Next Article in Journal
A Superficial Intramolecular Alignment of Carbon Nitride through Conjugated Monomer for Optimized Photocatalytic CO2 Reduction
Next Article in Special Issue
Technology Advances in Phenol Removals: Current Progress and Future Perspectives
Previous Article in Journal
MW-Promoted Cu(I)-Catalyzed P–C Coupling Reactions without the Addition of Conventional Ligands; an Experimental and a Theoretical Study
Previous Article in Special Issue
Solvent-Free Synthesis of SAPO-34 Zeolite with Tunable SiO2/Al2O3 Ratios for Efficient Catalytic Cracking of 1-Butene
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Catalysts
Volume 11
Issue 8
10.3390/catal11080934
catalysts-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

ZnCDs/ZnO@ZIF-8 Zeolite Composites for the Photocatalytic Degradation of Tetracycline

by
Yong Cheng
*,
Xiuxiu Wang
,
Yu Mei
,
Dan Wang
and
Changchun Ji
The Key Laboratory of Functional Molecular Solids, Ministry of Education, Anhui Laboratory of Molecule-Based Materials (State Key Laboratory Cultivation Base), College of Chemistry and Materials Science, Anhui Normal University, Wuhu 241002, China
*
Author to whom correspondence should be addressed.
Catalysts 2021, 11(8), 934; https://doi.org/10.3390/catal11080934
Submission received: 13 May 2021 / Revised: 12 July 2021 / Accepted: 20 July 2021 / Published: 30 July 2021
(This article belongs to the Special Issue Advances in Zeolite Catalysts)
Browse Figures
Versions Notes

Abstract

:
Considering the photocatalytic performance of CDs, ZnO, and the unique porous nanostructure and stability of ZIF-8, we prepared ZnCDs/ZnO@ZIF-8 zeolite composites. The resultant material represented an enhanced ability for the photodegradation of TC compared with that of ZnCDs and ZnO. The photocatalytic degradation efficiency reached over 85%. The catalytic activity of the composites was maintained after four cycles. The experimental result indicated that ⋅O2 radical was the active species in the reaction.

Graphical Abstract

1. Introduction

Tetracycline (TC) is widely used as a broad-spectrum antibiotic for treating a wide range of diseases, such as mycoplasmal pneumonia, hydatoncus, and the diagnosis of malignant tumor epidemic typhus [1,2]. However, as with other antibiotics, tetracycline can be only partially metabolized or absorbed by humans and animals and its residue ends up in wastewater [3]. Tetracycline residue in hydrosphere inevitably brings underlying hazard to human health. Consequently, the removal of TC from aqueous solutions is a crucial and significant goal. So far, researchers have explored various methods such as adsorption [4], biodegradation [5,6], and electrochemical [7] to combat pollution by antibiotics. However, most methods have been restricted owing to lack of efficiency, costliness, or sophisticated instrumentation. Photocatalytic technology has gained attention for the degradation of TC owing to its high efficiency, low cost, and environmentally friendly properties [8,9,10].
MOF-based composites have attracted much attention in recent years for their potential uses in adsorption [11], photocatalysis [12,13], fluorescence sensing [14], etc. Among of them, zeolitic imidazolate framework (ZIF-8), which is comprised of zinc and 2-methyl imidazole (2-mIm), is considered a highly appropriate host matrix to form composites owing to its exceptional chemical and thermal stability and relatively large cavities (11.6~3.8 Å) [15,16]. Various materials have been successfully combined with ZIF-8 and have acquired a synergistic effect [17,18,19,20]. For example, ZnO is a semiconductor and has been widely used as a photocatalyst, but it remains challenging to capture the target molecules for enhanced photocatalysis. It has been found that higher photocatalytic ability and photochemical activities were achieved as ZnO hybridized with ZIF-8 [21,22,23]. Nevertheless, the charge conductivity of ZnO@ZIF-8 is still unsatisfactory, which limits the improvement of photocatalytic capacity further.
Carbon dots (CDs)-based materials have been studied as a new generation of photocatalytic composites owing to the tunable photoluminescence and high efficiency light capturing capability [24,25,26]. For example, CDs@TiO2 absorbs more visible light compared to bare TiO2, which helps to increase the catalytic efficiency [27]. CDs@ZnO produced a newly formed conduction band, which contributes to an increased level of electron migration to the valence band and thereby enhances their photocatalytic activity [28,29]. It is proposed that CDs can modulate the band structure of semiconductors and improve the optical properties and impart novel functionalities to the as-synthesized composites. So, it is anticipated that higher photocatalysis should be achieved by incorporating CDs into ZnO@ZIF-8.
Herein, we prepared a ZnCDs/ZnO@ZIF-8 zeolite composite, in which ZnCDs/ZnO heterojunction was encapsulated by ZIF-8 crystal and formed a core–shell structure. It indicated that the resulting hybrid material exhibits excellent photocatalytic performance for the degradation of tetracycline. The photocatalytic efficiency reached over 85% after four cycles. The possible reaction mechanism was investigated using the radical scavenger technique. It is hoped that this work could pave the way for developing more photocatalytic zeolite composites.

2. Results and Discussion

2.1. Synthesis of ZnCDs/ZnO@ZIF-8

The synthesis procedure of ZnCDs/ZnO@ZIF-8 composites is shown in Scheme 1. The mixture of zinc nitrate hexahydrate, folic acid, and DMF was heated at 190 °C, and then cooled down. The product was separated into two parts: the solution was dialyzed and dried to obtain ZnCDs; the residual precipitate was calcined to form ZnO nanosphere, which was used as template for the preparation of ZnCDs/ZnO heterostructures. Finally, 2-methylimidazole was coordinated with zinc ions in the suspension of ZnCDs/ZnO to form the ZIF-8 crystal, which wrapped around ZnCDs/ZnO heterojunction nanosphere.

2.2. Characterization of ZnCDs/ZnO@ZIF-8

SEM imaging indicates that the morphology of ZnCDs/ZnO heterojunction was spherical in shape with a uniform size about 500 nm (Figure 1a). The ZnCDs/ZnO nanosphere was rough owing to aggregation of nanoparticles. Further observation from Figure 1b shows that many polyhedrons of ZIF-8 (~50 nm) appeared on the surface of ZnCDs/ZnO. Energy-dispersive X-ray spectroscopy (EDX) was performed on the as-prepared composites which determined the elemental composition to comprise Zn (26.35), N (3.07), O (34.80), C (35.78) wt.%.
TEM analysis of ZnCDs/ZnO@ZIF-8 composites suggests a core–shell nanosphere, where the inner core is ZnCDs/ZnO heterojunction (Figure 1c) and the outer shell is ZIF-8 crystal (Figure 1d). Figure 2a–d are the elemental mapping diagrams of Zn, O, C, and N in ZnCDs/ZnO@ZIF-8 composites, respectively. It can be seen from the figures that these elements were evenly distributed on the materials.
XRD analysis of ZnCDs/ZnO@ZIF-8 shows a series of typical characteristic peaks with 2θ at 7.32° (39.0), 10.36° (41.7), 12.71° (44.8), 14.68° (56.5), 16.42° (40.5), 18.01° (41.4), and 22.09° (54.5), because of the (011), (002), (112), (022), (013), and (222), (114) diffraction of ZIF-8 [30]; and the obvious diffraction peaks at 31.77° (2.81), 34.43° (2.60), 36.26° (2.47), 47.55° (1.91), 56.61° (1.62), 62.87° (1.47), and 67.96° (1.37), respectively, correspond to the (100), (002), (101), (102), (110), (103), and (112) of the tetragonal phase ZnO (JCPDS, No. 89-0511) [31] (Figure 3a). The interplanar distances are listed in the parentheses, respectively. It shows that ZnCDs/ZnO@ZIF-8 composites were successfully synthesized.
The FT-IR spectra also confirm the successful synthesis of the composites (Figure 3b). The ZIF-8 and ZnCDs/ZnO@ZIF-8 both exhibits adsorption peaks at 424, 752, 1141, 1306, 1423, 1582, 2928, and 3143 cm−1, The adsorption peaks at 1582 cm−1 is attributed to the stretching vibration of C=N bonds. The adsorption peaks at 752, 1141, and 1306 cm−1 are attributed to the bending vibrations of the imidazole ring, while the one at 1423 cm−1 is attributed to the stretching vibration of the imidazole ring [21,32]. The adsorption peaks at 2928 cm−1 and 3143 cm−1 are attributed to the aromatic and aliphatic C−H stretches [33]. The widened vibration peak between 400~500 cm−1 in ZnCDs/ZnO@ZIF-8 could be attributed to the Zn-O stretch in ZnO [28], which indicates ZnCDs/ZnO’s successful modification with ZIF-8.
XPS analysis was carried out to understand the surface composition and electronic states of the constituent elements present in the composites. In common, the high-resolution survey scan of ZnCDs/ZnO@ZIF-8 revealed four peaks of Zn(2p), C (1 s), N (1 s), and O (1 s) at the ranges of 1045.2, 285.1, 398.7, 530.6 eV, respectively (Figure 4a). The C (1 s) spectrum further splits into three peaks at binding energies of 284.32, 285.1, and 286.0 eV, which are attributed to C=C/C–C, C–N/O, C=N, respectively [34] (Figure 4b). The presence of Zn−O and hydroxyl group is determined from the XPS spectrum of O 1 s. The peaks are centered at 530.0, 530.63, and 531.96 eV, respectively (Figure 4c). All of the peak positions are aligned with the literature [35]. The high-resolution spectrum of N (1 s) revealed a dominant peak at 398.75 eV, which deconvoluted into two peaks at 398.75 eV and 399.9 eV, and corresponded to N−C or N-H, respectively [36] (Figure 4d). The peaks of Zn 2p at 1022.0 eV and 1045.2 eV assigned to Zn 2p3/2 and Zn 2p1/2, respectively (Figure 4e), proved the presence of Zn2+ in the sample [29]. The high-resolution XPS spectra of bare ZnO indicates the peaks at 1021.8 and 1044.9 eV, which were reported earlier [37]. Zn LM2 Scan Auger peak of ZnCDs/ZnO@ZIF-8, as shown in Figure 4f, also indicated that the formation of the composites [38].
Figure 5a shows the nitrogen adsorption−desorption isotherms of ZnCDs/ZnO@ZIF-8 and related materials ZnO, ZnCDs/ZnO, and ZIF-8. The curves of ZIF-8 are a typical type I nitrogen adsorption−desorption isotherm [39], which fit well with the microporous frameworks of ZIF-8. The curves for ZnCDs/ZnO are a type IV isotherm [39], which shows low adsorption at low pressure and multilayer adsorption at high pressures owing to slits caused by assembly of ZnO. The specific BET surface area is 9.94 m2/g. For comparison, the BET surface area of ZnCDs/ZnO@ZIF-8 is 583.3 m2/g, higher than that of ZnCDs/ZnO. The initial adsorption of ZnCDs/ZnO@ZIF-8 is higher than that of ZnO, indicating that micropores exist in ZnCDs/ZnO@ZIF-8, which can be attributed to the frameworks of ZIF-8. The multilayer adsorption at high pressure corresponds to spherical morphology of the sample, similar to that of ZnO [21]. Figure 5b summarized pore size distribution by BJH method [40]. It indicates that the pore size of ZnCDs/ZnO@ZIF-8 distribution is wide.
The optical absorption properties of ZnCDs/ZnO@ZIF-8 and various related materials are shown in Figure 6a. All the absorptions occurred in the wavelength range of 200~400 nm. The observation indicates that the absorption intensity of ZnCDs/ZnO@ZIF-8 is higher than that of ZnO nanospheres and ZIF-8, respectively. The absorption ability in the visible-light region is enhanced as ZnCDs/ZnO enveloped by ZIF-8, which is conducive to the utilization of the solar spectrum. The band gap energies (E) of direct transition semiconductor can be calculated according to the plot of (ahv)2 versus photon energy (hv) [41]. As shown in Figure 6b, the Eg of ZnCDs/ZnO@ZIF-8 estimated to be 2.41 eV, which is narrower than that of ZnO (2.72 eV) and ZIF-8 (4.41 eV), respectively, owing to the incorporation of ZnCDs/ZnO with ZIF-8.
The fluorescence spectra of the as-synthesized composites and the related samples exhibit emission peaks centered at around 650 nm (Figure 7a). The absorbance intensity of ZnCDs/ZnO@ZIF-8 increased with respect to that of ZnCDs/ZnO and ZIF-8. As everyone knows, the radius of each arc is relevant to charge-transfer resistance: the smaller the radius of the arc, the lower the corresponding impedance [42]. As displayed in Figure 7b, ZnCDs/ZnO@ZIF-8 shows the smallest charge-transfer resistance compared with that of ZnCDs/ZnO, ZnO, and ZIF-8, coinciding with the conclusion of the EIS results. The transient photocurrent responses and electrochemical impedance spectra of the composites were employed to further explore the separation efficiency of the photogenerated charge carriers [43]. As shown in Figure 7c, the photocurrent responses of ZIF-8 are quite low, which may stem from the fast recombination of electron-hole pairs. Compared with ZnCDs/ZnO, ZnO, and ZIF-8, ZnCDs/ZnO@ZIF-8 composites exhibits the highest photocurrent density. It can generate considerably enhanced photo-currents with four visible-light irradiation on–off cycles. This indicates ZnCDs/ZnO-loading accelerates the transfer of the photo-generated electrons and holes at the interface between ZnCDs/ZnO and ZIF-8.

2.3. Catalytic Performance of ZnCDs/ZnO@ZIF-8

Photocatalysis is one of the environmentally friendly and sustainable strategies to eliminate the TC pollution [44]. Here, ZnCDs/ZnO@ZIF-8 was evaluated for the photocatalytic degradation of TC under visible-light illumination (λ > 420 nm). Figure 8a is the linear relationship between the concentration and Uv-vis adsorbance of TC. Before the photocatalysis experiments, the suspension was magnetically stirred in the dark for 60 min to make sure an adsorption-desorption equilibrium containing the catalyst powders and TC aqueous without illumination. As shown in Figure 8b, the photolysis of TC in the absence of photocatalysts can be neglected, which demonstrates that TC is very stable and hardly decomposed. Apparently, there was little adsorption phenomenon in ZnO, ZnCDs/ZnO, and CDs/ZnO, while the samples decorated with ZIF-8 showed a discernible adsorption. This phenomenon could be ascribed to the strong adsorption capacity of the wide nanopores interconnected through 0.34 nm windows assembled as an analogue zeolite sodalite structure of ZIF-8 [45,46]. Significant degradation of TC occurs when ZnCDs/ZnO hybridized with ZIF-8 (Figure 8c). Furthermore, the degradation rate was effect by the quantity of ZnCDs/ZnO@ZIF-8, as depicted in Figure 8d, the optimum dosage is 100 mg.
In order to ascertain the reactive species that directly participate in photocatalytic system, active species trapping experiments were tested. BQ, EDTA-2Na, K2S2O8, and IPA were employed to quench ⋅O2−, h+, e− and ⋅OH in the photocatalytic process, respectively. As depicted in Figure 9a, the photocatalytic rate did not exhibit a noticeable change in the presence of EDTA-2Na, K2S2O8, and IPA. This indicates that h+, e−, and ⋅OH that participated in the photocatalytic process did not play a leading role. Whereas, when BQ was added to the reaction system, the degradation of TC was greatly inhibited. This result demonstrates that ⋅O2- is main reactive species for ZnCDs/ZnO@ZIF-8.
Furthermore, the stability of the photocatalyst was investigated through the cyclic degradation of TC under visible light irradiation. One hundred milligrams of ZnCDs/ZnO@ZIF-8 was used in the recycling experiment. After the photocatalysis, the mixture was centrifuged to obtain a catalyst to characterize IR and XRD, or for the next reaction. It can be clearly seen that the photocatalytic activity remained almost constant after five cycles which proves the as-synthesized composites have high stability (Figure 9b). The incorporation of ZIF-8 into the ZnCDs/ZnO nanospheres was therefore thought to enhance the visible light activity of ZnO and also inhibit the photo-corrosion of ZnO, leading to a stable and durable photocatalytic activity. The IR spectra and XRD of ZnCDs/ZnO@ZIF-8 is almost unchanged before and after the photocatalytic reaction (Figure 9c,d). It indicates that the catalyst is stable and recyclable during the photocatalytic process.
On the basis of the above experimental results over ZnCDs/ZnO@ZIF-8, photocatalytic mechanism is proposed and illustrated in Figure 10. The photocatalytic activity of ZnCDs/ZnO@ZIF-8 can be attributed to the ZnCDs/ZnO heterojunction and ZIF-8, which effectively facilitates the electron transfer and the separation of electron-hole pairs. During UV irradiation, electrons and holes are excited at the conduction band (CB) and the valence band (VB) on the composites, respectively. After that, electrons transfer from the excited state to the ZnCDs/ZnO and transform from O2 to ⋅O2−. ⋅O2− and holes at VB finally contribute to the degradation of tetracycline in the solution.

3. Materials and Methods

3.1. Materials

Zinc nitrate hexahydrate, DMF, alcohol were purchased from Sinopharm Group Chemical Reagent Co., Ltd. Shanghai, China. Tetracycline hydrochloride (TC) and 2-methyl imidazole (2-mIm) were purchase from Aladdin Chemical Reagent Co., Ltd. Shanghai, China. Folic acid was purchased from Macklin Technology Co., Ltd. Shanghai, China. Dialysis bag (MWCO: 1000 da) imported from the United States. All solvents and reagents were analytical grade and used without further purification.

3.2. Characterization

Fourier transform infrared spectroscopy (FT-IR) was recorded on a Nicolet iZ10 FT-IR Spectrophotometer (Thermo Electron Co., USA) with potassium bromide (KBr) as the dispersant to examine possible chemical bonds in adsorbents. X-ray diffraction (XRD) patterns were recorded on a German Brooke XRD-D8 Advance D8 with Cu Kα radiation (λ = 0.15406 nm, voltage 40 kV, current 40 mA) and irradiated at a scan rate of 0.1°/s in the range of 5°–80°. Ultraviolet-visible (UV-vis) spectra experiments were performed on Hitachi UV-vis 3010 spectrophotometer (Hitachi Ltd., Tokyo, Japan). The morphology and microstructure of the samples were characterized by scanning electron microscopy (SEM, Hitachi Ltd., Tokyo, Japan) and field emission scanning electron microscopy (FESEM, Hitachi S-4800, Hitachi Ltd., Tokyo, Japan) operated at 5 kV. X-ray photoelectron spectroscopy (XPS, Thermo Scientifific, EscaLab 250Xi spectrometer, USA) with a monochromatic Al Kα X-ray source was used to analyze elements (hv = 1486.6 eV, power 150 W, beam spot 650 um, voltage 14.8 kV, current 1.6 A and testing software is advantageous). Charge correction was carried out using polluted carbon C1s = 284.8 eV. A constant analyzer pass energy Ep narrow sweep 20 eV, wide sweep 100 eV, and vacuum degree 1×10−10 MBA. Photoluminescence spectroscopy (PL) was carried out using a Hitachi F-4500 fluorescence spectrophotometer (Hitachi Ltd., Tokyo, Japan). The sample was excited by a 360 nm laser light source. UV-vis diffuse reflectance spectroscopy (DRS) were tested in absorption mode at the range of 200–800 nm by a Shimadzu UV-2450 spectrometer (Shimadzu Ltd., Tokyo, Japan) with MgO powder as the reference. The MgO powder was firstly pressed into thin disc on the holder, and then the powder sample was evenly spread on an MgO disc and pressed again. A 500 W Xenon lamp was used as the light source (λ ≥ 420 nm). Electrochemical tests were carried out on a CHI760E electrochemical analyzer (CHIIns., Chenhua Ltd., Shanghai, China) in a conventional three-electrode configuration with a Pt foil as the counter electrode and Ag/AgCl (saturated KCl) as the reference electrode. The electrolyte solution was 1.0 mol⋅L−1 Na2SO4. The working electrode was prepared by mixing 10 mg catalyst with 10 μL 5 % Nafion and 10 mL ethyl alcohol to form a slurry, and then the slurry was coated onto a 1.0 cm2 ITO conductive glass. The scan rate was 0.1 V/sec and the testing potential was 2 V to start the scan to sweep until −2 V, maintaining the scan window between +2 V to −2 V (vs Ag/AgCl) using 1 M Na2SO4 as supporting electrolyte. Specific surface areas of samples were measured using nitrogen sorption isotherms through a standard Brunauer–Emmett–Teller (BET) analysis (Tristar II 3020, Micromeritics Instrument Corporation, Norcross, GA, USA).

3.3. Synthesis of ZnCDs

Folic acid (0.1 g) and DMF (10 mL) were mixed with Zn(NO3)2 (0.05 g). The solution was stirred and then transferred into a 25 mL Telfon steel autoclave and heated at 190 °C for 12 h. The solution of ZnCDs was obtained by dialysis against deionized water through a dialysis bag (MWCO: 1000 Da). It was evaporated to dryness for further use. A control sample without metal doping (bare CDs) was prepared under conditions similar to that of ZnCDs.

3.4. Synthesis of ZnO

Folic acid (0.1 g), DMF (10 mL) were mixed with Zn(NO3)2 (0.05 g). The solution transferred into a 25 mL Telfon steel autoclave and heated at 190 °C for 12 h. After the mixture was cooled down to room temperature, the precipitate was collected by centrifugation and washed with H2O and ethanol for several times. The solid was calcined at 500 °C for 4 h to obtain white powder ZnO.

3.5. Synthesis of ZnCDs/ZnO

ZnO (100 mg) was mixed with ZnCDs (10 mg) in CH3CH2OH (20 mL) and stirred for 6 h. The precipitate obtained was washed with H2O and CH3CH2OH, respectively, ZnCDs/ZnO formed and then dried in vacuum.

3.6. Synthesis of ZnCDs/ZnO@ZIF-8

Twenty milliliters of methanolic solution including ZnCDs/ZnO (80, 100, 200 mg), 160 mg of zinc nitrate hexahydrate (0.05 mmol), and 20 mL of methanolic solution including 410 mg of 2-methylimidazole (5 mmol) were mixed with stirred continuously at 50 °C for 4 h. A white powder, ZnCDs/ZnO@ZIF-8, was collected by centrifugation, then washed with methanol and dried at 80 °C for use. As a contrast, ZIF-8 was prepared according to the procedure in the literature [47].

3.7. Photocatalytic Degradation of Tetracycline

The photocatalytic activity of ZnCDs/ZnO@ZIF-8 composites was determined by the photodegradation of tetracycline. The reaction mixture was irradiated by a 500 W Xenon lamp for photodegradation while being stirred. During the reaction, a cooling water circulation device was used to maintain the reaction temperature at around 50~60 °C. In a typical process, 100 mg of photocatalyst ZnCDs/ZnO@ZIF-8 was added in 1000 mL of the tetracycline solution and stirred for 60 min in the dark to attain anadsorption/desorption equilibration. For the normal concentration of TC present in the natural environment (in manure and soil, 0~200 mg⋅kg−1 [48,49]; in the aquatic environment, 0~20 μg⋅L−1 [1,50]); we chose 20 mg⋅L−1 for the initial concentration of TC. In the photocatalytic process, 3 mL mixture was extracted and centrifuged to obtain clear liquor for the next residual TC detection using the spectrophotometer at a maximum absorption wavelength of 371 nm. Photocatalytic efficiency was calculated by the following formula:
P h o t o c a t a l y t i c e f f i c i e n c y = ( C 0 − C ) C 0 × 100
where C0 and C represent concentrations of tetracycline before and after irradiated, respectively.
Additives that could scavenge different active radicals were utilized in comparative trials to illuminate the degradation process of tetracycline. K2S2O8 (1 mM), disodium ethylenediaminetetraacetic acid (EDTA-2Na, 1 mmol⋅L−1), p-benzoquinone (BQ, 1 mmol⋅L−1) and tert-butanol (t-BuOH, 1 mmol⋅L−1) were introduced into the reaction system to capture electrons (e−), holes (h+), superoxide anion free radicals (⋅O2−), and hydroxyl free radicals (⋅OH). These tests were performed following the photocatalytic degradation process mentioned above.

4. Conclusions

In summary, we have prepared ZnCDs/ZnO@ZIF-8 composites via zeolite metal-organic frame ZIF-8 wrapped around ZnCDs/ZnO heterojunction. The hybrid material exhibits superior photocatalysis performance for the degradation of tetracycline, which was induced by synergistic effect of ZIF-8 and ZnCDs/ZnO. Our work may provide more thought to design zeolite MOF-decorated semiconductors and carbon dots-based composites that utilize visible light to solve the environmental problems.

Author Contributions

Y.C. designed the experiments and wrote them manuscript. C.J. supervised this study. X.W., D.W. and Y.M. supported the experiments and contributed to the scientific discussion. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the Natural Science Foundation of Education Department of Anhui Province. grant number: KJ2017A314.

Data Availability Statement

Data is contained within the article.

Acknowledgments

Y. Cheng is grateful to the Natural Science Foundation of Education Department of Anhui Province (KJ2017A314) for funding.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Bilal, M.; Mehmood, S.; Rasheed, T.; Iqbal, H.M.N. Antibiotics traces in the aquatic environment: Persistence and adverse environmental impact. Curr. Opin. Environ. Sci. Health. Health 2020, 13, 68–74. [Google Scholar] [CrossRef]
  2. Cheng, D.; Ngo, H.H.; Guo, W.; Chang, S.W.; Nguyen, D.D.; Liu, Y.; Wei, Q.; Wei, D. A critical review on antibiotics and hormones in swine wastewater: Water pollution problems and control approaches. J. Hazard. Mater. 2020, 387, 121682. [Google Scholar] [CrossRef]
  3. Välitalo, P.; Kruglova, A.; Mikola, A.; Vahala, R. Toxicological impacts of antibiotics on aquatic micro-organisms: A mini-review. Int. J. Hyg. Environ. Health 2017, 220, 558–569. [Google Scholar] [CrossRef] [Green Version]
  4. Zhang, L.; Song, X.; Liu, X. Studies on the removal of tetracycline by multi-walled carbon nanotubes. Chem. Eng. J. 2011, 178, 26–33. [Google Scholar] [CrossRef]
  5. Wang, J.L.; Wang, S.Z. Preparation, modification and environmental application of biochar: A review. J. Clean. Prod. 2019, 227, 1002–1022. [Google Scholar] [CrossRef]
  6. Wang, S.Z.; Hu, Y.M.; Wang, J.L. Biodegradation of typical pharmaceutical compounds by a novel strain Acinetobacter sp. J. Environ. Manag. 2018, 217, 240–246. [Google Scholar] [CrossRef] [PubMed]
  7. Wu, J.; Zhang, H.; Oturan, N.; Wang, Y.; Chen, L.; Oturan, M.A. Application of response surface methodology to the removal of the antibiotic tetracycline by electrochemical process using carbon-felt cathode and DSA (Ti/RuO2–IrO2) anode. Chemosphere 2012, 87, 614–620. [Google Scholar] [CrossRef]
  8. Gao, Y.; Wu, J.; Wang, J.; Fan, Y.; Zhang, S.; Dai, W. A novel multifunctional p-type semiconductor@MOFs nanoporous platform for simultaneous sensing and photodegradation of tetracycline. ACS Appl. Mater. Interfaces 2020, 12, 11036–11044. [Google Scholar] [CrossRef] [PubMed]
  9. Li, X.; Xiong, J.; Gao, X.; Ma, J.; Chen, Z.; Kang, B.; Liu, J.; Li, H.; Feng, Z.; Huang, J. Novel BP/BiOBr S-scheme nano-heterojunction for enhanced visible-light photocatalytic tetracycline removal and oxygen evolution activity. J. Hazard. Mater. 2020, 387, 121690. [Google Scholar] [CrossRef] [PubMed]
  10. Zha, Z.; Lai, J.; Li, Y.; Yang, J.; Cui, S.; Li, Y. The degradation of tetracycline by modified BiOCl nanosheets with carbon dots from the chlorella. J. Alloys Compd. 2021, 855, 157454. [Google Scholar] [CrossRef]
  11. Ponraj, Y.K.; Borah, B. Separation of methane from ethane and propane by selective adsorption and diffusion in MOF Cu-BTC: A molecular simulation study. J. Mol. Graph. Modell. 2020, 97, 107574. [Google Scholar] [CrossRef] [PubMed]
  12. Wu, T.; Liu, X.J.; Liu, Y.; Cheng, M.; Liu, Z.F.; Zeng, G.M.; Shao, B.B.; Liang, Q.H.; Zhang, W.; He, Q.Y.; et al. Application of QD-MOF composites for photocatalysis: Energy production and environmental remediation. Coord. Chem. Rev. 2020, 403, 213097. [Google Scholar] [CrossRef]
  13. Zhao, H.; Xing, Z.; Su, S.; Song, S.; Xu, T.; Li, Z.; Zhou, W. Recent advances in metal organic frame photocatalysts for environment and energy applications. Appl. Mater. Today 2020, 21, 100821. [Google Scholar] [CrossRef]
  14. Zhang, J.; Wang, X.-Y.; Wang, Y.-H.; Wang, D.-D.; Song, Z.; Zhang, C.-D.; Wang, H.-S. Colorable zeolitic imidazolate frameworks for colorimetric detection of biomolecules. Anal. Chem. 2020, 92, 12670–12677. [Google Scholar] [CrossRef] [PubMed]
  15. Huang, X.C.; Lin, Y.Y.; Zhang, J.P.; Chen, X.M. Ligand-directed strategy for zeolite-type metal-organic frameworks: Zinc(II) imidazolates with unusual zeolitic topologies. Angew. Chem. Int. Ed. 2006, 45, 1557–1559. [Google Scholar] [CrossRef]
  16. Weber, M.D.R.; Baker, T.L.; Dao, B.; Kwon, C.; Tian, F.Y. Exploring the aggregative growth of nanoporous zeolitic imidazolate framework ZIF-8. Cryst. Growth Des. 2020, 20, 2305–2312. [Google Scholar] [CrossRef]
  17. Wolf, A.; Diestel, L.; Lubkemann, F.; Kodanek, T.; Mohamed, T.; Caro, J.; Dorfs, D. Plasmonic semiconductor nanoparticles in a metal−organic framework structure and their in situ cation exchange. Chem. Mater. 2016, 28, 7511–7518. [Google Scholar] [CrossRef]
  18. Jian, M.P.; Wang, H.; Liu, R.P.; Qu, J.H.; Wang, H.T.; Zhang, X.W. Self-assembled one-dimensional MnO2@zeolitic imidazolate framework-8 nanostructures for highly efficient arsenite removal. Environ. Sci. Nano 2016, 3, 1186–1194. [Google Scholar] [CrossRef]
  19. Zhu, K.; Chen, C.; Xu, H.; Gao, Y.; Tan, X.; Alsaedi, A.; Hayat, T. Cr(VI) reduction and immobilization by core-double-shell structured magnetic polydopamine@zeolitic idazolate frameworks-8 microspheres. ACS Sustain. Chem. Eng. 2017, 5, 6795–6802. [Google Scholar] [CrossRef]
  20. Esken, D.; Turner, S.; Wiktor, C.; Kalidindi, S.B.; Van Tendeloo, G.; Fischer, R.A. GaN@ZIF-8: Selective formation of gallium nitride quantum dots. inside a zinc methylimidazolate framework. J. Am. Chem. Soc. 2011, 133, 16370–16373. [Google Scholar] [CrossRef]
  21. Wang, X.B.; Liu, J.; Leong, S.; Lin, X.C.; Wei, J.; Kong, B.; Xu, Y.F.; Low, Z.-X.; Yao, J.F.; Wang, H.T. Rapid construction of ZnO@ZIF-8 heterostructures with size-selective photocatalysis properties. ACS Appl. Mater. Interface 2016, 8, 9080–9087. [Google Scholar] [CrossRef] [PubMed]
  22. Yu, B.; Wang, F.; Dong, W.; Hou, J.; Lu, P.; Gong, J. Self-template synthesis of core–shell ZnO@ZIF-8 nanospheres and the photocatalysis under UV irradiation. Mater. Lett. 2015, 156, 50–53. [Google Scholar] [CrossRef]
  23. Zhan, W.-W.; Kuang, Q.; Zhou, J.-Z.; Kong, X.-J.; Xie, Z.-X.; Zheng, L.-S. Semiconductor@metal-organic framework core-shell heterostructures: A case of ZnO@ZIF-8 nanorods with selective photoelectrochemical response. J. Am. Chem. Soc. 2013, 135, 1926–1933. [Google Scholar] [CrossRef]
  24. Han, M.; Zhu, S.J.; Lu, S.Y.; Song, Y.B.; Feng, T.L.; Tao, S.Y.; Liu, J.J.; Yang, B. Recent progress on the photocatalysis of carbon dots: Classification, mechanism and applications. Nano Today 2018, 19, 201–218. [Google Scholar] [CrossRef]
  25. Chu, K.-W.; Lee, S.L.; Chang, C.-J.; Liu, L.Y. Recent progress of carbon dot precursors and photocatalysis applications. Polymers 2019, 11, 689. [Google Scholar] [CrossRef] [Green Version]
  26. Phang, S.J.; Tan, L.-L. Recent advances in carbon quantum dot (CQD)-based two dimensional materials for photocatalytic applications. Catal. Sci. Technol. 2019, 9, 5882–5905. [Google Scholar] [CrossRef]
  27. Hazarika, D.; Karak, N. Photocatalytic degradation of organic contaminants under solar light using carbon dot/titanium dioxide nanohybrid, obtained through a facile approach. Appl. Surf. Sci. 2016, 376, 276–285. [Google Scholar] [CrossRef]
  28. Zhao, W.; Yan, L.; Gu, H.; Li, Z.; Wang, Y.; Luo, Q.; Yang, Y.; Liu, X.; Wang, H.; Ma, C.-Q. Zinc oxide coated carbon dot nanoparticles as electron transport layer for inverted polymer solar cells. ACS Appl. Energy Mater. 2020, 3, 11388–11397. [Google Scholar] [CrossRef]
  29. Zhang, X.-Y.; Liu, J.-K.; Wang, J.-D.; Yang, X.-H. Mass production, enhanced visible light photocatalytic efficiency, and application of modified ZnO nanocrystals by carbon dots. Ind. Eng. Chem. Res. 2015, 54, 1766–1772. [Google Scholar] [CrossRef]
  30. Chin, M.; Cisneros, C.; Araiza, S.M.; Vargas, K.M.; Ishihara, K.M.; Tian, F. Rhodamine B degradation by nanosized zeolitic imidazolate framework-8 (ZIF-8). RSC Adv. 2018, 8, 26987–26997. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  31. Wang, Y.; Ge, S.; Cheng, W.; Hu, Z.; Shao, Q.; Wang, X.; Lin, J.; Dong, M.; Wang, J.; Guo, Z. Microwave hydrothermally synthesized metal−organic framework-5 derived C-doped ZnO with enhanced photocatalytic degradation of Rhodamine B. Langmuir 2020, 36, 9658–9667. [Google Scholar] [CrossRef]
  32. Lin, L.; Zhang, T.; Liu, H.; Qiu, J.; Zhang, X. In situ fabrication of a perfect Pd/ZnO@ZIF-8 core-shell microsphere as an efficient catalyst by a ZnO support-induced ZIF-8 growth strategy. Nanoscale 2015, 7, 7615–7623. [Google Scholar] [CrossRef]
  33. Hu, Y.; Kazemian, H.; Rohani, S.; Huang, Y.; Song, Y. In situ high pressure study of ZIF-8 by FTIR spectroscopy. Chem. Commun. 2011, 47, 12694–12696. [Google Scholar] [CrossRef] [PubMed]
  34. Zhao, S.; Lan, M.; Zhu, X.; Xue, H.; Ng, T.; Meng, T.; Lee, C.; Wang, P.; Zhang, W. Green synthesis of bifunctional fluorescent carbon dots from garlic for cellular imaging and free radical scavenging. ACS Appl. Mater. Interfaces 2015, 7, 17054–17060. [Google Scholar] [CrossRef]
  35. Xiao, J.; Zhang, X.; Li, Y. A Ternary g-C3N4/Pt/ZnO photoanode for efficient photoelectrochemical water splitting. Int. J. Hydrogen Energy 2015, 40, 9080–9087. [Google Scholar] [CrossRef]
  36. Mahala, C.; Sharma, M.D.; Basu, M. Type-II heterostructure of ZnO and carbon dots demonstrates enhanced photoanodic performance in photoelectrochemical water splitting. Inorg. Chem. 2020, 59, 6988–6999. [Google Scholar] [CrossRef]
  37. Mahala, C.; Sharma, M.D.; Basu, M. Near-field and far-field plasmonic effects of gold nanoparticles decorated on ZnO nanosheets for enhanced solar water splitting. ACS Appl. Nano Mater. 2020, 3, 1153–1165. [Google Scholar] [CrossRef]
  38. Biesingera, M.C.; Lau, L.W.M.; Gerson, A.R.; Smart, R.S.C. Resolving surface chemical states in XPS analysis of first row transition metals, oxides and hydroxides: Sc, Ti, V., Cu and Zn. Appl. Surf. Sci. 2010, 257, 887–898. [Google Scholar] [CrossRef]
  39. Kruk, M.; Jaroniec, M. Gas adsorption characterization of ordered organic-inorganic nanocomposite materials. Chem. Mater. 2001, 13, 3169–3183. [Google Scholar] [CrossRef]
  40. Gelb, L.D.; Gubbins, K.E. Pore size distributions in porous glasses: A computer simulation study. Langmuir 1999, 15, 305–308. [Google Scholar] [CrossRef]
  41. Cheng, Y.; Mei, Y.; Deng, S.Y.; Li, J. In situ synthesis and photocatalytic performance of three dimensional composites CdS@DMSA-GO. Chin. J. Inorg. Chem. 2020, 36, 714–729. [Google Scholar]
  42. Li, Y.; Jiang, Y.; Ruan, Z.; Lin, K.; Yu, Z.; Zheng, Z.; Xu, X.; Yuan, Y. Simulation-guided synthesis of graphitic carbon nitride beads with 3D interconnected and continuous meso/macropore channels for enhanced light absorption and photocatalytic performance. J. Mater. Chem. A 2017, 5, 21300–21312. [Google Scholar] [CrossRef]
  43. Bian, S.; Zhou, C.; Li, P.; Liu, J.; Dong, X.; Xi, F. Graphene quantum dots decorated titania nanosheets heterojunction efficient charge separation and enhanced visible-light photocatalytic performance. ChemCatChem 2017, 9, 3349–3357. [Google Scholar] [CrossRef]
  44. Guo, F.; Shi, W.; Wang, H.B.; Han, M.; Guan, W.; Huang, H.; Liu, Y.; Kang, Z. Study on highly enhanced photocatalytic tetracycline degradation of type ⅡAgI/CuBi2O4 and Z-scheme AgBr/CuBi2O4 heterojunction photocatalysts. J. Hazard. Mater. 2018, 349, 111–118. [Google Scholar] [CrossRef]
  45. Huang, W.Y.; Liu, N.; Zhang, X.D.; Wu, M.H.; Tang, L. Metal organic framework g-C3N4/MIL-53(Fe) heterojunctions with enhanced photocatalytic activity for Cr(VI) reduction under visible light. Appl. Surf. Sci. 2017, 425, 107–116. [Google Scholar] [CrossRef]
  46. Yuan, D.; Ding, J.; Zhou, J.; Wang, L.; Wan, H.; Dai, W.-L.; Guan, G. Graphite carbon nitride nanosheets decorated with ZIF-8 nanoparticles: Effects of the preparation method and their special hybrid structures on the photocatalytic performance. J. Alloys Compd. 2018, 762, 98–108. [Google Scholar] [CrossRef]
  47. Liang, X.; Quan, B.; Ji, G.; Liu, W.; Zhao, H.; Dai, S.; Lv, J.; Du, Y. Tunable dielectric performance derived from the metal−organic framework/reduced graphene oxide hybrid with broadband absorption. ACS Sustain. Chem. Eng. 2017, 5, 10570–10579. [Google Scholar] [CrossRef]
  48. Hamscher, G.; Sczesny, S.; Hoper, H.; Nau, H. Determination of persistent tetracycline residues in soil fertilized with liquid manure by high-performance liquid chromatography with electrospray ionization tandem mass spectrometry. Anal. Chem. 2002, 74, 1509–1518. [Google Scholar] [CrossRef] [PubMed]
  49. Ji, X.; Shen, Q.; Liu, F.; Ma, J.; Xu, G.; Wang, Y.; Wu, M. Antibiotic resistance gene abundances associated with antibiotics and heavy metals in animal manures and agricultural soils adjacent to feedlots in Shanghai, China. J. Hazard. Mater. 2012, 235, 178–185. [Google Scholar] [CrossRef]
  50. Xu, L.; Zhang, H.; Xiong, P.; Zhu, Q.; Liao, C.; Jiang, G. Occurrence, fate, and risk assessment of typical tetracycline antibiotics in the aquatic environment: A review. Sci. Total Environ. 2021, 753, 141975. [Google Scholar] [CrossRef]
Catalysts 11 00934 sch001 550
Scheme 1. Synthesis of ZnCDs/ZnO@ZIF-8 composites.
Scheme 1. Synthesis of ZnCDs/ZnO@ZIF-8 composites.
Catalysts 11 00934 sch001
Catalysts 11 00934 g001 550
Figure 1. (a) SEM of ZnO (b) SEM of ZnCDs/ZnO@ZIF-8 (c) TEM of ZnCDs/ZnO (d) TEM of ZnCDs/ZnO@ZIF-8 composites.
Figure 1. (a) SEM of ZnO (b) SEM of ZnCDs/ZnO@ZIF-8 (c) TEM of ZnCDs/ZnO (d) TEM of ZnCDs/ZnO@ZIF-8 composites.
Catalysts 11 00934 g001
Catalysts 11 00934 g002 550
Figure 2. Mapping of ZnCDs/ZnO@ZIF-8 composites (a) Zn (b) O (c) C (d) N.
Figure 2. Mapping of ZnCDs/ZnO@ZIF-8 composites (a) Zn (b) O (c) C (d) N.
Catalysts 11 00934 g002
Catalysts 11 00934 g003 550
Figure 3. (a) XRD and (b) IR of ZnCDs/ZnO@ZIF-8 composites and related materials.
Figure 3. (a) XRD and (b) IR of ZnCDs/ZnO@ZIF-8 composites and related materials.
Catalysts 11 00934 g003
Catalysts 11 00934 g004 550
Figure 4. (a) Survey scan (b) C 1 s (c) N1 s (d) O 1 s (e) Zn2p of XPS and (f) Zn LM2 Scan Auger peak of ZnCDs/ZnO@ZIF-8.
Figure 4. (a) Survey scan (b) C 1 s (c) N1 s (d) O 1 s (e) Zn2p of XPS and (f) Zn LM2 Scan Auger peak of ZnCDs/ZnO@ZIF-8.
Catalysts 11 00934 g004
Catalysts 11 00934 g005 550
Figure 5. (a) Nitrogen adsorption−desorption isotherm (b) BET of ZnCDs/ZnO@ZIF-8.
Figure 5. (a) Nitrogen adsorption−desorption isotherm (b) BET of ZnCDs/ZnO@ZIF-8.
Catalysts 11 00934 g005
Catalysts 11 00934 g006 550
Figure 6. (a) UV-vis DRS (b) Kubelka–Munk function spectrum.
Figure 6. (a) UV-vis DRS (b) Kubelka–Munk function spectrum.
Catalysts 11 00934 g006
Catalysts 11 00934 g007 550
Figure 7. (a) Fluorescence emission. (b) Electrochemical impedance spectrum. (c) Transient photocurrent response of ZnCDs/ZnO@ZIF-8 and related materials.
Figure 7. (a) Fluorescence emission. (b) Electrochemical impedance spectrum. (c) Transient photocurrent response of ZnCDs/ZnO@ZIF-8 and related materials.
Catalysts 11 00934 g007
Catalysts 11 00934 g008 550
Figure 8. (a) Linear relationship between the concentration and Uv-vis adsorbance of TC. (b) The photocatalytic performance of verious materials for the degradation of TC. (c) Linear relationship of degradation kinetics over ZnCDs/ZnO@ZIF-8 and other related materials. (d) The photocatalytic activity with different qualities of ZnCDs/ZnO@ZIF-8.
Figure 8. (a) Linear relationship between the concentration and Uv-vis adsorbance of TC. (b) The photocatalytic performance of verious materials for the degradation of TC. (c) Linear relationship of degradation kinetics over ZnCDs/ZnO@ZIF-8 and other related materials. (d) The photocatalytic activity with different qualities of ZnCDs/ZnO@ZIF-8.
Catalysts 11 00934 g008
Catalysts 11 00934 g009 550
Figure 9. (a) Time-dependent photodegradation of TC over Zn-CDs/ZnO@ZIF-8 in the presence of different scavengers. (b) Cycling runs of Zn-CDs/ZnO@ZIF-8 (c) IR of Zn-CDs/ZnO@ZIF-8. (d) XRD of Zn-CDs/ZnO@ZIF-8 before and after reaction.
Figure 9. (a) Time-dependent photodegradation of TC over Zn-CDs/ZnO@ZIF-8 in the presence of different scavengers. (b) Cycling runs of Zn-CDs/ZnO@ZIF-8 (c) IR of Zn-CDs/ZnO@ZIF-8. (d) XRD of Zn-CDs/ZnO@ZIF-8 before and after reaction.
Catalysts 11 00934 g009
Catalysts 11 00934 g010 550
Figure 10. Proposed mechanism of photocatalytic degradation for TC.
Figure 10. Proposed mechanism of photocatalytic degradation for TC.
Catalysts 11 00934 g010
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Cheng, Y.; Wang, X.; Mei, Y.; Wang, D.; Ji, C. ZnCDs/ZnO@ZIF-8 Zeolite Composites for the Photocatalytic Degradation of Tetracycline. Catalysts 2021, 11, 934. https://doi.org/10.3390/catal11080934

AMA Style

Cheng Y, Wang X, Mei Y, Wang D, Ji C. ZnCDs/ZnO@ZIF-8 Zeolite Composites for the Photocatalytic Degradation of Tetracycline. Catalysts. 2021; 11(8):934. https://doi.org/10.3390/catal11080934

Chicago/Turabian Style

Cheng, Yong, Xiuxiu Wang, Yu Mei, Dan Wang, and Changchun Ji. 2021. "ZnCDs/ZnO@ZIF-8 Zeolite Composites for the Photocatalytic Degradation of Tetracycline" Catalysts 11, no. 8: 934. https://doi.org/10.3390/catal11080934

APA Style

Cheng, Y., Wang, X., Mei, Y., Wang, D., & Ji, C. (2021). ZnCDs/ZnO@ZIF-8 Zeolite Composites for the Photocatalytic Degradation of Tetracycline. Catalysts, 11(8), 934. https://doi.org/10.3390/catal11080934

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop