Next Article in Journal
UVC Stokes and Anti-Stokes Emission of Ca9Y(PO4)7 Polycrystals Doped with Pr3+ Ions
Previous Article in Journal
Enhancing the Conductivity and Dielectric Characteristics of Bismuth Oxyiodide via Activated Carbon Doping
Previous Article in Special Issue
Direct Homogeneous Synthesis of Compounds with Two O Atoms and Long-Chain Hydrocarbons from CO and H2: Co–Ru/N-methylpyrrolidone Catalyst
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 29
Issue 9
10.3390/molecules29092083
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Chitosan as a Bio-Based Ligand for the Production of Hydrogenation Catalysts

by
Stefano Paganelli
1,2,*,
Eleonora Brugnera
1,
Alessandro Di Michele
3,
Manuela Facchin
1 and
Valentina Beghetto
1,2,4,*
1
Department of Molecular Sciences and Nanosystems, University Ca’ Foscari of Venice, Via Torino 155, 30172 Mestre, Italy
2
Consorzio Interuniversitario per le Reattività Chimiche e la Catalisi (CIRCC), Via C. Ulpiani 27, 70126 Bari, Italy
3
Dipartimento Fisica e Geologia, Università degli Studi di Perugia, Via Pascoli, 06123 Perugia, Italy
4
Crossing S.R.L., Viale della Repubblica 193/b, 31100 Treviso, Italy
*
Authors to whom correspondence should be addressed.
Molecules 2024, 29(9), 2083; https://doi.org/10.3390/molecules29092083
Submission received: 27 March 2024 / Revised: 24 April 2024 / Accepted: 26 April 2024 / Published: 1 May 2024
(This article belongs to the Special Issue Green Organic Synthesis: Novel Approaches)
Browse Figures
Versions Notes

Abstract

:
Bio-based polymers are attracting increasing interest as alternatives to harmful and environmentally concerning non-biodegradable fossil-based products. In particular, bio-based polymers may be employed as ligands for the preparation of metal nanoparticles (M(0)NPs). In this study, chitosan (CS) was used for the stabilization of Ru(0) and Rh(0) metal nanoparticles (MNPs), prepared by simply mixing RhCl3 × 3H2O or RuCl3 with an aqueous solution of CS, followed by NaBH4 reduction. The formation of M(0)NPs-CS was confirmed by Fourier Transform Infrared Spectroscopy (FT-IR), Differential Scanning Calorimetry (DSC), Thermal Gravimetric Analysis (TGA), Scanning Electron Microscopy (SEM), Energy-Dispersive X-ray Analysis (EDX), Transmission Electron Microscopy (TEM) and X-ray Diffraction (XRD). Their size was estimated to be below 40 nm for Rh(0)-CS and 10nm for Ru(0)-CS by SEM analysis. M(0)NPs-CS were employed for the hydrogenation of (E)-cinnamic aldehyde and levulinic acid. Easy recovery by liquid-liquid extraction made it possible to separate the catalyst from the reaction products. Recycling experiments demonstrated that M(0)NPs-CS were highly efficient up to four times in the best hydrogenation conditions. The data found in this study show that CS is an excellent ligand for the stabilization of Rh(0) and Ru(0) nanoparticles, allowing the production of some of the most efficient, selective and recyclable hydrogenation catalysts known in the literature.

Graphical Abstract

1. Introduction

The environmental impact of fossil-based non-biodegradable materials is pushing for their substitution with bio-based ones [1,2,3,4,5,6]. Nevertheless, most products commercialized today are still produced from virgin naphtha [7,8], and their inadequate disposal has turned into a major environmental emergency [9,10]. The use of bio-based polymers appears to be a very interesting and eco-friendly alternative to the use of fossil-based polymers [11,12,13,14,15], and many examples are reported in the literature regarding the use of renewable and very abundant biopolymers, such as carboxymethyl cellulose, starch and chitosan, for different industrial applications [16,17,18,19,20,21,22,23]. In particular, chitosan (CS), is the second most abundant natural polymer, available in large quantities from food-industry waste, and is a renewable, environmentally friendly, biodegradable polymer. CS, mostly produced by deacetylation of chitin derived from the shells of shrimps and other crustaceans [24,25], is widely used by the food, medical, pharmaceutical and agricultural industries and can also be used for water treatment [26,27,28,29,30]. Its wide range of applications makes CS an appealing material, such that the global market for chitin and derivates is expected to reach US$63 billion by 2024 with production of about 1012–1014 tons/year [31,32].
Due to its a large number of aminic groups and its solubility in water, CS is also a very interesting biopolymer for the stabilization of transition metals for catalytic reactions. In fact, CS has been widely studied as a ligand for the preparation of homogeneous and heterogeneous catalysts employed for carbon-carbon coupling, oxidation, hydrogenation and click reactions, among others [25,33,34,35,36,37,38,39]. Concerning hydrogenation reactions, various examples have been reported in the literature regarding the use of chitosan as a ligand in the presence of Pd(0) and Pd(0) nanoparticles supported on silica [33,36,40,41,42], while Rh(0) and Ru(0) have been investigated less [43,44,45,46].
Based on our interest in the synthesis of fine chemicals by catalytic reactions, we deemed it interesting to study the efficiency of Rh(0) and Ru(0) chitosan nanoparticles (Rh(0)-CS, Ru(0)-CS) for the hydrogenation of (E)-cinnamaldehyde (I) and levulinic acid (V) (Scheme 1) [47,48,49,50]. In fact, (I) contains a C=C double bond and a C=O double bond, making it possible to evaluate both the activity and the selectivity of metal nanoparticles. In fact, hydrogenation of (I) may be employed either for the production of hydrocinnamaldehyde (II) or cinnamyl alcohol (III), which are both very interesting products with wide industrial applications [51,52,53,54]. Additionally, catalytic hydrogenation of levulinic acid makes it possible to produce γ-valerolactone (VI), a promising building block for fuel additives, resins, herbicides, pharmaceuticals, aromatic substances and chemical intermediates with wide application potential [47,48,49,50,51,52,53,54]. Therefore, (E)-cinnamaldehyde (I) and levulinic acid (V) are commonly employed as standard substrates to study the efficiency of hydrogenation catalysts. It is interesting to note that, although many studies have been reported in the literature employing both noble and non-noble homogeneous and heterogeneous catalysts for the hydrogenation of (I) and (V) [55,56,57,58], to the best of our knowledge, chitosan nanoparticles have never been employed for the hydrogenation of (I) or (V) [59,60,61,62,63].
With all this in mind, in this work, metal nanoparticles supported on chitosan (M(0)NPs-CS) were prepared by simply mixing RhCl3 × 3H2O or RuCl3 with an aqueous solution of CS, followed by NaBH4 reduction in analogy to the protocol previously reported by Harrad and co-workers for the preparation of Ni(0)-MNPs [64]. The formation of M(0)NPs-CS was verified by Fourier Transform Infrared Spectroscopy (FT-IR), Differential Scanning Calorimetry (DSC), Thermal Gravimetric Analysis (TGA), Scanning Electron Microscopy (SEM), Energy-Dispersive X-ray Analysis (EDX), Transmission Electron Microscopy (TEM) and X-ray Diffraction (XRD). Thus, the catalytic activity and selectivity of the Rh(0) and Ru(0)-CS nanoparticles was tested in water or water/organic medium for the hydrogenation of (I) and (V). Preliminary hydrogenation reactions in the presence of (I) were carried out to find the best operational conditions, to verify the selectivity of the MNPs towards C=C or C=O hydrogenation and to compare the efficiency of the MNPs studied in this work with data from the literature [65,66,67,68,69].

2. Materials and Methods

2.1. General Remarks

All commercially available reagents, solvents and chemicals were provided by Merck (Milan, Italy) and used as received. Chitosan (MW 90,000 Da), with a deacetylation degree of 0.90, was purchased from G.T.C. Bio Corporation (Qingdao, China). The catalysts and products were characterized by different analytical and spectroscopic analyses such as SEM, EDX, XRD, FT-IR, NMR and GC-MS. Scanning electron microscopy (SEM) was carried out using a FE-SEM LEO 1525 ZEISS (Jena, Germany). The acceleration potential voltage was maintained at 15 keV, and measurements were carried out using an in-lens detector. Samples were deposited on conductive carbon adhesive tape and metallized by sputtering with chromium (8 nm). Elemental composition and chemical mapping were determined using a Bruker Quantax EDX (Karlsruhe, Germany). TEM images were obtained using a Philips 208 transmission electron microscope (FEI, Hillsboro, OR, USA). The samples were prepared by putting one drop of an ethanol dispersion of the sample powder on a copper grid pre-coated with a Formvar film and dried in air. The average size distribution of droplets was determined with ImageJ software (LOCI, University of Wisconsin, Madison, WI, USA) using both SEM and TEM images.
FT-IR spectra were recorded on a Spectrum One (Perkin Elmer) in the 500–4000 cm−1 range. The samples were prepared using the KBr pellet method. TGA and DSC analysis were performed with a Linseis STA PT-1000 instrument (Messgeraete GmbH, Selb, Germany). XRD patterns were collected with a diffractometer in Bragg–Brentano geometry (Bruker D8 Advance, Bruker AXS GmbH, Karlsruhe, Germany), provided with a Lynxeye XE-T fast detector; CuKα radiation was used (operative conditions: 40 keV and 40 mA, step size 0.014° 2θ, step scan 10 s). Bruker DIFFRAC.EVA V5 software (Karlsruhe, Germay) equipped with the COD was used for the phase identification. The samples were prepared by placing the catalyst powder on a copper grid pre-coated with a Formvar film. The 1H and 13C NMR spectra of the products were registered on a Bruker UltraShield 400 spectrometer (Karlsruhe, Germany) operating at 400.0 and 101.0 MHz, respectively. The samples were prepared by dissolving reagents and products in deuterated chloroform (CDCl3). Gas-liquid chromatography analyses were performed on an Agilent 6850 gas chromatograph; gas chromatography–mass spectrometry analyses were performed on an HP 5890 series II gas chromatograph interfaced to a HP 5971 quadrupole mass detector. The samples were prepared by dissolving 3 drops of analyte in 2 mL of diethyl ether. ICP analyses were performed with the ICP MS OES DV 5300, Perkin Elmer (Milan, Italy).

2.2. Preparation of M(0)NPs-CS

The preparation of Rh(0) and Ru(0) nanoparticles stabilized with CS using NaBH4 as a reductant was carried out according to the same procedure for both metals, starting from RhCl3 × 3H2O and RuCl3 respectively. For example, the preparation of Rh(0)-CS (M/CS: 1/8 mol/mol) nanoparticles was as follows: 10 mL of distilled water and 367.0 mg (1.86 mmol) of chitosan hydrochloride were added into a 150 mL two-neck flask, equipped with a magnetic stirring bar, under nitrogen flow and left under stirring until a homogeneous solution was formed (about 1 h). Then, 61.0 mg (0.23 mmol) of RhCl3 × 3H2O and a solution of 200 mg (0.53 mmol) of NaBH4 dissolved in 50 mL of water were added under nitrogen into the reaction flask. The solution was left under stirring for 24 h and then centrifuged, and the solid was dried under vacuum overnight at RT. Ru(0)-CS was prepared analogously, using 47.7 mg (0.23 mmol) of RuCl3.

2.3. General Procedure for the Hydrogenation Reactions with M(0)NPs-CS

Hydrogenation experiments were carried out in a magnetically stirred stainless steel autoclave (total volume 150 mL) connected to a thermostatic bath in order to keep the reaction temperature constant within ± 1 °C. The same experimental protocol was used for hydrogenation reactions and recycling experiments, with all different substrates tested. For example, the procedure for the hydrogenation of (E)-cinnamaldehyde (I) was as follows (entry 1, Table 1). Under an inert atmosphere, in a 50 mL vial equipped with a small magnetic bar, we introduced 2 mL of water, 2 mL of THF, 104 mg (0.79 mmol) of (I), 10.3 mg (7.9 × 10−3 mmol) of catalyst and 12 mg (0.08 mmol) of undecane as an internal standard. Then, the vial was placed in a pre-purged 150 mL autoclave, and 10 atm of H2 was added. The autoclave was then heated at 80 °C and kept under constant magnetic stirring. After 16 h, the autoclave was cooled to room temperature and the residual gas vented off, and the reaction mixture was analysed by gas chromatography to calculate reaction conversion. Products were recovered from the reaction mixture by extraction with diethyl ether, then dried with anhydrous Na2SO4, followed by organic evaporation. Products were characterized by GC-MS, FT-IR and 1H and 13C NMR, and the data were compared to the literature [68,69,70,71]. The water solution was kept under nitrogen and used for recycling experiments. All experiments were performed in triplicate. All recycling experiments were carried out in the same reaction conditions as the first run, unless otherwise specified.
Cinnamaldehyde (I): 1H NMR (300 MHz, CDCl3): δ = 9.46 (d, 1 H), 7.30–7.36 (m, 2 H), 7.16–7.22 (m, 4 H), 6.48 (dd, 1 H); 13C NMR (101 MHz, CDCl3): δ = 193.8 (CH), 152.9 (CH), 134.1 (Cquat), 131.4 (CH), 129.2 (CH), 128.7 (CH), 128.6 (CH); GC-MS m/z 132.06 (M+, 100), 133.06 (M+, 9.9), 103 (M+ − CHO, 45), 77 (C6H5, 27).
3-Phenylpropanal (II): 1H NMR (CDCl3): δ = 9.74 (s, CHO, 1H), 7.24–7.10 (m, 5H), 2.91–2.86 (t, 2H), 2.72–2.67 (m, 2H); 13C NMR (101 MHz, CDCl3): δ = 201.5, 140.3, 128.6, 128.2, 126.3, 45.2, 28.1; GC-MS m/z: 134 [M]+; 105 [M − CHO]+; 91; 78 [M − C3H4O]+.
Cinnamic alcohol (III) 1H NMR (300 MHz, CDCl3): δ = 7.38–7.35 (m, 2H), 7.27–7.24 (m, 3H), 6.62–6.58 (m, 1H), 6.33–6.28 (m, 1H), 4.26–4.25 (m, 2H), 2.58 (s, 1H). 13C NMR (101 MHz, CDCl3): δ = 142.0, 128.6, 128.5, 126.0, 62.4, 34.4, 32.2; GC-MS m/z 134 [M]+; 116 [M − H2O]+; 91 [M − C2H3O]+; 78 [M − C3H4O]+;
3-Phenylpropanol (IV): 1H NMR (300 MHz, CDCl3): δ = 7.31–7.28 (m, 2H), 7.21–7.18 (m, 3H), 3.69–3.67 (t, 2H), 2.73–2.71 (m, 2H), 1.93–1.88 (m, 2H). 13C NMR (101 MHz, CDCl3): δ = 142.0, 128.6, 128.5, 126.0, 62.4, 34.4, 32.2; GC-MS m/z 136 [M]+; 118 [M − H2O]+; 105 [M − CH2OH]+; 91 [M − C2H5O]+; 77 [MC3H7O]+;
Levulinic acid (V): 1H NMR (300 MHz, CDCl3): δ = 11.01 (br s, 1H), 2.74 (t, J = 6.5 Hz, 2H), 2.62 (t, J = 6.5 Hz, 2H), 2.19 (s, 3H) ppm; 13C NMR (101 MHz, CDCl3): δ = 206.6, 178.7, 37.8, 29.9, 27.9 ppm; GC-MS m/z 116 [M]+; 87 [M − CHO]+; 73 [M − C2H3O]+;
Γ-Valerolactone: 1H NMR (300 MHz, CDCl3): δ = 82.06 (s.3H), 2.2 (m, 1H), 2.4 (m, 1H), 2.9 (m, 1H), 4.25 (m, 2H), 4.38 (m, 2H); 13C NMR (101 MHz, CDCl3): 821.1, 26.3, 39.8, 63.1, 67.4, 171.1, 177.1; GC-MS m/z 100 [M]+; 85 [M − CH3]+; 56 [M − C2H4O]+; 28 [C2H4]+.

3. Results and Discussion

3.1. Preparation and Characterization of M(0)NPs-CS

M(0)NPs-CS were easily prepared by adding the RhCl3 × 3H2O or RuCl3 catalyst precursor to an aqueous solution of CS at room temperature, followed by reduction with NaBH4 [64]. Pre-reduction with NaBH4 was carried out following a similar procedure to the one reported by Harrad and co-workers to prepare Ni(0) carboxymethylcellulose nanoparticles in a highly efficient manner [64,72]. Additionally, it may be supposed that formation of Rh(0) and Ru(0)-CS nanoparticles occurs in a similar manner to that reported by Xiao [73] for M(0)NPs and CMCNa (Scheme 2).

3.1.1. Fourier Transform Infrared Spectroscopy (FT-IR) of MNP(0)-CS and Chitosan

Commercially available CS, Rh(0) and Ru(0)-CS nanoparticles were characterized by FT-IR (Figure 1). The intense band at 3420 cm−1 in the FT-IR spectrum of CS is characteristic of −OH functional group stretching, while stretching of the intramolecular hydrogen bonds of the polysaccharide and the axial −CH stretching are evidenced at 2917 cm−1. In this region, Rh(0)-CS and Ru(0)-CS nanoparticles show a similar FT-IR pattern, yet the signals are weaker and broader. This behaviour suggests a decrease in the intra-molecular hydrogen bonds between the chitosan chains, probably due to the presence of M(0)NPs. At 1630 cm−1, the typical absorption of the primary amide (C=O stretching) is identifiable, while adsorption bands between 1093–1083 cm−1 are attributed to the stretching of the polysaccharide skeleton. Signals of NH2 groups are present between 960–910 cm−1. Since only moderate differences were observed between CS and Rh(0) or Ru(0)-CS, further characterizations were carried out by DSC, TGA, SEM, EDX and XRD.

3.1.2. Differential Scanning Calorimetry (DSC) and Thermal Gravimetric Analysis (TGA) of MNP(0)-CS and Chitosan

In agreement with the literature, TGA analysis of CS showed three characteristic temperature intervals with weight loss % between 10 and 50% (Figure 2). The first degradation occurs between 45 °C and 150 °C with 10–15% weight loss, corresponding to the evaporation of water physically adsorbed in CS. The second weight loss (about 50%) occurs between 220 °C and 300 °C, due to depolymerization or decomposition of polymer chains through deacetylation and cleavage of glycosidic linkages [74,75]. Finally, at temperatures above 300 °C, the residual carbon backbone and the chains of the polysaccharide collapse loosing further 10–15% weight [75,76] due to the pyrolytic degradation of chitosan, as well assessed in the literature [76]. In agreement with the literature, Rh(0)-CS and Ru(0)-CS showed lower decomposition rates, providing higher thermal stabilities than CS (Figure 2).
The DSC results of Rh(0)-CS and Ru(0)-CS were very similar to those of CS (Figures S1–S3), except for Ru(0)-CS, where the second endothermic peak occurred at higher temperatures than for CS (350 °C versus 250 °C), probably due to higher stability of the catalyst compared to CS and Rh(0)-CS.

3.1.3. Scanning Electron Microscopy (SEM), Energy-Dispersive X-ray Analysis (EDX), Transmission Electron Microscopy (TEM) of MNP(0)-CS

Further characterizations were carried out by SEM and EDX. Mapping carried out on Rh(0)-CS and Ru(0)-CS by EDX (Figure 3 and Figure 4) evidenced a homogeneous dispersion of the metal within the polymeric matrix, and no regions with higher metal concentrations were observed, denoting the absence of nanoparticle aggregation.
SEM analysis further evidence that the metal particles have dimensions <40 nm in the case of Rh(0), suggesting the formation of aggregates, and <10 nm for Ru(0), confirming the homogeneous distribution within the polymer matrix (Figure 4).
In order to obtain a clear size evaluation of M(0)NPs (Figure 5), TEM images of the freshly prepared catalysts were acquired. Transmission electron microscopes are, in fact, capable of imaging at a significantly higher resolution than SEM devices and can be crucial for the size determination of M(0)-CS nanoparticles.
From TEM images on the fresh catalysts, the size of Rh(0)-CS was estimated to be around 2.1 nm, while Ru(0)-CS gave smaller nanoparticles of an average size of 1.4 nm. It was also evident that both Rh(0)-CS and Ru(0)-CS nanoparticles were homogeneously distributed in the chitosan, but the Rh(0)-CS nanoparticles tended to aggregate into 20 to 50 nm aggregates, confirming SEM results.

3.1.4. X-ray Diffraction (XRD) of MNP(0)-CS

X-ray diffraction (XRD) analysis results obtained for Rh(0)-CS and Ru(0)-CS are reported in Figure 5. Both graphs have in common the two characteristic peaks of chitosan (2θ = 10°, 19°), which indicate the high degree of crystallinity of the polymer. The absence of peaks below 2θ = 10° confirms the high deacetylation degree of the chitosan employed [77]. As regards Rh(0)-CS nanoparticles (Figure 6), typical peaks of nanometric-sized metallic Rh(0) are present at 2θ = 40°, 70° and 85° [78] (JCPDS card number 5-685).
In XRD of Ru(0)-CS, a peak at 2θ = 40°, characteristic of nanometric-sized metallic Ru(0), was present, while other relevant peaks were not evidenced [79].

3.2. Catalytic Hydrogenation in the Presence of M(0)NPs-CS

To study the activity of M(0)NPs-CS and optimize hydrogenation reaction conditions, preliminary experiments were carried out using (E)-cinnamaldehyde (I) as a model substrate and relevant data are reported in Table 1. As previously mentioned, the hydrogenation of (I) is challenging due to the possible formation of several by-products [44,80,81,82,83,84,85] and is often chosen as model reaction considering both its scientific and industrial relevance [84,85,86,87].
Preliminary hydrogenation reactions of (I) were performed in the presence of Rh(0)-CS with Rh/(I) mol/mol ratio = 1/100 at 80 °C and p(H2) = 10 atm for 16 h (entries 1–1r3, Table 1). Since (I) is not completely soluble in water, a solvent mixture 1/1 (vol/vol) of water/THF was used, the former to solubilize the catalyst and the latter as a solvent for the substrate and products.
Then, the influence of NaBH4 pre-reduction on Rh and Ru nanoparticles was investigated. A set of experiments were performed employing metal/CS solutions prepared in the absence of NaBH4, referred to as Rh(II)-CS and Ru(II)-CS, respectively. At 80 °C and p(H2) 10 atm, Rh(II)-CS gave decreased substrate conversions (<75%) and reduced selectivity in II (<50%) compared to nanoparticles pre-reduced with NaBH4 (see run 1, Table 1). A similar trend was observed employing Ru(II)-CS. Interestingly, recycling experiments showed that nanoparticles prepared without pre-reduction with NaBH4 totally lost catalytic activity, in contrast to pre-reduced M(0)NPs-CS. Although hydrogen employed during the catalytic reaction should reduce the metal centre with “in situ” generation of the M(0)NPs-CS, recycling experiments clearly show that this is not the case and that pre-reduction with NaBH4 is necessary to achieve highly active M(0)NPs-CS nano-catalysts. Further studies are ongoing to gain deeper understanding of this finding.
The data reported in Table 1 show that, in the reaction condition tested, Rh(0)-CS makes it possible to achieve total conversion of I and high selectivity towards C=C hydrogenation to aldehyde (II) even after one recycling experiment, the second most abundant product being 3-phenylpropanol (IV). From the second recycling experiment, both activity and selectivity decreased (entries 1–1r3, Table 1). According to Scheme 3, IV may be formed by hydrogenation of II or III. The data reported in Table 1 show that in the presence of the Rh(0)-CS nanoparticles tested, the increase in III formed from runs 1 to 1r3 was predominantly at the expense of II and might be due to partial deactivation and loss of selectivity of recycled Rh(0)-CS nanoparticles.
Further recycling led to the formation of increasing quantities of cinnamyl alcohol (III), probably as a consequence of partial catalyst deactivation. Reducing reaction time (entry 2, Table 1), a drastic drop in conversion was recorded, a drop that was also observed by decreasing either hydrogen pressure (entry 3, Table 1) or temperature (entry 4, Table 1) or by reducing catalyst loading (catalyst/substrate molar ratio 1/200) (entry 5, Table 1). It should be noted that, despite the reduced activity of the catalyst in these reaction conditions, higher selectivity towards the carbon–carbon double bond hydrogenation product was nevertheless obtained, and in the best reaction conditions, total selectivity in (II) was achieved (entry 5, Table 1).
Hydrogenation of (I) with Ru(0)-CS, carried out in the same reaction conditions employed in the presence of Rh(0)-CS, highlighted the reduced activity of this catalytic species compared to analogous Rh(0)-CS, albeit with comparable selectivity (compare entries 1 and 6, Table 1). Similar results were obtained when increasing p(H2) pressure from 10 to 20 atm (compare entries 6 and 7, Table 1), while at higher temperatures (100 °C), higher conversion could be achieved at the expense of selectivity (entry 8, Table 1). When p(H2) was raised to 20 atm, conversion was almost complete (97%), with higher selectivity towards 3-phenylpropanol (IV) (57%). Interestingly, recycling of the catalyst lead to an increase in selectivity in the fully hydrogenated product (IV) from 57% in the first experiment to 82% after the third recycling (compare entries 9–9r3, Table 1). Further, the high conversion obtained for all rounds of recycling confirms the stability of the Ru(0)-CS catalytic species. In agreement with the literature, Ru(0)-CS nanoparticles were active in more extreme conditions than Rh(0)-CS nanoparticles but were more recyclable than the latter [44].
Since no data are available on the hydrogenation of (I) with CS nanoparticles, in order to evaluate the efficiency of Rh(0) and Ru(0)-CS as tested in this work, was comparison with heterogeneous Rh(0) and Ru(0) catalysts reported in the literature was carried out [44,88]. According to a very recent work by Patil and co-workers, results achieved with Rh(0) and Ru(0)-CS are particularly interesting, since, in most cases, heterogeneous catalysts reported in the literature have modest activity and selectivity, requiring harsh conditions and environmentally unfriendly organic solvents [44,86,87,88,89,90,91,92,93,94,95].
For example, Liu reported the use of Rh@MIL-101 (Cr), a metal–organic framework (MOF) with high surface area and porosity, for the hydrogenation of (I) [89]. At 30 °C, p(H2) 10 atm, with a Rh/(I) molar ratio of 1/400, in ethanol as a solvent, conversion rates of up to 98% of (I) were achieved by 5 h, with selectivity in (II) of 99%. In analogous reaction conditions, commercially available Rh/C gave significantly lower conversions (53%) and selectivity in (II) (89%) [44]. Although Rh@MIL-101 (Cr) can be recycled up to two times with almost no change in activity and selectivity, its sustainability is low considering that MIL is synthesized using toxic chemicals such as N,N-dimethylformamide (DMF) or hydrofluoric acid (HF) [94]. Alternatively, Rh(0) porphyrins have been used for the hydrogenation of (I), but with modest selectivity in (II) (≤80%). Additionally, toluene was used together with water as reaction solvent and NEt3 had to be added to promote the solubility in water of the Rh porphyrin complex [93].
To widen the scope of the reaction further hydrogenation tests were carried out in the presence of levulinic acid (V) (Scheme 1). Levulinic acid is commonly employed as standard substrate to verify the efficiency of new protocols intending to valorise bio-based feedstocks to produce sustainable, bio-based building blocks in alternative to fossil-based ones. It is important to note that in 2004 the US Department of Energy, ranked levulinic acid as one of the twelve most important platform chemicals derived from biomass [94,95].
For example, several studies have been reported in the literature for the use ruthenium supported on carbon [96], ZrO2 [63], TiO2 [65] or alumina [97] as catalysts for the synthesis of (VI) from levulinic acid.
Since (V) is soluble in water, hydrogenation reactions were carried out in water as solvent and at the end of the reaction the products were extracted from the water solution with diethyl ether, the catalyst remaining confined in the aqueous phase, ready to be reused.
The catalytic tests reported in Table 2 showed complete conversion for the substrate (VI) at 80 °C, p(H2) 20 atm for 16 h, using Rh(0)-CS with a Rh(0)/(V) ratio of 1/100 (entry 1, Table 2). Total conversion was also obtained at lower hydrogen pressure and temperature (see entries 2 and 3, Table 2). However, in these reaction conditions, a significant decrease in the Rh(0)-CS activity was registered upon recycling (entry 3r1, Table 2). In order to verify whether the loss of the Rh(0)-CS activity could be a consequence of catalyst leaching, ICP analysis of the organic solution was carried out, revealing negligible traces of metal (<0.1%). If hydrogen pressure was further decreased from 10 to 5 atm at 50 °C, conversion into (VI) was reduced (36%), although total selectivity was maintained (entry 5, Table 2).
Interestingly, experiments carried out in the same reaction conditions reported in entry 5 of Table 2, but in the presence of Ru(0)-CS, clearly demonstrate that Ru(0)-CS is highly active for the hydrogenation of (V), giving total selectivity towards the desired product (VI), such that it was possible not only to lower p(H2) to 1 atm but also to recycle the catalyst up to three times with no loss of activity or selectivity (see entries 7–9r3, Table 2). With the aim of minimizing the consumption of Ru(0)-CS, further experiments were performed with a Ru/(V) ratio of 1/200 mol/mol, at 50 °C, p(H2) 5 atm, for 4 h, yet in these reaction conditions, the activity of the Ru(0)-CS catalyst upon recycling decreased to 87% (see entries 10–10r3, Table 1).
Thus, further hydrogenation reactions were performed in more drastic conditions (entries 11–11r3, Table 2), but with an even lower Ru/(V) mol/mol ratio (1/500). These experiments showed that at 80 °C, p(H2) 20 atm by 16 h, even lower catalyst concentrations could be used, making it possible to achieve total substrate conversion and product selectivity even after three recycling tests.
As in the case of (E)-cinnamyl aldehyde (I) (see Table 1), the data achieved for the hydrogenation of levulinic acid (V) with Ru(0)-CS (see Table 2) are extremely interesting and reveal high performance compared to data in the literature [61,98,99]. In fact, Ndolomingo and co-workers recently reported a comparison between the efficiency values of different MNPs employed for the hydrogenation of (V) [91], and from this work it emerged that Ru@Meso-SiO2 nanoparticles are among most efficient hydrogenation catalysts, leading to total substrate conversion and selectivity in (VI) at moderate p(H2) (10 atm) and in a short time (5 h), yet very high temperatures are required (150 °C), and dioxane is used as a solvent [100]. Ru/SiO2, Ru/Al2O3, Ru/ZnO2 and Ru/TiO2 have been reported by Tan for the hydrogenation of (V), but in this case as well, high temperatures are required to achieve high product yields [67]. It should also be noted that in agreement with the literature, Rh(0)-CS nanoparticles gave the highest activity and selectivity for the synthesis of (II), i.e., towards C=C hydrogenation, in contrast to Ru(0)-CS nanoparticles, which gave the best results for the hydrogenation of C=O to give (VI).

4. Conclusions

In this work, water-soluble M(0)NPs-CS were prepared starting from RhCl3 × 3H2O or RuCl3 in an aqueous environment using chitosan (CS) as a ligand, pre-reduced before use with NaBH4. FT-IR of M(0)NPs-CS showed no substantial differences from CS, while TGA highlighted higher stabilization of Rh(0)-CS and Ru(0)-CS than CS. As regards EDX analysis, Rh(0)-CS and Ru(0)-CS appeared to be homogeneously dispersed within the polymer matrix, and no areas of higher metal concentration were noted, as would be observed in the case of nanoparticle aggregation. SEM and XRD analyses further confirmed that the particles had dimensions on the order of nanometres.
The catalytic efficiency of Rh(0)-CS and Ru(0)-CS nanoparticles was tested in hydrogenation reactions of model substrates such as (E)-cinnamaldehyde (I) and levulinic acid (V), important platform chemicals of strong industrial interest. Rh(0)-CS made it possible to achieve complete conversions of (I) at 80 °C and p(H2) 10 atm by 16 h, with selectivity in (II) of up to 84%, although the latter detectably decreased upon recycling. Additionally, for the hydrogenation of levulinic acid (V), complete conversions were obtained with Rh(0)-CS at lower reaction temperatures (50 °C).
In contrast, Ru(0)-CS was less active for the hydrogenation of (I), requiring higher reaction temperatures than Rh(0)-CS, yet leading to higher selectivity in (III) (91–100%). Interestingly, Ru(0)-CS was more efficient for the hydrogenation of levulinic acid (V), giving total conversion and selectivity in γ-valerolactone (VI) even after three recycling tests. Comparison with literature data highlighted that M(0)NPs-CS have very high performances compared to the best heterogeneous catalysis known for the hydrogenation of (E)-cinnamaldehyde and levulinic acid. Further studies are ongoing in the presence of other water-soluble bio-derived substrates, bearing suitable functional groups for the anchoring of M(0)NPs, in order to compare their catalytic efficiency to those of M(0)NPs-CS as reported in this work.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/molecules29092083/s1, Figure S1: DSC and TGA profiles of Chitosan Hydrochloride; Figure S2: DSC and TGA profiles of Rh(0)-CS; Figure S3: DSC and TGA profiles of Ru(0)-CS.

Author Contributions

V.B.: conceptualization, investigation, writing—original draft, writing—review and editing; M.F.: data curation, writing—review and editing; E.B., S.P. and A.D.M.: data curation, formal analysis; S.P. and V.B.: supervision, formal analysis. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Informed consent was obtained from all subjects involved in the study.

Data Availability Statement

The original contributions presented in the study are included in the article/Supplementary Material, further inquiries can be directed to the corresponding authors.

Conflicts of Interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

References

  1. RameshKumar, S.; Shaiju, P.; O’Connor, K.E.; Ramesh Babu, P. Bio-based and biodegradable polymers—State-of-the-art, challenges and emerging trends. Curr. Opin. Green Sustain. Chem. 2020, 21, 75–81. [Google Scholar] [CrossRef]
  2. Partanen, A.; Carus, M. Biocomposites, find the real alternative to plastic—An examination of biocomposites in the market. Reinf. Plast. 2019, 63, 317–321. [Google Scholar] [CrossRef]
  3. Pudełko, A.; Postawa, P.; Stachowiak, T.; Malińska, K.; Dróżdż, D. Waste derived biochar as an alternative filler in biocomposites—Mechanical, thermal and morphological properties of biochar added biocomposites. J. Clean. Prod. 2021, 278, 123850. [Google Scholar] [CrossRef]
  4. Savov, V.; Antov, P.; Zhou, Y.; Bekhta, P. Eco-Friendly Wood Composites: Design, Characterization and Applications. Polymers 2023, 15, 892. [Google Scholar] [CrossRef] [PubMed]
  5. Trivedi, A.K.; Gupta, M.; Singh, H. PLA based biocomposites for sustainable products: A review. Adv. Ind. Eng. Polym. Res. 2023, 6, 382–395. [Google Scholar] [CrossRef]
  6. Muiruri, J.K.; Yeo, J.C.C.; Soo, X.Y.D.; Wang, S.; Liu, H.; Kong, J.; Cao, J.; Tan, B.H.; Suwardi, A.; Li, Z.; et al. Recent advances of sustainable Short-chain length polyhydroxyalkanoates (Scl-PHAs)—Plant biomass composites. Eur. Polym. J. 2023, 187, 111882. [Google Scholar] [CrossRef]
  7. Geyer, R.; Jambeck, J.R.; Law, K.L. Production, use, and fate of all plastics ever made. Sci. Adv. 2017, 3, e1700782. [Google Scholar] [CrossRef] [PubMed]
  8. Beghetto, V.; Sole, R.; Buranello, C.; Al-Abkal, M.; Facchin, M. Recent Advancements in Plastic Packaging Recycling: A Mini-Review. Materials 2021, 14, 4782. [Google Scholar] [CrossRef] [PubMed]
  9. Chen, W.-Q.; Ciacci, L.; Sun, N.-N.; Yoshioka, T. Sustainable Cycles and Management of Plastics: A Brief Review of RCR Publications in 2019 and Early 2020. Resour. Conserv. Recycl. 2020, 159, 104822. [Google Scholar] [CrossRef]
  10. Beghetto, V.; Gatto, V.; Samiolo, R.; Scolaro, C.; Brahimi, S.; Facchin, M.; Visco, A. Plastics today: Key challenges and EU strategies towards carbon neutrality: A review. Environ. Pollut. 2023, 334, 122102. [Google Scholar] [CrossRef]
  11. Haider, T.P.; Völker, C.; Kramm, J.; Landfester, K.; Wurm, F.R. Plastics of the future? The impact of biodegradable polymers on the environment and on society. Angew. Chem. Int. Ed. 2019, 58, 50–62. [Google Scholar] [CrossRef] [PubMed]
  12. Kabir, E.; Kaur, R.; Lee, J.; Kim, K.-H.; Kwon, E.E. Prospects of biopolymer technology as an alternative option for non-degradable plastics and sustainable management of plastic wastes. J. Clean. Prod. 2020, 258, 120536. [Google Scholar] [CrossRef]
  13. Nesic, A.; Castillo, C.; Castaño, P.; Cabrera-Barjas, G.; Serrano, J. Bio-based packaging materials, in Biobased Products and Industries; Galanakis, C.M., Ed.; Elsevier: Amsterdam, The Netherlands, 2020; pp. 279–309. [Google Scholar] [CrossRef]
  14. Ferraro, V.; Sole, R.; Bortoluzzi, M.; Beghetto, V.; Castro, J. Tris-isocyanide copper(I) complex enabling copper azide-alkyne cycloaddition in neat conditions. Appl. Organomet. Chem. 2021, 35, 6401–6411. [Google Scholar] [CrossRef]
  15. Walker, S.; Rothman, R. Life cycle assessment of bio-based and fossil-based plastic: A review. J. Clean. Prod. 2020, 261, 121158. [Google Scholar] [CrossRef]
  16. Kumar, S.; Mukherjee, A.; Dutta, J. Chitosan based nanocomposite films and coatings: Emerging antimicrobial food packaging alternatives. Trends Food Sci. Technol. 2020, 97, 196–209. [Google Scholar] [CrossRef]
  17. Lan, W.; He, L.; Liu, Y. Preparation and properties of sodium carboxymethyl cellulose/sodium alginate/chitosan composite film. Coatings 2018, 8, 291. [Google Scholar] [CrossRef]
  18. Nataraj, D.; Sakkara, S.; Meghwal, M.; Reddy, N. Crosslinked chitosan films with controllable properties for commercial applications. Int. J. Biol. Macromol. 2018, 120, 1256–1264. [Google Scholar] [CrossRef] [PubMed]
  19. Riaz, A.; Lagnika, C.; Luo, H.; Nie, M.; Dai, Z.; Liu, C.; Abdin, M.; Hashim, M.M.; Li, D.; Song, J. Effect of Chinese chives (Allium tuberosum) addition to carboxymethyl cellulose based food packaging films. Carbohydr. Polym. 2020, 235, 115944. [Google Scholar] [CrossRef] [PubMed]
  20. Roy, S.; Rhim, J.-W. Carboxymethyl cellulose-based antioxidant and antimicrobial active packaging film incorporated with curcumin and zinc oxide. Int. J. Biol. Macromol. 2020, 148, 666–676. [Google Scholar] [CrossRef]
  21. Tongdeesoontorn, W.; Mauer, L.J.; Wongruong, S.; Sriburi, P.; Rachtanapun, P. Physical and Antioxidant Properties of Cassava Starch–Carboxymethyl Cellulose Incorporated with Quercetin and TBHQ as Active Food Packaging. Polymers 2020, 12, 366. [Google Scholar] [CrossRef]
  22. Sole, R.; Buranello, C.; Di Michele, A.; Beghetto, V. Boosting physical-mechanical properties of adipic acid/chitosan films by DMTMM cross-linking. Int. J. Biol. Macromol. 2022, 209, 2009–2019. [Google Scholar] [CrossRef] [PubMed]
  23. Beghetto, V.; Gatto, V.; Conca, S.; Bardella, N.; Buranello, C.; Gasparetto, G.; Sole, R. Development of 4-(4,6-dimethoxy-1,3,5-triazin-2-yl)-4-methyl-morpholinium chloride cross-linked carboxymethyl cellulose films. Carbohydr. Polym. 2020, 249, 116810. [Google Scholar] [CrossRef] [PubMed]
  24. Pellis, A.; Guebitz, G.M.; Nyanhongo, G.S. Chitosan: Sources, Processing and Modification Techniques. Gels 2022, 8, 393. [Google Scholar] [CrossRef]
  25. Szőllősi, G.; Kolcsár, V.J. Highly Enantioselective Transfer Hydrogenation of Prochiral Ketones Using Ru(II)-Chitosan Catalyst in Aqueous Media. ChemCatChem 2018, 11, 820–830. [Google Scholar] [CrossRef]
  26. Bhattarai, N.; Gunn, J.; Zhang, M. Chitosan-based hydrogels for controlled, localized drug delivery. Adv. Drug Deliv. Rev. 2010, 62, 83–99. [Google Scholar] [CrossRef] [PubMed]
  27. Shukla, S.K.; Mishra, A.K.; Arotiba, O.A.; Mamba, B.B. Chitosan-based nanomaterials: A state-of-the-art review. Int. J. Biol. Macromol. 2013, 59, 46–58. [Google Scholar] [CrossRef] [PubMed]
  28. Guibal, E.; Vincent, T.; Navarro, R. Metal ion biosorption on chitosan for the synthesis of advanced materials. J. Mater. Sci. 2014, 49, 5505–5518. [Google Scholar] [CrossRef]
  29. Desbrières, J.; Guibal, E. Chitosan for wastewater treatment. Polym. Int. 2018, 67, 7–14. [Google Scholar] [CrossRef]
  30. Aranaz, I.; Acosta, N.; Civera, C.; Elorza, B.; Mingo, J.; Castro, C.; de Los Llanos Gandía, M.; Caballero, A.H. Cosmetics and Cosmeceutical Applications of Chitin, Chitosan and Their Derivatives. Polymers 2018, 10, 213. [Google Scholar] [CrossRef]
  31. Joseph, S.M.; Krishnamoorthy, S.; Paranthaman, R.; Moses, J.; Anandharamakrishnan, C. A review on source-specific chemistry, functionality, and applications of chitin and chitosan. Carbohydr. Polym. Technol. Appl. 2021, 2, 100036. [Google Scholar] [CrossRef]
  32. Dhillon, G.S.; Kaur, S.; Brar, S.K.; Verma, M. Green synthesis approach: Extraction of chitosan from fungus mycelia. Crit. Rev. Biotechnol. 2012, 33, 379–403. [Google Scholar] [CrossRef] [PubMed]
  33. Elyasi, Z.; Ghomi, J.S.; Najafi, G.R.; Sharif, M.A. Fabrication of uniform Pd nanoparticles immobilized on crosslinked ionic chitosan support as a super-active catalyst toward regioselective synthesis of pyrazole-fused heterocycles. Int. J. Biol. Macromol. 2023, 253, 126589. [Google Scholar] [CrossRef] [PubMed]
  34. Molnár, Á. The use of chitosan-based metal catalysts in organic transformations. Coord. Chem. Rev. 2019, 388, 126–171. [Google Scholar] [CrossRef]
  35. Devendrapandi, G.; Padmanaban, D.; Thanikasalam, R.; Panneerselvam, A.; Palraj, R.; Rajabathar, J.R.; Rajendiran, N.; Balu, R.; Oh, T.H.; Ramasundaram, S. Direct sunlight induced room temperature synthesis of anticancer and catalytic silver nanoparticles by shrimp shell waste derived chitosan. Int. J. Biol. Macromol. 2023, 252, 126205. [Google Scholar] [CrossRef] [PubMed]
  36. Bayat, A.; Lighvan, Z.M.; Sadjadi, S.; Bahri-Laleh, N.; Ghadimi, A. Pd on composite chitosan bead containing a star-like hybrid metal-organic framework: A promising catalyst for hydrogenation of lubricants. Inorg. Chem. Commun. 2023, 158, 111558. [Google Scholar] [CrossRef]
  37. Kolcsár, V.J.; Fülöp, F.; Szőllősi, G. Ruthenium(II)-Chitosan, an Enantioselective Catalyst for the Transfer Hydrogenation of N-Heterocyclic Ketones. ChemCatChem 2019, 11, 2725–2731. [Google Scholar] [CrossRef]
  38. Wu, L.-H.; Nordin, M.R.; Yaakob, Z.; Liew, K.-Y.; Li, J.-L. Effects of Fe on catalytic hydrogenation of palm oil in aqueous solution. Chem. Pap. 2017, 71, 119–126. [Google Scholar] [CrossRef]
  39. Cui, Q.; Zhao, H.; Luo, G.; Xu, J. An Efficient Chitosan/Silica Composite Core-Shell Microspheres-Supported Pd Catalyst for Aryl Iodides Sonogashira Coupling Reactions. Ind. Eng. Chem. Res. 2017, 56, 143–152. [Google Scholar] [CrossRef]
  40. Ahmadian, Z.; Kazeminava, F.; Afrouz, M.; Abbaszadeh, M.; Mehr, N.T.; Shiran, J.A.; Gouda, C.; Adeli, M.; Kafil, H.S. A review on the impacts of metal/metal nanoparticles on characteristics of hydrogels: Special focus on carbohydrate polymers. Int. J. Biol. Macromol. 2023, 253, 126535. [Google Scholar] [CrossRef]
  41. Ma, L.; Su, Y.; Chen, J.; Xu, J. Silica/Chitosan Core-Shell Hybrid-Microsphere-Supported Pd Catalyst for Hydrogenation of Cyclohexene Reaction. Ind. Eng. Chem. Res. 2017, 56, 12655–12662. [Google Scholar] [CrossRef]
  42. Zhang, C.; Lu, D.; Jiang, P.; Li, J.; Leng, Y. Thiol Functionalized Cross-Linked Chitosan Polymer Supporting Palladium for Oxidative Heck Reaction and Reduction of p-Nitrophenol. Catal. Lett. 2017, 147, 2534–2541. [Google Scholar] [CrossRef]
  43. Barskiy, D.A.; Kovtunov, K.V.; Primo, A.; Corma, A.; Kaptein, R.; Koptyug, I.V. Selective Hydrogenation of 1,3-Butadiene and 1-Butyne over a Rh/Chitosan Catalyst Investigated by using Parahydrogen-Induced Polarization. ChemCatChem 2012, 4, 2031–2035. [Google Scholar] [CrossRef]
  44. Patil, R.D.; Shelte, A.R.; Biradar, A.V.; Pratihar, S. Sustainable and selective transfer hydrogenation using waste shrimp shell-based tetrazene-Ru (II) para-cymene catalyst with ethanol as a hydrogen source. Appl. Organomet. Chem. 2023, 37, e7221. [Google Scholar] [CrossRef]
  45. Liu, J.; Li, P.; Jiang, R.; Liu, P.; Zheng, X.-C. Ru Nanoparticles Immobilized on Chitosan as Effective Catalysts for Boosting NH3BH3 Hydrolysis. ChemCatChem 2021, 13, 4142–4150. [Google Scholar] [CrossRef]
  46. Mousavi, H. A comprehensive survey upon diverse and prolific applications of chitosan-based catalytic systems in one-pot multi-component synthesis of heterocyclic rings. Int. J. Biol. Macromol. 2021, 186, 1003–1166. [Google Scholar] [CrossRef] [PubMed]
  47. Paganelli, S.; Alam, M.; Beghetto, V.; Scrivanti, A.; Amadio, E.; Bertoldini, M.; Matteoli, U. A pyridyl-triazole ligand for ruthenium and iridium catalyzed CC and CO hydrogenations in water/organic solvent biphasic systems. Appl. Catal. A Gen. 2015, 503, 20–25. [Google Scholar] [CrossRef]
  48. Sole, R.; Buranello, C.; Bardella, N.; Di Michele, A.; Paganelli, S.; Beghetto, V. Recyclable Ir Nanoparticles for the Catalytic Hydrogenation of Biomass-Derived Carbonyl Compounds. Catalysts 2021, 11, 914. [Google Scholar] [CrossRef]
  49. Matteoli, U.; Beghetto, V.; Scrivanti, A.; Aversa, M.; Bertoldini, M.; Bovo, S. An alternative stereoselective synthesis of (R)- and (S)-Rosaphen® via asymmetric catalytic hydrogenation. Chirality 2011, 23, 779–783. [Google Scholar] [CrossRef] [PubMed]
  50. Piccolo, O.; Arčon, I.; Aquilante, G.; Prai, A.; Paganelli, S.; Facchin, M.; Beghetto, V. Synthesis of Helional by Hydrodechlorination Reaction in the Presence of Mono and Bi-metallic Catalysts Supported on Alumina. Catalysts 2024, 14, 255. [Google Scholar] [CrossRef]
  51. Patil, K.N.; Manikanta, P.; Srinivasappa, P.M.; Jadhav, A.H.; Nagaraja, B.M. State-of-the-art and perspectives in transition metal-based heterogeneous catalysis for selective hydrogenation of cinnamaldehyde. J. Environ. Chem. Eng. 2023, 11, 109168. [Google Scholar] [CrossRef]
  52. Gallezot, P.; Richard, D. Selective Hydrogenation of α,β-Unsaturated Aldehydes. Catal. Rev. 1998, 40, 81–126. [Google Scholar] [CrossRef]
  53. Satagopan, V.; Chandalia, S.B. Selectivity aspects in the multi-phase hydrogenation of α,β-unsaturated aldehydes over supported noble metal catalysts: Part I. J. Chem. Technol. Biotechnol. 1994, 59, 257–263. [Google Scholar] [CrossRef]
  54. Claus, P. Selective hydrogenation of ά,β-unsaturated aldehydes and other C=O and C=C bonds containing compounds. Top. Catal. 1998, 5, 51–62. [Google Scholar] [CrossRef]
  55. Tan, J.; Jiang, M.; Yu, K.; Song, Y.; Zhang, W.; Gao, Q. Recent progress of Cu-based electrocatalysts for upgrading biomass-derived furanic compounds. Catal. Sci. Technol. 2023, 13, 2899–2921. [Google Scholar] [CrossRef]
  56. Zhang, J.; Wu, D. Aqueous phase catalytic hydrogenation of furfural to furfuryl alcohol over in-situ synthesized Cu–Zn/SiO2 catalysts. Mater. Chem. Phys. 2021, 260, 124152. [Google Scholar] [CrossRef]
  57. Zhao, M.; Yang, N.; Li, Z.; Xie, H. MOFs Derived Catalysts Prepared by Pyrolysis for Hydrogenation of Bio-Based Furfural: A Mini-Review. ChemistrySelect 2020, 5, 13681–13689. [Google Scholar] [CrossRef]
  58. Luneau, M.; Lim, J.S.; Patel, D.A.; Sykes, E.C.H.; Friend, C.M.; Sautet, P. Guidelines to Achieving High Selectivity for the Hydrogenation of α,β-Unsaturated Aldehydes with Bimetallic and Dilute Alloy Catalysts: A Review. Chem. Rev. 2020, 120, 12834–12872. [Google Scholar] [CrossRef]
  59. Wang, X.; Qi, X.; Qiu, M.; Shen, F.; Yang, J.; Shen, B. Bimetallic ordered mesoporous carbon from lignin for catalytic selective hydrogenation of levulinic acid to γ-valerolactone. Fuel 2023, 341, 127720. [Google Scholar] [CrossRef]
  60. Tang, Y.; Fu, J.; Wang, Y.; Guo, H.; Qi, X. Bimetallic Ni-Zn@OMC catalyst for selective hydrogenation of levulinic acid to γ-valerolactone in water. Fuel Process. Technol. 2023, 240, 107559. [Google Scholar] [CrossRef]
  61. García-Sancho, C.; Mérida-Robles, J.M.; Cecilia-Buenestado, J.A.; Moreno-Tost, R.; Maireles-Torres, P.J. The Role of Copper in the Hydrogenation of Furfural and Levulinic Acid. Int. J. Mol. Sci. 2023, 24, 2443. [Google Scholar] [CrossRef]
  62. Xu, Y.; Liang, Y.; Guo, H.; Qi, X. Catalytic hydrogenation of levulinic acid to γ-valerolactone over lignin-metal coordinated carbon nanospheres in water. Int. J. Biol. Macromol. 2023, 240, 124451. [Google Scholar] [CrossRef] [PubMed]
  63. Ftouni, J.; Genuino, H.C.; Muñoz-Murillo, A.; Bruijnincx, P.C.A.; Weckhuysen, B.M. Influence of Sulfuric Acid on the Performance of Ruthenium-based Catalysts in the Liquid-Phase Hydrogenation of Levulinic Acid to γ-Valerolactone. ChemSusChem 2017, 10, 2891–2896. [Google Scholar] [CrossRef]
  64. Harrad, M.A.; Boualy, B.; El Firdoussi, L.; Mehdi, A.; Santi, C.; Giovagnoli, S.; Nocchetti, M.; Ali, M.A. Colloidal nickel(0)-carboxymethyl cellulose particles: A biopolymer-inorganic catalyst for hydrogenation of nitro-aromatics and carbonyl compounds. Catal. Commun. 2013, 32, 92–100. [Google Scholar] [CrossRef]
  65. Lv, Y.; Han, M.; Gong, W.; Wang, D.; Chen, C.; Wang, G.; Zhang, H.; Zhao, H. Fe-Co Alloyed Nanoparticles Catalyzing Efficient Hydrogenation of Cinnamaldehyde to Cinnamyl Alcohol in Water. Angew. Chem. Int. Ed. 2020, 59, 23521–23526. [Google Scholar] [CrossRef]
  66. Zhou, X.; Feng, Z.; Guo, W.; Liu, J.; Li, R.; Chen, R.; Huang, J. Hydrogenation and Hydrolysis of Furfural to Furfuryl Alcohol, Cyclopentanone, and Cyclopentanol with a Heterogeneous Copper Catalyst in Water. Ind. Eng. Chem. Res. 2019, 58, 3988–3993. [Google Scholar] [CrossRef]
  67. Tan, J.; Cui, J.; Deng, T.; Cui, X.; Ding, G.; Zhu, Y.; Li, Y. Water-Promoted Hydrogenation of Levulinic Acid to γ-Valerolactone on Supported Ruthenium Catalyst. ChemCatChem 2015, 7, 508–512. [Google Scholar] [CrossRef]
  68. Stephan, M.; Panther, J.; Wilbert, F.; Ozog, P.; Müller, T.J.J. Heck Reactions of Acrolein or Enones and Aryl Bromides-Synthesis of 3-Aryl Propenals or Propenones and Consecutive Application in Multicomponent Pyrazole Syntheses. Eur. J. Org. Chem. 2020, 2020, 2086–2092. [Google Scholar] [CrossRef]
  69. Sole, R.; Gatto, V.; Conca, S.; Bardella, N.; Morandini, A.; Beghetto, V. Sustainable triazine-based dehydro-condensation agents for amide synthesis. Molecules 2021, 26, 191. [Google Scholar] [CrossRef] [PubMed]
  70. Beghetto, V.; Gatto, V.; Conca, S.; Bardella, N.; Scrivanti, A. Polyamidoamide dendrimers and cross-linking agents for stabilized bioenzymatic resistant metal-free bovine collagen. Molecules 2019, 24, 3611. [Google Scholar] [CrossRef]
  71. Scrivanti, A.; Bortoluzzi, M.; Sole, R.; Beghetto, V. Synthesis and characterization of yttrium, europium, terbium and dysprosium complexes containing a novel type of triazolyl–oxazoline ligand. Chem. Pap. 2018, 72, 799–808. [Google Scholar] [CrossRef]
  72. Harrad, M.A.; Valerga, P.; Puerta, M.C.; Houssini, I.; Ali, M.A.; El Firdoussi, L.; Karim, A. Ni(0)-CMC-Na Nickel Colloids in Sodium Carboxymethyl-Cellulose: Catalytic Evaluation in Hydrogenation Reactions. Molecules 2011, 16, 367–372. [Google Scholar] [CrossRef] [PubMed]
  73. Xiao, J.; Lu, Z.; Li, Y. Carboxymethylcellulose-Supported Palladium Nanoparticles Generated in Situ from Palladium(II) Carboxymethylcellulose: An Efficient and Reusable Catalyst for Suzuki-Miyaura and Mizoroki-Heck Reactions. Ind. Eng. Chem. Res. 2015, 54, 790–797. [Google Scholar] [CrossRef]
  74. Qu, L.; Yu, H.; Yu, F.; Yuan, B.; Xie, C.; Yu, S. Catalytic reduction of α-pinene using Ru nanoparticles stabilized by modified carboxymethyl cellulose. Appl. Surf. Sci. 2018, 453, 271–279. [Google Scholar] [CrossRef]
  75. Ziegler-Borowska, M.; Chełminiak, D.; Kaczmarek, H. Thermal stability of magnetic nanoparticles coated by blends of modified chitosan and poly(quaternary ammonium) salt. J. Therm. Anal. Calorim. 2014, 119, 499–506. [Google Scholar] [CrossRef]
  76. Corazzari, I.; Nisticò, R.; Turci, F.; Faga, M.G.; Franzoso, F.; Tabasso, S.; Magnacca, G. Advanced physico-chemical characterization of chitosan by means of TGA coupled on-line with FTIR and GCMS: Thermal degradation and water adsorption capacity. Polym. Degrad. Stab. 2015, 112, 1–9. [Google Scholar] [CrossRef]
  77. Anan, N.A.; Hassan, S.M.; Saad, E.M.; Butler, I.S.; Mostafa, S.I. Preparation, characterization and pH-metric measurements of 4-hydroxysalicylidenechitosan Schiff-base complexes of Fe(III), Co(II), Ni(II), Cu(II), Zn(II), Ru(III), Rh(III), Pd(II) and Au(III). Carbohydr. Res. 2011, 346, 775–793. [Google Scholar] [CrossRef] [PubMed]
  78. Gniewek, A.; Trzeciak, A.M. Rh(0) Nanoparticles: Synthesis, Structure and Catalytic Application in Suzuki-Miyaura Reaction and Hydrogenation of Benzene. Top. Catal. 2013, 56, 1239–1245. [Google Scholar] [CrossRef]
  79. Ghosh, S.; Ghosh, M.; Rao, C.N.R. Nanocrystals, Nanorods and other Nanostructures of Nickel, Ruthenium, Rhodium and Iridium prepared by a Simple Solvothermal Procedure. J. Clust. Sci. 2007, 18, 97–111. [Google Scholar] [CrossRef]
  80. Hao, J.; Zhang, Y.; Zhang, T.; Zhou, H.; Liu, Q.; Zhi, K.; Li, N.; He, R. A novel and highly efficient Zr-containing catalyst supported by biomass-derived sodium carboxymethyl cellulose for hydrogenation of furfural. Front. Chem. 2022, 10, 966270. [Google Scholar] [CrossRef]
  81. Gatto, V.; Conca, S.; Bardella, N.; Beghetto, V. Efficient triazine derivatives for collagenous materials stabilization. Materials 2021, 14, 3069. [Google Scholar] [CrossRef]
  82. Morandini, A.; Leonetti, B.; Riello, P.; Sole, R.; Gatto, V.; Caligiuri, I.; Rizzolio, F.; Beghetto, V. Synthesis and Antimicrobial Evaluation of Bis-morpholine Triazine Quaternary Ammonium Salts. ChemMedChem 2021, 16, 3172–3176. [Google Scholar] [CrossRef]
  83. Beghetto, V.; Bardella, N.; Samiolo, R.; Gatto, V.; Conca, S.; Sole, R.; Molin, G.; Gattolin, A.; Ongaro, N. By-products from mechanical recycling of polyolefins improve hot mix asphalt performance. J. Clean. Prod. 2021, 318, 128627. [Google Scholar] [CrossRef]
  84. Scrivanti, A.; Beghetto, V.; Bertoldini, M. New insights into the alkoxycarbonylation of propargyl alcohol. Mol. Catal. 2017, 443, 38–42. [Google Scholar] [CrossRef]
  85. Scrivanti, A.; Sole, R.; Bortoluzzi, M.; Beghetto, V.; Bardella, N.; Dolmella, A. Synthesis of new triazolyl-oxazoline chiral ligands and study of their coordination to Pd(II) metal centers. Inorganica Chim. Acta 2019, 498, 119129. [Google Scholar] [CrossRef]
  86. Han, Q.; Liu, Y.; Wang, D.; Yuan, F.; Niu, X.; Zhu, Y. Effect of Carbon Supported Pt Catalysts on Selective Hydrogenation of Cinnamaldehyde. J. Chem. 2016, 2016, 4563832. [Google Scholar] [CrossRef]
  87. Lan, X.; Wang, T. Highly selective catalysts for the hydrogenation of unsaturated aldehydes: A review. ACS Catal. 2020, 10, 2764–2790. [Google Scholar] [CrossRef]
  88. Sole, R.; Bortoluzzi, M.; Spannenberg, A.; Tin, S.; Beghetto, V.; de Vries, J.G. Synthesis, characterization and catalytic activity of novel ruthenium complexes bearing NNN click based ligands. Dalton Trans. 2019, 48, 13580–13588. [Google Scholar] [CrossRef]
  89. Liu, Q.; Li, Y.; Fan, Y.; Su, C.-Y.; Li, G. Chemoselective hydrogenation of α,β-unsaturated aldehydes over Rh nanoclusters confined in a metal–organic framework. J. Mater. Chem. A 2020, 8, 11442–11447. [Google Scholar] [CrossRef]
  90. Singh, B.K.; Lee, S.; Na, K. An overview on metal-related catalysts: Metal oxides, nanoporous metals and supported metal nanoparticles on metal organic frameworks and zeolites. Rare Met. 2020, 39, 751–766. [Google Scholar] [CrossRef]
  91. Ndolomingo, M.J.; Bingwa, N.; Meijboom, R. Review of supported metal nanoparticles: Synthesis methodologies, advantages and application as catalysts. J. Mater. Sci. 2020, 55, 6195–6241. [Google Scholar] [CrossRef]
  92. Singh, N.; Ogunseitan, O.A.; Wong, M.H.; Tang, Y. Sustainable materials alternative to petrochemical plastics pollution: A review analysis. Sustain. Horizons 2022, 2, 100016. [Google Scholar] [CrossRef]
  93. Stangel, C.; Charalambidis, G.; Varda, V.; Coutsolelos, A.G.; Kostas, I.D. Aqueous-Organic Biphasic Hydrogenation of trans-Cinnamaldehyde Catalyzed by Rhodium and Ruthenium Phosphane-Free Porphyrin Complexes. Eur. J. Inorg. Chem. 2011, 2011, 4709–4716. [Google Scholar] [CrossRef]
  94. Signoretto, M.; Taghavi, S.; Ghedini, E.; Menegazzo, F. Catalytic Production of Levulinic Acid (LA) from Actual Biomass. Molecules 2019, 24, 2760. [Google Scholar] [CrossRef] [PubMed]
  95. Leal Silva, J.F.; MacIel Filho, R.; Wolf MacIel, M.R. Process Design and Technoeconomic Assessment of the Extraction of Levulinic Acid from Biomass Hydrolysate Using n-Butyl Acetate, Hexane, and 2-Methyltetrahydrofuran. Ind. Eng. Chem. Res. 2020, 59, 11031–11041. [Google Scholar] [CrossRef]
  96. Obregón, I.; Gandarias, I.; Al-Shaal, M.G.; Mevissen, C.; Arias, P.L.; Palkovits, R. The Role of the Hydrogen Source on the Selective Production of γ-Valerolactone and 2-Methyltetrahydrofuran from Levulinic Acid. ChemSusChem 2016, 9, 2488–2495. [Google Scholar] [CrossRef]
  97. Tan, J.; Cui, J.; Ding, G.; Deng, T.; Zhu, Y.; Li, Y.-W. Efficient aqueous hydrogenation of levulinic acid to γ-valerolactone over a highly active and stable ruthenium catalyst. Catal. Sci. Technol. 2016, 6, 1469–1475. [Google Scholar] [CrossRef]
  98. Scrivanti, A.; Beghetto, V.; Bertoldini, M.; Matteoli, U. Catalyst-Free Suzuki-Type Coupling of Allylic Bromides with Arylboronic Acids. Eur. J. Org. Chem. 2012, 2012, 264–268. [Google Scholar] [CrossRef]
  99. Sole, R.; Cappellazzo, J.; Scalchi, L.; Paganelli, S.; Beghetto, V. Synthesis of 2-Alkylaryl and Furanyl Acetates by Palladium Catalyzed Carbonylation of Alcohols. Catalysts 2022, 12, 883. [Google Scholar] [CrossRef]
  100. Nemanashi, M.; Noh, J.-H.; Meijboom, R. Hydrogenation of biomass-derived levulinic acid to γ-valerolactone catalyzed by mesoporous supported dendrimer-derived Ru and Pt catalysts: An alternative method for the production of renewable biofuels. Appl. Catal. A Gen. 2018, 550, 77–89. [Google Scholar] [CrossRef]
Molecules 29 02083 sch001
Scheme 1. Hydrogenation reactions of (a) (E)-cinnamaldehyde (I) and (b) levulinic acid (V).
Scheme 1. Hydrogenation reactions of (a) (E)-cinnamaldehyde (I) and (b) levulinic acid (V).
Molecules 29 02083 sch001
Molecules 29 02083 sch002
Scheme 2. Proposed scheme of MNP formation by coordination of the metal to −COONa groups.
Scheme 2. Proposed scheme of MNP formation by coordination of the metal to −COONa groups.
Molecules 29 02083 sch002
Molecules 29 02083 g001
Figure 1. FTIR spectra of CS (black), Rh(0)-CS (purple) and Ru(0)-CS (green) in KBr.
Figure 1. FTIR spectra of CS (black), Rh(0)-CS (purple) and Ru(0)-CS (green) in KBr.
Molecules 29 02083 g001
Molecules 29 02083 g002
Figure 2. TGA (a) and DSC (b) profiles of CS (black), Rh(0)-CS (magenta) and Ru(0)-CS (green).
Figure 2. TGA (a) and DSC (b) profiles of CS (black), Rh(0)-CS (magenta) and Ru(0)-CS (green).
Molecules 29 02083 g002
Molecules 29 02083 g003
Figure 3. SEM (1 µm), EDX element mapping and energy spectrum of Rh(0)-CS (top) and Ru(0)-CS (bottom).
Figure 3. SEM (1 µm), EDX element mapping and energy spectrum of Rh(0)-CS (top) and Ru(0)-CS (bottom).
Molecules 29 02083 g003
Molecules 29 02083 g004
Figure 4. SEM images (100 nm and 20 nm) of Rh(0)-CS (top) and Ru(0)-CS (bottom).
Figure 4. SEM images (100 nm and 20 nm) of Rh(0)-CS (top) and Ru(0)-CS (bottom).
Molecules 29 02083 g004
Molecules 29 02083 g005
Figure 5. TEM images (50 nm) of Rh(0)-CS (a) and Ru(0)-CS (b).
Figure 5. TEM images (50 nm) of Rh(0)-CS (a) and Ru(0)-CS (b).
Molecules 29 02083 g005
Molecules 29 02083 g006
Figure 6. XRD patterns of Rh(0)-CS (left) and Ru(0)-CS (right).
Figure 6. XRD patterns of Rh(0)-CS (left) and Ru(0)-CS (right).
Molecules 29 02083 g006
Molecules 29 02083 sch003
Scheme 3. Schematic pathways of hydrogenation reaction of (E)-cinnamaldehyde (I).
Scheme 3. Schematic pathways of hydrogenation reaction of (E)-cinnamaldehyde (I).
Molecules 29 02083 sch003
Table 1. Hydrogenation of (I) in the presence of Rh(0) and Ru(0)-CS.
Table 1. Hydrogenation of (I) in the presence of Rh(0) and Ru(0)-CS.
EntryMNP(0)-CSp(H2) (atm)T (°C)Conv. (%) aII(%) aIII(%) aIV(%) a
1Rh(0)-CS108010084313
1r110082018
1r296711514
1r397711415
2 bRh(0)-CS1080329136
3Rh(0)-CS5805281136
4Rh(0)-CS1050259604
5 cRh(0)-CS10801910000
6Ru(0)-CS10804578913
7Ru(0)-CS208053601723
8Ru(0)-CS1010062522127
9Ru(0)-CS2010097202357
9r197192256
9r29513087
9r39714284
9r49613582
Reaction conditions: substrate (I): 25.4 mg (0.79 mmol); Rh/(I): 1/100 mol/mol; solvent: 2.0 mL H2O and 2.0 mL THF; t: 16 h, r: recycling experiment. a Data determined by GLC with undecane as internal standard. b t: 6 h. c Rh/(I): 1/200 (mol/mol).
Table 2. Hydrogenation of levulinic acid in the presence of M(0)NPs-CS.
Table 2. Hydrogenation of levulinic acid in the presence of M(0)NPs-CS.
EntryMNP(0)-CSM/St(h)p(H2) (atm)T (°C)Conv (%) aVI (%) a
1Rh(0)-CS1/100162080100100
2Rh(0)-CS1/100161080100100
3Rh(0)-CS1/100161050100100
3r11/1006868
4Rh(0)-CS1/100165503636
5Ru(0)-CS1/10016550100100
6Ru(0)-CS1/1004550100100
7Ru(0)-CS1/1004250100100
7r1100100
8Ru(0)-CS1/1004250100100
9Ru(0)-CS1/1004150100100
9r19999
9r29999
9r39999
10Ru(0)-CS1/2004550100100
10r18787
10r28585
10r38585
11Ru(0)-CS1/500162080100100
11r1100100
11r2100100
11r3100100
Reaction conditions: substrate: 0.59 mmol; solvent: 4.0 mL H2O. a Data determined by GLC with undecane as internal standard. r: recycling experiment.
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Paganelli, S.; Brugnera, E.; Di Michele, A.; Facchin, M.; Beghetto, V. Chitosan as a Bio-Based Ligand for the Production of Hydrogenation Catalysts. Molecules 2024, 29, 2083. https://doi.org/10.3390/molecules29092083

AMA Style

Paganelli S, Brugnera E, Di Michele A, Facchin M, Beghetto V. Chitosan as a Bio-Based Ligand for the Production of Hydrogenation Catalysts. Molecules. 2024; 29(9):2083. https://doi.org/10.3390/molecules29092083

Chicago/Turabian Style

Paganelli, Stefano, Eleonora Brugnera, Alessandro Di Michele, Manuela Facchin, and Valentina Beghetto. 2024. "Chitosan as a Bio-Based Ligand for the Production of Hydrogenation Catalysts" Molecules 29, no. 9: 2083. https://doi.org/10.3390/molecules29092083

APA Style

Paganelli, S., Brugnera, E., Di Michele, A., Facchin, M., & Beghetto, V. (2024). Chitosan as a Bio-Based Ligand for the Production of Hydrogenation Catalysts. Molecules, 29(9), 2083. https://doi.org/10.3390/molecules29092083