Next Article in Journal
A Super Anticorrosive Ultrathin Film by Restarting the Native Passive Film on 316L Stainless Steel
Previous Article in Journal
Uranium Removal from Aqueous Solutions by Aerogel-Based Adsorbents—A Critical Review
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 13
Issue 2
10.3390/nano13020365
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Improved Performance of Composite Bipolar Plates for PEMFC Modified by Homogeneously Dispersed Multi-Walled Carbon Nanotube Networks Prepared by In Situ Chemical Deposition

by
Wenkai Li
1,
Zhiyong Xie
1,*,
Shi Qiu
1,
Haodong Zeng
1,2,
Minqi Liu
1 and
Gangsheng Wu
1
1
Carbon-Carbon Composite Materials Research Institute of Powder Metallurgy Research Institute, Central South University, Changsha 410017, China
2
Guangdong Hydrogen Development New Material Technology Co., Ltd., A1 (Block 2), No. 28, Xingsheng East Road, Hecheng Street, Gaoming District, Foshan 528500, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2023, 13(2), 365; https://doi.org/10.3390/nano13020365
Submission received: 19 December 2022 / Revised: 12 January 2023 / Accepted: 13 January 2023 / Published: 16 January 2023
Browse Figures
Versions Notes

Abstract

:
Composite bipolar plates with excellent performance play a crucial role in improving the overall performance of proton-exchange-membrane fuel cells. However, for graphite/resin composite bipolar plates, their electrical conductivity and mechanical properties are often too complex to meet the needs of users at the same time. Although nanoconductive fillers can alleviate this problem, the performance improvement for composite bipolar plates is often limited due to problems such as agglomeration. In this study, a uniformly dispersed multi-walled carbon nanotube network was prepared by in situ vapor deposition on the surface and pores of expanded graphite, which effectively avoided the problem of agglomeration and effectively improved the various properties of the composite BPs through the synergistic effect with graphite. With the addition of 2% in situ deposited carbon nanotubes, the modified composite bipolar plate has the best conductivity (334.53 S/cm) and flexural strength (50.24 MPa), and all the properties can meet the DOE requirements in 2025. Using the in situ deposition of carbon nanotubes to modify composite bipolar plates is a feasible route because it can result in multi-walled carbon nanotubes in large quantities and avoid the agglomeration phenomenon caused by adding nanofillers. It can also significantly improve the performance of composite bipolar plates, achieving the high performance of composite bipolar plates at a lower cost.

1. Introduction

Proton-exchange-membrane fuel cells (PEMFCs) have the advantages of a high energy-conversion rate, environmental protection, and low noise and thus have attracted extensive research [1,2]. PEMFCs mainly comprises a proton exchange membrane, catalytic layer, bipolar plate (BPs), and gas diffusion layer (GDL). As one of the essential components of a proton-exchange-membrane fuel cell, the bipolar plate plays the role of hydrothermal management, conducting current between single cells, transporting gas, etc. Hence, it has an important impact on the performance of a PEMFC [3,4]. In addition, BPs can account for 30% of the cost and 80% of the mass of a fuel cell stack [5]. Due to the role of BPs in fuel cells, higher electrical conductivity and mechanical properties, lower hydrogen permeability, and interface contact resistance with GDL are necessary for BPs.
According to different materials, BPs can be divided into graphite BPs, metal BPs, and graphite/resin composite BPs. Graphite BPs are the most mature class of BPs at present, with the advantages of good electrical conductivity and low contact resistance. However, graphite BPs have high processing costs and poor mechanical properties [6]. Metal BPs have good electrical conductivity, mechanical properties, and easy processing [7], while the durability of metal BPs in the fuel-cell environment is not good, and the metal ions generated by corrosion will damage the proton exchange membrane and reduce the life of other components of the PEMFC. Therefore, additional costs are often required to prepare corrosion-resistant coatings to increase their durability [8,9,10,11]. The composite BPs are composed of graphite and resin, so the processing cost is lower, and their mechanical properties are also better than pure graphite BPs [12]. The fly in the ointment is that the electrical conductivity of the composite BPs is lower than that of graphite due to the presence of the non-conductive resin region, and it is difficult to achieve a balance between mechanical strength and electrical conductivity.
Many studies have been carried out to improve the performance of composite bipolar plates. Dong [13] used a modified epoxy resin to prepare a composite bipolar plate, which improved the interfacial compatibility of resin and graphite and improved the performance of the composite bipolar plate. Fengjing [14] introduced cactus-like carbon nanofibers into the composite bipolar plate by surface treatment, which improved the performance of the composite bipolar plate. Its electrical conductivity could reach 198.27 S/cm, and the contact resistance was reduced to 25.4 mΩ·cm2. R.B. Mathur et al. studied the effect of different conductive fillers on the performance of composite bipolar plates and found that carbon fibers, carbon nanotubes, and carbon black all play a positive role in the performance of composite bipolar plates [15]. BinHU et al. used graphite and NH4HCO3 to prepare a composite bipolar plate with a three-dimensional conductive network, which improved the electrical conductivity and the power density of proton-exchange-membrane fuel cells. The highest in-plane conductivity is 212.64 S/cm [16].
In fact, since the conductive paths inside the composite bipolar plate are often blocked due to the inhomogeneity of the material and the addition of resin, which will reduce the conductive performance of the composite bipolar plate, Therefore, a reasonable construction of conductive paths to ensure that the conductive paths inside the material are not blocked has also been proven to be an effective method to improve performance [17,18,19,20,21]. For example, Fan [22] uses the reasonable distribution of flake graphite (FG) and expanding graphite (EG) to construct a conductive path to improve the performance of the composite bipolar plate, and its conductivity can reach up to 332.64 S/cm. Additionally, the addition of conductive fillers can also effectively improve the electrical conductivity of composite bipolar plates [23,24,25,26]. At present, a variety of fillers have been proven to play a positive role in the performance of composite bipolar plates, such as carbon fibers (CF), multi-walled carbon nanotubes (MWCNTs), graphene, and conductive carbon black [27,28,29,30]. However, although nanoscale conductive fillers have good intrinsic conductivity, they tend to agglomerate in composites due to their excessively high surface energy, which will lead to reduced performance improvement and even the formation of regional agglomerated structures and will destroy the overall structure of composite BPs, resulting in performance degradation [31,32,33,34].
Chemical vapor deposition (CVD) is the mainstream process for preparing MWCNTs in large quantities, and the prepared MWCNTs have a high degree of graphitization. However, since MWCNTs are easy to agglomerate, adding the prepared MWCNTs to the graphite/resin mixed powder to prepare BPs can easily lead to the agglomeration of MWCNTs into particles. This will result in the inability of MWCNTs to play a role in improving performance [35,36]. However, by dispersing the catalyst particles on the CVD precursor by a suitable method, the uniform dispersion of the deposited product can be achieved, thereby avoiding agglomeration [37,38,39,40]. Therefore, the innovative in situ CVD method can avoid the agglomeration of nanofillers compared with the previous process using nanofillers to modify composite BPs. The MWCNTs without agglomeration can fully exploit their advantages in electrical and thermal conductivity, which is conducive to the further improvement of the performance of composite BPs.
This study successfully avoided this problem by adopting the in situ CVD method. The readily dispersible catalyst particles were uniformly dispersed on the surface of the graphite substrate in advance before deposition. Then CVD was performed to prepare MWCNTs directly on the surface of the graphite substrate. Since the catalyst particles have been dispersed in advance, the prepared MWCNTs also inherited this feature. In the composite BPs prepared by this method, the internal MWCNTs were dispersed together with the graphite particles, forming a uniform conductive path, which improved the conductivity of the composite BPs and reduced the contact resistance with GDL. At the same time, the in situ deposited MWCNTs also filled the structural defects of graphite particles and reduced the porosity and defects of composite BPs. Therefore, their mechanical properties were further improved, and can assist in expanding graphite and flake graphite together to build a conductive network. In this study, the process of modifying the properties of composite BPs was also compared with the current mainstream method of the direct addition of CNTs based on previous studies.

2. Experimental

2.1. Materials

The following raw materials were used in the preparation of in situ deposited carbon nanotubes: absolute ethanol (99.5%), cobalt nitrate hexahydrate (99%), high-purity nitrogen (99.9%), high-purity hydrogen (99.9%), and high-purity acetylene (99.5%).
The following raw materials were used in the preparation of composite BPs: PEEK resin (Mw = 200,000, Victrex Ltd, Shanghai, China.), flake graphite (quality purity 99.9%, mesh = 100, Shanghai Aladdin Co., Shanghai, China), expanded graphite (Purity = 99.9%, mesh = 800, Shanghai Aladdin Co., Shanghai, China ), and commercial multi-walled carbon nanotubes(Purity > 98%, length = 60–200 nm, average diameter = 12 nm, Sigma Aldrich (Shanghai) Trading Co., Shanghai, China) for comparison.

2.2. Preparation of MWCNTs by In Situ Chemical Vapor Deposition

In the pretreatment process of chemical deposition, a certain amount of expanded graphite powder was weighed, and cobalt nitrate hexahydrate equivalent to 5% mass fraction of the graphite mass was fully mixed with graphite under ultrasonic conditions heated to 70 ℃ to accelerate the volatilization of alcohol, and when the solution appeared as a paste, the solution was dried in an oven for 8 h to obtain the expanded graphite mixed with cobalt nitrate.
The treated expanded graphite powder loaded with cobalt nitrate was placed in a vapor deposition furnace. Heating in two steps—in situ reduction and in situ chemical vapor deposition. After heating to the reduction temperature at 400 °C, hydrogen was introduced for reduction for a period of time so that the 2-valent cobalt was reduced by hydrogen to catalytic monolithic cobalt particles. A vapor deposition furnace was then heated to the deposition temperature. In order to study the morphology of the in situ deposited MWCNTs at different temperatures, the in situ deposited MWCNTs prepared at X degrees Celsius were labeled as MWCNTsx. Based on our previous experiments. MWCNTs prepared at 780~900 degrees Celsius were mainly studied and labeled CNT750, CNT780, CNT810, CNT840, CNT870 and CNT900. The bipolar plate group with the addition of in situ deposited carbon nanotubes was named I-CBPs; the group with direct addition of commercial carbon nanotubes for comparison was named C-CBPs, and the blank control group without any nano-conducting agent was named BC-BPs.

2.3. Preparation of Composite Bipolar Plates

The powder prepared in the previous step was mixed with resin and flake graphite. After the mixed powder was obtained, it was put into a mold for hot pressing. The mold used in this study was 40 mm × 40 mm in size, and the sample’s thickness depended on the powder’s amount. In order to meet the thickness requirements of the composite bipolar plate, its thickness was controlled at 0.4 mm, the molding temperature was controlled at 270 °C, and the molding pressure was 80 MPa. Each time it was molded, the pressurization–depressurization was carried out three times, which was used to ensure that the air inside the mold was utterly pressed out. The whole preparation process is shown in Figure 1.

2.4. Characterization of Deposition Products and Composite Bipolar Plates

Scanning electron microscopy (SEM, JSM−7600F, Japan Electronics Corporation, Tokyo, Japan) was used to study the morphologies of in situ deposited MWCNTs and the surface morphologies and cross-sectional morphologies of the prepared composite bipolar plates.
Transmission electron microscopy (TEM, FEI tecnai F20, FEI Corporation, Hillsboro, USA) was used to further study the microscopic morphology of the deposited MWCNTs, such as the number of wall layers and the diameter and to study the structure of the conductive network at the microscopic level.
Raman spectroscopy (Oxford MAX20, Hitachi, Ltd., Tokyo, Japan) were used to study the degree of graphitization of the in situ deposited MWCNTs and the number of graphite stacking layers.
A Rigaku X-ray Diffractometer Miniflex 600 (Japan Science Corporation, Tokyo, Japan) was used to test the X-ray diffraction patterns of MWCNTs, and the scanning range was 5~90°.
A Instron 3369 Universal Mechanical Tester (Instron Shanghai Ltd, Shanghai, China) was used to test the bending strength. The sample was shaped into a long strip with a size of 40 × 20 mm2 and measured by the three-point bending method, with a bending moment of 20 mm, and the bending strength was calculated from the bending stress. The bending strength was calculated using the following formula as Equation (1) shows:
ε = 6 f · h L 2
σ = 3 P L 2 b h
where the displacement of the pressure head was taken as an approximation in this study; L was the span (mm); P was the bending loads (N), and b was the width (mm).
The conductivity of the composite bipolar plate was measured by the ST2258C four-probe method. The composite bipolar plate was prepared into a block sample of 40 mm × 40 mm. Its internal circuit and calculation formula were shown below. By dividing the measurement result by the thickness correction factor, the shape correction factor was obtained to calculate the conductivity of the composite bipolar plate. The conductivity test principle and equipment are shown in Figure 2A. The resistivity measured by the four-probe method can be calculated as shown in Equation (3) by the following equation.
σ = I π d v ln ( l 13 l 24 l 12 l 34 )
where I is the current, v is the voltage between point 2 and point 3, and d is the thickness of the BPs.
In order to obtain the hydrophobic performance of the composite bipolar plate, the JC2000A contact angle tester was used to test the contact angle of the composite bipolar plate, and the hydrophobic performance of the composite bipolar plate was obtained by calculating the angle between a single droplet and the surface of the composite bipolar plate.
The interface contact resistance (ICR) and area-specific resistance (ASR) measurement adopts the test standards in the DOE standard, and a FT361SJB ICR tester was used for testing ICR. The test principle and test circuit are shown in the Figure 2B, and the contact resistance between the composite bipolar plate and the GDL is calculated according to the following equation:
R = V · A s I 2
R t o t a l = 2 R G D L + 2 R G D L / C u + 2 R G D L / b + R b
R sys = 2 R G D L + 2 R G D L / C u + 2 R G D L / GDL
I C R = R GDL / B = ( R total - R sys - R b ) / 2
A S R = 2 I C R + R b
where R is the total contact resistance, V is the voltage drop through the setting, I is the applied current, and As represents the contact area of the sample. The test method is shown in Figure 2B, by placing two or three pieces of GDL into the test instrument, Rsys, RGDL/GDL can be measured, and and ICR can be obtained by Equations (4)–(8). Rtotal is the tested resistance with the BPs, and Rsys is the tested resistance without BPs. RGDL/Cu is the interface resistance between copper plates and carbon papers, and RGDL/b is the ICR. ASR can also be calculated.
The thermal conductivity of the samples was measured by hotdisk according to the international standard ISO 22007-2, using a Hot Disk TPS 2500S (Hot Disk Sweden, Stockholm, SWE) thermal conductivity measuring instrument
According to the DOE standard, a self-made device for testing the hydrogen permeability of the composite bipolar plate was made. A schematic diagram of the device is shown in the Figure 2C. By measuring the air pressure difference between the vacuum chamber and the gas chamber for a certain period of time, the hydrogen permeability rate was calculated by a formula.
In order to measure the electrochemical properties and corrosion resistance of composite bipolar plates, a Wavedriver100 Electrochemical Comprehensive Tester was used to test the corrosion resistance of composite bipolar plates. The corrosion resistance is characterized by measuring its tafel curve and calculating the corrosion current. According to the DOE standard, the specific parameters of the test are: conditions of 80 °C, 0.5 M H2SO4 and 2 × 10−6 M HF solution; the scanning range was from −0.5 V to 0.9 V, and the scan rate was 0.2 mV/s. The samples for the constant potential polarization method were tested at potentials of −0.1 V and 0.6 V, respectively, using the same solutions to simulate the positive and negative corrosion conditions of PEMFC.
The Mike ASAP2460 Automatic Specific Surface and Porosity Analyzer BET (Micron Instruments, Inc. (Shanghai Branch), Shanghai, China) was used to analyze the pore size distribution, porosity, average pore size and other parameters of the composite bipolar plate. In order to reduce errors, the crushed small block samples were passed through multiple mesh screens. The error caused by the size is small. The test condition was 100 °C under a nitrogen atmosphere, and the degassing time was 8 h. In order to analyze the pore size distribution and the filling effect of nanofillers, the analysis was carried out by the DFT method.

3. Results and Discussion

3.1. Morphology of MWCNTs Prepared at Different Temperatures and Its Effect on the Properties of BPs

To investigate the conditions under which the MWCNTs deposited in situ on EG can be uniformly dispersed on the EG surface to form a mesh-like conductive structure, the SEM images and TEM are shown in Figure 3 and Figure 4.
From SEM, the content of MWCNTs deposited on the EG surface was gradually increased with increasing deposition temperature, from sparse discrete MWCNTs at 750 °C and 780 °C, as Figure 3A,B shows; to a uniformly distributed network-like structure at 810 °C and 840 °C, as Figure 3C,D shows; and a sparsely encapsulated layer-like structure at higher temperatures, as Figure 3E,F shows. At lower temperatures, the dispersed metal particles did not agglomerate, but the reaction rate was also slower at this time, so the generated MWCNTs network was sparse. However, with further increase in temperature, the reaction rate was further accelerated, the mobility of catalyst particles was enhanced, and the diffusion rate of carbon atoms in the carbon source was accelerated, which led to the increase in the diameter of MWCNTs and the agglomeration on the EG surface and finally, the formation of loose carbon particles.
After studying the macroscopic distribution of MWCNTs on EG, TEM was used to analyze the diameter, wall thickness and content of MWCNTs to further investigate the properties of in situ deposited MWCNTs. From the TEM results, the thickness of MWCNTs gradually became thicker with increasing temperature; the graphene layers on their tube walls gradually became indistinct, as Figure 4A–E shows, and finally formed carbon particles, as Figure 4F shows without lattice stripes.
According to the formation mechanism of MWCNTs, MWCNTs were formed through a dissolution–diffusion mechanism [41,42]. At low temperatures, the reaction location was limited by the diffusion rate of C elements, so the reaction can only occur on the side of the catalyst droplet, forming completely hollow MWCNTs. As the temperature increased, the diffusion rate of C atoms gradually increased and was able to react on all sides of the catalyst, which led to the gradual disappearance of the tube walls of MWCNTs with an oriented structure. The diameter also increases with the increase of the diffusion–precipitation region, finally leading to the transformation of MWCNTs into C particles.
Raman spectroscopy was used to investigate the graphitization of in situ deposited MWCNTs, and the results are shown in Figure 4G. The complete single-crystal graphite has only a sharp peak (g-peak) at 1580 cm−1, and the incomplete single-crystal graphite material has a peak (d-peak) at 1360 cm−1. The peak intensity indicates the number of non-graphitized boundaries in the material, that is, the turbostratic non-graphitized structure. Therefore, the ratio of peak heights can be used to characterize the degree of graphitization R (Id/Ig) of carbon materials; the smaller R is, the higher the degree of graphitization is. The D-peaks of CNT810 and CNT840 were almost absent, which indicated that their graphitization was very high.
However, it should be noted that the Raman spectrum is often used to determine the average value in a small range, and for the group with a small amount of deposition, the graphite of the substrate may have a certain impact on the results. The results are shown in Figure 4H. Except for the product at 900 degrees, the rest of the products had the characteristic peaks of MWCNTs (2θ ≈ 26°, 2θ ≈ 43°), which was also consistent with the TEM image results, because under TEM, the product at 900 °C was carbon particles, not typical carbon nanotubes.
The 2% content of MWCNTs prepared at different temperatures was mixed with the 20% mass fraction of PEEK and the 80% of FG pressed into bipolar plates, and their conductivity and flexural strength were tested, as shown in Figure 5. It can be found that different MWCNTs have different effects on the performance of BPs under the condition of controlling a certain amount of MWCNTs addition. The MWCNTs produced at lower temperatures were only produced at specific parts of the EG, and no conductive network structure was produced, so the performance of BPs was poorly improved. As the temperature increased, the conductive network was gradually improved, and conductivity was gradually constructed. It can be found from the SEM image that the BPs filled the defects of graphite, such as the seams and holes of EG, so the conductivity of BPs was improved. The bending strength also has a certain improvement effect. When the temperature rose to a very high level, not only the graphitization decreased but also the formation of loose carbon particles did not improve the performance of BPs, so the bending strength and conductivity were lower. From the results of the experiments, the CNT810 were the most useful for the improvement of the properties of BPs, so the CNT810 were used for the subsequent experiments.

3.2. Effect of the Ratio of FG and EG on Structure and Properties of BPs

Different ratios of EG and FG can construct different structures of conductive pathways. In this subsection, the effects of different ratios of EG and FG on the structure and properties of BPs were investigated. Different proportions of EG and FG powders were mixed with resin and pressed into BPs, and the samples were named as shown in Table 1. The planar conductivity, flexural strength and contact resistance of the pressed BPs were tested, and the results are shown in Figure 6.
EG and FG have different morphologies and therefore have different effects on the structure of BPs: EG is an excellent thermal and electrical conductivity material, but because of its high porosity and low strength [43,44,45], too much EG in the composite BPs was conducive to the rise in electrical conductivity but led to a decline in flexural strength. At the same time, the small mesh size of EG was often difficult to form into a dispersion of the conductive channel because of agglomeration, and this led to cracks, as shown in Figure 6A. It is necessary to add a large mesh size with a large area ratio of laminated graphite to improve the bending strength and to improve the construction of the conductive channel to form the structure shown in Figure 6B. The conductivity of the bipolar plate can reach 289.37 S/cm, which is 7.6% higher than the 268.74 S/cm of the pure EG bipolar plate. The ICR with GDL was also reduced, as shown in Figure 6C,D, thanks to the graphite forming a complete conductive pathway. The increase in flexural strength was even greater, from 22.23 MPa to 39.37 MPa compared to pure EG. Compared to pure EG bipolar plate, there was a synergistic effect between FG and EG, which can form a more dispersed conductive pathway and therefore has a greater effect on the conductivity enhancement of BPs. Therefore, in the subsequent study, a resin ratio of FG:EG = 3:1 was used for further experiments.

3.3. Effect of In Situ Deposited MWCNTs on the Structure and Properties of BPs

Although the reasonably proportioned EG/FG has much-improved performance compared to the pure EG plate, there are still many defects and porosity and shortcomings in performance, as shown in Figure 6C. The ICR of any group of samples had difficulty in meeting the DOE requirement of 2025 (pressure = 1.5 MPa). MWCNTs, as nanomaterials, have high surface energy and are prone to agglomeration, while the in situ deposition of MWCNTs using catalyst particles already dispersed on the surface of graphite particles can effectively improve the agglomeration phenomenon as described in the previous section. Different ratios of in situ deposited MWCNTs and commercial MWCNTs added directly as a comparison were used to prepare BPs, and the samples are shown in Table 2. The control samples with the direct addition of commercial MWCNTs were named D-CBPs and with in situ deposited MWCNTs were named I-CBPs, and the BPs without any conductive filler added to the blank control group were named BC-BPs (Sample EG20FG60R20). The specific groups are shown in Table 2 below. The performance test of composite BPs is shown in Figure 7 and the FESEM images of the surfaces and sections of the composite BPs of different groups are shown in Figure 8. The specific performance values of all composite BPs are shown in Table 3.
The results of conductivity tests in Figure 7A show that the conductivity of I-CBPs increased with the addition of MWCNTs. This was due to the high intrinsic conductivity of MWCNTs and their ability to form conductive pathways inside the BPs. As shown in Figure 8E–G, MWCNTs covered the graphite surface and completed the conductive network. MWCNTs formed a network structure in the surface layer of EGs, which expanded the contact surface between conducting particles in BPs and filled the gaps between particles inside BPs as Figure 8H shows, thus contributing to the formation of a more complete and integral conducting network of FG/EGs, which effectively improved the electrical conductivity. Compared with the BC-BPs without any MWCNTs added as a conductive filler (289.37 S/cm), the conductivity was 334.57 S/cm at 2% addition and 342.49 S/cm at 2.5% addition for I-CBPs. The conductivity of C-CBPs with the direct addition of MWCNTs showed an increasing trend followed by a decreasing trend. This was because, although the direct addition of MWCNTs, followed by mechanical dispersion, can form a conductive pathway inside the BPs, this dispersion effect was not sufficient to completely disperse the MWCNTs into a homogeneous conductive network and can not be totally wetted, as Figure 8F shows. When too many MWCNTs were added, agglomerated micron-sized particles were formed, as shown in Figure 8J,K, which were less compatible with the resin and had a looser internal structure; instead, it left a lot of pores and gaps, thus having a negative effect on conductivity enhancement [46,47].
The results of the flexural strength tests of BPs are shown in Figure 7B. For I-CBPs, the flexural strength rose with low CNT content and decreased with high CNT content, and the best flexural strength was achieved under the condition that the mass fraction of MWCNTs was 2%, and its flexural strength could reach 50.24 MPa. MWCNTs as nano-fillers have a good strengthening effect on EG, and the surface-grown MWCNTs can not only make the contact points between graphite particles increase and make the graphite surface rougher [48] but also fills the pores of the matrix [49]. CNTs with the right content have a good strengthening effect on EG. However, this improvement effect is not unlimited; for I-CBPs, the excessive addition of in situ deposited MWCNTs will still form agglomeration, although the tendency is lower compared to C-CBPs, and the excessive CNTs were difficult to be wetted, thus generating a large number of voids and air residue, which was unfavorable to the improvement of the mechanical properties of composite BPs [50,51]. As shown in Figure 8F,I, the cross-sectional SEM image of BPs shows the particles formed by the agglomeration of MWCNTs; this agglomeration of brittle large particles for the stress-bearing effect is completely inferior to the uniformly dispersed network of MWCNTs. For C-CBPs, with low MWCNT content, MWCNTs could be dispersed inside the material, so the mechanical properties increased, but as the MWCNT content increased, MWCNTs agglomerate into particles. As the CNT content rose to a threshold value, the mechanical properties of the material decreased, which was consistent with previous reports in the literature [52]. CNTs that underwent agglomeration not only had poor mechanical properties but also poor compatibility with the resin phase, which led to an increase in defects and a decrease in flexural strength.
The results of the thermal conductivity measurement by hotdisk are shown in Figure 7C. The results are similar to those of the conductivity test, but the difference is that the intrinsic thermal conductivity was high for both the deposited CNTs and the directly added CNTs, so the improvement effectiveness for the thermal conductivity of the composite BPs was huge. Compared with BC-BPs, the introduction of small amounts of CNTs as secondary fillers can improve the electrical conductivity of carbon fiber or graphite-filled polymers. This was due to the small size, high aspect ratio and low permeation threshold of carbon nanotubes. CNTs can form secondary permeation networks and also act as bridges and fill small gaps between larger primary fillers, enhancing the thermal conductivity of composite BPs [53,54,55].
In order to investigate the effect of in situ deposited MWCNTs on the surface morphology and contact resistance of BPs in more depth, several groups of BPs with good overall performance were selected for ASR tests with different pressures, as Figure 7D shows. The ASR mainly includes the conductivity of the composite BPs themselves and the ICR with GDL. Previous studies have shown that MWCNTs had a positive effect on the conductivity of composite BPs, and, although the addition of MWCNTs caused the graphite part of the surface of the composite BPs to become rough, the ASR was tested under pressurized conditions, when the surface-dispersed reticular high-conductivity MWCNTs will fully play a role in reducing the ICR with GDL. For C-CBPs, the conductive effect of agglomerated CNTs was weakened, so the improvement was not as good as that of I-CBPs. As the content of CNTs increased, more and more CNTs were difficult to be wetted, which also had a negative effect on ASR [56]. On the other hand, molded composites often have an enriched layer of resin on the surface due to extrusion [57], which is extremely detrimental to ASR. In the composite BPs with CNTs added, the CNTs moved to the surface of the composite BPs with the resin, which also led to the decrease in the ASR of the composite BPs, as shown in Figure 8C,L.
The hydrogen permeability of the composite BPs is shown in Figure 7E. In order to investigate more deeply the filling effect of different forms of MWCNTs on the pores of the composite BPs and the mechanism of improving the gas tightness, I-CBPs-G80R20CNT2 and C-CBPs-G80R20CNT2, BC-BPs were selected for nitrogen adsorption–desorption tests, and the porosity was calculated according to the DFT method using the adsorption–desorption curve. The results are shown in Figure 9. The results show that the gas permeability of I-CBPs was lower and continues to decrease with increasing CNT content and was lower compared to C-CBPs, and the hydrogen permeability can meet the DOE requirements when the filling amount is greater than or equal to 2%. Combined with Figure 9, it can be found that the in situ deposited CNTs filled the pores well at all porosities, while C-CBPs had a better filling effect for large pores above 150 nm but almost no filling effect at all for pores between 50 and 100 nm. This may be because, compared with I-CBPs, the CNTs inside C-CBPs may be due to agglomeration, which makes it difficult to fill the surface of EG particles and the tiny pores between EG, FG and resin, but a small number of MWCNTs were still dispersed during the preparation process, so they can play a similar filling role as I-CBPs for the pores between 0~50 nm [58,59,60]. Therefore, the pores between 0~50 nm can be filled similarly to I-CBPs, although the effect is not as good as that of I-CBPs.
Hydrophobicity has a significant impact on the role of BPs in playing a key role in hydrothermal management. As mentioned earlier, for I-CBPs, the MWCNTs deposited in situ filled the pores of EGs well, thus making the surface more structurally complete with fewer defects. This led to the improvement of the hydrophobicity of BPs, but the opposite effect was observed for agglomerated MWCNTs. As the content of MWCNTs gradually became higher, it can reach 110.24°, as Figure 7F shows. As discussed in the ASR results, MWCNTs were able to be on the surface of composite BPs, but, due to compatibility and inability to be wetted, it reduced ASR and increased the conductive pathway on the surface; on the other hand, excessive MWCNTs led to cracks and defects on the surface. This was illustrated by the presence of a large number of MWCNTs in the cracks, as Figure 8C,L shows. For C-CBPs, the agglomeration is stronger and the dispersion was lower, so the improvement of the hydrophobicity of BPs was not as good as that of I-CBPs. In addition, it was shown that the increase in hydrophobicity was also related to the increase in the surface roughness of composite BPs and the increase in the exposure rate of graphite [60], while the SEM images of composite BPs showed that the surface of graphite deposited with CNTs had a fluff-like structure, which could improve the surface roughness of graphite.
Based on the previous ASR tests, the samples were tested for electrochemical corrosion, and the corrosion currents of the different samples were derived from Tafel curves, as Figure 10A,B shows. Due to the high corrosion resistance of the selected PEEK resin, all parts had good corrosion resistance. From the results of the corrosion resistance tests, I-CBP and C-CBP were found to meet DOE requirements. Since the corrosion current density was calculated using the surface area of the sample as a constant, when there are many defects and cracks on the surface of the sample, the actual contact area between the sample and the corrosion solution increases, resulting in an increase in the corrosion current [61,62]. The in situ deposited MWCNTs filled the defects and thus reduced the corrosion current density, while the agglomerated particles of C-CBPs are inherently porous and sparse in structure, which also led to an increase in the porosity of BPs and thus had less effect on reducing the corrosion current density than I-CBPs. As discussed in the chapter on hydrophobicity, MWCNTs have both a filling effect on the surface of the composite BPs and may increase their surface defects, the actual effect depending on which one prevails. So the trend of their corrosion current also decreased first and then increased with the increase in MWCNT content. The results of the constant potential polarization tests, as Figure 10C,D shows, also shows that the in situ deposited CNTs favored the reduction of corrosion currents in both cathodic and anodic simulated environments due to the dominant filling effect, while the direct addition of commercial CNTs accelerated corrosion, which is also consistent with previous reports in the literature. The test results in the constant current method show that the effect of increasing corrosion current dominated when the content of CNTs exceeded 2% in the C-CBPs group, so the corrosion resistance decreases continuously, as the content of CNTs continued to rise, and this trend of decreasing corrosion current first as the filler increases was also consistent with the previous literature studying the corrosion effect of bipolar plates [61,62,63]. In summary, thanks to the chemical inertness of PEEK resin and carbon materials, all samples showed good stability in the PEMFC simulation environment with pH = 1, and their lower corrosion current densities indicated that the materials were in the operating environment of PEMFC. It has good chemical stability and will not corrode because the pH value is too low.

4. Conclusions

The purpose of this study is to construct composite BPs with uniform conductive networks using in situ deposited MWCNTs assisted by FG and EG. The conductive pathways were constructed by reasonably controlling the ratio of EG and FG, and the BPs were enhanced by in situ deposited MWCNTs. Due to the advance dispersion of catalyst particles for deposition and controlled reaction temperature, uniformly dispersed network-like MWCNTs were obtained, which could play the role of filling pores and reducing micropores in the composite BPs, making the conductive network structure more perfect, so that highly conductive, high-strength and corrosion-resistant BPs can be obtained. Thanks to the characteristics of the CVD method, the deposited MWCNTs exhibited a uniform network-like structure and were dispersed on the surface of the graphite particles and within the defects. For the best I-CBPs-G80R20CNT2, the conductivity can reach 334.57 S/cm and the flexural strength 50.24 MPa. The corrosion resistance, hydrogen transmission rate, contact resistance and corrosion current density can meet the DOE standard by 2025. In addition, since in situ deposited MWCNTs are uniformly dispersed, only a small amount of addition is required to meet the demand, and the CVD method is one of the mainstream methods for preparing MWCNTs, so it is one of the candidates for composite BPs that can be produced in batches. Compared with the previously used method of the direct addition of CNTs, the in situ deposition of CNTs by CVD is not only beneficial to the performance of composite BPs and avoids the agglomeration problem often faced by nanofillers but also can effectively reduce the cost of composite BPs.

Author Contributions

Conceptualization, Z.X. and W.L.; methodology, M.L.; validation, W.L. and H.Z.; formal analysis, W.L.; investigation, M.L.; resources, Z.X. and S.Q.; data curation, Z.X. and W.L.; writing—original draft preparation, W.L. and G.W.; writing—review and editing, W.L. and Z.X.; supervision, Z.X.; project administration, Z.X. and S.Q.; funding acquisition, Z.X. and G.W. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the National Key Research and Development Program of China, grant number 2018YFB1502504.

Data Availability Statement

Data available on request due to restrictions, e.g., privacy or ethical. The data presented in this study are available on request from the corresponding author.

Acknowledgments

This work was financially supported by Tong Ji University.

Conflicts of Interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

References

  1. Habib, S.; Arefin, P.; Salam, A.; Ahmed, K.; Uddin, S.; Hossain, T.; Papri, N.; Islam, T. Proton Exchange Membrane Fuel Cell (PEMFC) Durability Factors, Challenges, and Future Perspectives: A Detailed Review. J. Inf. Secur. Res. Int. Res. J. Mater. Sci. 2020, 18, 217–234. [Google Scholar] [CrossRef]
  2. Lü, X.; Qu, Y.; Wang, D.; Qin, C.; Liu, G. A comprehensive review on hybrid power system for PEMFC-HEV: Issues and strategies. Energy Convers. Manag. 2018, 171, 1273–1291. [Google Scholar] [CrossRef]
  3. Song, Y.; Zhang, C.; Ling, C.-Y.; Han, M.; Yong, R.-Y.; Sun, D.; Chen, J. Review on current research of materials, fabrication and application for bipolar plate in proton exchange membrane fuel cell. Int. J. Hydrog. Energy 2020, 45, 29832–29847. [Google Scholar] [CrossRef]
  4. Liao, W.; Jiang, F.; Zhang, Y.; Zhou, X.; He, Z. Highly-conductive composite bipolar plate based on ternary carbon materials and its performance in redox flow batteries. Renew. Energy 2020, 15, 1310–1316. [Google Scholar] [CrossRef]
  5. Wu, S.; Yang, W.; Yan, H.; Zuo, X.; Cao, Z.; Li, H.; Shi, M.; Chen, H. A review of modified metal bipolar plates for proton exchange membrane fuel cells. Int. J. Hydrog. Energy 2021, 16, 8672–8701. [Google Scholar] [CrossRef]
  6. Zhang, Q.; Tong, Z.; Tong, S.; Cheng, Z. Research on water and heat management in the cold start process of proton exchange membrane fuel cell with expanded graphite bipolar plate. Energy Convers. Manag. 2021, 233, 113942. [Google Scholar] [CrossRef]
  7. Bauer, A.; Härtel, S.; Awiszus, B. Manufacturing of Metallic Bipolar Plate Channels by Rolling. J. Manuf. Mater. Process. 2019, 3, 48. [Google Scholar] [CrossRef] [Green Version]
  8. Che, J.; Yi, P.; Peng, L.; Lai, X. Impact of pressure on carbon films by PECVD toward high deposition rates and high stability as metallic bipolar plate for PEMFCs. Int. J. Hydrog. Energy 2020, 45, 16277–16286. [Google Scholar] [CrossRef]
  9. Yi, P.; Zhang, D.; Qiu, D.; Peng, L.; Lai, X. Carbon-based coatings for metallic bipolar plates used in proton exchange membrane fuel cells. Int. J. Hydrog. Energy 2019, 14, 6813–6843. [Google Scholar] [CrossRef]
  10. Madadi, F.; Rezaeian, A.; Edris, H.; Zhiani, M. Improving performance in PEMFC by applying different coatings to metallic bi-polar plates. Mater. Chem. Phys. 2019, 238, 121911. [Google Scholar] [CrossRef]
  11. Alaefour, I.; Shahgaldi, S.; Zhao, J.; Li, X. Synthesis and Ex-Situ characterizations of diamond-like carbon coatings for metallic bipolar plates in PEM fuel cells. Int. J. Hydrog. Energy 2021, 46, 11059–11070. [Google Scholar] [CrossRef]
  12. Mathew, C.; Mohamed, S.N.; Devanathan, L.S. A comprehensive review of current research on various materials used for developing composite bipolar plates in polymer electrolyte membrane fuel cells. Polym. Compos. 2022, 43, 4100–4114. [Google Scholar] [CrossRef]
  13. Jiang, F.; Liao, W.; Ayukawa, T.; Yoon, S.-H.; Nakabayashi, K.; Miyawaki, J. Enhanced performance and durability of composite bipolar plate with surface modification of cactus-like carbon nanofibers. J. Power Sources 2021, 482, 228903. [Google Scholar] [CrossRef]
  14. Lee, D.; Lim, J.W.; Gil Lee, D. Cathode/anode integrated composite bipolar plate for high-temperature PEMFC. Compos. Struct. 2017, 167, 144–151. [Google Scholar] [CrossRef]
  15. Mathur, R.; Dhakate, S.; Gupta, D.; Dhami, T.; Aggarwal, R. Effect of different carbon fillers on the properties of graphite composite bipolar plate. J. Mater. Process. Technol. 2007, 203, 184–192. [Google Scholar] [CrossRef]
  16. Hu, B.; Chen, L.; Guo, C.; He, G.; Cao, X.; Yin, X. Constructing three-dimensional conductive network in composite bipolar plates by sacrificial materials for improvement of proton exchange membrane fuel cell performance. J. Power Sources 2022, 552, 232261. [Google Scholar] [CrossRef]
  17. Lee, M.H.; Kim, H.Y.; Oh, S.M.; Kim, B.C.; Bang, D.; Han, J.T.; Woo, J.S. Structural optimization of graphite for high-performance fluorinated ethylene–propylene composites as bipolar plates. Int. J. Hydrog. Energy 2018, 43, 21918–21927. [Google Scholar] [CrossRef]
  18. Kuan, Y.-D.; Ciou, C.-W.; Shen, M.-Y.; Wang, C.-K.; Fitriani, R.Z.; Lee, C.-Y. Bipolar plate design and fabrication using graphite reinforced composite laminate for proton exchange membrane fuel cells. Int. J. Hydrog. Energy 2021, 46, 16801–16814. [Google Scholar] [CrossRef]
  19. Phuangngamphan, M.; Okhawilai, M.; Hiziroglu, S.; Rimdusit, S. Development of highly conductive graphite-/graphene-filled polybenzoxazine composites for bipolar plates in fuel cells. J. Appl. Polym. Sci. 2019, 136, 47183. [Google Scholar] [CrossRef]
  20. Liu, Z.; Wang, B.; Yu, L. Preparation and surface modification of PVDF-carbon felt composite bipolar plates for vanadium flow battery. J. Energy Chem. 2018, 27, 1369–1375. [Google Scholar] [CrossRef]
  21. Hu, B.; He, G.; Chang, F.; Yang, H.; Cao, X.; Yin, X. Low filler and highly conductive composite bipolar plates with synergistic segregated structure for enhanced proton exchange membrane fuel cell performance. Energy 2022, 251, 123982. [Google Scholar] [CrossRef]
  22. Fan, R.; Zheng, J.; Peng, Y.; Chen, J.; Zhan, Z.; Yao, D.; Zhang, C.; Ming, P. The conductive network optimization of composite graphite plates and its morphological analysis. Chem. Eng. J. 2022, 446, 136652. [Google Scholar] [CrossRef]
  23. Zheng, J.; Peng, Y.; Fan, R.; Chen, J.; Zhan, Z.; Yao, D.; Ming, P. Study on carbon matrix composite bipolar plates with balance of conductivity and flexural strength. Chin. Chem. Lett. 2022, in press. [Google Scholar] [CrossRef]
  24. Li, W.; Zeng, H.; Peng, T.; Gao, Z.; Xie, Z. A High Conductive Composite Bipolar Plate with Conductive Network Constructed by Chemical Vapor Deposition. Energies 2022, 15, 4979. [Google Scholar] [CrossRef]
  25. Dhakate, S.R.; Mathur, R.B.; Kakati, B.K.; Dhami, T.L. Properties of graphite-composite bipolar plate prepared by compression molding technique for PEM fuel cell. Int. J. Hydrog. Energy 2007, 32, 4537–4543. [Google Scholar] [CrossRef]
  26. Radzuan, N.A.M.; Sulong, A.B.; Somalu, M.R.; Abdullah, A.T.; Husaini, T.; Rosli, R.E.; Majlan, E.H.; Rosli, M.I. Fibre orientation effect on polypropylene/milled carbon fiber composites in the presence of carbon nanotubes or graphene as a secondary filler: Application on PEM fuel cell bipolar plate. Int. J. Hydrog. Energy 2019, 44, 30618–30626. [Google Scholar] [CrossRef]
  27. Zhang, H.Y.; Yang, X.D.; Liu, X.J.; Wang, T. Preparation of CF Reinforced PPS/Graphite Conductive Composite for Bipolar Plate. Adv. Mater. 2014, 2949, 1425–1429. [Google Scholar] [CrossRef]
  28. Chen, C.-K.; Kuo, J.-K. Nylon 6/CB polymeric conductive plastic bipolar plates for PEM fuel cells. J. Nanomater. 2015, 101, 3415–3421. [Google Scholar] [CrossRef]
  29. Yao, K.; Adams, D.; Hao, A.; Zheng, J.P.; Liang, Z.; Nguyen, N. Highly conductive and strong graphite-phenolic resin composite for bipolar plate applications. Energy Fuels 2017, 31, 14320–14331. [Google Scholar] [CrossRef]
  30. Kirkpatrick, S. Percolation and Conduction. Rev. Mod. Phys. 1973, 45, 574–588. [Google Scholar] [CrossRef]
  31. Radzuan, N.A.M.; Sulong, A.B.; Husaini, T.; Majlan, E.H.; Rosli, M.I.; Aman, M.F. Fabrication of multi-filler MCF/MWCNT/SG-based bipolar plates. Ceram. Int. 2019, 45, 7413–7418. [Google Scholar] [CrossRef]
  32. Alo, O.A.; Otunniyi, I.O.; Pienaar, H.; Sadiku, E.R. Electrical and mechanical properties of polypropylene/epoxy blend-graphite/carbon black composite for proton exchange membrane fuel cell bipolar plate. Mater. Today Proc. 2021, 38, 658–662. [Google Scholar] [CrossRef]
  33. Rigail, C.A.F.; Espinoza, A.M.; Medina, A.J.; Leal, Z.K. Expanded Graphite/Epoxy/Aliphatic Amine Composites for Bipolar Plates Applications in Polymer Electrolyte Fuel Cells. KEM 2019, 821, 426–432. [Google Scholar] [CrossRef]
  34. Akhtar, M.N.; Sulong, A.B.; Umer, A.; Bin Yousaf, A.; Khan, M.A. Multi-component MWCNT/NG/EP-based bipolar plates with enhanced mechanical and electrical characteristics fabricated by compression moulding. Ceram. Int. 2018, 44, 14457–14464. [Google Scholar] [CrossRef]
  35. Rubel, R.I.; Ali, H.; Jafor, A.; Alam, M. Carbon nanotubes agglomeration in reinforced composites: A review. AIMS Mater. Sci. 2019, 6, 756–780. [Google Scholar] [CrossRef]
  36. Ayodele, O.O.; Awotunde, M.A.; Babalola, B.J.; Olubambi, P.A. The influence of dispersion time on the mechanical properties of spark plasma–sintered carbon nanotubes reinforced nickel-aluminum matrix composites. Int. J. Adv. Manuf. Technol. 2022, 120, 4113–4122. [Google Scholar] [CrossRef]
  37. Olszówka-Myalska, A.; Wrześniowski, P.; Myalska-Głowacka, H.; Maziarz, W.; Godzierz, M. Multiwalled carbon nanotubes as an additive to Mg-Mg2Si in situ composite obtained by powder sintering. J. Alloys Compd. 2023, 931, 167548. [Google Scholar] [CrossRef]
  38. Mittal, G.; Rhee, K.Y. Chemical vapor deposition-based grafting of CNTs onto basalt fabric and their reinforcement in epoxy-based composites. Compos. Sci. Technol. 2018, 165, 84–94. [Google Scholar] [CrossRef]
  39. Xu, K.; Chen, X.; Zhou, H.; Bi, L.; Fu, S.; Li, W.; Liu, X.; Ma, F.; Zhang, K.; Liu, P. Preparation and formation mechanism of CNTs/Cu-Al2O3 composite powders by in situ CVD using internally-oxidized Cu-Al alloy powders. Mater. Lett. 2019, 254, 390–393. [Google Scholar] [CrossRef]
  40. Kong, L.; Qi, J.; Li, M.; Chen, X.; Yuan, X.; Wang, T.; Yang, J.; Huang, J.; Fan, X. Electromagnetic wave absorption properties of Ti3C2Tx nanosheets modified with in-situ growth carbon nanotubes. Carbon 2021, 183, 322–331. [Google Scholar] [CrossRef]
  41. Li, W.; Wen, J.; Ren, Z. Effect of temperature on growth and structure of carbon nanotubes by chemical vapor deposition. Appl. Phys. A 2002, 74, 397–402. [Google Scholar] [CrossRef]
  42. Gupta, N.; Gupta, S.M.; Sharma, S.K. Carbon nanotubes: Synthesis, properties and engineering applications. Carbon Lett. 2019, 29, 419–447. [Google Scholar] [CrossRef]
  43. Zhang, B.; Tian, Y.; Jin, X.; Lo, T.; Cui, H. Thermal and Mechanical Properties of Expanded Graphite/Paraffin Gypsum-Based Composite Material Reinforced by Carbon Fiber. Materials 2018, 11, 2205. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  44. Zhang, Z.; Fang, X. Study on paraffin/expanded graphite composite phase change thermal energy storage material. Energy Convers. Manag. 2006, 47, 303–310. [Google Scholar] [CrossRef]
  45. Karaipekli, A.; Biçer, A.; Sarı, A.; Tyagi, V.V. Thermal characteristics of expanded perlite/paraffin composite phase change material with enhanced thermal conductivity using carbon nanotubes. Energy Convers. Manag. 2017, 134, 373–381. [Google Scholar] [CrossRef]
  46. Bairan, A.; Selamat, M.Z.; Sahadan, S.N.; Malingam, S.A.; Mohamad, N. Effect of CNTS on the electrical and mechanical properties of polymeric composite as pem fuel cell bipolar plate. J. Teknol. 2018, 80, 115–122. [Google Scholar] [CrossRef] [Green Version]
  47. Naji, A.; Krause, B.; Pötschke, P.; Ameli, A. Extruded polycarbonate/Di-Allyl phthalate composites with ternary conductive filler system for bipolar plates of polymer electrolyte membrane fuel cells. Smart Mater. Struct. 2019, 28, 064004. [Google Scholar] [CrossRef]
  48. Boroujeni, A.Y.; Al-Haik, M.S. Interlaminar fracture toughness of hybrid carbon fiber-carbon nanotubes-reinforced polymer composites. Polym. Compos. 2019, 40, E1470–E1478. [Google Scholar] [CrossRef]
  49. Chan, K.; Zaid, M.; Mamat, S.; Liza, S.; Tanemura, M.; Yaakob, Y. Recent Developments in Carbon Nanotubes-Reinforced Ceramic Matrix Composites: A Review on Dispersion and Densification Techniques. Crystals 2021, 11, 457. [Google Scholar] [CrossRef]
  50. Taherian, R. RETRACTED: A review of composite and metallic bipolar plates in proton exchange membrane fuel cell: Materials, fabrication, and material selection. J. Power Sources 2014, 265, 370–390. [Google Scholar] [CrossRef]
  51. Witpathomwong, S.; Okhawilai, M.; Jubsilp, C.; Karagiannidis, P.; Rimdusit, S. Highly filled graphite/graphene/carbon nanotube in polybenzoxazine composites for bipolar plate in PEMFC. Int. J. Hydrog. Energy 2020, 45, 30898–30910. [Google Scholar] [CrossRef]
  52. Younas, T. Chapter 4—Bipolar plates for the permeable exchange membrane: Carbon nanotubes as an alternative. In PEM Fuel Cells; Kaur, G., Ed.; Elsevier: London, UK, 2021; pp. 71–89. [Google Scholar] [CrossRef]
  53. Dhakate, S.R.; Sharma, S.; Chauhan, N.; Seth, R.K.; Mathur, R.B. CNTs nanostructuring effect on the properties of graphite composite bipolar plate. Int. J. Hydrog. Energy 2010, 35, 4195–4200. [Google Scholar] [CrossRef] [Green Version]
  54. Tariq, M.; Syed, N.A.; Behravesh, A.H.; Pop-Iliev, R.; Rizvi, G. Synergistic enrichment of electrically conductive polypropylene-graphite composites for fuel cell bipolar plates. Int. J. Energy Res. 2022, 46, 10955–10964. [Google Scholar] [CrossRef]
  55. Darıcık, F.; Topcu, A.; Aydın, K.; Çelik, S. Carbon nanotube (CNT) modified carbon fiber/epoxy composite plates for the PEM fuel cell bipolar plate application. Int. J. Hydrog. Energy 2022, 48, 1090–1106. [Google Scholar] [CrossRef]
  56. Hu, B.; Chang, F.-L.; Xiang, L.-Y.; He, G.-J.; Cao, X.-W.; Yin, X.-C. High performance polyvinylidene fluoride/graphite/multi-walled carbon nanotubes composite bipolar plate for PEMFC with segregated conductive networks. Int. J. Hydrog. Energy 2021, 46, 25666–25676. [Google Scholar] [CrossRef]
  57. Seraji, A.A.; Aghvami-Panah, M.; Zadhoush, A.; Salimian, S.; Khoshnevis, H. Microstructural design and mechanical performance of epoxy/carbon nanotube fiber composite. J. Compos. Mater. 2022, 56, 3591–3602. [Google Scholar] [CrossRef]
  58. Hyeong, S.; Park, M.; Kim, S.; Park, S.; Choi, K.; Im, M.J.; Kim, N.D.; Kim, T.; Lee, S.H.; Park, J.; et al. Compacted Laser-Induced Graphene with Bamboo-Like Carbon Nanotubes for Transformable Capacitive Energy Storage Electrodes. Adv. Mater. Technol. 2022, 7, 2101105. [Google Scholar] [CrossRef]
  59. Li, M.; Chen, S.; Li, B.; Huang, Y.; Lv, X.; Sun, P.; Fang, L.; Sun, X. In situ growing N and O co-doped helical carbon nanotubes encapsulated with CoFe alloy as tri-functional electrocatalyst applied in Zn–Air Batteries driving Water Splitting. Electrochim. Acta 2021, 388, 138587. [Google Scholar] [CrossRef]
  60. Madadi, F.; Rezaeian, A.; Edris, H.; Zhiani, M. Influence of surface roughness and hydrophobicity of bipolar plates on PEM performance. Surf. Coat. Technol. 2020, 389, 125676. [Google Scholar] [CrossRef]
  61. de Oliveira, M.C.L.; Ett, G.; Antunes, R.A. Corrosion and thermal stability of multi-walled carbon nanotube–graphite–acrylonitrile–butadiene–styrene composite bipolar plates for polymer electrolyte membrane fuel cells. J. Power Sources 2013, 211, 345–355. [Google Scholar] [CrossRef] [Green Version]
  62. Ramírez-Herrera, C.; Tellez-Cruz, M.; Pérez-González, J.; Solorza-Feria, O.; Flores-Vela, A.; Cabañas-Moreno, J. Enhanced mechanical properties and corrosion behavior of polypropylene/multi-walled carbon nanotubes/carbon nanofibers nanocomposites for application in bipolar plates of proton exchange membrane fuel cells. Int. J. Hydrog. Energy 2021, 46, 26110–26125. [Google Scholar] [CrossRef]
  63. Antunes, R.A.; de Oliveira, M.C.L.; Ett, G. Investigation on the corrosion resistance of carbon black–graphite-poly(vinylidene fluoride) composite bipolar plates for polymer electrolyte membrane fuel cells. Int. J. Hydrog. Energy 2011, 36, 12474–12485. [Google Scholar] [CrossRef]
Nanomaterials 13 00365 g001 550
Figure 1. Schematic diagram of the preparation and structure of composite BPs.
Figure 1. Schematic diagram of the preparation and structure of composite BPs.
Nanomaterials 13 00365 g001
Nanomaterials 13 00365 g002 550
Figure 2. (A) Four-probe equipment and schematic diagram; (B) ICR testing equipment and schematic diagram; (C) hydrogen permeability testing equipment.
Figure 2. (A) Four-probe equipment and schematic diagram; (B) ICR testing equipment and schematic diagram; (C) hydrogen permeability testing equipment.
Nanomaterials 13 00365 g002
Nanomaterials 13 00365 g003 550
Figure 3. SEM images of MWCNTs prepared at different temperatures: (A) CNT750; (B) CNT780; (C) CNT810; (D) CNT840; (E) CNT870; (F) CNT900.
Figure 3. SEM images of MWCNTs prepared at different temperatures: (A) CNT750; (B) CNT780; (C) CNT810; (D) CNT840; (E) CNT870; (F) CNT900.
Nanomaterials 13 00365 g003
Nanomaterials 13 00365 g004 550
Figure 4. TEM images of MWCNTs prepared at different temperatures: (A) CNT750; (B) CNT780; (C) CNT810; (D) CNT840; (E) CNT870; (F) CNT900; (G) Raman spectra of MWCNTs prepared at different temperatures; (H) XRD of MWCNTs prepared at different temperatures.
Figure 4. TEM images of MWCNTs prepared at different temperatures: (A) CNT750; (B) CNT780; (C) CNT810; (D) CNT840; (E) CNT870; (F) CNT900; (G) Raman spectra of MWCNTs prepared at different temperatures; (H) XRD of MWCNTs prepared at different temperatures.
Nanomaterials 13 00365 g004
Nanomaterials 13 00365 g005 550
Figure 5. Electrical conductivity and flexural strength of composite BPs prepared from MWCNTs at different temperatures.
Figure 5. Electrical conductivity and flexural strength of composite BPs prepared from MWCNTs at different temperatures.
Nanomaterials 13 00365 g005
Nanomaterials 13 00365 g006 550
Figure 6. (A,B) SEM images of the composite BPs prepared by EG and FG; (C) effect of different ratios of EG and FG on ICR; (D) effect of different ratios of EG and FG on the performance of BPs.
Figure 6. (A,B) SEM images of the composite BPs prepared by EG and FG; (C) effect of different ratios of EG and FG on ICR; (D) effect of different ratios of EG and FG on the performance of BPs.
Nanomaterials 13 00365 g006
Nanomaterials 13 00365 g007 550
Figure 7. Effect of MWCNTs content and addition method on the performance of BPs: (A) in-plane conductivity; (B) flexural strength; (C) thermal conductivity; (D) area-specific resistance; (E) gas permeability; (F) contact angle.
Figure 7. Effect of MWCNTs content and addition method on the performance of BPs: (A) in-plane conductivity; (B) flexural strength; (C) thermal conductivity; (D) area-specific resistance; (E) gas permeability; (F) contact angle.
Nanomaterials 13 00365 g007
Nanomaterials 13 00365 g008 550
Figure 8. Surface morphology of composite bipolar plate: (A) BC-BPs; (B) I-CBPs; (C) C-CBPs; FESEM diagram of composite bipolar plate cross-section: (D) BC-BPs; (E) I-CBPs; (F) C-CBPs; (G) In situ deposited MWCNTs formed a network-like structure; (H) in situ deposited MWCNTs filled the pores of EG; (I) excess in situ deposited MWCNTs agglomerated inside BPs; (J,K) agglomerated MWCNTs particles inside C-CBPs; (L) surface morphology of BPs with crack.
Figure 8. Surface morphology of composite bipolar plate: (A) BC-BPs; (B) I-CBPs; (C) C-CBPs; FESEM diagram of composite bipolar plate cross-section: (D) BC-BPs; (E) I-CBPs; (F) C-CBPs; (G) In situ deposited MWCNTs formed a network-like structure; (H) in situ deposited MWCNTs filled the pores of EG; (I) excess in situ deposited MWCNTs agglomerated inside BPs; (J,K) agglomerated MWCNTs particles inside C-CBPs; (L) surface morphology of BPs with crack.
Nanomaterials 13 00365 g008
Nanomaterials 13 00365 g009 550
Figure 9. Results of BET DFT and the filling effect of different morphologies of MWCNTs on the pore space.
Figure 9. Results of BET DFT and the filling effect of different morphologies of MWCNTs on the pore space.
Nanomaterials 13 00365 g009
Nanomaterials 13 00365 g010 550
Figure 10. (A) Tafel curves of composite BPs; (B) corrosion current density of composite BPs; (C) constant potential polarization method to simulate PEMFC cathodic environment; (D) constant potential polarization method to simulate PEMFC anodic environment.
Figure 10. (A) Tafel curves of composite BPs; (B) corrosion current density of composite BPs; (C) constant potential polarization method to simulate PEMFC cathodic environment; (D) constant potential polarization method to simulate PEMFC anodic environment.
Nanomaterials 13 00365 g010
Table
Table 1. Ratio(wt%) of EG, FG and resin for different samples.
Table 1. Ratio(wt%) of EG, FG and resin for different samples.
SampleExpanded Graphite
wt%		Flake Graphite
wt%		Resin
wt%
FG80R200%80%20%
EG20FG60R2020%60%20%
EG40FG40R2040%40%20%
EG60FG20R2060%20%20%
EG80R2080%0%20%
Table
Table 2. Ratio(wt%) of graphite and MWCNTs for different samples.
Table 2. Ratio(wt%) of graphite and MWCNTs for different samples.
GroupsSampleGraphite
wt%		Resin
wt%		In Situ Deposited MWCNTs
wt%		Commercial MWCNTs
wt%
I-CBPsG80R20CNT0.580%20%0.5%0
G80R20CNT180%20%1%0
G80R20CNT1.580%20%1.5%0
G80R20CNT280%20%2%0
G80R20CNT2.580%20%2.5%0
C-CBPsG80R20CNT0.580%20%00.5%
G80R20CNT180%20%01%
G80R20CNT1.580%20%01.5%
G80R20CNT280%20%02%
G80R20CNT2.580%20%02.5%
BC-BPsG80R2080%20%00
Table
Table 3. Performance of composite BPs.
Table 3. Performance of composite BPs.
GroupsSampleElectrical Conductivity
/S·cm−1		Flexural Strength
/MPa		Thermal Conductivity
/W·(mK)−1		Hydrogen Permeability
/10−7cm3·(cm2·s)−1		Contact Angle
I-CBPsG80R20CNT0.5298.8840.2626.625.6397.25
G80R20CNT1309.5743.3732.483.22102.37
G80R20CNT1.5322.1647.2536.652.02105.56
G80R20CNT2334.5750.2438.061.66108.79
G80R20CNT2.5342.4944.5339.721.76110.24
C-CBPsG80R20CNT0.5296.5341.0325.16.6796.14
G80R20CNT1306.6242.3629.364.3498.56
G80R20CNT1.5310.2740.5631.253.21101.27
G80R20CNT2308.5442.2833.263.11102.56
G80R20CNT2.5300.1039.8634.572.88102.03
BC-BPsG80R20289.3739.3724.256.9394.47
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Li, W.; Xie, Z.; Qiu, S.; Zeng, H.; Liu, M.; Wu, G. Improved Performance of Composite Bipolar Plates for PEMFC Modified by Homogeneously Dispersed Multi-Walled Carbon Nanotube Networks Prepared by In Situ Chemical Deposition. Nanomaterials 2023, 13, 365. https://doi.org/10.3390/nano13020365

AMA Style

Li W, Xie Z, Qiu S, Zeng H, Liu M, Wu G. Improved Performance of Composite Bipolar Plates for PEMFC Modified by Homogeneously Dispersed Multi-Walled Carbon Nanotube Networks Prepared by In Situ Chemical Deposition. Nanomaterials. 2023; 13(2):365. https://doi.org/10.3390/nano13020365

Chicago/Turabian Style

Li, Wenkai, Zhiyong Xie, Shi Qiu, Haodong Zeng, Minqi Liu, and Gangsheng Wu. 2023. "Improved Performance of Composite Bipolar Plates for PEMFC Modified by Homogeneously Dispersed Multi-Walled Carbon Nanotube Networks Prepared by In Situ Chemical Deposition" Nanomaterials 13, no. 2: 365. https://doi.org/10.3390/nano13020365

APA Style

Li, W., Xie, Z., Qiu, S., Zeng, H., Liu, M., & Wu, G. (2023). Improved Performance of Composite Bipolar Plates for PEMFC Modified by Homogeneously Dispersed Multi-Walled Carbon Nanotube Networks Prepared by In Situ Chemical Deposition. Nanomaterials, 13(2), 365. https://doi.org/10.3390/nano13020365

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.