Ionogels Based on Poly(methyl methacrylate) and Metal-Containing Ionic Liquids: Correlation between Structure and Mechanical and Electrical Properties
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
IJMS
Volume 17
Issue 4
10.3390/ijms17040532
ijms-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Fast Conversion of Ionic Liquids and Poly(Ionic Liquid)s into Porous Nitrogen-Doped Carbons in Air

by
Yongjun Men
1,
Martina Ambrogi
1,
Baohang Han
2 and
Jiayin Yuan
1,*
1
Department of Colloid Chemistry, Max Planck Institute of Colloids and Interfaces, Potsdam D–14476, Germany
2
National Center for Nanoscience and Technology, Beijing 100190, China
*
Author to whom correspondence should be addressed.
Int. J. Mol. Sci. 2016, 17(4), 532; https://doi.org/10.3390/ijms17040532
Submission received: 16 March 2016 / Revised: 1 April 2016 / Accepted: 5 April 2016 / Published: 8 April 2016
(This article belongs to the Special Issue Ionic Liquids 2016 and Selected Papers from ILMAT III)
Browse Figures
Versions Notes

Abstract

:
Ionic liquids and poly(ionic liquid)s have been successfully converted into nitrogen-doped porous carbons with tunable surface area up to 1200 m2/g at high temperatures in air. Compared to conventional carbonization process conducted under inert gas to produce nitrogen-doped carbons, the new production method was completed in a rather shorter time without noble gas protection.

Graphical Abstract

1. Introduction

Carbonization is typically a high-temperature reaction converting organic substances into carbon-rich products through pyrolysis or destructive distillation [1,2,3,4,5,6,7,8,9,10,11,12,13,14,15,16,17,18,19]. This process is ideally (though not necessarily) conducted under inert atmosphere, such as N2 or Ar, because air at high temperature may quickly oxidize the carbons formed in situ into gaseous compounds, like CO or CO2, leading to degradation of the carbon products. Particularly challenging is producing porous carbons in air, as the amplified surface contact accelerates the aerobic degradation. It is therefore a matter of scientific curiosity whether one can produce porous carbons in the presence of air. Stucky et al. [20] recently reported the production of hollow, porous carbon spheres, which relied on physical confinement by a dense TiO2 barrier shell to block the access of O2. In fact, physcial confinement has been applied in industrial carbonization processes carried out in sealed chambers, where oxygen is first quickly consumed by the carbon precursors, and then it becomes a process protected by the remaining N2. Strictly speaking, carbonization under confinement is not a truly aerobic carbonization process, as it eliminates oxygen and produces a nitrogen-rich environment to protect the carbonization process. Our interest here is to discuss the production of porous carbons with the presence of air throughout the carbonization process.
Ionic liquids (ILs) are ionic materials in a liquid state below 100 °C. Poly(IL)s (PILs) incorporate ILs as their repeating units, and show improved mechanical stability and processability compared to ILs [21,22,23,24,25]. Recently, both ILs and PILs, due to their high nitrogen content and thermostability, have been used as precursors to nitrogen-doped carbons under N2 or in a confined environment [21,26,27,28,29,30,31,32]. It is known that nitrogen doping is able to adjust the physical properties of carbon via increasing the overall electron density at the Fermi level, which improves the electric conductivity and oxidation stability. Our previous research havs demonstrated the fire-retardant properties of these porous carbons [33]. These properties allow these carbons to remain stable and preservable in air for a defined time at high temperatures without severe mass loss. Bearing this in mind, herein we aimed to introduce a truly aerobic synthetic route to rapidly produce porous nitrogen-doped carbons from IL and PIL at elevated temperatures without the assistance of inert gas or confinement [34]. This method was further coupled with the superior processability of PILs to activate, biomass, hereby exemplified with nature cotton into porous carbon foam in air.

2. Results and Discussion

2.1. Carbonizaiton of Ionic Liquid in Air

In an initial test, the model IL (Scheme 1) was fired in air at 1300 °C with a butane/propane gas burner. It was observed that the IL turned from a transparent liquid to a turbid-black solution and rapidly to a dark solid in ca. 20 s. The dark residue was further combusted totally after 2 min. As this process was rather quick, it is impossible to stop at a specific stage to isolate the carbon product. To slow down this process, we lowered the pyrolysis temperature stepwise. It was found that at 450 °C, even after 1 h, a bulk black residue remained. With this positive observation, we performed more quantitative tests at this temperature. The same IL placed in different crucibles was then transferred into an air oven pre-heated to 450 °C. The samples were taken out sequentially after 5, 10, 15, 30, 60, and 120 min, respectively. All samples were black and used for yield determination, elemental analysis and gas sorption measurements. The results are summarized in Table 1 and Figure 1.
As can be seen from Entries 1–6 in Table 1 and Figure 1A, the carbonization yield drops gradually along extended holding time at 450 °C, from 43.7 wt % for 5 min to only 5.6 wt % for 120 min. This trend is actually expected, as long-term exposure to air at 450 °C will, though slowly, degrade the carbon products, because the favorable nitrogen doping retards but does not stop the oxidation process. When the dwelling time is limited to 60 min, the pore sizes are mainly less than 2 nm (Figure S1), i.e., microporous. The N2 sorption measurements show a peak value of SBET of 635 m2/g after exactly 10 min (Entry 2 in Table 1). Samples prepared either earlier or later than this carry lower SBET values. In our opinion, this implies a complex effect from two competitive reactions, namely the pore formation reaction and the oxidative etching of carbons. The pore formation involves the trimerisation of the cyano groups to build up a thermally stable network and the subsequent decomposition of the bis(trifluoromethanesulfonyl)imide (Tf2N) anion to introduce the pores. The decomposition of Tf2N anion at 450 °C can be monitored by elemental analysis, i.e., the residue sulfur in the carbon products, since in the IL only Tf2N contains sulfur. Figure 1B shows a plot of the C/H/N/S content vs. the carbonization time. A quick decrease in sulfur content occurs in the first 15 min, followed by a relatively smooth plateau close to zero. This result proves the pore indeed formed via anion decomposition, dominantly, in the initial 15 min. It is also supported by the rapid weight loss (yield) in the same period (Figure 1A), as Tf2N accounts for 66 wt % of the IL. The oxidative etching of the in situ generated carbon proceeds as long as the sample remains in air at 450 °C. It burnt away the formed porous carbon, lowering the SBET and the yield gradually. It is thus not surprising that the highest SBET value peaks at 10 min, before which the pore formation process prevails over the porous carbon degradation. This is a rather short period compared to the hours typically taken by the usual carbonization process under noble gas protection, not to mention the initial time for replacement of air by inert gas in the oven.
Carbonization temperature is another effect studied here by fixing the holding time to 5 min for all samples. The results (Entries 7–10 in Table 1) are displayed in Figure 1C. Generally, at high carbonization temperatures, a lower yield and more rapid weight loss were observed. For instance, above 600 °C the carbonization yield is less than 10 wt %, while at 450 °C it is as high as 43.7 wt %. The SBET, however, increases with the carbonization temperature. A maximum SBET of 1200 m2/g was found at 700 °C, with a pore size less than 4 nm (Figure S2). Nevertheless, at this temperature the carbonization yield is undesirably low, only 9 wt %. The elemental analysis in Figure 1D shows that the carbon content increases with the temperature due to the accelerated decomposition of the carbon-poor anion and the enhanced elimination of nitrogen and hydrogen atoms at high temperatures.
To get greater insight into thermal decomposition in air, Fourier transform infrared (FTIR) spectrometry measurement was performed on carbons prepared after 5 min of pyrolysis at different temperatures. The spectra are displayed in Figure 2. At 250 °C, the spectrum pattern of IL can be well indexed to each band. No obvious change was found when compared to that at room temperature. Right from 350 °C, the FTIR bands of the imidazolium cation structure at 854 and 926 cm−1 (=C–H bending from imidazole ring) vanished, indicating the thermal structure reorganization occurred and the fire retardant structure formed. The Tf2N anion bands (1050, 1122, 1184 and 1330 cm−1) remain untouched at 350 °C due to its superior thermal stability. Nitrogen sorption measurement of the carbon sample at 350 °C indicates limited surface area (<10 m2/g), since, as mentioned above, the pores form only after the anion decomposition. A large SBET was received once the oven temperature surpassed 350 °C to decompose the Tf2N anion, for example 1200 m2/g at 700 °C. FTIR spectrum of this sample at 700 °C in Figure 2 shows that the Tf2N anion-related bands completely disappeared. This result is understandable, since the surface area comes from the pores left by Tf2N.
The atomic structure of the carbon products was investigated by solid state 13C-NMR measurements [35]. The recorded spectra are displayed in Figure 3. At 450 °C for 5 min, the original sharp peaks from the IL at room temperature were replaced by two broad overlapping bands, i.e., the aromatic carbons (100–140 ppm) and the isolated melon structure (140–170 ppm) [36]. This indicates the occurrence of the trimerisation reaction of the nitrile groups in the IL. No sharp peak at 50–80 ppm was observed so that epoxy or ether structures were absent in the carbon matrix. Annealing at 450 °C for 1 h promotes the transition of the isolated melon structure into aromatic carbons, indicated by the dramatic shrinkage of the melon band between 140 and 170 ppm. When the sample was processed at 700 °C for 5 min, a similar pattern was observed. It implies either extending the annealing period (at 450 °C from 5 min to 1 h) or enhancing the temperature (from 450 to 700 °C, keep the holding time for 5 min) leads to the promoted formation of aromatic carbon frameworks.

2.2. Carbonizaiton of Poly(Ionic Liquid) and Poly(Ionic Liquid) Coated Cotton in Air

All aforementioned analysis indicates that the formation of nitrogen-doped porous carbons directly from pyrolyzing IL in air without any physical confinement is feasible. To extend this method to other materials, the first one we tried is the PILs—that is, polymers incorporate ILs as their repeating units, with similar structure (here, the one shown in Scheme 1) [22,23,24,25,30,31,37]. As shown in Table 2 (Entries 11–15), a carbonization yield of 30.4 wt %, a high nitrogen content of 19 wt % and a SBET~749 m2/g for PIL were obtained at 450 °C after 10 min (Entry 13). A reduced holding time at 450 °C, such as 5 or 6 min drops SBET below 200 m2/g (Entries 11 and 12), and pore sizes are majorly between 2.5 and 4 nm (Figure S3), i.e., small mesopores. At higher temperatures, such as 700 and 800 °C, the SBET increases further to 879 and 955 m2/g, respectively (Entries 14 and 15), and the micropores turned dominant. These experiments prove that the generation of nitrogen-doped porous carbon in air via the IL and PIL route is practically applicable by carefully choosing the pyrolyzing temperature and holding time.

2.3. Carbonizaiton of Poly(Ionic Liquid) Coated Cotton in Air

A further description of this method is by carbonization of PIL-coated cotton (PIL-cotton) in air. The design strategy is that the PIL, as demonstrated, can form a fire-retardant carbon network at around 350 °C, which can be utilized as a protection layer on other non-fire-retardant carbon precursors based on the excellent processibility and mechanical stability of PILs. Here, cotton was selected as the non-fire-retardant precursor due to its low cost and easy shaping properties. As shown in Figure 4, PIL could coat cotton fibers by soaking cotton in a PIL solution in acetonitrile (10 wt %) followed by drying in air. Due to the large pore volume of nature cotton, it is possible to test the aerobic production of porous carbon aerogel from biomass. When placed in air at 450 °C, pure cotton was rapidly burnt away in few seconds, while the PIL-cotton was ignited first, self-quenched within a few seconds and ended up with a dark shrunk foam (Figure 4), which is deformable. Table 2 (Entries 16–22) summarizes the experiments under different PIL loading content and dwelling time. All PIL-cotton carbon aerogels possess a SBET value above 400 m2/g and micropores (Figure S4). Even when only containing 5 wt % of PIL, the SBET value reached to 410 m2/g. The reason might be that the porous fire retardant protecting layer is not dense and thick enough to isolated most of the oxygen from air, and the leaking oxygen can etch the formed carbons as activating agent to increase the volume of micropores and decrease the yield. Compared to pure PIL in entries 11–15, the carbonization yield for carbon aerogels is lower, less than 20 wt % in general. This is understandable, since pure cotton under the same condition leaves nothing. The SEM characterization in Figure 4 proves the good preservation of the microstructure of cotton fiber morphology into the carbon foam. This explains the favorable shape deformability of the carbon foam.

3. Materials and Methods

3.1. Materials

1-Vinylimidazole (99%), bromoacetonitrile (97%), 1,3-bis(cyanomethyl)imidazolium bis(trifluoromethylsulfonyl)imide (≥94%), lithium bis(trifluoro methanesulfonyl)imide (99.95%) were obtained from Sigma-Aldrich (St. Louis, MO, USA) and used without further purification. 2,2′-Azobis(2-methylpropionitrile) (98%, Sigma-Aldrich) was recrystallized from methanol. The solvents and other materials were used as received.

3.2. Synthesis of the PIL Poly(3-cyanomethyl-1-vinyl imidazolium TFSI)

For the IL monomer synthesis, 0.1 mol of 1-vinylimidazole was dropwise added into a bromoacetonitrile (0.1 mol) solution in diethyl ether (50 mL) in a round bottom flask equipped with a condenser and a magnetic stirrer at 25 °C. After overnight stirring, a white precipitate appeared and was isolated. It was washed with ether (50 mL) 3 times and dried at room temperature under high vacuum overnight till constant weight. From this dried monomer powder, 8.4 g of the synthesized monomer was mixed with 160 mg of 2,2′-azobisisobutyronitrile (AIBN) in 100 mL of DMSO in a 250 mL Schlenk glass. After degassing by high vacuum and back-filling with argon, the polymerization was conducted at 90 °C for 12 h. A light yellow solid was obtained by precipitating the mixture solution twice in acetone and dried at 60 °C under vacuum to a constant weight. Yield: 80%. 1H-NMR (DMSO-d6, λ, ppm): 8.9–9.6 (1H), 7.0–8.5 (2H), 5.2–5.7 (2H), 3.5–4.6 (1H), 2.0–2.8 (2H). The apparent molecular mass and the polydispersity index of the PIL polymer was measured by gel permeation chromatography to be 1.15 × 105 g/mol and 2.95, respectively, using polystyrene as standard.

3.3. Carbonizaztion of IL/PIL in Air

An air oven was set at a desired temperature, and then the crucibles with PIL or IL samples were transferred inside directly for carbonization. After the pyrolysis, the crucible was taken out of the oven using tweezers and cooled down to room temperature.

3.4. Characterization Methods

Nitrogen sorption experiments were performed on a Quantachrome Autosorb-1 or Quadrasorb at liquid nitrogen temperature, and data analysis was performed with Quantachrome software. The surface area was calculated using the Brunauer–Emmett–Teller (BET) equation. The pore size distribution was calculated using the density functional theory (DFT) method. The samples were degassed at 200 °C for 15 h before measurements. Elemental analysis was performed for carbon, hydrogen, sulphur and nitrogen using a Vario EL Elementar.

4. Conclusions

In conclusion, we discussed and demonstrated the feasibility of producing nitrogen-doped porous carbons straightforwardly in air without protection gas or confinement by using IL/PIL here as an example. The success of this unique production mode is attributed to the high nitrogen content in the IL/PIL cation and a self-templating mechanism due to the large-sized anion. Compared to the conventional carbonization process under noble gas protection, this aerobic carbonization method is more rapid. Based on this prototype mode of the air-carbon synthesis, it is of future interest to increase the carbonization yield while keeping the high-surface-area nature of the carbon products during the synthesis. Additionally, the applicability of this synthetic strategy can be further expanded by employment of other cheaper and greener carbon precursors. For example, various fire retardant materials can be applied after careful design to generate in situ porous hybrid carbon materials by mixing with suitable dissipative templates without noble gas protection.

Supplementary Materials

Supplementary materials can be found at https://www.mdpi.com/1422-0067/17/4/532/s1.

Acknowledgments

The research work was supported by an international joint laboratory program between the Max Planck Institute of Colloids and Interfaces in Germany and the National Center for Nanoscience and Technology in China. Yongjun Men thanks Karoline Täuber for the SEM measurements.

Author Contributions

Yongjun Men and Jiayin Yuan planned the experiments; Yongjun Men and Martina Ambrogi performed the experiments; Yongjun Men and Jiayin Yuan wrote the paper; Yongjun Men, Martina Ambrogi, Baohang Han and Jiayin Yuan discussed the results and revised the manuscript; Jiayin Yuan supervised the project.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Wu, Z.Y.; Li, C.; Liang, H.W.; Chen, J.F.; Yu, S.H. Ultralight, flexible, and fire-resistant carbon nanofiber aerogels from bacterial cellulose. Angew. Chem. Int. Ed. 2013, 52, 2925–2929. [Google Scholar] [CrossRef] [PubMed]
  2. Liang, H.W.; Guan, Q.F.; Chen, L.F.; Zhu, Z.; Zhang, W.J.; Yu, S.H. Macroscopic-scale template synthesis of robust carbonaceous nanofiber hydrogels and aerogels and their applications. Angew. Chem. Int. Ed. 2012, 51, 5101–5105. [Google Scholar] [CrossRef] [PubMed]
  3. Han, B.H.; Zhou, W.; Sayari, A. Direct preparation of nanoporous carbon by nanocasting. J. Am. Chem. Soc. 2003, 125, 3444–3445. [Google Scholar] [CrossRef] [PubMed]
  4. Deng, Y.; Cai, Y.; Sun, Z.; Liu, J.; Liu, C.; Wei, J.; Li, W.; Liu, C.; Wang, Y.; Zhao, D. Multifunctional mesoporous composite microspheres with well-designed nanostructure: A highly integrated catalyst system. J. Am. Chem. Soc. 2010, 132, 8466–8473. [Google Scholar] [CrossRef] [PubMed]
  5. Liu, L.; He, D.; Wang, G.S.; Yu, S.H. Bioinspired crystallization of CaCO3 coatings on electrospun cellulose acetate fiber scaffolds and corresponding CaCO3 microtube networks. Langmuir 2011, 27, 7199–7206. [Google Scholar] [CrossRef] [PubMed]
  6. Mane, G.P.; Talapaneni, S.N.; Anand, C.; Varghese, S.; Iwai, H.; Ji, Q.; Ariga, K.; Mori, T.; Vinu, A. Preparation of highly ordered nitrogen-containing mesoporous carbon from a gelatin biomolecule and its excellent sensing of acetic acid. Adv. Funct. Mater. 2012, 22, 3596–3604. [Google Scholar] [CrossRef]
  7. Sun, X.; Li, Y. Colloidal carbon spheres and their core/shell structures with noble-metal nanoparticles. Angew. Chem. Int. Ed. 2004, 43, 597–601. [Google Scholar] [CrossRef] [PubMed]
  8. Luo, W.; Bommier, C.; Jian, Z.; Li, X.; Carter, R.; Vail, S.; Lu, Y.; Lee, J.J.; Ji, X. Low-surface-area hard carbon anode for Na-ion batteries via graphene oxide as a dehydration agent. ACS Appl. Mater. Interfaces 2015, 7, 2626–2631. [Google Scholar] [CrossRef] [PubMed]
  9. Borchardt, L.; Oschatz, M.; Kaskel, S. Tailoring porosity in carbon materials for supercapacitor applications. Mater. Horiz. 2014, 1, 157–168. [Google Scholar] [CrossRef]
  10. Wohlgemuth, S.A.; Vilela, F.; Titirici, M.M.; Antonietti, M. A one-pot hydrothermal synthesis of tunable dual heteroatom-doped carbon microspheres. Green Chem. 2012, 14, 741–749. [Google Scholar] [CrossRef]
  11. Su, D.S.; Perathoner, S.; Centi, G. Nanocarbons for the development of advanced catalysts. Chem. Rev. 2013, 113, 5782–5816. [Google Scholar] [CrossRef] [PubMed]
  12. Kowalewski, T.; Tsarevsky, N.V.; Matyjaszewski, K. Nanostructured carbon arrays from block copolymers of polyacrylonitrile. J. Am. Chem. Soc. 2002, 124, 10632–10633. [Google Scholar] [CrossRef] [PubMed]
  13. Lu, A.H.; Li, W.C.; Hao, G.P.; Spliethoff, B.; Bongard, H.J.; Schaack, B.B.; Schüth, F. Easy synthesis of hollow polymer, carbon, and graphitized microspheres. Angew. Chem. Int. Ed. 2010, 49, 1615–1618. [Google Scholar] [CrossRef] [PubMed]
  14. Qian, W.; Sun, F.; Xu, Y.; Qiu, L.; Liu, C.; Wang, S.; Yan, F. Human hair-derived carbon flakes for electrochemical supercapacitors. Energy Environ. Sci. 2014, 7, 379–386. [Google Scholar] [CrossRef]
  15. Li, Q.; Zhao, J.; Sun, B.; Lin, B.; Qiu, L.; Zhang, Y.; Chen, X.; Lu, J.; Yan, F. High-temperature solid-state dye-sensitized solar cells based on organic ionic plastic crystal electrolytes. Adv. Mater. 2012, 24, 945–950. [Google Scholar] [CrossRef] [PubMed]
  16. Adelhelm, P.; de Jongh, P.E. The impact of carbon materials on the hydrogen storage properties of light metal hydrides. J. Mater. Chem. 2011, 21, 2417–2427. [Google Scholar] [CrossRef]
  17. Bender, C.L.; Jache, B.; Adelhelm, P.; Janek, J. Sodiated carbon: A reversible anode for sodium-oxygen batteries and route for the chemical synthesis of sodium superoxide (NaO2). J. Mater. Chem. A 2015, 3, 20633–20641. [Google Scholar] [CrossRef]
  18. Zhang, P.; Gong, Y.; Li, H.; Chen, Z.; Wang, Y. Solvent-free aerobic oxidation of hydrocarbons and alcohols with PD@N-doped carbon from glucose. Nat. Commun. 2013, 4, 1593. [Google Scholar] [CrossRef] [PubMed]
  19. Xu, X.; Li, Y.; Gong, Y.; Zhang, P.; Li, H.; Wang, Y. Synthesis of palladium nanoparticles supported on mesoporous N-doped carbon and their catalytic ability for biofuel upgrade. J. Am. Chem. Soc. 2012, 134, 16987–16990. [Google Scholar] [CrossRef] [PubMed]
  20. Suh, W.H.; Kang, J.K.; Suh, Y.H.; Tirrell, M.; Suslick, K.S.; Stucky, G.D. Porous carbon produced in air: Physicochemical properties and stem cell engineering. Adv. Mater. 2011, 23, 2332–2338. [Google Scholar] [CrossRef] [PubMed]
  21. Paraknowitsch, J.P.; Zhang, Y.; Wienert, B.; Thomas, A. Nitrogen- and phosphorus-co-doped carbons with tunable enhanced surface areas promoted by the doping additives. Chem. Commun. 2013, 49, 1208–1210. [Google Scholar] [CrossRef] [PubMed]
  22. Li, S.; Qiu, L.; Shi, C.; Chen, X.; Yan, F. Water-resistant, solid-state, dye-sensitized solar cells based on hydrophobic organic ionic plastic crystal electrolytes. Adv. Mater. 2014, 26, 1266–1271. [Google Scholar] [CrossRef] [PubMed]
  23. Guo, J.; Yuan, C.; Guo, M.; Wang, L.; Yan, F. Flexible and voltage-switchable polymer velcro constructed using host-guest recognition between poly(ionic liquid) strips. Chem. Sci. 2014, 5, 3261–3266. [Google Scholar] [CrossRef]
  24. Fischer, S.; Schimanowitz, A.; Dawson, R.; Senkovska, I.; Kaskel, S.; Thomas, A. Cationic microporous polymer networks by polymerisation of weakly coordinating cations with CO2-storage ability. J. Mater. Chem. A 2014, 2, 11825–11829. [Google Scholar] [CrossRef]
  25. Men, Y.; Kuzmicz, D.; Yuan, J. Poly(ionic liquid) colloidal particles. Curr. Opin. Colloid Interface Sci. 2014, 19, 76–83. [Google Scholar] [CrossRef]
  26. Lee, J.S.; Wang, X.; Luo, H.; Baker, G.A.; Dai, S. Facile ionothermal synthesis of microporous and mesoporous carbons from task specific ionic liquids. J. Am. Chem. Soc. 2009, 131, 4596–4597. [Google Scholar] [CrossRef] [PubMed]
  27. Zhai, Y.; Dou, Y.; Zhao, D.; Fulvio, P.F.; Mayes, R.T.; Dai, S. Carbon materials for chemical capacitive energy storage. Adv. Mater. 2011, 23, 4828–4850. [Google Scholar] [CrossRef] [PubMed]
  28. Paraknowitsch, J.P.; Thomas, A.; Antonietti, M. A detailed view on the polycondensation of ionic liquid monomers towards nitrogen doped carbon materials. J. Mater. Chem. 2010, 20, 6746–6758. [Google Scholar] [CrossRef]
  29. Paraknowitsch, J.P.; Zhang, J.; Su, D.; Thomas, A.; Antonietti, M. Ionic liquids as precursors for nitrogen-doped graphitic carbon. Adv. Mater. 2010, 22, 87–92. [Google Scholar] [CrossRef] [PubMed]
  30. Soll, S.; Fellinger, T.P.; Wang, X.; Zhao, Q.; Antonietti, M.; Yuan, J. Water dispersible, highly graphitic and nitrogen-doped carbon nanobubbles. Small 2013, 9, 4135–4141. [Google Scholar] [CrossRef] [PubMed]
  31. Kuzmicz, D.; Prescher, S.; Polzer, F.; Soll, S.; Seitz, C.; Antonietti, M.; Yuan, J. The colloidal stabilization of carbon with carbon: Carbon nanobubbles as both dispersant and glue for carbon nanotubes. Angew. Chem. Int. Ed. 2014, 53, 1062–1066. [Google Scholar] [CrossRef] [PubMed]
  32. Ranjbar Sahraie, N.; Paraknowitsch, J.P.; Göbel, C.; Thomas, A.; Strasser, P. Noble-metal-free electrocatalysts with enhanced ORR performance by task-specific functionalization of carbon using ionic liquid precursor systems. J. Am. Chem. Soc. 2014, 136, 14486–14497. [Google Scholar] [CrossRef] [PubMed]
  33. Men, Y.; Siebenburger, M.; Qiu, X.; Antonietti, M.; Yuan, J. Low fractions of ionic liquid or poly(ionic liquid) can activate polysaccharide biomass into shaped, flexible and fire-retardant porous carbons. J. Mater. Chem. A 2013, 1, 11887–11893. [Google Scholar] [CrossRef]
  34. Ambrogi, M.; Men, Y.; Polzer, F.; Yuan, J. Salt-confinement enables production of nitrogen-doped porous carbons in an air oven. RSC Adv. 2014, 4, 37714–37720. [Google Scholar] [CrossRef]
  35. Jürgens, B.; Irran, E.; Senker, J.; Kroll, P.; Müller, H.; Schnick, W. Melem (2,5,8-triamino-tri-s-triazine), an important intermediate during condensation of melamine rings to graphitic carbon nitride: Synthesis, structure determination by X-ray powder diffractometry, solid-state nmr, and theoretical studies. J. Am. Chem. Soc. 2003, 125, 10288–10300. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  36. Sehnert, J.; Baerwinkel, K.; Senker, J. Ab initio calculation of solid-state NMR spectra for different triazine and heptazine based structure proposals of g-C3N4. J. Phys. Chem. B 2007, 111, 10671–10680. [Google Scholar] [CrossRef] [PubMed]
  37. Yuan, J.; Mecerreyes, D.; Antonietti, M. Poly(ionic liquid)s: An update. Prog. Polym. Sci. 2013, 38, 1009–1036. [Google Scholar] [CrossRef]
Ijms 17 00532 sch001 1024
Scheme 1. Chemical structures of the ionic liquid (left) and poly(ionic liquid) (right) used in this work for aerobic carbonization.
Scheme 1. Chemical structures of the ionic liquid (left) and poly(ionic liquid) (right) used in this work for aerobic carbonization.
Ijms 17 00532 sch001
Ijms 17 00532 g001 1024
Figure 1. Plots of (A) carbonization yield and SBET (Brunauer–Emmett–Teller specific surface area) vs. the pyrolysis time (Entries 1–6 in Table 1); (B) the C/H/N/S content of carbon products prepared at 450 °C at different time; (C) carbonization yield and SBET vs. the pyrolysis temperature (Entries 7–10 in Table 1); (D) the C/H/N/S content of carbon products prepared via 5 min pyrolysis at different temperatures.
Figure 1. Plots of (A) carbonization yield and SBET (Brunauer–Emmett–Teller specific surface area) vs. the pyrolysis time (Entries 1–6 in Table 1); (B) the C/H/N/S content of carbon products prepared at 450 °C at different time; (C) carbonization yield and SBET vs. the pyrolysis temperature (Entries 7–10 in Table 1); (D) the C/H/N/S content of carbon products prepared via 5 min pyrolysis at different temperatures.
Ijms 17 00532 g001
Ijms 17 00532 g002 1024
Figure 2. FTIR spectra of carbonization products of IL prepared after 5 min at temperatures from 25 to 700 °C.
Figure 2. FTIR spectra of carbonization products of IL prepared after 5 min at temperatures from 25 to 700 °C.
Ijms 17 00532 g002
Ijms 17 00532 g003 1024
Figure 3. Solid state 13C-NMR spectra of IL prepared at different holding time and temperatures.
Figure 3. Solid state 13C-NMR spectra of IL prepared at different holding time and temperatures.
Ijms 17 00532 g003
Ijms 17 00532 g004 1024
Figure 4. Preparation of carbon foam via carbonization in air and their corresponding SEM images (scale bar: 20 µM).
Figure 4. Preparation of carbon foam via carbonization in air and their corresponding SEM images (scale bar: 20 µM).
Ijms 17 00532 g004
Table
Table 1. Analysis results of carbon products obtained via pyrolysing ionic liquid (IL) in air at different holding times and temperatures. (SBET: Brunauer–Emmett–Teller specific surface area.)
Table 1. Analysis results of carbon products obtained via pyrolysing ionic liquid (IL) in air at different holding times and temperatures. (SBET: Brunauer–Emmett–Teller specific surface area.)
EntryTemperature (°C)Time (min)SBET (m2/g)Yield (wt %)Nitrogen Content (wt %)
1450545143.721.2
24501063530.327.1
34501551125.629.4
44502048124.030.5
5450605114.433.7
6450120765.634.4
7500556721.028.2
860057019.825.7
9700512009.018.6
10800510778.815.0
Table
Table 2. Analysis results of carbon products obtained via pyrolysing poly(IL)s (PILs) (Entries 11–15) and cotton-PIL composites (Entries 16–22) in air at different holding times and temperatures.
Table 2. Analysis results of carbon products obtained via pyrolysing poly(IL)s (PILs) (Entries 11–15) and cotton-PIL composites (Entries 16–22) in air at different holding times and temperatures.
EntryMaterialTemperature (°C)Time (min)SBET (m2/g)Yield (wt %)N (wt %)
11PIL45053357.913.2
12PIL450617448.114.8
13PIL4501074930.419.0
14PIL700587913.513.6
15PIL800595511.88.8
16cotton-PIL (0) [a]4505-00
17cotton-PIL (5)45054103.86.9
18cotton-PIL (10)45055759.68.8
19cotton-PIL (15)450559512.611.0
20cotton-PIL (15)450105176.513.3
21cotton-PIL (30)450571917.613.1
22cotton-PIL (30)4501052510.312.9
[a] The number in bracket in column “material” means the weight content of PIL in the material.

Share and Cite

MDPI and ACS Style

Men, Y.; Ambrogi, M.; Han, B.; Yuan, J. Fast Conversion of Ionic Liquids and Poly(Ionic Liquid)s into Porous Nitrogen-Doped Carbons in Air. Int. J. Mol. Sci. 2016, 17, 532. https://doi.org/10.3390/ijms17040532

AMA Style

Men Y, Ambrogi M, Han B, Yuan J. Fast Conversion of Ionic Liquids and Poly(Ionic Liquid)s into Porous Nitrogen-Doped Carbons in Air. International Journal of Molecular Sciences. 2016; 17(4):532. https://doi.org/10.3390/ijms17040532

Chicago/Turabian Style

Men, Yongjun, Martina Ambrogi, Baohang Han, and Jiayin Yuan. 2016. "Fast Conversion of Ionic Liquids and Poly(Ionic Liquid)s into Porous Nitrogen-Doped Carbons in Air" International Journal of Molecular Sciences 17, no. 4: 532. https://doi.org/10.3390/ijms17040532

APA Style

Men, Y., Ambrogi, M., Han, B., & Yuan, J. (2016). Fast Conversion of Ionic Liquids and Poly(Ionic Liquid)s into Porous Nitrogen-Doped Carbons in Air. International Journal of Molecular Sciences, 17(4), 532. https://doi.org/10.3390/ijms17040532

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop