Sulfur-Doped Carbon Nitride Polymers for Photocatalytic Degradation of Organic Pollutant and Reduction of Cr(VI)
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 22
Issue 4
10.3390/molecules22040580
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Growth, Structure, and Photocatalytic Properties of Hierarchical V2O5–TiO2 Nanotube Arrays Obtained from the One-step Anodic Oxidation of Ti–V Alloys

by
María C. Nevárez-Martínez
1,2,
Paweł Mazierski
3,*,
Marek P. Kobylański
3,
Grażyna Szczepańska
4,
Grzegorz Trykowski
4,
Anna Malankowska
3,
Magda Kozak
3,
Patricio J. Espinoza-Montero
2 and
Adriana Zaleska-Medynska
3,*
1
Facultad de Ingeniería Química y Agroindustria, Escuela Politécnica Nacional, Ladrón de Guevara E11-253, P.O. Box 17-01-2759, Quito 170525, Ecuador
2
Centro de Investigación y Control Ambiental “CICAM”, Departamento de Ingeniería Civil y Ambiental, Facultad de Ingeniería Civil y Ambiental, Escuela Politécnica Nacional, Ladrón de Guevara E11-253, P.O. Box 17-01-2759, Quito 170525, Ecuador
3
Department of Environmental Technology, Faculty of Chemistry, University of Gdansk, Gdansk 80-308, Poland
4
Faculty of Chemistry, Nicolaus Copernicus University, Torun 87-100, Poland
*
Authors to whom correspondence should be addressed.
Molecules 2017, 22(4), 580; https://doi.org/10.3390/molecules22040580
Submission received: 29 January 2017 / Revised: 30 March 2017 / Accepted: 1 April 2017 / Published: 5 April 2017
(This article belongs to the Special Issue Photon-involving Purification of Water and Air)
Browse Figures
Versions Notes

Abstract

:
V2O5-TiO2 mixed oxide nanotube (NT) layers were successfully prepared via the one-step anodization of Ti-V alloys. The obtained samples were characterized by scanning electron microscopy (SEM), UV-Vis absorption, photoluminescence spectroscopy, energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (DRX), and micro-Raman spectroscopy. The effect of the applied voltage (30–50 V), vanadium content (5–15 wt %) in the alloy, and water content (2–10 vol %) in an ethylene glycol-based electrolyte was studied systematically to determine their influence on the morphology, and for the first-time, on the photocatalytic properties of these nanomaterials. The morphology of the samples varied from sponge-like to highly-organized nanotubular structures. The vanadium content in the alloy was found to have the highest influence on the morphology and the sample with the lowest vanadium content (5 wt %) exhibited the best auto-alignment and self-organization (length = 1 μm, diameter = 86 nm and wall thickness = 11 nm). Additionally, a probable growth mechanism of V2O5-TiO2 nanotubes (NTs) over the Ti-V alloys was presented. Toluene, in the gas phase, was effectively removed through photodegradation under visible light (LEDs, λmax = 465 nm) in the presence of the modified TiO2 nanostructures. The highest degradation value was 35% after 60 min of irradiation. V2O5 species were ascribed as the main structures responsible for the generation of photoactive e− and h+ under Vis light and a possible excitation mechanism was proposed.

Graphical Abstract

1. Introduction

Over the past few decades, photocatalytic processes on the surface of TiO2 have been intensively studied due to a wide range of industrially oriented applications based on the conversion of sunlight into usable chemical energy [1,2,3,4,5,6]. Being non-toxic, abundant, chemically and physically stable, and photostable [7,8], TiO2 is a semiconductor material of great interest for environmental remediation [9,10], hydrogen evolution from water splitting [11,12], dye-sensitized solar cells [12,13], CO2 reduction [12,14], and self-cleaning surfaces [15,16]. However, the usage of TiO2 is limited not only by its wide bandgap (3.0–3.2 eV), which allows the absorption of only UV light corresponding to 4% of the incident solar energy [17], but also by the fast recombination rate of charge carriers [18,19]. In order to harvest sunlight, many TiO2 modification approaches have been developed [20,21], such as metal [22], nonmetal [23,24,25], or rare earth element doping [26], dye sensitization with organic and inorganic dyes [27], and the formation of photocatalytic heterostructures (coupling) with other semiconductors [28] or noble metals [29,30,31]. In particular, tuning TiO2 with V2O5 is an efficient way of improving TiO2 performance [32]. V2O5 is a small-bandgap semiconductor (~2.3 eV) which can extend the light absorption to the visible range [33]. Furthermore, photogenerated electrons and holes can be efficiently separated, and the surface charge carrier transfer rate is enhanced [34,35]. V2O5 itself has been used as a photocatalyst under UV light [36,37,38,39], visible light [40], and sunlight [41]. Xie, et al. [42] obtained photoactive V2O5-TiO2 nanocomposites for the oxidation of As(III). They stated that under visible light irradiation, h+ and O2− are the main active species responsible for the photoreaction. Choi, et al. [43] synthesized V2O5-TiO2 nanocomposite powder by DC arc plasma. They found that, in the presence of the nanocomposite, Rhodamine B was decomposed under visible light, while it was not decomposed in the presence of TiO2 nanopowder. They also reported visible photoactivation and an enhanced charge separation in the case of toluene removal in a dielectric barrier discharge reactor. These aspects make the V2O5-TiO2 system an attractive material for visible-light-driven photocatalytic applications.
Moreover, TiO2 performance also critically depends on mass transfer, charge transfer, and charge/ion transport on its surface and bulk [7,44]. These processes are mainly controlled by morphology, which can be 0D (nanoparticles), 1D (nanowires, rods and tubes), 2D (layers and sheets), or 3D (spheres) [7]. Among 1D structures, TiO2 nanotubes (NTs) have become an interesting material because of their high electron mobility, excellent electron hole separation ability, long-distance transport capability, high specific surface area, mechanical strength, and extremely high aspect ratio [45,46]; however, no major improvement was reported for photocatalytic air purification with respect to nanoparticles under similar conditions [47].
Electrochemical anodization under specific conditions appears to be the simplest, least expensive, and most straightforward technique to obtain self-organized, auto-aligned NT arrays [48,49] over the surface of various metals, e.g., Ti [45,50,51], Zr [52], Hf [53], or alloys, e.g., TiNb, TiZr, TiTa [54], TiV [55,56], TiW [57], TiMn [58], TiMoNi [59], Ti6Al4V [60], and TiAg [61]. Anatase TiO2 nanotube array films with exposed {001} nanofacets, obtained by a low temperature hydrothermal method, exhibited enhanced UV activity, which was attributed to the enhanced charge separation derived from the synergy between {001} and {101} facets [62]. However, an electrochemical method is the most efficient for preparing mixed oxide nanotubes from a Ti suitable alloy. V2O5-TiO2 NTs have been successfully fabricated by electro-synthesis using Ti-V alloys as a substrate by the Schmuki research group [55] and Yang, Kim, Yang and Schmuki [56]. These mixed oxide NTs showed, respectively, improved electrochromic and capacitive properties compared with those of pure TiO2 NTs. Nevertheless, despite the proven visible light absorption of V2O5-TiO2 nanotubes, there is still a lack of data regarding the photoactivity of the V2O5-TiO2 NTs obtained from the anodization of Ti-V alloys. In our previous work [63], self-organized TiO2-MnO2 NTs were successfully obtained by the one-step anodization of Ti-Mn alloys in a fluoride-containing ethylene glycol (EG)-based electrolyte. The as-prepared layers were highly organized and showed visible-light photoactivity towards the degradation of toluene in the gas phase. It was demonstrated that a Vis-excited composite of wide and narrow bandgap oxides could be obtained by the anodization of Ti/V alloys, and that the preparation parameters (e.g., applied voltage, content of the MnO2 in nanocomposite) affected both the morphology and photoactivity of the TiO2/MnO2 NTs.
In view of this, this work focuses on the synthesis of visible-light photoactive V2O5-TiO2 NTs through the one-step anodic oxidation of Ti-V alloys in an ethylene glycol-based electrolyte, and their application in the photocatalytic degradation of toluene. The effect of the vanadium content in the alloy, applied voltage, and electrolyte composition (water content) was systematically studied to determine the influence of these parameters on the morphology and gas phase photoactivity, evaluated for the first time, of the obtained nanomaterials. The as-prepared NTs were characterized by using scanning electron microscopy (SEM), X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX), micro-Raman spectroscopy, UV-Vis absorption, and photoluminescence spectroscopy. A possible mechanism of toluene degradation at the surface of V2O5-TiO2 NTs under the influence of visible light was also proposed.

2. Results and Discussion

2.1. Morphology and Growth Mechanism

Ti foils and Ti-V alloys of technical grade were anodically oxidized for 60 min, under the specific parameters summarized in Table 1. The effect of the applied potential (30, 40, and 50 V), vanadium content in the alloy (5, 10, and 15 wt %), and water content in the electrolyte (2, 5, and 10 vol %) on the morphology of the as-prepared samples were studied by scanning electron microscopy. The top-view and cross-sectional scanning electron microscopy (SEM) images are presented in Figure 1. The anodization of Ti sheets led to the formation of uniform and self-organized NTs with an open tube top and smooth walls, and the tube diameter and length ranged from 81 to 120 nm and from 1.5 to 16.2 μm, respectively (Ti_30V, Ti_50V, respectively). The samples anodized from the Ti-V alloys presented a different morphology, depending on the preparation parameters. The series of samples synthesized from alloys with a 10 wt % vanadium content generally exhibited a sponge-like structure integrated by overlapped layers with a tubular appearance. The registered diameters of these structures varied from 61 to 101 nm and the average thickness of the mixed oxide layers was 0.3–0.8 μm. The samples prepared from alloys with 15 wt % of vanadium and using electrolytes with different water contents showed different morphologies. The Ti85V15_40V_2% and Ti85V15_40V_10% samples presented a sponge-like structure made up of interconnected disordered bundles. Conversely, the Ti85V15_40V_5% sample had a tubular structure with ripples on the tube wall, although the nanotubular layer was not highly organized. NTs presented a diameter (103 nm) similar to that of pristine TiO2 NTs (100 nm) obtained at the same voltage (40 V), while the length (0.9 μm) was smaller than that of the analogous pristine sample (5 μm). The highest level of self-organization was achieved with the sample obtained from the anodization of the alloy with a 5 wt % of vanadium content (Ti95V5_40V), for which the synthesized NTs appeared to be composed of interconnected rings with a diameter of 86 nm and a length of 1 μm. As can be seen, the vanadium content in the alloy has a strong influence on the morphology of the samples. According to Yang, Kim, and Schmuki [55], the absence of a self-organized nanotube layer can be attributed to the low stability of the vanadium oxide, and therefore, the sample (Ti95V5_40V) synthesized from the alloy with the lowest vanadium content exhibited the best auto-alignment and self-organization. The influence of the other parameters, applied potential and water content, on the morphology of the samples was not clear due to the strong influence of the vanadium content in the alloy.
Considering these results, the SEM images of the Ti90V10_40V sample anodized during 4, 15, and 60 min (Figure 2d–f), together with literature data, a probable growth mechanism of V2O5-TiO2 NTs has been described. As can be seen in Figure 2a–c, the shape of the current density-time curves recorded for the V2O5-TiO2 samples were very similar to those of pristine TiO2 NTs. During the first stage, the formation of the V2O5-TiO2 oxide layer induced an exponential decrease in the current density, because of the reaction of Ti and V with the O2− and OH− ions from the water. The presence of this mixed oxide layer can be observed in Figure 2d, corresponding to the Ti90V10_40V sample after 4 min of anodization. Then, the current density progressively increased throughout the second stage due to the dissolution of the oxide layer, which led to an increase in the surface area of the electrode with the initiation of pore growth [64]. These soluble species correspond to the fluoride complexes, [TiF6]2− and [VF6]− [65,66]. Figure 2e shows the initial pores in the sample after 15 min of anodic oxidation. Finally, a regular and self-ordered NT layer, which can be appreciated in Figure 2f, is formed under a quasi-steady state, which is stablished due to the equilibrium between the formation and dissolution of the oxide layer. During this stage, pores equally share the available current [45].
The elemental composition of the obtained samples was analyzed through energy-dispersive X-ray spectroscopy (EDX) and the results presented in Table 1 show that the mass ratios between Ti and V in the V2O5-TiO2 mixed oxides nanostructures (NS) agree well with the nominal content of the alloy. In addition, no trace of elements other than Ti, V, C, and O, was observed. These findings confirm the chemical homogeneity of the nanotube layer. Furthermore, from the EDX mapping presented in Figure 3, it can be concluded that the aggregation of Ti and V was not observed.

2.2. Optical Properties

The UV-Vis spectra of the obtained samples were compared with those of pristine TiO2 NTs. Figure 4a clearly shows that the samples prepared from Ti90V10 alloys exhibited a stronger absorbance in the broad visible range of 400–750 nm than TiO2 NTs. The spectra of the series with different vanadium contents, displayed in Figure 4b, indicated that an increase in the vanadium content in the alloy led to an increase in the absorbance intensity in the visible range, together with a red-shift. In particular, the spectrum of the sample Ti85V15_40V presented a peak of maximum absorbance near 500 nm, which, according to literature data, corresponds to V2O5 [42,67]. The spectra of the series of samples prepared in an electrolyte with different water contents and plotted in Figure 4c are consistent with the previous statements and no clear effect of the water content on the UV-Vis properties was found. All of the spectra for this series of samples showed a peak of absorption in the Vis range near 500 nm, and the spectrum of the Ti85V15_40V_5% sample showed the highest absorbance intensity peak. It can be concluded that the presence of the V2O5 in V2O5-TiO2 matrix enhanced the light absorption in the range of 400–750 nm.
It is known that photoluminescence (PL) spectroscopy is a powerful tool for determining the presence of surface defects, trap states, and sub-band states in the mid-gap level of photocatalysts [68]. The PL spectra of the obtained photocatalysts are presented in Figure 5. It should be noted that the same emission and position peaks were observed among all series. Notably, the emission peak at approximately at 420 nm can be ascribed to the existence of self-trapped excitons from the TiO68− octahedron, while the two emission peaks at 450 and 485 nm could be assigned to the presence of surface defects, in the form of oxygen vacancies, which can create intermediate energy states located below the conduction band and which are able to trap electrons. The last peak at approximately 525 nm can be associated with the radiative recombination of the charge carriers [69,70].
The results mentioned above confirm the presence of surface/structural defects, which can play a role in the photocatalytic degradation of pollutants.

2.3. Structural Properties

XRD patters of the obtained photocatalysts are presented in Figure 6. The calculated average crystallite size for pristine and modified TiO2 NTs are gathered in Table 1. The average crystallite size was calculated using the Scherrer equation, based on the (101) diffraction peak. In the registered region, peaks at 2θ values of 25.67°, 37.97°, 48.31°, 54.16°, and 55.30° can be ascribed to (101), (004), (200), (105), and (211) planes, respectively, which are characteristic of the anatase phase (JCPDS card). The other peaks at 2θ = 35.4°, 38.70°, 40.77°, and 53.31° can be ascribed to planes of metallic Ti substrate. As was mentioned above, the diffraction peaks corresponding to the pure anatase TiO2 phase were found, but other phases assigned to V2O5 were not observed. There are three possible explanations for this. Firstly, it could be because V2O5 diffraction peaks exist; however, the intensity of peaks is too low for this to be true. The absence of peaks corresponding to V2O5 in the XRD patters may be due to the low content and amorphous character of V2O5 or the short-range crystalline. Eventually, the vanadium species are incorporated into the TiO2 lattice. On the other hand, in modified samples, the bands assigned to the anatase phase had a smaller and wider intensity. In particular, the intensity of the pick ascribed to the characteristic (101) plane of anatase decreased with the increase in the vanadium content in the alloy. This is related to the smaller crystallite size of V2O5-TiO2 NS than that of pristine TiO2 NTs [71].
Furthermore, it can be seen that the intensity of the anatase reflexes increased, while those of the substrate decreased, with the increase of the anodizing voltage. This is caused by the increasing thickness of the nanotube layer.
The average crystallite size varied from 30 to 36 nm among Ti-V series, and from 33 to 38 nm for pristine TiO2 NTs. The smallest crystallite size was found for the Ti90V10_50V sample, which reached 30 nm. A clear correlation between the crystallite size and (i) anodization potential; (ii) vanadium content in the alloy; and (iii) water content in the electrolyte, was not observed.
Micro-Raman spectroscopy was performed to determine the microstructure of the prepared samples. A 532 nm laser was used for the excitation. Figure 7 shows the Raman spectra of pristine TiO2 and V2O5-TiO2 NTs. The observed peaks at approximately 150, 396, 515, and 636 cm−1 are ascribed to the Eg, B1g, A1g + B1g, and Eg modes of the anatase phase, respectively, in agreement with previous reports [42,72,73,74]. The Eg modes are assigned to TiO2 symmetry, B1g to O-Ti-O bending, and A1g + B1g to Ti-O stretching [75]. All of the spectra also registered a weak combination band at ca. 800 cm−1, which is characteristic of the Raman signature of anatase [76]. No distinguishable crystalline V2O5 Raman bands were present at 703 and 997 cm−1 in any spectra, probably due to the low content of vanadium in the alloy precursors or to the highly dispersed state of V2O5 in V2O5-TiO2 NS. This was also reported by former publications for composites with the V2O5-TiO2 system [32,75,77].

2.4. Photocatalytic Performance

The effect of the anodization voltage, vanadium content in the alloy, and water content in the electrolyte on the photocatalytic activity was evaluated through the degradation of toluene from an air mixture (200 ppmv of toluene) under Vis irradiation (LEDs array, λmax = 465 nm). Figure 8 presents the degradation curves for the above-mentioned series and their comparison with the photoactivity of reference pristine TiO2 NTs. These plots show that V2O5-TiO2 samples from all series were active in the photodegradation reaction, in contrast with pristine TiO2 NTs which exhibited negligible toluene removal (ca. 5%). The highest degradation of toluene in the presence of samples prepared from the Ti90V10 alloys (see Figure 8a), after 60 min of irradiation, was observed for the sample anodized under 40 V (34%). The toluene removal reached by samples anodized under 30 V and 50 V were not that different from the best one (27% and 33%, respectively). In view of this, 40 V was selected as the potential for further synthesis, to determine the vanadium content in the alloy and the composition of the electrolyte solution, which are favorable for the photodegradation reaction. Figure 8b presents similar results, for the samples obtained from alloys with different vanadium contents. It can be observed that the vanadium content in the alloy slightly affected the photoactivity of the samples. The maximum toluene removal was found to be achieved for the sample with 10 wt % of vanadium in the alloy (Ti90V10_40V, 34% of degradation). The analysis of the effect of water content in the electrolyte was carried out with NS obtained from Ti85V15 alloys. As can be seen in Figure 8c, there is a slight difference in the photocatalytic performance between these samples, among this series. The highest degradation of toluene was exhibited by the sample anodized in the electrolyte containing 5% of water and it corresponded to 35% of toluene removal (Ti85V15_40V_5%). For a more detailed comparison of the obtained results, the initial reaction rate and reaction rate constants were calculated and presented in Table 1. The highest value for the initial reaction rate, among all series, was achieved in the presence of the Ti85V15_40V_5% sample (7.08 × 10−2 μmol·dm−3·min−1), which also exhibited the highest absorbance intensity peak near 500 nm and consisted of a NT layer which was not highly organized. This suggests that this NT composite effectively enhanced visible light harvesting and the consequent photocatalytic reaction, owing to the presence of V2O5 [35,43]. Furthermore, no correlation between the morphology and the photocatalytic performance of the samples was observed.
In conclusion, the highest photoactivity under visible light (465 nm) was observed in the presence of the Ti85V15_40V_5% sample. This sample not only exhibited the highest absorbance intensity at a wavelength of about 500 nm, but also reported the highest diameter (103 nm), the second longest NTs (0.9 μm), and the largest crystallite size (36 nm), from the modified samples. Its vanadium content, based on EDX analysis, was 9.08 wt %. On the other hand, the Ti85V15_40V_10% sample showed the lowest photoactivity. It had a sponge-like morphology with a vanadium content of 8.91%, based on EDX analysis, which is lower than the content of the sample with the highest photoactivity, considering that both were prepared from Ti85V15 alloys. Its crystallite size was 32 nm, smaller than that of the Ti85V15_40V_5% sample. The initial reaction rate achieved in the presence of this sample was 4.50 × 10−2 μmol·dm−3·min−1, which is 1.6 times lower than that reported for the most photoactive one (7.08 × 10−2 μmol·dm−3·min−1).
To further analyze the photocatalytic properties of the synthesized composites, the effect of different irradiation wavelengths was studied using the most photoactive sample (Ti85V15_40V_5%). The gas phase degradation of toluene was tested under 375, 415, and 465 nm and the obtained results are displayed in Figure 9. It can be observed that the highest degradation (52%) after 60 min of irradiation was achieved under UV light (375 nm). This can be explained by the presence of TiO2 in the NT matrix, which is the main active species under UV light irradiation. On the other hand, under the influence of visible light irradiation, 415 and 465 nm, the photocatalytic degradation reached almost the same level, in both cases, with values of 34% and 35%, respectively. This indicates that under Vis light irradiation, V2O5 are the main species responsible for the generation of e− and h+ (as presented in Figure 10, excitation mechanism) over the surface of NTs, which led to the photodegradation of toluene, and this is supported by the negligible degradation reported for pristine TiO2 NTs under Vis light.

3. Materials and Methods

3.1. Materials

Acetone, isopropanol, and methanol were purchased from P.P.H. “STANLAB” Sp. J. (Lublin, Poland), ethylene glycol (EG) was acquired from CHEMPUR (Piekary Śląskie, Poland), and ammonium fluoride was bought from ACROS ORGANICS (Geel, Belgium). Technical grade Ti foils and Ti-V alloys with 5, 10, and 15 wt % of vanadium content were provided by HMW-Hauner Metallische Werkstoffe (Röttenbach, Germany). Deionized (DI) water with a conductivity of 0.05 μS was used to prepare all of the aqueous solutions.

3.2. Synthesis of Pristine TiO2 and V2O5-TiO2 Nanotubes

Ti foils and Ti-V alloys were ultrasonically cleaned in acetone, isopropanol, methanol, and deionized water for 10 min. Then, the foils were dried in an air stream. The anodization processes were carried out at room temperature, in an electrochemical cell consisting of a platinum mesh as the counter electrode, and the Ti-V alloy (2.5 cm × 2.5 cm) as the working electrode. A reference electrode of Ag/AgCl connected to a digital multimeter (BRYMEN BM857a, New Taipei City, Taiwan) was used to control and record information about the actual potential and current on the alloy. The anodization was conducted in an electrolyte composed of EG, water, and NH4F 0.09 M, during 60 min, with a voltage in the range of 30–50 V which was applied with a programmable DC power supply (MANSON SDP 2603, Hong Kong, China). Three electrolyte solutions with different water contents were used (volume ratios of EG:water of 98:2, 95:5, and 90:10). The obtained samples were rinsed with deionized water, sonicated in deionized water (1 min), dried in air (80 °C for 24 h), and calcined (450 °C, heating rate 2 °C/min) for 1 h.

3.3. Characterization of Pristine TiO2 and V2O5-TiO2 Nanotubes

The morphology of the synthesized pristine TiO2 and V2O5-TiO2 nanotubes was determined by using scanning electron microscopy (SEM, FEI QUANTA 3D FEG, FEI Company, Brno, Czech Republic). Energy-dispersive X-ray spectroscopy (EDX) analysis was performed with a scanning electron microscope (SEM, Zeiss, Leo 1430 VP, Carl Zeiss, Oberkochen, Germany). The crystal structure of the samples was determined from X-ray diffraction patterns recorded in the range of 2θ = 20°–90°, using an X-ray diffractometer (X’Pert Pro, Panalytical, Almelo, The Netherlands) with Cu Kα radiation. The crystallite size was calculated based on the Scherrer formula. Raman spectra were measured with a micro-Raman spectrometer (Senterra, Bruker Optik, Billerica, MA, USA) with a 532 nm excitation laser.
The UV-Vis absorbance spectra were registered on a SHIMADZU (UV-2600) UV-VIS Spectrophotometer (SHIMADZU, Kioto, Japan) equipped with an integrating sphere. The measurements were carried out in the wavelength range of 300–800 nm, the baseline was determined with barium sulfate as the reference, and the scanning speed was 250 nm/min at room temperature. The photoluminescence (PL) spectra were recorded at room temperature with a LS-50B Luminescence Spectrometer equipped with a Xenon discharge lamp as an excitation source and a R928 photomultiplier (HAMAMATSU, Hamamatsu, Japan) as detector. The excitation radiation (300 nm) was directed onto the surface of the samples at an angle of 90°.

3.4. Measurement of Photocatalytic Activity

The photocatalytic activity of the as-prepared NTs was analyzed, for the first time, in the purification of air from toluene, which was used as a model pollutant. The photodegradation experiments were carried out in a stainless-steel reactor with a volume of ca. 35 cm3. The reactor included a quartz window, two valves, and a septum. The light source consisting of an array of 25 LEDs (λmax = 375, 415 and 465 nm, Optel, Opole, Poland) was located above the sample. The anodized foil was placed at the bottom side of the reactor and it was closed with the quartz window. A gas mixture (200 ppmv) was passed through the reactor during 1 min, the valves were then closed, and the reactor was kept in the dark for 30 min in order to achieve the equilibrium. Before starting the irradiation, a reference toluene sample was taken. The concentration was determined by using a gas chromatograph (TRACE 1300, Thermo Scientific, Waltham, MA, USA), equipped with an ionization flame detector (FID) and an Elite-5 capillary column. The samples (200 μL) were dosed with a gas-tight syringe for 10 min.

4. Conclusions

In summary, V2O5-TiO2 mixed oxide layers were successfully synthesized through the one-step anodization of Ti-V alloys in a fluoride-containing EG-based electrolyte. The obtained layers exhibited a sponge-like and nanotubular structure with highly enhanced optical and visible-light-photocatalytic properties, in contrast with pristine TiO2 NTs. The photoactivity of these anodically-obtained composites was evaluated for the first time in the degradation of toluene (200 ppmv) in the gas phase under visible light, with a twenty-five-LED array as the irradiation source (λmax = 465 nm). All of the V2O5-TiO2 samples were reported as photoactive and the initial degradation reaction rate was in the range of 4.50–7.08 × 10−2 μmol·dm−3·min−1. The visible light harvesting was attributed to the presence of the narrow-bandgap V2O5 species in the matrix of the V2O5-TiO2 composites. A morphological study was also reported and the vanadium content in the alloy was found as the key factor limiting the self-ordering of the electrochemically prepared thin layers. The highest photoactivity under visible light (465 nm) was observed in the presence of the Ti85V15_40V_5% sample. This sample not only exhibited the highest absorbance intensity at about 500 nm, but also reported the highest diameter (103 nm), the optimum length (0.9 μm), and the largest crystallite size (36 nm) among all of the modified samples. EDX analysis revealed that the vanadium content in this sample was equal to 9.08 wt %. In sum, the photocatalytic properties of these highly efficient nanocomposites, obtained through the most suitable method (electrochemical technique), permit new insights into the exploitation of industrially oriented applications, for instance, photocatalytic devices for air purification. The presented materials are photoactive under a low powered light source, and thus, the use of low cost light-emitting diodes (LEDs) as an irradiation source can significantly reduce the cost of photocatalytic air treatment processes, which is consistent with the principles of green chemistry.

Acknowledgments

This research was financially supported by the Polish National Science Center (research grant, Ordered TiO2/MxOy nanostructures obtained by electrochemical method; contract no. NCN 2014/15/B/ST5/00098).

Author Contributions

A.Z.-M. supervised and directed the project; A.Z.-M. and P.M. conceived the concept; M.C.N.-M., P.M., M.P.K., G.K., A.M., M.K. and G.S. performed the experiments; M.C.N.-M. and P.M. analyzed the data; M.C.N.-M. and P.M. contributed reagents/materials/analysis tools; M.C.N-M., P.M, P.J.E.-M. and A.Z.-M. wrote the paper.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Ghicov, A.; Schmidt, B.; Kunze, J.; Schmuki, P. Photoresponse in the visible range from Cr doped TiO2 nanotubes. Chem. Phys. Lett. 2007, 433, 323–326. [Google Scholar] [CrossRef]
  2. Kubacka, A.; Fernandez-Garcia, M.; Colon, G. Advanced nanoarchitectures for solar photocatalytic applications. Chem. Rev. 2012, 112, 1555–1614. [Google Scholar] [CrossRef] [PubMed]
  3. Schneider, J.; Bahnemann, D.; Ye, J.; Puma, G.L.; Dionysiou, D.D. Photocatalysis: Fundamentals and Perspectives; Royal Society of Chemistry: Cambridge, UK, 2016. [Google Scholar]
  4. Dionysiou, D.D.; Puma, G.L.; Ye, J.; Schneider, J.; Bahnemann, D. Photocatalysis: Applications; Royal Society of Chemistry: Cambridge, UK, 2016. [Google Scholar]
  5. Pichat, P. Photocatalysis: Fundamentals, Materials and Potential; MDPI: Basel, Switzerland, 2016. [Google Scholar]
  6. Colmenares Quintero, J.C.; Xu, Y.-J. Heterogeneous Photocatalysis: From Fundamentals to Green Applications; Springer: Berlin/Heidelberg, Germany, 2016; Volume 8, p. 416. [Google Scholar]
  7. Fattakhova-Rohlfing, D.; Zaleska, A.; Bein, T. Three-dimensional titanium dioxide nanomaterials. Chem. Rev. 2014, 114, 9487–9558. [Google Scholar] [CrossRef] [PubMed]
  8. Daghrir, R.; Drogui, P.; Robert, D. Modified TiO2 for environmental photocatalytic applications: A review. Ind. Eng. Chem. Res. 2013, 52, 3581–3599. [Google Scholar] [CrossRef]
  9. Ahmed, S.; Rasul, M.G.; Brown, R.; Hashib, M.A. Influence of parameters on the heterogeneous photocatalytic degradation of pesticides and phenolic contaminants in wastewater: A short review. J. Environ. Manag. 2011, 92, 311–330. [Google Scholar] [CrossRef] [PubMed]
  10. Pichat, P. Photocatalysis and Water Purification: From Fundamentals to Recent Applications; John Wiley & Sons: Weinheim, Germany, 2013. [Google Scholar]
  11. Kang, D.; Kim, T.W.; Kubota, S.R.; Cardiel, A.C.; Cha, H.G.; Choi, K.S. Electrochemical synthesis of photoelectrodes and catalysts for use in solar water splitting. Chem. Rev. 2015, 115, 12839–12887. [Google Scholar] [CrossRef] [PubMed]
  12. Highfield, J. Advances and recent trends in heterogeneous photo(electro)-catalysis for solar fuels and chemicals. Molecules 2015, 20, 6739–6793. [Google Scholar] [CrossRef] [PubMed]
  13. Ye, M.; Zheng, D.; Wang, M.; Chen, C.; Liao, W.; Lin, C.; Lin, Z. Hierarchically structured microspheres for high-efficiency rutile TiO2-based dye-sensitized solar cells. ACS Appl. Mater. Interfaces 2014, 6, 2893–2901. [Google Scholar] [CrossRef] [PubMed]
  14. Low, J.; Cheng, B.; Yu, J. Surface modification and enhanced photocatalytic CO2 reduction performance of Tio2: A review. Appl. Surf. Sci. 2017, 392, 658–686. [Google Scholar] [CrossRef]
  15. Wang, R.; Hashimoto, K.; Fujishima, A.; Chikuni, M.; Kojima, E.; Kitamura, A.; Shimohigoshi, M.; Watanabe, T. Light-induced amphiphilic surfaces. Nature 1997, 388, 431–432. [Google Scholar] [CrossRef]
  16. Pichat, P. Self-cleaning materials based on solar photocatalysis. In New and Future Developments in Catalysis: Solar Photocatalysis; Suib, S.L., Ed.; Elsevier: Amsterdam, The Netherlands, 2013; Volume 7, pp. 167–190. [Google Scholar]
  17. Li, Z.; Luo, W.; Zhang, M.; Feng, J.; Zou, Z. Photoelectrochemical cells for solar hydrogen production: Current state of promising photoelectrodes, methods to improve their properties, and outlook. Energy Environ. Sci. 2013, 6, 347–370. [Google Scholar] [CrossRef]
  18. Pfitzner, A.; Dankesreiter, S.; Eisenhofer, A.; Cherevatskaya, M. Heterogeneous semiconductor photocatalysis. In Chemical Photocatalysis; König, B., Ed.; De Gruyter: Berlin, Germany, 2013. [Google Scholar]
  19. Skinner, D.E.; Colombo, D.P.; Cavaleri, J.J.; Bowman, R.M. Femtosecond investigation of electron trapping in semiconductor nanoclusters. J. Phys. Chem. 1995, 99, 7853–7856. [Google Scholar] [CrossRef]
  20. Banerjee, S.; Pillai, S.C.; Falaras, P.; O’Shea, K.E.; Byrne, J.A.; Dionysiou, D.D. New insights into the mechanism of visible light photocatalysis. J. Phys. Chem. Lett. 2014, 5, 2543–2554. [Google Scholar] [CrossRef] [PubMed]
  21. Wang, Z.; Ma, W.; Chen, C.; Zhao, J. Sensitization of titania semiconductor: A promising strategy to utilize visible light. In Photocatalysis and Water Purification; Pichat, P., Ed.; Wiley-VCH: Weinheim, Germany, 2013; pp. 199–240. [Google Scholar]
  22. Choi, W.; Termin, A.; Hoffmann, M.R. The role of metal ion dopants in quantum-sized TiO2: Correlation between photoreactivity and charge carrier recombination dynamics. J. Phys. Chem. 1994, 98, 13669–13679. [Google Scholar] [CrossRef]
  23. Asahi, R.; Morikawa, T.; Ohwaki, T.; Aoki, K.; Taga, Y. Visible-light photocatalysis in nitrogen-doped titanium oxides. Science 2001, 293, 269–271. [Google Scholar] [CrossRef] [PubMed]
  24. Li, D.; Haneda, H.; Labhsetwar, N.K.; Hishita, S.; Ohashi, N. Visible-light-driven photocatalysis on fluorine-doped TiO2 powders by the creation of surface oxygen vacancies. Chem. Phys. Lett. 2005, 401, 579–584. [Google Scholar] [CrossRef]
  25. Mazierski, P.; Nischk, M.; Gołkowska, M.; Lisowski, W.; Gazda, M.; Winiarski, M.J.; Klimczuk, T.; Zaleska-Medynska, A. Photocatalytic activity of nitrogen doped TiO2 nanotubes prepared by anodic oxidation: The effect of applied voltage, anodization time and amount of nitrogen dopant. Appl. Catal. B Environ. 2016, 196, 77–88. [Google Scholar] [CrossRef]
  26. Mazierski, P.; Lisowski, W.; Grzyb, T.; Winiarski, M.J.; Klimczuk, T.; Mikołajczyk, A.; Flisikowski, J.; Hirsch, A.; Kołakowska, A.; Puzyn, T.; et al. Enhanced photocatalytic properties of lanthanide-TiO2 nanotubes: An experimental and theoretical study. Appl. Catal. B Environ. 2017, 205, 376–385. [Google Scholar] [CrossRef]
  27. Chatterjee, D.; Mahata, A. Demineralization of organic pollutants on the dye modified TiO2 semiconductor particulate system using visible light. Appl. Catal. B Environ. 2001, 33, 119–125. [Google Scholar] [CrossRef]
  28. Hirai, T.; Suzuki, K.; Komasawa, I. Preparation and photocatalytic properties of composite CdS nanoparticles–titanium dioxide particles. J. Colloid Interface Sci. 2001, 244, 262–265. [Google Scholar] [CrossRef]
  29. Zielińska-Jurek, A.; Zaleska, A. Ag/Pt-modified TiO2 nanoparticles for toluene photooxidation in the gas phase. Catal. Today 2014, 230, 104–111. [Google Scholar] [CrossRef]
  30. Nischk, M.; Mazierski, P.; Wei, Z.; Siuzdak, K.; Kouame, N.A.; Kowalska, E.; Remita, H.; Zaleska-Medynska, A. Enhanced photocatalytic, electrochemical and photoelectrochemical properties of TiO2 nanotubes arrays modified with Cu, AgCu and Bi nanoparticles obtained via radiolytic reduction. Appl. Surf. Sci. 2016, 387, 89–102. [Google Scholar] [CrossRef] [PubMed]
  31. Pichat, P. Surface-properties, activity and selectivity of bifunctional powder photocatalysts. New J. Chem. 1987, 11, 135–140. [Google Scholar]
  32. Wu, Z.; Dong, F.; Liu, Y.; Wang, H. Enhancement of the visible light photocatalytic performance of C-doped TiO2 by loading with V2O5. Catal. Commun. 2009, 11, 82–86. [Google Scholar] [CrossRef]
  33. Wang, Y.; Zhang, J.; Liu, L.; Zhu, C.; Liu, X.; Su, Q. Visible light photocatalysis of V2O5/TiO2 nanoheterostructures prepared via electrospinning. Mater. Lett. 2012, 75, 95–98. [Google Scholar] [CrossRef]
  34. Yang, X.; Ma, F.; Li, K.; Guo, Y.; Hu, J.; Li, W.; Huo, M.; Guo, Y. Mixed phase titania nanocomposite codoped with metallic silver and vanadium oxide: New efficient photocatalyst for dye degradation. J. Hazard. Mater. 2010, 175, 429–438. [Google Scholar] [CrossRef] [PubMed]
  35. Wang, Y.; Su, Y.R.; Qiao, L.; Liu, L.X.; Su, Q.; Zhu, C.Q.; Liu, X.Q. Synthesis of one-dimensional TiO2/V2O5 branched heterostructures and their visible light photocatalytic activity towards rhodamine b. Nanotechnology 2011, 22, 225702. [Google Scholar] [CrossRef] [PubMed]
  36. Li, B.; Xu, Y.; Rong, G.; Jing, M.; Xie, Y. Vanadium pentoxide nanobelts and nanorolls: From controllable synthesis to investigation of their electrochemical properties and photocatalytic activities. Nanotechnology 2006, 17, 2560–2566. [Google Scholar] [CrossRef] [PubMed]
  37. Fei, H.-L.; Zhou, H.-J.; Wang, J.-G.; Sun, P.-C.; Ding, D.-T.; Chen, T.-H. Synthesis of hollow V2O5 microspheres and application to photocatalysis. Solid State Sci. 2008, 10, 1276–1284. [Google Scholar] [CrossRef]
  38. Shahid, M.; Rhen, D.S.; Shakir, I.; Patole, S.P.; Yoo, J.B.; Yang, S.-J.; Kang, D.J. Facile synthesis of single crystalline vanadium pentoxide nanowires and their photocatalytic behavior. Mater. Lett. 2010, 64, 2458–2461. [Google Scholar] [CrossRef]
  39. Qiu, G.; Dharmarathna, S.; Genuino, H.; Zhang, Y.; Huang, H.; Suib, S.L. Facile microwave-refluxing synthesis and catalytic properties of vanadium pentoxide nanomaterials. ACS Catal. 2011, 1, 1702–1709. [Google Scholar] [CrossRef]
  40. Shen, T.F.R.; Lai, M.-H.; Yang, T.C.K.; Fu, I.P.; Liang, N.-Y.; Chen, W.-T. Photocatalytic production of hydrogen by vanadium oxides under visible light irradiation. J. Taiwan Inst. Chem. Eng. 2012, 43, 95–101. [Google Scholar] [CrossRef]
  41. Aslam, M.; Ismail, I.M.; Salah, N.; Chandrasekaran, S.; Qamar, M.T.; Hameed, A. Evaluation of sunlight induced structural changes and their effect on the photocatalytic activity of V2O5 for the degradation of phenols. J. Hazard. Mater. 2015, 286, 127–135. [Google Scholar] [CrossRef] [PubMed]
  42. Xie, L.; Liu, P.; Zheng, Z.; Weng, S.; Huang, J. Morphology engineering of V2O5/TiO2 nanocomposites with enhanced visible light-driven photofunctions for arsenic removal. Appl. Catal. B Environ. 2016, 184, 347–354. [Google Scholar] [CrossRef]
  43. Choi, S.; Lee, M.-S.; Park, D.-W. Photocatalytic performance of TiO2/V2O5 nanocomposite powder prepared by DC arc plasma. Curr. Appl. Phys. 2014, 14, 433–438. [Google Scholar] [CrossRef]
  44. Zhu, K.; Neale, N.R.; Miedaner, A.; Frank, A.J. Enhanced charge-collection efficiencies and light scattering in dye-sensitized solar cells using oriented TiO2 nanotubes arrays. Nano Lett. 2007, 7, 69–74. [Google Scholar] [CrossRef] [PubMed]
  45. Lee, K.; Mazare, A.; Schmuki, P. One-dimensional titanium dioxide nanomaterials: Nanotubes. Chem. Rev. 2014, 114, 9385–9454. [Google Scholar] [CrossRef] [PubMed]
  46. Macak, J.M.; Schmuki, P. Anodic growth of self-organized anodic TiO2 nanotubes in viscous electrolytes. Electrochim. Acta 2006, 52, 1258–1264. [Google Scholar] [CrossRef]
  47. Pichat, P. Are TiO2 nanotubes worth using in photocatalytic purification of air and water? Molecules 2014, 19, 15075–15087. [Google Scholar] [CrossRef] [PubMed]
  48. Albu, S.P.; Ghicov, A.; Macak, J.M.; Schmuki, P. 250 µm long anodic TiO2 nanotubes with hexagonal self-ordering. Phys. Status Solidi–R. 2007, 1, R65–R67. [Google Scholar] [CrossRef]
  49. Khudhair, D.; Bhatti, A.; Li, Y.; Hamedani, H.A.; Garmestani, H.; Hodgson, P.; Nahavandi, S. Anodization parameters influencing the morphology and electrical properties of TiO2 nanotubes for living cell interfacing and investigations. Mater. Sci. Eng. C 2016, 59, 1125–1142. [Google Scholar] [CrossRef] [PubMed]
  50. Nischk, M.; Mazierski, P.; Gazda, M.; Zaleska, A. Ordered TiO2 nanotubes: The effect of preparation parameters on the photocatalytic activity in air purification process. Appl. Catal. B Environ. 2014, 144, 674–685. [Google Scholar] [CrossRef]
  51. Mazierski, P.; Nadolna, J.; Lisowski, W.; Winiarski, M.J.; Gazda, M.; Nischk, M.; Klimczuk, T.; Zaleska-Medynska, A. Effect of irradiation intensity and initial pollutant concentration on gas phase photocatalytic activity of TiO2 nanotube arrays. Catal. Today 2016, 284, 19–26. [Google Scholar] [CrossRef]
  52. Bashirom, N.; Razak, K.A.; Yew, C.K.; Lockman, Z. Effect of fluoride or chloride ions on the morphology of ZrO2 thin film grown in ethylene glycol electrolyte by anodization. Procedia Chem. 2016, 19, 611–618. [Google Scholar] [CrossRef]
  53. Tsuchiya, H.; Schmuki, P. Self-organized high aspect ratio porous hafnium oxide prepared by electrochemical anodization. Electrochem. Commun. 2005, 7, 49–52. [Google Scholar] [CrossRef]
  54. Jha, H.; Hahn, R.; Schmuki, P. Ultrafast oxide nanotube formation on TiNb, TiZr and TiTa alloys by rapid breakdown anodization. Electrochim. Acta 2010, 55, 8883–8887. [Google Scholar] [CrossRef]
  55. Yang, Y.; Kim, D.; Schmuki, P. Electrochromic properties of anodically grown mixed V2O5-TiO2 nanotubes. Electrochem. Commun. 2011, 13, 1021–1025. [Google Scholar] [CrossRef]
  56. Yang, Y.; Kim, D.; Yang, M.; Schmuki, P. Vertically aligned mixed V2O5-TiO2 nanotube arrays for supercapacitor applications. Chem. Commun. 2011, 47, 7746–7748. [Google Scholar] [CrossRef] [PubMed]
  57. Paramasivam, I.; Nah, Y.C.; Das, C.; Shrestha, N.K.; Schmuki, P. WO3/TiO2 nanotubes with strongly enhanced photocatalytic activity. Chemistry 2010, 16, 8993–8997. [Google Scholar] [CrossRef] [PubMed]
  58. Ning, X.; Wang, X.; Yu, X.; Li, J.; Zhao, J. Preparation and capacitance properties of Mn-doped TiO2 nanotube arrays by anodisation of Ti-Mn alloy. J. Alloys Compd. 2016, 658, 177–182. [Google Scholar] [CrossRef]
  59. Allam, N.K.; Deyab, N.M.; Abdel Ghany, N. Ternary Ti-Mo-Ni mixed oxide nanotube arrays as photoanode materials for efficient solar hydrogen production. Phys. Chem. Chem. Phys. 2013, 15, 12274–12282. [Google Scholar] [CrossRef] [PubMed]
  60. Luo, B.; Yang, H.; Liu, S.; Fu, W.; Sun, P.; Yuan, M.; Zhang, Y.; Liu, Z. Fabrication and characterization of self-organized mixed oxide nanotube arrays by electrochemical anodization of Ti-6Al-4V alloy. Mater. Lett. 2008, 62, 4512–4515. [Google Scholar] [CrossRef]
  61. Mazierski, P.; Malankowska, A.; Kobylański, M.; Diak, M.; Kozak, M.; Winiarski, M.J.; Klimczuk, T.; Lisowski, W.; Nowaczyk, G.; Zaleska-Medynska, A. Photocatalytically active TiO2/Ag2O nanotube arrays interlaced with silver nanoparticles obtained from the one-step anodic oxidation of Ti-Ag alloys. ACS Catal. 2017, 7, 2753–2764. [Google Scholar] [CrossRef]
  62. Ding, J.; Huang, Z.; Zhu, J.; Kou, S.; Zhang, X.; Yang, H. Low-temperature synthesis of high-ordered anatase TiO2 nanotube array films coated with exposed {001} nanofacets. Sci. Rep. 2015, 5, 17773. [Google Scholar] [CrossRef] [PubMed]
  63. Nevárez-Martínez, M.C.; Mazierski, P.; Kobylański, M.; Szczepańska, G.; Trykowski, G.; Malankowska, A.; Kozak, M.; Espinoza-Montero, P.J.; Zaleska-Medynska, A. Self-organized TiO2-MnO2 nanotube arrays for efficient photocatalytic degradation of toluene. Molecules 2017, 22, 564. [Google Scholar] [CrossRef] [PubMed]
  64. Macak, J.M.; Tsuchiya, H.; Ghicov, A.; Yasuda, K.; Hahn, R.; Bauer, S.; Schmuki, P. TiO2 nanotubes: Self-organized electrochemical formation, properties and applications. Curr. Opin. Solid State Mater. Sci. 2007, 11, 3–18. [Google Scholar] [CrossRef]
  65. Wood, G.C.; Khoo, S.W. The mechanism of anodic oxidation of alloys. J. Appl. Electrochem. 1971, 1, 189–206. [Google Scholar] [CrossRef]
  66. Cox, B. 186. Complex fluorides. Part IV. The structural chemistry of complex fluorides of the general formula ABF6. J. Chem. Soc. 1956, 876–878. [Google Scholar] [CrossRef]
  67. Wu, J.C.S.; Chen, C.-H. A visible-light response vanadium-doped titania nanocatalyst by sol-gel method. J. Photochem. Photobiol. A Chem. 2004, 163, 509–515. [Google Scholar] [CrossRef]
