Next Article in Journal
Development of a Method for Peeling Off Paper from Celluloid Pictures for Animation Films
Previous Article in Journal
Radiation-Grafting on Polypropylene Copolymer Membranes for Using in Cadmium Adsorption
Previous Article in Special Issue
Preparation Methods and Functional Characteristics of Regenerated Keratin-Based Biofilms
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 15
Issue 3
10.3390/polym15030689
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Proporties and Synthesis of Biosilver Nanofilms for Antimicrobial Food Packaging

by
Gülay Baysal
1,2,*,
Cihat Demirci
2 and
Haydar Özpinar
1
1
Nutrition and Dietetics, Faculty of Health Sciences, Istanbul Aydin University, 34295 Istanbul, Turkey
2
Food Engineering, Engineering Faculty, Istanbul Aydin University, 34295 Istanbul, Turkey
*
Author to whom correspondence should be addressed.
Polymers 2023, 15(3), 689; https://doi.org/10.3390/polym15030689
Submission received: 29 June 2022 / Revised: 3 August 2022 / Accepted: 16 January 2023 / Published: 30 January 2023
(This article belongs to the Special Issue Bio-Based Polymer Materials: Contribution to Advancing Circular Economy II)
Browse Figures
Versions Notes

Abstract

:
In this original research, biodegradable corn starch (CS) and wheat gluten (wg)-based silver nanofilms were synthesized and analyzed by using goji berry extract taurine (ta), garlic extract (GC), whey powder (wh), and montmorillonite clay nanoparticles. Antibacterial-corn-starch-based nano films were analyzed by using the methods of high-performance liquid chromatography (HPLC), Fourier Transform infrared spectroscopy (FTIR-ATR), X-ray diffraction (XRD), dynamic and mechanical (DMA) analysis, and scanning electron microscopy (SEM). In addition, the antibacterial resistances of the corn starch nano films against the bacteria Salmonella and Staphylococcus aureus (S. aureus) and Listeria monocytogenes were examined and the migration assays were carried out. The migration analysis results of CS1, CS2, and CS3 nanocomposite films were found as 0.305, 0.297, and 0.297 mg/dm2, respectively. The inhibition zone of CS1, CS2, and CS3 nanocomposite films were found as 1547, 386, and 1884 mm2 against Salmonella bacteria. The results show that silver nanofilms are suitable as packaging films for the production of packaging in milk and dairy products, liquid foods, and acidic foods.

Graphical Abstract

1. Introduction

Goji berries have strong antioxidant features and a high level of beta carotene, iron, vitamins (C, B1, B6, and B2), and protein, as well as 18 amino acids and 21 minerals; moreover, they have more vitamin C than an oranger. They provide a feeling of satiety with its high fiber content of 21%. They are beneficial for treating high cholesterol and cancer since they protect retina cells and bones, etc., and they have bioactive benefits. It is also known that they provide energy, facilitate digestion, and are good for depression and anxiety disorders [1,2]. In this study, taurine was extracted from goji berries.
The taurine is a thiol-containing free amino acid that does not participate in the structure of proteins. As an essential amino acid and pharmacologically speaking, its clinical uses are expanding. The taurine extract, which is colorless, water-soluble, and strongly acidic due to its sulfonate group, has high antioxidant and antibacterial properties, much like whey powder [3,4,5].
As is known, the synthetic polymers used in food packaging contain components that are very harmful to the environment and human health. Petroleum-based synthetic polymers and derivatives cause serious damage to the environment due to the waste they transform. Plastic packaging materials, which are widely used in food packaging throughout the world, are a serious problem [6,7]. The mixing time of plastics with nature can last for centuries. In this sense, the need for biodegradable biopolymers is increasing day by day, especially in food packaging. However, their use in food packaging is limited due to the poor mechanical and barrier properties of biopolymers. Therefore, the biodegradable biopolymers are in great need of filling materials that improve their mechanical and barrier properties, as well as the bioactive components that enhance their antibacterial properties. Obtaining the preferred bioactive components from plant extracts, on the other hand, prevents the risks that may occur due to harmful migrations in food packages [8,9]. Additionally, antibacterial biopolymer packaging films, which can degrade in a short period of time without harming nature, are gaining importance [9,10]. In particular, antimicrobial food-packaging films prolong the shelf life of foods by inactivating the growth of pathogenic microorganisms in food products [11,12,13,14].
In this study, biopolymer food-packaging films, which display antimicrobial activity and contribute to the protection of nature in a short time, were synthesized. Initially, montmorillonite (Mt) clays were modified with taurine (ta) extracts obtained from goji berries dried at different temperatures, and the organoclays were synthesized. The resulting organoclays interacted with antibacterial garlic extract and whey powder, and corn starch and wheat gluten biopolymers. The antibacterial biopolymer packaging silver nanofilms, which have high antibacterial resistance, were synthesized. Synthesized silver nanofilms were analyzed by HPLC, FTIR, SEM, and DMA. The well diffusion method was applied to synthesized biofilms for antibacterial analyses for S. aureus, Listeria monocytogenes, and Salmonella bacteria, and migration analyses were performed.

2. Materials and Methods

2.1. Materials

Garlic, silver nitrate (AgNO3), DPPH (1,1-diphenyl-2-picrylhydrazyl; CAS-No: 1898-66-4), methanol anhydrous (99.8%), nutrient agar, hydrochloric acid (37%), sodium borohydride, and sodium hydroxide were purchased from Sigma-Aldrich (St. Louis, MO, USA). Corn starch, goji berry fruit, wheat gluten, and whey powder were supplied by a local producer (Food Market in Istanbul/Turkey). Na+-montmorillonite was provided by Southern Clay Products Inc. (Gonzales, TX, USA). The physical and chemical properties of sodium montmorillonite had the following the chemical formulas: (Na, Ca)0.33 (Al, Mg)2 Si4O10 (OH)2 6H2O, density: kg/dm3 2.860, specific surface area: 0.750 m2/kg, and CEC: 920 meq/kg; their composition was wt. %: 1.40 Na, 2.44 Ca, 9.99 Al, 8.88 Mg, 20.7 Si, 35.53 O, and 0.37 H.

2.2. Preparation of Samples

2.2.1. Preparation of Goji Berry Extract (Taurine)

The goji berry fruit was prepared by drying at 2 different temperatures—40 °C and 60 °C—for 24 h. The dried samples were ground into powder in a blender. The synthesis of the extracts of the obtained samples was done according to the literature [15]. The taurine extract obtained was analyzed by high-performance liquid chromatography (HPLC) analysis. As the final product, taurine extracts with different drying conditions, and ta40 and ta60 compounds as extracts, were obtained.

2.2.2. The Synthesis of Organoclays

In order for the montmorillonite clay to gain an organic character, it was modified with taurine extract obtained from goji berries. The modification procedure was performed according to the literature [8]. The organoclays modified were named Mt-ta40 and Mt-ta60, respectively.

2.2.3. The Synthesis of Silver Nanofilms

The synthesizing procedure of the silver nanofilms was carried out according to the literature [16]. The silver nanofilms were spread on glass slides (7.0 × 1.5 cm) and dried at room temperature for 10 days. The synthesis details of the silver nanofilms are shown in Table 1. The silver nanofilms were named CS1, CS2, and CS3, respectively.

2.2.4. Characterization

The taurine extracts were analyzed by HPLC-DAD-UV-Vis. Acetonitrile and 0. 1% trichloroacetic acid were used as mobile phase. The PDA detector wavelength was 470 nm, and the emission wavelength was 530 nm. The flow rate was 1.0 mL/min, the injection volume was 20 µL, and the temperature was 35 °C. The surface morphologies of nanocomposites were examined by using a JOEL JSM 5600 LV scanning electron microscope (SEM) (Tokyo, Japan) with an accelerating beam at a voltage of 40 kV. The organic groups on the silver nanofilms were determined by FTIR-ATR. The mechanical properties of the cornstarch silver nanofilms were analyzed by using TA Instruments’ dynamic mechanical analyzer (DMA), Model 2980, New Castle, DE, USA).

2.2.5. The Antibacterial Analysis

The bacteria Listeria monocytogenes, S. aureus, and Salmonella were used for the antibacterial analysis. The analysis procedure was applied according to the literature [17]. The nutrient agar was used as the medium.

2.2.6. The Migration Analysis

The Contact Analysis

Migration analyses were performed by preparing 50% ethanol, 10% ethanol, and 3% acetic acid solutions.
  • 50% ethanol; simulant imitating milk and milk products,
  • 10% ethanol; simulant imitating liquid foods,
  • 3% acetic acid; simulant imitating acidic foods.
The measurement method of the migration analysis has been carried out according to the literature [18], and TGK 2013/34 Article 8. The migration assays were carried out by using the procedures given in the Committee European Normalization Environment (CEN ENV) 1186 Prestandard.8 and TGK 2013/34 Article 8.

2.2.7. The Statistical analysis

For statistical analysis, the Minitab 16 software was used. ANOVA and Tukey’s test at a confidence level of 95% were used [12].

3. Results and Discussion

3.1. HPLC Analysis

Figure 1 shows the HPLC analysis spectrum of goji berry extracts ta40 and ta60. The peaks seen in the HPLC spectrum around 5.0–5.5 min and 8 min prove the presence of taurine in goji berry extract [15].

3.2. FTIR-ATR Analysis

The FTIR-ATR spectra of orgaoclays showed peaks at 1668 cm−1 assigned to carbon–carbon and carbon–nitrogen stretching vibrations in taurine extract. The band of O-H represents water adsorption on the montmorillonite at 3627 cm−1. The stretching region of C-H is related to the modified organoclay molecules in the region of 2850–2928 cm−1. These bands are based on the C-H antisymmetric and symmetric stretching bonds. The amin peaks shown in the spectrum of the wheat gluten amide I have been defined as mainly arising from amide carbonyl stretching, a combination of amide NH bending and CH stretching that can be used to characterize the protein secondary structures. A peak at 1650 cm−1 is associated with α-helical and a random structure, and the shoulder at ≈1668 cm−1 is associated with β-turns and could also be related to glutamine side chains. The amide I region of the hydrated gluten protein broad shoulders was observed at 1654–1650 cm−1, indicating α-helix conformation [19,20,21,22,23,24].
Moreover, the peaks at wave numbers around 1300 and 1500 cm−1 may be interpreted to the stretching vibrations of C=C and C=O, respectively, which exist in the FTIR-ATR spectra of taurine and garlic-loaded polymer [8,11,12,13,14,15,16]. The fact that the peaks at 2928–2941–2820–2863 cm−1 are higher than the spectrum of pure starch proves that the modification made by taurine and garlic extracts was successful. Moreover, it can be assumed that the interactions resulting from the modification originated from aliphatic C-H tensile bands [15,17,18,19,20,21,22].
In the spectrum of the wheat gluten (Figure 2b), the peaks at the wavelengths of 1178–1021 cm−1 showed C-O stretching vibrations in the C-O-C groups. The broad band that appeared at 3272 cm−1 represented hydroxyl groups bonded with hydrogen and N-H stretching bands. The FTIR-ATR spectra of the silver nanofilms are shown in Figure 2c–e. The peaks at 1641–1643–1640 cm−1 in Figure 2 originated from interactions of the taurine and garlic extracts that were used to modify the clay. The peak at 1641 cm−1 also represented the C-O stretching that overlapped with the N-H stretching in the same region (amide II).

3.3. The Antibacterial Analysis

Figure 3 and Table 2 show the inhibition zone analysis results for the silver nanofilms against the bacteria Listeria Monocytogenes, Salmonella, and S. aureus. As is known, the high antimicrobial resistance of nano films to prolonging the shelf life of foods is an effective parameter in packaging applications. CS1 and CS3 silver nanofilms showed maximum resistance to Salmonella, with an area of 1547.5 and 1884.3 mm2, respectively. In addition, it may assumed that the taurine and garlic extract showed higher antibacterial resistance, especially against Salmonella bacteria. According to the results of the antibacterial analysis, the whey powder and goji berry extract taurine dried at 60 °C created larger inhibition zones, whereas the goji berry extract taurine dried at 40 °C exhibited low antibacterial performance [25].
Salmonella bacteria are found in non-typhoidal poultry, eggs, raw meat, and products made from raw eggs. Moreover, the milk and dairy products, egg products (pasteurized and frozen eggs, egg powder, etc.), meat and meat products, fishery products, live bivalve mollusks, live sea urchins, live tunicates, broth tablets and powders, soups in dry form, seasonings, cream, and other foods in powder and tablet form such as whipped cream and sauces can be given as examples of food types with a high risk of carrying Salmonella bacteria. For this reason, packaging syntheses that are resistant to Salmonella bacteria, which have such a high risk factor, are of great importance. Figure 4 shows images of obtained silver nanofilms.

3.4. SEM Analysis

Figure 5 shows the surface morphology of the compounds. The silver nanofilms was measured through a JOEL JSM 5600 LV scanning electron microscope (SEM) with an accelerating voltage of 20 kV and a distance of 6 mm. The sample was fixed on the Ti/Al stub by double tape and coated with gold/palladium by a sputter coater for 90 s at 15 mA and 22 mbar pressure. In this study, solvents were evaporated from the environment during the boiling process in the nanofilm synthesis and plasticization stages. Therefore, the risks of keeping solvents in food packaging in electron spinning processes for SEM analysis were minimized. Thus, the migration of solvents to foods was prevented. The surface morphologies of silver nanofilms were observed between 200 nm and 1 µm. As is shown in Figure 5a,b, the surface morphology of the corn starch (CS) and wheat gluten were fluently smooth and homogeneous [26,27]. Figure 5 shows that the fractures formed as a result of the reactions occurring in the surface images of CS1 (c and d), CS2 (e and f), and CS3 (g and h) silver nanofilms, which formed a multilayered structure. These multi-layered structures also resulted in a rough morphology. The surface morphology of the samples was affected by the presence of taurine and garlic extract [26]. The addition of the nanoparticles resulted in a layered structure on the biomatrix surface, resulting in a stronger mechanical strength. The addition of extracts leads to an increase in tension and pressure on the polymer matrix surface, promoting the formation of strong bonds between the fibers [27]. The strong bonds formed also lead to an increase in the mechanical strength of the silver nanofilms. As is known, organoclays cause the formation of a layered structure on the polymer matrix surface. These results are also proof that the modification has taken place.

3.5. The Migration Analysis

Table 3 and Figure 6 show the results of the migration and statistical analysis. According to the results, silver nanofilms can be used as food packaging material according to Article 8 of TGK 2013/34, and the analysis values are well below the reference values. Although the migration concentration of the materials is 6 dm2 of packaging material per 1 kg in accordance with the European Regulation 10/2011 (EC, 2011), according to TGK 2013/34 Article 8 in Turkey, the migration limit concentration of materials for foods is 10 mg/dm2 [18,28,29,30]. Figure 6 shows the migration analysis results of the CS silver nanofilms. As a result, it was proven by the analysis results that the CS1, CS2, and CS3 nanocomposite films were suitable to be packaging films for packaging production in milk and milk products, liquid foods, and acidic foods. It can be seen that all of the migration analysis results are quite below the standards values. If they are evaluated only according to the migration analysis results, it is possible to say that the synthesized silver nanofilms can be used in all food packaging, but the antibacterial analysis results limit this area, so it is recommend that they be used primarily in the food packaging of milk and dairy products.
This means that the CS silver nanofilms were found to be packaging films appropriate for usage with all food products. The concentration values of the silver nanofilm’s migration analysis were calculated according to the method described in a previously published article [18]. Table 4 shows the migration analysis results according to the literature.

3.6. The Dynamic and Mechanical Analysis

The tensile stress (a), elastic modulus (b), and toughness (c) analysis results of the CS and CS silver nanofilms are shown in Figure 7. The tensile stress and the toughness of the CS silver nanofilms were enhanced compared to CS with no filler. The mechanical properties of corn starch silver nanofilms in the presence of montmorillonite clay, whey powder, and vegetable extracts improved.
Figure 7 shows the tensile stress, elastic modulus, and toughness of pure CS, CS1, CS2, and CS3 silver nanofilms. According to the analysis results obtained, the tensile stress and toughness values of the CS2 and CS3 silver nanofilms showed more improvement than the CS1 silver nanofilm. The tensile stresses of CS2 and CS3 were increased by 68%, and the tensile stress of CS1 was increased by 8%, respectively. The reason for this can be said to originate from organoclay contained in the CS2 and CS3 silver nanofilms. As is known, organoclays are filling materials that support mechanical durability. In addition, even if the absence of organoclay in CS1 has lower tensile stress than CS2 and CS3, it can be said that it develops compared to the mechanical properties of pure CS biopolymer [17]. Moreover, the elastic modulus of CS1 showed more improvement than CS2, CS3, and pure CS. The increase in elastic modulus tends to decrease by 68% for the CS2 and CS3 silver nanofilms.
The presence of organoclay in the structure of the CS2 and CS3 silver nanofilms is a factor that reduces elasticity. The improvement of the mechanical properties of the synthesized silver nanofilms is also confirmed by scanning electron microscope images. The roughness of the surfaces is proof that their mechanical properties have improved. Figure 7 shows images of obtained silver nanofilms. The different concentrations of silver nitrate and sodium borohydride (0.3, 0.5, and 0.8 mM) caused darker color tones of the silver nanofilms.
Foods are exposed to contact materials including cutlery and dishes, containers, processing machine, and packaging materials during all steps passed from farm to fork. Food industry has been conducting research and development activities on food packaging to increase shelf life, keep the food quality at optimum level, attract consumer interests, and reduce waste. A package material for any type of food should minimize aroma and flavor losses, constitute an excellent barrier for gas and water, provide a perfect hermetically sealed seam, as well as have a good mechanical properties. Food contact materials including food packaging are generally based on paper, metal, ceramic, aluminum, lacquers and coating, and plastic.
Food packaging is used to increase shelf life, to keep food quality at optimum level, to attract consumer interest, to facilitate the sale and distribution. Foods packaging provides information to consumers on product name, brand name, net weight, manufacturer information, price, production date, as well as the nutrient values in addition to keeping food at the desired amount in a single vessel and making it easier to bring a number of units to be moved into a single cluster and use. Therefore, food industry makes expenditures on the research and development activities of food packaging systems. The degree of the final product quality and safety, and consumer expectations from the ergonomic features of the package affects the acceptance criteria of a package material. A package material for any type of foods should minimize aroma and flavor losses, constitute an excellent barrier for gas and water, provide a perfect hermetically sealed seam, as well as have a good mechanical properties and offer chemical and biological protection against contamination [31,32].

4. Conclusions

In this study, three different nanocomposite films—CS1, CS2, and CS3—were synthesized. As a result of the analyzes made, it was confirmed by the FTIR, SEM, HPLC, and DMA results that the modification produced successful results. According to the results of antimicrobial studies, it has been proven that garlic-plant extract provides positive resistance against bacteria. In the migration analysis results, it was confirmed that the synthesized antimicrobial biopolymer food-packaging films were made in accordance with Article 8 of TGK 2013/34. It has been determined that the pore structure of the CS1 film has less gas permeability than CS2 and CS3, thus creating a stronger gas barrier. This is because of the whey powder used in CS1 synthesis. The synthesized films will play an effective role in increasing the shelf life of the food products to be used. As a result, the migration analyses of the synthesized nanocomposite antimicrobial films show that they are suitable for use in food packaging. The successful results have shown that the synthesized films are not dangerous. In addition, it was concluded that the need for additives and chemical preservatives in foods can be reduced. In this way, the shelf life of foods is extended with natural bioactive ingredients.

Author Contributions

G.B.: Conceptualization, experimental study, methodology, investigation and writing—original draft, resources and data curation, review and editing, and supervision. C.D.: Experimental study. H.Ö.: Writing—review and editing. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Institutional Review Board Statement

This research does not require ethical approval.

Data Availability Statement

Not applicable.

Acknowledgments

This study was carried out in Istanbul Aydın University Aziz Sancar Scientific Research Laboratory.

Conflicts of Interest

The authors declare that they have no conflict of interest.

References

  1. Öz, M. Health Benefits of Wolfberry, a Functional Nutrient: A Review. Adnan Menderes Univ. Fac. Health Sci. J. 2018, 2, 166–172. [Google Scholar]
  2. Tarakçı, Z.; Demirkol, D. The Effect of Dried Goji Berry Fruit (Lycium Barbarum) on the Physicochemical Properties of Yogurt. Ordu Univ. J. Sci. Technol. 2016, 6, 136–145. [Google Scholar]
  3. Chaoran, C.; Shu, F.X.; Jialiang, H.; Guangli, L.; Zhenxing, X.; Hongjie, H. Roles of taurine in cognitive function of physiology, pathologies and Toxication. Life Sci. 2019, 231, 116584. [Google Scholar] [CrossRef]
  4. Sherif, S.A.; Ihab, K.; Nashaat, N.I.; Hossam El Din, H.; Mohamed, A.E.F. The defensive role of taurine against gonadotoxicity and testicular apoptosis effects induced by cisplatin in rats. J. Infect. Chemother. 2020, 26, 51–57. [Google Scholar] [CrossRef]
  5. Kaixin, L.; Xiaoxia, S.; Mengxin, L.; Inamullah, P.W.; Mengren, Z.; Cong, Z.; Qiujuan, L.; Yachen, W.; Fengyuan, P. Taurine protects against myelin damage of sciatic nerve in diabetic peripheral neuropathy rats by controlling apoptosis of schwann cells via NGF/Akt/GSK3β pathway. Exp. Cell Res. 2019, 383, 111557. [Google Scholar] [CrossRef]
  6. Baysal, G.; Doğan, F. İnvestigation and Preparation of Biodegradable Starch-Based Silver nanofilms for Potential use of Curcumin and Garlic in Food Packaging Applications. J. Biomater. Sci. Polym. Ed. 2020, 31, 1–17. [Google Scholar] [CrossRef]
  7. Khodaeimehr, R.; Peıghambardoust, S.J.; Peıghambardoust, S.H. Preparation and Characterization of Corn Starch/Clay Nanocomposite Films: Effect of Clay Content and Surface Modification. Starch/Staerke 2018, 70, 3–4. [Google Scholar] [CrossRef]
  8. Baysal, G.; Yılmaz Çelik, B. Synthesis and Characterization of Antibacterial Biosilver nanofilms for Food Packaging. J. Environ. Sci. Health B 2018, 54, 79–88. [Google Scholar] [CrossRef]
  9. Demircan, B.; Ocak, Ö.Ö. Current and Future Application Potential of Transporting Food Additives using Edible Films and Coatings. Sinop Univ. J. Sci. 2019, 4, 130–150. [Google Scholar]
  10. Von Goetz, N.; Fabricius, L.; Glaus, R.; Weitbrecht, V.; Günther, D.; Hungerbühler, K. Migration of silver from commercial plastic food containers and implications for consumer exposure assessment. Food Addit. Contam. A Chem. Anal. Control Expo. Risk Assess. 2013, 30, 612–620. [Google Scholar] [CrossRef]
  11. Li, W.; Zheng, K.; Chen, H.; Feng, S.; Wang, W.; Qin, C. Influence of nano titanium dioxide and clove oil on chitosan-starch film characteristics. Polymers 2019, 11, 1418. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  12. Peıghambardoust, S.J.; Peighambardoust, S.H.; Mohammadzadeh, P.N.; Pakdel, P. Properties of Active Starch-Based Films İncorporating A Combination of Ag, Zno and Cuo Nanoparticles for Potential Use İn Food Packaging Applications. Food Packag. Shelf Life 2019, 22, 100420. [Google Scholar] [CrossRef]
  13. Martinez-Pardo, I.; Robert, A.S.; Benu, A.; Raju, A. Thermoplastic starch-nanohybrid films with polyhedral oligomericsilsesquioxane. Carbohydr. Polym. 2017, 173, 170–177. [Google Scholar] [CrossRef]
  14. Guanjie, Z.; Xiaoyong, S.; Fusheng, C.; Zhixiang, S. Physical and structural characterization of edible bilayer films made with zein and corn-wheat starch. J. Saudi Soc. Agric. Sci. 2018, 18, 324–331. [Google Scholar] [CrossRef]
  15. Sawabe, Y.; Tagami, T.; Yamasaki, K. Determination of taurine in energy drinks by HPLC using a pre-column derivative. J. Health Sci. 2008, 54, 661–664. [Google Scholar] [CrossRef] [Green Version]
  16. Abreu, A.S.; Oliveira, M.; De, S.A.; Rodrigues, R.M.; Cerqueira, M.A.; Vicente, A.A.; Machado, A.V. Antimicrobial nanostructured starch based films for packaging. Carbohydr Polym. 2015, 129, 127–134. [Google Scholar] [CrossRef] [Green Version]
  17. Ren, L.; Yan, X.; Zhou, J.; Tong, J.; Su, X. Influence of chitosan concentration on mechanical and barrier properties of corn starch/chitosan films. Int. J. Biol. Macromol. 2017, 105, 1636–1643. [Google Scholar] [CrossRef] [PubMed]
  18. O’Brien, A.; Leach, A.; Cooper, I. Polypropylene: Establishment of a rapid extraction test for overall migration limit compliance testing. Packag. Technol. Sci. 2000, 13, 13. [Google Scholar] [CrossRef]
  19. Ashutosh, S.; Rachid, L.; Sai Kranthi, V.; Chithra, K.; Valérie, O.; Vijaya, R. Effect of High Electric Field on Secondary Structure of Wheat Gluten. Int. J. Food Prop. 2016, 19, 1217–1226. [Google Scholar] [CrossRef]
  20. Haihua, Z.; Irakoze, P.C.; Qin, L.; Kexue, Z.; Wei, P.; Huiming, Z. Structural Modification of Wheat Gluten by Dry Heat-Enhanced Enzymatic Hydrolysis. Food Technol. Biotechnol. 2012, 50, 53–58. [Google Scholar]
  21. Sujka, K.; Kockon, P.; Ceglnska, A.; Ewa Reder, M. The Application of FT-IR Spectroscopy for Quality Control of Flours Obtained from Polish Producers. J. Anal. Methods Chem. 2017, 9, 4315678. [Google Scholar] [CrossRef] [PubMed]
  22. Zhou, M.; Liu, Q.; Wu, S.; Gou, Z.; Wu, X.; Xu, D. Starch/chitosan films reinforced with polydopamine modified MMT: Effects of dopamine concentration. Food Hydrocoll. 2016, 61, 678–684. [Google Scholar] [CrossRef]
  23. Nawrocka, A.; Cieœla, J. Influence of silver nanoparticles on food components in wheat. Int. Agrophys. 2013, 27, 49–55. [Google Scholar] [CrossRef]
  24. Nawrocka, A. Conformational changes in wheat gluten after using Ag-nanoparticles. Int. Agrophys. 2014, 28, 311–317. [Google Scholar] [CrossRef]
  25. Zhang, Y.; Li, S.; Xu, Y.; Shi, X. Engineering of hollow polymeric nanosphere-supported imidazolium-based ionic liquids with enhanced antimicrobial activities. Nano Res. 2022, 15, 5556–5568. [Google Scholar] [CrossRef]
  26. Dehghani, S.; Peighambardoust, S.H.; Peighambardoust, S.J.; Hosseini, S.V.; Regenstein, J.M. Improved mechanical and antibacterial properties of active LDPE films prepared with combination of Ag, ZnO and CuO nanoparticles. Food Packag. Shelf Life 2019, 22, 100391. [Google Scholar] [CrossRef]
  27. Saieh, S.E.; Eslam, H.K.; Ghasemi, E.; Bazyar, B.; Rajabi, M. Physical and morphological effects of cellulose nano-fibers and nano-clay on biodegradable WPC made of recycled starch and industrial sawdust. BioResources 2019, 14, 5278–5287. [Google Scholar] [CrossRef]
  28. Soleimani, J.; Ghanbarzadeh, B.; Dehgannya, J.; Islami, S.B.; Sorouraddin, S.M. Simulation of nanosilver migration from polystyrene nanocomposite into food simulants. Adv. Nano Res. 2018, 6, 243–255. [Google Scholar] [CrossRef]
  29. Spasojevic, P.; Zrilic, M.; Panic, V.; Stamenkovic, D.; Seslija, S.; Velickovic, S. The Mechanical Properties of a Poly(methyl methacrylate) Denture Base Material Modified with Dimethyl Itaconate and Di-n-butyl Itaconate. Int. J. Polym. Sci. 2015, 2015, 561012. [Google Scholar] [CrossRef] [Green Version]
  30. Ubeda, S.; Aznar, M.; Rosenmai, A.K.; Vinggaard, A.M.; Nerín, C. Migration studies and toxicity evaluation of cyclic polyesters oligomers from food packaging adhesives. Food Chem. 2019, 311, 125918. [Google Scholar] [CrossRef]
  31. European Commission (EC). Regulation (EC) No 1935/2004 of the European Parliament and of the Council of 27 October 2004 on materials and Articles Intended to Come into Contact with Food and Repealing Directives 80/590/EEC and 89/109/EEC. Off. J. Eur. Union 2004, L338, 4–17. [Google Scholar]
  32. Çinibulak, P. Migration in Food Packaging. Master’s Thesis, Namık Kemal University Institute of Science and Technology, Tekirdağ, Turkey, 2010. [Google Scholar]
Polymers 15 00689 g001 550
Figure 1. The HPLC analysis spectrum of goji berry extracts ta40 (a) and ta60 (b).
Figure 1. The HPLC analysis spectrum of goji berry extracts ta40 (a) and ta60 (b).
Polymers 15 00689 g001
Polymers 15 00689 g002 550
Figure 2. FTIR_ATR spectra of the corn starch (a),wheat gluten (b), CS1 (c), CS2 (d), and ve CS3 (e) silver nanofilms.
Figure 2. FTIR_ATR spectra of the corn starch (a),wheat gluten (b), CS1 (c), CS2 (d), and ve CS3 (e) silver nanofilms.
Polymers 15 00689 g002
Polymers 15 00689 g003 550
Figure 3. The inhibition zones of CS1 (1), CS2 (2), and CS3 (3) silver nanofilms against to Listeria monocytogenes, Salmonella and S. aureus, respectively.
Figure 3. The inhibition zones of CS1 (1), CS2 (2), and CS3 (3) silver nanofilms against to Listeria monocytogenes, Salmonella and S. aureus, respectively.
Polymers 15 00689 g003
Polymers 15 00689 g004 550
Figure 4. Images of obtained silver nanofilms.
Figure 4. Images of obtained silver nanofilms.
Polymers 15 00689 g004
Polymers 15 00689 g005a 550Polymers 15 00689 g005b 550
Figure 5. SEM images of corn starch CS (a), wheat gluten (b), CS1 (c,d), CS2 (e,f), and CS3 (g,h) nanocomposite films.
Figure 5. SEM images of corn starch CS (a), wheat gluten (b), CS1 (c,d), CS2 (e,f), and CS3 (g,h) nanocomposite films.
Polymers 15 00689 g005aPolymers 15 00689 g005b
Polymers 15 00689 g006 550
Figure 6. The migration analysis results of CS and CS silver nanofilms.
Figure 6. The migration analysis results of CS and CS silver nanofilms.
Polymers 15 00689 g006
Polymers 15 00689 g007 550
Figure 7. The tensile stress, elastic modulus and toughness analysis results of CS and CS silver naofilms.
Figure 7. The tensile stress, elastic modulus and toughness analysis results of CS and CS silver naofilms.
Polymers 15 00689 g007
Table
Table 1. The synthesis steps of nanocomposite films.
Table 1. The synthesis steps of nanocomposite films.
Samples (g)CS1CS2CS3
Mta-40-1.0-
Mtb-60--1.0
Taurine1.01.01.0
Allicin1.01.01.0
Wheat gluten2.02.02.0
Whey powder1.0--
Corn starch8.08.08.0
Table
Table 2. The inhibition zones of silver nanofilms (mm2).
Table 2. The inhibition zones of silver nanofilms (mm2).
Listeria monocytogenesSalmonellaS. aureus
CS172.95 ± 0.271547.5 ± 3.16382.02 ± 1.23
CS2379.9 ± 1.39386.88 ± 0.79331.18 ± 1.07
CS335.87 ± 0.131884.3 ± 3.65144.77 ± 0.46
Data are mean of triplicate measurements ± SD.
Table
Table 3. The results of migration analysis.
Table 3. The results of migration analysis.
SimulantAcetic Acid3%Ethanol 10%Ethanol 50%
Chemical consumption (L)0.150.150.15
Sample area (cm2)707070
Conditions (°C/h)40 °C/10 day40 °C/10 day40 °C/10 day
Average value of CS1 (mg/dm2)0.300 ± 0.00560.299 ± 0.00380.318 ± 0.0073
Average value of CS2 (mg/dm2)0.296 ± 0.00420.300 ± 0.00330.297 ± 0.0056
Average value of CS3 (mg/dm2)0.300 ± 0.00440.299 ± 0.00410.294 ± 0.0047
Data are mean of triplicate measurements ± SD.
Table
Table 4. According to the literature of migration analysis results.
Table 4. According to the literature of migration analysis results.
SimulantMigration Ratio (mg/dm2)References
Mt-GC-CS3.65 ± 0.46[6]
Plastic food containers7.90[18]
PET/PE5.29 ± 0.67[28]
PET/Alu/OPA/CPP3.42 ± 0.10[28]
nanosilver into food simulants1.65–2.37[28]
nanosilver into food simulants (A2–A3)0.000032–0.000034[10,11,12,13,14,15,16,17,18]
CS1, CS2, and CS30.300 ± 0.0033(in this study)
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Baysal, G.; Demirci, C.; Özpinar, H. Proporties and Synthesis of Biosilver Nanofilms for Antimicrobial Food Packaging. Polymers 2023, 15, 689. https://doi.org/10.3390/polym15030689

AMA Style

Baysal G, Demirci C, Özpinar H. Proporties and Synthesis of Biosilver Nanofilms for Antimicrobial Food Packaging. Polymers. 2023; 15(3):689. https://doi.org/10.3390/polym15030689

Chicago/Turabian Style

Baysal, Gülay, Cihat Demirci, and Haydar Özpinar. 2023. "Proporties and Synthesis of Biosilver Nanofilms for Antimicrobial Food Packaging" Polymers 15, no. 3: 689. https://doi.org/10.3390/polym15030689

APA Style

Baysal, G., Demirci, C., & Özpinar, H. (2023). Proporties and Synthesis of Biosilver Nanofilms for Antimicrobial Food Packaging. Polymers, 15(3), 689. https://doi.org/10.3390/polym15030689

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop