Next Article in Journal
BBUNS: Bluetooth Beacon-Based Underground Navigation System to Support Mine Haulage Operations
Next Article in Special Issue
Trends in Structure and Thermodynamic Properties of Normal Rare Earth Carbonates and Rare Earth Hydroxycarbonates
Previous Article in Journal
Quantification and Prediction of Bulk Gold Fineness at Placer Gold Mines: A New Zealand Example
Previous Article in Special Issue
REE Incorporation into Calcite Individual Crystals as One Time Spike Addition
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Minerals
Volume 7
Issue 11
10.3390/min7110227
minerals-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Short-Range Stacking Disorder in Mixed-Layer Compounds: A HAADF STEM Study of Bastnäsite-Parisite Intergrowths

by
Cristiana L. Ciobanu
1,*,
Alkis Kontonikas-Charos
1,
Ashley Slattery
2,
Nigel J. Cook
1,
Benjamin P. Wade
2 and
Kathy Ehrig
3
1
School of Chemical Engineering, The University of Adelaide, Adelaide, SA 5005, Australia
2
Adelaide Microscopy, The University of Adelaide, Adelaide, SA 5005, Australia
3
BHP Olympic Dam, Adelaide, SA 5000, Australia
*
Author to whom correspondence should be addressed.
Minerals 2017, 7(11), 227; https://doi.org/10.3390/min7110227
Submission received: 3 October 2017 / Revised: 11 November 2017 / Accepted: 13 November 2017 / Published: 20 November 2017
(This article belongs to the Special Issue Rare-Earth Carbonates)
Browse Figures
Versions Notes

Abstract

:
Atomic-scale high angle annular dark field scanning transmission electron microscopy (HAADF STEM) imaging and electron diffractions are used to address the complexity of lattice-scale intergrowths of REE-fluorocarbonates from an occurrence adjacent to the Olympic Dam deposit, South Australia. The aims are to define the species present within the intergrowths and also assess the value of the HAADF STEM technique in resolving stacking sequences within mixed-layer compounds. Results provide insights into the definition of species and crystal-structural modularity. Lattice-scale intergrowths account for the compositional range between bastnäsite and parasite, as measured by electron probe microanalysis (at the µm-scale throughout the entire area of the intergrowths). These comprise rhythmic intervals of parisite and bastnäsite, or stacking sequences with gradational changes in the slab stacking between B, BBS and BS types (B—bastnäsite, S—synchysite). An additional occurrence of an unnamed B2S phase [CaCe3(CO3)4F3], up to 11 unit cells in width, is identified among sequences of parisite and bastnäsite within the studied lamellar intergrowths. Both B2S and associated parisite show hexagonal lattices, interpreted as 2H polytypes with c = 28 and 38 Å, respectively. 2H parisite is a new, short hexagonal polytype that can be added to the 14 previously reported polytypes (both hexagonal and rhombohedral) for this mineral. The correlation between satellite reflections and the number of layers along the stacking direction (c*) can be written empirically as: Nsat = [(m × 2) + (n × 4)] − 1 for all BmSn compounds with S ≠ 0. The present study shows intergrowths characterised by short-range stacking disorder and coherent changes in stacking along perpendicular directions. Knowing that the same compositional range can be expressed as long-period stacking compounds in the group, the present intergrowths are interpreted as being related to disequilibrium crystallisation followed by replacement. HAADF STEM imaging is found to be efficient for depiction of stacking sequences and their changes in mixed-layer compounds, particularly those in which heavy atoms, such as rare-earth elements, are essential components.

1. Introduction

Advanced electron microscopy of foils prepared by focused ion beam-scanning electron microscopy (FIB-SEM) allows atomic-scale insight into patterns of element distribution in minerals, with significance for both petrogenesis and the minerals industry [1]. High angle annular dark field-scanning transmission electron microscopy (HAADF STEM) is a particularly useful technique for showing nanoscale features of materials, including nanoparticles, smallest atomic clusters, or the crystal-structural motifs in sulphosalt minerals with complex chemistry (e.g., [1,2,3]).
Among minerals of emerging economic significance are the REE-fluorocarbonates which comprise the majority of worldwide REE reserves (e.g., [4]). These minerals are reported from a variety of magmatic environments, ranging from basaltic vacuoles to pegmatites of either granitic or alkaline affiliation (e.g., [5,6,7]). REE-fluorocarbonates also appear concentrated within a range of deposits that are loosely affiliated to the iron-oxide copper gold (IOCG) clan, including the giant REE-deposit at Bayan Obo, Inner Mongolia, China (e.g., [8]) and Phalaborwa, South Africa [9]. REE-fluorocarbonates are also the dominant REE-carriers in the giant Olympic Dam Cu-U-Au-Ag deposit, South Australia [10,11], and in nearby mineralised prospects [12,13]. The stability of REE-fluorocarbonates could also be useful for tracking thermodynamic conditions of ore deposition since volatiles (F, CO3) are important hydrothermal ligands for transport and deposition of REE and other metals [4,14].
The bastnäsite-synchysite group (BSG) comprises REE-fluorocarbonates with mixed-layer structures in which REE- (hereafter, Ln) and Ca-bearing layers with various stacking arrangements can adapt to any intermediate composition between the end-members bastnäsite (LnFCO3; B slab) and synchysite (LnFCO3·CaCO3; S slab) [15,16,17]. Fluorine is contained within the Ln layer whereas CO3 groups form the ligand layers, either between two LnF layers, or between LnF and Ca layers (see below). There are currently only two other named mineral phases within the group: parisite (2LnFCO3·CaCO3; BS) and röntgenite (3LnFCO3·2CaCO3; BS2). In addition, a handful of BnSm polysomes and their polytypes, where n and m represent the number of B and S modules, are defined as long-range stacking compounds from transmission electron microscopy (TEM) studies (e.g., [16,18,19]; Table 1). Among these, the B2S polysome is also confirmed from X-ray single crystal studies [19].
The minerals in the group are illustrative of ‘polycrystals’ (syntaxic intergrowths of two chemically and structurally related species within the same crystal). They also represent one of the prototypes for mixed-layer stacking structures [15,16,20]. Euhedral crystals of parisite-(Ce) showing syntaxial intergrowths between various polysomes and their polytypes in the compositional range between parisite and B2S have been documented from a granite-hosted REE-deposit in Sichuan Province, SW China [18,19,21,22]. Epitaxial intergrowths of molybdenite with BSG species from the same Ca-poor side of the group (parisite, bastnäsite and their disordered lattice-scale intergrowths) were also reported in a preliminary TEM study of samples from mineralised granite in the vicinity of the Olympic Dam deposit [12]. In this case, the BSG minerals, intergrown with molybdenite and sericite, form an assemblage interpreted to pseudomorphically replace pre-existing plagioclase within red-stained granite [13]. They are illustrative of the link between early iron-metasomatism and REE-Mo-mineralisation at Olympic Dam since sub-µm-scale Fe-oxides are documented within pits along the parisite-dominant lamellae and also within K-feldspar in the same samples [12].
The present study employs atomic-scale HAADF STEM imaging supplementing TEM investigation to address the complexity of lattice-scale intergrowths in the aforementioned parisite-bastnäsite assemblages discussed by Kontonikas-Charos et al. [12]. The aims are firstly to define all species present within the intergrowths relative to the compositional range within the BSG minerals, and secondly, to assess the value of the HAADF STEM technique in resolving stacking sequences within long-period mixed layer compounds.

2. Background

Syntaxy and epitaxy are concepts used to describe crystals that show X-ray spectra indicating oriented intergrowths between species that are compositionally either the same (e.g., carborundum [25]), or closely related [15], and references therein). The term ‘polycrystal’ was suggested since most specimens analysed contain intergrowths of two species, with every pair observed except bastnäsite-synchysite [15]. The individual species share a pronounced pseudo-hexagonal centred lattice which is the basis for defining structures with common sub-motifs in terms of a′ = a/2cos30° and c‴ = c/n (n—integer), where there is a linear relationship between c‴ and the chemical composition, i.e., decreasing a′ and c′ from bastnäsite to synchysite [15]. Subsequent TEM studies have confirmed these findings and increased the number of species by adding seven unnamed polysomes (Table 1), which are recognisable as long-range stacking periods as well as their rhombohedral and/or hexagonal polytypes [16,18,19].
The crystal structure of minerals in this group was qualitatively described in terms of four types of layer, which are parallel to the hexagonal (000l) plane: (d) LnF ionic layers; (e) layers containing CO3 groups between two LnF layers; (f) layers with Ca ions; and (g) layers containing CO3 groups between a Ca- and a LnF-layer [15]. Such notation allows for representation of different structures in terms of stacking sequences as shown in Figure 1. The arrangement of CO3 groups in the (g) layers can be either perpendicular or diagonal to the layer stack defining hexagonal or rhombohedral lattice points.
The extensive syntaxy between the various species was recognised at a very fine scale in the first TEM study that addressed the mixed-layer model for structures of Donnay and Donnay [15], using both direct lattice imaging (in bright and dark field modes) and electron diffractions [16]. The study underpins the systematic variation between the number of satellite reflections on (000l)* rows (between strong reflections defining the pseudo-period c‴, c.f. [15]), and the number of layers within the two blocks/slabs, B and S. For example, parisite consisting of simple BS slabs shows five weak reflections leading to d0006 = c/6, corresponding to the six layers in the stacking sequence, i.e., two (de) and four (dgfg) layers in the B and S slabs, respectively (Table 1).
Despite the predictions that syntaxy among BSG phases is the governing rule, pure specimens were also found and used for crystal structure refinement using X-ray diffraction (XRD). These investigations confirm hexagonal symmetry for bastnäsite-(Ce) [17] but not for the two Ca-bearing species examined, synchysite-(Ce) and parisite-(Ce). These are instead interpreted to have monoclinic symmetry [23,24]. Furthermore, these XRD studies led to a different structural model whereby intergrowths of bastnäsite slabs with general formula: (CeF)n(CO3)n+1 (n = ∞ in bastnäsite, 1 in synchysite, 2 in parisite) are linked by (Ca) layers, the latter introducing a structural offset from hexagonal to monoclinic symmetry [23]. In complex mixed-layer BSG compounds or domains with large unit cells, ‘n’ can take different values [26].
The coplanar geometry of the Ca layer in both synchysite and parisite resembles that observed in vaterite, a CaCO3 polymorph [27]. Ni et al. [23] contend any compounds richer in Ca than synchysite are not possible as this would require Ca-Ca links resulting in vaterite-like slabs, unstable under geological conditions. Polytypism in both compounds is presumed by analogy with 2M micas [23,24].
The most recent structural interpretation of the bastnäsite-synchysite group, with the general formula: Cam(REE)n(CO3)n+m(F,OH)n (bastnäsite, m = 0, n = 1; synchysite, m = 1, n = 1; parisite, m = 1, n = 2; röntgenite, m = 2, n = 3 [28]), considers order-disorder (OD) formalism akin to that seen in vaterite [29]. In this case, the polytypism and OD phenomena are attributed only to the Ca-based layer (as in vaterite) whereas the REE-layers, although analogous to the Ca-based OD layer, has a p32 layer symmetry and thus their stacking does not lead to polytypism and OD phenomena.
As such, HAADF STEM imaging has not been applied to mixed-layer compounds in general, or to REE-fluorocarbonates specifically despite the potential of the technique for underpinning the layer complexity in long-period stacking sequences.

3. Experimental

The thin polished section from which the TEM samples are obtained was initially examined in backscatter electron (BSE) mode using an FEI Quanta 450 Field Emission Gun scanning electron microscope (FEI, Eindhoven, The Netherlands), equipped with a silicon-drift energy-dispersive X-ray spectrometer.
Electron probe microanalytical data on the REE-fluorocarbonate intergrowths was collected using a Cameca SX-Five electron probe microanalyzer (EPMA; Cameca, Paris, France) at Adelaide Microscopy, The University of Adelaide. The reader is referred to Supplementary Material Tables S2 and S3 in Schmandt et al. [11] (www.mdpi.com/2075-163X/7/10/202/s1) for full details of elements analysed, peak/background positions, count times, reference standards, set-up parameters, elemental overlap corrections and minimum limits of detection. The instrument was operated at 15 kV and 20 na and with a spot size of 1 µm.
Preparation of thinned (<100 nm) foils from the polished blocks for TEM investigation was performed using a FEI-Helios nanoLab (FEI, Hillsboro, OR, USA) Dual Focused Ion Beam and Scanning Electron Microscope (FIB-SEM) in the same laboratory. Extraction and thinning procedures followed [30]. Each TEM foil was attached to a copper grid.
Initial High-Resolution (HR)-TEM imaging in Bright Field mode (BF) and electron diffraction (illuminated area of 200 nm) were performed on a Philips CM200 TEM (Philips, Eindhoven, The Netherlands). The instrument is equipped with a LaB6 source, utilises a double-tilt holder and a Gatan Orius digital camera (Gatan Inc., Pleasanton, CA, USA) and was operated at 200 kV. Energy-dispersive X-Ray spectra (EDS) were acquired using an Oxford Instruments X-Max 65T SDD detector (Oxford Instruments, Abingdon, U.K.) running Aztec software. Diffraction measurements were performed using DigitalMicrograph™ 3.11.1 (Gatan Inc., Pleasanton, CA, USA) and Winwulff© 1.4.0 software (JCrystalSoft, Livermore, CA, USA). Data stored in the American Mineralogist Crystal Structure Database (http://rruff.geo.arizona.edu/AMS/amcsd.php) were used for indexing electron diffractions.
All HAADF STEM imaging and EDS measurements reported here were performed using an ultra-high resolution, probe-corrected, FEI Titan Themis S/TEM (FEI, Hillsboro, OR, USA) operated at 200 kV in the same laboratory. The spot size was 6 and the gun lens was 7 for this analysis. This instrument is equipped with the X-FEG Schottky source and Super-X EDS geometry. The Super-X EDS detector provides geometrically symmetric EDS detection with an effective solid angle of 0.8 sr. Probe correction delivered sub-Ångstrom spatial resolution and an inner collection angle greater than 50 mrad was used for HAADF experiments using the Fischione HAADF detector.

4. Results

4.1. Samples and Compositional Range of BSG Phases

In this study, we use two FIB-prepared TEM foils obtained from BSG intergrowths (Figure 2a–c) which occur as filling of a mm-sized grain of replaced feldspar [13]. The intergrowths are cut across sets of lamellae with varying composition, expressed by different contrast on BSE images. The intergrowths can be divided into those that are: (i) long (up to ~100 µm in length) and parallel to one another and with molybdenite (Foil 1; also documented in Kontonikas-Charos et al. [12]), and; (ii) shorter (<50 µm) sets of the same lamellae types but with variable orientation (Foil 2). In both cases, the brightest species on the BSE images (Ca-poor, bastnäsite) is subordinate to the darker one. The latter is often ‘pitted’ as it hosts sub- µm-sized inclusions of Fe-oxides (Figure 2b; [12]).
The bastnäsite is, in contrast, relatively clean. Some of the shorter and narrower lamellae appear distinct in that they feature rhythmical bands of bright and dark contrast within the same crystal/lamella (Figure 2c). HAADF STEM images of the two foils mimic the BSE images, whereas the BF TEM images show an inversed contrast with such images (e.g., Foil 2 in Figure 3 and Figure S1, respectively). The epitaxial associations between minerals in Foil 1 (BSG species, molybdenite and minor hematite), as well as HR-TEM images of lattice-scale intergrowths between bastnäsite and parisite, were discussed by Kontonikas-Charos et al. [12].
In Foil 2, the lamellar intergrowths between BSG phases are broadly oriented in two directions. At low magnification, most lamellae appear ‘composite’, either with gradational changes in colour, or contrasting bright and dark domains (Figure 3b). More homogenous parts of lamellae (Figure 3c), or stubby grains with well-defined edges are also identified (Figure 3e). In some cases, such lamella can display a rhythmic banding with bright and dark appearance representing bastnäsite and parisite, respectively (Figure 3f). For comparison with HAADF STEM imaging, Foil 2 and areas of interest are also imaged in BF TEM mode (Figure S1).
Electron probe microanalysis was carried out across the intergrowths around the areas with the FIB-cuts to compositionally constrain the brighter (Ca-poor) and darkest (Ca-richer) phases within the lamellar intergrowths (Figure 2d; Tables S1–S3). Microanalysis confirms predictions based on the stacking sequences and EDX spectra revealed in the preliminary TEM study in terms of the compositional range restricted to the compositional range between bastnäsite and parisite. EPMA data indicate that all species are Ce-dominant. The compositional data (32 individual analyses) plotted as Figure 2d defines compositions at the scale of the microprobe beam close to end-member bastnäsite and parisite but also within compositional space between parisite and B2S, and to a lesser extent between B2S and bastnäsite. Apart from REY, Ca and F, elements present at measurable concentrations were Sr and K (<0.05 wt % SrO and K2O), Th (up to 0.15 wt % ThO2), Fe (0.1–0.25 wt % FeO) and Cl (<0.1 wt %). Analyses with Fe concentrations > 0.3 wt % were not considered as this was readily attributed to mineral inclusions; Fe was not included in the formula calculation.

4.2. Stacking Sequences

Identification of stacking sequences was undertaken using electron diffractions and HAADF STEM imaging on identical areas. These were selected for the range of intergrowths and their heterogeneity as observed from TEM imaging.

4.2.1. Electron Diffractions and TEM Imaging

TEM BF imaging of both foils (Figure S2) shows that the lamellar intergrowths among BSG species vary widely in terms of the bright and dark rhythms (tens to hundreds of nm), rarely also displaying domains of an intermediate grey colour (identified in Foil 2). Other observed features include the cuspate edges of lamellae that show dark and bright sides, changes in the colour of the sequence along the lamella, as well as smaller, stubby grains or thin, single lamella that crosscut the regular lamellar sequences (Figure S2a–d). The latter are often typical of the darkest species on the BF TEM images, bastnäsite. Image contrast is mostly attributable to variation in chemistry as monitored by TEM EDS spectra giving a range of Ca-bearing BSG phases (brighter phases) and darkest phases with little or no Ca (bastnäsite). Such data is in agreement with [12]. In some cases, however, the variation in colour is also due to differences in orientation of lamellae from the same bundle.
Electron diffractions were obtained from the BSG phases tilted on the [−1100] and [10 − 10] zone axes, which are pertinent for interpreting stacking sequences from periodicity along the c* axis and their expression in 2-dimensional reciprocal space, respectively (Figure 4 and Figure 5). Although the [11 − 20] zone axis is similar or equivalent to the [10 − 10] zone axis, the latter will be used here for simplicity. Both ordered and disordered patterns were observed over the ~200 nm diameter of the selected area of electron diffraction (SAED). All SAEDs have orthogonal geometry indicating hexagonal lattices on both zone axes, whereby the smallest ac‴ subcells are marked as strong (Bragg) reflections, and the supercells are marked by satellite reflections with different periodicity along the c* axis (Figure 4 and Figure 5). The ordered supercells show 2-, 6- and 8-fold periodicities on the c* axis and correspond to stacking layers for c‴ in bastnäsite, parisite and the unnamed B2S compound (hereafter called ‘B2S’; Table 1; Figure 4a).
Bastnäsite from wider lamellae shows SAEDs with disorder (streaks between Bragg reflections) but no satellite reflections along c* (Figure 4b) when tilted on [−1100] zone axis. The 2 × c* (c = 2c‴~9.8 Å) periodicity of bastnäsite (Figure 4c) is rare and such SAEDs were obtained only from the small, stubby grains (Figure S2e,f) rather than from the coarser lamellae. On the same [−1100] zone axis, parisite is represented by 6 × c* (c′ = 6c‴~28 Å) patterns with no intensity variation (Figure 4d). In a few cases, however, the satellite reflections show variable intensity (cf. [16]; Figure 4e). TEM imaging of such parisite-bastnäsite sequences throughout both foils show ~28 Å and ~4.9 Å repeats along the c axis, respectively, with widespread defects as larger units (Figure S2g,h) as previously illustrated in Kontonikas-Charos et al. [12].
The 8-fold periodicity on the c* axis (c’ = 8c‴~37 Å) is attributable to B2S (Table 1; [19]) and was observed in areas of SAEDs that are otherwise representative of disordered bastnäsite (Figure 4f). These were obtained from lamellae that display domains with brightness intermediate between bastnäsite and parisite. The satellite reflections have generally the same intensity. Higher numbers of satellites, with variable intensity, as well as changes between bastnäsite and parisite along the c* axis, were also observed (Figure 4g,h).
All the SAEDs on [10 − 10] zone axis of the BSG species in the two foils show hexagonal symmetry (Figure 5a) but only the a2c‴ bastnäsite is well ordered (Figure 5b). The other SAEDs show a range of satellite reflections, variable in both number and intensity, along c* and parallel directions, suggesting intergrowths between different BSG species. For example, sequences with 6-fold periodicities along c* and parallel 3n rows displaying the ac′ superlattice of parisite are intercalated with 2 rows showing 2-fold (a2c‴ bastnäsite) periodicity, or with rows marked by strong disordering (Figure 5c,d). The latter are shown as streaks and satellite reflections of variable intensity, nonetheless marking a rectangular pattern indicating a hexagonal lattice. Comparable intergrowths are observed for SAEDs with 8-fold periodicities on the c* axis (Figure 5e). Such results require high-resolution imaging to reach a conclusion as to whether the stacking sequences represent (long period) polysomes of various types, or lattice-scale intergrowths between parisite, bastnäsite and B2S.

4.2.2. HAADF STEM Imaging

Several areas from Foil 2 were studied in closer detail (Figure 3) after low-magnification imaging both foils in HAADF STEM mode. The image contrast reveals banding within lamellae of various sizes, the smallest being a few hundred nm (Figure 6a,b). These low magnification images also show variation in the rhythms over several orders of magnitude, from just a few nm in width up to hundreds of nm within the same lamella. The colour variation due to orientation of the lamellae is highlighted by a decrease in contrast (e.g., Figure 6a). Wider parts of lamellar packages can have a homogenous appearance across widths of hundreds of nm (e.g., bastnäsite in Figure 6c). The mutual boundaries between individual lamellae within such aggregates show growth with imbricated relationships (Figure 6a–c), or triple junctions (Figure 6d). In the latter, the scale of banding is below tens of nm.
The stacking code for compounds in compositional range considered here is illustrated by atomic-scale HAADF STEM imaging of phases that contain both Ln(F) and Ca layers as, for example, in parisite. When tilted on [1 − 100] zone axis, this reveals bright atoms, attributable to Ln and Ca in order of decreasing intensity (d and f layers, respectively), forming parallel arrays along hh − 2h0 directions with ~3.6 Å distances between them (Figure 7a). These atomic arrays are separated from one another by darker strips at ~4.7 Å along c attributable to the lighter CO3 layers, e and g. Combinations of ‘de’ and ‘dgfg’ stacks form the B and S slabs along c with a BS repeat of ~14 Å, corresponding to one period of layer stacking in parisite (as shown in Figure 1a). The stacking code in HAADF STEM imaging is in good agreement with the distribution of atoms within the crystal structure of parisite (Figure 7b).
Longer sequences of regular B and BS slabs (up to tens of slab repeats in either case), and representing bastnäsite and parisite, respectively (Figure 8a,b), were imaged from many areas in both foils with the specimens tilted to [1 − 100] zone axis. Darkening of B slabs within bastnäsite (Figure 8a) is a common feature and could be interpreted as variation in the proportions of different Ln atoms (more La or Nd relative to Ce giving lesser or greater average atomic mass, respectively). Single slab defects are always present, as for example, SS slabs within parisite (Figure 8b).
The same stacking code is valid for HAADF STEM imaging of BSG phases on the [10 − 10] zone axis, as shown for parisite and the B2S phase (Figure 8c,d). In this case, however, the shortest distances along 0k − k0 directions are much smaller, ~2.1 Å, corresponding to the thickness of individual LnF or Ca layers (=a′/2). The B2S phase is identified from gradational sequences in area 1 of Foil 2 (Figure 3a,b). This consists of BBBS stacks with smallest width at ~38 Å (Figure 8d). Defects are present along both the c and b axes, as variable n × B stacks, or changes of layers from LnF to Ca, respectively. In the latter case, these can be recognised as an array of jogs accounting for a decrease in thickness of the B slabs (Figure 8d).
Irrespective of such single slab defects, longer stacking sequences in the 20 to 50 nm range can be recognised as regular bastnäsite, parisite and B2S intervals such as those imaged from area 1 in Foil 2 (Figure 9a–c). Such intervals can alternate with one another or form rhythms with decreasing widths (Figure 9a). The boundaries of longer intervals of parisite are marked by slab defects towards intervals of bastnäsite (Figure 9b). Likewise, the boundaries between B2S and parisite are marked by sequences with a greater abundance of B slabs alternating with BS (parisite) stacks (Figure 9c).
In closer detail, the stacking disorder observed over 20–30 nm intervals in parisite shows strips of 2–3 units of bastnäsite alternating with irregular sequences of B and S slabs (Figure 9d). Comparably, single S-stack defects within 5 or 6 × B slabs, as well as irregular sequences of B and S slabs over intervals of ~10 nm, are observed in bastnäsite (Figure 9e). Such stacking disorder most likely accounts for the SAEDs with streaks along c* (Figure 4b) observed in bastnäsite from lamellar intergrowths with parisite.
Lamellar intergrowths with strong contrast on HAADF STEM images such as those in area 6 (Figure 3f) are illustrative of one of the stacking sequence (~1 µm), in which longer rhythms of bastnäsite and parisite, tens to hundred nm in width, are seen (Figure 6a,c and Figure 10). This profile was imaged across the middle part between the two bastnäsite lamellae of 100–200 nm thickness forming the margins of the sequence (Figure 6a,c). The specimen was tilted on the [10 − 10] zone axis and representative SAEDs are shown in Figure 5c,d. The imaging shows three main domains of ~320 nm each: (i) on one side, one of the longest parisite intervals (>200 nm); (ii) in the middle part, short-range (tens of nm), irregular rhythms of bastnäsite and parisite with one interval including also the B2S (Figure 10); and (iii) at the other side, an interval of bastnäsite and parisite with gradational changes in the dominant component from the former to the latter (Figure 10). Throughout each of these intervals, stacking disorder is expressed either as single B or S slab defects, or as short range stacking irregularities as shown above (Figure 9).
Aside from changes in phase speciation via stacking disorder along the c axis, the BSG species also show changes in slab stacks and composition along other directions (Figure 11). The junctions between BSG phases in lamellae with slight offset to one another show relatively sharp boundaries (Figure 11a). In this case, co-crystallisation is suggested by the stepwise adjustment of B slabs on the longer side of a bastnäsite lamella matching the edges (between sets of S-slabs) of individual lamellae of disordered bastnäsite on the other side of the junction. Such an interpretation is also supported by the absence of open spaces and continuation of single S slabs, albeit with a kink, across the boundary.
Changes between B and S slabs on directions perpendicular to the c axis can lead to apparent transformation of bastnäsite into B2S or parisite stacking sequences across the c axis (Figure 11b,c). Such transformations are associated with aspects suggestive of overprinting rather than growth at equilibrium. These include layer-wide jogs between S and B slabs in the B2S and parisite sequences, slab darkening indicating absence of Ln or Ca cations (Figure 11c), as well as irregular interfaces associated with lattice strain in the slabs (Figure 11d).

5. Discussion

The present study provides further insights into: (i) the definition of species and crystal-structural modularity in mixed-layer REE-fluorocarbonate compounds in the bastnäsite-synchysite group; and (ii) the significance of short-range stacking disorder and coherent changes of stacks for genetic interpretations.
We report here a second occurrence of the B2S phase found among sequences of parisite and bastnäsite within the studied lamellar intergrowths. The longest BBS sequence (~19 Å wide) contains up to ~22 repeats, or 11 × B2S unit cells if we consider that 2 × BBS repeats represent a single unit cell with hexagonal symmetry. Indeed, both B2S and associated parisite show hexagonal lattices, as documented from electron diffractions and HAADF STEM imaging from the two zone axes (Figure 4d–f, Figure 5c–e and Figure 8b–d) obtained by tilting the specimen around the c* or c axis, respectively, at the same location. The lattice vectors defining the reciprocal space with distances at (~2 Å × 3) and (~4.7 Å × 6) do not give orthogonal solutions for indexing the electron diffractions when using the monoclinic cell for parisite [17].
Parisite and B2S species documented here are most likely 2H polytypes with c = 28 Å (c = 6 × c‴) and c = 38 Å (c = 8 × c‴), respectively. 2H parisite is a new, short hexagonal polytype that can be added to the 14 polytypes (both hexagonal and rhombohedral) that have been reported so far (Table S4; [16,21,22]). The 2H B2S polytype is a species among the seven variants reported from the occurrence in China (Table S4; [19]).
Two polytypes of bastnäsite are identified (Figure 4b,c and Figure 5b): the 2H polytype with P-62c space group [15,17], and a new species in which the presence of 000l reflections with l ≠ 2n indicates the absence of 2-fold operators along c. This is possibly a 1H polytype with P − 62m as one of the compatible space groups.
The specific features of diffraction patterns for mixed-layer compounds can be interpreted using a model superstructure in which two layer/slab types, although with different structures, fit epitaxially along the planar interfaces between the slabs [3]. Based on previous and present data, the correlation between satellite reflections and the number of layers along the stacking direction (c*) can be written empirically as: Nsat = [(m × 2) + (n × 4)] − 1 for all BmSn compounds with S ≠ 0 (Table 1). The number of satellites can vary; however, due to extinctions associated with symmetry elements in certain space groups, e.g., the number is half for phases within P − 62c space group due to the reflection condition 000l, l = 2n.
Variation in satellite intensity can occur due to lattice-scale intergrowths as interpreted here, or from the complexity of blocks within a given polysome. For example, the stacking sequence in the hexagonal polytype representing the B10S6 polysome can be written either as (3 × BBS)·(BS)·(BBS)·(BS), or the equivalent hierarchical sequence: B7S4·B3S2 (Figure 1b). The number of satellite reflections is predictable from the layer stacking (Table 1) but not the variation in the intensity of satellite reflections displayed along c* [18]. Its significance lies, however, within polysomatism in the group, requiring further studies with respect to modularity concepts akin to mixed-layer compounds. For example, a model of displacive modulation vectors have shown that the diffraction patterns, with two brightest reflections about the middle of d1*, are described by monotonic decrease of two modulations with increase in Bi in mixed-layered compounds from the tetradymite group in the compositional range Bi2Te3-Bi8Te3 [31].
Overall, the lattice-scale intergrowths account for the compositional range between bastnäsite and parisite revealed by electron probe microanalysis (Figure 2d; Tables S1–S3). In detail, the compositional range, which is almost continuous between parisite and B2S, is covered either by rhythmic intervals of parisite and bastnäsite, or by stacking sequences with gradational changes in the slab stacking between B, BBS and BS types as exemplified by the ~1 µm profile image shown as Figure 10. As shown in this study, HAADF STEM imaging is a well-suited tool for direct imaging of the stacking sequences as these are readily depicted by the arrays of heavier atoms (Ln and Ca). None of the polysome sequences defining the four species in the compositional range between the B2S phase and parisite (B7S4, B10S6, B3S2 and B8S6; Table 1, Figure 1b) were identified, although random blocks of variable B, BS, BBS or S slab widths are seen across any of the gradational intervals in the ~1 µm profile (Figure 10).
In contrast, the compositional interval between the B2S phase and parisite is covered by long-range polysomes and their polytypes, as known from the reported occurrence in China [18,19,21,22]. Such differences between the two occurrences may indicate that the same compositional range can be expressed by epitaxial intergrowths between either short- or long-range stacking polysomes/polytypes. In the present study, short-range stacking disorder occurs across blocks tens to hundreds of nm in size, precluding ordering of long-range period phases. Whereas both types of sequences can be presumed to originate via primary growth mechanisms, the growth rates differ depending upon the state of disequilibrium or (close-to-) equilibrium, respectively, of the thermodynamic system. We suggest that such phenomena, typical of syntaxial intergrowths, may be mechanisms for Ca-CO3 layer adjustment within hexagonal/rhombohedral lattices as opposed to the monoclinic shift interpreted from X-ray diffraction (XRD) studies of pure compounds [23,24].
In addition to the short-range stacking disorder, HAADF STEM imaging shows changes between different stacking sequences across grain boundaries, or along directions perpendicular to the stack (c axis; Figure 11). In the latter case, the interface between such changes is either straight or irregular (Figure 11c,d, respectively), inferring adjustment of the layers due to sharp chemical gradients. The irregular boundaries between bastnäsite and parisite, nonetheless preserving the coherence of atom arrays along the c axis, can be attributed to atom-scale replacement reactions whereby Ca-CO3 layers are converted into LnF-CO3 layers or vice versa. This can be attributed to processes responsible for chemical changes without open spaces such as metasomatism, with mechanisms of atom exchange invoking either diffusion across chemical gradients, or fluids that can infiltrate at lattice-scale. Such a process, imaged here at the atomic scale, is part of a broader spectrum of replacement reactions that advance by sharp fronts of fluid-mineral reaction by coupling dissolution with reprecipitation rates (CDRR; [32,33]). The importance of CDDR-driven mechanisms of mineral replacement throughout the hydrothermal evolution at Olympic Dam has been emphasised previously for different minerals and/or mineral pairs, including feldspars [12,13], uraninite ± Cu-Fe-sulphides [34,35,36], and hematite [37].

6. Implications and Outlook

In contrast to the lattice-scale intergrowths discussed here, end-member bastnäsite and synchysite have been documented from hematite-sericite-altered breccias hosting the Olympic Dam orebody [11]. On the other hand, the intimate, lattice-scale, relationships between BSG minerals and hematite [12] are not unique to this occurrence, a prospect distal to the deposit, but are also observed within the orebody, in which hematite hosts inclusions of BSG species [37]. These will be documented and discussed in further detail elsewhere. They are important for understanding the link between Fe- and REE-metasomatism at Olympic Dam, and for IOCG deposits in general. The present occurrence clearly carries significance in defining the early stage of magmatic feldspar alteration in deposits belonging to the IOCG clan, whereby Ca can be inferred to be derived from albitization and REE, F, and CO2 are introduced by hydrothermal fluids. The fact that such changes are mediated via CDRR (pseudomorphic replacement of feldspars) rather than open-fracture fluid circulation suggests that these elements are derived from the host granite rather than any other external source. The lattice-scale intergrowths documented here show that the compositional space between parisite and bastnäsite is accommodated by species within this interval without any synchysite present, supporting thermodynamic modelling of phase equilibria that indicate stepwise changes in composition between the two end-members in the group [4].
As shown here, HAADF STEM imaging is most appropriate for depiction of stacking sequences and their changes in mixed-layer compounds, particularly those in which heavy atoms (Ln) are essential components. This technique is however not readily applicable to visualisation of the lighter atoms; in this case, the internal geometry of the CO3 layers responsible for polytype identification. In follow-up studies, we will investigate if such atoms can be imaged by HAADF STEM at lower kV.
REE-fluorocarbonates are an exemplary group among other mixed-layer compounds which include shear structures, long-period antiphase boundary structures, polysynthetic twins, and in general periodic interface modulated structures [3]. Crystal structure modularity in such groups can be defined by different formalism concepts, as exemplified here by the polysomatic descriptions of BSG minerals [15,16,17,29]. Other examples of mixed-layer compounds that would benefit from atomic-scale HAADF STEM imaging of the stacking sequences include the NC-pyrrhotites, recently redefined by translation modulation interface ([38] and references therein), or the layer-module types which are considered to explain polysomatism in Bi- and Bi-Pb-chalcogenides of the tetradymite group and related aleksite series [31,39,40,41].

Supplementary Materials

The following are available online at www.mdpi.com/2075-163X/7/10/227/s1, Figure S1: BF TEM images showing Foil 2, Figure S2: BF low- and high-resolution TEM images showing aspects of the intergrowths in both foils, Table S1–S3: EPMA data, Table S4: Published data on polytypes of (A) parisite and (B) B2S.

Acknowledgments

This research was fully supported by BHP Olympic Dam. Adelaide Microscopy and the Australian Microscopy and Microanalysis Research Facility are gratefully acknowledged for access to instrumentation and the time for Titan Themis sessions. Cristiana L. Ciobanu acknowledges support from the “FOX” project (Trace elements in iron oxides: deportment, distribution, and application in ore genesis, geochronology, exploration, and mineral processing), sponsored by BHP Olympic Dam and the S.A. Mining and Petroleum Services Centre of Excellence. We thank two anonymous reviews for their insightful comments which help us improve our manuscript.

Author Contributions

Cristiana L. Ciobanu, Alkis Kontonikas-Charos, Ashley Slattery and Benjamin Wade performed all analytical work. Cristiana L. Ciobanu devised the project and guided all analysis and interpretation. Cristiana L. Ciobanu also wrote the paper, assisted by Nigel J. Cook, Alkis Kontonikas-Charos and Kathy Ehrig.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Ciobanu, C.L.; Cook, N.J.; Maunders, C.; Wade, B.P.; Ehrig, K. Focused Ion Beam and Advanced Electron Microscopy for Minerals: Insights and Outlook from Bismuth Sulphosalts. Minerals 2016, 6, 112. [Google Scholar] [CrossRef]
  2. Utsunomiya, S.; Ewing, R.C. Application of high-angle annular dark field scanning transmission electron microscopy, scanning transmission electron microscopy-energy dispersive X-ray spectrometry, and the energy-filtered transmission electron microscopy to the characterization of nanoparticles in the environment. Environ. Sci. Technol. 2003, 37, 786–791. [Google Scholar] [PubMed]
  3. Van Tendeloo, G.; Bals, S.; van Aert, S.; Verbeek, J.; van Dyck, D. Advanced electron microscopy for advanced materials. Adv. Mater. 2012, 24, 5655–5675. [Google Scholar] [CrossRef] [PubMed]
  4. Gysi, A.P.; Williams-Jones, A.E. The Thermodynamic Properties of Bastnäsite-(Ce) and Parisite-(Ce). Chem. Geol. 2015, 392, 87–101. [Google Scholar] [CrossRef]
  5. Guastoni, A.; Nestola, F.; Giaretta, A. Mineral Chemistry and Alteration of Rare Earth Element (REE) Carbonates from Alkaline Pegmatites of Mount Malosa, Malawi. Am. Mineral. 2009, 94, 1216–1222. [Google Scholar] [CrossRef]
  6. Miyawaki, R.; Yokoyama, K.; Husdal, T.A. Bastnäsite-(Nd), a new Nd-dominant member of the bastnäsite group from the Stetind pegmatite, Tysfjord, Nordland, Norway. Eur. J. Mineral. 2013, 25, 187–191. [Google Scholar] [CrossRef]
  7. Augé, T.; Bailly, L.; Wille, G. An Unusual Occurrence of Synchysite-(Ce) in Amygdules from the Esterel Volcanic Rocks, France: Implications for Rare-Earth Element Mobility. Can. Mineral. 2014, 52, 1–19. [Google Scholar] [CrossRef]
  8. Smith, M.P.; Henderson, P.; Campbell, L.S. Fractionation of the REE during Hydrothermal Processes: Constraints from the Bayan Obo Fe-REE-Nb Deposit, Inner Mongolia, China. Geochim. Cosmochim. Acta 2000, 64, 3141–3160. [Google Scholar] [CrossRef]
  9. Groves, D.I.; Vielreicher, N.M. The Phalabowra (Palabora) carbonatite-hosted magnetite-copper sulfide deposit, South Africa: An end-member of the iron-oxide copper-gold-rare earth element deposit group? Miner. Deposita 2001, 36, 189–194. [Google Scholar] [CrossRef]
  10. Ehrig, K.; McPhie, J.; Kamenetsky, V.S. Geology and mineralogical zonation of the Olympic Dam iron oxide Cu-U-Au-Ag deposit, South Australia. In Geology and Genesis of Major Copper Deposits and Districts of the World, a Tribute to Richard Sillitoe, Hedenquist, J.W., Harris, M., Camus, F., Eds. SEG Spec. Publ. 2012, 16, 237–268. [Google Scholar]
  11. Schmandt, D.S.; Cook, N.J.; Ciobanu, C.L.; Ehrig, K.; Wade, B.P.; Gilbert, S.; Kamenetsky, V.S. Rare earth element fluorocarbonate minerals from the Olympic Dam Cu-U-Au-Ag deposit, South Australia. Minerals 2017, 7, 202. [Google Scholar] [CrossRef]
  12. Kontonikas-Charos, A.; Ciobanu, C.L.; Cook, N.J.; Ehrig, K.; Krneta, S.; Kamenetsky, V.S. Feldspar Evolution in the Roxby Downs Granite, Host to Fe-Oxide Cu-Au-(U) Mineralisation at Olympic Dam, South Australia. Ore Geol. Rev. 2017, 80, 838–859. [Google Scholar] [CrossRef]
  13. Kontonikas-Charos, A.; Ciobanu, C.L.; Cook, N.J.; Ehrig, K.; Ismail, R.; Krneta, S.; Basak, A. Feldspar mineralogy and rare earth element (re)mobilization in iron-oxide copper gold systems from South Australia: A nanoscale study. Mineral. Mag. 2018, in press. [Google Scholar] [CrossRef]
  14. Williams-Jones, A.E.; Wood, S.A. A preliminary petrogenetic grid for REE fluorocarbonates and associated minerals. Geochim. Cosmochim. Acta 1992, 56, 725–738. [Google Scholar] [CrossRef]
  15. Donnay, G.; Donnay, J.D.H. The crystallography of bastnaesite, parisite, roentgenite and synchysite. Am. Mineral. 1953, 38, 932–963. [Google Scholar]
  16. Van Landuyt, J.; Amelinckx, S. Multiple Beam Direct Lattice Imaging of New Mixed-Layer Compounds of the Bastnaesite-Synchisite Series. Am. Mineral. 1975, 60, 351–358. [Google Scholar]
  17. Ni, Y.; Hughes, J.M.; Mariano, A.N. The Atomic Arrangement of Bastnäsite-(Ce), Ce(CO3)F, and Structural Elements of Synchysite-(Ce), Rontgenite-(Ce), and Parisite-(Ce). Am. Mineral. 1993, 78, 415–418. [Google Scholar]
  18. Wu, X.L.; Meng, D.W.; Pan, Z.L.; Yang, G.M.; Li, D.X. Transmission Electron Microscopic Study of New, Regular, Mixed-Layer Structures in Calcium-Rare-Earth Fluorocarbonate Minerals. Mineral. Mag. 1998, 62, 55–64. [Google Scholar]
  19. Meng, D.; Wua, X.; Han, Y.; Meng, X. Polytypism and microstructures of the mixed-layer member B2S, CaCe3(CO3)4F3 in the bastnaesite-(Ce)-synchysite-(Ce) series. Earth Planet. Sci. Lett. 2002, 203, 817–828. [Google Scholar] [CrossRef]
  20. Van Tendeloo, G.; van Dyck, D.; Kuypers, S.; Amelinckx, S. Electron Diffraction Effects in Mixed Layer Compounds. I. Theoretical Considerations. Phys. Statuds Solidi 1987, 101, 339–354. [Google Scholar]
  21. Meng, D.; Wu, X.; Mou, T.; Li, D. Microstructural investigation of new polytypes of parisite-(Ce) by high-resolution transmission electron microscopy. Can. Mineral. 2001, 39, 1713–1724. [Google Scholar] [CrossRef]
  22. Meng, D.; Wu, X.; Mou, T.; Li, D. Determination of six new polytypes in parisite-(Ce) by means of high-resolution electron microscopy. Mineral. Mag. 2001, 65, 797–806. [Google Scholar]
  23. Ni, Y.; Post, J.E.; Hughes, J.M. The Crystal Structure of Parisite-(Ce), Ce2CaF2(CO3)3. Am. Mineral. 2000, 85, 251–258. [Google Scholar] [CrossRef]
  24. Wang, L.; Ni, Y.; Hughes, J.M.; Bayliss, P.; Drexler, J.W. The atomic arrangement of synchysite-(Ce), CeCaF(CO3)2. Can. Mineral. 1994, 32, 865–871. [Google Scholar]
  25. Ungemach, H. Sur la syntaxie et la polytypie. Z. Krist.-Cryst. Mater. 1935, 91, 1–22. [Google Scholar] [CrossRef]
  26. Yang, G.M.; Tao, K.; Zhang, P. The symmetry transformations of modules in baestnasite-vaterite polysomatic series. N. Jahrb. Mineral. Monatsh. 1998, 1–12. [Google Scholar]
  27. Meyer, H.J. Struktur und Fehlordnung des Vaterits. Z. Krist.-Cryst. Mater. 1969, 128, 183–212. [Google Scholar] [CrossRef]
  28. Ferraris, G.; Makovicky, E.; Merlino, S. Crystallography of Modular Materials; Oxford University Press: Oxford, UK, 2008. [Google Scholar]
  29. Makovicky, E. Vaterite: Interpretation in terms of OD theory and its next of kin. Am. Mineral. 2016, 101, 1636–1641. [Google Scholar] [CrossRef]
  30. Ciobanu, C.L.; Cook, N.J.; Utsunomiya, S.; Pring, A.; Green, L. Focussed ion beam-transmission electron microscopy applications in ore mineralogy: Bridging micron- and nanoscale observations. Ore Geol. Rev. 2011, 42, 6–31. [Google Scholar] [CrossRef]
  31. Ciobanu, C.L.; Pring, A.; Cook, N.J.; Self, P.; Jefferson, D.; Dima, G.; Melnikov, V. Chemical-structural modularity in the tetradymite group: A HRTEM study. Am. Mineral. 2009, 94, 517–534. [Google Scholar] [CrossRef]
  32. Putnis, A. Mineral replacement reactions: From macroscopic observations to microscopic mechanisms. Mineral. Mag. 2002, 66, 689–708. [Google Scholar] [CrossRef]
  33. Ruiz-Agudo, E.; Putnis, C.V.; Putnis, A. Coupled dissolution and precipitation at mineral–fluid interfaces. Chem. Geol. 2014, 383, 132–146. [Google Scholar] [CrossRef]
  34. Macmillan, E.; Cook, N.J.; Ehrig, K.; Ciobanu, C.L.; Pring, A. Uraninite from the Olympic Dam IOCG-U-Ag deposit: Linking textural and compositional variation to temporal evolution. Am. Mineral. 2016, 101, 1295–1320. [Google Scholar] [CrossRef]
  35. Macmillan, E.; Ciobanu, C.L.; Ehrig, K.; Cook, N.J.; Pring, A. Chemical zoning and lattice distortion: Uraninite from Olympic Dam, South Australia. Am. Mineral. 2016, 101, 2351–2354. [Google Scholar] [CrossRef]
  36. Macmillan, E.; Ciobanu, C.L.; Ehrig, K.; Cook, N.J.; Pring, A. Replacement of uraninite by bornite via coupled dissolution-reprecipitation: Evidence from texture and microstructure. Can. Mineral. 2016, 54, 1369–1383. [Google Scholar] [CrossRef]
  37. Verdugo-Ihl, M.R.; Ciobanu, C.L.; Cook, N.J.; Ehrig, K.J.; Courtney-Davies, L.; Gilbert, S. Textures and U-W-Sn-Mo signatures in hematite from the Olympic Dam Cu-U-Au-Ag deposit, South Australia: Defining the archetype for IOCG deposits. Ore Geol. Rev. 2017, in press. [Google Scholar] [CrossRef]
  38. Harries, D.; Pollok, K.; Langenhorst, D. Translation interface modulation in NC-pyrrhotites: Direct imaging by TEM and a model toward understanding partially disordered structural states. Am. Mineral. 2011, 96, 716–731. [Google Scholar] [CrossRef]
  39. Cook, N.J.; Ciobanu, C.L.; Wagner, T.; Stanley, C.J. Minerals of the system Bi-Te-Se-S related to the tetradymite archetype: Review of classification and compositional variation. Can. Mineral. 2007, 45, 665–708. [Google Scholar] [CrossRef]
  40. Cook, N.J.; Ciobanu, C.L.; Stanley, C.J.; Paar, W.; Sundblad, K. Compositional data for Bi-Pb tellurosulfides. Can. Mineral. 2007, 45, 417–435. [Google Scholar] [CrossRef]
  41. Moëlo, Y.; Makovicky, E.; Mozgova, N.N.; Jambor, J.L.; Cook, N.; Pring, A.; Paar, W.; Nickel, E.H.; Graeser, S.; Karup-Møller, S.; et al. Sulfosalt systematics: A review. Report of the sulfosalt sub-committee of the IMA Commission on Ore Mineralogy. Eur. J. Mineral. 2008, 20, 7–62. [Google Scholar]
Minerals 07 00227 g001 550
Figure 1. Schematic representation of mixed-layer compounds in the bastnäsite-synchysite group based on the structural model of Donnay and Donnay [15]. Numbers in brackets represents the width of the sequence shown as: one period of the layer sequence except for bastnäsite and synchysite, which are shown as 2 periods (corresponding to 2 × a″ and 4 × a‴, respectively in (a)); (b) shows polysomes and their polytypes in the range between B2S and parisite [16,18]. H—hexagonal; R—rhombohedral.
Figure 1. Schematic representation of mixed-layer compounds in the bastnäsite-synchysite group based on the structural model of Donnay and Donnay [15]. Numbers in brackets represents the width of the sequence shown as: one period of the layer sequence except for bastnäsite and synchysite, which are shown as 2 periods (corresponding to 2 × a″ and 4 × a‴, respectively in (a)); (b) shows polysomes and their polytypes in the range between B2S and parisite [16,18]. H—hexagonal; R—rhombohedral.
Minerals 07 00227 g001
Minerals 07 00227 g002 550
Figure 2. (a–c) Back Scatter Electron (BSE) images showing bastnäsite-synchysite group (BSG) phases as lamellar aggregates intergrown with molybdenite (Moly) and sericite (Ser). Location of focused ion beam (FIB) cuts from where transmission electron microscopy (TEM) foils were obtained is shown in (b,c); (d) Plot REY vs. Ca from electron probe microanalyzer (EPMA) data showing the compositional range of analysed phases shown in (a–c) within the BSG phases.
Figure 2. (a–c) Back Scatter Electron (BSE) images showing bastnäsite-synchysite group (BSG) phases as lamellar aggregates intergrown with molybdenite (Moly) and sericite (Ser). Location of focused ion beam (FIB) cuts from where transmission electron microscopy (TEM) foils were obtained is shown in (b,c); (d) Plot REY vs. Ca from electron probe microanalyzer (EPMA) data showing the compositional range of analysed phases shown in (a–c) within the BSG phases.
Minerals 07 00227 g002
Minerals 07 00227 g003 550
Figure 3. Low-magnification high angle annular dark field-scanning transmission electron microscopy (HAADF STEM) images of Foil 2 in (a) and the areas of interest representing study cases as marked (b–f); The zone axis to which the specimen was tilted for HAADF STEM imaging is marked in (a); Bast—bastnäsite; Hm—hematite; Par—parisite.
Figure 3. Low-magnification high angle annular dark field-scanning transmission electron microscopy (HAADF STEM) images of Foil 2 in (a) and the areas of interest representing study cases as marked (b–f); The zone axis to which the specimen was tilted for HAADF STEM imaging is marked in (a); Bast—bastnäsite; Hm—hematite; Par—parisite.
Minerals 07 00227 g003
Minerals 07 00227 g004 550
Figure 4. (a) Selection of 000l* rows from selected areas of electron diffraction (SAEDs) in (b–g) showing the distribution of satellites between two Bragg reflections for different mixed-layer compounds as marked. Note that the number of satellite reflections Nsat corresponds to N − 1, where N is the number of layers within the composing B (=de) and S (=dgfg) slabs, i.e., Nsat = [(m × 2) + (n × 4)] − 1, for BmSn. Changes in the space group symmetry from P − 62c to P − 62m can be inferred based on the presence of 000l reflections with l ≠ 2n as shown in 2-fold bastnäsite (second strip from the top); (b,c) SAEDs on [1 − 100] zone axis of the studied BSG species. Disordered (space group P − 62c) and 2-fold (space group P − 62m) ordered bastnäsite are shown in (b) and (c), respectively. Parisite with satellite reflections of equal and variable intensity (I) are shown in (d,e); respectively; (f) The B2S phase with equal intensity of satellite reflections ordering along c* within a bastnäsite lattice; (g) Disordered n-fold sequence with variable intensity for satellite reflections along c*; (h) Changes in the BSG species along c* indicated by the occurrence of satellite reflections within a disordered bastnäsite lattice. Bast—bastnäsite; Par—parisite.
Figure 4. (a) Selection of 000l* rows from selected areas of electron diffraction (SAEDs) in (b–g) showing the distribution of satellites between two Bragg reflections for different mixed-layer compounds as marked. Note that the number of satellite reflections Nsat corresponds to N − 1, where N is the number of layers within the composing B (=de) and S (=dgfg) slabs, i.e., Nsat = [(m × 2) + (n × 4)] − 1, for BmSn. Changes in the space group symmetry from P − 62c to P − 62m can be inferred based on the presence of 000l reflections with l ≠ 2n as shown in 2-fold bastnäsite (second strip from the top); (b,c) SAEDs on [1 − 100] zone axis of the studied BSG species. Disordered (space group P − 62c) and 2-fold (space group P − 62m) ordered bastnäsite are shown in (b) and (c), respectively. Parisite with satellite reflections of equal and variable intensity (I) are shown in (d,e); respectively; (f) The B2S phase with equal intensity of satellite reflections ordering along c* within a bastnäsite lattice; (g) Disordered n-fold sequence with variable intensity for satellite reflections along c*; (h) Changes in the BSG species along c* indicated by the occurrence of satellite reflections within a disordered bastnäsite lattice. Bast—bastnäsite; Par—parisite.
Minerals 07 00227 g004
Minerals 07 00227 g005 550
Figure 5. (a) Two-dimensional sections through the reciprocal lattice of studied BSG species and their intergrowths (as marked) showing the distribution of satellite reflections on [10 − 10] zone axis selected from SAEDs in (b–e); Note the orthogonal patterns indicating a hexagonal lattice in all cases; (b–e) SAEDs on [10 − 10] zone axis for bastnäsite (b); intergrowths between parisite and bastnäsite (c); disordered parisite (d); and intergrowths between B2S and bastnäsite (e); Note the ordered 2-fold (or 2c‴) bastnäsite obtained by tilting the same grain shown for SAED on [−1100] zone axis in Figure 4c. The SAEDs in (c–e) represent intergrowths imaged on the same zone axis in Figure 10. Bast—bastnäsite; I—intensity; Par—parisite.
Figure 5. (a) Two-dimensional sections through the reciprocal lattice of studied BSG species and their intergrowths (as marked) showing the distribution of satellite reflections on [10 − 10] zone axis selected from SAEDs in (b–e); Note the orthogonal patterns indicating a hexagonal lattice in all cases; (b–e) SAEDs on [10 − 10] zone axis for bastnäsite (b); intergrowths between parisite and bastnäsite (c); disordered parisite (d); and intergrowths between B2S and bastnäsite (e); Note the ordered 2-fold (or 2c‴) bastnäsite obtained by tilting the same grain shown for SAED on [−1100] zone axis in Figure 4c. The SAEDs in (c–e) represent intergrowths imaged on the same zone axis in Figure 10. Bast—bastnäsite; I—intensity; Par—parisite.
Minerals 07 00227 g005
Minerals 07 00227 g006 550
Figure 6. Low-magnification HAADF STEM images of BSG intergrowths showing the wide range of lamellae thickness and their variation in contrast. Note crystal edges indicating such intergrowths include thinner (a few hundred nm) lamellae in (a,b); (a,b) Rhythmic variation displayed by sharp image contrast within each lamella. The rhythms vary in size from tens to hundreds of nm (a) and from a few to tens of nm in (b); (c) Edge of lamella showing one side with a wider (hundred nm) interval of bastnäsite (bright) and the other as fine-scale rhythms between species with sharp image contrast; (d) Triple junction (dotted line) between lamellae with fine-scale (less than a few to tens of nm) intergrowths with rhythmic or gradational changes in contrast. The bright phase at top left is bastnäsite.
Figure 6. Low-magnification HAADF STEM images of BSG intergrowths showing the wide range of lamellae thickness and their variation in contrast. Note crystal edges indicating such intergrowths include thinner (a few hundred nm) lamellae in (a,b); (a,b) Rhythmic variation displayed by sharp image contrast within each lamella. The rhythms vary in size from tens to hundreds of nm (a) and from a few to tens of nm in (b); (c) Edge of lamella showing one side with a wider (hundred nm) interval of bastnäsite (bright) and the other as fine-scale rhythms between species with sharp image contrast; (d) Triple junction (dotted line) between lamellae with fine-scale (less than a few to tens of nm) intergrowths with rhythmic or gradational changes in contrast. The bright phase at top left is bastnäsite.
Minerals 07 00227 g006
Minerals 07 00227 g007 550
Figure 7. Interpretation of the ‘stacking code’ for BSG compounds with both Ln and Ca layers as imaged in HAADF STEM mode. (a) Atomic-scale image of parisite viewed down to [−1100] zone axis with superimposed atoms and layers as marked; (b) Crystal structure of parisite (after Ni et al. [23]) showing the correspondence to the stacking layers. Unit cell marked in blue. The orientation (viewed down to a axis) is chosen so that the arrays of atoms correspond to the orthogonal lattice shown in (a).
Figure 7. Interpretation of the ‘stacking code’ for BSG compounds with both Ln and Ca layers as imaged in HAADF STEM mode. (a) Atomic-scale image of parisite viewed down to [−1100] zone axis with superimposed atoms and layers as marked; (b) Crystal structure of parisite (after Ni et al. [23]) showing the correspondence to the stacking layers. Unit cell marked in blue. The orientation (viewed down to a axis) is chosen so that the arrays of atoms correspond to the orthogonal lattice shown in (a).
Minerals 07 00227 g007
Minerals 07 00227 g008 550
Figure 8. HHADF STEM images showing the typical stacking sequences in the three BSG compounds identified. (a) Bastnäsite down to [−1100] showing the arrays of bright atoms interpreted as Ln (‘d’ layers). The B slab is represented by two rows of bright atoms. Darkening of layers represents most likely an artefact of the foil thickness/uneven orientation; (b,c) Parisite down to [−1100] and [10 − 10] zone axis, respectively. The sequence is characterised by two rows of bright atoms (B slab) and one row of slightly darker atoms (‘f’ layer in the middle of the S slab); (d) B2S imaged down to [10 − 10] zone axis. Note the density of atoms (at ~2 Å distance) along b axis in (c,d); The sequence is represented by three rows of bright atoms (2B slabs) and one row of slightly darker atoms (S slab). Defects as B slabs of variable width are arrowed in (d).
Figure 8. HHADF STEM images showing the typical stacking sequences in the three BSG compounds identified. (a) Bastnäsite down to [−1100] showing the arrays of bright atoms interpreted as Ln (‘d’ layers). The B slab is represented by two rows of bright atoms. Darkening of layers represents most likely an artefact of the foil thickness/uneven orientation; (b,c) Parisite down to [−1100] and [10 − 10] zone axis, respectively. The sequence is characterised by two rows of bright atoms (B slab) and one row of slightly darker atoms (‘f’ layer in the middle of the S slab); (d) B2S imaged down to [10 − 10] zone axis. Note the density of atoms (at ~2 Å distance) along b axis in (c,d); The sequence is represented by three rows of bright atoms (2B slabs) and one row of slightly darker atoms (S slab). Defects as B slabs of variable width are arrowed in (d).
Minerals 07 00227 g008
Minerals 07 00227 g009 550
Figure 9. HAADF STEM images showing ordered and disordered stacking sequences over longer (a–c) and shorter (d,e) intervals; (a) Alternating periods of ~20–35 nm of different phases as marked accounting for transitional contrast changes or compositional variation; (b,c) Longer (50–30 nm) periods of parisite and B2S phase, respectively, interspersed with B stacks of variable widths; (d,e) Details of stacking sequences in parisite (d) and bastnäsite intervals (e) showing stacking disorder as marked. Note the presence of 1- or 2-periods of BSS slab stacks (corresponding to röntgenite) but with isolated occurrence or erratic distribution throughout the host stacking sequence. Bast—bastnäsite; Par—parisite.
Figure 9. HAADF STEM images showing ordered and disordered stacking sequences over longer (a–c) and shorter (d,e) intervals; (a) Alternating periods of ~20–35 nm of different phases as marked accounting for transitional contrast changes or compositional variation; (b,c) Longer (50–30 nm) periods of parisite and B2S phase, respectively, interspersed with B stacks of variable widths; (d,e) Details of stacking sequences in parisite (d) and bastnäsite intervals (e) showing stacking disorder as marked. Note the presence of 1- or 2-periods of BSS slab stacks (corresponding to röntgenite) but with isolated occurrence or erratic distribution throughout the host stacking sequence. Bast—bastnäsite; Par—parisite.
Minerals 07 00227 g009
Minerals 07 00227 g010 550
Figure 10. Short-range stacking disorder over a ~1 µm-long profile across lamellar intergrowths from area 6 (marked on Figure 3f); specimen tilted down to [10 − 10] zone axis. The HAADF STEM imaging shows 100 nm periods of bastnäsite and parisite with gradational changes to intergrowths between 2- and 3-species (as marked). Bast—bastnäsite; Par—parisite.
Figure 10. Short-range stacking disorder over a ~1 µm-long profile across lamellar intergrowths from area 6 (marked on Figure 3f); specimen tilted down to [10 − 10] zone axis. The HAADF STEM imaging shows 100 nm periods of bastnäsite and parisite with gradational changes to intergrowths between 2- and 3-species (as marked). Bast—bastnäsite; Par—parisite.
Minerals 07 00227 g010
Minerals 07 00227 g011 550
Figure 11. Details of grain boundaries (a) and changes in the slab stack perpendicular to the layer stacking direction (c–e) illustrating co-crystallisation and overprint, respectively. HAADF STEM images are taken down to [−1100] for (a,d) and to [10 − 10] for (b,c); (a) Stepwise, 1–2 atom-wide adjustment between two lamellae of bastnäsite with variable defects as slabs of parasite; (b,c) Apparent transformation of bastnäsite into B2S or parisite stacking sequences across the c axis shown as changes between B and S slabs on directions perpendicular to the c axis; (d) Irregular interface between bastnäsite and parisite suggesting replacement between the two phases. Note the lattice strain in the slabs along this interface. Bast—bastnäsite; Par—parisite.
Figure 11. Details of grain boundaries (a) and changes in the slab stack perpendicular to the layer stacking direction (c–e) illustrating co-crystallisation and overprint, respectively. HAADF STEM images are taken down to [−1100] for (a,d) and to [10 − 10] for (b,c); (a) Stepwise, 1–2 atom-wide adjustment between two lamellae of bastnäsite with variable defects as slabs of parasite; (b,c) Apparent transformation of bastnäsite into B2S or parisite stacking sequences across the c axis shown as changes between B and S slabs on directions perpendicular to the c axis; (d) Irregular interface between bastnäsite and parisite suggesting replacement between the two phases. Note the lattice strain in the slabs along this interface. Bast—bastnäsite; Par—parisite.
Minerals 07 00227 g011
Table
Table 1. Chemistry, crystal structures and stacking sequences for all phases known in the bastnäsite-synchysite group.
Table 1. Chemistry, crystal structures and stacking sequences for all phases known in the bastnäsite-synchysite group.
NameFormula/Layer Types 1 * (after Ni et al. [17])CaCO3 (%)SlabsB/SLayer Types 2 ** (after Donnay and Donnay [15])NsatSpace Group/Symm #a (Å)b (Å)c‴ (Å)c (x n) (Å); n = number of c‴α (º)β (º)γ (º)References
Bastnäsite (B slab)Ce(CO3)F 0Bde2P − 62c7.167.164.899.79(×2)9090120[15,17], this study
1:1:0
CaCe3(CO3)4F325B2S22 × (de) ·dgfg8R, H7.137.134.7138.4(×8)9090120[19], this study
3:3:1
Ca4Ce11(CO3)15F11 26.7B7S41.757 × (de)·4 × (dgfg)30R, H~71[18]
11:11:4
Ca3Ce8(CO3)11F827.3B10S61.6710 × (de)·6 × (dgfg)44R, H~104[18]
8:8:3
Ca2Ce5(CO3)7F5 28.6B3S21.53 × (de)·2 × (dgfg)14R, H~33[16]
5:5:2
Ca3Ce7(CO3)10F7 30B8S61.338 × (de)·6 × (dgfg)40R, H~94[18]
7:7:3
ParisiteCaCe2(CO3)3F233BS1de·dgfg6R3; H7.127.124.6714(×3); 28(×6); 84.04(×18)9090120[15,16,21,22], this study
2:2:1Cc12.37.1128.259098.2490[23]
Ca4Ce7(CO3)11F736.4B3S40.753 × (de)·4 × (dgfg)22~104[16]
7:7:4
RöntgeniteCa2Ce3(CO3)5F340BS20.5de·2 × (dgfg)10R37.137.134.6223.1(×5); 69.4(×15)9090120[15]
3:3:2
Ca4Ce5(CO3)9F7 44.4BS40.25de·4 × (dgfg)18R, H~85[16]
5:5:4
Synchysite (S slab)CaCe(CO3)2F50S0dgfg4O, M, H?7.17.14.569.12(×2); 18.2(×4); 54.7(×12)[15,16]
1:1:1C2/c12.337.1118.7490102.6890[24]
* Layers 1 (after [17] are: CeF; CO3; Ca(CO3) of thickness = 2.24 Å except the latter which is 4.25 Å; ** Layers 2 (after [15]): d = LnF layer; e: CO3 layer between 2 LnF layers; f = Ca layer; g = CO3 layers between a CeF (or LnF) and Ca layers; # = both R and H polytypes documented from TEM studies [16,21,22]. c(×n) values for named mineral from [15] and for unnamed species calculated according for 1-period of layers in the stacking sequence (Layers 2). Other polytypes for parisite and B2S reported in the literature are given in Table S4. Nsat—number of satellites according to: Nsat = [(m × 2) + (n × 4)] − 1 for all BmSn compounds with S ≠ 0. H—hexagonal, O—orthorhombic; R—rhombohedral.

Share and Cite

MDPI and ACS Style

Ciobanu, C.L.; Kontonikas-Charos, A.; Slattery, A.; Cook, N.J.; Wade, B.P.; Ehrig, K. Short-Range Stacking Disorder in Mixed-Layer Compounds: A HAADF STEM Study of Bastnäsite-Parisite Intergrowths. Minerals 2017, 7, 227. https://doi.org/10.3390/min7110227

AMA Style

Ciobanu CL, Kontonikas-Charos A, Slattery A, Cook NJ, Wade BP, Ehrig K. Short-Range Stacking Disorder in Mixed-Layer Compounds: A HAADF STEM Study of Bastnäsite-Parisite Intergrowths. Minerals. 2017; 7(11):227. https://doi.org/10.3390/min7110227

Chicago/Turabian Style

Ciobanu, Cristiana L., Alkis Kontonikas-Charos, Ashley Slattery, Nigel J. Cook, Benjamin P. Wade, and Kathy Ehrig. 2017. "Short-Range Stacking Disorder in Mixed-Layer Compounds: A HAADF STEM Study of Bastnäsite-Parisite Intergrowths" Minerals 7, no. 11: 227. https://doi.org/10.3390/min7110227

APA Style

Ciobanu, C. L., Kontonikas-Charos, A., Slattery, A., Cook, N. J., Wade, B. P., & Ehrig, K. (2017). Short-Range Stacking Disorder in Mixed-Layer Compounds: A HAADF STEM Study of Bastnäsite-Parisite Intergrowths. Minerals, 7(11), 227. https://doi.org/10.3390/min7110227

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop