematically. As a result, three catechol-based POPs exhibit high phenol adsorption capacity compared with previously reported porous organic polymers. In particular, NTPOP and MCPOP reached 1195.30 mg/g and 1076.85 mg/g, which are greater than most POPs that have been reported. The difference between CCPOP, NTPOP, and MCPOP comes from the different structures of the catechol derivative monomers, which enable the three polymers to have different molecular sizes, specific surface areas, and phenolic pollutants’ adsorption capacities. The current work provides insights into the efficient adsorption of phenolic pollutants by sustainable biomass POPs.

2. Materials and Methods

2.1. Materials

Catechol (Ccol), 2,3-naphthalene diol (Ntdiol), and 4-methyl catechol (Mcol) were purchased from Shanghai McLean Biochemical Technology Co., Ltd. (Shanghai, China). Formaldehyde dimethyl acetal (FDA), bisphenol A (BPA), 4,4′-sulfonyldiphenol (BPS), phenol, 4-chlorophenol (4-CP), 2,4-dichlorophenol (DCP), and 2,4,6-trichlorophenol (TCP) were purchased from Sa’en Chemical Technology Co., Ltd. (Shanghai, China). 1,2-dichloroethane was purchased from Tianjin Fuyu Fine Chemical Co., Ltd. (Tianjin, China). FeCl3 was purchased from Tianjin Bodi Chemical Co., Ltd. (Tianjin, China). Methanol anhydrous was purchased from Tianjin Dongli District Tianda Chemical Reagent Factory (Tianjin, China). Activated carbon was purchased from Tianjin Beichen Fangzheng Reagent Factory (Tianjin, China).

2.2. Polymer Synthesis

The polymer synthesis process is shown in Scheme 1, according to the previously reported work [38]. In a typical Schlenk tube, 20 mmol of Ccol, Mcol, or Ntdiol was dissolved in 30 mL of 1,2-dichloroethane solvent separately. Further, 40 mmol of FDA and FeCl3 was added to the reaction mixtures under dry conditions. The resulting mixtures were stirred for 5 h at 45 °C and then heated to 80 °C for 19 h. After cooling, the resulting solids were collected by filtration and washed with methanol solvent until colorless filtrates were found. Moreover, the reaction mixtures were purified with methanol by the Soxhlet extraction process for 24 h and dried under the vacuum pump to obtain polymers, i.e., CCPOP, MCPOP, and NTPOP, respectively.

2.3. Characterization

The Fourier transform infrared (FT-IR) spectra of the polymers were tested by the JASCO IR-4100 spectrometer (JASCO, Tokyo, Japan). The solid-state 13C cross-polarization with magic-angle spinning (CP/MAS) results were collected by a 599.7 MHz nuclear magnetic resonance spectrometer (JNM-ECZ600R, Agilent, Santa Clara, CA, USA). Powder X-ray diffraction (PXRD) results were obtained by using a Rigku D/max-2400 diffractometer (40 kV, 200 mA) from 5° to 80° with a scanning rate of 2°/min (Bruker AXS, Madison, WI, USA). The scanning electron microscopy (SEM) analysis was examined by using HITACHI-SU5000 (HITACHI, Tokyo, Japan). The results of the adsorption and desorption of N2 were obtained by an analyzer called Quantachrome-Autosorb IQ (Quntachrome, Kanagawa, Japan). The thermogravimetric (TGA) analysis was executed by using Mettler Toledo TGA/DSC 3+ (Mettler Toledo, Greifensee, Switzerland) under a nitrogen atmosphere. Samples were heated from 25–800 °C with a 10 °C/min heating rate. The ultraviolet (UV) spectra of the polymers were measured by the JASCO V-750 (JASCO, Tokyo, Japan). The X-ray photoelectron spectroscopy (XPS) analysis was examined by using ESCALAB XI+ (thermo, Oxford, UK).

2.4. Batch Adsorption Experiments

Phenol, 4-CP, DCP, TCP, BPA, and BPS were used as model pollutants to study the adsorption properties of the polymers (CCPOP, NTPOP, and MCPOP). Solutions of phenol contaminants with a certain concentration gradient were prepared, the absorbance at different concentrations was measured by a UV spectrophotometer, and the peak values at the corresponding wavelengths (λPhenol = 269.8 nm, λ4-CP = 280 nm, λDCP = 284 nm, λTCP = 286.8 nm, λBPA = 276 nm, λBPS = 277 nm) were recorded. The standard curves were fitted to the absorbance concentrations according to the Lambert–Bier law. The actual concentration of the solution can be calculated from the standard curve. The polymeric adsorbents were added to an initial concentration of 100 mg/L of model aqueous solution (10 mL) for adsorption. After the adsorption experiment, the solid and liquid phases were separated by a 0.22 μm filter membrane syringe, and the filtrate was collected. The residual concentrations of phenol, 4-CP, DCP, TCP, BPA, and BPS in the filtrate were determined by UV spectrophotometry. The amount of adsorption at the equilibrium state ( Q e , mg/g) is calculated by the given equation.
Q e = ( C 0 − C e ) V m
in which  Q e  (mg/g) is the equilibrium adsorption capacity;  C 0  and  C e  (mg/L) are the initial and final equilibrium concentrations of phenol, 4-CP, DCP, TCP, BPA, and BPS in solution;  V  (mL) is the volume of solution; and  m  (mg) is the mass of the adsorbent.
Adsorption kinetics experiments were carried out at room temperature by magnetic stirring. CCPOP, NTPOP, and MCPOP (30 mg) were added to TCP aqueous solution (150 mg/L, 80 mL) and BPA aqueous solution (50 mg/L, 60 mL), respectively. The concentrations of TCP and BPA were calculated at different times by UV spectrophotometry. Pseudo-first-order and pseudo-second-order kinetic models were used to analyze the kinetics of the adsorption of phenolic pollutants. The kinetic model equations for pseudo-first-order and pseudo-second-order are as follows.
Q t = Q e ⁡ 1 − Q t e − k 1 t
Q t = k 2 Q e 2 t 1 + Q e k 2 t
in which  Q e  (mg/g) is the equilibrium adsorption amount,  t  (min) is the adsorption time,  Q t  (mg/g) is the phenolic pollutants adsorption amount at time  t  (min),  k 1  (min−1) is the pseudo primary rate constant, and  k 2  (g/(mg min)) is the pseudo secondary rate constant.
To assess the saturation adsorption capacity of the polymeric adsorbents for TCP and BPA, adsorption isotherms were tested at 25 °C. CCPOP, NTPOP, and MCPOP (4 mg) were added to an aqueous solution of TCP (concentration: 100–500 mg/L, 10 mL); CCPOP, NTPOP, and MCPOP (5 mg) were added to an aqueous solution of BPA (concentration: 50–300 mg/L, 10 mL) and adsorbed while stirring to ensure saturation of adsorption. The Langmuir and Freundlich models were used to quantify and compare the adsorption performance of different polymeric adsorbents (CCPOP, NTPOP, and MCPOP). The equations for the Langmuir and Freundlich models are as follows.
Q e = Q m K L C e 1 + K L C e
l n Q e = l n K F + 1 n l n C e
in which  K L  and  K F  are the constants of the Langmuir and Freundlich models, respectively,  1 n  is the empirical parameter of the Freundlich model,  C e  (mg/g) is the equilibrium concentration of phenolic pollutants,  Q e  (mg/g) is the equilibrium adsorption capacity, and  Q m  (mg/g) is the maximum adsorption capacity.

2.5. Adsorption Cycling Experiments

The adsorbent is desorbed and regenerated by immersion in a solution of acetone and ethanol. The precipitate was collected by centrifugal precipitation and dried at 80 °C for the next cycle. The regeneration performance of the adsorbent was explored through eight consecutive adsorption–desorption cycles. The pollutant removal efficiency after each cycle was calculated separately. Equilibrium removal efficiency (%) is calculated using the following equations.
R e m o v a l   e f f i c i e n c y   ( % ) = C 0 − C e C 0 × 100 %
where  C 0  and  C e  (mg/L) are the initial and final equilibrium concentrations of TCP in solution. The initial TCP concentration was 200 mg/L.

2.6. Adsorption Mechanism

To understand the mechanism of interaction between MCPOP and TCP, pH experiments and FT-IR spectroscopy were carried out. In the pH effect experiments, MCPOP (5 mg) was added to TCP aqueous solution (200 mg/L, 10 mL) at different pH (pH adjusted by HCl and NaOH), and the residual concentration was measured to calculate the adsorption amount.

3. Results and Discussion

3.1. Characterization of the Adsorbents

The FT-IR spectra of CCPOP, NTPOP, and MCPOP are shown in Figure 1a. For CCPOP, NTPOP, and MCPOP, the peaks at 2985 cm−1 and 2831 cm−1 (stretching vibration of C−H) are ascribed to the methylene group of the FDA. The source of the bands at 3500 cm−1 and 1200 cm−1 (O−H and C−O) is the hydroxyl group fixed on the aromatic ring. In addition, three polymers were further characterized by solid-state 13C cross-polarization magic-angle spinning (CP-MAS) NMR spectroscopy. As shown in Figure S1, the high-intensity characteristic resonance observed at 14–50 ppm represents the methylene signal of cross-linking with FDA in the framework, which indicates that the catechol-derived monomers were successfully cross-linked with FDA. Furthermore, the characteristic resonances observed at around 120–150 ppm represent the aromatic and non-substituted aromatic carbons on phenolic hydroxyl groups, and the specific resonance peaks indicate that the polymer is a chemical structure cross-linked by catechol monomers.
Powder X-ray diffraction (PXRD) plots show a broad rather than a sharp peak at around 2θ = 20° (Figure S2), indicating that all three polymers are not crystalline but amorphous structures. The XPS measurements were performed to investigate the elemental composition of CCPOP, NTPOP, and MCPOP. The XPS images (Figure 1b) indicated the existence of C and O in the CCPOP, NTPOP, and MCPOP. A consecutive series of binding energies in the range of 284.4–284.6 eV, 285.0–285.22 eV, 286.27–286.42 eV, and 288.70–288.81 eV were distinguished in the C1s XPS spectra (Figure 2a–c), which could be attributed to C=C, C−C, C−OH and C=O functional groups, respectively. The C−OH and C=O photoelectron peaks approximately appeared at 533.05 and 532.00 eV, respectively. In addition, the surface morphology of the polymers was investigated by scanning electron microscopy (SEM). As shown in Figure S3, after cross-linking to form the polymers, CCPOP and NTPOP are composed of fused small particles with partially spherical structures; in contrast, MCPOP shows a porous structure and irregular surface state. FeCl3 is loaded into the polymer by complexation with the O atoms in the catechol monomer [41].
The permanent porosities and surface areas of the three polymers were further measured and calculated by using N2 adsorption–desorption isotherm at 77 K. As shown in Figure 1c, the specific surface areas of CCPOP, NTPOP, and MCPOP were 33.89 m2/g, 93.26 m2/g, and 665.97 m2/g, respectively. MCPOP formed a type I adsorption and desorption curve while CCPOP and NTPOP formed type III adsorption and desorption graphs. Combined with pore-size distribution (PSD) (Figure 1d), the significant increase in adsorption at low pressure indicates a large number of micropores in the MCPOP. As shown in Table 1, the pore volume of MCPOP is significantly larger compared to CCPOP and NTPOP, indicating a better degree of cross-linking of MCPOP. MCPOP had large SBET and abundant pore space, which can be attributed to two reasons: (1) Different catechol monomers have different effects on the pore size, pore volume, and specific surface area of the polymer. Mcol as a reaction precursor significantly increases the pore volume and specific surface area of the polymer. The spatial site resistance effect is also an important factor. (2) The adjacent hydroxyl structure may not be conducive to Friedel-Crafts reaction cross-linking to form a network structure, as the FeCl3 catalyst tends to complex with the O atoms to deactivate the catalyst [31].
TGA was used for the thermal analysis of the three catechol polymers, as shown in Figure S4. First, the weight loss between room temperature and 100 °C was caused by the evaporation of water from the samples. The weights of the three catechol polymers remained essentially constant between 100 °C and 250 °C, indicating that the evaporation of crystalline water from the polymers was complete. Between 250 °C and 450 °C, the polymer weight loss increased sharply, presumably due to the decomposition of the polymers.

3.2. Batch Adsorption Experiments

To investigate the adsorption performance of the three polymers on phenolic pollutants in water, batch adsorption experiments were first performed on phenol, 4−CP, DCP, TCP, BPA, and BPS, as shown in Figure 3 and Figure S5. The 100 mg/L TCP solution was passed through the filter membrane as a blank control experiment. The error of approximately 4% is within reasonable limits. When the initial concentration of phenolic pollutants in water was 100 mg/L, all three polymers were able to adsorb them to some extent, and the adsorption amounts are shown in Table S1. Comparing the three polymer adsorbents, MCPOP had the highest adsorption capacity. For chlorophenols, the adsorption capacity of the adsorbent increased with the number of −Cl substituents on the benzene ring. Chlorophenol adsorption mainly relies on hydrogen bonding, and the more the number of −Cl substituents increases, the easier it is to form hydrogen bonds between the adsorbent and the chlorophenols. This leads to the significant adsorption of TCP by the polymer. In addition, CCPOP, NTPOP, and MCPOP also showed high adsorption amounts for BPA (0.3536 mmol/g, 0.2712 mmol/g, and 0.6368 mmol/g). Therefore, TCP and BPA were selected to further investigate the adsorption properties of the polymers.

3.3. Adsorption Kinetics

To study the adsorption capacity of polymeric adsorbents on TCP and BPA, we investigated the adsorption kinetics of TCP and BPA. The data are shown in Figure 4a–c and Figure S6a–c.
The adsorption of TCP rapidly increased in the initial stage of adsorption, indicating that CCPOP, NTPOP, and MCPOP have significant adsorption affinity for TCP. Moreover, during the adsorption of BPA, MCPOP reached the adsorption equilibrium within 60 min, and CCPOP and MCPOP reached the adsorption equilibrium within 480 min. The adsorption efficiency of the adsorbents on TCP and BPA was evaluated by pseudo-first-order and pseudo-second-order kinetic models. The corresponding parameters and correlation coefficients obtained from the two models are listed in Table 2 and Table S2. Predictably, for CCPOP, NTPOP, and MCPOP adsorbents, pseudo-second-order kinetics can better describe TCP and BPA adsorption (R2 > 0.996), indicating that the adsorption of CCPOP, NTPOP, and MCPOP is mainly by chemisorption.

3.4. Adsorption Isotherms

The maximum adsorption capacities of polymeric adsorbents for TCP and BPA were evaluated by adsorption isotherms.
The initial concentrations of aqueous solutions of TCP were in the range of 100–500 mg/L, and the initial concentrations of BPA were in the range of 50–300 mg/L. The adsorption processes of TCP and BPA were fitted using Langmuir and Flanders models, as shown in Figure 5a–c and Figure S7a–c, and the relevant parameters and correlation coefficients are listed in Table 3 and Table S3. The maximum adsorption amounts of TCP by CCPOP, NTPOP, and MCPOP were 808.06 mg/g, 1195.30 mg/g, and 1076.85 mg/g, respectively; the maximum adsorption amounts of BPA by CCPOP, NTPOP, and MCPOP were 203.94 mg/g, 272.94 mg/g, and 264.48 mg/g, respectively. The adsorption capacities of several representative materials in phenol solutions are presented in Table 4. The results illustrated that NTPOP and MCPOP have a higher adsorption capacity in solution compared to the reported adsorbent materials [42,43,44,45,46,47]. The adsorption capacity of activated carbon for TCP is 16.23 mg/g. The new polymers have a higher adsorption capacity for TCP. The higher saturation adsorption capacity can be attributed to the large specific surface area of the polymeric adsorbent, the rich pore structure, and the presence of a large number of o-hydroxyl groups on the benzene ring of the polymer. The adsorption process is influenced by several different factors such as hydrogen bonding, mass transfer, and π−π interactions. The polymers are structurally different, but the combined effect of many factors results in similar adsorption capacities.

3.5. Adsorption Cycling

The recoverability of phenolic adsorbents is an important indicator for achieving industrial applications. Specifically, the recoverability of MCPOP for TCP was investigated by cyclic adsorption–desorption experiments. As shown in Figure 6, after eight adsorption–desorption regeneration cycles, the removal efficiency of TCP decreased slightly and remained above 80%; presumably, the decrease in removal was mainly due to the partial loss of polymeric adsorbent during the cyclic regeneration process.

3.6. Adsorption Mechanism

To further analyze the adsorption mechanism of MCPOP-adsorbed TCP, we performed pH experiments and FT-IR spectroscopy studies on MCPOP.
As shown in Figure 7a, the adsorption of MCPOP was high and relatively stable when the pH was in the range of 3.0 to 8.0, but it decreased sharply as the pH in the solution continued to increase. It is presumed that this is due to the protonation of TCP under acidic conditions, which gives MCPOP the characteristics of strong electrostatic attraction and adhesion to TCP. However, under alkaline conditions, TCP deprotonates and forms electrostatic repulsion, resulting in the poorer adhesion of ionized MCPOP.
The FT-IR spectra of MCPOP polymer adsorbent before and after the adsorption of TCP are shown in Figure 7b, where the original −OH of MCPOP was red-shifted (from 3372 to 3341 cm−1) after adsorption, indicating the formation of hydrogen bonds between MCPOP and TCP [48]. Based on the above adsorption model fitting, pH experiments, and instrumental analysis results, Figure 8 shows a schematic representation of the adsorption of TCP by MCPOP, elucidating the electrostatic interactions, π–π interactions, and hydrogen bonding interactions between the adsorbent and the contaminant.

4. Conclusions

In this study, three new polyhydroxy biomass POPs, CCPOP, NTPOP, and MCPOP, were successfully constructed by cross-linking for sustainable catechol as the functional monomer and FDA as the linker. The small structural variations of the catechol derivatives produced significant differences in the specific surface area of the polymers, with CCPOP having a specific surface area of 33.89 m2/g and MCPOP having a specific surface area of 665.97 m2/g. As a result of the adsorption, the POPs showed highly efficient phenolic pollutants adsorption capacities of 808.06 mg/g (CCPOP), 1195.30 mg/g (NTPOP), and 1076.85 mg/g (MCPOP), which is much better than previously reported for POPs adsorbent materials, especially biomass materials. Moreover, the MCPOP in cycling experiments maintained an adsorption efficiency of over 80% after 10 cycles, which is more suitable for complex and realistic environments. This study is expected to facilitate the application of bio-based porous polymers in the field of phenolic pollutant adsorption.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/polym15112565/s1, Figure S1: Solid-state 13C NMR spectra for CCPOP, NTPOP, and MCPOP; Figure S2: X-ray diffraction (XRD) of CCPOP, NTPOP, and MCPOP; Figure S3: SEM images for CCPOP, NTPOP, and MCPOP; Figure S4: TGA curves for CCPOP, NTPOP, and MCPOP; Figure S5: UV-vis spectra of BPA and BPS aqueous solution; Table S1: The adsorption capacity of phenol, 4-CP, DCP, TCP, BPA, and BPS for CCPOP, NTPOP, and MCPOP. (Initial solution concentration: 100 mg/L); Figure S6: Kinetic modeling of BPA adsorption onto CCPOP (a), NTPOP (b), and MCPOP (c). (Adsorbents: 30 mg, initial concentration: 50 mg/L, V = 60 mL, temperature: 25 °C); Table S2: Parameters of the pseudo-first-order and pseudo-second-order models of adsorption BPA; Figure S7: Isothermal adsorption curves of BPA onto CCPOP (a), NTPOP (b), and MCPOP (c). (Adsorbents: 5 mg, V = 10 mL, temperature: 25 °C); Table S3: Parameters of Langmuir and Freundlich adsorption isotherm models of adsorption BPA.

Author Contributions

W.G. conceived and designed the experiments; X.Z. and Y.L. completed the synthesis; X.Z., Y.L. and Q.Z. analyzed the data and wrote the manuscript. All the authors discussed the results and commented on and proofread the manuscript. All authors have read and agreed to the published version of the manuscript.

Funding

Natural Science Foundation of Liaoning Province [No. 2019-MS-046].

Institutional Review Board Statement

Not applicable.

Data Availability Statement

All data related to this study are presented in this publication.

Acknowledgments

We are grateful for financial support from the Natural Science Foundation of Liaoning Province (No. 2019-MS-046), and the authors acknowledge the assistance of the DUT Instrumental Analysis Center.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Huggins, X.; Gleeson, T.; Kummu, M.; Zipper, S.C.; Wada, Y.; Troy, T.J.; Famiglietti, J.S. Hotspots for Social and Ecological Impacts from Freshwater Stress and Storage Loss. Nat. Commun. 2022, 13, 439–449. [Google Scholar] [CrossRef]
  2. Gleick, P.H.; Cooley, H. Freshwater Scarcity. Annu. Rev. Environ. Res. 2021, 46, 319–348. [Google Scholar] [CrossRef]
  3. Mulcahy, E. Too Little Effort in Tackling Pollution Is Resulting in Too Many Lives Being Lost. BMJ 2022, 377, 1481–1482. [Google Scholar] [CrossRef]
  4. Cao, X.T.; Wang, K.; Feng, X.S. Removal of Phenolic Contaminants from Water by Pervaporation. J. Membr. Sci. 2021, 623, 119043–119058. [Google Scholar] [CrossRef]
  5. Panigrahy, N.; Priyadarshini, A.; Sahoo, M.M.; Verma, A.K.; Daverey, A.; Sahoo, N.K. A Comprehensive Review on Eco-Toxicity and Biodegradation of Phenolics: Recent Progress and Future Outlook. Environ. Technol. Innov. 2022, 27, 102423–102454. [Google Scholar] [CrossRef]
  6. Li, K.J.; Yang, Y.; Bacha, A.U.R.; Feng, Y.Q.; Ajmal, S.; Nabi, I.; Zhang, L.W. Efficiently Complete Degradation of 2,4-DCP Using Sustainable Photoelectrochemical Reduction and Sequential Oxidation Method. Chem. Eng. J. 2019, 378, 122191–122201. [Google Scholar] [CrossRef]
  7. Lu, S.C.; Liu, Q.L.; Han, R.; Guo, M.; Shi, J.Q.; Song, C.F.; Ji, N.; Lu, X.B.; Ma, D.G. Potential Applications of Porous Organic Polymers as Adsorbent for the Adsorption of Volatile Organic Compounds. J. Environ. Sci. 2021, 105, 184–203. [Google Scholar] [CrossRef] [PubMed]
  8. Garba, Z.N.; Zhou, W.M.; Lawan, I.; Xiao, W.; Zhang, M.X.; Wang, L.W.; Chen, L.H.; Yuan, Z.H. An Overview of Chlorophenols as Contaminants and Their Removal from Wastewater by Adsorption: A Review. J. Environ. Manag. 2019, 241, 59–75. [Google Scholar] [CrossRef]
  9. Li, X.; Huang, G.H.; Chen, X.J.; Huang, J.; Li, M.N.; Ying, J.N.; Liang, Y.; Yao, Y.; Li, Y.P. A Review on Graphitic Carbon Nitride (g-C3N4) Based Hybrid Membranes for Water and Wastewater Treatment. Sci. Total Environ. 2021, 792, 148462–148481. [Google Scholar] [CrossRef]
  10. Liu, Y.L.; Zhu, J.Y.; Zheng, J.F.; Gao, X.Q.; Tian, M.M.; Wang, X.M.; Xie, Y.F.; Zhang, Y.T.; Volodin, A.; Bruggen, B.V.D. Porous Organic Polymer Embedded Thin-Film Nanocomposite Membranes for Enhanced Nanofiltration Performance. J. Membr. Sci. 2020, 602, 117982–117989. [Google Scholar] [CrossRef]
  11. Ren, Y.L.; Zhu, J.Y.; Cong, S.Z.; Wang, J.; Bruggen, B.V.D.; Liu, J.D.; Zhang, Y.T. High Flux Thin Film Nanocomposite Membranes Based on Porous Organic Polymers for Nanofiltration. J. Membr. Sci. 2019, 585, 19–28. [Google Scholar] [CrossRef]
  12. Chen, K.F.; Hao, S.L.; Lyu, H.; Luo, G.; Zhang, S.C.; Cheng, J.M. Ion Exchange Separation for Recovery of Monosaccharides, Organic Acids and Phenolic Compounds from Hydrolysates of Lignocellulosic Biomass. Sep. Purif. Technol. 2017, 172, 100–106. [Google Scholar] [CrossRef]
  13. Li, B.Y.; Zhang, Y.N.; Ma, D.X.; Xing, Z.Y.; Ma, T.L.; Shi, Z.; Jin, X.L.; Ma, S.Q. Creation of a New Type of Ion Exchange Material for Rapid, High-Capacity, Reversible and Selective Ion Exchange without Swelling and Entrainment. Chem. Sci. 2016, 7, 2138–2144. [Google Scholar] [CrossRef] [Green Version]
  14. Zhang, Z.Y.; Hu, W.J.; Ruan, W.J.; Ai, H.Y.; Yuan, B.L.; Fu, M.L. Highly Improved Dechlorination of 2,4-Dichlorophenol in Aqueous Solution by Fe/Ni Nanoparticles Supported by Polystyrene Resin. Chemosphere 2021, 266, 128976–128983. [Google Scholar] [CrossRef]
  15. Zimmermann, K.; Wright, J.; Bérubé, P.; Barbeau, B.; Mohseni, M. Biological Ion Exchange Capable of Sulphate-Based Secondary Ion Exchange during Long-Term DOC Removal. Water Res. 2021, 196, 117036–117043. [Google Scholar] [CrossRef]
  16. Wu, S.H.; Liu, H.Y.; Lin, Y.; Yang, C.P.; Lou, W.; Sun, J.T.; Du, C.; Zhang, D.M.; Nie, L.J.; Yin, K.; et al. Insights into Mechanisms of UV/Ferrate Oxidation for Degradation of Phenolic Pollutants: Role of Superoxide Radicals. Chemosphere 2020, 244, 125490–125499. [Google Scholar] [CrossRef] [PubMed]
  17. Pei, S.Z.; Wang, Y.; You, S.J.; Li, Z.G.; Ren, N.Q. Electrochemical Removal of Chlorophenol Pollutants by Reactive Electrode Membranes: Scale-Up Strategy for Engineered Applications. Engineering 2022, 9, 77–84. [Google Scholar] [CrossRef]
  18. Hunge, Y.M.; Yadav, A.A.; Khan, S.; Takagi, K.; Suzuki, N.; Teshima, K.; Terashima, C.; Fujishima, A. Photocatalytic Degradation of Bisphenol A Using Titanium Dioxide@nanodiamond Composites under UV Light Illumination. J. Colloid. Interface Sci. 2021, 582, 1058–1066. [Google Scholar] [CrossRef]
  19. Hunge, Y.M.; Yadav, A.A.; Kang, S.-W.; Kim, H. Facile Synthesis of Multitasking Composite of Silver Nanoparticle with Zinc Oxide for 4-Nitrophenol Reduction, Photocatalytic Hydrogen Production, and 4-Chlorophenol Degradation. J. Alloys Compd. 2022, 928, 167133. [Google Scholar] [CrossRef]
  20. Domínguez, J.R.; Durán-Valle, C.J.; Mateos-García, G. Synthesis and Characterisation of Acid/Basic Modified Adsorbents. Application for Chlorophenols Removal. Environ. Res. 2022, 207, 112187–112193. [Google Scholar] [CrossRef] [PubMed]
  21. Zhou, L.C.; Meng, X.G.; Fu, J.W.; Yang, Y.C.; Yang, P.; Mi, C. Highly Efficient Adsorption of Chlorophenols onto Chemically Modified Chitosan. Appl. Surf. Sci. 2014, 292, 735–741. [Google Scholar] [CrossRef]
  22. Hu, H.T.; Miao, K.K.; Luo, X.L.; Guo, S.F.; Yuan, X.Q.; Pei, F.; Qian, H.M.; Feng, G.D. Efficient Fenton-like Treatment of High-Concentration Chlorophenol Wastewater Catalysed by Cu-Doped SBA-15 Mesoporous Silica. J. Clean. Prod. 2021, 318, 128632–128641. [Google Scholar] [CrossRef]
  23. Das, S.; Heasman, P.; Ben, T.; Qiu, S.L. Porous Organic Materials: Strategic Design and Structure–Function Correlation. Chem. Rev. 2017, 117, 1515–1563. [Google Scholar] [CrossRef]
  24. Xu, F.; Wu, D.C.; Fu, R.W.; Wei, B.Q. Design and Preparation of Porous Polymers. Chem. Rev. 2017, 20, 3959–4015. [Google Scholar] [CrossRef]
  25. Dawson, R.; Cooper, A.I.; Adams, D.J. Nanoporous Organic Polymer Networks. Prog. Polym. Sci. 2012, 37, 530–563. [Google Scholar] [CrossRef]
  26. Gong, W.T.; Deng, X.R.; Dong, K.X.; Liu, L.; Ning, G.L. A Boranil-Based Conjugated Microporous Polymer for Efficient Visible-Light-Driven Heterogeneous Photocatalysis. Polym. Chem. 2021, 12, 3153–3159. [Google Scholar] [CrossRef]
  27. Zhang, S.Y.; Gong, W.T.; Qv, W.D.; Deng, X.R.; Dong, K.X.; Zhang, S.Y.; Ning, G.L. Construction of Ionic Porous Organic Polymers (IPOPs) via Pyrylium Mediated Transformation. Chin. J. Polym. Sci. 2020, 38, 958–964. [Google Scholar] [CrossRef]
  28. Wu, Q.H.; Song, Y.H.; Wang, Q.Q.; Liu, W.H.; Hao, L.; Wang, Z.; Wang, C. Combination of Magnetic Solid-Phase Extraction and HPLC-UV for Simultaneous Determination of Four Phthalate Esters in Plastic Bottled Juice. Food Chem. 2021, 339, 127855–127863. [Google Scholar] [CrossRef] [PubMed]
  29. Shen, X.J.; Zhang, C.F.; Han, B.X.; Wang, F. Catalytic Self-Transfer Hydrogenolysis of Lignin with Endogenous Hydrogen: Road to the Carbon-Neutral Future. Chem. Soc. Rev. 2022, 51, 1608–1628. [Google Scholar] [CrossRef]
  30. Pińkowska, H.; Wolak, P.; Złocińska, A. Hydrothermal Decomposition of Alkali Lignin in Sub- and Supercritical Water. Chem. Eng. J. 2012, 187, 410–414. [Google Scholar] [CrossRef]
  31. Li, Y.D.; Shuai, L.; Kim, H.; Motagamwala, A.H.; Mobley, J.K.; Yue, F.X.; Tobimatsu, Y.; Havkin-Frenkel, H.; Chen, F.; Dixon, R.A.; et al. An “Ideal Lignin” Facilitates Full Biomass Utilization. Sci. Adv. 2018, 4, 2375–2548. [Google Scholar] [CrossRef] [Green Version]
  32. Liu, Y.L.; Zhou, X.; Jin, C.; Liu, G.F.; Liu, Z.S.; Kong, Z.W. Efficient and Rapid Removal of Typical Phenolic Compounds from Water with Biobased Porous Organic Polymers. Ind. Crops Prod. 2022, 184, 114971–114981. [Google Scholar] [CrossRef]
  33. Shao, L.S.; Liu, N.; Wang, L.Z.; Sang, Y.F.; Wan, H.N.; Zhan, P.; Zhang, L.; Huang, J.H.; Chen, J.N. Facile Preparation of Oxygen-Rich Porous Polymer Microspheres from Lignin-Derived Phenols for Selective CO2 Adsorption and Iodine Vapor Capture. Chemosphere 2022, 288, 132499–132509. [Google Scholar] [CrossRef]
  34. Xu, M.M.; An, Y.J.; Wang, Q.Q.; Wang, Z.; Zhou, J.H.; Wu, Q.H. Construction of Hydroxyl Functionalized Magnetic Porous Organic Framework for the Effective Detection of Organic Micropollutants in Water, Drink and Cucumber Samples. J. Hazard. Mater. 2021, 412, 125307–125319. [Google Scholar] [CrossRef]
  35. Huang, L.J.; Shuai, Q.; Hu, S.Z. Tannin-Based Magnetic Porous Organic Polymers as Robust Scavengers for Methylene Blue and Lead Ions. J. Clean. Prod. 2019, 215, 280–289. [Google Scholar] [CrossRef]
  36. Jiang, S.C.; Meng, X.F.; Xu, M.M.; Li, S.F.; Wang, Q.Q.; Liu, W.H.; Hao, L.; Wang, J.M.; Wang, C.; Wang, Z.; et al. Green Synthesis of Novel Magnetic Porous Organic Polymer for Magnetic Solid Phase Extraction of Neonicotinoids in Lemon Juice and Honey Samples. Food Chem. 2022, 383, 132599–132607. [Google Scholar] [CrossRef] [PubMed]
  37. Xu, M.M.; Wang, J.M.; Zhang, L.H.; Wang, Q.Q.; Liu, W.H.; An, Y.J.; Hao, L.; Wang, C.; Wang, Z.; Wu, Q.H. Construction of Hydrophilic Hypercrosslinked Polymer Based on Natural Kaempferol for Highly Effective Extraction of 5-Nitroimidazoles in Environmental Water, Honey and Fish Samples. J. Hazard. Mater. 2022, 429, 128288–128296. [Google Scholar] [CrossRef]
  38. Patil, N.; Jérôme, C.; Detrembleur, C. Recent Advances in the Synthesis of Catechol-Derived (Bio)Polymers for Applications in Energy Storage and Environment. Prog. Polym. Sci. 2018, 82, 34–91. [Google Scholar] [CrossRef]
  39. Xia, N.N.; Zhang, H.Y.; Hu, Z.Z.; Kong, F.G.; He, F. A Functionalized Bio-Based Material with Abundant Mesopores and Catechol Groups for Efficient Removal of Boron. Chemosphere 2021, 263, 128202–128211. [Google Scholar] [CrossRef] [PubMed]
  40. Zhang, S.P.; Li, Y.K.; Shi, C.H.; Guo, F.Y.; He, C.Z.; Cao, Z.; Hu, J.; Cui, C.Z.; Liu, H.L. Induced-Fit Adsorption of Diol-Based Porous Organic Polymers for Tetracycline Removal. Chemosphere 2018, 212, 937–945. [Google Scholar] [CrossRef]
  41. Modak, A.; Bhanja, P.; Bhaumik, A. Microporous Nanotubes and Nanospheres with Iron-Catechol Sites: Efficient Lewis Acid Catalyst and Support for Ag Nanoparticles in CO2 Fixation Reaction. Chem.-Eur. J. 2018, 24, 14189–14197. [Google Scholar] [CrossRef] [PubMed]
  42. Oladipo, A.C.; Tella, A.C.; Clayton, H.S.; Olayemi, V.T.; Akpor, O.B.; Dembaremba, T.O.; Ogunlaja, A.S.; Clarkson, G.J.; Walton, R.I. A Zinc-Based Coordination Polymer as Adsorbent for Removal of Trichlorophenol from Aqueous Solution: Synthesis, Sorption and DFT Studies. J. Mol. Struct. 2022, 1247, 131274. [Google Scholar] [CrossRef]
  43. Lv, X.; Li, S. Graphene Oxide–Crospolyvinylpyrrolidone Hybrid Microspheres for the Efficient Adsorption of 2,4,6-Trichlorophenol. ACS Omega 2020, 5, 18862–18871. [Google Scholar] [CrossRef]
  44. Huang, Q.; Chai, K.; Zhou, L.; Ji, H. A Phenyl-Rich β-Cyclodextrin Porous Crosslinked Polymer for Efficient Removal of Aromatic Pollutants: Insight into Adsorption Performance and Mechanism. Chem. Eng. J. 2020, 387, 124020. [Google Scholar] [CrossRef]
  45. Simsek, E.B.; Aytas, B.; Duranoglu, D.; Beker, U.; Trochimczuk, A.W. A Comparative Study of 2-Chlorophenol, 2,4-Dichlorophenol, and 2,4,6-Trichlorophenol Adsorption onto Polymeric, Commercial, and Carbonaceous Adsorbents. Desalination Water Treat. 2016, 57, 29488–29499. [Google Scholar] [CrossRef]
  46. Wang, Y.X.; Bi, Y.P.; Cui, Y.Y.; Yang, C.X. Synthesis of Crown Ether-Based Microporous Organic Networks: A New Type of Efficient Adsorbents for Chlorophenols. J. Hazard. Mater. 2023, 443, 130268. [Google Scholar] [CrossRef] [PubMed]
  47. Hu, X.; Xu, G.; Zhang, H.; Li, M.; Tu, Y.; Xie, X.; Zhu, Y.; Jiang, L.; Zhu, X.; Ji, X.; et al. Multifunctional β-Cyclodextrin Polymer for Simultaneous Removal of Natural Organic Matter and Organic Micropollutants and Detrimental Microorganisms from Water. ACS Appl. Mater. Interfaces 2020, 12, 12165–12175. [Google Scholar] [CrossRef]
  48. Yang, Z.; Zhang, Y.; Wang, X.Z.; Tian, Z.Q.; Yang, W.B.; Graham, N.J.D. Efficient Adsorption of Four Phenolic Compounds Using a Robust Nanocomposite Fabricated by Confining 2D Porous Organic Polymers in 3D Anion Exchangers. Chem. Eng. J. 2020, 396, 125296–125306. [Google Scholar] [CrossRef]
Polymers 15 02565 sch001 550
Scheme 1. Chemical structures of catechol derivatives and the synthesis of POPs.
Scheme 1. Chemical structures of catechol derivatives and the synthesis of POPs.
Polymers 15 02565 sch001
Polymers 15 02565 g001 550
Figure 1. (a) Fourier transform infrared (FT-IR); (b) X-ray photoelectron spectroscopy (XPS); (c) N2 adsorption–desorption curves; (d) pore-size distribution curve of CCPOP, NTPOP, and MCPOP.
Figure 1. (a) Fourier transform infrared (FT-IR); (b) X-ray photoelectron spectroscopy (XPS); (c) N2 adsorption–desorption curves; (d) pore-size distribution curve of CCPOP, NTPOP, and MCPOP.
Polymers 15 02565 g001
Polymers 15 02565 g002 550
Figure 2. C1s (a) and O1s (d) spectra of CCPOP, C1s (b) and O1s (e) spectra of NTPOP, and C1s (c) and O1s (f) spectra of MCPOP.
Figure 2. C1s (a) and O1s (d) spectra of CCPOP, C1s (b) and O1s (e) spectra of NTPOP, and C1s (c) and O1s (f) spectra of MCPOP.
Polymers 15 02565 g002
Polymers 15 02565 g003a 550Polymers 15 02565 g003b 550
Figure 3. UV-vis spectra of (a) phenol, (b) 4-CP, (c) DCP, and (d) TCP aqueous solution. (Adsorbents: 5 mg, initial concentration: 100 mg/L, t = 8 h).
Figure 3. UV-vis spectra of (a) phenol, (b) 4-CP, (c) DCP, and (d) TCP aqueous solution. (Adsorbents: 5 mg, initial concentration: 100 mg/L, t = 8 h).
Polymers 15 02565 g003aPolymers 15 02565 g003b
Polymers 15 02565 g004 550
Figure 4. Kinetic modeling of TCP adsorption onto (a) CCPOP, (b) NTPOP, and (c) MCPOP. (Adsorbents: 30 mg, initial concentration: 150 mg/L, V = 80 mL, temperature: 25 °C).
Figure 4. Kinetic modeling of TCP adsorption onto (a) CCPOP, (b) NTPOP, and (c) MCPOP. (Adsorbents: 30 mg, initial concentration: 150 mg/L, V = 80 mL, temperature: 25 °C).
Polymers 15 02565 g004
Polymers 15 02565 g005 550
Figure 5. Isothermal adsorption curves of TCP onto (a) CCPOP, (b) NTPOP, and (c) MCPOP. (Adsorbents: 4 mg, V = 10 mL, temperature: 25 °C).
Figure 5. Isothermal adsorption curves of TCP onto (a) CCPOP, (b) NTPOP, and (c) MCPOP. (Adsorbents: 4 mg, V = 10 mL, temperature: 25 °C).
Polymers 15 02565 g005
Polymers 15 02565 g006 550
Figure 6. Removal efficiency of TCP by MCPOP in different cycles. (Adsorbents: 5 mg, V = 10 mL, C0 = 200 mg/L, t = 600 min).
Figure 6. Removal efficiency of TCP by MCPOP in different cycles. (Adsorbents: 5 mg, V = 10 mL, C0 = 200 mg/L, t = 600 min).
Polymers 15 02565 g006
Polymers 15 02565 g007 550
Figure 7. (a) The effect of pH on the adsorption of TCP by MCPOP; (b) FT-IR spectra of before and after loading phenolic pollutants.
Figure 7. (a) The effect of pH on the adsorption of TCP by MCPOP; (b) FT-IR spectra of before and after loading phenolic pollutants.
Polymers 15 02565 g007
Polymers 15 02565 g008 550
Figure 8. Adsorption mechanism of MCPOP for TCP.
Figure 8. Adsorption mechanism of MCPOP for TCP.
Polymers 15 02565 g008
Table
Table 1. Information on the polymers’ specific surface area, pore volume, and main pore size.
Table 1. Information on the polymers’ specific surface area, pore volume, and main pore size.
SamplesSBET (m2/g)VTotal (cm3/g)Pore Size (nm)
CCPOP33.890.052.38
NTPOP93.260.222.00
MCPOP665.970.420.67
Table
Table 2. Parameters of the pseudo-first-order and pseudo-second-order models of adsorption TCP.
Table 2. Parameters of the pseudo-first-order and pseudo-second-order models of adsorption TCP.
ModelsParametersCCPOPNTPOPMCPOP
Pseudo-first-order modelQe (mg/g)167.9811166.6401316.5042
k1 (min−1)0.07320.07460.1718
R20.97510.99500.9840
Pseudo-second-order modelQe (mg/g)182.6841180.6428335.2129
k2 (g·mg−1·min−1)5.7793 × 10−46.0143 × 10−47.7736 × 10−4
R20.99670.99780.9999
Table
Table 3. Parameters of Langmuir and Freundlich adsorption isotherm models of adsorption TCP.
Table 3. Parameters of Langmuir and Freundlich adsorption isotherm models of adsorption TCP.
ModelsParametersCCPOPNTPOPMCPOP
LangmuirQm (mg/g)808.061195.301076.85
KL (L/mg)0.00560.00390.0138
R20.99980.99270.9664
Freundlichn0.60271.60350.4672
KF [(mg·g−1)(mg·L−1)−1/n]17.251617.952568.5325
R20.98380.99910.9999
Table
Table 4. Comparison of adsorption rates and  Q m  with reported adsorbents.
Table 4. Comparison of adsorption rates and  Q m  with reported adsorbents.
AbsorbentsEquilibrium Time (min)Qm (mg/g)References
[Zn(hba)2(tmdp)]n180207.8[42]
GO-PVPP240466.7[43]
TEPM-MON3294.6[46]
β-CDP10108.0[47]
PCD-PCP(L)150816.5[48]
PCD-PCP(H)150647.6[48]
CCPOP120808.06This work
NTPOP1201195.30This work
MCPOP601076.85This work
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Zhao, X.; Liu, Y.; Zhu, Q.; Gong, W. Catechol-Based Porous Organic Polymers for Effective Removal of Phenolic Pollutants from Water. Polymers 2023, 15, 2565. https://doi.org/10.3390/polym15112565

AMA Style

Zhao X, Liu Y, Zhu Q, Gong W. Catechol-Based Porous Organic Polymers for Effective Removal of Phenolic Pollutants from Water. Polymers. 2023; 15(11):2565. https://doi.org/10.3390/polym15112565

Chicago/Turabian Style

Zhao, Xiaoxiao, Yiqiong Liu, Qimeng Zhu, and Weitao Gong. 2023. "Catechol-Based Porous Organic Polymers for Effective Removal of Phenolic Pollutants from Water" Polymers 15, no. 11: 2565. https://doi.org/10.3390/polym15112565

APA Style

Zhao, X., Liu, Y., Zhu, Q., & Gong, W. (2023). Catechol-Based Porous Organic Polymers for Effective Removal of Phenolic Pollutants from Water. Polymers, 15(11), 2565. https://doi.org/10.3390/polym15112565

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.