  68. Nishanthi, S.T.; Subramanian, E.; Sundarakannan, B.; Padiyan, D.P. An insight into the influence of morphology on the photoelectrochemical activity of TiO2 nanotube arrays. Sol. Energy Mater. Sol. Cell 2015, 132, 204–209. [Google Scholar] [CrossRef]
  69. Tang, H.; Berger, H.; Schmid, P.E.; Lévy, F. Optical properties of anatase (TiO2). Solid State Commun. 1994, 92, 267–271. [Google Scholar] [CrossRef]
  70. Knorr, F.J.; Mercado, C.C.; McHale, J.L. Trap-state distributions and carrier transport in pure and mixed-phase TiO2: Influence of contacting solvent and interphasial electron transfer. J. Phys. Chem. C 2008, 112, 12786–12794. [Google Scholar] [CrossRef]
  71. Chin, S.; Park, E.; Kim, M.; Jurng, J. Photocatalytic degradation of methylene blue with TiO2 nanoparticles prepared by a thermal decomposition process. Powder Technol. 2010, 201, 171–176. [Google Scholar] [CrossRef]
  72. Zhang, W.; He, Y.; Zhang, M.; Yin, Z.; Chen, Q. Raman scattering study on anatase TiO2 nanocrystals. J. Phys. D Appl. Phys. 2000, 33, 912. [Google Scholar] [CrossRef]
  73. Wu, Z.; Dong, F.; Zhao, W.; Wang, H.; Liu, Y.; Guan, B. The fabrication and characterization of novel carbon doped TiO2 nanotubes, nanowires and nanorods with high visible light photocatalytic activity. Nanotechnology 2009, 20, 235701. [Google Scholar] [CrossRef] [PubMed]
  74. Borbón-Nuñez, H.A.; Dominguez, D.; Muñoz-Muñoz, F.; Lopez, J.; Romo-Herrera, J.; Soto, G.; Tiznado, H. Fabrication of hollow TiO2 nanotubes through atomic layer deposition and MWCNT templates. Powder Technol. 2017, 308, 249–257. [Google Scholar] [CrossRef]
  75. Sethi, D.; Jada, N.; Tiwari, A.; Ramasamy, S.; Dash, T.; Pandey, S. Photocatalytic destruction of escherichia coli in water by V2O5/TiO2. J. Photochem. Photobiol. B 2015, 144, 68–74. [Google Scholar] [CrossRef] [PubMed]
  76. Ohsaka, T.; Izumi, F.; Fujiki, Y. Raman spectrum of anatase, TiO2. J. Raman Spectrosc. 1978, 7, 321–324. [Google Scholar] [CrossRef]
  77. Kim, Y.S.; Song, M.Y.; Park, E.S.; Chin, S.; Bae, G.N.; Jurng, J. Visible-light-induced bactericidal activity of vanadium-pentoxide (V2O5)-loaded TiO2 nanoparticles. Appl. Biochem. Biotechnol. 2012, 168, 1143–1152. [Google Scholar] [CrossRef] [PubMed]
Sample Availability: Samples of the compounds are available from the authors.
Molecules 22 00580 g001 550
Figure 1. Top-view and cross-sectional scanning electron microscopy (SEM) images of pristine TiO2 nanotubes (NTs) and Ti-V anodized alloys.
Figure 1. Top-view and cross-sectional scanning electron microscopy (SEM) images of pristine TiO2 nanotubes (NTs) and Ti-V anodized alloys.
Molecules 22 00580 g001
Molecules 22 00580 g002 550
Figure 2. Current density-time curves recorded for the anodization of technical grade Ti foil and Ti-V alloys for the study of (a) applied voltage; (b) vanadium content in the alloy; and (c) water content in the electrolyte. SEM images of Ti90V10_40V sample anodized during (d) 4 min; (e) 15 min; and (f) 60 min.
Figure 2. Current density-time curves recorded for the anodization of technical grade Ti foil and Ti-V alloys for the study of (a) applied voltage; (b) vanadium content in the alloy; and (c) water content in the electrolyte. SEM images of Ti90V10_40V sample anodized during (d) 4 min; (e) 15 min; and (f) 60 min.
Molecules 22 00580 g002
Molecules 22 00580 g003 550
Figure 3. Energy-dispersive X-ray spectroscopy (EDX) mapping of the Ti85V15_40V_5% sample.
Figure 3. Energy-dispersive X-ray spectroscopy (EDX) mapping of the Ti85V15_40V_5% sample.
Molecules 22 00580 g003
Molecules 22 00580 g004 550
Figure 4. UV-Vis spectra of pristine TiO2 NTs and V2O5-TiO2 nanostructures (NS). Effect of (a) anodization potential; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Figure 4. UV-Vis spectra of pristine TiO2 NTs and V2O5-TiO2 nanostructures (NS). Effect of (a) anodization potential; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Molecules 22 00580 g004
Molecules 22 00580 g005 550
Figure 5. Photoluminescence spectra of pristine TiO2 NTs and V2O5-TiO2 NS. Effect of (a) anodization potential; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Figure 5. Photoluminescence spectra of pristine TiO2 NTs and V2O5-TiO2 NS. Effect of (a) anodization potential; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Molecules 22 00580 g005
Molecules 22 00580 g006 550
Figure 6. X-ray diffraction (XRD) spectra of pristine TiO2 NTs and V2O5-TiO2 NS. Effect of (a) anodization potential; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Figure 6. X-ray diffraction (XRD) spectra of pristine TiO2 NTs and V2O5-TiO2 NS. Effect of (a) anodization potential; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Molecules 22 00580 g006
Molecules 22 00580 g007 550
Figure 7. Raman spectra of pristine TiO2 NTs and V2O5-TiO2 NS. Effect of (a) anodization potential; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Figure 7. Raman spectra of pristine TiO2 NTs and V2O5-TiO2 NS. Effect of (a) anodization potential; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Molecules 22 00580 g007
Molecules 22 00580 g008 550
Figure 8. Photoactivity of pristine TiO2 NTs and V2O5-TiO2 NS in gas phase degradation of toluene under Vis-light irradiation (λmax = 465 nm). Effect of (a) applied voltage; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Figure 8. Photoactivity of pristine TiO2 NTs and V2O5-TiO2 NS in gas phase degradation of toluene under Vis-light irradiation (λmax = 465 nm). Effect of (a) applied voltage; (b) vanadium content in the alloy; and (c) water content in the electrolyte.
Molecules 22 00580 g008
Molecules 22 00580 g009 550
Figure 9. Photoactivity of Ti85V15_40V_5% sample in gas phase degradation of toluene under different wavelengths of irradiation (λmax = 375, 415, 465 nm).
Figure 9. Photoactivity of Ti85V15_40V_5% sample in gas phase degradation of toluene under different wavelengths of irradiation (λmax = 375, 415, 465 nm).
Molecules 22 00580 g009
Molecules 22 00580 g010 550
Figure 10. Excitation mechanism of V2O5-TiO2 samples under visible light irradiation.
Figure 10. Excitation mechanism of V2O5-TiO2 samples under visible light irradiation.
Molecules 22 00580 g010
Table
Table 1. Sample labels, preparation parameters, characterization, and photocatalytic activity of V2O5-TiO2 nanotubes under Vis irradiation.
Table 1. Sample labels, preparation parameters, characterization, and photocatalytic activity of V2O5-TiO2 nanotubes under Vis irradiation.
Sample LabelPreparation ParametersExternal Diameter (nm)Tube Length (μm)Wall Thickness (nm)Average Crystallite Size (nm)EDX AnalysisPhotoactivity Vis Light (λmax = 465 nm)
ElectrolyteApplied Potential (V)Ti (wt %)V (wt %)C (wt %)O (wt %)Initial Reaction Rate × 102 (μmol·dm−3·min−1)Reaction Rate Constant × 103 (min−1)
Ti90V10_30VEG 98% (v/v), H2O 2% (v/v), NH4F 0.09 M30610.8133174.617.610.0117.785.345.98
Ti90V10_40VEG 98% (v/v), H2O 2% (v/v), NH4F 0.09 M40910.3193273.847.390.0118.786.767.57
Ti90V10_50VEG 98% (v/v), H2O 2% (v/v), NH4F 0.09 M501010.4303069.346.850.0123.796.567.35
Ti85V15_40V_2%EG 98% (v/v), H2O 2% (v/v), NH4F 0.09 M40Sponge-like structure3173.0912.140.0114.786.627.41
Ti85V15_40V_5%EG 95% (v/v), H2O 5% (v/v), NH4F 0.09 M401030.9203667.069.081.1022.777.087.92
Ti85V15_40V_10%EG 90% (v/v), H2O 10% (v/v), NH4F 0.09 M40Sponge-like structure3266.108.911.1423.864.505.04
Ti95V5_40VEG 98% (v/v), H2O 2% (v/v), NH4F 0.09 M40861.0113372.593.250.0224.145.396.04
Ti_30VEG 98% (v/v), H2O 2% (v/v), NH4F 0.09 M30811.5103371.470.000.1928.340.370.42
Ti_40VEG 98% (v/v), H2O 2% (v/v), NH4F 0.09 M401005.0133466.730.000.0333.240.430.49
Ti_50VEG 98% (v/v), H2O 2% (v/v), NH4F 0.09 M5012016.2183867.690.000.0332.280.640.72

Share and Cite

MDPI and ACS Style

Nevárez-Martínez, M.C.; Mazierski, P.; Kobylański, M.P.; Szczepańska, G.; Trykowski, G.; Malankowska, A.; Kozak, M.; Espinoza-Montero, P.J.; Zaleska-Medynska, A. Growth, Structure, and Photocatalytic Properties of Hierarchical V2O5–TiO2 Nanotube Arrays Obtained from the One-step Anodic Oxidation of Ti–V Alloys. Molecules 2017, 22, 580. https://doi.org/10.3390/molecules22040580

AMA Style

Nevárez-Martínez MC, Mazierski P, Kobylański MP, Szczepańska G, Trykowski G, Malankowska A, Kozak M, Espinoza-Montero PJ, Zaleska-Medynska A. Growth, Structure, and Photocatalytic Properties of Hierarchical V2O5–TiO2 Nanotube Arrays Obtained from the One-step Anodic Oxidation of Ti–V Alloys. Molecules. 2017; 22(4):580. https://doi.org/10.3390/molecules22040580

Chicago/Turabian Style

Nevárez-Martínez, María C., Paweł Mazierski, Marek P. Kobylański, Grażyna Szczepańska, Grzegorz Trykowski, Anna Malankowska, Magda Kozak, Patricio J. Espinoza-Montero, and Adriana Zaleska-Medynska. 2017. "Growth, Structure, and Photocatalytic Properties of Hierarchical V2O5–TiO2 Nanotube Arrays Obtained from the One-step Anodic Oxidation of Ti–V Alloys" Molecules 22, no. 4: 580. https://doi.org/10.3390/molecules22040580

APA Style

Nevárez-Martínez, M. C., Mazierski, P., Kobylański, M. P., Szczepańska, G., Trykowski, G., Malankowska, A., Kozak, M., Espinoza-Montero, P. J., & Zaleska-Medynska, A. (2017). Growth, Structure, and Photocatalytic Properties of Hierarchical V2O5–TiO2 Nanotube Arrays Obtained from the One-step Anodic Oxidation of Ti–V Alloys. Molecules, 22(4), 580. https://doi.org/10.3390/molecules22040580