Next Article in Journal
Optimization Design of an Inductive Energy Harvesting Device for Wireless Power Supply System Overhead High-Voltage Power Lines
Next Article in Special Issue
Inorganic p-Type Semiconductors: Their Applications and Progress in Dye-Sensitized Solar Cells and Perovskite Solar Cells
Previous Article in Journal
Progress in Heat Pump Air Conditioning Systems for Electric Vehicles—A Review
Previous Article in Special Issue
Molecular Level Factors Affecting the Efficiency of Organic Chromophores for p-Type Dye Sensitized Solar Cells
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Towards Renewable Iodide Sources for Electrolytes in Dye-Sensitized Solar Cells

by
Iryna Sagaidak
1,3,
Guillaume Huertas
1,2,3,
Albert Nguyen Van Nhien
2,3 and
Frédéric Sauvage
1,3,*
1
Laboratoire de Réactivité et Chimie des Solides, Université de Picardie Jules Verne, CNRS UMR 7314, 33 rue Saint Leu, Amiens 80039, France
2
Laboratoire de Glycochimie, des Antimicrobiens et des Agroressources, Université de Picardie Jules Verne, CNRS FRE3517, 33 rue Saint Leu, Amiens 80039, France
3
Institut de Chimie de Picardie, FR 3085 CNRS, UFR des Sciences, Université de Picardie Jules Verne, 33 rue Saint Leu, Amiens Cedex 1 80039, France
*
Author to whom correspondence should be addressed.
Energies 2016, 9(4), 241; https://doi.org/10.3390/en9040241
Submission received: 13 December 2015 / Revised: 14 March 2016 / Accepted: 15 March 2016 / Published: 26 March 2016
(This article belongs to the Special Issue Dye Sensitized Solar Cells)

Abstract

:
A novel family of iodide salts and ionic liquids based on different carbohydrate core units is herein described for application in dye-sensitized solar cell (DSC). The influence of the molecular skeleton and the cationic structure on the electrolyte properties, device performance and on interfacial charge transfer has been investigated. In combination with the C106 polypyridyl ruthenium sensitizer, power conversion efficiencies lying between 5.0% and 7.3% under standard Air Mass (A.M.) 1.5G conditions were obtained in association with a low volatile methoxypropionitrile (MPN)-based electrolyte.

Graphical Abstract

1. Introduction

The constant population growth combined with the increasing energy dependence raises fundamental questions on how energy can be supplied with the demand expecting to double by 2050 [1]. Energy production is currently dominated by the combustion of fossil fuels (ca. 80%). The increased awareness of the relationship between fossil fuel burning and greenhouse gas emissions together with the limited crude oil stocks prompt the development of a greener chemistry, synonymous with lower environmental footprints and new energy sources being sustainable and renewable. Solar energy gathers all these criteria to leverage the required energetic transition [2,3,4]. The deployment of 10% efficiency photovoltaic panels on 0.1% of Earth’s surface can sustain current humanity needs (1014 kWh) [5].
However, the intermittent and unpredictable character of solar power requires its hybridization to an external energy storage system capable of stabilizing electricity production and matching the offer with the population’s demand. Furthermore, current photovoltaic and battery costs are still not competitive enough compared to fossil fuel combustion. These two drawbacks impede the penetration of solar energy into the current energetic mix. An important impetus towards low cost, low environmental footprint photovoltaics was given by M. Graetzel et al. [6] back in the early 90s, reporting on an efficient dye-sensitized solar cell (DSC) technology based on nanocrystalline anatase TiO2 particles.
Rapidly passing the double digit threshold in 1993 [7], it has recently reached a power conversion efficiency (PCE) of 14.3% using two different organic dyes combined with [Co(phen)3]3+/2+ redox couple [8]. DSC also achieved ca. 10% stable PCE when combined with low-volatile nitrile solvents under Air Mass (A.M.) 1.5G conditions (100 mW/cm2) [9,10].
Although the best conversion performances are nowadays dominated by a series of one electron redox mediator based on cobalt +III/+II complexes, the stability still lags far behind the I3/I redox couple in conjunction with either a low-volatile solvent, e.g., alkoxynitriles [9], sulfolane [11], tetraglyme [12], or in solvent-free binary/ternary eutectic melts, extending the device service lifetime but at the expense of high efficiencies [13]. The source of iodide in the electrolyte is mainly originating from ionic liquids based on the series of 1,3 di-alkyl imidazolium compounds, issued from petroleum derivatives. Other types of cations have been synthesized and incorporated in electrolyte formulation with limited success [13,14,15]. Attempts to integrate greener solvents for organic PhotoVoltaics (OPV) and greener functionalized imidazolium salts in electrolytes for dye-sensitized solar cells demonstrated the potentialities of these new molecules to even improve some of the properties of the device compared to petroleum derivatives [16,17].
In this work, we report the development of a new series of iodide salts and ionic liquids based on carbohydrate d-glucose or d-mannose core units. Carbohydrates are a family of chemicals among the most abundant natural sources while having benign environmental and health impacts. These novel molecules, incorporated in 3-methoxypropionitrile electrolyte formulation, can exhibit as high as 7.3% PCE in combination with high molar extinction coefficient C106 ruthenium dye. The impact of the elimination of the labile anomeric acetal, the influence of the nucleophilic unit, as well as the functionalized hydroxyl group at C-2 on the electrolyte and device performance is herein discussed.

2. Results and Discussion

The new iodide-based carbohydrates were included into low-volatile electrolyte composition based on 3-methoxypropionitrile (MPN). The formulation is analogous to the current state-of-the-art in dye-sensitized solar cells enabling to pass ageing tests at 60 °C/hv (100 mW·cm−2) or under 80 °C/dark conditions [18], namely 1 M of iodide source, 0.15 M of iodine, 0.5 M of 1H-N-butylbenzimidazole (NBB) and 0.1 M of guanidinium thiocyanate (GuNCS). By way of comparison to current standards, the new electrolytes are permanently referred to the best performing 1,3-dimethylimidazolium iodide (DMII). For the different compounds synthesized, we gathered in Table 1 their main physical characteristics and corresponding properties when solubilized in electrolyte. DMII belongs to the class of ionic liquid compounds having a melting temperature of 93.6 °C as determined by differential calorimetric measurements. Besides M0(MII) and Ga(MII), which are viscous liquids at room temperature, the other compounds exhibit a melting point lying between 118 °C for Ga(TEA) and 140 °C for M0(TEA). These are consequently purely ionic salts by contrast to all N,N′-dialkylimidazolium iodide being ionic liquids [19]. These iodide carbohydrates are starting to thermally decompose in air at around 300 °C, thus being thermally stable above the temperature requirements of IEC61646 standard protocol. DSC measurements of the room-temperature liquid M0(MII) and Ga(MII) upon cooling to −100 °C did not show evidence of any solidification or crystallization exothermic peak. This observation is not really surprising since many ionic liquids (ILs) have a tendency to show a supercooling effect, owing to extremely slow kinetics of solidification [20]. Upon heating, a broad endothermic glass transition is experienced for which the onset is −19.1 °C (ΔCp = 0.67 J/g·K) for M0(MII) and −28.6 °C (ΔCp = 0.55 J/g·K) for Ga(MII).
Conductivity and ionic diffusion in electrolytes are two parameters controlled by the viscosity through Nernst-Einstein and Stokes-Einstein relationships [21]. In such kinds of electrolytes, the viscosity is principally dominated by the solvent characteristics for which its intrinsic viscosity is ca. 1.1 cP [22]. When the additives and iodine/iodide redox couple are incorporated, the viscosity increases to 2.10 cP for the benchmark DMII, and up to 3.8 cP for M0(MII). The lowest viscosity is 2.6 cP for the new electrolyte composed of the ionic liquid Ga(MII). It seems rather difficult to rationalize the relationship between the viscosity and iodide salt structure, as it is often the case with ILs and organic solvents. However, these results tend to suggest that the incorporation of ionic liquid into MPN limits the viscosity augmentation. Consequently, the transport properties are the greatest when using DMII. For the latter, ionic conductivity is 7.1 × 10−3 S·cm−1, the diffusion coefficient 9.4 × 10−4 cm2/s for iodide and slower for tri-iodide: 5.0 × 10−5 cm2/s determined by CV and 1.6 × 10−5 cm2/s by Electrochemical Impedance Spectroscopy (EIS). Although the two latter methods do not yield to exactly the same values, the trend is not affected. They are also in relatively good concordance with the values reported in the literature so far [9,15,23,24,25]. This result highlights that the diffusion of tri-iodide is kinetically the rate-limiting factor in the transport properties of the electrolytes, as one could expect. Nevertheless, it is remarkable that MII-based carbohydrates are offering ion transport characteristics relatively close to those of DMII; d-glucose being slightly better than d-mannose derivatives (Table 1).
Interestingly, the nature of the cation also influences the charge transfer resistance as expected from its different coordination environment and possibly solvation strength. For the DMII reference sample, we found an Rct value of 1.70 Ω·cm2. For the new sugar-based molecules, the values are greater, ranging from 2.90 Ω·cm2 for Ga(THT) to 8.80 Ω·cm2 for M0(MII). Comparing within this new library of materials, it was found that the d-glucose core unit is preferred to the d-mannose counterpart for maintaining low charge transfer resistances. The methoxy (OMe) in anomeric position also diminishes by about two times the charge transfer resistance suggesting a significant role of this group in the charge transfer process.
Chemical stability of the electrolyte was first evaluated in fluorine-doped tin oxide (FTO)-Pt symmetric cells accordingly to IEC61646 protocol at 60 °C/100 mW·cm−2 for 1000 h (Figure 1). At room-temperature/ambient conditions, all electrolytes revealed excellent stability properties. When accelerated ageing was carried out using the aforementioned conditions, electrolytes based on d-mannose failed systematically to reach 1000 h of ageing. All the devices assembled with such electrolytes are degrading, leading to electrolyte leakage after 500 h. Sealing issue cannot be incriminated as all electrolytes based on d-glucose and on N,N′-dialkylimidazolium iodide never showed such a feature. Consequently, we presume that d-mannose-based electrolytes are not chemically stable with respect to platinum nanoparticles leading to the formation of volatile by-products. This translates into the device (e.g., based on M0(TEA)) on a rapid loss of mass transport coming with an increase in both the charge transfer resistance at transparent conducting oxide (TCO)-Pt interface and electrolyte ohmic drop upon ageing at 60 °C under 100 mW/cm2 illumination (Figure 1).
Whereas the initial values for tri-iodide diffusion coefficient were favorable to DMII, upon ageing it is shown that the characteristics of Ga(THT) and, to a lesser extent Ga(TEA), can compete with the benchmark. The decrease of charge transfer resistance when using DMII is in good agreement with previous observations and is attributed to the formation of the so-called Solid Electrolyte Interphase (SEI) layer on platinum nanoparticles [26].
The light-to-electricity conversion performances in complete devices have been examined using the hydrophobic ruthenium(+II) polypyril C106 dye. [27] While the DSC assembled with the benchmark electrolyte exhibits a PCE of 8.0% with Jsc = 16.9 mA/cm2, Voc = 680 mV and ff = 69.3% (Table 2), we also reached reasonably worthy performances with new electrolytes based on iodide carbohydrates, PCE = 7.3% is associated with Ga(MII) and G0(MII), 6.9% and 6.7% for M0(TEA) and M0(MII), respectively. More modest performances were obtained with the electrolyte based on Ga(THT) with only 5.0% PCE resulting from a drop of 100 mV in the photovoltage and a low value of 53.2% for the fill factor (Table 2). Considering the difficulties for the synthesis of the tetrahydrothiophene to lead to final yield of less than 10%, the results underline that this nucleophilic group does not seem interesting neither in terms of synthesis nor for the application even though the characteristics in TCO-Pt symmetric cell were amongst the most appealing.
As aforementioned, compared to DMII, the main drawback of carbohydrates stems from their low fill factor value, which can be explained by their greater steric hindrance. This contributes to penalizing their intrinsic properties in terms of conductivity, redox diffusion coefficients and ohmic drop.
Based on our results, there is no consensual conclusion that can be drawn on whether it is preferable to select d-glucose or d-mannose as a core unit for obtaining high efficiencies. Indeed, whereas d-glucose performs better than the d-mannose in association with the MII nucleophilic group (ηM0(MII) = 6.7% vs. ηG0(MII) = 7.3%), opposite results were obtained in the case of TEA (ηM0(TEA) = 6.9% vs. ηG0(TEA) = 5.8%). The results obtained with TEA cation is in a good agreement with the observations made in literature by Graetzel et al. [15], who reported that TEA-based iodide ionic liquids are exhibiting inferior PCE and stability than DMII. Finally, it appears relatively clear from this branch of new molecules that the incorporation of a methoxy group in anomeric position in both cases is beneficial to limit the drop in the fill factor value. At the present stage of electrolyte formulation, we found that electrolytes based on carbohydrates core unit is comparatively less stable than DMII (Figure 2). Regardless of the type of electrolyte, our results show that the degradation rate is faster than in the complete cell. This is in good agreement with our recent report highlighting the harmful role played by the surface of TiO2 on the electrolyte stability when the 3-methoxypropionitrile is used as a solvent [26]. The loss of power conversion efficiency during ageing results from a drastic decreases of photocurrent and fill factor. The rate of photovoltage decline seems relatively comparable regardless of the electrolyte, suggesting that the source of iodide seems not playing any role in this loss. It seems again that d-glucose should be preferred for stability over the mannose counterpart. Even though it is likely that carbohydrates-based electrolytes require further optimization in the additive formulation for instance, one can find that cell degradation is faster in our case than in some publications in the literature showing stability with low-volatile MPN-based electrolytes. Note in this case that our ageing experiments were conducted without any external means of UV cut-off filters, which are well-established to prolong the device stability under light stress.
The best efficiencies are obtained with the methylimidazolium nucleophilic cation in association with the d-glucose core unit. From a fundamental point of view, it is worth mentioning that the immobilization of the methylimidazolium unit on sugar allows for the increase of the photovoltage by ca. 20 mV (Figure 3). In order to gain better insight on the origin of this photovoltage increase as well as to better delineate the effect of the carbohydrate structure on the interfacial charge transfer kinetics (recombination and transport), EIS was used to monitor these processes taking place within the millisecond time domain.
In Figure 4, we report the distribution of the trap states, electron lifetime and electron transport time as a function of either applied voltage or density of states (DOS). The DOS is usually determined for suitable interpretation of the electron lifetime and electron transport time in TiO2 as a function of the number of charges in TiO2. This was evaluated from the value of cell capacitance determined by impedance spectroscopy taking into account the geometric factor of the cell according to this relationship [14,28,29]:
DOS = 6.24   × 10 18 C [ d ( 1 p ) ]
where C is the film capacitance in F/cm2, d and p are the thickness (cm) and porosity of the TiO2 film, respectively. Interestingly, the single exponential distribution and related energy of the intra-band gap trap states depend on the type of iodide source used in the electrolyte. This testifies, as one could expect, to the obvious electrostatic interactions existing between the surface of TiO2 and the electrolyte components. Besides for Ga(THT), in which the energy of the traps is upshifted by comparison to DMII, the incorporation in electrolyte of iodide carbohydrates induces a slight downshift of the traps. This downshift is the most manifested with MII nucleophilic moiety on d-mannose.
The distribution and energy of the traps partly affect the dynamics of electron recombination and electron transport properties. Interestingly, the type of nucleophilic cation has a significant impact on the electron lifetime. This means that, to some extent, it hampers the electron capture by tri-iodide, likely as a result of its steric hindrance. In contrast, the nucleophilic cation has no or only a little influence on the electron transport process, which is provided by a surface trapping/detrapping mechanism [30]. This is particularly true if we make a comparison at the same DOS (Figure 4b). It has been shown in the literature that this electron surface transport is assisted by an ambipolar diffusion process with electrolyte cations. This seems to demonstrate that the guanidinium cation from the electrolyte controls this ambipolar diffusion in contrast with the nucleophilic cation immobilized on the carbohydrate core unit. Comparing DMII with carbohydrates, specifically those made of MII nucleophilic cation, the gain in electron lifetime is noticeable. It can reach up to one order of magnitude regardless if it as a function of bias voltage or compared at the same DOS. Consequently, the charge collection efficiency is getting improved when using MII-based carbohydrates. The gain of ca. 20 mV in photovoltage and greater photocurrent by immobilizing MII on the carbohydrate core unit is thus explained by this extended electron lifetime/enhanced charge collection efficiency. However, this is not the sole origin since the other carbohydrate molecules showed lower photovoltages, whereas their electron lifetime is also extended, although to a lower level. We can therefore speculate that other faster components are affected such as electron injection rate, dye regeneration or dye excited state lifetime. Finally, the lower electron lifetime of Ga(THT) leading to the poorer conversion performances does not come as a surprise since typically unsaturated cyclic solvent such as the THT is prohibited in photoelectrochemical applications, owing to their strong nucleophilic character tending to capture free electrons yielding to the ring opening [7]. This observation is again a new demonstration that it is needed to avoid the utilization of unsaturated cyclic rings for DSC applications.

3. Conclusions

First carbohydrate-based iodide ionic salts and liquids were synthesized from sugar and then successfully integrated as an iodide source in low-volatile electrolyte composition in dye-sensitized solar cells. In conjunction with the C106 ruthenium sensitizer, imidazolium-based d-glucose showed a PCE reaching 7.3% under standard A.M.1.5G illumination (100 mW/cm2). The structure of the cation in the electrolyte was found to strongly influence the device performance not only in terms of PCE but also through hindering the dynamics of charge recombination. It has been established in this work, among this new library of materials, that N-methyl-imidazolium cation supported on sugar, regardless if it is d-mannose or d-glucose, enables the improvement of the photovoltage of DSC compared to the benchmark DMII. The combination between d-glucose and its anomeric methoxy group can also increase the photocurrent as a result of enhanced charge collection efficiencies. Nevertheless, these carbohydrates are suffering so far from lower fill factor values. Consequently, their utilization can be beneficial and offer greater PCE under low light flux. Their integration with improved conversion performances calls for the development of a new electrolyte formulation better adapted to this class of molecules, in order to render their stability in complete devices competitive, and also requires the replacement of platinum catalyst to bring them above current standards based on petroleum sources. Although these first results highlight limited stability upon ageing at 60 °C/hv conditions, understanding the chemical interplay of these carbohydrates during ageing in dye solar cells will lever up this stability lack and possibly enhance the efficiency of such new types of electrolytes to a similar level with the petroleum derivatives.

4. Experimental Section

All chemicals and solvents were of reagent grade or better, purchased from Aldrich, Acros or Fisher Scientific. The 3-methoxypropionitrile was purchased from Aldrich.
Optical rotations were recorded in CH2Cl2 solution. 1H-NMR (300.13 MHz) and 13C-NMR (75.47 MHz) spectra were recorded in CDCl3, DMSO-d6 or MeOD-d4 (internal Me4Si), respectively. Thin Layer Chromatography (TLC) was performed on Silica F254 and detection was done by UV light at 254 nm or by charring with the phosphomolybdic-H2SO4 reagent. Fourier Transform Infra-Red (FT-IR) spectra were obtained on an AVATAR™ 320 neat in attenuated total reflectance (ATR) mode. Mass spectral data were acquired on a WATERS Micromass ZQ spectrometer or a WATERS Micromass Q-TOF spectrometer. Column chromatography was carried out on Silica Gel 60 (230 mesh). Cyclohexane and ethyl acetate were distilled before using.
Thermogravimetric (TGA) and differential scanning calorimetry (DSC) analyses were realized on a Netzsch thermal analyzer STA 449C Jupiter and Netzsch scanning calorimeter DSC 204 F1. TGA was coupled to a mass spectrometer QMS 403 Aëolos with a stainless steel capillary and a SEV detector (Channeltron, for analysis of gas release. The counting time for the mass spectrometer was 20 ms per m/z values (scanning width: m/z = 10–150 amu) with a dwelling time of 1 s. The samples (10–15 mg) were heated in an alumina crucible until 1000 °C under air for TGA, and cooled down to −100 °C and then heated up to 200 °C under argon for calorimetric analysis, applying in both cases a heating ramp of 10 °C·min−1.
The dye-sensitized solar cell assembly was made as follows. Two types of anatase TiO2 layers were deposited by manual screen-printing (Tiflex upon Nippon Sheet Glass (NSG10) FTO glass. The first, of ca. 9 µm thickness—63% porosity, consisted of nano-sized particles of 20 nm acidic anatase TiO2. This layer was sheltered by a second of ca. 5.5 μm thickness composed of 400 nm size anatase particles to back reflect unabsorbed photons in agreement with Mie scattering theory. Prior to screen printing, NSG10 glass was chemically treated by a 0.04 M TiCl4(aq) solution for 30 min at 70 °C to hamper excessive charge recombination from FTO to the electrolyte. A similar procedure has been applied to the post-annealed photo-anode to enhance the charge collection efficiency while reducing the electrode porosity to ca. 57%. The electrodes were submitted to a post-annealing treatment to remove terpineol and the binder/porogene accordingly to the literature [31]. Prior to sensitization, the photoanode was heated at 520 °C for 30 min in air to remove atmospheric residues adsorbed natively upon TiO2 surface. The photo-anode was then sensitized at room-temperature for 15 h in dark conditions. The dye utilized is the high molar extinction coefficient heteroleptic ruthenium (+II) C106 dye proposed first by Wang et al. [27]. The dye solution used for sensitization was composed of 300 µM of dye in a 1/1 v/v mixture of tertbutanol/acetonitrile solvent mixture including an equimolar ratio of chenodeoxycholic acid as de-aggregating agent.
TEC7 Pilkington FTO glass was used as a counter electrode. A hole of ca. 200 µm in diameter was drilled by sandblasting to enable electrolyte injection by vacuum back-filling. The glass was then cleaned one time for 15 min in 0.1 M HCl solution and twice for 15 min in ethanol using an ultrasonic bath. The counter-electrodes were kept in ethanol until using. A drop of 5 mM H2PtCl6 (EtOH) solution was cast and heat-treated at 450 °C for 15 min in air to yield a layer of PtOx-Pt nanoparticles. The two electrodes were assembled by a 25 μm thick transparent Surlyn® gasket polymer DuPont.
Tri-iodide diffusion coefficient and interfacial charge transfer resistance on FTO-Pt electrode were determined using EIS on FTO-Pt/electrolyte/Pt-FTO symmetric cell configuration. The EIS measurements were performed from 200 kHz down to 10 mHz with a superimposed sinusoidal of 10 mV perturbation in the dark at 25 °C (for both symmetric and DSC devices). The measurements were conducted with a Biologic VMP3 potentiostat/galvanostat/impedancemeter. The EIS data were analyzed using ZView 3.2b software by applying the Randles circuit theory [32]. The diffusion coefficient was determined using the equation D I 3 - = L 2 / W s , where L corresponds to the separation distance between the two FTO-Pt electrodes and Ws to the Warburg coefficient determined by the fitting analysis of low frequency Nernst diffusion part in the Nyquist plot. All kinetic parameters acquired from impedance spectroscopy were determined after simulation with adequate equivalent electrical circuit, e.g., transmission line model for DSC devices [33,34]. Ionic diffusion coefficients were also determined by cyclic-voltammetry using a Pt micro-electrode (limiting current approach).
Photo-current density-voltage (J-V) characteristics of DSCs were recorded by means of a computer controlled digital source meter (Keithley combined with a Newport SOL3A solar simulator (Location) with A.M.1.5G filter. The incident light power was measured by a silicon diode reference cell calibrated at National Renewable Energy Laboratory (NREL). (J-V) characteristics were measured under illumination by changing the bias voltage from short-circuit to open-circuit conditions. The active surface was masked by a black tape with an aperture 1mm larger than the TiO2 photo-anode area (0.152 cm2). The PCE values correspond to the best reproducible values obtained. The reproducibility in the values of efficiency obtained is in the range of ca. 0.1%.

5. Synthesis

A denomination was systematically followed to provide a short name to the new carbohydrate molecules. The first letter G stands for d-glucose and M for d-mannose. It is followed by “0” when no methoxy group is present in α position of the anomeric carbon and “a” when there is. The last group represent the short name of the positively charge nucleophilic unit, e.g., MII for 1-methyl-1H-imidazol-3-ium iodide, TEA for N,N,N-triethylammonium-iodide, THT for tetrahydro-1H-thiophen-1-ium.
These new functional ionic compounds based on iodide were prepared following a common synthetic approach starting from 1 [35] (Scheme 1) or 3 [36] (Scheme 2). In the first case, iodination was realized by using PPh3/I2/Imidazole to afford 2 in 79% yield. The ionic derivatives G0(MII) and G0(TEA) were obtained respectively by treating 2 in presence of N-methylimidazole (87%) at 80 °C or triethylamine at 120 °C (71%).
For the d-mannose derivatives, 3 was permethylated with CH3I in basic conditions leading to 4 in 61% yield over two steps. Following Scheme 1, the reduction of the anomeric position to afford 5 as well as the desilvation step was realized by using triethylsilane and trimethylsilyltrifluoromethanesulfonate in 78% yield. The iodide derivative 6 was obtained in 74% yield. Finally, the ionic d-mannose derivatives M0(TEA) and M0(MII) were obtained in a similar way in 37 and 90% yield, respectively.
In order to verify the possible influence of the OMe anomeric substituent in the composition of the new electrolyte, we undertook the synthesis of the OMe anomeric d-glucose IL derivatives. Starting from 7, the iodide derivative 8 was obtained in 61% yield by using PPh3/I2/Imidazole [37]. The substitution was then realized in the presence of N-methylimidazole, triethylamine or tetrahydrothiophene leading to Ga(MII), Ga(TEA) and Ga(THT) in 91%, 80% and 6% yield, respectively.
1,6-Dideoxy-6-iodo-2,3,4-trimethoxy-d-glucopyranoside (2). To a solution of 1 (1.00 g, 4.85 mmol) in toluene (20 mL) were added PPh3 (2.55 g, 9.7 mmol), imidazole (1.65 g, 24.25 mmol) and I2 (2.46 g, 9.7 mmol) (Scheme 1). After refluxing at 80 °C overnight, the solvent was eliminated under a vacuum and the reaction mixture purified by flash chromatography (EtOAc/cyclohexane, 30/70 v/v) yielding to compound 2 (1.21 g, 79%) as a yellow syrup.
[α] D 20 = +70° (c = 1.78, CH2Cl2); IR(ATR): ν (cm−1) 2933, 2901, 2831, 1461, 1371, 1215, 1165, 1118, 1091, 983, 886; NMR 1H (CD3OD, 300 MHz): δ (ppm) 3.99 (dd, 1 H, J1a,1b = 10.7 Hz, J1a,2 = 4.6 Hz, H1a), 3.54 (s, 3 H, MeO), 3.53 (s, 3 H, MeO), 3.39 (dd, 1 H, J6a,5 = 2.9 Hz, J6a,6b = 10.7 Hz, H6a), 3.38 (s, 3 H, MeO), 3.28 (dd, 1 H, J6b,5 = 5.1, J6b,6a = 10.7, H6b), 3.21–3.00 (m, 3 H, H1b, H2, H3); NMR 13C (CD3OD, 75 MHz): δ (ppm) 87.4 (C4), 82.9 (C3), 79.9 (C5), 77.5 (C2), 67.2 (C1), 60.8 (OMe), 60.6 (OMe), 58.7 (OMe), 7.54 (C6); High Resolution Mass Spectrometry (HRMS) calculated for C9H17IO4Na: 339.0073, found 339.0069.
1,6-Dideoxy-6-(1-methyl-1H-imidazol-3-ium iodide)-2,3,4-trimethoxy-d-glucopyranoside (G0(MII)). N-methylimidazole (0.80 mL, 6.7 mmol) was added to compound 2 (2.12 g, 6.7 mmol) and the reaction mixture stirred for 24 h at 80 °C. N-methylimidazole was eliminated under a vacuum, the reaction mixture was dispersed into ethyl acetate under ultrasound and filtrated yielding to the compound coded G0(MII) (2.33 g, 87%) as a yellow powder (Scheme 1).
[α] D 20 = +15° (c = 0.12, CH2Cl2); IR(ATR): ν (cm−1) 3458 (L), 3088, 3041, 2938, 2894, 1575, 1180, 1143, 1097, 1051, 984, 743; NMR 1H (CD3OD, 300 MHz): δ (ppm) 9.74 (s, 1 H, CH=N), 7.46 (t, 1 H, JCH=CH = 1.8 Hz, CH=CH), 7.30 (t, 1 H, JCH=CH = 1.8 Hz, CH=CH), 4.58 (dd, 1 H, J6a,6b = 14.3 Hz, J6a,5 = 2.4 Hz, H6a), 4.27 (dd, 1 H, J6b,6a = 14.3 Hz, J6b,5 = 8.2 Hz, H6b), 4.12 (s, 3 H, NCH3), 4.02 (dd, 1 H, J1a,1b = 11.1 Hz, J1b,2 = 4.6 Hz, H1b), 3.57 (s, 3 H, OMe), 3.56 (s, 3 H, OMe), 3.41 (s, 3 H, OMe), 3.40 (m, 1 H, J6a,5 = 2.4 Hz, J6b,5 = 8.2 Hz, H5), 3.21 (dd, 1 H, J1b,2 = 4.6 Hz, J2,3 = 8.6 Hz, H2), 3.15 (dd, 1 H, J6a,5 = 2.4 Hz, H4), 3.06 (dd, 1H, J1a,J1b = 11.1 Hz, H1a), 2.79 (dd, 1 H, J3,2 = 8.6 Hz, H3); NMR 13C (CD3OD, 75 MHz): δ (ppm) 137.5 (N=C), 123.8 (C=C), 123.1 (C=C), 87.2 (C4), 80.1 (C3), 79.7 (C5), 77.0 (C2), 67.5 (C1), 60.9, 60.7, 58.9 (3 x OMe), 51.3 (C6), 37.5 (Me-N); MS(ESI): [M] = 126.1 m/z; HRMS calculated for C13H23N2O4: 271.1657, found 271.1658.
1,6-Dideoxy-6-(N,N,N-triethylammonium-iodide)-2,3,4-trimethoxy-d-glucopyranoside (G0(TEA)). Triethylamine (2.39 mL, 17.8 mmol) was added to compound 2 (0.51 g, 1.6 mmol) and the reaction mixture stirred overnight at 120 °C. After removal of the solvent, diethyl ether was added and the reaction mixture was sonicated for 5 min. After filtration, the retrieved solid was washed with ethyl ether to remove traces of unreacted precursor yielding to the new compound coded G0(TEA) (0.48 g, 71%) as a light yellow powder (Scheme 1).
[α] D 20 = +63° (c = 0.16, CH2Cl2); IR(ATR): ν (cm−1) 2974, 2945, 1450, 1404, 1142, 1118, 1098, 1065, 1046, 990, 888, 789; NMR 1H (CD3OD, 300 MHz): δ (ppm) 3.97 (dd, 1 H, J1a,2 = 4.4 Hz, J1a,1b = 11.3 Hz, H1a), 3.71 (dd, 1 H, J3,4 = 8.9Hz, J4,5 = 4.8 Hz, H4), 3.63, 3.61, 3.44 (s, 9 H, 3× OMe), 3.63-3.44 (m, 8 H, 3× NCH2, H6a, H6b), 3.34 (t, 1 H, J1a,1b = J1b,2 = 11.3 Hz, H1b), 3.21 (m, 2 H, H2, H3), 1.38 (t, 9 H, JCH2,CH3 = 7.2 Hz, 3× CH3); NMR 13C (CD3OD, 75 MHz): δ (ppm) 87.4 (C2), 80.2 (C3), 79.4 (C5), 73.2 (C4), 67.1 (C1), 61.3 (OMe), 60.6 (OMe), 58.7 (OMe), 58.8 (C6), 54.6 (3× NCH2), 79 (3× CH3); MS(ESI): [M] = 126.1 m/z; HRMS calculated for C15H32NO4: 290.2331, found 290.2331.
6-O-Tertbutyldimethylsilyl-1,2,3,4-tetramethoxy-α-d-mannopyranoside (4). To a solution of 3 (1.0 g, 3.24mmol) in THF (20 mL) at 0 °C was added NaH 60% (0.47 g, 19.48 mmol). After stirring for 1 h, CH3I (2.77 g, 19.48 mmol) is added to the reaction mixture and left under stirring at room temperature overnight. After careful neutralization of NaH with water, the reaction mixture was extracted twice with CH2Cl2. The organic phase was dried over Na2SO4, filtered and the solvent eliminated under reduced pressure. After flash chromatography purification (cyclohexane/ethyl acetate, 70/30, v/v), compound 4 (0.47 g, 42%) was isolated as a colorless syrup (Scheme 2).
[α] D 20 = + 49° (c = 0.94, CH2Cl2); IR(ATR): ν (cm−1) 2951, 2928, 2905, 2856, 1251, 1190, 1129, 1110, 1101, 1063, 1018, 967, 833, 775, 677; NMR 1H (CD3OD, 300 MHz): δ (ppm) 4.71 (s, 1 H, H1), 3.71 (s, 2 H, H6), 3.52 (m, 2 H, H2, H4), 3.50 (s, 3 H, OMe), 3.46 (s, 3 H, OMe), 3.43 (s, 3 H, OMe), 3.40 (m, 2 H, H3, H5), 3.33 (s, 3 H, OMe), 0.84 (s, 9 H, tBu), 0.01 (s, 6 H, SiMe2); NMR 13C (CD3OD, 75 MHz): δ (ppm) 97.5 (C1), 81.5, 77.2, 76.5, 73.2 (C2, C3, C4, C5), 62.9 (C6), 60.9 (OMe), 58.7 (OMe), 57.8 (OMe), 54.8 (OMe), 25.1 (tBu), 4.4 (2× SiMe2); HRMS calculated for C16H34O6SiNa: 373.2021, found 373.2022.
1-Deoxy-2,3,4-trimethoxy-d-mannopyranoside (5). To a solution of 4 (504 mg, 1.44 mmol) in CH3CN (6.1 mL) placed under argon atmosphere were added triethylsilane (0.68 mL, 4.3 mmol) and TMSOTf (0.76 mL, 4.3 mmol). After stirring for 17 h, 6 mL of a saturated solution of NaHCO3 was added and the reaction mixture extracted five times with 8 mL of CH2Cl2. The organic solutions were gathered, dried over Na2SO4, filtered and the solvent was eliminated under reduced pressure. After flash chromatography purification (cyclohexane/ethyl acetate, 100/0 to 0/100, v/v), compound 5 (296 mg, 78%) was isolated as a colorless syrup (Scheme 2).
[α] D 20 = −9° (c = 0.17, CH2Cl2); IR(ATR): ν (cm−1) 3463, 2934, 2833, 1194, 1132, 1090, 1031, 1007, 991, 748; NMR 1H (CD3OD, 300 MHz): δ (ppm) 4.14 (dd, 1 H, J1a,1b = 12.8 Hz, J1a,2 = 2.2 Hz, H1a), 3.84 (dd, 1 H, J6a,6b = 11.7 Hz, J6a,5 = 2.9 Hz, H6a), 3.70 (dd, 1 H, J6b,6a = 11.7 Hz, J6b,5 = 5.5 Hz, H6b), 3.61 (ddd, 1 H, J2,1a = 2.0 Hz, J2,1b = 0.7 Hz, H2), 3.53 (s, 3 H, OMe), 3.48 (s, 3 H, OMe), 3.45 (s, 3 H, OMe), 3.39 (d, 1 H, J4,5 = 9.4 Hz, H4), 3.30 (dd, 1 H, J1b,1a = 12.8 Hz, J1b,2 = 1.0 Hz, H1b), 3.25 (dd, 1 H, J3,4 = 9.3 Hz, J4,2 = 3.3 Hz, H3), 3.16 (ddd, 1 H, J5,4 = 9.4 Hz, J5,6b = 5.5 Hz, J5,6a = 2.9 Hz, H5); NMR 13C (CD3OD, 75 MHz): δ (ppm) 84.6 (C5), 80.2, 77.0, 75.5 (C2, C3, C4), 66.0 (C6), 62.6 (C1), 61,0 (OMe), 57.6 (OMe), 57.4 (OMe); HRMS calculated for C9H18O5Na: 229.1042, found 229.1052.
1,6-Dideoxy-2,3,4-trimethoxy-d-mannopyranoside (6). Compound 5 (1.48 g, 7.2 mmol) was dissolved in toluene (30 mL). We successively added triphenylphosphine (3.32 g, 14.4 mmol), imidazole (2.16 g, 35.9 mmol) and iodine (3.19 g, 14.4 mmol). The mixture was stirred at 80 °C overnight. Solvent was eliminated under a vacuum and the reaction mixture purified by flash chromatography (EtOAc/cyclohexane, 40/60 v/v) yielding to compound 6 (1.70 g, 74%) as a yellow powder (Scheme 2).
[α] D 20 = −9° (c = 0.16, CH2Cl2); IR(ATR): ν (cm−1) 2925, 1203, 1151, 1130, 1114, 1100, 1069, 1006, 946, 748; NMR 1H (CD3OD, 300 MHz): δ (ppm) 4.21 (dd, 1 H, J1a,1b = 12.9 Hz, J1a,2 = 2.3 Hz, H1a), 3.62 (m, 1 H, H2), 3.59 (s, 3 H, OMe), 3.54 (dd, 1 H, J6a,6b = 16.6 Hz, J6a,5 = 2.6 Hz, H6a), 3.49 (s, 3H, OMe), 3.46 (s, 3 H, OMe), 3.37–3.21 (m, 4 H, H6b, H1b, H4, H3), 3.01 (m, 1H, H5); NMR 13C (CD3OD, 75 MHz): δ (ppm) 84.3 (C3), 80.4 (C4), 79.4 (C5), 75.3 (C2), 65.9 (C1), 61.4 (OMe), 57.4 (2× OMe), 6.8 (C6); HRMS calculated for C9H17IO4Na: 339.0069, found 339.0069.
1,6-Dideoxy-6-(N,N,N-triethylammonium-iodide)-2,3,4-trimethoxy-d-mannopyranoside (M0(TEA)). Triethylamine (8.86 mL, 63.2 mmol) was added to compound 6 (1 g, 3.16 mmol) and the reaction mixture was stirred for four days at 120 °C. After solvent removal, diethyl ether was added and the reaction mixture sonicated for 5 min. After filtration, the solid retrieved was washed using ethyl ether to remove traces of unreacted precursors yielding to M0(TEA) (488 mg, 37%) as a brown powder (Scheme 2).
[α] D 20 = −24° (c = 0.09, CH2Cl2); IR(ATR): ν (cm−1) 2975, 2902, 1107, 1084; NMR 1H (CD3OD, 300 MHz): δ (ppm) 4.08–3.95 (m, 3 H, H1a, H1b, H2), 3.68–3.09 (m, 10 H, H3, H4, H5, H6a, H6b, 3× NCH2), 3.54 (s, 1 H, OMe), 3.43 (s, 1 H, OMe), 3.40 (s, 1 H, OMe), 1.32 (t, 3× 3H, JNCH2-NCH3 = 7.2 Hz, NCH3); NMR 13C (CD3OD, 75 MHz): δ (ppm) 84.1 77.0, 74.8, (C2, C3, C4), 72.6 (C5), 66.1 (C1), 61.2, 57.7, 57.0 (3× OMe), 54.6 (NCH2), 46.6 (C6), 7.9 (NCH3); MS(ESI): [M] = 126.1 m/z; HRMS calculated for C15H32NO4: 290.2319, found 290.2331.
1,6-Dideoxy-6-(1-methyl-1H-imidazol-3-ium iodide)-2,3,4-trimethoxy-α-d-mannopyranoside (M0(MII)). N-Methylimidazole (0.07 mL, 0.87 mmol) was added to compound 6 (0.20 g, 0.58 mmol) and the reaction mixture stirred for 24 h at 80 °C. N-methylimidazole was eliminated under a vacuum. The reaction mixture was dispersed into ethyl acetate in ultrasonic bath. The product retrieved yields to M0(MII) (207 mg, 90%) as a slight yellow syrup (Scheme 2).
[α] D 20 = −26° (c = 0.32, CH2Cl2); IR(ATR): ν (cm−1) 3458, 3088, 3041, 2938, 2894, 1575, 1180, 1143, 1097, 1051, 984, 743; NMR 1H (CDCl3, 300 MHz): δ (ppm) 9.45 (s, 1 H, CH=N), 7.57, 7.37 (s, 2 H, 2× CH=CH), 4.50 (dd, 1 H, J6a,6b = 14.2 Hz, J6a,5 = 1.7 Hz, H6a), 4.16 (dd, 1 H, J6b,6a = 14.2 Hz, J6b,5 = 9.2 Hz, H6b), 4.03 (m, 4 H, H1a, NCH3), 3.47 (m, 2 H, H2, H3), 3.43, 3.33, 3.30 (s, 9 H, 3× OCH3), 3.29 (m, 1 H, H1b), 3.24 (dd, 1 H, J3,4 = 3.1 Hz, J4,5= 9.1 Hz, H4), 3.05(t, 1 H, J5,6b= J4,5= 9.2 Hz, H5); NMR 13C (CDCl3, 75 MHz): δ (ppm) 136.9 (N=C), 123.6 (C=C), 123.2 (C=C), 83.6 (C4), 76.8, 76.7 (C3, C5), 74.4 (C2), 65.8 (C1), 60.9, 57.4, 56.9 (3× OMe), 51.1 (C6), 37.2 (Me-N); MS(ESI): [M] = 126.1 m/z; HRMS calculated for C13H23N2O4: 271.1657, found 271.1658.
6-Deoxy-1,2,3,4-tetramethoxy-α-d-glucopyranoside (8). Compound 7 (9.89 g, 41.9 mmol) was dissolved in toluene (200 mL). After addition of triphenylphosphine (22.2 g, 83.8 mmol), imidazole (14.3 g, 83.8 mmol) and iodine (21.3 g, 83.8 mmol), the mixture was stirred overnight at 80 °C. Solvent was eliminated under a vacuum and the reaction mixture purified by flash chromatography (EtOAc/cyclohexane, 30/70 v/v) yielding to compound 8 (14.5 g, 83%) as a yellow syrup (Scheme 3).
[α] D 20 = +115.9° (c = 2.1, CH2Cl2); IR(ATR): ν (cm−1) 2984, 2931, 2907, 2832, 1465, 1444, 1412, 1374, 1327, 1270, 1186, 1162, 1093, 1084, 978; NMR 1H (CDCl3, 300 MHz): δ (ppm) 4.79 (d, 1 H, J1,2 = 3.6 Hz, H1), 3.58, 3.57, 3.48, 3.34 (s, 12 H, 4× OMe), 3.47 (m, 2 H, H3, H6a), 3.34–3.27 (m, 2 H, H5, H6b), 3.17 (d, 1 H, J2,3 = 9.6 Hz, H2), 2.93 (t, 1 H, J3,4 = J4,5 = 9.0 Hz, H4); NMR 13C (CDCl3, 75 MHz): δ (ppm) 97.4 (C1), 83.3, 83.0, 81.7 (C2, C3, C4), 69.2 (C5), 60.9 (OMe), 60.8 (OMe), 59.0 (OMe), 55.4 (OMe), 7.5 (C6); HRMS calculated for C10H19IO5Na: 369.0170, found 369.0175.
6-Deoxy-6-(1-methyl-1H-imidazol-3-ium-iodide)-1,2,3,4-tetramethoxy-α-d-glucopyranoside (Ga(MII)). N-Methylimidazole (0.26 mL, 2.3 mmol) was added to compound 8 (1.02 g, 2.9 mmol) and the reaction mixture stirred for 24 h at 80 °C under argon atmosphere. N-methylimidazole was eliminated under a vacuum. Dichloromethane was added to dissolve the reaction mixture and celite was added. After drying under a vacuum, the crude was incorporated into a celite pad and eluted consecutively with a mixture of ethyl acetate and methanol (100/0 to 90/10). The celite was eluted with ethylic ether and dichloromethane. The dichloromethane phase was retrieved and washed a second time with ethyl acetate and dichloromethane, dichloromethane phase was kept and the solvent eliminated under reduced pressure yielding to the compound Ga(MII) (925 mg, 91%) as a viscous yellow syrup (Scheme 3).
[α] D 20 = +63° (c = 0.16, CH2Cl2); IR(ATR): ν (cm−1) 3448, 3073, 2939, 2834, 1161, 1094, 1051, 987, 732; NMR 1H (CD3OD, 300 MHz): δ (ppm) 9.68 (s, 1 H, N=C), 7.66 (t, 1 H, CH=CH), 7.36 (t, 1 H, CH=CH), 4.78 (dd, 1 H, J1,2 = 3.6 Hz, H1), 4.54 (dd, 1 H, J6a,6b = 14.2 Hz, J6a,5 = 2.6 Hz, H6a), 4.38 (dd, 1 H, J6a,6b = 14.2 Hz, J6b,5 = 7.1 Hz, H6b), 4.11 (s, 3 H, NCH3), 3.70 (ddd, 1 H, J6a,5 = 2.6 Hz, J6b,5 = 7.1 Hz, J5,4 = 9.4 Hz, H5), 3.52 (s, 3 H, OMe), 3.50 (s, 3 H, 3 H, OMe), 3.47–3.35 (m, 1 H, H3), 3.42 (s, 3 H, OMe), 3.19 s, 3 H, OMe), 3.11 (dd, 1 H, J1,2 = 3.6 Hz, H2), 2.74 (dd, 1 H, J5,4 = 9.8 Hz, H4); NMR 13C (CD3OD, 75 MHz): δ (ppm) 137.7 (N=C), 124.0, 122.9 (CH=CH, CH=CH), 97.6 (C1), 82.9 (C3), 81.4 (C2), 79.7 (C4), 68.5 (C5), 60.5 (2× OMe), 59.0 (OMe), 55.9 (OMe), 50.8 (C6), 37.5 (NCH3); MS(ESI): [M] = 126.1 m/z; HRMS calculated for C14H25N2O5: 301.1760, found 301.1763.
6-Deoxy-6-(N,N,N-triethylammonium-iodide)-1,2,3,4-tetramethoxy-α-d-glucopyranoside (Ga(TEA)). Triethylamine (24.28 mL, 173.4 mmol) was added to compound 8 (3 g, 8.67 mmol) and the reaction mixture stirred for four days at 120 °C. After removing the solvent, diethyl ether was added and the reaction mixture sonicated for 5 min. After filtration, the solid was washed with ethyl ether to remove traces of unreacted starting material yielding to Ga(TEA) (3.10 g, 80%) as a light yellow powder (Scheme 3).
[α] D 20 = +120° (c = 0.16, CH2Cl2); IR(ATR): ν (cm−1) 2924, 2834, 1465, 1445, 1163, 1095, 1068, 1058, 1040, 1026, 996, 909, 743; NMR 1H (CD3OD, 300 MHz): δ (ppm) 4.72 (m, 1 H, H2), 3.79 (m, 1 H, H5), 3.75–3.27 (m, 18 H, 4× OCH3, H6a, H6b, H3, 3× NCH2), 3.13 (m, 1 H, H2), 2.95 (m, 1 H, H4), 1.35 (m, 9 H, NCH3); NMR 13C (CD3OD, 75 MHz): δ (ppm) 98.5 (C1), 83.0 (C3), 80.9 (C2), 80.2 (C4), 65.7 (C5), 61.4 (OMe), 60.7 (OMe), 59.3 (OMe), 58.8 (C6), 57.7 (OMe), 54.7 (3× NCH2), 8.1 (3× NCH3); MS(ESI): [M] = 126.1 m/z; HRMS calculated for C16H34NO5: 320.2432, found 320.2437.
6-Deoxy-6-(tetrahydro-1H-thiophen-1-ium-iodide)-1,2,3,4-trimethoxy-α-d-glucopyranoside (Ga(THT)). Triethylamine (15.29 mL, 173.4 mmol) was added to compound 8 (3 g, 8.67 mmol) and the reaction mixture stirred for four days at 120 °C. After removing the solvent, diethyl ether was added and the reaction mixture sonicated for 5 min. After filtration, the solid was washed with ethyl ether to remove traces of unreacted precursors yielding to Ga(THT) (0.200 g, 6%) as a beige powder (Scheme 3).
[α] D 20 = +87° (c = 0.140, CH2Cl2); IR(ATR): ν (cm−1) 2910.8, 2836.2, 1158.3, 1093.2, 1066.3, 1945.6, 1018.1, 988.5, 967.8; NMR 1H (CD3OD, 300 MHz): δ (ppm) 4.77 (d, 1 H, J1,2 = 3.5 Hz), H1), 4.06-3.67 (m, 7 H, H5, H6a, H6b, 2× CH2), 3.62-3.37 (m, 2 H, H3, H4), 3.59 (s, 3 H, OMe), 3.55 (s, 3 H, OMe), 3.47 (s, 3 H, OMe), 3.43 (s, 3 H, OMe), 3.22-3.05 (m, 1 H, H2), 2.71–1.56 (m, 4 H, 2× CH2S); NMR 13C (CD3OD, 75 MHz): δ (ppm) 98.2 (C1), 82.9, 81.9, 81.5 (C2, C3, C4), 67.5 (C5), 61.1 (OMe), 60.9 (OMe), 59.4 (OMe), 56.5 (OMe), 46.3 (CH2), 46.2 (CH2), 44.8 (C6), 29.4 5 (CH2S), 29.3 (CH2S); MS(ESI): [M] = 126.1 m/z; HRMS calculated for C14H27SO5: 307.1579, found 307.1588.

Acknowledgments

The authors wish to thank Vittoria Novelli for fruitful discussions on EIS measurements and their interpretation, and Matthieu Courty for TGA and calorimetric analysis. We also acknowledge the Conseil Régional de Picardie and FEDER for their financial support of ROBUST and CONCERTO research programs.

Author Contributions

GH and ANVH performed the synthesis. IS and GH carried out the cell assembly and measurements. GH and FS performed the electrochemical measurements. ANVH and FS supervised the work.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Green, M.A. Third Generation Photovoltaics: Advanced Solar Energy Conversion; Springer: Berlin, Germany, 2006; Volume 12. [Google Scholar]
  2. Lewis, N.S. Toward cost-effective solar energy use. Science 2007, 315, 798–801. [Google Scholar] [CrossRef] [PubMed]
  3. Schiermeier, Q.; Tollefson, J.; Scully, T.; Witze, A.; Morton, O. Energy alternatives: Electricity without carbon. Nat. News 2008, 454, 816–823. [Google Scholar] [CrossRef] [PubMed]
  4. World Energy Outlook; International Energy Agency: Paris, France, 2013.
  5. Grätzel, M. Solar energy conversion by dye-sensitized photovoltaic cells. Inorg. Chem. 2005, 44, 6841–6851. [Google Scholar] [CrossRef] [PubMed]
  6. O’Regan, B.; Grätzel, M. A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films. Nature 1991, 353, 737–740. [Google Scholar] [CrossRef]
  7. Nazeeruddin, M.K.; Kay, A.; Rodicio, I.; Humphry-Baker, R.; Müller, E.; Liska, P.; Vlachopoulos, N.; Grätzel, M. Conversion of light to electricity by cis-X2bis (2,2′-bipyridyl-4, 4′-dicarboxylate)ruthenium(II) charge-transfer sensitizers (X = Cl, Br, I, CN, and SCN) on nanocrystalline titanium dioxide electrodes. J. Am. Chem. Soc. 1993, 115, 6382–6390. [Google Scholar] [CrossRef]
  8. Kakiage, K.; Aoyama, Y.; Yano, T.; Oya, K.; Fujisawa, J.; Hanaya, M. Highly-efficient dye-sensitized solar cells with collaborative sensitization by silyl-anchor and carboxy-anchor dyes. Chem. Commun. 2015, 51, 15894–15897. [Google Scholar] [CrossRef] [PubMed]
  9. Sauvage, F.; Chhor, S.; Marchioro, A.; Moser, J.-E.; Graetzel, M. Butyronitrile-based electrolyte for dye-sensitized solar cells. J. Am. Chem. Soc. 2011, 133, 13103–13109. [Google Scholar] [CrossRef] [PubMed]
  10. Yu, Q.; Zhou, D.; Shi, Y.; Si, X.; Wang, Y.; Wang, P. Stable and efficient dye-sensitized solar cells: Photophysical and electrical characterizations. Energy Environ. Sci. 2010, 3, 1722–1725. [Google Scholar] [CrossRef]
  11. Marszalek, M.; Arendse, F.D.; Decoppet, J.-D.; Babkair, S.S.; Ansari, A.A.; Habib, S.S.; Wang, M.; Zakeeruddin, S.M.; Grätzel, M. Ionic Liquid-Sulfolane Composite Electrolytes for High-Performance and Stable Dye-Sensitized Solar Cells. Adv. Energy Mater. 2014, 4, 1301235–1301242. [Google Scholar] [CrossRef]
  12. Stergiopoulos, T.; Kontos, A.G.; Jiang, N.; Milliken, D.; Desilvestro, H.; Likodimos, V.; Falaras, P. High boiling point solvent-based dye solar cells pass a harsh thermal ageing test. Sol. Energy Mater. Sol. Cells 2016, 144, 457–466. [Google Scholar] [CrossRef]
  13. Zakeeruddin, S.M.; Graetzel, M. Solvent-Free Ionic Liquid Electrolytes for Mesoscopic Dye-Sensitized Solar Cells. Adv. Funct. Mater. 2009, 19, 2187–2202. [Google Scholar] [CrossRef]
  14. Lee, C.-P.; Chen, P.-Y.; Ho, K.-C. Ionic Liquid Based Electrolytes for Dye-Sensitized Solar Cells, Ionic Liquids: Theory, Properties, New Approaches; InTech: Rijeka, Croatia, 2011. [Google Scholar]
  15. Wyss, P.; Moehl, T.; Zakeeruddin, S.M.; Grätzel, M. Influence of cations of the electrolyte on the performance and stability of dye sensitized solar cells. J. Mater. Chem. 2012, 22, 24424–24429. [Google Scholar] [CrossRef]
  16. Strappaveccia, G.; Ismalaj, E.; Petrucci, C.; Lanari, D.; Marrocchi, A.; Drees, M.; Facchetti, A.; Vaccaro, L. A biomass-derived safe medium to replace toxic dipolar solvents and access cleaner Heck coupling reactions. Green Chem. 2015, 17, 365–372. [Google Scholar] [CrossRef]
  17. Ghavre, M.; Byrne, O.; Altes, L.; Surolia, P.K.; Spulak, M.; Quilty, B.; Thampi, K.R.; Gathergood, N. Low toxicity functionalised imidazolium salts for task specific ionic liquid electrolytes in dye-sensitised solar cells: a step towards less hazardous energy production. Green Chem. 2014, 16, 2252–2265. [Google Scholar] [CrossRef]
  18. Kuang, D.; Klein, C.; Ito, S.; Moser, J.-E.; Humphry-Baker, R.; Evans, N.; Duriaux, F.; Graetzel, C.; Zakeeruddin, S.M.; Grätzel, M. High-Efficiency and Stable Mesoscopic Dye-Sensitized Solar Cells Based on a High Molar Extinction Coefficient Ruthenium Sensitizer and Nonvolatile Electrolyte. Adv. Mater. 2007, 19, 1133–1137. [Google Scholar] [CrossRef]
  19. Wilkes, J.S. A short history of ionic liquids—From molten salts to neoteric solvents. Green Chem. 2002, 4, 73–80. [Google Scholar] [CrossRef]
  20. Mudring, A.-V. Solidification of ionic liquids: Theory and techniques. Aust. J. Chem. 2010, 63, 544–564. [Google Scholar] [CrossRef]
  21. Wu, J.; Lan, Z.; Lin, J.; Huang, M.; Huang, Y.; Fan, L.; Luo, G. Electrolytes in Dye-Sensitized Solar Cells. Chem. Rev. 2015, 115, 2136–2173. [Google Scholar] [CrossRef] [PubMed]
  22. Ue, M.; Ida, K.; Mori, S. Electrochemical Properties of Organic Liquid Electrolytes Based on Quaternary Onium Salts for Electrical Double-Layer Capacitors. J. Electrochem. Soc. 1994, 141, 2989–2996. [Google Scholar] [CrossRef]
  23. Kambe, S.; Nakade, S.; Kitamura, T.; Wada, Y.; Yanagida, S. Influence of the electrolytes on electron transport in mesoporous TiO2-electrolyte systems. J. Phys. Chem. B 2002, 106, 2967–2972. [Google Scholar] [CrossRef]
  24. Son, K.M.; Kang, M.G.; Vittal, R.; Lee, J.; Kim, K.-J. Effects of substituents of imidazolium cations on the performance of dye-sensitized TiO2 solar cells. J. Appl. Electrochem. 2008, 38, 1647–1652. [Google Scholar] [CrossRef]
  25. Wang, M.; Chen, P.; Humphry-Baker, R.; Zakeeruddin, S.M.; Grätzel, M. The Influence of Charge Transport and Recombination on the Performance of Dye-Sensitized Solar Cells. ChemPhysChem 2009, 10, 290–299. [Google Scholar] [CrossRef] [PubMed]
  26. Flasque, M.; Van Nhien, A.N.; Swiatowska, J.; Seyeux, A.; Davoisne, C.; Sauvage, F. Interface Stability of a TiO2/3-Methoxypropionitrile-Based Electrolyte: First Evidence for Solid Electrolyte Interphase Formation and Implications. ChemPhysChem 2014, 15, 1126–1137. [Google Scholar] [CrossRef] [PubMed]
  27. Cao, Y.; Bai, Y.; Yu, Q.; Cheng, Y.; Liu, S.; Shi, D.; Gao, F.; Wang, P. Dye-sensitized solar cells with a high absorptivity ruthenium sensitizer featuring a 2-(hexylthio) thiophene conjugated bipyridine. J. Phys. Chem. C 2009, 113, 6290–6297. [Google Scholar] [CrossRef]
  28. Peter, L.M. Dye-sensitized nanocrystalline solar cells. Phys. Chem. Chem. Phys. 2007, 9, 2630–2642. [Google Scholar] [CrossRef] [PubMed]
  29. O’Regan, B.; Durrant, J.R.; Sommeling, P.M.; Bakker, N.J. Influence of the TiCl4 treatment on nanocrystalline TiO2 films in dye-sensitized solar cells. 2. Charge density, band edge shifts, and quantification of recombination losses at short circuit. J. Phys. Chem. C 2007, 111, 14001–14010. [Google Scholar]
  30. Bisquert, J.; Fabregat-Santiago, F.; Mora-Seró, I.; Garcia-Belmonte, G.; Giménez, S. Electron lifetime in dye-sensitized solar cells: Theory and interpretation of measurements. J. Phys. Chem. C 2009, 113, 17278–17290. [Google Scholar] [CrossRef]
  31. Ito, S.; Murakami, T.N.; Comte, P.; Liska, P.; Grätzel, C.; Nazeeruddin, M.K.; Grätzel, M. Fabrication of thin film dye sensitized solar cells with solar to electric power conversion efficiency over 10%. Thin Solid Films 2008, 516, 4613–4619. [Google Scholar] [CrossRef]
  32. Hauch, A.; Georg, A. Diffusion in the electrolyte and charge-transfer reaction at the platinum electrode in dye-sensitized solar cells. Electrochim. Acta 2001, 46, 3457–3466. [Google Scholar] [CrossRef]
  33. Fabregat-Santiago, F.; Bisquert, J.; Garcia-Belmonte, G.; Boschloo, G.; Hagfeldt, A. Influence of electrolyte in transport and recombination in dye-sensitized solar cells studied by impedance spectroscopy. Sol. Energy Mater. Sol. Cells 2005, 87, 117–131. [Google Scholar]
  34. Fabregat-Santiago, F.; Bisquert, J. Dye-Sensitized Solar Cells; EPFL Press: Lausanne, Switzerland, 2010. [Google Scholar]
  35. Poletti, L.; Chiappe, C.; Lay, L.; Pieraccini, D.; Polito, L.; Russo, G. Glucose-derived ionic liquids: Exploring low-cost sources for novel chiral solvents. Green Chem. 2007, 9, 337–341. [Google Scholar] [CrossRef]
  36. El-Badri, M.H.; Willenbring, D.; Tantillo, D.J.; Gervay-Hague, J. Mechanistic studies on the stereoselective formation of β-mannosides from mannosyl iodides using α-deuterium kinetic isotope effects. J. Org. Chem. 2007, 72, 4663–4672. [Google Scholar] [CrossRef] [PubMed]
  37. Boultadakis-Arapinis, M.; Prost, E.; Gandon, V.; Lemoine, P.; Turcaud, S.; Micouin, L.; Lecourt, T. Carbene-Mediated Functionalization of the Anomeric C-H Bond of Carbohydrates: Scope and Limitations. Chem. Eur. J. 2013, 19, 6052–6066. [Google Scholar] [CrossRef] [PubMed]
Figure 1. Evolution of tri-iodide diffusion coefficient (a), charge transfer resistance at counter electrode (CE) (b) and cell ohmic drop (c) as a function of ageing time at 60 °C under 100 mW/cm2 light illumination for new iodide-based carbohydrates and compared to the standard DMII.
Figure 1. Evolution of tri-iodide diffusion coefficient (a), charge transfer resistance at counter electrode (CE) (b) and cell ohmic drop (c) as a function of ageing time at 60 °C under 100 mW/cm2 light illumination for new iodide-based carbohydrates and compared to the standard DMII.
Energies 09 00241 g001
Figure 2. Evolution of photovoltage (a), photocurrent (b), fill factor (c) and power conversion efficiency (PCE) (d) as a function of ageing time at 60 °C under 100 mW/cm2 light illumination without any UV cut-off filters for new iodide-based carbohydrates and compared to the standard DMII.
Figure 2. Evolution of photovoltage (a), photocurrent (b), fill factor (c) and power conversion efficiency (PCE) (d) as a function of ageing time at 60 °C under 100 mW/cm2 light illumination without any UV cut-off filters for new iodide-based carbohydrates and compared to the standard DMII.
Energies 09 00241 g002
Figure 3. (J-V) characteristics comparison of DSCs with Ga(MII), G0(MII) and DMII electrolytes under standard A.M.1.5G illumination.
Figure 3. (J-V) characteristics comparison of DSCs with Ga(MII), G0(MII) and DMII electrolytes under standard A.M.1.5G illumination.
Energies 09 00241 g003
Figure 4. Evolution of trap states distribution; (a) electron lifetime and transport time as a function of applied voltage or density of states (DOS) for the different iodide-based carbohydrates and compared to the standard DMII (b).
Figure 4. Evolution of trap states distribution; (a) electron lifetime and transport time as a function of applied voltage or density of states (DOS) for the different iodide-based carbohydrates and compared to the standard DMII (b).
Energies 09 00241 g004
Scheme 1. Synthesis of new deoxy anomeric d-glucose derivatives G0(MII) and G0(TEA).
Scheme 1. Synthesis of new deoxy anomeric d-glucose derivatives G0(MII) and G0(TEA).
Energies 09 00241 g005
Scheme 2. Synthesis of new deoxy anomeric d-mannose derivatives M0(MII) and M0(TEA).
Scheme 2. Synthesis of new deoxy anomeric d-mannose derivatives M0(MII) and M0(TEA).
Energies 09 00241 g006
Scheme 3. Synthesis of new deoxy anomeric d-glucose derivatives Ga(MII), Ga(TEA) and Ga(THT).
Scheme 3. Synthesis of new deoxy anomeric d-glucose derivatives Ga(MII), Ga(TEA) and Ga(THT).
Energies 09 00241 g007
Table 1. Values for melting temperature of the new iodide-based carbohydrates and evolution of viscosity, conductivity, I3 and I diffusion coefficient, charge transfer resistance (Rct) and ohmic drop in related 3-methoxypropionitrile (MPN)-based electrolyte. Note viscosity, conductivity and cyclic voltamperometry (CV) could not get measured for Ga(THT) owing to the low synthetic yield rendering it difficult to produce enough volume of electrolyte for these analyses (ca. 5 mL).
Table 1. Values for melting temperature of the new iodide-based carbohydrates and evolution of viscosity, conductivity, I3 and I diffusion coefficient, charge transfer resistance (Rct) and ohmic drop in related 3-methoxypropionitrile (MPN)-based electrolyte. Note viscosity, conductivity and cyclic voltamperometry (CV) could not get measured for Ga(THT) owing to the low synthetic yield rendering it difficult to produce enough volume of electrolyte for these analyses (ca. 5 mL).
MoleculeMelting Point (°C)Viscosity at 25 °C (cP)Conductivity (S/cm)I3 Diffusion Coefficient (cm2/s)I Diffusion Coefficient (cm2/s)Rct (Ω·cm2)
CVEIS
DMII
Energies 09 00241 i001
93.62.17.1 × 10−33.3 × 10−41.6 × 10−59.4 × 10−41.70
M0(MII)
Energies 09 00241 i002
Liquid3.85.0 × 10−31.2 × 10−49.1 × 10−63.3 × 10−48.80
M0(TEA)
Energies 09 00241 i003
1403.32.3 × 10−31.3 × 10−41.2 × 10−59.4 × 10−48.30
Ga(MII)
Energies 09 00241 i004
Liquid2.63.5 × 10−31.6 × 10−49.3 × 10−66.0 × 10−43.80
G0(MII)
Energies 09 00241 i005
1343.23.5 × 10−31.4 × 10−49.7 × 10−67.1 × 10−46.30
Ga(THT)
Energies 09 00241 i006
136---8.1 × 10−6-2.90
Ga(TEA)
Energies 09 00241 i007
1183.54.1 × 10−31.2 × 10−46.6 × 10−67.9 × 10−45.50
G0(TEA)
Energies 09 00241 i008
1383.23.1 × 10−31.5 × 10−41.2 × 10−58.8 × 10−48.30
Table 2. Current-Voltage (J-V) characteristics for C106-sensitized solar cells with the sugar-based electrolytes.
Table 2. Current-Voltage (J-V) characteristics for C106-sensitized solar cells with the sugar-based electrolytes.
CharacteristicGa(MII)G0(MII)M0(TEA)M0(MII)Ga(TEA)G0(TEA)Ga(THT)DMII
Voc (V)0.6960.6980.6560.7010.6800.6500.5810.680
Jsc (mA/cm2)16.217.516.616.916.517.116.116.9
ff (%)64.760.063.056.157.752.153.269.3
η (%)7.37.36.96.76.55.85.08.0

Share and Cite

MDPI and ACS Style

Sagaidak, I.; Huertas, G.; Nguyen Van Nhien, A.; Sauvage, F. Towards Renewable Iodide Sources for Electrolytes in Dye-Sensitized Solar Cells. Energies 2016, 9, 241. https://doi.org/10.3390/en9040241

AMA Style

Sagaidak I, Huertas G, Nguyen Van Nhien A, Sauvage F. Towards Renewable Iodide Sources for Electrolytes in Dye-Sensitized Solar Cells. Energies. 2016; 9(4):241. https://doi.org/10.3390/en9040241

Chicago/Turabian Style

Sagaidak, Iryna, Guillaume Huertas, Albert Nguyen Van Nhien, and Frédéric Sauvage. 2016. "Towards Renewable Iodide Sources for Electrolytes in Dye-Sensitized Solar Cells" Energies 9, no. 4: 241. https://doi.org/10.3390/en9040241

APA Style

Sagaidak, I., Huertas, G., Nguyen Van Nhien, A., & Sauvage, F. (2016). Towards Renewable Iodide Sources for Electrolytes in Dye-Sensitized Solar Cells. Energies, 9(4), 241. https://doi.org/10.3390/en9040241

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop