Next Article in Journal
Recent Strategies for the Immobilization of Therapeutic Enzymes
Next Article in Special Issue
Effects of Freeze–Thaw Cycles on Strength and Wave Velocity of Lime-Stabilized Basalt Fiber-Reinforced Loess
Previous Article in Journal
Synthesis and Vulcanization of Polymyrcene and Polyfarnesene Bio-Based Rubbers: Influence of the Chemical Structure over the Vulcanization Process and Mechanical Properties
Previous Article in Special Issue
RSM Modeling and Optimization of CO2 Separation from High CO2 Feed Concentration over Functionalized Membrane
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 14
Issue 7
10.3390/polym14071408
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Development of Amine-Functionalized Metal-Organic Frameworks Hollow Fiber Mixed Matrix Membranes for CO2 and CH4 Separation: A Review

by
Naveen Sunder
1,
Yeong Yin Fong
1,2,*,
Mohamad Azmi Bustam
1,3 and
Nadia Hartini Suhaimi
1
1
Department of Chemical Engineering, Universiti Teknologi PETRONAS, Bandar Seri Iskandar 32610, Malaysia
2
CO2 Research Center (CO2RES), R&D Building, Universiti Teknologi PETRONAS, Bandar Seri Iskandar 32610, Malaysia
3
Centre of Research in Ionic Liquids (CORIL), Universiti Teknologi PETRONAS, Bandar Seri Iskandar 32610, Malaysia
*
Author to whom correspondence should be addressed.
Polymers 2022, 14(7), 1408; https://doi.org/10.3390/polym14071408
Submission received: 11 February 2022 / Revised: 26 February 2022 / Accepted: 1 March 2022 / Published: 30 March 2022
(This article belongs to the Special Issue Fiber and Polymer Composites: Processing, Simulation, Properties and Applications)
Browse Figures
Review Reports Versions Notes

Abstract

:
CO2 separation from raw natural gas can be achieved through the use of the promising membrane-based technology. Polymeric membranes are a known method for separating CO2 but suffer from trade-offs between its permeability and selectivity. Therefore, through the use of mixed matrix membranes (MMMs) which utilizes inorganic or hybrid fillers such as metal-organic frameworks (MOFs) in polymeric matrix, the permeability and selectivity trade-off can be overcome and possibly surpass the Robeson Upper Bounds. In this study, various types of MOFs are explored in terms of its structure and properties such as thermal and chemical stability. Next, the use of amine and non-amine functionalized MOFs in MMMs development are compared in order to investigate the effects of amine functionalization on the membrane gas separation performance for flat sheet and hollow fiber configurations as reported in the literature. Moreover, the gas transport properties and various challenges faced by hollow fiber mixed matrix membranes (HFMMMs) are discussed. In addition, the utilization of amine functionalization MOF for mitigating the challenges faced is included. Finally, the future directions of amine-functionalized MOF HFMMMs are discussed for the fields of CO2 separation.

Graphical Abstract

1. Introduction

Gas separation processes are widely used in industries for the separation of one or more gases from a mixture such as CO2/CH4 separation for natural gas sweetening and biogas purification [1], CO2/N2 separation from flue gas [2], and H2/CO2 purification in the water-gas shift reaction (WGSR) [3]. Several conventional gas separation technologies are available including adsorption [4], absorption [5], and cryogenics distillation [6]. However, this conventional technology faces some drawbacks, for example, the absorption method is less efficient with cost restriction, and faces difficulties in scale-up due to the complexity of the design process and cryogenic distillation high-energy requirement, high operation cost, and high tendency for blockage of process equipment [6]. Therefore, membrane-based technology has drawn more attention due to its energy efficiency, ease of scale-up, and environmentally friendly nature [7] compared with conventional methods.
Membrane separation technologies have been applied since 1980s in the natural gas industry to remove CO2, N2, H2S, and NGLs [8]. Membranes for gas separation are typically classified into three main groups defined by their materials of fabrication: polymeric, inorganic, and mixed matrix membranes. Still, trade-off between permeability and selectivity becomes an issue in polymeric membranes as indicated by the Robeson plot [9]. On the other hand, inorganic membranes having difficulties with regard to reproducibility as well as complicated fabrication methods [10]. To overcome these limitations and increase the performance of polymer membranes, inorganic materials are integrated into polymer matrix to form mixed matrix membranes (MMMs). Over the years, several types of conventional inorganic fillers were used in the development of mixed matrix membrane such as zeolites [3], carbon molecular sieve (CMS) [11], activated carbon [12], metal-organic frameworks [13,14,15,16,17,18,19,20,21], carbon nanotubes (CNTs) [22], metal oxides, mesoporous materials, non-porous material, and lamellar inorganic materials [23]. Common types of MMMs contains two phases which are the polymer (continuous) phase and a dispersed inorganic phase [23]. Incorporation of inorganic filler in the polymer matrix should provide better separation performance due to their excellent chemical and thermal stability, higher affinity to CO2 molecules and molecular sieving effect [24]. Moreover, organic polymers are easily subjected to physical aging due to the imbalance in its structure which reduces their fractional free volume and that leads to an increase on the membrane’s gas permeability [25]. Despite that, with sufficient filler loading and good compatibility, the physical aging resistance of MMMs can be improved because the increased binding is forced between the filler’s surface and the polymer matrix as the MMM becomes more rigid and less prone to collapse [26].
Metal-organic frameworks (MOFs) are a satisfactory alternative to improve the permeation properties of membranes because of its large surface area, high porosity, adsorption capacity, and good compatibility [15]. This has led to the utilization of MOFs in numerous applications which include gas/liquid separation, catalysts, medicine, and electronics [27]. However, pure MOF film membranes are highly brittle and difficult to synthesize [28]. Consequently, MOFs based mixed matrix membranes have gained attention in the past few years as an alternative to improve on pure MOF film membranes. Yet, filler particle aggregation and interfacial defects are the major drawbacks that hinder the development of MOFs filler based MMMs. Due to accessible metals and ligands used in MOFs synthesis, modified structures can be tailored to enhance the interaction between MOF filler and polymer chains as well as provide exceptional physical and chemical properties [15]. Therefore, MOFs have become part of the selection of fillers for the development of MMMs for optimizing gas diffusion and selectivity.
The development of amine-functionalized MOFs mixed matrix membrane and hollow fiber mixed matrix membrane is potentially to be explored in gas separation. Incorporation of amine-functionalized MOFs into a polymer matrix are among the current efforts aimed to provide enhanced performance for CO2 gas separation. Therefore, this review aims to addresses recent trends in the use of amine-functionalized MOF in the fabrication of mixed matrix membrane for the improvement of gas separation performance of membranes, mainly on hollow fiber configuration. The challenges in the development of amine-functionalized MOFs based mixed matrix membranes for flat sheet and hollow fiber configurations will be highlighted.

2. Separation Mechanisms of Hollow Fiber Mixed Matrix Membranes

Gases passage through amine-functionalized MOF based hollow fiber mixed matrix membranes (HFMMMs) can incorporate several possible mechanisms such as solution diffusion [29], molecular sieving [30], and Knudsen diffusion [31,32] as shown in Figure 1.
The solution diffusion mechanism works in accordance with the solubility and diffusivity of the gas molecules in the polymer of the HFMMM. The gas molecule is initially absorbed into the polymer and diffusion in the polymer happens from a higher pressure or chemical gradient (upstream phase) and towards the lower gradient (downstream phase) before desorption from the polymer occurs [29]. Notably, the solution diffusion mechanism is the main mode of transportation for gas molecules. The separation process through the dense layer is quantified via permeability coefficient, P (cm3(STP)·cm/cm2·s·cmHg) measured in Barrer for flat sheet membranes, and permeance (cm3(STP)/cm2·s·cmHg) measured in GPU for hollow fiber configuration, a product between diffusivity coefficient, D (cm2/s), and solubility coefficient (cm3(STP)/cm3·cmHg). Undesirable interfacial defects may form surrounding the metal-organic framework (MOF) in the MMM due to the incompatibility between the MOF and the polymer [31] or surface delamination of the polymer chain during the composite membrane fabrication [26]. This can lead to a decrease in performance namely the gas pair selectivity of the membranes as the nanometer interfacial voids will allow larger gas molecules such as CH4 to easily pass through the membrane surface. This type of transport mechanism is known as Knudsen diffusion as shown in Figure 1. Amine-functionalized MOFs generally have an excellent interaction with polymer matrices therefore minimizing macrovoid formation on the membrane surface [33]. Molecular sieving is another method for gas transport to occur in MOFs whereby the gas molecules are separated based on the kinematic diameter of the gas molecule and the aperture size of the MOF particle matrix. The inability for larger kinetic diameter gases to pass through the smaller apertures of MOFs results in a molecular sieving being a highly selective mechanism for gas separation [30]. Yet, the study on the gas transport mechanism towards HFMMMs is still lacking and requires further research in order to accurately determine the various methods by which the gas molecules diffuse through the HFMMM layer compared with flat sheet configured membranes as well as how amine functionalization may enable better transport properties in HFMMMs.

3. Metal-Organic Framework Fillers

Metal-organic frameworks (MOFs) are porous materials constructed by using metal ions (or clusters) and organic linkers, which consolidate the features of both organic and inorganic components. There are a variety of MOFs constructed from diverse materials, and UiO-66 [34,35,36,37], MIL-53 [3,16,38,39], and ZIFs [40,41,42,43,44] are the type of MOFs which are commonly reported in the literature due to their exceptional properties which includes high porosity [45], large surface area, and variable pore size and apertures [46], fine tunable chemistry [25], and good thermo-chemical stability [47,48]. MOFs can also be synthesized in different sizes and dimensions from 0-D to three-dimensional by manipulating the ligands additives used and the reaction conditions [27].
Zr-based MOFs such as UiO-66 and UiO-67 (University of Oslo (UiO)) is created by oxo cluster nodes and linear dicarboxylate linkers [49]. UiO-66 is a zirconium-based MOF with the formula of Zr6O4(OH)4(-BDC)6, with a Langmuir surface area of 1187 m2/g, and thin triangular windows with an aperture size of 6.2 Ȧ [36,50]. Due to the zirconium metal center being connected to the BDC-linker (benzene-1,4-dicarboxylate), it allows UiO-66 to achieve a superior chemical and thermal stability. Meanwhile, MOF UiO-67(Zr) contains zirconium ions and biphenyl-4,4′-dicarboxylic acid. UiO-67 has an outstanding chemical stability, relatively large specific surface area, lower density, and microspore volume, with two types of cages including super-tetrahedral cages (11.5 Å) and super-octahedral cages (18.0 Å), with accessible microporous triangular window openings (8.0 Å) [51].
Materials Institute Lavoisier (MIL) is a type of MOF that is developed by connecting metal ions such as aluminum, chromium, and titanium, to organic linkers. MILs have been categorized on the basis on their distinguishable porous structure, which consists of different metallic ion clusters intimately connected with specific organic carboxylates, as well as their separate pore system and chemical composition, whilst numbers are names of MILs that represent specific structures with different metal ions and oxidation states [52]. Besides that, the aperture size of most MIL MOFs is larger than the kinetic diameter of H2 (2.9 Å), CO2 (3.3 Å), N2 (3.6 Å), and CH4 (3.8 Å) gas molecules [26,53].
MIL-53 (Al) is created by connecting aluminum-based octahedra AlO4(OH)2 with the 1,4-benzenedicarboxylate (BDC) ligand and has a chemical composition of Al(OH)(O2C-C6H4-CO2) [39,52]. MIL-53 is a three-dimensional porous structure with one-dimensional diamond-shaped channels [25,54]. MIL-101 (Cr) is composed of octahedral clusters of trimeric chromium (III) interconnected by 1,4-benzenedicarboxylates with the chemical formula of Cr3F(H2O)2OO2C-C6H4-CO23·nH2O [52,55]. On the other hand, a newly discovered titanium-based MIL-125 (Ti) MOF consists of 2 cage sizes of 6.1 Å and 12.6 Å with pore apertures of 6 Å, also possibly a smaller aperture when amine functionalization is introduced. The three-dimensional configuration of MIL-125 has octa-nuclear Ti-clusters which allows octahedral vacancies thus forming a quasi-cubic tetragonal structure with a chemical formula of (Ti8O8(OH)4[O2C-C6H4-CO2]6) [17,56].
Zeolitic imidazolate frameworks (ZIFs) are derived from zeolites but with tunable pore structures and higher thermal and chemical stability, therefore making them excellent sieving MOFs [42,43,57]. Common ZIF materials such as ZIF-7 and ZIF-8 are produced by varying the organic linkers of imidazolate ligands along with the metal ions present. ZIF-8 has large pores of up to 11.8 Å and a pore limiting diameter of 3.4 Å [2]. Moreover, ZIF-8 has a low hardness and elastic modulus, thus enabling it to have good elasticity among crystalline materials [37]. ZIF-7 has a hexagonal structure and is constructed by connecting zinc metal clusters with 1H-benzimidazole ligand to form a three-dimensional tetrahedral topological open framework [58]. The pore diameter of ZIF-7 ranges from 3.0 Å to 4.2 Å.
Besides that, copper (Cu)-based MOFs have also been highly researched on due to the potentially higher affinity for polar molecules compared with other metal organic frameworks because of the inclusion of unsaturated open metal sites [25]. For the MOF Cu3(BTC)2, it has a three-dimensional structure with small but highly electrostatic tetrahedron side pockets that have a pore size of 6 Å and cage sizes ranging from 10 Å to 12 Å. Furthermore, it also contains large but weak electrostatic square shaped channels connected by triangular windows of 3.5 Å diameter with the unsaturated Cu molecules being the center of the guest bindings [2,59]. On the other hand, Iron (Fe)-based MOFs are usually used to substitute Cu-based MOFs as iron is more reliable in toxic environments compared with copper [60]. Fe(BTC) MOF is comprised of iron trimeric octahedral clusters with similar vertex and removable H2O or OH ligands. Additionally, it contains two mesoporous cages with sizes of 25 Å and 29 Å and microporous windows of sizes 5.5 and 8.6 Å [60,61]. Table 1 shows the type of MOFs commonly reported in the literature and their structures.

4. Amine-Functionalized Metal-Organic Frameworks Fillers

Recently, MOFs are one of the most exciting materials for gas separation due to their distinct pore size and tunable functionalities. Incorporation of amine groups in MOFs was further developed because amine-functionalized MOFs exhibit higher affinity towards acidic gases such as CO2 and thus, are widely reported in the literature. Amine-functionalized MOFs contain several benefits which include: (i) highly selective gas adsorption properties and (ii) improved interaction between filler and polymer matrix for the formation of mixed matrix membranes. These amine-functionalized MOFs can be prepared mainly by three methods which are in situ synthesis, post-modification with amines, and physical mixing unfunctionalized MOFs and polyamines. Until now, grafting amines onto MOFs has been accomplished mainly by in situ synthesis with amine-containing ligands or through post-synthetic modification [69,70]. The various functionalization of MOFs are amine functions with ligands such as 2-amino-1,4-benzenedicarboxylate, 3-amino-1,2,4-triazole, and 4,4′,4′’-benzene-1,3,5-triyl-tribenzoic acid [70].
The inclusion of ligands containing additional functional moieties is not straightforward, because such groups may directly coordinate to the metal ions and therefore, inhibiting the MOF assembly depending on the reaction conditions used. An example of an amine-functionalized MOF is NH2-UiO-66. Due to the zirconium metal center being connected to the BDC-linker (benzene-1,4-dicarboxylate) with modifications with polar based functions such as with amino groups (-NH2), the NH2-UiO-66 is able to achieve a substantially higher chemical and thermal stability compared with the non-functionalized UiO-66 [35,47].
Furthermore, the supertetrahedral (ST) building blocks of MIL-101 (Cr) are generated by stiff terephthalate ligands. However, MIL-101’s existence of coordinatively unsaturated metal sites (CUSs) allows it to be used as a mild Lewis acid and, more importantly, to be post-functionalized through grafting of active species [71]. The functionalization of NH2-MIL-101(Al) can only be formed in specific synthesis conditions using solvothermal synthesis and using AlCl3 in DMF, where both the metal source and the solvent used play a key role, therefore achieving a higher thermal and chemical stability, high capacity and good regenerability [71]. Figure 2 shows the illustration of UiO-66, ZIF-8, and MIL-101 before and after amine functionalization, as well as the functionalization method. Generally, the pore size and surface area decrease after amine functionalization [72,73].

5. Amine-Functionalized Metal-Organic Frameworks Flat Sheet Mixed Matrix Membranes

Although MOFs based mixed matrix membrane (MMM) provides better separation performance, there are still a number of methods to be explored in order to enhance the MMMs’ performance such as the introduction of amine groups into the pore structure of MOFs which leads to the preferential adsorption of CO2 [17]. Apart from that, the presence of amine functional groups on the surface of the MOF crystals is considered beneficial to improve the compatibility between the dispersed filler material and the polymeric matrix, reducing interfacial defects between both phases which are known to be detrimental for the separation performance [79]. The advantages of the amine functionalization of MOFs in mixed matrix membrane for the separation of CO2/CH4 have been experimentally demonstrated in various studies reported in the literature [80,81]. MOFs are suitable as fillers for MMMs as most of their aperture sizes tend to be closer for the separation of CO2 which has a kinetic diameter of 3.3 Ȧ [47].
S. Meshkat et al. [38] incorporated MIL-53 and NH2-MIL-53 in poly(ether-b-amide) (PEBAX MH-1657) polymer for the fabrication of MMMs via a solution casting method for gas separation. Both the CO2 permeability and CO2/CH4 selectivity increased for MMM loaded with 10 wt% of filler. By increasing the filler loading up to 20 wt%, the permeability decreased significantly. They found that this result can be due to the formation of a rigid polymer layer around the MOF particles inside the matrix, the tortuosity introduced by the MOF, and MOF agglomeration leading to access restriction of gas molecules to a large portion of the porosity inside the matrix. Moreover, at filler loading of 10 wt%, the amine-functionalized NH2-MIL-53/PEBAX membrane demonstrated ideal selectivity of 20.5, which was lower than that of non-functionalized MIL-53/PEBAX membrane with an ideal selectivity of 23.3. This can be due to the presence of higher defects, formed in the membrane, possibly caused by the less compatibility between the amine-functionalized NH2-MIL-53 filler and PEBAX polymer. Guo et al. [82] tested NH2-MIL-125 (Ti)/PSf MMM at different operating pressures (3 and 10 bar). The CO2 permeability and CO2/CH4 selectivity increased as the loading of NH2-MIL-125 (Ti) increased at 3 bar. At pressure of 10 bar, the CO2 permeability increased as the loading of NH2-MIL-125 (Ti) increased but the CO2/CH4 selectivity showed a different trend. The increase in gas permeability was attributed to the extra pore network provided by the MOF particles for gas molecules while the reduction in selectivity at 10 bar indicated that the amine-functionalized membrane did not exhibit good resistance towards high pressure.
In another work, Waqas et al. [17] fabricated MIL-125/Matrimid and NH2-MIL-125/Matrimid for CO2 and CH4 gasses separation. They found that CO2 permeability increased as the filler loadings increased for both fillers, but the CO2/CH4 selectivity showed an opposite trend. Cross-sectional SEM images of the MMMs fabricated by Waqas et al. [17] are shown in Figure 3. Referring to Figure 3, the membrane displays little to no filler agglomeration for filler loadings of 5% and 15% which indicates that fillers and polymer have a good interaction. However, when the loading of fillers is increased to 30%, large filler agglomeration can be observed especially for NH2-MIL-125. Moreover, NH2-MIL-125/Matrimid MMMs exhibited a more significant increase in CO2 gas permeance compared with the MIL-125/Matrimid MMM by 85.18% while having similar CO2/CH4 gas pair selectivity at filler loading of 30%. The increase in gas permeation performance was possibly due to the good interaction between the amine-functionalized filler and the polymer because of the hydrogen bonding interaction between the -NH2 group at the filler surface and the polymer chains.
Meanwhile, Nik et al. [83] fabricated mixed matrix membranes by incorporating various MOFs including UiO-66 and MOF-199 with their amine-functionalized counterparts NH2-UiO-66 and NH2-MOF-199 into 6FDA-ODA polymer for the aim of determining the ligand functionalization effect (-NH2) on the adsorption properties and CO2/CH4 gas permeation and selectivity. Figure 4 shows the CO2 and CH4 adsorption isotherms of several types of MOFs at 35 °C based on the BET surface areas of the adsorbents. The adsorption isotherms shows that the amine-functionalized NH2-MOF-199 and NH2-UiO-66 have higher CO2 adsorption capacities compared with its non-functionalized counterparts. Cross-sectional SEM images of the UiO-66/6FDA-ODA and NH2-UiO-66/6FDA-ODA MMMs in Figure 5 shows that the amine-functionalized fillers were well-distributed in the 6FDA-ODA polymer matrix due to the presence of hydrogen bonding between -NH2 in the filler and carboxylic acid groups in the polymer chain. However, the interface between UiO-66 filler and the 6FDA–ODA polymer was found to have inferior quality. With the addition of the -NH2 group in NH2-UiO-66/6FDA–ODA, the filler/polymer interfacial interaction was shown to improve. For gas permeation performance, their results obtained for NH2-UiO-66/6FDA–ODA MMM showed a reduction in permeability by 5% and a massive 267% compared with the neat 6FDA–ODA and UiO-66/6FDA–ODA, respectively. Whereas, for the CO2/CH4 selectivity, the NH2-UiO-66/6FDA–ODA MMM demonstrated an increment by 17% and 18% compared with the neat 6FDA–ODA and UiO-66/6FDA–ODA, respectively.
Figure 6 summarizes the performance of several MMMs with different polymer-filler combinations into a Robeson plot. Table 2 summarizes the performances of the non-functionalized and amine-functionalized MOFs based mixed matrix membrane for CO2/CH4 separation. In most MMMs, amine-functionalized MMMs showed improved gas separation performance compared with MMM loaded with non-functionalized MOF.

6. Amine-Functionalized Metal-Organic Frameworks Hollow Fiber Mixed Matrix Membranes

Hollow fiber membranes (HFMs) are semipermeable cylindrical or capillary-shaped membranes with internal and exterior diameters of less than 0.25 mm and 1.00 mm, respectively. Hollow fiber configuration is more suitable for industrial gas separation due to their high surface to volume ratio and selectivity thus giving exceptional mass transfer properties for gas separations [86,87,88]. Hollow fiber mixed matrix membranes with a wide surface area and thin selective layers are recommended in most cases as the thickness of gas separation membranes is important [37,89]. To further enhance the performance of MMMs, incorporation of fillers into HFM configuration will form a hollow fiber mixed matrix membrane (HFMMM). HFMMMs have a significant advantage over conventional flat sheet membranes and hollow fiber membranes such as a better separation factor, mechanical strength, and thermal and chemical resistivity [90,91].

6.1. Hollow Fiber Mixed Matrix Membranes

Several advantages may be gained by incorporating high performance potential MMMs into a hollow fiber membrane configuration to generate HFMMMs. HFMMMs have a number of advantages over conventional flat sheet and hollow fiber membranes, including a higher separation factor, mechanical strength, and heat and chemical resistance [92]. Among the most popular methods currently utilized for the fabrication of HFMMMs which was first developed by Mahon at Dow Chemical in the 1960s is the solution spinning methods such as dry phase inversion spinning, wet phase inversion spinning, and dry-jet wet phase inversion spinning [93]. Figure 7 shows a spinning machine used for dry-jet wet phase inversion which is the most commonly used method to fabricate hollow fiber mixed matrix membranes for gas separation [94].
Sasikumar et al. [72] fabricated hollow fiber mixed matrix membranes (HFMMMs) which incorporated ZIF-8, S/ZIF-8, and amine-modified S/ZIF-8 (A@S/ZIF-8) of 0.5 wt% into polysulfone (PSf) matrix using a dry-wet phase inversion technique. Their research found that the addition of an amine group in the S/ZIF-8 MOF enhanced the interaction between the filler and PSf matrices, therefore improving the CO2/CH4 gas selectivity. The best performing HFMMM was achieved by the amine-functionalized A@S/ZIF-8 with a CO2 permeability of 41.15 GPU and CO2/CH4 selectivity of 22.25. The results show a selectivity increment of 61.46% compared with neat PSf hollow fiber membrane and 42.9% compared with ZIF-8/PSf HFMMM. They concluded that the facilitated CO2 transport with the amine group incorporated on the membrane results in increased membrane performance.
To date, there have not been sufficient works conducted on the use and comparison of HFMMMs before and after amine functionalization for gas separation despite the large potential it may have. Therefore, further efforts should be made focusing on this area for the investigation of amine-functionalized HFMMMs on gases separation.

6.2. Casting on PEBAX Thin Selective Layer

Thin layer composite membranes are formed by coating the outer layer of membrane surface with a selective layer and a highly permeable gutter layer [95]. PEBAX, which is a rubbery block copolymer containing Polyether oxide (PEO) segments, is used as the selective layer as it is reported to be high selective towards carbon dioxide [96]. The use of mixed matrix selective layer was first reported by Jia et al. in which they prepared a zeolite silicalite-1/PDMS selective layer on polyetherimide for O2 and N2 gases separation [97]. Thin layer composite membranes are preferred as they can manage large gas flux needs and are one of the most energy-efficient and industrially feasible CO2 capture possibilities [98].
Sutrisna et al. [37] incorporated UiO-66, UiO-66-NH2, UiO-66-(COOH)2, and ZIF-7 into a thin PEBAX selective layer on a PVDF support hollow fiber configuration as shown in Figure 8 with loadings from 30% for ZIF-7 and up to 80% for UiO-66. The choice of using a PEBAX/MOF selective layer instead of the conventional HFMMM fabrication was due to the PEBAX layering on the PVDF support provides a higher resistance towards plasticization. The CO2 and CH4 gas permeance and the CO2/CH4 selectivity was determined using pure gas. Hence, the best performing membrane was determined to be NH2-UiO-66/PEBAX with 50% loading giving a CO2 permeance of 320 GPU and CO2/CH4 gas pair selectivity of 23 at pressures of 2 bar. These results show an increase in 45% and 44% for the gas permeation and selectivity, respectively, compared with the non-amine functionalized UiO-66. This is possibly due to the addition of amine groups on the organic ligands which boosted UiO-66-NH2 selective CO2 absorption, resulting in greater CO2 solubility inside the PEBAX layer. The research also discovered that by adding nanoparticles into PEBAX polymer, the rigidity of the polymer increased due to the presence of more hydrogen bonds. The more rigid PEBAX polymer is preferred as it retains the molecular sieving capabilities. Table 3 shows the performances of non-functionalized and amine-functionalized MOFs based hollow fiber mixed matrix membrane for CO2/CH4 separation.

7. Challenges in Development of Amine-Functionalized Metal-Organic Frameworks (MOFs) Hollow Fiber Mixed Matrix Membranes

With the high rate of progress in the development of MOFs as fillers in HFMMM fabrication, most commercial polymers can be potentially superseded by HFMMMs due to them being a superior membrane-based gas separation technology with a larger surface area, and tunable functionalities including amine functionalities. While numerous studies and research have been conducted to overcome the initial challenges for developing HFMMMs, several challenges are still present when developing HFMMMs for the use of gas separation such as polymer-filler incompatibility, filler particle agglomeration, and plasticization which can hinder the separation performance of the membrane [9,32,101].

7.1. Polymer-Filler Interfacial Incompatibility

Compatibility between a filler with the polymer matrix is a key factor in the development of HFMMMs. Careful material selection is required for a compatible polymer-filler interaction [23,102]. Moreover, certain MMMs such as those based on zeolite type fillers tend to have poor adhesion between the polymer and filler which leads to void defects formed on the material interface causing gas molecules to non-selectively diffuse through the voids therefore reducing the separation performance of the membrane [103]. The causes of interfacial incompatibility are the dewetting of the polymer at the interface and differences in mechanical properties between components, particularly for glassy polymers. However, when rubbery polymers are utilized, the polymer phase can obstruct the porosity of MOFs through pore infiltration, therefore limiting the MOF’s molecular sieving capabilities [90,104]. Figure 9 shows the various cases HFMMMs may experience depending on the compatibility of the filler and the polymer matrix. Case 1 is an ideal condition in which the filler is completely integrated into the polymer matrix with no sign of incompatibility. In Case 2, the polymer matrix becomes rigid in the vicinity of the filler which leads in an increase in selectivity, but also in a decrease in permeability. Case 3 shows the formation of an interphase as a result of the particle’s incompatibility with the polymer matrix which leads to an increase in permeability and a decrease in selectivity as a result of the larger fractional free volume. Finally, in Case 4, polymer matrix penetrates the pores or empty spaces of the filler; therefore, both the permeability and the selectivity decrease significantly [105].
Various methods can be used to counteract the incompatibility and pore blockage challenges such as through careful material selection consideration between the polymer matrix and MOF filler since performance improvements are only present when the polymer-filler compatibility is achieved [106]. Besides that, the incorporation of amine-functionalized groups into organic MOF linkers increases compatibility due to the presence of more hydrogen bonding with the hydroxyl groups present in polymer interface [79,107].

7.2. Agglomeration of Fillers

MOF loading also presents an important factor to consider when developing MMMs as higher filler loading will cause the gas transport to be more based on the MOF’s transport mechanism which can potentially provide a larger separation performance. Although, a higher MOF loading can cause a severe issue in the form of filler agglomeration [32]. The formation of particle agglomeration in MMMs are undesirable because it will cause pinhole defects, which reduce the membrane gas performance by affecting the selectivity of the gases [108]. Therefore, this results in a trade-off between the MOF loading and the gas pair selectivity of the MMM. To increase the MOF loading tolerance, physical priming can be performed on MOF surfaces. Physical priming is the deposition of the polymer dope solution on the MOF surface covalently thus allowing adhesion between the polymer and filler to increase which consequently increases the polymer-filler compatibility [32]. Figure 10 shows the cross-sectional and outer surface SEM images of PEBAX® 2533-NH2-UiO-66/PP thin film HFMMM with the presence of severe agglomerations found as the NH2-UiO-66 loading increases to 20.0 wt% and 50.0 wt% based on the works by Li et al. [73]. They determined that with the severe agglomeration led to a decrease in CO2/N2 ideal selectivity and a 9% increase in CO2 permeance compared with the neat PEBAX® 2533 membranes.
Therefore, there are also a number of aspects by which particle agglomeration may occur which includes: (1) larger MOF filler size, (2) MOF interparticle interaction whereby the MOF to MOF interaction is stronger than MOFs to the polymer, and (3) fabrication conditions [109]. Additionally, the dispersion of the fillers into the polymer is essential to promote good polymer-filler interactions. The dispersion of the fillers however is affected by the MOF’s size, geometry, and surface chemistry [32]. Therefore, by adjusting these parameters, an optimized MOF can be produced for MMM development. The size and geometry of the MOF can be altered by manipulating the synthesize conditions such as NH2-MIL-101(Al) which can be formed under very specific synthesis conditions, where both the metal source and the solvent used perform a key role [71], or by utilizing nanosized MOF fillers. While the surface chemistry of MOFs can be tuned using modification such as amine functionalization [36].

7.3. Plasticization

The organic polymer matrix acts as the continuous phase in HFMMMs and they too can suffer from certain limitations such as plasticization. The incorporation of MOF fillers into the polymer matrix does reduce the effects of plasticization as the presence of sufficient filler loading is able to limit the polymer chain mobility. This potentially allows certain HFMMM with strong polymer-filler interactions to be able to withstand plasticization effects at high pressures of up to 20 bar [25]. However, due to the large percent of polymer present compared with MOFs, plasticization remains a challenge when fabricating HFMMMs with organic polymers. Plasticization can be defined as a phenomenon that arises when the concentration of a strong sorbing gas such as CO2 in a polymer matrix increases, causing the polymer to swell and raise the diffusion coefficients of all gases present, resulting in a drop in selectivity [110]. When plasticization occurs, usually at high pressures, the gas permeability for all gases increases significantly.
Through the introduction of amine-functionalized MOFs into the polymer matrix, plasticization effects may be reduced. In the works conducted by Rajati et al. [111], they found that by increasing the loading of NH2-MIL-101 (Cr) up to 7 wt% led to a higher resistance for the Matrimid polymer to plasticize, from 12 bar in the neat Matrimid to 26 bar. This can be explained by the increase in resistance in the Matrimid chain mobility with the introduction of NH2-MIL-101 in the polymer matrix as the amine functional groups form strong hydrogen bonds that make the polymer more rigid and resistant to plasticization [111].

8. Conclusions and Future Directions

Mixed matrix membranes (MMMs) in hollow fiber configuration show great potential application in gas separation; however, the significant problems such as low compatibility and poor adhesion between the inorganic and polymer materials resulted in the creation of imperfect void structures and pinholes and which deteriorates the properties of the membrane. As a result, metal-organic framework (MOF)-based MMMs have gained attention in the past few years. Although MOF-based MMMs provide better gas separation performance compared with the other fillers, new methods to further enhance the gas separation performances are required due to certain limitations of the MOFs. Therefore, introducing amino functional groups on the surface of the MOF crystals is considered beneficial to improve the interaction between polymer matrices and the filler. This will prevent the formation of voids at the polymer-filler interface.
A comprehensive review reveals that amine-functionalized MOFs based MMMs for gas separation evidently showed that research in this field has grown intensely over the past few years due to its high potential in gas separation, but multiple challenges faced by the membranes hinder the possibly higher performance. By incorporating amine-functionalized MOFs into polymer matrix, it demonstrated advantages in gases separation. However, the compatibility between amine-functionalized MOFs and polymer as well as against reproducibility and stability of membrane performance are still needed to be addressed. Next, the parameters of fabrication also should be concerned in order to reduce the potential of agglomeration which can affect the performance of membrane. Besides that, hollow fiber mixed matrix membranes (HFMMMs) have a higher potential to surpass many of the shortcomings faced by conventional flat sheet MMMs due to its higher surface to volume ratio and better industrial applicability, yet in the field of CO2 gas separation, it is still relatively new and rarely explored. In the future, further research on amine-functionalized MOFs based MMMs and HFMMMs should be explored in order to fabricate the resultant membranes with minimal defects to provide higher performance in terms of permeability and selectivity under various operating conditions, particularly high pressure, before they are scaled up for industrial applications.

Author Contributions

N.S.: Formal analysis, Investigation, Data curation, Writing-original draft, Visualization. Y.Y.F.: Conceptualization, Validation, Resources, Writing—review & Editing, Supervision, Funding acquisition, Project administration. M.A.B.: Conceptualization, Resources, Supervision. N.H.S.: Visualization, Writing—original draft, Investigation. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by YUTP research grant, cost center 015LCO-099.

Informed Consent Statement

Not applicable.

Acknowledgments

The financial and technical supports provided by Yayasan Universiti Teknologi PETRONAS (YUTP) Research Grant (Cost Center: 015LC0-099) and CO2 Research Centre, Universiti Teknologi PETRONAS are duly acknowledged.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Jusoh, N.; Yeong, Y.F.; Lau, K.K.; Shariff, A.M. Fabrication of silanated zeolite T/6FDA-durene composite membranes for CO2/CH4 separation. J. Clean. Prod. 2017, 166, 1043–1058. [Google Scholar] [CrossRef]
  2. Basu, S.; Odena, A.; Vankelecom, I.F. MOF-containing mixed-matrix membranes for CO2/CH4 and CO2/N2 binary gas mixture separations. Sep. Purif. Technol. 2011, 81, 31–40. [Google Scholar] [CrossRef]
  3. Perez, E.V.; Kalaw, G.J.; Ferraris, J.P.; Balkus, K.J.; Musselman, I.H. Amine-functionalized (Al) MIL-53/VTEC™ mixed-matrix membranes for H2/CO2 mixture separations at high pressure and high temperature. J. Membr. Sci. 2017, 530, 201–212. [Google Scholar] [CrossRef] [Green Version]
  4. Ahmed, S.; Ramli, A.; Yusup, S. CO2 adsorption study on primary, secondary and tertiary amine functionalized Si-MCM-41. Int. J. Greenh. Gas Control 2016, 51, 230–238. [Google Scholar] [CrossRef]
  5. Peters, L.; Hussain, A.; Follmann, M.; Melin, T.; Hägg, M.-B. CO2 removal from natural gas by employing amine absorption and membrane technology—A technical and economical analysis. Chem. Eng. J. 2011, 172, 952–960. [Google Scholar] [CrossRef]
  6. Carreon, M.A. Molecular sieve membranes for N2/CH4 separation. J. Mater. Res. 2018, 33, 32–43. [Google Scholar] [CrossRef] [Green Version]
  7. Zhang, Y.; Sunarso, J.; Liu, S.; Wang, R. Current status and development of membranes for CO2/CH4 separation: A review. Int. J. Greenh. Gas Control. 2013, 12, 84–107. [Google Scholar] [CrossRef]
  8. Rufford, T.; Smart, S.; Watson, G.; Graham, B.; Boxall, J.; da Costa, J.C.D.; May, E. The removal of CO2 and N2 from natural gas: A review of conventional and emerging process technologies. J. Pet. Sci. Eng. 2012, 94-95, 123–154. [Google Scholar] [CrossRef]
  9. Zhang, Y.; Feng, X.; Yuan, S.; Zhou, J.; Wang, B. Challenges and recent advances in MOF–polymer composite membranes for gas separation. Inorg. Chem. Front. 2016, 3, 896–909. [Google Scholar] [CrossRef]
  10. Jusoh, N.; Yeong, Y.F.; Chew, T.L.; Lau, K.K.; Shariff, A.M. Current Development and Challenges of Mixed Matrix Membranes for CO2/CH4 Separation. Sep. Purif. Rev. 2016, 45, 321–344. [Google Scholar] [CrossRef]
  11. Farnam, M.; Mukhtar, H.; Shariff, A.M. Analysis of the Influence of CMS Variable Percentages on Pure PES Membrane Gas Separation Performance. Procedia Eng. 2016, 148, 1206–1212. [Google Scholar] [CrossRef] [Green Version]
  12. Mushardt, H.; Müller, M.; Shishatskiy, S.; Wind, J.; Brinkmann, T. Detailed Investigation of Separation Performance of a MMM for Removal of Higher Hydrocarbons under Varying Operating Conditions. Membranes 2016, 6, 16. [Google Scholar] [CrossRef] [PubMed]
  13. Chen, X.Y.; Vinh-Thang, H.; Rodrigue, D.; Kaliaguine, S. Amine-Functionalized MIL-53 Metal–Organic Framework in Polyimide Mixed Matrix Membranes for CO2/CH4 Separation. Ind. Eng. Chem. Res. 2012, 51, 6895–6906. [Google Scholar] [CrossRef]
  14. Qiao, Z.; Wang, N.; Jiang, J.; Zhou, J. Design of amine-functionalized metal–organic frameworks for CO2 separation: The more amine, the better? Chem. Commun. 2016, 52, 974–977. [Google Scholar] [CrossRef] [Green Version]
  15. Zhu, H.; Jie, X.; Cao, Y. Fabrication of Functionalized MOFs Incorporated Mixed Matrix Hollow Fiber Membrane for Gas Separation. J. Chem. 2017, 2017, 1–9. [Google Scholar] [CrossRef]
  16. Hsieh, J.O.; Balkus, K.J.; Ferraris, J.P.; Musselman, I.H. MIL-53 frameworks in mixed-matrix membranes. Microporous Mesoporous Mater. 2014, 196, 165–174. [Google Scholar] [CrossRef]
  17. Anjum, M.W.; Bueken, B.; De Vos, D.; Vankelecom, I.F. MIL-125(Ti) based mixed matrix membranes for CO2 separation from CH4 and N2. J. Membr. Sci. 2016, 502, 21–28. [Google Scholar] [CrossRef]
  18. Ploegmakers, J.; Japip, S.; Nijmeijer, K. Mixed matrix membranes containing MOFs for ethylene/ethane separation Part A: Membrane preparation and characterization. J. Membr. Sci. 2013, 428, 445–453. [Google Scholar] [CrossRef]
  19. Friebe, S.; Diestel, L.; Knebel, A.; Wollbrink, A.; Caro, J. MOF-Based Mixed-Matrix Membranes in Gas Separation-Mystery and Reality. Chem. Ing. Tech. 2016, 88, 1788–1797. [Google Scholar] [CrossRef]
  20. Pal, N.; Agarwal, M. Advances in materials process and separation mechanism of the membrane towards hydrogen separation. Int. J. Hydrog. Energy 2021, 46, 27062–27087. [Google Scholar] [CrossRef]
  21. Galizia, M.; Chi, W.S.; Smith, Z.P.; Merkel, T.C.; Baker, R.W.; Freeman, B.D. 50th Anniversary Perspective: Polymers and Mixed Matrix Membranes for Gas and Vapor Separation: A Review and Prospective Opportunities. Macromolecules 2017, 50, 7809–7843. [Google Scholar] [CrossRef]
  22. Ismail, A.; Goh, P.; Sanip, S.; Aziz, M. Transport and separation properties of carbon nanotube-mixed matrix membrane. Sep. Purif. Technol. 2009, 70, 12–26. [Google Scholar] [CrossRef]
  23. Dong, G.; Li, H.; Chen, V. Challenges and opportunities for mixed-matrix membranes for gas separation. J. Mater. Chem. A 2013, 1, 4610–4630. [Google Scholar] [CrossRef]
  24. Cong, H.; Radosz, M.; Towler, B.F.; Shen, Y. Polymer–inorganic nanocomposite membranes for gas separation. Sep. Purif. Technol. 2007, 55, 281–291. [Google Scholar] [CrossRef]
  25. Ahmadi, M.; Janakiram, S.; Dai, Z.; Ansaloni, L.; Deng, L. Performance of Mixed Matrix Membranes Containing Porous Two-Dimensional (2D) and Three-Dimensional (3D) Fillers for CO2 Separation: A Review. Membranes 2018, 8, 50. [Google Scholar] [CrossRef] [Green Version]
  26. Buddin, M.S.; Ahmad, A. A review on metal-organic frameworks as filler in mixed matrix membrane: Recent strategies to surpass upper bound for CO2 separation. J. CO2 Util. 2021, 51, 101616. [Google Scholar] [CrossRef]
  27. Meng, L.; Yu, B.; Qin, Y. Templated interfacial synthesis of metal-organic framework (MOF) nano- and micro-structures with precisely controlled shapes and sizes. Commun. Chem. 2021, 4, 82. [Google Scholar] [CrossRef]
  28. Denny, M.S., Jr.; Moreton, J.C.; Benz, L.; Cohen, S. Metal–organic frameworks for membrane-based separations. Nat. Rev. Mater. 2016, 1, 16078. [Google Scholar] [CrossRef]
  29. Han, Y.; Ho, W.W. Recent advances in polymeric membranes for CO2 capture. Chin. J. Chem. Eng. 2018, 26, 2238–2254. [Google Scholar] [CrossRef]
  30. Shi, Y.; Liang, B.; Lin, R.-B.; Zhang, C.; Chen, B. Gas Separation via Hybrid Metal–Organic Framework/Polymer Membranes. Trends Chem. 2020, 2, 254–269. [Google Scholar] [CrossRef]
  31. Feng, C.; Khulbe, K.; Matsuura, T.; Farnood, R.; Ismail, A. Recent Progress in Zeolite/Zeotype Membranes. J. Membr. Sci. Res. 2015, 1, 49–72. [Google Scholar]
  32. Qian, Q.; Asinger, P.A.; Lee, M.J.; Han, G.; Rodriguez, K.M.; Lin, S.; Benedetti, F.M.; Wu, A.X.; Chi, W.S.; Smith, Z.P. MOF-Based Membranes for Gas Separations. Chem. Rev. 2020, 120, 8161–8266. [Google Scholar] [CrossRef] [PubMed]
  33. Sabetghadam, A.; Seoane, B.; Keskin, D.; Duim, N.; Rodenas, T.; Shahid, S.; Sorribas, S.; Le Guillouzer, C.; Clet, G.; Tellez, C.; et al. Metal Organic Framework Crystals in Mixed-Matrix Membranes: Impact of the Filler Morphology on the Gas Separation Performance. Adv. Funct. Mater. 2016, 26, 3154–3163. [Google Scholar] [CrossRef]
  34. Luu, C.L.; Van Nguyen, T.T.; Nguyen, T.; Hoang, T.C. Synthesis, characterization and adsorption ability of UiO-66-NH 2. Adv. Nat. Sci. Nanosci. Nanotechnol. 2015, 6, 025004. [Google Scholar] [CrossRef] [Green Version]
  35. Biswas, S.; Van Der Voort, P. A General Strategy for the Synthesis of Functionalised UiO-66 Frameworks: Characterisation, Stability and CO2 Adsorption Properties. Eur. J. Inorg. Chem. 2013, 2013, 2154–2160. [Google Scholar] [CrossRef]
  36. Anjum, M.W.; Vermoortele, F.; Khan, A.L.; Bueken, B.; De Vos, D.E.; Vankelecom, I.F.J. Modulated UiO-66-Based Mixed-Matrix Membranes for CO2 Separation. ACS Appl. Mater. Interfaces 2015, 7, 25193–25201. [Google Scholar] [CrossRef]
  37. Sutrisna, P.D.; Hou, J.; Zulkifli, M.Y.; Li, H.; Zhang, Y.; Liang, W.; D’Alessandro, D.M.; Chen, V. Surface functionalized UiO-66/Pebax-based ultrathin composite hollow fiber gas separation membranes. J. Mater. Chem. A 2018, 6, 918–931. [Google Scholar] [CrossRef]
  38. Meshkat, S.; Kaliaguine, S.; Rodrigue, D. Mixed matrix membranes based on amine and non-amine MIL-53(Al) in Pebax® MH-1657 for CO2 separation. Sep. Purif. Technol. 2018, 200, 177–190. [Google Scholar] [CrossRef]
  39. Mao, H.; Li, S.-H.; Zhang, A.-S.; Xu, L.-H.; Lu, H.-X.; Lv, J.; Zhao, Z.-P. Furfural separation from aqueous solution by pervaporation membrane mixed with metal organic framework MIL-53(Al) synthesized via high efficiency solvent-controlled microwave. Sep. Purif. Technol. 2021, 272, 118813. [Google Scholar] [CrossRef]
  40. Gong, X.; Wang, Y.; Kuang, T. ZIF-8-Based Membranes for Carbon Dioxide Capture and Separation. ACS Sustain. Chem. Eng. 2017, 5, 11204–11214. [Google Scholar] [CrossRef]
  41. Jusoh, N.; Yeong, Y.F.; Lau, K.K.; Shariff, A.M. Transport properties of mixed matrix membranes encompassing zeolitic imidazolate framework 8 (ZIF-8) nanofiller and 6FDA-durene polymer: Optimization of process variables for the separation of CO2 from CH4. J. Clean. Prod. 2017, 149, 80–95. [Google Scholar] [CrossRef]
  42. Etxeberria-Benavides, M.; David, O.; Johnson, T.; Łozińska, M.M.; Orsi, A.; Wright, P.A.; Mastel, S.; Hillenbrand, R.; Kapteijn, F.; Gascon, J. High performance mixed matrix membranes (MMMs) composed of ZIF-94 filler and 6FDA-DAM polymer. J. Membr. Sci. 2018, 550, 198–207. [Google Scholar] [CrossRef] [Green Version]
  43. Gao, J.; Mao, H.; Jin, H.; Chen, C.; Feldhoff, A.; Li, Y. Functionalized ZIF-7/Pebax® 2533 mixed matrix membranes for CO2/N2 separation. Microporous Mesoporous Mater. 2020, 297, 110030. [Google Scholar] [CrossRef]
  44. Zagho, M.M.; Hassan, M.K.; Khraisheh, M.; Al-Maadeed, M.A.A.; Nazarenko, S. A review on recent advances in CO2 separation using zeolite and zeolite-like materials as adsorbents and fillers in mixed matrix membranes (MMMs). Chem. Eng. J. Adv. 2021, 6, 100091. [Google Scholar] [CrossRef]
  45. Lin, R.; Ge, L.; Hou, L.; Strounina, E.; Rudolph, V.; Zhu, Z. Mixed Matrix Membranes with Strengthened MOFs/Polymer Interfacial Interaction and Improved Membrane Performance. ACS Appl. Mater. Interfaces 2014, 6, 5609–5618. [Google Scholar] [CrossRef]
  46. Liang, X.-X.; Wang, N.; Qu, Y.-L.; Yang, L.-Y.; Wang, Y.-G.; Ouyang, X.-K. Facile Preparation of Metal-Organic Framework (MIL-125)/Chitosan Beads for Adsorption of Pb(II) from Aqueous Solutions. Mol. 2018, 23, 1524. [Google Scholar] [CrossRef] [Green Version]
  47. Vinoba, M.; Bhagiyalakshmi, M.; Alqaheem, Y.; Alomair, A.A.; Pérez, A.; Rana, M.S. Recent progress of fillers in mixed matrix membranes for CO2 separation: A review. Sep. Purif. Technol. 2017, 188, 431–450. [Google Scholar] [CrossRef]
  48. Erucar, I.; Yilmaz, G.; Keskin, S. Recent Advances in Metal-Organic Framework-Based Mixed Matrix Membranes. Chem.-Asian J. 2013, 8, 1692–1704. [Google Scholar] [CrossRef]
  49. Vahabi, A.H.; Norouzi, F.; Sheibani, E.; Rahimi-Nasrabadi, M. Functionalized Zr-UiO-67 metal-organic frameworks: Structural landscape and application. Co-ord. Chem. Rev. 2021, 445, 214050. [Google Scholar] [CrossRef]
  50. Guo, H.; Liu, J.; Li, Y.; Caro, J.; Huang, A. Post-synthetic modification of highly stable UiO-66-NH2 membranes on porous ceramic tubes with enhanced H2 separation. Microporous Mesoporous Mater. 2021, 313, 110823. [Google Scholar] [CrossRef]
  51. Ma, W.; Yang, J.; He, F.; Zhang, H.; Li, X.; Zhang, H. Combination of heteropolyacid and UiO-67 (Zr) to generate heterogeneous nanocomposite catalyst for efficient oxidative desulfurization system. Inorg. Chem. Commun. 2021, 136, 109143. [Google Scholar] [CrossRef]
  52. Khan, S.; Guan, Q.; Liu, Q.; Qin, Z.; Rasheed, B.; Liang, X.; Yang, X. Synthesis, modifications and applications of MILs Metal-organic frameworks for environmental remediation: The cutting-edge review. Sci. Total Environ. 2021, 810, 152279. [Google Scholar] [CrossRef] [PubMed]
  53. Valero, M.; Zornoza, B.; Téllez, C.; Coronas, J. Mixed matrix membranes for gas separation by combination of silica MCM-41 and MOF NH2-MIL-53(Al) in glassy polymers. Microporous Mesoporous Mater. 2014, 192, 23–28. [Google Scholar] [CrossRef]
  54. Zhu, H.; Jie, X.; Wang, L.; Kang, G.; Liu, D.; Cao, Y. Effect of MIL-53 on phase inversion and gas separation performance of mixed matrix hollow fiber membranes. RSC Adv. 2016, 6, 69124–69134. [Google Scholar] [CrossRef]
  55. Ahmadipouya, S.; Ahmadijokani, F.; Molavi, H.; Rezakazemi, M.; Arjmand, M. CO2/CH4 separation by mixed-matrix membranes holding functionalized NH2-MIL-101(Al) nanoparticles: Effect of amino-silane functionalization. Chem. Eng. Res. Des. 2021, 176, 49–59. [Google Scholar] [CrossRef]
  56. Sun, Y.; Song, C.; Guo, X.; Hong, S.; Choi, J.; Liu, Y. Microstructural optimization of NH2-MIL-125 membranes with superior H2/CO2 separation performance by innovating metal sources and heating modes. J. Membr. Sci. 2020, 616, 118615. [Google Scholar] [CrossRef]
  57. Suhaimi, N.H.; Yeong, Y.F.; Ch’Ng, C.W.M.; Jusoh, N. Tailoring CO2/CH4 Separation Performance of Mixed Matrix Membranes by Using ZIF-8 Particles Functionalized with Different Amine Groups. Polym. 2019, 11, 2042. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  58. Li, Y.; Liang, F.; Bux, H.; Yang, W.; Caro, J. Zeolitic imidazolate framework ZIF-7 based molecular sieve membrane for hydrogen separation. J. Membr. Sci. 2010, 354, 48–54. [Google Scholar] [CrossRef]
  59. Keskin, S.; Liu, J.; Johnson, J.K.; Sholl, D.S. Atomically detailed models of gas mixture diffusion through CuBTC membranes. Microporous Mesoporous Mater. 2009, 125, 101–106. [Google Scholar] [CrossRef]
  60. Shahid, S.; Nijmeijer, K. High pressure gas separation performance of mixed-matrix polymer membranes containing mesoporous Fe(BTC). J. Membr. Sci. 2014, 459, 33–44. [Google Scholar] [CrossRef]
  61. Maihom, T.; Choomwattana, S.; Wannakao, S.; Probst, M.; Limtrakul, J. Ethylene Epoxidation with Nitrous Oxide over Fe-BTC Metal-Organic Frameworks: A DFT Study. ChemPhysChem 2016, 17, 3416–3422. [Google Scholar] [CrossRef] [PubMed]
  62. Syzgantseva, M.A.; Ireland, C.P.; Ebrahim, F.M.; Smit, B.; Syzgantseva, O.A. Metal Substitution as the Method of Modifying Electronic Structure of Metal–Organic Frameworks. J. Am. Chem. Soc. 2019, 141, 6271–6278. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  63. Kholdeeva, O.; Maksimchuk, N. Metal-Organic Frameworks in Oxidation Catalysis with Hydrogen Peroxide. Catalysts 2021, 11, 283. [Google Scholar] [CrossRef]
  64. Li, L.; Xiang, S.; Cao, S.; Zhang, J.; Ouyang, G.; Chen, L.; Su, C.-Y. A synthetic route to ultralight hierarchically micro/mesoporous Al(III)-carboxylate metal-organic aerogels. Nat. Commun. 2013, 4, 1774. [Google Scholar] [CrossRef] [Green Version]
  65. Jouyandeh, M.; Tikhani, F.; Shabanian, M.; Movahedi, F.; Moghari, S.; Akbari, V.; Gabrion, X.; Laheurte, P.; Vahabi, H.; Saeb, M.R. Synthesis, characterization, and high potential of 3D metal–organic framework (MOF) nanoparticles for curing with epoxy. J. Alloy. Compd. 2020, 829, 154547. [Google Scholar] [CrossRef]
  66. Ryder, M.; Civalleri, B.; Bennett, T.; Henke, S.; Rudic, S.; Cinque, G.; Fernandez-Alonso, F.; Tan, J.-C. Identifying the Role of Terahertz Vibrations in Metal-Organic Frameworks: From Gate-Opening Phenomenon to Shear-Driven Structural Destabilization. Phys. Rev. Lett. 2014, 113, 215502. [Google Scholar] [CrossRef] [Green Version]
  67. Anbu, N.; Dhakshinamoorthy, A. Cu3(BTC)2 metal-organic framework catalyzed N-arylation of benzimidazoles and imidazoles with phenylboronic acid. J. Ind. Eng. Chem. 2018, 65, 120–126. [Google Scholar] [CrossRef]
  68. Liu, C.; Yu, L.-Q.; Zhao, Y.-T.; Lv, Y.-K. Recent advances in metal-organic frameworks for adsorption of common aromatic pollutants. Mikrochim. Acta 2018, 185, 342. [Google Scholar] [CrossRef]
  69. Yuan, B.; Ma, D.; Wang, X.; Li, Z.; Li, Y.; Liu, H.; He, D. A microporous, moisture-stable, and amine-functionalized metal–organic framework for highly selective separation of CO2 from CH4. Chem. Commun. 2012, 48, 1135–1137. [Google Scholar] [CrossRef] [Green Version]
  70. Lin, Y.; Kong, C.; Chen, L. Amine-functionalized metal–organic frameworks: Structure, synthesis and applications. RSC Adv. 2016, 6, 32598–32614. [Google Scholar] [CrossRef]
  71. Serra-Crespo, P.; Ramos-Fernandez, E.V.; Gascon, J.; Kapteijn, F. Synthesis and Characterization of an Amino Functionalized MIL-101(Al): Separation and Catalytic Properties. Chem. Mater. 2011, 23, 2565–2572. [Google Scholar] [CrossRef]
  72. Sasikumar, B.; Bisht, S.; Arthanareeswaran, G.; Ismail, A.; Othman, M. Performance of polysulfone hollow fiber membranes encompassing ZIF-8, SiO2/ZIF-8, and amine-modified SiO2/ZIF-8 nanofillers for CO2/CH4 and CO2/N2 gas separation. Sep. Purif. Technol. 2021, 264, 118471. [Google Scholar] [CrossRef]
  73. Li, G.; Kujawski, W.; Knozowska, K.; Kujawa, J. Thin Film Mixed Matrix Hollow Fiber Membrane Fabricated by Incorporation of Amine Functionalized Metal-Organic Framework for CO2/N2 Separation. Mater. 2021, 14, 3366. [Google Scholar] [CrossRef]
  74. Shen, J.; Liu, G.; Huang, K.; Li, Q.; Guan, K.; Li, Y.; Jin, W. UiO-66-polyether block amide mixed matrix membranes for CO2 separation. J. Membr. Sci. 2016, 513, 155–165. [Google Scholar] [CrossRef]
  75. Trickett, C.A.; Gagnon, K.J.; Lee, S.; Gándara, F.; Bürgi, H.-B.; Yaghi, O.M. Definitive Molecular Level Characterization of Defects in UiO-66 Crystals. Angew. Chem. Int. Ed. 2015, 54, 11162–11167. [Google Scholar] [CrossRef]
  76. Raza, A.; Japip, S.; Liang, C.Z.; Farrukh, S.; Hussain, A.; Chung, T.-S. Novel Cellulose Triacetate (CTA)/Cellulose Diacetate (CDA) Blend Membranes Enhanced by Amine Functionalized ZIF-8 for CO2 Separation. Polymers 2021, 13, 2946. [Google Scholar] [CrossRef]
  77. Trung, T.K.; Ramsahye, N.A.; Trens, P.; Tanchoux, N.; Serre, C.; Fajula, F.; Férey, G. Adsorption of C5–C9 hydrocarbons in microporous MOFs MIL-100(Cr) and MIL-101(Cr): A manometric study. Microporous Mesoporous Mater. 2010, 134, 134–140. [Google Scholar] [CrossRef]
  78. Almasi, M.; Zeleňák, V.; Palotai, P.; Beňová, E.; Zelenakova, A. Metal-organic framework MIL-101(Fe)-NH 2 functionalized with different long-chain polyamines as drug delivery system. Inorg. Chem. Commun. 2018, 93, 115–120. [Google Scholar] [CrossRef]
  79. Rodenas, T.; van Dalen, M.; Crespo, P.S.; Kapteijn, F.; Gascon, J. Mixed matrix membranes based on NH2-functionalized MIL-type MOFs: Influence of structural and operational parameters on the CO2/CH4 separation performance. Microporous Mesoporous Mater. 2014, 192, 35–42. [Google Scholar] [CrossRef]
  80. Suhaimi, N.H.; Yeong, Y.F.; Jusoh, N.; Chew, T.L.; Bustam, M.A.; Suleman, S. Separation of CO2 from CH4 using mixed matrix membranes incorporated with amine functionalized MIL-125 (Ti) nanofiller. Chem. Eng. Res. Des. 2020, 159, 236–247. [Google Scholar] [CrossRef]
  81. Suhaimi, N.H.; Yeong, Y.F.; Jusoh, N.; Asri, M.F.M. Amine-Functionalized Metal Organic Framework (MOF)/6FDA-Durene Composite Membranes for CO2 Removal from CH4. Mater. Today: Proc. 2019, 19, 1730–1737. [Google Scholar] [CrossRef]
  82. Guo, X.; Huang, H.; Ban, Y.; Yang, Q.; Xiao, Y.; Li, Y.; Yang, W.; Zhong, C. Mixed matrix membranes incorporated with amine-functionalized titanium-based metal-organic framework for CO2/CH4 separation. J. Membr. Sci. 2015, 478, 130–139. [Google Scholar] [CrossRef]
  83. Nik, O.G.; Chen, X.Y.; Kaliaguine, S. Functionalized metal organic framework-polyimide mixed matrix membranes for CO2/CH4 separation. J. Membr. Sci. 2012, 413-414, 48–61. [Google Scholar] [CrossRef]
  84. Ahmad, M.Z.; Navarro, M.; Lhotka, M.; Zornoza, B.; Téllez, C.; de Vos, W.M.; Benes, N.E.; Konnertz, N.M.; Visser, T.; Semino, R.; et al. Enhanced gas separation performance of 6FDA-DAM based mixed matrix membranes by incorporating MOF UiO-66 and its derivatives. J. Membr. Sci. 2018, 558, 64–77. [Google Scholar] [CrossRef] [Green Version]
  85. Nordin, N.A.H.M.; Ismail, A.F.; Misdan, N.; Nazri, N.A.M. Modified ZIF-8 mixed matrix membrane for CO2/CH4 separation. AIP Conf. Proc. 2017, 1891, 020091. [Google Scholar]
  86. Moch, I., Jr. HOLLOW-FIBER MEMBRANES. Membr. Process. 2000, 1, 1–9. [Google Scholar]
  87. Liu, Y.; Liu, Z.; Morisato, A.; Bhuwania, N.; Chinn, D.; Koros, W.J. Natural gas sweetening using a cellulose triacetate hollow fiber membrane illustrating controlled plasticization benefits. J. Membr. Sci. 2020, 601, 117910. [Google Scholar] [CrossRef]
  88. Chen, H.Z.; Thong, Z.; Li, P.; Chung, N.T.-S. High performance composite hollow fiber membranes for CO2/H2 and CO2/N2 separation. Int. J. Hydrogen Energy 2014, 39, 5043–5053. [Google Scholar] [CrossRef]
  89. XChen, X.; Kaliaguine, S.; Rodrigue, D. A Comparison between Several Commercial Polymer Hollow Fiber Membranes for Gas Separation. J. Membr. Sep. Technol. 2017, 6, 1–15. [Google Scholar]
  90. Zhu, H.; Jie, X.; Wang, L.; Kang, G.; Liu, D.; Cao, Y. Enhanced gas separation performance of mixed matrix hollow fiber membranes containing post-functionalized S-MIL-53. J. Energy Chem. 2018, 27, 781–790. [Google Scholar] [CrossRef] [Green Version]
  91. Widiastuti, N.; Gunawan, T.; Fansuri, H.; Salleh, W.N.W.; Ismail, A.F.; Sazali, N. P84/ZCC Hollow Fiber Mixed Matrix Membrane with PDMS Coating to Enhance Air Separation Performance. Membranes 2020, 10, 267. [Google Scholar] [CrossRef] [PubMed]
  92. Li, G.; Kujawski, W.; Válek, R.; Koter, S. A review—The development of hollow fibre membranes for gas separation processes. Int. J. Greenh. Gas Control 2021, 104, 103195. [Google Scholar] [CrossRef]
  93. Wan, C.F.; Yang, T.; Lipscomb, G.G.; Stookey, D.J.; Chung, N.T.-S. Design and fabrication of hollow fiber membrane modules. J. Membr. Sci. 2017, 538, 96–107. [Google Scholar] [CrossRef]
  94. Zulhairun, A.; Ng, B.; Ismail, A.; Murali, R.S.; Abdullah, M. Production of mixed matrix hollow fiber membrane for CO2/CH4 separation. Sep. Purif. Technol. 2014, 137, 1–12. [Google Scholar] [CrossRef]
  95. Li, T.; Pan, Y.; Peinemann, K.-V.; Lai, Z. Carbon dioxide selective mixed matrix composite membrane containing ZIF-7 nano-fillers. J. Membr. Sci. 2013, 425–426, 235–242. [Google Scholar] [CrossRef]
  96. Car, A.; Stropnik, C.; Yave, W.; Peinemann, K.-V. Pebax®/polyethylene glycol blend thin film composite membranes for CO2 separation: Performance with mixed gases. Sep. Purif. Technol. 2008, 62, 110–117. [Google Scholar] [CrossRef] [Green Version]
  97. Jia, M.-D.; Pleinemann, K.-V.; Behling, R.-D. Preparation and characterization of thin-film zeolite–PDMS composite membranes. J. Membr. Sci. 1992, 73, 119–128. [Google Scholar] [CrossRef]
  98. Liu, M.; Nothling, M.D.; Zhang, S.; Fu, Q.; Qiao, G.G. Thin film composite membranes for postcombustion carbon capture: Polymers and beyond. Prog. Polym. Sci. 2022, 126, 101504. [Google Scholar] [CrossRef]
  99. Mubashir, M.; Fong, Y.Y.; Leng, C.T.; Keong, L.K.; Jusoh, N. Study on the effect of process parameters on CO2/CH4 binary gas separation performance over NH2-MIL-53(Al)/cellulose acetate hollow fiber mixed matrix membrane. Polym. Test. 2020, 81, 106223. [Google Scholar] [CrossRef]
  100. Mubashir, M.; Yeong, Y.F.; Lau, K.K.; Chew, T.L. Effect of spinning conditions on the fabrication of cellulose acetate hollow fiber membrane for CO2 separation from N2 and CH4. Polym. Test. 2019, 73, 1–11. [Google Scholar] [CrossRef]
  101. Hamid, M.R.A.; Jeong, H.-K. Recent advances on mixed-matrix membranes for gas separation: Opportunities and engineering challenges. Korean J. Chem. Eng. 2018, 35, 1577–1600. [Google Scholar] [CrossRef]
  102. Vaidhyanathan, R.; Iremonger, S.S.; Shimizu, G.K.H.; Boyd, P.G.; Alavi, S.; Woo, T.K. Direct Observation and Quantification of CO2 Binding Within an Amine-Functionalized Nanoporous Solid. Sci. 2010, 330, 650–653. [Google Scholar] [CrossRef] [PubMed]
  103. Mahajan, R.; Koros, W.J. Factors Controlling Successful Formation of Mixed-Matrix Gas Separation Materials. Ind. Eng. Chem. Res. 2000, 39, 2692–2696. [Google Scholar] [CrossRef]
  104. Li, Y.; Guan, H.-M.; Chung, T.-S.; Kulprathipanja, S. Effects of novel silane modification of zeolite surface on polymer chain rigidification and partial pore blockage in polyethersulfone (PES)–zeolite A mixed matrix membranes. J. Membr. Sci. 2006, 275, 17–28. [Google Scholar] [CrossRef]
  105. Escorihuela, S.; Valero, L.; Tena, A.; Shishatskiy, S.; Escolástico, S.; Brinkmann, T.; Serra, J.M. Study of the Effect of Inorganic Particles on the Gas Transport Properties of Glassy Polyimides for Selective CO2 and H2O Separation. Membr. 2018, 8, 128. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  106. Hu, L.; Clark, K.; Alebrahim, T.; Lin, H. Mixed matrix membranes for post-combustion carbon capture: From materials design to membrane engineering. J. Membr. Sci. 2021, 644, 1201401. [Google Scholar] [CrossRef]
  107. Lin, R.; Hernandez, B.V.; Ge, L.; Zhu, Z. Metal organic framework based mixed matrix membranes: An overview on filler/polymer interfaces. J. Mater. Chem. A 2018, 6, 293–312. [Google Scholar] [CrossRef]
  108. Ahmad, N.N.R.; Mukhtar, H.; Mohshim, D.F.; Nasir, R.; Man, Z. Surface modification in inorganic filler of mixed matrix membrane for enhancing the gas separation performance. Rev. Chem. Eng. 2016, 32, 181–200. [Google Scholar] [CrossRef]
  109. Cheng, Y.; Wang, Z.; Zhao, D. Mixed Matrix Membranes for Natural Gas Upgrading: Current Status and Opportunities. Ind. Eng. Chem. Res. 2018, 57, 4139–4169. [Google Scholar] [CrossRef]
  110. Genduso, G.; Pinnau, I. Quantification of sorption, diffusion, and plasticization properties of cellulose triacetate films under mixed-gas CO2/CH4 environment. J. Membr. Sci. 2020, 610, 118269. [Google Scholar] [CrossRef]
  111. Rajati, H.; Navarchian, A.H.; Rodrigue, D.; Tangestaninejad, S. Improved CO2 transport properties of Matrimid membranes by adding amine-functionalized PVDF and MIL-101(Cr). Sep. Purif. Technol. 2020, 235, 116149. [Google Scholar] [CrossRef]
Polymers 14 01408 g001 550
Figure 1. Transport mechanisms for gas transport through mixed matrix membrane with; (a) interfacial defect, (b) defect free layer [26].
Figure 1. Transport mechanisms for gas transport through mixed matrix membrane with; (a) interfacial defect, (b) defect free layer [26].
Polymers 14 01408 g001
Polymers 14 01408 g002 550
Figure 2. Schematic diagram of MOFs: (a) UiO-66 and NH2-UiO-66, (b) ZIF-8 and NH2-ZIF-8, (c) MIL-101 and NH2-MIL-101 [74,75,76,77,78].
Figure 2. Schematic diagram of MOFs: (a) UiO-66 and NH2-UiO-66, (b) ZIF-8 and NH2-ZIF-8, (c) MIL-101 and NH2-MIL-101 [74,75,76,77,78].
Polymers 14 01408 g002
Polymers 14 01408 g003 550
Figure 3. Cross-sectional SEM images of Matrimid with different filler loadings: (a–c) MIL-125 loading of 5%, 15%, and 30%, respectively, and (d–f) NH2-MIL-125 loadings of 5%, 15%, and 30%, respectively [17].
Figure 3. Cross-sectional SEM images of Matrimid with different filler loadings: (a–c) MIL-125 loading of 5%, 15%, and 30%, respectively, and (d–f) NH2-MIL-125 loadings of 5%, 15%, and 30%, respectively [17].
Polymers 14 01408 g003
Polymers 14 01408 g004 550
Figure 4. CO2 and CH4 adsorption isotherms of NH2-MOF-199, NH2-UiO-66, MOF-199, UiO-66, and UiO-67 reported by Nik et al. [83].
Figure 4. CO2 and CH4 adsorption isotherms of NH2-MOF-199, NH2-UiO-66, MOF-199, UiO-66, and UiO-67 reported by Nik et al. [83].
Polymers 14 01408 g004
Polymers 14 01408 g005 550
Figure 5. Cross-sectional SEM images of (a) UiO-66/6FDA-ODA and (b) NH2-UiO-66/6FDA-ODA [83].
Figure 5. Cross-sectional SEM images of (a) UiO-66/6FDA-ODA and (b) NH2-UiO-66/6FDA-ODA [83].
Polymers 14 01408 g005
Polymers 14 01408 g006 550
Figure 6. The Robeson plot of CO2/CH4 gas pair selectivity against CO2 permeability for MMMs; MIL-53/6FDA-ODA and NH2-MIL-53/6FDA-ODA [13], ZIF-8/6FDA-durene and NH2-ZIF-8/6FDA-durene [81], MOF-199/6FDA-ODA and NH2-MOF-199/6FDA-ODA [83], and MIL-125/Matrimid 9725 and NH2-MIL-125/Matrimid 9725 [17].
Figure 6. The Robeson plot of CO2/CH4 gas pair selectivity against CO2 permeability for MMMs; MIL-53/6FDA-ODA and NH2-MIL-53/6FDA-ODA [13], ZIF-8/6FDA-durene and NH2-ZIF-8/6FDA-durene [81], MOF-199/6FDA-ODA and NH2-MOF-199/6FDA-ODA [83], and MIL-125/Matrimid 9725 and NH2-MIL-125/Matrimid 9725 [17].
Polymers 14 01408 g006
Polymers 14 01408 g007 550
Figure 7. Schematic diagram for the spinning machine setup for the fabrication of hollow fiber mixed matrix membranes for gas separation [94].
Figure 7. Schematic diagram for the spinning machine setup for the fabrication of hollow fiber mixed matrix membranes for gas separation [94].
Polymers 14 01408 g007
Polymers 14 01408 g008 550
Figure 8. PEBAX thin selective layer [88].
Figure 8. PEBAX thin selective layer [88].
Polymers 14 01408 g008
Polymers 14 01408 g009 550
Figure 9. Schematic diagram on the types of cases for the polymer-filler interactions HFMMMs [105].
Figure 9. Schematic diagram on the types of cases for the polymer-filler interactions HFMMMs [105].
Polymers 14 01408 g009
Polymers 14 01408 g010 550
Figure 10. SEM images of cross-section (1 and 2) and outer surface (3 and 4) of PEBAX® 2533-UiO-66NH2/PP thin film HFMMM-(A) 20 wt% NH2-UiO-66, and (B) 50 wt% NH2-UiO-66 [73].
Figure 10. SEM images of cross-section (1 and 2) and outer surface (3 and 4) of PEBAX® 2533-UiO-66NH2/PP thin film HFMMM-(A) 20 wt% NH2-UiO-66, and (B) 50 wt% NH2-UiO-66 [73].
Polymers 14 01408 g010
Table
Table 1. Illustration of MOF structures.
Table 1. Illustration of MOF structures.
Metal-Organic FrameworkPore SizeMOF StructureReference
UiO-666.2 Å Polymers 14 01408 i001Reprinted with permission from Refs. [32,62]
UiO-678.0 Å Polymers 14 01408 i002[51,63]
MIL-53 (Al)8.5 Å Polymers 14 01408 i003[38,64]
MIL-101 (Cr)12 Å Polymers 14 01408 i004[32,65]
MIL-125 (Ti)6 Å Polymers 14 01408 i005[63]
ZIF-42.1 Å Polymers 14 01408 i006[66]
ZIF-73.0–4.2 Å Polymers 14 01408 i007[58,66]
ZIF-83.4–11.8 Å Polymers 14 01408 i008[2,66]
Cu3(BTC)26 Å Polymers 14 01408 i009[67,68]
Fe-BTC5.5–8.6 Å Polymers 14 01408 i010[60,61]
Table
Table 2. Summary of the performances of amine and non-amine functionalized MOFs based mixed matrix membrane for CO2/CH4 separation.
Table 2. Summary of the performances of amine and non-amine functionalized MOFs based mixed matrix membrane for CO2/CH4 separation.
Amine-Functionalized MOFs MMMOperating ParametersPerformanceReference
FillerPolymerParticle Loading (%)Temperature (K)/Pressure (Bar)CO2 Permeability (Barrer)CO2/CH4 Selectivity
ZIF-86FDA-durene5.0298/3.5693.516.5[41]
APTMS-ZIF-80.5649.6 17.4 [57]
AAPTMS-ZIF-80.5825.1 26.2
AEPTMS-ZIF-80.5713.8 27.9
APTMS-ZIF-81.0518.3 13.5
AAPTMS-ZIF-81.0582.5 18.2
AEPTMS-ZIF-81.0561.615.0
MIL-53PEBAX MH-16575.0311.15/10.0127.418.7[38]
10.0129.023.3
15.0105.417.4
20.095.717.2
NH2-MIL-535.0134.619.1
10.0149.120.5
15.0125.620.6
20.063.317.3
UiO-666FDA-DAM14.0308/3.01700.031.0[84]
NH2-UiO-660.0997.029.2
16.01223.030.0
NH2-MIL-125 (Ti)6FDA-durene0.0298/3.5510.38.6[80]
1.0922.823.0
3.0930.027.0
5.01020.029.5
7.01115.737.5
9.0961.831.0
NH2-ZIF-8PSF0.0300/4.059.018.0[85]
0.521.234.0
ZIF-86FDA-durene1.0308/5.0600.015.0[81]
ZIF-8-AAPTMS1.0540.016.8
ZIF-8-AEPTMS1.0520.011.5
NH2-MIL-125 (Ti)PSf10.0303/3.018.528.3[82]
20.029.329.5
30.040.029.2
10.0303/10.015.028.5
20.022.829.5
30.036.85.7
-6FDA-ODA-308/10.014.444.1[83]
UiO-6625.050.446.1
NH2-UiO-6613.751.6
MOF-19921.851.2
NH2-MOF-19926.659.6
MIL-125Matrimid 972515.0308/9.018.044.0[17]
30.027.037.0
NH2-MIL-12515.017.050.0
30.050.037.0
MIL-536FDA-ODA25.0308/10.321.044.5[13]
NH2-MIL-5325.014.566.0
Table
Table 3. Summary of non-functionalized and amine-functionalized MOFs based hollow fiber mixed matrix membrane for CO2/CH4 separation.
Table 3. Summary of non-functionalized and amine-functionalized MOFs based hollow fiber mixed matrix membrane for CO2/CH4 separation.
Amine-Functionalized HFMMMOperating ParameterPerformanceReference
FillerPolymerLoading (%)Temperature (K)/Pressure (Bar)CO2 Permeability (GPU)CO2/CH4 Selectivity
UiO-66 in PEBAXPVDF50.0298/2220.016.0[37]
NH2-UiO-66 in PEBAX320.023.0
NH2-MIL-53CA15.0303/32.911.8[99]
NH2-MIL-53CA15.0298/36.716.0[100]
ZIF-8PSf0.5303/431.015.6[72]
A@S/ZIF-841.222.3
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Sunder, N.; Fong, Y.Y.; Bustam, M.A.; Suhaimi, N.H. Development of Amine-Functionalized Metal-Organic Frameworks Hollow Fiber Mixed Matrix Membranes for CO2 and CH4 Separation: A Review. Polymers 2022, 14, 1408. https://doi.org/10.3390/polym14071408

AMA Style

Sunder N, Fong YY, Bustam MA, Suhaimi NH. Development of Amine-Functionalized Metal-Organic Frameworks Hollow Fiber Mixed Matrix Membranes for CO2 and CH4 Separation: A Review. Polymers. 2022; 14(7):1408. https://doi.org/10.3390/polym14071408

Chicago/Turabian Style

Sunder, Naveen, Yeong Yin Fong, Mohamad Azmi Bustam, and Nadia Hartini Suhaimi. 2022. "Development of Amine-Functionalized Metal-Organic Frameworks Hollow Fiber Mixed Matrix Membranes for CO2 and CH4 Separation: A Review" Polymers 14, no. 7: 1408. https://doi.org/10.3390/polym14071408

APA Style

Sunder, N., Fong, Y. Y., Bustam, M. A., & Suhaimi, N. H. (2022). Development of Amine-Functionalized Metal-Organic Frameworks Hollow Fiber Mixed Matrix Membranes for CO2 and CH4 Separation: A Review. Polymers, 14(7), 1408. https://doi.org/10.3390/polym14071408

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.