Influence of Substituents in Terephthalate Linker on the Structure of MOFs Obtained from Presynthesized Heterometallic Complex
Previous Article in Journal
Investigating the Factors Affecting the Ionic Conduction in Nanoconfined NaBH4
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Inorganics
Volume 9
Issue 1
10.3390/inorganics9010003
inorganics-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effect of Silane Functionalization on Properties of Poly(Lactic Acid)/Palygorskite Nanocomposites

by
Anton Kasprzhitskii
1,2,
Georgy Lazorenko
1,2,*,
Alexander Kruglikov
1,
Irina Kuchkina
3 and
Vadim Gorodov
4
1
Department of Physics, Rostov State Transport University, Narodnogo Opolcheniya Sq., 344038 Rostov-on-Don, Russia
2
Mineralica Limited Liability Company, Skolkovo Innovation Center, 42 Bolshoy Boulevard, 121205 Moscow, Russia
3
Enikolopov Institute of Synthetic Polymer Materials, Russian Academy of Sciences, 70 Profsoyuznaya Street, 117393 Moscow, Russia
4
Nesmeyanov Institute of Organoelement Compounds, Russian Academy of Sciences, 28 Vavilova Street, 119991 Moscow, Russia
*
Author to whom correspondence should be addressed.
Inorganics 2021, 9(1), 3; https://doi.org/10.3390/inorganics9010003
Submission received: 30 November 2020 / Revised: 18 December 2020 / Accepted: 24 December 2020 / Published: 2 January 2021
Browse Figures
Versions Notes

Abstract

:
Poly(lactic acid) (PLA)/palygorskite (Paly) nanocomposites were prepared using the melt compounding technique. Paly modified by 3-aminopropyltriethoxysilane (APTES) and vinyltrimethoxysilane (VTMS) was used as nanofiller for PLA with concentrations in the 1–7 wt% range. It has been found that the functionalization allows a covalent bond between the hydroxyl groups of the Paly and the PLA matrix, evidenced by the improvement in mechanical properties. Paly modification with VTMS has better properties compared with Pale modification with APTES. This indicates a better adhesion between the Paly-VTMS and PLA matrix, and a good dispersion of the nanofiller in the polymer matrix.

1. Introduction

Poly(lactic acid) or polylactide (PLA) is a biodegradable polymer synthesized from renewable resources such as corn, rice, potatoes, or sugarcane [1,2]. It is of greater interest because of its manufacturability during heat treatment, high melting point, plasticity [2,3], the possibility of recycling [4,5], biocompatibility, good biodegradation rate [6,7,8], as well as relatively low cost [9]. Moreover, upon degradation, PLA breaks down into non-toxic components [10]. This opens up prospects for the introduction of PLA in a wide range of production areas, primarily in the food and agricultural sectors of the economy, as a material for packaging, as well as in the pharmaceutical and medical industries [11]. However, the use of PLA has limitations associated with its high brittleness, low elongation at break, low impact strength, and poor crystallizability. Its low mechanical, barrier properties, and low thermal stability in comparison with major industrial polymers limit the extensive use of PLA in its native form [12,13,14,15,16,17,18,19]. The addition of reinforcing components into the PLA polymer matrix allows expanding the possibilities of its application [20,21]. In this case, the morphology of the filler and its compatibility with the polymer matrix play a key role in improving the physical and mechanical properties of the nanocomposite [22]. In most studies on the improvement of PLA properties, the researchers used layered aluminosilicates as a filler, in particular montmorillonite and its organomodified forms [23,24,25,26]. Still, the question of the effect of morphology on the physical and mechanical properties of PLA is insufficiently investigated [11]. In this respect, it is interesting to study palygorskite (also known as attapulgite) with a fiber morphology (with diameter up to 25 nm and length up to 1000 nm) and a porous structure (the size of nano-channels is 0.64 × 0.37 nm), having the following chemical formula: (Si,Al)8O20(Mg,Al,Fe)5(OH)2(OH2)44H2O, where H2O is zeolitic water, OH2 is coordinated water, and OH is structural water [27]. A large surface area and needle-like morphology of palygorskite (Paly) raise the possibility of obtaining a pronounced reinforcing effect at polymer nanocomposites. Using organomodification for Paly should not only provide dispersion of the mineral in the polymer matrix, but also enhance their interaction. This is manifested in the improvement of the mechanical and thermal properties of the nanocomposite containing Paly [28,29,30,31,32]. One of the strategies for organomodification of clay minerals is the grafting silylation reaction. Silane is used as a coupling agent because of its ability to react with clays by hydrolysis/condensation, and its end groups can also react with polymers. The effect in this case is achieved owing to the formation of covalent bonds [33,34]. In this case, it is interesting to evaluate the effect of Paly modification with various silanes on the properties of PLA/Paly nanocomposites, which has been poorly understood until recently. However, there are examples of successful applications of silanes for other clay minerals [35,36,37].
The aim of this work is to carry out a comparative analysis of the effect of pre-modified Paly on the morphological, mechanical, and thermal properties of PLA/Paly nanocomposites. 3-aminopropyltriethoxysilane (APTES) and vinyltrimethoxysilane (VTMS) were chosen as Paly modifiers. The nanocomposites were prepared by melt blending. For comparative evaluation, a multiple research was performed using Fourier transform infrared spectroscopy (FTIR), mechanical bending tests, transmission electron microscopy (TEM), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC).

2. Material and Methods

2.1. Materials

PLA (4032D) with a number average molecular weight of 200 kDa was obtained from NatureWorks LLC (Minnetonka, MN, USA). Palygorskite (Cimsil G30) was purchased from TOLSA S.A. (Madrid, Spain). The silanes (3-aminopropyltriethoxysilane and vinyltrimethoxysilane) were purchased from MAS Albion Ltd. (Moscow, Russia). The structures of chemical compounds are given in Table 1.

2.2. Modification of Palygorskite

The Paly functionalization procedure is shown in Figure 1. For homogenization, Paly (1 g) was mixed with ethyl alcohol (20 g). The resulting mixture was subsequently subjected to 30 min of ultrasonic treatment (magnetostrictive emitter with the frequency of 22 kHz, amplitude of 50 μm, and output power of 500 W) and 30 min of mixing on a magnetic stirrer (1500 rpm at room temperature) (Figure 1a). For modification, APTES or VTMS (250 mg) was added to the mixture. Then, the mixture was brought to pH 4.5–5.5 by adding a solution of acetic acid (1.25 mL) in deionized water (30 mL). The resulting mixture was stirred for 4 h on a magnetic stirrer (1500 rpm, 65 °C) (Figure 1b). Finally, the sample was centrifuged at 9000 rpm to obtain a solid substance, after which it was dried at room temperature.

2.3. Preparation of Poly(Lactic Acid)/Palygorskite Nanocomposites

PLA/Paly nanocomposites with 1, 3, 5, and 7 wt% filler content (Paly-APTES and Paly-VTES) were prepared using the melt extrusion technique using LTE 26–48 co-rotating twin-screw extruder, with a screw speed of 80 rpm. Before processing, the PLA and the filler were dried for 12 h at 80 °C. This blending process was conducted with temperature profiles of the extruder barrels; the ten zones of the hopper were 175, 180, 185, 185, 185, 190, 190, 195, 195, 195, and head 190 °C. The extrudate was then passed through a chilled water bath and pelletized. The scheme for obtaining PLA/Paly-APTES or PLA/Paly-VTMS is depicted in Figure 1c. The PLA, PLA/Paly-APTES, and PLA/Paly-VTMS paddle-shaped samples (150 × 20 × 4 mm) were prepared in injection molding machine (Haibo HBT700L) at 185, 195, 200, and head 190 °C cylinder temperature, and 35 °C mould temperature at 5 s holding time under the pressure range of 1200–600 bar (Figure 1d).

2.4. Characterization Methods

Fourier transform infrared (ALPHA-E; Bruker, Billerica, MA, USA) spectroscopy was used to analyze the chemical structures of the nanocomposites. The spectrum ranged from 500 to 4000 cm−1, the resolution was 4 cm−1, and the number of scans was 32. Flexural modulus was measured according to ASTM D790-17 standard using ZwickiLine Materials Testing machine 5 kN at a constant crosshead speed of 2 mm/min. By transmission electron microscopy (Tecnai Spirit G2; Philips, Amsterdam, The Netherlands), the dispersion of Paly-APTES or Paly-VTMS in PLA/Paly nanocomposite was observed. A synchronous thermal analyzer (STA 449 F3; NETSCH, Selb, Germany) combining thermo gravimetric analysis with differential scanning calorimetry was used. The effect of Paly-APTES or Paly-VTMS on the thermal stability of the nanocomposite was studied. In synchronous mode (TGA and DSC), we used the sample weighing about 6–9 mg, and the temperature was raised from 40 °C to 500 °C with a heating rate of 10 °C/min. Argon (air) was used as the purge and protection gas, and the flow rate of argon (air) was 30 mL/min. Corundum crucibles with a hole in the lid were used for measurements. In DSC mode, the test volume was about 6–9 mg, and the temperature was raised from 25 °C to 300 °C with a heating rate of 10 °C/min. It was cooled from 300 °C to 25 °C at a cooling rate of 5 °C/min. Sealed aluminum crucibles were used for measurements.

3. Results and Discussion

3.1. FTIR Analysis

The FTIR spectra of pristine Paly and silane-functionalized Paly are displayed in Figure 2. FTIR spectrum of Paly demonstrates tetrahedral (Si–O–Si, 950–1250 cm−1) [38,39] and octahedral (Al–Al–OH, 913 cm−1; Al–Fe–OH, 865 cm−1; and Mg–Mg–OH, 647 cm−1 [40]) vibrations with bands connected with hydroxyl groups and water molecules in the range 3200–3400, 3562 cm−1 [41], and 1668 cm−1 [42], respectively.
Surface modification of the Paly using APTES is revealed in a decrease in the intensity of Si–O vibrations due to the response of APTES and Paly [38,39] (Figure 2a). The vibrational frequencies of silane molecules interacting with fibrous silicates are in the range of 1200–2000 cm−1. The band at 1630 cm−1 is associated with the stretching vibration C=C, and the band at 1720 cm−1 is associated with the stretching vibration C=O [42,43]. In addition, new peaks at 1566, 1496, and 690 cm−1(Figure 2b), which correspond to bending vibrations of –NH2, –CH2, and deformation of –CH out of plane, once again confirm this conclusion [44,45]. All these observations are consistent with the APTES grafting onto the Paly surface [46]. In Paly modification with silane (Figure 2c), there occurs a new peak at 2930 cm−1, and one more small hump at 2850 cm−1, associated with C–H asymmetric and symmetric stretching of the –CH2 groups, which confirms the presence of silane on the mineral surface [47].
Surface modification of the Paly surface using VTMS is characterized by new Si–O–Si bands appearing in the FTIR spectrum at 1120, 1080, 1031, and 790 cm−1 [48,49,50,51] (Figure 2a). Moreover, stripes with asymmetric stretch –CH2 at 3062 cm−1, C=C stretch at 1600 cm−1, and –CH in-plane band at 1274 cm−1 (Figure 2b,c) [52]. Thus, the presence of silane bands in all spectra of functionalized clays confirms that the OH group on the inner/outer surface and edge of clays can chemically react with alkoxysilane Si–OR groups.
FTIR spectra of PLA, PLA/Paly-APTES, and PLA/Paly-VTMS are shown in Figure 3. For PLA, there are stretching frequencies for C=O, asymmetric, and symmetric vibrations of –CH3 group at 1746, 2997, and 2943 cm−1, respectively. At 1180 cm−1, one can observe a band associated with the O–C–O groups, as well as three peaks at 1128, 1081, and 1042 cm−1 belonging to the C–C–O group. In addition, bending frequencies for –CH3 are determined at 1452, 1380, and 1359 cm−1 [53,54]. In Figure 3a, the excess of the intensity of the maximum in the region of 1650 cm−1 is observed, related to the hygroscopic water of Paly oscillation, for PLA/Paly-APTES with 5 wt% filler content over a sample containing 7 wt% filler; this can be attributed to the heterogeneity of filler distribution in the PLA matrix witnessed in TEM images (Section 3.3).
This finding shows that there is less accessibility of surface hydroxyl groups because of the modification of the Paly surface with a silane. The carbonyl group that appears at 1745 cm−1 for pure PLA shifts slightly towards the higher wavenumber (1746 cm−1) in the PLA/Paly-APTES and PLA/Paly-VTMS nanocomposites in the case of 7 wt% content of Paly-APTES (Paly-VTMS), indicating a certain degree of chemical interaction between Paly-APTES (Paly-VTMS) and PLA matrix. In this case, the largest number of surface-active groups of the Paly-APTES (Paly-VTMS) filler interacting with the PLA matrix may be retained.

3.2. Mechanical Properties

The flexural modulus of PLA, PLA/Paly-APTES, and PLA/Paly-VTMS nanocomposites is shown in Figure 4. The increase in flexural strength modulus with increasing silylated Paly concentration to 7 wt% indicates a positive effect of silanization on nanofiller dispersion in the PLA polymer matrix. The overall flexural strength of PLA/Paly-VTMS composites is higher than that of PLA/Paly-APTES. This happens owing to better interfacial adhesion between the matrix and filler, which improves stress transfer and leads to higher flexural strength values. The presence of agglomerates with an increasing concentration of Paly-APTES is also the reason for underestimated values of the flexural modulus of PLA/Paly-APTES composites. A simultaneous increase in the flexure modulus for PLA/Paly-APTES and PLA/Paly-VTMS nanocomposites with the addition of 1 wt% silylated Paly compared with pure PLA from 3.3 GPa to 3.392 and 3.394 GPa, respectively, was witnessed. This indicates that Paly intrinsic stiffness has a positive effect on the overall stiffness of the PLA/Paly nanocomposites, which increases the flexural modulus of nanocomposites. Improving the flexural modulus for PLA and its nanocomposites is important for sustainable packaging applications [55] as it is a measure of the stiffness of a material. The positive effect of functionalization with silanes APTES and VTMS of clay minerals such as montmorillonite, halloysite, and sepiolite on the mechanical properties of thermoplastic polymers was also scrutinized by Raji et al. [39].

3.3. Morphology Analysis

Paly-VTMS particles are dispersed in the PLA polymer matrix, which can be clearly seen in Figure 5a. Despite the concentration of 7 wt% Paly-VTMS in the polymer matrix, no signs of particle agglomeration are detected, which indicates a clear interaction between Paly-VTMS and the PLA matrix. In contrast, for Paly-APTES particles in the PLA matrix for the case of 7 wt% concentration, areas of particle agglomeration are observed (Figure 5b). This indicates a reduced interaction between the modified APTES Paly and polymer matrix.

3.4. Thermogravimetric Analysis

Figure 6 displays the TGA curves of PLA, PLA/Paly-VTMS, and PLA/Paly-APTES samples. At temperatures up to 300 °C, the mass of PLA/Paly-VTMS (Figure 6a,c) and PLA/Paly-APTES (Figure 6b,d) samples is stable in both argon atmosphere and air. At temperatures above 300–305 °C in argon atmosphere and in air, there is pyrolytic decomposition of all samples, with an almost complete loss of weight by 380 °C. Closer to 500 °C, the residual mass of PLA/Paly-VTMS and PLA/Paly-APTES samples increases. This is due to the increase in the content of the Paly-APTES and Paly-VTMS filler remaining after heating (Table 2).

3.5. Differential Scanning Calorimetry

Figure 6 represents the DSC curves of PLA, PLA/Paly-VTMS, and PLA/Paly-APTES samples. With an increase in the content of silanized Paly from 1 to 5 wt%, an augmentation in the crystallinity index (Xc) is detected, which indicates that the clay filler can act as a nucleation agent to induce the PLA crystallization [56,57]. Adding 7 wt% silanized Paly diminishes this effect (Table 2). An increase in crystallinity results in a higher glass transition temperature (Tg). The addition of silanized Paly to PLA did not significantly affect the melting temperature (Tm), except for samples with 7 wt% filler content, indicating a better packaging and organization caused by the clay filler [58]. Similar behavior was also observed in the work of Lai et al. for PLA nanocomposites filled with organic-modified montmorillonite clay [56].

4. Conclusions

Nanocomposites based on PLA and modified palygorskite were prepared by melt blending. Palygorskite was modified with two organosilanes (APTES and VTMS), which promoted the formation of covalent bonds between the polymer and the clay through reactive extrusion, allowing strong interactions between the clay and the PLA matrix. Spectral studies were performed to characterize the successful grafting of silanes onto palygorskite. It has been found that the functionalization method allows a covalent bond between the hydroxyl groups of the clay minerals and the polymer matrix, as evidenced by the improvement in mechanical properties. Thus, for the flexural modulus, PLA increases from 3300 MPa to 3930 MPa at 7 wt% for Paly-VTMS. The obtained results prove that silylation of palygorskite is an important method for increasing the interfacial adhesion between palygorskite and the PLA matrix.

Author Contributions

Conceptualization, A.K. (Anton Kasprzhitskii) and G.L.; methodology, A.K. (Anton Kasprzhitskii); investigation, A.K. (Anton Kasprzhitskii), G.L., A.K. (Alexander Kruglikov), I.K., and V.G.; resources, G.L.; writing—original draft preparation, A.K. (Anton Kasprzhitskii); writing—review and editing, G.L.; visualization, A.K. (Anton Kasprzhitskii); project administration, A.K. (Anton Kasprzhitskii). All authors have read and agreed to the published version of the manuscript.

Funding

The work was performed according to the state assignment of the Federal Agency for Railway Transport of the Russian Federation (protocol ROSZHELDOR of 15.04.2020 No.VCh-23). The company had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Acknowledgments

Investigation of TGA and DSC characteristics was made using the equipment of the Collaborative Access Center “Center for Polymer Research” of ISPM RAS.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Pandey, J.K.; Reddy, K.R.; Kumar, A.P.; Singh, R.P. An overview on the degradability of polymer nanocomposites. Polym. Degrad. Stab. 2005, 88, 234–250. [Google Scholar] [CrossRef]
  2. Lim, L.-T.; Auras, R.; Rubino, M. Processing technologies for poly(lactic acid). Prog. Polym. Sci. 2008, 33, 820–852. [Google Scholar] [CrossRef]
  3. Auras, R.; Harte, B.; Selke, S. An Overview of Polylactides as Packaging Materials. Macromol. Biosci. 2004, 4, 835–864. [Google Scholar] [CrossRef] [PubMed]
  4. Piemonte, V.; Sabatini, S.; Gironi, F. Chemical recycling of PLA: A great opportunity towards the sustainable development? J. Polym. Environ. 2013, 21, 640–647. [Google Scholar] [CrossRef]
  5. Plichta, A.; Lisowska, P.; Kundys, A.; Zychewicz, A.; Debowski, M.; Florjanczyk, Z. Chemical recycling of poly(lactic acid) via controlled degradation with protic (macro) molecules. Polym. Degrad. Stab. 2014, 208, 288–296. [Google Scholar] [CrossRef]
  6. Dorgan, J.R.; Lehermeier, H.J.; Palade, L.I.; Cicero, J. Poly lactides: Properties and prospects of an environmentally benign plastic from renewable resources. Macromol. Symp. 2001, 175, 55–66. [Google Scholar] [CrossRef]
  7. Pantani, R.; Sorrentino, A. Influence of crystallinity on the biodegradation rate of injection-moulded poly(lactic acid) samples in controlled composting conditions. Polym. Degrad. Stab. 2013, 98, 1089–1096. [Google Scholar] [CrossRef]
  8. Gorrasi, G.; Pantani, R. Effect of PLA grades and morphologies on hydrolytic degradation at composting temperature: Assessment of structural modification and kinetic parameters. Polym. Degrad. Stab. 2013, 98, 1006–1014. [Google Scholar] [CrossRef]
  9. Garlotta, D. A Literature Review of Poly(Lactic Acid). J. Polym. Environ. 2011, 9, 63–84. [Google Scholar] [CrossRef]
  10. Nel, A.; Xia, T.; Mädler, L.; Li, N. Toxic potential of materials. Science 2007, 311, 622–627. [Google Scholar] [CrossRef] [Green Version]
  11. Raquez, J.-M.; Habibi, Y.; Murariu, M.; Dubois, P. Polylactide (PLA)-based nanocomposites. Prog. Polym. Sci. 2013, 38, 1504–1542. [Google Scholar] [CrossRef]
  12. Rasal, R.M.; Janorkar, A.V.; Hirt, D.E. Poly(lactic acid) modifications. Prog. Polym. Sci. 2010, 35, 338–356. [Google Scholar] [CrossRef]
  13. Anderson, K.S.; Schreck, K.M.; Hillmyer, M.A. Toughening polylactide. Polym. Rev. 2008, 48, 85–108. [Google Scholar] [CrossRef]
  14. Liu, H.; Zhang, J. Research progress in toughening modification of poly(lactic acide). J. Polym. Sci. Part B Polym. Phys. 2011, 49, 1051–1083. [Google Scholar] [CrossRef]
  15. Fortunati, E.; Armentano, I.; Iannoni, A.; Barbale, M.; Zaccheo, S.; Scavone, M.; Visai, L.; Kenny, J.M. New multifunctional poly(lactide acid) composites: Mechanical, antibacterial, and degradation properties. J. Appl. Polym. Sci. 2012, 124, 87–98. [Google Scholar] [CrossRef]
  16. Rosli, N.A.; Ahmad, I.; Anuar, F.H.; Abdullah, I. Mechanical and thermal properties of natural rubber-modified poly(lactic acid) compatibilized with telechelic liquid natural rubber. Polym. Test. 2016, 54, 196–202. [Google Scholar] [CrossRef]
  17. Rasal, R.M.; Hirt, D.E. Toughness decrease of PLA–PHBHHx blend films upon surface-confined photopolymerization. J. Biomed. Mater. Res. Part A 2008, 88A, 1079–1086. [Google Scholar] [CrossRef] [PubMed]
  18. Hiljanen-Vainio, M.; Varpomaa, P.; Seppala, J.; Tormala, P. Modification of poly(l-lactides) by blending: Mechanical and hydrolytic behavior. Macromol. Chem. Phys. 1997, 197, 1503–1523. [Google Scholar] [CrossRef]
  19. Grijpma, D.W.; Nijenhuis, A.J.; Van Wijk, P.G.T.; Pennings, A.J. High impact strength as-polymerized PLLA. Polym. Bull. 1992, 29, 571–578. [Google Scholar] [CrossRef]
  20. Kruglikov, A.; Vasilchenko, A.; Kasprzhitskii, A.; Lazorenko, G. Atomic-level understanding of interface interactions in a halloysite nanotubes-PLA nanocomposite. RSC Adv. 2019, 9, 39505–39514. [Google Scholar] [CrossRef] [Green Version]
  21. Bordes, P.; Pollet, E.; Avérous, L. Nano-biocomposites: Biodegradable polyester/nanoclay systems. Prog. Polym. Sci. 2009, 34, 125–155. [Google Scholar] [CrossRef]
  22. Ray, S.S.; Okamoto, M. Polymer/layered silicate nanocomposites: A review from preparation to processing. Prog. Polym. Sci. 2003, 28, 1539–1641. [Google Scholar] [CrossRef]
  23. Paul, M.A.; Alexandre, M.; Degèe, P.; Henrist, C.; Rulmont, A.; Dubois, P. New Nanocomposite Materials Based on Plasticized Poly(l-Lactide) and Organo-Modified Montmorillonites: Thermal and Morphological Study. Polymer 2003, 44, 443. [Google Scholar] [CrossRef]
  24. Lazorenko, G.; Kasprzhitskii, A.; Yavna, V. Synthesis and structural characterization of betaine- and imidazoline-based organoclays. Chem. Phys. Lett. 2018, 692, 264–270. [Google Scholar] [CrossRef]
  25. Alexandre, M.; Dubois, P. Polymer-layered silicate nanocomposites: Preparation, properties and uses of a new class of materials. Mater. Sci. Eng. R Rep. 2000, 28, 1–63. [Google Scholar] [CrossRef]
  26. Lazorenko, G.; Kasprzhitskii, A.; Yavna, V. Comparative study of the hydrophobicity of organo-montmorillonite modified with cationic, amphoteric and nonionic surfactants. Minerals 2020, 10, 732. [Google Scholar] [CrossRef]
  27. Suárez, M.; García-Romero, E. Advances in the crystal chemistry of sepiolite and palygorskite. Elsevier Developm. Clay Sci. 2011, 3, 33–65. [Google Scholar] [CrossRef]
  28. Yin, H.; Chen, H.; Chen, D. Viscoelastic behavior of poly(acrylonitrile)/attapulgite nanocomposite solution. Colloids Surf. A Physicochem. Eng. Asp. 2010, 367, 52. [Google Scholar] [CrossRef]
  29. Sun, L.; Yang, Z.; Li, X. Effects of the treatment of attapulgite and filler contents on tensile properties of PTFE and attapulgite reinforced fabric composites. Compos. A 2009, 40, 1785. [Google Scholar] [CrossRef]
  30. Shen, L.; Lin, Y.; Du, Q.; Zhong, W. Studies on structure-property relationship of polyamide-6/attapulgite nanocomposites. Compos. Sci. Technol. 2006, 66, 2242. [Google Scholar] [CrossRef]
  31. Peng, L.; Zhou, L.; Li, Y.; Pan, F.; Zhang, S. Synthesis and properties of waterborne polyurethane/attapulgite nanocomposites. Compos. Sci. Technol. 2011, 71, 1280. [Google Scholar] [CrossRef]
  32. Hu, F.; Li, T.; Zhong, F.; Wen, S.; Zheng, G.; Gong, C.; Qin, C.; Liu, H. Preparation and properties of chitosan/acidified attapulgite composite proton exchange membranes for fuel cell applications. J. Appl. Polym. Sci. 2020, 137, 49079. [Google Scholar] [CrossRef]
  33. Bujdák, J.; Danko, M.; Chorvát, D.; Czímerová, A.; Sýkora, J.; Lang, K. Selective modification of layered silicate nanoparticle edges with fluorophores. Appl. Clay Sci. 2012, 65–66, 152–157. [Google Scholar] [CrossRef]
  34. Piscitelli, F.; Posocco, P.; Toth, R.; Fermeglia, M.; Pricl, S.; Mensitieri, G.; Lavorgna, M. Sodium montmorillonite silylation: Unexpected effect of the aminosilane chain length. J. Colloid Interface Sci. 2010, 351, 108–115. [Google Scholar] [CrossRef] [PubMed]
  35. Silva, A.A.; Dahmouche, K.; Soares, B.G. Nanostructure and dynamic mechanical properties of silane-functionalized montmorillonite/epoxy nanocomposites. Appl. Clay Sci. 2011, 54, 151–158. [Google Scholar] [CrossRef]
  36. Ianchis, R.; Corobea, M.C.; Donescu, D. Advanced functionalization of organoclay nanoparticles by silylation and their polystyrene nanocomposites obtained by miniemulsion polymerization. J. Nanopart. Res. 2012, 14, 1233. [Google Scholar] [CrossRef]
  37. Maisanaba, S.; Ortuño, N.; Jordá-Beneyto, M.; Aucejo, S.; Jos, A. Development, characterization and cytotoxicity of novel silane-modified clay minerals and nanocomposites intended for food packaging. Appl. Clay Sci. 2017, 138, 40–47. [Google Scholar] [CrossRef]
  38. Fan, Q.H.; Shao, D.D.; Hu, J.; Wu, W.S.; Wang, X.K. Comparison of Ni2+ sorption to bare and ACT-graft attapulgites: Effect of pH, temperature and foreign ions. Surf. Sci. 2008, 602, 778–785. [Google Scholar] [CrossRef]
  39. Raji, M.; Mekhzoum, M.E.M.; Rodrigue, D.; Qaiss, A.E.K.; Bouhfid, R. Effect of silane functionalization on properties of polypropylene/clay nanocomposites. Compos. B Eng. 2018, 146, 106–115. [Google Scholar] [CrossRef]
  40. Mishra, A.K.; Allauddin, S.; Narayan, R.; Aminabhavi, T.M.; Raju, K.V.S.N. Characterization of surface-modified montmoril-lonite nanocomposites. Ceram. Int. 2012, 38, 929–934. [Google Scholar] [CrossRef]
  41. Cai, Y.; Xue, J.; Polya, D.A. A Fourier transform infrared spectroscopic study of Mg-rich, Mg-poor and acid leached palygorskites. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 2007, 66, 282–288. [Google Scholar] [CrossRef] [PubMed]
  42. Helmy, A.K.; de Bussetti, S.G.; Ferreiro, E.A. The surface energy of palygorskite. Powder Technol. 2007, 171, 126–131. [Google Scholar] [CrossRef]
  43. Posthumus, W.; Magusin, P.C.M.M.; Brokken-Zijp, J.C.M.; Tinnemans, A.H.A.; van der Linde, R. Surface modification of oxidic nanoparticles using 3-methacryloxypropyltrimethoxysilane. J. Colloid Interface Sci. 2004, 269, 109–116. [Google Scholar] [CrossRef] [PubMed]
  44. Yan, W.; Yuan, P.; Chen, M.; Wang, L.; Liu, D. Infrared spectroscopic evidence of a direct addition reaction between palygorskite and pyromellitic dianhydride. Appl. Surf. Sci. 2013, 265, 585–590. [Google Scholar] [CrossRef]
  45. De Faria, E.H.; Ciuffi, K.J.; Nassar, E.J.; Vicente, M.; Trujillano, R.; Calefi, P.S. Novel reactive amino-compound: Tris(hydroxymethyl)aminomethane covalently grafted on kaolinite. Appl. Clay Sci. 2010, 48, 516–521. [Google Scholar] [CrossRef]
  46. Xue, A.; Zhou, S.; Zhao, Y.; Lu, X.; Han, P. Effective NH2-grafting on attapulgite surfaces for adsorption of reactive dyes. J. Hazard. Mater. 2011, 194, 7–14. [Google Scholar] [CrossRef]
  47. Laaziz, S.A.; Raji, M.; Hilali, E.; Essabir, H.; Rodrigue, D.; Bouhfid, R.; el kacem Qaiss, A. Bio-composites based on polylactic acid and argan nut shell: Production and properties. Int. J Biol. Macromol. 2017, 104, 30–42. [Google Scholar] [CrossRef]
  48. Marini, M.; Pourabbas, B.; Pilati, F.; Fabbri, P. Functionally modified core-shell silica nanoparyicles by one-pot synthesis. Colloids Surf. A 2008, 317, 473–481. [Google Scholar] [CrossRef]
  49. Wang, L.H.; Sheng, J. Controlled/«Living» radical polymerization. Halogen atom transfer radical polymerization promoted by a Cu(I)/Cu(II) redox process. J. Macromol. Sci. Part A Pure Appl. Chem. 2003, 40, 1135–1146. [Google Scholar] [CrossRef]
  50. Olejniczak, Z.; Łe˛czka, M.; Cholewa-Kowalska, K.; Wojtach, K.; Rokita, M.; Mozgawa, W. 29Si MAS NMR and FTIR study of inorganic-organic hybrid gels. J. Mol. Struct. 2005, 744, 465–471. [Google Scholar] [CrossRef]
  51. Wu, Z.; Ahn, I.-S.; Lee, C.-H.; Kim, J.-H.; Shul, Y.G.; Lee, K. Enhancing the organic dye adsorption on porous xerogels. Colloids Surf. A 2004, 240, 157–164. [Google Scholar] [CrossRef]
  52. Kuznetsova, A.; Wovchko, E.A.; Yates, J.T. FTIR study of the adsorption and thermal behavior of vinyltriethoxysilane chemisorbed on γ-Al2O3. Langmuir 1997, 13, 5322–5328. [Google Scholar] [CrossRef]
  53. Chieng, B.W.; Ibrahim, N.A.; Wan Yunus, W.M.Z.; Hussein, M.Z. Effects of graphene nanopletelets on poly(lactic acid)/poly(ethylene glycol) polymer nanocomposites. Adv. Mater. Res. 2014, 1024, 136–139. [Google Scholar] [CrossRef]
  54. Fortunati, E.; Luzi, F.; Puglia, D.; Dominici, F.; Santulli, C.; Kenny, J.M.; Torre, L. Investigation of thermo-mechanical, chemical and degradative properties of PLA-limonene films reinforced with cellulose nanocrystals extracted from Phormium tenax leaves. Eur. Polym. J. 2014, 56, 77–91. [Google Scholar] [CrossRef]
  55. Armentano, I.; Bitinis, N.; Fortunati, E.; Mattioli, S.; Rescignano, N.; Verdejo, R.; Lopez-Manchado, M.A.; Kenny, J.M. Multifunctional nanostructured PLA materials for packaging and tissue engineering. Prog. Polym. Sci. 2013, 38, 1720–1747. [Google Scholar] [CrossRef] [Green Version]
  56. Lai, S.-M.; Wu, S.-H.; Lin, G.-G.; Don, T.-M. Unusual mechanical properties of melt-blended poly(lactic acid) (PLA)/clay nanocomposites. Eur. Polym. J. 2014, 52, 193–206. [Google Scholar] [CrossRef]
  57. Fukushima, K.; Tabuani, D.; Camino, G. Poly(lactic acid)/clay nanocomposites: Effect of nature and content of clay on morphology, thermal and thermo-mechanical properties. Mater. Sci. Eng. C 2012, 32, 1790–1795. [Google Scholar] [CrossRef]
  58. Gomez-Gamez, A.B.; Yebra-Rodriguez, A.; Peñas-Sanjuan, A.; Soriano-Cuadrado, B.; Jimenez-Millan, J. Influence of clay percentage on the technical properties of montmorillonite/polylactic acid nanocomposites. Appl. Clay Sci. 2020, 198, 105818. [Google Scholar] [CrossRef]
Inorganics 09 00003 g001 550
Figure 1. Schematic representation of the processes for modification of Paly (a,b) and preparation of poly(lactic acid) (PLA)/palygorskite (Paly) nanocomposites (c,d). APTES, 3-aminopropyltriethoxysilane; VTMS, vinyltrimethoxysilane.
Figure 1. Schematic representation of the processes for modification of Paly (a,b) and preparation of poly(lactic acid) (PLA)/palygorskite (Paly) nanocomposites (c,d). APTES, 3-aminopropyltriethoxysilane; VTMS, vinyltrimethoxysilane.
Inorganics 09 00003 g001
Inorganics 09 00003 g002 550
Figure 2. Fourier transform infrared (FTIR) spectra of Paly, Paly-APTES, and Paly-VTES for wavenumber (cm−1) ranges: (a) 700–1200; (b) 1300–1800; and (c) 2700–3700.
Figure 2. Fourier transform infrared (FTIR) spectra of Paly, Paly-APTES, and Paly-VTES for wavenumber (cm−1) ranges: (a) 700–1200; (b) 1300–1800; and (c) 2700–3700.
Inorganics 09 00003 g002
Inorganics 09 00003 g003 550
Figure 3. FTIR spectra of PLA, PLA/Paly-VTMS, and PLA/Paly-APTES for wavenumber (cm−1) ranges: (a) 1500–1950 and (b) 2750–3250.
Figure 3. FTIR spectra of PLA, PLA/Paly-VTMS, and PLA/Paly-APTES for wavenumber (cm−1) ranges: (a) 1500–1950 and (b) 2750–3250.
Inorganics 09 00003 g003
Inorganics 09 00003 g004 550
Figure 4. The flexural modulus of PLA/grafted Paly nanocomposites.
Figure 4. The flexural modulus of PLA/grafted Paly nanocomposites.
Inorganics 09 00003 g004
Inorganics 09 00003 g005 550
Figure 5. Transmission electron microscopy (TEM) micrographs of (a) PLA/Paly-VTMS (7 wt%) and (b) PLA/Paly-APTES (7 wt%) nanocomposites.
Figure 5. Transmission electron microscopy (TEM) micrographs of (a) PLA/Paly-VTMS (7 wt%) and (b) PLA/Paly-APTES (7 wt%) nanocomposites.
Inorganics 09 00003 g005
Inorganics 09 00003 g006 550
Figure 6. Thermogravimetric analysis (TGA) and differential scanning calorimeter (DSC) curves of PLA nanocomposites with different proportions of PPV (Paly-VTMS) and PPA (Paly-APTES) addition in air (a,b) and in argon atmosphere (c,d).
Figure 6. Thermogravimetric analysis (TGA) and differential scanning calorimeter (DSC) curves of PLA nanocomposites with different proportions of PPV (Paly-VTMS) and PPA (Paly-APTES) addition in air (a,b) and in argon atmosphere (c,d).
Inorganics 09 00003 g006
Table
Table 1. Structure and chemical characteristics of poly(lactic acid) and silane molecules.
Table 1. Structure and chemical characteristics of poly(lactic acid) and silane molecules.
LabelChemical NameStructural FormulaMolecular Weight (g/mol)
PLAPolylactide Ingeo 4032D Inorganics 09 00003 i001123,000.00
APTES3-Aminopropyltriethoxysilane Inorganics 09 00003 i002221.37
VTMSVinyltrimethoxysilane Inorganics 09 00003 i003148.23
Table
Table 2. Thermal parameters obtained from thermogravimetric analysis (TGA) and differential scanning calorimeter (DSC) analysis (in argon). PPV, Paly-VTMS.
Table 2. Thermal parameters obtained from thermogravimetric analysis (TGA) and differential scanning calorimeter (DSC) analysis (in argon). PPV, Paly-VTMS.
SampleGlass Transition Temperature, Tg (°C)Melting Temperature, Tm (°C)Crystallinity Index, Xc (%)Weight Loss (%)
PLA591700.994.2
PPV (1 wt%)5917017.698.0
PPV (3 wt%)6017034.091.7
PPV (5 wt%)6017041.290.4
PPV (7 wt%)6116311.486.1
PPA (1 wt%)5917015.692.2
PPA (3 wt%)5716829.188.1
PPA (5 wt%)5816842.488.0
PPA (7 wt%)6116423.585.2
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Kasprzhitskii, A.; Lazorenko, G.; Kruglikov, A.; Kuchkina, I.; Gorodov, V. Effect of Silane Functionalization on Properties of Poly(Lactic Acid)/Palygorskite Nanocomposites. Inorganics 2021, 9, 3. https://doi.org/10.3390/inorganics9010003

AMA Style

Kasprzhitskii A, Lazorenko G, Kruglikov A, Kuchkina I, Gorodov V. Effect of Silane Functionalization on Properties of Poly(Lactic Acid)/Palygorskite Nanocomposites. Inorganics. 2021; 9(1):3. https://doi.org/10.3390/inorganics9010003

Chicago/Turabian Style

Kasprzhitskii, Anton, Georgy Lazorenko, Alexander Kruglikov, Irina Kuchkina, and Vadim Gorodov. 2021. "Effect of Silane Functionalization on Properties of Poly(Lactic Acid)/Palygorskite Nanocomposites" Inorganics 9, no. 1: 3. https://doi.org/10.3390/inorganics9010003

APA Style

Kasprzhitskii, A., Lazorenko, G., Kruglikov, A., Kuchkina, I., & Gorodov, V. (2021). Effect of Silane Functionalization on Properties of Poly(Lactic Acid)/Palygorskite Nanocomposites. Inorganics, 9(1), 3. https://doi.org/10.3390/inorganics9010003

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop