Next Article in Journal
Direct Transesterification for Biodiesel Production and Testing the Engine for Performance and Emissions Run on Biodiesel-Diesel-Nano Blends
Previous Article in Journal
Air-Filled Bubbles Stabilized by Gold Nanoparticle/Photodynamic Dye Hybrid Structures for Theranostics
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 11
Issue 2
10.3390/nano11020416
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Assessing Surface Coverage of Aminophenyl Bonding Sites on Diazotised Glassy Carbon Electrodes for Optimised Electrochemical Biosensor Performance

by
Zari Tehrani
1,*,†,
Hina Yaqub Abbasi
1,†,
Anitha Devadoss
1,
Jonathan Edward Evans
1 and
Owen James Guy
1,2
1
Centre for Nano Health, College of Engineering, Swansea University, Swansea SA2 8PP, UK
2
Department of Chemistry, College of Science, Swansea University, Swansea SA2 8PP, UK
*
Author to whom correspondence should be addressed.
†
Z.T. and H.Y.A. contributed equally to this work as first authors.
Nanomaterials 2021, 11(2), 416; https://doi.org/10.3390/nano11020416
Submission received: 3 January 2021 / Revised: 31 January 2021 / Accepted: 2 February 2021 / Published: 6 February 2021
Browse Figures
Versions Notes

Abstract

:
Electrochemical biosensors using carbon-based electrodes are being widely developed for the detection of a range of different diseases. Since their sensitivity depends on the surface coverage of bioreceptor moieties, it necessarily depends on the surface coverage of amine precursors. Electrochemical techniques, using ferrocene carboxylic acid as a rapid and cheap assay, were used to assess the surface coverage of amino-phenyl groups attached to the carbon electrode. While the number of electrons transferred in the first step of diazotisation indicated a surface coverage of 8.02 ± 0.2 × l0−10 (mol/cm2), and those transferred in the second step, a reduction of nitrophenyl to amino-phenyl, indicated an amine surface coverage of 4–5 × l0−10 (mol/cm2), the number of electrons transferred during attachment of the amine coupling assay compound, ferrocene carboxylic acid, indicated a much lower available amine coverage of only 2.2 × l0−11 (mol/cm2). Furthermore, the available amine coverage was critically dependent upon the number of cyclic voltammetry cycles used in the reduction, and thus the procedures used in this step influenced the sensitivity of any subsequent sensor. Amine coupling of a carboxyl terminated anti-beta amyloid antibody specific to Aβ(1-42) peptide, a potential marker for Alzheimer’s disease, followed the same pattern of coverage as that observed with ferrocene carboxylic acid, and at optimum amine coverage, the sensitivity of the differential pulse voltammetry sensor was in the range 0–200 ng/mL with the slope of 5.07 µA/ng·mL−1 and R2 = 0.98.

1. Introduction

There are several studies that highlight the need for rapid, sensitive techniques and emphasise that biosensor performance is highly dependent on substrate material [1,2]. Carbon-based electrochemical sensor platforms remain a high priority in the biosensor market owing to their low-cost, high sensitivity and simple surface chemistry. This gives great flexibility in designing carbon-based sensors for a wide range of analytes for early disease diagnostics. Various immobilisation strategies have been developed to attach biomolecules to the carbon sensor platform. Here, the selection of the functionalisation process plays a key role in determining the overall sensor performance. Diazonium grafting is one of the most promising methods as it provides a simple technique to immobilise functional groups via covalent attachment [3,4] onto a variety of substrates [5,6]. Diazotisation of carbon electrodes via reducing nitro group to amino group was first reported by M. Delamer et al. in the early 1990′s [7]. Diazonium surface modification and the chemical structure of the modification are shown in Scheme 1.
Later, functionalisation of materials via diazotisation has garnered interest, with several studies dedicated to exploring its potentials in sensing applications [8,9,10,11]. Surface-immobilised groups can induce specific chemical and physicochemical properties to the surface, which may be used in fields, such as chemical [9,12,13] or biological sensing [14,15,16,17,18,19], molecular electronics [20,21,22], microbial fuel cells [11] and energy conversion applications [23,24]. Additionally, diazonium salts have been used for the attachment of metal (aluminium, gold, etc.) nanoparticles [25,26,27], oxide nanoparticles [28,29,30] and nanotextured anti-icing surfaces [31].
Quantifying the efficiency of surface modification is critical to achieving the best sensor performance. A wide range of tools has been reported to determine the efficiency of the diazonium grafting process and quantify the surface coverage of nitrophenyl groups produced. For example, in 1995, Y. C. Liu et al. used high sensitivity surface Raman spectroscopy to obtain spectra from the monolayers of nitrophenyl groups covalently bonded to glassy carbon (GC) and highly ordered pyrolytic graphite (HOPG). They demonstrated that the electrochemical reduction of 4-nitrophenyl diazonium ions in acetonitrile resulted in the formation of 4-nitrophenyl radicals, which, in turn, covalently bonded to the glassy carbon surface. In their work, cyclic voltammetry, X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy data were used to estimate the surface coverage of 4-nitrophenyl as 6.5 × l0−10 mol/cm2 and 1.6 × l0−10 mol/cm2 on glassy carbon and HOPG, respectively. Surface coverages from the reduction of diazonium salts for different methods and substrates are given in Table 1.
Antibody immobilisation plays a critical role in determining the immunosensor performance.
Antibodies are composed of hundreds of amino acids to form the characteristic Y-shape, where the carboxyl (–COOH) group is positioned at the lower end of this Y-shape structure (Fc region- = —Scheme 2a). Through the two upper end parts of this Y-shape, which are amine-terminated (Fab region), each antibody is able to bind two antigen species. The orientation, chemical species for targeting, dimensions of antibodies all influence the attachment of the functional groups, such as -NH2 and –COOH, to the substrate.
Traditionally, the carboxyl group of the support surface is activated by carbodiimide and reacted with amino groups of antibodies to result in their cross-linking. This will lead to the random orientation of the antibody [37,38]. Therefore, ethyl-3-(3-(dimethylamino)-propyl) carbodiimide hydrochloride (EDC)/ N-hydroxysuccinimide (NHS) (EDC/NHS) coupling of antibody amine and carboxyl groups to surface carboxyl and amine groups [37] was selected to ensure correct orientation of antibody (Scheme 2b).
Alternatively, activating the carboxylic acid (Fc region) of the antibody and attaching them onto the amine-terminated support surface would improve the antibody orientation [39].
Additionally, our recent work already demonstrated that improving and optimising the amine surface coverage onto the support system (carbon, graphene, etc) would improve the sensor performance by improving the antibody immobilisation via carbodiimide reaction [17,40,41,42]. In addition, the utilisation of carboxylic acid groups of antibodies for binding also prevents the potential loss of biological activity of the antibody fragment.
Our primary motivation for this work was to establish a clear understanding of the influence of diazonium functionalisation efficiency over the biosensor performance. Our interest lies in developing electrochemical biomedical sensors made by reduction of electrode bound nitrophenol groups to amines, followed by reaction of these amine groups with sensor molecules, such as antibody receptors. A key factor in determining sensor sensitivity is the surface coverage of receptor molecules, and this, in turn, depends on the surface coverage of the intermediate aminophenyl groups. Despite extensive research on diazotisation of carbon-based substrates, previous studies have not quantified the electrochemical conversion of 4-nitrophenyl groups to aminophenyl groups [33,34]. This research aimed to combat exactly these problems; we provided not only the optimum conditions but also a rapid technique that is effective. Our focus was to report the quantification of the electrochemical conversion of 4-nitrophenyl groups to aminophenyl groups, which, to the best of our knowledge, has never been reported. The effect of the number of CV scans was also discussed in detail. Furthermore, in order to prove this argument, we attached the antibodies on diazotised surfaces of all different scan rates.
In this work, we explored this issue by quantifying the amine group coverage via measurement of electron transfer during electrochemical addition of ferrocene carboxylic acid (FCA) to aminophenyl groups on glassy carbon and highly ordered pyrolytic graphite (HOPG) electrodes. Here, we also investigated the effect of nitro to amino CV reduction scans by controlling the number of scans. The efficiency of our experimental parameter optimisation was studied by developing biosensors prepared by coupling between the electrode bound phenylamino and a carboxyl-terminated anti-beta amyloid antibody specific to Aβ (1-42) peptide, a potential marker for Alzheimer’s disease. Here, Aβ (1-42) was used as a model biomarker to illustrate the successful diazotisation and validate our claim of achieving diazotisation via optimisation of the experimental parameters. Aβ (1-42) is a promising biomarker for Alzheimer’s disease detection, and our group has also previously worked with it and as such made an active decision to use it as the biomarker for supporting better amine coverage in this work.

2. Materials and Methods

Materials 4-nitrobenzenediazonium tetrafluoroborate 97% (4-NPD), tetrabutylammonium tetrafluoroborate 99% (BU4NBF4), 1-ethyl-3-(3-(dimethylamino)-propyl) carbodiimide hydrochloride (EDC), N-hydroxysuccinimide (NHS), ferrocene carboxylic acid (FCA), potassium chloride, acetonitrile (ACN) and phosphate-buffered saline tablets (PBS; pH 7.4) were all purchased from Sigma Aldrich (St. Louis, MO, USA) and used as received. All reagents were of analytical grade, and the deionised water was used for the cleaning of the glassy carbon electrodes. Highly ordered pyrolytic graphite (HOPG) was purchased from MikroMasc (Wetzlar, Germany) with the following specifications: grade ZYA, mosaic spread with the value of 0.4° ± 0.1°, double-sided and with thickness 1 mm and the size of 10 × 10 mm2.
Biomarker amyloid-beta peptides Aβ ((1-42) (ab120301)) and anti-beta amyloid antibody (ab224275), specific to Aβ (1-42) peptide Aβ, were purchased from Abcam (Cambridge, UK).
Amyloid-beta (1-42) was supplied in the lyophilised form by Abcam (Cambridge, UK). It was then dissolved in 10 mM sodium hydroxide, followed by gentle Vortex for less than 1 min to make a homogeneous solution. The peptide stock solution was then aliquoted and stored at −20 °C. Under these highly alkaline conditions, the peptide is fully dissolved and exists only as monomers [43].

2.1. Electrochemical Measurements

Electrochemical experiments were carried out on an Autolab electrochemical workstation (PGSTAT 302N Metrohm, Utrecht, The Netherlands) at room temperature using a conventional three-electrode system: a bare or modified glassy carbon electrode (GCE) (MF-2012, 3 mm diameter, BASI, West Lafayette, IN, USA) was used as the working electrode, with a platinum wire counter electrode and Ag/AgCl (3 M NaCl, + 0.197 V vs Standard Hydrogen Electrode (SHE)) reference electrode, and a scan rate of 50 mV/s. The GCEs were polished stepwise with aqueous alumina slurries of 0.3 and 0.05 μm particle size using micro-cloth, followed by rinsing thoroughly with isopropyl alcohol (IPA) and then with deionised water for 30 min.
Electrochemical grafting of the diazonium salt was performed using 0.1 M BU4NBF4 electrolyte in acetonitrile. Typically, blank cyclic voltammetry (CV) was recorded using a freshly cleaned GCE in the electrolyte, following which, the active diazonium compound (5 mM) was added to the electrolyte, and further voltammograms were recorded for 5 cycles.
Subsequent electrochemical reduction of the nitro group (NO2) to an amino group (NH2) was carried out in 0.1 M KCl in water:ethanol (9:1) electrolyte, using reduction cyclic scanning at 50 mV/s scan rate between −1.2 V and + 1 V vs Ag/AgCl.
Functionalising the amine groups with FCA was carried out as follows: 5 mM EDC/NHS (ratio 1:1) solution was added to 250 µM FCA solution, followed by 40 min of incubation at room temperature. The resultant solution was drop-cast onto the freshly prepared amine-terminated GC and left for 10 min before scanning between −0.3 V and 0.3 V at 5 mV/s in fresh PBS solution, which acted as the electrolyte.
Diazonium functionalisation to prepare a sensor incorporating a carboxyl terminated anti-beta amyloid antibody specific to Aβ (1-42) peptide was carried out using an EDC/NHS protocol [3,22,30]. The Aβ antibody was “activated” in 5 mM EDC/NHS solution for 40 min. This was followed by drop-casting the solution over the electrode surface and incubating for 30 min at 4 °C. The electrode was then rinsed thoroughly with deionised water and dried with N2. After that, amyloid-beta (Aβ (1-42)) peptides were added to the electrode surface ranging from 0 ng/mL to 200 ng/mL at 4 °C, each for an incubation time of 20 min. Differential pulse voltammograms (DPV), obtained by sweeping the potential from −0.4 V to +0.3 V with a step potential of 5 mV, an amplitude of 25 mV and interval time of 0.5 s, were used in examining the attachment of antigens to antibody.

2.2. Characterisation Techniques

The layers that form the electrodes were characterised to determine their thickness and topography using different techniques to check the quality of the functionalisation of the layers. These techniques included atomic force microscopy (AFM) and scanning electron microscopy (SEM). These were applied to the different stages of functionalisation.
Atomic force microscopy (AFM) was carried out using a JPK NanoWizard II (Berlin, Germany), in intermittent contact mode with tip resonant frequency, spring constant and nominal radius of 320 kHz, 40 N/m and 8 nm, respectively.
Scanning electron microscopy (SEM; Ultra-High-Resolution FE-SEM S-4800, Hitachi, Tokyo, Japan) was carried out at 10 kV acceleration voltage and a 20 mA emission current. The magnification was approximately × 3 k and working distance 10 mm.

3. Results and Discussion

3.1. Surface Functionalisation of Glassy Carbon via Diazotisation

Figure 1 shows the cyclic voltammetry response of GCEs before and after the addition of diazonium to the electrolyte. As anticipated, no redox processes were noticed for the blank scan (black line), and with the diazonium salt present, a broad irreversible peak (orange curve) was observed at 0.2 V (vs Ag/AgCl), which corresponded to electron transfer associated with the cleavage of dinitrogen from the diazonium salt. This peak completely disappeared in subsequent scans, indicating no further reduction, presumably due to saturation of the available GCE surface with nitrophenyl groups (olive green curve). This observation was consistent with previous reports [44].

3.2. Electrochemical Reduction of 4-Nitrophenyl Layers on Glassy Carbon

Electrochemical reduction of the nitro group (NO2) to an amino group (NH2) reduction occurs in three steps, as shown in Scheme 3 [19].
Figure 2 shows the cyclic voltammetry response of 4-nitrophenyl-modified GCEs upon subsequent reduction cycles. A strong irreversible reduction peak was observed at −0.9 V at the first scan corresponding to the formation of the hydroxylamine (PhNHOH). In the subsequent scans, a pair of reversible redox peaks disappeared at a half-wave potential of approximately (−0.45 V). This reversible electrochemistry was attributed to the formation of the hydroxy aminophenyl on the GCE surface. The CV data indicated that the reduction of Ar-NO2 was irreversible.
It was also observed from Figure 2 that three CV scans were sufficient for aminophenyl conversion, as overlap in the reduction peaks indicated that no further reduction occurred on the electrode surface after three scans (Figure 2 inset).

3.3. Quantification of Surface Amine Groups

The surface coverage of amines on the modified electrode was quantified by functionalising the amine groups with FCA, using a standard N-(3-dimethylaminopropyl)-N’-ethyl carbodiimide EDC/NHS coupling reaction (Scheme 4), as follows.
Carboxyl-to-amine crosslinking used the carbodiimide EDC and sulfo-NHS. Addition of NHS or Sulfo-NHS to EDC reactions increases efficiency and enables molecules terminated with the carboxylic acid, such as FCA, to be activated for storage and later use. NHS-activation is the basis for synthesising amine-reactive labelling reagents and crosslinking compounds. This mechanism is very well known and reported [44].
Figure 3 shows the CV measurements performed in order to confirm the attachment of FCA to surface-bound amino phenyl groups.
The surface coverage of FCA was estimated using Equation (1):
Γ = Q/nFA
where Γ is the surface coverage of FCA (mol/cm2), A is the surface area of the electrode (cm2), n represents the number of electrons involved in the reaction, F is the Faraday constant (C/mol), Q is the total amount of charge calculated from the integration of the reduction peak recorded using cyclic voltammetry. To calculate the surface coverage of the working electrode, the area under the reduction part of the CV curve can be integrated.
As anticipated, our electrochemical measurements showed no FCA attachment to measurements conducted on the first control of blank GCE due to the lack of amine surface groups on pristine GCE (first control).
It was expected to observe strong FCA binding to the GCE-PhNO2 (reduction scan-1) as the current literature reports that the large irreversible reduction peak in the first scan, towards the negative potential, is due to the reduction of p-nitrophenyl to p-aminophenyl. However, in striking contrast, the scan, where GCE-PhNO2 (reduction scan-1) underwent only a single reduction cycle in KCl, showed no redox peaks upon FCA functionalisation. However, FCA binding was observed for the electrodes under consecutive scans (reduction scan 2–5 in KCl). The surface coverage of FCA at reduction scan-2 was found to be 14.7 pmol/cm2. This might be due to the fact that a single reduction of GCE-PhNO2 is not sufficient to generate amine surface moieties, instead produces only an intermediate GCE-PhNHOH moiety, which further needs additional scans to generate amine groups [45].
It was also found that the surface coverage of FCA varied strongly, depending on the number of reduction scans (as shown in Figure 3). It was found that the maximum degree of surface coverage was achieved for the sample prepared at reduction scan-3 (21.7 pmol/cm2), whereas any further increase in scan reduced the FCA coverage. The decrease in the surface coverage of FCA in scans 4 and 5 could be attributed to the possible loss of amine groups due to the oxidation. Thus, it is significant to achieve an optimal number of reduction scans (in our case, three scans) to achieve the maximum generation of amino phenyl, beyond which, there is a possibility of losing the generated amines via an oxidation process.

3.4. Electrochemical Sensing via Analysis of the Electrodes

In order to confirm this behaviour in a practical sensor, we used diazonium functionalisation to prepare a sensor, incorporating a carboxyl-terminated anti-beta amyloid antibody specific to Aβ (1-42) peptide, a potential marker for Alzheimer’s disease. In this case, the sensor response is a reduction in current in differential pulse voltammetry (DPV) as the bound peptide acts as a barrier to electron transfer at the electrode surface [46,47].
Figure 4 shows the percentage current reduction (%IR) plotted against the log of analyte concentrations. The sensing results indicated that electrode made from an amino substrate prepared using reduction scan-3 showed significantly higher sensitivity (slope: 5.07 and R2 = 0.98) than those prepared using scan-5 (slope: 2.85 and R2 = 0.65). The regression equation had a logarithmic linear relation with Aβ (1-42) concentration (0 ng/mL to 200 ng/mL), with R² = 0.98 as the correlation coefficient.
It is worth mentioning that the control electrodes (GCE, reduction scan-0 and reduction scan-2, Figure 5a,b) showed weak to no significant change in signal upon exposure to Aβ (1-42) peptide. This confirmed that the experimental conditions of diazotisation greatly influenced the sensor performance, and the nitrophenyl to amino phenyl conversion occurred at the reduction scan-2, instead of reduction scan-1.
The pattern of results obtained from these reduction cycles with antibodies matching those conducted with FCA attachment and utilising FCA is a novel, fast and cheap way of gauging the potential sensitivity of a sensor platform made by any particular process, without the need for complete manufacture of the sensor itself.

3.5. Characterisation of Surface Morphology Electrode

The effect of surface diazotisation on surface morphology was investigated using AFM on the HOPG electrode. The 40 × 40 µm2 AFM scans were conducted in intermittent contact mode. The data were levelled using a linear background, and a high pass filter was used to remove large scale undulations in the HOPG. The roughness and morphology of the functionalised substrate are shown in Figure 6.
The surface roughness appeared similar between the samples after one, three and five scans, with graphite step edges still visible after five cycles. The root mean square (RMS) roughness was generally higher on the blank samples (~5 nm) when compared with the functionalised samples (1–2 nm). However, no clear difference was observed in roughness values between the functionalised samples, with similar topography apparent in the AFM images (Figure 6b–d).
Scanning electron microscopy (SEM) of the HOPG surface revealed a similar suppression of surface features following initial functionalisation with diazotisation method (Figure 7a,b), in agreement with AFM.
However, a reduction in visible step edges in the underlying HOPG with an increasing number of cycles was also observed (Figure 7b–d). This could be explained by the suppression of low energy secondary electron contrast at step edges due to the presence of an overlayer or thin-film [48].
It is possible that AFM in intermittent contact mode is probing some underlying topography through the functional layer, explaining this discrepancy in observed surface morphology.

4. Conclusions

Despite diazotisation being a well-researched topic, there have been no previous reports concerning the quantification of surface coverage of aminophenyl groups, following the conversion of 4-nitrophenyl films (deposited via electrochemical methods), or the optimal conditions required for this reaction. Understanding the extent of conversion of the nitro moiety on different electrode surfaces provides useful information for electroanalytical chemistry researchers in their design of surfaces, and electrochemical procedures, for biosensor molecule immobilisation.
Ferrocene carboxylic acid was introduced as a rapid and cheap assay to assess surface coverage of amino-phenyl groups on electrodes. The number of electrons transferred during the attachment of ferrocene carboxylic acid indicated an available amine coverage of only ca 1/40th, which might be expected from the number of electrons used in the initial diazotisation process, i.e., 2.2 × l0−11 mol/cm2 compared to 8.02 ± 0.2 × l0−10 (mol/cm2). Furthermore, the available amine coverage was critically dependent upon the number of CV cycles used in the reduction, and thus the procedures used in this step influenced the sensitivity of any subsequent sensor. The applicability of these ideas was demonstrated via developing a sensor, incorporating a carboxyl-terminated anti-beta amyloid antibody specific to Aβ (1-42) peptide, a potential marker for Alzheimer’s disease. At optimum amine coverage, the sensitivity of the differential pulse voltammetry sensor was in the range 0–200 ng/mL, with a slope of 5.07 µA/ng·mL−1 and R2 = 0.98. Our work demonstrated an electrochemical-based low-cost surface quantification technique, which could be utilised in combination with other sensor parameters’ optimisation to develop commercially viable, high-performance, carbon-based electrochemical biosensors. Future developments of this work will need to focus on exploring and optimising the sensitivity and selectivity of sensors and using a range of different biomarkers.

Author Contributions

For Conceptualisation: Z.T.; Methodology: Z.T., H.Y.A.; Validation: Z.T., H.Y.A.; Formal Analysis: Z.T., H.Y.A.; Investigation: Z.T., H.Y.A., J.E.E.; Resources: Z.T., O.J.G.; Writing—Original Draft: Z.T., H.Y.A.; Writing—Review and Editing: Z.T., H.Y.A., A.D.; Visualisation: Z.T., H.Y.A.; Supervision: Z.T., O.J.G.; Project Administration: Z.T.; Funding Acquisition: Z.T., H.Y.A., O.J.G. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the Welsh Government and European Commission under European Regional Development Funds (ERDF) through Ser Cymru II Fellowships (Project Number: 80761-su-100); and the European Union’s Horizon 2020 Marie Skłodowska-Curie Actions-ITN-ETN BBDiag project (Grant Number: 721281); and Engineering and Physical Sciences Research Council (EPSRC) funding (Grant Number: EP/M006301/1).

Data Availability Statement

No new data were created or analyzed in this study. Data sharing is not applicable to this article.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Asal, M.; Özen, Ö.; Şahinler, M.; Baysal, H.T.; Polatoğlu, İ. An overview of biomolecules, immobilization methods and support materials of biosensors. Sens. Rev. 2019, 39, 377–386. [Google Scholar] [CrossRef]
  2. Sonawane, M.D.; Nimse, S.B. Surface modification chemistries of materials used in diagnostic platforms with biomolecules. J. Chem. 2016, 2016, 1–20. [Google Scholar] [CrossRef] [Green Version]
  3. Booth, M.A.; Kannappan, K.; Hosseini, A.; Partridge, A. In-depth electrochemical investigation of surface attachment chemistry via carbodiimide coupling. Langmuir 2015, 31, 8033–8041. [Google Scholar] [CrossRef]
  4. Revenga-Parra, M.; Villa-Manso, M.A.; Briones, M.; Mateo-Martí, E.; Martínez-Periñán, E.; Lorenzo, E.; Pariente, F. Bioelectrocatalytic platforms based on chemically modified nanodiamonds by diazonium salt chemistry. Electrochim. Acta 2020, 357, 136876. [Google Scholar] [CrossRef]
  5. Pichereau, L.; López, I.; Cesbron, M.; Dabos-Seignon, S.; Gautier, C.; Breton, T. Controlled diazonium electrografting driven by overpotential reduction: A general strategy to prepare ultrathin layers. Chem. Commun. 2019, 55, 455–457. [Google Scholar] [CrossRef]
  6. Cesbron, M.; Dabos-Seignon, S.; Christelle, G.; Breton, T. Enhanced electrocatalytic activity on TEMPO mixed film grafted by diazonium reduction. Electrochim. Acta 2020, 345, 136190. [Google Scholar] [CrossRef]
  7. Delamar, M.; Hitmi, R.; Pinson, J.; Saveant, J.M. Covalent modification of carbon surfaces by grafting of functionalized aryl radicals produced from electrochemical reduction of diazonium salts. J. Am. Chem. Soc. 1992, 114, 5883–5884. [Google Scholar] [CrossRef]
  8. Downard, A.J. Electrochemically assisted covalent modification of carbon electrodes. Electroanalysis 2000, 12, 1085–1096. [Google Scholar] [CrossRef]
  9. Pinson, J.; Podvorica, F. Attachment of organic layers to conductive or semiconductive surfaces by reduction of diazonium salts. Chem. Soc. Rev. 2005, 34, 429–439. [Google Scholar] [CrossRef]
  10. McCreery, R.L. Advanced carbon electrode materials for molecular electrochemistry. Chem. Rev. 2008, 108, 2646–2687. [Google Scholar] [CrossRef]
  11. Picot, M.; Lapinsonnière, L.; Rothballer, M.; Barrière, F. Graphite anode surface modification with controlled reduction of specific aryl diazonium salts for improved microbial fuel cells power output. Biosens. Bioelectron. 2011, 28, 181–188. [Google Scholar] [CrossRef]
  12. Leroux, Y.R.; Hui, F.; Noël, J.-M.; Roux, C.; Downard, A.J.; Hapiot, P. Design of robust binary film onto carbon surface using diazonium electrochemistry. Langmuir 2011, 27, 11222–11228. [Google Scholar] [CrossRef]
  13. Hetemi, D.; Combellas, C.; Kanoufi, F.; Pinson, J.; Podvorica, F.I. Surface modification by electrochemical reduction of alkyldiazonium salts. Electrochem. Commun. 2016, 68, 5–9. [Google Scholar] [CrossRef]
  14. Zen, F.; Angione, M.D.; Behan, J.A.; Cullen, R.J.; Duff, T.; Vasconcelos, J.M.; Scanlan, E.M.; Colavita, P.E. Modulation of protein fouling and interfacial properties at carbon surfaces via immobilization of glycans using aryldiazonium chemistry. Sci. Rep. 2016, 6, 24840. [Google Scholar] [CrossRef] [Green Version]
  15. Guy, O.J.; Burwell, G.; Tehrani, Z.; Castaing, A.; Walker, K.A.; Doak, S.H. Graphene nano-biosensors for detection of cancer risk. Mater. Sci. Forum 2012, 711, 246–252. [Google Scholar] [CrossRef]
  16. Guy, O.J.; Castaing, A.; Tehrani, Z.; Doak, S.H. Fabrication of ultrasensitive graphene nanobiosensors. Proc. IEEE Sens. 2010, 711, 907–912. [Google Scholar] [CrossRef]
  17. Tehrani, Z.; Burwell, G.; Azmi, M.A.M.; Castaing, A.; Rickman, R.H.; Almarashi, J.; Dunstan, P.R.; Beigi, A.M.; Doak, S.H.; Guy, O.J. Generic epitaxial graphene biosensors for ultrasensitive detection of cancer risk biomarker. 2D Mater. 2014, 1, 025004. [Google Scholar] [CrossRef]
  18. Tehrani, Z.; Thomas, D.J.; Guy, O.J. Electrochemical biofunctionalization of highly oriented pyrolytic graphite for immunosensor applications. e-J. Surf. Sci. Nanotechnol. 2016, 14, 193–197. [Google Scholar] [CrossRef] [Green Version]
  19. Gui, A.L.; Liu, G.; Chockalingam, M.; Le Saux, G.; Luais, E.; Harper, J.B.; Gooding, J.J. A Comparative study of electrochemical reduction of 4-nitrophenyl covalently grafted on gold and carbon. Electroanalysis 2010, 22, 1824–1830. [Google Scholar] [CrossRef]
  20. Mahmoud, A.M.; Bergren, A.J.; Pekas, N.; McCreery, R.L. Towards integrated molecular electronic devices: Characterization of molecular layer integrity during fabrication processes. Adv. Funct. Mater. 2011, 21, 2273–2281. [Google Scholar] [CrossRef]
  21. Lud, S.Q.; Steenackers, M.; Jordan, R.; Bruno, P.; Gruen, D.M.; Feulner, P.; Garrido, J.A.; Stutzmann, M. Chemical grafting of biphenyl self-assembled monolayers on ultrananocrystalline diamond. J. Am. Chem. Soc. 2006, 128, 16884–16891. [Google Scholar] [CrossRef]
  22. Bekyarova, E.; Itkis, M.E.; Ramesh, P.; Berger, C.; Sprinkle, M.; De Heer, W.A.; Haddon, R.C. Chemical modification of epitaxial graphene: Spontaneous grafting of aryl groups. J. Am. Chem. Soc. 2009, 131, 1336–1337. [Google Scholar] [CrossRef] [PubMed]
  23. Zhong, Y.L.; Midya, A.; Ng, Z.; Chen, Z.-K.; Daenen, M.; Nesládek, M.; Loh, K.P. Diamond-based molecular platform for photoelectrochemistry. J. Am. Chem. Soc. 2008, 130, 17218–17219. [Google Scholar] [CrossRef]
  24. Abrahamson, J.T.; Song, C.; Hu, J.H.; Forman, J.M.; Mahajan, S.G.; Nair, N.; Choi, W.; Lee, E.-J.; Strano, M.S. Synthesis and energy release of nitrobenzene-functionalized single-walled carbon nanotubes. Chem. Mater. 2011, 23, 4557–4562. [Google Scholar] [CrossRef]
  25. Atmane, Y.A.; Sicard, L.; Lamouri, A.; Pinson, J.; Sicard, M.; Masson, C.; Nowak, S.; DeCorse, P.; Piquemal, J.-Y.; Galtayries, A.; et al. Functionalization of aluminum nanoparticles using a combination of aryl diazonium salt chemistry and iniferter method. J. Phys. Chem. C 2013, 117, 26000–26006. [Google Scholar] [CrossRef]
  26. Nguyen, V.Q.; Ai, Y.; Martin, P.; Lacroix, J.-C. Plasmon-induced nanolocalized reduction of diazonium salts. ACS Omega 2017, 2, 1947–1955. [Google Scholar] [CrossRef] [PubMed]
  27. Ahmad, R.; Boubekeur-Lecaque, L.; Nguyen, M.; Lau-Truong, S.; Lamouri, A.; DeCorse, P.; Galtayries, A.; Pinson, J.; Felidj, N.; Mangeney, C. Tailoring the surface chemistry of gold nanorods through Au–C/Ag–C covalent bonds using aryl diazonium salts. J. Phys. Chem. C 2014, 118, 19098–19105. [Google Scholar] [CrossRef]
  28. Griffete, N.; Lamouri, A.; Herbst, F.; Félidj, N.; Ammar, S.; Mangeney, C. Synthesis of highly soluble polymer-coated magnetic nanoparticles using a combination of diazonium salt chemistry and the iniferter method. RSC Adv. 2011, 2, 826–830. [Google Scholar] [CrossRef]
  29. Griffete, N.; Herbst, F.; Pinson, J.; Ammar, S.; Mangeney, C. Preparation of water-soluble magnetic nanocrystals using aryl diazonium salt chemistry. J. Am. Chem. Soc. 2011, 133, 1646–1649. [Google Scholar] [CrossRef]
  30. Maldonado, S.; Smith, T.J.; Williams, R.D.; Morin, S.; Barton, E.; Stevenson, K.J. Surface modification of indium tin oxide via electrochemical reduction of aryldiazonium cations. Langmuir 2006, 22, 2884–2891. [Google Scholar] [CrossRef]
  31. Gam-Derouich, S.; Pinson, J.; DeCorse, P.; Luo, Y.; Herbaut, R.; Royon, L.; Mangeney, C. Diazonium salt chemistry for the design of nano-textured anti-icing surfaces. Chem. Commun. 2018, 54, 8983–8986. [Google Scholar] [CrossRef] [PubMed]
  32. Liu, Y.; McCreery, R.L. Reactions of organic monolayers on carbon surfaces observed with unenhanced raman spectroscopy. J. Am. Chem. Soc. 1995, 117, 11254–11259. [Google Scholar] [CrossRef]
  33. Saby, C.; Ortiz, B.; Champagne, G.Y.; Bélanger, D. Electrochemical modification of glassy carbon electrode using aromatic diazonium salts. 1. Blocking effect of 4-nitrophenyl and 4-carboxyphenyl groups. Langmuir 1997, 13, 6805–6813. [Google Scholar] [CrossRef]
  34. Ortiz, B.; Saby, C.; Champagne, G.; Bélanger, D. Electrochemical modification of a carbon electrode using aromatic diazonium salts. 2. Electrochemistry of 4-nitrophenyl modified glassy carbon electrodes in aqueous media. J. Electroanal. Chem. 1998, 455, 75–81. [Google Scholar] [CrossRef]
  35. Downard, A.J. Potential-dependence of self-limited films formed by reduction of aryldiazonium salts at glassy carbon electrodes. Langmuir 2000, 16, 9680–9682. [Google Scholar] [CrossRef]
  36. Shin, D.; Tokuda, N.; Rezek, B.; Nebel, C. Periodically arranged benzene-linker molecules on boron-doped single-crystalline diamond films for DNA sensing. Electrochem. Commun. 2006, 8, 844–850. [Google Scholar] [CrossRef]
  37. Welch, N.G.; Scoble, J.A.; Muir, B.W.; Pigram, P.J. Orientation and characterization of immobilized antibodies for improved immunoassays (Review). Biointerphases 2017, 12, 02D301. [Google Scholar] [CrossRef] [Green Version]
  38. Yen, Y.-K.; Huang, C.-Y.; Chen, C.-H.; Hung, C.-M.; Wu, K.; Lee, C.-K.; Chang, J.-S.; Lin, S.; Huang, L.-S. A novel, electrically protein-manipulated microcantilever biosensor for enhancement of capture antibody immobilization. Sens. Actuators B Chem. 2009, 141, 498–505. [Google Scholar] [CrossRef]
  39. Ferreira, N.S.; Sales, M.G.F. Disposable immunosensor using a simple method for oriented antibody immobilization for label-free real-time detection of an oxidative stress biomarker implicated in cancer diseases. Biosens. Bioelectron. 2014, 53, 193–199. [Google Scholar] [CrossRef] [Green Version]
  40. Devadoss, A.; Forsyth, R.; Bigham, R.; Abbasi, H.; Ali, M.M.; Tehrani, Z.; Liu, Y.; Guy, O.J. Ultrathin functional polymer modified graphene for enhanced enzymatic electrochemical sensing. Biosensors 2019, 9, 16. [Google Scholar] [CrossRef] [Green Version]
  41. Walters, F.; Ali, M.M.; Burwell, G.; Rozhko, S.; Tehrani, Z.; Daghigh Ahmadi, E.; Evans, J.E.; Abbasi, H.; Bigham, R.; Mitchell, J.J.; et al. A facile method for the non-covalent amine functionalization of carbon-based surfaces for use in biosensor development. Nanomaterials 2020, 10, 1808. [Google Scholar] [CrossRef] [PubMed]
  42. Azmi, M.M.; Tehrani, Z.; Lewis, R.; Walker, K.-A.; Jones, D.; Daniels, D.; Doak, S.; Guy, O. Highly sensitive covalently functionalised integrated silicon nanowire biosensor devices for detection of cancer risk biomarker. Biosens. Bioelectron. 2014, 52, 216–224. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  43. House, E.; Collingwood, J.; Khan, A.; Korchazkina, O.; Berthon, G.; Exley, C. Aluminium, iron, zinc and copper influence the in vitro formation of amyloid fibrils of Aβ42 in a manner which may have consequences for metal chelation therapy in Alzheimer’s disease. J. Alzheimer’s Dis. 2004, 6, 291–301. [Google Scholar] [CrossRef]
  44. Thermo fisher Scientific Website. Available online: https://www.thermofisher.com/order/catalog/product/77149#/7714917 (accessed on 15 January 2021).
  45. Wang, W.; Ge, L.; Sun, X.; Hou, T.; Li, F. Graphene-assisted label-free homogeneous electrochemical biosensing strategy based on aptamer-switched bidirectional DNA polymerization. ACS Appl. Mater. Interfaces. 2015, 7, 28566–28575. [Google Scholar] [CrossRef]
  46. Wu, C.-C.; Ku, B.-C.; Ko, C.-H.; Chiu, C.-C.; Wang, G.-J.; Yang, Y.-H.; Wu, S.-J. Electrochemical impedance spectroscopy analysis of A-beta (1-42) peptide using a nanostructured biochip. Electrochim. Acta 2014, 134, 249–257. [Google Scholar] [CrossRef]
  47. Sethi, J.; Van Bulck, M.; Suhail, A.; Safarzadeh, M.; Perez-Castillo, A.; Pan, G. A label-free biosensor based on graphene and reduced graphene oxide dual-layer for electrochemical determination of beta-amyloid biomarkers. Microchim. Acta 2020, 187, 1–10. [Google Scholar] [CrossRef] [Green Version]
  48. Shihommatsu, K.; Takahashi, J.; Momiuchi, Y.; Hoshi, Y.; Kato, H.; Homma, Y. Formation mechanism of secondary electron contrast of graphene layers on a metal substrate. ACS Omega 2017, 2, 7831–7836. [Google Scholar] [CrossRef]
Nanomaterials 11 00416 sch001 550
Scheme 1. Electrografting of 4-nitrobenzenediazonium tetrafluoroborate salt.
Scheme 1. Electrografting of 4-nitrobenzenediazonium tetrafluoroborate salt.
Nanomaterials 11 00416 sch001
Nanomaterials 11 00416 sch002 550
Scheme 2. (a) Antibody important chemical species for targeting, (b) EDC/NHS coupling of the antibody carboxyl group to surface amine group.
Scheme 2. (a) Antibody important chemical species for targeting, (b) EDC/NHS coupling of the antibody carboxyl group to surface amine group.
Nanomaterials 11 00416 sch002
Nanomaterials 11 00416 g001 550
Figure 1. Cyclic voltammograms (50 mV/s) of glassy carbon electrode (GCE) in Bu4NBF4 in acetonitrile 0.1 M before (black curve) and after the addition of diazonium (DIZ) (orange curve); after repeated voltammetry cycles (five scans, fifth scan olive green curve), there was no further reduction. The experiment was repeated four times.
Figure 1. Cyclic voltammograms (50 mV/s) of glassy carbon electrode (GCE) in Bu4NBF4 in acetonitrile 0.1 M before (black curve) and after the addition of diazonium (DIZ) (orange curve); after repeated voltammetry cycles (five scans, fifth scan olive green curve), there was no further reduction. The experiment was repeated four times.
Nanomaterials 11 00416 g001
Nanomaterials 11 00416 sch003 550
Scheme 3. Electrochemical reduction pathway of the nitro group (NO2) to an amino group (NH2) in an aqueous electrolyte.
Scheme 3. Electrochemical reduction pathway of the nitro group (NO2) to an amino group (NH2) in an aqueous electrolyte.
Nanomaterials 11 00416 sch003
Nanomaterials 11 00416 g002 550
Figure 2. Cyclic voltammograms (50 mV/s) of the reduction of surface-grafted 4-nitrophenyl on GCE in 0.1 M KCl in water:ethanol (9:1) electrolyte: (a) black curve—one scan; (b) green curve—five scans. The inset figure shows the change of peak current with the number of cycles at −0.2 V. The experiment was repeated four times.
Figure 2. Cyclic voltammograms (50 mV/s) of the reduction of surface-grafted 4-nitrophenyl on GCE in 0.1 M KCl in water:ethanol (9:1) electrolyte: (a) black curve—one scan; (b) green curve—five scans. The inset figure shows the change of peak current with the number of cycles at −0.2 V. The experiment was repeated four times.
Nanomaterials 11 00416 g002
Nanomaterials 11 00416 sch004 550
Scheme 4. Immobilisation mechanism of electrochemically active ferrocene carboxylic acid (FCA) on to an amine-modified glassy carbon electrode (GCE) through carbodiimide linking.
Scheme 4. Immobilisation mechanism of electrochemically active ferrocene carboxylic acid (FCA) on to an amine-modified glassy carbon electrode (GCE) through carbodiimide linking.
Nanomaterials 11 00416 sch004
Nanomaterials 11 00416 g003 550
Figure 3. (a) Cyclic voltammograms (5 mV/s) of ferrocene carboxylic acid (FCA)-functionalisation of amine-functionalised GCEs prepared using a different number of reduction scans (scans 1–5), in PBS electrolyte. (b) The bar chart shows the degree of FCA functionalisation, which is a maximum for the amine-functionalised GCE prepared using three scans.
Figure 3. (a) Cyclic voltammograms (5 mV/s) of ferrocene carboxylic acid (FCA)-functionalisation of amine-functionalised GCEs prepared using a different number of reduction scans (scans 1–5), in PBS electrolyte. (b) The bar chart shows the degree of FCA functionalisation, which is a maximum for the amine-functionalised GCE prepared using three scans.
Nanomaterials 11 00416 g003
Nanomaterials 11 00416 g004 550
Figure 4. Differential pulse voltammetry (DPV) results for Aβ (1-42) peptide sensors made from amino-functionalised substrates using different numbers of reduction scans. (a,b) three and five scans; (c,d) corresponding calibration curves of %IR (I (Ia – Io) / Io) %) (percentage current reduction) against log Aβ(1-42) concentrations.
Figure 4. Differential pulse voltammetry (DPV) results for Aβ (1-42) peptide sensors made from amino-functionalised substrates using different numbers of reduction scans. (a,b) three and five scans; (c,d) corresponding calibration curves of %IR (I (Ia – Io) / Io) %) (percentage current reduction) against log Aβ(1-42) concentrations.
Nanomaterials 11 00416 g004
Nanomaterials 11 00416 g005 550
Figure 5. Control experiments pulse voltammetry (DPV) results for Aβ (1-42) peptide sensors made from amino-functionalised substrates using different numbers of reduction scans carried out by (a) absence of amine and (b) negligible amount of amine are shown.
Figure 5. Control experiments pulse voltammetry (DPV) results for Aβ (1-42) peptide sensors made from amino-functionalised substrates using different numbers of reduction scans carried out by (a) absence of amine and (b) negligible amount of amine are shown.
Nanomaterials 11 00416 g005
Nanomaterials 11 00416 g006 550
Figure 6. Morphology of highly ordered pyrolytic graphite (HOPG) electrode with atomic force microscopy (AFM). (a) blank—before diazotisation, (b) after diazotisation—one scan, (c) after three scans, (d) after five scans.
Figure 6. Morphology of highly ordered pyrolytic graphite (HOPG) electrode with atomic force microscopy (AFM). (a) blank—before diazotisation, (b) after diazotisation—one scan, (c) after three scans, (d) after five scans.
Nanomaterials 11 00416 g006
Nanomaterials 11 00416 g007 550
Figure 7. Morphology of HOPG electrode with scanning electron microscopy (SEM). (a) blank—before diazotisation, (b) after diazotisation—one scan, (c) after three scans, (d) after five scans.
Figure 7. Morphology of HOPG electrode with scanning electron microscopy (SEM). (a) blank—before diazotisation, (b) after diazotisation—one scan, (c) after three scans, (d) after five scans.
Nanomaterials 11 00416 g007
Table
Table 1. 4-p-nitrophenyl surface coverage on carbon-based substrates.
Table 1. 4-p-nitrophenyl surface coverage on carbon-based substrates.
SubstratePotential (V)Surface Coverage (mol/cm2) × l0−10ConditionsRef.
GC 144 min electrolysis[3]
GC 6.5 ± 0.510 min electrolysis[32]
GC 184 min electrolysis[33]
GC 5.64 min electrolysis[34]
GC−1.0619 ± 1t = 10 and 100 min[35]
SD−1.171.3N2 purged Glove box[36]
EG 16.6RT, argon atm. 20 h[18]
GC−0.822Argon (oxygen free)[5]
GC−0.68.02 ± 0.2Air (atmospheric), 1 min, RTThis work
GC—glassy carbon; SD—single-crystalline diamond surface; EG—epitaxial graphene; RT—room temperature.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Tehrani, Z.; Abbasi, H.Y.; Devadoss, A.; Evans, J.E.; Guy, O.J. Assessing Surface Coverage of Aminophenyl Bonding Sites on Diazotised Glassy Carbon Electrodes for Optimised Electrochemical Biosensor Performance. Nanomaterials 2021, 11, 416. https://doi.org/10.3390/nano11020416

AMA Style

Tehrani Z, Abbasi HY, Devadoss A, Evans JE, Guy OJ. Assessing Surface Coverage of Aminophenyl Bonding Sites on Diazotised Glassy Carbon Electrodes for Optimised Electrochemical Biosensor Performance. Nanomaterials. 2021; 11(2):416. https://doi.org/10.3390/nano11020416

Chicago/Turabian Style

Tehrani, Zari, Hina Yaqub Abbasi, Anitha Devadoss, Jonathan Edward Evans, and Owen James Guy. 2021. "Assessing Surface Coverage of Aminophenyl Bonding Sites on Diazotised Glassy Carbon Electrodes for Optimised Electrochemical Biosensor Performance" Nanomaterials 11, no. 2: 416. https://doi.org/10.3390/nano11020416

APA Style

Tehrani, Z., Abbasi, H. Y., Devadoss, A., Evans, J. E., & Guy, O. J. (2021). Assessing Surface Coverage of Aminophenyl Bonding Sites on Diazotised Glassy Carbon Electrodes for Optimised Electrochemical Biosensor Performance. Nanomaterials, 11(2), 416. https://doi.org/10.3390/nano11020416

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop