Highly Sensitive Fluorescent Detection of Acetylcholine Based on the Enhanced Peroxidase-Like Activity of Histidine Coated Magnetic Nanoparticles
Previous Article in Journal
Gas Porosimetry by Gas Adsorption as an Efficient Tool for the Assessment of the Shaping Effect in Commercial Zeolites
Previous Article in Special Issue
Mixed Metal Oxide by Calcination of Layered Double Hydroxide: Parameters Affecting Specific Surface Area
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 11
Issue 5
10.3390/nano11051206
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Preparation of MgGa Layered Double Hydroxides and Possible Compositional Variation

by
Rattanawadee (Ploy) Wijitwongwan
1,
Soontaree (Grace) Intasa-ard
2 and
Makoto Ogawa
1,*
1
School of Energy Science and Engineering, Vidyasirimedhi Institute of Science and Technology (VISTEC), 555 Moo 1 Payupnai, Wangchan, Rayong 21210, Thailand
2
School of Molecular Science and Engineering, Vidyasirimedhi Institute of Science and Technology (VISTEC), 555 Moo 1 Payupnai, Wangchan, Rayong 21210, Thailand
*
Author to whom correspondence should be addressed.
Nanomaterials 2021, 11(5), 1206; https://doi.org/10.3390/nano11051206
Submission received: 26 March 2021 / Revised: 21 April 2021 / Accepted: 26 April 2021 / Published: 1 May 2021
(This article belongs to the Special Issue Natural and Engineered Clays: Two-Dimensional Nano-Building Blocks for Functional Nanomaterials)
Browse Figures
Versions Notes

Abstract

:
Layered double hydroxides (LDHs), shown as the general formula of [M2+1−xM3+x(OH)2]x+(An−)x/n∙yH2O, are useful for various applications such as anion exchangers/adsorbents, catalysts and catalysts’ supports, and drug/gene carriers due to their structural, compositional and morphological characteristics and their variation. The x value (M3+/(M2+ + M3+) ratio) in layered double hydroxides (LDHs), corresponding to the layer charge density, is one of the important parameters for controlling the properties of LDHs. The x values in commonly available LDHs are limited (0.2 < x < 0.3). In order to obtain LDHs with x < 0.2, Mg2+ Ga3+–LDHs with interlayer iodide were examined. The linear correlation between lattice parameter a and x value in the products with x of 0.06–0.24 was seen, suggesting the successful substitution of Mg2+ in the brucite-like sheet with Ga3+. Carbonate and dodecyl sulfate types MgGa–LDH were prepared by ion exchange with carbonate anion and reconstruction in aqueous solution of sodium dodecyl sulfate. The products with x of 0.06 were dispersed in water and hexanol better than those with x of 0.24 for MgGa–LDHs containing carbonate and dodecyl sulfate, respectively, suggesting effects of the lower layer charge density on the dispersion.

1. Introduction

Layered double hydroxides (LDHs) are a class of layered materials consisting of positively charged brucite-like sheets of metal hydroxide, where some of divalent metal cations (M2+) are substituted with trivalent metal cations (M3+) to give positive charge as [M2+1−xM3+x(OH)2]x+, and the charge compensating interlayer exchangeable anions (An−). The overall composition is expressed as the following general formula of [M2+1−xM3+x(OH)2]x+(An−)x/n∙yH2O. Owing to the versatile compositional variation of LDHs by the selection of metal ions in the hydroxide sheets and the interlayer anions, as well as their quantity (x values in [M2+1−xM3+x(OH)2]x+(An−)x/n), possible applications of LDHs have been reported such as polymer additives [1], drug/gene carriers [2,3], catalysts and catalysts’ supports [4,5] and anion exchangers/adsorbents [6,7,8]. Various synthetic methods have been examined and developed to prepare LDHs with desired composition and morphology [9,10].
One of the important parameters for controlling the properties of LDHs is the x value, which corresponds to the anion exchange capacity as well as the layer charge density. Preparation of LDHs with varied x values has been examined and the values of 0.2 < x < 0.3 are commonly approved for pure LDH phases. Apart from the range of 0.20–0.33, products are normally mixtures of LDHs and impurity phases [11,12]. These mixtures were obtained in the preparation of MgAl–LDHs [13,14,15,16,17,18,19], CaAl–LDHs [20], CaFe–LDHs [21], CoFe–LDHs [22,23], and NiAl–LDHs [24] with x < 0.20. It was thought that the limitation of the x value in pure LDHs was caused by a difference in the ionic radii of divalent and trivalent metal cations in framework of LDHs and a large distance between the adjacent interlayer anion in the interlayer space [12].
In order to obtain an LDH with x < 0.20, M2+ and M3+ shall have similar ionic radii to obtain the substitution of M2+ in the brucite-like sheet with M3+ without phase separation [11]. If compared with CaAl–LDHs, CaFe–LDHs, MgAl–LDHs, and NiAl–LDHs, which have been extensively investigated among available LDHs, MgGa–LDH is composed of similar size ions ((RM2+ − RM3+)/RM2+ = 47% for CaAl, 36% for CaFe, 26% for MgAl, 22% for NiAl, and 13% for MgGa) [25], while the preparation of MgGa–LDHs has been scarcely reported [26,27,28]. Besides the combination of M2+ and M3+ in the framework of LDHs, a large distance between the adjacent interlayer anions for LDHs with smaller x values may cause a collapse of the interlamellar domain, leading to the phase segregation [11]. Sasaki and his coworkers have proposed the template concept of interlayer cation to obtain lepidocrocite-type layered titanates (AyTi2−y/3Liy/3O4) with varied layer charge densities. The lepidocrocite-type layered titanates are one group of layered materials consisting of negatively charged titanate sheets and the charge-balancing interlayer cations. It has been reported that the lepidocrocite-type layered titanates with varied y values were obtained using different interlayer cations (A = Cs, Rb and K) and larger cation gave smaller y values [29].
In this study, iodide (0.21 nm) was used as the interlayer anion to avoid possible collapse of the layered structures of MgGa–LDHs due to the size of iodide. Once layered structures of the MgGa–LDHs with varied x formed by coprecipitation, carbonate and dodecyl sulfate forms of the MgGa–LDHs were prepared by the anion exchange with carbonate anion and the reconstruction in aqueous solution of sodium dodecyl sulfate after calcination. The effect of x value on the dispersions of the MgGa–LDHs in water for the carbonate form and in hexanol for the dodecyl sulfate form was examined by the observation of the sedimentation of the solids before and after the storage without agitation.

2. Materials and Methods

2.1. Materials

Magnesium nitrate hexahydrate (Mg(NO3)2 6H2O) was obtained from Sigma-Aldrich. Gallium nitrate hydrate (Ga(NO3)3 xH2O, 99.9%) was purchased from Alfa Aesar. Potassium iodide (KI) and sodium carbonate (Na2CO3) were supplied by Merck Millipore. Potassium hydroxide (KOH) was obtained from Carlo Erba Reagents. Brucite (Mg(OH)2) was obtained from Nacalai Tesque. Sodium dodecyl sulfate (C12H25NaO4S, >95.0%), hexanol (C6H14O, >98.0%), and benzene (C6H6, >99.5%) were supplied by Tokyo Chemical Industry Co., Ltd. These chemicals were used without further purification. Deionized water was obtained from a Milli-Q system (18.2 MΩ-cm, Merck Millipore, Darmstadt, Germany).

2.2. Synthesis of MgGa–LDHs Intercalated with Iodide

MgGa–LDHs with varied x were prepared by coprecipitation from aqueous solutions at controlled pH. The starting solution was prepared by dissolving 3.84 g of Mg(NO3)2 6H2O and 1.28 g of Ga(NO3)3 xH2O in 20 mL of deionized water for the preparation of the MgGa–LDH with x = 0.25. The starting solution was added dropwise to 40 mL of aqueous solution containing KI (the mole of KI is two times of the total nitrate from the metal salts) with vigorous stirring at 40 °C under nitrogen gas bubbling. The pH of the mixture was kept at 11–12 through the reaction by addition of 0.9 M aqueous solution of KOH as schematically shown in Scheme 1. The MgGa–LDHs were prepared using the same procedure by varying the x of 0.20, 0.13, 0.10, 0.09, and 0.08 in the starting solution. After the reaction, the precipitate was separated from the suspension by centrifugation at 10,000 rpm for 10 min and washed several times with deionized water. Half of the precipitate was dried at 80 °C for 24 h in oven and another half was freeze dried at −108 °C for 24 h. The products thus obtained by the coprecipitation followed by drying in oven and in freeze-dryer are designated as MgGa(I)-x and MgGa(I)-x_F, respectively, where x is the ratio of Ga3+/(Mg2+ + Ga3+) in the product as determined by ICP analysis.

2.3. Anion Exchange from Iodide to Carbonate in MgGa–LDHs

To the aqueous solution of Na2CO3 (1.27 g in 60 mL) 0.3 g of MgGa(I)-x_F (x = 0.24 and 0.06) was added and shaken for 3 h at room temperature. The solid was separated by the centrifugation at 10,000 rpm for 10 min, washed several times with deionized water, and freeze dried. The products are designated as MgGa(CO3)-x_F.

2.4. Reconstruction of MgGa–LDHs in Aqueous Solution of Sodium Dodecyl Sulfate

MgGa(CO3)-x_F (x = 0.24 and 0.06) (0.05 g) were calcined at 500 °C in air under ambient pressure (the heating rate of 10 °C/min), and then, allowed to react with the aqueous solution of sodium dodecyl sulfate (0.50 and 0.15 g of sodium dodecyl sulfate in 25 mL of deionized water for the samples with x of 0.24 and 0.06, respectively), then shaken for 10 h at room temperature. After the centrifugation at 10,000 rpm for 10 min, the solid was washed several times with deionized water, and freeze dried. The products are designated as MgGa(DS)-x_F.

2.5. Preparation of Suspension

In total, 10 mg of sample was added to 10 mL of deionized water or hexanol in a vial and sonicated (using Sonorex Digitec, Bandelin) for 2 min.

2.6. Characterization

Powder X-ray diffraction (XRD) patterns of the products were recorded at the scan speed of 5.47°/min with step size of 0.1002° using New D8 Advance instrument (Bruker, Billerica, Massachusetts, United States) equipped with Ni filtered Cu Kα radiation (λ = 0.15406 nm). Infrared spectra were obtained using Frontier Fourier transform infrared spectrophotometer (PerkinElmer, Inc., Waltham, MA, USA) by attenuated total reflection (ATR) mode with the resolution of 4.0 cm−1. In total, 32 scans were recorded for each sample. The composition was determined by ICP analysis (700 Series ICP-OES, Agilent Technologies, Santa Clara, CA, USA) after dissolving a weighed amount of sample with 1 M aqueous solution of HCl. The zeta potential was measured 3 times at pH of 10–10.5 without any additives using NanoPlus instrument (Micromeritics, Norcross, GA, USA). Prior to the measurement, 3.5 mg of sample was dispersed in 10 mL of deionized water under sonication for 30 min. Scanning electron micrographs (SEM) were obtained on a JSM-7610F field emission scanning electron microscope (JEOL, Ltd., Tokyo, Japan) without a coating.

3. Results and Discussion

The XRD patterns of MgGa(I)-x (x = 0.24, 0.18, 0.11, 0.10, 0.08, and 0.06) are shown in Figure 1A. For MgGa(I)-x (x = 0.24, 0.18), reflections characteristic to the hydrotalcite structure were seen and the segregation of brucite, which has been seen in the previous reports on the preparation of MgAl–LDHs [13,14,15,16,17,18,19], CoFe–LDHs [22,23], and NiAl–LDHs [24] with the x < 0.2, was not observed. The reflections with the d values of 0.82 and 0.41 nm were seen, which are consistent with the d(003) and d(006) spacings of the reported MgAl–LDHs containing iodide as the interlayer anion, respectively [30].
For the products with smaller x values (x = 0.11, 0.10, 0.08, and 0.06), the basal reflection of brucite was not observed. A reflection at 2θ of 20° and characteristic reflections of brucite at 2θ of 38, 50, 62° (JCPDS No. 07-0239) were seen together with the characteristic reflections of the hydrotalcite with the basal spacing of 0.82 nm (0.82/0.41 nm series) in Figure 1A(c–f). The difference in the XRD patterns suggested that the x value in MgGa(I)-x, where x value corresponds to the quantity of interlayer anion, affected the crystal structure of the products. The irregular stacking sequence of LDHs has been proposed on CoFe–LDH with 0.14 < x < 0.2 prepared by the post-synthetic oxidation [23]. A reflection revealing the occurrence of the interstratified structure was not observed as proposed by Sasaki [23], it was thought to be caused from the difference in the synthetic methods and the conditions, which affect crystallinity of the products. These observations suggested that MgGa(I)-x (x = 0.11, 0.10, 0.08, and 0.06) had an interstratified structure as proposed in Figure 2.
The lattice parameter a, which corresponds to the metal–metal distance in the hexagonal framework of brucite-like sheet [12], can be used to determine the composition from the correlation between the lattice parameter a and x value. The lattice parameter was smaller when the x values in the products were larger because of the substitution of larger Mg2+ ion (0.072 nm) by smaller Ga3+ ion (0.062 nm), where the radii of Mg2+ and Ga3+ with coordination number of 6 were reported by Shannon [25]. The correlation between a and x value is shown in Figure 1B, where linear correlation is seen, suggesting the successful substitution of Mg in the brucite-like sheet with Ga. The correlation was extrapolated to x = 0 to obtain a value of 0.3147 nm, which is the same as the lattice parameter a of brucite (0.3147 nm, JCPDS No. 07-0239). In the previous studies on MgAl–LDHs, NiAl–LDHs and NiFe–LDHs with x values of 0.1–0.3, the lattice parameter a extrapolated at x = 0 gave smaller values (0.3108 [14] and 0.3125 nm [18] for MgAl–LDHs and 0.3093 nm [31] for NiAl– and NiFe–LDHs) than those of Mg(OH)2 and Ni(OH)2, suggesting that some divalent cations in the brucite-like layer were not substituted with trivalent cations and precipitated separately as metal hydroxides. For the reported carbonate type MgGa–LDHs [32,33] and iodide type CoFe–LDHs [22,23] with x < 0.2, the products were mixtures of LDHs and brucite. In the present study, the MgGa–LDHs (x = 0.06–0.24) containing iodide were obtained without segregation of brucite, which were thought to be possible by the matching of ionic radii of Mg2+ and Ga3+ as well as by the template effect of iodide, which prevented the collapse of LDH.
Figure 3 shows the IR spectra of MgGa(I)-x (x = 0.24, 0.11, and 0.06). The absorption at around 3400–3600 cm−1 was attributed to the OH stretching vibration of hydroxyl groups hydrogen bonded with water molecules and interlayer anion. The absorption at 3697 cm−1, which was assigned to free hydroxyl groups in the brucite-like sheet [34], was seen for MgGa(I)-0.11 and MgGa(I)-0.06. These IR results supported the proposed stacking sequence of the products (x = 0.24, 0.11, and 0.06) (Figure 2).
The chemical composition of the products, which was determined by ICP analysis, is summarized in Table 1. The x values (M3+/(M2+ + M3+) ratios) of the products prepared at the pH of the mixture at around 11–12 were smaller than those in the starting solution. It was reported that the loss of Ga as soluble Ga complexes in the preparation of MgGa–LDH at the pH above 10 [28]. In addition to the chemical composition determined by ICP analysis, the distribution of Mg and Ga in the platy particles was examined by EDS elemental mapping (Figure 4) equipped with SEM, showing the uniform distribution of Mg and Ga through the products. The Ga/I ratios in the products were larger than 1.0, suggesting the possible coexistence of some anions with I- to compensate the positive charge by the MgGa substitution. As the coexisting interlayer anion, the presence of nitrate anion in the products was confirmed by the absorption due to NO stretching vibration at 1342 cm−1 (MgGa(I)-0.24) and 1350 cm−1 (MgGa(I)-0.11 and MgGa(I)-0.06) observed in the IR spectra (Figure 3).
The zeta potential of the products is summarized in Table 1. The trend of the values correlated with the composition and the values are different from that of the commercial brucite, supporting the possible variation of layer charge density, which depends on the composition.
The area per charge (and the layer charge density) of MgGa(I)-0.24, MgGa(I)-0.11 and MgGa(I)-0.06 were estimated from the x value and the lattice parameter a of the products as summarized in Table 1. Due to the lower layer charge density, MgGa(I)-0.06 was expected to be dispersed in water better if compared with MgGa(I)-0.24. In order to accelerate the dispersion, the samples were freeze dried to obtain LDH particles with less aggregation for stable dispersion. The samples dried by heating and by freeze drying showed a difference in the particle aggregation, while the freeze-dried sample had a lower degree of aggregation. The difference derived from the drying method was seen by the SEM images of MgGa(I)-0.06 and MgGa(I)-0.06_F (Figure 5A,B). This difference is reflected to the apparent density as shown by the photograph of the samples in the capillary tube (Figure 5C), where 10 mg of MgGa(I)-0.06_F had larger volume in the capillary than MgGa(I)-0.06 (corresponding to lower bulk density). Note that all samples exhibited platy particles in their SEM images to support the successful formation of LDHs.
The XRD patterns of the freeze-dried samples (MgGa(I)-x_F, x = 0.24 and 0.06) are shown in Figure 6 together with the corresponding samples dried by heating (MgGa(I)-x, x = 0.24 and 0.06). For the products with x of 0.24, the (003) and (006) reflections with the d values of 0.82 and 0.41 nm were observed in both MgGa(I)-0.24 and MgGa(I)-0.24_F (Figure 6a,b), suggesting the regular stacking of iodide intercalation in the interlayer of the MgGa–LDH. On the contrary, for the products with x of 0.06, the XRD pattern of MgGa(I)-0.06 (Figure 6c) showed the characteristic reflections of interstratified structure with the basal spacings of 0.82 and 0.45 nm as schematically shown in Figure 2. The (003) reflection was not seen for MgGa(I)-0.06_F (Figure 6d), suggesting an irregular layer stacking. This difference between MgGa(I)-0.24_F (regular stacking) and MgGa(I)-0.06_F (irregular stacking) was thought to be caused by the difference in the swelling due to the difference in the layer charge density, which is expected to correspond to the x value.
The carbonate forms of LDH were prepared by the ion exchange with sodium carbonate. The ion exchange of the interlayer anion of LDHs results in the change in the interlayer spacing. To induce the ion exchange, the electrostatic interactions between LDH layer and exchanging anions should be larger than that between LDH layer and original anions [12,36]. The XRD patterns and IR spectra of MgGa(CO3)-0.24_F and MgGa(CO3)-0.06_F are shown in Figure 7A,B. MgGa(CO3)-0.24_F showed the basal spacing of 0.78 nm, which is consistent with the basal spacing of MgGa–LDHs containing carbonate anion as the interlayer anion [11], indicating the successful ion exchange of iodide and nitrate anions with carbonate. The results are in agreement with the reported sequence of the ion exchange of MgAl–LDH as the order of iodide < nitrate < carbonate [28]. The basal spacing of MgGa(CO3)-0.24_F (0.78 nm) was smaller than MgGa(I)-0.24_F (0.82 nm), which is related to the size of anions as CO32− = 0.38 nm and I- = 0.42 nm [37,38,39]. For MgGa(CO3)-0.06_F, the (003) reflection was not observed in the XRD pattern as shown in Figure 7A, suggesting the irregular layer stacking. It was thought that the MgGa(CO3)-0.06_F swollen to some extent during the anion exchange thanks to the lower layer charge density, resulting in the irregular stacking by applying freeze drying. The anion exchange was indicated by the IR spectrum (Figure 7B), where the absorption due to the C-O stretching vibration of carbonate anion in the interlayer was seen at 1376 cm−1. The layered structure was maintained after the ion exchange of the iodide with carbonate. This suggested that the collapsing of the layered structure in the previous studies [32,33] occurred during the formation (precipitation) of LDH and once layered structure formed, the structure was relatively stable to accommodate different anions by the ion exchange.
Reconstruction of MgGa(CO3)-0.24_F and MgGa(CO3)-0.06_F were examined by the calcination at 500 °C and subsequent reaction with the aqueous solution of sodium dodecyl sulfate (SDS). The calcination of MgGa(CO3)-x_F (x = 0.24 and 0.06) at 500 °C caused the dehydration, decarbonation, and dehydroxylation to give mixed metal oxides, which is known to form LDH structure by up-taking the anion from aqueous solution [16]. The transformation to the oxide by the calcination was confirmed by XRD patterns (Figure 8A(b),B(b)), where diffraction peaks at 2θ of 36, 42, and 62° (corresponding to the characteristic reflections of periclase (MgO) phase (JCPDS No. 04-0829)) were observed. The oxide reconstructed to the original LDH structures after the reaction with SDS as shown by the XRD patterns (Figure 8A(c),B(c)). The XRD pattern of MgGa(DS)-0.24_F exhibited the basal spacing of 2.8 nm (Figure 8A (inset)), suggesting the incorporation of dodecyl sulfate (DS) anion in the interlayer space. If compared with the reported MgAl with x of 0.32 [40], the basal spacing of MgGa(DS)-0.24_F was smaller because of the difference in the layer charge density of the host. The layer charge density was reported to influence the orientation of DS in the interlayer space [41,42,43]. For MgGa(DS)-0.06_F, the (003) reflection was not seen in Figure 8B(c), suggesting the irregular stacking, which was thought to be caused by the swelling due to the lower layer charge density. The incorporation of DS anion in MgGa(DS)-0.06_F was confirmed by the absorption at 2922 and 2853 cm−1 due to C-H stretching vibration and those at 1200 and 1058 cm−1 due to S=O stretching vibration observed in the IR spectrum of MgGa(DS)-0.06_F (Figure 9). The IR results are consistent with those for the reported MgAl LDH containing DS as the interlayer anion [44].
The effect of x value on the dispersion was examined using MgGa(CO3)-x_F (x = 0.24 and 0.06) to be dispersed in water. Figure 10A,B shows the photograph of the dispersion before and after the storage for 6 h without agitation. MgGa(CO3)-0.24_F sedimented while MgGa(CO3)-0.06_F was dispersed. The dispersion of MgGa(DS)-x_F (x = 0.24 and 0.06) in hexanol was also examined and the appearance of the dispersion are shown in Figure 10C,D. MgGa(DS)-0.06_F was dispersed in hexanol, while MgGa(DS)-0.24_F sedimented. Since particles sizes were not different significantly for the samples, the difference in the dispersion behavior was thought to be a result of the difference in the layer charge density.

4. Conclusions

MgGa–LDHs with varied x of 0.06–0.24 were prepared by coprecipitation using iodide as interlayer anion. The linear correlation between lattice parameter a and the x values as well as the uniform distribution of Mg and Ga through the particles supported the successful substitution of Mg in the brucite-like sheet with Ga at x of 0.06–0.24. Interstratification was suggested for the sample with smaller x values, while those with larger values of 0.18 < x < 0.24 showed regular stacking of LDH layers with intercalated anion in c-axis. The zeta potential supported the possible variation of layer charge density due to the difference in the x values. Once layered structures of the MgGa–LDHs with varied x formed, the MgGa–LDHs with x of 0.06 and 0.24 were exchanged with carbonate by ion exchange and reconstructed with dodecyl sulfate after calcination, which were confirmed by the change in the basal spacing and the existence of stretching vibrations of the anions in the interlayer space. For the effect of x value on the dispersion, the carbonate type MgGa–LDH with x of 0.06 was dispersed in water and the MgGa–LDH with x of 0.06 containing dodecyl sulfate was dispersed in hexanol better than those of MgGa–LDHs with x of 0.24, suggesting possible effects of the layer charge density on the dispersion.

Author Contributions

Conceptualization, R.W. and M.O.; writing—original draft preparation, R.W., S.I. and M.O.; writing—review and editing, R.W., S.I. and M.O.; supervision, M.O. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the Research Chair Grant 2017 (grant number FDA-CO-2560-5655) from the National Science and Technology Development Agency (NSTDA), Thailand and the Research Chair Grant 2020 (grant number B05F630117) from Program Management Unit (PMU) and Office of National Higher Education Science Research and Innovation Policy Council (NXPO), Thailand.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Acknowledgments

R.W. and S.I. acknowledge Vidyasirimedhi Institute of Science and Technology for the scholarship to their Ph.D. study.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Liu, Y.; Gao, Y.; Wang, Q.; Lin, W. The synergistic effect of layered double hydroxides with other flame retardant additives for polymer nanocomposites: A critical review. Dalton Trans. 2018, 47, 14827–14840. [Google Scholar] [CrossRef]
  2. Mishra, G.; Dash, B.; Pandey, S. Layered double hydroxides: A brief review from fundamentals to application as evolving biomaterials. Appl. Clay Sci. 2018, 153, 172–186. [Google Scholar] [CrossRef]
  3. Choy, J.H.; Choi, S.J.; Oh, J.M.; Park, T. Clay minerals and layered double hydroxides for novel biological applications. Appl. Clay Sci. 2007, 36, 122–132. [Google Scholar] [CrossRef]
  4. Fan, G.; Li, F.; Evans, D.G.; Duan, X. Catalytic applications of layered double hydroxides: Recent advances and perspectives. Chem. Soc. Rev. 2014, 43, 7040–7066. [Google Scholar] [CrossRef]
  5. Yang, Z.; Wang, F.; Zhang, C.; Zeng, G.; Tan, X.; Yu, Z.; Zhong, Y.; Wang, H.; Cui, F. Utilization of LDH-based materials as potential adsorbents and photocatalysts for the decontamination of dyes wastewater: A review. RSC Adv. 2016, 6, 79415–79436. [Google Scholar] [CrossRef]
  6. Claverie, M.; Garcia, J.; Prevost, T.; Brendlé, J.; Limousy, L. Inorganic and hybrid (organic–inorganic) lamellar materials for heavy metals and radionuclides capture in energy wastes management—A review. Materials 2019, 12, 1399. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  7. Inomata, K.; Ogawa, M. Preparation and properties of Mg/Al layered double hydroxide–oleate and–stearate intercalation compounds. Bull. Chem. Soc. Jpn. 2006, 79, 336–342. [Google Scholar] [CrossRef]
  8. Taviot-Guého, C.; Prévot, V.; Forano, C.; Renaudin, G.; Mousty, C.; Leroux, F. Tailoring hybrid layered double hydroxides for the development of innovative applications. Adv. Funct. Mater. 2018, 28, 1703868. [Google Scholar] [CrossRef]
  9. Wijitwongwan, R.P.; Intasa-ard, S.G.; Ogawa, M. Preparation of layered double hydroxides toward precisely designed hierarchical organization. Chem. Eng. 2019, 3, 68. [Google Scholar] [CrossRef] [Green Version]
  10. Intasa-Ard, G.S.; Imwiset, J.K.; Bureekaew, S.; Ogawa, M. Mechanochemical methods for the preparation of intercalation compounds, from intercalation to the formation of layered double hydroxides. Dalton Trans. 2018, 47, 2896–2916. [Google Scholar] [CrossRef]
  11. Rives, V. Layered Double Hydroxides: Present and Future; Nova Science Publishers Inc.: New York, NY, USA, 2001. [Google Scholar]
  12. Evans, D.G.; Slade, R.C.T. Structural aspects of layered double hydroxides. Struct. Bond. 2006, 119, 1–87. [Google Scholar]
  13. Mascolo, G.; Marino, O. A new synthesis and characterization of magnesium-aluminium hydroxides. Miner. Mag. 1980, 43, 619–621. [Google Scholar] [CrossRef]
  14. Lee, J.Y.; Gwak, G.H.; Kim, H.M.; Kim, T.I.; Lee, G.J.; Oh, J.M. Synthesis of hydrotalcite type layered double hydroxide with various Mg/Al ratio and surface charge under controlled reaction condition. Appl. Clay Sci. 2016, 134, 44–49. [Google Scholar] [CrossRef]
  15. Bellotto, M.; Rebours, B.; Clause, O.; Lynch, J.; Bazin, D.; Elkaïm, E. A reexamination of hydrotalcite crystal chemistry. J. Phys. Chem. 1996, 100, 8527–8534. [Google Scholar] [CrossRef]
  16. Miyata, S. Physico-chemical properties of synthetic hydrotalcites in relation to composition. Clays Clay Miner. 1980, 28, 50–56. [Google Scholar] [CrossRef]
  17. Brindley, G.W.; Kikkawa, S. A crystal-chemical study of Mg, Al and Ni, N hydroxy-perchlorates and hydroxycarbonates. Am. Mineral. 1979, 64, 836–843. [Google Scholar]
  18. Kooli, F.; Chisem, I.C.; Vucelic, M.; Jones, W. Synthesis and properties of terephthalate and benzoate intercalates of mg− Al layered double hydroxides possessing varying layer charge. Chem. Mater. 1996, 8, 1969–1977. [Google Scholar] [CrossRef]
  19. Ogawa, M.; Asai, S. Hydrothermal synthesis of layered double hydroxide− deoxycholate intercalation compounds. Chem. Mater. 2000, 12, 3253–3255. [Google Scholar] [CrossRef]
  20. Milagres, J.L.; Bellato, C.R.; Vieira, R.S.; Ferreira, S.O.; Reis, C. Preparation and evaluation of the Ca-Al layered double hydroxide for removal of copper (II), nickel (II), zinc (II), chromium (VI) and phosphate from aqueous solutions. J. Environ. Chem. Eng. 2017, 5, 5469–5480. [Google Scholar] [CrossRef]
  21. Sipiczki, M.; Kuzmann, E.; Homonnay, Z.; Megyeri, J.; Pálinkó, I.; Sipos, P. The structure and stability of CaFe layered double hydroxides with various Ca:Fe ratios studied by Mössbauer spectroscopy, X-ray diffractometry and microscopic analysis. J. Mol. Struct. 2013, 1044, 116–120. [Google Scholar] [CrossRef]
  22. Ma, R.; Liang, J.; Takada, K.; Sasaki, T. Topochemical synthesis of Co−Fe layered double hydroxides at varied Fe/Co ratios: Unique intercalation of triiodide and its profound effect. J. Am. Chem. Soc. 2011, 133, 613–620. [Google Scholar] [CrossRef]
  23. Ma, R.; Liang, J.; Liu, X.; Sasaki, T. General insights into structural evolution of layered double hydroxide: Underlying aspects in topochemical transformation from brucite to layered double hydroxide. J. Am. Chem. Soc. 2012, 134, 19915–19921. [Google Scholar] [CrossRef] [PubMed]
  24. Caravaggio, G.A.; Detellier, C.; Wronski, Z. Synthesis, stability and electrochemical properties of NiAl and NiV layered double hydroxides. J. Mater. Chem. 2001, 11, 912–921. [Google Scholar] [CrossRef]
  25. Shannon, R.D. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Cryst. 1976, 32, 751–767. [Google Scholar] [CrossRef]
  26. Stepanova, L.N.; Belskaya, O.B.; Salanov, A.N.; Serkova, A.N.; Likholobov, V.A. SEM study of the surface morphology and chemical composition of the MgAl-and MgGa-layered hydroxides in different steps of platinum catalysts Pt/Mg(Al, Ga)Ox synthesis. Appl. Clay Sci. 2018, 157, 267–273. [Google Scholar] [CrossRef]
  27. Johnsen, R.E.; Wu, Q.; Sjåstad, A.O.; Vistad, Ø.B.; Krumeich, F.; Norby, P. Nanostructured materials produced by mixing and restacking of delaminated layered double hydroxides. J. Phys. Chem. 2008, 112, 16733–16739. [Google Scholar] [CrossRef]
  28. Petersen, L.B.; Lipton, A.S.; Zorin, V.; Nielsen, U.G. Local environment and composition of magnesium gallium layered double hydroxides determined from solid-state 1H and 71Ga NMR spectroscopy. J. Solid State Chem. 2014, 219, 242–246. [Google Scholar] [CrossRef] [Green Version]
  29. Sasaki, T.; Kooli, F.; Iida, M.; Michiue, Y.; Takenouchi, S.; Yajima, Y.; Izumi, F.; Chakoumakos, B.C.; Watanabe, M. A mixed alkali metal titanate with the lepidocrocite-like layered structure. Preparation, crystal structure, protonic form, and acid− base intercalation properties. Chem. Mater. 1998, 10, 4123–4128. [Google Scholar] [CrossRef]
  30. Miyata, S. Anion-exchange properties of hydrotalcite-like compounds. Clay Clay Miner. 1983, 31, 305–311. [Google Scholar] [CrossRef]
  31. Carteret, C.; Grégoire, B.; Ruby, C. Tunable composition of NiII–AlIII and NiII–FeIII layered hydroxides within a wide range of layer charge. Solid State Sci. 2011, 13, 146–150. [Google Scholar] [CrossRef]
  32. López-Salinas, E.; García-Sánchez, M.; Ramon-Garcia, M.L.; Schifter, I. New Gallium-substituted hydrotalcites: [Mg1-xGax (OH)2](CO3)x/2· mH2O. J. Porous Mater. 1996, 3, 169–174. [Google Scholar] [CrossRef]
  33. López-Salinas, E.; Garcia-Sanchez, M.; Montoya, J.A.; Acosta, D.R.; Abasolo, J.A.; Schifter, I. Structural characterization of synthetic hydrotalcite-like [Mg1-x Gax(OH)2](CO3)x/2· mH2O. Langmuir 1997, 13, 4748–4753. [Google Scholar] [CrossRef]
  34. Miyata, S. The syntheses of hydrotalcite-like compounds and their structures and physico-chemical properties—I: The systems Mg2+-Al3+-NO3−, Mg2+-Al3+-Cl−, Mg2+-Al3+-ClO4−, Ni2+-Al3+-Cl− and Zn2+-Al3+-Cl−. Clay Clay Miner. 1975, 23, 369–375. [Google Scholar] [CrossRef]
  35. Xu, Z.P.; Zeng, H.C. Abrupt structural transformation in hydrotalcite-like compounds Mg1-xAlx(OH)2(NO3)x∙nH2O as a continuous function of nitrate anions. J. Phys. Chem. B 2001, 105, 1743–1749. [Google Scholar] [CrossRef]
  36. Palin, L.; Milanesio, M.; Van Beek, W.; Conterosito, E. Understanding the ion exchange process in LDH nanomaterials by fast in situ XRPD and PCA-assisted kinetic analysis. J. Nanomater. 2019, 2019. [Google Scholar] [CrossRef] [Green Version]
  37. Iyi, N.; Fujii, K.; Okamoto, K.; Sasaki, T. Factors influencing the hydration of layered double hydroxides (LDHs) and the appearance of an intermediate second staging phase. Appl. Clay Sci. 2007, 35, 218–227. [Google Scholar] [CrossRef]
  38. Zhao, X.J.; Zhu, Y.Q.; Xu, S.M.; Liu, H.M.; Yin, P.; Feng, Y.L.; Yan, H. Anion exchange behavior of MIIAl layered double hydroxides: A molecular dynamics and DFT study. Phys. Chem. Chem. Phys. 2020, 22, 19758–19768. [Google Scholar] [CrossRef]
  39. Roobottom, H.K.; Jenkins, H.D.B.; Passmore, J.; Glasser, L. Thermochemical radii of complex ions. J. Chem. Educ. 1999, 76, 1570. [Google Scholar] [CrossRef]
  40. Toson, V.; Conterosito, E.; Palin, L.; Boccaleri, E.; Milanesio, M.; Gianotti, V. Facile intercalation of organic molecules into hydrotalcites by liquid-assisted grinding: Yield optimization by a chemometric approach. Crys. Growth Des. 2015, 15, 5368–5374. [Google Scholar] [CrossRef]
  41. Meyn, M.; Beneke, K.; Lagaly, G. Anion-exchange reactions of layered double hydroxides. Inorg. Chem. 1990, 29, 5201–5207. [Google Scholar] [CrossRef]
  42. Naik, V.V.; Vasudevan, S. Effect of alkyl chain arrangement on conformation and dynamics in a surfactant intercalated layered double hydroxide: Spectroscopic measurements and MD simulations. J. Phys. Chem. C 2011, 115, 8221–8232. [Google Scholar] [CrossRef]
  43. Clearfield, A.; Kieke, M.; Kwan, J.; Colon, J.L.; Wang, R.C. Intercalation of dodecyl sulfate into layered double hydroxides. J. Incl. Phenom. Mol. Recognit. Chem. 1991, 11, 361–378. [Google Scholar] [CrossRef]
  44. Alansi, A.M.; Alkayali, W.Z.; Al-qunaibit, M.H.; Qahtan, T.F.; Saleh, T.A. Synthesis of exfoliated polystyrene/anionic clay MgAl-layered double hydroxide: Structural and thermal properties. RSC Adv. 2015, 5, 71441–71448. [Google Scholar] [CrossRef]
Nanomaterials 11 01206 sch001 550
Scheme 1. Experimental setup for the synthesis of MgGa–LDHs intercalated with iodide.
Scheme 1. Experimental setup for the synthesis of MgGa–LDHs intercalated with iodide.
Nanomaterials 11 01206 sch001
Nanomaterials 11 01206 g001 550
Figure 1. (A) XRD patterns of MgGa(I)-x (x = 0.24 (a), 0.18 (b), 0.11 (c), 0.10 (d), 0.08 (e), and 0.06 (f)). (B) Relation between the lattice parameter a and the x value in the MgGa–LDHs.
Figure 1. (A) XRD patterns of MgGa(I)-x (x = 0.24 (a), 0.18 (b), 0.11 (c), 0.10 (d), 0.08 (e), and 0.06 (f)). (B) Relation between the lattice parameter a and the x value in the MgGa–LDHs.
Nanomaterials 11 01206 g001
Nanomaterials 11 01206 g002 550
Figure 2. Proposed structure images of MgGa(I)-x (x = 0.24, 0.11, and 0.06).
Figure 2. Proposed structure images of MgGa(I)-x (x = 0.24, 0.11, and 0.06).
Nanomaterials 11 01206 g002
Nanomaterials 11 01206 g003 550
Figure 3. IR spectra of MgGa(I)-x (x = 0.24, 0.11, and 0.06).
Figure 3. IR spectra of MgGa(I)-x (x = 0.24, 0.11, and 0.06).
Nanomaterials 11 01206 g003
Nanomaterials 11 01206 g004 550
Figure 4. SEM image and elemental mapping of MgGa(I)-0.06. The element was presented by Mg (green) and Ga (red).
Figure 4. SEM image and elemental mapping of MgGa(I)-0.06. The element was presented by Mg (green) and Ga (red).
Nanomaterials 11 01206 g004
Nanomaterials 11 01206 g005 550
Figure 5. SEM images of MgGa(I)-0.06 (A) and MgGa(I)-0.06_F (B). (C) Photograph of the products in a capillary tube to show the difference in the density, 10 mg of sample in the capillary without compressing; MgGa(I)-0.06 (left) and MgGa(I)-0.06_F (right).
Figure 5. SEM images of MgGa(I)-0.06 (A) and MgGa(I)-0.06_F (B). (C) Photograph of the products in a capillary tube to show the difference in the density, 10 mg of sample in the capillary without compressing; MgGa(I)-0.06 (left) and MgGa(I)-0.06_F (right).
Nanomaterials 11 01206 g005
Nanomaterials 11 01206 g006 550
Figure 6. XRD patterns of MgGa(I)-0.24 (a), MgGa(I)-0.24_F (b), MgGa(I)-0.06 (c), and MgGa(I)-0.06_F (d).
Figure 6. XRD patterns of MgGa(I)-0.24 (a), MgGa(I)-0.24_F (b), MgGa(I)-0.06 (c), and MgGa(I)-0.06_F (d).
Nanomaterials 11 01206 g006
Nanomaterials 11 01206 g007 550
Figure 7. (A) XRD patterns and (B) IR spectra of MgGa(CO3)-0.24_F and MgGa(CO3)-0.06_F.
Figure 7. (A) XRD patterns and (B) IR spectra of MgGa(CO3)-0.24_F and MgGa(CO3)-0.06_F.
Nanomaterials 11 01206 g007
Nanomaterials 11 01206 g008 550
Figure 8. XRD patterns of MgGa(CO3)-x_F (a), calcined MgGa(CO3)-x_F (b), and MgGa(DS)-x_F (c); x of 0.24 (A) and 0.06 (B). Inset: the (003) reflection of MgGa(DS)-0.24_F at 2θ of 3°.
Figure 8. XRD patterns of MgGa(CO3)-x_F (a), calcined MgGa(CO3)-x_F (b), and MgGa(DS)-x_F (c); x of 0.24 (A) and 0.06 (B). Inset: the (003) reflection of MgGa(DS)-0.24_F at 2θ of 3°.
Nanomaterials 11 01206 g008
Nanomaterials 11 01206 g009 550
Figure 9. IR spectra of MgGa(DS)-0.24_F and MgGa(DS)-0.06_F.
Figure 9. IR spectra of MgGa(DS)-0.24_F and MgGa(DS)-0.06_F.
Nanomaterials 11 01206 g009
Nanomaterials 11 01206 g010 550
Figure 10. Photographs of dispersion of MgGa(CO3)-x_F in water (A,B) and MgGa(DS)-x_F in hexanol (C,D) before and after the storage for 6 h.
Figure 10. Photographs of dispersion of MgGa(CO3)-x_F in water (A,B) and MgGa(DS)-x_F in hexanol (C,D) before and after the storage for 6 h.
Nanomaterials 11 01206 g010
Table
Table 1. Summary of the chemical composition, the estimated area per charge, the estimated layer charge density, and zeta potential of the products and the commercial brucite.
Table 1. Summary of the chemical composition, the estimated area per charge, the estimated layer charge density, and zeta potential of the products and the commercial brucite.
Samplex
(starting solution)		x
(products)		Ga/I (products)Estimated Area per Charge (nm2/(+)) 1Estimated Layer Charge Density ((+)/nm2) 2ζ-Potential (mV)
MgGa(I)-0.240.250.242.00.352.8638.71
MgGa(I)-0.180.200.182.10.472.13NA.3
MgGa(I)-0.110.130.112.40.761.3134.47
MgGa(I)-0.100.100.102.70.931.07NA.3
MgGa(I)-0.080.090.082.91.070.93NA.3
MgGa(I)-0.060.080.063.41.310.7630.81
Mg(OH)2-----16.94
1 Estimated area contains one positive charge = a2sin60o/x [35]. 2 Layer charge density = 1/(estimated area per charge). 3 NA. = not analyzed.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Wijitwongwan, R.; Intasa-ard, S.; Ogawa, M. Preparation of MgGa Layered Double Hydroxides and Possible Compositional Variation. Nanomaterials 2021, 11, 1206. https://doi.org/10.3390/nano11051206

AMA Style

Wijitwongwan R, Intasa-ard S, Ogawa M. Preparation of MgGa Layered Double Hydroxides and Possible Compositional Variation. Nanomaterials. 2021; 11(5):1206. https://doi.org/10.3390/nano11051206

Chicago/Turabian Style

Wijitwongwan, Rattanawadee (Ploy), Soontaree (Grace) Intasa-ard, and Makoto Ogawa. 2021. "Preparation of MgGa Layered Double Hydroxides and Possible Compositional Variation" Nanomaterials 11, no. 5: 1206. https://doi.org/10.3390/nano11051206

APA Style

Wijitwongwan, R., Intasa-ard, S., & Ogawa, M. (2021). Preparation of MgGa Layered Double Hydroxides and Possible Compositional Variation. Nanomaterials, 11(5), 1206. https://doi.org/10.3390/nano11051206

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop