Next Article in Journal
Isolation and Characterization of Cellulose Nanocrystals from Oil Palm Mesocarp Fiber
Next Article in Special Issue
Polystyrene Chain Growth from Di-End-Functional Polyolefins for Polystyrene-Polyolefin-Polystyrene Block Copolymers
Previous Article in Journal
Poly(3,4-ethylenedioxythiophene) (PEDOT) Derivatives: Innovative Conductive Polymers for Bioelectronics
Previous Article in Special Issue
Use of Vanadium Complexes Bearing Naphthalene-Bridged Nitrogen-Sulfonate Ligands as Catalysts for Copolymerization of Ethylene and Propylene
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 9
Issue 8
10.3390/polym9080353
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Facile, Efficient Copolymerization of Ethylene with Norbornene-Containing Dienes Promoted by Single Site Non-Metallocene Oxovanadium(V) Catalytic System

by
Kaiti Wang
1,2,
Jiabao Wang
3,
Yanguo Li
2,
Li Pan
1,* and
Yuesheng Li
1
1
Tianjin Key Lab of Composite & Functional Materials, School of Materials Science and Engineering, Tianjin University, Tianjin 300072, China
2
Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China
3
National Center for Nanoscience and Technology, Beijing 100190, China
*
Author to whom correspondence should be addressed.
Polymers 2017, 9(8), 353; https://doi.org/10.3390/polym9080353
Submission received: 23 July 2017 / Revised: 8 August 2017 / Accepted: 8 August 2017 / Published: 11 August 2017
(This article belongs to the Special Issue Olefin Polymerization and Polyolefin)
Browse Figures
Versions Notes

Abstract

:
Non-metallocene oxovanadium(V) complexes bearing either [ONNO]-type amine pyridine bis(phenolate) ligands or [ONN]-type amine pyridine phenolate ligands were employed as efficient catalysts to copolymerize ethylene with several unsymmetrical norbornene-containing dienes, such as 5-vinyl-2-norbornene (VNB), 5-ethylidene-2-norbornene (ENB) or dicyclopentadiene (DCPD), producing copolymers with high comonomer incorporations (VNB: 33.0 mol %; ENB: 30.4 mol %; DCPD: 31.6 mol %, respectively) and high molecular weight (VNB: 86.4 kDa; ENB: 256 kDa; DCPD: 86.4 kDa, respectively). The enchainment of the dienes was proven to be exclusive of vinyl-addition via the C=C double bond of the norbornene ring while the other double bond was retained near the backbone without crosslinking. During the copolymerization of ethylene with ENB, a positive ‘comonomer effect’ was observed. The catalytic activities of the catalysts as well as the molecular weights and comonomer incorporations of the resultant copolymers could be tuned within a wide range by varying the structures of the catalysts and copolymerization conditions. The [ONN]-type oxovanadium(V) complexes showed higher catalytic activities than those of [ONNO]-type oxovanadium(V) complexes, irrespective of the structure of the dienes. In addition, the dominant chain transfer pathway of the non-metallocene oxovanadium(V) catalytic system promoted copolymerization was proven to be transfer to aluminum compounds.

Graphical Abstract

1. Introduction

The synthesis of well-defined polyolefin with reactive pendent vinyl group, which can be easily converted into functional groups by further chemical transformations, has drawn much attention over recent decades [1,2,3,4,5,6,7,8,9,10]. Among the various dienes successfully incorporated into the linear polyethylene (PE) or polypropylene (PP) main chain, the unsymmetrical dienes, such as p-(3-butenyl) styrene and dicyclopentadiene (DCPD), are very promising because of their two double bonds usually showing different selectivity toward coordinative incorporation and subsequent chemical transformation, respectively. The undesired crosslinking thus could be avoided and the microstructure of the resulting copolymers therefore might be well-controlled [11,12]. For instance, the cyclic olefin copolymers (COCs), which are usually synthesized from copolymerization of ethylene with cyclic olefin, are kinds of materials have higher modulus than high density polyethylene (HDPE) and PP, and exceptional moisture barrier for a clear polymer along with low moisture absorption rate. The COCs containing the reactive olefin groups are expected to provide functional COCs with substantially improved properties, and thus have attracted increasing attentions [13,14,15,16,17,18,19,20,21,22]. Several catalytic systems, including Ziegler–Natta catalysts [21], metallocenes [15] and non-metallocenes [13,14,16], have demonstrated good performance in the copolymerization of ethylene with various cyclic dienes.
Among the classical Ziegler–Natta type catalysts, vanadium catalysts show outstanding catalytic properties for the manufacture of synthetic rubber and elastomers [23,24,25,26,27]. For example, Christman D.L. et al. reported that either VOCl3/Et3Al2Cl3 or VO(OtBu)3/Et3Al2Cl3 showed high cyclic dienes incorporation ability in the terpolymerization with ethylene and propylene [23]. Since the vanadium catalysts might be deactivated during the polymerization because of the reduction to low-valent, inactive species [27], introduction of bulky and polydentate ancillary ligands to stabilize active vanadium(V) species has been proven to be an effective approach to keep vanadium at high-oxidation and subsequently prolong the catalytic lifetime [28,29,30,31,32,33,34,35,36]. In our previous work, the synthesized [ONNO]-type and [ONN]-type oxovanadium(V) complexes also showed high catalytic activities and promising stabilities in copolymerization of ethylene with norbornene (NBE), and produced E/NBE copolymers with high NBE contents [37,38]. Their good performance prompts us to further investigate their capability of copolymerizing ethylene and norbornene derivatives with an additional C=C double bond, including 5-vinyl-2-norbornene (VNB), 5-ethylidene-2-norbornene (ENB), and DCPD. In this context, we presented the result of copolymerization of ethylene and above mentioned norbornene-containing comonomers by using several selected vanadium complexes with different ligand, including both [ONNO]-type (a–c) and [ONN]-type (d,e) oxovanadium(V) complexes (Scheme 1).

2. Materials and Methods

2.1. General Procedures and Materials

All air- and moisture-sensitive compounds were manipulated using standard Schlenk techniques or in an MBraun glovebox (Shanghai, China) under a dry nitrogen atmosphere. All solvents used were purified from an MBraun SPS system (Shanghai, China). Ethyl trichloroacetate (ETA) were purchased from Aldrich (Shanghai, China), dried over calcium hydride at room temperature and then distilled. VO(OnPr)3, phenol compounds, and amine compounds were purchased from Aldrich (Shanghai, China). Diethylaluminium chloride was obtained from Albemarle Corp (Charlotte, NC, USA). Commercial ethylene was directly used for polymerization without further purification. VNB, ENB, and DCPD were purchased from J&K Scientific Ltd. (Beijing, China), dried over calcium hydride at room temperature and then distilled under reduced pressure. The oxovanadium(V) complexes a–e were synthesized according to our previously reported procedures [37,38].

2.2. Characterization

The NMR results of polymers were obtained through a Bruker 400 MHz spectrometer (Beijing, China) at 120 °C with o-C6D4Cl2 as the solvent. The molecular weights and the polydispersities of the polymer samples were determined at 150 °C by use of a PL-GPC 220 type high-temperature chromatograph (Beijing, China) equipped with three PL gel 10 μm Mixed-B LS type columns. 1,2,4-Trichlorobenzene (TCB) was employed as an elute solvent at a flow rate of 1.0 mL/min. The calibration was made by the polystyrene standard Easi Cal PS-1 (PL Ltd., Beijing, China).

2.3. General Procedure for Copolymerization

The copolymerizations were carried out in a mechanically stirred 200 mL stainless steel autoclave, equipped with an electric heating mantle controlled by a thermocouple dipping into the reaction mixture. The autoclave was baked under vacuum for 4 h at 150 °C and then thermostatted to the desired temperature. The prescribed amounts of toluene, comonomer (ENB, VNB, or DCPD), Et2AlCl, ETA, and a toluene solution containing vanadium complex were added. Additional toluene was injected into this system via a syringe to keep a total volume of 50 mL. Subsequently, the reaction mixture was pressurized to the prescribed ethylene pressure and maintained throughout the polymerization. After a desired time, the stirring motor was stopped, the reactor was vented, and the resultant mixture was poured into EtOH/HCl (95/5). The resultant polymer as white precipitate was collected by filtration, adequately washed with EtOH and dried under vacuum at 60 °C until a constant weight was achieved.

3. Results and Discussion

3.1. Copolymerization of Ethylene with VNB

The copolymerization of ethylene with VNB was carried out at 50 °C under 4 atm of ethylene pressure. The typical copolymerization results were summarized in Table 1. Although the catalytic activities of the copolymerization are lower than those of ethylene homopolymerization under similar reaction conditions, both [ONNO]-type oxovanadium(V) complexes and [ONN]-type oxovanadium(V) complexes showed pretty good performance in the copolymerization of ethylene with VNB in toluene under mild conditions. Moreover, the [ONN]-type oxovanadium(V) catalysts d and e showed much higher catalytic activities than those of the [ONNO]-type analogues (complexes a–c), owing to their less steric hindrance around the metal center (entries 2, 4, and 6 vs. 16 and 18, Table 1). However, the copolymers produced by the latter possessed higher molecular weights (MWs). All the resultant copolymers exhibited unimodal molecular weight distribution, suggesting the single site catalytic behaviors of these catalysts. Among these three [ONNO]-type oxovanadium(V) complexes, complex b showed the highest catalytic activities in both homopolymerization of ethylene and copolymerization because of its less steric hindrance originated from the longer bridge between the pendant pyridine donor and the ligand skeleton, and produced copolymers with moderate MWs. Besides the reduction in catalytic activities, the MWs of the resultant polymers were decreased remarkably, and they were further decreased with the increase of VNB concentration in feed (entries 4, 9–14). This result indicated that, during the copolymerization, the continuous coordination-insertion process might be terminated by stable coordination of the pendant vinyl group with the active vanadium center and thus the chain growth was terminated. This was further proved by the Npolym/Ncat values showed in Table 1. The numbers of polymer chains produce by one catalytic molecule decreased as the VNB concentration in feed increased. A similar phenomenon has also been observed in the copolymerization of ethylene with VNB by using half-metallocene zirconium(IV) catalysts [39]. When the feedstock of the Et2AlCl was increased from 2000 to 6000, the MWs of the resulting copolymers obtained by complex b were also decreased (entries 4, 7, and 8, Table 1), and the number of polymer chains produce by one catalytic molecule increased, indicating that the chain transfer to aluminum compounds was the dominant chain transfer pathway during the copolymerization of ethylene with VNB.
With the same concentration of VNB in feed (0.5 mol/L), complexes b and e produced copolymers with higher VNB incorporations (11.9 and 10.4 mol %, respectively) than those of other catalysts. As shown in Figure 1, the VNB incorporation was increased steadily (from 8.3 to 33.0 mol %) with the increase of comonomer feedstock concentration (from 0.25 to 3.0 mol/L, entries 4, 9–14, Table 1), which means that the incorporation of VNB in the copolymers could be easily tuned in a wide range by adjusting the VNB feedstocks. Moreover, all the copolymers with high VNB contents were completely soluble in toluene at 50 °C with undetectable crosslinking.
The incorporations and stereoselectivity of VNB were unambiguously revealed by 1H, 13C, and DEPT NMR spectra. All resonances were clearly identified and the data agreed well with the previously reported values [15,16]. No signals around 6.1 ppm relative to the C=C double bond of norbornene presented, while the resonances between 4.8 and 6.0 ppm corresponding to the pendant vinyl groups could be observed in the lH NMR spectra of the copolymers. The enchainment of VNB was therefore proven to be exclusively via 2, 3 vinyl-addition of the norbornene ring. The insertion manner was also supported by the 13C NMR spectra of the copolymers, which presented the signals of pendant vinyl groups at 144.89 (=CH, exo), 142.18 (=CH, endo), 114.85 (=CH2, endo), and 112.09 ppm (=CH2, exo), respectively, with no detectable signals of the C=C double bond of norbornene around 136.9 ppm. According to the 13C NMR spectra, we could draw a conclusion that the incorporated VNB units showed two stereo-configurational structures in the E/VNB copolymer chains (1A endo and 1B exo, respectively, Figure 2). The chemical shifts of carbon 6 in 13C NMR spectra was significantly influenced by the endo/exo-configuration (6n: endo; 6x: exo, respectively), while the chemical shift of bridge carbon 7 was not affected. In addition, only the signals assigned to isolated VNB units and E/VNB alternating sequences were observed in the 13C NMR spectra. Even at high VNB concentration in feed, the signals of VNB continuous sequences were undetectable. This result is consistent with the fact that no homopolymer was obtained in homopolymerization of VNB by these catalytic systems.

3.2. Copolymerization of Ethylene with ENB

The copolymerizations of ethylene with ENB were also carried out under similar reaction conditions. Different with the phenomenon of copolymerization of ethylene and VNB, a “positive comonomer effect” was observed when the ENB feed concentration was enhanced [40,41]. As observed in Table 2, both [ONNO]-type oxovanadium(V) complexes and [ONN]-type oxovanadium(V) complexes showed much higher catalytic activities in the copolymerization than those of ethylene homopolymerizations (entries 3, 5, 15, and 17 in Table 1). The catalytic activities of catalyst b first enhanced with the increase of the ENB feedstock, achieved the maximum value of 68.3 kg/mmolv h at 0.75 mol/L of ENB in-feed concentration (Figure 3). Copolymers with high MWs (101–256 kDa) and moderate to high ENB incorporations (11.5–30.4 mol % of ENB content, entries 1, 7–9, Table 2) were obtained. With the feedstock of Et2AlCl increasing, the MWs of the obtained copolymers decreased and the number of polymer chains produce by one catalytic molecule increased (entries 1, 3, and 4, Table 2), indicating that the dominant chain transfer pathway in E/ENB copolymerization was also transfer to aluminum compounds. Additionally, the resultant E/ENB copolymers also exhibited unimodal distribution originating from the single site catalytic behavior. Polymerization temperature and reaction time as significant reaction parameters were also explored. Both the catalytic activities and incorporation increased with reaction temperature, whereas the MWs of the copolymers decreased (entry 1 vs. 5, Table 2). This may be explained by the fact that higher reaction temperature accelerates both chain propagation and chain transfer. Neither the MW value nor ENB incorporation changed much with prolongation of reaction time from 5 min to 10 min (entry 1 vs. 6, Table 2). Similar to the copolymerization of ethylene with VNB, the [ONN]-type oxovanadium(V) complexes also showed higher catalytic activities than the [ONNO]-type oxovanadium(V) complexes in E/ENB copolymerizations, while the resultant copolymers produced by [ONNO]-type oxovanadium(V) complexes showed higher MWs as well (entries 1 and 2 vs. 10 and 11, Table 2).
As compared in Table 2, not only the catalytic activities of these oxovanadium complexes, but also the MWs of the obtained E/ENB copolymers were enhanced about one order of magnitude than those of the corresponding ethylene homopolymerizations. These results might benefit from the proper steric hindrance around the ethylidene group in ENB molecules. The coordination of the pendant ethylidene group to the central metal, which might result in deactivation of the catalysts, would be suppressed by its steric effect [39]. The prepared E/ENB copolymers by these oxovanadium(V) catalysts possessed much higher comonomer contents than those of the E/VNB copolymers. When the ENB concentration in feed was 0.5 mol/L, the comonomer incorporations were up to 16.9–18.8 mol %, irrespective of which oxovanadium(V) catalysts was employed. The ENB incorporation up to 30.4 mol % was achieved by increasing the in-feed concentration of ENB to 1.0 mol/L (Entry 9, Table 2). In addition, as observed, the increase of Al/V molar ratio led to an evident increase in both activity and comonomer incorporation (entries 1, 3, and 4, Table 2).
As shown in Figure 4a, the lH NMR spectra of the E/ENB copolymers (2B and 2C) showed typical resonances at 5.1 and 5.3 ppm assigned to the ethylidene groups. The absence of resonances around 6.00 ppm implied that ENB inserted into the polymer chain exclusively via its intra cyclic C=C double bonds while the pendant C=C bonds remained. The E/Z configurational isomers mole ratio of 5:1 of the ENB monomer was also revealed and presented in Figure 4a [42]. This value is consistent with that of the raw ENB monomer (2A in Figure 4a), and indicates that both the two ENB isomers show the same reactivity toward these vanadium catalysts. The microstructure of copolymer sample 2C (entry 9, Table 2) was also investigated by 13C NMR spectrum (Figure 4b). Similar to the E/VNB copolymer, the microstructures of the copolymer produced by complex b only possessed isolated ENB inserted units and E/ENB alternating sequence. The resonances assigned to continuous ENB insertion were not observed.

3.3. Copolymerization of Ethylene with DCPD

The copolymerizations of ethylene with DCPD catalyzed by these selected oxovanadium(V) complexes were also conducted in an efficient manner as well. Compared with the ethylene homopolymerization behavior, all of these oxovanadium catalysts showed slightly lower catalytic activities in E/DCPD copolymerizations, and the activities further decreased as the concentration of DCPD increased (Figure 5). It was revealed that the increase in comonomer concentration in feed is an effective approach to enhance DCPD incorporations in the resulting copolymers. When the concentration of DCPD was 1.00 mol/L, the DCPD content in the resultant copolymer was up to 31.6 mol %. In comparison with [ONNO]-type oxovanadium(V) complexes, the [ONN]-type analogues not only displayed much higher catalytic activities, but also yielded copolymers with higher DCPD contents (entries 1 and 8 vs. entries 11 and 12, Table 3). These phenomena should be ascribed to the less steric hindrance of the latter complexes which could allow the bulky DCPD comonomer to incorporate easily. The catalytic activities of these selected catalysts toward E/DCPD copolymerization and the MWs of resultant copolymers were lower than those of E/ENB copolymers, while higher than those of E/VNB copolymers. This result further demonstrated that the reactivity of the comonomer was influenced greatly by the steric environment around the unincorporated C=C bond. The Et2AlCl feedstock showed negligible influences on both the catalytic activities of oxovanadium(V) catalysts and the DCPD incorporations of the resultant copolymers, while the MWs of the copolymers decreased and the number of polymer chains produced by one catalytic molecule increased as the Al/V molar ratio raised from 2000 to 6000. These phenomena signified that the chain transfer to aluminum compounds was also the dominant chain transfer pathway in E/DCPD copolymerization.
The microstructures of E/DCPD copolymers were also investigated by 1H and 13C NMR spectra (Figure 6). The signals at 5.53 and 5.65 ppm in 1H NMR spectrum as well as the peaks at 132.8 and 130.6 ppm in 13C NMR spectrum were assigned to the unreacted C=C double bond of the cyclopentene ring. It demonstrated that the copolymerization of ethylene with DCPD was achieved through a selective enchainment of norbornene ring because of its higher ring strain. Other signals of typical ethylene/DCPD copolymers in 13C NMR spectrum were assigned according to the literature report [14]. No evidence of crosslinking was detected for all ethylene/DCPD copolymers. Similar to the E/VNB and E/ENB copolymers, there were only isolated DCPD units and E/DCPD altering sequences existing in the copolymer chains, no continuous DCPD inserted sequences were detected, even for copolymers with high a DCPD incorporation of 31.6 mol %.

4. Conclusions

In the presence of Et2AlCl as a cocatalyst and ETA as a reactivating agent, a series of oxovanadium(V) complexes were proven to be efficient catalysts for copolymerizing ethylene with norbornene-containing dienes including VNB, ENB and DCPD, and copolymers possessing high comonomer content (above 30 mol %) and high molecular weight (up to 256 KDa) were obtained. The unimodal distribution (MW/Mn < 2.3) of the resultant copolymers indicated the single site catalytic behaviors of these catalysts. Benefiting from its proper steric environment around the metal center, complex b not only exhibited high catalytic activities toward the copolymerization, but also produced copolymers with promising MWs and comonomer incorporations. The selected dienes inserted into the polymer chain via the enchainment of the C=C double bond of the norbornene ring, and the other double bond was retained without crosslinking. ENB showed the highest reactivity among the three selected dienes, and the comonomer incorporations as well as the MWs of E/ENB copolymers were much higher than the other two types of copolymers because of the steric environment around the pendant ethylidene group. The dominant chain transfer pathway during the copolymerizations was proven to transfer to aluminum compounds, and the catalytic activities of the catalysts as well as the MWs and the comonomer incorporations of the copolymers could be tuned in a wide range by varying the reaction conditions.

Acknowledgments

The authors are grateful for financial support by the National High Technology Research and Development Program of China (No. 2015AA034002) and the National Natural Science Foundation of China (No. 21234006).

Author Contributions

Yuesheng Li and Li Pan conceived and designed the experiments; Kaiti Wang and Jabao Wang performed the experimental work and the analysis of structural data; Yanguo Li contributed regents/materials/analysis tools; Kaiti Wang and Li Pan wrote the paper.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Chung, T.C.; Lu, H.L.; Li, C.L. Synthesis and functionalization of unsaturated polyethylene: Poly(ethylene-co-1,4-hexadiene). Macromolecules 1994, 27, 7533–7537. [Google Scholar] [CrossRef]
  2. Chung, T.C.; Dong, J.Y. Synthesis of linear ethylene/divinylbenzene copolymers by metallocene catalysis. Macromolecules 2002, 35, 2868–2870. [Google Scholar] [CrossRef]
  3. Chung, T.C. Synthesis of functional polyolefin copolymers with graft and block structures. Prog. Polym. Sci. 2002, 27, 39–85. [Google Scholar] [CrossRef]
  4. Hustad, P.D.; Coates, G.W. Insertion/isomerization polymerization of 1,5-hexadiene: Synthesis of functional propylene copolymers and block copolymers. J. Am. Chem. Soc. 2002, 124, 11578–11579. [Google Scholar] [CrossRef] [PubMed]
  5. Nomura, K.; Takemoto, A.; Hatanaka, Y.; Okumura, H.; Fujiki, M.; Hasegawa, K. Polymerization of 1,5-hexadiene by half-titanocenes-MAO catalyst systems: Factors affecting the selectivity for the favored repeated 1,2-insertion. Macromolecules 2006, 39, 4009–4017. [Google Scholar] [CrossRef]
  6. Nomura, K.; Hatanaka, Y.; Okumura, H.; Fujiki, M.; Hasegawa, K. Polymerization of 1,5-hexadiene by the nonbridged half-titanocene complex-MAO catalyst system: Remarkable difference in the selectivity of repeated 1,2-insertion. Macromolecules 2004, 37, 1693–1695. [Google Scholar] [CrossRef]
  7. Kobayashi, S.; Lu, C.; Hoye, T.R.; Hillmyer, M.A. Controlled polymerization of a cyclic diene prepared from the ring-closing metathesis of a naturally occurring monoterpene. J. Am. Chem. Soc. 2009, 131, 7960–7961. [Google Scholar] [CrossRef] [PubMed]
  8. Li, X.; Baldamus, J.; Nishiura, M.; Tardif, O.; Hou, Z. Cationic rare-earth polyhydrido complexes: Synthesis, structure, and catalytic activity for the cis-1,4-selective polymerization of 1,3-cyclohexadiene. Angew. Chem. Int. Ed. 2006, 45, 8184–8188. [Google Scholar] [CrossRef] [PubMed]
  9. Nomura, K.; Liu, J.; Fujiki, M.; Takemoto, A. Facile, Efficient functionalization of polyolefins via controlled incorporation of terminal olefins by repeated 1,7-octadiene insertion. J. Am. Chem. Soc. 2007, 129, 14170–14171. [Google Scholar] [CrossRef] [PubMed]
  10. Wang, X.Y.; Wang, Y.X.; Li, Y.S.; Pan, L. Convenient Syntheses and Versatile Functionalizations of Isotactic Polypropylene Containing Plentiful Pendant Styrene Groups with High Efficiency. Macromolecules 2015, 48, 1991–1998. [Google Scholar] [CrossRef]
  11. Mulhaupt, R.; Ovenall, D.W.; Ittel, S.D. Control of composition in ethylene copolymerizations using magnesium mhloride supported Ziegler–Natta catalysts. J. Polym. Sci. Part A Polym. Chem. 1988, 26, 2487–2500. [Google Scholar] [CrossRef]
  12. Tsujino, T.; Saegusa, T.; Furukawa, J. Polymerization of norbornene by modified Ziegler-catalysts. Die Makromol. Chem. 2003, 85, 71–79. [Google Scholar] [CrossRef]
  13. Pan, L.; Ye, W.P.; Liu, J.Y.; Hong, M.; Li, Y.S. Efficient, regioselective copolymerization of ethylene with cyclopentadiene by the titanium complexes bearing two β-enaminoketonato ligands. Macromolecules 2008, 41, 2981–2983. [Google Scholar] [CrossRef]
  14. Pan, L.; Hong, M.; Liu, J.Y.; Ye, W.P.; Li, Y.S. Living copolymerization of ethylene with dicyclopentadiene using titanium catalyst: Formation of well-defined polyethylene-block-poly(ethylene-co-dicyclopentadiene)s and their transformation into novel polyolefin-block-(functional polyolefin)s. Macromolecules 2009, 42, 4391–4393. [Google Scholar] [CrossRef]
  15. Lasarov, H.; Pakkanen, T.T. Copolymerization of ethylene with 5-vinyl-2-norbornene in the presence of the Ph2C(Flu)(Cp)ZrCl2/MAO catalyst. Macromol. Chem. Phys. 2000, 201, 1780–1786. [Google Scholar] [CrossRef]
  16. Liu, J.Y.; Liu, S.R.; Pan, L.; Li, Y.S. Facile, efficient copolymerization of ethylene with bicyclic, non-conjugated dienes by titanium complexes bearing bis(β-enaminoketonato) ligands. Adv. Synth. Catal. 2009, 351, 1505–1511. [Google Scholar] [CrossRef]
  17. Hou, Z.M.; Luo, Y.J.; Li, X.F. Cationic rare earth metal alkyls as novel catalysts for olefin polymerization and copolymerization. J. Organomet. Chem. 2006, 691, 3114–3121. [Google Scholar] [CrossRef]
  18. Li, X.F.; Nishiura, M.; Mori, K.; Mashiko, T.; Hou, Z.M. Cationic scandium aminobenzyl complexes. Synthesis, structure and unprecedented catalysis of copolymerization of 1-hexene and dicyclopentadiene. Chem. Commun. 2007, 40, 4137–4139. [Google Scholar] [CrossRef] [PubMed]
  19. Li, X.F.; Hou, Z.M. Organometallic catalysts for copolymerization of cyclic olefins. Coord. Chem. Rev. 2008, 252, 1842–1869. [Google Scholar] [CrossRef]
  20. Li, X.F.; Hou, Z.M. Scandium-catalyzed regio- and stereospecific cis-1,4-polymerization of 1,3-cyclohexadiene and copolymerization with ethylene. Macromolecules 2010, 43, 8904–8909. [Google Scholar] [CrossRef]
  21. Hasan, T.; Ikeda, T.; Shiono, T. Homo- and copolymerization of norbornene derivatives with ethene by ansa-fluorenylamidodimethyltitanium activated with methylaluminoxane. J. Polym. Sci. Part A Polym. Chem. 2007, 45, 4581–4587. [Google Scholar] [CrossRef]
  22. Nishii, K.; Hayano, S.; Tsunogae, Y.; Cai, Z.G.; Nakayama, Y.; Shiono, T. Highly Active Copolymerization of Ethylene and Dicyclopentadiene with [(η1-t-BuN)SiMe2(η1-C29H36)]TiMe2(THF) Complex. Chem. Lett. 2008, 37, 590–591. [Google Scholar] [CrossRef]
  23. Christman, D.L.; Keim, G.I. Reactivities of nonconjugated dienes used in preparation of terpolymers in homogeneous systems. Macromolecules 1968, 1, 358–363. [Google Scholar] [CrossRef]
  24. Carrick, W.L.; Kluiber, R.W.; Bonner, E.F.; Wartman, L.H.; Rugg, F.M.; Smith, J.J. Transition Metal Catalysts. I. Ethylene polymerization with a soluble catalyst formed from an aluminum halide, tetraphenyltin and a vanadium halide. J. Am. Chem. Soc. 1960, 82, 3883–3887. [Google Scholar] [CrossRef]
  25. Carrick, W.L. Mechanism of ethylene polymerization with vanadium catalysts. J. Am. Chem. Soc. 2002, 80, 6455–6456. [Google Scholar] [CrossRef]
  26. Doi, Y.; Ueki, S.; Keii, T. “Living” Coordination polymerization of propene initiated by the soluble V(acac)3-Al(C2H5)2Cl System. Macromolecules 1979, 12, 814–819. [Google Scholar] [CrossRef]
  27. Adisson, E.; Deffieux, A.; Fontanille, M. Polymerization of ethylene at high temperature by vanadium-based heterogeneous Ziegler–Natta catalysts. I. study of the deactivation process. J. Polym. Sci. Part A Polym. Chem. 1993, 31, 831–839. [Google Scholar] [CrossRef]
  28. Wu, J.Q.; Li, Y.S. Well-defined vanadium complexes as the catalysts for olefin polymerization. Coord. Chem. Rev. 2011, 255, 2303–2314. [Google Scholar] [CrossRef]
  29. Gambarotta, S. Vanadium-based Ziegler–Natta: Challenges, promises, problems. Coord. Chem. Rev. 2003, 237, 229–243. [Google Scholar] [CrossRef]
  30. Hagen, H.; Boersma, J.; van Koten, G. Homogeneous vanadium-based catalysts for the Ziegler–Natta polymerization of α-Olefins. Chem. Soc. Rev. 2002, 31, 357–364. [Google Scholar] [CrossRef] [PubMed]
  31. Redshaw, C. Vanadium procatalysts bearing chelating aryloxides: Structure-activity trends in ethylene polymerisation. Dalton Trans. 2010, 39, 5595–5604. [Google Scholar] [CrossRef] [PubMed]
  32. Nomura, K.; Zhang, S. Design of vanadium complex catalysts for precise olefin polymerization. Chem. Rev. 2011, 111, 2342–2362. [Google Scholar] [CrossRef] [PubMed]
  33. Wang, K.T.; Wang, Y.X.; Wang, B.; Li, Y.G.; Li, Y.S. Introduction of constrained cyclic skeleton into β-enaminoketonato vanadium complexs: A strategy for stabilization of active center of vanadium catalyst for ethylene polymerization. J. Polym. Sci. 2017, 35, 1110–1121. [Google Scholar]
  34. Tomov, A.K.; Gibson, V.C.; Zaher, D.; Elsegood, M.R.; Dale, S.H. Bis(benzimidazole)amine vanadium catalysts for olefin polymerisation and co-polymerisation: Thermally robust, single-site catalysts activated by simple alkylaluminium reagents. Chem. Commun. 2004, 17, 1956–1957. [Google Scholar] [CrossRef] [PubMed]
  35. Redshaw, C.; Rowan, M.A.; Homden, D.M.; Dale, S.H.; Elsegood, M.R.; Matsui, S.; Matsuura, S. Vanadyl C and N-capped tris(phenolate) complexes: Influence of pro-catalyst geometry on catalytic activity. Chem. Commun. 2006, 31, 3329–3331. [Google Scholar] [CrossRef] [PubMed]
  36. Homden, D.M.; Redshaw, C.; Hughes, D.L. Vanadium complexes possessing N2O2S2-based ligands: Highly active procatalysts for the homopolymerization of ethylene and copolymerization of ethylene/1-hexene. Inorg. Chem. 2007, 46, 10827–10839. [Google Scholar] [CrossRef] [PubMed]
  37. Wang, J.B.; Lu, L.P.; Liu, J.Y.; Li, Y.S. [ONN]-type amine pyridine(s) phenolate-based oxovanadium(V) catalysts for ethylene homo- and copolymerization. Dalton Trans. 2014, 43, 12926–12934. [Google Scholar] [CrossRef] [PubMed]
  38. Wang, J.B.; Lu, L.P.; Liu, J.Y.; Mu, H.L.; Li, Y.S. [ONNO]-type oxovanadium(V) complexes containing amine pyridine bis(Phenolate) ligands: Synthesis, characterization and catalytic behavior for ethylene (co)polymerization. J. Mol. Catal. A Chem. 2015, 398, 289–296. [Google Scholar] [CrossRef]
  39. Li, Y.L.; Yang, J.X.; Wang, B.; Li, Y.S. Efficient copolymerization of ethylene with norbornene or its derivatives using half-metallocene zirconium(IV) catalysts. RSC Adv. 2016, 6, 59590–59599. [Google Scholar] [CrossRef]
  40. Chien, J.C.W.; Nozaki, T. Ethylene-hexene copolymerization by heterogeneous and homogeneous Ziegler–Natta catalysts and the “comonomer” effect. J. Polym. Sci. A 1993, 31, 227–237. [Google Scholar] [CrossRef]
  41. Koivumiiki, J.; Seppälä, J.V. Observations on the rate enhancement effect with MgC12/TiCl4 and Cp2ZrCl2 catalyst systems upon 1-hexene addition. Macromolecules 1994, 27, 2008–2012. [Google Scholar] [CrossRef]
  42. Suzukamo, G.; Fukao, M.; Minobe, M. Preparation of new solid super base and its catalytic activity. Chem. Lett. 1987, 16, 585–588. [Google Scholar] [CrossRef]
Polymers 09 00353 sch001 550
Scheme 1. Structures of [ONNO]-type (a–c) and [ONN]-type (d,e) oxovanadium(V) complexes.
Scheme 1. Structures of [ONNO]-type (a–c) and [ONN]-type (d,e) oxovanadium(V) complexes.
Polymers 09 00353 sch001
Polymers 09 00353 g001 550
Figure 1. The influences of VNB concentration in feed on the catalytic activities of complex b and VNB incorporations in the copolymers.
Figure 1. The influences of VNB concentration in feed on the catalytic activities of complex b and VNB incorporations in the copolymers.
Polymers 09 00353 g001
Polymers 09 00353 g002 550
Figure 2. 13C and 1H NMR spectra of E/VNB copolymer with VNB incorporation of 33.0 mol % produced by b/Et2AlCl/ETA catalytic system (Entry 14 in Table 1).
Figure 2. 13C and 1H NMR spectra of E/VNB copolymer with VNB incorporation of 33.0 mol % produced by b/Et2AlCl/ETA catalytic system (Entry 14 in Table 1).
Polymers 09 00353 g002
Polymers 09 00353 g003 550
Figure 3. The influences of ENB concentration in feed on the catalytic activities of catalyst b and ENB incorporations in the E/ENB copolymers.
Figure 3. The influences of ENB concentration in feed on the catalytic activities of catalyst b and ENB incorporations in the E/ENB copolymers.
Polymers 09 00353 g003
Polymers 09 00353 g004 550
Figure 4. (a) 1H NMR spectra of ENB monomer (2A), E/ENB copolymer with 17.8 mol % of ENB content (2B, Entry 1 in Table 2) and E/ENB copolymer with 30.4 mol % of ENB content (2C, Entry 9 in Table 2), respectively; (b) 13C NMR spectrum of E/ENB copolymer prepared by b/Et2AlCl/ETA catalytic system (ENB incorporation: 30.4 mol %, Entry 9 in Table 2).
Figure 4. (a) 1H NMR spectra of ENB monomer (2A), E/ENB copolymer with 17.8 mol % of ENB content (2B, Entry 1 in Table 2) and E/ENB copolymer with 30.4 mol % of ENB content (2C, Entry 9 in Table 2), respectively; (b) 13C NMR spectrum of E/ENB copolymer prepared by b/Et2AlCl/ETA catalytic system (ENB incorporation: 30.4 mol %, Entry 9 in Table 2).
Polymers 09 00353 g004
Polymers 09 00353 g005 550
Figure 5. The influences of DCPD concentration on the catalytic activities of catalyst b and DCPD incorporations of the E/DCPD copolymers.
Figure 5. The influences of DCPD concentration on the catalytic activities of catalyst b and DCPD incorporations of the E/DCPD copolymers.
Polymers 09 00353 g005
Polymers 09 00353 g006 550
Figure 6. (a) 1H spectrum and (b) 13C spectrum of E/DCPD copolymer with DCPD of 15.7 mol % (entry 7 in Table 3) prepared by e/Et2AlCl/ETA catalytic system.
Figure 6. (a) 1H spectrum and (b) 13C spectrum of E/DCPD copolymer with DCPD of 15.7 mol % (entry 7 in Table 3) prepared by e/Et2AlCl/ETA catalytic system.
Polymers 09 00353 g006
Table
Table 1. Ethylene/VNB copolymerization by oxovanadium(V) complexes.
Table 1. Ethylene/VNB copolymerization by oxovanadium(V) complexes.
EntryCat. (μmol)Al/V (Molar Ratio)VNB (mol/L)Activity (kg/mmolV h)VNB Incorp. aMw b (kDa)PDI bTg c (°C)Npolym/Ncat d
1a (2.0)400003.36-1131.9-5.00
2a (2.0)40000.500.548.986.42.0521.00
3b (2.0)4000032.4-1932.1-28.0
4b (2.0)40000.503.4811.959.12.2549.80
5c (2.0)400006.00-1351.8-7.40
6c (2.0)40000.501.869.133.62.0529.20
7b (2.0)20000.502.8212.562.12.1557.60
8b (2.0)60000.503.8111.642.82.05314.0
9b (2.0)40000.255.798.367.62.05114.0
10b (2.0)40000.752.6114.835.91.95612.0
11b (2.0)40001.001.5019.325.71.9749.70
12b (2.0)40001.500.9326.610.91.88214.0
13b (2.0)40002.000.7229.26.421.8881.90
14b (2.0)40003.000.4133.05.121.9911.40
15d (1.0)4000017.8-2203.3-13.0
16d (1.0)40000.508.228.730.42.15145.0
17e (1.0)4000058.3-62.42.3-156
18e (1.0)40000.509.2410.434.62.25345.0
19e (1.0)40001.005.1617.931.01.97328.0
Polymerization conditions: the copolymerizations were carried out in 50 mL of toluene at 50 °C under 4 atm of ethylene pressure, the polymerization time was 10 min, ETA (300 equiv. to vanadium complexes) was employed as reactivating agent; a VNB incorporations were (mol %) calculated from 1H NMR spectra; b Weight-average molecular weight (Mw) and polydispersity indexes (PDI) of the copolymers were determined by high temperature GPC at 150 °C in 1,2,4-trichlorobenzene; c The glass transition temperatures of the copolymers were determined by DSC; d The number of polymer chains produced by one catalytic molecule, which was calculated by the follow formula: (Mass of polymer/MW of polymer)/Molar of catalyst.
Table
Table 2. Ethylene/ENB copolymerization by oxovanadium(V) complexes.
Table 2. Ethylene/ENB copolymerization by oxovanadium(V) complexes.
EntryCat. (μmol)Al/V (Molar Ratio)VNB (mol/L)Activity (kg/mmolV h)ENB Incorp. aMw b (kDa)PDI bTg c (°C)npolym/ncat d
1b (0.25)40000.5061.017.81682.0733.00
2c (0.25)40000.508.1618.12392.1730.30
3b (0.25)20000.5025.917.22212.1701.00
4b (0.25)60000.5064.318.51491.9753.60
5 eb (0.25)40000.5048.515.32562.2631.60
6 fb (0.25)40000.5049.916.71952.1694.30
7b (0.25)40000.2560.011.51772.0542.80
8b (0.25)40000.7568.323.91692.1803.40
9b (0.25)40001.0049.430.41532.3872.70
10d (0.10)40000.5092.416.91382.0715.60
11e (0.10)40000.5012218.81012.07710.0
Polymerization conditions: the copolymerizations were carried out in 50 mL of toluene at 50 °C under 4 atm of ethylene pressure, polymerization for 5 min, ETA (300 equiv. to the catalyst) was employed as reactivating agent; a ENB incorporations (mol %) were calculated from 1H NMR spectra; b Mw and PDI of the copolymers were determined by high temperature GPC at 150 °C; c The glass transition temperatures of the copolymers were determined by DSC; d The number of polymer chains produced by one catalytic molecule, which was calculated by the follow formula: (Mass of polymer/MW of polymer)/Molar of catalyst; e Copolymerization was carried out at 25 °C; f Polymerization for 10 min.
Table
Table 3. Ethylene/DCPD copolymerization by oxovanadium(V) complexes.
Table 3. Ethylene/DCPD copolymerization by oxovanadium(V) complexes.
EntryCat. (μmol)Al/V (Molar Ratio)DCPD (mol/L)Activity (kg/mmolV h)DCPD Incorp. aMw b (kDa)PDI bTg c (°C)Npolym/Ncat d
1b (0.50)40000.5023.310.61032.15538.0
2c (0.50)40000.501.328.554.21.7524.00
3b (0.50)20000.5029.811.11342.35637.0
4b (0.50)60000.5026.310.387.42.15550.0
5 eb (0.50)40000.5024.79.796.82.05221.0
6b (0.50)40000.2527.56.81311.95135.0
7b (0.50)40000.7514.015.789.41.96526.0
8b (0.50)40001.0012.520.163.11.67733.0
9d (0.25)40000.5039.419.880.92.07681.0
10e (0.25)40000.5050.921.471.42.279119
11e (0.25)40001.0032.931.659.72.19892.0
Polymerization conditions: the copolymerizations were carried out in 50 mL of toluene at 50 °C under 4 atm of ethylene pressure, polymerization for 10 min, ETA (300 equiv. to vanadium complexes) was employed as reactivating agent. a DCPD incorporation (mol %) were calculated by 1H NMR spectra; b Weight-average molecular weight and polydispersity index of the copolymers were determined by high temperature GPC at 150 °C; c The glass transition temperatures of the copolymers were determined by DSC; d The number of polymer chains produced by one catalytic molecule, which was calculated by the follow formula: (Mass of polymer/MW of polymer)/Molar of catalyst; e Copolymerization for 5 min.

Share and Cite

MDPI and ACS Style

Wang, K.; Wang, J.; Li, Y.; Pan, L.; Li, Y. Facile, Efficient Copolymerization of Ethylene with Norbornene-Containing Dienes Promoted by Single Site Non-Metallocene Oxovanadium(V) Catalytic System. Polymers 2017, 9, 353. https://doi.org/10.3390/polym9080353

AMA Style

Wang K, Wang J, Li Y, Pan L, Li Y. Facile, Efficient Copolymerization of Ethylene with Norbornene-Containing Dienes Promoted by Single Site Non-Metallocene Oxovanadium(V) Catalytic System. Polymers. 2017; 9(8):353. https://doi.org/10.3390/polym9080353

Chicago/Turabian Style

Wang, Kaiti, Jiabao Wang, Yanguo Li, Li Pan, and Yuesheng Li. 2017. "Facile, Efficient Copolymerization of Ethylene with Norbornene-Containing Dienes Promoted by Single Site Non-Metallocene Oxovanadium(V) Catalytic System" Polymers 9, no. 8: 353. https://doi.org/10.3390/polym9080353

APA Style

Wang, K., Wang, J., Li, Y., Pan, L., & Li, Y. (2017). Facile, Efficient Copolymerization of Ethylene with Norbornene-Containing Dienes Promoted by Single Site Non-Metallocene Oxovanadium(V) Catalytic System. Polymers, 9(8), 353. https://doi.org/10.3390/polym9080353

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.