Next Article in Journal
Effect of Washing on the Electrochemical Performance of a Three-Dimensional Current Collector for Energy Storage Applications
Next Article in Special Issue
CFD Development of a Silica Membrane Reactor during HI Decomposition Reaction Coupling with CO2 Methanation at Sulfur–Iodine Cycle
Previous Article in Journal
Quantitative Visualization of the Nanomechanical Young’s Modulus of Soft Materials by Atomic Force Microscopy
Previous Article in Special Issue
Solar-Powered Photodegradation of Pollutant Dyes Using Silver-Embedded Porous TiO2 Nanofibers
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 11
Issue 6
10.3390/nano11061595
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Electronic Structure and d-Band Center Control Engineering over Ni-Doped CoP3 Nanowall Arrays for Boosting Hydrogen Production

by
Jing Qi
,
Tianli Wu
*,
Mengyao Xu
,
Dan Zhou
and
Zhubing Xiao
*
Henan Key Laboratory of Photovoltaic Materials, Henan University, Kaifeng 475004, China
*
Authors to whom correspondence should be addressed.
Nanomaterials 2021, 11(6), 1595; https://doi.org/10.3390/nano11061595
Submission received: 12 May 2021 / Revised: 10 June 2021 / Accepted: 15 June 2021 / Published: 17 June 2021
(This article belongs to the Special Issue Hybrid Porous Nanomaterials for Energy and Environment)
Browse Figures
Versions Notes

Abstract

:
To address the challenge of highly efficient water splitting into H2, successful fabrication of novel porous three-dimensional Ni-doped CoP3 nanowall arrays on carbon cloth was realized, resulting in an effective self-supported electrode for the electrocatalytic hydrogen-evolution reaction. The synthesized samples exhibit rough, curly, and porous structures, which are beneficial for gaseous transfer and diffusion during the electrocatalytic process. As expected, the obtained Ni-doped CoP3 nanowall arrays with a doping concentration of 7% exhibit the promoted electrocatalytic activity. The achieved overpotentials of 176 mV for the hydrogen-evolution reaction afford a current density of 100 mA cm−2, which indicates that electrocatalytic performance can be dramatically enhanced via Ni doping. The Ni-doped CoP3 electrocatalysts with increasing catalytic activity should have significant potential in the field of water splitting into H2. This study also opens an avenue for further enhancement of electrocatalytic performance through tuning of electronic structure and d-band center by doping.

1. Introduction

Electrocatalytic splitting of water into hydrogen is one of the most simple, eco-friendly, and promising approaches to solving gradual environmental pollution, the energy crisis, and issues related to global warming [1,2,3,4,5]. The key to practical application is to develop highly efficient and inexpensive non-noble-metal electrocatalysts as substitutes for noble-metal electrocatalysts, which are expensive and scarce [6,7,8,9,10]. Transition-metal phosphides (TMPs) have been reported recently as promising hydrogen-evolution-reaction (HER) electrocatalysts because they have a structure similar to hydrogenase [11,12,13]. However, since they suffer from sluggish kinetics, the electrocatalytic activity of TMPs is far less than that of noble-metal electrocatalysts with close to zero overpotential. Therefore, increasingly greater attention has been paid to the improvement of TMPs catalytic efficiency via reduction of the overpotential and enhancement of the electrocatalytic HER durability.
Among such TMPs, Co phosphides (Co2P, CoP, CoP2, and CoP3) have attracted much research interest owing to their fine electrocatalytic performance and stability [14,15,16,17]. Moreover, heteroatom doping can tune the electronic structures and energy-level modulation so as to tune the HER electrocatalytic capability and to reduce the hydrogen adsorption free energy in catalysts [18,19,20]. Thus far, Fe-, Mn-, Cu-, and N-doped Co2P and CoP have been studied extensively [21,22,23,24], with the results indicating that the doped CoP and Co2P exhibit enhanced electrochemical performance compared with undoped electrocatalysts. In our recent work, CoP3 was shown to exhibit outstanding electrochemical activity due to having more active sites (P*) compared with Co2P and CoP [25,26]. However, to meet the requirement for industrial applications, several issues must still be addressed, including the following: (i) improvement of the electrocatalytic activity in CoP-based electrocatalysts, and (ii) elucidation of the real active species for HER activity, which has not yet been realized [27,28,29]. Therefore, modifying the electronic structures and energy levels and developing the morphologies of the TMP catalysts are crucial factors for improving their catalytic activity, which can be an achievable yet challenging task.
Motivated by the above analysis, an electronic band structure and d-band central control scheme of CoP3 nanowall arrays (NWAs) is proposed to accelerate the HER process in acidic and alkaline media, simply via vacuum-phosphorizing precursors in a sealed quartz tube. In virtue of the rapid gaseous transfer and diffusion during the electrocatalytic procedure endowed by the 3D interconnected porous structure, the NWAs exhibit highly efficient catalytic HER activity, exceeding the efficiency of both dopant-free catalysts and the majority of the previously reported non-noble-metal electrocatalysts. Moreover, with combined spectroscopic studies and theoretical calculations, it is confirmed that the enhanced electrocatalytic activity originates from the change of both the electronic band structure and d-band center following Ni doping, whereby the downward movement of the d-band center from the Fermi level weakens the H binding strength. This study opens an avenue for further enhancing the electrocatalytic activity by tuning the electronic structures and d-band center via doping.

2. Materials and Methods

2.1. Materials and Chemicals

Co(NO3)3·6H2O, NaH2PO4, Na2HPO4, H2SO4, KOH, urea, and NH4F were purchased from Aladdin Ltd. (Shanghai, China). Nafion ethanol solution (5 wt.%) and commercial Pt/C (20 wt.%) electrocatalysts were purchased from Adamas. All other chemical reagents used were of analytical grade sans additional purification. CC was provided by Shanghai Hesen Corp.

2.2. Synthesis of Ni-Doped CoP3 NWAs

The Ni-doped CoP3 NWAs on CC were prepared using the procedure illustrated in Figure 1. The hydroxide precursor on the CC was prepared via the hydrothermal method, the precursor and P were then sealed in a quartz tube by vacuum, and finally annealed at 750 °C to yield porous Ni-doped CoP3 NWAs/CC. These processes are schematically elucidated in Figure 1. In a typical synthesis procedure, to prepare the hydroxide precursor on CC, Co(NO3)2·6H2O (1.1640 g), Ni(NO3)2·6H2O (0.116 g), NH4F (0.3720 g), and urea (1.200 g), dissolved in 80 mL of deionized water (DI), were energetically stirred and transferred into a Teflon™-lined stainless-steel autoclave (50 mL) after 40 min. Meanwhile, a slice of CC (3 cm × 2 cm) was cleaned sequentially with acetone, DI, and ethanol solution. The autoclave with the mixture solution, in which the treated CC was immersed, was sealed and heated at 120 °C for 6 h in an electric oven. The CC with hydroxide precursor was washed thoroughly with DI water when the electric oven cooled down to room temperature. Then, to prepare Ni-doped CoP3 NWAs on CC, a piece of CC (0.6 cm × 1.5 cm) with hydroxide precursor and 30 mg of red phosphorus were vacuum-sealed (10−4 Pa) into a quartz tube, which was then heat-treated at 750 °C for 5 h in a furnace.

2.3. Materials Characterization

X-ray-diffraction (XRD) analysis with Cu Kα radiation at 40 kV and 50 mA was carried out using a diffractometer (PANalytical X’pert, PANalytical B.V., Almelo, Holland). The samples’ morphology, size, composition, and structure were characterized using field-emission scanning electron microscopy (FE-SEM, TESCAN MARI3, Tescan Ltd., Brno, Czech) and transmission electron microscopy (TEM, FEI TECNAI G2 F20, FEI Co., Hillsboro, OR, USA), combined with energy-dispersive X-ray (EDX) spectroscopy. The samples were measured by XPS using an Al Kα (1486.6 eV) X-ray source on a spectrometer (ESCALAB 250XI, Thermo Fisher Scientific Co., Waltham, MA, USA). The C 1s peak at 284.6 eV was selected for energy calibration to eliminate sample charging during analysis. The adsorption–desorption isotherms of nitrogen were acquired on a surface-area analyzer (JW-BK200A, Beijing JWGB Sci. & Tech. Co., Ltd., Beijing, China) in which all samples were deaerated at 100 °C prior to measurement. Hydrogen adsorption experiment was characterized by adding 30 mg of active materials into 50 mL of 1 M hydrochloric acid solution. After the solution was stirred for 2 h, the centrifugation was carried out and the pH change of the supernatant was measured to determine the amount of hydrochloric acid adsorbed by the active materials.

2.4. Electrochemical Measurements

Electrochemical workstations (CHI 660E, Chenhua Co., Shanghai, China) were used to analyze the HER polarization curves in 0.5 M H2SO4 at room temperature. A saturated calomel electrode (SCE) and graphite rod were used as the reference electrode and counter electrode, respectively. The SCE electrode was calibrated relative to the reversible hydrogen electrode (RHE). Linear-sweep-voltammetry (LSV) data were collected at a scanning rate of 2 mV s−1. The time dependence of the catalytic current during the electrolysis of the catalyst in 0.5 M H2SO4 was measured at potentiostatic voltage. Electrochemical impedance spectroscopy (EIS) were made in the 0.01–105 Hz frequency range.

2.5. Theoretical Calculation

The detailed calculations were based on published literature [30]. In general, first-principles calculation was performed using the Vienna ab initio simulation package (VASP) based on the density-functional theory (DFT) and the electron–ion interactions were conducted by generalized gradient approximation Perdew–Burke–Eznerhof (GGA-PBE) method. All the models were forced to a self-consistent accuracy of 10−5 eV. The kinetic energy cut-off of 500 eV for the plane-wave basis restriction and K-points were taken under Monkhorst-Pack for Brillouin-zone integration. The periodic images of the slab were separated by 15 Å of vacuum. To calculate the electronic properties and hydrogen evolution activity, a 5 × 5 × 1 supercell was used. The HER characteristics were evaluated by ΔGH* defined as ΔGH* = ΔEH + ΔEZPE − TΔSH, where ΔEH, ΔEZPE, and ΔSH are the differential hydrogen adsorption energy, change in the zero point energy, and entropy between adsorbed hydrogen and molecular hydrogen in the gas phase, respectively, and T is the temperature.

3. Results and Discussion

The Ni-doped CoP3 NWAs/CC were fabricated using the procedure illustrated in Figure 1. Briefly, the hydroxide precursor on CC was first prepared via a hydrothermal method, the subsequent annealing under high vacuum at 750 °C gave rise to the porous Ni-doped CoP3 NWAs/CC. SEM and TEM were employed to observe the morphologies of the Co-based precursor NWAs/CC and CoP3 NWAs/CC. The SEM images (Figure 2a,b) show that the Ni-doped Co-based precursor has an assembly walls-like morphology characterized by a smooth surface approximately 20–30 nm in thickness that evenly covers the CC surfaces. At a heating rate of 2 °C min−1 for topotactic phosphorization, the Ni-doped CoP3 NWAs maintain the three-dimensional (3D) NWA structures and original morphology of Ni-doped precursor (Figure 2c). The fact that all surfaces of the Ni-doped CoP3 NWAs are rough is confirmed both by HRSEM images (Figure 2d) and TEM images (Figure 2e), demonstrating that the as-synthesized CoP3 NWAs/CC have high porosity and a large surface area, which is verified by subsequent specific surface-area measurements. Such a rough and porous surface can significantly increase the number of active sites, thereby increasing the electrochemical surface area. The active sites of the electrocatalyst are enhanced, and the specific surface area increased, by the porous structure. The HRTEM image shown in Figure 2f reveals a clear crystal-lattice fringe with an interplanar spacing of 0.543 nm that corresponds to the (110) plane of Ni-CoP3, indicating that the prepared Ni-CoP3 nanowalls are highly crystalline. In addition, elemental mapping shows that Co, P, and Ni are uniformly distributed in the nanowall of Ni-CoP3 after doping (Figure 2g) at an atom ratio of Ni:Co:P = 0.063:1:2.94 (Figure S1).
The XRD pattern (Figure 3a) for the as-phosphorized products shows that diffraction peaks are indexed to the planes of CoP3, which agreed well with the CoP3 standard pattern (JCPDS Card No. 29-0496). In addition, no peaks related to any impurities are present, except two peaks from the CC (JCPDS Card No. 26-1080), which demonstrate the high phase purity of the products. The diffraction peaks of Ni-CoP3 NWAs/CC shift to a large angle by degrees with increment of Ni concentration (Figure 3a), which reflect that the replacement Co (atomic radius 152 pm) by Ni (149 pm) in the CoP3 cause the deflation of the CoP3 lattice. However, because of their similar atomic sizes, this atom replacement do not change the crystal structure of CoP3. After XRD refinement, the lattice parameter of Ni-CoP3-7 is calculated to be a = b = c = 7.703 Å, which is slightly lower than that of CoP3 (a = b = c = 7.711 Å), meaning that the lattice parameter decreases with the increment of Ni substitution degree. In short, the morphology and composition of Ni-doped CoP3 NWAs were controlled by high vacuum and a slow ramping rate during the phosphorization process.
The N2 adsorption/desorption isotherm of Ni-CoP3-7 NWAs exhibits a large specific surface area of ca. 73 m2 g−1, which is slightly smaller than that of CoP3. This may be due to the slight decrease in the crystallization quality derived from Ni doping (see Figure S2 in the Supplementary Material). The large specific surface area confers more catalytic active sites, thus promoting transfer of electrons to the catalytic active sites and a reaction with the osmotic electrolyte to produce hydrogen. The pore size distribution curve of the Ni-CoP3-7 NWAs shows a broad peak ranging from 2 to 25 nm, with a dominant peak at ca. 3 nm and a relatively high pore volume as compared to that of the CoP3 NWAs. Additionally, the H+ adsorption amount (based on HCl) is 7.13 g g−1 following stable adsorption in the H+ adsorption experiments (Figure S3), proving that large amounts of protons can accumulate on the surface of the Ni-CoP3-7 NWAs/CC, which may be conducive to the excellent HER activity of the Ni-CoP3-7 NWAs/CC.
The composition and elemental valence states of as-prepared samples were measured by XPS. In Figure 3b, the XPS survey spectrum of Ni-CoP3-7 NWAs/CC indicates the coexistence of Ni, Co, and P elements in the sample. The Co 2p spectrum shows the characteristic peaks for Co 2p3/2 (Figure 3c), the binding energy (BE) of which is at 780.0 eV, certifying the existence of Co3+ [31,32]. In addition, the Co 2p1/2 peak is located at 794.7 eV, accompanied by a satellite peak at 798.3 and 782.3 eV [21,22]. The characteristic peaks at 129.7 and 130.5 eV are assigned to P 2p1/2 and P 2p3/2 (Figure 3d), respectively [33]. The peak of oxidized P species at 134.6 eV was also observed due to the exposure of the samples to air [34]. It is worth mentioning that the XPS spectrum of Co 2p in Ni-CoP3-7 are mostly identical to that of pure CoP3 [14]. However, the P 2p peak in the Ni-CoP3-7 NWs/CC shifted to low energy, compared with that of pure CoP3 [14]. A greater negative shift of BEs signified that the sites of P can easily gather the electrons to join the catalytic reaction, and the electrocatalytic performance can correspondingly be enhanced [35]. In Figure 3e, the weak peaks at 852.9 (Ni 2p3/2) and 869.7 eV (Ni 2p1/2) belong to Ni-P bonds, indicating the successful doping of Ni atoms. In short, XRD and XPS analysis results confirm the successful synthesis of Ni-doped CoP3 NWAs/CC.
To study the HER catalytic activity and stability of the Ni-doped CoP3 NWAs/CC, electrochemical evaluations were carried out in a three-electrode system with iR-compensation under identical conditions. To activate the catalysts before recording data, all test electrodes were cycled 50 times between −0.6 and 0 V versus RHE at 10 mV s−1. Figure 4a plots the LSV curves at a scan rate of 2 mV s−1 in 0.5 M H2SO4 electrolyte. The bare CC shows negligible HER activity (Figure S4). The commercial Pt/C electrode exhibits highly efficient catalytic activity with an onset overpotential close to zero for the HER, while the Ni-CoP3-7 NWs/CC exhibits the best catalytic performance toward the HER, only acquiring overpotentials of −95 and −177 mV at 10 and 100 mA cm−2, respectively (Figure 4a,b). The electrocatalytic performance of Ni-CoP3-7 toward HER at high current density is indeed better than the previously reported HER electrocatalysts as shown in Table S1. The Tafel slope (Figure 4c) values are 66, 59, 54, 46, and 84 mV dec−1 for pure CoP3, Ni-CoP3-3, Ni-CoP3-5, Ni-CoP3-7, and Ni-CoP3-10, respectively, further revealing the super-catalytic behavior of Ni-CoP3-7 NWAs/CC. The exchange current density of the Ni-CoP3-7 is calculated to be −0.217 mA cm−2, which is larger than most of the non-noble-metal HER electrocatalysts (Table S1). Another important contributor to the electrocatalytic activity is the electrochemically active surface area, which is estimated by the specific double-layer capacitance (Cdl) at the solid–electrolyte interface. As shown in Figure S5, the Ni-CoP3-7 NWAs show a Cdl of 108 mF cm−2, which is larger than that of CoP3, indicating that Ni-CoP3-7 NWAs have higher active surface area than that of CoP3 NWAs. The HER performance of Ni-CoP3 NWAs was further evaluated based on turnover frequency (TOF). Figure S6 exhibits the polarization curves of various electrocatalysts normalized by the active sites. Both the TOF and Tafel slope indicate that the intrinsic performance of CoP3 can be enhanced by doping. Moreover, Figure 4d clearly depicts that the final polarization curve (after 1000 and 10,000 cycles) is slightly different from the original. In addition, the I-t curve also shows little loss for the HER after 30 h (Figure 4e), confirming the superior electrocatalytic stability of Ni-CoP3-7 toward the HER. To better understand the enhanced HER performance, impedance measurements were made for all Ni-doped CoP3 NWAs/CC. Figure 4f shows the corresponding Nyquist plots: the lower resistance of Ni-CoP3-7 NWAs/CC suggests that doping changes the electronic structure of the materials, resulting in a decrease in its impedance. In this case, the tuning of electronic structures can influence the surface-adsorption strength of intermediate species and the activation energy for the catalytic step in electrocatalysis, in agreement with the LSV curves and Tafel slopes. In addition, this conclusion is also confirmed by calculation of electron band structure and Gibbs free energy below. The excellent HER activity of the Ni-CoP3-7 NWAs/CC make it a promising catalyst for water-splitting.
The HER electrocatalytic activity of Ni-CoP3-7 NWAs/CC in 1.0 M PBS and 1.0 M KOH solutions was also investigated. As shown in Figure 5, the 3D Ni-CoP3-7 NWAs/CC needs an overpotential of −139 mV to realize a current density of 10 mA cm−2 and shows a low Tafel slope of 128 mV dec−1 with excellent durability in 1.0 M PBS solution after 5000 cycles, demonstrating its high-efficiency catalytic activity in 1.0 M PBS solution compared with most of the reported non-noble-metal electrocatalysts (Table S2). Ni-CoP3-7 NWAs/CC in a 1.0 M KOH solution (Figure 5) requires an overpotential of -106 mV to achieve a current density of 10 mA cm−2 and has a Tafel slope of 112 mV dec−1 after 5000 cycles when comparing its electrocatalytic activity to the non-noble-metal electrocatalysts from previous reports (Table S3). The composition, structure and morphology after electrocatalytic test maintain the same to the as-prepared catalysts (Figures S7 and S8). Therefore, the Ni-CoP3-7 NWAs/CC exhibits competitive electrocatalytic performance and excellent stability over a large pH range, proving it to be a promising non-noble-metal alternative with great potential for industrial production of hydrogen.
The mechanism for enhanced HER electrocatalytic activity of the Ni-CoP3 NWAs is discussed using experimental results and DFT calculations. It can be seen from Figure 3 that the BEs of Co 2p3/2 (780.0 eV) and P 2p3/2 (129.7 eV) are slightly shifted from those of metallic Co (778.3 eV) and elemental P (130.1 eV), respectively. This indicates that the Co and P atoms in Ni-CoP3-7 NWAs have a partial positive and negative charge, respectively [6,25]. Therefore, a small number of electrons are transferred from Co to P, which is conducive to the catalytic adsorption and desorption of hydrogen atoms. Therefore, the CoP3 NWAs have a similar catalytic mechanism as the metal and hydrogenase complex catalysts [36,37].
To reveal the intrinsic effect of Ni dopant on the electrocatalytic performance of CoP3 and gain new insight into the catalytically active centers, DFT was used to calculate the electronic band structure, adsorption free energy of hydrogen (ΔGH*) on Ni dopant and the d-band center for hydrogen. The calculation results indicate that it is very beneficial for the Ni substitution of Co in CoP3. First, the calculated electronic band structures of CoP3 and Ni-CoP3 are illustrated in Figure S9. Comparing with CoP3, Ni-CoP3 has a small bandgap and a larger dispersion of hybridized orbitals in CB and VB since Ni orbitals contribute to the band structures. The larger dispersion of hybridized orbitals and small bandgap lead to a good electrical conductivity. In addition, ΔGH* is a reasonable hydrogen evolution performance descriptor [38,39]. A good HER electrocatalyst requires a value of ΔGH* close to 0 eV to strike a balance between proton transfer and removal of adsorbed hydrogen [40]. The configuration of hydrogen adsorption on CoP3 and Ni-CoP3 is shown in Figure S10. ΔGH* on the original CoP3 (110) surface is −0.23 eV (Figure 6a), consistent with previous studies [41]. Apparently, ΔGH* with Ni doping is −0.13 eV, which is significantly closer to thermal neutrality than that of the original CoP3 and comparable to Pt (−0.09 eV), demonstrating a suitable H-binding energy. This generally indicates the optimal HER activity. In KOH solutions, however, in addition to ΔGH*, the water dissociation kinetic barrier is another critical factor that reflects the performance of, and sometimes even governs, the entire HER process [42]. A lower kinetic barrier for water dissociation can be effectively realized through synergistic effects [43,44]. Thus, the equilibrium between the hydrolysis barrier and hydrogen BEs determines the optimal HER performance of Ni-CoP3 NWAs in 1 M KOH. Furthermore, a previous study [45] suggested that Ni is more conducive to the desorption of OH−, while Co exhibits higher performance for the Heyrovsky and Tafel steps in alkaline solutions. Therefore, in the process of hydrogen evolution, the Ni active sites on the surface facilitate hydrolysis dissociation, while Co active sites promote the generation and release of H2 [46,47]. To better understand why Ni doping leads to the excellent electrocatalytic hydrogen-evolution activity and how Ni doping alters the electronic energy-band structure of CoP3, the DOS was calculated. The d-band center is lowered from the Fermi level (Figure 6b) and the d-band center decreases from −1.56 eV in CoP3 to −1.69 eV after Ni doping, resulting in a decrease of H binding strength [48]. These studies essentially provide the intrinsic finding that the lowering of the d-band center reduces the adsorption energy of H, which is conducive to the desorption of H from the electrocatalyst surface for HER.

4. Conclusions

In summary, Ni-doped CoP3 NWAs integrated on CC are prepared by a simple hydrothermal and high-vacuum phosphorization method. Based on the above results, the Ni-doped CoP3 NWAs show excellent HER electrocatalytic activity over a wide range of pH, and the reasons for the improved catalytic HER activity are summarized as follows: (1) the rough surface and NWA structure of CoP3 NWAs/CC provide a large specific surface area and high density of active sites; (2) the Ni-doped character of CoP3 offers great intrinsic electrocatalytic performance; (3) Ni-doped CoP3 NWAs provide good electrical conductivity, which is conducive to rapid electron transfer; and (4) the asymmetric Ni-H and Co–H bonds, as well as a low ΔGH*, facilitate the adsorption and desorption of H atoms to produce H2. It is therefore clarified in this work that a promising alternative of non-noble-metal electrocatalysts is offered for energy-conversion and energy-storage applications by nearly metallic Ni-doped CoP3 NWAs owing to earth-abundant components, facile preparation, extraordinary performance over a wide pH range, and excellent stability.

Supplementary Materials

The following are available online at https://www.mdpi.com/article/10.3390/nano11061595/s1. Figure S1. EDX spectrum of Ni-CoP3-7 NWAs/CC, Figure S2. (a) Nitrogen adsorption/desorption isotherm and (b) the BJH pore-size distribution curve of CoP3 and Ni-CoP3-7 NWAs, respectively, Figure S3. The dependence of the adsorption time on the amount of absorbed H+ (based on the quality of HCl) on the Ni-CoP3-7 NWAs catalysts in 5 mM aqueous solution, Figure S4. Polarization curves of CC in 0.5 M H2SO4, Figure S5. Cyclic voltammograms in the region of −0.18–0.02 V vs. SCE at various scan rates and the corresponding linear fitting of the capacitive currents vs. scan rates to estimate the double layer capacitance: (a) Ni-CoP3-7 NWAs/CC and (b) CoP3 NWAs/CC; (c) The capacitive currents were measured at −0.08 V vs. SCE plotted as a function of scan rate, Figure S6. TOF curves of CoP3 and Ni-CoP3-7, Figure S7. (a) XRD patterns of Ni-CoP3-7 NWAs/CC and (b), (c), (d) the XRD patterns of Ni-CoP3-7 NWAs/CC electrode after 5000 cycles CV scanning at pH 0, pH 7 and pH 14, respectively, Figure S8. SEM images after 5000 cycles CV scanning at pH 0 (a), pH 7 (b) and pH 14 (c), respectively, Figure S9. Electronic band structure of (a) CoP3 and (b) Ni-CoP3, Figure S10. The configuration of hydrogen adsorption on CoP3 (a) and Ni-CoP3 (b), Table S1. Comparison of HER performance in acid media for CoP3 HSs/CC with other TMPs HER electrocatalysts, Table S2. Comparison of HER performance in neutral media for Ni-CoP3-7 NWAs/CC with other HER electrocatalysts, Table S3. Comparison of HER performance in alkaline media for CoP3 NPAs/CC with other HER electrocatalysts.

Author Contributions

Conceptualization, Z.X. and T.W.; methodology, J.Q., D.Z. and T.W.; formal analysis, J.Q. and M.X.; Investigation, J.Q. and T.W.; writing—original draft preparation, J.Q. and M.X.; writing—review and editing, J.Q. and T.W.; supervision, T.W. and Z.X. All authors have read and agreed to the published version of the manuscript.

Funding

The work is supported by the Natural Science Foundation of Henan Province (Grant no. 202300410068), and Postdoctoral Foundation of Henan Province (201902029). Key Scientific Research Projects of Higher Education in Henan Province (21zx008). Graduate Education Innovation and Quality Improvement Plan of Henan University (CX3040A0950132).

Data Availability Statement

The data provided in this study are available on request from The correspondence author.

Conflicts of Interest

The authors declare no competing financial interest.

References

  1. Yu, L.; Zhou, H.; Sun, J.; Qin, F.; Yu, F.; Bao, J.; Yu, Y.; Chen, S.; Ren, Z. Cu nanowires shelled with NiFe layered double hydroxide nanosheets as bifunctional electrocatalysts for overall water splitting. Energy Environ. Sci. 2017, 10, 1820–1827. [Google Scholar] [CrossRef]
  2. Seh, Z.W.; Kibsgaard, J.; Dickens, C.F.; Chorkendorffff, I.; Nørskov, J.K.; Jaramillo, T.F. Combining theory and experiment in electrocatalysis: Insights into materials design. Science 2017, 355, eaad4998. [Google Scholar] [CrossRef] [Green Version]
  3. Sun, H.M.; Yan, Z.H.; Liu, F.M.; Xu, W.C.; Cheng, F.Y.; Chen, J. Self-supported transition-metal-based electrocatalysts for hydrogen and oxygen evolution. Adv. Mater. 2020, 32, 1806326. [Google Scholar] [CrossRef] [PubMed]
  4. Li, X.; Hao, X.; Abudula, A.; Guan, G. Nanostructured catalysts for electrochemical water splitting: Current state and prospects. J. Mater. Chem. A 2016, 4, 11973–12000. [Google Scholar] [CrossRef]
  5. Gusnao, R.; Sofer, Z.; Pumera, M. Metal phosphorous Trichalcogenides (MPCh(3)): From synthesis to contemporary energy challenges. Angew. Chem. Int. Ed. 2019, 58, 9326–9337. [Google Scholar] [CrossRef] [PubMed]
  6. Zhang, Z.P.; Yang, S.X.; Li, H.Y.; Zan, Y.X.; Li, X.Y.; Zhu, Y.; Dou, M.L.; Wang, F. Sustainable carbonaceous materials derived from biomass as metal-free electrocatalysts. Adv. Mater. 2019, 31, 1805718. [Google Scholar] [CrossRef] [PubMed]
  7. Chen, H.; Liang, X.; Liu, Y.P.; Ai, X.; Asefa, T.; Zou, X.X. Active site engineering in porous electrocatalysts. Adv. Mater. 2020, 32, 2002435. [Google Scholar] [CrossRef]
  8. Wang, Y.; Kong, B.; Zhao, D.; Wang, H.; Plebanski, M. Strategies for developing transition metal phosphides as heterogeneous electrocatalysts for water splitting. Nano Today 2017, 15, 26–55. [Google Scholar] [CrossRef]
  9. Duan, J.; Chen, S.; Zhao, C. Ultrathin metal-organic framework array for efficient electrocatalytic water splitting. Nat. Commun. 2017, 8, 15341. [Google Scholar] [CrossRef] [Green Version]
  10. Hu, C.; Chen, X.; Dai, Q.; Wang, M.; Qu, L.; Dai, L. Earth-abundant carbon catalysts for renewable generation of clean energy from sunlight and water. Nano Energy 2017, 41, 367–376. [Google Scholar] [CrossRef]
  11. Li, Y.; Dong, Z.H.; Jiao, L.F. Multifunctional transition metal-based phosphides in energy-related electrocatalysis. Adv. Energy Mater. 2019, 10, 1902104. [Google Scholar] [CrossRef]
  12. Du, C.; Yang, L.; Yang, F.; Cheng, G.; Luo, W. Nest-like NiCoP for highly efficient overall water splitting. ACS Catal. 2017, 7, 4131–4137. [Google Scholar] [CrossRef]
  13. You, B.; Jiang, N.; Sheng, M.; Bhushan, M.W.; Sun, Y. Hierarchically porous urchin-like Ni2P superstructures supported on nickel foam as efficient bifunctional electrocatalysts for overall water splitting. ACS Catal. 2016, 6, 714–721. [Google Scholar] [CrossRef]
  14. Wu, T.; Pi, M.; Zhang, D.; Chen, S. 3D structured porous CoP3 nanoneedle arrays as an efficient bifunctional electrocatalyst for the evolution reaction of hydrogen and oxygen. J. Mater. Chem. A 2016, 4, 14539–14544. [Google Scholar] [CrossRef]
  15. Men, Y.; Tan, Y.; Li, P.; Cao, X.; Jia, S.; Wang, J.; Chen, S.; Luo, W. Tailoring the 3d-orbital electron filling degree of metal center to boost alkaline hydrogen evolution electrocatalysis. Appl. Catal. B: Environ. 2021, 284, 119718. [Google Scholar] [CrossRef]
  16. Geng, S.; Tian, F.Y.; Li, M.G.; Guo, X.; Yu, Y.S.; Yang, W.W.; Hou, Y.L. Hole-rich CoP nanosheets with an optimized d-band center for enhancing pH-universal hydrogen evolution electrocatalysis. J. Mater. Chem. A 2021, 9, 8561–8567. [Google Scholar] [CrossRef]
  17. Wang, J.; Yang, W.; Liu, J. CoP2 nanoparticles on reduced graphene oxide sheets as a super-efficient bifunctional electrocatalyst for full water splitting. J. Mater. Chem. A 2016, 4, 4686–4690. [Google Scholar] [CrossRef]
  18. Liu, W.; Geng, P.; Li, S.Q.; Liu, W.H.; Fan, D.Y.; Lu, H.D.; Li, Z.H.; Liu, Y.P. Tuning electronic configuration of WP2 nanosheet arrays via nickel doping for high-efficiency hydrogen evolution reaction. J. Energy Chem. 2021, 55, 17–24. [Google Scholar] [CrossRef]
  19. Anjum, M.A.R.; Lee, J.S. Sulfur and nitrogen dual-doped molybdenum phosphide nanocrystallites as an active and stable hydrogen evolution reaction electrocatalyst in acidic and alkaline media. ACS Catal. 2017, 7, 3030–3038. [Google Scholar] [CrossRef]
  20. El-Refaei, S.M.; Russo, P.A.; Pinna, N. Recent advances in multimetal and doped transition-metal phosphides for the hydrogen evolution reaction at different pH values. ACS Appl. Mater. Interfaces 2021, 13, 22077–22097. [Google Scholar] [CrossRef] [PubMed]
  21. Tang, C.; Zhang, R.; Lu, W.; He, L.; Jiang, X.; Asiri, A.M.; Sun, X. Fe-doped CoP nanoarray: A monolithic multifunctional catalyst for highly efficient hydrogen generation. Adv. Mater. 2017, 29, 1602441. [Google Scholar] [CrossRef]
  22. Liu, T.T.; Ma, X.; Liu, D.N.; Hao, S.; Du, G.; Ma, Y.J.; Asiri, A.M.; Sun, X.P.; Chen, L. Mn doping of CoP nanosheets array: An efficient electrocatalyst for hydrogen evolution reaction with enhanced activity at all pH values. ACS Catal. 2017, 7, 98–102. [Google Scholar] [CrossRef]
  23. Pan, Y.; Liu, Y.; Lin, Y.; Liu, C. Metal doping effect of the M-Co2P/nitrogendoped carbon nanotubes (M = Fe, Ni, Cu) hydrogen evolution hybrid catalysts. ACS Appl. Mater. Inter. 2016, 8, 13890–13901. [Google Scholar] [CrossRef] [PubMed]
  24. Wang, X.Q.; Cheng, Y.F.; He, J.R.; Yu, B.; Wang, B.; Zhang, X.J.; Li, W.X.; Ranadoss, M.; Zhang, W.L.; Yang, D.X. Vertical V-doped CoP nanowall arrays as a highly efficient and stable electrocatalyst for the hydrogen evolution reaction at all pH values. ACS Appl. Energy Mater. 2020, 3, 1027–1035. [Google Scholar] [CrossRef]
  25. Callejas, J.F.; Read, C.G.; Popczun, E.J.; McEnaney, J.M.; Schaak, R.E. Nanostructured Co2P electrocatalyst for the hydrogen evolution reaction and direct comparison with morphologically equivalent CoP. Chem. Mater. 2015, 27, 3769–3774. [Google Scholar] [CrossRef]
  26. Popczun, E.J.; Read, C.G.; Roske, C.W.; Lewis, N.S.; Schaak, R.E. Highly active electrocatalysis of the hydrogen evolution reaction by cobalt phosphide nanoparticles. Angew. Chem. Int. Ed. 2014, 53, 5531–5534. [Google Scholar] [CrossRef]
  27. Wang, H.; Lu, Z.; Xu, S.; Kong, D.; Cha, J.J.; Zheng, G.; Hsu, P.C.; Yan, K.; Bradshaw, D.; Prinz, F.B.; et al. Electrochemical tuning of vertically aligned MoS2 nanofilms and its application in improving hydrogen evolution reaction. Proc. Natl. Acad. Sci. USA 2013, 110, 19701–19706. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  28. Zhao, D.; Zhuang, Z.W.; Cao, X.; Zhang, C.; Peng, Q.; Chen, C.; Li, Y.D. Atomic site electrocatalysts for water splitting, oxygen reduction and selective oxidation. Chem. Soc. Rev. 2020, 49, 2215–2264. [Google Scholar] [CrossRef] [PubMed]
  29. Zhu, J.; Hu, L.S.; Zhao, P.X.; Lee, L.Y.S.; Wong, K.Y. Recent advances in electrocatalytic hydrogen evolution using nanoparticles. Chem. Rev. 2020, 120, 851–918. [Google Scholar] [CrossRef] [PubMed]
  30. Pan, Y.; Sun, K.; Lin, Y.; Cao, X.; Cheng, Y.; Liu, S.; Zeng, L.; Cheong, W.; Zhao, D.; Wu, K.; et al. Electronic structure and d-band center control engineering over M-doped CoP (M = Ni, Mn, Fe) hollow polyhedron frames for boosting hydrogen production. Nano Energy 2019, 56, 411–419. [Google Scholar] [CrossRef]
  31. Liu, Q.; Tian, J.; Cui, W.; Jiang, P.; Cheng, N.; Asiri, A.M.; Sun, X. Carbon nanotubes decorated with CoP nanocrystals: A highly active non-noble-metal nanohybrid electrocatalyst for hydrogen evolution. Angew. Chem. Int. Ed. 2014, 126, 6710–6714. [Google Scholar] [CrossRef] [PubMed]
  32. Andrew, P.G.; Stephen, D.W.; Cavell, G.; Arthur, M. Examination of the bonding in binary transition-metal monophosphides MP (M) Cr, Mn, Fe, Co) by X-ray photoelectron spectroscopy. Inorg. Chem. 2005, 44, 8988–8998. [Google Scholar]
  33. Pi, M.; Guo, W.; Wu, T.; Wang, X.; Zhang, D.; Wang, S.; Chen, S. Pulsed laser deposition-assisted synthesis of porous WP2 nanosheet arrays integrated on graphite paper as a 3D flexible cathode for efficient hydrogen evolution. J. Power Sources 2017, 364, 253–257. [Google Scholar] [CrossRef]
  34. Wu, T.; Dang, Y.; He, J.; Li, T.; Qu, G.; Gao, Y.; Tan, F. Synthesis and mechanism investigation of three-dimensional porous CoP3 nanoplate arrays as efficient hydrogen evolution reaction electrocatalyst. Appl. Surf. Sci. 2019, 494, 179–186. [Google Scholar] [CrossRef]
  35. Tian, J.; Liu, Q.; Cheng, N.; Asiri, A.M.; Sun, X. Self-supported Cu3P nanowire arrays as an integrated high-performance three-dimensional cathode for generating hydrogen from water. Angew. Chem. 2014, 126, 9731–9735. [Google Scholar] [CrossRef]
  36. Wilson, A.D.; Newell, R.H.; McNevin, M.J.; Muckerman, J.T.; Dubois, M.R.; Dubois, D.L. Hydrogen oxidation and production using nickel-based molecular catalysts with positioned proton relays. J. Am. Chem. Soc. 2006, 128, 358–366. [Google Scholar] [CrossRef]
  37. Barton, B.E.; Rauchfuss, T.B. Hydride-containing models for the active site of the nickel-iron hydrogenases. J. Am. Chem. Soc. 2010, 132, 14877–14885. [Google Scholar] [CrossRef] [Green Version]
  38. Skúlason, E.; Karlberg, G.S.; Rossmeisl, J.; Bligaard, T.; Greeley, J.; Jónsson, H.; Nørskov, J.K. Density functional theory calculations for the hydrogen evolution reaction in an electrochemical double layer on the Pt(111) electrode. Phys. Chem. Chem. Phys. 2007, 9, 3241–3250. [Google Scholar] [CrossRef] [Green Version]
  39. Hinnemann, B.; Moses, P.G.; Bonde, J.; Jørgensen, K.P.; Nielsen, J.H.; Horch, S.; Chorkendorff, I.B.; Nørskov, J.K. Biomimetic hydrogen evolution:  MoS2 nanoparticles as Catalyst for Hydrogen Evolution. J. Am. Chem. Soc. 2005, 127, 5308–5309. [Google Scholar] [CrossRef]
  40. Greeley, J.; Nørskov, J.K. Large-scale, density functional theory-based screening of alloys for hydrogen evolution. Surf. Sci. 2007, 601, 1590–1598. [Google Scholar] [CrossRef]
  41. Kibsgaard, J.; Tsai, C.; Chan, K.; Benck, J.D.; Nørskov, J.K.; Abild-Pedersen, F.; Jaramillo, T.F. Designing an improved transition metal phosphide catalyst for hydrogen evolution using experimental and theoretical trends. Energy Environ. Sci. 2015, 8, 3022–3029. [Google Scholar] [CrossRef]
  42. Ling, T.; Yan, D.Y.; Wang, H.; Jiao, Y.; Hu, Z.; Zheng, Y.; Zheng, L.; Mao, J.; Liu, H.; Du, X.W.; et al. Activating cobalt(II) oxide nanorods for efficient electrocatalysis by strain engineering. Nat. Commun. 2017, 8, 1509. [Google Scholar] [CrossRef] [Green Version]
  43. Liu, J.; Zhu, D.; Ling, T.; Vasileff, A.; Qiao, S.Z. S-NiFe2O4 ultra-small nanoparticle built nanosheets for efficient water splitting in alkaline and neutral pH. Nano Energy 2017, 40, 264–273. [Google Scholar] [CrossRef]
  44. Zheng, Y.; Jiao, Y.; Vasileff, A.; Qiao, S.Z. The hydrogen evolution reaction in alkaline solution: From theory, single crystal models, to practical electrocatalysts. Angew. Chem. Int. Ed. 2018, 57, 7568–7579. [Google Scholar] [CrossRef] [PubMed]
  45. Staszak-Jirkovsky, J.; Malliakas, C.D.; Lopes, P.P.; Danilovic, N.; Kota, S.S.; Chang, K.C.; Genorio, B.; Strmcnik, D.; Stamenkovic, V.R.; Kanatzidis, M.G.; et al. Design of active and stable Co-Mo-Sx chalcogels as pH-universal catalysts for the hydrogen evolution reaction. Nat. Mater. 2016, 15, 197–203. [Google Scholar] [CrossRef]
  46. Zhang, R.; Wang, X.; Yu, S.; Wen, T.; Zhu, X.; Yang, F.; Sun, X.; Wang, X.; Hu, W. Ternary NiCo2Px nanowires as pH-universal electrocatalysts for highly efficient hydrogen evolution reaction. Adv. Mater. 2017, 29, 1605502. [Google Scholar] [CrossRef] [PubMed]
  47. Subbaraman, R.; Tripkovic, D.; Strmcnik, D.; Chang, K.C.; Uchimura, M.; Paulikas, A.P.; Stamenkovic, V.; Markovic, N.M. Enhancing hydrogen evolution activity in water splitting by tailoring Li+-Ni(OH)2-Pt interfaces. Science 2011, 334, 1256–1260. [Google Scholar] [CrossRef] [PubMed]
  48. Hammer, B.; Norskov, J.K. Why gold is the noblest of all the metals. Nature 1995, 376, 238–240. [Google Scholar] [CrossRef]
Nanomaterials 11 01595 g001 550
Figure 1. Schematic of synthesis procedure of Ni-doped CoP3 nanowall arrays.
Figure 1. Schematic of synthesis procedure of Ni-doped CoP3 nanowall arrays.
Nanomaterials 11 01595 g001
Nanomaterials 11 01595 g002 550
Figure 2. (a,c) SEM images of Ni-doped cobalt precursor NWAs/CC. (b,d) SEM images of Ni-CoP3-7 NWAs/CC. (e) TEM and (f) HRTEM images of Ni-CoP3-7 NWAs/CC. (g) TEM and corresponding elemental mapping images of Ni, Co, and P for Ni-CoP3-7 NWAs/CC.
Figure 2. (a,c) SEM images of Ni-doped cobalt precursor NWAs/CC. (b,d) SEM images of Ni-CoP3-7 NWAs/CC. (e) TEM and (f) HRTEM images of Ni-CoP3-7 NWAs/CC. (g) TEM and corresponding elemental mapping images of Ni, Co, and P for Ni-CoP3-7 NWAs/CC.
Nanomaterials 11 01595 g002
Nanomaterials 11 01595 g003 550
Figure 3. (a) XRD patterns and XPS (b) survey, (c) Co 2p, (d) P 2p, and (e) Ni 2p spectra of Ni-CoP3-7 NWAs/CC sample.
Figure 3. (a) XRD patterns and XPS (b) survey, (c) Co 2p, (d) P 2p, and (e) Ni 2p spectra of Ni-CoP3-7 NWAs/CC sample.
Nanomaterials 11 01595 g003
Nanomaterials 11 01595 g004 550
Figure 4. (a) HER performance of as-prepared Ni-CoP3 NWAs/CC with different Ni concentrations and commercial Pt/C catalyst in 0.5 M H2SO4. (b) HER overpotentials for delivering current densities of 100 mA cm−2 and (c) corresponding Tafel slopes for Ni-CoP3 NWAs/CC with different Ni concentrations. (d) LSV curves of Ni-CoP3-7 before and after 10,000 cycles of cyclic-voltammetry scans. (e) Time dependence of current density for Ni-CoP3-7 at static overpotential of 172 mV for 30 h. (f) EIS for Ni-CoP3 NWAs/CC with different Ni concentrations.
Figure 4. (a) HER performance of as-prepared Ni-CoP3 NWAs/CC with different Ni concentrations and commercial Pt/C catalyst in 0.5 M H2SO4. (b) HER overpotentials for delivering current densities of 100 mA cm−2 and (c) corresponding Tafel slopes for Ni-CoP3 NWAs/CC with different Ni concentrations. (d) LSV curves of Ni-CoP3-7 before and after 10,000 cycles of cyclic-voltammetry scans. (e) Time dependence of current density for Ni-CoP3-7 at static overpotential of 172 mV for 30 h. (f) EIS for Ni-CoP3 NWAs/CC with different Ni concentrations.
Nanomaterials 11 01595 g004
Nanomaterials 11 01595 g005 550
Figure 5. LSV curves of the Ni-CoP3-7 NWAs/CC in (a) 1.0 M PBS (pH 7) and (c) 1.0 M KOH (pH 14), and the corresponding Tafel plots in (b,d).
Figure 5. LSV curves of the Ni-CoP3-7 NWAs/CC in (a) 1.0 M PBS (pH 7) and (c) 1.0 M KOH (pH 14), and the corresponding Tafel plots in (b,d).
Nanomaterials 11 01595 g005
Nanomaterials 11 01595 g006 550
Figure 6. DFT calculations. (a) Calculated free-energy diagram of Pt, Ni-CoP3, and CoP3. (b,c) Calculated DOS curves for CoP3 and Ni-CoP3, respectively.
Figure 6. DFT calculations. (a) Calculated free-energy diagram of Pt, Ni-CoP3, and CoP3. (b,c) Calculated DOS curves for CoP3 and Ni-CoP3, respectively.
Nanomaterials 11 01595 g006
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Qi, J.; Wu, T.; Xu, M.; Zhou, D.; Xiao, Z. Electronic Structure and d-Band Center Control Engineering over Ni-Doped CoP3 Nanowall Arrays for Boosting Hydrogen Production. Nanomaterials 2021, 11, 1595. https://doi.org/10.3390/nano11061595

AMA Style

Qi J, Wu T, Xu M, Zhou D, Xiao Z. Electronic Structure and d-Band Center Control Engineering over Ni-Doped CoP3 Nanowall Arrays for Boosting Hydrogen Production. Nanomaterials. 2021; 11(6):1595. https://doi.org/10.3390/nano11061595

Chicago/Turabian Style

Qi, Jing, Tianli Wu, Mengyao Xu, Dan Zhou, and Zhubing Xiao. 2021. "Electronic Structure and d-Band Center Control Engineering over Ni-Doped CoP3 Nanowall Arrays for Boosting Hydrogen Production" Nanomaterials 11, no. 6: 1595. https://doi.org/10.3390/nano11061595

APA Style

Qi, J., Wu, T., Xu, M., Zhou, D., & Xiao, Z. (2021). Electronic Structure and d-Band Center Control Engineering over Ni-Doped CoP3 Nanowall Arrays for Boosting Hydrogen Production. Nanomaterials, 11(6), 1595. https://doi.org/10.3390/nano11061595

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.