Next Article in Journal
Structural, Thermal, and Release Properties of Hybrid Materials Based on Layered Zinc Hydroxide and Caffeic Acid
Previous Article in Journal
Indocyanine Green-Nexturastat A-PLGA Nanoparticles Combine Photothermal and Epigenetic Therapy for Melanoma
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 10
Issue 1
10.3390/nano10010162
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Preparation and Characterization of Epoxy Resin Filled with Ti3C2Tx MXene Nanosheets with Excellent Electric Conductivity

by
Ailing Feng
1,
Tianqi Hou
2,
Zirui Jia
2,*,
Yi Zhang
2,
Fan Zhang
3,* and
Guanglei Wu
2,4,*
1
Institute of Physics & Optoelectronics Technology, Baoji University of Arts and Sciences, Baoji 721016, China
2
Institute of Materials for Energy and Environment, State Key Laboratory of Bio-Fibers and Eco-Textiles, College of Materials Science and Engineering, Qingdao University, Qingdao 266071, China
3
School of Materials Sciences and Engineering, East China Jiaotong University, Nanchang 330013, China
4
Key Laboratory of Engineering Dielectrics and Its Application, Ministry of Education, Harbin University of Science and Technology, Harbin 150080, China
*
Authors to whom correspondence should be addressed.
Nanomaterials 2020, 10(1), 162; https://doi.org/10.3390/nano10010162
Submission received: 14 December 2019 / Revised: 13 January 2020 / Accepted: 14 January 2020 / Published: 17 January 2020
(This article belongs to the Section Nanocomposite Materials)
Browse Figures
Versions Notes

Abstract

:
MXene represents new kinds of two-dimensional material transition metal carbides and/or carbonitrides, which have attracted much attention in various applications including electrochemical storage devices, catalysts, and polymer composite. Here, we report a facile method to synthesize Ti3C2Tx MXene nanosheets and prepare a novel electrically conductive adhesive based on epoxy resin filled with Ti3C2Tx MXene nanosheets by solution blending. The structure, morphology, and performance of Ti3C2Tx MXene nanosheets and epoxy/Ti3C2Tx MXene nanosheets composite were investigated. The results show that Ti3C2Tx MXene possesses nanosheet structure. Ti3C2Tx MXene nanosheets were homogeneously dispersed in epoxy resin. Electrical conductivity and mechanical properties measurements reveal that the epoxy/Ti3C2Tx MXene nanosheet composite exhibited both good electrical conductivity (4.52 × 10−4 S/m) and favorable mechanical properties (tensile strength of 66.2 MPa and impact strength of 24.2 kJ/m2) when the content of Ti3C2Tx MXene nanosheets is 1.2 wt %. Thus, Ti3C2Tx MXene is a promising filler for electrically conductive adhesive with high electric conductivity and high mechanical performance.

1. Introduction

With the progression of science and technology, electronic units are developing towards the direction of miniaturization, portability, and high integration [1,2,3,4,5]. Therefore, the electronic packaging industry demands interconnect bonding technology, which could offer excellent electrical conductivity, good flexibility, and satisfied mechanical strength [6,7,8,9]. Besides, it should be cost effective and environmentally benign. In this regard, electrical conductive adhesives (ECAs) are regarded as one of the most feasible alternative interconnection materials for future applications due to low processing temperature, fine pitch interconnect, and environmental friendliness [10,11,12,13].
ECAs consist of polymer (such as, acrylate resin, silicone, or epoxy resin) and electrical conductive fillers (such as, Ag, Au, Ni, or carbon materials). The polymer resin provides interconnect bonding properties while conductive fillers conduct electricity in ECAs. This polymer is widely used because of its low density, high specific strength, dimensional stability, and chemical resistance [14,15,16,17,18]. Many researches have studied epoxy-based ECAs [19]. The formation of effective conductive paths in the ECAs is the key to obtain high electrical conductivity. Several conductive fillers have been studied in ECAs; these include cobalt nanoparticles [20], zinc complexes [21,22], cadmium [23], metal oxide [24], and so on. However, there are some issues such as aggregation and poor interconnect between conductive fillers with polymer resin, which need to be solved.
MXenes is a new kind of transition metal carbide/nitride two-dimensional material with graphene-like structure. Their chemical formulas are Mn+1Xn, where M is an early transition metal, X is C and/or N, and n represents the number of X (1, 2, or 3). MXenes are promising conductive fillers due to intrinsic high conductivity and unique structure [25,26,27]. Carbon materials (graphene or carbon nanotube) have to be oxidized to introduce oxygen-containing functional groups, which prevent carbon materials aggregating in the polymer resin and assist binding between graphene/carbon nanotube and EP resin. However, the appearance of some functional groups decreases the electronic conductivity. MXene does not require any pretreatment to composite with other materials, as the surface atomic of MXenes is Ti, which can easily bind the O atomic of EP resin. Therefore, MXenes could well be dispersed in the polymer resin and provide high electric conductivity.
Herein, we report on the structure and performance of EP/MXene ECAs. Ti3AlC2 was used as the MAX precursor to prepare Ti3C2Tx MXene nanosheets. The crystal structure and morphology of Ti3C2Tx MXene nanosheets were characterized by scanning electron microscope (SEM), X-ray diffraction (XRD), and transmission electron microscopy (TEM). Different amounts of Ti3C2Tx MXene nanosheets were introduced into ECAs to study the effect of Ti3C2Tx MXene nanosheets on the electrical properties and mechanical performance of the EP/Ti3C2Tx MXene nanosheet ECAs. The results show that the electrical property and mechanical performance of the EP/Ti3C2Tx MXene nanosheets ECAs could be improved compared to pure EP resin. Our work may shed lights on the development of ECAs with high electric conductivity and high mechanical performance in the electronic industry.

2. Experimental

2.1. Material

Epoxy resin and hardener tetrahyelrophthalic anhydride were purchased from Sigma-Aldrich. The titanium carbide (TiC) powders were obtained from Alfa Aesar. Commercially available Ti2AlC was obtained from Kanthal Co., Ltd., Stockholm, Sweden; 36% hydrochloric acid (HCl) and lithium fluoride (LiF, 98%) were bought from Sinopharm Chemical Reagent Co., Ltd., Shanghai, China.

2.2. Preparation of EP/Ti3C2Tx MXene Nanosheets ECAs

The Ti3AlC2 was prepared by mixing Ti2AlC and TiC powders in a 1:1 M ratio, followed by ball-milling at 300 rpm for 18 h. After being milled, the mixture was heated to 1350 °C at 5 °C/min in an Al2O3 tube furnace under Ar atmosphere. Then, the mixture was reacted at 1350 °C for 2.0 h before cooling again. The resulting product is Ti3AlC2.
First, 0.66 g LiF was added in 6 M HCI solution; 1.0 g Ti3AlC2 powders were immersed in 50 mL LiF/HCl solution. The mixture was stirred for 48 h at 40 °C. The resulting suspension was washed using distilled water five times and centrifuged to separate the powder from the supernatant. Then, the obtained powder was sonicated for 2.0 h and rinsed three times with deionized water. Ti3C2Tx MXene nanosheets were collected and dried in vacuum at 80 °C for 24 h.
The resin mixture was uniformly mixed at the epoxy resin and curing agent (methyl tetrahyelrophthalic anhydride) mass ratio equal to 100:32. Then, different amounts of Ti3C2Tx MXene nanosheets added into resin mixture. To achieve uniform dispersion of Ti3C2Tx MXene nanosheets in the epoxy resin, the mixture was mixed with a Flacktek Speed mixer at a speed of 2000 rpm for 0.5 h. The curing process took place at 100 °C for 2 h, 120 °C for 2 h and 160 °C for 4 h. After cooling to room temperature, the resulting EP/Ti3C2Tx MXene nanosheets composites were obtained. The schematic illustration of preparation of EP/Ti3C2Tx MXene nanosheets composites is illustrated in Figure 1.

2.3. Characterization and Measurement

The surface morphology of Ti3AlC2 and Ti3C2Tx MXene nanosheets and the fracture surfaces of pure EP, EP/Ti3C2Tx MXene nanosheets composites were characterized by SEM (FEI, Quanta 250, Washington, WA, USA). The element contents in Ti3C2Tx MXene nanosheets were characterized by energy-dispersive X-ray (EDX, FEI, Quanta 250). The phase structures of Ti3AlC2 and Ti3C2Tx MXene were characterized by X-ray powder diffraction (XRD, Rint-2000, Rigaku, Berlin, Germany) using Cu Kα radiation (λ = 1.5418 Å) operated at a voltage of 30 kV and a current of 10 mA. Fourier transform infrared spectrum (FTIR, IRpresitge-21 model, Tokyo, Japan) was used to record the Fourier transform infrared spectra of Ti3AlC2 and Ti3C2Tx MXene. The internal morphology of Ti3C2Tx MXene nanosheets were studied using transmission electron microscope (TEM, JEOL, JEM-2100 HT, Tokyo, Japan). There are four methods (Volt-Ampere, double bridge, direct current four probe, and digital multimeter) to measure the conductivity of composites. We used digital multimeter (830/F-33 model, Beijing Jiaxin Instrument, Ltd., Beijing, China) to test the resistance (R) of EP/Ti3C2Tx MXene nanosheets composites. Composite circles with a diameter of 20 mm and a thickness of 2 mm were prepared. Then we calculated the resistivity (ρ) of composite based on the diameter and thickness of samples. Electrical conductivity (K) is the reciprocal of resistivity (ρ) as follows: K = 0.0637/R (S/cm). The mechanical properties of EP/Ti3C2Tx MXene nanosheets composites were tested using tensile testing machine (UTM-2460 model, Hebei JInjian Co., Ltd., Tangshan, China).

3. Results and Discussion

3.1. The Structure and Morphology of Ti3AlC2 and Ti3C2Tx MXene

The SEM images of Ti3AlC2, Ti3C2Tx, and Ti3C2Tx nanosheets are shown in Figure 2. SEM images (Figure 2a,b) show that Ti3AlC2 display a solid bulk morphology with uneven sizes. The smaller Ti3AlC2 MAX is about 2 μm while the larger one is about 20 μm. After HF etching, Ti3C2Tx show a loosely packed structure consist of multilayered Ti3C2Tx nanosheets, which had typical diameters of 2 μm (Figure 2c,d). The interlayer space of multilayered Ti3C2Tx is ~200 nm. This morphology is because the LiF/HF treatment removes Al layers from Ti3AlC2 MAX. By sonication, the loosely packed Ti3C2Tx MXene is converted to nanosheets (Figure 2e,f). The Ti3C2Tx MXene nanosheets have smooth surface, which show a structure similar to that of graphene. The thin sheet is of ~10 nm thick, which corresponds to roughly 5 Ti3C2Tx layers.
To study the elements of Ti3C2Tx nanosheets, energy dispersive X-ray (EDX) analysis were carried out. Figure 3 reveal EDX spectrum and SEM-EDX element mappings of Ti3C2Tx MXene nanosheets. As shown in Figure 3a, Ti3C2Tx MXene thin nanosheets have diameters of 3 μm. In the EDX spectrum (Figure 3b), four strong peaks are belonged to C, Ti, O, and F, whereas a weak peak assigns to Al. As shown in Figure 3c, the uniform C, Ti, O, and F elemental distributions are observed. The composition of Ti3C2Tx nanosheets, as calculated from EDS analysis, is shown in Table 1. The results showed that the Ti3C2Tx MXene contains 11.0 wt % C, 69.0 wt % Ti, 11.1 wt % O, 7.8 wt % F and 1.1 wt % Al. The F and O elements are attributed to presence of –F, –OH, and –COOH.
The structural properties of Ti3AlC2 and Ti3C2Tx MXene were tested using XRD and Fourier transform infrared spectroscopy (FTIR), as shown in Figure 4. The diffraction pattern (Figure 4aA) has eleven broad peaks at 9.5°, 19.0°, 34.0°, 36.8°, 38.8°, 41.9°, 45.1°, 48.5°, 52.7°, 56.6°, and 60.2°, corresponding to (002), (004), (101), (103), (104), (105), (106), (107), (108), (109), and (110) of Ti3AlC2 MAX (JCPDS No. 52-0875) [28,29], respectively. It can be seen in the XRD patterns that the crystallinity and structural order of Ti3AlC2 decrease after HF treatment. As shown in Figure 4aB, no characteristic diffraction peaks of at 2θ = 36.9°, 38.9°, 42.0° belonged to Ti3AlC2 are observed (Figure 4aA) because of the removal of Al layers from Ti3AlC2 MAX. Moreover, the characteristic (002) peak at 2θ = 9.5° shifted to a lower value (2θ = 8.3°) and became broadened, displaying an increase in c-spacing when the Al atoms are removed away and replaced by –F and –OH. The FTIR spectra of Ti3AlC2 MAX and Ti3C2Tx MXene nanosheets are shown in Figure 4b. There is no obvious peak in Ti3AlC2 MAX curve, which means there is no organic functional groups on Ti3AlC2 MAX. From Figure 4b, the obvious band at 3490 cm−1 is indicative of the presence of obvious strongly hydrogen-bonded –OH on the surface of Ti3C2Tx MXene nanosheets. A weak peak at 1216 cm−1 can be observed. This weak peak is a characteristic of covalent C–F bond stretching vibrations [30]. FTIR result confirmed that Al atoms are replaced by –F, –OH, and –COOH functional groups, which is consistent with the XRD result.
Figure 5 show TEM image and the corresponding selected-area electron diffraction (SAED) of Ti3C2Tx MXene nanosheets. Figure 5a indicates a typical low-magnification TEM image of the synthesized Ti3C2Tx MXene, in which thin nanosheet morphology formed, and the thin nanosheet has five layers, which is consistent with the SEM result. HRTEM was used to characterize the Ti3C2Tx MXene nanosheets (Figure 5b). The Ti3C2Tx MXene sample shows the characteristic spacings of 0.31 nm for the (110) lattice planes of Ti3C2Tx [31]. The SAED pattern of Ti3C2Tx MXene nanosheets showed a hexagonal arrangement at the atomic scale, revealing the typical hexagonal crystalline structure of Ti3C2Tx phase.

3.2. The Structure of EP/Ti3C2Tx MXene Nanosheets ECAs

Figure 6 shows XRD patterns of the epoxy (a), Ti3C2Tx MXene nanosheets (b), EP/Ti3C2Tx MXene nanosheets composite containing 0.4 wt % Ti3C2Tx (c), EP/Ti3C2Tx MXene nanosheets composite containing 1.0 wt % Ti3C2Tx (d), and EP/Ti3C2Tx MXene nanosheets composite containing 1.6 wt % Ti3C2Tx (e). The epoxy has a broad peak at 2θ = 16.8°, whereas Ti3C2Tx MXene nanosheets have peaks at 2θ = 8.8°, 60.2° belonged to (002) and (110) planes. For EP/Ti3C2Tx MXene nanosheets composite, the characteristic (002) peak of Ti3C2Tx MXene nanosheets shifted to a lower value. The EP composite containing 0.4 wt % filler did not give any discernible (002) or (110) peaks (Figure 6c), most likely because the Ti3C2Tx loading was not sufficient to yield any signal. At a higher loading fraction of 1.0 wt %, the composite had the (110) peak and also a similar (002) peak shift. The EP composite containing 1.6 wt % still had the (110) peak which become broad. Explanation for this might be that EP polymer molecular chains are incorporated in the Ti3C2Tx MXene layers which make the d-spacing increase.

3.3. Electrical Conductivity and Mechanical Performance

The electrical conductivity (K) of the EP/Ti3C2Tx MXene nanosheets composite under various mass fractions of Ti3C2Tx MXene nanosheets is illustrated in Figure 7. From Figure 7 we can observe that the electrical conductivity of the EP/Ti3C2Tx MXene nanosheets composite increases gradually as the increasing of Ti3C2Tx MXene nanosheets filler content. When the content of Ti3C2Tx MXene nanosheets is lower than 0.4 wt %, the electrical conductivity slowly increases with increasing content of Ti3C2Tx MXene nanosheets. When the content of Ti3C2Tx MXene nanosheets increases to 0.6 wt %, the electrical conductivity of the EP/Ti3C2Tx MXene nanosheets composite increases significantly. The critical content of filler is regarded as the percolation threshold. Thus the percolation threshold of the EP/Ti3C2Tx MXene nanosheets composite is ~0.85 wt %. The electrical conductivity of the EP/Ti3C2Tx MXene nanosheets composite in percolation threshold is 1.81 × 10−6 S/m, that is, ten orders of magnitude higher than that of the pure epoxy resin (about 1.03 × 10−16 S/m). After that, the electrical conductivity of the EP/Ti3C2Tx MXene nanosheets composites also increases as the content of Ti3C2Tx MXene nanosheets increases. However, its electrical conductivity increases slowly.
The percolation theory was applied for the calculation of the percolation threshold of composites. The dependence of the electrical conductivity of EP/Ti3C2Tx MXene nanosheets composite on Ti3C2Tx MXene content can be described in σm = σn(P-Pc)β, where σn is the conductivity of Ti3C2Tx MXene nanosheets, σm is the electrical conductivity of EP/Ti3C2Tx MXene nanosheets composite, P is the volume fraction of Ti3C2Tx MXene nanosheets, Pc is the percolation threshold, β is the conductivity exponent which is approximately 1.3 and 2.0 for three-dimensional and two-dimensions randomly distributed nanocomposites, respectively, in the percolation model [32]. The density of the Ti3C2Tx MXene nanosheets is ~5 greater than the EP polymer. Therefore, we calculate that the conductivity exponent for EP/Ti3C2Tx MXene nanosheets composite as β = 0.84. The Ti3C2Tx MXene nanosheets electrical conductivity is about 24 S/cm which is much higher than conventional non-conductive polymer (~10−16 S/cm) and the Ti3C2Tx MXene nanosheets have a large aspect ratio (~100–500), which can be observed in the SEM photograph of the Ti3C2Tx MXene nanosheets. Such an extreme geometry might be a factor contributable to the high electrical conductivity and low conductivity exponent. We can infer that the percolation threshold of EP/Ti3C2Tx MXene nanosheets composite is about 0.28 vol % (0.85 wt %). The percolation threshold of EP/Ti3C2Tx MXene nanosheets composite (0.85 wt %) is higher than that of aligned multi-wall carbon nanotube/EP composite (0.0025 wt %) because aligned CNT by an injection CVD method overcome the obstacle of aggregation and show higher electrical conductivity [32]. However, usually CNT is easy to aggregate in polymer composites, which hamper their high electrical conductivity. So the percolation threshold of our composite is lower than that of usual CNT-based polymer composite [33].
The mechanical properties (tensile strength and impact strength) of the EP/Ti3C2Tx MXene nanosheets composite are tested with electronic tensile testing machine. The dependencies of tensile strength (a) and impact strength (b) of the EP/Ti3C2Tx MXene nanosheets composite on the content of the Ti3C2Tx MXene nanosheets are shown in Figure 8. Figure 8 shows that the tensile strength and impact strength of the EP/Ti3C2Tx MXene nanosheets composite first increases with the content of Ti3C2Tx MXene nanosheets increasing. When the content of Ti3C2Tx MXene nanosheets increases to 1.2 wt %, the tensile strength and impact strength of composite arrive at the highest value of 66.2 MPa and 24.2 kJ/m2, which is better than that in some papers [34]. After that, the tensile strength and impact strength of composite then gradually decreases. It is known that the tensile strength and impact strength of polymer resin is related to the rigidity of the polymer chains. As the content of Ti3C2Tx MXene nanosheets increase, the rigidity of the EP/Ti3C2Tx MXene nanosheets composite increases due to Ti3C2Tx MXene nanosheets that connect many single EP polymer chains by –F, –OH, and –COOH functional groups. However, when the content of Ti3C2Tx MXene nanosheets is more than 1.2 wt %, the EP/Ti3C2Tx MXene nanosheets composite possesses more Ti3C2Tx MXene nanosheets agglomeration, reducing their tensile strength and impact strength.

3.4. The Morphology of EP/Ti3C2Tx MXene Nanosheets Composite

To understand the effect of the content of Ti3C2Tx Mxene nanosheets in NH2–CF/MXene/EP composites on mechanical properties, SEM was used to observe the fracture surfaces of EP composites after impact strength test. Figure 9a–d presents the fracture source of EP/Ti3C2Tx MXene nanosheets composite containing 0.4 wt %, 0.8 wt %, 1.2 wt %, and 1.6 wt % Ti3C2Tx MXene nanosheets. The EP/Ti3C2Tx MXene nanosheets composite containing 0.4 wt % Ti3C2Tx MXene nanosheets display comparatively slippery fracture (Figure 9a). The fracture surfaces of EP/Ti3C2Tx MXene nanosheets composite containing 0.8 wt % or 1.2 wt % Ti3C2Tx MXene nanosheets are rougher. In Figure 9d, we can observe that there is apparent agglomeration on the fracture surface of EP/Ti3C2Tx MXene nanosheets composite containing 1.6 wt % Ti3C2Tx MXene nanosheets. The agglomeration of Ti3C2Tx MXene nanosheets could decrease the impact strength of the EP composites. So the SEM results are consistent with the impact strength shown in Figure 8b.

4. Conclusions

In summary, a novel ECA based on EP resin filled with Ti3C2Tx MXene nanosheets was prepared by a simple solution blending. Ti3C2Tx MXene is of nanosheet structure, which contains 11.0 wt % C, 69.0 wt % Ti, 11.1 wt % O, 7.8 wt % F, and 1.1 wt % Al. These –F, –OH, and –COOH functional groups make Ti3C2Tx MXene nanosheets homogeneously disperse in EP resin. The electrical conductivity of the EP/Ti3C2Tx MXene nanosheets composite increases gradually as Ti3C2Tx MXene nanosheets content increases, and the percolation threshold of EP/Ti3C2Tx MXene nanosheets composite is 0.85 wt %. The electrical conductivity of EP/Ti3C2Tx MXene nanosheets composite in percolation threshold is 1.81 × 10−6 S/m, which is ten orders of magnitude higher than that of the pure epoxy resin (~1.03 × 10−16 S/m). The increase in Ti3C2Tx MXene nanosheets content may increase the tensile strength and impact strength of epoxy/Ti3C2Tx MXene nanosheets composite when the content of filler is low. When the content of filler is 1.2 wt %, the properties of epoxy/Ti3C2Tx MXene nanosheets composite are optimum (electrical conductivity of 4.52 × 10−4 S/m, tensile strength of 66.2 MPa and impact strength of 24.2 KJ/m2). This work presents more applications of MXene-polymer composites.

Author Contributions

A.F. conceived the idea of the paper; T.H. collected and classified the related literature; Z.J. and G.W. also gave helpful advice during the writing process. Y.Z. and F.Z. also gave some great enlightenment and helpful advices during calculating the percolation threshold and the revising process. A.F. wrote the paper. All authors have read and agreed to the published version of the manuscript.

Funding

This work was financially supported by the Natural Science Foundation of Shandong Province (No. ZR2019YQ24), the Qingchuang Talents Induction Program of Shandong Higher Education Institution (Research and Innovation Team of Structural–Functional Polymer Composites), National Natural Science Foundation of China (No. 51407134, No. 51801001), China Postdoctoral Science Foundation (No. 2016M590619, No. 2016M601878), Qingdao Postdoctoral Application Research Project, Provincial Key Research and Development Program of Shaanxi (No. 2019GY-197), Key Laboratory of Engineering Dielectrics and Its Application (Harbin University of Science and Technology), Ministry of Education (No. KFZ1803), Key Project of Baoji University of Arts and Sciences (No. ZK2018051), Baoji Science and Technology Project (No. 16RKX1-29) and Baoji Engineering Technology Research Center for Ultrafast Optics and New Materials (No. 2015CXNL-1-3). Feng AL is supported by The Thousand Talents Plan for Young Professionals of Shaanxi Province.

Acknowledgments

The authors thank the colleagues in the laboratory for their support.

Conflicts of Interest

The authors declare no conflicts of interest.

References

  1. Jakubinek, M.B.; Ashrafi, B.; Zhang, Y.; Martinez-Rubi, Y.; Kingston, C.T.; Johnston, A.; Simard, B. Single-walled carbon nanotube—Epoxy composites for structural and conductive aerospace adhesives. Compos. Part B 2015, 69, 87–93. [Google Scholar] [CrossRef]
  2. Hou, T.; Wang, B.; Jia, Z.; Wu, H.; Lan, D.; Huang, Z.; Feng, A.; Ma, M.; Wu, G. A review of metal oxide-related microwave absorbing materials from the dimension and morphology perspective. J. Mater. Sci. 2019, 30, 10961–10984. [Google Scholar] [CrossRef]
  3. Rubinstein, M.; Colby, R.H. Polymer Physics; Oxford university press: New York, NY, USA, 2003; pp. 88–89. [Google Scholar]
  4. Feng, A.; Wu, G.; Pan, C.; Wang, Y. Synthesis, preparation and mechanical property of wood fiber-reinforced poly (vinyl chloride) composites. J. Nanosci. Nanotechnol. 2017, 17, 3859–3863. [Google Scholar] [CrossRef]
  5. Tyson, W.R.; Miller, W.A. Surface free energies of solid metals: Estimation from liquid surface tension measurements. Surf. Sci. 1977, 62, 267–276. [Google Scholar] [CrossRef]
  6. Wu, G.L.; Cheng, Y.H.; Yang, Z.H.; Jia, Z.R.; Wu, H.J.; Yang, L.J.; Li, H.L.; Guo, P.Z.; Lv, H.L. Design of Carbon Sphere/Magnetic Quantum Dots with Tunable Phase Compositions and Boost Dielectric Loss Behavior. Chem. Eng. J. 2018, 333, 519–528. [Google Scholar] [CrossRef]
  7. Kurlyandskaya, G.V.; Safronov, A.P.; Terzian, T.V.; Volodina, N.S.; Beketov, I.V.; Lezama, L.; Prieto, L.M. Fe45Ni55 magnetic nanoparticles obtained by electric explosion of wire for the development of functional composites. IEEE Magn. Lett. 2015, 6, 1–4. [Google Scholar] [CrossRef]
  8. Zhou, X.F.; Jia, Z.R.; Feng, A.L.; Wang, X.X.; Liu, J.J.; Zhang, M.; Cao, H.J.; Wu, G.L. Synthesis of fish skin -derived 3D carbon foams with broadened bandwidth and excellent electromagnetic wave absorption performance. Carbon 2019, 152, 827–836. [Google Scholar] [CrossRef]
  9. Gao, Z.G.; Xu, B.H.; Ma, M.L.; Feng, A.L.; Zhang, Y.; Liu, X.H.; Jia, Z.R.; Wu, G.L. Electrostatic self-assembly synthesis of ZnFe2O4 quantum dots (ZnFe2O4@C) and electromagnetic microwave absorption. Compos. Part B 2019, 179, 107417. [Google Scholar] [CrossRef]
  10. Li, Z.; Le, T.; Wu, Z.; Yao, Y.; Li, L.; Tentzeris, M.; Moon, K.; Wong, C.P. Rational Design of a Printable, Highly Conductive Silicone-based Electrically Conductive Adhesive for Stretchable Radio-Frequency Antennas. Adv. Funct. Mater. 2015, 25, 464–470. [Google Scholar] [CrossRef]
  11. Du, Z.X.; Li, J.X. The synthesis, structure and magnetic properties of a mononuclear cobalt compound with dipyrimidine sulfane ligand derived from 2-thio-barbituric acid. Inorg. Chim. Acta 2015, 436, 159–162. [Google Scholar] [CrossRef]
  12. Li, J.X.; Du, Z.X.; Wang, J.G.; Wang, T.; Lv, J.N. Zinc and manganese coordination polymers constructed by a new coordination mode of 4,5-dicyanoimidazolate ligand: Syntheses, crystal structures, fluorescent and magnetic properties. Inorg. Chem. Commun. 2012, 15, 243–247. [Google Scholar] [CrossRef]
  13. Ren, H.; Guo, Y.; Huang, S.; Zhang, K.; Yuen, M.; Fu, X.; Yu, S.; Sun, R.; Wong, C. One-step preparation of silver hexagonal microsheets as electrically conductive adhesive fillers for printed electronics. ACS Appl. Mater. Int. 2015, 7, 13685–13692. [Google Scholar] [CrossRef] [PubMed]
  14. Wu, G.L.; Jia, Z.R.; Zhou, X.F.; Nie, G.Z.; Lv, H.L. Interlayer Controllable of Hierarchical MWCNTs@C@FexOy Cross-linked Composite with Wideband Electromagnetic Absorption Performance. Compos. Part A 2020, 128, 105687. [Google Scholar] [CrossRef]
  15. Wu, W.; Yu, C.; Chen, J.; Yang, Q. Fluorometric detection of copper ions using click chemistry and the target-induced conjunction of split DNAzyme fragments. Int. J. Environ. Anal. Chem. 2019. [Google Scholar] [CrossRef]
  16. Jia, Z.R.; Wang, C.; Feng, A.L.; Shi, P.B.; Zhang, C.H.; Liu, X.H.; Wang, K.K.; Wu, G.L. A low dielectric decoration strategy to achieve absorption dominated electromagnetic shielding material. Compos. Part B 2020, 183, 107690. [Google Scholar] [CrossRef]
  17. Pan, C.; Zhang, J.Q.; Kou, K.C.; Zhang, Y.; Wu, G.L. Investigation of the through-plane thermal conductivity of polymer composites with in-plane oriented hexagonal boron nitride. Int. J. Heat Mass Tran. 2018, 120, 1–8. [Google Scholar] [CrossRef]
  18. Jia, Z.R.; Wang, B.B.; Feng, A.L.; Liu, J.J.; Zhang, C.H.; Zhang, M.; Wu, G.L. Fabrication of NixCo3−xS4 hollow nanosphere as wideband electromagnetic absorber at thin matched thickness. Ceram. Int. 2019, 45, 15854–15859. [Google Scholar] [CrossRef]
  19. Zhao, J.; Zhang, D. Epoxy-based adhesives filled with flakes Ag-coated copper as conductive fillers. Polym. Compos. 2017, 38, 846–851. [Google Scholar] [CrossRef]
  20. Li, J.X.; Du, Z.X.; Feng, X. A new binuclear NiII complex with tetrafluorophthalate and 2,2′-bipyridine ligands: Synthesis, crystal structure and magnetic properties. Z. Naturforsch. 2019, 74, 833–838. [Google Scholar] [CrossRef] [Green Version]
  21. Li, J.X.; Du, Z.X.; Wang, J.; Feng, X. Two mononuclear zinc(II) complexes constructed by two types of phenoxyacetic acid ligands: Syntheses, crystal structures and fluorescence properties. Z. Naturforsch. 2019, 74, 839–845. [Google Scholar] [CrossRef]
  22. Li, J.X.; Du, Z.X.; Bai, R.F. Crystal structure of aqua-bis(5-bromo-6-methyl-picolinato-κ2N,O)zinc(II) dihydrate, C14H16Br2N2O7Zn. Z. Krist. New Cryst. Struct. 2019, 235, 63–65. [Google Scholar] [CrossRef] [Green Version]
  23. Li, J.X.; Du, Z.X. A Binuclear Cadmium (II) Cluster Based on π–π Stacking and Halogen-Halogen Interactions: Synthesis, Crystal Analysis and Fluorescent Properties. J. Clust. Sci. 2019, 22, 1–5. [Google Scholar] [CrossRef]
  24. Feng, A.; Ma, M.; Jia, Z.; Zhang, M.; Wu, G. Fabrication of NiFe2O4@carbon fiber coated with phytic acid-doped polyaniline composite and its application as an electromagnetic wave absorber. RSC Adv. 2019, 9, 25932–25941. [Google Scholar] [CrossRef] [Green Version]
  25. Simon, P. Two-dimensional MXene with controlled interlayer spacing for electrochemical energy storage. ACS Nano 2017, 11, 2393. [Google Scholar] [CrossRef] [Green Version]
  26. Ding, L.; Wei, Y.; Li, L.; Zhang, T.; Wang, H.; Xue, J.; Ding, L.; Wang, S.; Caro, J.; Gogotsi, Y. MXene molecular sieving membranes for highly efficient gas separation. Nat. Commun. 2018, 9, 155. [Google Scholar] [CrossRef]
  27. Nam, S.; Umrao, S.; Oh, S.; Shin, K.H.; Park, H.S.; Oh, I.K. Sonochemical self-growth of functionalized titanium carbide nanorods on Ti3C2 nanosheets for high capacity anode for lithium-ion batteries. Compos. Part B 2020, 181, 107583. [Google Scholar] [CrossRef]
  28. Ahmed, B.; Anjum, D.H.; Gogotsi, Y.; Alshareef, H. Atomic layer deposition of SnO2 on MXene for Li-ion battery anodes. Nano Energy 2017, 34, 249–256. [Google Scholar] [CrossRef] [Green Version]
  29. Hou, T.; Wang, B.B.; Ma, M.L.; Feng, A.L.; Huang, Z.Y.; Zhang, Y.; Jia, Z.; Tan, G.X.; Cao, H.J.; Wu, G.L. Preparation of two-dimensional titanium carbide (Ti3C2Tx and NiCo2O4 composites to achieve excellent microwave absorption properties. Compos. Part B 2020, 180, 107577. [Google Scholar] [CrossRef]
  30. Wang, F.; Cao, M.; Qin, Y.; Zhu, J.; Wang, L.; Tang, Y. ZnO nanoparticle-decorated two-dimensional titanium carbide with enhanced supercapacitive performance. RSC Adv. 2016, 6, 88934–88942. [Google Scholar] [CrossRef]
  31. Zhang, Y.; Guo, B.; Hu, L.; Xu, Q.; Li, Y.; Liu, D.; Xu, M. Synthesis of SnS nanoparticle-modified MXene (Ti3C2Tx) composites for enhanced sodium storage. J. Alloys Compd. 2018, 732, 448–453. [Google Scholar] [CrossRef]
  32. Sandler, J.; Kirk, J.E.; Kinloch, I.A.; Shaffer, M.S.P.; Windle, A.H. Ultra-low electrical percolation threshold in carbon-nanotube-epoxy composites. Polymer 2003, 44, 5893–5899. [Google Scholar] [CrossRef]
  33. Tjong, S.C.; Liang, G.D.; Bao, S.P. Electrical behavior of polypropylene/multiwalled carbon nanotube nanocomposites with low percolation threshold. Scr. Mater. 2007, 57, 461–464. [Google Scholar] [CrossRef]
  34. Lu, T.; Jiang, M.; Jiang, Z.; Hui, D.; Wang, Z.; Zhou, Z. Effect of surface modification of bamboo cellulose fibers on mechanical properties of cellulose/epoxy composites. Compos. Part B 2013, 51, 28–34. [Google Scholar] [CrossRef]
Nanomaterials 10 00162 g001 550
Figure 1. The schematic illustration for the synthetic procedure of the EP/Ti3C2Tx MXene nanosheets composites.
Figure 1. The schematic illustration for the synthetic procedure of the EP/Ti3C2Tx MXene nanosheets composites.
Nanomaterials 10 00162 g001
Nanomaterials 10 00162 g002 550
Figure 2. SEM images of Ti3AlC2 MAX (a) at a lower magnification, (b) at a higher magnification; SEM images of accordion-like multi-layered Ti3C2Tx (c) at a lower magnification, (d) at a higher magnification); SEM images of Ti3C2Tx nanosheets (e) at a lower magnification, and (f) at a higher magnification).
Figure 2. SEM images of Ti3AlC2 MAX (a) at a lower magnification, (b) at a higher magnification; SEM images of accordion-like multi-layered Ti3C2Tx (c) at a lower magnification, (d) at a higher magnification); SEM images of Ti3C2Tx nanosheets (e) at a lower magnification, and (f) at a higher magnification).
Nanomaterials 10 00162 g002
Nanomaterials 10 00162 g003 550
Figure 3. (a) SEM image of Ti3C2Tx nanosheets, (b) energy-dispersive X-ray spectroscopy (EDX) spectrum of Ti3C2Tx nanosheets, and (c) element mappings of Ti3C2Tx nanosheets.
Figure 3. (a) SEM image of Ti3C2Tx nanosheets, (b) energy-dispersive X-ray spectroscopy (EDX) spectrum of Ti3C2Tx nanosheets, and (c) element mappings of Ti3C2Tx nanosheets.
Nanomaterials 10 00162 g003
Nanomaterials 10 00162 g004 550
Figure 4. (a) XRD patterns of Ti3AlC2 MAX (A) and Ti3C2Tx nanosheets (B). (b) FTIR spectra of Ti3C2Tx nanosheets.
Figure 4. (a) XRD patterns of Ti3AlC2 MAX (A) and Ti3C2Tx nanosheets (B). (b) FTIR spectra of Ti3C2Tx nanosheets.
Nanomaterials 10 00162 g004
Nanomaterials 10 00162 g005 550
Figure 5. (a) TEM image of Ti3C2Tx nanosheets, (b) HRTEM image of Ti3C2Tx nanosheets, and (c) selected-area electron diffraction (SAED) of Ti3C2Tx nanosheets.
Figure 5. (a) TEM image of Ti3C2Tx nanosheets, (b) HRTEM image of Ti3C2Tx nanosheets, and (c) selected-area electron diffraction (SAED) of Ti3C2Tx nanosheets.
Nanomaterials 10 00162 g005
Nanomaterials 10 00162 g006 550
Figure 6. XRD patterns of epoxy (a), Ti3C2Tx MXene nanosheets (b), EP/Ti3C2Tx MXene nanosheets composite containing 0.4 wt % Ti3C2Tx (c), EP/Ti3C2Tx MXene nanosheets composite containing 1.0 wt % Ti3C2Tx (d), and EP/Ti3C2Tx MXene nanosheets composite containing 1.6 wt % Ti3C2Tx (e).
Figure 6. XRD patterns of epoxy (a), Ti3C2Tx MXene nanosheets (b), EP/Ti3C2Tx MXene nanosheets composite containing 0.4 wt % Ti3C2Tx (c), EP/Ti3C2Tx MXene nanosheets composite containing 1.0 wt % Ti3C2Tx (d), and EP/Ti3C2Tx MXene nanosheets composite containing 1.6 wt % Ti3C2Tx (e).
Nanomaterials 10 00162 g006
Nanomaterials 10 00162 g007 550
Figure 7. The electrical conductivity (K, S/m) of the EP/Ti3C2Tx MXene nanosheets composite under various mass fractions of Ti3C2Tx MXene nanosheets.
Figure 7. The electrical conductivity (K, S/m) of the EP/Ti3C2Tx MXene nanosheets composite under various mass fractions of Ti3C2Tx MXene nanosheets.
Nanomaterials 10 00162 g007
Nanomaterials 10 00162 g008 550
Figure 8. The (a) tensile strength and (b) impact strength of the EP/Ti3C2Tx MXene nanosheets composite under various contents of the Ti3C2Tx MXene nanosheets.
Figure 8. The (a) tensile strength and (b) impact strength of the EP/Ti3C2Tx MXene nanosheets composite under various contents of the Ti3C2Tx MXene nanosheets.
Nanomaterials 10 00162 g008
Nanomaterials 10 00162 g009 550
Figure 9. The fracture surfaces of the EP/Ti3C2Tx MXene nanosheets composite containing 0.4 wt % Ti3C2Tx MXene nanosheets (a), 0.8 wt % Ti3C2Tx MXene nanosheets (b), 1.2 wt % Ti3C2Tx MXene nanosheets (c), and 1.6 wt % Ti3C2Tx MXene nanosheets (d).
Figure 9. The fracture surfaces of the EP/Ti3C2Tx MXene nanosheets composite containing 0.4 wt % Ti3C2Tx MXene nanosheets (a), 0.8 wt % Ti3C2Tx MXene nanosheets (b), 1.2 wt % Ti3C2Tx MXene nanosheets (c), and 1.6 wt % Ti3C2Tx MXene nanosheets (d).
Nanomaterials 10 00162 g009
Table
Table 1. Element content of Ti3C2Tx MXene nanosheets.
Table 1. Element content of Ti3C2Tx MXene nanosheets.
ElementAtomic %Weight %
C27.411.0
Ti40.869.0
O19.011.1
F11.67.8
Al1.21.1

Share and Cite

MDPI and ACS Style

Feng, A.; Hou, T.; Jia, Z.; Zhang, Y.; Zhang, F.; Wu, G. Preparation and Characterization of Epoxy Resin Filled with Ti3C2Tx MXene Nanosheets with Excellent Electric Conductivity. Nanomaterials 2020, 10, 162. https://doi.org/10.3390/nano10010162

AMA Style

Feng A, Hou T, Jia Z, Zhang Y, Zhang F, Wu G. Preparation and Characterization of Epoxy Resin Filled with Ti3C2Tx MXene Nanosheets with Excellent Electric Conductivity. Nanomaterials. 2020; 10(1):162. https://doi.org/10.3390/nano10010162

Chicago/Turabian Style

Feng, Ailing, Tianqi Hou, Zirui Jia, Yi Zhang, Fan Zhang, and Guanglei Wu. 2020. "Preparation and Characterization of Epoxy Resin Filled with Ti3C2Tx MXene Nanosheets with Excellent Electric Conductivity" Nanomaterials 10, no. 1: 162. https://doi.org/10.3390/nano10010162

APA Style

Feng, A., Hou, T., Jia, Z., Zhang, Y., Zhang, F., & Wu, G. (2020). Preparation and Characterization of Epoxy Resin Filled with Ti3C2Tx MXene Nanosheets with Excellent Electric Conductivity. Nanomaterials, 10(1), 162. https://doi.org/10.3390/nano10010162

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop